separations of aromatics from gasoline , or similar wide - boiling mixtures , such as petroleum naphtha , are improved by means of a pervaporation membrane process employing a mixed phase vapor - liquid feed . the extent of feed vaporization is controlled , as detailed hereinafter , a consequence of which aromatic selectivity of the permeate is increased . higher permeate yields of aromatics are also made possible in adiabatic operations . simplified system configurations are enabled with the present invention . partial vaporization of gasoline feed concentrates the higher boiling fraction of the feed which is rich in aromatic components in the liquid fraction . preferential wetting of the membrane surface by this liquid phase results in higher aromatic concentrations contacting the membrane , thereby improving flux and selectivity when compared to processing the full boiling range gasoline as a liquid . lower boiling aliphatic components of the gasoline preferentially remain in the vapor phase , thereby reducing competitive permeation through the membrane . furthermore , adiabatic operation of the pervaporation membrane separation process is improved by employing mixed phase vapor - liquid feed . progressive condensation of the vapor phase , provides heat to the membrane thereby minimizing the temperature change of the membrane resulting from the endothermic pervaporation process . significant permeate yield gains are made possible from near adiabatic operation using mixed - phase feed . consequently , the membrane area required can be reduced . pervaporation of mixed - phase vapor / liquid feed enables considerable simplifications to the process scheme , i . e . predistillation of lower boiling components in the feed can be avoided , along with the associated pumps and controls . interstage and / or internal heat exchangers to maintain pervaporation temperature can be reduced or eliminated . referring to fig1 , there is shown a very simplified schematic illustration of the membrane separation system of the present invention . a feed reservoir contains the wide boiling range material ( 1 ) that is intended for membrane separation , such as conventional gasoline or naphtha , for example . the term “ wide boiling range ” in the context of gasoline or naphtha means a boiling range of greater than about 50 ° c . and preferably great than 150 ° c . from the initial boiling point to the final boiling point as determined by astm methodd86 - 05 . gasoline boiling ranges from 30 ° to 200 ° c . are typical based on this method . aromatic constituents are found in fractions boiling above about 80 ° c . pump means ( 2 ) is used to feed and pressurize the feed material to the membrane apparatus ( 5 ). the desired feed rate is controlled by a flow control valve ( 3 ). the desired feed pressure is controlled by back pressure regulating means ( 8 ) operating on the retentate ( 7 ) selected based on the composition of the feed and desired operating temperature of the membrane . heater means ( 4 ) is used to control the temperature of the feed to the membrane apparatus ( 5 ). in a preferred embodiment , the feed pressure p f and membrane temperature t f are controlled to provide an optimal vapor liquid mixture to the membrane . by optimal , we mean a vapor liquid mixture whereby the aromatic components in the feed are concentrated in the liquid portion contacting at least a portion of the membrane . conversely , the lower boiling point aliphatics are concentrated in the vapor . in a preferred embodiment , the aromatics in the liquid portion of the vapor liquid mixture fed to the membrane are concentrated by greater than about 10 %, more preferably greater than about 25 %, and most preferably greater than about 50 %. the end result of which is to condense a liquid layer onto the membrane that is rich in the constituents of the feed that comprise the preferred permeate while maintaining the remaining feed in a vapor state . the term “ preferred permeate ” means the constituents of the feed that the invention &# 39 ; s user wish to separate , as permeate , from the feed . the term “ preferred retentate ” means the constituents of the feed that the invention &# 39 ; s user wish to separate as retentate and which , if in liquid form at the separation membrane , would compete with the preferred permeate . in this embodiment , the preferred retentate contains aliphatic constituents of the feed that have a lower boiling range than the preferred permeate . feed material is partially vaporized to maintain dual feed states , liquid ( 1 a ) and vapor ( 1 b ). the term “ partially vaporized ” means there is sufficient vaporization to provide the optimal vapor liquid mixture to the membrane . as illustrated in the figure , the liquid ( 1 a ) contacts and wets the pervaporation membrane ( 5 a ). as previously described , liquid ( 1 a ) has an increased content of the preferred permeate ( relative to the feed ), while the vapor ( 1 b ) phase has an increased content of the preferred retentate . the pervaporation membrane ( 5 a ) is a selective membrane , selected to preferentially permeate the preferred permeate . in a preferred embodiment where feed ( 1 ) comprises gasoline or naphtha , for example , and the preferred permeate is aromatics rich hydrocarbons , pervaporation membrane ( 5 a ) is an aromatic selective membrane such as described in u . s . pat . no . 