Investigation of Effects of Mig Welding on Corrosion Behaviour of AISI 1010 Carbon Steel
This paper presents the corrosion behaviour of welded low carbon steel at different welding voltages and filler materials. The welding process was conducted on butt joint 
specimens using the metal inert gas (MIG) technique at a welding voltage range of 19 to 21 V with 1 V interval, and the filler materials used were ER 308L and ER 70S-6 with 
1.2 mm diameter. Heat treatment through full annealing was done to the welded low carbon steel, and the corrosion behaviour was tested using a synthetic seawater 
environment with 3.5 wt% NaCl. Microstructure changes were observed using a scanning electron microscope (SEM). The results showed that the corrosion rate decreased when the welding voltage increased, as it directly affected the welding heat input. The welding heat input was found to have a significant effect on the corrosion rate as it changed the ferrite content in the microstructure of the specimens. Decrease in the corrosion rate was also found when the full annealing process was done to the 
specimens and ER 308L filler material was used. From a metallographic study, iron oxides and pitting were found on the surface of the exposed area after the corrosion test. 
It is apparent that the combination of higher welding voltage, heat treatment and the use of ER 308L filler material can reduce the corrosion rate of AISI 1010 carbon steel.
Effect of Ferritic - Martensitic Constituent on Mechanical Property and Corrosion Behaviour of Medium Carbon Dual Phase (DP) Steel
This investigation was carried out to study the effect ferritic-martensitic constituent on mechanical property and corrosion behaviour of medium carbon DP steel. Several stages of heat treatment were applied on the as-received medium carbon steel which composed of lamellarizing, quenching and tempering process. As-received medium carbon steel was assigned as a reference sample for comparison analysis. Mechanical property was evaluated using Vickers hardness to examine the effect of changing the ferritic-martensitic constituent of the medium carbon steel. Besides, the effect of this constituent on the corrosive behaviour of the medium carbon DP steel was investigated using 1 M hydrochloric acid solution.
Morphological characterization of Eustrongylides sp. larvae (Nematoda, Dioctophymatoidea) parasite of Rhinella marina (Amphibia: Bufonidae) from Eastern Amazonia.
Absctract Eustrongylides spp. nematodes have birds as final hosts and uses other vertebrates as intermediate/paratenic host (fish, amphibians and reptiles) and have zoonotic potential. In amphibians, the larvae may be located in the subcutaneous tissues, liver and mesentery, between the muscle fibres, especially in the lower limbs. Rhinella marina, which is widely observed in Brazil, has exhibited complex diversity in its helminth fauna, reflecting the unique habitat of the Amazon biome. For the first time, this study describes the morphological aspects of third-stage larvae of Eustrongylides sp. in Rhinella marina from Santa Cruz do Ararí, Marajó Archipelago, Eastern Amazonia, using light and scanning electron microscopy.