Basalt FRP Spike Repairing of Wood Beams
This article describes aspects within an experimental program aimed at improving the structural performance of cracked solid fir-wood beams repaired with Basalt Fiber Reinforced Polymer (BFRP) spikes. Fir wood is characterized by its low density, low compression strength, and high level of defects, and it is likely to distort when dried and tends to fail under tension due to the presence of cracks, knots, or grain deviation. The proposed repair technique consists of the insertion of BFRP spikes into timber beams to restore the continuity of cracked sections. The experimental efforts deal with the evaluation of the bending strength and deformation properties of 24 timber beams. An artificially simulated cracking was produced by cutting the wood beams in half or notching. The obtained results for the repaired beams were compared with those of solid undamaged and damaged beams, and increases of beam capacity, bending strength and of modulus of elasticity, and analysis of failure modes was discussed. For notched beams, the application of the BFRP spikes was able to restore the original bending capacity of undamaged beams, while only a small part of the original capacity was recovered for beams that were cut in half.
Structural Characterization of Hybrid Fiber-Reinforced Polymer-Glulam Panels for Bridge Decks
The structural characterization of hybrid fiber-reinforced polymer (FRP)–glued laminated (glulam) panels for bridge deck construction is examined using a combined analytical and experimental approach. The structural system is based on the concept of sandwich construction with strong and stiff FRP composite skins bonded to an inner glulam panel. The FRP composite material was made of E-glass reinforcing fabrics embedded in a vinyl ester resin matrix. The glulam panels were fabricated with bonded eastern hemlock vertical laminations. The FRP reinforcement was applied on the top and bottom faces of the glulam panel by wet layup and compacted using vacuum bagging. An experimental protocol based on a two-span continuous bending test configuration is proposed to characterize the stiffness, ductility, and strength response of FRP-glulam panels under simulated loads. Half-scale FRP-glulam panel prototypes with two different fiber orientations, unidirectional (0°) and angle-ply (±45°), were studied and the structu...
Experimental study on bond behavior between high-strength grout and deformed steel bars
Abstract Engineers use high-strength grout to connect precast concrete members for its low shrinkage and good fluidity. This paper designed 87 central pull-out specimens using the control variable method to investigate the influence of factors on the rebar-grout bond property such as compressive strength, steel grade, bar diameter, transverse stirrups, and bond length. The test result showed that improving grout compressive strength (85.8 MPa–122.7 MPa) cannot improve the bond strength, which was different from the previous conclusions of concrete pull-out tests. Simplified formulas were presented for calculating the characteristic values of bond strength, residual strength, peak slip, and relative slip of load-holding platform based on parameter analysis. Then, a constitutive model was proposed to predict the full-range bond stress-slip curve of high-strength grout and steel bar specimens from bearing to failure. Finally, FEA models were established to evaluate the applicability and accuracy of the constitutive model.