Optical loss stability of a fiber cable under lateral force and optimum design of the coated fiber structure.
Optical loss increase characteristics under lateral force were investigated to determine the load limit for coated fiber. Plastic deformation of the coating was analyzed, and the loss increase was found to occur in the large deformation region beyond a limit theoretically determined using structural dimensions (diameter and thickness) and the material constant of the coating. The optimum coating structure for preventing loss increase has been designed by introducing the result of the lateral deformation limit as well as fiber stress induced by the lateral force and fiber strain at low temperature. The nylon outer and silicone layer diameters are 0.9 and 0.4 mm, respectively.
Infrared loss increase phenomenon of coated optical fibers at high temperatures
The loss increase phenomenon of coated optical fibers at high temperature has been studied. The wavelength dependent loss increase, observed for plastic-coated fibers at 200°C, is found to be irreversible. During heating, the absorption peak of second overtone of Ge-OH preferentially appeared. The dependence of the loss increase on temperature, heating time, and dopant is also examined. The loss increase level is strongly dependent on phosphorous concentration. The experimental results indicate that the loss increase is caused by chemical reactions between fiber constituent materials and hydrogen generated from coating materials. It is also confirmed that the heating test of secondary coated fiber is a practical, useful method to evaluate the hydroxyl loss increase of optical fibers.
Single-mode optical fiber cable.
A single-mode optical fiber cable was manufactured; loss increase characteristics due to cabling were evaluated. The existence of wide V-value regions without cabling loss increases is shown by a suitable selection of fiber parameters and optical wavelengths. A selection method for fiber parameters, which minimizes cabling and splicing loss increases, is discussed. Selected values are Delta = 0.2% and V = 2.2, based on experimental results.