while the making and using of various embodiments of the present invention are discussed in detail below , it should be appreciated that the present invention provides many applicable inventive concepts which can be embodied in a wide variety of specific contexts . the specific embodiments discussed herein are merely illustrative of specific ways to make and use the invention , and do not delimit the scope of the present invention . referring initially to fig1 , therein is depicted a polymeric dispersed liquid crystal light shutter device or , more succinctly , a liquid crystal shutter that is schematically illustrated and generally designated 10 . liquid crystals are substances that exhibit a phase of matter that has properties between those of a conventional liquid , and those of a solid crystal . for instance , a liquid crystal may flow like a liquid , but have the molecules in the liquid arranged and / or oriented in a crystal - like way . one type of liquid crystal , in the aforementioned polymer dispersed liquid crystal or pdlc , comprises micro - size droplets of low - molecular weight nematic liquid crystals dispersed in a polymer binder system . the liquid crystal shutter 10 includes a pdlc material interposed between substrates having transparent conducting electrodes . in fig1 , the liquid crystal shutter 10 is being utilized as a window 12 , behind which , an individual 14 is standing . upon application of a voltage , as shown by arrow 14 , across the electrodes of the liquid crystal shutter 10 , the liquid crystal shutter 10 , switches from an opaque , high scattering state to a clear , transparent state , wherein the individual 14 can be seen standing behind the window 14 . upon removal of the voltage , as shown by arrow 18 , the liquid crystal shutter 10 switches from the clear , transparent state to the opaque , high scattering state . it should be appreciated that although the liquid crystal shutter 10 is presented as a window , the teachings presented herein extend to any type of aperture including apertures for looking through , apertures having a need for clear and opaque states , switchable glass , privacy glass , smart windows , smart glasses . further the light crystal shutter may be glass , plexiglass , polycarbonate or other material as will be discussed hereinbelow . fig2 depicts one embodiment of the liquid crystal shutter 10 wherein encapsulated liquid crystal microdroplets 20 are distributed uniformly in a polymer binder system 22 , which may have the form of a plastic matrix , to create the pdlc material that is then sandwiched between two transparent substrates 24 , 26 . in one implementation , the substrates are positioned parallel to each other and include a transparent body having a transparent conducing layer therewith . the transparent body may be selected from materials consisting of glasses and plastics , for example . moreover , the transparent body may include a refractive index from about 1 . 51 to about 1 . 52 . the polymer binder system 22 may also have a refractive index from about 1 . 51 to about 1 . 52 . it should be appreciated that the refractive indexes of the transparent substitutes 24 , 26 and the polymer binder system 22 are matched as close as possible to improve transparency . the transparent conducting layer may comprise an indium - tin - oxide conducting layer or often suitable conducting layer , for example . fig2 shows a light scattering state 28 of the liquid crystal microdroplets 20 in the polymer binder system 22 , in the absence of an applied electric field . within each of the liquid crystal microdroplets 20 , liquid crystals have tangential wall alignment ; however , there is a two dimension random orientation of molecules in comparing various liquid crystal microdroplets 20 . in terms of optical properties , this corresponds to a highly light scattering state . that is , in the absence of an applied electric field ({ right arrow over ( e )}= 0 ), the optic axes of the liquid crystal microdroplets have no preferred direction in which to point in the plane , so that incident light encounters a mismatch between the refraction index n p of the matrix and the average refraction index (˜ n e ) of the liquid crystal microdroplets . the result of the mismatch is that the light is scattered and the liquid crystal shutter 10 appears opaque . on the other hand , if an electrical field is { right arrow over ( e )} applied as shown in fig3 , the orientations of molecules among various microdroplets is completely aligned . the applied electric field { right arrow over ( e )} aligns the directors within the droplets to a transparent state . with reference to the light scattering state 28 of fig2 , the optic axis of the droplets is indicated by n e . if the ordinary refractive index of the liquid crystal , n 0 , matches that of the polymer binder system 22 , n p , then light scatters according to the value and orientation distribution of n e . if n e & gt ; n 0 and is 2 - d randomly oriented ( off state ), light is strongly scattered . if n e is reoriented to be parallel to the direction of normally incident light , as in