Vapor phase reactor off-gas recycle system for use in the vapor state polymerization of monomers
SUMMARY OF THE INVENTION 
     This invention relates to a novel process for the essentially total recycle of reactor off-gases from a continuous, vapor phase polymerization reactor and, more specifically, to a novel, continuous, essentially isobaric process for the essentially total recycle of reactor off-gases during the vapor phase polymerization of a monomer or mixture thereof in a horizontal, quench-cooled, stirred-bed reactor. 
     In accordance with the instant invention a continuous, essentially isobaric process is taught for the essentially total recycle of reactor off-gases during the vapor phase polymerization of a monomer or mixture thereof in a horizontal, quench-cooled, stirred-bed, tubular reactor containing a polymer bed wherein the quench liquid contained in the reactor off-gases is at least in part separated in a separation zone from monomer, hydrogen, if used, and entrained polymer fines and thereafter a major amount of such quench liquid and the polymer fines are returned to the reactor and a minor amount of the quench liquid returned to a catalyst make-up zone and thereafter to the reactor and wherein separated gaseous monomer and hydrogen together with make-up amounts of monomer and hydrogen are returned largely or completely below the surface of the stirred, polymer bed in the reactor. 
     BACKGROUND OF THE INVENTION 
     One of the problems in solution or slurry polymerization of monomers is the capital costs required in the production thereof. Monomer polymerization using a vapor phase process cn be considerably more economical if certain problems inherent in vapor state polymerization can be solved. These include problems of carrying out the polymerization in a thermally controlled fashion so as to avoid hot spots, maintaining a proper product particle size distribution and, in the case where catalysts are utilized which have extremely high yields but are extremely sensitive to poisoning, decreasing to a minimum the amount of make-up material seen by the catalyst per amount of product formed. Now we have discovered a reactor off-gas treatment process which largely solves the above referred to problems and realizes important economic benefits through savings in energy consumption, raw materials and capital equipment. 
     In U.S. Pat. No. 2,936,303 (Goins) a vapor state polymerization of ethylene, propylene or mixtures thereof is carried out in a countercurrent, fluidized bed in the presence of inert diluent gas. In the process described therein catalyst in solid form is passed downwardly in the reactor and, for example, ethylene mixed with diluent gas is passed countercurrently up through a series of vertical fluidized bed reaction zones. In this process the reaction in the various reaction zones can be controlled independently by taking off-gas from the last reaction zone, cooling it, and recycling portions of such off-gas to each of the reaction zones. However, because of the use of diluent gas and a fluidized bed large quantities of gas must be passed through the reactor per unit of polymer produced. 
     In U.S. Pat. No. 3,023,203 (Dye) a suspended, gas phase polymerization of olefins using a reactor having three concentric superimposed vertical sections, comminuted catalyst addition suspended in the entering gases and temperature regulation by gas cooling is shown. The process includes polymer removal without pressure letdown. 
     In U.S. Pat. No. 3,254,070 (Roelen) a method for the gas phase polymerization of ethylene using conventional cooling is described wherein a mixture of reaction products and solid or liquid catalysts is constantly being mechanically subdivided. This patent additionally teaches that the reacting material may be agitatingly moved through a number of stages each with different polymerization conditions. An additional mode described therein teaches that the first few stages may be carried out using liquid phase polymerization finishing up with polymerization in the vapor phase. Different polymerization temperatures may be used in the separate reactors. 
     In U.S. Pat. No. 3,256,263 (Wisseroth et al.) a method of removing heat and producing intensive movement of the polymeric product produced during the gas phase polymerization of olefins in a stirred, vertical, fluidized reactor is described using mechanical agitation and introduction of the polymerization monomer immediately after expansive cooling in the form of moving gas or liquid jets. 
     In U.S. Pat. No. 3,300,457 (Schmid et al.) polymerization of mono-olefins, particularly ethylene and propylene, is accomplished in a fluidized bed using a stirred, vertical reactor. Catalysts and polymer in the reactor are moved in the direction of flow of the mono-olefin by the stirring and heat is removed by cooling the walls of the vessel, by conduction using the gas stream, or by the introduction of liquefied mono-olefin. 
     In U.S. Pat. No. 3,469,948 (Anderson et al.) a horizontal, paddle type polymerization reactor using pulsed gases including the polymerization olefin is described. The teaching of this patent is directed to the use of longitudinally oriented paddles which are suitably shaped to give forward movement to the solid polymer resulting from the vapor phase polymerization. 
     In U.S. Pat. No. 3,652,527 (Trieschmann et al.) a process for the gas phase polymerization of propylene in a stirred-bed, vertical reactor using evaporative cooling of the reaction is described. This patent teaches that it is essential that one component of the catalyst combination must be directly placed on the bed of solid polymer produced in the polymerization and the second catalyst component must be introduced in the gas phase above the bed. 
     Finally, in British Patent No. 1,354,020 (Badische) a vapor phase olefin polymerization process is described in which the heat generated in the polymerization process is removed by the introduction of the monomer and heat transfer agents in gaseous or liquid state in the polymerization zone. However, the use of multiple polymerization temperatures in the vertical, stirred, fluid-bed reactor is not taught and it is difficult to see how much individual control could be accomplished in the apparatus described. 
    
    
     SHORT DESCRIPTION OF THE DRAWING 
     The FIGURE shows one embodiment of the process described herein. 
    
