in the following description of the present invention the term stress - induced defect when used in conjunction with silicon substrates is intended to mean dislocations , stacking faults and other silicon crystal plane defects . fig1 is a top view of a polysilicon - bounded test diode for use in a test system for detecting and monitoring stress - induced defects in semiconductor devices according to the present invention . in fig1 polysilicon - bounded test diode 100 is formed in a silicon substrate 105 . polysilicon - bounded test - diode 100 includes a p + diffusion region 110 having a length “ l d ” and a width “ w d ” formed over an n - well region 115 . p + diffusion region 110 is bounded by a peripheral shallow trench isolation ( sti ) region 120 . a peripheral polysilicon gate 125 overlaps the entire sti / p + diffusion region interface 130 giving polysilicon - bounded test diode 100 a high perimeter to area ratio . polysilicon gate 125 has a width “ w p ” and overlaps p + diffusion region 110 by a distance “ o p .” polysilicon - bounded test diode 100 also includes a first probe pad 135 electrically connected to p + diffusion region 110 by a first contact 140 , a second probe pad 145 electrically connected to polysilicon gate 125 by a second contact 150 and a third probe pad 155 connected to an n + diffusion region 160 by a third contact 165 . n + diffusion region 160 provides low resistance electrical connection to n - well 115 . both sti 120 and n + diffusion region 160 are formed in the shapes of rings , the n + diffusion region surrounding the sti . fig2 is a partial cross - sectional view through 2 — 2 of the polysilicon - bounded test diode of fig1 according to the present invention . in fig2 polysilicon gate 125 includes a dielectric layer 170 formed on a top surface 175 of silicon substrate 105 and a polysilicon layer formed on top of the gate dielectric layer . p + diffusion region 110 does not extend below a bottom surface 185 of sti 120 . also , the overlap of polysilicon gate 125 of sti 120 and p + diffusion region 110 is clearly illustrated . in one example , “ l d ” is about 50 to 500 microns , w d ) is about 2 to 10 microns , “ w p ” is about 0 . 5 to 1 . 5 microns and “ o p ” is about 0 . 1 to 0 . 6 microns . gate dielectric layer 170 may be thermal oxide about 1 to 10 nm thick . the lower limit of “ l d ” is chosen so as not to impact the sensitivity of the measurement to be performed and the upper limit is constrained by silicon real estate concerns . that is , large : devices consume valuable silicon area and small devices are subject to noise . the lower limit of “ w p ” is limited by technology ground rules and process equipment limitations ( i . e . photolithography and etching .) the upper limit must be high enough to provide low noise to signal ratios for the measurement being performed , narrow devices being noisier than wider devices . the upper and lower limits of “ o p ” are primarily driven by technology ground rules and process equipment limitations . polysilicon - bounded diode 100 comprises a first portion of a defect test system , the test device . a second portion of the defect test system comprises a control or calibration device and is illustrated in fig3 and 4 and described below . fig3 is a top view of a sti - bounded reference diode for use in a test system in conjunction with the polysilicon - bounded test diode of fig1 for detecting and monitoring stress - induced defects in semiconductor devices , according to the present invention . in fig3 sti - bounded reference diode 200 is formed in silicon substrate 105 . sti - bounded reference diode 200 includes a p + diffusion region 210 having a length “ l d ” and a width “ w d ” formed over n - well region 215 . p + diffusion region 210 is bounded by a peripheral sti 220 . sti - bounded reference diode 200 has a high perimeter to area ratio . sti - bounded reference diode 200 also includes a first probe pad 235 electrically connected to p + diffusion region 210 by a first contact 240 and a second probe pad 255 connected to an n + diffusion region 260 by a second contact 265 . n + diffusion region 260 provides low resistance electrical connection to n - well 215 . both sti 220 and n + diffusion region 260 are formed in the shapes of rings , the n + diffusion region surrounding the sti . fig4 is a partial cross - sectional view through 4 — 4 of the sti - bounded reference diode of fig3 according to the present invention . in fig4 p + diffusion region 210 does not extend below a bottom surface 285 of sti 220 . in one example , “ l d ” is about 50 to 500 microns and “ w d ” is about 2 to 10 microns . in practice , “ l d ” and “ w p ” of polysilicon - bounded test diode 100 would be the same as the “ l d ” and “ w p ” of sti - bounded reference diode 200 . if more than one size of polysilicon - bounded test diode 100 is used , then corresponding sizes of sti - bounded reference diode 200 are used . both polysilicon - bounded test diode 100 and sti - bounded reference diode 200 are fabricated simultaneously and the sti , n - well , p + diffusion and n + diffusion processes would be common to both devices . for both polysilicon - bounded test diode 100 and sti - bounded reference diode 200 reverse polarity diodes may be used . p + diffusion regions would be replaced by n + diffusions , n + diffusions by p + diffusions and n - well by p - well . while sti technology has been illustrated other types of isolation such as local oxidation of silicon ( locos .) the test and reference structures of the first embodiment of the present invention are suitable for both testing both logic devices / processes using complimentary metal - oxide - silicon ( cmos ) and dram technologies . the test and reference structures of the second embodiment are more suited to testing dram technology devices / processes and are illustrated in fig5 and 6 and described below . fig5 is a partial cross - sectional view of a test dram device adapted for use in a test system for detecting and monitoring stress - induced defects in semiconductor devices according to the present invention . in fig5 a test dram device 300 is formed in a p + silicon substrate 305 and in a p − epitaxial layer 310 grown on the p + silicon substrate . formed in p epitaxial layer 310 is a n - well 315 . a p − region 320 of p − epitaxial layer 310 remains p type doped between n - well 315 and p + substrate 305 . an n + diffusion 325 provides low resistance electrical connection to n - well 315 . also formed in n - well 315 is sti 330 . sti 330 does not extend into p − region 320 . further formed in n - well 315 is a deep trench capacitor 335 . deep trench capacitor 335 extends through n - well 315 , p − region 320 and into p + substrate 305 . deep trench capacitor 335 comprises a polysilicon core 340 surrounded by a dielectric liner 342 . formed in n - well 315 , between sti 330 and deep trench capacitor 335 is a pfet transfer device 345 . pfet transfer device 345 comprises a first p + diffusion 350 a adjacent to sti 330 , a second p + diffusion region 350 b adjacent to deep trench capacitor 335 , channel region 355 and a polysilicon gate 360 . first p + diffusion 350 a and second p + diffusion 350 b are separated by a channel region 355 of n - well 315 . polysilicon gate 360 is formed over channel region 355 and aligned to first and second p + diffusions 350 a and 350 b . polysilicon gate 360 comprises a gate dielectric portion 365 formed over channel region 355 and a polysilicon portion 370 formed on top of the gate dielectric portion . a metal strap 375 electrically connects deep trench capacitor 335 to second p + diffusion 350 b . schematically illustrated in fig5 is a substrate contact 380 to p + substrate 305 , an n - well contact 385 to n + diffusion 325 , a bit - line contact 390 to first p + diffusion 350 a and a word line contact 395 to polysilicon gate 360 . test dram device 300 comprises a first portion of a defect test system , the test device . a second portion of the defect test system comprises a control or calibration device and is illustrated in fig6 and described below . fig6 is a partial cross - sectional view of a reference device adapted for use in a test system in conjunction with the test dram of fig5 for detecting and monitoring stress - induced defects in semiconductor devices , according to the present invention . in fig6 a reference device 400 is formed in a p + silicon substrate 305 and in a p − epitaxial layer 310 grown on the p + silicon substrate . formed in p − epitaxial layer 310 is an n - well 415 . a p − region 320 of p − epitaxial layer 310 remains p type doped between n - well 415 and p + substrate 305 . an n + diffusion 425 provides low resistance electrical connection to n - well 415 . also formed in n - well is sti 430 . sti 430 does not extend into p − region 320 . further formed in n - well 415 is a deep trench capacitor 435 . deep trench capacitor 435 extends through n - well 415 , p − region 320 and into p + substrate 305 . deep trench capacitor 435 comprises a polysilicon core 440 surrounded by a dielectric liner 442 . formed in n - well 415 , between sti 430 and deep trench capacitor 435 is a p + diffusion 450 . a metal strap 475 electrically connects deep trench capacitor 435 to p + diffusion 450 . schematically illustrated in fig6 is a substrate contact 480 to p + substrate 305 , an n - well contact 485 to n + diffusion 425 and a p + diffusion contact 495 to p + diffusion 450 . while a pfet transfer device has been illustrated for test dram device 300 and a p + diffusion for reference device 400 , the present invention is equally applicable to a test dram device using an nfet transfer device in conjunction with a reference device using a n + diffusion . when used for semiconductor process development or product testing and / or screening , multiplicities of polysilicon - bounded test diodes 100 with or without sti - bounded reference diodes 200 and / or test dram devices 300 with / or without reference devices 400 may , in one example , be formed in the kerf areas of chips on semiconductor wafers during chip fabrication and tested at appropriate points in the process . sets of polysilicon - bounded test diodes 100 , sti - bounded reference diodes 200 of varying dimension “ w d ”, “ l d ”, “ o p ” and “ w p ” may be used . it should be noted that whenever a test methodology uses a test dram device 300 ( see fig5 ) the terms “ bit line contact ( 390 )” and “ first p + diffusion region ( 350 a )” are interchangeable , the terms “ word line contact ( 395 )” and “ gate ( 360 )” are interchangeable , the terms “ n - well contact ( 385 )” and “ n - well ( 315 )” are