Intelligent Sensors for Atomization Processing of Molten Metals and Alloys
ABSTRACT We briefly introduce the principles of atomization processing of molten metals and alloys, discuss potentially applicable instrumentation, and propose opportunities for developing intelligent sensors for monitoring and control of the process. Particle size and velocity are considered the two most important variables to monitor and control the atomization process. Several on-line sensors suitable for atomization of molten metals and alloys are compared: laser light scattering methods using small angle scattering analysis, moderate angle scattering analysis, and doppler analysis, electrical methods using surface ionization and triboelectric charging, and image analysis. The isokinetic sampling probe is introduced as a direct method to sample powders at the desired point in the atomized spray. Prospects and problems of integrating instruments based on these principles into intelligent processing of materials (IPM) scenarios are discussed.
Single Fluid Atomization Fundamentals
Atomization is simply defined as the breakup of a liquid into droplets. It can be achieved in many ways including spraying through nozzle, pouring on to a rotating disc, etc. Atomization practice and research usually involve materials processing in their liquid state either at or near room temperature (oil-based liquids, paint spraying, aerosol sprays, etc.) or at high temperature (metal melts). Most of the literature describing atomization mechanisms pertains to two fluid atomization in which a second fluid is applied to break up a melt stream into droplets. Two fluid atomization techniques for molten metals are described in Chap. 3.
The crystal structure of stilpnomelane. Part II. The full cell
Summary The structural formula of stilpnomelane averaged from 37 representative literature analyses and based on the determined structure is (Ca,Na,K)4(Ti0·1Al2·3Fe35·5Mn0·8Mg9·3)[Si63Al9](O,OH)216·nH2O. Ferrostilpnomelanes have up to 12 R 3+ cations in the octahedral sheet, ferristilpnomelanes commonly have between 24 and 30 R 3+ cations, rarely up to 37. The two groups can be distinguished by accurate X-ray powder diffraction, ferrostilpnomelanes having d 001 less and a greater than have ferristilpnomelanes. The unit cell is triclinic, a = b∼21·8 Å, γ = 120°, d 001∼12·2 Å, P . Hexagonal groups or ‘islands’ of 24 silicon-oxygen tetrahedra co-ordinate to the octahedral sheet, the centres of the ‘islands’ are displaced by 5a/12, 8b/12 on either side of the octahedral sheet as a result of warping of this sheet to permit articulation with the smaller tetrahedral sheet. The 24-tetrahedra ‘islands’ are linked laterally by 6-member rings of inverted tetrahedra, which in turn link at their apices to like rings connecting the next sheet of ‘islands’. Thus a single tetrahedral layer is 4 tetrahedra thick and has symmetry 6/m. The 6-member rings of tetrahedra act as hinges permitting up to 0·5 Å extension or contraction of the tetrahedral sheet to accommodate variations in the octahedral sheet dimensions with varying R 2+/R 3+ ratio.