Some new reactive polymers for the immobilization of enzymes.
From poly(vinyl alcohol) precursors, various reactive carriers for the immobilization of enzymes were synthesized. As insoluble starting polymers, the following products were used: poly(vinyl alcohol), gels crosslinked with terephthalaldehyde, hydrolyzed beads of crosslinked poly(vinyl acetate), poly(vinyl acetate-co- ethylene) tubes coated with poly(vinyl alcohol), and poly(vinyl alcohol)-containing synthetic pulp. Reactive groups introduced into these carriers or methods for their activation included the diazonium- and isothiocyanato group, and the glutardialdehyde-, BrCN, 2, 4, 6-trichloro-s-triazien, and p-benzoquinone methods. Furthermore, SH-specific reactive groups such as N-substituted maleimide groups or activated mixed disulfides with 2-thiopyridyl groups could be introduced into PVA-polymers. Enzymes like hydrolases (e.g. papain, trypsin, chymotrypsin, urease), oxidoreductases (e.g. glucose oxydase, catalase, glucose-6-phosphate dehydrogenase) as well as the example of transferase hexokinase coimmobilized with glucose-6-phosphate dehydrogenase, were immobilized by reactive poly(vinyl alcohol) carriers. The properties of the immobilized enzymes were investigated.
Catalase immobilization—A review
Abstract This interdisciplinary review covers the updated information about the natural and the synthetic materials based on polymers or low molecular compounds, organic or inorganic ones, utilized by researchers to immobilize the most popular enzyme named “CATALASE”. Keeping in mind that the immobilized enzyme is intensively applied in various domains such as textile and food industries, treatment of the waste waters, cosmetics and pharmaceutical formulations to determine the hydrogen peroxide quantity or to remove the excess of H2O2, it will be useful for the upcoming selection and especially to design new specific and versatile carriers by specialists according with the final purpose and applications.
Microstructure of the solder-casting zone in bridges of dental gold alloys.
The composition and structure were studied in the cast and in the solder of bridges which had failed clinically. Both materials were gold alloys but with different contents of Pt, Ag and Zn. The metallographic investigation revealed defects mostly in the solder, situated in the subsurface layer. SEM studied of the fracture surface revealed large porosites and a structure of dense parallel lines--striations--, indicating that the material had failed from fatigue. The materials in the fractured bridges were identified by micro-probe measurements. It was stated that cast material and solder material used together, were of different composition.