Preparation and performance of a novel core-shell Gel Polymer Electrolytes
A novel core-shell latex Gel Polymer Electrolytes (GPE) based on poly (methyl methacrylate-acrylonitrile -styrene) (P(MMA-AN-ST)) was prepared for applications in Li-ion batteries. The structure and the performance of the polymer and the GPE were characterized with FTIR, DSC/TG, TEM, SEM, LSV and CA. It is shown that the copolymer has a high thermal stability up to 320°C and the porous structure of the membrane was formed effectively. As-prepared gel polymer electrolytes exhibits a high ionic conductivity of 3.52×10−3 Scm−1 at 25°C and it is electrochemically stable up to 5.2V (vs. Li). This novel GPE can be potentially applied to the manufacture of PLBs.
Crystallinity and order of poly(ethylene oxide)/lithium triflate complex confined in nanoporous membranes
Abstract The confinement of poly(ethylene oxide), PEO, electrolyte in pores of 13, 35, 55 and 100 nm in diameter in nanoporous alumina membranes was seen to have effects on the ionic conduction properties. Specific conductivity values for the PEO/lithium triflate complex in the 13 and 35 nm pores, for temperatures below the melt temperatures, were increased by a factor of four compared to the non-confined polymer and the 55 and 100 nm pore systems. Thermal analysis data indicate the melting temperature for the PEO electrolyte in the pores is directly proportional to the pore size such that as the pore size of confinement is decreased, the T m decreases as well. The same behavior is seen for the amount of crystallinity, with less crystallinity being observed as the pores become smaller. Perhaps the observed conduction behavior could be attributed to less crystallinity. However, it is known that confinement of polyethers in pores results in stretching and ordering of the backbone and that such ordering can increase ion conduction. This ordering would seem to be the major factor involved in these results. The enhanced conduction only being seen in the 13 and 35 nm pores and not the 55 and 100 nm pores is attributed to the larger size for the latter which allows a more bulk-like behavior with less ordering.
Experimental investigation of the geotechnical properties and microstructure of lime-stabilized saline soils under freeze-thaw cycling
Abstract The Song-Nen Plain in northeastern China holds one of the three largest expanses of soda saline-alkali soil in the world. Due to its disadvantageous geotechnical properties, the saline soil in this area is unable to meet the needs of construction projects. This study evaluates the stabilizing effect of adding lime to such soils. Specifically, it investigates how the physicochemical and mechanical properties and microstructure of soda saline-alkali soil are altered by lime and how these changes are affected by both freeze-thaw cycling and the duration of curing. The results reveal that adding lime to saline soil transforms clay particles into sand and silt particles and causes the pore size distribution (PSD) to become bimodal, with small-pore and macropore populations. An increase in lime content leads to an increase in the unconfined compressive strength (UCS) but a gradual decrease in both the cation exchange capacity (CEC) and plastic index. Freeze-thaw cycles break up coarse particles and aggregate finer particles, increasing the diameter of macropores and decreasing the USC; however, the effect on specimens with >9% lime is negligible. It is further shown that the geotechnical properties of the soil change immediately after the addition of lime, indicating that the cation exchange reaction takes place very quickly. Furthermore, the pozzolanic reaction leads to an increase in the percentage of sand-sized particles and a decrease in porosity after 28 days of curing. Overall, these results indicate that it is feasible to use lime to improve the engineering properties of soda saline-alkali soil in this area.