Restructuring of an Ir(210) electrode surface by potential cycling
Summary This study addresses the electrochemical surface faceting and restructuring of Ir(210) single crystal electrodes. Cyclic voltammetry measurements and in situ scanning tunnelling microscopy are used to probe structural changes and variations in the electrochemical behaviour after potential cycling of Ir(210) in 0.1 M H2SO4. Faceted structures are obtained electrochemically as a function of time by cycling at a scanrate of 1 V·s−1 between −0.28 and 0.70 V vs SCE, i.e., between the onset of hydrogen evolution and the surface oxidation regime. The electrochemical behaviour in sulfuric acid solution is compared with that of thermally faceted Ir(210), which shows a sharp characteristic voltammetric peak for (311) facets. Structures similar to thermally-induced faceted Ir(210) are obtained electrochemically, which typically correspond to polyoriented facets at nano-pyramids. These structures grow anisotropically in a preferred direction and reach a height of about 5 nm after 4 h of cycling. The structural changes are reflected in variations of the electrocatalytic activity towards carbon monoxide adlayer oxidation.
Preparation and electrochemical characterization of palladium single crystal electrodes in 0.1 M H2SO4 and HClO4: Part I. Low-index phases
The electrochemical properties of Pd( 111), Pd( 1 0 0) and Pd( 1 10) single crystal bead electrodes, prepared by a novel electron beam heating and inductive annealing technique, have been characterized in 0.1 M sulfuric acid and 0.1 M perchloric acid by cyclic voltammetry and chronoamperometry. Hydrogen and (hydrogen) sulfate adsorption as well as surface oxidation were found to depend strongly on the crystallographic orientation and the nature of the electrolyte. The combination of charge displacement and voltammetric experiments allowed the determination of the potentials of zero total charge (E pztc ) of Pd(1 1 1) and Pd(100). The values of E pztc in sulfuric acid were found to be more negative than in perchloric acid. The estimation of E pztc for Pd(1 1 0) was hampered by the superposition with hydrogen absorption. The electro-oxidation of irreversible adsorbed carbon monoxide monolayers was studied on the three low-index Pd electrodes. The onset potential of the CO oxidation reaction follows the sequence Pd(100) < Pd( 110) <Pd( 111). Chronoamperometric experiments revealed a pronounced structure sensitivity of the reaction kinetics. The processes involved are determined by nucleation of oxygen-containing species on defect (step) sites and by slow diffusion of CO ads on (1 1 1) terrace sites.
Comparative Analysis of the Main Business Intelligence Solutions
Nowadays, Business Intelligence solutions are the main tools for analyzing and monitoring the companyâ€™s performance at any organizational level. This paper presents a comparative analysis of the most powerful Business Intelligence solutions using a set of technical features such as infrastructure of the platform, development facilities, complex analysis tools, interactive dashboards and scorecards, mobile integration and complex implementation of performance management methodologies.