in fig1 there is shown , in cross - section , an optical fiber ribbon 11 having twelve optical fibers 12 arrayed in side - by - side parallel relationship in a single plane . each of the fibers 12 comprises a core 13 and a cladding 14 , a first , inner coating 16 and a second , outer coating 17 , and the several fibers 12 are held together in their planar array by a matrix 18 . although not visible in fig1 outer coating or layer 18 has an identifying colored ink thereon for facilitating identification of each of the fibers relative to the others . it is to be understood that instead of first and second layers 16 and 17 , each fiber may have only a single layer instead of the two shown , and , further , that layer or coating 17 may have a colorant incorporated therein . it is virtually a necessity that the coloring layer , whatever its make - up , i . e ., ink , dye , or colorant incorporation not be removed or otherwise obscured when the matrix 18 is removed to gain access to the fibers . the material of matrix 18 and the surface of the color identifier is selected to have an interfacial bonding characteristic such that the bonding interface between the two materials is weaker than the bonding interface of the ink or colorant to the coating 17 on the fiber , or the coating 16 if coating 17 is not used . such a desideratum can be achieved , for example , by the application of a release agent , not shown , over the ink or colorant , or by the inclusion of a release agent in the ink or colorant or matrix . the release agent creates a weak boundary layer at the interface of the matrix material and the colorant material . further , to this end , the surface energy ( surface tension ) of the ink and matrix materials should be 20 - 35 mj / m 2 . by adjusting the surface energies , a course adjustment can be made to the ink - to - matrix adhesion . a fine adjustment of this adhesion parameter can be made by adjusting the surface cure of the ink . a measure of the surface cure is given by the residual acrylate unsaturation ( rav ) of a uv colored fiber , which should be lower than 20 %. in practice , it has been found that a range of 2 to 17 % works best . a greater rau leads to increased matrix adhesion . uv curable matrix bonding material comprises , for example , a mixture comprising a resin , a diluent , and a photoinitiator . the resin may include an aliphatic or aromatic urethane acrylate and / or an epoxy acrylate / methacrylate . the diluent may comprise monofunctional or multifunctional acrylic acid esters having a molecular weight of 100 - 1000 dalton . for the photoinitiator , the composition may include ketonic compounds such as 1 - hydroxycyclohexyl phenyl ketone , diethoxyacetophenone , acetophenone , benzophenone , benzoin , anthraquinone , and benzil dimethyl ketal . in composition , the bonding matrix may include 50 - 90 percent weight resin , 5 to 10 percent diluents , and 1 to 10 percent photoinitiator . additives containing silicon ( si ) or fluorine ( f ) atoms may be added to improve the release properties of the bonding material . a uv curable coloring material ( uv ink ) is a mixture similar to that of the uv bonding material with the addition of pigments to achieve the desired color . another important property of the matrix bonding material is its modulus as related to temperature . ideally , the modulus should not change significantly over the expected temperature range of operation , generally considered as - 40 ° f . to 180 ° f . where the fiber has a dual coating , layers 16 and 17 , inner layer 16 generally has a modulus of about 1 mpa at room temperature and the outer layer has a modulus of approximately 1 gpa at room temperature . the matrix material 18 is a uv curable bonding material which has a modulus greater than 1 mpa , preferably in the range of 600 - 1200 mpa at room temperature . a higher modulus material may be used when the inner layer 16 comprises a relatively low modulus material . if the modulus is relatively high , thereby insuring sufficient mechanical strength , the release agent insures an easy release between the fiber and the colorant so that the colorant remains with the fiber where the matrix is removed . fig2 is a graph of a desired matrix bonding material elastic modulus versus temperature characteristic ( gray area ) as opposed to the modulus versus temperature characteristic of prior art matrix bonding material . as can be seen in fig2 the matrix material of the invention has , at room is temperature ( 25 ° c .) an elastic modulus of approximately 700 to 1000 mpa . as pointed out hereinbefore , the range at room temperature can extend from 600 to 1200 mpa . this range is highly satisfactory for accessing the fibers without destroying or weakening the ribbon . examples 2 and 3 show too high a modulus at room temperature , which makes it more difficult to break out the fibers , while example 1 has an extremely low modulus , where accessing the fibers can seriously weaken the ribbon . also , as pointed out hereinbefore , the elastic modulus should be relatively high at stripping temperatures ( 75 ° c .- 150 ° c .). it can be seen from fig2 that the modulus of the material of the invention is , over almost the entire stripping temperature range , higher than the examples 1 , 2 and 3 . further , over the design range (- 50 ° c .