Recycling Waste Bakelite As A Carbon Resource In Ironmaking
Bakelite is a 3-dimensional cross-linked network structured thermosetting polymer which is difficult to recycle after use. However, it contains high levels of carbon and CaCO3 that can be recovered for use as reductant and fluxing agent in ironmaking. In this work we report the use of postconsumer bakelite as reductant for the production of metallic iron from iron oxide in a horizontal tube furnace through the composite pellet approach.Gas emission studies were conducted by pyrolysing raw bakelite at different temperatures within the temperature range 1200-1600 °C in a horizontal tube furnace. Following this,composite pellets were then formed from mixtures of iron oxide and post-consumer bakelite.The iron oxide-bakelite composites were heated from room temperature to 1200 °C and then between 1200-1600 °C in a continuous stream of pure argon and the off gas was analysed continuously using an infrared (IR) gas analyser. Elemental analyses of samples of the reduced metal were performed chemically for its oxygen content using a LECO oxygen/nitrogen analyser. The extent of reduction after ten minutes was determined from the oxygen content. Gas emission studies revealed the emission of large volumes of the reductant gases CO and CH4along with CO2.It is further demonstrated that post-consumer bakelite is effective at reducing iron oxide to produce metallic iron.
Recycling Waste Polyurethane as a Carbon Resource in Ironmaking
Globally, major avenues available for dealing with waste Poly-Urethane (PU) are disposal at landfill sites and incineration. However, PU contains high levels of carbon and hydrogen that can be recovered for use as reductant in metal extraction processes. In this work the use of post-consumer PU as reductant for the production of metallic iron from iron oxide was investigated in a horizontal tube furnace through the composite pellet approach. Composite pellets were formed from mixtures of iron oxide and post-consumer PU. The iron oxide-PU composites were heated from room temperature to 1200 °C and then between 1200-1600 °C in a continuous stream of pure argon and the off gas was analysed continuously using an infrared (IR) gas analyser. Elemental analyses of samples of the reduced metal were performed chemically for its oxygen content using a LECO oxygen/nitrogen analyser. The extent of reduction was then determined at two temperatures 1200 °C and 1550 °C. Gas emission studies revealed the emission of large volumes of the reductant gas CO along with CO 2 . It is further demonstrated that post-consumer PU is effective at reducing iron oxide to produce metallic iron with complete reduction achieved in less than 4 min at 1550 °C. Keywords : Polyurethane, Composite Pellets, Infrared gas Analyser, LECO Carbon/Sulphur Analyser
Evaluation of Impact of Yarn Count and Stitch Length on Pilling, Abrasion, Shrinkage and Tightness Factor of 1 ? 1 Rib Cotton Knitted Fabrics
This study investigates the impact of yarn count and stitch length of 100% cotton knitted fabrics. 1 × 1 ribs structured fabrics were used in this research work. The stitch length 2.50 mm, 2.52 mm, 2.60 mm, 2.70 mm, 2.80 mm and 2.96 mm were used of the yarn count of 26Ne, 28Ne and 36Ne. The areal densities of the grey fabrics were in various amounts. The impacts of yarn count and stitch length were measured concerning pilling resistance, abrasion resistance, and shrinkage and tightness factor. The result showed that the fabric pilling grade decreased while number of cycle increased. Abrasion resistance decreased but length wise shrinkage increased despite the fact that the stitch length increased. The results also exposed that the tightness factor of the fabric increased with the increase of the stitch length in both dyeing and washing state and finished state compared to grey state for the yarn count 26Ne and homogeneous result not found for yarn count 28Ne and 36 Ne. Evaluation of Impact of Yarn Count and Stitch Length on Pilling, Abrasion, Shrinkage and Tightness Factor of 1 × 1 Rib Cotton Knitted Fabrics