Polythiol accelerated radiation crosslinking of olefinically unsaturated allylically halogenated polymers
CROSS REFERENCE TO RELATED APPLICATIONS 
     This is a continuation of application Ser. No. 531,628, filed Dec. 11, 1974 now abandoned which is a continuation-in-part of U.S. application Ser. No. 232,275 filed Mar. 6, 1972 now U.S. Pat. No. 3,864,229. 
    
    
     BACKGROUND OF THE INVENTION 
     Radiation curing of polymers is well known in the art. Though difficulties have been encountered in radiation curing or vulcanizing of polymers, improved results have been obtained by the use of additives. For example, in the case of polyethylene, it has been demonstrated that the addition of unsaturated polyfunctional monomers will produce comparable cross-link densities at reduced dose levels, in contrast to the radiation of ordinary polyethylene. 
     It is well known that polymers such as polyisobutylene are effectively destroyed when exposed to ionizing radiation. See for example, &#34;Calorimetric Study of Radiation Crosslinking of Polyisobutylene In The Presence of Monomer Additives,&#34; Dokl. Akad, Nauk SSSR (Phys. Chem.) 193 (4), 855-857 (1970). The addition of small amounts of polyfunctional monomers such as p-divinylbenzene causes effective crosslinking of polyisobutylene as does the addition of acrylonitrile to polyisobutylene blends. Allyl acrylate has also been found to cause crosslinking of polyisobutylene under ionizing radiation conditions, see for example Polymer Letters, 2, pages 819-821 (1964). Although crosslinking does occur, degradation of the polyisobutylene results even in the presence of the allyl acrylates or allyl methacrylates at higher dose levels, e.g., above about 0.8 megarads. 
     Butyl rubber being substantially polyisobutylene also, not surprisingly, has been found to degrade in the presence of ionizing radiation. 
     The use of dithiols in the conventional curing of polymers is well known in the art. For example, the heat curing of a cellulose methacrylate derivative with simple dithiols is disclosed in British patent 588,018. Sulfur vulcanization of styrene butadiene is accelerated by the addition of bis-mercaptophenyl diphenyl oxide (see, for example, U.S. Pat. No. 3,326,822). Chlorinated butyl rubber has been vulcanized with dithiols. See, for example, Hodges, Rubber Plastics Weekly 141 pages 666-668 (196) wherein glycol dimercapto acetate is recommended because of its low odor. 
     Elastomers have been prepared from long-chain dithiols with long-chain diolefins using as the cross-linking agent triolefin or long-chain trithiols; see, for example, Klotz et al, I and EC Product Research and Development 7, pages 165-169 September (1968). 
     In the present invention, it was surprisingly found that butyl type polymers containing allyic chlorine or bromine are radiation crosslinked rather than degraded in the presence of polythiolds. In such cures, polythiols are unexpectedly more effective than dithiols. In contrast to the clean dithiol cure via addition of polydiene elastomers, the curing method of the present allylically halogenated elastomers, in the presence of polythiols, involves hydrogen halide elimination to a major extent. 
     SUMMARY OF THE INVENTION 
     It has been found that the crosslinking of certain olefinically unsaturated polymers by ionizing radiation is surprisingly accelerated by minor amounts of polythiols. As unsaturated polymers, macromolecules having olefinic bonds in excess of 15 mole percent or allylic halogens above 0.5% mole, are suitable for this method of crosslinking. The preferred polymers of this invention are elastomeric polymers. Typical examples of suitable elastomers are styrene-butadiene rubber (SBR) and Chlorobutyl. The preferred polythiol accelerators are hydrocarbon polythiols, particularly aliphatic thioether polythiols, having on the average more than three thiol groups per molecule. 
     DETAILED DESCRIPTION OF THE INVENTION 
     This invention relates to a method of radiation crosslinking of olefinically unsaturated polymers, particularly elastomers such as halogenated butyl rubber polybutadiene and styrene butadiene rubber (SBR), which comprises incorporating into the elastomer composition polythiol accelerator and/or crosslinking agent. In particular, this invention relates to the improvement in radiation vulcanization of unsaturated elastomers by polythiols having an average of at least three thiol groups and is normally liquid at room temperature having a molecular weight of at least 150 and preferably less than 3,000. More preferably, the polythiol is normally liquid at ambient temperatures. 
     The improved radiation curing process of this invention is applicable to any olefinically unsaturated polymer which preferably has a molecular weight in excess of 1,500, more preferably in excess of 10,000, and most preferably in excess of 50,000. These polymers contain (1) at least 15 mole % unsaturation, or (2) at least 0.5 mole % halogen in the allylic position, e.g. chlorine, bromine. Elastomers having a number average molecular weight (M n ) of at least 50,000 are preferred. Both types of functionality may be present in the same polymer. For example, halogenated conjugated dienes, polymers and copolymers, e.g. polychloroprene, contain both the requisite levels of unsaturation and the allylic halogen. 