5 , 670 , 052 for example . the selective pervaporation membrane ( 5 a ) may include a physical porous support means ( not shown ) such as thermo mechanically expanded polytetrafluoroethylene , commercially available as gore - tex ™, a registered trademark of w . l . gore and associates , for example , capable of providing physical support of the selective pervaporation membrane ( 5 a ) under the temperature , pressure , and materials conditions described herein . alternative supports include sintered metal or ceramic porous media . a preferred support means includes an asymmetric porous media such as a porous ceramic tube or monolith having a microporous surface material , such as described in co - pending application u . s . ser . no . 60 / 836 , 319 . in a preferred embodiment , selective pervaporation membrane ( 5 a ) comprises a cross - linked polyimide - polyadipate membrane polymer supported on a porous ceramic support means . a feature of the present invention is the substantially adiabatic operation of the pervaporation membrane ( 5 a ). the pervaporation process is endothermic . as previously described , the feed material is maintained partially vaporized . progressive condensation of the higher boiling temperature constituents of the vapor phase feed onto the pervaporation membrane supplies heat to the membrane , offsetting the heat lost to the endothermic pervaporation process . yet another feature of the present invention is the liquid layer ( 1 a ) that contacts the separation membrane ( 5 a ). the membrane temperature t f and the pressure on the membrane feed side p f are maintained to condense a relatively thin layer of preferred permeate rich condensate on the membrane surface . though not intending to be bound by any particular theory , in a preferred embodiment the liquid layer ( 1 a ) is maintained as a relatively thin layer to facilitate achieving and maintaining both thermal and compositional equilibrium between vapor , liquid and membrane . in the embodiment where feed comprises conventional gasoline or naphtha and the preferred permeate is the aromatic constituents of the feed , the liquid layer is maintained by control of t m and p f such that the condensation rate of aromatic - rich constituents is about equal to the permeate rate of such constituents . permeate ( 6 ), having increased concentration of the preferred permeate , is condensed and collected by conventional means illustrated by pump means ( 9 ). the examples presented below illustrate and exemplify the subject matter for this invention . an aromatic selective membrane of the type described in u . s . pat . no . 5 , 670 , 052 was used to concentrate aromatics from the gasoline in the permeate . the polyimide - polyadipate membrane used was crosslinked with diepoxidecyclooctane ( deco ). the polyimide hard segment contains pyromellitic dianhydride ( pmda ) and 4 , 4 ′- methylene bis ( 2 - chloroaniline ) ( moca ). the soft segment polyadipate had a molecular weight of about 2000 . the pei - deco polymer was coated on a 0 . 1 micron porosity gore - tex ™ support to a thickness of about 40 microns . the polymer film was protected by an additional layer of 0 . 05 micron porosity gore - tex ™ overlayer , thereby creating a sandwich structure with a total membrane thickness of about 150 microns . spiral - wound membrane elements of 0 . 9 m 2 active area each were fabricated from the coated sheets and used for the separations as described in examples 3 and 4 . a plate - frame ( wafer cassette ) module design with internal heating was also used as noted in the examples . polymer coating thickness was 7 microns . two sheets were layered together , front to back , for a nominal total pei - deco polymer thickness of 14 microns , followed by an additional 0 . 05 micron porosity gortex overlayer . several sheets were used flat and sealed by means of viton o - rings to obtain 0 . 2 m 2 area . a simplified process schematic of the apparatus used in this example is provided in fig2 . a conventional gasoline feed ( 20 ) was pressurized by pump ( 21 ) to obtain the desired feed pressure . feed flow was controlled by a mass flow control valve ( 22 ). the feed was heated to the desired temperature by means of a heat exchanger ( 23 ) by contacting against a circulating hot ethylene glycol - water mixture , for this example , typically maintained at 120 ° c . alternatively , a silicone oil bath was used to obtain gasoline feed temperatures up to about 160 ° c . the preheated feed is substantially vapor upon delivery into the membrane module ( 24 ). backpressure on the membrane was controlled by means of a pressure regulator ( 25 ) operating on the retentate stream ( 28 ) thereby providing the desired operating pressure p f . the permeate ( 26 ) was recovered under vacuum provided by a vacuum pump ( 32 ). the permeate vapor was cooled by means of heat exchanger ( 27 ) to about 30 ° c . the “ heavy ” permeate condensate ( 26 a ) was separated , by means of the gas / liquid vacuum separator ( 30 ), from the remaining permeate vapor ( 26 b ), and recovered by means of a liquid pump ( 29 ) then stored in gasoline reservoir ( 31 ) which , in this example , is a high octane fuel reservoir . the remaining permeate vapor ( 26 b ) was compressed by the vacuum pump ( 32 ) and cooled to about 30 ° c . by heat exchanger ( 33 ) to obtain additional “ light ” liquid permeate ( 26 c ) from the vacuum exhaust . alternatively , the entire permeate ( 26 ) was cooled by heat exchanger ( 27 ) and compressed by vacuum pump ( 32 ) to obtain the high octane fuel . hot retentate ( 28 ) was cooled to about the ambient temperature of 20 ° c . by means of forced air - fin heat exchanger ( 37 ) and stored in reservoir ( 39 ) which serves in this example as a low octane gasoline reservoir . in some examples , a portion of the hot retentate ( 28 ) was recycled by means of pump ( 36 ) to mix with the membrane feed ( 20 ) prior to heating with heat exchanger ( 23 ). for this embodiment , a polymer coated ceramic monolith was constructed in the following manner : a solution of poly ( ethylene adipate ) “ pea ,” pyromellitic dianhydride “ pmoa ,” 4 , 4 ′- methylene bis ( 2 chloroaniline ) and 1 , 2 , 5 , 6 - diepoxycyclo octane “ deco ” was mixed with equal amounts of dmf and acetone to create an approximate 2 . 