Photocurable polyene-polythiol compositions containing the adduct of diallylmalate and toluene diisocyanate
United States Patent 11 1 Guthrie et al.  
 [ PHOTOCURABLE POLYENE-POLYTHIOL COMPOSITIONS CONTAINING THE ADDUCT OF DIALLYLMALATE AND TOLUENE DIISOCYANATE [75] Inventors: James L. Guthrie, Ashton; Francis J. Rendulic, Ellicott City, both of Md.  
 [73] Assignee: W. R. Grace and C0., New York,  
 [22] Filed: Aug. 14, 1974 [21] Appl. N0.: 497,427  
  Related US. Application Data [60] Division of Ser. No. 409,615, Oct. 25, 1973, which is a continuation-in-part of Ser. No. 209,369, Dec. 17, 1971, Pat. No. 3,787,303.  
  M; 260/368 XA; 260/31.8 Z; 260/332 R; 260/4595; 260/75 s; 260/75 UA; 260/829;  
  260/837 R; 260/861; 260/862; 260/865; 260/873 51 1111. c1 ..B41j1/10;B05c 5/00; BOlj 1/12; 801] 1/10 [58] Field ofSearch..... 204/159515, 159.14, 159.18, 204 159.19; 260/861, 862, 873, 79.5 R, 79,  
 75 s, 75 UA; 117/9331 [56] References Cited UNITED STATES PATENTS 3,625,925 12/1971 Oswald et al. 204/l59.l8  
 1451 Apr. 15, 1975 Primary Examiner-Murray Tillman Assistant ExaminerRichard B. Turer Attorney, Agent, or FirmCharles L. Harness [57] ABSTRACT The invention disclosed is directed to a methodfor overcoating which includes applying to a substrate a novel photocurable lacquer composition having as essential ingredients a polyene selected from a particular group of polyenes which contain at least 2 reactive unsaturated carbon-to-carbon bonds per molecule, a polythiol containing 2 or more thiol groups per molecule and a resin component; and thereafter exposing the applied composition to actinic radiation for a period of time sufficient to photocure the applied composition to provide an overcoating. Optionally, a sensitizer may be included if desired to decrease curing time and improve efficiency. The method is particularly useful for high speed overcoating printed metal articles such as cans. Overcoatings thus provided are found to be characterized by high strength, good scratch resistance, freedom from tackiness and excellent transparency.  
 6 Claims, No Drawings PHOTOCURABLE EPOLYENEPOLYTHKOL COMPOSKTTONS CONTAINHNG THE ADDUCT OF DHALLYLMALATE AND TOLUENE DllllSOCYANATE This application for U8. Letters Patent is a division of Ser. No. 409,615, filed Oct. 25, 1973, which in turn is a continuation-in-part of Ser. No. 209,369, filed Dec 17, 1971, now US. Pat. No. 3,787,303.  
  The present invention relates to a photocurable lacquer composition which includes a polyene component containing at least two unsaturated carbon-towarbon bonds per molecule, a polythiol component containing on the average at least two -SH functional groups per molecule, and a resin component. The invention also provides a method for overcoating articles wherein an applied coating of the composition is cured by means of actinic radiation to produce a protective coating which is typically clear, tough and durable.  
  It is well known in the art that protective functional overlaye rs of transparent synthetic organic coating materials may be formed on various substrates. Typically, the prior art coating materials have been baked at high temperatures to form coatings on substrates, printed and non-printed. Many prior art coating materials contain various harmful solvents which are released as vapors upon baking. Not only do the released vapors present pollution problems, but also baking is costly and time consuming. Further. use of high bake temperatues often results in discoloration of inks or pigments disposed on the articles being coated. Generally, use of lower bake temperatures further slows the prior art lacquering processes, while use of higher temperatures further limits the types ofinks which may be satisfactorily applied prior to applying protective overcoatings. In preparing printed cartons from printed paperboard, it is conventional to apply overcoatings such as heatcurable lacquers and press varnishes which, in practice, generally have required in process dusting with starch powders or the like and extended aging prior to making cartons from the overcoated sheets. For a broad description of the art, the reader is referred to US. Pat. Nos. 3,625,925 (Oswald, et a1), 3.656999 (Lundsager), 3,661,744 and 3,662,023 (Kehr, et al,).  
  The above-cited application, U.S. Ser. No. 209,369, discloses an invention whereby printed or non-printed articles may be overlayered with a transparent protective coating in rapid, simple and efficient manner without requiring high temperatures or evolution of solvent vapor. Numerous defects of prior art overcoating compositions and methods may be effectively overcome by the invention which provides a clear coating composition and method for overcoating using actinic radiation to cure an applied coating of the composition. Upon exposure to actinic radiation, the composition cures rapidly to a typically clear coating which has good lubricity, withstands abrasion, exhibits high gloss, effectively adheres to a variety of substrates, and is substan tially odorless. The method is especially useful for highspeed coating on metal substrates such as metal sheets, printed and non-printed, from which articles such as cans are formed. Upon curing, the composition effectively adheres to both the metal and to intermediate layers such as inks and the like which typically are disposed on the metal in the metal decorating field. Other printed substrates which may be coated using the method include magazine-quality paper and paperboard. Typically, printed paperboard may be coated using the method and thereafter passed to carton finishing operations without requiring aging and without need for dusting.  
  Generally stated, the present invention provides a method of overcoating which includes applying to a substrate a photocurable lacquer composition having (a) a polythiol component containing at least two -SH groups per molecule, (b) a polyene component selected from particular polyenes (subsequently set forth herein) which contain 2 or more terminally positioned unsaturated carbon-to-carbon bonds per molecule. contain at least one of the following: N, O, and six membered carbon containing ring, and are characterized in that they will react with the polythiol to form tough and durable coatings, and (c) a resin component. Optionally, a sensitizer component may be included if desired to decrease curing time and improve efficiency. Curing of the applied composition is effected by exposure to a free radical generator such as actinic radiation to form, typically, clear, tough, durable polythioether coatings.  
  Polyenes containing at least one of N, O, and six member carbon containing ring which are useful herein include triallyl isocyanurate; Bisphenol A diallyl ether; the diadduct of diallyl amine and Bisphenol A 4,4- diglycidyl ether; the urethane diadduct of a member selected from the ene-ol group consisting of ally alcohol, diallyl malate, and trimethylolpropane diallyl ether and a member. selected from the cyclic C containing diisocyanate group consisting of toluene diisocyanate, 3,3- dimethyl-4,4-biphenylene diisocyanate, 3- isocyanatomethyl-3,5,5-trimethylcyclohexyl isocyanate, 4,4-methylenebis-(cyclohexyl isocyanate), and Solithane 291 (trademark for a polyester isocyanate product by Thiokol having molecular weight of about 2,800 and prepared by reacting ethylene glycol, propylene glycol, adipic acid and toluene diisocyanate). The various polyenes may be obtained commercially or may be readily prepared from commercially available reactants. Methods exemplifying preparation of these polyenes are set forth subsequently in the examples included in this description. Preferred polyenes are triallyl isocyanurate, Bisphenol A diallyl ether and the diadduct of toluene diisocyanate and diallyl malate.  
