Studies on electrical and thermal properties of dental glass ionomer cement
A commercially available dental Glass Ionomer Cement (GIC) was studied after setting at room temperature (300 K) to understand its DC electrical conductivity, dielectric and thermal properties. The dental GIC’s are supposed to have free mobile charge carriers like F- ions. Interestingly this material loses its conductivity above 80°C and behaves like a non-polar substance. The frequency dependent dielectric studies also indicate the loss of mobile charge carriers in the samples annealed at 80°C. The DSC and TGA studies indicate that the material loses H2O exothermically at 100°C. This is attributed to the onset of a secondary setting reaction.
X-ray Diffraction Study of Acid-degradable Glasses
The composition of the degradable glasses used in commercial dental glass-ionomer cements determines their leaching behavior and hence the properties of the cement. The objective of the present study was to assess if the composition and leaching in acetic acid solutions are reflected in the x-ray diffraction characteristics of these glasses. The position (26) of the maximum of the first sharp diffraction peak shifts to higher diffraction angles with increasing number and ionic radius of mono- and bivalent cations in the glass. Upon acid-leaching, these ions are preferentially leached out, so that (26) decreases. These results can be related to the decreasing Si-Si distance in the glass network with increasing modifier radius.
Unidirectional hexagonal rare-earth disilicide nanowires on vicinal Si(100)-2×1
Rare-earth disilicide nanowires grown on vicinal Si(100) with a miscut of 2–2.5° toward the [110] azimuth at 600 °C were studied by scanning tunneling microscopy and compared with those grown on flat Si(001). In contrast to rare-earth disilicide nanowires grown on flat Si(100) surfaces, the nanowires grow unidirectionally along the [01̄1] direction of the vicinal Si(100) surface. Rare-earth disilicide nanowires form bundles composed of single nanowire units on both flat and vicinal surfaces. Yet, on the vicinal surface, the bundle width is comparable to the width of the terrace. The average nanowire length on the vicinal substrate is longer than that on the flat substrate. Scanning tunneling spectroscopy shows that the rare-earth disilicide nanowires have metallic properties.