Stabilized polyolefin compositions
D United States Patent 1 [111 3,880,805  
 Needham Apr. 29, 1975 STABILIZED POLYOLEFIN 3.098,842 7/l963 Armitage et al. 2450/4595 COMPOSITIONS 3.455.863 7/1969 Williams 260/33.4  
 [75] Inventor: Donald G. Needham, Bartlesville, OTHER PUBLICATIONS Okla- Compounding Ingredients for Rubber, Third Edition, Assigneel Petroleum p y, &amp; Rubber World, edi- Bartlesville, Okla. tors [22] Filed: June 17,1970 Primary Examiner-V. P. Hoke [21] Appl. No.: 47,146  
 [57] ABSTRACT 52 n 5 5 260334 Polyolefin compositions, stabilized against ultraviolet 260M595 light decomposition by incorporation of stabilizers, are 511 Int. Cl. C08f 45/58 improved y the inclusion of glycerine which masks [58] Field of Search H 3 4 p 2 0 595 the color-effect of the stabilizer and improves the resistance to embrittlement of the resulting polyolefin [56] References Cited Composition- UNITED STATES PATENTS 3/1961 Hardy et al. ..i 260/45.95  
 4 Claims, No Drawings 1 STABILIZED POLYOLEFIN COMPOSITIONS This invention pertains to stabilized polyolefin compositions.  
  In one of its more specific aspects, this invention pertains to adjuvants to polyolefin stabilizers.  
  Polyolefin compositions, such as polyethylene and polypropylene and related materials formed by olefin polymerizations, are widely used in outdoor installa- The stabilizing system comprised of the ultraviolet light stabilizer and the glycerine can be incorporated into the thermoplastic in any suitable manner which insures thorough dispersal therein. The two components of the system may be separately introduced into the thermoplastic or may be introduced thereinto as a mixture.  
  Two samples of a polymer composition were prepared Sample 1 was comprised of an ethylene homopolymer of 0.945 density and 0.2 MI, 0.5 weight percent of a pigment, 0.0005 weight percent carbon black and 0.6 weight percent of the UV stabilizer 2-hydroxy- 4-n-octoxybenzophenone.  
  Sample 2 was of identical composition except that it contained 1 weight percent glycerine.  
  Both samples were identically mixed and subjected to elongation tests after exposure to ultraviolet light by means of conventional methods.  
 Results were as follows:  
 Hours on Test Tensilc Strength, psi Elongation, Color (Accelerated) Sample 1 Sample 2 Sample 1 Sample 2 Sample 1 Sample 2 0 3460 3420 545 570 1000 3625 3520 35 215 2000 3700 3550 27 40 3000 3250 3100 21 53 4000 3550 3650 5 34 Severe Unchanged Darkening in spite of such pigments as it might also contain, certain color casts which are undesirable.  
  35 This invention solves this problem which is inherent in the use of conventional and commercial stabilizers. According to this invention there is provided a method of color stabilizing thermoplastic compositions against ultraviolet light which involves incorporating in &#39;the thermoplastic composition an ultraviolet light stabiplastic composition, the ultraviolet light stabilizer being 50 present in those amounts in which they are usually em- .ployed, that is, from about 0.05 to about 1.0 percent by weight of the thermoplastic composition.  
  The use of UV stabilizers in thermoplastics is well known. One of the most satisfactory of these is a composition in which the effective agent is 2-hydroxy-4-noctoxybenzophenone. However, this stabilizer imparts a yellow coloration to the thermoplastic; this yellow color tends to offset the effect of those pigments which are incorporated in the thermoplastic. However, incorporation of the glycerine suppresses this color-effect of thestabilizer. Additionally, incorporation of the glycerine improves resistance to embrittlement as shown by the residual elongation results of the following test. This is wholly unexpected since glycerine, when used individually, does not exhibit stabilizing properties.  
  These data indicate that the incorporation of the glycerine unexpectedly improved the resistance to embrittlement and therewith provided a definite supplementary effect to the UV stabilization provided by the 2-hydroxy-4-n-octoxybenzopphenone.  
  It will be apparent from the foregoing that various modifications can be made to the method and composition of this invention. Such, however, are considered within the scope of the invention.  
 What is claimed is:  
  l. A method of stabilizing a polymonoolefin composition which comprises incorporating in said composition a stabilizing system consisting essentially of 2- hydroxy-4-n-octoxybenzophenone and glycerine thereby forming a thermoplastic composition in which said 2-hydroxy-4-n-octoxybenzophenone is present in an amount of about 0.05 to about 1.0 percent by weight of the thermoplastic composition and said glycerine is present in an amount from about 0.75 to about 1.25 percent by weight of the thermoplastic composition.  
 2. A method of claim 1 wherein the monoolefin is 5 ethylene.  
  3. A thermoplastic composition consisting essentially of a monoolefin polymer, 2-hydroxy-4-noctoxybenzophenone present in an amount of about 0.05 to about 1.0 percent by weight of the thermoplas- 0 tie composition and glycerine present in an amount of about 0.75 to about 1.25 percent by weight of the thermoplastic composition.  
  4. A thermoplastic composition of claim 3 wherein the monoolefin is ethylene.