  It has now been found that 2,4,6-tris(allyloxy)striazine is an excellent polyene component which is now included among the preferred polyenes.  
  The polythiol component has a molecular weight in the range from about to about 20,000 and the general formula:  
 wherein R represents a polyvalent organic moiety free from reactive carbon-to-carbon unsaturation and B is a numeral of at least 2. Thus, R may contain cyclic groupings and hetero atoms such as N, P, or O and primarily contains carbon-to-carbon, carbon-hydrogen, carbon-oxygen or silicon-oxygen containing chain linkages free of any reactive carbon-to-carbon unsaturation. The ene/thiol mole ratio is selected so as to provide a solid, self-supporting cured product under ambient conditions in the presence of a free radical generator.  
  The polythiol may be a simple or complex organic compound having a multiplicity of pendant or termipersion or plasticizer. Operable polythiols usually have molecular weights in the range about 100 to about 20,000, and preferably from about 200 to about 10,000.  
  One class of polythiols curable with polyenes to obtain essentially odorless polythioether products are esters of thiol-containing acids of the formula HS-R COOH where R is an organic moiety containing no reactive carbon-to-carbon unsaturation with polyhydroxy compounds of structure R -OH),, where R, is an organic moiety containing no reactive carbon-to-carbon unsaturation, and n is 2 or greater. These components will react under suitable conditions to give a polythiol having the general structure:  
 R (Dea -stu where R and R are organic moieties containing no reactive carbon-to-carbon unsaturation, and n is 2 or greater.  
  Certain polythiols such as the aliphatic monomeric polythiols exemplified by ethane dithiol, hexamethylene dithiol, decamethylene dithiol, tolylene-2,4-dithiol, and the like, and some polymeric polythiols such as a thiol-terminated ethylcyclohexyl dimercaptan polymer, and the like, and similar polythiols which are conveniently and ordinarily synthesized on a commercial basis, although having obnoxious odors, are operable but many of the end products may not be widely accepted from a practical, commercial point of view.  
  The preferred polythiol compounds are characterized by a low level or mercaptan-like odor initially, and after reaction, give essentially odorless polythioether coatings which are commercially attractive and practically useful for both indoor and outdoor applications.  
  Examples of the polythiol compounds preferred because of relatively low odor level include but are not limited to esters of thioglycolic acid (HS-CH- COOH), 2-mercaptopropionic acid (HS-CH(CH- 3 )COOH) and 3 -mercaptopropionic acid (HSCH CH COOH) with polyhydroxy compounds such as glycols, triols, tetraols, pentaols, hexaols, and the like. Specific examples of the preferred polythiols include but are not limited to ethylene glycol bis (thioglycolate), ethylene glycol bis (3-mercaptopropionate), trimethylolpropane tris (thioglycolate), trimethylolpropane tris (3-mercaptopropionate), pentaerythritol tetrakis (thioglycolate), pentaerythritol tetrakis (3-mercaptopropionate), all of which are commercially available, and pentaerythritol tris (3-mercaptopropyl ether), which may be prepared as set forth in the examples infra. A specific example of a preferred polymeric polythiol is polypropylene ether glycol bis (3-mercaptopropionate) which is prepared from polypropyleneether glycol (e.g, Pluracol P2010, Wyandotte Chemical Corp.) and 3-mercaptopropionic acid by esterification.  
  Resins useful herein include normally solid, solvent soluble linear or branched polyesters, preferably linear,  
 having molecular weight from about 500 to about 100,000 and preferably from about 1000 to about 50,000 which may be prepared by reacting a polybasic acid or a polybasic acid anhydride having the following general formulas I and II. respectively:  
  0 l oo a on a o z on) tR +--+can r 2 with a polyhydric alcohol having the general formula [R -OH),,. In the formulas, x and y are numerals of 2 or more and preferably 2 to 4, and R and R are saturated or unsaturated hydrocarbyl or oxyhydrocarbyl groups having valence of x and y respectively and which may have from 2 to about 21 and from 2 to about 30 carbon atoms respectively. and preferably from 2 to about 10 and from 2 to about 8 carbon atoms respectively; z is 0 or I; Z is a saturated or unsaturated hydrocarbyl group having a valence of 2 when z is 0, a va lence of 3 when z is l, and from about 2 to about 12 carbon atoms and preferably from 2 to about 6 carbon atoms. Typically, the reaction is carried out using about one equivalent weight of 01 functionality per one equivalent weight of acid functionality.  
  The polybasic acid or anhydride reactant may be, for example, phthalic acid or phthalic anhydride, maleic acid or maleic anhydride, adipic acid, trimellitic acid or trimellitic anhydride, succinic acid or succinic anhydride, fumaric acid, terephthalic acid, itaconic acid, glutaric acid, isophthalic acid, the tribasic Diels-Alder adduct of levopimaric acid with maleic acid, 1,4,5,8- naphtha]enetetracarboxylic acid, and mixtures thereof.  
 The polyhydric alcohol reactant may be, for exam- 1 ple, ethylene glycol, diethylene glycol, polyethylene glycol, propylene glycol, dipropylene glycol, polypropylene glycol, 1,3-propanediol, 1,4-butanediol, neopentyl glycol, pentaerythritol (a tetraol), glycerol, trimethylolpropane (a triol), Bisphenol A (4,4- isopropylidenediphenol), and 1,4-dihydroxymethylbenzene.  
  Resins preferred herein are solvent-soluble normally solid polyester products prepared by esterifying saturated or unsaturated C to about C hydrocarbyl or exyhydrocarbyl diols, triols, tetraols or mixtures thereof with one or more dibasic, and tetrabasic saturated or unsaturated C to about C hydrocarbyl carboxylic acids, their anhydrides and mixtures thereof. The acid or anhydride reactants useful in preparing such resins include phthalate ester forming acids of anhydrides, i.e., phthalic acid, phthalic anhydride, isophthalic acid, terephthalic acid, trimellitic acid, trimellitic anhydride or mixtures thereof in amounts constituting a percentage of the total acid and/or acid anhydride reactants effective for aiding in providing overcoatings characterized by high strength. good scratch resistance and substantial freedom from tackiness. Polyesters prepared from acid or anhydride reactants comprising from about 5 to parts by weight of phthalate ester forming acids, acid anhydrides or mixtures thereof per 100 parts by weight of the total hydrocarbyl acid or anhydride reactants are found suitable. Preferably phthalate ester forming acids, acid anhydrides or mixtures RRR thereof are included in an amount from about 50 to (b) -o gag, 100 arts b wei ht. h  
  P y g R Another especially effective phthalate containing polyester may be prepared by reacting phthalic acid or 5 R R phthalic anhydride, maleic acid or maleic anhydride, (c) adipic acid, and diethylene glycol using mole ratios of the reactants in the order given of about 3: l 1 :5 to prov vide about 1 equivalent weight of acid or anhydride f T functionality per about I equivalent weight 01 function- 10 ality. The above molar ratio, corresponding to about 65 R parts by weight of phthalic anhydride per 100 parts by (e) {L weight total hydrocarbyl acid, may be varied to provide residual acid, anhydride or 01 functionality for subse- R quent capping of the resin as described subsequently n R p R herein. I Ll.  
