Method of manufacturing a zeolitic adsorbent useful for aromatic separation
United States Patent 1191 Rosback 1451 Apr. 15, 1975 [54] METHOD OF MANUFACTURING A ZEOLITIC ADSORBENT USEFUL FOR AROMATIC SEPARATION Donald H. Rosback, Elmhurst, Ill.  
 [73] Assignee: Universal Oil Products Company, Des Plaines, Ill.  
 [22] Filed: Sept. 28, 1973 [21] App]. No.: 401,783  
  Related U.S. Application Data [63] Continuation-in-part of Ser. No. 356,666, May 2,  
 [75] Inventor:  
 Primary E.taminerC. Dees Attorney, Agent, or FirmJames R. Hoatson, Jr.; Thomas K. McBride; William H. Page, II  
 [5 7] ABSTRACT A method of manufacturing a solid adsorbent which method comprises the steps of: contacting a base material containing type X or type Y zeolite with a fluoride-containing solution of sodium hydroxide at first ion exchange conditions to effect the addition of sodium cations to and the extraction of alumina from the base material; ion exchanging the base material at second ion exchange conditions to effect the essentially complete exchange of sodium cations; and, drying the exchanged zeolite at conditions ro reduce the LOl at 900C. to less than about 10 wt. The sodium cations can be essentially completely exchanged with either barium and potassium cations in a weight ratio of from about 1.5 to 200 or with barium cations alone.  
 The combination fluoride-caustic treatment prior to the exchange with potassium and barium or with barium alone produces a superior adsorbent for separating the para isomer from a feed mixture comprising at least two bi-alkyl substituted monocyclic aromatic isomers, including the para isomer, the isomers having from 8 to about 18 carbon atoms per molecule. The adsorbent so produced has faster para isomer transfer rates and higher aromatic capacity than one produced either from untreated base material or from base material treated with fluoride or caustic alone. Additionally a fluoride treatment of base material alone or in combination with or subsequent to a caustic treatment, prior to potassium and barium or barium ion exchange, essentially eliminates a troublesome dustiness characteristic of adsorbents prepared from untreated base material.  
 14 Claims, No Drawings 1 METHOD OF MANUFACTURING A ZEOLITIC ADSORBENT USEFUL FOR AROMATIC SEPARATION RELATED APPLICATIONS This application is a continuation-in-part application of copending application Ser. No. 356,666. filed May 2, 1973 all the teachings of which copending application are incorporated herein by specific reference thereto.  
 BACKGROUND OF THE INVENTION 1. Field of the Invention The field of art to which this invention pertains is crystalline aluminosilicate adsorbent production. More specifically, this invention relates to a method of manufacturing an adsorbent having characteristics desirable for the separation of certain aromatic isomers.  
 2. Description of the Prior Art There are numerous methods for the manufacture and ionexchange of various crystalline aluminosilicates, particularly the type X and type Y crystalline aluminosilicates, to yield products useful for effecting given hydrocarbon reactions or separations. In the method of this invention, a manufacturing method has been discovered whereby an adsorbent material is pro duced having superior properties with respect to the separation of the para isomer from a feed mixture comprising at least two bi-alkyl substituted monocyclic aromatic isomers. including the para-isomer. the isomers having from 8 to 18 carbon atoms per molecule.  
  A common problem encountered with most adsorbents and many catalysts is dust which can form excessive pressure drop after the adsorbent or catalyst has been loaded into the adsorbent chambers or reaction vessel. Certainly it is for this reason that adsorbents and catalysts are manufactured to meet certain minimum physical strength requirements and that they are loaded into chambers and vessels with care to avoid breakage. Although operations such as screening can be used to remove most of the interstitial smaller particles and dust such operations generally fail to remove dust which may coat particles of adsorbent or catalyst of the proper size. This type of dust, apparently held to the particle by electrostatic attraction, may then later be removed by liquid passing through the adsorbent chamber or catalyst vessel and accumulate to form excessive pressure drops.  
  I have discovered that the troublesome dustiness characteristic of adsorbents is virtually eliminated by a fluoride treatment of the base material. It is thought that the fluoride solublizes the dust by reacting with combined aluminum compounds present in the dust thereby removing the dust from the particles.  
  In the method of our invention I have additionally found that an ion-exchange of a base material with a fluoride-containing aqueous solution of sodium hydroxide followed by an ion-exchange with potassium and barium or with barium alone and then a drying step produces and adsorbent with faster transfer rates and higher aromatic capacity than adsorbents produced by either fluoride or caustic treatment alone or with untreated base. Although it is hypothesized that the ionexchange with aqueous sodium hydroxide replaces non-sodium cations such as H+ or Group II-A cations occupying exchangeable sites within the zeolite and thereby permits higher amounts of barium and potassium or barium alone to be added during a subsequent ion-exchange step. the synergistic result obtained by combining the fluoride treatment with the sodium ionexchange is neither expected nor understood.  
