Process for preparing colored synthetic leather
United States Patent 1191 Maeda et a1.  
 [451 Apr. 22, 1975 1 1 PROCESS FOR PREPARING COLORED SYNTHETIC LEATHER [75] Inventors: Shigeo Maeda; Minoru Ozutsumi;  
 lsao Niimura; l-lideo Okazaki. all of Tokyo, Japan Related U.S. Application Data [63] Continuation-impart of Scr. No. 376.387. July 5.  
 1973. abandoned.  
 [30] Foreign Application Priority Data July 5. 1972 Japan 47-66647 Aug. 17, 1972 Japan 47-81822 [52] U.S. Cl. 260/37 N; 260/145 A; 260/145 B; 260/146 D; 260/147; 260/149; 260/151 [51] Int. Cl. C08g 51/66 [58] Field of Search 260/147. 149.151. 37 N. 260/37 ND. 146 D [56] References Cited UNITED STATES PATENTS 2.660.574 11/1953 Jones 260/37 NP 3.086.967 4/1963 Davies 260/151 3.137.671 6/1964 Bosshard 260/37 N 3.391.132 7/1968 Beffa 260/147 3.417.073 12/1968 Mciningcr 260/147 3.459.727 8/1969 Steincr 260/147 3.658.747 4/1972 3.730.950 5/1973 Barnes 260/37 N Primary E.\&#39;aminerHarry Wong. .Ir.  
 Assistant E.\&#39;aminer-Pau1 R. Michl Attorney, Agent, 0&#34; FirmOb1on. Fisher. Spivak,  
 McClelland &amp; Maier [57] ABSTRACT A colored synthetic polyurethane leather is prepared by reacting a polyisocyanate with a polyol or a polyurethane substrate and a 2 1 complex metal dye which contains an isocyanate-reactive group selected from the group consisting of amino. alkylamino. and hydroxyl and which has the formula wherein A and A are the same or different and each represent phenylene which can have non-dissociated substituents; B and B are the same or different and each represent coupling components which can contain nondissociated substituents within each component and are disposed in the dye molecule so that the bridging groups D and D are in an ortho position rela tive to the bridging azo groups; Z and Z are the same or different and each represent O. or -COO which are disposed in an ortho position relative to the azo bridging groups; D and D are the same or different and each represent O.  
 M represents chromium or cobalt; [N] represents aliphatic ammonium or acyclic ammonium, [Q] represents hydrogen, sodium, ammonium. aliphatic ammonium or acyclic ammonium, N&#39; represents aliphatic ammonium or acyclic ammonium, and n represents an integer from l-6.  
 10 Claims, No Drawings PROCESS FOR PREPARING COLORED SYNTHETIC LEATHER CROSS-REFERENCE TO RELATED APPLICATIONS This application is a continuation-in-part of application Ser. No. 376,387, filed July 5, 1973 now abancloned.  
 BACKGROUND OF THE INVENTION 1. Field of the Invention This invention relates to a process for preparing a colored polyurethane synthetic leather.  
 2. Description of the Prior Art Various pigments or dyes have been used to color synthetic polyurethane leather. However, the use of pigments have produced a number of disadvantages. Pigments generally do not contain solubilizing groups, so often large particles of the pigments will form secondary and tertiary particle aggregations during product production. This particle aggregation is particularly prominent in the drying step. Usually, it is difficult to reduce the aggregated particles to a primary particle size by simple mechanical crushing. Because of these difficulties, polyurethane leathers dyed with conventional pigments often easily lose their color or result in dark, unsuitable colors. Even if these disadvantages are overcome such as by addition of dispersing agents into the pigments, the water and oil resistance of the synthetic leather product will be decreased which results in dissolution bleeding or color migration of the coloring agent. These factors adversely affect product quality.  
  Dyes, on the other hand, usually have solubilizing groups within the molecule which facilitates dispersion of the dye in oil or water. However, dyes have the disadvantage in that they impart low weather durability, water resistance, oil resistance, and bleeding resistance to the leather. For these reasons, no completely satisfactory method has been developed for the coloring of synthetic leather products. Conventional practice has called for the use of overcoats of nylon or polyurethane on top of the colored urethane leather to prevent bleeding of the coloring agent. To further complicate matters, satisfactory top coats have not been developed. lnspite of these disadvantages, dyes still are the most prominent coloring agents used for synthetic polyurethane leather products because of their excellent clear hue and transparency and because of the variety of colors available.  
