valve body 10 , shown in fig1 is an alloy steel structure having cavities including flow passages 12 and valve chamber 14 which are to be provided with a corrosion resistant lining . to prepare for the addition of metal powder , can 16 , having thin tube 18 , flat bottom 20 and thin sleeve 22 extending through the intermediate portion of tube 18 is inserted into valve chamber 14 . bottom 20 is sealed to the end of tube 18 as by welding and sleeve 22 is also sealed to tube 18 as by welding . thin tube 24 is inserted through passages 12 and sleeve 22 as shown . ring 26 is welded to the exterior of can 16 and to the exterior of body 10 as shown and rings 28 and 30 are welded around the ends of tube 24 and to the exterior of body 10 . fill tube 32 extends through ring 26 and fill tube 34 extends through ring 30 . the structure of can 16 , tube 24 and their sealing rings 26 , 28 and 30 provides a space 36 within the walls of passages 12 and chamber 14 . this structure functions as a pressure transmitting yieldable mold or thin metal sealed structure as hereinafter explained . it is important that all of the welds in the structure of can 16 , sleeve 22 and tube 24 be air tight and remain so during the consolidation step to exclude air from the heated metal powder . space 26 within body cavities 12 and 14 is then filled through fill tubes 32 and 34 with a suitable metal powder , such as 316 stainless steel . it is recommended that body 10 be vibrated during filling of space 36 so that it is completely filled with the metal powder before proceeding to the next step . it is preferred that the material of can 16 , tube 24 and rings 26 , 28 and 30 be similar to the material used for the lining . also , it is suggested that space be sufficiently large to provide a lining of consolidated metal which is sufficiently thick to allow for machining to the final shape without any depressions or holidays in the finished lining . when the same material is used for can 16 and tube 24 , a portion of the finished lining may be the material of can 16 and tube 24 . when space 36 is completely filled , a vacuum is drawn thereon by connection of suitable means such as a vacuum pump ( not shown ) to either or both of fill tubes 32 and 34 . sufficient vacuum should be drawn so that the amount of gases present in space 36 will not interfere with the formation of a suitable consolidated metal lining . when the desired vacuum is reached fill tubes 32 and 34 are closed and sealed . if desired , suitable valves ( not shown ) may be secured thereon so that they may be closed when the vacuum drawing step is finished . such valves are recommended to be leak proof when subjected to forming conditions . thereafter , body 10 is placed in an autoclave ( not shown ) or other suitable device wherein it is subjected to forming temperature ( 2100 ° f . approximately and pressure ( 15 , 000 psi approximately ). the body 10 is retained in such forming condition for several hours and then it is allowed to cool . during exposure to forming conditions in the autoclave , can 16 and tube 24 , being yieldable , are expanded to compress the powdered metal against the walls of passages 12 and chamber 14 . the heat and pressure thus cause the metal to be consolidated into a solid lining within the body which is completely bonded to the walls of passages 12 and chamber 14 . if can 16 and tube 24 are made of the same material as the lining , they will be integral with the lining and may form a part of the final product . the cooled body 10 is heat treated as required to obtain the desired mechanical properties and then machined to the shape shown in fig3 . it then has a uniform smooth corrosion resistant lining 40 on the walls of passages 12 and chamber 14 . if can 16 and tube 24 are made of a different material from the lining , they will preferably be entirely removed during the machining step . the modified structure shown in fig4 is positioned in the flow passages 50 and valve chamber 52 of valve body 54 and includes can 56 positioned within valve chamber 52 and spaced from the walls thereof and cans 58 positioned in flow passages 50 and spaced from the walls of such passages . cans 58 also have their bottoms 60 spaced a sufficient distance from the sidewall 62 of can 56 so that during the forming steps none of the cans interfere with the desired movement of any of the other cans . as shown , each of cans 56 and 58 has a bottom welded to its tubular portion as hereinbefore described with respect to can 16 in fig1 . also , cans 56 and 58 ( and can 16 ) may be single piece , deep drawn , structure keeping in mind that they are to remain air tight during the consolidation step . ring 63 is welded around the portion of can 56 extending out of valve body 54 and is welded around its outer periphery to the exterior of valve body 54 as shown . rings 64 and 66 are welded around the portions of cans 58 extending from body 54 and are also welded around their outer peripheries to the exterior of body 54 as shown . fill tube 68 extends through ring 63 to communicate with the space between the exterior of cans 56 and 58 and the interior of body 54 . fill tube 70 extends through ring 64 in a similar manner . the operation of lining the cavities of valve body 54 are as described above with respect to valve body 10 . it is important that cans 56 and 58 be supported in a position to be spaced substantially uniformly from the walls of flow passages 50 and valve chamber 52 so that a substantially uniform thickness of condensed metal is provided on such internal surfaces . it is suggested that the walls to be lined by the method of the present invention be nickel plated as preparation for the forming of a lining by the method of the present invention . it is believed that the nickel plating prevents oxidation , helps obtain bond continuity and prevents the chrome in the metal powder from migrating into the alloy and forming an undesired martensitic structure . it is contemplated that the method of the present invention may be used to provide linings of nickel , nickel alloys , tantalum , hastelloy alloys , copper , copper alloys , cobalt base alloys , stainless steel and titanium alloys and carbides bonded to a body of various grades of alloy steel , carbon steel or stainless steels . the method of the present invention provides a lining on the walls of intersecting bores or cavities in a thick - walled pressure vessel by using the pressure vessel as the base metal to accept the hot isostatic pressed metal powder . the structure shown and described is an alloy steel valve body lined with stainless steel . the method may be used to line the bore and guideways of a blowout preventer body by using two stainless steel tubes as the mold around the space in which the metal powder is placed in place of the tube and can described . the formation conditions ( temperature , pressure , time and degree of vacuum ) are well known and should be adjusted to the particular materials being used .