Study of the miscibility of poly(styrene-co-4-vinylbenzoic acid) with poly(ethyl methacrylate) or with poly[ethyl methacrylate-co-(2-N,N-dimethylaminoethyl) methacrylate] by inverse gas chromatography.
Poly(styrene) is immiscible with poly(ethyl methacrylate). The introduction of a small amount of 4-vinylbenzoic acid units along poly(styrene) chains (PS-VBA) enhanced its miscibility with poly(ethyl methacrylate) (PEMA) or with poly[ethyl methacrylate-co-(2-N,N-dimethylaminoethyl) methacrylate] (PEMA-DAE), as observed from the appearance of a single composition dependent glass transition temperature for each binary system using inverse gas chromatography. The negative values of the apparent polymer-polymer interaction parameter, chi(23)app, determined with different families of molecular probes, for three blend compositions and over a range of temperature confirm quantitatively the miscibility of these blends. The chi(23)app values for PEMA(PS-VBA) and (PEMA-DAE)-(PS-VBA) blends are dependent of the chemical nature of the probes, the temperature and the blend composition.
Characterization of semicrystalline polymers by inverse gas chromatography. 1. Poly(vinylidene fluoride)
Etude du PVF2 en utilisant 20 solutes differents (sonde); variation du volume de retention de ces sondes avec la phase support solide, le debit gazeux et la charge de PVF2; proposition d'une methode de correction de ces facteurs. Calcul des parametres d'interaction de Flory des sondes, de la cristallinite du PVF2 et du volume specifique de PVF2. Discussion des donnees thermodynamiques en relation avec la contribution des groupes methyl des alcanes et des groupes carbonyls des acetates
Photoinduced spin-state transition of Co3+ in the layered perovskite manganite thin film
The photoinduced effect, at different temperatures, on layered perovskite manganite La1.2Sr1.8Mn1.8Co0.2O7 thin film deposited on a SrTiO3(100) substrate has been studied using a He–Ne laser (632.8 nm) with the power of output 25 mW at low temperatures. The electrical transport and magnetic properties of the film are investigated systematically in the temperature region from 20 to 300 K. The resistance shows a significant decrease at low temperatures (T<90 K) under laser irradiation, which can be interpreted in terms of the spin-state transition of Co3+ ions. The magnetic field combined with the laser is also used to detect the photoinduced effect of the spin-glass state. The time dependence of the metastable system under several applied fields was also discussed. The system has the ability to keep a persistent memory of the magnetic history imprinted in its zero-field resistance.