  Other soluble resins which are useful herein are m c Diii R polyester-polyenes which may be prepared by capping R the polyester resins described hereinabove with a member having the general formula III which follows:  
  0 where q is 0 or an integer from 1 to 9 and preferably a H 0 or 1; h is 0 or 1; and the various R members are radi- (nn [no I Ran-Q7); cals which may be selected from the group consisting of hydrogen, fluorine, chlorine, furyl, thienyl, pyridyl, wherein 6 is a hydrocarbyi member free of remotely phenyl and substituted phenyl, benzyl and substituted internal non-aromatic ene and yne functionality and b l, alkyl and b tituted alkyl, alkoxy and substihaving a valence of q plus s and from about 2 to about tuted alkoxy, and cycloalkyl and substituted cycloalkyl, 10 and preferably from about 2 to about 7 carbon where the substituents on the substituted members are a m p i or 1; q is anumerai f m 1 t0 1 n pr fselected from the group consisting of nitro, chloro, erably 1 to about 2; r is O or 1; s is a numeral from i fluoro, c ro id phenyl, benzyl, alkyl, to 10 and preferably 1 to about 2. Typically, where p oxy and cycloalkyl. Alkyl and alkoxy have from 1 to 9 iS 0, t u 0f numerals y in the formuia I 5- )U carbon atoms and cycloalkyl has from 3 to 8 carbon supra and q are approximately equal to (a) x in the fOratoms. Preferably, R is selected from the group consistmula I supra where the polyesters are prepared from a ing of hydrogen and methyl. Poiybasic acid of 2 P Z in the formula ii Supra Useful capping agents include, for example, allyl alwhere the polye ter are prep r f m a p lyba ie coho], trimethylolpropane diallyl ether, diallyl malate, a d an y and Where P is q is approximately the diallyl tartrate, 2-vinyloxyethanol, vinyl hydroxyethyl number required for y to equal (C) th Sum q P X sulfide, IO-undecylenyl alcohol, allyl maleate, ally] where the polyesters are prepared from a polybasic phthal t diallyl trim llitate, N-methyl-N- acid or (cl) the sum of q plus 2 plus 2 where the polyesvinylethanolamine, 4-vinyloxybenzyl alcohol, and ters are prepared from a polybasic anhydride. Alternaacrylic acid. The capping agents may be obtained comtively stated, the number of ester-forming 01 groups is mercially or readily prepared from commercially availtypically app x y equal to the number of esierable reactants using well known methods. In order that forming carbonyl groups in the preparation of he the use of formula III in selecting capping agents will be capped polyesters. As used in the description supra remore f ll apparent, h capping agents Set f h bo garding the formula III and in the claims which follow, are l ifi d i h bl b l polyeste upolyenes the term remotely internal means disposed more preferred herein are the reaction products prepared by then 8 Carbon atoms capping the preferred polyester resins with one or more 0 of the useful capping agents set forth supra. The polyester-polyene resin has a molecular weight firm the &#39;P&#39; in the range from about 100 to 20,000, preferably moiety. about 200 to about 10,000, and a viscosity in the range In the above formula III, R may be selected from the from essentially O to 20 million centipoises at C as group consisting of: measured by a Brookfield viscometer. The polyesterpolyene is characterized by having at least two unsatufi 5 rated carbon-to-carbon bonds disposed at terminal or (a) V near terminal positions on a main chain of the molecu- R lar or pendant therefrom.  
  5 7 .5. .L .i r .i. use Allyl alums/T. CH =CiI-CH (a) n 0 1 s 1 1 (a) Acrylic acld CH2=CH- H I l 0 l 0 Table Continued Cagginc: M7351; R R (a) R E g g r s h 1C-m-1dczt rlozie :lconc-l CZ-l =CiI (CH 0 H 0 l 0 l 9 (a) 4vir-.yloxybcnzyl alcciol O -CH CXI =CH Fl 0 l l l 0 (h) I-vfgqioxyethaaol -CH -CH CH =C(=&#39;- )O H O l l l 0 Trimothyloloropane H C-CH ctcn :7:;c;-&#39;.--o- H 0 1 l 2 l 3 Z 2 3 mallyl ether (cl Vinyl hydroxyethyl sulfide CH -CH Crl =C r-S H 0 1 1 1 (91, (d) 1 N-methyl-N-vinyl- CH CH CEI =Crt-:i- H on 0&#39;5 0 1 l 1 ethanolamine CH on N O (f) I Allyl maleate -CH=CR- QE2=CH-CHZ-Q-C H 1 1 l l l I Allyl phthalate c =c -ctq -0-c- H l l 1 l 1 9 niallyl trimellitate cn =cn-c:: -o-cn 1 1 1 2 l Diallyl malate -CH LH- CH =Cli-ClI -OC- H &#39;O 1 1 2 l t u mallyl artrate C!I {3H cg t. z n a 1 a a It is found that the polyester-polyene resin is cocurable, i.e., upon exposing the lacquer to a free radical generator such as actinic radiation the polyesterpolyene reacts with a portion of the polythiol in the manner generally analogous to the polyene component to form polythioether linkages. Advantageously, however, the polyester-polyenes generally minimize the amount of polythiol necessary to effect curing of the lacquer composition to solid durable overcoatings.  
  The polyester-polyenes are disclosed in copending Guthrie application, Curable Liquid Pigment Composition and Method, Ser. No. 188,608, filed Oct. 12, 1971, assigned to the same assignee hereof and incor porated herein in pertinent part by reference.  
  Other resins which may be included in the present lacquer composition include, for example, carbohydrates, preferably sucrose octa-acetate and sucrose acetate-butyrate. Still other resins useful herein include, for example, polyvinyl acetate, polyvinyl alcohol, polystyrene, esters of abietic acid, polymers of a-or B-pinene, indenecoumarone copolymers, and the like.  
  Other resins which may usefully be included in the lacquer composition are liquid plasticizers such as polyethylene glycol having molecular weight of up to about 400. dioctyl phosphate, dibutyl phthalate and the like.  
  The resin component may be included in any effective amount. Generally. the resin may suitably be included in an amount from about 1 to about 50 parts by weight, and preferably from about 10 to about 50 parts by weight, per 100 parts by weight of polyene-polythiol combination.  
  The polyene has two or more reactive unsaturated carbon-to-carbon bonds located terminal from the main chain. The polythiol has two or more thiol groups per molecule. After the polyene, polythiol and resin are combined and if desired, with additional materials, as may be required, the curable lacquer composition is applied to a substrate which may be printed and thereafter exposed to a free radical generator such as actinic radiation to give an essentially odorless solid elastomeric overcoating. Although as a practical matter, actinic radiation is preferred, it is recognized that chemical free radial generating reagents may be employed as well as high energy radiation bombardment.  