     As it is generally defined, the allylic halogen in the present elastomers may be bound to a primary, secondary or tertiary allylic carbon, i.e. a carbon next to an olefinically unsaurated carbon: ##STR1## 
     In most halogen-containing elastomers having olefinic substitution, secondary and tertiary allylic halogen structures are more prevalent than primary structures. This is exemplified by polychloroprene wherein the predominant reactive crosslinking unit is the tertiary allylic chlorine from 1,2 polymerization of chloroprene. ##STR2## 
     The secondary and tertiary allylic halide groups may occur in the main polymer chain, e.g. in the case of Chlorobutyl most of the chlorine is in unit I and some of it is in unit II. ##STR3## 
     Surprisingly, when conventional butyl rubber is halogenated to Chlorobutyl or Bromobutyl, it can be readily cured by the method of the present invention. 
     The term &#34;butyl rubber&#34; as employed in the specification and claims is intended to include copolymers made from the polymerization of reactant mixtures having therein about 70 to about 99.5 percent by weight of an isoolefin which has about 4 to 7 carbon atoms, e.g., isobutylene, and about 0.5 to 30 percent by weight of a conjugated multiolefin having about 4 to about 14 carbon atoms, e.g., isoprene, piperylene, cyclopentadiene, etc. The resulting copolymer contains 85 to 99.8 percent by weight of combined isoolefin, and about 0.5 to about 15 percent of combined multiolefin. Butyl rubber generally has a Staudinger molecular weight of about 20,000 to about 500,000, preferably about 25,000 to about 400,000, especially about 100,000 to about 400,000, Wijs Iodine Number of about 0.5 to about 50, preferably about 1 to about 15. 
     The preparation of butyl rubber is described in U.S. Pat. No. 2,356,128 which is incorporated herein by reference. 
     For the purposes of this invention, the butyl rubber may have incorporated therein about 0.2 to about 10 mole percent of combined multiolefin, preferably about 0.5 to about 6 percent, more preferably about 1 to about 4 percent, e.g., 2 percent. Illustrative of such a butyl rubber is Exxon Butyl 268 (Exxon Chemical Company) having viscosity average molecular weight of about 450,000, a mole percent unsaturation of about 1.5% and a Mooney viscosity of about 55° at 260° F. 
     Halogenated butyl rubber is commercially available and may be prepared by halogenating butyl rubber in a solution containing about 1 to about 60 percent by weight of butyl rubber in a substantially inert C 5  -C 8  hydrocarbon solvent, such as pentane, hexane, heptane, etc., and contacting this butyl rubber cement with a halogen gas for a period of about 0.5 to about 25 minutes, whereby halogenated butyl rubber and a hydrogen halide are formed; the copolymer containing up to 1 halogen atom per double bond in the copolymer. 
     The preparation of halogenated butyl rubber is old in the art, see for example U.S. Pat. No. 3,099,644 which is incorporated herein by reference. This invention is not intended to be limited in any way by the manner in which butyl rubber is halogenated, and both chlorinated and brominated butyl rubber are suitable for use in this invention. 
     Illustrative of halogenated butyl rubbers is Exxon Butyl HT-10-66, a chlorinated butyl rubber containing about 1.3 weight percent chlorine having about 1.7 mole percent unsaturation and a viscosity average molecular weight of about 357,000. 
     Styrene butadiene rubber (SBR) is well known to the art. Typically these polymers contain about 5 to about 40 weight percent of styrene and have a Wijs Iodine Number of about 300 to about 5,000 and a number average molecular weight of about 30,000 to about 600,000, preferably about 100,000 to about 150,000. The polymer may be prepared either by the bulk polymerization of styrene and butadiene or polymerization of the rubber in a latex form by emulsion polymerization, a suspension polymerization. This invention is in no way intended to be limited by the method of preparation of the styrene-butadiene rubber. 
     Polybutadiene is well known in the art and may be prepared in various ways including lithium catalysis of butadiene. Illustrative examples of polybutadiene are: Firestone Diene 55 having 45% 1,4 cis enchainment, 45% 1,4 trans enchainment and 10% 1,2 vinyl pendant groups; Phillips&#39; Cis 4 having 92% 1,4 cis, 2% 1,2 adduct of butadiene and some 1,4 trans enchainment. 
     Other elastomers suitable for use in the practice of this invention include polychloroprene and acrylonitrile-butadiene copolymers. 
     The elastomers suitable for use in the practice of this invention preferably have a M n  of at least 50,000, more preferably at least 100,000, most preferably at least 120,000. 
