A novel processing approach for free-standing porous non-oxide ceramic supports from polycarbosilane and polysilazane precursors
In this contribution, a low-pressure/low-temperature casting technique for the preparation of novel free-standing macrocellular polymer-derived ceramic support structures is presented. Preceramic polymers (polycarbosilane and poly(vinyl)silazane) are combined with sacrificial porogens (ultra-high molecular weight polyethylene microbeads) to yield porous ceramic materials in the Si—C or Si—C—N systems, exhibiting well-defined pore structures after thermal conversion. The planar-disc-type specimens were found to exhibit biaxial flexural strengths of up to 60 MPa. In combination with their observed permeability characteristics, the prepared structures were found to be suitable for potential applications in filtration, catalysis, or membrane science.
Polymer-Derived Silicoboron Carbonitride Foams for CO2 Capture: From Design to Application as Scaffolds for the in Situ Growth of Metal-Organic Frameworks.
A template-assisted polymer-derived ceramic route is investigated for preparing a series of silicoboron carbonitride (Si/B/C/N) foams with a hierarchical pore size distribution and tailorable interconnected porosity. A boron-modified polycarbosilazane was selected to impregnate monolithic silica and carbonaceous templates and form after pyrolysis and template removal Si/B/C/N foams. By changing the hard template nature and controlling the quantity of polymer to be impregnated, controlled micropore/macropore distributions with mesoscopic cell windows are generated. Specific surface areas from 29 to 239 m(2)  g(-1) and porosities from 51 to 77 % are achieved. These foams combine a low density with a thermal insulation and a relatively good thermostructural stability. Their particular structure allowed the in situ growth of metal-organic frameworks (MOFs) directly within the open-cell structure. MOFs offered a microporosity feature to the resulting Si/B/C/N@MOF composite foams that allowed increasing the specific surface area to provide CO2 uptake of 2.2 %.
Formation of Open Micropores in Nanoporous Ceramics Based on Organosilicon Polymers
Micropores in nanoporous ceramics produced by pyrolysis of organosilicon polymers are investigated using BET and mercury porometry methods. The poor reproducibility of the obtained micropore structure is interpreted in the context of synergism.