  Although the mechanism of the curing reaction is not completely understood, it appears most likely that the curing reaction may be initiated by almost any chemical free radical generating reagent which dissociates or abstracts a hydrogen atom from an SH group, or accomplishes the equivalent thereof.  
  Generally the rate of the curing reaction may be increased by increasing the temperature of the composition at the time of initiation of cure. In many applications, however, the curing is accomplished conve-- niently and economically by operating at ordinary room temperature conditions.  
  The present curable lacquer compositions are characterized by insensitivity to visible light, rendering them generally free from setting on, for example, apparatus which may be used to apply the composition to a substrate. Upon exposure to actinic light, the present lacquer compositions are found to be rapidly curable making them eminently suitable for use in high speed coating operations.  
  A class of actinic light useful herein for curing is ultraviolet light and other forms of actinic radiation which are normally found in radiation emitted from the sun or from artificial sources such as type RS sunlamps, carbon arc lamps, xenon arc lamps, mercury vapor lamps, tungsten halide lamps and the like. Ultraviolet radiation may be used most efficiently if the curable lacquer composition contains a suitable photocuring rate accelerator. Ultraviolet radiation having a wave length from about 100 to about 4,000 Angstroms, and  
 preferably from about 2,200 to about 4,000 Angstroms, is suitable.  
  Curing periods may be adjusted to be very short and hence commercially economical by proper choice of ultraviolet source, photocuring rate accelerator and concentration thereof, temperature and molecular weight, and reactive group functionality of the polyene and polythiol. Curing periods of less than about 1 second duration are possible in preparing lacquer coatings having thickness in the range from about 0.1 to about 0.5 mil and even to about 2 mils in some applications.  
  Conventional curing inhibitors or retarders which may be used in order to stabilize the components of the curable lacquer compositions so as to prevent premature onset of curing may include hydroquinone; p-tert.- butyl catechol; 2,6-ditert.-butyl-p-methylphenol; phenothiazine; N-phenyl-2-naphthylamine; inert gas atmospheres such as helium, argon, nitrogen and carbon dioxide; vacuum; and the like. Acidic stabilizers such as phosphorus acid and the like may be usefully employed.  
  It is further understood that the polyene and the polythiol may be formed in situ in the photocurable lacquer composition without departing from the spirit of this invention.  
 Specifically useful herein are chemical photocuring 30 rate accelerators such as benzophenone, acetophenone, azobenzene, acenaphthene-quinone, o-methoxy benzophenone, Thioxanthen-9-one, xanthen-9-one, 7- H-Benz [de] anthracen-7-one, dibenzosuberone, lnapththaldehyde 4,4-bis (dimethylamino) benzophenone, fluorene-9-one, l -acetonaphthone, 2- acetonaphthone, anthraquinone, l-indanone, 2-tert.- butyl anthraquinone, valerophenone, hexanophenone, 8-phenyl-butyrophenone, p-morpholinopropiophenone, 4-morpholino-benzophenone, morpholinodeoxybenzoin, p-diacetylbenzene, 4- aminobenzophenone, 4-methoxyacetophenone, benzaldehyde, a-tetralone, 9-acetylphenanthrene 2- acetylphenanthrene, lO-thioxanthenone, 3- acetylphenanthrene, 3-acetylindole, 1,3,5-triacetylbenzene and the like, including blends thereof to greatly reduce the exposure times.  
  The curing rate accelerators are usually added in an amount ranging from about 0.0005 to about 50 percent by weight of the photocurable lacquer composition, with a preferred range being from about 0.05 to about 25 percent by weight. Preferred photocuring rate accelerators are the aldehyde and ketone carbonyl compounds having at least one aromatic nucleus attached directly to the group.  
  The relative amounts of polyene and polythiol included in the photocurable lacquer composition are selected such that the mole ratio of enezthiol is from about 0.221 to about 5:1, and preferably from about 0.75:1 to about :1.  
  Practice of the present invention will be further illustrated by the following non-limiting examples wherein all parts and percentages given are by weight unless indicated otherwise.  
 EXAMPLE 1 275 grams (1.86 moles) of phthalic anhydride, 60.8 grams (0.62 mole) of maleic anhydride, 90.5 grams (0.62 mole) of adipic acid, and 328 grams (3.09 moles) of diethylene glycol were heated in a vessel for three hours at 200C. The resulting polyester resin product was cooled and removed from the vessel. A photocurable lacquer composition was prepared by mixing at 50C 10 grams of the resin (a solid at 25C) with 10 grams (0.04 mole) of triallyl isocyanurate, 14 grams (0.03 mole) of pentaerythritol tetrakis (3-mercaptopropionate), 0.5 gram of benzophenone, 0.025 gram of phosphorous acid, and 0.05 gram of Irganox 1076 (trademark for a hindered phenol antioxidant product by Geigy Industrial Chemicals). The mixture was heated to C to dissolve the benzophenone producing a clear homogeneous mixture having a viscosity in the range of 12,000 to 18,000 cps and a pH in the range of 4.5 to 5.5.  
  The photocurable lacqure was applied at 25C to steel can body stock having a red printing ink printed thereon by conventional techniques. The lacquer was applied as a liquid film having a thickness of 0.2 to 0.4 mil using a conventional roller coater. The area of application included the printed area plus adjacent nonprinted portions of the steel. The applied liquid film was exposed to ultraviolet light using a 5,000 watt Hanovia lamp positioned 4 inches from the film. Exposure was for 3 to 5 seconds, during which time the liquid film cured to a clear solid coating which was found to be characterized with high gloss, strong bonding to both the printed ink and steel, and excellent abrasion resistance.  
 EXAMPLE 2 A polyester resin was prepared at 200C. using the resin preparation of Example 1 except that, prior to cooling, 4.3 grams (0.02 mole) of trimethylolpropane diallyl ether was added and the temperature of the reactants was increased to 240C, which temperature was maintained for one hour. The resin product was-cooled and removed from the vessel. Analysis of the product showed it to be a polyester-tetraene which was a solid at 25C. A curable lacquer composition was prepared by mixing 10 grams of this polyester-tetraene at 60C with 10 grams (0.04 mole) of triallyl isocyanurate, 14 grams (0.03 mole) of pentaerythritol tetrakis (S-mercaptopropionate), 0.5 gram of benzophenone, 0.025 gram of phosphorus acid and 0.05 gram of Irganox 1076. This lacquer composition was applied as a film on printed steel can body stock and thereafter cured using this application and curing procedures of Example 1. The cured lacquer coating was found to be characterized with good clarity, high gloss, strong bonding to the printed ink and the steel, and excellent abrasion resistance.  
 EXAMPLE 3 12 grams of commercially available polyethylene glycol having a molecular weight of 400 was mixed with 10 grams of triallyl isocyanurate, 14 grams of pentaerythritol tetrakis (3-mercaptopropionate), 0.5 gram of benzophenone, 0.025 gram of phosphorus acid, and 0.05 gram of lrganox 1076. The resulting photocurable lacquer composition was roller-coated at 20 to 30C onto paperboard having ink printed theron. The area of lacquer application included printed and non-printed areas. The coated paperboard was exposed to ultraviolet light using a 5,000 watt Hanovia lamp positioned 3 inches from the paperboard. Exposure was for 3 to seconds, during which time the lacquer cured to a clear solid coating which was found to be characterized with high gloss, strong bonding to both the printed ink and the paperboard, and excellent abrasion resistance.  