     Any polythiol having at least two preferably three thiol groups which has a molecular weight of at least 150, may be used in the practice of this invention, assuming that it has no groups other than SH which are sensitive to radiation. Although the polythiol structure may include other atoms besides carbon, hydrogen, and sulfur; e.g., nitrogen, or oxygen in the form of amides, ethers, esters, etc., the preferred polythiols are hydrocarbon polythiol oxy and thioethers. The preferred polythiols have a molecular weight of about 150 to about 3,000 and have at least 2, preferably about 3 to about 5 thiol groups per molecule; more preferably, about 200 to about 1,000: most preferably about 250 to about 400. Hydrocarbon thioether polythiols which are most preferred in general contain one, two, three or more thioether groups. The number of thioether groups is about 1 to 100, preferably 1 to 25, more preferably 1 to 10, most preferably 1 to 5. The number of thioether groups is limited by economic considerations since these polythiols are used on an equivalent thiol basis. These cure enhancers are incorporated in the polymer at about 0.5 to about 6 parts per hundred (phr) by weight of the rubber, more preferably about 1 to about 3 phr. 
     Useful dithiols are hydrocarbon dithiols such as dodecane dithiol, dipentene dimercaptan, vinyl cyclohexene dimercaptan. Such dithiols are generally prepared by reacting a large excess of hydrogen sulfide with a diolefin or acetylene. 
     More preferred dithiols are thioether dithiols such as those derived by the reaction of excess hydrogen sulfide or dithiols with diunsaturates, such as ethylene diarcylate and methylacetylene. 
     Even more preferred are trithiols such as hydrocarbon trithiols exemplified by triallyl cyanurate trimercaptan, triacryloyl triazine trimercaptan, cyclodecatriene trimercaptan, trivinyl cyclohexane trimercaptan, vinyl butyl acetylene trimercaptan. Such trithiols are prepared by reacting a very large excess of hydrogen sulfide with a triunsaturated compound. 
     Also highly preferred are polythiols containing more than three thiol groups such as a low molecular weight polybutadiene polymercaptan. 
     Most preferred are thioether trithiols, tetrathiols and pentathiols. Such compounds are prepared, by the addition (preferably in an anti-Markovnikov manner) of excess hydrogen sulfide and excess dithiols to trienes and polyenes. Especially preferred species are derived by the addition of H 2  S and C 2  to C 14  alkylene dithiols to C 9  to C 20  trienes, especially trivinyl compounds, for example, triterminal trienes such as trivinyl cyclohexane. Such adducts have 3 to 5 thiol groups on the average. The preparation of such polythiols and polythioether polythiols is described in U.S. Pat. No. 3,625,925 by Oswald et al. 
     Illustrative examples of the polythioether polythiols are the reaction product of trivinylcyclohexane and 1,3-propanedithiol, which has the general formula ##STR4## trimethylol propane tris-thiolglycoate, pentaerythritol tetra-3-mercaptopropionate, pentaerythritol tris-3-mercaptopropionate, the reaction product of cyclodedecatriene and 1,3-propanedithiol, which is a mixture of thioether thiols having the general formula ##STR5## such as trimethylol propane tris-mercaptoacetate, the reaction product of H 2  S and/or dithiols with polyepoxides. See U.S. Pat. No. 3,625,925 incorporated herein by reference for other suitable polythiols and their method of preparation. 
     The term &#34;radiation&#34; as used in the specificaand claims includes light of different wavelengths, α- and β-irradiation and heat irradiation. 
     The preferred &#34;ionizing radiation&#34; as used in the specification and claims is intended to include gamma radiation and electron beam (β-ray) irradiation. 
     The Co 60  gamma radiation source referred to in the Examples of this specification is a 2,900 Curie source (1.2 Mev). Electron beam irradiation was produced from a Dynamitron. For a description of this equipment, see Harmer and Ballentine, &#34;Radiation Processing&#34;, Chemical Engineering, pages 98-116 (Apr. 19, 1971). Although gamma radiation has greater penetrating power than electron beams, this characteristic was not a factor in these experiments since the test samples were 100 mil sheets or less. Where significant differences occur between the results from Co 60  and electron beam irradiation, it is attributable to differences in dose rate, the former at 0.01 megarad/minute and the latter at 30 megarad/minute. 
     The olefinically unsaturated polymers of this invention may be sulfur vulcanized subsequent to radiation curing. The radiation precure has process advantages where handling of shapes on sheets is necessary prior to vulcanization. Sulfur vulcanization may be carried out using free sulfur and accelerators or in the absence of free sulfur using sulfur donors. The term &#34;sulfur vulcanized&#34; means vulcanization using either free sulfur or sulfur donors. Both methods of sulfur vulcanization are well known to the art and are discussed in detail in Chapters 2 and 3 of Vulcanization and Vulcanizing Agents, W. Hofmann, Palmerton Publishing Col, New York (1967) incorporated herein by reference. 
     Illustrative examples of accelerators which may be used in the sulfur cure of polymers of this invention are dithiocarbamates, xanthates, thiurams, thiazoles, aldehyde-amine accelerators and basic accelerators such as guanidine accelerators. Specific examples of these accelerators are zinc dimethyl dithiocarbamate, zinc diethyl dithiocarbamate, ammonium-N&#39;-pentamethylene dithiocarbamate, tellurium diethyl dithiocarbamate, sodium isopropyl xanthate, zinc butyl xanthate, tetramethyl thiuram monosulfide, tetraethyl thiuram disulfide, dimethyl diphenyl thiuram disulfide, 2-mercapto-benzothiazole, etc. 
     The advantages of the instant invention may be more readily appreciated by reference to the following examples. 
    
