Evaluation of single liquid primers with organic sulfur compound for bonding between indirect composite material and silver-palladium-copper-gold alloy.
The purpose of this study was to evaluate the effect of primers on bonding between a silver-palladium-copper-gold alloy and an indirect composite material. Cast disks were air-abraded with alumina, conditioned with one of five primers (Alloy Primer, Luna-Wing Primer, Metal Primer II, Metaltite, M.L. Primer), and bonded with a light-activated indirect composite. Shear bond strengths were determined after 20,000 times of thermocycling. The results showed that four of the primers, except the Luna-Wing Primer, were effective in enhancing the bond strength as compared with the unprimed control group. Of these four primers, Alloy Primer, Metal Primer II, and M.L. Primer exhibited significantly greater bond strengths. It can be concluded that the effectiveness of primers varies considerably according to the organic sulfur compounds added to the solvent, and that care must be taken in selecting priming agents for bonding the composite material and the silver-palladium-copper-gold alloy.
Effect of thione primers on adhesive bonding between an indirect composite material and Ag-Pd-Cu-Au alloy.
The current study evaluated the effect of primers on the shear bond strength of an indirect composite material joined to a silverpalladium-copper-gold (Ag-Pd-Cu-Au) alloy (Castwell). Disk specimens were cast from the alloy and were air-abraded with alumina. Eight metal primers were applied to the alloy surface. A light-polymerized indirect composite material (Solidex) was bonded to the alloy. Shear bond strength was determined both before and after the application of thermocycling. Two groups primed with Metaltite (thione) and M. L. Primer (sulfide) showed the greatest post-thermocycling bond strength (8.8 and 6.5 MPa). The results of the X-ray photoelectron spectroscopic (XPS) analysis suggested that the thione monomer (MTU-6) in the Metaltite primer was strongly adsorbed onto the Ag-Pd-Cu-Au alloy surface even after repeated cleaning with acetone. The application of either the thione (MTU-6) or sulfide primer is effective for enhancing the bonding between a composite material and Ag-Pd-Cu-Au alloy.
Single step formation of biocompatible bimetallic alloy nanoparticles of gold and silver using isonicotinylhydrazide.
Manufacturing nanoparticles with controlled physicochemical properties using environment-friendly routes have potential to open new prospects for a variety of applications. Accordingly, several approaches have been established for manufacturing metal nanoparticles. Many of these approaches entail the use of hazardous chemicals and could be toxic to the environment, and cannot be used readily for biomedical applications. In the present work, we report a single step bio-friendly approach to formulate gold (Au), silver (Ag), and Au-Ag alloy nanoparticles with desired surface corona and composition using isonicotinylhydrazide (INH) as a reducing agent. INH also functioned as a stabilizing agent by enabling a surface corona around the nanoparticles. Remarkably, within a single step INH could also provide a handle in regulating the composition of Au and Ag in bimetallic systems without any additional chemical modification. The physicochemical and surface properties of the different nanoparticles thus obtained have been examined by analytical, spectroscopic and microscopic techniques. Cell cytotoxicity (release of lactate dehydrogenase), cell viability and intracellular reactive oxygen species (ROS) assays confirmed that the Au, Ag, and Au-Ag bimetallic nanoparticles prepared with INH are biocompatible. Finally, the presence of organic surface corona of INH on the nanoparticles was found to impart nanozyme activity and antimycobacterial sensitivity to the nanoparticles.