Thermal behaviour of succinic acid, sodium succinate and its compounds with some bivalent transitions metal ions in dynamic N2 and CO2 atmospheres
Thermal stability and thermal decomposition of succinic acid, sodium succinate and its compounds with Mn(II), Fe(II), Co(II), Ni(II), Cu(II) and Zn(II) were investigated employing simultaneous thermogravimetry and differential thermal analysis (TG-DTA) in nitrogen and carbon dioxide atmospheres and TG-FTIR in nitrogen atmosphere. On heating, in both atmospheres the succinic acid melt and evaporate, while for the sodium succinate the thermal decomposition occurs with the formation of sodium carbonate. For the transition metal succinates the final residue up to 1180 oC in N2 atmosphere was a mixture of metal and metal oxide in no simple stoichiometric relation, except for Zn compound, where the residue was a small quantity of carbonaceous residue. For the CO2 atmosphere the final residue up to 980 oC was: MnO, Fe3O4, CoO, ZnO and mixtures of Ni, NiO and Cu, Cu2O.
Synthesis‚ characterization and thermal behaviour of solid 4-methoxybenzoates of heavier trivalent lanthanides
Abstract Solid-state Ln–4-MeO-Bz compounds, where Ln stands for trivalent Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu and Y and 4-MeO-Bz is 4-methoxybenzoate, have been synthesized. Simultaneous thermogravimetry and differential thermal analysis (TG–DTA), differential scanning calorimetry (DSC), X-ray powder diffractometry, infrared spectroscopy and complexometry were used to characterize and to study the thermal behaviour of these compounds. The results led to information about the composition, dehydration, phase transition, coordination mode, structure, thermal behaviour and thermal decomposition of the isolated compounds. The phase transition observed in the some compounds has been reported for the first time.
Thermodynamics on the Carbochlorination of Titanium-bearing Ores
The equilibrium compositions of the multi-component, multi-phase and multi-reaction system of carbochlorination of titanium-bearing ores are calculated with HSC, a computational chemistry software. The thermodynamic equilibrium calculation of the reaction system shows that a complete conversion of titanium-bearing ores is feasible at a temperature near 200oC. At temperatures ranging from 800 to 1600oC, the products of the reaction system are all in gaseous phase. Thermodynamic analysis accords with the industrial practice. The simulated results provide reasonable scientific basis for improving suitable technological conditions of the carbochlorination reduction.