A study on the changes in attractive force of magnetic attachments for overdenture
PURPOSE Although magnetic attachment is used frequently for overdenture, it is reported that attractive force can be decreased by abrasion and corrosion. The purpose of this study was to establish the clinical basis about considerations and long term prognosis of overdenture using magnetic attachments by investigating the change in attractive force of magnetic attachment applied to the patients. MATERIALS AND METHODS Among the patients treated with overdenture using magnetic attachments in Dankook University Dental Hospital, attractive force records of 61 magnetic attachments of 20 subjects who re-visited from July 2013 to June 2014 were analyzed. Dental magnet tester (Aichi Micro Intelligent Co., Aichi, Japan) was used for measurement. The magnetic attachments used in this study were Magfit IP-B Flat, Magfit DX400, Magfit DX600 and Magfit DX800 (Aichi Steel Co., Aichi, Japan) filled with Neodymium (NdFeB), a rare-earth magnet. RESULTS Reduction ratio of attractive force had no significant correlation with conditional variables to which attachments were applied, and was higher when the maintenance period was longer (P<.05, r=.361). Reduction ratio of attractive force was significantly higher in the subject group in which attachments were used over 9 years than within 9 years (P<.05). Furthermore, 16.39% of total magnetic attachments showed detachment of keeper or assembly. CONCLUSION Attractive force of magnetic attachment is maintained regardless of conditional variables and reduction ratio increased as the maintenance period became longer. Further study on adhesive material, attachment method and design improvement to prevent detachment of magnetic attachment is needed.
A retentive attachment for overdentures.
A technique is described that incorporates an extracoronal attachment within an overdenture to provide increased retention. This type of retentive attachment is easily fabricated. It's durability, simplicity, adjustability, and adaptability to a wide variety of situations make it most useful. The retentive attachment may be used with either removable partial dentures or complete dentures.
Joint strength of aluminum ultrasonic soldered under liquidus temperature of Sn–Zn hypereutectic solder
Abstract In order to obtain high-strength aluminum joints, ultrasonic soldering of 1070 aluminum was conducted under liquidus temperature of Sn–Zn hypereutectic solder. A device for ultrasonic soldering was assembled, which propagated ultrasonic vibrations in a direction perpendicular to joining surfaces. This device joined 1070-Al using quasi-melting Sn–Zn hypereutectic solder without using any artificial spacers. The strength of the solder joints was evaluated by tensile tests. The optimum joining conditions were determined, and the effects of solder compositions and soldering temperature on the joint strength and the solder layer thickness were examined. In this ultrasonic soldering process, the highest tensile strength was obtained for the solder joints fabricated at 220 °C for the Sn–23Zn and Sn–40Zn solder compositions. The joint strength was equivalent to that of 1070-Al heat treated at 220 °C. The sound joints were obtained at 300 °C using Sn–82Zn solder, the liquid phase volume fraction of which was theoretically only 0.24. The present work also revealed that the thickness of retained solder layer in the joint after ultrasonic soldering could be estimated. Accordingly, ultrasonic soldering under the liquidus temperature of Sn–Zn hypereutectic solder could be a spacer-free soldering method to obtain high-strength aluminum joints.