Experimental and Numerical Studies on Self-Propagating High-Temperature Synthesis of Ta 5 Si 3 Intermetallics
Formation of Ta5Si3 by self-propagating high-temperature synthesis (SHS) from elemental powder compacts of Ta:Si = 5:3 was experimentally and numerically studied. Experimental evidence showed that the increase of either sample density or preheating temperature led to the increase of combustion wave velocity and reaction temperature. The apparent activation energy, Ea ≈ 108 kJ/mol, was determined for the synthesis reaction. Based upon numerical simulation, the Arrhenius factor of the rate function, K0 = 2.5 × 10 s, was obtained for the 5Ta + 3Si combustion system. In addition, the influence of sample density on combustion wave kinetics was correlated with the effective thermal conductivity (keff) of the powder compact. By adopting 0.005 ≤ keff/kbulk ≤ 0.016 in the computation model, the calculated combustion velocity and temperature were in good agreement with experimental data of the samples with compaction densities between 35% and 45% theoretical maximum density (TMD).
An overview of powder processing of silicides and their composites
Abstract The use of powders to prepare fully dense silicides and their composites is reviewed. Since most of the techniques are well known, we concentrate on recent developments in this field, including the effects of processing techniques on composition, microstructure and mechanical properties. The use of hybrid processes to produce silicides is described, as are hybrid materials resulting from these processes. Included in the latter are functionally graded materials (FGM). The paper concludes with a brief discussion of in-situ melt processing as a competitive means to produce aligned composite structures
Evaluation of Impact of Yarn Count and Stitch Length on Pilling, Abrasion, Shrinkage and Tightness Factor of 1 ? 1 Rib Cotton Knitted Fabrics
This study investigates the impact of yarn count and stitch length of 100% cotton knitted fabrics. 1 × 1 ribs structured fabrics were used in this research work. The stitch length 2.50 mm, 2.52 mm, 2.60 mm, 2.70 mm, 2.80 mm and 2.96 mm were used of the yarn count of 26Ne, 28Ne and 36Ne. The areal densities of the grey fabrics were in various amounts. The impacts of yarn count and stitch length were measured concerning pilling resistance, abrasion resistance, and shrinkage and tightness factor. The result showed that the fabric pilling grade decreased while number of cycle increased. Abrasion resistance decreased but length wise shrinkage increased despite the fact that the stitch length increased. The results also exposed that the tightness factor of the fabric increased with the increase of the stitch length in both dyeing and washing state and finished state compared to grey state for the yarn count 26Ne and homogeneous result not found for yarn count 28Ne and 36 Ne. Evaluation of Impact of Yarn Count and Stitch Length on Pilling, Abrasion, Shrinkage and Tightness Factor of 1 × 1 Rib Cotton Knitted Fabrics