Difatty acyl urea from corn oil: synthesis and characterization.
In this study, difatty acyl urea has been successfully synthesized from corn oil using sodium ethoxide as a catalyst. Ethyl fatty ester and glycerol were produced as by-products. In this reaction, corn oil was refluxed with urea in ethanol. The highest conversion percentage (78%) was obtained when the process was carried out for 8 hours using urea to corn oil ratio of 5.6: 1.0 at 78 degrees C. Both difatty acyl urea and ethyl fatty ester have been characterized using elemental analysis, Fourier transform infrared (FTIR) spectroscopy and (1)H nuclear magnetic resonance (NMR) technique.
Structure-property studies of thermoplastic and thermosetting polyurethanes using palm and soya oils-based polyols.
Palm and soya oils were converted to monoglycerides via transesterification of triglycerides with glycerol by one step process to produce renewable polyols. Thermoplastic polyurethanes (TPPUs) were prepared from the reaction of the monoglycerides which act as polyol with 4,4'-methylenediphenyldiisocyanate (MDI) whereas, thermosetting polyurethanes (TSPUs) were prepared from the reaction of glycerol, MDI and monoglycerides in one pot. Characterization of the polyurethanes was carried out by FT-IR, (1)H NMR, and iodine value and sol-gel fraction. The TSPUs showed good thermal properties compared to TPPUs as well as TSPUs exhibits good properties in pencil hardness and adhesion, however poorer in flexural and impact strength compared to TPPUs. The higher percentage of cross linked fraction, the higher degree of cross linking occurred, which is due to the higher number of double bond presents in the TSPUs. These were reflected in iodine value test as the highest iodine value of the soya-based thermosetting polyurethanes confirmed the highest degree of cross linking. Polyurethanes based on soya oil showed better properties compared to palm oil. This study is a breakthrough development of polyurethane resins using palm and soya oils as one of the raw materials.
On the fractionation of β-lactoglobulin and α-lactalbumin
Abstract Existing methods for the preparation of α-lactalbumin and β-lactoglobulin are examined critically. It is proposed that the most satisfactory method for the preparation of the whey protein fraction from bovine milk is (NH 4 ) 2 SO 4 fractionation. A number of new gentle procedures for the fractionation of the whey proteins are compared with some existing methods. The distribution of total protein at various stages is determined by total Kjeldahl nitrogen and the kind of protein by starch-gel electrophoresis. The effect of variables, such as pH, salt concentration and temperature on the separation of α-lactalbumin and serum albumin from β-lactoglobulin is studied. Differences in the behavior ( e.g. solubility) of genetic variants of β-lactoglobulin are noted. The solubility of each of the major whey proteins, under similar conditions to those used in the fractionation, is compared with its solubility in the whey protein mixture. The understanding gained of factors important in the fractionation is used in recommending new procedures for α-lactalbumin and β-lactoglobulin isolation.