The structure of ultrathin Langmuir-Blodgett films of cadmium behenate.
Grazing incidence x-ray-diffraction investigations of the structures of Langmuir-Blodgett films of cadmium behenate with 1, 2, 3, 5, and 21 monolayers are reported. The single monolayer film, deposited on a hydrophilic substrate, showed a hexagonal structure, whereas the bilayer film, deposited on a hydrophobic substrate, had a rectangular structure with herringbone orientation of the acyl chains. With multilayer films formed on a hydrophilic substrate, it was possible to detect that the hexagonal structure of the first layer was retained when additional layers were deposited and that the additional layers had the same rectangular structure as the bilayer.
Structure and Elastic Properties of 10−12 Pentacosadiyonic Acid Langmuir Films
Monolayers of the polymerizable 10−12 pentacosadiyonic acid amphiphile spread on a basic buffer are studied both before and after polymerization. We have established the phase diagram of the unpolymerized Langmuir film by isotherm measurements, Brewster angle microscopy, and grazing incidence X-ray diffraction experiments. Diffuse scattering experiments performed at the European Synchrotron Radiation Facility allowed us to investigate the structure and elastic properties of the different monomer phases and the modifications induced by polymerization.
Finite Difference Modeling on the Temperature Field of Substrate in Friction Surfacing
Friction surfacing is an advanced process of great potential, especially in the field of repair and reclamation of worn and damaged components. As a kind of thermal processing technology, the temperature profile and changes of the substrate in friction surfacing are important factors to get coatings of high quality. In this paper, the temperature field of the substrate during the process is simulated by finite difference method. The results are consistent with experiments, reappearing the temperature change of the substrate during friction surfacing, allowing further study on figuration and quality of coatings.