interchangeable and the terms “ substrate contact ( 380 )” and “ substrate ( 305 )” are interchangeable . it should be noted that whenever a test methodology uses a reference device 400 ( see fig6 ) the terms “ p + diffusion contact ( 495 )” and “ p + diffusion ( 450 )” are interchangeable and the terms “ substrate contact ( 480 )” and “ substrate ( 305 )” are interchangeable . fig7 a through 7c are flowcharts illustrating first , second and third test methodologies respectively , according to a first embodiment of the present invention . referring to fig7 a , in step 500 , a polysilicon - bounded test diode 100 ( see fig1 and 2 ) is selected . in step 505 , polysilicon - bounded test diode 100 is maintained at a pre - selected temperature . in one example , the pre - selected temperature is 180 ° c . however , any temperature in the range of about 100 to 200 ° c . may be used . in step 510 , polysilicon gate 125 , n - well 115 and substrate 105 ( see fig1 ) are held at ground potential . in one example , ground potential is about 0 volts . in step 515 , p + diffusion region 110 ( see fig1 ) is ramped from about 0 volts to about − 6 volts . in step 520 , the current through polysilicon gate 125 ( see fig1 ) is monitored for current spikes . an example is illustrated in fig8 and 9 and described below . referring . to fig7 b , in step 525 , a test dram device 300 ( see fig5 ) is selected . in step 530 , test dram device 300 is maintained at a pre - selected temperature . in one example , the pre - selected temperature is 180 ° c . however , any temperature in the range of about 100 to 200 ° c . may be used . in step 535 , n - well contact 385 , and bit line contact 390 are held at ground potential and word line contact 395 is held at a voltage sufficient to turn on transfer device 345 ( see fig5 ) in one example , ground potential is about 0 volts and the turn on voltage is about − 2 volts . in step 540 , substrate contact 380 ( see fig5 ) is ramped from about 0 volts to about − 6 volts . in step 545 , the current through bit line contact 390 ( see fig5 ) is monitored for current spikes . referring to fig7 c , in step 550 , a test dram device 300 ( see fig5 ) is selected . in step 555 , test dram device 300 is maintained at a pre - selected temperature . in one example , the pre - selected temperature is 180 ° c . however , any temperature in the range of about 100 to 200 ° c . may be used . in step 560 , n - well contact 385 , by substrate contact 380 and wordline contact 395 ( see fig5 ) are held at ground potential . in - one example , ground potential is about 0 volts . in step 565 , bit line contact 390 ( see fig5 ) is ramped from about 0 volts to about − 6 volts . in step 570 , the current through word line contact 395 ( see fig5 ) is monitored for current spikes . fig8 is a plot of p + diffusion and gate currents versus diffusion reverse bias voltage for the polysilicon - bounded test diode of fig1 having no stress - induced defects and fig9 is a plot of p + diffusion and gate currents versus diffusion reverse bias voltage for the polysilicon - bounded test diode of fig1 having stress - induced defects . while fig8 and 9 are for polysilicon - bounded test diodes having a gate dielectric of five nm of thermal oxide , similar plots would be obtained for the test dram device of fig3 . it is clear from fig8 and 9 , that the diffusion reverse bias leakage is higher for a polysilicon - bounded diode with stress - induced defects then for a polysilicon - bounded diode without stress - induced defects . comparing fig8 and 9 , it may be seen that the gate current for a polysilicon - bounded diode with stress - induced defects exhibits spiking or sudden increases by as much as ten times more than the background gate leakage , as the p + diffusion reverse bias voltage is changed from 0 to about − 4v . this behavior is not present for the polysilicon - bounded test diodes without stress - induced defects . for reverse bias voltages more negative than − 4 v , the gate current increases exponentially due to fowler - nordhein tunneling , and the gate current becomes more significant than the spiking due to the stress - induced defects . the spiking in gate current occurs because of carrier generation at the site of the stress - induced defects , which act as carrier - generation sites . in the case of a test dram device , the processing of the deep trench could cause stress - induced defects to be generated in the p + substrate very close to the outer surface of the thin insulator of the deep trench . under the second test methodology the presence of stress - induced defects causes spiking in the current flowing through the thin insulator of the deep trench , which then flows from the polysilicon filling the deep trench , through the channel of the transfer device and can be measured at the diffusion terminal . under the third test methodology , stress - induced defects in the n - well / p + diffusion close to the thin gate dielectric of the transfer device are detected . when polysilicon - bounded test diodes 100 and test dram devices 300 are used in testing for stress - induced defects under the first , second and third test methodologies , the screen or fail limit for gate current spiking due to presence of stress - induced defects is about a three times increase in gate current over