the crystalline molecular sieve material of this invention , emm - 7 , is a single crystalline phase which can be prepared in essentially pure form with little or no detectable impurity crystal phases and has an x - ray diffraction pattern which in its as - synthesized , uncalcined form includes the d - spacing maxima listed in table 1 : in tables 1 and 2 , the interplanar spacings , d &# 39 ; s , are calculated in angstrom units ( å ), and the relative intensities of the lines , i / i o , where the intensity of the strongest line above background , i o , is counted as 100 , are derived with the use of a profile fitting routine ( or second derivative algorithm ). the intensities are uncorrected for lorentz and polarization effects . the relative intensities are given in terms of the symbols vs ( or vs )= very strong ( greater than 60 to 100 ), s ( or s )= strong ( greater than 40 to 60 ), m ( or m )= medium ( greater than 20 to 40 ) and w ( or w )= weak ( 0 to 20 ). it should be understood that diffraction data listed as single lines may consist of multiple overlapping lines which under certain conditions , such as differences in crystallographic changes , may appear as resolved or partially resolved lines . typically , crystallographic changes can include minor changes in unit cell parameters and / or a change in crystal symmetry , without a change in the structure . these minor effects , including changes in relative intensities , can also occur as a result of differences in cation content , framework composition , nature and degree of pore filling , and thermal and / or hydrothermal history . in one embodiment , the present crystalline material is an aluminosilicate compound having , in its as - synthesized , anhydrous form , a composition in terms of mole ratios of oxides , in the range : the crystalline molecular sieve material described herein may be prepared from a hydrothermal reaction mixture containing at least one source of potassium , at least one source of an oxide of trivalent element x , e . g ., aluminum , at least one source of an oxide of tetravalent element y , e . g ., silicon , and water , the hydrothermal reaction mixture having a composition , in terms of mole ratios of oxides , within the following ranges : the source of silicon used in the above mixture may be a silicate , e . g ., fumed silica , such as aerosil ( available from degussa ), a tetraalkyl orthosilicate , or an aqueous colloidal suspension of silica , for example that sold by e . i . du pont de nemours under the tradename ludox . examples of suitable aluminum sources include hydrated aluminum oxides , such as boehmite and pseudoboehmite . crystallization of the emm - 7 can be carried out at either static or stirred conditions in a suitable reactor vessel , such as for example , polypropylene jars or teflon lined or stainless steel autoclaves , at a temperature of about 95 ° c . to about 250 ° c . for a time sufficient for crystallization to occur at the temperature used , e . g ., from about 12 hours to about 30 days . thereafter , the crystals are separated from the liquid and recovered . after recovery , the crystals can be subjected to a variety of conventional post synthesis techniques , especially ammonium ion exchange and calcination to convert the molecular sieve from its potassium form to its catalytically active hydrogen form . it should be realized that the reaction mixture components can be supplied by more than one source . the reaction mixture can be prepared either batch - wise or continuously . crystal size and crystallization time of the new crystalline material will vary with the nature of the reaction mixture employed and the crystallization conditions . synthesis of the emm - 7 may be facilitated by the presence of at least 0 . 01 percent , preferably at least 0 . 10 percent and still more preferably at least 1 percent , seed crystals ( based on total weight ) of crystalline product . in its active form , emm - 7 exhibits significant acid activity , with an alpha value well in excess of 1 . in this respect , alpha value is an approximate indication of the catalytic cracking activity of a catalyst compared to a standard catalyst and it gives the relative rate constant ( rate of normal hexane conversion per volume of catalyst per unit time ). it is based on the activity of silica - alumina cracking catalyst taken as an alpha value of 1 ( rate constant = 0 . 016 sec - 1 ). the alpha test is described in u . s . pat . no . 