one aspect of the invention relates to a process by which a glass - coated wire is exposed to an acid solution . in one example , the glass - coated wire is a microwire , and is introduced in the acid bath in a discrete batch , exposed to the solution for a specified time , and then removed and rinsed . in another example , the glass - coated wire is continuously drawn on an arrangement of spools and pulleys through an acid - solution bath , out of the solution , and through a rinse bath . in this example , the rate of motion of the spools and the size of the baths determine the exposure time . one example of a process is the reduction in the thickness of the glass coating at a defined rate of removal , with the end result being the removal , either full removal or partial removal , of the glass coating from the metal substrate or core . hereinafter , removal of the insulating coating will be understood to include full or partial removal . the wire can be formed of a metal alloy containing one or more , or combinations of aluminum , chromium , cobalt , copper , gold , iron , lead , nickel , palladium , platinum , silver , tin , titanium , tungsten , and zirconium . the metal alloy used in the wire can be amorphous , crystalline or micro - crystalline . additionally , the wire composition can be chosen to include one or more elements from the following classes : ( 1 ) ferrous amorphous ( e . g ., fe , co , ni , cr , mn , ga , al , si , cr , nb , vr , hf , b , c , and p ), ( 2 ) non - ferrous amorphous ( e . g ., al ti , zr , be , nb , ga , la , y , pd , ni , cu , zn , b , p , si , and sn ), ( 3 ) ferrous crystalline ( e . g ., fe , co , ni , mo , cr , c , and b ), or ( 4 ) non - ferrous crystalline ( e . g ., al , cu , w , au , pt , pd , rh , cr , and mn ). the insulating coating on the wire is typically a glass , but the coating could also be ceramic or glass - ceramic material . examples of insulating coatings are glass , silicon dioxide , phosphosilicate glass ( psg ), boro - phosphosilicate glass ( bpsg ), aluminum oxynitride , barium titanate , beryllium oxide , boron nitride , cerium hexaboride , germanium dioxide , hafnium diboride , lanthanum gallium silicate , lanthanum hexaboride , lead zirconate titanate , magnesium oxide , molybdenum silicide , silicon carbide , silicon nitride , strontium titanate , titanium boride , tungsten nitride , and tungsten silicide , or combinations thereof . the glass - coated wire is preferably etched in a fluorine - based acid solution . examples of fluorine - based acid solutions are hydrofluoric acid ( hf ), hydrofluorosilicic ( hfs ) acid , fluoric acid , fluohydric acid , hydrofluoride , fluorine monhydride , or a mixture of hydrofluoric ( hf ) and hydrofluorosilicic ( hfs ) acid . the invention also contemplates various combinations of the previously mentioned fluorine - based acids . hydroxide compounds can also be used to etch the glass coating , however , these are less preferred due to the need to maintain high pressures and temperatures to be effective . examples of hydroxide compounds are : sodium hydroxide ( naoh ), potassium hydroxide ( koh ), caesium hydroxide ( csoh ), tetramethylammonium hydroxide (( ch3 ) 4noh ). phosphoric acid could also be used , however , it would have a very long reaction time . the invention also contemplates the use of plasma ( i . e ., dry ) etching as a means for removing the glass coating . it is possible to control the etching process by adjusting the chemistry of the acid solution . alternative fluorine - containing ionic species may be introduced to adjust the kinetics of the reaction with the silica glass . metal ions may also be introduced that control the activity of the solution relative to the alloy constituents of the metal core . these metal ions , as embodied by the invention , prevent the dissolution of the alloy and thus protect the surface and protect the surface finish and diameter of the metal core . if metal ions are not added to the acid solution , the metal wire can be pitted and damaged to the point where it can not be used in the application . one or more types of metal ions can be introduced to the acid solution to prevent the pitting and / or etching of the metal wire surface . in one example , cobalt metal is dissolved into the acid solution to ensure the presence of an excess of cobalt + 2 ions . this impedes the dissolution of a cobalt - alloy upon the removal of the glass coating and prevents pitting of the wire surface . alternatively , the cobalt + 2 ions may be introduced by adding a cobalt salt , including but not limited to , cosif 6 , co ( hsif 6 ) 2 , and / or coco 3 . in this example , it is important that the metal ions that are used be the majority alloy constituents of the metal core . majority alloy constituent is defined as the element in greatest quantity within the alloy . for example , the majority alloy constituent in an alloy comprised of 60 % cobalt and 40 % iron ( i . e ., co 60 fe 40 ), would have cobalt as the majority alloy constituent ( i . e ., 60 % is greater than 40 %). also in this example , it is important to control the valence of the metal ions in the acid solution to prevent their reaction with the metal core . one way to control the valence is to ensure that an excess of cobalt metal is present in the solution to avoid the formation of cobalt + 3 ions . cobalt + 3 ions will react with co atoms present on the wire surface to form cobalt + 2 , which can damage the wire surface due to pitting . additionally , the presence of oxygen can oxidize cobalt + 2 ions to cobalt + 3 ions . as another specific example , the wire is formed of a ferrous - amorphous metal , co 66 . 5 fe 4 cr 4 si 12 b 13 . 5 . for this type of wire , cobalt metal powder is added to the etching solution to prevent the solution from etching or pitting the wire surface . in this example , cobalt is the majority constituent of the metal alloy ( i . e ., cobalt at 66 . 5 % versus iron at 4 % versus chromium at 4 % versus silicon at 12 % versus boron at 13 . 