EBSD study of angular deviations from the Goss component in grain-oriented electrical steels.
The magnetic properties of grain-oriented (GO) electrical steels strongly depend on the distribution of the α and β angles, i.e., the deviations of the easy magnetisation <100> from the rolling direction (RD) in the rolling plane and out of the rolling plane, respectively. However, most Electron Backscatter Diffraction (EBSD) studies consider the standard Goss deviation angle, which includes the rotation of the (110) plane about the RD. Therefore, in the present work, a new procedure is demonstrated for deriving the α and β angles from EBSD mappings to obtain a quantitative texture characterisation in line with the magnetic properties. This procedure is later applied to 37 GO steels after secondary recrystallisation that exhibit a wide range of permeability levels. The relation between the texture and the polarisation at 800A/m (J800) that is measured in the present study by EBSD is compared to the one that has been determined in previous papers with optical goniometers and X-ray diffraction techniques, and this relation is subsequently used to define a relevant parameter to describe the orientation quality of the grains. The results indicate that the average angle of the α and β deviations is a relevant deviation parameter for the characterisation of grain orientations. Finally, it is demonstrated that the combination of the quantitative correlation between polarisation and texture with the orientation imaging of EBSD offers the possibilities of both studying the crystallographic environment of highly oriented grains in the primary recrystallised matrix for the production of high-permeability steels and evaluating the spatial distribution of the angular deviations in GO steels after secondary recrystallisation.
Magnetic domain structure and crystallographic orientation of electrical steels revealed by a forescatter detector and electron backscatter diffraction.
The magnetic properties of non-oriented electrical steels (NOES) are an important factor in determining the efficiency of electric vehicle drivetrains. Due to the highly variable texture of NOES, the relationships between crystal orientation, the magnetic domain structure, and the final magnetic properties are complicated and not fully understood. In this study, a NOES sample was characterized with a method capable of imaging surface magnetic domains using scanning electron microscopy (SEM) with an electron backscatter diffraction (EBSD) system equipped with a forescatter detector. This method used type II magnetic contrast without a specialized SEM setup, and imaged with a resolution limit of approximately 250-300nm. The domain structure of the NOES sample was successfully related to β, which was defined as the angle between the closest magnetic easy axis and the surface of the sample (the RD-TD plane). However, it was shown that if the easy axes were aligned between neighbouring grains with respect to the grain boundary normal, the domain structure could align with an easy axis that was not the closest to the surface, and complex domain structures could be become wider. This structure and width change of complex domain structures has not been previously observed from single crystal or large-grained material studies. The successful application of this method to reveal the influence of surrounding grains can be used to better understand the magnetic properties of NOES.
Gender Politics and Research: Male and Female Violence in Intimate Relationships
This article reviews a wide range of research reports on male and female violence in intimate relationships and highlights the political nature of domestic violence research. The authors review incidence and prevalence-based research that uses quantitative surveys and illustrate how quantitative, family-focussed researchers tend to ignore the political and social context of domestic violence and the complex issues of gender and power. The authors argue that understanding the complexities of domestic violence requires clear definitions of what constitutes domestic violence and multi-method approaches to research, using a combination of quantitative and qualitative methodologies.