    
     STATEMENT OF THE INVENTION 
     The invention described herein is a process for the essentially isobaric, essentially total reactor off-gas recycle from a horizontal, vapor phase, polymerization reactor, which reactor operates in a quench-cooled, stirred-bed fashion. The recycle process is particularly adapted for use with polymerization catalysts and cocatalysts which produce very high yields of polymeric product. 
     In general, the process involves a controlled introduction of catalyst components, monomer or mixtures thereof and quench liquid into the one or more polymerization sections of the horizontal reactor directly onto a stirred, subfluidized bed of polymer forming from the polymerization of monomer from the gas phase in and over such polymer bed. The process introduces recycle gases largely underneath the polymer bed, quench liquid onto the moving surface of the bed and catalyst components into or onto the bed. 
     The reactor may have one or more polymerization sections separated from each other by weirs or other suitably shaped baffles to prevent gross backmixing between sections and each section may be individually controlled in terms of polymerization temperature and/or polymer production rate so that a polymeric product having a controlled spread of molecular weight and particle size may be produced. Provision may also be made to divide the reactor into two or more compartments each compartment having a separately controllable hydrogen partial pressure and a separate separation zone and recycle vapor return. 
     Reactor off-gases are removed along the top of the reactor after advantageously substantially removing polymer fines from the off-gases. The reactor off-gases are then taken to a separation zone wherein the quench liquid is at least in part separated along with further polymer fines and some of the catalyst components from the polymerization monomer or monomers and hydrogen, if used, which monomer or monomers and hydrogen are then recycled to inlets in the various polymerization sections along the reactor generally underneath the generally subfluidized polymer bed contained therein. A portion of the quench liquid is taken off the separation zone and a major portion of such take-off containing the further polymer fines returned to the inlets at the various sections along the top of the reactor and a minor portion, essentially purified of cocatalyst, if used, and polymer fines is fed into a catalyst make-up zone for dilution purposes so that fresh quench liquid need not be introduced for that purpose. 
     Provision may be made to introduce the catalyst components, quench liquid and recycle gases at different rates into the different sections of the reactor so that the polymerization temperatures and polymer production rates of the individual sections may be individually controlled. The concentration of catalyst components may be varied in the various sections in order to change and control polymer production rate, polymer molecular weight and particle size distribution. Catalyst components may be added into or onto the stirred bed. 
     The recycle system of the process is designed so it together with the reactor operate essentially isobarically. That is, preferably there is not more than a ± 25 psig pressure change in the recycle system and reactor, more preferably, ± 10 psig which is the normal pressure drop expected from operations. 
     By the term vapor state reactor or process is meant a reactor or process, the monomer or monomers of which are vapors or gases under conditions prevailing in the reactor. 
     One embodiment of the process is shown in detail in the Figure and such process can be roughly divided into two areas, the reactor area and the reactor off-gas treatment (quench liquid separation) and catalyst make-up area. 
     As may be seen by looking at the Figure, horizontal polymerization reactor 101 is divided into several stirred sections 167, 169, 171 and 173 to provide for the possibility of operating the sections of the reactor at different polymerization temperatures and polymer production rates. The polymer bed of the reactor is stirred by impellors formed by a plurality of transversely extending paddles adjacently attached along a longitudinally placed drive shaft 104, which shaft is typically located concentrically in the reactor. Polymerization takes place in each of the aforementioned sections to form a polymer bed distributed throughout the reactor. 
     The polymerization temperature in each of the sections may be individually controlled by a combination of methods including the stirring, the controlled differential introduction of vapor recycle into each of the sections through inlets 175, 177, 179 and 181 along the bottom of the reactor and, the introduction into each of the sections of inert quench liquid and catalyst components at different rates through quench liquid inlets 153, 155, 157 and 159 and catalyst inlets 123, 125, 127 and 129 spaced along the top of the reactor. 
     Where the reactor is to operate in a differential hydrogen mode, the reactor is further divided into two or more compartments each having a controllable vapor composition by one or more dividing structures within the reactor, which structures extend upwardly filling the cross-section of the reactor. A perforation or opening is made in each of such dividing structures below the bed height so that the polymeric powder in the bed may travel freely from one compartment to the adjacent one and ultimately out in polymer take-off vessel 103. The dividing structures are provided so that intermixing of the vapors in adjacent compartments can be controlled. In such a mode each of the compartments has a separate reactor off-gas separation zone and vapor recycle system and provision may be made for the introduction of differential amounts of hydrogen and monomer into each of the compartments. 
     Generally, the dividing structures are designed to prevent extensive intermixing of the vapors in the individual compartments, however, in one mode of multiple hydrogen operation the vapors are deliberately mixed by feeding the vapors from the hydrogen poor compartment to the hydrogen rich compartment and adding make-up monomer, similarly to the hydrogen poor compartment and hydrogen make-up similarly to the hydrogen rich compartment. 
     Reactor off-gases are removed through outlets 183, 185, 187 and 189. Since a certain deleterious amount of polymer fines may be produced in the reactor they are advantageously, substantially removed prior to transfer of the reactor off-gases to the reactor off-gas separation and catalyst make-up areas by using traps, filters, settlers, cyclones or scrubbers or a combination thereof. 
     A plurality of catalyst and quench inlets can be used in reactor 101 and one or more pairs of catalyst and quench inlets may be used for each reactor section 167 to 173. The catalyst and quench inlets are typically designed so that catalyst and quench liquid are distributed onto the top of the stirred bed at roughly the same location. Such introduction of catalyst and quench liquid combined with adequate agitation has been found to provide more uniform polymerization and prevent localized polymer fusion in the polymer bed and hence reduce the number of molten plugs of polymer and give more trouble free performance of the reactor. It is advantageous in one mode of carrying out polymerization in the reactor to provide for separately controlled addition of catalyst components and quench liquid on the polymerization sections by means of, for example, valves. Such separately controlled additions into reactor sections 167-173 provide for separate control of reactor polymerization temperatures and polymer production rates among the sections and can be used to vary and control the molecular weight, molecular weight distribution and particle size distribution of the polymer. 
