Study on Paper-Based Fiberboard and Vacuum Treatment
According to the required fiber quality and the technical conditions of manufacturing fiberboard, the technology on paper-based fiberboard manufacturing and vacuum treatment was studied. After thorough investigation, the optimum technical conditions have been gained as follows: hot pressing temperature 160¿, hot pressing time 6 min, forming pressure 11MPa and the quantity of adhesive 10 percent. After vacuum treatment by the steam jet system in conditions as chamber below 700 Pascal, temperature in chamber 80¿, treatment time two hours, the contained proportion and emission quantity of the urea formaldehyde resin meet the requirements of GBT11718-1999. In addition to this, the mechanical properties of the paper-based fiberboard are greatly improved at the same time.
Canola straw as a bio-waste resource for medium density fiberboard (MDF) manufacture.
Canola straw as an agricultural residue has been investigated for MDF production. The variables were steaming time (2, 5 and 8 min), the resin content (9% and 11%), and press time (4 and 6 min). Common physical and mechanical properties of experimental boards including modulus of rupture (MOR), modulus of elasticity (MOE), internal bond strength (IB) and thickness swelling (TS) were measured. Fiber properties of canola straw including length, diameter and cell wall thickness were determined. The results showed that all the tested mechanical properties improved with the increase of steaming time level. The results were close to the minimum requirements of MDF specified in the ANSI A208.2 standard. Dimensional stability of the MDFs improved as adhesive content increased. The IB values are positively affected by the increase of press time. MDF properties made from canola straw possess acceptable qualities as compared to those made from other non-wood plants. Furthermore, the fiber dimensions of canola straw were also in the range of reported values in hardwoods.
Neutron Residual Stress Measurements on Rail Sections for Different Production Conditions
Rail sectioning with subsequent neutron diffraction experiments has been used to assess residual stresses in the rails. In this study we present the results of neutron stress measurements performed at the NIST Center for Neutron Research (NCNR) on rail sections from rails that were produced under various conditions. Specifically, these are air-cooled, air-cooled and roller-straightened, head-hardened and head-hardened and roller-straightened. More significantly, a head-hardened and roller-straightened rail was also studied after service to elucidate evolution of the service-induced residual stresses. In the latter case both a transverse-cut slice and the central region of a 0.53 m long piece were studied. Measurements on this piece are the first in which triaxial stresses have been determined for an intact rail. Neutron strain measurements with 3×3×3 mm3 spatial resolution were successfully employed for transversally cut slices to verify the difference in the stress state depending on the production process. Although examination of slices allows determination of only two-dimensional stresses in the plane of the slice, additional measurements on obliquely-cut slices, which were also carried out, and utilization of FEM gives the possibility of reconstructing the full triaxial stress distribution. Together, these approaches provide a better understanding of rail fabrication and the possibility of improving the durability and safety of rails in the future.Copyright © 2004 by ASME