Comparison between leached metakaolin and leached diatomaceous earth as raw materials for the synthesis of ZSM-5
Inexpensive raw materials have been used to prepare ZSM-5 zeolites with SiO2/Al2O3 molar ratios in the range 20 – 40. Kaolin or Bolivian diatomaceous earth was used as aluminosilicate raw materials and sodium hydroxide and n- butylamine were used as mineralizing agents and template. Dealumination of the raw materials by acid leaching made it possible to reach appropriate SiO2/Al2O3 ratios and to reduce the amount of iron and other impurities. After mixing the components and aging, hydrothermal treatment was carried out and the products were recovered The results clearly show for the first time that well-crystallized ZSM-5 can be directly prepared from leached metakaolin or leached diatomaceous earth using sodium hydroxide and n-butylamine as mineralizing agents and template under appropriate synthesis conditions. A longer induction time prior to crystallization was observed for reaction mixtures prepared from leached diatomaceous earth, probably due to slower digestion of the fossilized diatom skeletons as compared with that for microporous leached metakaolin. The use of leached diatomaceous earth allowed higher yield of ZSM-5 crystals within comparable synthesis times. However, low amounts of Mordenite formed, which was related to the high calcium content of diatomaceous earth. Another considerable advantage of diatomaceous earth over kaolin is that diatomaceous earth does not require heat treatment at high temperature for metakaolinization.
Solution-mediated growth of NBA-ZSM-5 crystals retarded by gel entrapment
Abstract The synthesis of flat tablet-shaped ZSM-5 crystals from a gel using metakaolin as aluminosilicate source and n -butyl amine as structure directing agent was investigated. The evolution inside the solid phase was characterized by X-ray diffraction, scanning electron microscopy, energy dispersive spectroscopy, thermogravimetry and mass spectrometry. A kinetic study indicated that the nucleation of the majority crystals occurred concurrently with the formation of the gel upon heating the starting liquid suspension. Microstructural evidences undeniably showed that the gel precipitated on ZSM-5 crystals and mineral impurities originating from kaolin. As a result, crystal growth was retarded by gel entrapment, as indicated by the configuration and morphology of the embedded crystals. The results presented herein are harmonized with a solution-mediated nucleation and growth mechanism. Our observations differ from the autocatalytic model that suggests that the nuclei rest inside the gel until released when the gel is consumed. Our results show instead that it is crystals that formed in an early stage before entrapment inside the gel that rest inside the gel until exposed at the gel surface. These results illustrate the limitation of the classical method used in the field to determine nucleation profiles when the crystals become trapped inside the gel.
Comparison between Two Chemicals for Reducing Scale Formation in Reverse Osmosis Systems
In this present research was transacted with the calcium carbonate scale inhibition on the membrane surface of the reverse osmosis desalination system. Influence of changing feed solution flow rate (10-25)l/h, pH of the feed solution (6-10) on the recovery ,penetrate flow rate and total dissolved solid in (RO) system by using solution of calcium carbonate as feed solution was investigated, furthermore the effect of adding two types of scale inhibitor ,zinc chloride and polyamino polyether methylene phosphonate with difference concentration (2-8)mg/l for zinc chloride and (8-15) mg/l for polyamino polyether methylene phosphonate was calculated. The results showed that the permeate rate increases as the feed flow rate augmentation ,while it reducing with time, the total dissolved solids decreases as the feed flow rate increases while it increases with time and recovery rate decreases as the feed flow rate increases and it also decreases with time. It was concluded that the permeate rate decreases as the feed solution pH value increases and it cause high scale forming thus decrease the permeate TDS.By adding the scale inhibitor, it was found that the permeate rate and recovery rates increases as the concentration of inhibitor increases while the total dissolved solids decreases in the permeate with increasing the concentration of both inhibitors .It was discovered that Polyamino polyether methylene phosphonate more sturdy than zinc chloride as scale inhibitor for reverse osmosis desalination system in all concentrations was studied in this article.