Account of Non-Diagonal d-d-Electron Couplings in CoNi Liquid Alloy
The partial Wills-Harrison effective pair potentials in liquid equiatomic Co-Ni alloy are considered. It is shown that the account of the non-diagonal d-d couplings between electrons leads to similar changes in characteristics of the pair-potential first minimum as for Fe-Co and Fe-Ni equiatomic alloys.
Non-Diagonal Couplings between d Electrons: Generalization to Binary Alloys of Transition Metals
Suggested earlier correction to the Wills-Harrison model is extended to a binary mixture of transition metals. It is found that the full account of the non-diagonal couplings between d electrons leads to the vanishing the d-electron contributions to the partial pair interactions.
Evolution of carbide precipitates in Hastelloy N joints during welding and post weld heat treatment
Abstract The effects of welding and post weld heat treatment (PWHT) on the morphology, composition and lattice parameter of the precipitates in the welding joints of Hastelloy N alloy have been investigated. Joint samples were prepared using a gas tungsten arc welding process with ERNiMo-2 fillers, and then solid-solution treated at 1100 °C for 20 min. After welding, eutectic M6C carbides can be observed in the heat affected zones (HAZ) and weld zones (WZ). These eutectic M6C carbides become spheroidized during the following PWHT. The concentration of Si decreases during the transformation from the primary ones to eutectic ones, and then increases during the spheroidizing process. The total concentration of Si + Cr in M6C carbides remains stable during welding and PWHT. At the same time, the heat leads to the outward diffusion of Mo from the M6C carbides, which results in a decrease of the lattice parameter.