as stated hereinbefore , the preferred chemicals for making the methanol barrier on the cathode are porphyrins , particularly chosen from among amino -, hydroxy -, pyrrole - and vinyl - substituted porphyrins . the porphyrins may contain metals in the substituting groups . metal ion may be contained in the central porphyrin location , as occurs in certain natural substances such as heme . the general formula of the said porphyrin , in which x indicates a wide range of substituents , is shown in fig2 . some substituents x , that form different porphyrins adapted for use in this invention , are indicated on fig2 , which also indicates the abbreviations used to define the various porphyrins defined by said substituents . by way of example , said porphyrins may be chosen from among tetrakis ( ortho - aminophenyl ) porphyrin , fig2 and the foregoing list , however , are illustrative but not limitative : other porphyrins can be used in this invention , such as vinyl substituted porphyrins , e . g . protoporphyrin ix . in most of the following examples , three - electrode cells are considered . the three - electrode cells comprise a working electrode , a counter electrode and a reference electrode . a scheme of the three - electrode cell is shown in fig9 , which is self - explanatory ( see a . j . bard and l . r . faulkner , “ electrochemical methods , fundamentals and applications ”, john wiley , 1980 ). experimental set - up : the experiment was conducted in a conventional three - electrode cell ( half - cell configuration ). one of two glassy carbon electrodes cast in teflon and supplied by metrohm ( switzerland ) ( a = 0 . 07 cm 2 ) ( abbreviated : a and b ) served as working electrode , a pt wire in a separate compartment served as counter electrode and a saturated calomel electrode ( sce ) as reference electrode . potential was applied between the working and reference electrodes using a 273 potentiostat ( eg & amp ; g ). treatment and coating of working electrodes : electrodes a and b were first polished with a water emulsion of 0 . 3μ alumina and then coated with pt ( as an oxygen reduction catalyst ) by applying a current of 5 ma / cm 2 for 10 minutes from an 10 − 2 m h 2 ptcl 6 + 1 m h 2 so 4 solution at room temperature . electrode a was then coated with an electropolymerized film of ( o - nh 2 ) tpp ( abbreviated : poly ( o - nh 2 ) tpp ) by cycling the potential 20 cycles from 0 to + 1 . 2 v at a scan rate of 50 mv / s from a solution of h 2 ( o - nh 2 ) tpp dissolved in 1 m h 2 so 4 ( 1 mg / ml ) at room temperature . electrode b was not coated with this film . results : fig3 shows chronoamperometric curves obtained for oxygen reduction at room temperature at a potential of + 0 . 2 v in a solution of 1m h 2 so 4 + 1m methanol continuously bubbled with air ( 100 cc / min ): curves ( a ) and ( b ) for electrodes a and b , as working electrode , respectively . it can be seen from the figure that when the electrode is coated with the methanol barrier film ( as in electrode a ), the steady oxygen reduction current at + 0 . 2 v and in the presence of 1m methanol is − 105 μa / cm 2 . however , in the absence of this film ( as in electrode b ), the steady oxygen reduction current is only − 0 . 33 μa / cm 2 . this means that the methanol barrier film causes less methanol to reach the electrode and thus less catalytic platinum catalytic sites are poisoned by methanol and are therefore available for oxygen reduction . experimental set - up : the same experimental set - up ( half - cell configuration ) as described in example 1 was used . treatment and coating of working electrodes : the glassy carbon electrodes a and b were polished and then coated with pt as in example 1 . electrode a was then coated with poly ( o - nh 2 ) tpp by stepping the potential 30 times from 0 ( 10 s ) to + 1 . 2 v ( 60 s ) from a solution of h 2 ( o - nh 2 ) tpp dissolved in 1m h 2 so 4 ( 1 mg / ml ) at 60 ° c . electrode b was not coated with this film . results : fig4 a shows oxygen reduction polarization curves ( at a scan rate of 5 mv / s ) obtained in 1m h 2 so 4 solution at 70 ° c . continuously bubbled with air ( 100 cc / min ) for electrode a in the absence ( curve a ) and presence of 0 . 5 m methanol ( curve b ). fig4 b shows oxygen reduction polarization curves ( 5 mv / s ) obtained in the same solution and conditions as in fig3 for electrode b in the absence ( curve a ) and presence of 0 . 5 m methanol ( curve b ). table i summarizes the currents obtained at two potentials ( vs . sce ) for electrodes a and b . curves ( fig4 a and 4b ) in 1m h 2 so 4 at it can be seen from fig4 a and 4b and from table i that while only 55 % of the current for oxygen reduction at + 0 . 