Simultaneous retardation compensation during bending of plastic film coated with a polymer layer of opposite birefringence.
We proposed a method of eliminating the bending-induced retardation of a plastic film by coating it with a polymer layer with an opposite birefringence. We coated a polystyrene (PS) or a poly(methyl methacrylate) (PMMA) layer on a polycarbonate (PC) plastic film. The bare PC film is composed of main-chain-type polymers and showed an increase in retardation with bending. The main-chains of the PC polymer are reoriented along the circular arc direction during bending, resulting in a positive birefringence. In contrast, the 11 wt. % PS-coated and the 19 wt. % PMMA-coated PC films showed minimal change in the retardation regardless of the radius of curvature. The PS and the PMMA polymers are of the side-chain-type, and the side-chains were aligned perpendicular to the circular arc direction during bending, resulting in a negative birefringence. Consequently, the bending-induced retardation of the PC film can be compensated by the PS or the PMMA layer during bending of the film. This method of compensating for the bending-induced retardation of the plastic film can be useful for flexible display applications.
New Clues to the Factors Governing the Perpendicular Alignment of Liquid Crystals on Rubbed Polystyrene Film Surfaces
We have investigated the surfaces of rubbed polystyrene (PS) films in detail using atomic force microscopy and have discovered a previously unknown surface feature:  submicroscale meandering groove-like structures composed of gravel-like grooves in tens of nanometers are present, oriented perpendicular to the rubbing direction. This unusual surface morphology is a significant departure from the surface topographies observed so far for rubbed PS and other polymer films, for which grooves are usually only found parallel to the rubbing direction. We also conclude from retardation analysis and linearly polarized infrared (IR) spectroscopy that the phenyl side groups of the PS chains are reoriented perpendicular to the rubbing direction, with para-directions that are nearly normal to the film plane, whereas the vinyl backbones of the PS chains are reoriented along the rubbing direction. This is the first time IR spectroscopic techniques have been used to determine the three-dimensional reorientation geometry o...
Engineering bio-inks for 3D bioprinting cell mechanical microenvironment
Three-dimensional (3D) bioprinting has become a promising approach to construct­ing functional biomimetic tissues for tissue engineering and regenerative medicine. In 3D bioprinting, bio-inks are essential for the construction of cell microenviron­ment, thus affecting the biomimetic design and regenerative efficiency. Mechanical properties are one of the essential aspects of microenvironment, which can be char­acterized by matrix stiffness, viscoelasticity, topography, and dynamic mechanical stimulation. With the recent advances in functional biomaterials, various engineered bio-inks have realized the possibility of engineering cell mechanical microenviron­ment in vivo. In this review, we summarize the critical mechanical cues of cell micro­environments, review the engineered bio-inks while focusing on the selection princi­ples for constructing cell mechanical microenvironments, and discuss the challenges facing this field and the possible solutions for them.