  A need continues to exist, however, for new techniques of coloring synthetic leathers which have good solubility, dispersibility, water resistance, oil resistance and weather durability and which have a very clear hue which will not bleed from the leather.  
 SUMMARY OF THE INVENTION Accordingly, one object of the invention is to provide a process for preparing colored synthetic leather having excellent weather durability, water and oil resistance, and bleeding resistance, while having a clear hue.  
  Another object of the invention is to provide a process for preparing colored synthetic polyurethane leather wherein the dye is bonded to the polymer matrix of th-e leather.  
  Briefly, these objects and other objects of this invention as hereinafter will become readily apparent can be attained by a process for preparing colored synthetic polyurethane leather in whih the synthetic leather substrate is reacted with a 2:1 complex metal dye which contains isocyanate reactive groups such as amino groups, alkylamino groups or hydroxyl groups and which has the formula wherein A and A are the same or different and each represent phenylene which can have a non-dissociated substituent; B and B&#39; can be the same or different, and each represent coupling components which can contain non-dissociated substituents within each component, and are disposed so that the bridging groups D and D are in an ortho position relative to the bridging azo groups; Z and Z can be the same or different and each represent O- or COO-- which are disposed in an ortho position relative to the azo bridging groups; D and D can be the same or different and each represent O, NH-, or N-alkyl; M represents chromium or cobalt; [N] represents aliphatic ammonium or acyclic ammonium; [Q] represents hydrogen, sodium, ammonium, aliphatic ammonium or acyclic ammonium; N represents aliphatic ammonium or acyclic ammonium; and n represents an integer from l-6. The alkyl group is preferably a lower alkyl group having l-l5 carbon atoms.  
 DESCRIPTION OF THE PREFERRED EMBODIMENTS In the preparation of the dyed synthetic leather products of this invention an isocyanate reactive group such as amino, alkylamino or hydroxyl of a 2:1 complex metal dye reacts with the free polyisocyanate components of the polyurethane substrate. Any one of several procedures is suitable for the reaction between the complex dye and the isocyanate component of the polyurethane substrate. By the phrase alkylamino group of course is intended to include the substituted alkylamino groups of substituents which do not interfere with the reactions. The phrase hydroxyl&#34; is used in the restrictive sense as meaning alcoholic hydroxyl. In one method the reactive complex dye is mixed with a polyisocyanate, a polyol and a solvent and the resulting solution can be coated onto a substrate such as a film, sheet, plate, or the like. The polyurethane is formed by the reaction of the polyisocyanate and polyol components. In another method the reactive complex dye is mixed with a polyisocyanate, a polyurethane and a solvent and the resulting solution is coated on a substrate. Still another method involves mixing the reactive complex dye with a polyurethane and a solvent and the resulting solution is coated on a substrate. To  
 the coated mixture is added a solution of a polyisocyanate or a mixture of a polyisocyanate and a polyurethane in a solvent, wherein the polyisocyanate component is reacted with the reactive complex dye.  
  The polyisocyanates which are used in this invention to form the synthetic polyurethane leather substrate include aromatic isocyanates, aliphatic isocyanates and multi-functional compounds derived from isocyanate. Suitable aromatic isocyanates include 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, 1,5-naphthalene diisocyanate, cumene-2,4-diisocyanate, 4-methoxy- 1,3-phenylene diisocyanate, 4-chloro-l,3-phenylene diisocyanate, 4-ethoxy-l,3-phenylene diisocyanate, biphenylene-4,4&#39;-diisocyanate, 3-nitro-biphenylene-4,4&#39;- diisocyanate, 4,4&#39;-methylene diphenyl diisocyanate, 3,3&#39;-dimethyl-4,4&#39;-methylene diphenyl diisocyanate, 3,3 &#39;-dimethyl-4,4-diisocyanate diphenyl, 4,4- diisocyanate diphenyl ether and triphenyl methane triisocyanate. Suitable aliphatic isocyanates include hexamethylene diisocyanate, tetramethylene diisocyanate, decamethylene diisocyanate, l,4cyclohexylene diisocyanate, 4,4-methylene dicyclohexyldiisocyanate, pxylene diisocyanate, and 1,4-phenylene diethylenediisocyanate. The multifunctional compounds derived from the isocyanate include the isocyanates IIICO NCO l NCO and CHzO CONll-(CHzhNCO ll5C2-CCH2O CONH(CH;)5NCO CHRO C ONH-(CHaMNCO which are prepared by reacting 2,4-tolylene diisocyanate or hexamethylene diisocyanate with trimethylol propane.  
