Aromatic polymers obtained by precipitation polycondensation: 4. Synthesis of poly(ether ketone ketone)s☆
Abstract High molecular weight aromatic poly(ether ketone ketone)s were synthesized by the Friedel-Crafts polyacylation condensation of iso- and terephthaloyl chlorides with diphenyl ether, 1,4- and 1,3-bis(4-phenoxybenzoyl)benzenes. Depending on the monomers used for polycondensation, polyketones of regular structure with different iso-/tereisomer repeating unit ratio ( 100 0 , 50 50 , 0 100 ) in the main chain were obtained. Polymers of each repeating isomer unit were prepared in two different ways. All the polymer syntheses were performed as precipitation polycondensations and the resulting polymers were obtained in particle form. The influence of reaction conditions and preparation route on the polymer properties were examined. The monomer concentration and monomer stoichiometric ratio were found to affect the polymer viscosity. The size and shape of the polyketone particles obtained were also found to be governed by reaction conditions and preparation route.
Morphology Control of Aromatic Polymers in Concert with Polymerization
Morphology control methods of aromatic polymers in concert with polymerization reaction are described in this review. Many attractive methods have been developed including reaction-induced phase separation of oligomers, epitaxial polymerization, shear-induced chain orientation during gelation, template-based polymerization, suspension polycondensation, solid-state polycondensation and liquid-liquid interfacial precipitation and so on. Among them, the reaction-induced phase separation of oligomers, in which there are two modes of crystallization and liquid-liquid phase separation, possess practically high potentiality to create novel polymer materials since it can control not only the morphology but also the molecular chain orientation. Ultimate goal is the embodiment of the nature system in a flask, that is, the control of the materials from primary structures to super structures. The morphology control methods by using polymerization reaction afford the valuable methodology for the three-dimensional structure architecture.
Effects of the mineral phase and valence of vanadium on vanadium extraction from stone coal
The influence of roasting on the leaching rate and valence of vanadium was evaluated during vanadium extraction from stone coal. Vanadium in stone coal is hard to be leached and the leaching rate is less than 10% when the raw ore is leached by 4 mol/L H2SO4 at 90°C for 2 h. After the sample is roasted at 900°C for 2 h, the leaching rate of vanadium reaches the maximum, and more than 70% of vanadium can be leached. The crystal of vanadium-bearing mica minerals decomposes and the content of V(V) increases with the rise of roasting temperature from 600 to 900°C, therefore the leaching rate of vanadium increases significantly with the decomposition of the mica minerals. Some new phases, anorthite for example, form when the roasting temperature reaches 1000°C. A part of vanadium may be enwrapped in the sintered materials and newly formed phases, which may impede the oxidation of low valent vanadium and make the leaching rate of vanadium drop dramatically. The leaching rate of vanadium is not only determined by the valence state of vanadium but also controlled by the decomposition of vanadium-bearing minerals and the existence state of vanadium to a large extent.