Abrasion resistance of surface-modified steels used for artillery weapon barrels
A barrel is one of the most tribologically and thermally loaded parts of artillery weapons. The influence of the salt bath nitrocarburizing and hard-chrome plating of three steels used for artillery barrels on their abrasion resistance is studied in this paper. The tested steels are 42CrMo4, 30CrNiMo8, and 36CrNiMo4 in the initial quenched and tempered state. The test results from the ''dry sand/rubber wheel'' method, after 700 m of wear path, showed that the hard-chrome plating of 42CrMo4 and 30CrNiMo8 steels improved their abrasion resistance. In addition, reduced abrasive wear of 42CrMo4 steel samples was also achieved by nitrocarburizing. Hard chrome-plated samples exhibited good wear resistance due to their greater hardness and bigger thickness of the compound zone in comparison with that obtained on nitrocarburized samples.
Investigation of the material chemical composition influence on artillery weapons barrel hardness
The weapon barrel is exposed to strong thermal, mechanical and chemical effect of the powder gasses and the projectile. That causes the appearance of the intensive wear process of the barrel bore. In this paper the analysis of the samples’ chemical composition is performed, the metallographic structure of the samples’ material is imaged, the possible modification of the barrel bore surface is tested and the hardness over the samples cross section was measured. The hardness of the barrel material is one of the essential factors which contribute to increased barrel’s wear resistance. Therefore, modelling of HV5 hardness as a function of the chemical composition of materials was conducted. Determined correlations should allow an easier selection of the wear resistant barrel material as well as the material of other parts of the artillery weapons, with the need to establish a small number of influential parameters, without carrying out extensive tests.
Joint strength of aluminum ultrasonic soldered under liquidus temperature of Sn–Zn hypereutectic solder
Abstract In order to obtain high-strength aluminum joints, ultrasonic soldering of 1070 aluminum was conducted under liquidus temperature of Sn–Zn hypereutectic solder. A device for ultrasonic soldering was assembled, which propagated ultrasonic vibrations in a direction perpendicular to joining surfaces. This device joined 1070-Al using quasi-melting Sn–Zn hypereutectic solder without using any artificial spacers. The strength of the solder joints was evaluated by tensile tests. The optimum joining conditions were determined, and the effects of solder compositions and soldering temperature on the joint strength and the solder layer thickness were examined. In this ultrasonic soldering process, the highest tensile strength was obtained for the solder joints fabricated at 220 °C for the Sn–23Zn and Sn–40Zn solder compositions. The joint strength was equivalent to that of 1070-Al heat treated at 220 °C. The sound joints were obtained at 300 °C using Sn–82Zn solder, the liquid phase volume fraction of which was theoretically only 0.24. The present work also revealed that the thickness of retained solder layer in the joint after ultrasonic soldering could be estimated. Accordingly, ultrasonic soldering under the liquidus temperature of Sn–Zn hypereutectic solder could be a spacer-free soldering method to obtain high-strength aluminum joints.