Effect of relative humidity on the migration of benzophenone from paperboard into the food simulant Tenax® and modelling hereof
The aim of this study was to investigate the effect of relative humidity on the migration of benzophenone from paperboard into the food simulant Tenax®. Kinetic migration investigations were carried out with three relative humidities in the interval between 39% and >73%. All investigations were carried out at a constant temperature of 34°C. It was found that the migration of benzophenone after more than 30 days was 4.8 times higher at a relative humidity of 64%–71%, and 7.3 times higher at a relative humidity of >73%, compared with that at a relative humidity of 39%–49%. Diffusion and partition coefficients were derived from the results by using a software for modelling migration in multilayer materials. Both the diffusion coefficient and the partition coefficient, between paperboard and Tenax®, decrease with increasing relative humidity. The experimental results were correctly modelled only when the paperboard was regarded as a one-layer system as compared with a two-layer system: where the main part of the paperboard (B1) has a high diffusion rate and a thin part of the paperboard (B2) in contact with the foodstuff has a lower diffusion rate.
Model studies of migration from paper and board into fruit and vegetables and into Tenax™ as a food simulant
Four samples of paper and board (P/B) of a type used for packaging dry foods were subjected to migration tests using mushrooms, apples, potatoes and bananas, and using the polymeric powder Tenax™ as a food simulant. The P/B samples contained only low levels of diisopropylnaphthalene (DiPN) and diisobutyl phthalate (DiBP) and so the experiments were conducted after impregnating the P/B with added model substances. These were o-xylene, acetophenone, dodecane, benzophenone, DiPN and DiBP. Migration levels depended strongly on the nature of the substance and on the nature of the food and much less on the characteristics of the P/B, except insofar as they affected the contact area – flexible papers giving more extensive contact with the food than thick rigid board. Migration into Tenax™ was at least a factor of 10 higher than migration into the fresh fruit and vegetables. The food samples were placed in contact with the P/B and then overwrapped loosely with aluminium foil and so this correction factor will tend to be conservative compared with a more open storage of the packed foods. Washing, peeling or cooking the fruits and vegetables after contact with the P/B had a surprisingly small effect on contaminant levels in general, and no one processing step was effective in giving a significant reduction of all the types of chemicals studied. This was because either they had penetrated into the food (so resisting peeling), or were not freely water-soluble (so resisting washing) or were not particularly volatile (so resisting loss by evaporation during cooking).
Formation and Strength of Magnesia Whiskers
The formation of single-crystal magnesia whiskers during the compressive deformation of single crystals at room temperatures is described. These whiskers can have strengths of the order of millions of pounds per square inch. They are formed during fracture as a result of the discontinuous propagation of cracks which are mechanically relieving internal stresses resulting from plastic flow