Electrodeposited CuInSe2 Thin Film Junctions
We have investigated thin films and junctions based on copper indium diselenide (CIS) which have been grown by electrochemical deposition. CIS is a leading candidate for use in polycrystalline thin film photovoltaic solar cells. Electrodeposition is a cost-effective method for producing thin-film CIS. We have produced both p and n type CIS thin films from the same aqueous solution by simply varying the deposition potential. A CIS pn junction was deposited using a step-function potential. Stoichiometry of the single layer films was determined by energy dispersive spectroscopy. Carrier densities of these films increased with deviation from stoichiometry, as determined by the capacitance versus voltage dependence of Schottky contacts. Optical bandgaps for the single layer films as determined by transmission spectroscopy were also found to increase with deviation from stoichiometry. Rectifying current versus voltage characteristics were demonstrated for the Schottky barriers and for the pn junction.
SYNTHESIS AND CHARACTERIZATION OF P-TYPE COPPER INDIUM DISELENIDE ( CIS ) NANOWIRES EMBEDDED IN POROUS ALUMINA TEMPLATES Sri
OF THESIS Synthesis and Characterization of P-type Copper Indium Diselenide (CIS) Nanowires embedded in Porous Alumina templates This work focuses on a simple template assisted approach for fabricating I-III-VI semiconductor nanowire arrays. Vertically aligned nanowires of p-CIS of controllable diameter and thickness are electrodeposited, from an acidic electrolyte solution, inside porous aluminum templates using a three electrode set up with saturated calomel electrode as the reference. AAO template over ITO-glass was used as starting template for the device fabrication. The deposited CIS is annealed at different temperatures in a reducing environment (95% Ar+ 5% H2) for 30 minutes. X-ray diffraction of the nanowires showed nanocrystalline cubic phase structures with a strong orientation in the <112> direction. The effective bandgap of the deposited CIS nanowires determined using the Near Infrared (NIR) Spectrometer was found to be 1.07eV. The type of CIS electrodeposited inside the porous alumina template is determined to be p-type from the Schottky diode obtained with ITO-CIS-Au structure. Schottky diodes were characterized and analyzed at room temperature.
Electrical properties of CuInSe2 single crystals
Abstract Various bulk electrical properties and device characteristics have been measured. It has been shown that the majority carrier type is dependent on crystal stoichiometry. Mobilities of 660 cm2/V sec and 30 cm2/V sec have been measured for n-and p-type samples, respectively. Rectifying contacts and p-n junctions have been investigated by small signal analysis and the associated doping levels and equilibrium band diagrams have been determined. Photovoltage measurements on rectifying contacts have shown that the band-gap has a value of 0.95 ± 0.01eV.