- 85 ° c .) the prior art materials undergo steep dielines in modulus , as well as relatively abrupt changes therein , while the elastic modulus of the material of the invention undergoes a smooth predictable decrease . the remaining portion of the disclosure is directed to methods of accessing or breaking out fibers from the ribbon , in which the importance of the matrix properties , as enumerated hereinbefore , become apparent . fig3 depicts the method of achieving the desired separation so that individual fibers may be accessed for splicing or other operations thereon . as shown in fig3 the fiber ribbon 11 which is to be accessed is affixed to a flat ( i . e ., infinite radius of curvature ) plate 21 by means of a double sided adhesive tape 22 . prior to the ribbon 11 being affixed , it can be , although not absolutely necessarily , pre - wiped with a textured pad to introduce stresses and cracks therein and then it is immersed in a softening agent , preferably an ethanol bath , which covers the area in which break - out is to occur . alternatively , the designated area may be covered with an ethanol gel . the ethanol functions to cause the matrix material to swell and soften , and to weaken the bond between the matrix 18 and the outer coating 17 and its colorant , i . e ., ink . as pointed out before , the fiber may have only a single coating layer 16 , with the colorant applied thereto or incorporated therein . after the matrix 18 has been softened , which preferably takes less than 10 minutes , a pulling member such as a card , adhesive tape 23 , or other flexible member , is affixed to the matrix 18 and the matrix 18 is pulled from one side of ribbon 11 by means of a back tension in the direction of arrow at approximately a 30 ° angle . this angled back tension has a vertical component as indicated by the arrow 26 , which component separates the matrix from one side of the ribbon 11 , as shown in fig3 . after the matrix 18 has been separated from the ribbon 11 in the desired location , the ribbon is turned over and the process is repeated for the other side of the ribbon 11 or the fibers themselves may be lifted from the matrix that remains attached to the tape . what is then left are the fibers themselves with their coating or coatings 16 and 17 and the colorant intact . the fiber or fibers to be operated on ( as by splicing ) are then wiped clean of any remnant matrix material , by the use of , for example , reagent grade isopropyl alcohol . in the process just described , the fibers remain flat / straight at all times and , their transmission of signals during the process is unaffected thereby . in fig4 there is shown a tool 27 that can be carried in the tool kit of the installer , and that presents a smooth curved surface 28 upon which the ribbon 11 is affixed by the double sided tape 22 . the main limitation on the surface 28 is that its radius of curvature substantially exceed the critical bend radius of the fibers , thereby preventing the introduction of losses or distortions resulting from too sharp bending of the fibers . in all other respects , the process of the invention is the same as for that shown in fig3 . fig5 illustrates a second preferred embodiment of the process of the invention which , as is the first embodiment of fig3 and 4 , includes the steps of treating the matrix material 18 with ethanol , then laying the ribbon on a smooth flat surface of a flat plate 21 . the double - sided adhesive tape 22 of fig3 is not absolutely necessary , although it may be used if desired . preferably , a small adhesive patch 31 serves to anchor the ribbon 11 to the plate 21 . instead of the matrix 18 being pulled from the ribbon 1 as in the first embodiment , the matrix 18 is removed by being rubbed with a textured cloth or pad 32 in which it is stroked in the direction of the arrow 33 . the pad 32 may be , for example , a polyethylene pad which has a textured surface that , in effect , abrades the matrix 18 but is soft enough that it does not abrade the fiber coating 17 nor the colorant layer or coating . it is usually the case that the entire section of the matrix 18 may be removed without the necessity of turning the ribbon over . on the other hand , as an additional assurance that the material 18 may be completely removed , the ribbon 11 may be turned over and the rubbing step repeated . after the rubbing step , the fibers may be cleaned by the use of , for example , reagent grade isopropyl alcohol , which does not affect the colorant . in many cases it may be desirable to access only one or two fibers from the ribbon . in that case , any of the foregoing procedures may be used to remove the bonding matrix and thus access all of the fibers in a short portion of the , e . g ., approximately 5 cm . then , as shown in fig6 any desired individual fiber or fibers or integral sub - unit comprising a plurality of fibers may be separated further along the ribbon 11 by using a thin , flexible cord - like member 36 such as dental floss , held in a tool or holder 37 . the member 37 and cord 36 are inserted between the fiber and / or sub - unit to be separated and moved parallel to the longitudinal dimension of the ribbon 11 , thereby freeing the fiber from the bonding matrix 18 without damage thereto or disrupting the mechanical integrity of the adjacent sub - units or without inducing bit errors in the actively transmitting fibers or adjacent sub - units . from the foregoing , it can be seen that the method of the present invention makes break - out or individual fiber access in a ribbon fiber possible without introducing losses or signal distortions in the transmitting fibers . it is not necessary to stop signal transmission in performing the break - out , and the break - out , itself , is relatively simple and easy to perform . the invention and the principles thereof have been discussed with regard to a single matrix material , which is usable with virtually any commercial stripper . it is conceivable that future methods or apparatus may require or operate best with two matrix materials , for example , without departing from the principles set forth in the foregoing . in concluding the detailed description , it should be noted that it will be obvious to those skilled in the art that many variations and modifications may be made to the preferred embodiment without substantial departure from the principles of the present invention . all such variations and modifications are intended to be included herein as being within the scope of the present invention . further , in the claims hereafter , the corresponding structures , materials , and acts and equivalents of all means or step plus function elements are intended to include any structure , material , or acts for performing the functions with other claimed elements or steps as specifically claimed .