Effect of heterogeneously distributed pre-existing dispersoids on the recrystallization behavior of a cold-rolled Al-Mn-Fe-Si alloy
It is well known that strong concurrent precipitation, mainly located along grain/subgrain boundaries, results in a coarse and elongated grain structure, and unusual sharp P {011} and/or M {113} texture components during annealing of supersaturated AA3xxx-series alloys. In this study, a supersaturated as-cast Al–Mn–Fe–Si alloy was annealed at three temperature–time paths after cold rolling and their effects on the softening behavior have been analyzed and compared in terms of final grain structure and texture. In particular, material conditions with dispersoids located along grain/sub-grain boundaries were produced prior to annealing. The effects of pre-existing dispersoids as well as dispersoids formed during annealing (concurrent precipitation), both of which are heterogeneously distributed along grain/sub-grain boundaries, on the recrystallization behavior of the deformed material were investigated and compared. The results clearly show that, due to their larger sizes, these pre-existing dispersoids do not significantly increase the strength of the P/M texture components as compared to the dispersoids formed during annealing, even though the former can still affect the grain structure. It can be concluded that sharp P/M textures develop when recrystallization takes place at low temperature where nucleation of other orientations, whether from particle stimulated nucleation (PSN) or other nucleation mechanisms are suppressed by concurrent precipitation.
P-Texture Effect on the Fatigue Crack Propagation Resistance in an Al-Cu-Mg Alloy Bearing a Small Amount of Silver
P-texture effect on the fatigue crack propagation (FCP) resistance in an Al-Cu-Mg alloy containing a small amount of Ag, is investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and electron back scattering diffraction (EBSD). Results shows that the high intensity P-texture sheet has lower σ0.2/σb, lower FCP rate and higher damage tolerance than random texture sheet. Fracture analysis indicates that the striations spacing of high intensity P-texture sheet is much smaller than that of random texture sheet and it has a rougher fatigue fracture surface, which causes a significant roughness induced crack closure (RICC) effect. The calculation results manifest that high intensity P-texture sheet possesses a higher crack closure level reaching 0.73 as compared to random texture sheet (only 0.25). The statistical analysis results reveal the P-grains have large twist angle of 105–170° and tilt angle of 5–60° with neighboring grains, which is similar to Goss-grains. This is the fundamental reason that P-texture sheet has the same FCP resistance and induces fatigue crack deflection as Goss-texture sheet. Additionally, the most {111} slipping planes of P-grains are distributed in the range of 30–50° deviating from transverse direction of the sheet. This results in more {111} slipping planes to participate in cyclic plastic deformation, which is beneficial to reduce fatigue damage accumulation and improve the damage tolerance of Al-Cu-Mg-Ag alloy.
Timber, its nature and behaviour
Preface. Acknowledgements. Chapter 1 - Structure of Timber. Chapter 2 - Appearance of Timber in Relation to its Structure. Chapter 3 - Mass Volume Relationships. Chapter 4 - Movement in Timber. Chapter 5 - Flow in Timber. Chapter 6 - Deformation Under Load. Chapter 7 - Strength and Failure in Timber. Chapter 8 - Durability of Timber. Chapter 9 - Processing of Timber. Index.