Implantation, damage, and regrowth of high Tc superconductors
Abstract We have observed superconductivity in thin films of (La1−xSrx)2CuOy which are fabricated by implanting evaporated La/Cu multilayer films with Sr and annealing in oxygen. The films are insulating and partially transparent as-implanted, but they darken and become conducting at annealing temperatures as low as 500°C. The resistive behavior is very sensitive to the annealing conditions and the superconducting layer appears to be buried beneath the surface. Similarly, implantation of F, O, and Ne into single crystals and high quality (χmin
Epitaxial order and resistivity of high temperature superconductors grown on SrTiO3
Thin films of YBa2Cu3O7−δ grown on 〈001〉-oriented SrTiO3 substrates attain zero resistance at a temperature of T=92 K and have a superconducting critical current, jc, of more than 3×106 Acm-2 at T=77 K. A low resistivity superconducting Cu-rich phase shows great promise for epitaxial growth on SrTiO3 substrates because of an improved lattice match in the growth direction and strong epitaxial ordering due to the presence of the new phase.
LABORATORY AND FIELD TESTING OF SEED SPACING UNIFORMITY FOR SUGARBEET PLANTERS
Five planter configurations were evaluated for seed spacing uniformity at three field speeds using a seed 
location method in the field and a laboratory method involving an opto-electronic sensor system. Planter seed spacing 
uniformity was described using the Coefficient of Precision (CP3) measure. Results showed that CP3 measures 
determined using the laboratory test method were significantly different from those determined using the field test method. 
This indicated the laboratory test method cannot be used to predict planter seed spacing uniformity in the field. Seed 
spacing uniformity determined in laboratory tests was higher than, or equal to, seed spacing uniformity determined in 
field tests. This indicated the laboratory test method may be useful to screen out planters or planter units with poor 
uniformity of seed metering. Field testing of the planters that perform well in laboratory tests must be conducted to 
adequately determine the seed spacing uniformity of those planters in the field. Results from laboratory and field tests 
could be useful in determining areas for improvement of planters or planter units.