to address the problem of providing adequate quantitative and qualitative analysis to batches of silicone adhesive containing compositions , two ir methods were developing using the near ir ( 2500 nm - 1100 nm ) and mid ir ( 4000 cm - 1 to 650 cm - 1 ) regions found in the electromagnetic spectrum . both methods were used to predict two different lots of silicone adhesive supplied by dow corning . the concentrations determined were within acceptable limits for an analytical test method . in addition , an out of specification lot was measured using the qualitative method to assess conformity with prior good lots . one of the unique aspects of the near ir method is that the method requires no clean up of the instrument . the samples are measured in flat and optically clear borosilicate glass vials using a diffuser that reflects light back to the detector . this makes analysis time extremely rapid . total analysis time is less than one minute ( approximately 30 - 35 seconds ). for the mid ir method , a single bound diamond atr ( attenuated total reflectance ) accessory is used that is able to be cleaned with petroleum distillates and dodecylbenzensulphonic acid . once the adhesive is removed and solvent is applied , the atr accessory can be cleaned and dried with dilute soap and water and alcohol . total analysis time is about 2 minutes or less . one embodiment of the invention is a method of validating the amount of silicone adhesive in a composition comprising silicone adhesive and silicone polymer , wherein the silicone adhesive and silicone polymer are not the same compound , which comprises of the steps of : ( a ) making calibration standard compositions containing silicone adhesive and silicone polymer wherein at least one of said calibration standard compositions is within the range selected from the group consisting of within 1 . 0 wt . % and within 0 . 5 wt . % of the pre - determined acceptable range for the amount of silicone adhesive ; ( b ) optionally , subjecting the calibration standard compositions from step ( a ) to : wherein the ir spectra obtained from the calibration standard composition is used to form ( 1 ) a calibration curve representing the amount of silicone adhesive ; and ( 2 ) an ir spectra fingerprint unique to the pre - determined acceptable range for the amount of silicone adhesive in the silicone adhesive and silicone polymer containing composition ; ( c ) obtaining a sample from a composition comprising silicone adhesive and silicone polymer ; comparing ir spectra obtained in step ( d ) with the calibration curve and ir spectra fingerprint from step ( b ), wherein a composition comprising silicone adhesive and silicone polymer is validated when having substantially the same pre - determined acceptable range for the amount of silicone adhesive as determined by the calibration curve and having substantially the same ir spectra fingerprint . in another embodiment of the method described above , prior to step ( a ) a pre - determined acceptable range for the amount of silicone adhesive is established for the silicone adhesive and silicone polymer containing composition ; in another embodiment of the method described above , the method of validating is repeated for a different composition comprising silicone adhesive and silicone polymer with the exception of steps ( a ) and ( b ). in another embodiment of the method described above , the amount of silicone adhesive and silicone polymers in the composition is selected from the group of wt . % consisting of greater than 90 wt . %, greater than 95 wt . %, greater than 99 wt . % and 100 wt . %, based on the total weight of the composition . in another embodiment of the invention , the making of the calibration standard compositions containing silicone adhesive and silicone polymer wherein at least one of said calibration standard compositions is within 0 . 5 wt . % of the pre - determined acceptable range for the amount of silicone adhesive also includes making calibration standard compositions which have lesser and / or greater amounts of silicone adhesive relative to the pre - determined acceptable range ; the lesser or greater amounts can be within ± 50 wt . % of the pre - determined acceptable range . in another embodiment of the invention , the making of the calibration standard compositions containing silicone adhesive and silicone polymer wherein more than one of said calibration standard compositions is within 1 . 0 wt . % of the pre - determined acceptable range and wherein the calibration standard composition is obtained from multiple lots / batches of the compositions containing silicone adhesive and silicone polymer . in another embodiment of the method described above , the weight of the calibration standard composition is from 0 . 00001 % to 1 % of the weight of the composition comprising silicone adhesive and silicone polymer to be validated . in another embodiment of the method described above , the silicone adhesive is selected from the group consisting of substituted polysiloxane or cross - linked substituted polysiloxane . in another embodiment of the method described above , the silicone polymer is a polysiloxane or cross - linked polysiloxane . another embodiment of the invention is a method of determining the amount of silicone adhesive in an oral care composition which comprises : a composition comprising silicone adhesive and silicone polymer , wherein the silicone adhesive and silicone polymer are not the same compound ; wherein the method comprises of the steps ( a )-( d ) described above and which further comprises : ( e ) mixing the validated composition comprising silicone adhesive and silicone polymer from step ( d ) with an active agent and an orally acceptable carrier to form the oral care composition ; ( f ) obtaining a sample of the oral care composition from step ( e ) and subjecting it to : wherein the obtained ir spectra is compared against the calibration curve from step ( b ) to determine the amount of silicone adhesive in the oral care composition . in another embodiment of the method described above , the amount of silicone adhesive in the oral care composition relative to the amount of silicone adhesive in the composition comprising silicone adhesive and silicone polymer is selected from the ranges consisting of 50 wt . % to less than 100 wt . %, 60 wt . % to 90 wt . % and 70 wt . % to 80 wt . %, based on the total weight of the oral care composition . in another embodiment of the method described above , the silicone adhesive is selected from the group consisting