Adsorption behavior of propylamine on activated carbon fiber surfaces as induced by oxygen functional complexes.
In this study, the surfaces of activated carbon fibers (ACFs) were modified by nitric acid to introduce surface oxygen complexes and to observe the influence of those complexes on the propylamine adsorption of the ACFs. It was found that the oxygen complexes including carboxylic and phenolic groups were predominantly increased, resulting in the increase of total surface acidity. However, the specific surface areas and the total pore volumes of the modified ACFs were decreased by 5-8% due to the increased blocking (or demolition) of micropores in the presence of newly introduced complexes. Despite the decrease of textural properties, it was found that the amount of propylamine adsorbed by the modified ACFs was increased by approximately 17%. From the XPS results, it was observed that propylamine reacted with strong or weak acidic groups, such as COOH or OH, on the ACF surfaces, resulting in the formation of pyrrolic-, pyridonic-, or pyridine-like structures.
Nitric Acid-Treated Carbon Fibers with Enhanced Hydrophilicity for Candida tropicalis Immobilization in Xylitol Fermentation
Nitric acid (HNO3)-treated carbon fiber (CF) rich in hydrophilic groups was applied as a cell-immobilized carrier for xylitol fermentation. Using scanning electron microscopy, we characterized the morphology of the HNO3-treated CF. Additionally, we evaluated the immobilized efficiency (IE) of Candida tropicalis and xylitol fermentation yield by investigating the surface properties of nitric acid treated CF, specifically, the acidic group content, zero charge point, degree of moisture and contact angle. We found that adhesion is the major mechanism for cell immobilization and that it is greatly affected by the hydrophilic–hydrophilic surface properties. In our experiments, we found 3 hto be the optimal time for treating CF with nitric acid, resulting in an improved IE of Candida tropicalis of 0.98 g∙g−1 and the highest xylitol yield and volumetric productivity (70.13% and 1.22 g∙L−1∙h−1, respectively). The HNO3-treated CF represents a promising method for preparing biocompatible biocarriers for multi-batch fermentation.
Measuring Sheet Resistances of Dielectrics Using Co‐Planar Hydrogel Electrochemical Cells with Practical Applications to Characterize the Protective Quality of Paints on Sculptures
Electrical properties of thin dielectric films at the solid-liquid phase boundary are an important performance characteristic of many devices, coatings and sensors. In this paper, co-polymeric hydrogels of polyacrylic acid co-sulfonic acid, swollen with a salt solution to act as the solid electrolyte, were used to assess interfaces using electrochemical impedance spectroscopy (EIS) in a co-planar geometry. Silane-modified glasses were characterized by the co-planar hydrogel EIS cell and found to be distinguishable based on their surface monolayer chemistry. EIS measurements were also made on primed and painted metal substrates, using both test panels and an outdoor sculpture, Tony Smith's Stinger. The panels were then exposed to accelerated and outdoor weathering and showed degradation on the surface paint layers, which was observable electrochemically using EIS and confirmed visually by SEM. Electrochemical spectral features were compared between data from a standard paint-test cell versus this co-planar hydrogel cell; both cell types were able to measure coating capacitance, providing useful information about the condition of the bulk coating. Yet, sheet resistance (Rs) was a spectral feature seen only by the co-planar hydrogel cell. Thus, it can be concluded that the use of such co-planar hydrogel cells can provide an earlier warning sign to coating degradation and such cells provide a new type of spectral information that is not assessable by the standard geometry.