    
     EXAMPLE 1 
     A polythioether polythiol, formed by the reaction product of trivinylcyclohexane and 1,3-propane dithiol was used as the vulcanizing crosslinking agent. This compound has the general formula ##STR6## The calculated molecular weight of the polythiol is 912, but the actual molecular weight determined by vapor pressure osmometry was 818. This product was designated E2323 III. It contains .0049 mole equivalents of SH per gram. 
     The polythiol was compounded with SBR and natural rubber (NR) according to the formulations shown in Table I. 
     
                       TABLE I                                                     
______________________________________                                    
POLYTHIOETHER POLYTHIOL IN SBR                                            
AND NATURAL RUBBER                                                        
Component   1        2      3    4    5    6                              
______________________________________                                    
SBR 1502.sup.(2)                                                          
            100.sup.(1)                                                   
                     100    100                                           
Natural Rubber                   100  100  100                            
Zinc Oxide  5        5      5    5    5    5                              
Stearic Acid                                                              
            1        1      1    1    1    1                              
E2323 III   --       2.3    4.6  --   2.3  4.6                            
Moles SH/Gram                                                             
            --       0.011  0.022                                         
                                 --   0.011                               
                                           0.022                          
Elastomer                                                                 
______________________________________                                    
 .sup.(1) Emulsion polymerized at 50° F comprising about 23.5%     
 styrene having a Mooney Viscosity at 212° F of 52.                
 .sup.(2) All amounts as parts per hundred of elastomers by weight.       
 
