Experimental study on recycled steel fiber concrete
Some basic properties of recycled steel fiber aggregate were tested, such as surface features, water absorption, apparent ensity, crushing index, cube compressive strength and so on. Recycled steel fiber aggregate were used to replace the natural aggregate by 0%, 25%, 50% and 100% proportion to make concrete. Afterward, compressive strength, splitting tensile strength and flexural strength were investigated at ages 3, 7 and 28 days. The results showed that thorn appearance of recycled steel fiber aggregate makes packing density decrease, crushing value and absorption increase. The compressive strength, splitting tensile strength and flexural strength of the recycled concrete depend on the mix proportions. Generally, the strength of recycled concrete can be 15–25% lower than that of concrete made with virgin aggregate.
Compressive Strength of Steel Fiber Reinforced Polymer Modified Recycled Aggregate Concrete
Demolish existing structures for better economic gains, functional and structural performance, and non-availability of land or disposal sites in nearby areas of all major cities worldwide turned as a significant reason for the crushing demolished concrete instead of using it as landfill. Research work aimed at arriving Recycled Concrete (RC) with the help of two materials, i.e. Steel Fibers (SF) and Styrene-Butadiene Rubber (SBR) latex, as additives to improve strength parameters of it. SF and SBR added in RC to examine & strengthen and termed as Steel Fiber Reinforced Polymer Modified Recycled Aggregate Concrete (SFRPMRAC). For this purpose, 198 cubes each of M20 (trial-1) and M25 (trial-2) cast separately to check compressive strength and its stress-strain behaviour for Natural Concrete (NC), RC & SFRPMRAC. The volume fractions of SF added 0.5%, 1% & 1.5% m3 of concrete and dosages of SBR latex varied from 2.5%, 5% and 7.5% by cement weight for preparation of cubes made of RC. From experimental results, SFRPMRAC with SF volume fraction of 1% m3 of concrete and 5% by cement weight provides an improvement in compressive strength by 8.62 % & 10.73 % for trial -1 and 11.51 % & 12.57 % for trial - 2 at 28 & 90 days when compared with NC. Compression stress-strain behaviour for SFRPMRAC with SF 1% m3 of concrete and 5% by weight of cement shows higher strain values at the peak stress. SFRPMRAC arrests the sudden drop of load due to co-matrix bond formation between SF and SBR in a linear direction compared to a similar NC & RC mix for both trials. It reflects significant improvement and approval of compressive strength for the desired purpose.
Mechanical behaviour and durability of high volume fly ash cementitious composites
The purpose of this research is to separate different morphological particles of ASTM class F fly ash, and study their effect on mechanical behaviour and durability of high volume cementitious mixtures. In this research wet separation of raw fly ash is carried out, which resulted in three layers of different morphological particles. The first layer of particles float, comprise of about 1-5% of fly ash, is identified as cenospheres or hollow spheres. The second layer of particles is measured to be 55-60% of raw fly ash and consisting of porous spherical and rounded particles rich in Si and Al. The third layer particles is measured to be about 35-40% of raw fly ash. High volume fly ash cementitious composites containing second or third layer particles are tested under compression and bending, highlighting a higher strength and ductility in comparison to cementitious ones containing raw fly ash particles. KEYWORDS. Cementitious matrix; Raw fly ash; Second layer particles; Third layer particles.