nited States Patent 1 91 Srail 1 Apr. 29, 1975 BENZOTHIAZOLE ACCELERATOR SYSTEMS [75] Inventor: Raymond C. Srail, Parma, Ohio [73] Assignee: The B. F. Goodrich Company, New  
  York, NY.  
 [22] Filed: Mar. 19, 1973 [21] Appl. No.: 342,747  
 Related U.S. Application Data [63] Continuation-impart of Scr. No. 118.172. Feb. 23.  
 1971, abandoned.  
 [56] References Cited UNITED STATES PATENTS 1,904,573 4/1933 Tuley 260/794 3.135.716 6/1964 Uraneck 260/45.5  
 Primary Examiner-Christopher A. Henderson Attorney, Agent, or Firm.l. Hughes Powell, Jr.  
 [ ABSTRACT Improved accelerator systems comprising a benzothiazole accelerator and an amine-blocked diisocyanate are provided for vulcanization of polymers. These accelerator systems are stable during processing, thereby minimizing scorch of the polymer, but at vulcanization temperatures provide very rapid cures.  
 7 Claims, No Drawings 1 BENZOTJ-IIAZOLE ACCELERATOR SYSTEMS I CROSS-REFERENCE TO RELATED APPLICATION This application is a continuation-impart of application Ser. No. 118,172 filed doned.  
  BACKGROUND OF THE INVENTION Various benzothiazole compounds are well known accelerators used throughout the industry to provide Feb. 23, 1971 now aban-j fin-derived homopolymers and copolymers for which thefpresent accelerator system is useful include: natural cure rates could be obtained. It would be particularly I I desirable if with these activated benzothiazole accelerator systemsthere was little or no effect on the scorch at temperatures typically employed for processing elastomers. It would then be possible to obtain very rapid cure with little or no reduction in the scorch time of the rubber. For the rubber compounder this would minimize or completely eliminate any change in the compounding and processing of the rubber stock prior to vulcanization as is often required when more active accelerators are employed.  
  Activators for accelerators are known. For example, diphenyl guanidine and its derivatives are often combined with other&#39;accelerator compounds to obtain improved cure rates. However, both components of the mixture function as accelerators and while the cure rate is generally improved there is a proportional decrease in the scorch time at lower temperatures. It would be highly advantageous to have an accelerator system wherein as the cure rate is increased the scorch time is not proportionately decreased.  
 SUMMARY OF THE INVENTION DETAILED DESCRIPTION The accelerator system of this invention comprises an amine-blocked. diisocyanate with a thiobenzothiazole accelerator, the combination providing an improved balance of search safety and rapid cure. The accelerator systems of this invention are useful with any rubber, natural or synthetic, capable of sulfur cure.  
  Especially useful rubbers for the purposes of the present invention are derived from conjugated diolefins containing from 4 to 6.c arbon atoms .such as 1,3- butadiene, isoprene, piperylene,. butadiene-1,3 and thelike. The conjugated diolefin will constitute from about 30 to. 100% by weight of the overall polymer composition. Also useful are stereoregular rubbers containing 80% or more of the 1,4- addition product which has predominantly one stereo configuration (cisor trans-) Typical conjugated diole- 2,3-dimethylrubber and synthetic natural rubber (cis-polyisoprene), trans-polyisoprene, polybutadiene, chloroprene polymers (neoprene), butyl rubbers (copolymers of isobutylene and isoprene), GR-S (copolymers of styrene and butadiene), nitrile rubbers (copolymers of butadiene and acrylonitrile) and copolymers of conjugated diolefins with lower alkyl acrylates or lower alkyl methacrylates or similar monomers. Such rubber compositions contain olefinic unsaturation constituting from about 0.5 to 50% by weight of the overall polymer composition.  
 I .The present accelerator systems are also useful for polymers derived from a-monoolefins which contain olefinic unsaturation as a result of polymerizing one or &#39;more monomers containing multiple unsaturation.  
