the problem of light trapping in oleds is well known . in the so - called top - emission device design wherein the light is emitted upwardly from a device disposed on a light - reflecting substrate , a very large percentage of the generated light can be trapped in upper device layers , including oled or electrode layers , which are typically of higher refractive index than protective covering layers or the surrounding atmosphere . ideally , a device covering layer of equal or higher refractive index than , for example , the top electrode layer can promote the efficient collection of light emitted through the electrode , but some means for efficiently extracting light from the device covering layer is still required . in bottom - emission device designs the bottom oled layer is typically in contact with a transparent bottom electrode disposed on a transparent substrate composed , for example , of glass . the bottom electrode is generally of relatively high refractive index in comparison to the glass substrate , however , so trapping of generated light within oled layers or the electrode can again occur . in accordance with one study , a bottom emission diode design evaluated using a classical ray model calculated that 51 % of the initially generated light is trapped within the active organic and electrode layers , 31 . 5 % of the light is trapped within the glass substrate , and only 17 . 5 % of the light is coupled out into the air . thus , in both bottom - and top - emission device designs , some means for reducing internal reflections and allowing more of the generated light to be emitted from the diode structures is needed . the benefits of more efficient light extraction from oleds and other electroluminescent devices go beyond increasing light emission at a given operating power level . the service lives of such devices are influenced by device drive voltages . therefore , improving the light extraction efficiency of such devices would allow operation at lower power levels while achieving the same light outputs . a properly engineered light scattering system , whether in the form of a surface scattering layer or a bulk scattering material , can significantly improve light extraction from these devices . while the opal glass light - scattering layers disclosed in accordance with the present description can be employed to improve the function of a wide variety of light - emitting electroluminescent devices , they offer particular advantages when incorporated into led and oled devices . accordingly , the following descriptions include specific illustrative embodiments of oled designs even though the benefits are not limited thereto . the opal glass materials employed in accordance with the present disclosure typically comprise at least two phases , with the major phase in particular embodiments comprising a silicate glass phase of li 2 o — tio 2 — sio 2 composition . in some embodiments , a li 2 o — tio 2 - sio 2 glass phase comprises a phase wherein the glass comprises li 2 o , tio 2 , and sio 2 , i . e ., with those oxides making up at least about 65 , 70 , 75 , or 80 % by weight of the glass . the light - scattering phase of tio 2 generally comprises only a minor volume fraction ( i . e ., less than 10 % by volume ) of the material . most opal glasses within the above ranges of composition have melting temperatures not exceeding 1400 ° c ., making them well suited for manufacture by conventional melting and forming methods . thus they can be conveniently formed into glass sheets within a thickness range , for example , of about 50 - 500 μm , or about 50 , 100 , 200 , 300 , 400 , or 500 nm thick . such thicknesses provide a level of light scattering that is sufficient to significantly improve light extraction from current oled devices even where relatively rapid quenching of the glass during sheet - forming is employed . moreover , controlling the thermal history of the glass permits tuning of the opacity during forming , securing scattering through the thicknesses of the glass layers as appropriate for any particular device application . securing a light attenuation below about 0 . 01 , 0 . 02 , 0 . 03 , 0 . 04 , 0 . 05 , 0 . 06 , 0 . 07 or 0 . 08 cm − 1 at a light wavelength of 400 nm in these glasses requires that the concentration of light - attenuating species in the glass , particularly including light absorbing transition metals such as iron , be controlled . for that reason opal glass sheet herein , as well as the light - scattering opal glass layers in the oled devices , will generally have compositions comprising less than about 0 . 5 , 0 . 4 , 0 . 3 , 0 . 2 , 0 . 1 , or 0 . 05 % total weight of oxides of iron , nickel , chromium , and manganese . the use of low - iron silica sources such as low - iron sand can help to achieve the necessary limitations on transition metal oxide levels . particular embodiments of opal glass compositions for glass sheets and device layers provided in accordance with the present description comprise those wherein the opal glasses have compositions comprising , in weight percent , about 60 - 85 sio 2 , 10 - 30 tio 2 , and 5 - 15 li 2 o . in addition , however , the glasses may further comprise conventional glass modifiers in limited proportions to the extent not adversely affecting the light - scattering efficiencies of the glasses . as specific examples , these glasses may further comprise , in weight percent , up to about 10 % total of oxides selected from the group consisting of b 2 o 3 , al 2 o 3 , na 2 o k 2 o , and / or cao , and up to about 5 % total of oxides selected from the group consisting of mgo and al 2 o 3 . the opal glass compositions may further comprise conventional glass fining aides such as as 2 o 3 and / or sb 2 o 3 . depending upon the particular device designs selected for the inclusion of light - scattering layers as herein disclosed , the use of opal glasses having refractive indices even higher than about 1 . 6 , 1 . 7 , 1 . 8 , 1 . 9 , or 2 . 0 , may be advantageous . opal scattering layers intended for use in oled devices incorporating transparent electrodes of very high refractive index should be of higher refractive index . for these applications it can be useful to modify the compositions of the disclosed li 2 o — tio 2 — sio 2 glasses by adding refractive - index - increasing constituents to the glass . particular embodiments of such compositions include those wherein the opal glass further contains at least one refractive - index - modifying constituent selected from the group consisting of la 2 o 3 , nb 2 o 5 , ta 2 o 5 , pbo and bi 2 o 3 . opal glass sheets and device layers having refractive indices of at least 1 . 