Click construction of spiro- and bridged-quatrefoil polymer topologies with kyklo-telechelics having an azide group.
Unprecedented tetracyclic polymer topologies with spiro- and a bridged-type quatrefoil forms are effectively constructed through an alkyne-azide, click-linking reaction by employing a kyklo-telechelic poly(tetrahydrofuran), poly(THF), precursor having an azide group, obtained through an electrostatic self-assembly and covalent fixation (ESA-CF) process, and complementary tetrafunctional alkyne reagents of either a pentaerythritol derivative or a four-armed star telechelic polymer precursor.
Junction-Controlled Topological Polymerization.
Methodology that enables the controlled synthesis of linear and branched polymers from an identical monomer will be a novel pathway for polymer synthesis and processing. Herein we first describe the control of one or both of the C(3)-C(3') and C(6)-C(6') coupling reactions of carbazolyl. In a second approach, an identical monomer containing two carbazolyls is polymerized using chemical and electrochemical oxidizers, leading to topologically controllable growth of linear polymers in weak oxidizer or of cross-linked polymer chains in strong oxidizer, with satisfactory long chain propagation of step growth polymerization (Mn =6.0×104  g mol-1 , Mw /Mn =2.3). This very simple polymerization with cheap reagents and low levels of waste has provided a flexible pathway for synthesis and processing of polymers.
Unidirectional hexagonal rare-earth disilicide nanowires on vicinal Si(100)-2×1
Rare-earth disilicide nanowires grown on vicinal Si(100) with a miscut of 2–2.5° toward the [110] azimuth at 600 °C were studied by scanning tunneling microscopy and compared with those grown on flat Si(001). In contrast to rare-earth disilicide nanowires grown on flat Si(100) surfaces, the nanowires grow unidirectionally along the [01̄1] direction of the vicinal Si(100) surface. Rare-earth disilicide nanowires form bundles composed of single nanowire units on both flat and vicinal surfaces. Yet, on the vicinal surface, the bundle width is comparable to the width of the terrace. The average nanowire length on the vicinal substrate is longer than that on the flat substrate. Scanning tunneling spectroscopy shows that the rare-earth disilicide nanowires have metallic properties.