Ultra-shallow Junction Formed by Plasma Doping and Laser Annealing
We investigated ultra-shallow junction prepared by plasma doping (PLAD) and laser annealing (LA). Although PLAD is promising doping technology for the sub-45nm technology node due to the high dose rate at low energy, it has problems which is related with hydrogen or fluorine. The implanted hydrogen generally increases damage in the Si substrate. The fluorine also retards dopant activation and increases dopant deactivation during post-annealing step. Conventional one step annealing processes such as rapid thermal annealing (RTA) or excimer laser annealing (LA) are not effective method for high dopant activation. To minimize the effect of hydrogen or fluorine, we propose additional pre-annealing followed by conventional laser annealing. By employing low temperature pre-annealing, we can improve electrical characteristics such as low sheet resistance, high activation rates, shallow junction depth and reduced dopant deactivation. The improvement can be explained by reduced defect density and out-diffusion of fluorine or hydrogen which in turn enhances dopant activation during ELA
Damage in hydrogen plasma implanted silicon
The damage and defects created in silicon by hydrogen plasma immersion ion implantation (PIII) are not the same as those generated by conventional beamline ion implantation due to the difference in the ion energy distribution and lack of mass selection in PIII. Defect generation must be well controlled because damage in the implanted and surface zones can easily translate into defects in the silicon-on-insulator structures synthesized by the PIII/wafer bonding/ion-cut process. The defect formation and its change with annealing temperature were investigated experimentally employing channeling Rutherford backscattering spectrometry, secondary ion mass spectrometry, and atomic-force microscopy. We also calculated the damage energy density of the three dominant hydrogen species in the plasma (H+, H2+, and H3+) as well as displacement of silicon atoms in the silicon wafer. H2+ creates the most damage because its damage energy density is very close to the silicon threshold energy. The effects of atmospheric gas...
Anomalous Annealing Behavior of Arsenic Implanted Silicon as a Function of Dose and Energy
Anomalous annealing behavior of damage in As implanted Si has been investigated by channeling effect measurements. Room temperature As implants with doses from 1014 to 2 × 1016cm-2 at energies ranging from 50 to 250 keV into Si were annealed over the range of 600°C to 1100°C. Anneal temperatures ≥ 950°C reduce the disorder for ion doses of 0.5 to 1 × 1016 cm-2 at energies between 50 and 250 keV. Anomalously high residual disorder was found for the intermediate doses of 2 × 1014 to 2 × 10/cm2 implanted above 100 keV. For this intermediate dose, annealing of implants performed at liquid nitrogen temperatures did not show significant reduction in this damage. However implants at 200° to 300°C indicate a lower amount of damage compared to the room temperature implants.