Effect of Modification on the Physicochemical and ThermalProperties of Organophilic Clay Modified with Octadecylamine
Organophilic clay was modified by ion exchange reactions using Octadecylamine. The reaction process was carried out at a temperature of 70oC for 90 minutes reaction time in a batch reactor equipped with a mechanical stirrer rotating at a speed of 300 rpm. Physicochemical and thermal 
properties of the clay before and after modification were determined and compared using Field Emission Scanning Electron Microscope/ Energy Dispersive X-ray spectroscopy (FESEM/EDX),Fourier transform infrared spectroscopy (FT-IR) and Thermogravimetric Analyzer (TGA). FESEM images show clearly the micro structural differences between the modified and unmodified clay while EDX shows a compositional changes between modified and unmodified 
clay with the presence of 7.27% carbon in the modified clay. The analysis of FT-IR spectra shows the attachment of some functional groups which are mostly alkyl and hallo-alkyl groups. This is an indication of proper modification. TGA plots of both pure unmodified and organically modified clay attained stability at a temperature between 500oC and 900oC after reduction in weight due to evaporation of moisture and decomposition of the adhered Alkylammonium salts between 30oC and 500oC. This confirmed that thermal stability of the organically modified clay compared favorably with pure natural clay under TGA.
Comparative adsorption of Ni(II) and Cd(II) ions on epichlorohydrin crosslinked chitosan–clay composite beads in aqueous solution
Abstract Removal of Ni(II) and Cd(II) by adsorption on epichlorohydrin crosslinked chitosan–clay composite beads was examined in solutions representative of contaminated solutions containing heavy metals. Several important parameters influencing the adsorption of Ni(II) and Cd(II) ions such as contact time, pH, temperature and effect of metal concentration were investigated systematically by batch experiments. Langmuir and Freundlich adsorption models were used to describe adsorption isotherms and constants. The obtained results showed that the equilibrium adsorption behavior of Ni (II) and Cd (II) on epichlorohydrin crosslinked chitosan–clay composite beads could be applied to Langmuir and Freundlich models respectively. Maximum adsorption capacities for Ni(II) and Cd(II) ions were found as 32.36 mg g−1 and 72.31 mg g−1 respectively. The recovery of the metal ions after adsorption and the regeneration of the adsorbent was carried out by treatment of the loaded beads with either 0.1 M HNO3, or 0.01 M EDTA. The adsorbents were characterized by FTIR, SEM and TGA analysis.
Timber, its nature and behaviour
Preface. Acknowledgements. Chapter 1 - Structure of Timber. Chapter 2 - Appearance of Timber in Relation to its Structure. Chapter 3 - Mass Volume Relationships. Chapter 4 - Movement in Timber. Chapter 5 - Flow in Timber. Chapter 6 - Deformation Under Load. Chapter 7 - Strength and Failure in Timber. Chapter 8 - Durability of Timber. Chapter 9 - Processing of Timber. Index.