7 , or in some embodiments at least 1 . 8 , are examples of higher index scattering layers of tuned refractive index that can readily be provided through the use of such constituents . as noted above , light - scattering opal glass sheets or layers provided in accordance with the present description can be advantageously employed in a wide variety of oled device designs . these include use in direct contact with top - emission and bottom - emission oled devices , or as covering and / or encapsulating layers for the electrodes used in such devices . light - scattering opal glass sheets can also provide device - supporting substrates , for example , in bottom - emission oled device configurations . illustrative examples of oled device designs incorporating light - scattering opal glass light extraction layers or substrates in accordance with the disclosure are schematically illustrated in fig1 - 3 of the drawings . fig1 presents a schematic cross - sectional view , not in true proportion or to scale , of a top - emitting oled device 10 , the predominant direction of light emission from the device being indicated by the upwardly directed arrow in the figure . device 10 comprises an electron transport layer 12 disposed on and in electrical contact with a hole transport layer 14 to form a light - emitting junction . layer 12 is covered by and in electrical contact with transparent electrode 16 while layer 14 is in electrical contact with opposite light - reflecting electrode 18 , those electrodes operating to power the device . all of the layers are supported on a device substrate 20 . in accordance with the present disclosure , device 10 is further provided with a light - scattering opal glass covering layer 22 , that layer being disposed over and in contact with transparent electrode 16 . the opal glass layer operates to collect and then scatter light traversing the transparent electrode when the device is activated , thereby increasing the amount of light extracted from the device . fig2 of the drawings presents a similar schematic cross - sectional view of a bottom - emitting oled device 30 , the predominant direction of light emission from the device being indicated by the downwardly directed arrow in the figure . device 30 again incorporates an electron transport layer 12 in contact with a hole transport layer 14 to provide a light - emitting junction . in the case of device 30 , however , light reflecting electrode 18 is disposed over electron transport layer 12 while transparent electrode 16 is disposed beneath hole transport layer 14 to allow for the collection and downward emission of light generated within the device . also included in device 30 in accordance with the present disclosure is a light - scattering opal glass layer 22 , disposed between transparent electrode 18 and a transparent device substrate 20 . light - scattering layer 22 operates to extract and downwardly scatter light emitted from the diode junction that collects within transparent electrode 18 . thus the amount of light directed into and downwardly traversing transparent substrate 20 is increased by layer 22 . fig3 of the drawings presents a schematic cross - sectional view of an alternative bottom - emitting oled device 50 , the predominant direction of light emission from the device again being indicated by the downwardly directed arrow in the drawing . the arrangement of electron and hole transport layers 12 and 14 as well as the positioning of transparent electrode 20 and light - reflecting electrode 18 in device 50 are analogous to the arrangements and positioning employed in the design of device 30 . however , device substrate 22 a in device 50 provides a dual function in the oled design , providing both a substrate for supporting the device and a light - scattering functionality for the purpose of increasing the amount of light emitted by the device . for those purposes substrate 22 a comprises a thin sheet of a li 2 o — tio 2 — sio 2 opal glass incorporating a light - scattering tio2 phase as disclosed above , that sheet acting to extract light from transparent electrode 20 and scatter it downwardly from the device . illustrative examples of glass compositions suitable for providing light - scattering opal glass layers or substrates within the scope of the present description are set forth in table 1 below . the glass compositions are reported in parts by weight on the oxide basis as calculated from the batches for melting the glasses . in a typical glass manufacturing procedure , batches for the above glasses are compounded , ball - milled , and melted in platinum crucibles at 1400 ° c . the melts are then cast into glass sheets and annealed at about 490 ° c . to provide stress - free glass castings . the light - transmitting characteristics of the glasses thus provided are evaluated by conducting light transmission measurements on opal glass sheets of known thickness . measurements are taken on both glass samples as initially cast , and on similar samples subjected to supplemental heat treatments to maximize the development of light - scattering tio 2 phases in the glasses . due to the rapid development of light - scattering phases in these glasses , even the samples as cast can exhibit a relatively high degree of opacity due to light scattering . as noted above , a wide range of scattering levels can be produced in these glasses , both through variations in composition and variations in the thermal history of the glass as affected by variations in the forming methods and heat treatments used in manufacture . fig4 of the drawings illustrates the range of variations in light transmission that can be exhibited by the glasses set forth in table 1 . fig4 is a graph presenting curves plotting the light transmissions of samples of these glasses over the wavelength range of visible light as reported on the horizontal axis of the graph . the measured levels of light transmission through the samples are reported in percent transmission on the vertical axis of the graph . transmission curve a in fig4 plots light transmission through a 1 . 2 mm thick sample of glass a from table 1 above as cast from the melt , while transmission curves a ′ and a ″ reflect light transmission through samples of the same glasses , at thicknesses of 0 . 17 mm and 0 . 