Hydrogen-Induced Delayed Cracking in TRIP-Aided Lean-Alloyed Ferritic-Austenitic Stainless Steels
Susceptibility of three lean-alloyed ferritic-austenitic stainless steels to hydrogen-induced delayed cracking was examined, concentrating on internal hydrogen contained in the materials after production operations. The aim was to study the role of strain-induced austenite to martensite transformation in the delayed cracking susceptibility. According to the conducted deep drawing tests and constant load tensile testing, the studied materials seem not to be particularly susceptible to delayed cracking. Delayed cracks were only occasionally initiated in two of the materials at high local stress levels. However, if a delayed crack initiated in a highly stressed location, strain-induced martensite transformation decreased the crack arrest tendency of the austenite phase in a duplex microstructure. According to electron microscopy examination and electron backscattering diffraction analysis, the fracture mode was predominantly cleavage, and cracks propagated along the body-centered cubic (BCC) phases ferrite and α’-martensite. The BCC crystal structure enables fast diffusion of hydrogen to the crack tip area. No delayed cracking was observed in the stainless steel that had high austenite stability. Thus, it can be concluded that the presence of α’-martensite increases the hydrogen-induced cracking susceptibility.
Fracture analysis of the threaded joint of the level gauge in a reabsorption tower
Abstract The fracture of the threaded joint of the level gauge in the reabsorption tower has been analyzed. Through the investigation of operational condition, macroscopic examination of the broken threaded joint, chemical composition analysis of the threaded joint material, metallographic examination of the threaded joint and specimens with cracks, mechanical property analysis, microscopic appearance analysis and energy spectrum analysis, the cracking mode can be attributed to Stress Corrosion Cracking (SCC) of austenitic stainless steel caused by the combined action of wet H2S and Cl− in medium. In this case, the material of the broken threaded joint was not 304 stainless steel, but a high Mn substituted Ni steel, beside, the threaded joint produced a lot of induced martensite during large deformation of cold working which greatly increase the sensitivity of SCC, so the material did not meet the requirements was the main factor in this fracture accident.
Degradable polymers : principles and applications
1. Why Biodegradable Polymers? G. Scott. 2. An Overview of Biodegradable Polymers and Biodegradation of Polymers S.H. Huang. 3. Degradation and Stabilization of Carbon-Chain Polymers G. Scott. 4. Techniques and Methods of Polymer Degradation S. Karlsson, A.-C. Albertsson. 5. Biodegradation of Aliphatic Polyesters Suming Li, M. Vert. 6. Starch-Polymer Composites C. Bastioli. 7. Polymers from Renewable Sources E. Chiellini, et al. 8. Sustainable Poly(Hydroxyalkanoate) (PHA) Production G. Braunegg. 9. Polyhydroxyalkanoates: Properties and Modification for High Volume Application I. Chodak. 10. Biodegradable Polymers in Medicine E Piskin. 11. Environmentally Biodegradable Water-Soluble Polymers G. Swift. 12. Plastics and the Environment J. Guillet. 13. Degradable Hydrocarbon Polymers in Waste and Litter Control G. Scott, D.M. Wiles. Subject Index.