the carrier release sheet of this invention may be used to make a sandwich composite with a resin or cross - linkable polymeric resin such as unsaturated polyester , for example , sheet molding compound (“ smc ”). typically , molding compounds contain styrene monomer , a reinforcing agent such as fiberglass , and particulate filler such as calcium carbonate . molding compound and methods of preparation thereof are described in u . s . pat . no . 4 , 444 , 829 . the sheet may include a top extruded skin layer and a bottom extruded skin layer . the top and bottom skin layers may be the same or different . a skin layer may comprise a blended admixture of a high density polyalkylene or a linear polyalkylene . the polyalkylene wherein the alkylene groups each contain 2 to 18 carbon atoms . a representative example of high density polyalkylene is high density polyethylene ( hdpe ). the polyalkylenes may contain one or more different alkylene monomers . representative examples of linear polyalkylenes include linear polyethylene including linear low density polyethylene ( lldpe ), linear polyhexene , linear polybutene , linear polyoctene , and blends thereof . the admixture also contains a blended adhesive amount of a compatible adhesive resin to impart selected low adhesive bond strength to the center layer by the top and bottom skin layers . the admixture which forms a skin layer may contain from about 20 to about 90 percent hdpe , alternatively from about 40 to about 60 percent by weight hdpe . the admixture may contain from about 20 to about 90 percent by weight linear polyalkylene , alternatively from about 25 to about 45 percent by weight . the admixture may also contain from about 10 to about 50 percent by weight of the adhesive resin , and in one embodiment of this invention may contain from about 20 to about 35 percent by weight of the adhesive resin . the top and bottom skin layers may also include , optionally , a low but effective amount of an antiblocking agent such as , but not limited to , particulate materials such as silica , which may be present in an amount ranging from about 0 . 1 to about 5 percent by weight . the amount of adhesive resin in the admixture should be sufficient to impart low adhesive bond strength between the top and bottom layers to the center barrier layer . preferably , the adhesive resin is compatible with the admixture . the adhesive resin , for example , may comprise an anhydride - modified polyolefin such as anhydride - modified lldpe . the anhydride may be an acid anhydride such as , but not limited to , aromatic acid anhydrides such as phthalic anhydride , and unsaturated dicarboxylic anhydrides such as succinic and maleic acid anhydrides . one adhesive resin particularly suitable for use in the invention is an anhydride - modified lldpe available from dupont which is available under the name bynel ™ cxa 4164 . in one embodiment of this invention , the film &# 39 ; s first skin layer is a non - seal layer which may contain from about 25 to about 90 percent by weight hdpe . the second sealant layer may contain from about 5 to about 90 percent hdpe and from about 5 to about 90 percent by weight lldpe . the hdpe may have a density of about 0 . 96 or more to improve the water barrier characteristics of the film . the center extruded layer may comprise any polymeric material which provides a barrier for a given monomer of a heat - curable resin composition . preferably , the polymeric material is useful as a barrier to styrene monomer , which is present in resin compositions employed in the sheet molding industry . for example , the release sheet may comprise a center extruded polymeric barrier layer such as a polyamide . a representative example of one such polyamide is nylon 6 / 66 , which is a copolyamide of hexamethylene diamine , adipic acid , and caprolactam . the top and bottom skin layers may be heat - sealed to each other at the edges . in the sandwich composite , the top skin layer and the bottom skin layer adhere to the center barrier layer with low adhesive bond strength . the low strength bond permits the top and bottom skin layers , or both , to be easily peeled from the center barrier layer of the sandwich composite . the adhesive resin employed in the admixture may vary in composition . since sheets may be sealed together , prior to compression rolling of a sandwich ( formed of release film / molding compound / release film ), the sealed edge serves to trap the compound in the sandwich . similarly , because the sealed edge provides a barrier to styrene , styrene losses are significantly reduced such that compound losses are dramatically decreased through use of the release film of this invention . furthermore , the sealed edge allows for the resin filler paste to be pushed to the sealed edges which become a resin - filler dam . a continuous weight of molding compound can thus be developed . that is , the weight per area at the center can be close to that at the edges . advantageously , this characteristic may enable a molding compound user to weigh charges less frequently . moreover , sealing of the edges further reduces loss of styrene of the molding compound . as a result , the film of this invention advantageously reduces the losses of molding compound heretofore frequently experienced by end users of such compound . the multiple layer carrier release sheet of this invention may vary in total thickness . typically , the sheet has a thickness of about 0 . 