A fast real time measurement system to track in and out of plane optical retardation/ birefringence, true stress, and true strain during biaxial stretching of polymer films.
An instrumented and highly integrated biaxial stretching system was designed and constructed to obtain true stress, true strain, and optical behavior of polymeric films during biaxial stretching. With programmable drive motors, any form of temporally varying biaxial deformation profiles, including linear, exponential, logarithmic as well as cyclic, can be applied to a square-shaped films. This machine allows the investigation of mechano-optical behavior of films under profiles captured in industrial processes. To overcome the edge effects, the samples are painted with a dot pattern that is imaged using a high speed video capture system. This system accurately determines the locations of the each dot matrix in subsequent images acquired and calculates the true strains in both directions. The in-plane optical retardation is determined using spectral birefringence method that uses polarized white light and optical spectrometer in the optical train. This is carried out automatically at less than 10 nm in retardation resolution with the light beam passing through the symmetry center of the sample. Out of plane retardation is measured with an identical optical train tilted 45° to the plane of the film with its light beam going through the same spot on the sample as 0° beam. The true stress and birefringences are calculated with the determined instantaneous thickness of the film. With this system, the stress optical behavior of PET's is determined up to very large deformation levels at moderate to high deformation rates. Beyond the initial linear stress optical behavior, these films exhibit sudden positive deviation from linearity and this start of nonlinearity was directly associated with the stress induced crystallization.
A simple constrained uniaxial tensile apparatus for in situ investigation of film stretching processing.
A simple constrained uniaxial tensile apparatus was designed and constructed to obtain stress-strain curve during stretching and subsequent structural evolution of polymeric films. Stretch is carried out through two motor driven clamps in the machine direction and scissor-like clamps in the transverse direction keeping the sample width constant. The force information during film stretching process is recorded by a tension sensor and structural evolution can be obtained by in situ X-ray scattering technique. All parameters related to film stretching manufacturing, such as temperature, draw ratio, and stretching speed can be set independently, making the apparatus an effective method to explore the relationship between processing parameters and structure.
Studies on the biaxial stretching of polypropylene film. VII. Refractive index of film measured with abbé refractometer
The refractive index of a film measured with an Abbe refractometer differs often depending on which surface of the film faces the refracting prism of the refractometer. This phenomenon was elucidated by using well-characterized films especially prepared for the purpose. The experimental results led to the conclusion that the measurement with an Abbe refractometer gives the refractive index of the film surface facing the refracting prism independently of the refractive index distribution within the film. The importance of this conclusion is stressed in relation to the structural studies of polymer films, especially of biaxially stretched films.