STUDY OF STEEL TESTS OF STATIC CORROSION EXPERIMENTS IN LIQUID METAL PB-BI
We try to evaluate the possibility of maintaining the corrosion-resistance of a structural material under the operational temperature and flow velocity of the optimized HYPER (HYbrid Power Extraction Reactor)[1] cooling system. It was attempted to consider the control of the oxygen concentration in the range of 350~650°C. Currently, we are performing static corrosion tests with the oxygen contents of a reduced and 10~ 10 wt% atmospheres at the temperature of 600°C. The concentration was controlled by adjusting the H2 and H2O vapor ratio. In this paper, we will show the result of the experiment performed under the reduced atmosphere with an exposure time up to 1500 hours. The corrosion of 316L is irregularly severe under the reduced atmosphere due to the solubility of the nickel at Pb and Pb-Bi. Also small amount of iron and chromium was dissolved near the surface. On the other hand, the T91 and HT9 maintained the corrosion-resistance under the same condition.
Martensitic/ferritic steels as container materials for liquid mercury target of ESS
In the previous report, the suitability of steels as the ESS liquid mercury target container material was discussed on the basis of the existing database on conventional austenitic and martensitic/ferritic steels, especially on their representatives, solution annealed 316 stainless steel (SA 316) and Sandvik HT-9 martensitic steel (HT-9). Compared to solution annealed austenitic stainless steels, martensitic/ferritic steels have superior properties in terms of strength, thermal conductivity, thermal expansion, mercury corrosion resistance, void swelling and irradiation creep resistance. The main limitation for conventional martensitic/ferritic steels (CMFS) is embrittlement after low temperature ({le}380{degrees}C) irradiation. The ductile-brittle transition temperature (DBTT) can increase as much as 250 to 300{degrees}C and the upper-shelf energy (USE), at the same time, reduce more than 50%. This makes the application temperature range of CMFS is likely between 300{degrees}C to 500{degrees}C. For the present target design concept, the temperature at the container will be likely controlled in a temperature range between 180{degrees}C to 330{degrees}C. Hence, CMFS seem to be difficult to apply. However, solution annealed austenitic stainless steels are also difficult to apply as the maximum stress level at the container will be higher than the design stress. The solution to the problem is very likely to use advanced more » low-activation martensitic/ferritic steels (LAMS) developed by the fusion materials community though the present database on the materials is still very limited. « less
History, criminology and the ‘use’ of the past
This article considers why, despite an apparent congruence of subject matter and methodologies, the disciplines of sociological criminology and criminal justice history are not more closely aligned. It contends that intellectual traffic between the two fields is not usually limited by institutional barriers, nor is it a legacy of the disciplinary antipathy which existed between history and sociology in Britain during the mid-twentieth century. Rather, it is due to the different ‘purposes’ with which sociological criminologists and criminal justice historians imbue their work and to the differing disciplinary perceptions of the relationship between the past, present and future which result from this. These different ‘purposes’ are traced via a consideration of the paths of development of the two disciplines from the 1940s. The article concludes by proposing an arena for future collaboration between criminal justice historians and sociological criminologists.