Advanced Dispenser Cathodes
Controlled porosity reservoir cathodes offer significantly improved performance over conventional impregnated cathodes. Optimized performance requires additional design to achieve reduced barium deposition on adjacent surfaces, increased lifetime, and high current density emission. This paper describes the achievable performance and the associated design requirements.
Controlled porosity cathodes from sintered tungsten wires
In this paper, we describe a simple technique for controlling the porosity of tungsten cathodes and replacing the barium compound impregnated matrix with a reservoir of barium producing compounds. Consequently, the cathode thus produced yields a uniform work function surface and significantly longer life than porous tungsten cathodes. The process uses existing sintering equipment and readily available, modestly priced materials. It is anticipated that successful development of this process will lead to less expensive, higher quality cathodes.
EFFECT OF SAMPLE PREPARATION ON WATER TREE RESISTANCE OF XLPE/SEBS BLENDS
The effects of an aromatic polymer, such as poly[styrene-b-(ethylene-co-butylene)b-styrene] (SEBS), and its preparation processes on water tree resistance, morphology, crystallinity, dielectric constant and dielectric loss tangent of crosslinked polyethylene (XLPE)/SEBS and XLPE/SEBS/ethylene vinyl acetate (EVA) blends were investigated. The XLPE/SEBS samples were characterized by means of differential scanning calorimetry, scanning electron microscopy, dielectric spectral analysis and the accelerated water treeing experiment. The results clearly showed that although SEBS was partially compatible with LDPE and it was dispersed evenly in XLPE matrix, the blends demonstrated excellent dielectric performances, such as dielectric constant and dissipation factor. The crystallinity of XLPE/SEBS blends was decreased with increase in SEBS content and it was further decreased with the addition of EVA. SEBS could effectively improve the water-tree resistance of XLPE and both SEBS and EVA were found to improve the water tree resistance of XLPE synergistically as expected. The differences in sample preparation processes could change the phase morphology and dielectric performance of the blends, and could also influence the dispersion of SEBS in XLPE matrix as well as the crystallinity of the blends. Different preparation processes led to different water tree resistance behaviours of the samples. The improvement of SEBS dispersion in XLPE matrix helped to improve the water tree resistance of XLPE.