Lightweight Aggregate as Internal Curing Agent to Limit Concrete Shrinkage
Drying shrinkage is a principal cause of cracking in concrete structures. The cracking can be accommodated or modified so that the performance of the overall structure is not affected. This is not true for bridge decks where drying shrinkage cracking combines with plastic shrinkage, settlement, and thermal cracking to lower the durability of the deck by allowing water and deicing chemicals to penetrate the concrete and increase the susceptibility of the reinforcing steel to corrosion. Work is underway at the University of Kansas to develop concrete mixtures that will minimize concrete shrinkage to minimize cracking in bridge decks. It has been well established that the lower restraint provided by lightweight aggregates (LWAs) can lead to increased drying shrinkage compared with mixtures containing normal aggregates, and if not adequately prewettted, the unsatured pores lead to greater water demand during construction and result in inadequate water for hydration. Due to the absorption and desorption properties of the aggregate, vacuum-saturated LWAs can readily provide an internal source of water to increase hydration and lessen the drying effects on a concrete mixture. The effectiveness of prewetted, vacuum saturated (PVS) light-weight aggregates as an internal curing agent to reduce concrete shrinkage is evaluated for curing periods of 7 and 14 days in this paper.
Improved Concrete Materials with Hydrogel-Based Internal Curing Agents
This research article will describe the design and use of polyelectrolyte hydrogel particles as internal curing agents in concrete and present new results on relevant hydrogel-ion interactions. When incorporated into concrete, hydrogel particles release their stored water to fuel the curing reaction, resulting in reduced volumetric shrinkage and cracking and thus increasing concrete service life. The hydrogel’s swelling performance and mechanical properties are strongly sensitive to multivalent cations that are naturally present in concrete mixtures, including calcium and aluminum. Model poly(acrylic acid(AA)-acrylamide(AM))-based hydrogel particles with different chemical compositions (AA:AM monomer ratio) were synthesized and immersed in sodium, calcium, and aluminum salt solutions. The presence of multivalent cations resulted in decreased swelling capacity and altered swelling kinetics to the point where some hydrogel compositions displayed rapid deswelling behavior and the formation of a mechanically stiff shell. Interestingly, when incorporated into mortar, hydrogel particles reduced mixture shrinkage while encouraging the formation of specific inorganic phases (calcium hydroxide and calcium silicate hydrate) within the void space previously occupied by the swollen particle.
PREVENTION OF CRACKS IN CONCRETE BRIDGE DECKS: REPORT ON SURVEYS OF EXISTING BRIDGES
Cracking in newly constructed concrete bridge decks is a concern in Pennsylvania. This project aimed at examining the performance of existing bridge decks in Pennsylvania. Transverse cracking was identified as the prevalent type of cracking. The main cause of transverse cracking noted in the bridge decks was concrete shrinkage. Concrete shrinkage was the result of loss of heat of hydration during curing (thermal shrinkage) and loss of mix water after curing (drying shrinkage). Recommendations regarding aggregate type, cement type and content, and cold weather curing of concrete are provided to reduce shrinkage and minimize cracking.