Development of Oxidation Protection Coatings for Gamma Titanium Aluminide Alloys
Metallic material systems play a key role in meeting the stringent weight and durability requirements for reusable launch vehicle (RLV) airframe hot structures. Gamma titanium aluminides (gamma-TiAl) have been identified as high-payoff materials for high-temperature applications. The low density and good elevated temperature mechanical properties of gamma-TiAl alloys make them attractive candidates for durable lightweight hot structure and thermal protection systems at temperatures as high as 871 C. However, oxidation significantly degrades gamma-TiAl alloys under the high-temperature service conditions associated with the RLV operating environment. This paper discusses ongoing efforts at NASA Langley Research Center to develop durable ultrathin coatings for protecting gamma-TiAl alloys from high-temperature oxidation environments. In addition to offering oxidation protection, these multifunctional coatings are being engineered to provide thermal control features to help minimize heat input into the hot structures. This paper describes the coating development effort and discusses the effects of long-term high-temperature exposures on the microstructure of coated and uncoated gamma-TiAl alloys. The alloy of primary consideration was the Plansee alloy gamma-Met, but limited studies of the newer alloy gamma-Met-PX were also included. The oxidation behavior of the uncoated materials was evaluated over the temperature range of 704 C to 871 C. Sol-gel-based coatings were applied to the gamma-TiAl samples by dipping and spraying, and the performance evaluated at 871 C. Results showed that the coatings improve the oxidation resistance, but that further development is necessary.
Oxidation protection of gamma-titanium aluminide using glass-ceramic coatings (vol 203, pg 1797, 2009)
Abstract γ-TiAl intermetallic alloys are presently considered an efficient structural material for advanced turbine blades and aero-engine components due to their various advantages compared to the traditionally used superalloys. However, their poor oxidation resistance at temperatures > 750 °C severely limits their wider application. The present study dealt with the improvement of oxidation resistance of this alloy by applying impervious glass–ceramic coatings by vitreous enameling technique. Results showed that MgO–SiO 2 –TiO 2 glass–ceramic coating could offer excellent oxidation resistance to γ-TiAl at 800 °C even up to 100 h with negligible weight gain (~ 0.10 mg/cm 2 ) compared to that of the bare alloy (~ 1.3 mg/cm 2 ). The coatings those were belonging from BaO–MgO–SiO 2 , ZnO–Al 2 O 3 –SiO 2 and BaO–SiO 2 systems also extend appreciable improvement in the oxidation resistance of the alloy at 800 °C up to 100 h. At further higher temperature such as at 1000 °C, the ABK-13 and ABK-103 glass–ceramic coatings offered significant protection to the alloy up to 25 h of exposure in air with minimum weight gain (~ 0.34 mg/cm 2 ). However, after that the coated layers started to peel off from the alloy surface.
Turbine blade temperature calculation and life estimation - a sensitivity analysis
Abstract The overall operating cost of the modern gas turbines is greatly influenced by the durability of hot section components operating at high temperatures. In turbine operating conditions, some defects may occur which can decrease hot section life. In the present paper, methods used for calculating blade temperature and life are demonstrated and validated. Using these methods, a set of sensitivity analyses on the parameters affecting temperature and life of a high pressure, high temperature turbine first stage blade is carried out. Investigated uncertainties are: (1) blade coating thickness, (2) coolant inlet pressure and temperature (as a result of secondary air system), and (3) gas turbine load variation. Results show that increasing thermal barrier coating thickness by 3 times, leads to rise in the blade life by 9 times. In addition, considering inlet cooling temperature and pressure, deviation in temperature has greater effect on blade life. One of the interesting points that can be realized from the results is that 300 hours operation at 70% load can be equal to one hour operation at base load.