01 mils or more . in certain embodiments , the thickness may range from about 0 . 3 to about 2 . 0 mils , with skin layers generally ranging from about 0 . 1 to about 5 mils and the center layer typically ranging from about 0 . 1 to 10 mils . cast processes may be used to make films having a thickness of up to about 20 mils ( the film typically has a thickness of from about 0 . 5 mils to about 12 mils ). hdpe employed in the skin layers may have a density of about 0 . 94 ± 10 %. the polyalkylene , such as the polyoctene , may have a density of about 0 . 920 ± 15 %. the melt index of the hdpe may be about 0 . 2 . the melt index of the polyalkylene may be about 1 . 0 . advantageously , the film of this invention may be made using conventional processes . thus , the film may be made using a blown film co - extrusion process . likewise , a standard casting process may be employed to produce the release sheet of this invention . the multiple layer release carrier sheet of the invention is particularly useful in forming sandwich composites with heat - curable styrene monomer resins , wherein the styrene monomer resin forming the center of the sandwich . the multiple layer release carrier sheets of the invention may be easily removed and typically have a low peelability bond strength between the skin layers and the center barrier , with the bond strength being about zero or substantially zero . the bond strength may be from about 0 . 6 to about 6 pounds . the sandwich composite may be used in a compression molding process such as to make , for example , automobile parts such as fenders . the multiple layer release carrier film may be easily removed and disposed of prior to the compression molding . the release carrier sheet of the invention provides that the outer edges of the sandwich composite may be easily sealed to each other . thus , this invention provides a sandwich composite with heat - sealed top and bottom edges . furthermore , the ability to seal edges of the film allows a resin dam to build up during sandwich manufacture , thereby facilitating preparation of more continuous sheets . moreover , sealed edges reduce styrene losses in the compound at edges of the sandwich . the sealed bond can be easily destroyed by interfacial peeling due to the top and bottom skin layers having low bond strength to the center barrier layer . thus , when the edges of the top and bottom skins are heat - sealed together , the center ( core ) layer is unaffected , thereby permitting the easy removal of the skin layers by an operator . the multiple layer carrier release film of the invention provides a very effective barrier for styrene or other monomers or volatile materials of the heat - curable thermosetting resins ( e . g ., smc ). the release film also provides top and bottom skin layers that may be easily removed from the barrier layer prior to the use of the sandwich composite . the release film may be heat - sealed along the edges in forming the sandwich composite . it may be desirable to add a visible color agent to one or more of the extruded layers of the release sheet , such as the skin layers . this may provide greater visibility of the sheet material during use . generally , a colored pigment or dye agent , like an orange pigment , is incorporated in the skin layer composition . the color agent may be added in an amount from about 0 . 1 to about 5 . 0 % by weight . a color agent , if used , should preferably be selected such that the agent does not detrimentally affect sheet performance . a three layer blown , co - extruded carrier release sheet of the invention has been prepared as shown in fig1 . the heat carrier release sheet so prepared was employed in preparing a sandwich composite . the three - layer co - extruded sheet was composed of the following layers : the resulting film had a moisture vapor transmission rate (“ mvtr ”) of about 1 . 