  The prior art has neither disclosed nor suggested the method of our invention to produce these results.  
 SUMMARY OF THE INVENTION It is an object of the present invention to provide a process for the manufacture of a zeolitic adsorbent which process employs a type X or type Y structured zeolite as an intregal component of the finished adsorbent. It is another object of the present invention to provide a new method for the manufacture of an adsorbent which has superior properties when used for the separation of para aromatic isomers and in particular for the separation of para-xylene.  
  In brief summary, my invention is, in one embodiment, a method of manufacturing a solid adsorbent useful for the separation of the para-isomer from a feed mixture comprising at least two bi-alkyl substituted aromatic isomers. including the para-isomer. said isomers having from 8 to about 18 carbon atoms per molecule which method comprises the steps of: (a) contacting a base material containing type X or type Y zeolite with a fluoride-containing solution of sodium hydroxide solution at first ion-exchange conditions to effect the addition of sodium cations to and the extraction of alumina from the base material; (b) ion-exchanging the base material at second ion-exchange conditions to effect the essentially complete exchange of sodium cations; and, (c) drying the resulting exchanged mass at conditions to reduce the LOI at 900 C. to less than about 10 wt. 7:.  
 DESCRIPTION OF THE INVENTION The type X and type Y crystalline aluminosilicates or zeolites herein contemplated are described as a threedimensional network of fundamental structural units consisting of silicon-centered SiO and aluminumcentered AlO tetrahedra interconnected by a mutual sharing of apical oxygen atoms. The space between the tetrahedra is occupied by water molecules and subsequent dehydration or partial dehydration results in a crystal structure interlaced with channels of molecular dimension.  
 where M represents at least one cation having a valence of not more than 3, n represents the valence of M and y is a value up to about 8 depending upon the identity of M and the degree of hydration of the crystal. The cation M may be one or more of a number of cations such as the hydrogen cation, the alkali metal cation, or  
 the alkaline earth cations or other selected cations and is generally referred to as an exchangeable site.  
  The type Y structured zeolite in the hydrated or partially hydrated form can be represented in terms of the mole oxides for the sodium form as represented by Formula 2 below:  
 Formula 2 (0.9102)Na O:Al O :wSiO :yH O  
 where w is a value of greater than about 3 up to 8. and y may be any value up to about 9.  
  The term type X zeolite and type Y zeolite&#34; as employed herein shall refer not only to type X structured and type Y structured zeolites containing sodium cations but to those containing other cations such as the hydrogen cations. the alkali metal cations or the alkaline earth cations. Typically both the type X and type Y structured zeolites as initially prepared are predominantly in the sodium form but they may contain. possibly as impurities. the other cations as mentioned above.  
  The term base material as used herein shall refer to a type X or type Y zeolite-containing starting material used to make final adsorbent by the method of this invention. Usually such base material will be predominantly in the sodium form of the zeolite. Generally the base material will be in the form of particles such as extrudates, aggregates, tablets. pills. macro-spheres, or granules produced by grinding any of the above to a desired size range. The type X or type Y zeolite can be present in the base material in concentrations generally ranging from about 75 wt. 7( to about 90 wt. 7: of the base material based on a volatile free composition. The remaining material in the base material generally comprises amorphous silica or alumina or both which is present in intimate mixture with the zeolite material. This amorphous material may be an adjunct of the manufacturing process of the type X or type Y zeolite (for example. intentionally incomplete purification of the zeolite during its manufacture) or it may be added to the relatively pure zeolite to aid in forming particles of the zeolite.  
  A specific base material is commercially available nomi&#39;nal l/l6-inch extrudate comprising 13X zeolite and a minor amount of amorphous material as binder. This base material is primarily in the sodium form; that is, the cation represented as M in Formula 2 above is primarily sodium. By chemical analysis the Na OlAl O ratio is usually about 0.7 or less and can typically be about 0.6 or less which, it should be noted, is less than the 09:02 indicated in Formula 1 above. Other cations such as H+ and any of the Group &#34;A metal cations may be present. primarily as impurities, to supply the remainder of the cations needed for chemical balance. The silica to alumina ratio of this starting material by X-ray determination is about 2.5 and the same ratio by chemical analysis is about 2.6. Normally the starting material whether in the extrudate or pellet form is granulated to a particle size range of about -40 mesh (Standard U.S. Mesh) before the first ion exchange step is begun. This is approximately the desired particle size of the finished adsorbent.  
  The first ion exchange with a fluoride-containing sodium hydroxide solution replaces non-sodium cation impurities in the type X or type Y zeolite contained in the base material thereby converting the zeolite essentially completely to the sodium form. Increasing the sodium content of the. zeolite permits a higher loading of barium and potassium cations or of the barium cation alone into the zeolite structure on a subsequent ion exchange. To produce an acceptable adsorbent it is preferred that the sodium content of the starting material. as characterized by the weight ratio Nago/Algog be increased to a ratio greater than about 0.70 and more preferably from about 0.75 to L0. [on exchange conditions should be so regulated to achieve this degree of ion exchange.  