  The polyols which are reacted with the various isocyanates of this invention to form the synthetic polyurethane leather substrates can be essentially linear hydroxyl terminated polyesters.  
  Representative of these polyester diols are those obtained by esterification of aliphatic dibasic acids or anhydrides thereof with glycols. Preferably, in the synthesis of the polyesters the glycol component is employed in excess of the stoichiometric amount required to react with the acid or anhydride in order to ensure that the polyesters are hydroxyl-terminated. Suitable dicarboxylic acids (or anhydrides) employed in the preparation of the polyester diols include adipic, succinic, pimelic, suberic, azelaic, sebacic, terephthalic acids and mixtures thereof, or their anhydrides Adipic acid is the preferred acid. Suitable glycols employed in the preparation of the polyester diols are the straight chain aliphatic glycols containing from 2 to carbon atoms, and include ethylene glycol, propane-1,3-diol, butanel,4-diol, 2-butene-l ,4-diol, hexane-l ,6-diol, octanel,8-diol, and decane-l,lO-diol, and mixtures of two or more glycols. A preferred group of polyester diols is that which isobtained by esterifying adipic acid with an excess of a mixture of 9 parts ethylene glycol and 1 part of propane-1,2-diol.  
  The final dyed synthetic leather product can be ob- 5 tained as shown in the equations (a)-(d). These equations demonstrate the manner in which the different types of isocyanates reactive groups which include the amino, alkylamino (including alkylamino) and hydroxyl (alcoholic) groups that are a part of the 2:1  
 10 complex metal dye (formula 1) react with the free isocyanate functional groups of the polyisocyanate components of the synthetic leather. By this mechanism the complex metal dyes are chemically bonded to the synthetic leather substrate through urea or urethane type bonds. The resulting leather products have the desired clear hue and do not bleed.  
  (a) [2:1 complex metal dyeH-NH: OCN 1 N00 (polyisocyanate) HO I: lOH  
  (p y &#34;I r [2:1 complex metal dye-NHO-synthetic leather] J n L (b) [2:1 complex metal dye?01i OCN r 1 N00 (polyisocyanate) 110i lOH L .J p0ly0l) [2:1 complex metal dye-: l O(&#39;I;NH-s[ ynthetic leather] (c) [2: 1 complex metal dyejT-NHz OCN 1 N00 (polyisocyanate) F I NHCOO-polyurethane- L l&#39; I NCOO 1 th ne L W yum a .l  
 CONH :l ayu CONHC2:1 metal complex dye] [2:1 complex metal dyej0H OCN 1 N00 &#39;l- (polyisocyanate) l&#39; &#39;l NHCOO-polyu.rethane NCOO polyurethane- L J OONH NH L Y I I r C 0 0L2:1 complex metal dye (polyisocyanate) HOT OH (p yol) [synthetic leather]-NHC ONH-{2:1 complex metal dye] Q OCN NCO a N )n 9 G9 [2:1 complex metal dye: l- -01l (s 03 M n 0 C N- N C 0 (polyisocyanate) HO- OIl (p y l) [synthetic leather]NH C O O[2: 1 complex metal dyel 6 69 [2:1 complex metal dye}- -Nll s w av n 0 ON .1 NC 0 L (polyisocyanate) I&#39; 1 NH O 0 O polyurethane L J N 0 O O polyurethane L l .l  
 C O NH NH I qea C ONHL2:1 complex metal dye (s Oa NQB 6 69 [2:1 complex metal dye} -OH-l (s 03 M 0 CN- 3-NO 0 (polyisocyanate) NH C O O-polyurethane L l&#39; 1 -N 0 O O-polyurethane L J 0 ON H NH 9 9 (1O O-E2:1 complex metal dye] Q 6 In all of the reactions which are used to form the dyed synthetic leather products of this invention, the polyisocyanates serve the dual function of supplying the groups which react with the coupling groups of the complex metal dyes and acting as a monomer with the polyol component to form the polyurethane substrate.  
