Fabrication Of A-C:B/N-Si Solar Cells With Low Positive Bias By Custom-Made-CVD
Boron doped amorphous carbon (a-C:B) film fabricated on n-type silicon using waste palm oil precursor by low positive bias voltage is presented. The rectifying curve were found for all samples under dark measurement revealed that those samples were p-type semiconductor. The +30 V was found the optimized of the electronic properties with the open circuit voltage (VOC), current density (JSC), fill factor (FF) and efficiency (%) were approximately 0.259034 V, 1.299456 mA/cm 2 , 0.240011, and 0.080788 %, respectively. The conversion efficiency of a-C:B has been improved under the influenced of low positive bias.
P-type properties of micro and nano-structured carbon films from hydrocarbon palm oil in photovoltaic heterojunction solar cell applications
The micro and nano-structured amorphous carbon as p-type films prepared from natural palm oil precursor for heterojunction solar cell were presented. Field-emission scanning electron microscopy (FESEM) revealed the micro and nano structured films had particle size in the range of 382 nm to 689 nm and 28 to 34 nm, respectively. The energy-dispersive spectroscopy (EDS) showed the existing of carbon in micro-structured amorphous carbon film and carbon together with boron in nano-structured amorphous carbon film. Solar simulator analysis results showed an open circuit voltage (VOC), current density (JSC), fill-factor(FF) and conversion efficiency (η) of Au/a-C/n-Si/Au were 264.62 mV, 1.50434 mA/cm2, 0.32632, and 0.130154 %, respectively. Meanwhile, the VOC, JSC, FF and η of Au/a-C:B/n-Si/Au solar cell were 271.25 mV, 14.91723 mA/cm2, 0.33582, and 1.542622 %, respectively. The conversion efficiency was increased as the p-type film was in nanostructure form.
Evaluation of Impact of Yarn Count and Stitch Length on Pilling, Abrasion, Shrinkage and Tightness Factor of 1 ? 1 Rib Cotton Knitted Fabrics
This study investigates the impact of yarn count and stitch length of 100% cotton knitted fabrics. 1 × 1 ribs structured fabrics were used in this research work. The stitch length 2.50 mm, 2.52 mm, 2.60 mm, 2.70 mm, 2.80 mm and 2.96 mm were used of the yarn count of 26Ne, 28Ne and 36Ne. The areal densities of the grey fabrics were in various amounts. The impacts of yarn count and stitch length were measured concerning pilling resistance, abrasion resistance, and shrinkage and tightness factor. The result showed that the fabric pilling grade decreased while number of cycle increased. Abrasion resistance decreased but length wise shrinkage increased despite the fact that the stitch length increased. The results also exposed that the tightness factor of the fabric increased with the increase of the stitch length in both dyeing and washing state and finished state compared to grey state for the yarn count 26Ne and homogeneous result not found for yarn count 28Ne and 36 Ne. Evaluation of Impact of Yarn Count and Stitch Length on Pilling, Abrasion, Shrinkage and Tightness Factor of 1 × 1 Rib Cotton Knitted Fabrics