175 mm , respectively , after four - hour heat treatments at 600 ° c . and 650 ° c ., respectively . curve b plots light transmission values as measured on a 0 . 125 mm thick sample of glass b from table 1 as cast from the melt . the extensive development of light - scattering tio2 phases indicated by the transmission measurements on these glasses confirm that even very thin opal glass layers or substrates are all that will be required to achieve high levels of light scattering and light extraction from oleds and other electroluminescent devices incorporating such glasses . the effectiveness of light - scattering li 2 o — tio 2 — sio 2 opal glass layers for enhancing the extraction of light from electroluminescent devices is shown by the emitted light intensity data presented in fig5 a and 5 b of the drawings . each of those figures comprises a photomicrograph resulting from a three - second exposure to a photoluminescent sample during activation by a uv light source . each figure further comprises a plot of the light extraction data as measured from the photomicrograph . preparation of the photoluminescent samples for measurement comprises providing each sample with a coating of index - matching oil and then covering the right - hand segments of each sample with a light - scattering opal glass sheet of the glass a composition reported in table 1 above . the opal glass sheet employed in fig5 a is of 100 μm thickness and the sheet in fig6 a is of 200 μm thickness . the relative light extraction efficiencies of the two samples are indicated by the enhanced brightness of the opal - glass - covered right - hand segments of the illuminated fields shown in the photomicrographs ( fig5 b and 6b ). the data plotted in the graphs show a brightness enhancement of 2 . 1 × for the 100 μm opal glass sample of fig5 a , and an enhancement of 1 . 4 × for the 200 um opal glass sample of fig6 a . the marked enhancements in light extraction provided by both of the light - scattering opal glass sheets are evident from these figures . yet a further advantage imparted to oled devices provided in accordance with particular embodiments is that the opal glass light - scattering layers comprising the tio 2 light - scattering phases are essentially free of specular transmission and exhibit substantially wavelength - independent lambertian scattering . fig7 of the drawings plots the value of the bidirectional transmittance distribution function ( ccbtdf ) for transmitted light scattered over scattering angles from − 90 ° to + 90 ° through a 0 . 1 mm - thick sample of an opal glass having the composition of glass a from table 1 above . uniform ( lambertian ) scattering is shown at each of the plotted blue ( 400 nm ), green ( 600 nm ), orange ( 800 ) and red ( 1000 ) light wavelengths , with all plots being absent intensity peaks at 0 ° which would be indicative of specular transmission through the sample . while the disclosure has referenced particular embodiments of oled devices and light - scattering opal glass layers and substrates , it will be apparent from those descriptions that the embodiments presented are merely illustrative of the various devices and glasses that may be selected by those of skill in the art for the practice of embodiments within the scope of the appended claims . as used herein , the singular forms “ a ,” “ an ” and “ the ” include plural referents unless the context clearly dictates otherwise . thus , for example , reference to a “ metal ” includes examples having two or more such “ metals ” unless the context clearly indicates otherwise . ranges can be expressed herein as from “ about ” one particular value , and / or to “ about ” another particular value . when such a range is expressed , examples include from the one particular value and / or to the other particular value . similarly , when values are expressed as approximations , by use of the antecedent “ about ,” it will be understood that the particular value forms another aspect . it will be further understood that the endpoints of each of the ranges are significant both in relation to the other endpoint , and independently of the other endpoint . disclosed are materials , compounds , compositions , and components that can be used for , can be used in conjunction with , can be used in preparation for , or are embodiments of the disclosed method and compositions . these and other materials are disclosed herein , and it is understood that when combinations , subsets , interactions , groups , etc . of these materials are disclosed that while specific reference of each various individual and collective combinations and permutation of these compounds may not be explicitly disclosed , each is specifically contemplated and described herein . thus , if a class of substituents a , b , and c are disclosed as well as a class of substituents d , e , and f , and an example of a combination embodiment , a - d is disclosed , then each is individually and collectively contemplated . thus , in this example , each of the combinations a - e , a - f , b - d , b - e , b - f , c - d , c - e , and c - f are specifically contemplated and should be considered disclosed from disclosure of a , b , and c ; d , e , and f ; and the example combination a - d . likewise , any subset or combination of these is also specifically contemplated and disclosed . thus , for example , the sub - group of a - e , b - f , and c - e are specifically contemplated and should be considered disclosed from disclosure of a , b , and c ; d , e , and f ; and the example combination a - d . this concept applies to all aspects of this disclosure including , but not limited to any components of the compositions and steps in methods of making and using the disclosed compositions . thus , if there are a variety of additional steps that can be performed it is understood that each of these additional steps can be performed with any specific embodiment or combination of embodiments of the disclosed methods , and that each such combination is specifically contemplated and should be considered disclosed it will be apparent to those skilled in the art that various modifications and variations can be made to the present disclosure without departing from its spirit and scope . since modifications combinations , sub - combinations and variations of the disclosed embodiments incorporating the spirit and substance of the disclosure may occur to persons skilled in the art , the disclosure should be construed to include everything within the scope of the appended claims and their equivalents .