The Microstructure and Wear Resistance of a Copper Matrix Composite Layer on Copper via Nitrogen-Shielded Arc Cladding
A TiN and TiN·Ti2Cu reinforced copper matrix composite layer was cladded onto a T3 copper substrate to improve the anti-wear performance of copper products by means of the nitrogen-shielded gas tungsten arc cladding method (N2-GTAC). Better than the traditional preparation method of TiN, the TiN particles in the cladding layer were in situ generated using N atoms of shielding gas and Ti atoms of pre-deposited metal powders. In addition, the composite phase TiN·Ti2Cu occurred in the cladding layer, which also had a positive effect on anti-wearing. As Ti increased, the amount and grain size of TiN·Ti2Cu and TiN increased as a result. The hardness of the cladding layer increased with the increasing amount of reinforced phase generated in the layer. The hardness of the layer reached a maximum of 410 HV, which is nearly 5.1 times greater than that of copper. The TiN·Ti2Cu- and TiN-reinforced phases improved the wear resistance of the cladding layers. The cladding layer with 15 wt % Ti had the longsest launch stage (600 s) and the lowest fiction coefficient (0.56).
The Investigation on Wear Resistance of Fe-Based Alloy Coating by Argon Arc Cladding
By argon arc cladding technology, a Fe-based alloy coating was prepared on the surface of Q235 steel. The microstructure of the cladding coating was investigated by optical microscope (OM) and scanning electron microscope(SEM). The microhardness and wear resistance performance of the coating were tested by microhardness tester and friction-wear tester. The results show that the alloy coating with martensite, alloy solid solution and (Cr, Fe) 7C3/Fe3C/ Fe2B compounds is prepared on the surface of Q235 steel, the microhardness of the coating reaches as high as 600 HV and the wear resistance of the coating is about 8 times higher than that of Q235 steel substrate. When deposited a wear-resistant layer on the surface of mild steel , the high plasticity and ductility are preserved as well as the hardness and wear resistance of the cladding layer are improved greatly.
Photoinduced spin-state transition of Co3+ in the layered perovskite manganite thin film
The photoinduced effect, at different temperatures, on layered perovskite manganite La1.2Sr1.8Mn1.8Co0.2O7 thin film deposited on a SrTiO3(100) substrate has been studied using a He–Ne laser (632.8 nm) with the power of output 25 mW at low temperatures. The electrical transport and magnetic properties of the film are investigated systematically in the temperature region from 20 to 300 K. The resistance shows a significant decrease at low temperatures (T<90 K) under laser irradiation, which can be interpreted in terms of the spin-state transition of Co3+ ions. The magnetic field combined with the laser is also used to detect the photoinduced effect of the spin-glass state. The time dependence of the metastable system under several applied fields was also discussed. The system has the ability to keep a persistent memory of the magnetic history imprinted in its zero-field resistance.