High-Density Recording Characteristics of Obliquely Oriented Particulate Magnetic Tapes by Removal of Disoriented Surface Layer
In order to achieve high recording densities, wide bandwidth and high output, a magnetic tape should have a high Bs, perpendicular orientation, a smooth surface, good head contact, and a small longitudinal component. By using a "LIPS" orienting process which produces media with a longitudinally oriented inside layer and a perpendicular oriented surface layer, we have fabricated obliquely oriented magnetic films based on acicular metal particles; of these, tape oriented at 45° had the widest-bandwidth characteristics. But a significant improvement in output was not obtained because of the existence of disoriented particles in the surface layer, resulting from calendering treatment. We tried to remove this surface layer using polishing sheets. An obliquely oriented (45°) tape exhibited an improvement in short-wavelength output (by 10 dB at 0.3 ¿m) after the thickness of the disoriented layer was reduced by 0.12 ¿m.
Analysis due to vector magnetic field for recording characteristic of metal evaporated tape
Metal-evaporated tape (ME tape) is one of the most promising materials for high-density magnetic recording. In a previous study, we reported that the recording characteristics of ME tape are directly affected by the columnar microstructure of the magnetic layer (Co-Ni-O magnetic film). In this study, we have conducted the theoretical analysis of the effects of both head motion and the vector magnetic field H θ , which is essentially parallel to the columnar longitudinal axis. The results of this analysis offer an effective explanation of the recording characteristics of ME tape.
Study on urea-modified phenol formaldehyde resin adhesive
A reasonable technology to synthesize Urea-Modified Phenol Formaldehyde resins is realized by reacting phenol,urea and formaldehyde.The resin's feasibility is explored.The experiment result of shows that storable stability of the modified resin is good.The curing temperature of PUF resins was 25 ℃,lower than that of PF resins.The curing speed of PUF resins is faster than that of PF resins at the same curing temperature.The physical properties of the birch plywood bonded with PUF resins is similar to that of the birch plywood bonded with normal PF resins.The mechanical properties of the birch plywood bonded with PUF resins can achieve the demands of GB/T9846-1988.Free formaldehyde content of plywood is lower than the E1 level set by GB18580-2001.The cost of the adhesive is lowered for the use of urea,and its comprehensive properties is better than that of PF resins.