Effect of a titanium nitride interlayer on the densification, properties and microstructure of cermets based on alumina and nickel — Part 2: Microstructures
SEM microstructural analyses in conjunction with EDX and TEM microstructural analyses have been conducted with cermets based on nickel and alumina, the latter as such and with a chemical-vapour-deposited titanium nitride layer. It has been proved that there is excellent bonding at both the Al2O3/TiN and the TiN/Ni interface, whereas Al2O3 and Ni do not adhere to each other. This is the reason for the observation that the mechanical properties as well as the densification of cermets consisting of Al2O3 and Ni are enhanced by applying a TiN interlayer between the ceramic phase and the metallic phase.
Effect of a titanium nitride interlayer on the densification, properties and microstructure of cermets based on alumina and nickel — Part 1: Densification and properties
In order to manufacture cermets based on Al2O3 and Ni, Al2O3 particles were first coated with TiN by CVD and then mixed with pure Ni powder. The cermets were produced from the mixed powders by powder metallurgy processes. The relative density and the mechanical properties of the cermets are improved due to the presence of the TiN interlayer. The contribution of this interlayer to the mechanical properties of the cermets produced by hot-pressing is superior to that by pressureless sintering.
Precise Nondestructive Determination of the Density of Porous Ceramics
A fast, accurate inexpensive, and nondestructive method to determine the density of very porous ceramics is discussed. This method is an extension of the water-displacement technique with three weighings and the use of glycerol instead of water. For small (1.13 g), 29% porosity B/sub 4/C/sub 3/ pellets, the precision is 0.002 g/cm/sup 3/ and the accuracy is better than 0.006 g/cm/sup 3/ compared with the geometric density.