The effect of various silver tin oxide materials on contact performance under motor load (a.c.)
The new contact material AgSnO/sub 2/ which is replacing AgCdO in many applications, requires the addition of additives to improve electrical contact performance. These additives such as copper oxide (Cu/sub 2/O) and bismuth oxide (Bi/sub 2/O/sub 3/), can significantly affect contact performance. An investigation was undertaken to compare the changes in contact performance between silver cadmium oxide (internally oxidized) and three silver tin oxide based materials containing (1) no additive, (2) copper additive and (3) bismuth plus copper additives. Performance changes and physical characteristics of each material such as formability (tensile properties), contact resistance and contact material erosion (arc erosion) were evaluated. The silver tin oxide based materials containing copper additive exhibited significantly higher resistance to arc erosion than silver cadmium oxide based material and other silver tin oxide materials evaluated. The resistance to welding and changes in electrical resistance were dependent on the chemistry of each material. The results suggested that the chemistry of the material was the chief reason silver tin oxide based material with copper additive performed better than silver cadmium oxide based material under identical motor load.
Optimization of silver tin oxide chemistry to enhance electrical performance in a.c. application
The addition of copper oxide (0.37-0.53%) to silver tin oxide based material substantially improved the electrical performance in a.c. application. The erosion behavior of the material was directly related to the level of copper oxide in the silver tin oxide based materials. The investigation was undertaken to correlate the changes in contact performance as the copper oxide additive varied. Performance changes and physical characteristics of each material, such as formability (tensile properties), contact resistance and contact material erosion (arc erosion) were evaluated. The resistance to arc erosion of silver tin oxide based material containing 0.37-0.53% copper oxide by weight was superior in comparison to other silver tin oxide based materials containing 0.025%, 0.065% and 0.96% of copper oxide. In addition changes in electrical resistance were not dependent on the chemistry of each material. The results suggested copper oxide addition of 0.37-0.53% by weight was the chief reason silver tin oxide based materials out-performed other doped silver tin oxide based material under the same test conditions.
Effect of Calcium Glycerophosphate on Demineralization in an in vitro Biofilm Model
The aim was to investigate the anti-caries properties of calcium glycerophosphate (CaGP) using an in vitro bacterial flow cell model. Four flow cells, inoculated from a chemostat containing a seven-organism bacterial consortium, were pulsed with sucrose twice daily, to provide an acidic challenge and pH-cycling conditions. Blocks of enamel and dentine were mounted in each flow cell. In a study on the effect of CaGP concentration, CaGP was pulsed into three of the flow cells, at the same time as the sucrose, to give concentrations of 0.10, 0.25 and 0.50%. Water was pulsed into the fourth flow cell with the sucrose. Microradiography revealed a significant dose response of decreasing demineralization as CaGP concentration increased. Reductions at 0.25 and 0.5% were significant when compared to the control. A second study investigated the effect of timing of CaGP pulsing, relative to sucrose, on enamel and dentine demineralization. CaGP (flow cell concentration 0.2%), was pulsed 1 h before, during or 1 h after the sucrose pulse; a water control was employed. In enamel, pulsing CaGP before the sucrose reduced demineralization significantly compared to concurrent pulsing, which in turn gave a significant reduction compared to pulsing after sucrose, which did not reduce demineralization significantly compared to the water control. In dentine, CaGP reduced demineralization significantly only when pulsed before the sucrose. The findings suggest that in vivo, the anti-caries potential of CaGP may be greater if it is applied before a cariogenic challenge.