  Although mild ion exchange conditions are employed. this step additionally removes a small amount of silica and alumina. Total silica and alumina removal from the base material is from about l to about 15% and is generally in the range of about 1 to 5 wt. 7:. Analyses indicate that the bulk of both soluble and insoluble material removed from the base material is aluminum, as alumina or sodium aluminate. At least a portion of the alumina extracted appears to be from the zeolite itself rather than from any amorphous material since there is some nominal loss of zeolite as detected by X-ray analysis after this step. It is not known whether the small amount of silica removed from the base material came from the crystalline (zeolite) portion or the amorphous portion of the base material.  
  The degree of ion exchange and extraction of alumina achieved is a function of the three variables of caustic and fluoride concentrations. temperature at which the ion exchange is conducted, and the length of time the ion exchange is continued.  
  The preferred fluoride-containing sodium hydroxide solution employed will be sodium hydroxide and sodium fluoride dissolved in water. Suitable concentrations to obtain the desired ion exchange can be from about 0.5 to 10 wt. 7: of sodium hydroxide with the preferred concentration being from about 0.5 to 5 wt. &#34;/1 and from about 0.1 wt. 7: up to the solubility limit (about 5%) of sodium fluoride. By using solutions containing sodium hydroxide and sodium fluoride within these ranges of concentration. the desired ion exchange can be obtained at temperatures from about 50 to 250 F. with temperatures from about 150 to 250 F. being especially preferred. Operating pressure is not critical and need only be sufficient to insure a liquid phase. Operating pressures can range from about atmospheric pressure to about psig. The length of time required for the ion exchange will vary, depending upon the solution concentration and temperature, from about 0.5 to 5 hours. Within the above preferred concentrations and temperature ranges, a contact time which has been shown to be especially preferred is about 2 to 3 hours. Continuous or batch-type operations can be employed. The ion exchange step should be controlled so that the zeolite structure will not be destroyed and so that the final product will have a Nap/A1 0 ratio greater than about 0.7.  
  After the first ion exchange step the sodium exchanged particles are treated at second ion-exchange conditions to effect essentially complete exchange of the sodium cations with both barium and potassium cations in a weight ratio of from about 1.5 to 200 or with barium cations alone.  
  Second ion exchange conditions will include a temperature of from about 50 F to about 250F. and a pH sufficient to preclude the formation of the hydrogen form of the zeolite. The pH will therefore be greater than 7 and preferably within the range of 7 to l0. Operation pressure is not critical and need only be sufficient to insure a liquid phase. Operating pressures can range from about atmospheric pressure to about 150 psig. The length of time for the essentially complete exchange of the sodium cations will be from about 0.5 to about 5 hours depending upon the concentration of the cation in the ion exchange medium and the temperature. The term essentially complete exchange&#34; as used herein shall mean that the sodium cation content has been reduced to about 2.0 wt. 7: or less and more preferably to about 1 wt. 7( or less.  
  The preferred method of ion-exchange when the adsorbent contains both barium and potassium cations is a two-step procedure wherein the sodium-exchanged particles are intially treated in contact with an aqueous solution of a potassium salt. preferably an aqueous solution of potassium chloride, for a time sufficient to reduce the sodium cations to less than about 2 wt. of the zeolite and yield the potassium form of the zeolite. The exchange can be either a continuous or a batch type operation. The ion-exchange is suitably accomplished on passing a 7 wt. 7( aqueous potassium chloride solution through a bed of the sodium-exchanged particles at about 180 F. at a liquid hourly space velocity of about one until a total of approximately 13 pounds of solution per pound of said particles has been passed in contact therewith.  
  The potassium-exchanged particles can then be washed with water to remove excess ion exchange solution.  
  The washing medium will be water which has a pH adjusted to and maintained within the range of 7 to by adding small amounts of potassium hydroxide. Since the primary purpose of the sodium cation ion exchange was to remove hydrogen cation (and metal cation) contaminants, this pH range is necessary to avoid redepositing hydrogen cation on the adsorbent mass. Washing temperatures can include temperatures within the range of about 100 F. to about 200 F. with a temperature of about 100 F. to 145 F. preferred. Although the washing step can be done in a batch manner with one aliquot of wash water at a time, the washing step is generally and preferably done on a continuous flow type basis with water passed through a bed of the adsorbent at a given liquid hourly space velocity and a temperature for a period of time in order than from about 1 to about 5 gallons of water per pound of starting material is used to wash the material. Preferred washing conditions include using liquid hourly space velocities from about 0.5 to 5. with [.5 being preferred, to pass from about 1 to about 3 gallons of wash water per pound of starting material over the ion exchanged adsorbent.  
