Evaluation of Stability of Amylose Inclusion Complexes Depending on Guest Polymers and Their Application to Supramolecular Polymeric Materials
This paper describes the evaluation of the stability of amylose–polymer inclusion complexes under solution state in dimethyl sulfoxide (DMSO) depending on guest polymers. The three complexes were prepared by the vine-twining polymerization method using polytetrahydrofuran (PTHF), poly(ε-caprolactone) (PCL), and poly(l-lactide) (PLLA) as guest polymers. The stability investigation was conducted at desired temperatures (25, 30, 40, 60 °C) in DMSO solutions of the complexes. Consequently, the amylose–PTHF inclusion complex was dissociated at 25 °C, while the other complexes were stable under the same conditions. When the temperatures were elevated, the amylose–PCL and amylose–PLLA complexes were dissociated at 40 and 60 °C, respectively. We also found that amylose inclusion supramolecular polymers which were prepared by the vine-twining polymerization using primer-guest conjugates formed films by the acetylation of amylose segments. The film from acetylated amylose–PLLA supramolecular polymer had higher storage modulus than that from acetylated amylose–PTHF supramolecular polymer, as a function of temperature.
Formation of Supramolecular Soft Materials from Amylosic Inclusion Complexes with Designed Guest Polymers Obtained by Vine-Twining Polymerization
Amylose forms supramolecular inclusion complexes with polymeric guests in the phosphorylase-catalyzed enzymatic polymerization field, so-called “vine-twining polymerization”. However, such inclusion complexes have not exhibited specific properties and processability as functional supramolecular materials. In this study, we found that amylosic inclusion complexes, which were obtained by vine-twining polymerization using a designed guest polymer, that is, an amphiphilic triblock copolymer poly(2-methyl-2-oxazoline-block-tetrahydrofuran-block-2-methyl-2-oxazoline), exhibited gel and film formation properties. The characterization results of the products suggested that enzymatically elongated amylose chains complexed with the polytetrahydrofuran block in the triblock copolymer. Accordingly, the outer poly(2-methyl-2-oxazoline) blocks constructed hydrophilic spaces among the inclusion complex segments. Furthermore, the presence of such outer blocks affected the lower regularity of crystalline alignment among the inclusion complex segments in the products. Such higher-order structures probably induced the formation of supramolecular soft materials, such as gels and films.
Development of polyamide curable modified epoxy novolac resins with improved adhesion and chemical resistance
Purpose – To prepare modified epoxy resins from resorcinol, cresol and phenol for improved adhesion and chemical resistance. To evaluate the properties of such modified epoxy resins.Design/methodology/approach – Epoxy novolac resins (ENRs) were synthesised by condensing epichlorohydrin with novolacs based on different types of substituted phenols for improving adhesion and chemical resistance. Various compositions were made by incorporating different proportions of polyamide resin. The chemical and adhesive strengths of the conventional epoxy and the modified epoxy resins were characterised.Findings – The modified ENR using substituted phenols showed significant enhancement of chemical and adhesive strengths over the conventional DGEBA resin. The modified ENR had an increased number of glycidyl groups (thus increased functionality) of resin, which was responsible for improved chemical and adhesive strengths over the conventional DGEBA resin.Research limitations/implications – The EPN resins used in the pr...