Characterization of Ion Implanted Silicon Annealed with a Graphite Radiation Source
A Varian IA-200 isothermal annealer has been used to anneal ion implantation damage and electrically activate dopants in As and B implanted silicon with minimal redistribution of the impurity. The anneal occurs in vacuum using infrared radiation from a resistively heated sheet of graphite. Good quality anneals of /sup 11/B implanted samples have been obtained with minimal boron diffusion. Arsenic implanted wafers have also be annealed with excellent results except for a substantial loss of As which occurs unless the wafer has an SiO/sub 2/ cap. The anneal quality of (100) wafers was independent of dose, however, the anneal quality of the (111) wafers improved with increasing As dose.
Anomalous Annealing Behavior of Arsenic Implanted Silicon as a Function of Dose and Energy
Anomalous annealing behavior of damage in As implanted Si has been investigated by channeling effect measurements. Room temperature As implants with doses from 1014 to 2 × 1016cm-2 at energies ranging from 50 to 250 keV into Si were annealed over the range of 600°C to 1100°C. Anneal temperatures ≥ 950°C reduce the disorder for ion doses of 0.5 to 1 × 1016 cm-2 at energies between 50 and 250 keV. Anomalously high residual disorder was found for the intermediate doses of 2 × 1014 to 2 × 10/cm2 implanted above 100 keV. For this intermediate dose, annealing of implants performed at liquid nitrogen temperatures did not show significant reduction in this damage. However implants at 200° to 300°C indicate a lower amount of damage compared to the room temperature implants.
Traceability strategy for gear-pitch-measuring instruments: development and calibration of a multiball artifact
There is a strong demand to ensure the traceability of gear-measuring instruments (GMIs). We propose a multiball artifact (MBA) for the evaluation of pitch-measuring accuracy. The aim of the MBA is to transfer the minimum uncertainty from a calibrated value at the National Metrology Institute of Japan (NMIJ) to a measured value of GMIs at a shop floor. The MBA is composed of equally spaced high-accuracy balls around an axis. The pitch-measuring accuracy of GMIs is evaluated by measuring the angular pitch deviation of the balls instead of the angular pitch deviation of a gear. We calibrated the angular pitch deviation using a coordinate measuring instrument (CMM) at the NMIJ and adapting a multiple-orientation technique. We proposed a calibration strategy of the angular pitch deviation. The calibration value of the pitch deviation for the MBA at the NMIJ was obtained with a measurement uncertainty (U95) of 0.2 µm. We evaluated the pitch-measuring accuracy of a GMI using the calibrated MBA. Each value of U95 for the cumulative and single pitch deviations for the left and right flanks was less than or equal to 0.5 µm. The small uncertainty was transferred from the NMIJ to the GMI.