5 %) and is chosen as the metal ion to be added to the etching solution . it is important that the etching solution is saturated with the metal powder ; providing an excess of metal guarantees that this is accomplished . fig1 illustrates an exemplary geometry of a glass - coated metal wire . the glass - coating 12 is disposed on the surface of a metal core 14 and is continuous along its length . the core 14 is solid metal and retains a sharp interface with the glass coating 12 . wires of this type are typically referred to as microwires due to their extremely small diameters , on the order of 1 - 200 microns . alternatively , the wires could be oval , square , rectangular , trapezoidal or any other shape in cross - section . one process that can be used to fabricate glass - coated metal wires is the taylor - ulitovsky process . the metal cores 14 , obtained with the taylor - ulitovsky process , typically range between 0 . 5 - 150 microns thick and the glass coating 12 typically ranges between 1 - 50 microns thick . the diameter of the core 14 and thickness of the coating 12 may be controllably varied according to the requirements of the application . fig2 is a schematic of a gas - filled proportional radiation detector with an amorphous metal anode wire 22 and a cathode 24 . the amorphous metal anode wire 22 is manufactured from glass - coated microwire that has had the glass coating removed . a proportional radiation detector is a gas - filled device that , when a high voltage v is applied , creates an electrical pulse when a neutron interacts with the gas . the absorption of a neutron causes the prompt emission of a nucleus or proton respectively . these charged particles can then cause ionization in the gas , which is collected as an electrical pulse . through the use of electronic discriminator circuits , the amount of radiation can be measured by monitoring the change in resistance . fig3 is a schematic illustration of a glass - removal apparatus 300 , as embodied by the invention , in which a wire 310 is exposed to acid 320 in discrete batches . the acid 320 could be a fluorine - based acid , and is used to remove the glass coating from wire 310 . in this apparatus , acid 320 is placed in non - reactive beaker 330 ( such as a beaker formed of teflon ™) that is placed atop a magnetic stirring plate 340 . a plastic - coated stirring magnet 350 can be placed at the bottom of the beaker 330 . the glass - coated microwire 310 is placed on a non - reactive spool 360 ( such as teflon ™) and submerged in the acid solution 320 for the required time . the magnetic stirring plate 340 induces the stirring magnet 350 to spin , and in so doing , agitates and stirs the acid 320 . the agitated acid 320 flows around the wire 310 and reacts with the glass coating . the flow induced by the stirring magnet 350 ensures that the wire 310 is uniformly exposed to acid 320 . alternatively , the wire 310 may be wound around the stirring magnet 350 . after glass removal , the spool 360 is removed from the solution , rinsed and dried . the wire 310 can be rinsed in deionized water or any other suitable rinsing solution . the wire 310 can be dried in ambient air or by using a heated airflow , or any other suitable means for drying wire 310 can be employed . fig4 is a schematic illustration of another glass - removal apparatus 400 , as embodied by the invention , the apparatus 400 provides the wire 410 to be drawn continuously through an acid solution 420 and then drawn through a rinse bath 430 . the wire 410 is fed out from a source spool 440 and wound around a system of pulleys 445 that allow the wire 410 to be submerged in the acid solution 420 and the rinse bath 430 . the wire 410 is taken up on a take up spool 450 that is run by a variable speed motor drive ( not shown ). the residence time of the wire in the acid bath is determined by the speed of the motor and the length of wire submerged in the bath during operation . examples of acid solution 420 could be fluorine - based acids or any other suitable acid used to dissolve insulating coatings . examples of fluorine - based acid solutions are hydrofluoric acid ( hf ), hydrofluorosilicic ( hfs ) acid , fluoric acid , fluohydric acid , hydrofluoride , fluorine monhydride , or a mixture of hydrofluoric ( hf ) and hydrofluorosilicic ( hfs ) acid . the invention also contemplates various combinations of the previously mentioned fluorine - based acids . examples of other acids are sodium hydroxide ( naoh ), potassium hydroxide ( koh ), caesium hydroxide ( csoh ), tetramethylammonium hydroxide (( ch3 ) 4noh ), and phosphoric acid . rinse bath 430 could be deionized water or any other suitable rinsing agent used to neutralize acid 420 . the pulley system 445 can be a series of pulleys that are comprised of materials resistant to acid 420 and rinsing bath 430 . means ( not shown in the drawing ) can also be provided to replenish any loss of acid 420 or rinse bath 430 . appropriate level sensors or level sensing circuitry and devices ( not shown ) can also be provided to monitor the respective levels of acid 420 and rinse bath 430 . microwires can also be used in magnetic sensing applications . in magnetic sensing applications it can be useful to partially remove the glass coating from the microwire . the magnetic response of the microwire core is related to the stress state of the microwire . the glass coating imparts a compressive axial stress on the wire , and this stress is a function of the thickness of the glass coating . as the thickness of the glass coating changes , the stress on the microwire changes , and therefore the magnetic response also changes . a specific magnetic response of the microwire can be obtained , by uniformly reducing the thickness of the glass coating by a predetermined amount . exemplary embodiments of a method and etchant for removing or etching an insulating coating are described above in detail . while the invention has been described in terms of various specific embodiments , those skilled in the art will recognize that the invention can be practiced with modification within the spirit and scope of the following claims .