in the present invention , a freshly formed glass article , such as a bottle , is removed from an annealing lehr and cooled below the annealing range to a temperature on the order of room temperature to 200 ° f . the outside surface of the glass article , while still bare and untreated , is then coated by means of a curtain overflow coating process , spraying , dipping , or roller coating . if the coated article is a bottle , for example , special care is taken to avoid the invasion of the interior thereof by the coating solution . this solution consists generally of a dilute aqueous solution of resin , including a crosslinking agent for the resin and a lubricious additive , the resin being selected so that in its crosslinked form , it retains some carboxylic functionality . a particularly desirable binder resin for use in this invention is a low molecular weight , styrene maleic anhydride adduct copolymer available from arco chemical company , under the trade name &# 34 ; sma resins &# 34 ;. such copolymers are available in styrene - maleic anhydride ratios of 1 : 1 , 2 : 1 , and 3 : 1 , all of which are useful in the present invention . scripset styrene - maleic anhydride resins sold by monsanto may also be used . these resins are available with their carboxylic functionality in esterified or partially esterified form , including the disodium salt and the amide and ammonium salt forms . the average molecular weight of these resins varies from 10 , 000 to 50 , 000 . all of these resins may be used in the present invention . these resins may be neutralized by either strong or weak bases to form water soluble salts . such solubilization occurs when the resin is dispersed in an ammonium hydroxide solution . while sodium hydroxide may also be used , ammonium hydroxide is preferred so that the film formed on application and drying is free of the neutralizing base due to evaporation of ammonia . note that because of the carboxylic functionality of the resin , it is readily disperible as an aqueous solution . the remaining carboxylic functionality in the crosslinked form of the resin in the coating is also effective to render the coating relatively hydrophilic so that it is receptive to decorating inks and label adhesives . such resins are crosslinkable by zinc ions , for example , through the formation of an intermediate zinc ammonium complex producing a zinc salt of the resin as ammonia escapes . the proportion of crosslinking agent present will determine the degree to which the resin is crosslinked which will in turn determine the resistance of the coating to deterioration in water and to loss of clarity . permanent coatings which cure rapidly at low temperatures and which have excellent water resistance can be achieved with polyfunctional aziridines as a crosslinking agent . good permanent coatings can also be achieved by crosslinking agents , such as epoxies and formaldehyde condensation resins . the latter , while they require a higher temperature cure , perhaps even above room temperature to the 200 ° f . range , provide good chemical resistance . other binder resins which may be used are the ionomers described in u . s . pat . nos . 3 , 264 , 272 and 3 , 836 , 386 , as well as acrylic acid copolymers , styrene butadiene resins , styrene acrylic copolymers , such as those commercially available from the b . f . goodrich co . as carboset resins . still further , polyacrylamide vinyl / acrylic copolymers , and polyesters , all having some carboxylic functionality may also be used . resins having some hydroxyl functionality may also be crosslinked and utilized in accordance with the present invention . where better alkali resistance is required , vinyl homopolymer and copolymer resins may be used as binder resins or blended with styrene , maleic anhydride , or other polymers . the lubricious additives included in the composition of the present invention may be comprised of oxidized polyethylene ( with an acid number of less than 20 to comply with fda specifications for certain applications ), and the oxidized polyethylene may be emulsified by conventional emulsifying techniques known in the art . it is preferable to use fugitive emulsifiers so that after application , the water sensitivity of the film is reduced . high melting polyethylenes are also preferable for high water resistance and autoclavibility . polyethylene emulsions using non - oxidized polyethylenes may also be prepared by emulsion polymerization of ethylene . fatty acid derivatives , such as ethylene bis - steramide , are difficult to emulsify by themselves . however , these may be more easily coemulsified with polyethylene . other lubricating agents which may be solubilized in an aqueous base or water may also be blended directly with the binder resin without pre - emulsifying . it is preferable to blend the binder resin with the lubricating agent , such as polyethylene or ethylene bis - oleamide , in a solids ratio of 80 / 20 to 70 / 30 respectively , although in some applications , lower lubricant ratios of 90 / 10 or higher lubricant ratios up to 40 / 60 may be desired . still higher lubricant ratios may also be employed but the hot water resistance of the coating decreases significantly when the lubricant concentration in the coating exceeds 60 %. if hot water resistance is not important in a specific application , coatings with good abrasion resistance may be formulated with higher lubricant concentrations . following are four examples in which bottles have been coated in accordance with the present invention : styrene - maleic anhydride copolymer -- sma 3000 ( arco chemical co .) powder was dissolved in aqueous ammonia using deionized water and 28 % concentrated ammonium hydroxide at 2 % solids . the ph was adjusted to 8 . 