3 , 354 , 078 ; in the journal of catalysis 4 , 527 ( 1965 ); 6 , 278 ( 1966 ); and 61 , 395 ( 1980 ), each incorporated herein by reference as to that description . the experimental conditions of the test used herein include a constant temperature of 538 ° c . and a variable flow rate as described in detail in the journal of catalysis 61 , 395 ( 1980 ). the crystalline material described herein can be used to adsorb dry gases and liquids ; for selective molecular separation based on size and polar properties ; as an ion - exchanger ; as a catalyst in organic conversion reactions , such as cracking , hydrocracking , disproportionation , alkylation , isomerization , oxidation and synthesis of monoalkylamines and dialkylamines ; as a chemical carrier ; in gas chromatography ; and in the petroleum industry to remove normal paraffins from distillates . when used as a catalyst , the present crystalline material can be intimately combined with a hydrogenating component such as tungsten , vanadium , molybdenum , rhenium , nickel , cobalt , chromium , manganese , or a noble metal such as platinum or palladium where a hydrogenation - dehydrogenation function is to be performed . such component can be in the composition by way of cocrystallization , exchanged into the composition to the extent a trivalent element , e . g ., aluminum , is in the structure , impregnated therein or intimately physically admixed therewith . such component can be impregnated in or on to crystalline material such as , for example , by , in the case of platinum , treating emm - 7 with a solution containing a platinum metal - containing ion . thus , suitable platinum compounds for this purpose include chloroplatinic acid , platinous chloride and various compounds containing the platinum amine complex . the present crystalline material , when employed either as an adsorbent or as a catalyst in an organic compound conversion process is preferably dehydrated , at least partially . this can be done by heating to a temperature in the range of 100 ° c . to about 370 ° c . in an atmosphere such as air , nitrogen , etc ., and at atmospheric , subatmospheric or superatmospheric pressures for between 30 minutes and 48 hours . dehydration can also be performed at room temperature merely by placing the emm - 7 in a vacuum , but a longer time is required to obtain a sufficient amount of dehydration . as in the case of many catalysts , it may be desirable to incorporate emm - 7 with another material resistant to the temperatures and other conditions employed in organic conversion processes . such materials include active and inactive materials and synthetic or naturally occurring zeolites as well as inorganic materials such as clays , silica and / or metal oxides such as alumina . the latter may be either naturally occurring or in the form of gelatinous precipitates or gels including mixtures of silica and metal oxides . use of a material in conjunction with the new crystal , i . e ., combined therewith or present during synthesis of the new crystal , which is active , tends to change the conversion and / or selectivity of the catalyst in certain organic conversion processes . inactive materials suitably serve as diluents to control the amount of conversion in a given process so that products can be obtained economically and in orderly manner without employing other means for controlling the rate of reaction . these materials may be incorporated into naturally occurring clays , e . g ., bentonite and kaolin , to improve the crush strength of the catalyst under commercial operating conditions . said materials , i . e ., clays , oxides , etc ., function as binders for the catalyst . it is desirable to provide a catalyst having good crush strength because in commercial use it is desirable to prevent the catalyst from breaking down into powder - like materials . these clay and / or oxide binders have been employed normally only for the purpose of improving the crush strength of the catalyst . naturally occurring clays which can be composited with emm - 7 include the montmorillonite and kaolin family , which families include the subbentonites , and the kaolins commonly known as dixie , mcnamee , georgia and florida clays or others in which the main mineral constituent is halloysite , kaolinite , dickite , nacrite , or anauxite . such clays can be used in the raw state as originally mined or initially subjected to calcination , acid treatment or chemical modification . binders