     Catalyst, dissolved or slurried in recycle quench liquid, is advantageously introduced onto the surface of the bed in at least one of the various reactor sections through inlets 123, 125, 127, and 129. Similarly placed inlets 153, 155, 157 and 159 are used to introduce recycle quench liquid, which may contain cocatalyst make-up from line 147, onto the bed in the individual reactor sections. However, depending upon the nature of the catalyst, cocatalyst and monomer to be polymerized, catalyst and/or cocatalyst can be sprayed or otherwise introduced into the reactor neat or in other non-polymerizable vehicles. Alternatively, for some monomers, catalyst and cocatalyst can be added in make-up zone 145 and together added to reactor 101. 
     In one mode of operation it has been found advantageous to make the catalyst and quench liquid inlets concentric so that the catalyst and quench liquid are sprayed into the reactor and onto the surface of the polymer bed in such a way as to more evenly distribute catalyst components on the polymer bed surface. However, the catalyst and quench inlets may be made separate and the catalysts and quench liquid introduced separately onto the bed. 
     The reactor off-gases are taken via line 131 to scrubber tower 133 wherein the quench liquid component of the off-gases is at least in part removed from the polymerizable monomer and hydrogen, if used. Such polymerizable monomer and hydrogen containing some quench liquid are removed from the top of scrubber tower 133 after, advantageously, passing through heat exchanger 160, separator 161 and blower 144 via vapor recycle line 156 with additional hydrogen and monomer make-up being added via lines 163 and 165. Alternatively, monomer and hydrogen can be returned from scrubber tower 133 to reactor 101 bypassing heat exchanger 160 and separator 161. The amount of the vapor recycle introduced into the individual sections of the reactor via inlets 175, 177, 179, and 181 can be individually controlled by valves 191, 193, 195, and 197. The quench liquid of separator 161 is essentially free of polymer fines and catalyst components and suitable for use in catalyst make-up zone 145. 
     Quench liquid, separated from the reactor off-gases, is cooled by heat exchanger 154 and returned in major portion to the top of scrubber tower 133. A minor portion of the quench liquid is returned through line 137, heat exchanger 143, pump 139 and quench liquid recycle line 151 to quench liquid inlets 153, 155, 157, and 159 carrying with it some monomer, hydrogen and any polymer fines carried by the off-gases into scrubber tower 133. In the important embodiment in which cocatalyst is used, make-up cocatalyst may be introduced via line 147 as a solution or slurry in the recycle quench liquid stream. A small portion separated quench liquid essentially free of polymer fines and catalyst components is taken off separator 161 via line 134 and pumped through pump 136 to catalyst make-up zone 145. Make-up quench liquid is added through line 140. 
     Polymerization in catalyst make-up zone 145 or associated line 149 and inlet 123-129 can cause serious plugging problems and may be controlled by keeping the cocatalyst concentration in catalyst make-up zone 145 below a certain value, the value depending upon the catalyst and cocatalyst used and the monomer to be polymerized. In a case where cocatalyst is introduced through catalyst make-up zone 145, polymerization, if a problem, can be reduced by temperature lowering of, shortening the residence time in, etc., make-up zone 145. Alternatively, make-up quench liquid from line 147 can be used in catalyst make-up zone 145 in place of recycle quench liquid to prevent polymerization of monomer is said zone. 
     Valve 199 has been provided in the catalyst make-up zone bypass line in order to more easily vary the concentration of catalyst in the catalyst make-up introduced into the reactor. It has been found that particle size of the polymer produced in reactor 101 can be advantageously varied by varying the concentration of the catalyst being introduced through inlets 123, 125, 127 and 129. Further, it has been found advantageous to vary the catalyst concentration either by changing its concentration in make-up zone 145 or, alternatively, to change its concentration by introducing quench liquid into catalyst line 149 via valve 199 just prior to the point where the catalyst enters the catalyst inlets. Make-up catalyst is added through line 142. 
     The interior of the reactor is equipped with a rotating paddle drive shaft 104 extending longitudinally through reactor 101 to which are attached paddles extending transversely from the shaft and making close clearance with the inside wall of reactor 101 to insure adequate bed mixing at the reactor wall. The paddles are preferably flat to maximize bed agitation for a given rotational speed and preferably two paddles per impellor are used. The width of the paddles is such that between about four to about 12 impellors (eight to 24 paddles) will be present in a reactor section of about 3 feet in length. The orientation of the paddles on adjacent impellors is about 90°.  The paddles are so constructed to minimize any forward or backward movement of the bed during stirring and are driven at such a speed as to give a slow turnover of the entire polymer bed contained in the reactor. The speed at which the impellors turn should be fast enough to provide the desired heat and mass transfer between liqid, solid and gas but not so fast that the finer portions of the polymer bed are thrown up in large quantities into the space above the bed. That is, the speed typically is about 5 to about 30 RPM so that the integrity of the bed is maintained. 
     The section after the take-off barrier and above the take-off vessel may be likewise equipped with one or more two-paddle impellors, the number of which depends upon the size of the take-off. However, other take-off assemblies such as end or side take-off apertures, which assemblies replace the take-off barrier, may be used as may be understood by one skilled in the art. 
     Vapor recycle which includes the polymerizable monomer and hydrogen, if used, is brought in through vapor recycle line 156 to vapor recycle inlets 175 to 181 generally at a rate designed to prevent fluidization of the bed. The rate at which the vapor recycle gases are introduced into the individual sections 167 to 173 can be controlled by valves 191 to 197 and such control may be used to help vary the section polymerization temperatures. 
