a color filter for a liquid crystal display device is manufactured starting from a glass plate . a plurality of filters can be simultaneously manufactured on this plate . the starting material may also be , for example , quartz . after the glass plate has been cleaned in fuming nitric acid , a black matrix is first provided in this embodiment by first vapor - depositing a thin layer of chromium and providing it with the desired pattern by way of a photolithographic process . the glass plate provided with a black matrix is subsequently cleaned by treating it in an ozonic atmosphere for 2 minutes while simultaneously irradiating it with ultraviolet light . in the present embodiment a source with a substantially parallel beam was used , which emitted wavelengths between 150 and 300 nm ( by means of a low - pressure mercury lamp with the main electron transitions at 185 and 254 nm ). the intensity was 10 mw / cm 2 at a distance of 2 . 5 cm above the glass plate at a wavelength of 254 nm . more generally , the total exposure period is dependent on the intensity used and the spectral composition of the uv source , as well as on the distance between the glass plate and the source , and on the ozone percentage . the glass plate is subsequently cleaned in , for example , distilled water after it has been slightly heated , if necessary . subsequently the assembly is coated with a colorable acrylate lacquer , for example a solution ( 10 %) of copolymers in methyl glycol or a gelatin ( di ) chromate or another suitable colorable polymeric material layer . said layer is provided , for example , by means of spin - coating and the spin - coating speed may also be dependent on the desired color density of the color to be provided . the layer thus provided is subsequently patterned photolithographically . the patterned resin layer is subsequently provided with a first color pattern by adding the suitable dyes . generally , known dyes ( acidic , direct and reactive dyes ) can be used for this purpose . for this first pattern , for example , a red dye r - 24p of the firm of nihon kayaku or &# 34 ; red grl &# 34 ; of the firm of ciba - geigy is chosen . the glass plate with the red color pattern thus obtained is subsequently subjected again to a treatment in an ozonic atmosphere for 7 to 8 minutes . with this treatment it is achieved that the color pattern is fixed and that the substrate is cleaned for providing a subsequent color pattern . a possible explanation is that cross - linkage takes place in the polymeric material layer under the influence of the ultraviolet radiation while oxygen ions or oxygen atoms are simultaneously built in due to the presence of ozone . like the above - mentioned first cleaning treatment , the duration of this treatment may vary again between approximately 1 and 20 minutes , dependent on wavelength used , energy density , distance , etc . the assembly is subsequently coated again with a colorable acrylate lacquer which is patterned similarly as described hereinbefore , whereafter the patterned polymeric material layer is provided with a second color pattern , for example green . for example , g - 1p of the firm of nihon kayaku or &# 34 ; green 3gs &# 34 ; of the firm of ciba - geigy is used as a green dye . the glass plate thus obtained is again subjected to a combined fixing and cleaning treatment as described hereinbefore , after providing of the red pattern , whereafter the assembly is again coated with a colourable acrylate lacquer . a patterned polymeric material layer provided with a third color pattern , in this example blue is obtained again . for example , b - 5p of the firm of nihon kayaku or &# 34 ; blue 8g &# 34 ; of the firm of ciba - geigy is used as a blue dye . after the blue pattern has also been fixed and cleaned simultaneously , the polymeric material layer provided with a colour pattern thus obtained is coated with a top coat which in the case of liquid crystal display devices protects the red - green - blue colour pattern chemically ( against the influence of liquid crystal material ) as well as mechanically ( against the influence of spacers ). since , as described above , fixing is effected during the cleaning treatment , namely in a completely different way than described in the japanese patent application no . 58 - 207010 laid open to public inspection , the use of toxic antimony potassium tartrate can be avoided . also tannic acid is no longer used so that antimony potassium tartrate and tannic acid need not be stored . in addition to a shorter process , the method according to the invention thus also has a logistic advantage . the latter is all the more true because said chemicals have a limited storage life and must be regularly tested for their usability . the invention is of course not limited to the example described , but other substrates such as , for example , a silicon substrate in which a photosensitive sensor such as a ccd or a bbd is integrated may also be chosen , while color filters in , for example , camera tubes may also be considered . other composite color may also be chosen such as , for example , cyan , yellow and magenta , while the black mask may be omitted , if necessary .