 EXAMPLE 4 grams of liquid polyester resin LB 104-45 (commercially available from Marco Chemical Div. of W. R. Grace and Co.) was mixed with 10 grams of 2,4,- 6-tris(allyloxy)s-triazine, 14 grams of pentaerythritol tetrakis (3-mercaptopropionate), 0.5 gram of benzophenone, 0.025 gram of phosphorous acid, and 0.05 gram of lrganox 1076. A thin film of the resulting photocurable lacquer composition was applied to inkprinted and non-printed areas of steel can body stock using a roller. Next, the film was cured using the curing procedure of Example 1. The cured lacquer coating was found to be characterized with good clarity, high gloss, strong bonding to the printed ink and the steel, and excellent abrasion resistance.  
 EXAMPLE 5 A curable lacquer composition was prepared by mixing at 55C 10 grams of the polyester-tetraene resin of Example 2 with 10 grams (0.04 mole) of triallyl isocyanurate, 10 grams of Bisphenol A diallyl ether, 23 grams of pentaerythritol tetrakis (3-mercaptopropionate), 0.5 gram of dibenzosuberone and 0.05 gram of Irganox 1076. This lacquer composition was applied as a 3-mil film on printed steel can body stock and thereafter cured using the application and curing procedures of Example 1. The cured lacquer coating was found to be characterized with good clarity, high gloss, strong bonding to the printed ink and steel and excellent abrasion resistance.  
 EXAMPLE 6 A photocurable lacquer was prepared at 65C by mixing 10 grams of the polyester-tetraene resin of Example 2 with 31 grams of Bisphenol A diallyl ether,, 24 grams of pentaerythritol tetrakis (3-mercaptopropionate), 1 gram of benzophenone and 0.05 gram of Irganox 1076. This photocurable lacquer was applied at 25-30C to steel can body stock having ink printed thereon. The lacquer was applied as a liquid film with a thickness of 0.3 to 0.5 mil using a conventional roller coater. The area of application included the printed area plus adjacent non-printed portions of the steel. The applied liquid film was exposed to ultraviolet light, using a 4,000 watt Ferro lamp positioned 3 to 4 inches from the film. Exposure was for 3-5 seconds, during which time the liquid film cured to a clear solid coating which was found to be characterized with high gloss, strong bonding to both the printed ink and the steel, and excellent abrasion resistance.  
 EXAMPLE 7&#39; A photocurable lacquer was prepared at 60C by mixing 10 grams of the polyester-tetraene resin of Example 2 with 31 grams of BisphenolA diallyl ether, 24 grams of pentaerythritol tetrakis (3-mercaptopropyl ether), 2 grams of benzophenone, and 0.05 gram of [rganox 1076. A thin film of this photocurable lacquer composition was applied at 25C to magazine quality paper having ink printed thereon. The lacquer was applied as a liquid film having a thickness of 0.05 to 0.1 mil using a conventional roller coater. The area of application included the printed area plus non-printed portions of the paper. The applied liquid film was exposed to ultraviolet light using a 5,000 watt Hanovia lamp positioned 4 inches from the film. Exposure was for about 3 seconds, during which time the liquid film cured to a clear solid coating which was found to be characterized with high gloss, strong bonding to both the printed ink and the paper, and excellent abrasion resistance.  
 EXAMPLE 8 459 grams (3.1 moles) of phthalic anhydride and 296 grams (3.09 moles) of ethylene glycol were heated in a vessel for 4 hours at C. Next, 4.28 grams (0.02 mole) of trimethylolpropane diallyl ether was added. The temperature of the reactants was increased to 230C, which temperature was maintained for 1 hour. The resin product was cooled and removed from the vessel. Analysis of the product showed it to be a polyester-tetraene which was a solid at 25C. A curable lacquer composition was prepared by mixing 12 grams of this polyester-tetraene at 50C. with 10 grams of triallyl isocyanurate, 14 grams of pentaerythritol tetrakais (3-mercaptopropionate), 0.5 gram of benzophenone, 0.025 gram of phosphorus acid, and 0.05 gram of Irganox 1076. This lacquer composition was applied as a thin film at 25 to 30C on printed steel can body stock and-thereafter cured using the application and curing procedures of Example 1. The cured lacquer coating was found to be characterized with good clarity, high gloss, strong bonding to the printed ink and the steel and excellent abrasion resistance.  
 EXAMPLE 9 To a resin kettle maintained under a nitrogen atmosphere and equipped with a condenser, stirrer, thermometer and gas inlet and outlet was added 174 grams 1 mole) of toluene diisocyanate, 428 grams (2 moles) of diallyl malate, along with 0.3 gram of stannous octoate as catalyst, and the reaction was continued for 2 hours at 60c. 20 grams of the thus formed tetraene diadduct of diallyl malate and toluene diisocyanate was combined with l6..3 grams of pentaerythritol tetrakis (Ebmercaptopropionate), 15 grams of the resin of Example 8, 0.5 gram of benzophenone and 0.05 gram of Irganox 1076. A thin photocured lacquer coating was formed of this photocurable lacquer composition on printed steel can body stock using the application and curing procedures of Example 1 The cured lacquer coating was characterized with good clarity, high gloss, excellent abrasion resistance and strong bonding to both the printed ink and the steel.  
 EXAMPLE 1b 7 The procedure of Example 9 was repeated except that 528 grams (2 moles) of 3,3-dimethyl-4,4&#39;- biphenylene diisocyanate was substituted for the toluene diisocyanate. The results were substantially the same.  
 EXAMPLE 1 l The procedure of Example 9 was repeated except that 358 grams (2 moles) of 3-isocyanatomethyl-3,5,5- trimethylcyclohexyl isocyanate was substituted for the toluene diisocyanate. The results were substantially the same.  
 EXAMPLE 12 The procedure of Example 9 was repeated except that 500 grams (2 moles) of 4,4-  
 methylenebis(cyclohexyl isocyanate) was substituted for the toluene diisocyanate. The results were substantially the same.  
 EXAMPLE 13 The procedure of Example 9 was repeated except that 116 grams (2 moles) of allyl alcohol was substituted for the diallyl malate. The results were substantially the same.  
 EXAMPLE 14 The procedure of Example 9 was repeated except that 430 grams (2 moles) of trimethylol propane diallyl ether was substituted for the diallyl malate. The results were substantially the same.  
