Numerical Study on Single Point Incremental Sheet Metal Forming Process
-Single Point Incremental Sheet Forming (SPIF) is an innovative forming approach for sheet materials. In this process, the forming tool is moved along a predefined tool path which is a series of contour constructed a final shape of product by using numerical controlled technology. This paper investigated finite element analysis simulation to predict the mechanical failures in single point incremental sheet metal forming (SPIF). In the present paper, some of these aspects, namely, the phenomenon of the wall thickness overstretch along depth and the effect of the tool path on the distribution of the wall thickness using finite element simulations etc. are investigated. It is observed from the analysis that the single point incremental sheet metal forming is very much time consuming and also the depth of stretch with different step size and tool diameters have been implemented.
Tool Path and Sheet Thickness Distribution of Axisymmetric Cup in Single Point Incremental Forming
This study involved planning different tool paths for an axisymmetric cup to explore the forming characteristics of the single point incremental forming (SPIF) process. In addition, this study developed a gradient theory to compute the inclined angle between the tangential and horizontal directions of the cup formed using single point incremental forming. The sheet thickness distribution of the cup was also calculated. To verify the theory, circle arc cups were formed by CNC machining using different tool paths. It was found that the cup formed using the spiral evolutional snail-line tool path produced a better surface than that formed using the equal height evolutional tool path. The sheet thicknesses of circle arc cups obtained by the experiment and using the cosine law were compared. A larger deviation was noted in the initial portion of the cup, whereas a smaller deviation was found in the other portion. This study also adopted a dual-conical cup to investigate the relationship between thickness and the initial inclined angle at the initial portion. It was found that a larger initial inclined angle led to good coincidence between the experimental and theoretical sheet thicknesses.
Measuring Sheet Resistances of Dielectrics Using Co‐Planar Hydrogel Electrochemical Cells with Practical Applications to Characterize the Protective Quality of Paints on Sculptures
Electrical properties of thin dielectric films at the solid-liquid phase boundary are an important performance characteristic of many devices, coatings and sensors. In this paper, co-polymeric hydrogels of polyacrylic acid co-sulfonic acid, swollen with a salt solution to act as the solid electrolyte, were used to assess interfaces using electrochemical impedance spectroscopy (EIS) in a co-planar geometry. Silane-modified glasses were characterized by the co-planar hydrogel EIS cell and found to be distinguishable based on their surface monolayer chemistry. EIS measurements were also made on primed and painted metal substrates, using both test panels and an outdoor sculpture, Tony Smith's Stinger. The panels were then exposed to accelerated and outdoor weathering and showed degradation on the surface paint layers, which was observable electrochemically using EIS and confirmed visually by SEM. Electrochemical spectral features were compared between data from a standard paint-test cell versus this co-planar hydrogel cell; both cell types were able to measure coating capacitance, providing useful information about the condition of the bulk coating. Yet, sheet resistance (Rs) was a spectral feature seen only by the co-planar hydrogel cell. Thus, it can be concluded that the use of such co-planar hydrogel cells can provide an earlier warning sign to coating degradation and such cells provide a new type of spectral information that is not assessable by the standard geometry.