Dependence of the electro-optical properties of polymer dispersed liquid crystals on the photopolymerization process
We have studied the dependence of the electro-optical properties of polymer dispersed liquid crystals (PDLC) on the ultraviolet (UV) cure of the solution of monomer and liquid crystal. The kinetics of UV polymerization and its effect on the morphology of the phase separated droplets of liquid crystal determine the switching voltage, response time, and luminance of the PDLC. Using a series of statistically designed experiments, we have mapped the dependence of these responses on the weight fraction of liquid crystal, the temperature of the cell during cure, and light intensity. Temperature and composition are strongly coupled parameters that influence switching voltage, luminance, and response times. Switching voltages are minimized at 4–5 V for an 8 μm cell gap over a large region of temperature-composition space. An abrupt transition line occurs through that space. On one side of the transition line, voltage increases linearly either as temperature increases or composition decreases, and on the other sid...
Polymer-Dispersed Liquid Crystals: Boojums at Work
The idea of dispersing micron-size birefringent particles in a polymer to selectively scatter light is not new. In the 1930s Land patented a light polarizing material in which small, oriented solid crystallites were suspended in a clear polymer. The polymer material was selected so that its refractive index matched one of the principal refractive indices of the crystallites while the other did not. The resuit was a light polarizer tha t would pass one component of polarized light but scatter the other component out of the beam path. This idea was substantially expanded by the introduction of liquid crystals as the birefringent material. The orientation of the particles (in this case droplets), and hence the refractive index match and the scattering, could be controlled by an electric field. Such a material could be used as a light shutter for either unpolarized or polarized light. In the mid-1970s this basic concept was applied by Hilsum, but having no way to disperse droplets of liquid crystals in a polymer, he did the opposite and put optically isotropic solid particles in the birefringent liquid crystal. Although Hilsum demonstrated the concept, no commercial device was produced, probably because the shutter contrast was limited. Since then several ways have been found to disperse droplets in a polymer: filling the pores of a microfilter; emulsifying the liquid crystal in a water soluble polymer; and using phase separation methods to create a dispersion of droplets in non-aqueous polymer materials.
Preparation of hydrophilic poly(vinyl butyral) hollow fiber membrane via thermally induced phase separation
Abstract Hydrophilic microporous hollow fiber membranes were prepared via thermally induced phase separation (TIPS). Poly(vinyl butyral) (PVB) and three kinds of polyethylene glycols (PEG) with the molecular weight of 200, 400 and 600 were used as polymer and diluents. In all cases, liquid–liquid (L–L) phase separation occurred and asymmetric cellular structures with the smaller pores at the outer surface were obtained. The properties of membranes such as pore size, water permeability, solute rejection and intensity were investigated by changing molecular weight of PEG, concentration of PVB, composition of the bath and air gap distance. The smaller molecular weight of PEG, the more PEG in the bath and the shorter air gap distance resulted in the higher water permeability, the lower solute rejection property and the lower mechanical strength.