Flexural Behaviour of Carbon Textile-Reinforced Concrete with Prestress and Steel Fibres
Four-point bending tests were adopted to investigate the influences of the number of textile layers, volume content of steel fibres, and prestress on the flexural behaviour of carbon textile-reinforced concrete (TRC). The failure mode of the specimen changed from debonding failure to shear failure, accompanied by the matrix-textile interfacial debonding with an increasing number of textile layers. The interfacial bonding performance between the textile and matrix improved with the addition of steel fibres in the TRC specimens. The presence of prestress or steel fibres improved first-crack and ultimate stresses of the TRC specimen. In comparison with the first-crack stress, a more pronounced enhancement in the ultimate stress was achieved by the addition of steel fibres. However, the effect of prestress on the first-crack stress was found to be more significant than on the ultimate stress. The prestress combined with steel fibres further improved the flexural behaviour of the TRC specimens. The prestressed TRC specimens with 1% volume content of steel fibres effectively avoided debonding. Thus, the utilization of the textiles could be improved.
Improved mechanical properties of textile reinforced concrete thin plate
Textile reinforced concrete (TRC) is especially suitable for the thin-walled and light-weight structural elements with a high load-bearing capacity. For this thin element, the concrete cover thickness is an important factor in affecting the mechanical and anti-crack performance. Therefore, the influences of the surface treatment of the textile and mixing polypropylene fiber into the concrete on the properties of the components with different cover thickness were experimentally studied with four-point bending tests. The experimental results show that for the components with the same cover thickness, sticking sand on epoxy resin-impregnated textile and adding short fiber into the concrete are helpful to improve their mechanical performance. The 2–3 mm cover thickness is enough to meet the anchorage requirements of the reinforcement fiber and the component has good crack pattern and mechanical behavior at this condition. Comparison between the calculated and the experimental values of flexural capacity reveals satisfactory agreement. Finally, based on the calculation model of the crack spacing of reinforced concrete structures, the crack extension of this thin-wall component was qualitatively analyzed and the same results with the experimental were obtained.
Determination of Shear Strength of Masonry Panels Through Different Tests
This study addresses the problem of evaluation of strength of masonry walls. In-plane behavior of masonry panels has been studied under monotonic diagonal-compression and shear-compression loading in quasi-static test facility. The results of 35 laboratory and in situ tests are analyzed to show that in the case of the diagonal compression test results are lower than the strength of masonry walls evaluated trough the shear-compression test, highlighting the problem of choosing the test which best simulates to the real behavior of the masonry when stressed by lateral loads. A presentation is also given of the results of a F.E. investigation for shear strength evaluation of masonry walls. F.E. modeling non-linear procedure was used for the representation of masonry panels. The numerical simulations are compared with experimental results and the reliability of the different finite element models is discussed, thus confirming the different shear strength values measured in the experimental campaign.