  The potassium-exchanged particles arethen treated in contact with an aqueous solution of a barium salt in the second step of the two-step ion-exchange procedure to achieve the desired weight ratio of barium to potassium on the finished adsorbent. Preferably an aqueous solution of from about 0.2 to about 5 wt. 7: barium chloride is recycled through the particle bed at about 180F, and at a liquid hourly space velocity of from about I to about 5 until the-desired degree of exchange has been achieved. After the barium-exchange step is completed, the water-washing step is repeated,  
 again maintaining a pH of 7 or greater in order to prevent or minimize the possibility of formation of the hydrogen form of the zeolite. A good indication of complete washing can be made by quantitatively testing the effluent wash water for the presence of the anion portion of the salt used in the ion exchange solution.  
  The above-mentioned two-step potassium and barium ion-exchange procedure is not necessarily limiting as it has been found possibly to employ a single step ion-exchange in which both barium and potassium are placed on the zeolite. However, the two-step procedure allows more precise control of the amount of cations placed on the zeolite.  
  When it is desired that the sodium cations be essentially completely exchanged with only barium cations then a procedure like that of the second step of the above described two-step procedure will be used alone to effect the exchange with barium cations. l have found that by the method of this invention a suitable adsorbent can be prepared without the potassium catlOnS.  
  When the wash step is completed the wet adsorbent particles will usually contain from about 30 to about 50 wt. 7: volatile matter (water) as measured by loss on ignition to 900 C. [n this specification, the volatile matter content of the zeolitic adsorbent is determined by the weight difference obtained before and after drying a sample of adsorbent in a high temperature furnace at 900 C. under an inert purge gas stream such as nitrogen for a period of time sufficient to achieve a constant weight. The difference in weight, calculated as a percentage of the sample&#39;s initial weight. is reported as loss on ignition (LOl) at 900 C. and represents the volatile matter present within the adsorbent. The remaining step in the method of manufacture then is the drying step to reduce the LO] at 900 C. to less than about 10 wt. 7: with the preferred LOl being about 3 to 7 wt. /1. After the washing has been completed, the particles can be unloaded and dried in a force air oven at temperatures above the boiling point of water but less than about 500 C. and preferably about C., for a period of time sufficient to remove enough water so that the volatile matter content of the zeolite is below about 10 wt. &#34;/1. Other methods of drying may be used which can include drying in the presence of an inert gas or under a vacuum. or both.  
  The anticipated use for the adsorbent prepared by the method of this invention is in various processes for the separation of the para isomer from a feed mixture comprising at least two-bialkyl substituted monocyclic aromatic isomers, including the paraisomer, said isomer having from 8 to about 18 carbon atoms per molecule. Specifically, our adsorbent is useful for separating the para-xylene from a feed mixture comprising paraxylene and at least one other C aromatic isomer.  
  -The particular usefulness of this adsorbent and general insight into its desirable characteristics may be better understood by brief reference to such aromatic isomers and separation processes. Specifically, the feed stocks which can be used in the process of this invention are characterized by the formula shown in Formula 3 below:  
 Formula 3 Wherein, R,, R R and R are selected from the group of alkyl chains in a manner to allow an essentially bialkyl substitution at either ortho-, meta-. or paraisomer positions. The R substitutional groups can inelude alkyl groups ranging from methyl substitution groups up to and including chains having 1 l or less carbon atoms per molecule. The alkyl side chains can be both normal and branched in nature and are preferably saturated chains.  
  Specific representative compounds which can be utilized as feedstocks in the process include those feedstocks containing the xylene isomers and ethylbenzene and the various isomers of methylethylbenzene. diethylbenzene. isopropyltoluene, the methylpropylbenzenes. ethylpropylbenzenes. methylbutylbenzenes. ethylbutylbenzene, dipropylbenzenes, methylpentylbenzene. etc.. and combinations thereof. The above list only represents a small fraction of compounds whose isomers can be separated by the specific adsorbent produced by the method of this invention.  
  The isomers of such compounds are separated by this adsorbent according to their configuration depending whether they are of a para-. metaor ortho-isomer construction. Specifically. the para isomer is selectively adsorbed relative to the other isomers. It is contemplated that with feed stocks containing mixtures of more than one class of isomers. for example. C isomers in mixture with C or C isomers. molecular weight differences will unduly interfere with selective adsorption based upon isomer configuration differences. It is therefore preferred that the process utilizing the adsorbent produced by the method of this invention to employ feed stocks comprising only a single class of aromatic isomers, that is, aromatic isomers having an equal number of carbon number per molecule. It is more preferable to use isomers having as their only differences the location of the alkyl substituted groups in a para-, metaor ortho-position. The alkyl structures should preferably be the same for each isomer of a class. In some instances an isomer may have alkyl chains which are both normal or branched or one branched and one normal.  
