Metal Rubber is special materials and used in aerospace, especially under extreme conditions. It has characteristics of strong adaptability, corrosion resistance, radiation resistance and designability. In this paper, we have manufactured Metal Rubber components, and done some research on the influence of previous deformation to Metal Rubber material's structure and performance, its characteristic parameters such as Poisson's ratio, Elastic modulus were studied. Research results are basic but essential for finite element analysis of Metal Rubber materials; these results also play an important role of engineering application.
DESCRIPTION OF AN ARBITRARY MULTI-AXIAL LOADING PROCESS FOR NON-LINEAR VIBRATION ISOLATORS
Masing's principle with non linear transformations gives a general and simple method for the description of the arbitrary loading process of vibration isolators with large non linear stiffness and non linear damping. It is possible to use this method for precise calculations of dynamic processes in non linear vibration systems
A New Vacuum Pressure Infiltration CFRP Method and Preparation Experimental Study of Composite
In order to prepare a carbon-fiber-reinforced polymer composite (CFRP) with ideal microstructure and properties, a new vacuum pressure infiltration CFRP method is proposed based on an analysis of existing CFRP preparation process methods. Research on composite material preparation systems was carried out by using this new method principle. The system mainly includes a fiber pre-forming module, a vacuum heating infiltration module, a hot-press curing molding module, and a data acquisition control module. Under the conditions of natural curing at 0 MPa + 6 h + 25 °C, vacuum heating curing at –0.05 MPa + 30 min + 80 °C, and hot-press curing at 0.7 MPa + 5 min + 50 °C, a two-dimensional (2D) CFRP with excellent microstructure and properties was successfully prepared. Observing the microstructure of the prepared composite material, it can be found that the inside of the composite material was sufficiently and uniformly infiltrated, and common preparation defects such as holes and delamination were effectively controlled. Through the performance test, the bending strength of the material reached 790 MPa.