the background value . this increase in gate current can be observed by any of several techniques known in the art , such as connecting an oscilloscope to the polysilicon gate terminal . fig1 a and 10b are flowcharts illustrating fourth and fifth test methodologies respectively , according to a second embodiment of the present invention . referring to fig1 a , in step 575 , one or more polysilicon - bounded test diodes 100 ( see fig1 and 2 ) is selected . in step 580 , for each polysilicon - bounded test diode 100 , polysilicon gate 125 , n - well 115 and substrate 105 ( see fig1 ) are held at ground potential . in one example , ground potential is about 0 volts . in step 585 , for each polysilicon - bounded test diode 100 , p + diffusion region 110 ( see fig1 ) is ramped from about 0 volts to about 0 . 85 volts . in step 590 , for each polysilicon - bounded test diode 100 , the current through p + diffusion region 110 ( see fig1 ) is measured as a function of voltage and a frequency distribution analysis of the slope of the forward bias voltage / p + diffusion current at a pre - selected forward bias voltage is performed . in step 595 , one or more sti - bounded reference diodes 200 ( see fig3 and 4 ) is selected . in step 600 , for each sti - bounded reference diode 200 , n - well 215 , and substrate 105 ( see fig3 ) are held at ground potential . in one example , ground potential is about 0 volts . in step 605 , for each sti - bounded reference diode 200 , p + diffusion 210 ( see fig3 ) is ramped from about 0 volts to about 0 . 85 volts . in step 610 , the current through p + diffusion region 210 ( see fig3 ) is measured as a function of voltage and a frequency distribution analysis of the slope of forward bias voltage / p + diffusion current at the pre - selected forward bias voltage is performed . in step 615 , the frequency distributions of the slope of the forward bias voltage / p + diffusion current at the pre - selected voltage value for polysilicon - bounded diodes 100 and sti - bounded reference diodes 200 are compared . an example forward bias voltage versus p + diffusion current and of a frequency distribution analysis are illustrated in fig1 and 12 and described below . referring to fig1 b , in step 620 , one or more test dram devices 300 ( see fig5 ) is selected . in step 625 , for each test dram devices 300 , n - well contact 385 and substrate contact 380 are held at ground potential and in step 630 , word line contact 395 is held at a voltage sufficient to turn off transfer device 345 ( see fig5 .) in one example , ground potential is about 0 volts and the turn off voltage is about 2 volts . in step 635 , for each test dram devices 300 , bit line contact 390 ( see fig5 ) is ramped from about 0 volts to about 0 . 85 volts . in step 640 , for each test dram devices 300 , the current through bit line contact 390 ( see fig5 ) is measured as a function of voltage and a frequency distribution analysis of the slope of forward bias voltage / bit line current at a pre - selected forward bias voltage is performed . in step 645 , one or more reference devices 400 is selected . in step 650 , for each reference device 400 , n - well contact 485 and substrate contacts 490 are held at ground potential . in one example , ground potential is about 0 volts . in step 655 , for each reference device 400 , p + diffusion contact 495 ( see fig6 ) is ramped from about 0 volts to about 0 . 85 volts . in step 660 , for each reference device 400 , the current through p + diffusion contact 495 ( see fig6 ) is measured as a function of voltage and a frequency distribution analysis of the slope of forward bias voltage / bit line current at the pre - selected forward bias voltage is performed . in step 665 , the frequency distributions of the slope of the forward bias voltage / bit line current at the pre - selected voltage value for the test dram 300 and reference device 400 are compared . fig1 is a plot of the forward bias current versus forward bias voltage for three different polysilicon - bounded test diodes of fig1 each having different quantities of stress - induced defects and fig1 is a histogram of the distribution of the slope , in mv / decade of current versus the forward bias current voltage characteristics of polysilicon - bounded test diodes of fig1 and sti - bounded reference diodes of fig3 . while fig1 and 12 are for polysilicon - bounded test diodes and sti - bounded reference diodes , similar plots would be obtained for the test dram device of fig5 and the reference device of fig6 . the forward bias slope of forward bias current versus bias voltage is defined by the amount of forward bias voltage / decade of diode current . this slope has a value of 59 . 4 mv / decade at room temperature ( 27 ° c .) for a silicon diode without stress - induced defects . using equation ( 1 ) the value of the forward bias slope may be calculated to be 59 . 4 mv / decade at room temperature ( 27 ° c .) diodes with stress - induced defects show forward bias slopes higher than 59 . 