Fluoroborate glass exhibiting fluorescence at 1.06 micrometers
ite tates Shaw et a1.  
 [ Apr. 29 1975 1 FLUOROBORATE GLASS EXHIBITING FLUORESCENCE AT 1.06 MICROMETERS [73] Assignee: American Optical Corporation,  
 Southbridge, Mass.  
 [22] Filed: Jan. 11, 1973 [21] Appl. No.: 322,671  
 Shaw et a1 106/47 R OTHER PUBLICATIONS Handbook of Chemistry &amp; Physics (1970), pub. by  
 Chemical Rubber Co., pp. B32 &amp; B33.  
 Primary ExaminerWinston A. Douglas Assistant ExaminerMark Bell Attorney, Agent, or Firm-Andrew E. Pierce; William C. Nealon; Howard R. Berkenstock, .1r.  
 [5 7] ABSTRACT A novel glass exhibits fluorescence from trivalent neodymium ions at a wavelength of approximately 1.06 micrometers. The glass consists essentially of about 98 weight percent of a host glass and about 2 weight percent of a compound which contributes trivalent neodymium ions to the glass. The host glass is a fluoroborate and consists essentially of 10 to 60 mol percent of 8,0 and 40 to 90 mol percent of a fluoride glass modifier selected from the group consisting of BaF- LaF All-&#34; PbF and combinations thereof. The neodymium compound is selected from the group consisting of Nd O and NdF 6 Claims, 1 Drawing Figure PMENTEDAPR29|QY5 RELATIVE INTENSITY FLUOROBORATE GLASS EXHIBITING FLUORESCENCE AT 1.06 MICROMETERS CROSS-REFERENCES TO RELATED APPLICATIONS None.  
 BACKGROUND OF THE INVENTION This invention is related to novel glasses and ismore particularly concerned with such glasses which exhibit fluorescence when doped with trivalent neodymium ions.  
  In recent years, the glass laser has become an extremely important class of lasers. The glasses are doped generally with trivalent rare earth ions. Predominant among these rare earth laser ions is the neodymium ion. Glass lasers doped with trivalent neodymium ions are capable of generating very high power outputs at relatively high efficiencies.  
  Glass has various characteristics which make it an ideal laser hostmaterial; It can be made in large pieces of diffraction-limited optical quality, e.g. with an index of refraction variation of less than one part per million across a 2.5 centimeter diameter. In addition, glass lasers have been made&#39;in a variety of shapes and sizes from fibers of a few microns diameter supporting only a single dielectric waveguide mode, to rods which are two meters long and7.5 centimeters in diameter. Fur thermore, pieces of glass with quite different optical properties can be fused to solve certain system design problems.-For example, glasscompositions can be var ied in order to acquire an index of refraction varying throughout the range of from 1.5 to 2.0. Therefore, those skilled in the art are constantly searching for new glassy materials which can serve as viable hosts for the trivalent neodymium laser ions. This is done in order to enlarge the spectrum of physical, optical, and chemical properties in order to provide a glass laser material totally compatible with the designers system requirements.  
  When searching for such viable host .materials,,it is characteristicn-to examine the fluorescence spectrum exhibited blythexhost material when doped with the trivalent neodymium ions. When one acquires such a host material, it; is highly probable that an operable laser material can be formed of the new glass. The limitations on this generally revolve around the ability to manufacture the glass in sufficient quantity and of sufficient optical quality.  
 SUMMARY OF THE INVENTION Accordingly, it is an object of the present invention to providenovel laser materials which exhibit fluorescence at the characteristic wavelength, 1.06 micrometers, generally associated with the trivalent neodymium ion.  
  Theinvention further comprises a fluoroborate glass consisting essentially of about 98 weight percent of a host glass consisting essentially of 10 to 50 mol percent of B 0 25 to45 mol percent of AIF and 25 to 45 mol *percent of PbF and approximately 2 weight percent of NdF  Further objects, advantages, and features of the invention will be apparent from the following detailed description of the invention.  
 DESCRIPTION OF THE DRAWING In the drawing, the sole FIGURE is a graphical representation of a typical fluorescence spectrum of a glass according to the present invention.  
 DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS In the drawing, a typical fluorescence spectrum curve is shown. The curve shows two peaks, at approximately 1.06 micrometers and at approximately 0.9 micrometers. The peak at 1.06 micrometers is generally the most important in glasses doped with neodymium. The peaks have relative intensity values A and B, associated with the peaks at 0.9 and 1.06 micrometers, respectively.  
  The fluorescence curves shown were measured in a Cary 14 spectrophotometer by placing the glass sample in a copper fixture which in turn was placed in the sample compartment of the Cary. The glass was irradiated at right angles with a Xenon arc lamp through a filter which blocked the transmission of wavelengths longer approximately approximtely 800 nm. The fluorescent spectrum was recorded using the automatic slit control which adjusted the slit width so that the output of a coiled tungsten filament lamp with a filament temperature of approximately 2800K produced a constant deflection on the recording chart for all wavelengths. Thus the recording chart must be corrected to obtain the true relative intensities by dividing the chart deflection by a factor proportional to the energy radiated by the tungsten lamp at the wavelengths of interest. We have estimated the correction factor to be approximately unity at the wavelengths of interest. This estimate was made by using the tungsten emissivities measured by J. C. DeVos (J. C. DeVos, Physics 20,690 (I954) for a ribbon filament tungsten lamp operating at 2800K in a calculation of the energy radiated by the coiled filament lamp at the two wavelengths of interest. The intensity ratios reported here were measured directly from the Cary charts using no correction factor.  
