Influence of demagnetization in remanence curves of magnetic thin films
Remanent magnetization curves of perpendicular magnetic thin films are simulated and measured. The simulations are used to investigate the theoretical influence of the strong demagnetizing field present in these films. Conclusions are drawn from this on how remanence curves should be measured and how they should be corrected for the demagnetizing influence. The experimental part consists of measurements on Fe‐Alumite, Co‐Pt–based multilayers, and Co‐Cr. In addition the latter material is also artificially patterned into microstrips in order to investigate the influence of demagnetization on remanence curves experimentally.
Low-temperature crystallisation of Heusler alloy films with perpendicular magnetic anisotropy
Abstract We demonstrate that perpendicular anisotropy can be induced in Co2FeAl0.5Si0.5 by depositing the Heusler alloy on a tungsten seed layer. This is increased by elevating the deposition temperature to a moderate value up to 335 K. These perpendicular layers can be implemented into GMR devices, showing layer-thickness dependent switching without the use of an antiferromagnetic pinning-layer. These layers can be implemented into the manufacturing process of read-heads, where temperatures are limited.
Characterization of Aqueous Dispersions and Gels Made of Sodium Caseinate and Basil Seed Gum: Phase Behavior, Rheology, and Microstructure
The interactions between sodium caseinate (NaCas) and basil seed gum (BSG) in the presence of calcium chloride (CaCl 2 ) were investigated. The phase behavior of the mixed aqueous dispersions and their gels revealed a homogeneous mixture, obtained at the higher concentrations of both CaCl 2 and BSG. The Herschel-Bulkley model sufficiently fitted the flow behavior of the mixture solution data. Apparent viscosity increased significantly ( p  < 0.05) by increasing the concentration of BSG, where the addition of CaCl 2 had no significant effect on the viscosity of the samples ( p  > 0.05). Furthermore, there was an increase in thixotropy due to the higher concentrations of BSG and CaCl 2 . Based on the frequency sweep test, at the low frequencies, a more gel-like behavior was observed in the case of the higher concentrations of either BSG or CaCl 2 . The rheological and SEM data suggested that the stronger structure of NaCas-BSG gel in the presence of the higher concentrations of CaCl 2 was related to the induction of complex formation between the two biopolymers.