Fatigue Behavior of a Box-Type Welded Structure of Hydraulic Support Used in Coal Mine
Hydraulic support is the main supporting equipment of the coal mining systems, and they are usually subjected to fatigue failure under the high dynamic load. The fracture positions are generally at welded joints where there is a serious stress concentration. In order to investigate and further improve the fatigue strength of hydraulic support, the present work first located the possible position where fatigue failure occurs through finite element analysis, and then fatigue tests were carried out on the different forms of welded joints for the dangerous parts. Finally, Fatigue strength-life (S-N) curves and fracture mechanism were studied. This research will provide a theoretical reference for the fatigue design of welded structures for hydraulic support.
Weld Detail Fatigue Life Improvement Techniques
Abstract : Fatigue cracks in steel ships often occur at welded joints where stress concentrations due to the joint geometry are relatively high and the fatigue strength of the weld is reduced in comparison to that of the base metal. This becomes more critical in ships built of High Strength Steels (HSS) because the fatigue strength of steel in the a welded condition does not increase in proportion to the yield or tensile strength. In many cases, the fatigue performance of severely loaded details can be improved by employing good detail design practices, for example by upgrading the welded detail class to one having a higher fatigue strength. In some cases, however, there may be no better alternatives to the detail in question and modification of the detail may not be practicable. As an alternative to strengthening the structure at a considerable increase in costs, procedures which reduce the severity of the stress concentration at the weld, remove imperfections, and/or introduce local compressive stresses at the weld can be used for improvement of the fatigue life. Similarly, these fatigue improvement techniques can be applied as remedial measures to extend the fatigue life of critical welds that have failed prematurely and have been repaired. To date, weld fatigue life improvement techniques have been successfully applied in several industries. While there has been increasing interest in the application of fatigue life improvement techniques to ship structures, at present there is a lack of guidance on the use of such techniques for design, construction and repair. Hence the key elements of this project were to compile available data on fatigue life improvement techniques, assess the feasibility and practicality for their application to ship details, identify gaps in the technology, and finally to recommend design, construction and repair requirements.
SR topography of plastically deformed Fe-Si bicrystals - observation in situ and post mortem
SR reflection topography was applied to study the interaction of slip dislocations with the grain boundaries in Fe-4at%Si bicrystals deformed by compression. Three experimental settings with either a white or monochromatic beam were used and the corresponding orientation contrast analysed. Dislocation transmission through the grain boundary was observed in bicrystals with favourable geometry of the slip systems.