     In an important embodiment of the process described herein in which the polymerization temperature of one or more of the sections is held at a different value than that in the other sections (dual temperature operation or multi-temperature operation), it is advantageous to vary the amounts of any or all of the catalyst components being introduced into the various sectons. Particle size distribution and molecular weight distribution are advantageously affected thereby. This may be accomplished by feeding the catalyst inlets of the different sections individually. Even in single temperature operation, it can be advantageous to feed one or more of the sections with catalyst components in different amounts than catalyst components being introduced into the other section or sections. 
     The overall reactor temperature range for a polymerization depends upon the particular monomer which is being polymerized and the commercial product desired therefrom and as such are well known to those skilled in this art. In general, the temperature range used varies between about 40°C up to the softening temperature of the bed. The total polymerization pressure is composed of the polymerizable monomer pressure, vaporized quench liquid pressure and hydrogen pressure, if used, and such total pressure typically varies from above about atmospheric to about 600 p.s.i.g. The individual partial pressures of the components making up the total pressure determine the rate at which polymerization occurs, the molecular weight, and the molecular weight distribution of the polymer to be produced. The temperature of polymerization is controlled as may be understood by one skilled in the art. 
     The process described herein may be applied to the polymerization of polymerizable monomers which are polymerizable below the softening points of their polymeric forms including ethene, propene, 4-methylpentene-1, butene-1, vinyl chloride, butadienes, styrene, poly(ethyleneterephthalate) and mixtures of such monomers. Particularly suitable are the polymerization of ethene and propene. 
     The quench liquid used for temperature control is a readily volatilizable liquid which can be sprayed onto the surface of the polymer bed to evaporatively conduct heat away from the polymer bed and thus must be inert to the monomer being polymerized, the catalyst components used in the polyermization, and have as high a heat of evaporation as is consistent with readily volatilization of the quench liquid in the reactor at the polymerization temperature. In general alkanes such as propane, a butane, a pentane, or a hexane or closely boiling mixtures thereof may be used. The preferred quench liquid for ethene is isobutane or isopentane. It should be understood that where the monomer to be polymerized is readily condensible, e.g. propene, the quench liquid can be liquified monomer or a mixture of liquified monomer and an additional quench liquid. 
     The rate of quench liquid addition should be low enough to keep the polymer bed dry, i.e. maintain the partial pressure of the quench liquid vapor below the due point, yet large enough to obtain the maximum cooling effect of the quench liquid. Generally, the quench liquid will carry away fifty percent or more of the heat of polymerization. For propene polymerization over ninety percent of the heat of polymerization is desirably removed by the quench liquid. At a 200°F polymerization temperature in the polymerization of ethene, desirably more than seventy percent of the heat of polymerization is removed using isobutane and more than 50 percent of the heat is removed using isopentane. 
     In general, the catalysts which are most useful to the process described herein are those which are very active and give a high yield on catalyst. Included in this group are cocatalysts composed of organometallic compounds of Periodic Groups IA, IIA and IIIA and catalysts which are based on transition metal compounds. Aluminum alkyl compound coatalysts are especially preferred and include trialkylaluminums and alkylaluminum halides such as a dialkylaluminum chloride. The transition metal catalyst can be a metal compound of Group IV or Group V such as a titanium or vanadium compound, a compound of Group VI such as chromium or molybdenum oxide or may be one of the above catalysts supported on a magnesium-based support or a support such as alumina, silica, or silica-alumina. 
     The preferred catalysts and cocatalysts are as aforesaid high yield catalysts, By high yield is meant catalysts and cocatalysts, the residues of which, do not have to be removed from the products of the process. 
     The preferred catalysts and cocatalysts for ethene polymerization are a trialkylaluminum cocatalyst with a catalyst which is a titanium compound supported on magnesium-based support or chromium oxide supported on alumina, silica or silica-alumina. For propene polymerization it is preferable to use a dialkylaluminum chloride cocatalyst and a catalyst which is an active titanium trichloride. However, the process and apparatus described herein are not meant to be limited to the catalyst and cocatalyst used except in that the process operates best using high yield catalysts. 
     While the invention is described in connection with the specific Examples below, it is to be understood that these are for illustrative purposes only. Many alternatives, modifications, and variations will be apparent to those skilled in the art and such alternatives, modifications and variations fall within the spirit and scope of the appended claims. 
     EXAMPLE I 
     A supported titanium chloride catalyst was suspended in isopentane at a concentration of 30 milligrams/liter and pumped continuously to the reactor at a rate of 300 milliliters/hour. Aluminum triethyl diluted with isopentane to 1000 milligrams/liter was pumped continuously at a rate to maintain the desired weight ratio of aluminum triethyl/catalyst, 3/1 to 15/1. Ethylene was charged continuously at the rate of polymerization to maintain pressure, 300 psig. A continuous stream of gas, 0.3 cubic feet/hour, was removed from the reactor for gas chromatographic analysis to maintain the hydrogen concentration in the reactor at 34 mol percent by intermittent hydrogen addition for polymer molecular weight control. The reactor polymer bed temperature was held at 160°F. by continuously spraying isopentane at the apropriate rate onto the 30 R.P.M. stirred polymer bed. The vaporized isopentane was condensed and recycled. The non-condensed gas (40° to 50°F.) was continuously recycled back into the bottom of the stirred polymer bed. The polymer bed level was maintained by the opening position in the retaining weir. The polymer overflow spilled out into the melter which was maintained at 350° to 400°F. by a combination of polymerization heat and external electrical heat. The melted polymer pumps to the bottom and was forced through a horizontal piece of 3/4 inch diameter × 4 foot long pipe at 400° to 500°F. by the reactor pressure. Water was injected continuously into the polymer melt between the melter and catalyst deactivator at a rate of 10 milliliters/hour. Polymer melt extrudes from the catalyst deactivator through a 3/8 inch diameter opening and is drawn through a water bath and chopped. Polymer was produced at the rate of 1 to 3 pounds/hour at a yield level of 100,000 grams polymer/gram catalyst. Physical properties of the polymer taken out of the melter are shown below in Table I and some properties of the polymer powder taken from the reactor are shown in Table II. 
     
