Thermal Analysis of the Fuse with Unequal Fuse Links Using Finite Element Method
In this paper a three dimensional thermal model of high breaking capacity fuse with unequal fuse links is proposed for both steady-state or transient conditions. The influence of ambient temperature and electric current on the temperature distribution inside the fuse, has been investigated. A thermal analysis of the unbalanced distribution of the electric current through the fuse elements and their influence on fuse link temperature rise, has been performed. To validate the three dimensional thermal model, some experimental tests have been done. There is a good correlation between experimental and simulation results. Keywords—Electric fuse, fuse links, temperature distribution, thermal analysis.
Steady-State Thermal Analysis of Electric Fuse using Finite Element Method
Electric fuses are widely used for electrical safety purposes for many years in different levels of electrical systems. In this paper, the steady-state thermal analysis of an automotive fuse using the finite element method is presented. A fuse thermal model was developed as a simulation benchmark. Thermal characterization tests were carried out to validate the thermal model with an average error between simulation and measurements of ∼4.4%. The thermal model provides a useful tool for fuse design and development.
Thermal incompatibility analysis of metal-ceramic systems based on flexural displacement data.
The feasibility of simple tests or analytical methods for prediction of residual stress states in metal-ceramic (MC) prostheses has not been demonstrated. Biomaterial metal-ceramic strips have been proposed to provide sensitive measures of transient and residual stress states through the measurement of midpoint deflection after cooling from the ceramic sintering temperature. The objective of this study was to apply the elastic-viscoelastic analogy to calculate transient and residual midpoint deflections in MC biomaterial strips and to compare these values with deflections measured with a beam-bending viscometer (BBV). Calculations and measurements were made for five MC systems that were found from a clinical study to be "thermally compatible" systems. Metal strips, 64 mm in length, 3 mm wide, and either 0.5 mm, 1.0 mm, or 2.0 mm in thickness, were veneered with four 0.25-mm thick layers of opaque porcelain. Midpoint deflection of the MC strips (ceramic oriented in the posterior position) was measured during cooling from an initial temperature of 700 degrees C. In general, the directions of the measured residual deflections did not agree with the "textbook" convention that negative deflections are associated with positive thermal contraction mismatch (alpha(M) - alpha(c) > 0) regardless of metal thickness. For a metal thickness of 0.5 mm, the residual midpoint deflection for all thermal contraction mismatch cases, except one, was positive (upward deflection) whereas the residual midpoint deflections were all negative when the metal thickness was increased to 1 or 2 mm, independent of the thermal contraction mismatch. The best agreement between calculated and measured values of residual midpoint deflection (+16 microns vs. +14 +/- 2.3 microns, respectively was obtained for MC biomaterial strips with a Ni-Cr alloy (0.5 mm thick) while the largest difference (+346 microns vs. +61 +/- 43.8 microns) was obtained for MC bimaterial strips with a Au-Pd allow (0.5 mm thick). In all but one case, changes in deflection direction as a function of metal thickness were correctly predicted by the viscoelastic analysis. The results of this study indicate that a viscoelastic model is useful for estimating thermal compatibility conditions of MC systems.