X-ray diffraction study of K3NdSi7O17: a new framework silicate with a linear Si-O-Si bond.
Hydrothermal investigations in the high-silica region of the K(2)O-Nd(2)O(3)-SiO(2) system, carried out in a search for novel fast-ion conductors (FICs), yielded the new compound tripotassium neodymium heptasilicate, K(3)NdSi(7)O(17). Single-crystal X-ray methods revealed that K(3)NdSi(7)O(17) crystallizes in space group P3, has lattice constants a = 16.131 (2) and c = 7.7146 (19) A, Z = 4, and 22 atoms in the asymmetric unit. Refinement was carried out to a residual, R(F), of 0.0253 and a weighted residual, wR(F(2)), of 0.0702 using anisotropic displacement parameters for all atoms. The silicate anion forms an interrupted framework, within which both Nd octahedra and K polyhedra are situated. The structure is unusual in that it contains a symmetry-constrained Si-O-Si bond angle of 180 degrees. No isomorphs to K(3)NdSi(7)O(17) are known.
High-pressure synthesis and structural investigation of H3P8O8N9: a new phosphorus(V) oxonitride imide with an interrupted framework structure.
The first crystalline phosphorus oxonitride imide H(3)P(8)O(8)N(9) (=P(8)O(8)N(6)(NH)(3)) has been synthesized under high-pressure and high-temperature conditions. To this end, a new, highly reactive phosphorus oxonitride imide precursor compound was prepared and treated at 12 GPa and 750 °C by using a multianvil assembly. H(3)P(8)O(8)N(9) was obtained as a colorless, microcrystalline solid. The crystal structure of H(3)P(8)O(8)N(9) was solved ab initio by powder X-ray diffraction analysis, applying the charge-flipping algorithm, and refined by the Rietveld method (C2/c (no. 15), a=1352.11(7), b=479.83(3), c=1820.42(9) pm, β=96.955(4)°, Z=4). H(3)P(8)O(8)N(9) exhibits a highly condensed (κ=0.47), 3D, but interrupted network that is composed of all-side vertex-sharing (Q(4)) and only threefold-linking (Q(3)) P(O,N)(4) tetrahedra in a Q(4)/Q(3) ratio of 3:1. The structure, which includes 4-ring assemblies as the smallest ring size, can be subdivided into alternating open-branched zweier double layers {oB,2(2)(∞)}[(2)P(3)(O,N)(7)] and layers containing pairwise-linked Q(3) tetrahedra parallel (001). Information on the hydrogen atoms in H(3)P(8)O(8)N(9) was obtained by 1D (1)H MAS, 2D homo- and heteronuclear (together with (31)P) correlation NMR spectroscopy, and a (1)H spin-diffusion experiment with a hard-pulse sequence designed for selective excitation of a single peak. Two hydrogen sites with a multiplicity ratio of 2:1 were identified and thus the formula of H(3)P(8)O(8)N(9) was unambiguously determined. The protons were assigned to Wyckoff positions 8f and 4e, the latter located within the Q(3) tetrahedra layers.
Proprietes d'echange d'ions des pyrochlores AB2O6—I Preparation et etude structurale de nouveaux pyrochlores AMWO6 . H2O (A = Li, Na; M = Nb, Ta, Sb)
Resume Les proprietes d'echange d'ions appliquees aux pyrochlores H 3 O M WO 6 ( M = Nb, Ta, Sb) ont permis d'isoler six nouveaux pyrochlores cubiques AM WO 6 . H 2 O ( A = Li, Na; M = Nb, Ta, Sb). Les caracteristiques structurales de ces phases ont ete determinees et discutees.