1 g / 100 square inch / day at 90 % relative humidity , as measured using astm f - 1249 . fig1 shows a sectional view of the multi - layer release sheet of the invention 10 , which comprises a center extruded barrier layer 12 for styrene resins which may be comprised of nylon , a top extruded skin carrier layer 14 , and a bottom extruded skin carrier layer 16 . the skin layers 14 and 16 comprise an admixture of high density polyethylene ( hdpe ), a linear polyethylene ( pe ), an adhesive resin to impart selected adhesive properties to the hdpe and pe , and an antiblock agent . fig2 shows a process 20 of preparing a sandwich composite 30 for later use in a compression molding system using the sheet material 10 of fig1 . sheet material 10 is unwound as a bottom carrier sandwich layer , and a layer of a heat - curable liquid styrene monomer resin 22 is cast onto the top surface of the sheet material 10 ( e . g ., ¼ ″- ½ ″) and chopped glass fiber 24 is deposited onto ( or previously admixed with ) resin 22 . a second roll of sheet material 10 is unwound and pressed onto the top surface of the monomer / chopped glass fiber layer to form a sandwich 30 . the sandwich is then subjected to compaction in a compaction area 26 by passage between a plurality of rolls to reduce the thickness of the sandwich , e . g ., from 1 - ½ ″ to ¼ ″- ⅜ ″. after compaction , the outer edges on each side of the sandwich 30 are heat - sealed together by an edge heat - sealer 28 . the compacted , edge - sealed sandwich composite 30 may be rolled up for future use or may be sent to a compression mold station 32 for molding in a cured glass fiber resin product 34 , after the top and bottom sheets 10 have been peeled from the resin - glass fiber layer 22 - 24 optionally at a peeling station 38 . alternatively , edge heat - sealer 28 may be positioned prior to compaction area 26 . fig3 is a sectional view along lines 3 — 3 of fig2 showing the top and bottom sheets 10 heat - sealed 36 at each edge by the heat - sealable top and bottom skin layers of the sheet 10 to enclose the partially cured styrene monomer resin 22 - glass fiber 24 layers . thus , the carrier release sheet of the invention provides for the effective aromatic hydrocarbon ( e . g ., styrene ) barrier through the use of a nylon or blended nylon central layer , and permits the top and bottom skin layers to be easily removable from the center layer and prior to compression molding , for example . the carrier release sheet further permits the top and bottom skin layers to be edge heat - sealed together when forming the sandwich composite . the sandwich composite may subsequently be either placed in inventory or removed to a compression molder formation to be compression molded into a cured fiberglass reinforced product . the multiple layer carrier release sheet of the invention thus overcomes many of the disadvantages of the prior art , yet provides effective barrier coating , easy peelability , and edge heat sealing . another example of the film of this invention was made by co - extrusion in a manner similar to the above - described film . the film contained three layers , each layer having been prepared from the following amounts of components : the film was produced by co - extrusion using a blown film process using standard techniques . the first extruder used for the non - seal skin layer generated 180 pounds per hour using barrel temperatures set to 370 ° f ., 410 ° f ., 370 ° f ., and 320 ° f . and pressure of 2770 psig . a second extruder generated 240 pounds per hour for the center layer using barrel temperatures set to 390 ° f ., 400 ° f ., 410 ° f ., 420 ° f ., 420 ° f . and pressure of 1470 psig . a third extruder generated 180 pounds per hour to form the sealant layer using barrel temperatures set to 370 ° f ., 410 ° f ., 390 ° f ., 340 ° f ., and 320 ° f ., at a pressure of 5950 psig . the resulting three layer film surprisingly good water barrier properties . thus , the nylon core retained its resiliency and was less prone to breakdown , thereby facilitating improved processing capability relative to the film above in which hdpe having a density of about 0 . 094 g / cc was employed in the skin layers . it is believed that the increase in hdpe density provides the decrease in water transmission through the skin layers . the film had the following physical properties at 0 . 95 mil : impact , dart drop f50 ( astm d - 1709 )& lt ; 40 grams ; tensile strength , ultimate md 8068 psi ; td 6 , 993 psi ( astm d - 882 ); elongation , ultimate md 349 %, td 406 % ( astm d - 882 ); 1 % secant modulus , md - 124 , 257 psi , td 135 , 054 psi ( astm d - 882 ); cof ( slip ), non - sealant 0 . 35 , sealant 0 . 32 ( astm d - 1894 ); tear strength , md - 16 grams , td - 192 grams ( astm d - 1922 ); yield at 1 . 0 mil 27 , 144 square inch per pound ; mvtr 0 . 2132 gram / 100 square inch / day at 90 % relative humidity . the film had excellent peel seal capabilities and was a stiffer film as compared to the above - identified exemplary film . it should be appreciated that the skin layers &# 39 ; thickness also contributes to water uptake with thicker films generally providing greater barrier to water . in addition , the film had excellent aromatic hydrocarbon barrier properties . it is believed that the nylon layer , including the thickness of the nylon layer , provides the enhanced styrene barrier properties of this invention &# 39 ; s film . it should be recognized that those persons skilled in the art may make various changes , modifications , improvements and additions to the invention described and claimed herein , all of which fall within the spirit and scope of the invention .