Impression materials: effect of hydrophilicity and viscosity on ability to displace water from dentin surfaces.
The water-displacing ability of hydrophilic and hydrophobic impression materials was determined and related to the hydrophilicity and viscosity of the materials. The water-displacing ability of the materials was determined on a network of grooves in a dentin surface covered by a drop of water. After setting of the material, the number of crossings reproduced in the impression was calculated in percent of the total number of crossings. The hydrophilicity was assessed by measuring the contact angle between water and impression material. To determine viscosity, a rotoviscosimeter was used. Impression materials with contact angles less than 70 degrees showed a significant negative correlation between water-displacing ability and contact angle, i.e. the reproducing ability decreased with decreasing hydrophilicity of the materials. Impression materials with contact angles above 70 degrees showed a significant positive correlation between water-displacing ability and viscosity, i.e. the water-displacing ability improved with increasing viscosity.
Investigation of a new approach to measuring contact angles for hydrophilic impression materials.
PURPOSE
The purpose of this investigation was to examine the initial water contact angles of seven unset impression materials using commercially available equipment, in an effort to determine whether polyether impression materials (Impregum) have lower contact angles and are, therefore, more hydrophilic than VPS impression materials.


MATERIALS AND METHODS
The hydrophilic properties of unset polyether and VPS impression materials were analyzed with respect to their water contact angle measurements using the commercially available Drop Shape Analysis System DSA 10. Twenty-five data points per second were collected via video analysis. There was no delay from start of measurement and data collection. Data was collected for approximately 12 s. Droplet size was determined on the thickness of canula. If the droplets became too small in volume, the water that evaporated during the measurement was large in comparison to the volume of the droplet. Therefore, 5 microl was chosen as the lowest volume. Five trials were conducted per series for each featured material. Contact angles were calculated using the circle fitting method. Three tests using this technique were designed to control the variables of contact angle measurement with regard to time, the varying amount of fluid in contact with impression material during clinical use, and material thickness. Sample thickness of impression material was controlled by stripping the paste flat on a glass plate using a marking template to ensure a constant film thickness. Tests were conducted in a climatized room at 24 degrees C +/- 1 degree C. Deionized water was used as the fluid. The device was calibrated according to manufacturer's instruction for Young-Laplace fitting prior to the measurements. Results were analyzed using One-Way ANOVA, Tukey test, and t-test, as appropriate.


RESULTS
Comparing the fast setting impression materials by One-Way ANOVA and Tukey tests (p < .05) revealed the initial contact angles to range from 66.2 +/- 1.5 degrees to 127.5 +/- 4.4 degrees , of which the polyether material was the lowest after 45 s (66.2 +/- 1.5 degrees ), 120 s (70.3 +/- 2.8 degrees ), and 24 h (80.3 +/- 1.0 degrees ) after start of the mix. The selected times represent the different stages of unset material, ranging from 45 s as the earliest practical data collection time to 24 h, at which a stone model would be poured. The polyether materials tested exhibited lower contact angles and, thus, significantly higher initial hydrophilicity than all measured VPS materials. Additionally, Impregum impression materials are more hydrophilic in the unset stage than in the set stage. VPS may show a stepwise development of hydrophilicity in the set stage that was not observed in the unset stage.


CONCLUSIONS
The polyether impression materials tested were significantly more hydrophilic before, during, and after setting than that of VPS impression materials. Regardless of the amount of water in contact with the impression material, the polyether impression materials showed a significantly higher hydrophilicity in the unset stage than the VPS materials. The initial contact angle was not dependent on the thickness of the material. All parameters, including variation of time, volume of water droplet, and thickness of material, resulted in different absolute contact angles, but did not lead to a dramatic change in the ranking of the materials with regard to their hydrophilic behavior.
Joint strength of aluminum ultrasonic soldered under liquidus temperature of Sn–Zn hypereutectic solder
Abstract In order to obtain high-strength aluminum joints, ultrasonic soldering of 1070 aluminum was conducted under liquidus temperature of Sn–Zn hypereutectic solder. A device for ultrasonic soldering was assembled, which propagated ultrasonic vibrations in a direction perpendicular to joining surfaces. This device joined 1070-Al using quasi-melting Sn–Zn hypereutectic solder without using any artificial spacers. The strength of the solder joints was evaluated by tensile tests. The optimum joining conditions were determined, and the effects of solder compositions and soldering temperature on the joint strength and the solder layer thickness were examined. In this ultrasonic soldering process, the highest tensile strength was obtained for the solder joints fabricated at 220 °C for the Sn–23Zn and Sn–40Zn solder compositions. The joint strength was equivalent to that of 1070-Al heat treated at 220 °C. The sound joints were obtained at 300 °C using Sn–82Zn solder, the liquid phase volume fraction of which was theoretically only 0.24. The present work also revealed that the thickness of retained solder layer in the joint after ultrasonic soldering could be estimated. Accordingly, ultrasonic soldering under the liquidus temperature of Sn–Zn hypereutectic solder could be a spacer-free soldering method to obtain high-strength aluminum joints.