Synthesis and Swelling Behavior of Carrageenans-Graft-Poly(Sodium Acrylate)/Kaolin Superabsorbent Hydrogel Composites
In the present paper, a novel superabsorbent hydrogel composite based on carrageenan have been prepared via graft copolymerization of acrylic acid (AA) in the presence of kaolin powder using methylenebisacrylamide (MBA) as a crosslinking agent and ammonium persulfate (APS) as an initiator. The certain variables of the graft copolymerization (i.e. the monomer, the initiator and the crosslinker concentration as well as kaolin/carrageenan weight ratio) affected on the ultimate water-swelling capacity were optimized. The composite structure was confirmed using FTIR spectroscopy. A new absorption band at 1707 cm in the 1 composite spectrum confirmed kaolin-organic polymer linkage. The effect of kaolin amount and MBA concentration showed that with increasing of these parameters, the water absorbency of the superabsorbent composite was decreased. Because of their exceptional properties, i.e. anhydrogalactose units (13). The types of carrageenans biocompatibility, biodegradability, renewability and differ only in the position and number of ester sulfate non-toxicity, polysaccharides and proteins are the groups. Following a continuous research on modification main part of the natural-based superabsorbent of carrageenans (14), in this work, we attempt to hydrogels. The higher production cost and low gel synthesize and characterize new superabsorbent strength of these superabsorbents, however, restrict composites based on carrageenan in the presence of their application widely. To improve these limitations, kaolin particles. The preparation of the biopolymer-based inorganic compounds with low cost can be used. The superabsorbent composites can also improve the introduction of inorganic fillers to a polymer matrix mechanical properties of materials and can lower the cost increases its strength and stiffness properties. of the finished product compared with the synthetic Among inorganic compounds, special attention has counterparts as well as providing biodegradable been paid to clay minerals in the field of nanocomposites characteristics.
Novel polymeric hydrogel composites: Synthesis, physicochemical, mechanical and biocompatible properties
In this research study, novel hydrogel composite films were constructed using different ratios of poly (vinyl alcohol) (PVA)/kappa-carrageenan (KC) (PVA90/KC10%, PVA80/KC20%, PVA70/KC30%, PVA60/KC40%) crosslinked with glutaraldehyde (0.025%) and investigated their physicochemical characteristics such as mechanical, thermal, morphological, swelling behaviour, and cell viability. SEM and FTIR revealed that surface morphology changed to heterogeneous and the presence of molecular interaction among the polymers. PVA90KC10 and PVA60KC40 exhibited smaller and larger pores on surface respectively. The change in the proportion of PVA and KC also triggered the tensile strength (Ts) of the film and the highest Ts observed were 21.60 MPa for PVA60KC40. Moreover, the thermal analysis showed three-phase degradation, and an increase in KC40 concentration results inversely proportional to a decrease in the rate of thermal degradation. Further, swelling and in-vitro biodegradation study confirmed the enhanced perseverance of water uptake for PVA60KC40 (286%) due to pores structure of the hydrogel film and PVA and KC alone degraded faster as compare to other films results suggested higher concentration of PVA90KC10 showed lower degradation rate and highest for PVA60KC40 about 6% and 22% respectively. Further, the cell viability was studied with MTT assay method by using NIH3T3 and HEK-293 cells for biocompatibility study revealed NIH3T3 cells were more biocompatible than HEK-293 and cell viability percent for PVA60KC40 showed the highest cell attachment about 99%. Overall corroborating data obtained from the study attested to the average swelling, appreciable mechanical characters, good interaction between molecules, and cell viability of the constructed PVA/KC hydrogel film, these all characters pave to be used as a potential template for biomedical applications such as tissue engineering and drug delivery.
Liposomal ophthalmic drug delivery. III. Pharmacodynamic and biodisposition studies of atropine
Abstract The potential of liposomes as an ophthalmic drug delivery system was investigated by comparing disposition and pupillary dilatory effect of atropine base and atropine sulphate in solution and various liposomal forms when topically instilled to the rabbit eye. Atropine base entrapped in multilamellar lipid vesicles (MLVs) with positive surface charge displayed the most prolonged effect lasting up to 12 h. MLVs with neutral and negative charges maintained the effect for 9 h while atropine in solution form was effective for only 7 h. Preparations containing atropine sulphate displayed a similar pattern although were shorter-acting than corresponding base products. All preparations whether salt or base, were equally effective in producing maximal response. In vivo drug disposition studies indicated the liposomal form produced significantly higher drug levels in the anterior tissues of the eye up to 8 h after instillation. Increased ocular bioavailability of atropine to these tissues was attributed to enhancement of pulse entry with little evidence of sustained drug release. It could be concluded that liposome encapsulation extended the duration of action and favourably altered disposition of atropine when topically instilled to the rabbit eye.