Microstructures and Properties of AlMgTi-Based Metal-Intermetallic Laminate Composites by Dual-Steps Vacuum Hot Pressing
AlMgTi-based metal–intermetallic laminated composites were successfully fabricated through an innovative dual-step vacuum hot pressing. First, this study prepares the AlTi-based laminated composites by vacuum hot pressing at 650 °C. Then, the researchers place the Mg-Al-1Zn (AZ31) magnesium alloy between the prepared AlTi-based laminated composites at 430 °C for hot pressing. This study investigates the microstructure, phase composition, and microhardness distribution across interfaces of the intermetallics and metal. A multilayer phase (Mg17Al12, Al3Mg2, and transition layers) structure can be found from the diffusion layers between Al and AZ31. The microhardness of the material presents a wavy distribution in the direction perpendicular to the layers; the maximum can be up to 600.0 HV0.2 with a minimum of 28.7 HV0.2 The microhardness gradient of an AlMgTi-based composite is smoother due to the different microhardness of the layers, and reduces the interface stress concentration. The bending strength of AlMgTi-based composites can reach 265 MPa, and the specific strength is 105 × 103 Nm/kg, higher than AlTi-based composites.