Deterioration of wood-based boards subjected to outdoor exposure in Tsukuba
Various types of wood-based boards were analyzed for deterioration after being exposed to an outdoor environment for 5 years in Tsukuba, Japan. In phenol–formaldehyde resin bonded particleboard (PB(PF)) and aspen oriented strand board (OSB(aspen)), longer exposure caused a greater reduction in the modulus of rupture and internal bond strength, an increase in the coefficients of variation, and a decrease in 95 % lower tolerance limit at the 75 % confidence level (95TL). Nail-head pull-through and lateral nail resistance were also reduced by outdoor exposure, but their coefficients of variation and 95TL were not significantly affected. In contrast, methylene diphenyl diisocyanate bonded medium density fiberboard (MDF(MDI)) only showed a slight deterioration of these properties even after 5-year exposure, and the coefficients of variation and 95TL hardly changed. After 5-year exposure, the retention of shear load in one-plane at relative displacement of 1.0 mm was high in MDF(MDI) and OSB(aspen) at 93.5 and 78.5 %, respectively, but low in PB(PF) at 41.1 %. As with PB(PF), OSB(aspen) also showed a sharp decrease in the modulus of rupture and internal bond strength, but only slightly reduced shear load in one-plane.
Effects of water soaking and outdoor exposure on nail joint properties of particleboard
Phenol-formaldehyde resin-bonded particleboard (PF board) and isocyanate resin-bonded particleboard (MDI board) were soaked in water at 40, 70 and 100 °C, and the relationships between soaking conditions and nail joint properties were analyzed. The soaking time to reach the lower limit of nail-head pull-through (NHPT) of the PF board was 2 h at 100 °C, while it took 168 h at 70 °C. The soaking time to reach the lower limit of lateral nail resistance (LNR) of the PF board was 24 h at 100 °C, but it did not take 168 h at 70 °C to reach it. The lower limits of NHPT and LNR for the MDI board were higher than those for the PF board. For the PF board, there was a high correlation between modulus of rupture, internal bond strength and nail joint properties. Based on the results of water soaking and outdoor exposure, it was shown that thickness change has a significant effect on NHPT and LNR, and that the reduction in NHPT and LNR results from the collapse of bonding points owing to swelling of the board.
Analysis of ASTM D 1037 accelerated-aging test
On analyse l'essai de vieillissement accelere a six cycles pour les panneaux de fibres et de particules afin de determiner la contribution de chaque etape a la degradation des panneaux