the case under an applied electric field , then , in principle , no light is scattered ( n 0 ˜ n p ). it should be appreciated that the liquid crystal microdroplets may be fabricated as spherical or elliptical shapes and that the shape of the liquid crystal microdroplets may change shape and size due to compression and other factors when the liquid crystal shutter is assembled . as mentioned , in fig3 , in response to an application of an electric field ({ right arrow over ( e )}=↑) across the transparent substrates 24 , 26 , the liquid crystal shutter provides transmission of light . the electric filed causes the optic axes of the liquid crystal microdroplets 20 to align parallel to the field and normal to the surfaces of the transparent substrates 24 , 26 . in this transmission state 30 , incident light detects no mismatch between average refractive index of the liquid crystal droplet (˜ n 0 ) and the polymer binder system 22 ( n p ) and light is transmitted so that the liquid crystal shutter 10 appears clear . as mentioned , by the application and removal of the driving voltage the liquid crystal shutter 10 may be alternated between the layout scattering state 28 of fig2 and the light transmission state 30 of fig3 . the liquid crystal shutter is more particularly a polymer dispersed liquid crystal light shutter device that includes liquid crystals dispersed in the polymer binder system . in one embodiment , the liquid crystals comprise a mixture product of at least one compound expressed by the general formula ( i ), at least one compound expressed by the general formula ( ii ), at least one compound expressed by the general formula ( iii ), at least one compound expressed by the general formula ( iv ), and at least one compound selected from the group of compounds expressed by the general formulas ( v ), ( vi ), and ( vii ); all of these general formulas presented in the following table , table i , wherein r 1 through r 7 each respectively denote a straight - chain alkyl having 2 to 7 carbon atoms . it should be appreciated that r 1 through r 7 may vary or be identical , depending on the application . moreover , in one implementation , the liquid crystals further comprise a mixture product of at least two compounds expressed by the general formula ( i ). the liquid crystals may comprise about 10 % to about 50 %, by weight of the liquid crystals , of a compound of the general formula ( i ); about 10 % to about 20 %, by weight of the liquid crystals , of a compound of the general formula ( ii ); about 10 % to about 15 %, by weight of the liquid crystals , of a compound of the general formula ( iii ); about 5 % to about 15 %, by weight of the liquid crystals , of a compound of the general formula ( iv ); and about 10 % to about 15 %, by weight of the liquid crystals , of at least one compound selected from the group of compounds expressed by the general formulas ( v ), ( vi ), and ( vii ). in one embodiment , the polymer binder system includes epoxy resins and mercaptan curing agents . additionally , a catalyst may be utilized . the present invention will now be illustrated by reference to the following non - limiting working examples wherein procedures and materials are solely representative of those which can be employed , and are not exhaustive of those available and operative . the following examples and the accompanying test methods illustrate the advantages of the present liquid crystal shutter . the following glossary enumerates the components utilized in the examples and test methods presented hereinbelow . capcure ® 3 - 800 curing agent is a mercaptan ( sh ) terminated liquid curing agent which imparts rapid - cure characteristics to epoxy resins in combination with selected amines from cognis s . a . ( cognis usa headquarters in cincinnati , ohio ). capcure ® 40 curing agent is a pre - catalyzed mercaptan - based epoxy hardener that possesses extremely rapid - setting at ambient temperature from cognis s . a . ( cognis usa headquarters in cincinnati , ohio ). capcure ® eh - 30 is a brand name for 2 , 4 , 6 - tris ( dimethylaminomethyl ) phenol , which is c 15 h 27 n 3 o from cognis s . a . ( cognis usa headquarters in cincinnati , ohio ). epon ™ resin 812 is an epoxy monomer for embedding resin systems from shell chemicals ( houston , tex . ); suitable substitutes include embed 812 from electron microscopy sciences ( hatfield , pa .) and spi - pon 812 from spi supplies / structure probe , inc . ( west chester , pa . ), for example . epon ™ resin 815 is a low viscosity liquid bisphenol a based epoxy resin containing a commercial grade of n - butyl glycidyl ether from hexion specialty chemicals , inc . ( columbus , ohio ). epon ™ resin 828 is an undiluted clear difunctional bisphenol a / epichlorohydrin derived liquid epoxy resin from hexion specialty chemicals , inc . ( columbus , ohio ). erl - 4221 ™ resin , 3 , 4 - epoxycyclohexyl methyl - 3 , 4 - epoxy - cyclohexanecarboxylate , is a cycloaliphatic , diepoxy functional organic compound that is a useful building block in the production of semi - hard to hard cured epoxy resins ; available from union carbide company ( danbury , conn .). erl - 4299 ™ resin , bis ( 3 , 4 - epoxycyclohexyl ) adipate , is a multi - functional epoxy that is a useful building block in the production of semi - hard to hard cured epoxy resins ; available from union carbide company ( danbury , conn .). spacers may be spherical - shaped spacers dispersed between substrates to provide for spacing . a polymer system having a refractive index of 1 . 