Basalt FRP Spike Repairing of Wood Beams
This article describes aspects within an experimental program aimed at improving the structural performance of cracked solid fir-wood beams repaired with Basalt Fiber Reinforced Polymer (BFRP) spikes. Fir wood is characterized by its low density, low compression strength, and high level of defects, and it is likely to distort when dried and tends to fail under tension due to the presence of cracks, knots, or grain deviation. The proposed repair technique consists of the insertion of BFRP spikes into timber beams to restore the continuity of cracked sections. The experimental efforts deal with the evaluation of the bending strength and deformation properties of 24 timber beams. An artificially simulated cracking was produced by cutting the wood beams in half or notching. The obtained results for the repaired beams were compared with those of solid undamaged and damaged beams, and increases of beam capacity, bending strength and of modulus of elasticity, and analysis of failure modes was discussed. For notched beams, the application of the BFRP spikes was able to restore the original bending capacity of undamaged beams, while only a small part of the original capacity was recovered for beams that were cut in half.
Screws with continuous threads in timber connections
Screws, bolts and dowels loaded perpendicular to the fastener axis are all dowel-type fasteners, whose load-carrying capacity in timber-to-timber connections may be determined based on Johansen ́s yield theory (Johansen, 1949). The ultimate load of joints with dowel-type fasteners loaded perpendicular to the fastener axis is limited by the embedding strength of the timber members and the bending capacity of the fasteners. Exploiting the withdrawal capacity of long screws with continuous threads leads to increased load-carrying capacities and hence more economic connections. In order to avoid bending of screws they are not placed perpendicular to the interface between the members to be connected but arranged under an angle of about 45°. The load is then transferred by a truss-like system where the screw is loaded in tension and the contact surface between the members in compression. The paper presents a comparison between the test results of connections with inclined screws and fasteners loaded perpendicular to their axis and shows a number of opportunities for connections with inclined screws.
Recent progress in engineering near-infrared persistent luminescence nanoprobes for time-resolved biosensing/bioimaging
Persistent luminescence nanoprobes (PLNPs) can remain luminescent after ceasing excitation. Due to the ultra-long decay time of persistent luminescence (PersL), autofluorescence interference can be efficiently eliminated by collecting PersL signal after autofluorescence decays completely, thus the imaging contrast and sensing sensitivity can be significantly improved. Since near-infrared (NIR) light shows reduced scattering and absorption coefficient in penetrating biological organs or tissues, near-infrared persistent luminescence nanoprobes (NIR PLNPs) possess deep tissue penetration and offer a bright prospect in the areas of in vivo biosensing/bioimaging. In this review, we firstly summarize the design of different types of NIR PLNPs for biosensing/bioimaging, such as transition metal ions-doped NIR PLNPs, lanthanide ions-doped NIR PLNPs, organic molecules-based NIR PLNPs, and semiconducting polymer self-assembled NIR PLNPs. Notably, organic molecules-based NIR PLNPs and semiconductor self-assembled NIR PLNPs, for the first time, were introduced to the review of PLNPs. Secondly, the effects of different types of charge carriers on NIR PersL and luminescence decay of NIR PLNPs are significantly emphasized so as to build up an in-depth understanding of their luminescence mechanism. It includes the regulation of valence band and conduction band of different host materials, alteration of defect types, depth and concentration changes caused by ion doping, effective radiation transitions and energy transfer generated by different luminescence centers. Given the design and potential of NIR PLNPs as long-lived luminescent materials, the current challenges and future perspective in this rapidly growing field are also discussed.