The effect of quenching and defects size on the HCF behaviour of Boron steel
Abstract This work investigates the effect of natural and artificial surface defects and quenching on the fatigue strength of a Boron steel (22MnB5). A vast experimental campaign has been undertaken to study the high cycle fatigue behaviour and more specifically the fatigue damage mechanisms observed in quenched and untreated materials, under different loading conditions and with differents artificial defects sizes (from 25 μm to 370 μm radius). In order to test the sheet metal in shear an original test apparatus is used. The critical defect size is determined to be 100 ± 50 μm. This critical size does not appear to depend on the loading type or the microstructure of the material (i.e. ferritic–perlitic or martensitic). However, for large defects, the quenched material is more sensitive to the defect size than the untreated material. For a defect size range of 100–300 μm the slope of the Kitagawa–Takahashi diagram is approximately −1/3 and −1/6 for the quenched and untreated materials respectively. A probabilistic approach that leads naturally to a probabilistic Kitagawa type diagram is developed. This methodology can be used to explain the relationship between the influence of the heat treatment and the defect size on the fatigue behaviour of this steel.
Simulation of the Kitagawa-Takahashi diagram using a probabilistic approach for cast Al-Si alloys under different multiaxial loads
Abstract This article describes a microstructural-based high cycle fatigue strength modelling approach applied to different cast Al-Si alloys used in an automotive context. Thank to different casting processes (gravity die casting and lost foam casting), associated with several heat treatment (T7 and Hot Isostatic Pressing-HIP), three alloys with very different microstructures have been obtained. In a vast experimental campaign undertaken to investigate the fatigue damage mechanisms governing these alloys under different multiaxial loading conditions, it was shown that the principal crack initiation mechanisms for the porosity-free alloy are either the formation of persistent slip bands (PSB) or the rupture and/or debonding of eutectic particles. For the porosity-containing alloys, the fatigue damage is always controlled by crack growth from pores. In order to take into account these fatigue damage mechanisms, a probabilistic model using a combination of the Dang Van and a modified LEFM criteria is proposed. The modified LEFM criterion is able to take into account the influence of the grain size on the threshold of the stress intensity factor. It is shown that for the porosity-free alloy, the predictions are good for combined tension-torsion loads with R = - 1 . However, because the crack initiation mechanisms are not the same depending on the hydrostatic stress, the predictions are non-conservative for the uniaxial and equibiaxial tension loads with R = 0.1 . For the porosity-containing alloys, the predictions are very good for the uniaxial, combined tension-torsion and equibiaxial tension loads with both R = - 1 and R = 0.1 . As observed experimentally, the proposed model can also predict a more pronounced effect of casting porosity for the uniaxial and combined tension-torsion loads, when compared to pure torsion loads.
Neutron Residual Stress Measurements on Rail Sections for Different Production Conditions
Rail sectioning with subsequent neutron diffraction experiments has been used to assess residual stresses in the rails. In this study we present the results of neutron stress measurements performed at the NIST Center for Neutron Research (NCNR) on rail sections from rails that were produced under various conditions. Specifically, these are air-cooled, air-cooled and roller-straightened, head-hardened and head-hardened and roller-straightened. More significantly, a head-hardened and roller-straightened rail was also studied after service to elucidate evolution of the service-induced residual stresses. In the latter case both a transverse-cut slice and the central region of a 0.53 m long piece were studied. Measurements on this piece are the first in which triaxial stresses have been determined for an intact rail. Neutron strain measurements with 3×3×3 mm3 spatial resolution were successfully employed for transversally cut slices to verify the difference in the stress state depending on the production process. Although examination of slices allows determination of only two-dimensional stresses in the plane of the slice, additional measurements on obliquely-cut slices, which were also carried out, and utilization of FEM gives the possibility of reconstructing the full triaxial stress distribution. Together, these approaches provide a better understanding of rail fabrication and the possibility of improving the durability and safety of rails in the future.Copyright © 2004 by ASME