  The feed stocks may contain small quantities of straight or branched chain paraffins. cyclo-paraffins or olefinic material. It is preferable to have these quantities at a minimum amount in order to prevent contamination of products from this process by materials which are not selectively adsorbed or separated by the adsorbent. Preferably the above-mentioned contaminants should be less than about of the volume feed stock passed into the process.  
  To separate the para isomer contained in the feed mixture, the feed is contacted with a bed or beds of the structured zeolite adsorbent and the para isomer is selectively retained by the adsorbent while the unadsorbed or raffinate mixture which comprises the other isomers is removed from the interstitial void spaces between the particles or adsorbent and the surface of the adsorbent. The adsorbent is then contacted with a desorbent material which is capable of displacing the adsorbed para isomer from the adsorbent.  
  The adsorbent can be contained in a single chamber where through programmed flow into and out of the chamber separation of the para isomer is effected. A particularly preferred process to use the adsorbent of our invention employs the simulated moving-bed countercurrent operations similar to those disclosed in the pattern of operations in US. Pat. No. 2,985,589. The preferred process for separating the para isomer from a feed mixture containing at least two bi-alkyl substituted monocyclic aromatic isomers, including the paraisomer, said isomers having from 8 to about 18 carbon atoms per molecule would comprise the steps of: contacting the feed mixture with the adsorbent at adsorption conditions to effect the selective adsorption of para-isomer by the adsorbent. withdrawing from the bed of adsorbent a rafflnate stream comprising less selectively adsorbed aromatic isomers, contacting the adsorbent with a desorbent material at desorption conditions to effect desorption of para isomer from the adsorbent. and withdrawing a stream containing the para isomer and desorbent from the adsorbent.  
  Preferred operating conditions for both adsorption and desorption of this particular process include a temperature within the range of from about F. to about 450 F. and a pressure within the range of from about atmospheric to about 500 psig. Furthermore. both adsorption and desorption of the para isomer are affected at conditions selected to maintain liquid phase throughout the bed of adsorbent.  
  The adsorbent produced by the method of this invention may, of course, be used in other selective adsorption processes for separating aromatic isomers. These might include, for instance, swing-bed or moving-bed processes. Adsorption and desorption in such proceses may both be conducted in the vapor phase or liquid phase or one operation may be conducted in the vapor phase and the other in the liquid phase. Operating pressures and temperatures for adsorption and desorption might be the same or different.  
 The desorbents which can be used in the processes .employing this adsorbent will vary depending on the generally operated at substantially constant pressures and temperatures, the desorbent relied upon must be judiciously selected in order that it may displace the adsorbed isomer from the adsorbent without unduly preventing the adsorbed isomer from displacing the desorbent in a following adsorption cycle.  
  Desorbents which can be used in the process of this invention should also be materials that are easily separable from the feed mixture that is passed into the process. In desorbing the preferentially adsorbed component of the feed both desorbent and the desorbed feed component are removed from the adsorbent in admixture. Without a method of separation in these two materials, the purity of the selectively adsorbed component of the feed stock would not be very high since it would be diluted with&#39;desorbent. It is contemplated that a desorbent having a&#39;different boiling range than the feed mixture used should be used in this process. The use of a desorbent of a different boiling range allows a simple separation by fractionation or other methods to remove desired feed components from the desorbent and allow reuse of the desorbent in the process. Specific desorbents which can be used in the process of this invention include benzene, toluene. esters. alcohols. cyclic dienes. the ketones or a feed component material which has a significantly different boiling range than a boiling range of the feed stock used. It is contemplated that desorbents having both higher and lower boiling points in the feed stock can be utilized. Gaseous materials such as nitrogen, hydrogen. methane. ethane. etc.. can also be used as a desorbent materials where the desorbent operation takes place by a purging step.  
  With the type of processes employing adsorbent to separate aromatic isomers now in mind, one can appreciate that certain characteristics of adsorbents are highly desirable. if not absolutely necessary, to the successful operation of the selective adsorptive process. Among such characteristics are: adsorptive capacity for some volume of the para isomer per volume of adsorbent; adsorption for the para isomer with respect to the other aromatic isomers and the desorbent; and sufficiently fast rates of adsorption and desorption of the para isomer to and from the adsorbent. Low or no initial dustiness of the adsorbent and attrition resistance are equally important to avoid possible pressure drop problems after the adsorbent has been loaded.  
  Capacity of the adsorbent for adsorbing a specific volume of para isomer is of course a necessity; without such capacity the adsorbent is useless for adsorptive separation. Furthermore. the higher the adsorbents capacity for the species to be adsorbed. the better is the adsorbent. The increased aromatic capacity of the particular adsorbent produced by the method of this invention makes it possible to reduce the amount of adsorbent needed to separate the desired species contained in a particular rate of hydrocarbon feed mixture. A reduction in the amount of adsorbent required for a specific adsorptive separation reduces the cost of the separation process. It is, of course, important that the good initial capacity of the adsorbent be maintained during actual use in the separation process over some economically desirable life.  
