Effect of Post Heat Treatment on the Microstructure and Microhardness of Friction Stir Processed NiAl Bronze (NAB) Alloy
NiAl bronze (NAB) alloy is prepared by using friction stir processing (FSP) technique at a tool rotation rate of 1200 rpm and a traverse speed of 150 mm/min. A post heat treatment is performed at the temperature of 675 °C. The effect of heat treatment on the microstructure and microhardness is studied. The results show that the microstructure of the FSP NAB alloy consists of high density dislocations, retained β phase (β′ phase) and recrystallized grains. When annealed at 675 °C, discontinuous static recrystallization (DSRX) takes place. The content of β′ phase gradually decreases and fine κ phase is precipitated. After annealing for 2 h, both the microhardness of the FSP sample in the stir zone (SZ) and the difference in hardness between the SZ and base metal decrease due to the reduction of the dislocation density and β′ phase, accompanying recrystallized grain coarsening. With further increasing of the annealing time to 4 h, the aforementioned difference in hardness nearly disappears.
Cavitation erosion of NiAl-bronze layers generated by friction surfacing
Abstract Friction surfacing is a solid-state process, which allows deposition welding at temperatures below the melting range. For this investigation coating layers of NiAl-bronze were deposited by friction surfacing on self-mating substrates, followed by microstructural characterisation. Further, cavitation tests were performed in order to investigate wear resistance. Cavitation erosion mechanisms were analysed by means of optical and electron microscopy. All coatings show incubation periods about twice as long as those of the substrate material, while their average rate of material loss is about one half of that of the substrate. The differences in cavitation erosion resistance are due to more ductile behaviour of the coatings, as well as corrosion increasing the wear of the as-cast material.
Coated-wire electrodes containing polymer immobilized ionophores blended with poly(vinyl chloride).
Polymers containing covalently attached 18-crown-6 or 2.2.2 cryptand units were incorporated into plasticized PVC membranes and the composite membranes were examined as potassium ion sensor elements. Ionophores were linked to carboxy-PVC and to poly(acrylic acid) via amide linkages to an alkyl spacer unit. Coated-wire electrodes (CWEs) from the immobilized ionophores gave acceptable responses, but conventional ion-selective membrane electrodes (ISEs) prepared by solvent casting were inactive. Dip-cast membranes did give active ISEs. Potassium electrode performance was independent of the loading of the ionophore within the acrylate support polymer, but depended upon the spacer length. Ion selectivity varied with the ionophore loading within the support polymer. Selectivity is a composite of the ionophore selectivity and ion-exchange interactions with the acrylate backbone, giving selectivities akin to carboxylate substituted crown ethers, notably enhanced monovalent/divalent ion discrimination relative to the ionophore in solution. Polymer immobilization extended the lifetime of active electrodes.