4 mv / decade . fig1 indicates that the increase in the slope becomes more significant as the density of dislocations increases from none to low to high . in fig1 , measurements on a set of polysilicon - bounded test diodes with no stress - induced defects , a low level of stress - induced defects , a medium level of stress - induced defects and a high level of stress - induced defects are plotted . the level of stress - induced defects was verified by transmission electron microscopy ( tem .) fig1 is a histogram of the distribution of the slope , in mv / decade of current versus the forward bias current - voltage characteristics of polysilicon - bounded test diodes of fig1 and sti - bounded reference diodes of fig3 . in fig1 , the distribution of forward bias voltage versus current slopes is plotted as a histogram for one or more polysilicon - bounded test diodes and one or more sti - bounded reference diodes at a predetermined forward bias voltage ( in this example , 0 . 45 volts .) sti - bounded reference diodes have no stress - induced defects ( see below .) the dimensions for both polysilicon - bounded and sti - bounded diodes was , in this example , “ w p ”= 0 . 5 microns and “ l d ”= of 100 microns ( see fig1 .) fig1 illustrates that for diodes with stress - induced defects , the forward bias versus current slopes at the pre - determined forward bias voltage have values well in excess of 59 . 4 mv / decade of current , reaching as high as 112 mv / decade of current . when this test methodology is used for testing the screen or fail limit for the forward bias slope ( at a pre - determined voltage ), indicating presence of stress - induced defects may be set , in one example , at 64 mv / decade , which is about 8 % above the target value of 59 . 4 mv / decade for the forward bias slope of diodes without dislocations . this 8 % tolerance allows for variations in measurement sensitivity . experiments performed with sti - bounded reference diodes , showed normal forward bias slope with no indication of stress - induced defects indicating sti - bounded reference diodes are suitable for use as control devices . the presence of stress - induced defects ( in one example , dislocations ) in polysilicon - bounded test diodes and lack of stress - induced defects ( dislocations ) in sti - bounded reference diodes was verified by transverse electron microscope ( tem ) analysis . determination of forward bias voltage versus current slope at about 0 . 4 to 0 . 5 volts of forward bias is optimum for this test methodology . use of about 0 . 4 to 0 . 5 volts of forward bias voltage , with semiconductor stress - induced defects , results in the maximum increase in forward bias versus current slope with the presence of stress - induced defects , resulting in high sensitivity for the detection and characterization of stress - induced defects . fig1 a , 13 b and 13 c are flowcharts illustrating sixth , seventh and eighth test methodologies respectively , according to a third embodiment of the present invention . referring to fig1 a , in step 670 , one or more polysilicon - bounded test diodes 100 ( see fig1 and 2 ) is selected . in step 675 , each polysilicon - bounded test diode 100 is maintained at a pre - selected temperature . in one example , the pre - selected temperature is 160 ° c . however , any temperature in the range of about 100 to 200 ° c . may be used . in step 680 , for each polysilicon - bounded test diode 100 , n - well 115 , substrate 105 and polysilicon gate 125 ( see fig1 ) are held at ground potential . in one example , ground potential is about 0 volts . in step 685 , for each polysilicon - bounded test diode 100 , a pre - determined voltage is applied to p + diffusion region 110 ( see fig1 ) for at least a pre - determined time . in one example , the predetermined voltage is about − 6 . 3 volts or less and the pre - determined time is about 0 . 5 hours or more . in step 690 , for each polysilicon - bounded test diode 100 , the current through polysilicon gate 125 ( see fig1 ) is monitored for “ soft ” breakdown . “ soft ” breakdown is defined as an increase in gate current of about 10 to 50 times the breakdown current of an unstressed gate . “ hard ” breakdown is defined as an increase in gate current greater than about 50 times the breakdown current of an unstressed gate . ( in the present example , − 6 . 3 volts for 0 . 5 hours are the stress conditions .) referring to fig1 b , in step 700 , one or more test dram devices 300 is selected . in step 705 , each test dram device 300 is maintained at a pre - selected temperature . in one example , the pre - selected temperature is 160 ° c . however , any temperature in the range of about 100 to 200 ° c . may be used . in step 710 , for each test dram device 300 , n - well contact 385 and bit line contact 390 ( see fig5 ) are held at ground potential . in one example , ground potential is about 0 volts . in step 715 , for each test dram device 300 , word line contact 395 is held at a voltage sufficient to turn on transfer device 345 ( see fig5 .) in step 72 g , for each test dram device 300 , a pre - determined voltage is applied to substrate contact 380 ( see fig5 ) for at least a pre - determined time . in one example , the predetermined voltage is about − 5 . 0 volts or less and the pre - determined time is about 0 . 