  The amounts of the polyisocyanate, the polyol and the polyurethane which are used, and the solvent and reaction conditions are selected depending upon the type of synthetic leather required. As far as the manner in which the complex dye is reacted with the polyisocyanate component which in turn is reacted with the polyurethane or the polyol is concerned, any of the well known conventional procedures can be used for the formation of the synthetic polyurethane leather products. Therefore, a general discussion on the conventional procedures for forming the synthetic polyurethane leather products will not be presented.  
  The coloring process of this invention is completely different from the conventional methods of coloring synthetic polyurethane synthetic leather products. In the conventional coloring methods, a coloring agent which is a pigment or dye is simply dispersed or solubilized in the synthetic leather composition. However, in this invention, free isocyanate groups of the polyisocyanate components in the synthetic leather react with the complex metal dye through the amino, alkylamino or hydroxyl groups of the dye. By this mechanism the individual dye molecules are bonded to the synthetic leather substrate through covalent bonds. The bonding mechanism is not at all dissimilar to that which links a reactive dye to a substrate such as cotton or wool. This type of covalent bond substantially improves the washing fastness and rubbing fastness of the dyed fabric. Further, bleeding of the dyed substrates is substantially reduced.  
  In the process of this invention, the coloring agents or dyes having formulas l) and l can be easily prepared by reacting a chromium or cobalt compound by conventional procedures, with a monoazo dye having the formula wherein A and B are as defined above; X, represents hydroxyl or carboxyl; X represents hydroxyl, amino or (ontinucd The following list shows typical cations with the appropriate component numeral which are useful in this invention.  
 C omponcnt numeral sodium potassium ammonium n-octylammonium monomethylaminopropylammonium monoethylaminobutylammonium Z-ethylbutylammonium 3-methoxypropylammonium dibutylaminopropylammonium monobuty]aminobutylammonium aminopropylethanolammonium dicthylaminopropylammonium methyliminobispropylammonium dimethyluminopropylammonium diammonium ion of 1.2-diaminopropane diammonium ion of l,3-dimcthy1aminopropanc 2-ethy1hcxylammonium monocthylaminopropylammonium tctradecylammonium N-aminopropyl-Z-pipecolinium (21&#34;) piperazinium piperidinium hydrogen ion N.N-dibutyl-propylammonium stearylammonium In a preferred embodiment of the process of the invention, one or more of the dyes of formula [1] or [1&#39;] is dissolved in a solvent which is inert to the polyisocyanate constituent such as methylethyl ketone, ethylacetate, tetrahydrofuran, toluene, dimethylformamide, or the like and a polyisocyanate component and a polyol component are added to the mixture. The mixture is blended and coated uniformly on a substrate and is reacted at 50-80C for 4 hours. By this procedure suitable synthetic leather products are obtained which have a clear hue and which do not bleed. Suitable substrates include cloth, non-woven fabrics, polyvinylchlo- Bleeding test:  
  A 5X5 cm colored synthetic leather is covered with a polyvinylchloride sheet and a 1 kg of weight is placed on the sheet at C for 5 hours. The amount of coloring in the polyvinyl chloride caused by bleeding of the dye from the leather is observed.  
 Water bleeding test:  
  A 5X5 cm colored synthetic leather is covered with a wet, white silk cloth and a 1 kg of weight is placed on the cloth at 25C for 5 hours. The amount of coloring in the silk cloth caused by bleeding of the dye from the leather is observed.  
 The polyurethane materials which are used in the Examples are Nippolane 5121, a polyurethane prepared by reacting diphenylmethanediisocyanate with polybutyleneadipate and Nippolane 5034, a polyol prepared by reacting tolylenediisocyanate with the adipic acid coester of ethyleneglycol and diethyleneglycol.  
 EXAMPLE l-a 4-n-octy1-2-amino phenol was diazotized and coupled with 1-amino-6-naphthol. The resulting monoazo dye was treated with a chromium compound by a conventional process to yield a 2:1 complex chromium dye having the formula 1 Part of the complex dye obtained was dissolved in 20 parts of dimethylformamide and 1.2 parts of a polyisocyanate (urethane triisocyanate prepared by reacting 1 mole of trimethylolpropane with 3 moles of 2,4- tolylenediisocyanate with a purity of 74.6% in 25.4% ethyl acetate-Colonate L manufactured by Nippon Polyurethane Ind., Co.), 20 parts of 45 percent polyol dissolved in 33 percent toluene and 22 percent ethy- A comparison of the bleeding properties of the two synthetic leathers prepared showed that the bleeding properties of the product of this invention was substantially better than the comparitve product. No visible bleeding was found on the polyvinyl chloride sheet in the bleeding test when the complex dye of this invention was used. When the comparative complex dye which contained no amino group was used. the polyvinyl chloride sheet used in the bleeding test assumed a dark blue color.  
