On the thermo-mechanical events during friction surfacing of high speed steels
This paper is concerned with the friction surfacing of high-speed steels, BM2, BT15 and ASP30 onto plain carbon steel plate. The events that the matrix and carbides experience as the coating material pass from the coating rod to the substrate, in forming the coating, is described. The coating is observed to harden automatically within a few seconds of being deposited onto the cold substrate. This autohardening is observed to be an inherent feature of the friction surfacing process and the only post-coating heat treatment required is tempering, as with traditionally hardened high-speed steels. The mechanism of autohardening is discussed in terms of the mechtrode/coating/substrate thermal system.
Investigation on the wear and corrosion behaviour of friction surfaced mild steel
It is one of the methods used by friction surfacing in mild steel where wear resistance and corrosion resistance improved. This work is done by using end milling machine. Hardness, wear and corrosion resistance were conducted by the corresponding ASTM standard and results were compared with the base metals. Enhancement in mechanical properties were found with the new specimen and the friction surfacing was found to be the suitable process that can improve the mechanical properties like hardness, wear and corrosion.
Growth and Characterization of β-RDX Single-Crystal Particles
1,3,5-Trinitrohexahydro-s-triazine (RDX) single-crystal particles crystallized in the β phase have been successfully grown by sublimation–recrystallization. Synchrotron X-ray diffraction results confirm that the recrystallized products are β-RDX single crystals. Compared to the traditional solution deposition methods, the sublimation method used in this work breaks through the mass limitations during the growth of β-RDX. The distribution of α- and β-RDX on different substrates reveals that hydrophilic substrates are prone to grow β-RDX single crystals and that hydrophobic substrates prefer α-RDX single crystals. The sublimation rate dominates the growth of pure β-RDX. The mechanisms of the phase transition from β-RDX to α-RDX during the process of sublimation–recrystallization have been studied. The current results can promote the potential application of β-RDX in the propellant, explosives, and military fields.