CHARACTERIZATION OF LOW TEMPERATURE CREEP PROPERTIES OF CRACK SEALANTS USING BENDING BEAM REHOMETRY Prepared
Crack sealing has been widely used as a routine preventative maintenance practice. Given its proper installation, crack sealants can extend pavement service life by three to five years. However, current specifications for the selection of crack sealants correlate poorly with field performance. The purpose of this research was to develop performance guidelines for the selection of hot-poured bituminous crack sealants at low temperature. In this part of the research, the creep behavior of crack sealant at low temperature is measured and performance criteria for material selection were developed. Because various pavement and State agencies are well acquainted with and own the Bending Beam Rheometer (BBR), which was developed during the Strategic Highway Research Program (SHRP), an attempt was made to utilize the same setup to test hot-poured bituminous-based crack sealants. Testing conducted in this research project indicated that the standard BBR was inappropriate for testing soft bituminous-based hot-poured crack sealant, even at-40°C. The measured deflection exceeded the BBR limit, for some sealants, after only a few seconds of loading. To address this issue, the moment of inertia of the tested beam was increased by doubling its thickness (from 6.35mm to 12.7mm). For the new beam dimensions, it was found that only 4% of the beam center deflection is due to shear, a value deemed acceptable for sealant evaluation and comparison. In an effort towards developing a robust testing procedure, 15 sealants from various manufacturers were included in the study and tested between –4°C and –40°C. In addition, five sealants, which have known field performance, were tested to validate the laboratory results and establish specification thresholds for the selection guidelines. Since stiffness calculation in the BBR test method requires that measurements be made within the linear region of viscoelastic behavior, validation of this theory was conducted for crack sealants. This was found to be generally the case with crack sealants, which allowed for the use of the time-temperature superposition. If the temperature-superposition principle is applied, the stiffness at 240s at a given temperature can be used to predict the stiffness after 5hr of loading at a temperature that is 6°C lower. With the assumption of linear viscoelastic behavior, sealants performance can be characterized through stiffness, average creep rate, and dissipated energy ratio. Stiffness was found to be sensitive to temperature changes and could be used to differentiate between sealants. The measurements of the average creep rate and the dissipated energy ratio …
STATE-OF-THE-ART SURVEY OF FLEXIBLE PAVEMENT CRACK SEALING PROCEDURES IN THE UNITED STATES
Abstract : A survey of all 50 United States was conducted in September of 1990 to determine the state of the art of crack sealing procedures on flexible asphalt concrete pavements. The results were tabulated and a summary report prepared. A meeting was held at the U.S. Army Cold Regions Research and Engineering Laboratory to discuss the draft report; the comments and suggestions received were incorporated into this report. At the meeting the group identified the need for a trade organization to develop uniform specifications and terminology and to promote proper equipment, methodology, materials, training and education in the pavement crack sealing industry. Crack sealing, Pavement routing, National survey.
Formation and Strength of Magnesia Whiskers
The formation of single-crystal magnesia whiskers during the compressive deformation of single crystals at room temperatures is described. These whiskers can have strengths of the order of millions of pounds per square inch. They are formed during fracture as a result of the discontinuous propagation of cracks which are mechanically relieving internal stresses resulting from plastic flow