1 v remains after the addition of methanol for electrode b , which is uncoated with a methanol barrier film , 96 % of the current remains at the same conditions for the electrode coated with the methanol barrier film ( electrode a ). the fact that almost no methanol crosses the barrier film can also be concluded from the very low oxidation current observed after the addition of methanol at + 0 . 5 v ( originating from methanol oxidation ) for the electrode coated with the barrier film , compared to the very high current observed for the non - coated electrode ( 0 . 01 and 19 . 7 ma / cm 2 , for electrodes a and b , respectively ). experiments with commercially available cathodes and anodes for fuel cells were conducted first in a three - electrode ( half cell ) and then with a two - electrode ( full cell ) configuration set - up . example 3 describes an experiment conducted with a commercially available cathode . in the two - electrode experiment , the cell used was not as illustrated in fig1 : a solution of acid was used as the electrolyte instead of a solid polymer membrane , and the same setup was used as for the three - electrode experiment setup , but the counter and reference electrodes were short - circuited . half - cell experimental set - up : the three - electrode set - up was similar to that of experiments 1 and 2 . however , the working electrode used in this experiment was a commercially available electrode supplied by e - tek : efcg “ s ” type electrode on tgfh - 120 toray carbon paper , 10 % pt / c , 0 . 5 mg / cm 2 pt loading . part of the electrode was brushed with masking paint so that only 1 cm 2 was exposed to the electrolytic solution . treatment and coating of working electrode : the reactivity of the above electrode towards the cathodic reduction of oxygen in a 1m h 2 so 4 solution at 60 ° c . and continuously bubbled with air is low . this can be deduced by the polarization curve a ( obtained at a scan rate of 1 mv / s ) in fig5 . however , we found that after applying a potential of + 1 . 1 v ( between this electrode and the reference electrode sce ) in the same solution and temperature as indicated above , the polarization curves obtained for oxygen reductions show higher currents . this is shown in fig5 for different times of treatment at + 1 . 1 v ( curves b , c , d and e are for ⅓ , 1 , 2 and 3 hours treatment , respectively ). after a three - hour treatment , the oxygen reduction current at + 0 . 15 v increased from 0 . 18 to 1 . 6 ma / cm 2 , i . e ., an 8 . 9 - fold increase . we attribute this effect as resulting from the evolvement of oxygen due to electrochemical oxidation of water at + 1 . 1 v . the gas evolved in narrow pores contained in the electrode structure probably causes the increase of the catalytic effective area , a process that we call : “ electrochemical digging ”. the second treatment step was to coat with a thick polymeric film which smoothens the surface morphology . the polymer which we found that is suitable for this purpose is poly ( aniline sulfonic acid ). this polymer also is a good proton conductor ( due to the presence of the sulfonic groups ), a necessary property of electrodes in fuel cells . coating of the electrode with this polymer was conducted electrochemically ( electropolymerization ) by cycling the potential applied on the electrode between 0 and + 0 . 8 v ( scan rate of 50 mv / s , 60 cycles ) in a solution containing 1m h 2 so 4 and 5 × 10 − 2 m monomeric aniline sulfonic acid at a temperature of 60 ° c . fig6 shows the polarization oxygen reduction curve obtained ( same solution and temperature as in fig5 ) after this coating procedure , compared to that obtained after the “ electrochemical digging ” procedure ( curves b and a , respectively ). further coating of poly ( aniline sulfonic acid ) on the same electrode was achieved by applying a constant potential of + 0 . 8 v for 30 minutes in the h 2 so 4 + aniline sulfonic acid solution ( 60 ° c .). curve c represents the polarization reduction curve for oxygen after this step . from fig6 , it can be deduced that the polymeric coating does not perturb oxygen diffusion to the catalytic layer . moreover , this coating even increases the electrode reactivity towards oxygen reduction , probably due to the introduction of proton conductive sulfonic acid groups into the catalytic layer . continuation of the coating process , however , causes decrease of the oxygen reduction current ( probably due to decrease of oxygen permeability onto very thick polymeric films ). the last treatment step was to coat a layer of poly ( o - nh 2 ) tpp on top of the poly ( aniline sulfonic acid ) layer by applying a constant potential of + 1 . 05 v from a solution of h 2 ( o - nh 2 ) tpp dissolved in 1m h 2 so 4 ( 1 mg / ml ) at 60 ° c . polarization curves were recorded as after the previous treatments and the currents obtained at + 0 . 