Bias Stress Induced Conduction Mechanism Evolution in Silica Based Inter-Metal Dielectrics
The real-time conduction mechanism evolution during bias stress of three silica based inter-metal dielectrics in Cu damascene structures was investigated. Capacitance measurements at 1 MHz and I-V measurements were intermittently inserted into the process of bias stress to monitor the conduction mechanism evolution with time. All experiments show that the capacitance is constant and the I-V curve slope decreases with bias stress and converges to the half of the initial value. Based on these findings, we conclude that the conduction mechanism changes from a normal Frenkel-Poole emission to an "abnormal" Frenkel-Poole emission with bias stress
Leakage mechanism in Cu damascene structure with methylsilane-doped low-K CVD oxide as intermetal dielectric
This letter investigates the leakage mechanism in the Cu damascene structure with methylsilane-doped low-k CVD organosilicate glass (OSG) as the intermetal dielectric (IMD). The leakage between Cu lines was found to be dominated by the Frenkel-Poole (F-P) emission in OSG for the structure using a 50-nm SiC etching stop layer (ESL). In the structure using a 50-nm SiN ESL, the leakage component through SiN also made a considerable contribution to the total leakage in addition to the bulk leakage from trapped electrons in OSG. An appropriate ESL of sufficient thickness is essential to reduce the leakage for application to a Cu damascene integration scheme.
Submicron polymer structures with X-ray lithography and hot embossing
This article describes the process chain for replication of submicron structures with varying aspect ratios (AR) up to 6 in polymethylmethacrylate (PMMA) by hot embossing to show the capability of the entire LIGA process to fabricate structures with these dimensions. Therefore a 4.7 μm thick layer of MicroChem 950k PMMA A11 resist was spin-coated on a 2.3 μm Ti/TiOx membrane. It was patterned with X-ray lithography at the electron storage ring ANKA (2.5 GeV and λc ≈ 0.4 nm) at a dose of 4 kJ/cm3 using a Si3N4 membrane mask with 2 μm thick gold-absorbers. The samples were developed in GG/BDG and resulted in AR of 6–14. Subsequent nickel plating at 52°C resulted in a 200 μm thick nickel tool of 100 mm diameter, which was used to replicate slit-nozzles and columns in PMMA. Closely packed submicron cavities with AR 6 in the nickel shim were filled to 60% during hot embossing.