Adsorption behavior of propylamine on activated carbon fiber surfaces as induced by oxygen functional complexes.
In this study, the surfaces of activated carbon fibers (ACFs) were modified by nitric acid to introduce surface oxygen complexes and to observe the influence of those complexes on the propylamine adsorption of the ACFs. It was found that the oxygen complexes including carboxylic and phenolic groups were predominantly increased, resulting in the increase of total surface acidity. However, the specific surface areas and the total pore volumes of the modified ACFs were decreased by 5-8% due to the increased blocking (or demolition) of micropores in the presence of newly introduced complexes. Despite the decrease of textural properties, it was found that the amount of propylamine adsorbed by the modified ACFs was increased by approximately 17%. From the XPS results, it was observed that propylamine reacted with strong or weak acidic groups, such as COOH or OH, on the ACF surfaces, resulting in the formation of pyrrolic-, pyridonic-, or pyridine-like structures.
Polar nitrogen compounds and their behaviour in the drinking water treatment process.
Aliphatic and alicyclic amines as well as ethanolamines are extremely polar compounds, frequently found in the environment, and some of them have high toxicity. To address the contamination of selected German surface waters examined and the importance of bank filtration in Eastern Germany, investigations on the behaviour of polar organic nitrogen compounds during water treatment were carried out. Test conditions were designed appropriately for drinking water treatment conditions, and the tests were carried out using model water as well as bank filtrate. Test filter studies of microbial degradation of selected compounds demonstrated the following order of biodegradability: ethanolamine > dimethylamine > pyrrolidine > ethylenediamine. piperidine > diethylamine > morpholine > piperazine > cyclohexylamine. Flocculation tests using iron salts as well as aluminium salts as coagulants showed very low removal rates for the amines. The best results for the removal of the polar organic nitrogen compounds from the water were obtained using ozonation. Based on the reaction-rate constants, the order of degradation by ozone is: piperazine > morpholine > ethylenediamine > piperidine, cyclohexylamine > dimethylamine > ethanolamine > pyrrolidine > diethylamine. Disinfection by chlorine-containing agents under drinking water treatment conditions did not give effective elimination of the selected polar nitrogen compounds.
Evaluation of CuAl2O4 as an Oxygen Carrier in Chemical-Looping Combustion
The chemical-looping combustion (CLC) process is a novel solution for efficient combustion with intrinsic separation of carbon dioxide. The process uses a metal oxide as an oxygen carrier to transfer oxygen from an air to a fuel reactor where the fuel, or gasification products of the fuel, reacts with the solid oxygen carrier. In this work, copper(II) aluminate (CuAl2O4) was assessed as a potential oxygen carrier using methane as fuel. The carrier particles were produced by freeze–granulation and calcined at 1050 °C for a duration of 6 h. The chemical-looping characteristics were evaluated in a laboratory-scale fluidized-bed reactor in the temperature range of 900–950 °C during 45 alternating redox cycles. The oxygen carrier exhibited reproducible and stable reactivity behavior in this temperature range. Neither agglomeration nor defluidization was noticed in any of the cycles carried out at 900–925 °C. However, after reactivity tests at 950 °C, soft agglomeration and particle fragmentation were observed. Systematic phase analysis of the Cu–Al–O system during the redox cycle was carried out as a function of duration of reduction and oxygen concentration during the oxidation period. It was found that the CuAl2O4 is reduced to copper(I) aluminate (CuAlO2; delafossite), Cu2O, and elemental Cu. The CuAlO2 phase is characterized by slow kinetics for oxidation into CuO and CuAl2O4. Despite this kinetic limitation, complete conversion of methane with reproducible reactivity of the oxygen carrier is achieved. Thus, CuAl2O4 could be a potential oxygen carrier for chemical-looping combustion.