Development of NanoCAP (nano composite advanced particles) technology for high density recording
In this paper, nanosized spherical magnetite particles, with the coercivity force of about 3000 Oe was developed. This material was named NanoCAP (nano composite advanced particles). This study described both magnetic and structural properties of NanoCAP. The crystal structure and the microstructure of the particles were examined using an X-ray diffractometer and high resolution transmission electron microscope, respectively. The obtained magnetization and coercivity of the particles were 89 emu/g and 2900 Oe, respectively. NanoCAP is expected to be the most promising candidate for ultrahigh capacity recording tapes.
Magnetic Properties of Fe16N2 Fine Particles.
Heat conditions for synthesis of Fe16N2 tine particles and the resulting magnetic properties were investigated. Commercial ultra fine γ - Fe2O3 particles were first reduced under hydrogen gas at temperatures between 200°C and 700°C for 8 hours and nitrided under an ammonia-argon mixed gas at 140°C for 24 hours. The powder reduced at 500°C and nitrided at 140°C was identified as nearly Fe16N2 single phase by X-ray diffraction and Mossbauer analysis. Saturation magnetization at room temperature was about 200 emu/g. Maximum coercive force (2250 Oe) was achieved in the Fe16N2 powder with the largest specific surface area.
Sustainable production of toxin free marine microalgae biomass as fish feed in large scale open system in the Qatari desert.
Mass cultivation of microalgae biomass for feed should be cost effective and toxin free. Evaporation loss in Qatar can be as high as 2 cm/d. Hence, production of marine microalgae biomass in Qatar would also require mitigating water loss as there was only very limited groundwater reserve. To address these issues, a combination of four growth conditions were applied to a 25,000 L raceway pond: locally isolated microalgae strain was selected which could grow in elevated salinity; strain that did not require silica and vitamins; volume of the culture would increase over time keeping denser inoculum in the beginning, and evaporation water loss would be balanced by adding seawater only. A local saline tolerant Nannochloropsis sp. was selected which did not require silica and vitamins. When the above conditions were combined in the pond, average areal biomass productivities reached 20.37 g/m(2)/d, and the culture was not contaminated by any toxic microalgae.