Thermoelectric Properties of Films and Monocrystalline Whiskers of Tellurium
Tellurium is an interesting semiconductor for thermoelectric applications because its thermopower is high (500 muV/K). Its figure of merit is low in the bulk because it has high thermal conductivity. However, in confined geometries, the phonon conductivity decreases due to phonon scattering. Therefore we have investigated the thermoelectric properties of Te films and whiskers. We report a study of the thermoelectric properties of Te films obtained by vacuum-condensation method on glass, polyamide, mica at various temperatures of condensation. The crystallographic structure of the films is characterized by the distribution function of the grain major axis. It is shown that the films condensed at 433 K possess the highest mobility. Te whiskers were grown from the paragas phase and they were single crystals in the form of hexahedral cylinder having cavities inside. When deposited on cold substrate, the cylinders had no cavities. The direction of the whisker crystal growth was always [0001] with respect to the whiskers length. It is shown that in films with the thickness of ~1 mum, the room temperature thermopower S is 330 muV/K and increases with temperature increasing (S = 450 muV/K at 450 K). The resistivity decreases with the temperature growth, as a result the power factor alpha2sigma increases by almost a factor of two. The 77 K electric conductivity of Te whiskers is 2-to-3 order-of-magnitude higher than in bulk crystals, presumably due to high structural perfection of whisker crystals. The thermopower in the range of 300 K is S = 400-750 muV/K
Electrodeposition of tellurium film on polyaniline-coated macroporous phenolic foam and its thermopower
Tellurium film was successfully electrodeposited on to macroporous phenolic foam with the assistance of a conducting polyaniline coating layer. The thermopower of the obtained macroporous Te film was measured. The dense and uniform Te film was composed of columnar crystals that preferably oriented along c-axis direction. The seebeck coefficient of the macroporous Te film showed a peak value of 342 μV/K at 473 K.
Evaluation of Impact of Yarn Count and Stitch Length on Pilling, Abrasion, Shrinkage and Tightness Factor of 1 ? 1 Rib Cotton Knitted Fabrics
This study investigates the impact of yarn count and stitch length of 100% cotton knitted fabrics. 1 × 1 ribs structured fabrics were used in this research work. The stitch length 2.50 mm, 2.52 mm, 2.60 mm, 2.70 mm, 2.80 mm and 2.96 mm were used of the yarn count of 26Ne, 28Ne and 36Ne. The areal densities of the grey fabrics were in various amounts. The impacts of yarn count and stitch length were measured concerning pilling resistance, abrasion resistance, and shrinkage and tightness factor. The result showed that the fabric pilling grade decreased while number of cycle increased. Abrasion resistance decreased but length wise shrinkage increased despite the fact that the stitch length increased. The results also exposed that the tightness factor of the fabric increased with the increase of the stitch length in both dyeing and washing state and finished state compared to grey state for the yarn count 26Ne and homogeneous result not found for yarn count 28Ne and 36 Ne. Evaluation of Impact of Yarn Count and Stitch Length on Pilling, Abrasion, Shrinkage and Tightness Factor of 1 × 1 Rib Cotton Knitted Fabrics