                                           TABLE I                                 
__________________________________________________________________________
Conditions: 160°F, 300 psig, 34 mol percent H.sub.2, 13/1 to 15/1  
triethyl                                                                  
aluminum/catalyst weight ratio                                            
General Properties           Run A Run B.sup.(1)                          
__________________________________________________________________________
Unnannealed density, grams/cubic centimeter                               
                             0.961 0.959                                  
Annealed density, grams/cubic centimeter                                  
                             0.977 0.977                                  
Inherent viscosity, dl/gram  1.87  2.29                                   
Melt index, MF.sub.1, grams/10 minutes                                    
                             0.92  0.44                                   
Melt index, MF.sub.10, grams/10 minutes                                   
                             38    24                                     
Flow rate ratio, MF.sub.10 /MF.sub.1                                      
                             41.4  54.5                                   
Hexane extractables, weight percent                                       
                             0.47  0.41                                   
Oven volatiles content, weight percent                                    
                             0.20  0.28                                   
Stiffness, psig              165,000                                      
                                   160,000                                
Molecular Weight Parameters, GPC                                          
Molecular weight distribution, Mw/Mn                                      
                             7.6   10.5                                   
Tensile Properties                                                        
Tensile strength at yield, psig at 2 inches/minute                        
                             4540  4600                                   
Tensile strength at ultimate, psig at 2 inches/minute                     
                             3410  2810                                   
Elongation at yield, percent at 2 inches/minute                           
                             10    11                                     
Elongation at ultimate, percent at 2 inches/minute                        
                             1200  689                                    
Impact Properties                                                         
Tensile impact strength, ft-lb/in.sup.2                                   
                             65    88                                     
Izod impact strength, ft-lb/in notch                                      
                             9.2   9.8                                    
Thermal Properties                                                        
Vicat softening point, °F                                          
                             266   262                                    
Brittleness temperature, °C                                        
                             --    --                                     
__________________________________________________________________________
 .sup.(1) Triethylaluminum/catalyst weight ratio = 2.6/1 to 3.75/1.       
 
