Study of the miscibility of poly(styrene-co-4-vinylbenzoic acid) with poly(ethyl methacrylate) or with poly[ethyl methacrylate-co-(2-N,N-dimethylaminoethyl) methacrylate] by inverse gas chromatography.
Poly(styrene) is immiscible with poly(ethyl methacrylate). The introduction of a small amount of 4-vinylbenzoic acid units along poly(styrene) chains (PS-VBA) enhanced its miscibility with poly(ethyl methacrylate) (PEMA) or with poly[ethyl methacrylate-co-(2-N,N-dimethylaminoethyl) methacrylate] (PEMA-DAE), as observed from the appearance of a single composition dependent glass transition temperature for each binary system using inverse gas chromatography. The negative values of the apparent polymer-polymer interaction parameter, chi(23)app, determined with different families of molecular probes, for three blend compositions and over a range of temperature confirm quantitatively the miscibility of these blends. The chi(23)app values for PEMA(PS-VBA) and (PEMA-DAE)-(PS-VBA) blends are dependent of the chemical nature of the probes, the temperature and the blend composition.
FTIR study of hydrogen bonding of blends of poly(mono n-alkyl itaconates) with poly(N,N-dimethylacrylamide) and poly(ethyloxazoline)
This paper reports a FTIR study of blends of poly(mono n-alkyl itaconates) with poly(N,N-dimethylacrylamide) (PDMA) and poly(ethyloxazoline) (PEOX). Strong hydrogen bonding has been found, and both polybases have shown similar acceptor strengths. The extent of the interassociation has been estimated by spectral curve fitting of the polybase carbonyl band. The solvent medium employed to cast the sample has been shown to have a negligible influence on the interassociation degree attained in the blend, whenever casting did not lead to phase-separated blends due to the Δχ effect. Results show that the interaction degree in blends with PEOX does not depend on the length of the poly(monoalkyl itaconate) side group, while an interassociating ability loss is observed in blends with PDMA as the side group size of the polyacid increases. This different behavior is attributed to the greater interspacing between vicinal carbonyl groups in PEOX. In any case, this band shows conformational sensitivity and reflects the ...
Determination of the Polymer-Polymer Interaction Parameter for the Polystyrene-Polybutadiene Pair
Abstract : The light scattering technique was utilized to measure the phase separation temperatures (cloud points) of mixtures containing a polystyrene and a polybutadiene of various molecular weights and also of mixtures containing a polystyrene and a random or block copolymer of styrene and butadiene. The data was analyzed to obtain the polymer-polymer interaction parameter for the styrene-butadiene pair as a function of temperature and concentration. The value of the parameter deduced from the homopolymer mixtures agrees well with that obtained from the mixtures containing a copolymer. The polymer-polymer interaction parameter thus evaluated was compared with a theoretical expression derived on the basis of the Flory equation-of-state theory. The effect of the free volume disparity between the two components was found to play a relatively minor role in determining the interaction parameter when the two polymers lack any specific interactions which would make them mutually miscible. (Author)