Cyclic Oxidation Testing and Modelling: A NASA Lewis Perspective
The Materials Division of the NASA Lewis Research Center has been heavily involved in the cyclic oxidation of high temperature materials for 30 years. Cyclic furnace and burner rig apparati have been developed, refined, and replicated to provide a large scale facility capable of evaluating many materials by a standard technique. Material behavior is characterized by weight change data obtained throughout the test, which has been modelled in a step-wise process of scale growth and spallation. This model and a coupled diffusion model have successfully described cyclic behavior for a number of systems and have provided insights regarding life prediction and variations in the spalling process. Performance ranking and mechanistic studies are discussed primarily for superalloys and coating alloys. Similar cyclic oxidation studies have been performed on steels, intermetallic compounds, thermal barrier coatings, ceramics, and ceramic composites. The most common oxidation test was performed in air at temperatures ranging from 800 deg. to 1600 C, for times up to 10000 h, and for cycle durations of 0.1 to 1000 h. Less controlled, but important, test parameters are the cooling temperature and humidity level. Heating and cooling rates are not likely to affect scale spallation. Broad experience has usually allowed for considerable focus and simplification of these test parameters, while still revealing the principal aspects of material behavior and performance. Extensive testing has been performed to statistically model the compositional effects of experimental alloys and to construct a comprehensive database of complex commercial alloys.
High Temperature cyclic Oxidation Furnace Testing at NASA Lewis Research Center
A standardized method of testing the cyclic oxidation resistance of various alloys in static air up to 1200°C has been developed and routinely used at the National Aeronautics and Space Administration (NASA) Lewis Research Center. Test specimens are automatically raised and lowered into a resistance wound furnace for a series of fixed-interval heating and cooling cycles. Spall catchers collect the accumulated spall from each specimen. The specimens are weighed intermittently to generate specific weight change with time data. At various test times the specimens and the accumulated spall are analyzed by X-ray diffraction. A computer program is used to print out the specific weight change versus time data and the X-ray data in tabular form and to plot the specific weight change versus time data in a publishable format. The data are also organized and indexed. So far several hundred iron-, nickel-, and cobalt-base alloys have been tested using this basic procedure and will form the basis of a series of cyclic oxidation handbooks to be published by NASA. Such specific weight change/time data have been used to estimate the oxidative metal consumption by several computer modeling techniques both to rank alloys and to estimate life.
Isothermal and cyclic oxidation at 1000 and 1100 deg C of four nickel-base alloys: NASA-TRW VIA, B-1900, 713C, and 738X
The isothermal and cyclic oxidation resistance of four cast Ni-base gamma + gamma prime alloys, NASA-TRW Via, B-1900, 713C, and 738X, was determined in still air at 1000 and 1100 C. The oxidation process was evaluated by specific sample weight change with time, sample thickness change, X-ray diffraction of the scales, and sample metallography. The behavior is discussed in terms of the Cr, Al, and refractory metal contents of the alloys.