  The other important adsorbent characteristic is the ability of the adsorbent to separate components of the feed; or. in other words. the selectivity (B), of the adsorbent for one component as compared to another component. Selectivity can be expressed not only for the desired aromatic isomer (para isomer) as compared to undesired isomers but can also be expressed between any feed stream isomer and the desorbent. The selectivity (B) as used throughout this specification is defined as the ratio of the two components of the adsorbed phase over the ratio of the same two components in the unadsorbed phase at equilibrium conditions.  
 Selectivity is shown as Equation 1 below:  
 Equation 1 [voLpercent C/vol. percent DIA where C and D are two components of the feed represented in volume percent and the subscripts A and U represent the adsorbed and unadsorbed phases respectively. The equilibrium conditions as defined here were determined when the feed passing over a bed of adsorbent did not change composition after contacting the bed of adsorbent. In other words. there was no net transfer of material occurring between the unadsorbed and adsorbed phases.  
  As can be seen where the selectivity of two components approaches l.0 there is no preferential adsorption of one component by the adsorbent. As the (B) becomes less than or greater than 1.0 there is a preferential selectivity by the adsorbent of one component. When comparing the selectivity by the adsorbent of one component C over component D, a (B) larger than 1.0 indicates preferential adsorption of component C within the adsorbent. A (B) less than 1.0 would indicate that component D is preferentially adsorbed leaving an unadsorbed phase richer in component C and an adsorbed phase richer in component D. Desorbents ideally would have a selectivity equal to about 1 or slightly less than I.  
  The third important characteristic is the rate of exchange of the adsorbed para-isomer with the desorbentor. in other words. the relative rate of desorption of the para-isomer. This characteristic relates directly to the amount of desorbent that must be employed in the process to recover the adsorbed isomer from the adsorbent. The adsorbent produced by the method of this invention not only has higher aromatic capacity and good selectivity but has faster transfer rates.  
  The remaining important characteristic. not only for adsorbents but for catalysts as well. is low initial dustiness. This characteristic must of course be coupled with sufficient particle mechanical strength to resist subsequent dust formation during process usage. Such dust. whether present initially or developed later. may migrate within the adsorbent chamber or reaction vessel during process use to form flow restrictions from which excessive pressure drops can result. Such pressure drops grind up adsorbent or catalyst present in the chamber or vessel and can exceed equipment mechanical limitations thereby forcing premature process shutdowns. We have discovered that the dustiness characteristic of adsorbents can be eliminated by a fluoride treatment step in the manufacture of such adsorbents. We would expect that such a step could be incorporated in catalyst manufacturing procedures as well as to eliminate the dustiness characteristic of any such catalyst.  
  In order to test various adsorbents to measure the characteristics of adsorptive capacity. selectivity. and the rate of desorption, a dynamic testing apparatus is employed. The apparatus consists of an adsorbent chamber of approximately cc volume having inlet and outlet portions at opposite ends of the chamber. The chamber is contained within a temperature control means and, in addition. pressure control equipment is used to operate the chamber at a constant predetermined pressure. Attached to the outlet line of the chamber is chromatographic analysis equipment used to analyze the effluent stream leaving the adsorbent chamber.  
  A pulse test. performed using this apparatus and the following general procedure. is used to determine selectivities and other data for various adsorbent systems. The adsorbent was filled to equilibrium with a particular desorbent by passing the desorbent through the adsorbent chamber. At a convenient time. a pulse of feed containing known concentrations of a nonadsorbed paraffmic tracer (n-nonane) and of aromatic isomers all diluted in desorbent is injected for a duration of several minutes. Desorbent flow is resumed, and the tracer and the aromatic isomers are eluted as in a liquid-solid chromatographic operation. The effluent is analyzed by on-stream chromatographic equipment and traces of the envelopes of corresponding component peaks are developed.  
  From information derived from the chromatographic traces adsorbent performance can be rated in terms of capacity index for the para isomer. selectivity for the para isomer with respect to the other isomers and rate of desorption of the para isomer by the desorbent. The capacity index is characterized by the distance between the center of the para isomer peak envelope and the C 7 tracer peak envelope. It is expressed in terms of the volume in cubic centimeters of desorbent pumped during this time interval. Selectivity. (B). for paraisomer with respect to the other isomers (p/m. p/o) is characterized by the ratio of the distance between the center of the para isomer peak envelope and the C tracer peak envelope to the corresponding distances for the other isomers. The transfer rates are. we have found. best characterized by the widths of the tracer peak envelopes at half intensity. The narrower the peak widths the faster the transfer rates.  
  In addition to the para isomer retention volume derived from the pulse test total aromatic capacity is also obtained by measuring the volume of a particular para isomer adsorbed per 70 cc of adsorbent. In this test the adsorbent is first loaded to equilibrium with a feed blend of known concentrations of aromatic isomers and a tracer component. These are then displaced with a desorbent containing a different para isomer than that of the feed. The amount of the latter para isomer adsorbed is termed the total aromatic capacity.  