    
     It was observed in other radiation curing experiments that the presence of zinc oxide provided an added accelerating effect to that of the polythiol. Thus, the control compounds in both elastomer blends contain this ingredient. Sample compounds were molded at 175° F for five minutes to form a 0.025 inch film protected with Mylar; prior to radiation all samples were soluble in cyclohexane. Samples were then exposed to electron beam radiation at 30 megarads per minute for 2.5, 5, 10, and 15 MR. Network properties were determined by volume swelling in cyclohexane and converted to the parameters of Mc and XL/cc, wherein Mc is Molecular weight between crosslinks and XL/cc is crosslinks per cc. The results are shown in Table II. 
     
                       TABLE II                                                    
______________________________________                                    
Effect of Electron Beam Exposure                                          
Physical                                                                  
Properties                                                                
at Electron Beam                                                          
            SBR           NR                                              
Exposure of:                                                              
            1       2      3    4     5     6                             
______________________________________                                    
0 Megarads          Solu-             Solu-                               
                    ble               ble                                 
2.5 MR                                                                    
% Vol. Increase     443    328        Loose                               
                                      Gel                                 
% Soluble   Loose   10.4   9.2                                            
Mc × 10.sup.-3                                                      
            Gel     9.2    6.0                                            
XL/cc × 10.sup.-19                                                  
                    2.69   4.42                                           
(Orig. Pol. Vol.)                                                         
5 MR                                                                      
% Vol. Increase                                                           
            2300    316    242  Loose 2765  2420                          
% Soluble   40      7.7    7.0  Gel   26.3  24.6                          
Mc × 10.sup.-3                                                      
            110     5.6    3.9        135   102                           
XL/cc × 10.sup.-19                                                  
            .14     4.63   6.7        .16   .20                           
10 MR                                                                     
% Vol. Increase                                                           
            949     279    202  1940  1078  1006                          
% Soluble   19.6    7.0    6.3  20.1  11.7  11.4                          
Mc × 10.sup.-3                                                      
            29      4.7    2.9  .78   32    29                            
XL/cc × 10.sup.-19                                                  
            0.76    5.48   8.9  .30   .81   .89                           
15 MR                                                                     
% Vol. Increase                                                           
            595     251    187  1170  752   716                           
% Soluble   12.8    6.5    5.9  12.1  7.9   8.0                           
Mc ×  10.sup.-3                                                     
            14.2    4.0    2.7  36    18    16.5                          
XL/cc × 10.sup.-19                                                  
            1.68    6.53   9.71 .71   1.47  1.57                          
______________________________________                                    
 
    
     The effect of the polythiol on the radiation induced crosslinking of SBR is extremely great at the levels used. This can be noted especially at the lower levels of radiation dose wherein % volume increase, % soluble and Mc are all markedly lower, and crosslinked densities are manyfold greater. This is evident also at higher dose levels. The emulsion polymerization of butadiene would be random in nature with considerable 1,2 addition resulting in very reactive pendant vinyl groups. The effect with natural rubber is much less pronounced but still evident on the basis of swelling derived network parameters. Generated crosslink densities are increased 2 to 3 fold at the higher dose levels of 10 and 15 MR while displaying evidences of network formation at the 5 MR level. The control composition 4 has not formed a desirable network at this point. This lower reactivity or response to the polythiol is a reflection of the substituted internally unsaturated isoprenoid structure of cis-polyisoprene. 
     EXAMPLE 2 
     Chlorinated butyl rubber under radiation tends to quickly reach a crosslinking limit where further radiation begins to promote chain scission. It is also dose rate sensitive so that as the rate of energy absorption is increased, reaction selectivity is shifted from crosslinking to chain scission. In contrast to more highly unsaturated general purpose elastomers, a mild radiation procedure of a compounded formulation detracts from a subsequent thermal curing process. The radiation-induced crosslinking of chlorinated butyl rubber can be greatly enhanced by small amounts of polythioether polythiols as illustrated by the following experiments. 
     The polythiol used is the reaction product of cyclododecatriene and 1,3 propane dithiol, designated E1255 VII. The polythiol is a mixture of the following compounds: ##STR7## the molecular weight of the mixture by Vapor Pressure Osmometry was found to be 578. For purposes of compounding, the functionality per unit weight was based on VPO molecular weight of 578 or approximately .005 SH/gm. See U.S. Pat. No. 3,625,925 incorporated herein by reference for methods of preparing this polythiol. The glycol dimercapto acetate has a functionality of 0.0095 SH/gm. Table III shows blends prepared for a comparison of E1255 VII and the glycol dimercapto acetate in the radiation crosslinking of chlorinated butyl rubber. 
     