0 - 9 . 0 . the solution was warmed to about 70 ° c . and stirred for about 1 to 2 hours until all the powder dissolved . a non - ionic emulsion of high density polyethylene wax with a softening point of 138 ° c . and acid value of 16 ( allied chemical &# 39 ; s ac 316 ), emulsified with ethoxylated nonyl phenol and other emulsifying agents , at 30 % solids ( available from chemical corporation of america , chemcor , east rutherford , n . j .) was diluted with deionized water to 2 % solids solution . 70 parts by volume of the 2 % sma 3000 solution was mixed with 30 parts by volume of 2 % emulsion 316 solution . 0 . 8 ml . of a solution of zinc ammonium carbonate containing 20 % zinc oxide solids ( available from sherwin williams co .) was mixed with every 100 mls . of the blend prepared as above . all ingredients in this formulation are in compliance with applicable fda food contact regulations . a 1 % solution of partially esterified styrenemaleic anhydride copolymer , sma 2625 ( arco chemical co . ), was dissolved in aqueous ammonia as described in example 1 . an anionic coemulsion prepared by emulsifying a high density polyethylene wax p . e . d . 121 ( commercially available from american hoechst ) and ethylene bis - oleamide in the solids ratio of 9 / 1 , respectively , using diethyl ethanolamine stearate as emulsifier , with total solids 25 % ( available from the chemical corporation of america under the trade name , emulsion 267a ) was diluted to 1 % solids by adding deionized water . seventy ( 70 ) parts by volume of the 1 % sma 2625 solution was mixed with twenty - five ( 25 ) parts by volume of 1 % emulsion 267a . 0 . 2 mils of a solution of ammonium zirconium carbonate containing 20 % zirconium oxide solids ( from magnesium elektron , inc ., flemington , n . j . under the trade name of bacote - 20 ) was mixed in with every 100 mls . of this blend . a 3 % solids solution of sma 3000 was prepared by dissolving sma 3000 powder in aqueous ammonia as described in example 1 . a 3 % solution of ac316 emulsion and a 3 % solution of emulsion 267a were also prepared as described in example 1 . seventy ( 70 ) parts by volume of 3 % sma 3000 was mixed with fifteen ( 15 ) parts by volume of 3 % emulsion 316 and ten ( 10 ) parts by volume of 3 % emulsion 267a . three ( 3 ) mls . of cx - 100 polyfunctional aziridine crosslinking agent ( polyvinyl chemicals , inc .) was added per 100 mls . of blend . this composition includes minor amounts of a constituent ( cx 100 ) not aproved by the fda . if all fda - approved constituents are required , the cx - 100 in this example may be replaced by beetle 65 , a urea resin available from american cyanamid and the applied coating cured at 400 ° f . for 5 minutes . these coatings provide good abrasion protection after an automatic detergent wash cycle . a 40 % dispersion of carboxylate acrylic copolymer neutralized with a volatile neutralizing agent such as ammonium hydroxide ( carboset 514h from b . f . goodrich co .) was diluted with ammonia water to 2 % solids . seventy - five ( 75 ) parts by volume of 2 % 514h solution was mixed with twenty - five ( 25 ) parts by volume of 2 % emulsion 316 ( as described in example 1 ). 0 . 2 ml . of zirconium ammonium carbonate solution ( bacote - 20 as described in example 2 ) was added per 100 mls . of the blend . freshly - made pristine , borosilicate flint bottles with no pretreatment were coated with the coating compositions described in examples 1 to 4 . coating was applied to the exterior surfaces of glass bottles by spraying , roller coating , and dip coating . the temperature of the surface of the bottles was about 100 ° f . the coated bottles were air dried at room temperature . for comparison , glass bottles with and without a titanium oxide &# 34 ; hot - end &# 34 ; pretreatment were coated with three commonly used prior art &# 34 ; cold - end &# 34 ; coatings : except for oleic acid which is applied by vapor deposition , the other bottles were roller coated and compared with no pretreatment bottles roller coated with the new inventive coating compositions . bottles treated as described above were tested with a scratch test machine to evaluate the effectiveness of the respective coatings . the scratch test machine ( ball packaging -- glass container manufacturers institute ( gcmi )-- bulletin 64 ) is designed to abrade the surface of one glass against the surface of a similar bottle . one bottle is fastened securely in a stationary lower set of chucks . the other bottle is fastened in the upper set of chucks which are positioned so that the axis of the bottles will be at 90 ° to each other . the test load is applied to the upper bottle which is driven at a constant speed in a direction 45 ° to the axis of each bottle . by this design , a fresh surface on one bottle is always contacted with