Improved adhesion for thermoplastic polymers using oxyfluorination
Industrial applications of thermoplastic polymers are often limited by their poor adhesion properties. In this work the effect of surface oxyfluorination on the adhesion properties was investigated for polyethylene (PE), polyoxymethylene (POM), polybutylene terephthalate (PBT) and polyamide 6 (PA6). The adhesive joint strength was quantified using lap-shear tests. These results were correlated with the changes in the chemical composition of the surface, determined by X-ray photoelectron spectroscopy (XPS), in the surface free energy, measured by the contact angle method, and in the topography, using white-light confocal microscopy. The adhesive strength is strongly improved for all four polymers, but the degree of this increase depends on the polymer type. The surface free energy shows a similar trend for all four polymers. A high surface free energy exceeding 50 mN/m was observed after oxy-fluorination, whereby the polar component was strongly predominant. Surface topography measurements show no significant increase of the surface roughness. So the effect of oxyfluorination results primarily in increased wettability and polarity, due to changes of the chemical composition of the surface. XPS measurements confirm the integration of fluorine and oxygen groups in the polymer chain, which correlates with the increased polarity.
Surface treatment of polymers. II. Effectiveness of fluorination as a surface treatment for polyethylene
An effective surface treatment for adhesive bonding of polyethylene has been developed. It involves exposing the polymer to an environment of elemental fluorine or fluorine diluted in argon. By this treatment, extensive fluorination of the surface region is effected. The fluorinated surface permits formation of strong adhesive joints by conventional adhesive bonding techniques even though the wettability of the new surface is similar to polytetrafluoroethylene. We believe that treatment of the polymer with elemental fluorine effectively eliminates the weak boundary layer associated with polyethylene by either crosslinking or by increasing the molecular weight in the surface region.
Finite Difference Modeling on the Temperature Field of Substrate in Friction Surfacing
Friction surfacing is an advanced process of great potential, especially in the field of repair and reclamation of worn and damaged components. As a kind of thermal processing technology, the temperature profile and changes of the substrate in friction surfacing are important factors to get coatings of high quality. In this paper, the temperature field of the substrate during the process is simulated by finite difference method. The results are consistent with experiments, reappearing the temperature change of the substrate during friction surfacing, allowing further study on figuration and quality of coatings.