                       TABLE III                                                   
______________________________________                                    
                1    2       3       4                                    
______________________________________                                    
Chlorinated butyl rubber.sup.(1)                                          
HT 10-68          100    100     100   100                                
Zinc Oxide        --     5       5     5                                  
Glycol Dimercapto Acetate        2                                        
El255 VII                              2                                  
______________________________________                                    
 .sup.(1) chlorinated butyl rubber of about 450,000 viscosity average     
 molecular weight having 1.3 weight % chlorine and 1.7 mole % unsaturation
                                                                          
 
    
     The chlorinated butyl rubber used has approximately .032 equivalent Cl functionality per 100 grams. Two grams of E1255 VII polythiol is the equivalent to the addition of 0.01 SH groups per 100 grams of chlorinated butyl rubber. One hundred grams of chlorinated butyl rubber contain 0.032 allylic chlorine groups. 
     The compounds of Table III were molded as 0.025 inch at 200° F. for 5 minutes between mylar film and exposed to Cobalt 60 radiation for various time periods. After exposure, the film was subjected to solvent swelling analysis in a cyclohexane to determine the extent of crosslinking. The results are tabulated in Table IV. 
     
                       TABLE IV                                                    
______________________________________                                    
SWELLING IN CYCLOHEXANE AT ROOM                                           
TEMPERATURE AS A FUNCTION OF MEGARAD                                      
DOSE (MR), CO.sup.60 IRRADIATION                                          
Physical Properties                                                       
after Co.sup.60 1       2       3     4                                   
______________________________________                                    
0 MR (Megarads) Solu-   Solu-   Solu- Solu-                               
                ble     ble     ble   ble                                 
4.3 MR                                                                    
 % Vol. Increase                      607                                 
 % Soluble                            3.7                                 
 Mc × 10.sup.-3 (Gel)           14.2                                
 XL/cc × 10.sup.-19 (Orig.      1.87                                
  Volume Basis)                                                           
5.5 MR                                                                    
 % Vol. Increase                                                          
                1322    1339    1162  516                                 
 % Sol.         10.4    8.8     9.6   3.7                                 
 Mc × 10.sup.-3                                                     
                50      54      41    10.8                                
 XL/cc × 10.sup.-19                                                 
                0.51    0.50    0.64  2.45                                
10.5 MR                                                                   
 % Vol. Increase                                                          
                970     870     854   470                                 
 % Sol.         9.8     8.0     7.8   4.3                                 
 Mc × 10.sup.-3                                                     
                30      25.5    24.5  8.6                                 
 XL/cc × 10.sup.-19                                                 
                0.78    1.02    1.07  2.83                                
15.2 MR                                                                   
 % Vol. Increase                                                          
                810     740     751   444                                 
 % Sol.         10.6    7.4     8.2   4.3                                 
 Mc × 10.sup.-3                                                     
                22.5    19.5    20    8.6                                 
  XL/cc × 10.sup.-19                                                
                1.11    1.32    1.29  3.1                                 
______________________________________                                    
 
