Polyester fibres structure modification using some organic solutions
The treatment causes only minor decrease in fi bre, i.e. yarn strength, while breaking elongation increases signifi cantly, almost up to 150 % in comparison to the untreated sample. Organic solvents, i.e. plasticizer solutions in the organic solvents mixture infl uence fi bre properties in a very favorable way, i.e. they can enable better dyeing, better moisture absorption, easier treatment in further phases of textile products manufacture and generally better usability. X-ray structural analysis was used to examine the infl uence of the treatment of polyester fi bres in the form of fi lament yarn, fi neness 75/26 dtex, with solutions 0.3, 0.6 and 0.9 % hydroquinone and α-naphtole in the solvent mixture which contained chlorophorm and methanol (solubility parameter δ=11.7) on changing of crystalline degree and crystallite size. It was found that treated fi bres showed sharper refl exion on diffractograms than untreated ones, i.e. they showed higher crystalline degree but smaller crystallite size.
Solvent‐ and glow‐discharge‐induced surface wetting and morphological changes of poly(ethylene terephthalate) (PET)
The effects of argon glow discharge and selected organic solvents on the surface wettability of poly(ethylene terephthalate) (PET) and on the wettability decay of glow discharged PET films were studied. Glow discharge in argon (30 W/1 min) drastically reduced the initial water contact angle (CA) measurement of PET from 67.0 to 26.2°. The glow-discharge-induced wetting, however, decayed during the first 7 days and stabilized at 33.1°. Treatments in dimethyl sulfoxide, dimethyl formamide, pyrdine, and water at 80°C caused some improvement in surface wettability as shown by decreases of water CAs in the range of 53–56°. When the solvent and glow discharge treatments were applied consecutively on PET, additive effects on improving surface wettability were observed. The stabilized water CAs of the solvent-and-glow-discharged films ranged from 25.0 to 32.1° depending upon the solvent type. The solvent treatments prior to glow discharge either reduced the extent of CA decay or the time taken to reach stabilization on PET films. Scanning electron microscopic evaluation showed no difference between the solventtreated and the untreated PET surfaces, but a finely etched surface was observed on the glow discharged PET at a 40,000 magnification and above. The distinctly different surface of the DMSO-and-glow-discharged PET indicated that morphological changes on PET surface were induced by the solvent.
CNC Desktop Vertical Machining Bench Design and Cooling Fluid Application
Today's manufacturing technologies, the human work force is used and at least a minimum level of margin of error is used in CNC machines. Desktop CNC machine tools and CNC machine tools are developed in parallel with the development of personal computers. This study provides CNC training institutions for education, small and medium-sized enterprises for commercial purposes use the low-cost desktop machine has been designing and manufacturing of CNC vertical machining was carried out. Desktop CNC machine tools and production capacity to handle the kind of material was applied to increase the cooling fluid. Through A199 and Fe37 the cooling fluid application desktop CNC machine tools, such as processing of materials that are difficult to successfully processed. Keywords—CNC, Desktop CNC Machine, CNC Design