The influence of switching arcs on contact resistance of Ag/SnO2 materials
Silver tin oxide (Ag/SnO2) contact materials are widely used for relays and contactor applications. Device approbation in accordance to standards requires several types of temperature rise test in new and switched conditions. Significant differences in temperature rise after the various switching sequences are experienced. In addition, differences between individual phases of one device - especially in switched condition - are known from test. In this work, the contact resistance evaluation under different load conditions has been studied. Therefore the arcing events at make and break operation during different endurance tests (AC-3 and AC-4) have been analyzed and correlated to the contact resistances at rated current level during temperature rise test. Surface layer changes of contact materials after load are characterized by metallurgical methods. The paper shows the formation of different surface layers as a function of arcing energies during make and break operation. The results demonstrate that make and break arc together are creating the surface layers defining the final contact resistance.
Effects of different loads on the surface of silver metal oxide contacts for general-purpose relays
Silver metal oxides have become very popular as contact materials in electromechanical switching devices due to their high resistance to erosion and contact welding. Initially, these materials were developed for contactors and circuit breakers. Investigations on silver metal oxide contacts for general-purpose relays were conducted in order to gain an insight into the effects and failure mechanism of such contacts under specific loads, such as resistive and inrush current loads. It will be shown that contact failures may be influenced by very thin silver layers on the surface of silver metal oxide materials and the behavior of these layers at thermal stress. The silver layers are a result of the mechanical treatment in the production of rivets and the following riveting process. The results support the development of new silver metal oxide materials for general-purpose relay applications.
Evaluation of Impact of Yarn Count and Stitch Length on Pilling, Abrasion, Shrinkage and Tightness Factor of 1 ? 1 Rib Cotton Knitted Fabrics
This study investigates the impact of yarn count and stitch length of 100% cotton knitted fabrics. 1 × 1 ribs structured fabrics were used in this research work. The stitch length 2.50 mm, 2.52 mm, 2.60 mm, 2.70 mm, 2.80 mm and 2.96 mm were used of the yarn count of 26Ne, 28Ne and 36Ne. The areal densities of the grey fabrics were in various amounts. The impacts of yarn count and stitch length were measured concerning pilling resistance, abrasion resistance, and shrinkage and tightness factor. The result showed that the fabric pilling grade decreased while number of cycle increased. Abrasion resistance decreased but length wise shrinkage increased despite the fact that the stitch length increased. The results also exposed that the tightness factor of the fabric increased with the increase of the stitch length in both dyeing and washing state and finished state compared to grey state for the yarn count 26Ne and homogeneous result not found for yarn count 28Ne and 36 Ne. Evaluation of Impact of Yarn Count and Stitch Length on Pilling, Abrasion, Shrinkage and Tightness Factor of 1 × 1 Rib Cotton Knitted Fabrics