    
     A comparison of columns 1 and 2 shows that zinc oxide has a very mild activating effect upon the radiation-induced crosslinking of chlorinated butyl rubber. The presence of glycol dimercapto acetate provides little or no additional benefit (column 3). On the other hand, the addition of E1255 VII polythiol (column 4) provides a marked enhancement or radiation-induced crosslinking. By any criterion: lower volume swelling, soluble polymer, molecular weight Mc or crosslinked density (XL/cc), the polythioether polythiol has a marked accelerating effect. On the basis of crosslinks formed, it provides about a threefold increase over the control of column 2 and an increase of about 21/2 times over the dimercaptan of column 3. 
     EXAMPLE 3 
     In order to study the concentration effect of E1255 VII polythiol of Example 2 on radiation curing, samples were prepared in the manner of Example 2 at various polythiol concentrations. The samples were molded at 175° F. for 5 minutes. The formulations are shown in Table V. 
     
                       TABLE V                                                     
______________________________________                                    
VARIATION IN E1255 VII CONCENTRATION                                      
             0    1      2      3    4    5                               
______________________________________                                    
Chlorinated butyl rubber                                                  
 HT-10-68      100    100    100  100  100  100                           
Zinc Oxide     --     5      5    5    5    5                             
Stearic Acid   --     1      1    1    1    1                             
E1255 VII      --     --     0.5  1.0  2.0  4.0                           
______________________________________                                    
 Note:                                                                    
 All samples were soluble in cyclohexane before irradiation.              
 
    
     The results of Cobalt 60 exposure are tabulated in Table VI. 
     
                       TABLE VI                                                    
______________________________________                                    
Co.sup.60 Radiation                                                       
at .01 MR/min.                                                            
Network Properties from Volume                                            
Swelling - Cyclohexane                                                    
Dose           0       1       2     3    4                               
______________________________________                                    
4.7 MR                                                                    
 % Vol. Increase                                                          
               1138    1203    1040  843  511                             
 % Sol.        13      11.6    11.6  7.9  3.8                             
 Mc × 10.sup.-3 (Gel)                                               
               39      43      34    24.5 10.5                            
 XL/cc × 10.sup.-19                                                 
               .64     .58     .72   1.09 2.45                            
  (Orig. Pol. Vol.)                                                       
10.5 MR                                                                   
 % Vol. Increase                                                          
               915     763     720   624  447                             
 % Sol.        10.3    8.0     8.0   6.8  4.4                             
 Mc × 10.sup.-3                                                     
               27      20      18.5  15   8.2                             
 XL/cc × 10.sup.-19                                                 
               .94     1.26    1.38  1.73 3.08                            
15.3 MR                                                                   
 % Vol. Increase                                                          
               727     645     654   566  406                             
 % Sol.        11.6    8.0     8.0   7.2  5.0                             
 Mc × 10.sup.-3                                                     
               19      15.6    15.8  12.5 7.2                             
 XL/cc × 10.sup.-19                                                 
               1.31    1.61    1.59  2.06 3.51                            
______________________________________                                    
 
    
     There is a progressive crosslinking response to the chlorinated butyl rubber system toward radiation as the amount of polythiol is increased. Volume swelling, soluble polymer and Mc between crosslinks all drecrease at any given megarad dose level. The generated crosslinked density is increased about 3 to 4 times over the control column 1 at the highest concentration of polythiol. 
     EXAMPLE 4 
     The effects of polythioether polythiol E1255 VII on the electron beam irradiation response of chlorinated butyl rubber was evaluated by repeating the experiments of Example 3, substituting electron beam irradiation for Cobalt 60 radiation. The results are shown in Table VII. 
     
                       TABLE VII                                                   
______________________________________                                    
EFFECT OF POLYTHIOETHER POLYTHIOL (E1255 VII)                             
IN INCREASING QUANTITIES ON THE ELECTRON                                  
BEAM IRRADIATION RESPONSE OF                                              
CHLORINATED BUTYL RUBBER                                                  
Component       0      1      2    3    4    5                            
______________________________________                                    
Chlorinated butyl                                                         
               100    100    100  100  100  100                           
Rubber HT-10-68                                                           
Zinc Oxide     --     5      5    5    5    5                             
Stearic Acid   --     1      1    1    1    1                             
E1255 (VII)    --     --     0.5  1.0  2.0  4.0                           
______________________________________                                    
 Note: All samples were soluble in cyclohexane before irradiation.        
 
