Permeation characteristics of electrolytes and neutral solutes through titania nanofiltration membranes at high temperatures.
Nanoporous titania membranes with controlled pore sizes ranging from 0.7 to 2.5 nm, which had molecular weight cutoffs (MWCO) ranging from 500 to 2000, were successfully prepared by sol-gel processing, and the transport characteristics were evaluated across a temperature range of 30-80 degrees C. With increasing temperature, the permeate flux increased 2- to 3-fold, depending on the pore size. The water permeation mechanism was found to be different from viscous flow and was explained by the state of the water (free water/bound water/nonfreezing water) inside confined pores. The rejection of neutral solutes such as raffinose, the separation mechanism of which is molecular sieving (steric hindrance), decreased with temperature whereas that of electrolytes (MgCl(2) and NaCl), the separation mechanism of which is the charge effect (Donnan exclusion), was approximately constant. The temperature dependence of neutral and electrolyte solutes was analyzed using the Spiegler-Kedem equation by combining the Arrhenius equations for diffusivity and viscosity, which we obtained DeltaE(m), the activation energy of diffusion, after eliminating the effect of viscosity. For large DeltaE(m), which corresponds to the rejection of neutral solutes on the basis of molecular sieving, rejection decreased with temperature but remained unchanged for small DeltaE(m), which corresponds to the rejection of electrolytes based on the charge effect.
Development of robust organosilica membranes for reverse osmosis.
Hybrid organically bridged silica membranes have attracted considerable attention because of their high performances in a variety of applications. Development of robust reverse osmosis (RO) membranes to withstand aggressive operating conditions is still a major challenge. Here, a new type of microporous organosilica membrane has been developed and applied in reverse osmosis. Sol-gel derived organosilica RO membranes reject isopropanol with rejection higher than 95%, demonstrating superior molecular sieving ability for neutral solutes of low molecular weight. Due to the introduction of an inherently stable hybrid network structure, the membrane withstands higher temperatures in comparison with commercial polyamide RO membranes, and is resistant to water to at least 90 °C with no obvious changes in filtration performance. Furthermore, both an accelerated chlorine-resistance test and Fourier transform infrared analysis confirm excellent chlorine stability in this material, which demonstrates promise for a new generation of chlorine-resistant RO membrane materials.
Magnetic properties of Lu2Fe17 crystals
Abstract We present the results of crystal structure and magnetization studies of three single crystals grown from melts of different nominal compositions in the vicinity of the Lu2Fe17 stoichiometry. The ferromagnetic state of the crystals is strongly dependent on the real sample composition and the local atomic ordering. A drastic difference is observed in the behaviour of the ferro–antiferromagnetic transition, even in crystals for which almost identical composition and crystal parameters were determined by microprobe and X-ray analysis.