Magnetic phase transition and Mossbauer spectroscopy of ErNi2Mnx compounds
Investigation of ErNi2Mnx with 0.90 ≤ x ≤ 1.10 indicates that the MgCu2-type structure (with space group Fd-3m) is formed within x = 0.97−1.10. Curie temperature TC = 50 K of ErNi2Mn is significantly higher than those of the corresponding ErNi2 (TC = 7 K) and ErMn2 (TC = 15 K) compounds. Detailed analyses of DC magnetization data demonstrate that the magnetic phase transition at the Curie temperature is second order. The magnetic entropy change around TC has been found to be 4.8 J/kg K for a magnetic field change of 0 to 5 T with its relative cooling power ∼283 J/kg. 57Fe Mossbauer spectra below TC have been fitted with three sub-spectra representing three inequivalent local magnetic environments while the paramagnetic spectra are fitted using two sub-spectra for two inequivalent crystal sites (8a and 16d), which supports the conclusion based on Rietveld refinement that Mn atoms occupy at both 8a and 16d sites.
Effect of Mn substitution on the volume and magnetic properties of Er2Fe17
The effects of Mn substitution on the magnetic properties of Er2Fe17−xMnx compounds have been investigated by different experimental techniques. An unusual composition dependence of the unit cell volume at room temperature occurs due to a strong magnetovolume effect, which has been confirmed by high temperature linear thermal expansion measurements. From magnetization measurements the composition dependence of the spontaneous magnetization of the 3d-sublattice magnetic moment and of the Curie temperature has been determined. Spin reorientation has been detected for compounds with 3⩽x⩽5.5, as well as remarkable magnetic history effects.
Strategies for glass based photonic system integration
There is a clear tendency to integrate more and more opto-electronic and micro-optical components like optical fibers, laser diodes, modulators, isolators, beam-splitting components and micro lenses in also increasingly dense and complex assemblies. The paper will discuss thin glass as a very promising base material for that kind of photonic packaging on interposer and board level including optical interconnection using fibers.