 EXAMPLE 15 343 grams 1.1 mole) of 4,4-diglycidyl ether of Bisphenol A (commercially available under the name Epon 828 by Shell Chemical Co.) was charged to a dry resin kettle maintained under nitrogen and equipped with a condenser, stirrer, thermometer and gas inlet and outlet. 190 grams (2 moles) of diallyl amine was added to the kettle and the reaction was continued with stirring for 3 hours at 70C. A photocurable lacquer composition was prepared at 55C by mixing 12.6 grams of the thus formed tetraene diadduct with 122 grams of pentaerythritol tetrakis (3-mercaptopropionate), 10 grams of the polyester-tetraene resin of Example 2, 1 gram of dibenzosuberone and 0.05 gram of Irganox 1076. A film of this photocurable lacquer composition was applied&#39;to printed steel can body stock and thereafter cured using the coating and curing procedures of Example 1. The results were substantially the same.  
 EXAMPLE 16 To a resin kettle maintained under a nitrogen atmosphere and equipped with a condenser, stirrer, thermometer and a gas inlet and outlet was added 179 gram (1 mole) of 3-isocyanatornethyl-3,5,5-trimethylcyclohexyl isocyanate. 1 16 grams (2 moles) of allyl alcohol was added and the reaction was continued for 4 hours at 90C with stirring. 100 grams of the resulting diene diadduct of allyl alcohol with the 3- is0cyanatomethyl-3,5,5-trimethylcyclohexyl isocyanate was mixed with 83.5 grams of pentaerythritol tetrakis (3-mercaptopropyl ether), 40 grams of the polyester-tetraene resin prepared in Example 8, 2 grams of dibenzosuberone, and 0.2 gram of Irganox 1076. This photocurable lacquer composition was applied as a film and thereafter cured on steel can body stock having ink printed thereon using the application and curing procedures of Example 1. The results were substantially the same.  
 EXAMPLE 17 4.3 grams (0.2 mole) of trimethylolpropane diallyl ether was added to a resin kettle maintained under a nitrogen atmosphere having a condenser, stirrer, thermometer, and gas outlet and inlet. Next, 264 grams (1 mole) of 3,3-dimethyl-4,4-phenylene diisocyanate and 0.5 gram of dibutyl tin dilaurate catalyst were added. Reaction was continued for 5 hours at 120C with stirring. 20 grams of the resulting tetraene diadduct was mixed with 16 grams of pentaerythritol tetrakis (3-mercaptopropionate), 10 grams of the polyestertetraene resin of Example 2, 1 gram of dibenzosuberone and 0.1 gram of Irganox 1076. A cured coating of this photocurable lacquer composition was formed on printed steel can body stock using the application and curing procedures of Example 1. The results were substantially the same.  
 EXAMPLE 18 275 grams (1.86 moles) of phthalic anhydride, 60.8 grams (0.62 mole) of maleic anhydride, 90.5 grams (0.62 mole) of adipit acid, and 328 grams (3.09 moles) of diethylene glycol were heated in a vessel for three hours at 200C. The resulting polyester resin product was cooled and removed from the vessel. A photocurable lacquer composition was prepared by mixing at 50C, 10 grams of the resin (a solid at 25C) with 9.8 grams (0.04 mole) of 2,4,6-tris(allyloxy)s-triazine,.14 grams (0.03 mole) of pentaerythritol tetrakis (3-mercaptopropionate), 0.5 gram of benzophenone, 0.025 gram of phosphorous acid, and 0.05 gram of Irganox 1076 (trademark for a hindered phenol antioxidant product by Geigy Industrial Chemicals). The mixture was heated to C to dissolve the benzophenone producing a clear homogeneous mixture having a viscosity in the range of 12,000 to 18,000 cps and a pH in the range of 4.5 to 5.5.  
  The photocurable lacquer was applied at 25C to steel can body stock having a red printing ink printed thereon by conventional techniques. The lacquer was applied as a liquid film having a thickness of 0.2 to 0.4 mil using a conventional roller coater. The area of application included the printed area plus adjacent nonprinted portions of the steel. The applied liquid film was exposed to ultraviolet light using a 5,000 watt Hanovia lamp positioned 4 inches from the film. Exposure was for 3 to 5 seconds, during which time the liquid film cured to a clear solid coating which was found to be characterized with high gloss, strong bonding to both the printed ink and the steel, and excellent abrasion resistance.  
 EXAMPLE 19 A polyester resin was prepared at 200C. using the resin preparation procedure of Example 1 except that, prior to cooling, 4.3 grams (0.02 mole) of trimethylolpropane diallyl ether was added and the temperature of the reactants was increased to 240C, which temperature was maintained for one hour. The resin product was cooled and removed from the vessel. Analysis of the product showed it to be a polyester-tetraene which was a solid at 25C. A curable lacquer composition was prepared by mixing 10 grams of this polyester-tetraene at 60C with 9.8 grams (0.04 mole) of 2,4,6-tris(allyloxy)s-triazine, 14 grams (0.03 mole) of pentaerythritol tetrakis (3-mercaptopropionate), 0.5 gram of benzophenone, 0.025 gram of phosphorous acid and 0.05 gram of lrganox 1076. This lacquer composition was applied as a film on printed steel can body stock and thereafter cured using the application and curing procedures of Example 1. The cured lacquer coating was found to be characterized with good clarity, high gloss, strong bonding to the printed ink and the steel, and excellent abrasion resistance.  
 EXAMPLE 20 12 grams of commercially available polyethylene glycol having a molecular weight of 100 was mixed with 9.8 grams of 2,4,6-tris(allyloxy)s-triazine, 14 grams of pentaerythritol tetrakis (3-mercaptopropionate), 0.5 gram of benzophenone, 0.025 gram of phosphorous acid, and 0.05 gram of lrganox 1076. The resulting photocurable lacquer composition was roller-coated at 20 to 30C onto paperboard having ink printed thereon. The area of lacquer application included printed and non-printed areas. The coated paperboard was exposed to ultraviolet light using a 5,000 watt ll-lanovia lamp positioned 3 inches from the paperboard. Exposure was for 3 to seconds, during which time the lacquer cured to a clear solid coating which was found to be characterized with high gloss, strong bonding to both the printed ink and the paperboard, and excellent abrasion resistance.  
 EXAMPLE 21 grams of liquid polyester resin LB 104-45 (commercially available from Marco Chemical Div. of W. R. Grace and Co.) was mixed with 9.8 grams of 2,4- ,6-tris(allyloxy)s-triazine, 14 grams of pentaerythritol tetrakis (3-mercaptopropionate), 0.5 gram of benzophenone, 0.025 gram of phosphorous acid, and 0.05 gram of lrganox 1076. A thin film of the resulting photocurable lacquer composition was applied to inkprinted and non-printed areas of steel can body stock using a roller. Next, the film was cured using the curing procedure of Example 1. The cured lacquer coating was found to be characterized with good clarity, high gloss, strong bonding to the printed ink and the steel, and excellent abrasion resistance.  
 EXAMPLE 22 A curable lacquer composition was prepared by mixing at 55C, 10 grams of the polyester-tetraene resin of Example 2 with 9.8 grams (0.04 mole) of 2,4,6-tris(allyloxy)s-triazine, 10 grams of Bisphenol A diallyl ether, 23 grams of pentaerythritol tetrakis (3-mercaptopropionate), 0.5 gram of benzosuberone and 0.05 gram of lrganox 1076. This lacquer composition was applied as a 3-mil film on printed steel can body stock and thereafter cured using the application and curing procedures of Example 1. The cured lacquer coating was found to be characterized with good clarity, high gloss, strong bonding to the printed ink and steel and excellent abrasion resistance.  
