Industrial Potentiality of Alluvial Clays Deposits from Cameroon: Influence of Lateritic Clayey Admixture for Fired Bricks Production
The cartography and characterization of an alluvial clay deposit from Ebebda (Central region of Cameroon) were carried out in order to assess its suitability for the production of fired clay bricks. The clayey area investigated is ~ 50,000 m2 with an average thickness of the exploitable layer of 2.2 m, suggesting a deposit of about ~2.2 × 105 tonnes of clay. Mineralogy, physico-chemical and thermal analyses as well as firing properties were performed on representative clay samples. Kaolinite and quartz are the major minerals associated to illite. Upon heating to 900℃ - 1200℃, the linear shrinkage varies from 1.5% to 15%, the water absorption from 1.5% to 24% and the bending strength from 2 to 12 MPa. The admixture of lateritic clays (widely available) at 50%, 60%, 70% and 80% allow to decrease the shrinkage and bending strength, and to increase the water absorption. Overall, properties were satisfying the requirement for fired brick with 70% of laterite in the mixture.
Suitability of Foumban Clays (West Cameroon) for Production of Bricks and Tiles
Particle size analysis, Atterberg limits, X-ray diffraction, X-ray fluorescence and firing tests were used to determine physico-chemical, mineralogical and technological characteristics of residual lateritic (K1M, Ma2) and alluvial (KB3, KG3) clays from Foumban (West-Cameroon). For technological properties, the samples were pressed and fired over a temperature range of 900d relative high feldspars (20%) and illite contents (10%) in KB3 and MA2; high smectite content in KG3 (up to 20%). Chemical analyses indicate high SiO2 (49% - 77%) and low Al2O3 (14% - 23%) contents in the four samples, with comparatively low contents of iron oxides (4% - 7% in samples KB3 and KG3, 2.5% in MA2 and ~1.5% in sample K1M). The particle size distribution of the alluvial clays (KG3 and KB3) differs considerably: 7% to 37% of clay fraction, 20% to 78% of silt, and 15% to 58% of sand, while residual clays (K1M and MA2) present on average 12% of clay, 51% of silt and 37% of sand. Two raw clays (KB3 and MA2) can be used for bricks/tiles production without beneficiation or addition. K1M requires some flux addition to decrease the sintering temperature while KG3 presents poor properties due to the combined occurrence of smectite and a high clayey fraction (37%). Such mineralogical composition is responsible for very high plasticity (PI: 50), high shrinkage (LS: 5% - 16%), low porosity (OP: up to 21%) and high flexural strength (FS: 16 - 23 N/mm2) above 1050&degC. This last clay is therefore less appropriate for bricks and roofing tiles production since degreasers must be added to the raw material.
Mississippian Barnett Shale: Lithofacies and depositional setting of a deep-water shale-gas succession in the Fort Worth Basin, Texas
The Mississippian Barnett Formation of the Fort Worth Basin is a classic shale-gas system in which the rock is the source, reservoir, and seal. Barnett strata were deposited in a deeper water foreland basin that had poor circulation with the open ocean. For most of the basin's history, bottom waters were euxinic, preserving organic matter and, thus, creating a rich source rock, along with abundant framboidal pyrite. The Barnett interval comprises a variety of facies but is dominated by fine-grained (clay- to silt-size) particles. Three general lithofacies are recognized on the basis of mineralogy, fabric, biota, and texture: (1) laminated siliceous mudstone; (2) laminated argillaceous lime mudstone (marl); and (3) skeletal, argillaceous lime packstone. Each facies contains abundant pyrite and phosphate (apatite), which are especially common at hardgrounds. Carbonate concretions, a product of early diagenesis, are also common. The entire Barnett biota is composed of debris transported to the basin from the shelf or upper oxygenated slope by hemipelagic mud plumes, dilute turbidites, and debris flows. Biogenic sediment was also sourced from the shallower, better oxygenated water column. Barnett deposition is estimated to have occurred over a 25-m.y. period, and despite the variations in sublithofacies, sedimentation style remained remarkably similar throughout this span of time.