Cellulose Diacetate-g-poly(p-dioxanone) Co-polymer: Synthesis, Properties and Microsphere Preparation
A novel biodegradable graft co-polymer based on cellulose diacetate (CDA) and poly(p-dioxanone) was synthesized by ring-opening polymerization of p-dioxanone (PDO). The molecular structure of co-polymers was characterized by one- and two-dimensional NMR. The graft co-polymers with different lengths of PPDO side-chains could be controllably synthesized by changing the in-feed ratio of CDA/PDO. It was found that the PPDO content had great effect on the thermal transition behavior, crystallization ability and thermal stability of the graft co-polymer. The in vitro degradation rates of CDA-g-PPDO were higher than that of linear PPDO due to their lower crystallinity. Moreover, porous microspheres of graft co-polymers with a diameter of about 5 μm, prepared through the solvent evaporation of water-in-oil emulsion (W/O), indicated it may have potential applications in drug-delivery systems.
Formation of core/shell nanoparticles with a lipid core and their application as a drug delivery system.
A novel preparation method for core/shell nanoparticles with a drug-loaded lipid core was designed and characterized. The lipid core is composed of lecithin and a drug, and the polymeric shell is composed of Pluronics (poly(ethylene oxide)-poly (propylene oxide)-poly(ethylene oxide) triblock copolymer, F-127). For the formation of stabilized core/shell nanoparticles, freeze-drying was performed in the presence of trehalose used as a cryoprotectant. Cryogenic transmittance electron microscopy (cryo-TEM), differential scanning calorimetry (DSC), and a particle size analyzer were used to observe the formation of the stabilized core/shell nanoparticles. For the application of the core/shell nanoparticles as a drug carrier, paclitaxel, a potent anticancer drug, was loaded into the core/shell nanoparticles, and the drug loading amount and the drug release pattern were observed.
A Rapid Eco‐Friendly Synthesis of Poly(butylene succinate) by a Direct Polyesterification under Microwave Irradiation
A rapid and eco-friendly synthesis of poly(butylene succinate) (PBS) using microwaves was developed in the presence of 1,3-dichloro-1,1,3,3-tetrabutyldistannoxane as catalyst. To determine the optimum conditions, the effect of catalyst concentration, bulk vs. solution polymerization, reaction time, temperature, and stoichiometry of the monomers were studied. Based on the optimum conditions, PBS with a weight-average molecular weight of 2.35 x 104 was obtained in a short time of 20 min.