5 hours or more . in step 725 , for each test dram device 300 , the current through bit line contact 390 ( see fig5 ) is monitored for “ soft ” breakdown . referring to fig1 c , in step 730 , one or more test dram devices 300 ( see fig5 ) is selected . in step 735 , each test dram device 300 is maintained at a pre - selected hi temperature . in one example , the pre - selected temperature is 160 ° c . however , any temperature in the range of about 100 to 200 ° c . may be used . in step 740 , for each test dram device 300 , n - well contact 385 , substrate contact 380 and word line contact 395 ( see fig5 ) are held at ground potential . in one example , ground potential is about 0 volts . in step 745 , for each test dram device 300 , a pre - determined voltage is applied to bit line contact 390 ( see fig5 ) for at least a pre - determined time . in one example , the predetermined voltage is about − 6 . 3 volts or less and the pre - determined time is about 0 . 5 hours or more . in step 750 , for each test dram device 300 , the current through word line contact 395 ( see fig5 ) is monitored for “ soft ” breakdown . fig1 is a plot of the polysilicon gate current versus stress time for polysilicon - bounded test diodes of fig1 with and without stress - induced defects . the data plotted in fig1 was obtained from a polysilicon - bounded test diode having 5 nm of thermal oxide gate dielectric . the stress conditions were − 6 . 3 volts at 160 ° c . for about 1 . 5e5 seconds . it may be readily seen from fig1 that the gate current prior to breakdown ( prior to about 2 . 8e4 seconds ) is about the same for diodes with and without stress - induced defects . fig1 clearly illustrates that polysilicon - bounded test diodes with stress - induced defects show earlier breakdown than polysilicon - bounded test diodes without stress - induced defects . the earlier gate breakdown in polysilicon - bounded test diodes having stress - induced defects is attributed to the stress - induced defects causing spikes in the gate current which in turn stresses the gate dielectric causing it to breakdown . fig1 also clearly illustrates polysilicon - bounded diodes with stress - induced defects exhibit “ soft ,” limited , breakdown as defined above . in “ hard ” breakdown , the increase in gate current is limited only by the external circuit resistance , with almost no resistance contribution due to the gate oxide . while fig1 is for polysilicon - bounded test diodes , similar plots would be obtained for the test dram device of fig5 . the seventh test methodology ( illustrated in fig1 b and described above ) is particularly suited to detect stress - induced defects in the substrate near the deep trench capacitor . the eighth test methodology ( illustrated in fig1 c and described above ) is particularly suited to detect stress - induced defects in the p + diffusion / n - well interface near the gate dielectric of the transfer device . it should be noted that the optimization of the polysilicon - bounded test diode / sti - bounded reference diode test system for the detection and characterization of the semiconductor stress - induced defects is a strong function of the perimeter - to - area ratio of polysilicon gate 125 of polysilicon - bounded test diode 100 of fig1 . the sensitivity of stress - induced defect detection using the polysilicon - bounded test diode / sti - bounded reference diode test system increases as the gate perimeter to area ratio increases . a polysilicon gate perimeter - to - area ratio of 1 . 48 / microns has been found to give satisfactory sensitivity . it should also be noted that that the optimization of the polysilicon - bounded test diode / sti - bounded reference diode test system for the detection and characterization of the semiconductor stress - induced defects is also a function of the overlap space of polysilicon gate 125 with p + diffusion region 110 (“ o p ” in fig1 ) an “ o p ” value of about 0 . 26 microns has been found to give satisfactory sensitivity . the structures and the test methodologies of the present invention may be used to monitor formation of stress - induced defects during fabrication of semiconductor devices providing a powerful tool for improving those processes in order to lower the number of stress - induced defects those processes cause . by use of the structures and the test methodologies of the present invention , processes and tools that contribute stress - induced defects can be more easily identified and corrected . it has been found because of the sensitivity of polysilicon - bounded test diode 100 ( see fig1 and 2 ), such a device having intentionally created dielectric defects will function as an antifuse . we now turn our attention to this embodiment of the present invention . a diode ( or antifuse ) having a p + diffusion region in an n - well is defined as a pn diode ( or pn antifuse .) a diode ( or antifuse ) having a n + diffusion region in a p - well is defined as an np diode ( or antifuse .) fig1 a through 15k are partial cross - sectional views illustrating fabrication of an antifuse according to the present invention . a top view is illustrated in fig1 and the sections illustrated in fig1 a through 15k are taken through line 2 — 2 of fig1 . fig1 a through 15k illustrate formation of a pn diode . an np diode may be formed in a similar manner . only the processes illustrated in fig1 se and described below differ from the processes that may be used to fabricate polysilicon - bounded test diode 100 . in the case of an antifuse the following dimensions are applicable ( see fig1 ): “ l d ” is about 1 to 500 microns , “ w d ” is about 1 to 10 microns , “ w p ” is about 0 . 