0 wt % polymer solution . the final molar ratios of the components were nominally 1 - pea2000 / 2 - pmda / 1 - moca / 2 - deco . the solution was maintained at room temperature or lower after adding deco . the solution was used to coat a porous ceramic monolith by drawing the liquid polymer into the porous surface of the monolith . the coated monolith was caused to form a polymer film of the composition described in u . s . pat . no . 5 , 670 , 052 on the surfaces , including the interior surfaces , of the porous monolith , forming a polymer coating substantially free of voids and holes , having a surface area of about 0 . 1 m 2 . the membrane was used in the simplified process and apparatus depicted in fig2 . a conventional gasoline comprising japanese regular unleaded winter grade gasoline was used as feed ( 21 ). the feed gasoline was tested to determine its octane rating and composition , having about 90 . 3 ron , about 33 . 9 wt % aromatics , and about 23 . 1 wt % c5 minus light aliphatic hydrocarbons . the process illustrated in fig2 was operated under two sets of conditions , the first to produce a liquid phase feed to the membrane system , the second to produce a mixed liquid / vapor feed in accordance with the present invention . liquid phase feed conditions were obtained by operating at a membrane feed pressure p f of about 960 kpa ( absolute ), and a membrane outlet pressure of about 950 kpa ( absolute ). membrane feed temperature was maintained at about 140 ° c . these pressures are substantially above the bubble point pressure of the gasoline feed at 140 ° c ., whereby the membrane feed is maintained in a liquid state . the same apparatus was used under a second set of process conditions to produce a mixed liquid / vapor phase feed . accordingly , the membrane inlet pressure was maintained at about 465 kpa ( absolute ) measured after control valve ( 22 ), and membrane outlet at about 445 kpa ( absolute ) measured at the back pressure regulator ( 25 ). membrane feed temperature was maintained at about 140 ° c ., measured at the inlet distributor to the membrane element after heat exchanger ( 23 ). under these conditions , feed to the membrane was estimated to be about 45 wt % liquid and 55 wt % vapor . outlet temperatures were measured in the retentate stream exiting the membrane element . in both the liquid phase case and the mixed liquid / vapor case , vacuum was maintained on the cooled permeate by means of an eductor pump ( 32 ). table 1 below compares permeate rate , permeate octane number , permeate density , permeate aromatics , and permeate aliphatics for both liquid and mixed liquid / vapor feed . operating with liquid phase conditions resulted in a permeate rate of 0 . 11 g / s . the adiabatic temperature drop resulting from the pervaporation process was 21 ° c . the permeate pressure obtained by condensing and pumping away the permeate was 40 . 7 kpa . the permeate obtained with liquid phase feed had increased aromatic content , but a substantial increase in c5minus light hydrocarbon content . the light hydrocarbons resulted in a higher vapor pressure permeate and consequently higher permeate pressure . it should be noted that an effect of use of the eductor ( 32 ) is that the permeate pressure is affected by the permeate stream control and is not independently set by the user . the octane number increased corresponding to the increased aromatic content . mixed phase vapor / liquid feed to the membrane in accordance with the present invention , produced improved membrane separation performance . permeate rate increased to 0 . 17 g / s . the adiabatic temperature drop was less at 11 ° c ., a consequence of vapor condensation in the membrane feed channels balancing the heat loss associated with the endothermic pervaporation process . vacuum improved with the permeate pressure at 23 kpa and a corresponding decrease in the volatile c5minus hydrocarbons in the permeate . the aromatic content of the permeate increased substantially to 52 . 5 %. the permeate octane rating increased to 97 . 8 ron corresponding to the increased aromatics content and reduced c5minus content . similar to example 2 , a conventional gasoline 40 was pressurized by pump ( 41 ) to obtain the desired feed pressure . feed flow was controlled by a mass control valve , not shown . the feed was heated to the desired temperature by heat exchanger ( 43 a ). the pre - heated feed is substantially vapor upon delivery to first membrane module ( 44 a ). the feed pressure p f and temperature t f were maintained to provide an estimated optimal vapor - liquid mixture to the membrane whereby a relatively thin layer of liquid is maintained in contact with the membrane to contact the membrane with aromatics rich liquid . the temperature t f and pressure p f are controlled such that the condensation rate of aromatic rich feed constituents is about equal to the permeation rate of such constituents . the retentate ( 45 ) from the first membrane module ( 44 a ) is re - heated by heat exchanger ( 43 b ) and fed to second membrane module ( 44 b ), operated in substantially the same manner as described for first membrane module ( 44 a ). aromatics - rich permeate ( 46 a ) and 46 b ) from the first and second membrane modules are collected and cooled by heat exchange ( 47 ), separated by separator means ( 50 ) and stored in the high ron reservoir ( 51 ). retentate ( 49 ) from the second membrane module ( 46 b ) is either cooled by heat exchanger ( 57 ) and stored in low ron reservoir ( 59 ), or recycled to supplement fresh feed ( 40 ).