  Several examples of glasses according to the present invention are given in the following examples. Each of these glasses was formed in approximately a 50 gram meltfThe glass is preferably formed in the following manner. The components was added to the batch as H Nd O and all others as the fluoride compound. The constituents were added in the known stoichiometric amounts to yield a glass having a final composition as given in the following examples. The glass making materials must be of high purity and, in particular, must be free of contamination from iron or other elements which would cause light absorption at the primary fluorescence wavelength, 1.06 micrometers, if present in the glass. The finished glass, for example,  
 &#34; should not contain more than 5 parts per million of iron materials in a platinum crucible heated in a Globar electric furnace, an RF induction coil, or a gas flame. No special atmosphere was necessary in the furnace. The raw materials were mixed intimately and as completely as possible in a mixing device that does not introduce any contamination. The mixed batch was loaded into a platinum crucible which did not contaminate the melt with undesired impurities. The crucible was raised to a melting temperature of approximately 1 100C. The batch was held at this temperature for approximately 15 minutes for the 50 gram samples. During this time, the melt was stirred with a platinum rod. The glass was then cast onto an iron plate at room temperature. lt is to be understood that larger samples require a different procedure.  
 EXAMPLE 1 A glass which consists of about 98 weight percent of a host glass and about 2 weight percent of NdF has values for A and B of 0.38 and 0.90 respectively on the fluorescent emission spectrum. The composition, in mol percent, of the host glass is essentially LiF 40 BuF [0 EXAMPLE 2 EXAMPLE 3 A glass which consists of about 98 weight percent of a host glass and about 2 weight percent of NdF has values for A and B of 0.25 and 0.67 respectively on the fluorescent emission spectrum. The composition, in mol percent, of the host glass is essentially 2 3 LiF EXAMPLE 4 A glass which consists of about 98 weight percent of a host glass and about 2 weight percent of NdF has values for A and B of 0.25 and 0.78 respectively on the fluorescent emission spectrum. The composition, in mol percent, of the host glass is essentially B203 60 Lara, 40  
 EXAMPLE 5 A glass which consists of about 98 weight percent of a host glass and about 2 weight percent of NdF has values for A and B of 0.31 and 0.78 respectively on the fluorescent emission spectrum. The composition, in mol percent, of the host glass is essentially B203 40 MR, 30 PbF, 3o  
 EXAMPLE 6 A glass which consists of about 98&#39;weight percent of a host glass and about 2 weight percent of NdF has values for A and B of 0.35 and 0.82 respectively on the fluorescent emission spectrum. The composition, in mol percent, of the host glass is essentially B103 50 LaF 5O EXAMPLE 7 A glass which consists of about 98 weight percent of a host glass and about 2 weight percent of Nd o has values for A and B of 0.23 and 0.47 respectively on the fluorescent emission spectrum. The composition, in mol percent, of the host glass is essentially 13 0 60 LiF 40 EXAMPLE 8 A glass which consists of about 98 weight percent of a host glass and about 2 weight percent of NdF has values for A and B of 0.25 and 0.66 respectively on the fluorescent emission spectrum. The composition, in mol percent, of the host glass is essentially PbF 25 EXAMPLE 9 A glass which consists of about 98 weight percent of a host glass and about 2 weight percent of NdF has values for A and B of 0.30 and 0.80 respectively on the fluorescent emission spectrum. The composition, in mol percent, of the host glass is essentially B203 PbF, 35 AlFa 35 EXAMPLE 10 9,0 20 PbF, 40 AlF 4o EXAMPLE 1 l A glass which consists of about 98 weight percent of a host glass and about 2 weight percent of &#39;NdF has values for A and B of 0.35 and 0.97 respectively on the fluorescent emission spectrum. The composition, in mol percent, of the host glass is essentially 8,0 PbFg 45 AIF 45 The invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. The present embodiments are therefore to be considered in all respects as illustrative and not restrictive, the scope of the invention being indicated by the appended claims rather than by the foregoing description, and all changes which come within the meaning and range of equivalency of the claims are therefore intended to be embraced therein.  
 What is claimed is:  
  l. A fluoroborate glass which exhibits fluorescence at a wavelength of 1.06 micrometers consisting essentially of about 98 weight percent ofa host glass consisting essentially of 10 to 50 mol percent of B 0 to 45 mol percent of AIR, and 25 to 45 mol percent of PbF and approximately 2 weight percent of NdF 2. A fluoroborate glass according to claim 1, wherein the host glass has essentially the following composition as given in mol percent B20, 40 AIF&#34; Pm 30 and wherein the compound contributing trivalent neodymium ions is NdF 3. A fluoroborate glass according to claim 1, wherein the host glass has essentially the following composition as given in mol percent B 0 30 AIR, 35 PbF 35 and wherein the compound contributing trivalent neodymium ions is NdF 5.iA fluoroborate glass according to claim 1, wherein the host glass has essentially the following composition as given in mol percent B203 20 Am, 40 PbF 40 and wherein the compound contributing trivalent neodymium ions is NdF 6. A fluoroborate glass according to claim 1, wherein the host glass has essentially the following composition as given in mol percent Bio: 10 AIR, 45 PbF 45 and wherein the compound contributing trivalent neodymium ions is NdF