EFFECT OF MAGNESIUM ENHANCEMENT ON MECHANICAL PROPERTY AND WEAR BEHAVIOUR OF LM6 ALUMINUM ALLOY
For last several decades aluminium and aluminium alloys are widely used in automotive industries because for their favourable properties like low density (about 2700 Kg/m 3 ), good malleability, high formability, high corrosion resistance and high electrical and thermal conductivity. High machinability and workability of aluminium alloys are prone to porosity due to gases dissolved during melting processes. However, in the engineering application pure aluminium and its alloys still have some problems such as relatively low strength, unstable mechanical properties and low wear resistance. The microstructure can be modified and mechanical properties, wear resistance can be improved by alloying, cold working and heat treatment. In this regards, the present paper reports the influences of enhancement of magnesium contents on the mechanical properties and wear behavior of LM 6 aluminum alloy. Index Terms: LM 6 Aluminum alloy, wear rate 1. Introduction: Aluminium and aluminium alloy are gaining huge industrial significance because of their outstanding combination of mechanical, physical and tribological properties over the base alloys. These properties include high specific strength, high wear and seizure resistance, high stiffness, better elevated temperature strength, controlled thermal expansion coefficient and improved damping capacity (1). These properties obtained through addition of alloying elements, cold working and heat treatment. Alloying elements are selected based on their effects and suitability. For the purpose of understanding their effects and importance, alloying elements for majority of alloys are best classified as major and minor elements, microstructure modifiers or impurities, however the impurity elements in some alloys might be major elements in others (2). LM6 is one of the most important Aluminium alloy falls under Aluminium - Silicon alloying system in which aluminium is the predominant metal and high levels of silicon (4% to 13%) are added that contributes to give good casting characteristics and increases fluidity, by which we can produce castings of thick as well as thin sections according to the required design. Other typical alloying elements are Copper, Magnesium, Manganese, Silicon, Zinc, Iron, Nickel, Lead and Tin.
Effects of magnesium on wear characteristics of SiC and AI203 reinforced aluminum metal matrix composites
ii Chapter
SR topography of plastically deformed Fe-Si bicrystals - observation in situ and post mortem
SR reflection topography was applied to study the interaction of slip dislocations with the grain boundaries in Fe-4at%Si bicrystals deformed by compression. Three experimental settings with either a white or monochromatic beam were used and the corresponding orientation contrast analysed. Dislocation transmission through the grain boundary was observed in bicrystals with favourable geometry of the slip systems.