Structural and Physical Properties Diversity of New CaCu5-Type Related Europium Platinum Borides
Three novel europium platinum borides have been synthesized by arc melting of constituent elements and subsequent annealing. They were characterized by X-ray powder and single-crystal diffraction: EuPt4B, CeCo4B type, P6/mmm, a = 0.56167(2) nm, c = 0.74399(3) nm; Eu3Pt7B2, Ca3Al7Cu2 type as an ordered variant of PuNi3, R3̅m, a = 0.55477(2) nm, c = 2.2896(1) nm; and Eu5Pt18B6–x, a new unique structure type, Fmmm, a = 0.55813(3) nm, b = 0.95476(5) nm, c = 3.51578(2) nm. These compounds belong to the CaCu5 family of structures, revealing a stacking sequence of CaCu5-type slabs with different structural units: CaCu5 and CeCo3B2 type in EuPt4B; CeCo3B2 and Laves MgCu2 type in Eu3Pt7B2; and CaCu5-, CeCo3B2-, and site-exchange ThCr2Si2-type slabs in Eu5Pt18B6–x. The striking motif in the Eu5Pt18B6–x structure is the boron-centered Pt tetrahedron [BPt4], which build chains running along the a axis and plays a decisive role in the structure arrangement by linking the terminal fragments of repeating blocks of fused Eu polyhedra. Physical properties of two compounds, EuPt4B and Eu3Pt7B2, were studied. Both compounds were found to order magnetically at 36 and 57 K, respectively. For EuPt4B a mixed-valence state of the Eu atom was confirmed via magnetic and specific heat measurements. Moreover, the Sommerfeld value of the specific heat of Eu3Pt7B2 was found to be extraordinarily large, on the order of 0.2 J/mol K2.
Ternary gallides of the Ce2+nRh3+3nGa1+2n (n = 0—5) structure family
The structures of nine ternary intermetallic compounds (IMCs) of the cerium—rhodium—gallium system containing 50 at.% rhodium were determined by single-crystal X-ray diffraction. The compounds are built up of alternating Ce2Rh3Ga fragments with the Mg2Cu3Si (MgZn2 type) or Mg2Ni3Si (MgCu2 type) structure and CeRh3Ga2 fragments with the CeCo3B2 (CaCu5 type) structure and form a homologous series of the composition R2+nT3+3nM1+2n (n = 0—5). These compounds can be classified into trigonal (R-3m) or hexagonal (P63/mmc) branches depending on the Laves phase-type fragment.
Evaluation of Impact of Yarn Count and Stitch Length on Pilling, Abrasion, Shrinkage and Tightness Factor of 1 ? 1 Rib Cotton Knitted Fabrics
This study investigates the impact of yarn count and stitch length of 100% cotton knitted fabrics. 1 × 1 ribs structured fabrics were used in this research work. The stitch length 2.50 mm, 2.52 mm, 2.60 mm, 2.70 mm, 2.80 mm and 2.96 mm were used of the yarn count of 26Ne, 28Ne and 36Ne. The areal densities of the grey fabrics were in various amounts. The impacts of yarn count and stitch length were measured concerning pilling resistance, abrasion resistance, and shrinkage and tightness factor. The result showed that the fabric pilling grade decreased while number of cycle increased. Abrasion resistance decreased but length wise shrinkage increased despite the fact that the stitch length increased. The results also exposed that the tightness factor of the fabric increased with the increase of the stitch length in both dyeing and washing state and finished state compared to grey state for the yarn count 26Ne and homogeneous result not found for yarn count 28Ne and 36 Ne. Evaluation of Impact of Yarn Count and Stitch Length on Pilling, Abrasion, Shrinkage and Tightness Factor of 1 × 1 Rib Cotton Knitted Fabrics