Abstract—minor Problems Arising from Optimizations By
welding of fixed prostheses frameworks can be identified by macroscopic and microscopic visual inspection. The purpose of this study was to highlight the visible discontinuities present in the laser welds of dental Ni-Cr alloys. Ni-Cr base metal alloys designated for fixed prostheses manufacture were selected for the experiments. Using cast plates, preliminary tests were conducted by laser welding. Macroscopic visual inspection was done carefully to assess the defects of the welding rib. Electron microscopy images allowed visualization of small discontinuities, which escapes visual inspection. Making comparison to Ni-Cr alloys taken in the experiment and laser welded, after visual analysis, the best welds appear for Heraenium NA alloy.
Optimization of operator and physical parameters for laser welding of dental materials
Objective Interactions between lasers and materials are very complex phenomena. The success of laser welding procedures in dental metals depends on the operator's control of many parameters. The aims of this study were to evaluate factors relating to the operator's dexterity and the choice of the welding parameters (power, pulse duration and therefore energy), which are recognized determinants of weld quality.Design In vitro laboratory study.Materials and methods FeNiCr dental drawn wires were chosen for these experiments because their properties are well known. Different diameters of wires were laser welded, then tested in tension and compared to the control material as extruded, in order to evaluate the quality of the welding. Scanning electron microscopy of the fractured zone and micrograph observations perpendicular and parallel to the wire axis were also conducted in order to analyse the depth penetration and the quality of the microstructure. Additionally, the micro-hardness (Vickers type) was measured both in the welded and the heat-affected zones and then compared to the non-welded alloy.Results Adequate combination of energy and pulse duration with the power set in the range between 0.8 to 1 kW appears to improve penetration depth of the laser beam and success of the welding procedure. Operator skill is also an important variable.Conclusion The variation in laser weld quality in dental FeNiCr wires attributable to operator skill can be minimized by optimization of the physical welding parameters.
Mechanical properties of laser-welded cast and wrought titanium.
This study evaluated the mechanical properties of laser-welded cast and wrought titanium base and compared them with those of a brazed type IV casting gold alloy. Ultimate tensile strength, 0.2% yield strength, and percent elongation were recorded for joined and unjoined bars of the previously mentioned materials. Sections of titanium bars were laser-welded, and gold alloy bars were brazed. Both joining methods significantly reduced the ductility of the material. The strength of the cast gold alloy was superior to that of titanium. However, the strength of the laser-welded titanium equaled that of the brazed gold alloy, which suggests that dental restorations made of cast and wrought titanium would satisfy ordinary clinical requirements.