5177 is made by mixing the ingredients of table ii . a polymer system having a refractive index of 1 . 517 is made by mixing the ingredients of table iii . a polymer system having a refractive index of 1 . 5178 is made by mixing the ingredients of table iv . a liquid crystal mixture is made by stirring the ingredients of table v in a beaker at 80 ° c . or higher until the mixture becomes an isotropic liquid . stirring continues until the liquid crystal is well mixed in the isotropic state . the mixture is then cooled . as noted in table v , the respective general formula class of the constituent compounds are also shown . a liquid crystal mixture was prepared substantially according to the procedures presented in example lcm - i with the components noted in table vi . a liquid crystal mixture was prepared substantially according to the procedures presented in example lcm - ii with the components noted in table vii . a liquid crystal shutter is made by stirring the ingredients of table viii in a beaker at ambient conditions until the mixture is homogenous . the mixture is applied individually to two substrates having indium - tin - oxide conducting layers . the substrates are then laminated together and cured at 65 ° c . for approximately 8 hours . following curing , the liquid crystal shutter is cooled to room temperature . a liquid crystal shutter was prepared substantially according to the procedures presented in example lcs - i with the components noted in table ix . a liquid crystal shutter was prepared substantially according to the procedures presented in example lcs - i with the components noted in table x . a liquid crystal shutter was prepared substantially according to the procedures presented in example lcs - i with the components noted in table xi . a liquid crystal shutter was prepared substantially according to the procedures presented in example lcs - i with the components noted in table xii . a liquid crystal shutter was prepared substantially according to the procedures presented in example lcs - i with the components noted in table xiii . test method i . with reference to fig4 and 5 and graphs 40 , 42 , percent transmission was measured as a function of voltage for embodiments of the liquid crystal shutter display of fig1 . in particular , the formulations according to examples lcs - i through lcs - vi are depicted . with respect to fig4 , the drive voltages for examples lcs - i through lcs - iii are between about 12v and about 17v and the saturated transmissions vary between about 86 % and about 92 %. with respect to fig5 , the drive voltages for examples lcs - iv through lcs - vi are between about 20v and about 40v and the saturated transmissions vary between about 78 % and about 91 %. test method ii . with reference to fig6 and 7 and graphs 44 , 46 , viewing angle as a function of percent transmission was measured for embodiments of the liquid crystal shutter display of fig1 and particularly examples lcs - i through lcs - vi . with respect to fig6 , the viewing angles are wide from positive 40 degrees to negative 40 degrees and there is less than 10 % transmission drops as compared to saturated transmission . with respect to fig7 , the viewing angle is wide from positive 40 degrees to negative 40 degrees and the transmissions vary between about 78 % and about 90 %. test method iii . percent transmission was measured as a function of viewing angle comparing various liquid crystal shutters presented herein to existing liquid crystal shutter solutions . with reference to fig8 , existing solutions 1 and 2 are driven by 100v . existing solution 3 is driven by 100v and existing solution 4 is driven by 70v . test method iv . percent transmission of uv , visible , and ir light were measured during the off state to compare various liquid crystal shutters presented herein to existing liquid crystal shutter solutions . the results are noted in table xiv . the existing solutions are the same as those presented for test method iii . as test methods i - iv demonstrate , the liquid crystal shutters presented herein provide wide viewing angle , low driving voltage , and low percent transmission in the off state . additionally , high contrast ratio and broad operating temperature range are provided . while this invention has been described with reference to illustrative embodiments , this description is not intended to be construed in a limiting sense . various modifications and combinations of the illustrative embodiments as well as other embodiments of the invention , will be apparent to persons skilled in the art upon reference to the description . it is , therefore , intended that the appended claims encompass any such modifications or embodiments .