useful for compositing with the present crystal also include inorganic oxides , such as silica , zirconia , titania , magnesia , beryllia , alumina , and mixtures thereof . in addition to the foregoing materials , the new material can be composited with a porous matrix material such as silica - alumina , silica - magnesia , silica - zirconia , silica - thoria , silica - beryllia , silica - titania as well as ternary compositions such as silica - alumina - thoria , silica - alumina - zirconia silica - alumina - magnesia and silica - magnesia - zirconia . the relative proportions of emm - 7 , preferably finely divided , and inorganic oxide matrix may vary widely , with the emm - 7 content ranging e . g . from about 1 to about 90 percent by weight and more usually , particularly when the composite is prepared in the form of beads , in the range of about 2 to about 80 weight percent of the composite . in order to more fully illustrate the nature of the invention and the manner of practicing same , the following examples are presented . 9 . 9 g of water , 2 g of 45 % koh and 5 g of 10 % koh solutions are mixed with 0 . 6 g of al ( oh ) 3 powder (˜ 53 % alumina ) in a plastic autoclavable bottle . ludox hs - 40 silica ( 40 wt % silica , 60 wt % water , available from dupont chemcial co .) is added ( 12 . 5 g ) and the mixture homogenized by shaking . the bottle is sealed , heated in a parr autoclave filled with water at 190 ° c . and sampled at 120 , 140 and 170 hrs . the final product is found to be predominantly emm - 7 based on the unique principal x - ray diffraction peaks with the positions and intensities as in table 4 : the as - synthesized product has the following composition : 72 % silica , 5 . 66 % alumina , 5 . 66 % k and 0 . 31 % na . cation exchange with 2 m ammonium nitrate solution , 3 treatments at room temperature , demonstrates exchangeability of the alkali cations resulting , after calcinations , in the following composition of the solid product : silica 79 . 4 %, alumina 6 . 69 %, k 0 . 3 % and na 0 . 01 %. nitrogen adsorption / desorption tests reveal the product to have a bet surface area of 189 m 2 / g and 0 . 077 cm 3 / g micropore volume . measurement of nitrogen sorption isotherms and of bet surface area is well known in the art , e . g . as astm method d 4365 - 95 “ standard test method for determining micropore volume and zeolite area of catalysts ”. alpha test shows catalytic activity towards hydrocarbons , with an alpha value of 9 . 1 . 9 g of water and 15 g of 10 % koh solution are mixed with 0 . 6 g of al ( oh ) 3 powder (˜ 53 % alumina ) in a plastic autoclavable bottle . ludox hs - 40 silica is added ( 12 . 5 g ) and the mixture homogenized by shaking . the bottle is sealed , heated in a parr autoclave filled with water at 190 ° c . and discharged , filtered and washed with water after 180 hrs . the final product is found to be predominantly emm - 7 based on the unique principal x - ray diffraction peaks with the positions and intensities as in table 6 below . the as - synthesized product has the following composition : 74 . 4 % silica , 7 . 13 % alumina , 7 . 39 % k and 0 . 13 % na . cation exchange with 1 m ammonium nitrate solution , 3 treatments at room temperature , demonstrates exchangeability of the alkali cations resulting , after calcinations , in the following composition of the solid product : silica 81 . 7 %, alumina 7 . 71 %, k 0 . 55 % and na 0 . 018 %. nitrogen adsorption / desorption tests reveal the product to have a bet surface area of 197 m 2 / g and 0 . 077 cm 3 / g micropore volume . 0 . 12 g of al ( oh ) 3 powder (˜ 53 % alumina ) is added to 126 g of water with 36 g of ludox - hs - 40 in a 250 ml plastic autoclavable bottle and shaken to homogenize . 12 g of 45 . 5 % koh is added to the mixture . the bottle is sealed , heated in a parr autoclave filled with water at 190 ° c . and discharged , filtered and washed with water after 200 hrs . the final product is found to be predominantly emm - 7 based on the unique principal x - ray diffraction peaks with the positions and intensities as in table 7 : while the present invention has been described and illustrated by reference to particular embodiments , those of ordinary skill in the art will appreciate that the invention lends itself to variations not necessarily illustrated herein . for this reason , then , reference should be made solely to the appended claims for purposes of determining the true scope of the present invention .