 EXAMPLE 23 459 grams (3.1 moles) of phthalic anhydride and 296 grams (3.09 moles) of ethylene glycol were heated in a vessel for 4 hours at 190C. Next, 4.28 grams (0.02 mole) of trimethylolpropane diallyl ether was added.  
 The temperature of the reactants was increased to 230C, which temperature was maintained for 1 hour. The resin product was cooled and removed from the vessel. Analysis of the product showed it to be a polyester-tetraene which was a solid at 25C. A curable lacquer composition was prepared by mixing 12 grams of this polyester-tetraene at 50C with 9.8 grams of 2,4,6-tris(alloxy)s-triazine, 14 grams of pentaerythritol tetrakis (3-mercaptopropionate), 0.5 gram of benzophenone, 0.025 gram of phosphorous acid, and 0.05 gram of lrganox 1076. This lacquer composition was applied as a thin film at 25 to 30C on printed steel can body stock and thereafter cured using the application and curing procedures of Example 1. The cured lacquer coating was found to be characterized with good clarity, high gloss, strong bonding to the printed ink and the steel and excellent abrasion resistance.  
 EXAMPLE 24 To a resin kettle maintained under a nitrogen atmosphere and equipped with a condenser, stirrer, thermometer and gas inlet and outlet was added 174 grams (1 mole) of toluene diisocyanate, 428 grams (2 moles) of diallyl malate, along with 0.3 gram of stannous octoate as catalyst, and the reaction was continued for 2 hours at 60C. 20 grams of the thus formed tetraene diadduct of diallyl malate and toluene diisocyanate was combined with 16.3 grams of pentaerythritol tetrakis (3-mercaptopropionate(, 15 grams of the copped resin of Example 2, 0.5 gram of benzophenone and 0.05 gram of lrganox 1076. A thin photocured lacuqer coating was formed of this photocurable lacquer composition on printed steel can body stock using the application and curing procedures of Example 1. The cured lacquer coating was characterized with good clarity, high gloss, excellent abrasion resistance and strong bonding to both the printed ink and the steel.  
 EXAMPLE 25 The procedure of Exampel 24 was repeated except that 18 grams of the resin of Example 1 was substituted for the ene capped resin. The cured lacquer coating was characterized with good clarity, high gloss, excellent abrasion resistance and strong bonding to both the printed ink and the steel.  
 EXAMPLE 26 The procedure of Example 24 was repeated except that the trimethlolpropane diallyl ether was replaced by 2.32 grams (0.04 mole) of allyl alcohol. The cured lacquer coating was characterized with good clarity, high gloss, strong bonding to the printed ink and the steel, and excellent abrasion resistance.  
 EXAMPLE 27 The procedure of Example 24 was repeated except that the trimethylolpropane diallyl ether was replaced by 2.88 grams (0.04 mole) of&#39; acrylic acid. The cured lacquer coating was characterized with good clarity, high gloss, strong bonding to the printed ink and the steel, and excellent abrasion resistance.  
 EXAMPLE 28 The procedure of Example 24 was repeated except that the trimethylolpropane diallyl ether was repalced by 2.80 grams (0.04 mole) of IO-undecylenic alcohol. The cured lacquer coating was characterized with good clarity, high gloss, strong bonding to the printed ink and the steel, and excellent abrasion resistance.  
 EXAMPLE 29 The procedure of Example 24 was repeated except that the trimethylolpropane diallyl ether was replaced by 6.0 grams (0.04 mole) of 4-vinyloxybenzyl alcohol. The cured lacquer coating was characterized with good clarity, high gloss, strong bonding to the printed ink and the steel, and excellent abrasion resistance.  
 EXAMPLE 30 The procedure of Example 24 was repeated except that the trimethylolpropane diallyl ether was replaced by 3.48 grams (0.04 mole) of 2-vinyloxyethanol. The cured lacquer coating was characterized with good clarity, high gloss, strong bonding to the printed ink and the steel, and excellent abrasion resistance.  
 EXAMPLE 31 The procedure of Example 24 was repeated except that the trimethylolpropane diallyl ether was replaced by 8.24 grams (0.04 mole) of vinyl hydroxyethyl sulfide. The cured lacquer coating was characterized with good clarity, high gloss, strong bonding to the printed ink and the steel, and excellent abrasion resistance.  
 EXAMPLE 32 The procedure of Example 24 was repeated except that the trimethylolpropane diallyl ether was replaced by 4.04 grams (0.04 mole) of N-methyl-N-vinylethanolamine. The cured lacquer coating was characterized with good clarity, high gloss, strong bonding to the printed ink and the steel, and strong abrasion resistance.  
 EXAMPLE 33 The procedure of Example 24 was repeated except that the trimethylolpropane diallyl ether was replaced by 7.84 grams (0.04 mole) of allyl maleate. The cured lacquer coating was characterized with good clarity, high gloss, strong bonding to the printed ink and the steel, and strong abrasion resistance.  
 EXAMPLE 34 The procedure of Example 24 was repeated except that the trimethylolpropane diallyl ether was replaced by 9.84 grams (0.04 mole) of allyl phthalate. The cured lacquer coating was characterized with good clarity, high gloss, strong bonding to the printed ink and the steel, and strong abrasion resistance.  
 EXAMPLE 35 The procedure of Example 24 was repeated except that the trimethylolpropane diallyl ether was replaced by 5.80 grams (0.02 mole) of diallyl trimellitate. The cured lacquer coating was characterized with good clarity, high gloss, strong bonding to the printed ink and the steel, and strong abrasion resistance.  
 EXAMPLE 36 The procedure of Example 24 was repeated except that the trimethylolpropane diallyl ether was replaced by 4.28 grams (0.02 mole) of diallyl malate. The cured lacquer coating was characterized with good clarity, high gloss, strong bonding to the printed ink and the steel, and strong abrasion resistance.  
 EXAMPLE 37 The procedure of Example 24 was repeated except that the trimethylolpropane diallyl ether was replaced by 4.60 grams (0.02 mole) of diallyl tartrate. The cured lacquer coating was characterized with good clarity, high gloss, strong bonding to the printed ink and the steel, and strong abrasion resistance.  
 EXAMPLES 38-62 The procedures of Examples 1 to 25 inclusive were repeated separately except that the pentaerythritol tetrakis (3-mercaptopropionate) of Examples 1 to 6, 8 to 15, and 17 to 25 and pentaerythritol tetrakis (3-mercaptopropyl ether) of Examples 7 and 16 were replaced by trimethylolpropane tris (3-mercaptopropionate) in amounts providing approximately equivalent amounts of thiol groups in the polythiol components. Thus, for example, about 1.1 grams of trimethylolpropane tris (3-mercaptopropionate) was used per one gram of pentaerythritol tetrakis (3-mercaptopropionate) since these polythiols have thiol equivalent weights of about 122 and 133, respectively. The results were substantially the same as the results for Examples 1 to 25.  