    
     
                       TABLE II                                                    
______________________________________                                    
Conditions: 160°F, 300 psig, 34 mol percent H.sub.2, 13/1 to 14/1  
triethylaluminum/catalyst weight ratio                                    
                  RUN A      RUN B                                        
Cut number          5R     8R     10R                                     
______________________________________                                    
Total polymer produced, grams                                             
                    3628   5509   6637 1952                               
Inventory turnover (No. of times)                                         
                    3.0    4.6    5.5  1.6                                
Percent original inventory remaining                                      
                    5      1      0.4  20                                 
Bulk density, grams/cubic centimeter                                      
                    0.36   0.37   0.37 0.41                               
MF.sub.10           28.7   38.7   48.2 --                                 
MF.sub.1            0.89   1.0    1.3  --                                 
MF.sub.10 /MF.sub.1 32.3   38.7   37.1 --                                 
______________________________________                                    
 
    
     EXAMPLE II 
     A carbon steel reactor approximately 2 feet in diameter by 3.0 feet in length was used in this continuous ethylene-propylene polymerization. Temperatures were 181°F at one end of the reactor, 171°F at the center of the reactor and 181°F near the take-off weir end and reactor total pressure was 400 psig. Ethylene was fed to the reactor at 20.57 pounds/hour and propylene was added at 0.29 pounds per hour. The recycle gas rate was 2.29 actual cubic feet per minute and the recycle quench liquid, isopentane, rate was 0.29 gallons/minute. The supported titanium catalyst was added at about 0.3 grams per hour as a dilute slurry in isopentane. The amount of slurry added was about 3 gallons per hour. Triethylaluminum cocatalyst was added as a solution in isopentane at a rate of 35 milliliters per hour at a concentration of 0.025 grams triethylaluminum per milliliter. 
     Gas analyses of reactor recycle gases were continuously made and typical values were: hydrogen, 37 mol percent; ethane, 0.3 mol percent; propene, 1.1 mol percent; isopentane, 1 mol percent and ethene, 60.6 mol percent. 
     The melt index of product was about 0.58 grams/10 minutes. 
     EXAMPLE III 
     Ethylene was polymerized in the same manner described in EXAMPLE I. The catalyst was 2.0 weight percent chromium trioxide on W. R. Grace No. 952SiO 2 . Catalyst was calcined at 1200°F. with dry oxygen for 12 hours. Catalyst, triisobutylaluminum and ethylene were continuously charged to the reactor at 210°F. under 300 psig. pressure. Hydrogen was charged as needed to maintain 35 mol percent H 2  in the reactor. The mole ratio of Al(i-Bu) 3  /CrO 3  was 3. Polymer yield based on catalyst was 4,600 grams/gram. Polymer was removed continuously as a melt. The polymer produced showed the following physical properties; 
     
                                           TABLE III                               
__________________________________________________________________________
                 Wt. Percent                                              
                         Wt. Percent                                      
Cut                                                                       
   M.I.                                                                   
       MF.sub.10                                                          
           MF.sub.10 /MF.sub.1                                            
                 Extractables                                             
                         Volatiles                                        
                                 Mw/Mn                                    
__________________________________________________________________________
5  0.20                                                                   
       22.2                                                               
           111   1.5     0.65    14.7                                     
6  0.12                                                                   
       16.6                                                               
           138   1.6     0.87    17.0                                     
7  0.12                                                                   
       20.2                                                               
           168   1.8     0.98    15.4                                     
__________________________________________________________________________
 
    
     EXAMPLE IV 
     Propylene was polymerized by an active titanium chloride catalyst with diethylaluminum chloride cocatalyst continuously in the gas phase under conditions tabulated in Table IV. The propylene served as its own quench liquid for heat removal. Polymer was intermittently removed as particulate through a double ball-valved lock chamber attached to the take-off end of the reactor. 
     
                                           TABLE IV                                
__________________________________________________________________________
POLYMERIZATION OF PROPYLENE                                               
                  Catalyst: Titanium trichloride                          
                  Cocatalyst: Diethylaluminum chloride                    
                  Conditions: 160°F, 300 psig, 1 mole percent      
                  hydrogen                                                
__________________________________________________________________________
Time on stream, minutes                                                   
             145       270       153      225       162                   
Type of catalyst addition                                                 
             Batch     Batch     Continuous                               
                                          Batch     Continuous            
Et.sub.2 AlCl/TiCl.sub.3 ratio                                            
             2.8       2.8       3.0      2.8       2.9                   
TiCl.sub.3 addition rate,                                                 
             48.sup.(1)                                                   
                       24-48.sup.(2)                                      
                                 45       24-48.sup.(2)                   
                                                    46                    
milligrams/hour                                                           
Total polymer produced,                                                   
             165       486       296      358       300                   
grams                                                                     
Polymer yield, grams/gram                                                 
             (0-145 min) 1970                                             
                       (0-270 min) 3120                                   
                                 (0-153 min) 2600                         
                                          (0-225 min) 2980                
                                                    (0-162 min) 2040      
             (0-60 min) 640                                               
                       (0-60 min) 1225    (0-90 min) 172                  
             (60-145 min) 4600                                            
                       (60-120 min) 3800  (90-225 min) 7200               
__________________________________________________________________________
 
    
     EXAMPLE V 
     A supported titanium chloride catalyst and triethylaluminum catalyst were employed in the same manner as described in Example I using approximately 3 mol percent propylene in the reactor gas to copolymerize with the ethylene. Liquid propene was added continuously at the rate of 30 milliliters/hour which maintained its concentration at 3 mol percent in the reactor gas. Copolymer was removed by way of a double ball-valved lock chamber attached to the take-off end of the reactor as particulate. Catalyst and cocatalyst were deactivated by treating the copolymer with 250°F. steam. A copolymer inhibitor package was added and the product thereof was melt extruded in the normal manner to form product pellets. Conditions of two such runs are shown in Table V below. 
     