 When the complex dye of this invention was substituted with a methylamino group or a B-aminoethyl amino group, a blue colored synthetic leather which underwent no visible bleeding was obtained. When a polyurethane sheet was used instead of the polyvinylchloride sheet, similar results were obtained.  
  EXAMPLE H7 05 Part of the complex dye of Example l-a was dissolved in 10 parts of dimethylformamide and 10 parts of a solution of a polyurethane (Nippolane 5121 manufactured by Nippon Polyurethane lnd. Co.) was added to form a uniform solution. The polyurethane solution containing the complex dye was coated on a polyvinylchloride sheet and dried at 110C for 5 minutes. The colored synthetic polyurethane leather was coated with a solution of 10 parts of said polyurethane solution, 0.6 parts of a polyisocyanate compound prepared by reacting 1 mole of trimethylolpropane with 3 moles of 2,4- tolylenediisocyanate (Colonate L) and 6 parts of ethylacetate. The coated synthetic leather was dried at C for 5 minutes and a blue colored synthetic leather was obtained which did not bleed when subjected to either of the two tests.  
  On the other hand, when the polyisocyanate compound was omitted in the coating solution, bleeding of the complex dye from in the leather substrate was found. When the chromium 2:1 complex dye which had no amino group was used, bleeding of the complex dye from the substrate was found in both tests.  
  When a polyurethane sheet was substituted for the polyvinylchloride sheet as a substrate, similarly good results were obtained.  
 EXAMPLE l-c 0.5 part of the complex dye of Example l-a was dissolved in 10 parts of dimethylformamide and 10 parts of polyurethane (Nippolane 5121) was added to form a uniform solution. To the solution was added 0.6 parts of a polyisocyanate (urethanetriisocyanate prepared by reacting 1 mole of trimethylpropane with 3 mole of 2,4- tolylenediisocyanate) to form a polyurethane solution containing the coloring material. The resulting polyurethane solution was coated on a polyvinylchloride sheet and was cured at 50C for 4 hours. A blue colored synthetic leather was obtained which did not bleed when subjected to either test.  
 EXAMPLE 2 4-Nitro-2-aminophenol was diazotized and was coupled with N,N-bis-(2-aminoethyl)-m-amino phenol. The resulting monoazo dye was treated with a chromium compound by a conventional procedure and a 2:] complex chromium dye having the following formula was obtained.  
  0.5 Part of the 2:1 complex chromium dye was dissolved in a solvent mixture of 10 parts of methylethyl ketone and 10 parts of ethyl acetate. 1.2 Parts of polyisocyanate (Colonate L) and 20 parts of polyol (Nippolane 5034) were added to the dye solution to form a uniform solution. The urethane composition solution containing the complex dye was uniformly coated on a polyurethane sheet and was dried at 50C for 4 hours. A clear, red colored synthetic leather was obtained. The resulting synthetic leather was compared in the bleeding test to a colored synthetic leather prepared by the same process except that a similar 2:1 complex chromium dye having no amino group was used. The results showed a significant difference in the bleeding properties of the two samples, wherein no visible bleeding was found for the colored synthetic leather of this invention.  
  When 6-nylon sheet was used instead of the polyurethane sheet, similar results were obtained.  
 EXAMPLE 3 2-Amino-5-chloro benzoic acid was diazotized and coupled with l-(3&#39;-aminophenyl)barbituric acid to yield a monoazo dye. The monoazo dye was treated with a chromium compound by a conventional procedure and a 2:1 complex chromium dye having the following formula was obtained.  
 ooNu  
  I Part of the 2:1 complex chromium dye was reacted by the process of Example 1 and a yellow colored synthetic leather was obtained. The resulting synthetic leather was compared in the bleeding test to a colored synthetic leather prepared by the same process except that a similar 2:] complex chromium dye having no amino group was used. The results showed a significant difference in the bleeding of the two dyed substrates wherein no visible bleeding was found for the colored synthetic leather of this invention.  
