Effect of Mill Type on Morphology of AA6013 Aluminium Powder
In conventional recycling method, metal chips are cast after pressing and melting in electric arc furnace. Material loss occurs during the recycling from liquid metal due to the several reasons. Direct recycling method which produces the aluminium powder from aluminium chips using mechanical mill can be an alternative to conventional recycling method. Thus material and energy losses, and labour cost will be reduced by direct recycling method without melting. In this study, the particle morphology of powder direct recycled from AA6013 aluminium alloy chips with cryogenic, disc and ball type grinders is investigated. Mechanical milling resulted flaky and irregular shaped AA6013 particles. It was ascertained that the chips did not break sufficiently in despite of the long duration milling mechanisms by ball mill. Cryogenic mill provides the energy required for milling mechanisms to act. Disc mill has the highest impact energy was determined. Consequently, efficiency of ball mill is lower than the efficiency of cryogenic and disc type mills. Shape factors of powders produced with ball and cryogenic mills were found greater than that of the powder produced by disc mill. Disc mill has the most efficient and effective impact energy which produces the smaller particles per minute, was determined.
Direct recycling of aluminium chips into extruded products
Abstract In the paper is described the method of direct convertion of aluminium and its alloys chips into final products. The chips were comminuted in cutting device, and for the future processing the granulated chips larger than 5 mm in length were eliminated. Such prepared chips were pre-pressed with the pressure of 210 MPa and hot extruded for final products. High density and good properties of products can be obtained at high extrusion temperature which makes possible the plastic flow of matrix into pores and voids and at relatively low extrusion rates which gives the time for diffusional transport of matter.
Evaluation of Impact of Yarn Count and Stitch Length on Pilling, Abrasion, Shrinkage and Tightness Factor of 1 ? 1 Rib Cotton Knitted Fabrics
This study investigates the impact of yarn count and stitch length of 100% cotton knitted fabrics. 1 × 1 ribs structured fabrics were used in this research work. The stitch length 2.50 mm, 2.52 mm, 2.60 mm, 2.70 mm, 2.80 mm and 2.96 mm were used of the yarn count of 26Ne, 28Ne and 36Ne. The areal densities of the grey fabrics were in various amounts. The impacts of yarn count and stitch length were measured concerning pilling resistance, abrasion resistance, and shrinkage and tightness factor. The result showed that the fabric pilling grade decreased while number of cycle increased. Abrasion resistance decreased but length wise shrinkage increased despite the fact that the stitch length increased. The results also exposed that the tightness factor of the fabric increased with the increase of the stitch length in both dyeing and washing state and finished state compared to grey state for the yarn count 26Ne and homogeneous result not found for yarn count 28Ne and 36 Ne. Evaluation of Impact of Yarn Count and Stitch Length on Pilling, Abrasion, Shrinkage and Tightness Factor of 1 × 1 Rib Cotton Knitted Fabrics