                                           TABLE V                                 
__________________________________________________________________________
Run period         1   2   3  4   5A 5B 6  7  8  9   10 11                
__________________________________________________________________________
Time on stream, hours, minutes                                            
                   5,12                                                   
                       3   5,20                                           
                              4,22                                        
                                  3,8                                     
                                     3,8                                  
                                        6,37                              
                                           7,10                           
                                              6,55                        
                                                 4,22                     
                                                     3,15                 
                                                        2,45              
Temperature, °F                                                    
                   179 178 179                                            
                              177 178                                     
                                     178                                  
                                        180                               
                                           182                            
                                              186                         
                                                 185 207                  
                                                        207               
Total pressure, psig                                                      
                   300 300 300                                            
                              300 300                                     
                                     300                                  
                                        300                               
                                           300                            
                                              300                         
                                                 300 300                  
                                                        300               
Ave. catalyst, feedrate,                                                  
milligrams/hour    37.0                                                   
                       29.1                                               
                           30.9                                           
                              33.3                                        
                                  40.2                                    
                                     40.2                                 
                                        42 37 33.3                        
                                                 37.9                     
                                                     39.2                 
                                                        41.0              
*TEA/CAT           7.5 7.5 7.5                                            
                              7.5 7.5                                     
                                     15 7.5                               
                                           7.5                            
                                              7.5                         
                                                 15  15 7.5               
Recycle gas composition, mol percent                                      
Hydrogen           38  35  36 31  40 40 42 41 39 36  36 36                
Ethylene           52  44  52 61  48 48 41 46 50 55  52 52                
Ethane             6.6 20.5                                               
                           7.8                                            
                              4.2 8.6                                     
                                     8.6                                  
                                        12.6                              
                                           8.8                            
                                              7.0                         
                                                 5.1 8.3                  
                                                        8.3               
Propylene          2.3 3.2 3.2                                            
                              3.2 2.6                                     
                                     2.6                                  
                                        3.1                               
                                           2.9                            
                                              3.4                         
                                                 2.9 3.2                  
                                                        3.2               
Isopentane         1   1   1  1   1  1  1  1  1  1   1  1                 
Reactor bleedrate, cubic feet/hour                                        
                   0.87                                                   
                       0.86                                               
                           0.59                                           
                              0.61                                        
                                  0.69                                    
                                     0.69                                 
                                        0.63                              
                                           0.64                           
                                              0.63                        
                                                 0.62                     
                                                     0.59                 
                                                        0.59              
Polymer produced, grams                                                   
                   500 690 822                                            
                              1357                                        
                                  0  165                                  
                                        339                               
                                           1416                           
                                              1015                        
                                                 1764                     
                                                     754                  
                                                        348               
Catalyst yield, gram/grams                                                
                   2600                                                   
                       8000                                               
                           4980                                           
                              9320                                        
                                  0  620                                  
                                        1150                              
                                           5345                           
                                              4410                        
                                                 10,660                   
                                                     5915                 
                                                        3130              
Melt index, grams/10 minutes                                              
                   0.17                                                   
                       0.2 0.2                                            
                              0.17-  -- -- 6-7                            
                                              6-7                         
                                                 6- 7                     
                                                     6-7                  
                                                        6-7               
                              1.0                                         
Run period                                                                
Time on stream, hours, minutes                                            
                   4, 53                                                  
                       5, 15                                              
Temperature, °F                                                    
                   193 200                                                
Total pressure, psig                                                      
                   300 300                                                
Av. cat. feedrate, milligrams/hour                                        
                   40  28                                                 
TEA/CAT*           7.5 7.5                                                
Recycle gas comp., mol percent                                            
Hydrogen           44  42                                                 
Ethylene           45  46                                                 
Ethane             7.0 8.0                                                
Propylene          2.9 2.95                                               
Isopentane         1   1                                                  
Reactor bleedrate, cubic feet/hour                                        
                   0.62                                                   
                       0.67                                               
Polymer produced, grams                                                   
                   1055                                                   
                       1539                                               
Catalyst yield, grams/grams                                               
                   5375                                                   
                       8800                                               
Melt index, grams/10 minutes                                              
                   12-20                                                  
                       17-19                                              
__________________________________________________________________________
 *TEA/CAT is the weight ratio of triethylaluminum to catalyst used.       
 
    
     EXAMPLE VI 
     A supported titanium chloride catalyst and triethylaluminum cocatalyst were employed for the polymerization of ethylene in the same manner as Example I. Polymer was removed by way of a double ball-valved lock chamber as particulate. Catalyst was deactivated by treating with steam at 250°F. Polymer inhibitor package was added and the result thereof was melt extruded in the normal manner to form product pellets. Polymerization product conditions and properties of the various cuts are shown below in Tables VI and VII. 
     
