Electrolysis of Gold from Filtration Waste by Means of Mechanical Activation
The intensification of the gold thiourea leaching from a filtration waste (Kosice, Slovakia) using mechanical activation as the pretreatment step has been studied. The leaching of “as-received“ sample in an acid thiourea solution resulted in 65 % Au dissolution. However, after mechanical activation in a planetary mill 99 % of the gold was leached. The optimum redox potential for electrolysis is in the range 500-523 mV for the gold extraction 99.79 % from the mechanically activated sample. The mechanical activation resulted in an increase of the specific surface area of the waste from 0.7 m 2 g -1 to a maximum value of 13.5 m 2 g -1 . The physicochemical changes in the filtration waste as a consequence of mechanical activation had a pronounced influence on the subsequent gold extraction.
A processing method of the goldsmith's and electronic Au-Ag-containing wastes
Sposob spracovania zlatnickych a elektronických Au-Ag odpadov Veľke množstva odpadov z elektrických a elektronických zariadeni sa hromadia v celej Europe. Každý spotrebiteľ vyprodukuje priemerne 16 kg tohto odpadu za rok, co v Europe predstavuje celkovo sesť milionov ton za rok. Ide o obrovske plytvanie zdrojmi. Znamena to taktiež veľke ekologicke nebezpecenstvo, keďže elektricke spotrebice a elektronicke zariadenia obsahuju vysoko toxicke ťažke kovy a organicke znecisťujuce latky. Podľa nových predpisov EU budu musieť výrobcovia odteraz platiť za zber a likvidaciu týchto výrobkov. Odpady usľachtilých kovov Au-Ag predstavuju siroku skalu typov a foriem odpadov s roznymi balastnými prvkami aj zložkami. Problematika spracovania odpadov s obsahom Au a Ag je vysoko aktualnou v celosvetovom meradle z hľadiska hodnoty a specifických vlastnosti týchto kovov ako aj ich nenahraditeľnosti v oblasti bankovnictva, zdravotnictva, priemyslu a v neposlednom rade aj v samotnej výrobe a predaji zlatnickych výrobkov. Predkladaný navrh možnosti spracovania Au-Ag zlatnickych a elektronických odpadov si kladie za cieľ ziskať zlato a striebro v kovovej forme. Aplikacia navrhovaneho procesu spracovania uvedených Au-Ag odpadov predstavuje pre spolocnosť praktický, ekonomický a zaroveň ekologický význam pri ich spracovavani. Ziskavanie zlata, resp. striebra z Au-Ag odpadov je mimoriadne doležite v podmienkach inflacneho vývoja, kedy tieto usľachtile kovy su stabilným zdrojom pokrývania potrieb spolocnosti.
Thiosulfate leaching of gold from a mechanically activated CuPbZn concentrate
Abstract The hydrometallurgical processing of complex concentrates represents an ecologically attractive alternative with respect to classical pyrometallurgical technologies. The leaching of gold from a mechanochemically pretreated CuPbZn complex sulfide concentrate of Slovak origin using ammonium thiosulfate was studied. Physicochemical transformations in the concentrate due to mechanical activation have an influence on the rate of extraction and the recovery of gold. It was possible to achieve 99% gold recovery within 45 min for a sample mechanically activated at an energy input of 403 kWh t −1 . Only 54% of gold were recovered from the as-received concentrate in 120 min. Mechanical activation proved to be an appropriate pretreatment for this CuPbZn concentrate before extraction of gold into thiosulfate leaching solution.