Improving the reliability of radar T/R module with precise cleaning technology
Because we adopt high precision microelectronic assembly technologies during the manufacturing of radar T/R modules, these modules are complex and delicate. Common cleaning technologies such as ultrasonic cleaning can't satisfy the requirement of high precision cleaning of these modules. This article introduces some precise cleaning technologies, these cleaning technologies not only can make T/R module achieve a high cleanness, but also does little harm to them, and they will greatly improve the reliability of T/R module.
A new bumping process using lead-free solder paste
In this paper, we report development of a new process for lead-free solder bumping with no flux residues, using stencil printing and hydrogen radicals, which can lessen both the environmental load and the manufacturing cost of solder bumping. In this process the reduction of the hydrogen radicals, instead of the flux, will eliminate the surface oxides of the stencil printed lead-free solder paste. Sn-3.0Ag-0.5Cu lead-free solder paste, which contains no residue flux was printed on an 8-in wafer. Hydrogen plasma was radiated for a minute during the reflow process, and the printed paste formed a bump. Reflow experiments without hydrogen radicals treatment were also carried out for comparison, where no successful reflow could be observed.
Failure analysis for poor solderability of Au surface of PCB
Nonwetting is one of the common problems and is always rejected in electronic assemblies. ENIG pads of a PCBA exhibited nonwetting after lead-free reflow soldering. With the aid of stereomicroscope, SEM&EDS and XRF, a series of analysis was performed. And after visual inspection, surface and cross section analysis, thickness measurement and solderability test, it can be inferred that oxidation of plating surface was the main reason for nonwetting, and corrosion in Ni plating caused an adverse impact on solderalibity.