Adsorption behavior of propylamine on activated carbon fiber surfaces as induced by oxygen functional complexes.
In this study, the surfaces of activated carbon fibers (ACFs) were modified by nitric acid to introduce surface oxygen complexes and to observe the influence of those complexes on the propylamine adsorption of the ACFs. It was found that the oxygen complexes including carboxylic and phenolic groups were predominantly increased, resulting in the increase of total surface acidity. However, the specific surface areas and the total pore volumes of the modified ACFs were decreased by 5-8% due to the increased blocking (or demolition) of micropores in the presence of newly introduced complexes. Despite the decrease of textural properties, it was found that the amount of propylamine adsorbed by the modified ACFs was increased by approximately 17%. From the XPS results, it was observed that propylamine reacted with strong or weak acidic groups, such as COOH or OH, on the ACF surfaces, resulting in the formation of pyrrolic-, pyridonic-, or pyridine-like structures.
Interactive effects of pore size control and carbonization temperatures on supercapacitive behaviors of porous carbon/carbon nanotube composites.
Porous carbon-based electrodes were prepared by carbonization with poly(vinylidene fluoride) (PVDF)/carbon nanotube (CNT) composites to further increase the specific capacitance for supercapacitors. The specific capacitance, pore size distribution, and surface area of the PVDF/CNT composites were measured, and the effect of the carbonization temperatures was examined. The electrochemical properties were examined by cyclic voltammetry, impedance spectroscopy, and galvanostatic charge-discharge performance using a two-electrode system in TEABF(4) (tetraethylammonium tetrafluoroborate)/acetonitrile as a non-aqueous electrolyte. The highest specific capacitance of ∼101 Fg(-1) was obtained for the samples carbonized at 600 °C. The pore size of the samples could be controlled to below 7 nm through the carbonization process. This suggests that micropores make a significant contribution to the specific capacitance due to improved charge transfer between the pores of the electrode materials and the electrolyte.
Immersive haptic interaction with media
New 3D video representations enable new modalities of interaction, such as haptic interaction, with 2D and 3D video for truly immersive media applications. Haptic interaction with video includes haptic structure and haptic motion for new immersive experiences. It is possible to compute haptic structure signals from 3D scene geometry or depth information. This paper introduces the concept of haptic motion, as well as new methods to compute haptic structure and motion signals for 2D video-plus-depth representation. The resulting haptic signals can be rendered using a haptic cursor attached to a 2D or 3D video display.