Etch rates for Si-face 4H-SiC using H2 and a C3H8 partial pressure
In an effort to calibrate nitrogen incorporation into the growing layer, a nitrogen step-doped sample was grown. In an attempt to reduce or eliminate incidental etching during pre- and post- growth temperature ramps, additional samples were etched under different propane partial pressures. With increasing propane partial pressure the etch rate decreases.
Effect of Additional Silane on In Situ H2 Etching prior to 4H-SiC Homoepitaxial Growth
We have investigated the influence of in-situ H2 etching on the surface morphology of the 4H-SiC substrate prior to homoepitaxial growth. In this study, we varied the types of gas atmosphere during in-situ H2 etching; namely, hydrogen (H2) alone, hydrogen-propane (H2+C3H8), and hydrogen-silane (H2+SiH4). We found that in-situ H2 etching using H2 + SiH4 significantly improved the surface morphology of 4H-SiC substrate just after in-situ H2 etching. By adding SiH4, formation of bunched step structure during in-situ H2 etching could be significantly suppressed. In addition, H2 etching using H2 + SiH4 was able to remove scratches by etching a thinner layer than that using H2 alone. We also discussed the in-situ H2 etching mechanism under the additional SiH4 condition.
In situ substrate preparation for high-quality SiC chemical vapour deposition
Abstract In situ preparation of 4H and 6H silicon carbide substrate surfaces in hydrogen and hydrogen-propane etching systems has been studied. The etching of on-axis(0001) 6H-SiC substrates resulted in regular straight terraces and one unit high steps. The etching of on-axis (0001) 4H-SiC substrates resulted in broad terraces interrupted by large step formations. The 4H- and 6H-SiC (0001) off-axis substrates (3.5° towards 〈112¯0〉 yield smooth etched surfaces with the exception of stripe-like defects on the 4H polytype which are shown to be related to stacking-faults. The stacking faults are suggested to be a cause for step-bunching and surface roughening. Hydrogen-etching prior to growth has been shown to improve the epitaxial layer quality both concerning defect formation and step-bunching.