 Such polymers include, for example, ethylenepropylene-diene and ethylene-butene-diene terpolymers wherein the diene monomers will typically be 1,4- hexadiene, methyl-1,4-hexadiene, a 1,4,9-decatriene, a methyl-1,4,9-decatriene, dicyclopentadiene, vinylcyclohexene, vinyl norbornene, ethylidene norbornene, methylenenorbornene, methyl norbornadiene, methyltetrahydroindene and the like. a-Olefin-derived polymers of this type may contain about 0.3 to 20% by weight of the diene monomer polymerized with about 30&#39;to 80% by weight ethylene and 20 to 70% by weight propylene or butene-l.  
  In addition to the above-mentioned preferred rubber compositions derived from conjugated diolefins and a-monoolefins, the present accelerator systems are also effective to obtain rapid cure with minimum scorch with other sulfur-vulcanizable polymers such as polyoctenomers and polypentenomers, silicone rubbers, thiokols, acrylate rubbers and otherrelated compositions. Any sulfur curable polymers will be effectively cured and are within the scope of the present invention. The improved accelerator systems of this invention contain as one of the essential components a benzothiazole compound which is substituted in the 2-position with athio radical. Any Z-thiobenzothiazole which functions as a vulcanization accelerator may be employed with the amine-blocked diisocyanate and is within the scope of the present invention. The benzothiazole compounds have the structural formula wherein X is a member selected from the group consisting of hydrogen; 2-thiobenzothiazole; substituted mino; alkyl; aryl; halo-, nitro-, anilinoand alkyl-substituted aryl; 5- or 6-membered heterocycles containing one or more oxygen, nitrogen or sulfur heteroatoms; a monoor divalent radical selected from the group ammonium, sodium, potassium, calcium, zinc, cadmium, copper and lead. When X is a divalent metal the second valence of the metal may be satisfied with an alkyl, aryl,  
 substituted-aryl or preferably with a second 2- wherein Me is the divalent metal, preferably zinc, cadmium or lead. Exemplary benzothiazole compounds include: 2-mercaptobenzothiazole, sodium 2-mercaptobenzothiazole, potassium Z-mercaptobenzothiazole, ammonium 2-mercaptobenzothiazole. zinc 2-mercaptobenzothiazole, 2-(2.4-dinitrophenylthio)- benzothiazole, N-cyclohexyl-2-benzothiazolesulfenamide, N-oxydiethylene-2-benzothiazolesulfenamide. di-2-benzothiazyl disulfide and the like. Excellent results have been obtained with Z-mercaptobenzothiazole. zinc 2-mercaptobenzothiazole and di-2- benzothiazyl disulfide.  
 7 iron or the like. Best results are obtained when the metal oxide or metal salt is derived from zinc, cadmium or lead. Zinc oxide and zinc fatty acids are especially Although the 2-thiobenzothiazoles are especially use- The amount of 2-thiobenzothiazole present in the rubber will range between about 0.2 and parts&#39;by weight per 100 parts rubber. Excellent results are obtained when from 0.5 to 3 parts of the benzothiazole I compound are employed per 100 parts of the rubber.  
