Assessment of Durability of Reactive Powder Concrete Using Oxygen Permeability Index
-Durability of concrete is very important parameter for using natural resources effectively and reducing the cost of reconstruction, maintenance and repair of structure. This paper focuses on need of much of the need for concrete repair can be eliminated, if sufficient consideration and attention is given to control of surface quality of concrete at the construction stage. A South African approach is used to measure the oxygen permeability index testing and concluded that the method is applicable to actual project and is durability index is a parameter to evaluate the durability of RPC and cover zone concrete. RPC shows a good OPI value indicating impermeable concrete and its use can be justified for special purpose.
The South African durability index tests in an international comparison
Over the last decade, an approach to improving the durability of reinforced concrete construction has been developed in South Africa. The durability index test methods applied in this approach are unique to the country. Internationally, similar trends can be observed and a number of test methods for the quality assessment of hardened concrete, particular the cover zone have been developed world-wide. A group of researchers from different parts of the world carried out comparative tests on the quality of concrete cover, applying the most commonly accepted international test methods. The results indicate that the South African oxygen permeability and chloride conductivity test methods are successful in characterising the concrete cover in respect of important deterioration mechanisms. A good correlation exists between results obtained from these index test methods and those obtained from related test procedures applied overseas.
Curing and the durability of OPC, fly ash and blast-furnace slag concretes
This paper presents preliminary results of a research project into the influence of moist curing on the potential durability of concrete. Durability is characterized by measuring the oxygen permeability and water absorption at various depths in the covercrete. Concretes containing plain OPC, an OPC-FA blend and an OPC-GGBS blend were used. A range of strength grades was tested for each of these binder types. Concretes were exposed to moist curing conditions for 1, 3, 7 and 28 days before being tested at 28 days after casting. The main conclusions are: (i) moist curing has a marked influence on the potential durability of concrete and (ii) a relatively greater influence on durability can be effected by extending the duration of early-age moist curing rather than decreasing the binder/water ratio.ResumeOn présente les résultats préliminaires d'un projet de recherche sur l'influence de la conservation en condition humide sur la durabilité potentielle du béton, qui se caractérise par la mesure de la perméabilité à l'oxygène et l'absorption d'eau à différentes profondeurs dans l'épaisseur d'enrobage du béton. On décrit aussi la mise au point d'un perméamètre économique à chute de pression contrôlée qu'on a utilisé pour mesurer la perméabilité à l'oxygène dans le béton.On a utilisé pour les séries d'essai des bétons contenant du ciment Portland ordinaire (OPC), un mélange OPC-cendres volantes et OPC-laitier; chacun a été essayé sur un éventail de degrés de résistance. Les bétons ont été exposés à la conservation en condition humide pendant 1, 3, 7 et 28 jours avant d'être essayés à 28 jours après moulage.On a ensuite découpé des disques de béton sur les éprouvettes cubiques, parallèlement à une face de moulage, correspondant à des profondeurs de 0–15, 15–30 et 30–45 mm. On a essayé la perméabilité à l'oxygène et la capacité de sorption d'eau de ces disques, qui marquent le développement de la microstructure de la phase du ciment, et par conséquent la durabilité.En conclusion, (i) la conservation en condition humide a une influence certaine sur la durabilité potentielle; (ii) cette influence peut être relativement accrue plutôt en allongeant la durée de conservation en condition humide aux jeunes âges qu'en diminuant le rapport eau/liant; (iii) sur les trois types de liants essayés, les résultats les plus faibles de perméabilité à l'oxygène et de capacité de sorption d'eau ont été obtenus avec les bétons OPC-cendres volantes et les valeurs les plus élevées avec les bétons OPC-laitier.