Mechanism of Enhancing Extraction of Vanadium from Stone Coal by Roasting with MgO
In this paper, the extraction of vanadium from stone coal by roasting with MgO and leaching with sulfuric acid has been investigated, and the mechanism analysis of stone coal roasting with MgO was studied. The results indicated that under the conditions that the mass fraction of the particles with grain size of 0–0.074 mm in raw ore was 75%, the roasting temperature was 500 °C, the roasting time was 1 h, MgO addition was 3 wt %, the sulfuric acid concentration was 20 vol %, the liquid-to-solid ratio was 1.5 mL/g, the leaching temperature was 95 °C, and leaching time was 2 h, resulting in a vanadium leaching efficiency of 86.63%, which increased by 7.73% compared with that of blank roasting. The mechanism analysis showed that the degree of calcite decomposition was low and, thus, magnesium vanadate was more easily formed than calcium vanadate below 500 °C. Moreover, magnesium vanadate was easier to dissolve than calcium vanadate during the sulfuric acid leaching process. Thus, the vanadium leaching efficiency was enhanced by using MgO as a roasting additive below 500 °C. Additionally, at high temperature the formation of tremolite would consume calcium oxide produced from the decomposition of calcite, thus, the formation of calcium vanadate was hindered, and V2O5 would react with MgO to form magnesium vanadate. Therefore, the vanadium leaching efficiency of roasting with MgO was higher than that of blank roasting at high temperature.
Synthesis of Di-(2-ethylhexyl) Phosphoric Acid (D2EHPA)-Tributyl Phosphate (TBP) Impregnated Resin and Application in Adsorption of Vanadium(IV)
In order to improve the adsorption capability of solvent-impregnated resins (SIRs) for vanadium(IV) (V(IV)), the dual extractant (D2EHPA (Di-(2-ethylhexyl) phosphoric acid) and TBP (Tributyl phosphate)) impregnated resins (D-TIRs) were prepared by impregnating AmberliteTM XAD-16HP macroporous resins with the mixed extractant that is composed by different molar ratios of D2EHPA to TBP. The effects of the ratio of D2EHPA to TBP on the performance of D-TIRs were investigated. The results show that the impregnation ratio of the D-TIRs decreases gradually with the increasing proportion of TBP in the mixed extractant. The sole-TBP impregnated resins (TIRs) have no adsorption capability for V(IV), indicating that the adsorption of V(IV) is attributed to D2EHPA. The adsorption capacity of D-TIRs for V(IV) attained the maximum when the ratio of D2EHPA to TBP is 7:3 at pH 1.8, and it can be improved by increasing the extractants concentration during the impregnation process. Adsorption isotherm indicates that the addition of TBP can increase the adsorption capacity of D-TIRs for V(IV) from 24.65 to 29.75 mg/g after 16 h reaction. Adsorption kinetics verifies that the addition of TBP can largely accelerate the adsorption equilibrium of V(IV) onto the D-TIRs and V(IV). Electrospray ionization (ESI) mass spectra and Fourier transform infrared spectra (FT-IR) analysis indicates that the addition of TBP to D2EHPA can make some dimeric D2EHPA change to monomers by breaking the hydrogen bonds of D2EHPA-dimers, leading to the result that the pseudo-second order kinetic for the adsorption of V(IV) onto the D2EHPA impregnated resins (DIRs) converts to the pseudo-first order kinetic for that onto the D-TIRs. Also, D-TIRs have better separation capability of V(IV) from Fe(II) and Al(III) in the vanadium leaching solution than DIRs.
Timber, its nature and behaviour
Preface. Acknowledgements. Chapter 1 - Structure of Timber. Chapter 2 - Appearance of Timber in Relation to its Structure. Chapter 3 - Mass Volume Relationships. Chapter 4 - Movement in Timber. Chapter 5 - Flow in Timber. Chapter 6 - Deformation Under Load. Chapter 7 - Strength and Failure in Timber. Chapter 8 - Durability of Timber. Chapter 9 - Processing of Timber. Index.