  To obtain optimum advantages of this accelerator system, a vulcanization activator should also be present. Well known vulcanization activators are listed in Materials and Compounding Ingredients for Rubber, Rubber World, 1970 Edition. These vulcanization activators are typically a metal oxide or hydroxide or a metal salt. The activator may be introduced as part of the accelerator compound as in metal Z-mercaptobenzothiazole, such as zinc Z-mercaptobenzothiazole. If the activator is introduced in the form of a metal oxide about 1 to 10 parts and more preferably from about 1.5 to 4 parts per 100 parts rubber will be added. When a metal oxide is employed it is desirable and advantageous to also add a fatty acid having a total carbon atom content ranging from 12 to 24 carbon atoms, such as stearic acid. It is felt that by the addition of such fatty acids the metal is solubilized so that it may better participate in the vulcanization. The amount of fatty acid employed will range from about 0.5 to 5 parts per 100 parts of the rubber. While the incorporation of metal oxide and fatty acid as separate entities is generally preferred based on economic considerations, if desired, a preformed metal salt of a fatty acid containing from 12 to 24 carbon atoms such as zinc laurate, zinc palmitate, zinc stearate or the like may be employed. If preformed metals are employed they will range from about 0.5 to 5 parts per 100 parts rubber and more preferably from about 0.75 to 2 parts. The metal will generally be a divalent metal such as zinc, cadmium, lead, calcium,  
 useful activators for use with the present activator systems.  
  The present accelerator systems are useful with a wide variety of rubber compositions which may additionally contain conventional processing aids and oils, fillers. reinforcing agents, extenders, curing additives, cure retarders and modifiers and various stabilizers including antioxidants and antiozonants. Any phenolic stabilizer can be employed in any useful amount. When amine stabilizers are present as antiozonants it is preferred that p-phenylenediamines wherein the amine function is sterically hindered such as N-l ,3- dimethylbutyl-N&#39;-phenyl-p-phenylenediamine or other sterically hindered amines be employed.  
  The amine-blocked isocyanate is formed by the reaction of a diphenyl diisocyanate or an aromatic diisothiocyanate with a dialkylamine or heterocyclic amine. The reaction can be represented as follows XH HX where X is O or S; R and R are alkyl radicals, either the same or different, containing l to 6 carbon atoms or R, and R together with the nitrogen atom form a heterocyclic amine containing 3 to 8 atoms of carbon, nitrogen, oxygen and/or sulfur; and R is a bivalent aromatic radical.  
  The amines employed are strong amines i.e., amines having a pK dissociation constant in aqueous solution of about 4 or below (see Lange&#39;s Handbook of Chemistry, Revised 10th Edition, Page 1214 [967) and Handbook of Chemistry&#39;and Physics, 45th Edition, Page D-76 (1964)). The amines can be dialkyl amines wherein the alkyl radicals contain 1 to 6 carbon atoms or heterocyclic amines. Examples of the amines are dimethylamine, diethylamine, dipropylamine. diisopropylamine, dibutylamine, diamylamine, methylethylamine, and the like, and heterocyclic amines such as pyrrolidine, piperidine. 2-, 3-, or 4-pipecoline. and the like.  
  The diisocyanates employed are diphenyl diisocyanates or aromatic diisothiocyanates. Examples of the diphenyl diisocyanates are diphenylmethane-p,pdiisocyanate, di( 3-methylphenyl)methane-p,pdiisocyanate. diphenylisopropylidene-p,p&#39;-  
 diisocyanate. di(3-methylphenyl)p,p&#39;-diisocyanate. di- (3-methoxyphenyl)-p,p-diisocyanate, and the like. Examples of aromatic diisothiocyanates are p-phenylene diisothiocyanate, p-toluene diisothiocyanate, p-3- fluorophenyl diisothiocyanate, naphthalene-1,5- diisothiocyanate. naphthalenel ,8-diisothiocyanate and the like. I  
  Blocked isocyanates are known and are readily prepared by reaction between isocyanates and an amine. The reaction is rapid and essentially quantitative. The reaction is normally conducted in a solvent or diluent to control the reaction temperature. Equimolar or a molar excess of amine for each mol of isocyanate group is usually employed. The reaction may be carried out, for example, in a solvent medium as dry toluene. Because of the reactivity of isocyanate groups with water a dry solvent or diluent is employed. The dried reaction products are generally white friable solids.  