 EXAMPLE 4 3-Amino-4-hydroxy-N-(B-hydroxyethyl the same process except that a similar 2:1 complex chromium dye having no N-B-oxyethyl group was used. The test results showed a substantial difference between the two substrates wherein no visible bleeding was found for the colored synthetic leather of this invention.  
 EXAMPLE 5 4-Methyl-2-aminophenol was diazotized and coupled with 4(B-aminoethylaminosulfonyl)-acetoacetic anilide to yield a monoazo dye. 3-Amino-4-hydroxy-N-(B- hydroxyethyl)-benzene sulfonamide was diazotized and benzenesulfonamide was diazotized and coupled with 35 coupled with 4-methylacetoacetic anilide to yield a -t-butyl-B-naphthol. The resulting monoazo dye was monoazo dye. The two types of monoazo dyes were treated with a chromium compound by a conventional treated with a cobalt compound by a conventional proprocedure and a 2:] complex chromium dye having the cedure and an asymmetrical 2:1 complex cobalt dye following formula was obtained. 7 having the following formula was obtained.  
 l tCqHg e S O&#39;JNHCHICHIOH N=N o I 0 on, &#39;Ha aHoNaHoNli-a 0 0 Q -Q s dhNHCHzCHzOH ,Hu 4&#39;;  
  COCH:  
 \ bNH-s02NHomomNH= 0 O a) C4Hg 0 Nmom H 0.8 Part of the asymmetrical 2:] complex cobalt dye was dissolved in a solvent mixture of 10 parts of methyethylketone and 10 parts of ethylacetate and was reacted by the process of Example I and a clear, yellowish-pink colored synthetic leather was obtained. The resulting synthetic leather was compared in a bleeding test to a colored synthetic leather prepared by the same process except that a similar 2:1 complex cobalt dye having no ethylamino group and no methylamino group was used. The test results showed a significant difference between the two products wherein no visible bleeding was found for the colored synthetic leather of this invention.  
 EXAMPLES 6 TO 36 In accordance with the process of Example 1, colored synthetic polyurethane synthetic leather products were prepared by reacting the leather products with 2:] complex dyes prepared by treating a series of monoazo dyes with a chromium compound or a cobalt compound. The monoazo dyes are described in Table I by the diazo component numerals, the coupling component numerals and the cation component numerals shown. No visible bleeding was found for any of the resulting clear, colored synthetic leather products ob- 25 tained. The colors of. the synthetic leathers are also shown in the Table.  
 treated with isooctylamine. A 2:1 complex chromium dye having the following formula was obtained.  
 TABLE I Example Monoazo dye Metal Cation Type of Color diazo coupling complex component component (Nl dye 6 (7) (8&#39;) Cr (4&#34;) symmetric violet 7 (9) (l l) Cr (6&#34;) asymmetric bluish grcy (7&#39;) v 8 (14) (28) Cr (7&#34;) symmetric pinkish rcd 9 (ll) (24&#39;) Cr rcd l0 (l5) (5) Ci (8&#34;) violct ll (l6) (l2&#39;) Cr (7&#34;) blue 12 (34) (62&#39;) Cr (9&#34;) yellow sh red I3 (30&#39;) Cr (10&#34;) yellowish pink I4 (37) (31&#39;) Cr (4&#34;) asymmetric pinkish brown (38) (32&#39;) g 15 (2) (54&#39;) Cr (2l) symmetric red l6 (I4) Co &#39;1 yellow 17 (23) Cr H2&#34;) yellow l8 (18) (23&#39;) Cr (14&#34;) reddish blue l9 (19) Cr (23&#34;) red 20 (40) (64) Cr 15&#34;) symmetric greenish yellow 2l (6) (33&#39;) Cr (22&#34;) p nk 22 (l) (40&#39;) Cr (7&#34;) asymmetric pink sh red 23 (26) (66&#39;) Cr (7&#34;) symmetric reddish blue 24 (l) (2 l Cr (16&#34;) asymmetric blue (2 25 (2) (56&#39;) Cr (23&#34;) symmetric red 26 (3) (48&#39;) Cr (17&#34;) yellow 27 (2!) (59&#39;) Cr (4&#34;) asymmetric brown (2|) 28 (29) (18&#39;) Cr (5&#34;) Syml&#39;l&#39;l CIl&#39;lC blue 29 (23) (5&#39;) Cr (18&#39;1) I black 3O (18) (61&#39;) Co (ll) brown 31 (3) (47&#39;) Cr l4&#34;) asymmetric yellow (3) H2) 32 (l) (12) Cr (5&#34;) symmetric blue 33 (20) H4) Cr (l7&#34;) I blue 34 (l) (15&#39;) Cr (4&#34;) I black 35 (2) (16) Cr (1&#34;) H black 36 (l) Cr (l7&#34;) red In the following Examples, 2:1 complex chromium 60 dyes are used which have at least one sulfo group.  
