Low Turn-on Voltage InGaP / GaAsSb / GaAs DHBT Grown by MOCVD
In this work, an InGaP/GaAsSb/GaAs DHBT with carbon doping up to 4E19/cm GaAsSb base was studied. A current gain of 115 at the collector current density of 25KA/cm2 was achieved for the Rbs of about 530ohm/sq. Over 100mV turn-on voltage and knee voltage reduction and 2/3 offset voltage were obtained for the GaAsSb based HBT compared with the standard InGaP/GaAs SHBT. The DC gain of the device is less temperature dependence (the DC gain variation is less than 3% for the temperature range from 25 degree C to 100 degree C.) due to the larger valence band discontinuity between InGaP emitter and GaAsSb base, compare with the standard InGaP/GaAs SHBT. These results indicate that GaAsSb is a great choice for the base material of a low turn-on voltage HBT.
InGaP/GaAsSb/GaAs DHBTs with low turn-on voltage and high current gain
An InGaP/GaAsSb/GaAs double heterojunction bipolar transistor (DHBT) is presented. It features the use of a fully strained pseudomorphic GaAsSb (Sb composition: 10.4%) as the base layer and an InGaP layer as the emitter, which both eliminates the misfit dislocations and increases the valence band discontinuity at the InGaP/GaAsSb interface. A current gain of 200 has been obtained from the InGaP/GaAsSb/GaAs DHBT, which is the highest value obtained from GaAsSb base GaAs-based HBTs. The turn-on voltage of the device is typically 0.914 V for the 10.4% Sb composition, which is 0.176 V lower than that of traditional InGaP/GaAs HBT. The results show that GaAsSb is a suitable base material for reducing the turn-on voltage of GaAs HBTs.
The REX-ISOLDE project
The Radioactive Beam Experiment REX-ISOLDE [1–3] is a pilot experiment at ISOLDE (CERN) testing the new concept of post acceleration of radioactive ion beams by using charge breeding of the ions in a high charge state ion source and the efficient acceleration of the highly charged ions in a short LINAC using modern ion accelerator structures. In order to prepare the ions for the experiments singly charged radioactive ions from the on-line mass separator ISOLDE will be cooled and bunched in a Penning trap, charge bred in an electron beam ion source (EBIS) and finally accelerated in the LINAC. The LINAC consists of a radiofrequency quadrupole (RFQ) accelerator, which accelerates the ions up to 0.3 MeV/u, an interdigital H-type (IH) structure with a final energy between 1.1 and 1.2 MeV/u and three seven gap resonators, which allow the variation of the final energy. With an energy of the radioactive beams between 0.8 MeV/u and 2.2 MeV/u a wide range of experiments in the field of nuclear spectroscopy, astrophysics and solid state physics will be addressed by REX-ISOLDE.