  The amine-blocked diisocyanates of the present invention are distinguished from known blocked isocyafur donor compounds such as dithiodimorpholine are employed the amount required will be varied to supply these amounts of sulfur on a theoretical ,basis. The amount of sulfur will be varied depending on the temnates by their use to prepare unique sulfur vulcanizable 5 perature of cure, the particular rubber, the cure time compositions having an improved balance of scorch and the d r of cure desired. Safety and rapid Cure Yete- This Combination of rapid The present accelerator systems are useful for a wide cure and improved scorch safety is obtainable only with variety of rubber compositions which may additionally the amine-blocked diisocyanates disclosed hereincontain conventional processing aids fillers, oils, fillers p 9 5 Shows the use Of 10 reinforcing agents, extenders, curing additives, cure realkyl and/01&#39; aromatic e (monoisocyanatel COITF tardants and modifiers, stabilizers, antioxidants. antipounds in curing rubber. However. when these comozonams d h lik Pounds were evaluated in rubber Compositions y The following Examples serve to illustrate the invenyielded inferior Scorch safety Compared to the aminetion more fully but are not intended to limit the scope blocked diisocyanates of the present invention. The imthereof. In these examples all parts and percentages are proved scorch safety results from using the diphenylreported on a weight basis unless otherwise indicated. diisocyanates or aromatic diisothiocyanates to prepare Cure and scorch properties were determined with a the amine-blocked diisocyanate. There is a definite one curometer such as described in US. Pat. No. need for greater scorch safety in rubber compositions. 3,494,172 by measuring the torque (in/lbs.) developed particularly in view of the use of fast-acting accelerawith time (min.). Data obtained from the resulting cure tors, carbon blacks and other compounding ingredients curves are as follows: Cure time (T the time required which tend to accelerate cure, and the use of higher to reach 90% of maximum torque (1 scorch time processing and vulcanizing temperatures to increase (T,.) the time required for the torque to increase two product output. in/lbs. over the minimum torque (7 and cure rate When the amine-blocked diisocyanate breaks down (CR,,,,,, equal Ar/AT determined in lbs/min. at a sec at vulcanization temperatures, the liberated amine tion of the curve having maximum slope. must act uickl and efficientl to cure the rubbercompositici n. Th e use of the di sclosed dialkylamines EXAMPLE] and heterocyclic amines, both types further having a A rubber masterbatch was prepared as follows: pK dissociation constant of about 4 or below, provides rapid cure at vulcanization temperature. Weak amines Ll l i provide a substantially slower cure rate. For example, US. Pat. No. 3.135.716 shows a blocked lsocyanate Aromatic oil 40.6 consisting of diphenylamine and tolylene-2,4- blink g5 Ste-uric acid 1.0 dnsocyanate. Dlphenylamme 1s a weak amine, havmg Zinc oxide 3,0 a pK value of 13.1. When the disclosed diphenylamine e e g Oil l5 blocked isocyanate was used in a rubber composition Ammx&#39;dam/ummonum the composition exhibited a substantially longer cure An accelerator system comprised of 2.2- time at vulcanization temperatures than compositions benzothiazyl disulfide (MBTS) with an amine-blocked employing the amine-blocked diisocyanates of the 40 diisocyanate of pyrrolidine and diphenylmethane-p,ppresent invention. diisocyanate (PYR/MDl) was evaluated in the above The total amount of the 2-thiobenzothiazole and rubber masterbatch and the results compared with the amine-blocked diisocyanate in the rubber will range cure obtained with MBTS alone. The amine-blocked between about 0.5 to 8 parts per 100 parts of the rubdiisocyanate (PYR/MDI) and MBTS were milled into her and more preferably from about 1 to 5 parts per the rubber masterbatch at a temperature of 150: 5F. 100 parts of rubber. The weight ratio of the amine- The sulfur was then added and the rubber sample blocked diisocyanate to the 2-thiobenzothiazole will be milled for 5 minutes at this same temperature. About from about 0.2:1 to 4:1 and more preferably from 12 to 15 gram samples were placed in the cone curomeabout 0.5:1 to 2:1. The order of addition ofthe accelerter cavity and evaluated over the temperature range ator components is not critical nor is any special pro- 220 to 360F. Torque values were measured and concessing required with these additives. tinuously charted, and T,., T and CR,,,,,, determined To obtain acceptable cures with the present acceleraand reported in Table l. T. was not obtained at tempertor systems the amount of sulfur employed for vulcaniatures below 330F. due to the long times required to zation can range from about 0.3 to about 6 parts by arrive at such values and the lack of significance weight per partsof the rubber. It is generally prethereof. The styrene content of a styrene-butadiene ferred, however, that the sulfur be present from about rubber was about 23% and the 4 minutes Mooney value 0.5 to about3 parts per 100 parts of the rubber. lf sulat 212F. was about 50.  
