Vibration characteristics of aluminum surface subjected to ultrasonic waves and their effect on wetting behavior of solder droplets.
The vibration characteristics of an aluminum surface subjected to ultrasonic waves were investigated with a combination of numerical simulation and experimental testing. The wetting behavior of solder droplets on the vibrating aluminum surface was also examined. The results show that the vibration pattern of the aluminum surface is inhomogeneous. The amplitude of the aluminum surface exceeds the excitation amplitude in some zones, while the amplitude decreases nearly to zero in other zones. The distribution of the zero-amplitude zones is much less dependent on the strength of the vibration than on the location of the vibration source. The surface of the liquid solder vibrates at an ultrasonic frequency that is higher than the vibration source, and the amplitude of the liquid solder is almost twice that of the aluminum surface. The vibration of the surface of the base metal (liquid solder) correlates with the oxide film removal effect. Significant removal of the oxide film can be achieved within 2s when the amplitude of the aluminum surface is higher than 5.4 μm or when the amplitude of the liquid solder surface is higher than 10.2 μm.
Joint strength of aluminum ultrasonic soldered under liquidus temperature of Sn–Zn hypereutectic solder
Abstract In order to obtain high-strength aluminum joints, ultrasonic soldering of 1070 aluminum was conducted under liquidus temperature of Sn–Zn hypereutectic solder. A device for ultrasonic soldering was assembled, which propagated ultrasonic vibrations in a direction perpendicular to joining surfaces. This device joined 1070-Al using quasi-melting Sn–Zn hypereutectic solder without using any artificial spacers. The strength of the solder joints was evaluated by tensile tests. The optimum joining conditions were determined, and the effects of solder compositions and soldering temperature on the joint strength and the solder layer thickness were examined. In this ultrasonic soldering process, the highest tensile strength was obtained for the solder joints fabricated at 220 °C for the Sn–23Zn and Sn–40Zn solder compositions. The joint strength was equivalent to that of 1070-Al heat treated at 220 °C. The sound joints were obtained at 300 °C using Sn–82Zn solder, the liquid phase volume fraction of which was theoretically only 0.24. The present work also revealed that the thickness of retained solder layer in the joint after ultrasonic soldering could be estimated. Accordingly, ultrasonic soldering under the liquidus temperature of Sn–Zn hypereutectic solder could be a spacer-free soldering method to obtain high-strength aluminum joints.
Submicron polymer structures with X-ray lithography and hot embossing
This article describes the process chain for replication of submicron structures with varying aspect ratios (AR) up to 6 in polymethylmethacrylate (PMMA) by hot embossing to show the capability of the entire LIGA process to fabricate structures with these dimensions. Therefore a 4.7 μm thick layer of MicroChem 950k PMMA A11 resist was spin-coated on a 2.3 μm Ti/TiOx membrane. It was patterned with X-ray lithography at the electron storage ring ANKA (2.5 GeV and λc ≈ 0.4 nm) at a dose of 4 kJ/cm3 using a Si3N4 membrane mask with 2 μm thick gold-absorbers. The samples were developed in GG/BDG and resulted in AR of 6–14. Subsequent nickel plating at 52°C resulted in a 200 μm thick nickel tool of 100 mm diameter, which was used to replicate slit-nozzles and columns in PMMA. Closely packed submicron cavities with AR 6 in the nickel shim were filled to 60% during hot embossing.