an embodiment of the invention will be explained with reference to the drawings hereinafter . fig1 shows a cylindrical oil retaining sintered bearing produced by the production method of the invention . the sintered bearing 1 is formed with an annular stepped portion 11 consisting of a planar surface along the radial direction , and the stepped portion 11 divides the outer surface of the bearing 1 into a large diameter portion 12 and a small diameter portion 13 . the bearing 1 has a bearing hole 14 at its center , into which a rotating shaft ( not shown ) is inserted , has a uniform diameter , and the inner surface of the bearing hole 14 is employed as a bearing surface . the surface of the bearing 1 except for the bearing surface 14 a , that is , the outer peripheral surfaces 12 a and 13 a of the large diameter portion 12 and the small diameter portion 13 , and end surfaces 15 and 16 of the large and small diameter portions 12 and 13 , and end surface of the stepped portion 11 , are covered by a resin coating 20 having a uniform thickness , as shown in fig2 . fig2 shows the surface layer of the outer surface 12 a of the large diameter portion 12 . as shown in fig2 , pores 10 in the bearing 1 is impregnated with a lubricating oil l . the thickness of the resin coating 20 is set according to required specifications . a production method for producing the bearing 1 will be explained hereinafter . an alloy raw material powder having a predetermined chemical composition such as an fe — cu type alloy powder mainly consisting of fe and cu for a bearing is compacted into a green compact having a shape similar to that shown in fig1 . then , the green compact is sintered into a sintered bearing compact at a suitable temperature and time . a resin for forming a resin coating is dispersed in an electrolyte charged into an electrodeposition vessel at a predetermined proportion to prepare a coating medium , and the coating medium is agitated and maintained for a predetermined time . an electrode and the bearing compact separated from each other are dipped into the coating medium , and a dc voltage is applied between both for predetermined time . by the interaction of the applied voltage , the resin particles having a charge in the electrolyte electrophoretically move toward the bearing compact , and adhere there to form a resin coating . the bearing compact after forming a resin coating is baked in a baking and drying furnace , and the resin coating is cured on the surface of the bearing compact . these treatments are the electrodeposition process , in which a sintered bearing formed with a resin coating over the entire surface thereof is thus produced . the sintered bearing formed with the resin coating over the entire surface thereof is subjected to a sizing step . in the sizing step , the bearing surface contacting with a rotating shaft is machined so as to remove the resin coating formed on the bearing surface , and to finish the inner diameter into a designed size . a lubricating oil is impregnated through the bearing surface which is exposed by removing the resin coating into pores in the bearing by vacuum impregnation . the oil retaining sintered bearing 1 shown in fig1 is thus obtained . according to the bearing 1 , leakage of the lubricating oil l and release of noxious gases are restrained since the resin coating 20 is formed over the surface of the bearing 1 except for the bearing 14 a . the resin coating 20 avoids the bearing 1 from contacting with air and from being penetrated with water thereinto , and corrosion resistance is therefore improved . the bearing surface 14 a is usually lubricated by the lubricating oil provided from the pores 10 , and good sliding performance with a rotating shaft is obtained . in the production method of the invention , the thickness of the resin coating 20 can be easily controlled and made uniform since the resin coating 20 is formed over the surface of the bearing 1 by electrodeposition . the thickness of the resin coating 20 is easily controlled by controlling the voltage applied in the electrodeposition , applying time , temperature of the electrolyte , and the like . the thickness of the resin coating 20 is uniform according to the characteristics of the electrodeposition , and oil retaining sintered bearings having suitable coating thickness according to equipment employed are therefore produced . furthermore , the coating thickness can be extremely thin , so that size reliability originally provided in sintered bearings is maintained , and the bearings can be applied to small parts and mass - production . in addition , pores 10 are reliably sealed since the electrophoretic resin penetrates into the small pores 10 on the surface of the bearing in the electrodeposition , so that the pores are sufficiently sealed and the penetrated resin into the pores functions as an anchor , and the resin is rigidly secured to the surface to avoid from being stripped therefrom . furthermore , the sintered bearing is employed as an electrode , and a uniform resin coating 20 is easily formed even for bearings having complicated shape . furthermore , a large amount of lubricating oil l can be impregnated into the pores 10 at inner portion of the bearing 1 . the lubricating oil l filled in the pores 10 is effectively held since the surface of the sintered bearing except for the bearing surface 14 a is covered by the resin coating 20 , and the interval for resupplying a lubricating oil l can be extended . furthermore , the density of the lubricating oil l in the bearing 1 can be large , so that fitting performance between the bearing 1 and a rotating shaft , wear resistance , corrosion resistance , cleanliness , and the like , can be improved . it should be noted that grooves for generating radial dynamic pressure may be formed on a bearing surface 14 a of the bearing 1 . the grooves may be formed in another sizing process , in which the bearing 1 is compacted again , and the axial length , outer diameter , and inner diameter are finished to a designed size while coining the grooves . several types of grooves are applied to the invention . for example , as shown in fig3 , herringbone grooves 30 comprised of multiple v - shaped grooves are mentioned . the herringbone grooves 30 are formed parallel to each other at a constant distance and the intersecting portions thereof converge toward the rotational direction r of a rotating shaft . in this modification with the dynamic pressure generating grooves 30 , the oil film formed between the rotating shaft and the bearing surface 14 a has a high pressure due to the rotation of the rotating shaft , and the rotating shaft is supported with highly precise rotation in a non - contacted manner and in a low torque . fig4 is a sem photograph showing surface layer of a sintered bearing in the embodiment shown in fig1 produced by forming a resin coating followed by partially removing the resin coating . the thicknesses of the resin coating at the outer surfaces 12 a and 13 a of the large and small diameter portions 12 and 13 , at the end surface 15 of the large diameter portion 12 , and at the bearing surface 14 a were measured from the sem photograph . fig4 shows a surface layer of the outer surface 13 a of the small diameter portion 13 , and the photograph demonstrated that a resin coating with uniform thickness of from 50 to 60 μm was formed on only the surface layer and the pores in inner portion from the resin coating were vacant . in addition , it was confirmed that pores on the outer surface 13 a on which the resin coating was formed were closely filled with the resin and that the resin was rigidly secured to the surface by the anchoring function of the pores . an oil retaining sintered bearing is produced by subjecting such a sintered bearing to the impregnating step .