 TABLE 1 Sample MBTS (PYR/MDl) Sulfur Cone Curometer Data (pphr (pphr) (pphr) Property Temperature 360F. 330F. 280F. 240F. 220F.  
 A 0.88 1.03 1.65 T,. 2.68 6.35 T. 1.00 1.95 11.0 63.8 CR,,,,,, 29.4 11.9 1.93 0.38 0.121 B 0.88 None 1.65 T,. 4.34 1 1.05 T,. 1.45 2.90 15.4 82.2 196 CR,,,,,, 9.10 4.47 0.98 0.167 0.091  
 &#34; pphr parts per hundred parts rubber It is seen from the data presented in Table I that improved cure rates are obtained with Sample A containing the accelerator system of the present invention. with excellent scorch protection at temperatures typi- A high degree of cure is obtained in a very short time, and the vulcanizates have excellent physical properties. Similar results are obtained when employing the amineblocked diisocyanates of the present invention with ciscally employed for processing. It is also significant to l.4-p0ly1s0prene rubber and pale crepe natural rubber.  
 TABLE ll Sample MBT Amine- Sulfur Property Cone Curometer Data (pphr) blocked (pphr) Temperature diisocyan- 360F. 330F. 280F. 240F. 220F. ate (pphr) C 0.88 None 1.65 T,. 4.56 13.55  
  T 1.60 3.20 16.9 79.5 193.5 CR,,,.,, 8.93 3.65 0.86 0.15 0.075 D 0.88 PYR/MDI&#39; I.65 T,. 2.55 6.25  
 1.03 T 0.95 1.75 l 1.0 1.5 I53 C 28.6 11.3 1.90 0 30 0.10 E 0.1111 PYR/MDI&#39; 1.54 T,. 2.48 5.30 1.45 T 0.95 1.90 1 1.0 60.4 161 CR,,,,,, 29.1 ll.6 1.72 0 0.07 F L lYR/MDl l.65 T,. 1.99 4.65 1.45 T 0.88 L8] 9.3 52.6 129 CR,,,,, 1 38.5 15.1 2.63 0.41 0.14 O 0.88 DMA/MDI&#34; l.65 T,. 2.68 6.20 0.90 r. 0.911 1.x5 9.6 53.5 131 CR,,,.,, 25.0 12.8 2.41 0.40 0.144 H 1.25 DMA/MDI 1.65 T. 1.97 4.314 L28 T, 0.90 1.74 11.7 46.3 114 reaction product of pyrrolidinc and diphcn lrnethanc-p.p&#39;-diisocyanale reaction product of tlimcthylaminc and diphen [methane-p41&#39;-diisocyan;ttc  
 note that with Sample A as the cure rate increases with increased temperature the scorch values are not proportionately decreased as they are with Sample B containing MBTS alone. For example. from a comparison of the data obtained for Sample A and B at 330F. and 360F. it is seen that with Sample A the cure rate approximately triples with a F. rise in temperature whereas with Sample B the cure rate is only approximately doubled. Scorch times. however. for both Samples A and B are only approximately halved as the temperature is raised 30F. The advantages of the present improved accelerator systems thus become evident.  
