the present invention teaches a continuous process for the manufacture of olefinic containing nanostructured chemicals and chemical derivatives from them that are useful as building blocks for the reinforcement of polymer coils , domains , chains , and segments at the molecular level in thermoset and thermoplastic resins , oil or aqueous emulsions , latexes , and suspensions . nanostructured chemicals , such as the olefin poss structures illustrated in fig1 , can exist as solids , waxes , and oils . a variety of olefinic r groups such as cyclohexene , norbornene , allyl , and styrenyl can be considered for inclusion on nanostructured chemicals . however , the lowest cost systems that are also commercially available commercially are the vinylsilanes . vinyltrialkoxysilanes and vinyltrichorosilane are commercially available in industrial quantities . historically the synthesis process for vinyl poss systems has been plagued by low yields , long reaction times , and irreproducible product yields . the chemical equation for synthesis of vinyl poss involving trichloro or alkoxy silanes can be generically represented as follows : the chemical reactions illustrated in equations 1 , 2 , and 3 are shown in nonstoichiometric form as the effects of water , hcl , roh ( alcohol ), and concentration of silane have dramatic influences on product yield and the purity of isolated product . a wide variety of olefin poss structures can be obtained as illustrated in fig1 . to illustrate this point , fig2 and 3 describe the complex relationship of water and acid relative to yield of the vinyl poss cage . furthermore , the concentration of the acid in equations 2 and 3 can be varied from 1 % to 39 % with a preferred concentration of 37 . 9 %. in the design of a continuous process it is also desirable to recognize the chemical stability and the ability to isolate the olefin poss products from the reaction medium . in equations 1 - 3 , the vinyl poss is both chemically stable to the reaction medium and insoluble . the insolubility of the poss product , in the reaction medium , facilitates its collection via filtration of the reaction mixture . the collection of product is further facilitated by running the reaction at room temperature which avoids the loss of product due to reactions or solubilzation that can occur at elevated temperatures . the concentration of silane added to the reaction medium can be varied from 0 . 01 m - 5 . 0 m . a preferred concentration range is 0 . 3 m to 2 . 0 m , and a more preferred concentration for continuous reaction purposes is 1 . 3 m - 1 . 5 m . while a continuous process has been established for each reaction illustrated in equations 1 - 3 , equations 1 and 3 are less desirable , as they require equipment investments to handle corrosive hcl byproducts . equation 2 is more easily managed though use of readily available plastic or glass lined reaction vessels and filtration equipment . it should be further noted that equations 1 and 3 produce three equivalents of hcl for each equivalent of vinyltrichlorosilane while equation 2 produces three equivalents of alcohol per equivalent of vinytrialkoxy silane . the liberation of alcohol in equation 2 is highly desirable as it aids in solubilization of the starting materials and in the solubilization of vinyl poss intermediates and resinous by - products . in the case of equations 1 and 3 , alcohol is required to rinse the final poss products to remove such intermediates , oligomers and polymers . finally , the formation of vinyl poss in equations 1 - 3 is driven by the precipitation of the product from the acid methanol solution . a resinous by - product is also produced in the reaction but it does not precipitate from the reaction as it remains soluble in methanol . as is typical with chemical processes , there are a number of variables that can be used to control the purity , selectivity , rate and mechanism of any process . variables influencing the process for the formation of nanostructured chemicals ( e . g . poss / pos , etc .) include the size , polydispersity , and composition of the nanostructured chemical desired , the kinetics , thermodynamics , and aids used during the reaction process such as catalysts , cocatalyst , supports , and surfactants , and other factors such as temperature , pressure , templates , solvent , gases and mixtures thereof . vinyl poss can be produced from vinyltrimethoxy , vinyltriethoxy silane or vinyltrichloro silane ( or related derivatives ), either via the filtration of product every 24 hours or by filtration of the product after the addition of silane over a period of successive 24 hour additions . in general it is preferred to filter and collect the reaction product once every 24 hours . in the case of synthesis from vinyltrichloro silane , the vinyltrichloro silane is premixed for 10 minutes with 3 . 