 EXAMPLE 37 5-Nitro-2-aminophenol was diazotized and coupled with 2-amino-8-naphthol-6-sulfonic acid (y-acid). The 65 resulting monoazo dye was treated with a chromium compound by a conventional procedure and was leather product was found.  
 EXAMPLE 38 NztO: S  
 The dye was treated with a cobalt compound and fur- .her treated with N,N-dibutyl-propylamine. A 2:1 com- )lex cobalt dye having the following formula was obained.  
 llgC;  
  G3 6 NClI CllzClhNHaSOx /i MD/ lhe process of Example 1 was followed except that 0.5 mart of the complex dye was used and a clear, orange :olored synthetic polyurethane synthetic leather prodict which did not bleed was obtained.  
 EXAMPLE 39 -Nitro-2-aminophenol was diazotized and coupled with 2-hydroxy-6-(N-B-aminoethyhnaphthalenesulfonamide to yield a monoazo dye. 4- Chloro-2-aminophenol was diazotized and coupled with 2-naphthol-6-sulfonic acid to yield a monoazo dye. Both of the monoazo dyes were treated with a chromium compound and an asymmetric 2:1 complex chromium dye was obtained which was treated with stearylamine to form a salt having the formula The process of Example 1 was followed except that 0.8 part of the complex dye was used and a clear, violet colored synthetic polyurethane leather was obtained which did not bleed.  
 EXAMPLE 40 The process of Example 1 was followed except that 0.6 part of the 2:1 complex chromium dye having the following formula was used (the salt was formed by treating the complex with isooctylamine). A clear, red colored synthetic polyurethane leather was obtained which did not bleed.  
  The process of Example 1 was followed except that 1 part of the 2:1 complex chromium dye having the following formula was used (the salt was formed by treating the complex with isooctylamine). A black, colored synthetic polyurethane leather was obtained which did not bleed.  
 O2N A N112 Q J H2N L V J The various components which constitute the monoazo dyes of Examples 42-68 are shown in Table 11 below as well as the colors of the dyed synthetic leather products obtained.  
 or different and each represent O-, or COO- which are disposed in an ortho position relative to the azo bridging groups; D and D are the same or different and each represent O,  
  TABLE ll Example Monoazo dye Metal Cation Type of Color diazo coupling complex component component [M*] N dye 42 (47) (88&#39;) Cr (1&#34;)(4&#34;) symmetric reddish yellow 43 (91) Cr (23&#34;)(5) violet-yellow 44 (I8) (92) Co (l&#34;)(l0&#34;) reddish yellow 45 (12) (88) Cr (17)( 17&#34;) asymmetric yellow (12) (87&#39;) 46 (54) (70&#39;) Cr l&#34;)(20&#34;) symmetric red-orange 47 (24) (79) Cr l&#34;)(8&#34;) violet-blue 48 (55) (80&#39;) Cr (l&#34;)(l7) black 49 (I9) (81&#39;) Co (l&#34;)(l7&#34;) black 50 (49) (27) Cr (1&#34;)( l0) reddish yellow 51 (50) (75) Cr (3)( l7&#34;) blue-black 52 (5|) (93) Cr (1)(4&#34;) yellow 53 (47) (82&#39;) Cr (l5 )(l5) violet 54 (48) (71) Co (l&#34;)(21&#34;) red 55 (19) (72) Cr (l)(ll) orange-red 56 Cr (l&#34;)(5&#34;) asymmetric black (1 3&#39;) 57 Cr l l( l2&#34;) symmetric red-orange 58 (51) (63&#39;) Cr (l&#34;)(l3&#34;) greenish yellow 59 (47) (94) Cr l)(14&#34;) violetbluc 60 (l) (84&#39;) Cr (l&#34;)(l5&#34;) black 61 5) Co (2&#39;.Z&#34;)(Z2&#34;) red 63 (48) (73) Cr (l)(l7&#34;) red 63 (52) (79) Cr l&#34;)(9&#34;) symmetric violet-blue 64 (2) Cr (l)(17) blue 65 (73) Cr (l&#34;)(l&#34;) red 66 (86) Cr (l&#34;)(l6&#34;) blue 67 (53) Cr (l&#34;)(l7&#34;) orange 8 (l) (74&#39;) (47) (57) Cr (1&#34;)( l7&#34;) asymmetric red Having now fully described this invention, it w1ll be NII or Nalkyl; apparent to one of ordinary skill in the art that many l changes and modifications can be made thereto with- 5 out departing from the spirrt or scope of the invention as Set folth M represents chromium or cobalt; [N] represents ali- What IS claimed as new and intended to be covered I phatic ammonium or acyclic ammonium, [Q] repreby Letters Patent is: h d h 40 SBHIS y rogen, SO rum, ammonium, 8. 1p atlC ammo- I. In a process for preparing a colored synthetic polyurethane leather by reacting a polyisocyanate with a polyol or a polyurethane, the improvement which comprises reacting the polyisocyanate with a 2:1 complex metal dye which contains an isocyanate-reactive group selected from the group consisting of amino, alkylamino, and hydroxyl and which has the formula,  
