Measurement of hydrogen ion conductivity through proton exchange membrane
Proton exchange membrane is the prime part of proton exchange membrane fuel cell (PEMFC). In this work, it has focused to the proton conduction through two different conductive polymer membranes such as Nafion 212 and Fumapem AM (PBI). The conductivity has measured by the two probe method with the help of electrochemical impedance spectroscopic (EIS) analysis. To increase the conductivity, Fumapem AM (PBI) membrane has been doped with 85 % concentrated H3PO4 acid at ambient temperature. Due to acid doping, it has swelled 41 % compare to prior on. The highest conductivity has recorded as 3.54 and 2.24 mS/cm under 60 °C temperature for Nafion 212 and Fumapem AM (PBI) respectively. The proton conductivity of both membranes is fully dependent on the surrounding temperature.
A Novel Method for Humidity-Dependent Through-Plane Impedance Measurement for Proton Conducting Polymer Membranes
In this study, we introduce a through-plane electrochemical measurement cell for proton conducting polymer membranes (PEM) with the ability to vary temperature and humidity. Model Nafion and 3M membranes, as well as anisotropic composite membranes, were used to compare through plane and in plane conductivity. Electrochemical impedance spectroscopy (EIS) was applied to evaluate the proton conductivity of bare proton exchange membranes. In the Nyquist plots, all membranes showed a straight line with an angle of 60–70 degrees to the Z’-axis. Equivalent circuit modeling and linear extrapolation of the impedance data were compared to extract the membrane resistance. System and cell parameters such as high frequency inductance, contact resistance and pressure, interfacial capacitance were observed and instrumentally minimized. Material-related effects, such as swelling of the membranes and indentation of the platinum mesh electrodes were examined thoroughly to receive a reliable through-plane conductivity. The received data for model Nafion and 3M membranes were in accordance with literature values for in-plane and through-plane conductivity of membrane electrode assemblies. Anisotropic composite membranes underlined the importance of a sophisticated measurement technique that is able to separate the in-plane and through-plane effects in polymer electrolytes.
Measuring Sheet Resistances of Dielectrics Using Co‐Planar Hydrogel Electrochemical Cells with Practical Applications to Characterize the Protective Quality of Paints on Sculptures
Electrical properties of thin dielectric films at the solid-liquid phase boundary are an important performance characteristic of many devices, coatings and sensors. In this paper, co-polymeric hydrogels of polyacrylic acid co-sulfonic acid, swollen with a salt solution to act as the solid electrolyte, were used to assess interfaces using electrochemical impedance spectroscopy (EIS) in a co-planar geometry. Silane-modified glasses were characterized by the co-planar hydrogel EIS cell and found to be distinguishable based on their surface monolayer chemistry. EIS measurements were also made on primed and painted metal substrates, using both test panels and an outdoor sculpture, Tony Smith's Stinger. The panels were then exposed to accelerated and outdoor weathering and showed degradation on the surface paint layers, which was observable electrochemically using EIS and confirmed visually by SEM. Electrochemical spectral features were compared between data from a standard paint-test cell versus this co-planar hydrogel cell; both cell types were able to measure coating capacitance, providing useful information about the condition of the bulk coating. Yet, sheet resistance (Rs) was a spectral feature seen only by the co-planar hydrogel cell. Thus, it can be concluded that the use of such co-planar hydrogel cells can provide an earlier warning sign to coating degradation and such cells provide a new type of spectral information that is not assessable by the standard geometry.