  A comparison of the dust content in adsorbents can be made by simply pouring 10 ml. of the adsorbent into ml. of methanol contained in a 25 X 95 mm 8 dram vial and mixing the contents. The dust will be dispersed in the alcohol and the degree of opacity will serve as an index of the dust content.  
  To translate pulse test data and total aromatic capacity data into a practical aromatic separation process requires actual testing of the best system in a continuous countercurrent liquidsolid contacting device.  
  The general operating principles of such a devise have been previously described and are found in Broughton U.S. Pat. No. 2,985,589 and a specific laboratory-size apparatus utilizing these principles is described in deRoset. et al., U.S. Pat. No. 3,706,812. The equipment comprises multiple adsorbent beds with a number of access lines attached to distributors within the beds and terminating at a rotary distributing valve. At a given valve position, feed and desorbent are being introduced through two of the lines and raffinate and extract are withdrawn through two more. All remaining access lines are inactive and when the position of the distributing valve is advanced by one index all active positions will be advanced by one bed. This simulates a condition in which the adsorbent physically moves in a direction countercurrent to the liquid flow. Additional details on adsorbent testing and evaluation may be found in the paper Separation of C, Aromatics by Adsorption&#34; by A. J. deRosset, R. W. Neuzil, A. J. Korous and D. H. Rosback presented at the American Chemical Society, Los Angeles. Calif. Mar. 28-Apr. 2,  
  The superior performance of the adsorbents prepared by the method of this invention which was indicated by the pulse test was confirmed by continuous testing in this device.  
 EXAMPLE In this example four adsorbents were prepared from the same base material and tested to illustrate the desired properties achieved by the method of this invention.  
  The four adsorbents were prepared from base material comprising commercially available 13X zeolite in the form of nominal l/16 X /za-inch extrudate. This base material was ground to produce 20-40 U.S. Standard Mesh particle size material and divided into four portions from which four adsorbents were prepared.  
  One portion was simply barium exchanged to produce Adsorbent A. A 190 cc portion of the base material was treated upflow with 28 liters of 0.015 BaCl. ,-2- H O solution at C. and 1.8 liquid hourly space velocity (LHSV). The material was then washed at 70 C. with 2 liters of water over a 2.5 hour period.  
  A second portion was treated with a solution of NaF only and then barium exchanged to produce Adsorbent B. A 300 cc portion of the base material was batch treated for 3.5 hours at 90 C. with 30 g. NaF dissolved in 600 ml. of deionized water. The material was decantwashed and then barium exchanged in the manner of Adsorbent A.  
  A third portion was treated with a solution containing both NaF and NaOH and then barium exchanged to produce Adsorbent C. A 200 cc portion of the base material was batch treated for 2 hours at 90 C. with a solution of 25 g. NaF and 20 g. NaOH dissolved in 500 ml. of deionized water. The material was batch washed at -85 C. for /2 hour periods with eight 250 ml. portions of deionized water and then barium exchanged in the manner described above.  
  The fourth portion of ground base material was treated with a solution of NaOH only and then barium exchanged to produce Adsorbent D. A 200 ml. portion of the base material was batch treated for 2 hours at C. with a solution of 20 g. NaOH dissolved in 500 ml. of deionized water. The material was batch washed with water and then barium exchanged.  
  All four adsorbents were dried for 16 hours at 185 C. with perfluent N and then rehydrated to 4 wt. 7: water prior to being tested for performance by the pulse test previously described.  
  The testing apparatus was maintained at a controlled temperature of C. with sufficient pressure to ensure liquid phase operations. A desorbent of 30 vol. 7: para-diethylbenzene and 70 vol. 7c n-heptane was run through the apparatus at a rate of 1.5 cc per minute. At a convenient time interval the desorbent was stopped and a feed pulse consisting of 5 vol. 7: para-xylene, metaxylene. ortho-xylene, ethyl benzene, and n-nonane as a tracer and 75 vol. 7: desorbent was charged to the adsorbent chamber for a ten-minute interval at 1 LHSV.  
  From the chromatographic tracers of the envelopes of component peaks. peak envelope widths. paraxylene capacity. and selectivities were determined.  
  The amount of para-diethylbenzene adsorbed was determined by loading the adsorbent to equilibrium with a feed pulse consisting of 24 vol. 7! each of the C aromatics and 4 vol. 7: n-nonane tracer and then charging the desorbent of 30 vol. &#34;/1 para-diethylbenzene and 70 vol. n-heptane to the adsorbent chamber. The amount of para-diethylbenzene adsorbed was then calculated from the breakthrough front of paradiethylbenzene measured from the disappearance of the tracer.  
  Dust condition of the four adsorbents was&#39;determined by the degree of opacity resulting from the simple methanol test previously described.  