  The following examples illustrates a method for preparing pentaerythritol tris (3-mercaptopropyl) ether.  
 EXAMPLE 63 a. Preparation of Triallyl Ether of Pentaerythritol Into a 5 liter three-necked flask fitted with condenser and addition funnel was placed a solution of 650 g. (16.25 equivalents) of sodium hydroxide in 650 ml. of water. To this was added 272 g. (two moles) of pentaerythritol. This mixture was stirred by means of a magnetic bar and heated to C. Then 1,936 g. 1,385 ml., 16 moles) of allyl bromide was added over an eighthour period at such a rate that the temperature stayed between 70 and C. Following this, heating was resumed, keeping the temperature at 80-82C for an additional four hours. Volatile materials were removed by distillation at atmospheric pressure until the temperature of the condensing vapor reached 98C.  
  One liter of water was added to the hot residue (to prevent crystallization of the salts). The product was cooled to room temperature and the layers were separated. The water layer was extracted twice with 300 ml. portions of diethyl ether. The combined organic layers were dried over anhydrous magnesium sulfate and then distilled at atmospheric pressure to remove the diethyl ether. The triallyl ether of pentaerythritol product weighed 451 g. (88% conversion) and had a boiling range of l20l2lC at 1 mm., n 1.4625. The infrared and NMR spectra were those expected for the triallyl ether of pentaerythritol.  
 b. Conversion of Triallyl Ether to Trithiol Ten drops of tert-butyl hydroperoxide was added to 85.2 g. (1 equivalent of saturation) of pentaerythritol triallyl ether (prepared above) in a 500 ml. flask equipped with a condenser and magnetic stirrer. This mixture was heated to 40C, and 76 g. 1 mole) of thiolacetic acid was added during one hour at such a rate that the temperature did not exceed 90C. After the addition was complete, the product was kept at 80C for an hour and then allowed to cool to room temperature overnight.  
  To the product was added a solution of 100 g. (2.5 where z is or 1, Z is a saturated or unsaturated hydroeq) of sodium hydroxide in 200 ml. of water. This mix- Carbyl group having from about 2 to about 12 carbon ture was heated under reflux for three hours and then atoms and a valence of 2 when z is 0 and a valence of cooled to room temperature and diluted with 300 ml. 3 when 2 is l with a p y y alcohol having the of ether to facilitate separation of the layers. After sep- 5 general lfofmula [R5 OH)Y Where 5 is 21 Saturated 0 aration, the water layer was acidified to pH 25 with unsaturated hydrocarbyl oxyhydrocarbyl g p l-lCl and then extracted twice with 400 ml. portions of g a Valence and from 2 to about 30 Carbon atoms ether. Ether was evaporated from the combined orand y is at least ganic layers, and the residue was diluted with an equal volume of toluene. The resulting solution was washed with 5% aqueous sodium bicarbonate, then with 5% aqueous hydrochloric acid, and with water. The toluene and other volatile contaminants were removed by distillation at 0.1 mm. Hg until the temperature of the residue reached 225C. The product (pentaerythritol tris (3-mercaptopropyl) ether) weighed 119 g. (100% 0 conversion) and had a mercaptan content of 7.09 1 meg/q. This is 84.6% of the theoretical amount. [no (CilSlHHPGl r \R7) 5] Part of the trithiol was distilled at 0.1 mm. Hg. The distillate had a boiling range of 243245C and a mer- 2. The photocurable lacquer composition of claim 1 wherein the polyester component is prepared by capping the product of the reaction of (i) or (ii) and (iii) with a member having the general formula captan content of 7.88 meq/g. (94% of theoretical wherein R is a hydrocarbyl member free of remotely value). internal non-aromatic ene and yne functionality and It is understood that the foregoing detailed descriphaving a valence of q plus 5 and from about 2 to about tion is given merely by way of illustration and that nu- 10 carbon atoms; p is 0 or 1; q is a numeral from 1 to merous variations can be made therein without depart- 10; r is 0 or 1; s is a numeral from 1 to 10; and R is seing from the spirit or scope of the present invention. lected from the group consisting of R R R R R R R R I I I I -t &#39;I---c=c-n -O--EC-}-C=C-R -S-C=C-R I 9 h I R R R R 0 R R R I I I I II I I I -N-C=C-R -ic-] C&#39;=&#39;c-R and -c0-lc :i c=c-R I R a What is claimed is: where g is 0 or an integer from 1 to 9; h is 0 or 1; and l. A photocurable lacquer composition comprising the various R radicals are selected from the group con- (A) a polythiol component containing at least 2 -S1-I sisting of hydrogen, fluorine, chlorine, furyl, thienyl, groups per molecule; (B) as a pol ene component, the pyridyl, phenyl and substituted phenyl, benzyl and subdiadduct of diallyl malate and toluene diisocyanate; the Stituted y a y and Substituted y alkoxy and mole ratio of ene to thiol being from about 0.221 to substituted alkoxy, and cycloalkyl and substituted cyabout 5:1; (C) from about 0.0005 to about percent cloalkyl, where the substituents on the substituted by weight of the composition of a photocuring rate acmembers are selected from the group consisting of nicelerator component; (D) from 1 to about 50 parts by tro, chloro, fluoro, acetoxy, acetamide, phenyl, benzyl, weight per 100 parts by weight of the polyene-polythiol 50 alkyl, alkoxy and cycloalkyl, the alkyl and alkoxy combination of a normally solid, solvent soluble polyesgroups having from 1 to 9 carbon atoms and the cycloter component having a molecular weight from about alkyl groups having from 3 to 8 carbon atoms. 500 to about 100,000 prepared by reacting (i) a p 3. The method for overcoating which comprises apbaslc havmg the general formula plying to a substrate the lacquer composition of claim 0 1, and thereafter exposing the applied composition to actinic radiation for a period of time sufficient to pho- X tocure the composition.  
  4. The method for overcoating which comprises applying to a substrate the lacquer composition of claim 2, and thereafter exposing the applied composition actinic radiation for a period of time sufficient to photocure the composition.  
 where R is a saturated or unsaturated hydrocarbyl group having valence ofx and from 2 to about 21 carbon atoms and x is at least 2 or (ii) a polybasic acid anhydride having the general formula 0 5. The method of claim 3 wherein the applied comc II position is from about 0.1 to about 2 mils in thickness. 0 O z 6. The method of claim 3 wherein the lacquer com- E position is applied to a substrate printed with ink.  
  UNITED STATES PATENT OFFICE CERTIFICATE OF CORRECTION PATENT NO. i 3 877 971 DATED 1 April 15, 1975 INVENTORKS) I James L. Guthrie and Francis J. Rendulic It is certified that error appears in the above-identified patent and that said Letters Patent are hereby corrected as shown below:  
 In column 20, line 5, correct &#34;general lformula [R -OH) to read: -general formula [R i{OH) In column 20, line 60, after &#34;composition&#34; insert Signed and Sealed this twenty-sixth Day Of August 1975 [SEAL] Attest:  