the preferred embodiments will be illustrated with reference to the drawings . various other embodiments should become readily apparent from this description to those skilled in this art . experiments were conducted on a gama - 1 ™ automated wet station , manufactured by akrion llc , allentown , pa . the gama - 1 ™ automated wet station is capable of running two process sequences ; multi - tank and single tank insitu process . the process flow is illustrated schematically in fig4 and 5 . test conditions are also detailed in fig6 . a conventional lucid ™ dryer chamber was modified to function as a combined etching , rinsing , and drying chamber , and a chemical injection system according to fig3 was added . the chamber was constructed of pvdf with two walls having scalloped edges . the openings in the side - mounted fill tubes are angled upward so that during a fill cycle di water flows between the wafers and hits the tank walls two inches below the bottom of the scalloped edge . the tank is also specially designed to allow for uniform etching of dielectric films e . g . sio 2 . an outer weir directs cascading liquid into the module drain . a quick - dump port was installed on the bottom of the tank . chemical ( hf ) was drawn from a reservoir 11 by an adjustable metering pump 12 , injected into the di water supply stream 13 and blended by an in - line static mixer 14 . injection 15 into the tank can occur before or after wafers are delivered to the tank . an optional soak period can be programmed after the injection cycle , followed by the standard dry cycle . wafers were processed in the tool prior to the epitaxial growth steps in the reactor . to simulate patterned wafers situations , silicon wafers were sandwiched between dummy oxide wafers , thereby providing the simulated contamination to the silicon wafers from the oxide wafers under the most difficult conditions . etch byproducts were deposited from the oxide wafers onto the bare silicon wafers . the method of the invention was compared to prior cleaning techniques . when the low level sensor 17 in the reservoir 11 detects no liquid , a signal from the computer activates the three - way pneumatic solenoid , causing the normally - closed ( nc ) valve 16 to open . chemical flows through the manual valve 18 and the pneumatic solenoid into the reservoir 11 until the normal level sensor 19 is tripped . the chemical reservoir will automatically refill when the liquid level drops below the low level sensor 17 as long as no injection is occurring . if an injection is occurring , the refill is delayed until the inject time parameter has expired and the injection is finished . to fill the tank with a diw : chemical solution , the computer turns on the metering pump 12 . the pump 12 may be turned on during the pre - cycle stage or after product has been delivered to the tank , depending on how the inject on / off parameter is set . the pump 12 draws chemical from the reservoir 11 and sends it through the check valve 20 into the di water stream 13 . at the same time as the computer signals the pump 12 on , it also opens the di water valve ( not shown ), sending di water into the static mixer 14 . pressure from the di water stream causes the chemical and di water to flow into the static mixer 14 where the solution is blended before flowing into the process tank / dryer . the pump remains on for the time set by the software parameter inject time . when inject time expires , the computer signals the pump to turn off . di water continues to flow into the tank until the tank &# 39 ; s liquid level sensor is tripped . a comparative sequence of sc1 / rinse / hf / rinse / dry was used first to remove the contaminants resulting , as shown in fig1 in particle addition in the many thousands range . a second comparative sequence wherein surfactant was added to the hf bath to improve the wettability of wafers and hence reducing the particle deposition onto the wafers resulted in improved , i . e ., lower particle addition , but the presence of trace amounts of the surfactant interfered with the epitaxial growth process . the method of the invention resulted in an average of less than 50 particles added at 0 . 12 μm . to the wafers for hydrophobic cleans ( and worse case scenario of sandwiching oxide wafers with the test wafer ) as shown in fig2 while the average particle addition is − 6 ( 1σ = 11 ) for hydrophilic cleans as shown in fig8 . when using only bare silicon wafers ( control ), the conventional hf - last process yields comparable low particle addition , as shown in fig9 . the average particle addition was less than 40 particles at 0 . 12 μm . in addition , post - epi defects were also fairly low (˜ 1 . 26 defects / cm 2 ), as shown in fig1 . silicon wafers were sandwiched between oxide fillers to simulate typical wafer manufacturing . results show that conventional hf - last process used in this situation ( sc1 / rinse / hf / rinse / dry ) produces high particle counts at 0 . 12 μm (& gt ; 10 , 000 ) as shown in fig1 . consequently , the post epitaxial defects were also high (& gt ; 30 000 , not shown ). these lpds ( light point defects ) are considered to be nucleation sites during the epitaxial deposition . conventional wafer transfer between tanks plays a significant role in increasing silicate deposition into silicon wafers . the invention process and system minimizes exposing the wafer to an air / liquid interface where contaminants may reside . such contaminants deposit on the wafers during insertion into or pulling out of the liquid . the chemical injection system allows processing the wafers in the dryer . when wafers were processed with no transfer between cleaning steps , much lower particle deposition was obtained . as shown in fig1 and 13 , an average of less than 50 particles were added to the wafers . it is important to mention here that the use of ozonated rinse after hf and before going to the sc1 step is very critical in eliminating any potential for metal - induced pitting on the hydrophobic surface . the oxide chemically grown in the ozonated rinse is stable and thick enough ( 7 - 10 angstroms , see plots fig1 ) to protect the silicon surface from any metal roughening effects . the post - epi cleaning results for the insitu method are shown in fig1 . the average lpd density per wafer is about 0 . 89 defects / cm 2 . this level is significantly lower than any published data at 0 . 12 μm . clearly , the lower the hf - last defects , the lower the post - epi deposition defects , as shown in fig1 . the results of different cleaning recipes of the invention are summarized in fig7 . different wafer types were used also as fillers to investigate if the filler wafer type has any negative impact on the results . the results showed that the most critical step to achieve extremely low post epi deposition defects is the insitu hf / rinse / dry with no wafer transfer between steps . measurements were also taken to characterize the background oxide thickness as a measure of the [ o ] content on the wafer surface . the lower the [ o ] content on an h - passivated surface the lower the particle deposited as shown in fig1 . results of the experiments show significant reduction in particle deposition when compared to a conventional hf - last cleaning process . the insitu processing ( one step etch / rinse / dry ) has shown to be a key factor in eliminating particle deposition on exposed silicon areas on the wafer surface . experiments showed that the use of dilute chemicals and insitu hf / rinse / drying yields significantly lower defects ( post clean and epitaxial deposition ) than those obtained during conventional multi - tank wafer processing . etching of thin films was conducted also in this process bath . results show that while this process achieved the lowest particle addition to wafer under worst case scenario , uniform etching was also obtained as shown in fig1 . a standard deviation of 1 . 8 - 2 . 6 angstroms was obtained repeatedly when etching an average film thickness of 26 angstroms . while the invention and preferred embodiments have been described and illustrated in sufficient detail that those skilled in this art may readily make and use the invention , various alternatives , modifications , and improvements should become readily apparent to those skilled in this art without departing from the spirit and scope of the invention .