of a substituted polysiloxane or cross - linked substituted polysiloxane . in another embodiment of the method described above , the silicone polymer is selected from the group consisting of polysiloxane or cross - linked polysiloxane . in another embodiment of the method described above , the active agent is selected from the group consisting of abrasives , amino acids , anti - bacterial agents , anti - plaque agents , bleaching agents , breath freshening agents , a fluoride ion source , stannous ion source , tartar control agent , whitening agents , zinc salts and mixtures thereof . in another embodiment of the method described above , the active agent is a whitening agent selected from the group consisting of peroxide compounds , metal chlorites and persulfate . in another embodiment of the method described above , the whitening agent is a peroxide compound , wherein the peroxide compound is hydrogen peroxide bound to polyvinylpyrrolidone . embodiments of the present invention are further described in the following examples . the examples are merely illustrative and do not in any way limit the scope of the invention as described and claimed . foss nirsystems xds near ir with rapid solid analyzer ( range 2500 nm - 400 nm ) measurement parameters : 4 cm - 1 x axis spacing , 16 co - added scans ( can increase scan number for better signal / noise , but the measurement time will increase exponentially . ( 2 ) calculate weight of silicone required to dilute silicone adhesive sample to the pre - determined amount / range ; seven calibration standard concentrations prepared for use in the quantitative method the near ir and mid ir quantitative calibration was developed by correlating the regions with strong adhesive vibrational response to the concentrations prepared in the laboratory by weight ( see fig1 and 2 ). since the analytical balance was used to prepare the calibration standards , the ir is considered a primary method of detection when used for concentration determination . the calibration algorithm used is called partial least squares uses factor analysis to correlate the matrix of vibrational responses to the y matrix of concentrations . then uses a leave one out approach to optimize the number of terms in the model by predicting each of the standards as a true unknown when it is left out of the calibration . this method ensures the minimum number of terms ( principal components ) are used in the final calibration model thus avoiding overfitting the model with extraneous signal . the qualitative conformity methods were developed also by using the regions that are highly specific for adhesive . the method uses principal component analysis , an algorithm that only uses the vibrational fingerprint and ignores the concentration matrix . in developing a qualitative method , the calibration set typically contains samples that are known to be physically and chemically in specification . thus , only the 40 % samples should be used . once a model is developed that maps the fingerprint and variability of the good samples , it can be used to predict the distance between a new lot of material and the good sample model . the prediction is reported in units of mahalanobis distance and is analogous to an euclidean distance or standard deviation . the near ir calibration results are found in fig3 & amp ; table 1 . fig3 shows the calibration fingerprint used to create the calibration curve . the strong bands are found near the oh ( 1400 nm ) and ch ( 1700 nm ) regions . the combination band region from 1900 nm to 2300 nm was not used to create the final calibration curve as it was found to introduce error due to nonlinear detector response . table 1 shows the final calibration curve which compares the actual amount of silicone adhesive in wt . % vs . the amount predicted using the near ir method ; the data was obtained via pls ( partial least squares ) regression analysis of near ir fingerprint versus adhesive concentration . the plot shows the leave one out results ( prediction vs . actual concentration ). the correlation between the spectra and concentration is & gt ; 0 . 999 using 2 or 3 principal components ( modeling terms ) in the final equation . table 2 shows the validation results of various lots of 40 % adhesive along with some of the outlier samples containing 85 % adhesive , and 0 % adhesive . the conformity index was marginal for detecting the difference between pure dimethicone and with adhesive but is able to quantify adhesive concentration differences between 0 % % and 85 % adhesive with good accuracy . the agreement between the determined concentrations and the actual concentrations was exceptional within the range of concentrations used to calibrate the instrument . the calibration results for the mid ir method is found in fig4 & amp ; table 3 . fig4 shows the calibration fingerprint used in the final equation . the bands showing the strongest intensity are the vibrational frequencies with the most weighting for prediction of adhesive concentration . as you can see a strong band exists near 790 cm - 1 . table 3 shows the final calibration curve which compares the actual amount of silicone adhesive in wt . % vs . the amount predicted using the mid ir method ; the data was obtained via pls ( partial least squares ) regression analysis of mid ir fingerprint versus adhesive concentration . with 2 - 3 principal components a correlation greater than 0 . 99 is obtained . table 4 provides the validation evidence when using the method to predict the concentration of on - target adhesive samples and out of specification samples . the conformity prediction is found to be significantly out of specification compared with the specification limit of 3 for both the dimethicone and pure adhesive material . the concentrations determined were within expectation . the accuracy of measuring the 40 % samples was excellent and comparable to the near ir method . the mid ir had a much larger conformity value for dimethicone , indicating that the specificity for detection of the presence of adhesive is better than near ir . in conclusion , both the mid ir and near ir methods can be used ensure in - coming adhesive is chemically equivalent in concentration to the 40 % concentration levels tested in early ship tested samples . as those skilled in the art will appreciate , numerous changes and modifications may be made to the embodiments described herein without departing from the spirit of the invention . it is intended that all such variations fall within the scope of the appended claims .