 EXAMPLE II To further demonstrate the advantage of the present improved accelerator systems, Z-mercaptobenzothiazole (MBT) was employed with the rubber masterbatch of Example I. Various amine-blocked diisocyanates were employed to activate the MBT accelerator. Cone curometer data was obtained at temperatures between 220 and 360F. and reported in Table II.  
  The utility of the vulcanizates obtained is evident from a consideration of the physical properties of the cured rubber. For example. for Sample F the following physical properties were obtained when cured at 360F. for varying periods:  
 EXAMPLE III A rubber masterbatch was prepared for use in evaluating various blocked isocyanates. The composition of the masterbatch is as follows (in parts by weight):  
 Polybutadiene&#34; N285 carbon black Aromatic oil Stearic acid Zinc oxide Agerite Resin D&#34; Antioxidant&#34; 23.5&#39;71 styrene. 76.5% hutadiene by weight 98% cis-lA-hutadicnc &#34;polymerized trimcthylol/dihydroquinolinc N- l .3-tlimcth lhut \&#39;l-N&#39;-phcnyl-p-phenylcnediamine 2 3 6 12 24 known blocked isocyanates or ureas are made on an Mmme Mmute equal mole basis, adjusted for the moles of amine liber- Tensile (psi) 1950 1990 2000 1900 1x50 ated per compound if need be. Elongation 800 780 799 The sam les re ared and data obtained ar a f 300% Modulus (psi) 490 520 510 510 510 p p p e S lows:  
 TABLE III Sample blocked Parts per T at T,. at Maximum T,. 360F.  
 isocyanate I00 parts 240F. 360F. torque ruhher minutes minutes at 360F. T 240F.  
 l Monomethyl urea 0.56 32.00 2.43 53.0 0.075: 2 l.3-dimethyl urea 0.63 38.60 2.93 50.3 0.0759 3 LZ-diethyl urea 0.86 22.96 L80 63.8 0.0784 4 l-ethyl-l-phen &#39;l-3-nbutyl urea I.6l 56.20 3.6] 43.0 0.0642  
 TABLE lll Continued Sample Blocked Parts per T. at T,. at Maximum T,- 360F.  
 lsocyanate l parts 240F. 360F. torque rubber minutes minutes at 360F. T 240F.  
  Z-phenyl urea 0.99 48.80 3.2] 48.3 0.0653 6 diphenyIamine/toluene diisocyanate product L88 67.00 3.72 46.2 0.0555 7 dimethylamine/toluene diisocyanate product 0.96 33.66 2.07 57.8 0.0615 8 dimethylamine/diphenylmethane-p.p-  
  diisocyanate product I 24 57.80 2.46 54.8 0.0426 9 pyrrolidine/diphenylmethane-p.p&#39;-  
  diisocyanatc product 1.44 63.78 .57 53.0 0.0403 pyrrolidine/p-phenylenediisothiocyanate product 1.24 57.40 7 50 52 5 0.0435  
  Samples I to 5 use blocked isocyanates within the scope of U.S. Pat. No. 1,904,573; i.e.. monoisocyanates. Sample 6 uses the diphenylamine/toluene diisocyanate adduct shown in U.S. Pat. No. 3.135.716. Samplc 7 uses the reaction product of dimethylamine and a monophcnyldiisocyanate which is outside the scope of the present invention. Samples 8 to 10 employed amine-blocked diisocyanates of the invention. A high value of T,- at 240F. indicates good processing safety. A low value ofT at 360F. indicates fast cure at vulcanization temperature. A low value for the ratio T,- 360F./T 240F. indicates a good balance between processing (scorch) safety and rapid cure. The lower the value. the more ideal the balance between safety and rate of cure.  
