Artificial-Crack-Behavior Test Evaluation of the Water-Leakage Repair Materials Used for the Repair of Water-Leakage Cracks in Concrete Structures
There are no existing standard test methods at home and abroad that can verify the performance of water leakage repair materials, and it is thus very difficult to perform quality control checks in the field of water leakage repair. This study determined that the key factors that have the greatest impact on the water leakage repair materials are the micro-behaviors of cracks, and proposed an artificial-crack-behavior test method for the performance verification of the repair materials. The performance of the 15 kinds of repair materials that are currently being used in the field of water leakage repair was evaluated by applying the proposed test method. The main aim of such a test method is to determine if there is water leakage by injecting water leakage repair materials into a crack behavior test specimen with an artificial 5-mm crack width, applying a 2.5 mm vertical behavior load at 100 cycles, and applying 0.3 N/mm2 constant water pressure. The test results showed that of the 15 kinds of repair materials, only two effectively sealed the crack and thus stopped the water leakage. The findings of this study confirmed the effectiveness of the proposed artificial-crack-behavior test method and suggest that it can be used as a performance verification method for checking the responsiveness of the repair materials being used in the field of water leakage repair to the repetitive water leakage behaviors that occur in concrete structures. The study findings further suggest that the use of the proposed test method makes it possible to quantify the water leakage repair quality control in the field.
Performance Evaluation of Waterproofing Membrane Systems Subject to the Concrete Joint Load Behavior of Below-Grade Concrete Structures
Below-grade structures such as parking lots, underground subway tunnels, and basements are growing in scale and reaching deeper below-ground levels. In this type of environment, they become subject to higher water pressure. The concrete material of the structures is exposed to wet conditions for longer periods of time, which makes the proper adhesion of waterproofing membranes difficult. Joint movements from increased structural settlement, thermal expansion/shrinkage, and physical loads from external sources (e.g., vehicles) make securing durable waterproofing challenging. While ASTM Guides, Korean Codes, and BS Practice Codes on below-grade waterproofing stress the importance of manufacturer specification for quality control, ensuring high quality waterproofing for the ever-changing scale of construction remains a challenge. This study proposes a new evaluation method and criteria which allow for the selection of waterproofing membranes based on specific performance attributes and workmanship. It subjects six different waterproofing membrane systems (installed on dry and wet surface conditioned mortar slab specimens with an artificial joint to different cyclic movement widths) to 300 cycles in water to demonstrate that inadequate material properties and workmanship are key causes for leakages.
Experimental study on bond behavior between high-strength grout and deformed steel bars
Abstract Engineers use high-strength grout to connect precast concrete members for its low shrinkage and good fluidity. This paper designed 87 central pull-out specimens using the control variable method to investigate the influence of factors on the rebar-grout bond property such as compressive strength, steel grade, bar diameter, transverse stirrups, and bond length. The test result showed that improving grout compressive strength (85.8 MPa–122.7 MPa) cannot improve the bond strength, which was different from the previous conclusions of concrete pull-out tests. Simplified formulas were presented for calculating the characteristic values of bond strength, residual strength, peak slip, and relative slip of load-holding platform based on parameter analysis. Then, a constitutive model was proposed to predict the full-range bond stress-slip curve of high-strength grout and steel bar specimens from bearing to failure. Finally, FEA models were established to evaluate the applicability and accuracy of the constitutive model.