                                           TABLE VI                                
__________________________________________________________________________
Polymerization Conditions                                                 
Temperature, Zone 1 °F                                             
                  180  160-205                                            
                             160-205                                      
                                   160-205                                
                                         160-205                          
                                               205                        
Zone 2 °F  175  160-205                                            
                             160-205                                      
                                   160-205                                
                                         160-205                          
                                               205                        
Exit port °F                                                       
                  165  170   170   170   170   170                        
Solvent reservoir 137  150   150   145   150   150                        
Pressure, psig    300  300   300   300   300   300                        
Reaction as composition, mol %                                            
Hydrogen          25   22    22    20    25    25                         
Ethylene          74   77    77    79    73    72                         
Ethane            0.2  0.3   0.3   0.2   0.4   0.9                        
Isopentane        1    1     1     1                                      
Reactor vent rate, cubit feet/hour                                        
                  0.67       0.67  0.67  1.92  1.05                       
Catalyst                                                                  
Feeder conc., milligrams/liter                                            
                  125  125   62.5  62.5  62.5  62.5                       
Feed rate, milligrams/hour                                                
                  31.9 25.2  10.6  8.7   11.9  4.85                       
Cocatalyst                                                                
AlE.sub.3 feeder conc., milli-                                            
grams/liter       1,250                                                   
                       1,250 625   625   625   625                        
AlEt.sub.3 feed rate, milli-                                              
grams/hour        319  252   106   87    119   485                        
Weight ratio AlEt.sub.3 /catalyst                                         
                  10   10    10    10    10    10                         
Polymerization Results                                                    
Total run time, hours                                                     
                  9.8  14.8  1.8   6.2   7.5   7.8                        
Total polymer produced, grams                                             
                  663  2,107 781   619   1,146 749                        
Polymer yield on catalyst,                                                
grams/gram        2,000                                                   
                       5,660 41,700                                       
                                   11,600                                 
                                         12,800                           
                                               19,700                     
Polymerization Conditions                                                 
Temperature, Zone 1 °F                                             
                  190  195   195   185   190   190                        
Zone 2 °F  189  192   190   182   186   190                        
Exit port °F                                                       
                  173  175   172   170   174   170                        
Solvent reservoir 152  152   152   152   156   140                        
Pressure, psig    300  300   300   300   300   300                        
Reaction gas composition, mol %                                           
Hydrogen          60   35    42    40    44    55                         
Ethylene          39   64    56    59    55    41                         
Ethane            0.3  0.6   0.6   0.4   3.0   0.4                        
Isopentane                                                                
Reactor vent rate, cubit feet/hour                                        
                  0.20 0.65  0.72  0.77  0.75  0.80                       
Catalyst                                                                  
Feeder conc., milligrams/liter                                            
                  62.5 125   80    62.5  31.2  40                         
Feed rate, milligrams/hour                                                
                  21.8 17.2  9.1   2.9   11.6  11.0                       
Cocatalyst                                                                
AlE.sub.3 feeder conc., milli-                                            
grams/liter       625  1,250 800   625   313   200                        
AlEt.sub.3 feed rate, milli-                                              
grams/hour        218  172   91    29    116   55                         
Weight ratio AlEt.sub.3 /catalyst                                         
                  10   10    10    10    7.5   55                         
Polymerization Results                                                    
Total run time, hours                                                     
                  20.9 7.5   2.5   5.8   6.5   22.9                       
Total polymer produced, grams                                             
                  52   366   429   3,335 2.05  3.077                      
Polymer yield on catalyst,                                                
grams/gram        --   2,830 19,240                                       
                                   204,000                                
                                         2,715 12,200                     
__________________________________________________________________________
 
    
     
                       TABLE VII                                                   
______________________________________                                    
                 Cuts 13-22                                               
                         Cuts 23-39                                       
______________________________________                                    
General Properties                                                        
Annealed density, g/cc                                                    
                   0.9734    0.9787                                       
Inherent viscosity, dl/g                                                  
                   1.99      1.28                                         
Melt index, MF.sub.1, g/10 min                                            
                   1.1       7.3                                          
Melt index, MF.sub.10, g/10 min                                           
                   35        234                                          
Flow rate ratio, MF.sub.10 /MF.sub.1                                      
                   32        32                                           
Hexane extractables, wt %                                                 
                   0.30      0.70                                         
Oven volatiles content, wt %                                              
                   0.04      0.33                                         
Stiffness, psig    137,000   179,000                                      
Tensile Properties                                                        
Tensile strength at yield, psig                                           
at 2 in/min        4,520     --                                           
Tensile strength at ultimate, psig                                        
at 2 in/min        2,940     4,850                                        
Elongation at yield, % at 2 in/min                                        
                   11        --                                           
Elongation at ultimate, % at 2 in/min                                     
                   1,100     9.9                                          
Impact Properties                                                         
Tensile impact strength, ft-lb/in.sup. 2                                  
                   82        22                                           
Izod impact strength, ft-lb/in.sup.2                                      
                   9.7       0.55                                         
Thermal Properties                                                        
Vicat softening point, °F                                          
                   263       259                                          
______________________________________                                    
 
    
     EXAMPLE VII 
     Propylene was polymerized in essentially the same manner described in EXAMPLE I. The recycle gas and quench liquid were propylene. The melter temperature was 350°F. while the catalyst kill section operated at 400°F. An active titanium chloride catalyst (35 milligrams) with diethylaluminum chloride cocatalyst (77 milligrams), mol ratio Al/Ti = 3, was charged to the reactor every thirty minutes. Hydrogen was added as needed to maintain 2.9 mol percent in the reactor gas cap. The reactor temperature was maintained at 160°F. and the reactor pressure was controlled at 300 psig by maintaining the temperature of the recycle condenser at about 120°F. A polymer yield based on catalyst of 10,000 grams/gram was obtained. The polymer was removed from the reactor as a melt. The polymer showed a melt flow rate of 16.4 grams/10 minutes at 230°C. under a load of 2,060g. The 68°C. n-hexane extractables was 4.0 weight percent. Physical properties of the product are shown in Table VII. 
     EXAMPLE VIII 
     Ethylene was polymerized in the same manner described in EXAMPLE I except in this case two sections of the reactor were maintained at different temperatures. Reactor section one was operated at 160°F. while reactor section two was operated at 210° to 230°F. This was accomplished by varying the amount of isopentane quench added to each section. The catalyst used was a supported titanium compound and an aluminum triethyl cocatalyst was added in a weight ratio of cocatalyst to catalyst of three to one. The reactor pressure was controlled at 300 psig. and the hydrogen concentration was maintained at 40 mol percent. A polymer yield of 62,000 grams of polymer/gram of catalyst was obtained. The polymer melt index was measured at 5.5 with a MF 10  /MF 1  of about 40 and a spiral flow of 18 inches. Polymer made under single temperature conditions having the same M.I. showed an MF 10  /MF 1  value of about 34 and demonstrated a spiral flow of about 16 inches. 
     Spiral flow is an empirical method of assessing ease of processability of a polymer by measuring the length of flow in a special mold under specified temperature and pressure conditions. The longer the spiral flow the easier is the processability.