ELABORATION AND TESTING OF MATERIALS USING CONCENTRATED SOLAR ENERGY
1. Brief history of the use of solar energy to transform matter 2. Main characteristics of solar furnaces 3. Elaboration of materials using concentrated solar energy 3.1 Surface treatments 3.2 Melting and purification of bulk materials 3.3 Production of chemical commodities and ceramics 3.4 Elaboration of carbon molecules, nanomaterials and thin films 4. Testing of materials using concentrated solar energy 4.1 Original devices at the focus of solar furnaces 4.2 Test of materials for aerospace applications 4.2.1 Atmopsheric re-entry (oxidation and catalycity) 4.2.2 Solar probe mission 4.3 Test of materials for future system of energy production 5. Conclusion Bibliography Biographical Sketches
Evaluation of Heat-Treated AISI 316 Stainless Steel in Solar Furnaces to Be Used as Possible Implant Material
The appropriate selection of implant materials is very important for the long-term success of the implants. A modified composition of AISI 316 stainless steel was treated using solar energy in a vertical axis solar furnace and it was subjected to a hyper-hardening treatment at a 1050 °C austenitizing temperature with a rapid cooling in cold water followed by three variants of tempering (150, 250, and 350 °C). After the heat treatment, the samples were analyzed in terms of hardness, microstructure (performed by scanning electron microscopy), and corrosion resistance. The electrochemical measurements were performed by potentiodynamic and electrochemical impedance spectroscopy in liquids that simulate biological fluids (NaCl 0.9% and Ringer’s solution). Different corrosion behaviors according to the heat treatment type have been observed and a passivation layer has formed on some of the heat-treated samples. The samples, heat-treated by immersion quenching, exhibit a significantly improved pitting corrosion resistance. The subsequent heat treatments, like tempering at 350 °C after quenching, also promote low corrosion rates. The heat treatments performed using solar energy applied on stainless steel can lead to good corrosion behavior and can be recommended as unconventional thermal processing of biocompatible materials.
Failure analysis for poor solderability of Au surface of PCB
Nonwetting is one of the common problems and is always rejected in electronic assemblies. ENIG pads of a PCBA exhibited nonwetting after lead-free reflow soldering. With the aid of stereomicroscope, SEM&EDS and XRF, a series of analysis was performed. And after visual inspection, surface and cross section analysis, thickness measurement and solderability test, it can be inferred that oxidation of plating surface was the main reason for nonwetting, and corrosion in Ni plating caused an adverse impact on solderalibity.