The beneficial effect of Zn additions on the microstructure of SnCu and SnCuNi solder joints to Cu substrates
The commercial success as Pb-free solders of alloys based on a trace addition of Ni to Sn-0.7Cu and the academic recognition of the metallurgical effects that deliver the excellent performance in soldering processes and in service, means that Sn-Cu-Ni is now well established as one of the main alloy systems on which the electronics industry depends for the assembly of reliable circuitry. One important effect of the Ni addition is the stabilization of the hexagonal form of the Cu6Sn5 phase that forms at the interface between the solder and the Cu substrate. However, with the limited amount of Ni available in a solder joint, growth of the intermetallic layer by reaction with a copper substrate can result in the Ni level in the Cu6Sn5 falling below that required for stabilization. Increasing the Ni in the solder alloy beyond the level required for optimization of properties such as fluidity that are important in soldering processes can result in the appearance of undesirable high melting point Sn-Ni phases, It would therefore be useful if a second stabilizing element could be introduced to the system to support the effect of the Ni. Ni works as a stabilizer by partially substituting for Cu in the Cu6Sn5 so potential additives were considered on the basis of reports of their partially replacing either Cu or Ni in that crystal structure. Zn was selected for this study because it can partially substitute for Sn in the Cu6Sn5 crystal, potentially complementing the role of Ni. The effect of a Zn addition was studied in the basic Sn-0.7Cu and when there was also an addition of Ni. By itself a Zn addition did not promote a eutectic microstructure in the way that a Ni addition does so powerfully but alone or with Ni it substantially reduced undercooling and in the alloy with both Ni and Zn there was an overall refinement in the near completely eutectic microstructure. In combination with the Ni the Zn significantly refined the grain size of the Cu6Sn5 that formed at the solder/Cu interface. By itself the Zn did not suppress the formation of Cu3Sn at the interface between the Cu and the Cu6Sn5 in the way that Ni does but it does not interfere with that beneficial effect of the Ni. Diffraction studies with high energy synchrotron-generated X-rays confirm that as well as stabilizing the hexagonal form of the Cu6Sn5, Zn reduces the anisotropy of this phase and increases the randomness of the crystal orientation in the intermetallic layer. These effects should result in a stronger intermetallic layer that is less likely to degrade during thermal cycling. The combination of all of these effects mean that an addition of Zn to the widely used Sn-Cu-Ni lead free solders should result in an overall increase in reliability of the solder joint, particularly in harsh environments.
Effect of Bismuth Additions on Wettability, Intermetallic Compound, and Microhardness Properties of Sn-0.7Cu on Different Surface Finish Substrates
The influence of bismuth (Bi) addition on wettability, thickness of interfacial intermetallic compound (IMC), and microhardness properties of Sn-0.7Cu + xBi solder alloy using different types of substrate were examined. The 0.5, 1.0, 1.5, and 2.0 wt. % Bi was added into Sn-0.7Cu and fabricated using the casting process. The result shows that the influence of 1.5 wt. % Bi in the Sn-0.7Cu solder soldered on copper organic solderability preservative (Cu-OSP) and immersion tin (Im-Sn) surface finish has improved the wettability and microhardness. Subsequently, the IMC thickness of Sn-0.7Cu+1.5Bi solder alloy on Im-Sn surface finish gives a better result than reflowed on Cu-OSP. Generally, with the addition of 1.5 wt. % Bi in Sn-0.7Cu solder alloy reflowed on the Im-Sn surface finish had enhanced the performance in terms of wettability, thickness of IMC and microhardness properties compared to on Cu-OSP surface finish.
Evolution of carbide precipitates in Hastelloy N joints during welding and post weld heat treatment
Abstract The effects of welding and post weld heat treatment (PWHT) on the morphology, composition and lattice parameter of the precipitates in the welding joints of Hastelloy N alloy have been investigated. Joint samples were prepared using a gas tungsten arc welding process with ERNiMo-2 fillers, and then solid-solution treated at 1100 °C for 20 min. After welding, eutectic M6C carbides can be observed in the heat affected zones (HAZ) and weld zones (WZ). These eutectic M6C carbides become spheroidized during the following PWHT. The concentration of Si decreases during the transformation from the primary ones to eutectic ones, and then increases during the spheroidizing process. The total concentration of Si + Cr in M6C carbides remains stable during welding and PWHT. At the same time, the heat leads to the outward diffusion of Mo from the M6C carbides, which results in a decrease of the lattice parameter.