Properties of PAN Fibers Solution Spun into a Chilled Coagulation Bath at High Solvent Compositions
In this work, multifilament, continuous polyacrylonitrile (PAN) fiber tow was solution spun mimicking industrial processing at the small pilot scale (0.5 k tow), while carefully altering the composition of the coagulation bath, in order to determine the effect on the resulting fiber shape, density, orientation, and tensile properties at varying points in the spinning process. Novel here are the abnormally high coagulation bath solvent compositions investigated, which surpass those often reported in the literature. In addition, the coagulation bath was maintained at a slightly chilled temperature, contrary to reported methods to produce round fibers. Further, by altering the composition of the bath in a step-wise fashion during a single spinning run, variations in all other process parameters were minimized. We found that with increasing solvent composition in the coagulation bath, the fibers not only became round in cross section, but also became smaller in diameter, which persisted down the spin line. With this decrease in diameter, all else equal, came an accompanying increase in apparent fiber density via a reduction in microvoid content. In addition, molecular orientation and tensile properties also increased. Therefore, it was found that inadequate understanding of the coagulation bath effects, and spinning at low coagulation bath solvent compositions, can hinder the ability of the fiber to reach optimum properties.
Effects of different coagulation conditions on polyacrylonitrile fibers wet spun in a system of dimethylsulphoxide and water
Polyacrylonitrile (PAN) precursors were prepared by the wet spinning way. The effects of the coagulation conditions, such as coagulation temperature, coagulation ratio, and coagulation concentration, are discussed in detail. While keeping the coagulation bath concentration constant, as the coagulation bath temperature increased, the cross section deviated less from a circular form, and the as-spun fiber diameter decreased. Measurement to the rate of the boundary movement has been calculated depending on the coagulation rate. While keeping the coagulation bath temperature constant, high coagulation bath concentration can cause more coagulant to diffuse into the solution to the polymer precipitated consequently, which led to a faster coagulation rate. The as-spun fiber from high coagulation concentration was compacted than those from low concentration. The character of the formed structure reflected the system mobility and capability to crystallize. Improvement in fiber density in the as-spun fiber resulted in improvements in the tensile strength of the as-spun fiber. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 104: 3723–3729, 2007
Inhibition of Mild Steel Corrosion Using L-tryptophan and Synergistic Surfactant Additives
The corrosion inhibition characteristics of nitrogen containing amino acid L-tryptophan on mild steel in 0.1 M HCl solution, in the temperature range of 30-50 o C, was studied by weight loss and potentiodynamic polarization measurements. L-tryptophan significantly reduces the corrosion rates of mild steel; the maximum inhibition efficiency being 83% at 50 o C in presence of inhibitor concentration of 500 ppm. The effect of the addition of very small concentrations of anionic surfactant, sodium dodecyl sulfate (SDS), and of cationic surfactant, cetyl trimethyl ammonium bromide (CTAB), on the corrosion inhibition behavior of L-tryptophan was also studied. The inhibition efficiency (IE) of L-tryptophan significantly improved in presence of both surfactants. The effect of SDS and CTAB on the corrosion inhibition behavior of L-tryptophan appears to be synergistic in nature, the values of synergism parameter being greater than unity. The adsorption of inhibitors on mild steel surface obeyed Langmuir’s adsorption isotherm. The calculated thermodynamic parameters for adsorption reveal a strong interaction between the inhibitors and the mild steel surface. The results obtained by electrochemical studies are consistent with the results of the weight loss measurements. L-tryptophan acts more anodic than cathodic inhibitor.