Intelligent Sensors for Atomization Processing of Molten Metals and Alloys
ABSTRACT We briefly introduce the principles of atomization processing of molten metals and alloys, discuss potentially applicable instrumentation, and propose opportunities for developing intelligent sensors for monitoring and control of the process. Particle size and velocity are considered the two most important variables to monitor and control the atomization process. Several on-line sensors suitable for atomization of molten metals and alloys are compared: laser light scattering methods using small angle scattering analysis, moderate angle scattering analysis, and doppler analysis, electrical methods using surface ionization and triboelectric charging, and image analysis. The isokinetic sampling probe is introduced as a direct method to sample powders at the desired point in the atomized spray. Prospects and problems of integrating instruments based on these principles into intelligent processing of materials (IPM) scenarios are discussed.
Comparative measurements using different particle size instruments
This paper discusses the measurement and comparison of particle size and velocity measurements in sprays. The general nature of sprays and the development of standard, consistent research sprays are described. The instruments considered in this paper are: pulsed laser photography, holography, television, and cinematography; laser anemometry and interferometry using visibility, peak amplitude, and intensity ratioing; and laser diffraction. Calibration is by graticule, reticle, powders with known size distributions in liquid cells, monosize sprays, and, eventually, standard sprays. Statistical analyses including spatial and temporal long-time averaging as well as high-frequency response time histories with conditional sampling are examined. Previous attempts at comparing instruments, the making of simultaneous or consecutive measurements with similar types and different types of imaging, interferometric, and diffraction instruments are reviewed. A program of calibration and experiments for comparing and assessing different instruments is presented.
Measuring Sheet Resistances of Dielectrics Using Co‐Planar Hydrogel Electrochemical Cells with Practical Applications to Characterize the Protective Quality of Paints on Sculptures
Electrical properties of thin dielectric films at the solid-liquid phase boundary are an important performance characteristic of many devices, coatings and sensors. In this paper, co-polymeric hydrogels of polyacrylic acid co-sulfonic acid, swollen with a salt solution to act as the solid electrolyte, were used to assess interfaces using electrochemical impedance spectroscopy (EIS) in a co-planar geometry. Silane-modified glasses were characterized by the co-planar hydrogel EIS cell and found to be distinguishable based on their surface monolayer chemistry. EIS measurements were also made on primed and painted metal substrates, using both test panels and an outdoor sculpture, Tony Smith's Stinger. The panels were then exposed to accelerated and outdoor weathering and showed degradation on the surface paint layers, which was observable electrochemically using EIS and confirmed visually by SEM. Electrochemical spectral features were compared between data from a standard paint-test cell versus this co-planar hydrogel cell; both cell types were able to measure coating capacitance, providing useful information about the condition of the bulk coating. Yet, sheet resistance (Rs) was a spectral feature seen only by the co-planar hydrogel cell. Thus, it can be concluded that the use of such co-planar hydrogel cells can provide an earlier warning sign to coating degradation and such cells provide a new type of spectral information that is not assessable by the standard geometry.