Explosibility of Polyamide and Polyester Fibers
The current research is aimed at investigating the explosion behavior of hazardous materials in relation to aspects of particulate size. The materials of study are flocculent (fibrous) polyamide 6.6 (nylon) and polyester (polyethylene terephthalate). These materials may be termed nontraditional dusts due to their cylindrical shape which necessitates consideration of both particle diameter and length. The experimental work undertaken is divided into two main parts. The first deals with the determination of deflagration parameters for polyamide 6.6 (dtex 3.3) for different lengths: 0.3 mm, 0.5 mm, 0.75 mm, 0.9 mm and 1 mm; the second involves a study of the deflagration behavior of polyester and polyamide 6.6 samples, each having a length of 0.5 mm and two different values of dtex, namely 1.7 and 3.3. (Dtex or decitex is a unit of measure for the linear density of fibers. It is equivalent to the mass in grams per 10,000 m of a single filament, and can be converted to a particle diameter.) The explosibility parameters investigated for both flocculent materials include maximum explosion pressure (Pmax), size-normalized maximum rate of pressure rise (KSt), minimum explosible concentration (MEC), minimum ignition energy (MIE) and minimum ignition temperature (MIT). ASTM protocols were followed using standard dust explosibility test equipment (Siwek 20-L explosion chamber, MIKE 3 apparatus and BAM oven). Both qualitative and quantitative analyses were undertaken as indicated by the following examples. Qualitative observation of the post-explosion residue for polyamide 6.6 indicated a complex interwoven structure, whereas the polyester residue showed a shiny, melt-type appearance. Quantitatively, the highest values of Pmax and KSt were obtained at the shortest length and finest dtex for a given material. For a given length, polyester displayed a greater difference in Pmax and KSt at different values of dtex than polyamide 6.6. Long ignition delay times were observed in the BAM oven (MIT measurements) for polyester, and video framing of explosions in the MIKE 3 apparatus (MIE measurements) enabled observation of secondary ignitions caused by flame propagation after the initial ignition occurring at the spark electrodes.
Review of the explosibility of nontraditional dusts
This paper explores the explosion characteristics of three nontraditional dusts: nanomaterials, flocculent materials, and hybrid mixtures. Nanomaterials have a high likelihood of explosion with minimum ignition energies potentially less than 1 mJ. These low ignition energies may therefore allow nanomaterials to ignite due to electrostatic sparks, collision, or mechanical friction. The severity of nanomaterial explosions is affected by agglomeration and coagulation of the particles. Flocculent materials with a high length-to-diameter ratio exhibit explosion behavior patterns similar to those for spherical dusts. The length of flocculent particles plays a role in explosion likelihood which is not yet fully understood. High voltage discharge during the electrostatic flocking process is a common flocculent ignition hazard. Hybrid mixtures of a combustible dust and a flammable gas/vapor display a higher explosion severity and a lower minimum explosible concentration than that of the dust alone. Violent hybrid ...
Evolution of carbide precipitates in Hastelloy N joints during welding and post weld heat treatment
Abstract The effects of welding and post weld heat treatment (PWHT) on the morphology, composition and lattice parameter of the precipitates in the welding joints of Hastelloy N alloy have been investigated. Joint samples were prepared using a gas tungsten arc welding process with ERNiMo-2 fillers, and then solid-solution treated at 1100 °C for 20 min. After welding, eutectic M6C carbides can be observed in the heat affected zones (HAZ) and weld zones (WZ). These eutectic M6C carbides become spheroidized during the following PWHT. The concentration of Si decreases during the transformation from the primary ones to eutectic ones, and then increases during the spheroidizing process. The total concentration of Si + Cr in M6C carbides remains stable during welding and PWHT. At the same time, the heat leads to the outward diffusion of Mo from the M6C carbides, which results in a decrease of the lattice parameter.