table 1 shows characteristics of fiber to be used for example 1 and comparative examples 1 and 2 . fibers having the compounding ratios of table 1 are supplied to a manufacturing apparatus shown in fig8 and fig9 to manufacture a female member ( nonwoven ) of a hook - and - loop fastener . manufacturing was conducted under the following conditions . specifically , four nozzles 13 a , each having the hole diameter of 1 . 0 mm and the pitch of 50 mm , are arranged , hot air jet with the temperature of 150 ° c . and an air volume of 0 . 12 m 3 / min / m 2 is then blown from the hot air jet nozzles 13 , and hot blast 20 with the temperature of 150 ° c . and an air volume of 15 m 3 / min / m 2 is thereafter blown in the hot blast heater 15 for approximately 10 seconds . thereby , the air through nonwoven according to the example 1 , having a surface with a basis weight in 35 g / m 2 , a pitch of the rib portions 4 in 5 mm , and a width of the groove 5 in 1 . 3 mm , is obtained . in this case , the groove 5 has apertures 6 formed with the pitch of 5 mm in the md direction . on the other hand , air through nonwovens according to comparative examples 1 and 2 are manufactured at the compounding ratios shown in table 1 under the same conditions as those of example 1 . comparative example 1 is manufactured without the hot air jet being blown from the hot air jet nozzle 13 . comparative example 2 is manufactured by changing the air volume condition of the hot air jet in example 1 to 10 m 3 / min ./ m 2 . comparative example 2 is a nonwoven thicker than example 1 . evaluation is made for peel strength , fluff , holding power , and engagement stickiness using male members all having the same structure which is to be engaged with example 1 and comparative examples 1 and 2 in the md direction . results are shown in table 2 . the thicknesses are shown in table 1 . an evaluation method will be described below . a sample of 10 cm square is measured with the load of 3 g / cm 2 by using a thickness gauge ( product name “ peacok dial thickness gauge no . ci1352 ”). the nonwoven which is a female member is cut into a test piece of 3 to 5 cm × 5 cm . this test piece is bonded to a 5 cm × 8 cm spunbonded nonwoven ( 20 to 30 g / cm 2 ) with a two - sided adhesive tape so as not to be peeled off and this is used as a female member sample 53 . in contrast , a 2 cm × 3 cm male member is bonded to a 12 cm × 3 cm spunbonded nonwoven ( 20 to 30 g / cm 2 ) with a two - sided adhesive tape so as not to be peeled off and this is used as a male member sample 56 . the female member sample 53 is bonded to a 6 cm × 10 cm stainless plate with a two - sided adhesive tape so as not to be creased . thereafter , the male member sample 56 is placed on the female member sample 53 . then , a 700 g roller reciprocates once thereon at a rate of 300 mm / min , so that the test piece ( female member ) and the male member are engaged . after that , a 500 g load is put on the engaged male member sample 56 from its one end for three seconds so that shearing force would act on the engagement surface . note that , the width of the roller is 45 mm and the diameter thereof is 95 mm , and a tape pressure roller of tester sangyo co ., ltd . is used . fig1 shows a 135 ° peel tester in which the above - described stainless plate is attached to an autograph and the male member sample 56 is pulled from one end thereof and to be peeled off so that a peeling angle between the female member sample 53 and the male member sample 56 is to be 135 °. force needed for this peeling is set to be 135 ° peeling force . measurement conditions : load cell = 5 kg , a pulling rate = 300 mm / min between an upper side zipper and a sample = 50 mm ( in vertical direction ) a female member sample 59 to be used for a holding power test as shown in fig1 is made by bonding a 5 cm × 5 cm female member 61 to a 10 cm × 10 cm spunbonded nonwoven ( 20 to 30 g / cm 2 ) with a two - sided adhesive tape so as not to be peeled off . in addition , a male member sample to be used for the holding power test is made by bonding a 2 cm × 4 cm male member 54 to a 4 cm × 8 cm spunbonded nonwoven ( 20 to 30 g / cm 2 ) with a two - sided adhesive tape so as not to be peeled off . the above - described male member sample is placed on the female member sample 59 . thereafter , a 700 g roller reciprocates once thereon at a rate of 300 mm / min so that the male member 54 and the female member 61 are engaged . then , this sample is left under conditions of 20 ° c . and 60 % rh for 30 minutes . fig1 shows a holding power tester in a state where the upper end of the female member sample 59 is suspended by a fastening device 63 . the holding power tester in this state is left in an atmosphere of 40 ° c . with an 800 g weight 64 being suspended at the lower end of the male member sample 62 . then , time until the weight 64 falls when the engagement is peeled off , is measured . this time is set to be holding power . in this case , if the weight 64 does not fall even after 60 minutes , the maximum holding power is set to be 60 minutes . a female member sample used for an engagement stickiness test fig1 is made by sticking a 2 cm × 4 cm female member on a 3 cm × 5 cm spunbonded nonwoven ( 20 to 30 g / cm 2 ) with a two - sided adhesive tape so as not to be peeled off . the size of a male member used for the engagement stickiness test is 1 . 5 cm × 3 cm and a two - sided adhesive tape is stuck on the back surface thereof . this male member is placed on the female member sample . then , a 700 g roller reciprocates once thereon at a rate of 300 mm / min , so that the male member and the female member are engaged . fig1 shows an engagement stickiness tester in which a sample 68 having the male member and the female member being engaged is sandwiched between two of upper and lower l - shaped metal fittings ( weight of 13 . 5 g ) 67 and is attached on the upper and lower l - shaped metal fittings 67 with a two - sided adhesive tape . thereafter , the upper and lower l - shaped metal fittings 67 are attached to the upper and lower autographs 69 so as to measure engagement stickiness force . the measurement is done by setting a displacement distance at the maximum loading to be “ maximum displacement .” as shown in table 2 , with regard to both the front surface and back surface of the female member of example 1 , all results on peel strength of the first to fifth 135 ° peel tests , on fluff , on the holding power test , and on the engagement stickiness test are preferable . in example 1 , on the back surface , the result of the holding power in the fifth peel test is higher than the holding power in the first peel test . the reason is that engagement force is increased because the thickness of the female member is recovered by repeating the peel test . in contrast , in comparative example 1 , peel strength and fluff are preferable , while the holding power test and the engagement stickiness test are not preferable . in comparative example 2 , the sample is peeled off and broken at the fifth peel test . accordingly , the female members according to comparative examples 1 and 2 are not on a level as a preferable female member . here , the broken state is such that connection of the material itself is released in the z direction ( thickness direction ) and the material is peeled off having the male member stuck thereon in a layered state . fig1 shows a characteristic view of the engagement stickiness in the peel test . a curve e shows the engagement stickiness on the front surface of example 1 and a curve f shows the engagement stickiness on the back surface of example 1 . a curve g shows the engagement stickiness of the front surface of comparative example 1 and a curve h shows the engagement stickiness of the front surface of comparative example 2 . in example 1 , both the front surface and the back surface have large stickiness . this application is based upon and claims the benefit of priority from the prior japanese patent application no . jp 2008 - 056903 , filed on mar . 6 , 2008 ; the entire contents of which are incorporated herein by reference . as described above , according to a female member of a hook - and - loop fastener of the present invention , elastic deformation in which a height is increased as a width is narrowed is caused when a dense fiber portion in which a fibrous material has a high basis weight is elongated in a thickness direction . accordingly , engagement with a male member gains stickiness , which results in preferable engagement with the male member . as a result , an absorbent article , such as a disposable paper diaper , a sanitary napkin , a pantiliner is available .