Computational modeling of accelerating corrosion in primary coolants of a typical PWR
High temperature and pressure environment along with large neutron and gamma-ray flux lead to significantly large corrosion in the stainless steel used in the primary coolant circuit of pressurized water reactors (PWRs). The corrosion products become activated in the reactor core upon circulation. Corrosion rate depends on reactor power and it can be a linear as well as a nonlinear function of time. Computer simulation offers a novel approach to study the effect of corrosion acceleration on coolant activity under transient conditions. We present two related mathematical models for corrosion acceleration under high temperature and flow rate transient conditions. In the first part of the work, we have formulated a mathematical model based on a system of coupled first order ordinary differential equations governing the isotopic concentration. In the second part, flow rate transients have been forced through non-homogeneous conditions. Numerical simulations show that for Na-24, Mn-56, Fe-59, Co-60 and Mo-99, the values of specific activities approach the equilibrium value fairly rapidly under normal operating conditions. Spikes are observed in the specific activity values of the primary coolant when corrosion acceleration and flow rate transients are employed in the model. Both the height and time of these spikes has been found to depend on the value of acceleration in corrosion.
Measurements of radioiodine species in samples of pressurized water reactor coolant
Samples of primary coolant at two pressurized water reactors in the United States have been collected and analyzed to determine the fraction of the radioiodine present in volatile forms. The volatile species, I{sup 2} and organic iodides, would be available for prompt release following a steam generator tube rupture (SGTR) accident, which overpressurizes the secondary coolant system and causes venting to the atmosphere. Coolant samples were collected at full power, during power reduction at the start of an outage, and up to 48 h after shutdown. Radioiodine concentrations spiked as power was decreased, and an increase in the volatile species fraction to {approximately}20% was seen with 2 h of shutdown. A second peak of 30 to 40% volatile species occurred at {approximately} 1.5 days after shutdown, but is not significant for SGTR accidents.
A New Vacuum Pressure Infiltration CFRP Method and Preparation Experimental Study of Composite
In order to prepare a carbon-fiber-reinforced polymer composite (CFRP) with ideal microstructure and properties, a new vacuum pressure infiltration CFRP method is proposed based on an analysis of existing CFRP preparation process methods. Research on composite material preparation systems was carried out by using this new method principle. The system mainly includes a fiber pre-forming module, a vacuum heating infiltration module, a hot-press curing molding module, and a data acquisition control module. Under the conditions of natural curing at 0 MPa + 6 h + 25 °C, vacuum heating curing at –0.05 MPa + 30 min + 80 °C, and hot-press curing at 0.7 MPa + 5 min + 50 °C, a two-dimensional (2D) CFRP with excellent microstructure and properties was successfully prepared. Observing the microstructure of the prepared composite material, it can be found that the inside of the composite material was sufficiently and uniformly infiltrated, and common preparation defects such as holes and delamination were effectively controlled. Through the performance test, the bending strength of the material reached 790 MPa.