 wherein A and A are the same or different and each represent phenylene which can have non-dissociated substituents; B and B are the same or different and each represent coupling components which&#39;can contain non-dissociated substituents within each component and are disposed in the dye molecule so that the bridging groups D and D are in an ortho position relative to the bridging azo groups; Z and Z are the same nium or acyclic ammonium; and N represents aliphatic ammonium or acyclic ammonium; and n represents an integer from 1-6.  
  2. The process of claim 1, wherein the terminal hydroxyl froups of said 2:1 complex metal dye are reacted with said polyisocyanate component which has previously reacted with said polyol component or said polyurethane substrate.  
  3. The process of claim 1, wherein said 2:1 complex metal dye is mixed with said polyisocyanate component, said polyol component and a solvent and the resulting solution is coated on a substrate.  
  4. The process of claim 1, wherein said 2:1 complex metal dye is mixed with said polyisocyanate component, said polyurethane and a solvent and the resulting solution is coated on a substrate.  
  5. The process of claim 1, wherein said 2:1 complex metal dye is mixed with said polyurethane and a solvent and the resulting solution is coated on a substrate over which is applied a solution of said polyisocyanate component and said polyurethane.  
  6. The process of claim 1, wherein the amount of said polyisocyanate component added is more than the equivalent amount necessary to react with said 2:1 complex metal dye.  
  7. The process of claim 1, wherein said 2:1 complex metal dye is prepared by reacting a chromium or cobalt compound with a monoazo dye having the formula wherein A and B are defined as above; X represents hydroxyl or carboxy]; X represents hydroxyl, amino,  
 wherein R, and R are hydrogen, lower alkyl, amino or hydroxy substituted lower alkyl, N-alkyl-amino or N- hydroxylalkylamino-substituted lower alkyl; R, and be a 2 combined may be hetero six member ring containing an imino group; X; represents SO NH- SO CO- or NHCO; 2 represents an integer from l4; Y may be bonded with A or B or both A and B; x represents 1 or 2 and y represents 1, 2 or 3.  
  8. A colored synthetic polyurethane leather which comprises the reaction product of a polyisocyanate with a polyol or a polyurethane substrate and a 2:1 complex metal dye which contains an isocyanatereactive group selected from the group consisting of amino, alkylamino, and hydroxyl and which has the formula wherein A and A are the same or different and each represent phenylene which can have non-dissociated substituents; B and B are the same or different and each represent coupling components which can contain non-dissociated substituents within each component and are disposed in the dye molecule so that the bridging groups D and D are in an ortho position relative to the bridging azo groups; Z and Z are the same or different and each represent --O, or COO- which are disposed in an ortho position relative to the azo bridging groups; D and D are the same or different and each represent O-, NH,  
 M represents chromium or cobalt; [NT represents aliphatic ammonium or acyclic ammonium; [01 represents hydrogen, sodium, ammonium, aliphatic ammothe resulting solution is coated onto a substrate.