Evaluation of Stability of Amylose Inclusion Complexes Depending on Guest Polymers and Their Application to Supramolecular Polymeric Materials
This paper describes the evaluation of the stability of amylose–polymer inclusion complexes under solution state in dimethyl sulfoxide (DMSO) depending on guest polymers. The three complexes were prepared by the vine-twining polymerization method using polytetrahydrofuran (PTHF), poly(ε-caprolactone) (PCL), and poly(l-lactide) (PLLA) as guest polymers. The stability investigation was conducted at desired temperatures (25, 30, 40, 60 °C) in DMSO solutions of the complexes. Consequently, the amylose–PTHF inclusion complex was dissociated at 25 °C, while the other complexes were stable under the same conditions. When the temperatures were elevated, the amylose–PCL and amylose–PLLA complexes were dissociated at 40 and 60 °C, respectively. We also found that amylose inclusion supramolecular polymers which were prepared by the vine-twining polymerization using primer-guest conjugates formed films by the acetylation of amylose segments. The film from acetylated amylose–PLLA supramolecular polymer had higher storage modulus than that from acetylated amylose–PTHF supramolecular polymer, as a function of temperature.
Preparation of polysaccharide supramolecular films by vine-twining polymerization approach.
In this study, we investigated the preparation of polysaccharide supramolecular films through the formation of inclusion complexes by amylose in vine-twining polymerization using carboxymethyl cellulose-graft-poly(ε-caprolactone) (CMC-g-PCL) as a new guest polymer. First, hydrogels were prepared by phosphorylase-catalyzed enzymatic polymerization in the presence of CMC-g-PCL according to the vine-twining polymerization manner. The XRD result of a powdered sample obtained by lyophilization of the resulting hydrogel indicated the presence of inclusion complexes of amylose with the PCL graft-chains between intermolecular (CMC-g-PCL)s, which acted as supramolecular cross-linking points for the hydrogelation. Then, the supramolecular films were obtained by adding water to the powdered samples, followed by drying. The mechanical properties of the selected films examined by tensile testing were superior to those of a CMC film. The effect of the supramolecular cross-linking structures on the mechanical properties of the films was evaluated further by several investigations.
Enzymatic synthesis of dendritic amphoteric α-glucans by thermostable phosphorylase catalysis.
This article reports the enzymatic synthesis of dendritic amphoteric α-glucans having both glucuronic acid and glucosamine residues at the non-reducing ends by thermostable phosphorylase-catalyzed successive glucuronylation and glucosaminylation of a glucan dendrimer having α-(1 → 4)-glucan non-reducing ends using α-D-glucuronic acid 1-phosphate and α-D-glucosamine 1-phosphate as glycosyl donors, respectively. The structure of the products is confirmed by the (1)H NMR analysis. The products exhibit inherent isoelectric points (pIs) determined by the ζ-potential measurement. These materials self-assemble in water at pH = pI to form large aggregates, but disassemble at pH shifted from pI.