Effective Parameters in Axial Injection Suspension Plasma Spray Process of Alumina-Zirconia Ceramics
Suspension plasma spray (SPS) is a novel process for producing nano-structured coatings with metastable phases using significantly smaller particles as compared to conventional thermal spraying. Considering the complexity of the system there is an extensive need to better understand the relationship between plasma spray conditions and resulting coating microstructure and defects. In this study, an alumina/8 wt.% yttria-stabilized zirconia was deposited by axial injection SPS process. The effects of principal deposition parameters on the microstructural features are evaluated using the Taguchi design of experiment. The microstructural features include microcracks, porosities, and deposition rate. To better understand the role of the spray parameters, in-flight particle characteristics, i.e., temperature and velocity were also measured. The role of the porosity in this multicomponent structure is studied as well. The results indicate that thermal diffusivity of the coatings, an important property for potential thermal barrier applications, is barely affected by the changes in porosity content.
Phase Formation and Transformation in Alumina/YSZ Nanocomposite Coating Deposited by Suspension Plasma Spray Process
Suspension Plasma Spray process was used for deposition of pseudo-eutectic composition of alumina-yttria-stabilized zirconia as a potential thermal barrier coating using Mettech axial III torch. Process variables including feed and plasma parameters were altered to find their effects on the formation of phases in the composite coating. The in-flight particle velocity was found to be the crucial parameter on phase formation in the resulting coatings. Low particle velocities below 650 m/s result in the formation of stable phases i.e., α-alumina and tetragonal zirconia. In contrast, high particle velocities more than 750 m/s favor the metastable γ-alumina and cubic zirconia phases as dominant structures in as-deposited coatings. Accordingly, the plasma auxiliary gas and plasma power as influential parameters on the particle velocity were found to be reliable tools in controlling the resulting coating structure thus, the consequent properties. The noncrystalline portion of the coatings was also studied. It was revealed that upon heating, the amorphous phase prefers to crystallize into pre-existing crystalline phases in the as-deposited coating. Thus, the ultimate crystalline structure can be designed using the parameters that control the particle velocity during plasma spray coating.
Traceability strategy for gear-pitch-measuring instruments: development and calibration of a multiball artifact
There is a strong demand to ensure the traceability of gear-measuring instruments (GMIs). We propose a multiball artifact (MBA) for the evaluation of pitch-measuring accuracy. The aim of the MBA is to transfer the minimum uncertainty from a calibrated value at the National Metrology Institute of Japan (NMIJ) to a measured value of GMIs at a shop floor. The MBA is composed of equally spaced high-accuracy balls around an axis. The pitch-measuring accuracy of GMIs is evaluated by measuring the angular pitch deviation of the balls instead of the angular pitch deviation of a gear. We calibrated the angular pitch deviation using a coordinate measuring instrument (CMM) at the NMIJ and adapting a multiple-orientation technique. We proposed a calibration strategy of the angular pitch deviation. The calibration value of the pitch deviation for the MBA at the NMIJ was obtained with a measurement uncertainty (U95) of 0.2 µm. We evaluated the pitch-measuring accuracy of a GMI using the calibrated MBA. Each value of U95 for the cumulative and single pitch deviations for the left and right flanks was less than or equal to 0.5 µm. The small uncertainty was transferred from the NMIJ to the GMI.