05 v before and after the addition of 1 % methanol in solution are summarized in table ii for increasing times of h 2 ( o - nh 2 ) tpp electropolymerization . presence of 1 % methanol in 1 m h 2 so 4 at from table ii , it can be deduced that increasing the electropolymerization time from 2 to 5 hours increases the oxygen reduction current obtained in the absence of methanol . moreover , less decrease of the current is observed after addition of methanol which indicates that less methanol crosses the coating when increasing the electropolymerization time from 2 to 5 hours . a further increase from 5 to 9 hours causes decrease of the current in the absence of methanol with only a small contribution to the ratio of currents after and before the methanol addition ( currents ratio increase from 89 . 7 to 90 . 5 %). the performance of the electrode with its special treatment and coating that we have developed towards oxygen reduction in the presence of methanol was compared to that of a similar electrode which has been treated by “ electrochemical digging ”, but which has not been coated with poly ( aniline sulfonic acid ) and poly ( o - nh 2 ) tpp . instead , this electrode was treated with a conventional nafion coating ( dipping for a half hour in a 5 % nafion solution ). fig7 shows the oxygen reduction polarization curves obtained in 1 m h 2 so 4 + 2 % methanol at 60 ° c . ( air flow rate : 100 cc / min ) for the nafion treated electrode ( curve a ), compared to the electrode coated with poly ( aniline sulfonic acid ) and poly ( o - nh 2 ) tpp ( curve b ). it can be clearly seen from this figure that methanol poisons the nafion coated electrode much more than the electrode with the coating that we developed . this can be deduced by the high anodic currents observed at high positive potentials for the nafion coated electrode (+ 2 ma / cm 2 at + 0 . 5 v , compared to − 0 . 03 ma / cm 2 at the same potential for the other electrode ) as well by the higher cathodic currents for oxygen reduction obtained for the electrode with the coating that we developed (− 3 . 7 ma / cm 2 at + 0 . 05 v , compared to − 1 . 4 ma / cm 2 at the same potential for the nafion coated electrode ). example 4 describes an experiment conducted with a commercially available cathode and anode in a two - electrode ( full - cell ) configuration . full - cell experimental set - up : the cathode used in this experiment was the same electrode used in example 3 , supplied by e - tek ( efcg “ s ” type electrode on tgfh - 120 toray carbon paper , 10 % pt / c , 0 . 5 mg / cm 2 pt loading ). this electrode was first treated by “ electrochemical digging ” and then coated with poly ( aniline sulfonic acid ) and then poly ( o - nh 2 ) tpp , as described in example 3 . the anode , also supplied by e - tek , was an efcg electrode : tgph - 120 toray carbon paper , 10 % pt / ru / c ( 1 : 1 a / o ), 0 . 5 mg / cm 2 pt / ru . part of the electrode was brushed with masking paint so that only 1 cm 2 was exposed to the electrolytic solution . the two electrodes were introduced in a solution of 1 m h 2 so 4 at 60 ° c ., bubbled continuously with air ( 100 cc / min ) and the cathode and anode reactions were driven by a potentiostat ( eg & amp ; g , model 273 ). fig8 shows the current / potential curves obtained ( at a scan rate of 1 mv / s ) in the presence of 1 and 2 % methanol ( curves a and b , respectively ). the figure also shows the current / potential curve obtained in 1 m h 2 so 4 + 2 % methanol at 60 ° c . when air is replaced by oxygen ( curve c ). this figure demonstrates the concept we developed : it is possible to operate a fuel cell without using a membrane separating the cathode from the anode if the cathode is coated with a special thin film which prevents ( or reduces ) methanol to permeate through the catalytic layer of the cathode . the low currents obtained in this research stage can be increased by using the cathode as a gas diffusion electrode , a property which has not yet been exploited . moreover , use of anodes with a smaller pt content will also improve the fuel cell performance , since oxygen reaching the anode is reduced at this electrode and therefore reduces the overall current . it has been found that in some cases the presence of the methanol barrier film on the cathode permits to omit the presence of the electrolyte membrane in the cell , thus simplifying its construction . this is particularly true in applications employing low current densities , e . g . less than 10 ma / cm 2 . while examples have been given by way of illustration of embodiments , it will be apparent that the invention is not limited to them , and can be carried into practice with many modifications , variations and adaptations , without departing from its spirit or exceeding the scope of the claims .