a fresh surface of the other . after each pass , the bottles are examined for scratches and the force or load in pounds required to scratch the bottle is noted . the maximum load that could be applied to this unit was 75 lbs . the scratch protection was measured on coated bottles after : ( 1 ) autoclaving at 121 ° c . for sixty minutes at 15 psi ; ( 2 ) washing in an automatic dishwasher without detergent ; ( 3 ) washing in a an automatic dishwasher with &# 34 ; cascade &# 34 ; detergent ; and ( 4 ) dry heat sterilization at 400 ° f . for 4 hours . since this scratch test simulated relatively mild abuse of glassware , another abrasion test was also devised to simulate more severe abuse . a bottle was placed on its side on a scale , and another bottle held in hand by its mouth and base was placed over the bottle lying on the scale so that the axis of the bottles were at 90 ° to each other and rubbed by sliding back and forth . the force exerted by hand was increased until a scratch was observed and the force noted on the scale . this type of abrasion testing produces scratches at a lower force than indicated by the ball scratch tester since the surface of one bottle is not always abrading with a fresh surface of the other bottle . the abrasion test results are shown in table 1 . another property that was measured was lubricity . lubricity is measured by determining the angle at which the top bottle in a pyramid of three bottles , on their sides , will start to slide when the support is tilted . untreated bottles will reach an angle of 35 ° to 40 ° before sliding . a good lubricious surface will permit a dry bottle to slide at about 8 ° to 16 °. lubricity measured on bottles with no pretreatment and coated with the new inventive coating compositions described herein were found to be within the range of 8 ° to 14 °. table 1__________________________________________________________________________number of pounds to produce scratch dishwasher dishwasher wash - no wash - with afterinitial detergent detergent autoclaveball hand ball hand ball hand ball handscratch scratch scratch scratch scratch scratch scratch scratchtester test tester test tester test tester tester__________________________________________________________________________untreated 5 2 5 2 5 2 5 2bottlestitanium / ap - 5 75 + 40 75 10 45 2 65 10ap - 5 10 2 10 5 5 1 5 1titanium / ap - 4 75 + 30 40 10 40 5 75 + 15ap - 4 25 5 5 1 5 1 10 1titanium / myrj - 52s 75 + 30 75 8 45 6 75 + 10myrj - 52s 35 10 5 1 5 1 10 2example 1 75 + 55 75 + 65 10 2 75 + 35example 2 75 + 60 75 + 65 20 2 75 + 40example 3 75 + 70 + 75 + 65 75 35 75 + 60example 4 75 + 40 75 + 35 75 + 35__________________________________________________________________________ the above results demonstrate the superior abrasion protection and durability of the new inventive coating compositions applied over untreated bottles as compared to prior art &# 34 ; coldend &# 34 ; coatings applied ove treated and untreated bottles . dry heat sterilized bottles exposed to 400 ° f . for 4 hours using example 1 coating showed a hand abrasion of 60 lbs . as compared to titanium / ap5 , titanium / ap4 and titanium / myrj52s coated bottles varying from 5 - 15 lbs . the hydrophilic nature of the carboxylic functionality of the resin in the coatings of the present invention , which represents a substantial portion of the coating composition , provides a surface that is compatible with conventional label adhesives and printing inks used on glassware . label adhesion tests conducted with pressure sensitive labels with adhesives based on rubbers and acrylics and on bottles with no coating and bottles coated with the inventive coating composition described herein were tested at 120 ° f . and high humidity conditions . no differences in adhesion was noted between uncoated and coated bottles . slight improvement in adhesion was noted for coated bottles under high humidity conditions as compared to uncoated bottles . the crosslinking reaction of the carboxylated resins with polyvalent metal ions as described herein is ionic in nature and is not temperature dependent . therefore , no heat is specifically required to cure these coatings . the crosslinking reaction proceeds as the volatile neutralizing agent , such as ammonia , escapes from the thin coating applied on the bottle surface . crosslinking with cx - 100 polyfunctional aziridine also proceeds rapidly at ambient temperatures . it is preferable to use resin concentrations of 1 - 5 % solids in the coating compositions of the present invention , although higher total solids concentration can also be used . the coating thickness on bottles coated in accordance with the present invention , at 1 - 5 % sma resin solid concentration was estimated by microscopy and by a thickness measurement instrument with a sensitivity of 50 angstroms based on a mechanical stylus ( alfa step profiler from tencor instruments , mountain view , calif .). the coating thickness thus measured varied from 500 to 5 , 000 angstroms . while this invention has been described with reference to specific embodiments thereof , it is not limited thereto , and the appended claims are intended to be construed to encompass the present invention in all of its forms and embodiments as may be devised by those skilled in the art .