Al2O3/InSb/Si quantum well MOSFETs having an ultra-thin InSb layer
The fabrication and the properties of Al2O3-InSb-Si QW MOSFETs having an ultra thin InSb channel layer is reported. The good characteristic of ID-VD with an transconductance of 67 mS/mm demonstrates that the ultra thin InSb channel layer grown directly on Si can be used for MOSFET channels. The results show that the InSb/Si pseudomorphic quantum well MOSFETs is a promising candidate for future VLSIs.
Characterization of Al2O3/InSb/Si MOS diodes having various InSb thicknesses grown on Si(1 1 1) substrates
This paper discusses the capacitance–voltage (C–V) characteristics of Al2O3/InSb/Si (1 1 1) MOS diodes grown using MBE via InSb bi-layer with special care to the surface reconstruction. This growth technique is based on our finding that the InSb layer grown on a Si (1 1 1) substrate is rotated by 30° with respect to the substrate under certain initial conditions. This rotation drastically reduces the lattice mismatch from 19.3% to 3.3%, and improves the crystal quality of an InSb layer. To investigate the possibilities of InSb MOSFETs on Si substrates, we fabricated MOS diodes having an Al2O3 insulator film deposited by atomic layer deposition. C–V characteristics were measured both at RT and 77 K. It was found that the InSb grown on Si shows a degraded C–V curve compared to the InSb substrate, even though the mobility of the grown layer is quite high. We also investigated the effects of InSb thickness on the C–V characteristics of the MOSFETs. It was found that the quality of MOS diodes first degrades when decreasing the InSb thickness from 1 μm to 50 nm; further reduction of the InSb thickness improves it again. It was demonstrated that the MOS diode having a 10 nm InSb layer shows a good C–V curve, which is comparable to that of the InSb substrate. Finally, we discussed the possibility of the InSb/Si pseudomorphic MOSFETs.
Effects of In and Sb mono-layers to form rotated InSb films on a Si(1 1 1) substrate
A new method for InSb heteroepitaxial growth on a Si substrate was introduced in our previous work, in which an InSb film was formed via an InSb bi-layer. In the present work, to study the effects of In and Sb individual layers on the InSb film quality, InSb was deposited onto an InSb bi-layer, In mono-layer, and Sb mono-layer on a Si substrate. It was found that both In and Sb layers (in other words, InSb bi-layer) were essential to form a fine InSb film.