Oxidation or Nitridation Behavior of Pure Chromium and Chromium Alloys Containing 10 mass%Ni or Fe in Atmospheric Heating
The oxidation or nitridation behavior of pure chromium and chromium alloys containing 10 mass%Ni or 10 mass%Fe in atmospheric heating was investigated in the temperature range of 1073 to 1373 K. The formation behavior of the outer oxide phase of Cr2O3 and its growth kinetics in both chromium alloys was very similar to that of pure chromium. The nitride layer with the Cr2N phase was formed beneath the oxide phase at temperatures above 1273 K in pure chromium. Marked internal nitridation with the formation of the Cr2N phase was observed in the Cr-10 mass%Fe alloy, while the formation of Cr2N was negligible in the Cr-10 mass%Ni alloy. Neither Ni nor Fe were detected inside the Cr2O3 phase, and was enriched in the subsurface layer between the oxide layer and the base alloy in a respective alloy. The Ni-enriched layer in Cr-10 mass%Ni alloy had a relatively narrow width, but a very high concentration of Ni compared with the Fe-enriched layer formed in the Cr-10 mass%Fe alloy. [doi:10.2320/matertrans.47.2540]
High-temperature nitridation of Ni-Cr alloys
The nitriding behavior of nickel-chromium alloys was investigated at 1398 K over the range 1 to 6000 bar of external nitrogen pressure. The morphology of the nitrided zone depends on the concentration of chromium in the initial alloy and the N2 pressure (fugacity) applied upon the system. The transition from CrN to Cr2N precipitation was observed within the reaction zone after nitriding at 100 to 6000 bar of N2 when the chromium content in the initial alloys was 28.0 at. pct or higher. It is shown that the ternary phase π (Cr10Ni7N3) is formed in this system at 1273 K. through a peritectoid reaction between Cr2N and nickel solid solution and becomes unstable above 1373 K. The thermodynamic evaluation of the Ni-Cr-N system was performed and phase equilibria calculated. Evidence for “up hill” diffusion of nitrogen near the reaction front during the internal nitridation of Ni-Cr alloys at 1398 K was found. It was attributed to the relative instability of chromium nitrides and strong Cr-N interaction in the matrix of the Ni-based solid solution within the nitrided zone.
The properties of a chromium-titanium-nitrogen alloy
Abstract An account is given of the formation and influence of a titanium nitride dispersion on the mechanical properties and recovery of chromium.