Influence of Coal Blending on Ash Fusibility in Reducing Atmosphere
Coal blending is an effective way to organize and control coal ash fusibility to meet different requirements of Coal-fired power plants. This study investigates three different eutectic processes and explains the mechanism of how coal blending affects ash fusibility. The blended ashes were prepared by hand-mixing two raw coal ashes at five blending ratios, G:D = 10:90 (G10D90), G:D= 20:80 (G20D80), G:D = 30:70 (G30D70), G:D = 40:60 (G40D60), and G:D = 50:50 (G50D50). The samples were heated at 900 °C, 1000 °C, 1100 °C, 1200 °C, and 1300 °C in reducing atmosphere. XRD and SEM/EDX were used to identify mineral transformations and eutectic processes. The eutectic processes were finally simulated with FactSage. Results show that the fusion temperatures of the blended ashes initially decrease and then increase with the blending ratio, a trend that is typical of eutectic melting. Eutectic phenomena are observed in D100, G10D90, and G30D70 in different degrees, which do not appear in G100 and G50D50 for the lack of eutectic reactants. The main eutectic reactants are gehlenite, magnetite, merwinite, and diopside. The FactSage simulation results show that the content discrepancy of merwinite and diopside in the ashes causes the inconsistent eutectic temperatures and eutectic degrees, in turn decrease the fusion temperature of the blended ash and then increase them with the blending ratio.
Thermodynamics of reactive dye adsorption from aqueous solution on the ashes from city heating station
This paper describes the adsorption thermodynamics of textile reactive dyes from aqueous solution on the waste ashes formed by burning brown coal at a city heating station. The values of thermodynamic parameters are the actual indicators for practical application in the adsorption process. Based on characteristic diagrams the thermodynamic parameters, enthalpy and entropy of adsorption are determined, and based on those data the Gibbs's free energy changes were determined. In all cases, there is a negative sign of the thermodynamic parameters. Entropy change (–2 to –3 J/K⋅mol) increases with increasing initial concentration of the adsorbate and decreases with increasing amount of adsorbent, suggesting a decrease in disordered system at the interface of solid solution during the adsorption of dye on the ashes. Free energy (–1.7 to 5 kJ/mol) decreases with the concentration of adsorbate discontinuously but continuously with increasing temperature, which is associated with spontaneous nature of the process. Small negative values of enthalpy change (–2 to –6 kJ/mol), point to the physical nature and the energy stability of the reactive dyes adsorption by ashes.
MAS-NMR spectroscopy studies in the setting reaction of glass ionomer cements.
OBJECTIVES
The main objective is the characterisation of the setting reaction in glass ionomer cements based on experimental ionomer glasses with different fluorine content and a commercial glass ionomer cement liquid by using 13C CP/MAS-NMR, 29Si, 27Al and 31P MAS-NMR spectroscopy in order to receive information specifically about the cross-linking process.


METHODS
Different fluorine containing glass compositions based on 4.5SiO2-3Al2O3-1.5P2O5-(5-z)CaO-zCaF(2) where z=0-3, were mixed with a commercially available polymer liquid to form glass ionomer cements. The cements were subjected to 27Al, 13C CP/MAS, 29Si, and 31P MAS-NMR analysis.


RESULTS
The 27Al spectra showed clearly the formation of six-fold coordinate Al(VI), that may crosslink the carboxyl groups in the poly-acid molecules. A shift towards to more positive values of the carboxyl peak in the 13C CP/MAS-NMR spectra showed clearly the proton dissociation of the carboxyl groups. A shift towards more negative values was observed in the 29Si MAS-NMR spectra, suggesting formation of hydrated silica gel and consequently formation of additional Si-O-Si bonds. 31P MAS-NMR spectra also reflected changes in the coordination state around a PO4(3-) tetrahedron. Increasing the fluorine content of the glasses resulted generally in increased reactivity during setting, due to promoting cross-linking and repolymerisation of the silicate phase, followed by clear changes in the MAS-NMR spectra.


CONCLUSIONS
The cross-linking process during the setting reaction of glass ionomer cements can be followed by MAS-NMR spectroscopy observing the conversion of Al(IV) to Al(VI). The acid base setting reaction is completed in 1 day and no further significant changes in the MAS-NMR spectra can be observed. Further study is required in order to understand the role of phosphorus.