5 to 1 . 5 microns and “ o p ” is about 0 . 1 to 0 . 6 microns . in fig1 a , a silicon substrate 800 is provided . a ring of sti 805 is formed in silicon substrate 800 by , for example , well known trench etch and chemical - mechanical - polish ( cmp ) processes . sti 805 has an inner perimeter 807 and an outer perimeter 808 . in one example , silicon substrate 800 is doped p − with boron ( b ) at a concentration of 5e15 atoms / cm 2 . in fig1 b , an n - well 810 is formed by ion implantation of phosphorus ( p .) in one example , multiple phosphorous implants are performed , a first p implant at an energy of 650 kev and a dose of 2 . 4e13 atoms / cm 2 , a second p implant at an energy of 300 kev and a dose of 5e12 atoms / cm 2 and a third p implant at an energy of 35 kev and a dose of 1e12 atoms / cm 2 . for a np diode , boron would be implanted to form a p - well instead of an n - well . in one example , for an np diode , the first implant is b at an energy of 260 kev and a dose of 2 . 2e13 atoms / cm 2 , the second implant is b at an energy of 130 kev and a dose of 6e12 atoms / cm 2 and the third implant is bf 2 at an energy of 35 kev and dose of 1e12 atoms / cm 2 . n - well 810 extend below a bottom 815 of sti 805 . in fig1 c , a gate dielectric layer 820 is formed on a top surface 825 of silicon substrate 800 and a polysilicon layer 830 is formed on a top surface 835 of the dielectric layer . in one example , dielectric layer 820 is thermal oxide about 10 to 120 å thick and polysilicon layer 830 is about 1200 to 2000 å thick formed by well known low pressure chemical vapor deposition ( lpcvd ) processes . in fig1 d , dielectric layer 820 and polysilicon layer 830 are selectively removed by well know photolithographic and reactive ion etch ( rie ) to form polysilicon gate 840 . polysilicon gate 840 has an inner perimeter 842 and an outer perimeter 843 . polysilicon gate 840 overlaps inner perimeter 807 of sti 805 . in fig1 e , a protective layer 845 is formed on top surface 825 of substrate 800 . a photoresist layer 850 is formed and patterned ( by well known photolithographic processes ) on top of protective layer 845 . protective layer 845 is exposed only inside of antifuse area 855 . in one , example , protective layer 845 is about 60 å of thermal oxide . a heavy ion specie implant is performed in order to create defects in the inner perimeter 860 of gate dielectric 820 . in one example , the heavy ion specie is germanium ( ge ) implanted at an energy of 40 kev , a dose of 3e15 atoms / cm 2 and an angle of 7 degrees . in a second example , the heavy ion specie is arsenic ( as ) implanted at an energy of 45 kev , a dose of 5e15 atoms / cm 2 and an angle of 7 degrees . the higher the atomic weight of the heavy ion specie , the lower the implantation dose and energy required in order to induce the desired damage in inner perimeter 860 of gate dielectric 820 . then photoresist layer 850 is removed . in fig1 f , protective layer 845 of fig1 e is removed . first silicon nitride spacers 865 are formed by well - known processes , on sidewalls 870 of polysilicon gates 840 . in one example first silicon nitride spacers 865 are formed from about a 125 å thick film of silicon nitride . then an angled halo ion implant is performed . in the case of a pn diode , the halo implant includes a relatively low energy and low dose implant ( s ) selected from the group consisting of germanium , arsenic , indium , boron and combinations thereof . in the case of a np diode , the halo implant includes a relatively low energy and low dose implant ( s ) selected from the group consisting of germanium , arsenic , boron ( as bf 2 ) and combinations thereof . in fig1 g , second silicon nitride spacers 875 are formed over first silicon nitride spacers 865 by well - known processes . in one example second silicon nitride spacers 875 are formed from about a 800 å thick film of silicon nitride . in fig1 h , a photoresist layer 880 is formed and patterned ( by well known photolithographic processes ) on top surface 825 of silicon substrate 800 . an ion implant is performed to form n + n - well contacts 885 . the ion implant includes relatively low energy and low to high dose implant ( s ) selected from the group consisting of germanium , phosphorous and combinations thereof . in the case of a np diode , the ion implant includes a relatively low energy and low to high dose implant ( s ) selected from the group consisting of germanium , boron and combinations thereof . photoresist layer 880 is then removed . in fig1 i , a photoresist layer 885 is formed and patterned ( by well known photolithographic processes ) on top surface 825 of silicon substrate 800 . an ion implant is performed to form a p + diffusion region 890 in n - well 810 between sti 815 . the ion implant includes relatively low energy and low to high dose implant ( s ) selected from the group consisting of germanium , boron and combinations thereof . in the case of a np diode , the ion implant includes a relatively low energy and low to high dose implant ( s ) selected from the group consisting of germanium , phosphorus and combinations thereof to form an n + diffusion region . photoresist layer 885 is then removed . in fig1 j , a silicide layer 895 is formed by well - known processes on n - well contact 885 , p + diffusion region 890 and on top of gates 840 . in one example , silicide layer is cobalt silicide , titanium silicide or combinations thereof . in fig1 k , a dielectric layer 900 is formed on top lo , surface 825 of substrate 800 . a multiplicity of stud contacts 905 are formed in dielectric layer 900 to make electrical contact to n - well contacts 905 and thence to n - well 810 , gates 840 and p + diffusion region 890 . fig1 is a weibull distribution for time - to - fail ( t bd ) and charge - to - breakdown ( q bd ) for a polysilicon - bounded test diode of fig1 used as an antifuse , with and without stress - induced defects . fig1 compares a pn antifuse represented having a gate dielectric thickness of 5 nm of thermal oxide and having received a 7 degree angled germanium ion implant of 3e14 atoms / cm 2 at an energy of 40 kev as illustrated in fig1 e and described above to a pn antifuse without the germanium implant . stress conditions were polysilicon gate and n - well at ground , p + diffusion at − 6 . 3 volts and temperature at 160 ° c . fig1 is a plot of the dielectric breakdown field at 30 ° c . versus germanium implantation dose of the antifuse of fig1 k . for an antifuse to be reliably programmed a current density sufficient to induce a breakdown of the gate dielectric must flow through the dielectric . the voltage applied to the gate to obtain breakdown of the gate dielectric is the programming voltage . implantation of heavy ion specie degrades the gate dielectric quality , effectively allowing more current through the gate dielectric for a given gate voltage then would occur without the implant thus causing more damage to the dielectric for a given voltage . prior to heavy ion specie implantation , the gate dielectric breakdown electric field for dielectric thickness at or below 12 nm is about 14 mv / cm . fig1 clearly shows that electric field required for breakdown of the gate dielectric is very sensitive to heavy ion specie implant dose and is significantly lowered even at relatively low implant doses . fig1 is a plot of dielectric breakdown voltage versus the inverse of absolute temperature of the antifuses of fig1 k , fabricated with two thickness of dielectric . fig1 indicates that the breakdown voltage drop with increasing temperature has an activation energy of about 0 . 0124 ev . from the required energy to induce the required gate dielectric breakdown , it was determined that the minimum required programming current is under 2 micro amperes to be applied for a duration of about 0 . 05 seconds or a pn antifuse fabricated as illustrated in fig1 a through 15g and described above and having a “ l d ”= 1 . 5 cm and a “ w d ”= 1 . 0 μm . fig1 is a plot of dielectric breakdown voltage versus germanium implantation dose of the antifuse of fig1 k at three temperatures . similar plots can be directly obtained for any other gate dielectric thickness using equation ( 2 ): t ox is the effective electrical thickness of the gate dielectric taking into account any polysilicon depletion or surface depletion effects ; and where δh is the activation energy ( 0 . 0124 ev from fig1 ); the area of the damaged edge of the gate dielectric following germanium implantation is very small ( much less than one square micrometer .) thus , the area of the antifuse fuse of the present invention may be very small , for example , as small as about 1 - 2 square micrometers . in fact , the area of the antifuse is limited only by the minimum critical dimension of the photolithographic system used to fabricate the antifuse . the gate dielectric resistance prior to breakdown is in excess of 10 10 ohms at one volt . the gate dielectric resistance following breakdown is equal to or less than 1000 ohms , at one volt . thus , the ratio of the dielectric resistance prior to breakdown , to that following breakdown , at one volt , is greater than 10 7 . the plots illustrated in fig1 , 18 and 19 may be used to determine the required implantation dose of germanium necessary to induce breakdown at any desired voltage and temperature . in one example : for a polysilicon - bounded pn diode used as an antifuse , having a gate dielectric thickness of 5 nm and receiving a 7 degree germanium implantation at an energy of 40 kev and a dose of 3e15 atom / cm 2 , the required breakdown voltage is about 3 . 3v at 30 ° c . thus , it has been shown that the programming voltage of antifuse of the present invention is controlled by or tunable by heavy ion implant dose , gate dielectric thickness and temperature . it has further been shown that the programming voltage of antifuse of the present invention is dependent upon : the area of the region of the gate dielectric damaged by heavy ion specie implant and independent of the total area of the antifuse . the description of the embodiments of the present invention is given above for the understanding of the present invention . it will be understood that the invention is not limited to the particular embodiments described herein , but is capable of various modifications , rearrangements and substitutions as will now become apparent to those skilled in the art without departing from the scope of the invention . therefore it is intended that the following claims cover all such modifications and changes as fall within the true spirit and scope of the invention .