Visible to infrared low temperature photoluminescence of rare earth doped bismuth germanate crystals.
In this paper, the influence of a series of rare earth (Eu, Tm, Nd) and Cr ion doping on the optical properties of BGO was investigated by means of photoluminescence (PL) from visible to IR region in the 10-300K temperature range using different types of detectors, namely, photomultiplier tube (PMT), InGaAs (IGA), and Si. Several samples were investigated having dopants concentrations of 0.3wt%Nd, 0.4wt%Tm, 0.06wt% Cr and 3ppm Eu. The PL spectra of the samples showed different luminescence behaviour which is assigned to the 4f intra shell transition from rare earth ions. The temperature dependence of the PL from rare earth doped BGO crystals is also examined.
Radiation resistance and fluorescence of europium doped BGO crystals
Abstract We report on a study of the radiation resistance and fluorescence of bismuth germanate scintillation crystals doped with europium (BGO: Eu). The transmission spectrum, the light output and the fluorescence spectrum of BGO: Eu crystals were measured before and after irradiation. The radiation resistance of BGO: Eu crystals was found to be increased with increase of europium doping. A red fluorescence emission around 600 nm was found for BGO: Eu samples, which has a 1.5 ms decay time.
Development of Poly(HEMA-Am) Polymer Hydrogel Filler for Soft Tissue Reconstruction by Facile Polymerization
The number of breast reconstruction surgeries has been increasing due to the increase in mastectomies. Surgical implants (the standard polydimethylsiloxane (PDMS) implants) are widely used to reconstruct breast tissues, however, it can cause problems such as adverse immune reactions, fibrosis, rupture, and additional surgery. Hence, polymeric fillers have recently garnered increasing attention as strong alternatives for breast reconstruction materials. Polymeric fillers offer noninvasive methods of reconstruction, thereby reducing the possible adverse effects and simplifying the treatment. In this study, we synthesized a 2-hydroxylethylmethacrylate (HEMA) and acrylamide (Am) copolymer (Poly(HEMA-Am)) by redox polymerization to be used as a biocompatible filler material for breast reconstruction. The synthesized hydrogel swelled in phosphate buffered saline (PBS) shows an average modulus of 50 Pa, which is a characteristic similar to that of the standard dermal acrylamide filler. To investigate the biocompatibility and cytotoxicity of the Poly(HEMA-Am) hydrogel, we evaluated an in vitro cytotoxicity assay on human fibroblasts (hFBs) and human adipose-derived stem cells (hADSCs) with the hydrogel eluate, and confirmed a cell viability of over 80% of the cell viability with the Poly(HEMA-Am) hydrogel. These results suggest our polymeric hydrogel is a promising filler material in soft tissue augmentation including breast reconstruction.