  It is seen in the data that the amine-blocked diisocyanates of the invention (samples 8 to 10) yielded a significantly lower T../T value than the known blocked isocyanates. Of further note, samples 4, 5 and 6 are all prepared using phenylamines, and all three samples yielded inferior maximum torque values than the other samples. This indicates that the state of cure of the vulcanizate is inferior when using phenylamines to prepare the blocked isocyanates. In contrast. the amines used in the present invention all yield a high state of cure. The three samples using phenylamines (samples 4-6) also have high cure times at 360F. which leads to decreased product output. Sample 7 using a monophenyl diisocyanate yielded a significantly inferior balance of scorch safety and cure rate, i.e., a high T,/T value. compared to samples 8 and 9 employing the diphenyl diisocyanates of this invention. Sample 10 uses a diisothiocyanate of the invention. and a good balance of safety and cure rate was obtained.  
 1 claim:  
  l. A composition comprising (1) a sulfur-vulcanizable rubber having from about 0.5 to 50% by weight of olefinic unsaturation derived from conjugated diolefins containing from 4 to 6 carbon atoms, (2) sulfur. (3) a metal vulcanization activator selected from the group consisting of metal oxides. hydroxides, and salts wherein the metal is selected from the group consisting of zinc, cadmium. lead, calcium and iron, and (4) an accelerator system consisting essentially of (a) a 2- thiobenzothiazole accelerator of the formula wherein X is selected from the group consisting of hydrogen. 2-thiobenzothiazole, an amine, alkyl, aryl. alkaryl, halo, nitro, anilino, 5- or 6-membered heterocycles containing oxygen, nitrogen, or sulfur heteroatoms, a monovalent radical selected from the group consisting of ammonia, sodium. and potassium, and a divalent radical selected from the group consisting of calcium, zinc. cadmium, copper and lead, and attached thereto an alkyl. aryl. substituted aryl or a second thiobenzothiazole radical; and (b) an amine-blocked diisocyanate of (i) a heterocyclic amine having a pK dissociation constant of about 4 or below and (ii) a diisocyanate selected from the group consisting of diphenyldiisocyanates and aromatic diisothiocyanates.  
  2. A composition of claim 1 wherein the total weight of 2-thiobenzothiazole accelerator and the amineblocked diisocyanate is present at a level from about 0.5 to 8 parts by weight per parts by weight of the rubber, and the weight ratio of the amine-blocked diisocyanate to Z-thiobenzothiazole accelerator is from about 0.221 to 4:1.  
  3. A composition of claim 2 wherein the amineblocked diisocyanate is derived from (i) a heterocyclic amine selected from the group consisting of pyrrolidine, piperidine, 2-pipecoline, 3-pipecoline, and 4- pipecoline and (ii) a diisocyanate selected from the group consisting of diphenylmethane-p,p&#39;- diisocyanate. di( 3-methylphenyl)methane-p,p diisocyanate, diphenylisopropylidene-p,p diisocyanate, di( 3-methylphenyl )-p,p&#39;-diisocyanate,  
 di(3-methoxyphenyl)p,p&#39;-diisocyanate, p-phenylene diisothiocyanate. p-toluene diisothiocyanate. p-3- fluorophenyl diisothiocyanate. naphthalene-1,5- diisothiocyanate, and naphthalene-1,8- diisothiocyanate.  
  4. A composition of claim 3 wherein the metal vulcanization activator is a zinc salt of a fatty acid, and the 2-thiobenzothiazole is selected from the group consisting of Z-mercaptobenzothiazole, zinc-2-mercaptobenzothiazole and di-2-benzothiazole disulfide.  
  5. A composition of claim 4 where the amineblocked diisocyanate is of pyrrolidine and diphenylmethane-p,p-diisocyanate.  
  6. A composition of claim 4 where the amineblocked diisocyanate is of piperidine and diphenylmethane-p,p&#39;-diisocyanate.  
  7. A composition of claim 4 where the amineblocked diisocyanate is of pyrrolidine and p-phenylenediisothiocyanate.