5 equivalents of methanol . the prereacted solution ( 0 . 85 %) is then added to a stirred solution of methanol ( 65 . 7 % v / v ), hcl ( 32 . 7 % v / v ), and water ( 0 . 65 % v / v ). the periodic addition of a solubilizing amount of methanol is required to minimize the foil cation of a sticky white resinous by - product that can contaminate the octavinyl poss . the amount of meoh required is variable and is determined by visual solubilization of any sticky precipitated resin on the walls of the reaction vessel . in a 1000 ml round bottom flask containing methanol ( 500 ml ), hcl ( 250 ml ), and water ( 5 ml ) the mixture was allowed to come to room temperature . vinyl trimethoxy silane ( 6 . 5 ml ) was added slowly to the reaction mixture and reaction was continued for 24 hours with stirring ( magnetic stirrer ). in one case it was filtered and the reactor charged with additional silane ( 6 . 5 ml ), and the process is repeated 5 to 20 times . 20 time addition and filtration produced 35 . 3 % vi8t8 . ( yield was based on the final product , which was washed with methanol and dried .) 10 times addition and no filtration produces 32 . 8 % vi8t8 . ( yield was based on the final product , which was washed with methanol and acetone and dried in vacuum ). in a 1000 ml round bottom flask containing methanol ( 500 ml ), hcl ( 250 ml ), and water ( 5 ml ) added slowly , the mixture was allowed to come to room temperature . vinyl trimethoxy silane ( 6 . 5 ml ) was added slowly to the reaction mixture and reaction was continued for 24 hours with stirring ( magnetic stirrer ). total yield of 5 times addition / filtration was 40 . 8 %. total yield of 5 times addition / no filtration was 40 . 8 %. ( yield was based on the final product which was washed with methanol and dried ) the process for producing octavinyl poss from vinyltrimethoxy silane involves the room temperature addition of the silane ( 0 . 85 % v / v ) every 24 hours to a stirred solution of methanol ( 65 . 7 % v / v ), hcl ( 32 . 7 % v / v ), water ( 0 . 65 % v / v ). the reaction mixture is capable of continuously producing octavinyl poss either via the successive filtration of product or by the continuous addition of silane . alternately , in a 1000 ml round bottom flask containing methanol ( 500 ml ), hcl ( 250 ml ), and water ( 5 ml ) added slowly , the mixture was allowed to come to room temperature . vinyl trimethoxy silane ( 6 . 5 ml ) was added slowly to the reaction mixture and reaction was continued for 24 h with stirring ( magnetic stirrer ). in one case it was filtered and the reactor charged with additional silane ( 6 . 5 ml ), and the process repeated 5 to 20 times . in another case the reactor was charged with additional silane ( 6 . 5 ml ) and the process was repeated 5 to 20 times . the hydroamination of olefins is a well known reaction . fig5 illustrates hydroamination of vinyl poss . a 50 g sample of vinyl poss is suspended in a liquid ammonia solution and to this ptbr 2 and nbu 4 pbr is added . the mixture was allowed to react over 8 hours to product the desired octaminoethyl poss . the product was isolated as a white solid . a 50 g sample of octaminoethyl poss was reacted with phosgene for 4 hours at 50 ° c . to produce the octaethylisocyante poss . the product was isolated as a white solid . fig6 illustrates polyisocyanate formation with poss . transition metal oxides such as oso 4 and mno 4 − have long been known to be powerful oxidizing agents . amine catalyzed osmylation followed by hydrolysis is a known method to produce dialcohol products from vinyl groups . a 50 g sample of vinyl poss was stirred into osmium tetroxide . the mixture was allowed to react for 2 hours and then washed with aqueous acid to produce a white solid of octaethylglycol poss that was collected through filtration . fig7 schematically shows the process of alcohol formation . while certain representative embodiments and details have been shown for purposes of illustrating the invention , it will be apparent to those skilled in the art that various changes in the methods and apparatus disclosed herein may be made without departing from the scope of the invention which is defined in the appended claims .