  The results of the testing for the four adsorbents are shown in table l below.  
 c. drying the thus exchanged base material at conditions to reduce the L01 at 900C. to less than about 2. The method of claim 1 further characterized in that said base material has a Na O/Al O ratio of about 0.7 or less.  
  3. The method of claim 1 further characterized in thatsaid solution contains sodium fluoride in a concentration of less than its solubility limit and sodium hydroxide in a concentration of from about 0.5 to about 4. The method of claim 1 further characterized in that said first ion exchange conditions include a temperature within the range of from about 50 F. to about 250 F.  
  5. The method of claim 1 further characterized in that said sodium exchanged base material has a M 0- /Al O., ratio greater than about 0.7.  
 Table 1 Pulse Test and Capacity Data for Adsorbents Adsorbent A B C D Treatment none NaF NaF/NaOH NaOH Wt. &#34;/1 BaO 30.4 31.4 35.6 32.6 Wt. Na 1.40 1.74 1.02 1.05 Peak Envelope Widths. cc. for:  
 n-nonane 14.5 10.1 9.9 11.5  
 ethylbcnzene (EB) 20.4 15.4 15.0 19.2  
 para-xylene (P) 22.1 13.9 13.2 18.7  
 meta-xylene (M) 16.8 13.2 13.5 15.7  
  ortho-xylene (O) 16.8 12.6 13.5 15.5 Para-xylene retention volume. cc. 19.6 23.0 23.5 24.8 selectivities P/EB 1.71 1.68 1.73 1.91  
  P/O 2.81 3.27 3.19 4.42 Para-dicthylbenzene capacity. cc.  
  per 70 cc adsorbent 6.38 8.00 9.75 9.15 Dust Condition dusty no dust no dust dusty The higher para-diethylbenzene capacities for Adsorbents C and D indicate that both NaOH/NaF or NaOH treatments confer high total aromatics capacity. The narrowest peak envelope widths for Adsorbent C indicates that the NaOH/NaF treatment confers the fastest para-xylene transfer rates. The table also shows that the best selectivities were obtained with the NaOH treatment alone (Adsorbent D) with next best selectivities obtained with the NaOH/NaF treatment (Adsorbent C). Additionally the table shows that NaF treatment with or without NaOH treatment eliminates dusting (Adsorbents B and C).  
  The combination of NaOH and NaF treatment renders an adsorbent having the best combination of performance characteristics. This combination is not attainable by either treatment alone and is certainly superior to those of an adsorbent made with neither treatment.  
 1 claim as my invention:  
  1. A method of manufacturing a solid adsorbent comprising the steps of:  
 a. contacting a base material comprising X or Y zeolite with a fluoride-containing aqueous solution of sodium hydroxide at first ion exchange conditions to effect the addition of sodium cations to and the extraction of alumina from said base material;  
 b. treating the sodium-exchanged base material at second ion exchange conditions to effect the essentially complete exchange of sodium cations with barium or barium and potassium cations; and.  
  6. The method of claim 1 further characterized in that said second ion exchange conditions include a pH sufficient to preculde formation of the hydrogen form of the zeolite. and a temperature within the range of from about F. to about 250 F.  
  7. The method of claim 1 further characterized in that said sodium-exchanged base material is essentially completely exchanged with barium and potassium cations.  
 8. The method of claim 7 further characterized in that the weight ratio of barium over potassium cations is from about 1.5 to 200.  
  9. The method of claim 1 further characterized in that said sodium-exchanged base material is essentially completely exchanged with barium cations.  
  10. A method of manufacturing a solid adsorbent which comprises the steps of:  
 a. contacting a base material comprising a X or Y structured zeolite having a Nap/A1 0 ratio of about 0.7 or less with a fluoride-containing aqueous sodium hydroxide solution at first ion exchange conditions to increase the sodium cation content of said mass to a Nap/A1 0 ratio of greater than about 0.7 and extract less than about 5% of the alumina from said base material;  
 b. treating the sodium-exchanged base material at second ion exchange conditions, including a pH sufficient to preclude the formation of the hydrogen form of the zeolite and a temperature within the range of from about 50F. to about 250F., to effect the essentially complete exchange of sodium cations with barium or barium and potassium cations; and.  
 c. drying the thus re-exchanged base material at conditions sufficient to reduce the LO] at 900C. to less than about lOwtf/r.  
  11. The method of claim 10 further characterized in that said solution contains sodium fluoride in a concentration less than its solubility limit and sodium-hydroxide in a concentration of from about 0.5 to about 10 wt. 7?.  
  12. The method of claim 10 further characterized in that said sodium-exchanged base material is essentially completely exchanged with barium and potassium cations in a weight ratio of from about 1.5 to 200.  
 13. The method of claim 10 further characterized in reduce the 1.01 at 900C. to less than about 10 wt. 7?.