    
     
         Electron Beam                                                             
at 30 MR/Min.                                                             
Network Properties from Volume                                            
Swelling - Cyclohexane                                                    
Physical Properties                                                       
after electron beam                                                       
irradiation at:                                                           
                0      1      2    3    4    5                            
______________________________________                                    
5.2 MR                                                                    
% Vol. Increase                                                           
               1830   1745   1496 1280 737  520                           
% Soluble      15.5   14.0   12.3 11.7 6.9  6.6                           
Mc × 10.sup.-3 (Gel)                                                
               83     76     61   46   19.5 11.0                          
XL/cc × 10.sup.-19                                                  
               0.29   0.33   .41  .55  1.35 2.34                          
(Orig. Pol. Vol.)                                                         
9.8 MR                                                                    
% Vol. Increase                                                           
               1270   1182   1085 978  615  435                           
% Soluble      18.9   15.7   16.2 13.9 9.2  7.2                           
Mc × 10.sup.-3                                                      
               47     42     36   31   14.4 8.1                           
XL/cc × 10.sup.-19                                                  
               .50    .59    .67  .79  1.78 3.07                          
15 MR                                                                     
% Vol. Increase                                                           
               1121   970    923  792  562  423                           
% Soluble      17.2   14.3   14.2 13.3 8.7  7.8                           
Mc × 10.sup.-3                                                      
               39     30     28   21.5 12.2 8.3                           
XL/cc × 10.sup.-19                                                  
               0.62   0.79   0.86 1.13 2.06 3.17                          
______________________________________                                    
 
    
     It is evident that the presence of the polythioether polythiol promotes gelation and retards chain scission. 
     EXAMPLE 5 
     A comparison of various polythiols was made using the polythiols shown in Table VIII. 
     
                                           TABLE VIII                              
__________________________________________________________________________
POLYTHIOETHER POLYTHIOLS DERIVED FROM TRIENE-DITHIOL                      
POLY ADDITIONS DESCRIBED IN U.S. PAT. APPL. SER. NO. 665,728              
Polythiol                                                                 
      Mol. Wt.                                                            
             Thiol Funct.                                                 
Ref. No.                                                                  
      Calc.                                                               
         Found                                                            
             Calc.                                                        
                Found                                                     
                      Chemical Structure and Derivation                   
__________________________________________________________________________
E1255 VII                                                                 
      487                                                                 
         578 3  2.8                                                       
                     ##STR8##                                             
E1221 VIII                                                                
      494                                                                 
         500 4  --                                                        
                     ##STR9##                                             
E1260 VI                                                                  
      796                                                                 
         897 4  --                                                        
                     ##STR10##                                            
E1262 VII                                                                 
      529                                                                 
         728 3  --                                                        
                     ##STR11##                                            
E1263 VII                                                                 
         1698                                                             
             2                                                            
                     ##STR12##                                            
                    and 1,4-butane dithiol.                               
__________________________________________________________________________
 .sup.(1) Polythioether derived from methylacetylene and 1,4-butane       
 dithiol, the preparation of which is described in U.S. 3,592,798         
 incorporated herein by reference.                                        
 .sup.(2) Method for preparing these polythiols are taught in U.S. Pat.   
 3,625,925 incorporated herein by reference.                              
 
    
     In addition to the polythiols of Table VIII, the Thiokol liquid polysulfide dithiol rubber LP3 was also evaluated. This rubber had a specification molecular weight of 1,000 and a wt. % mercaptan range of 5.9 to about 7.7 (average 6.8). This is equivalent to .002 SH groups per gram compared to 0.005 SH groups per gram of E1255 VII. Samples were prepared in the manner of Example 4, the polythiols being incorporated in the compositions at equivalent SH functionality. The compositions and the effect of Cobalt 60 radiation on these compositions is shown in Table IX. 
     
                                           TABLE IX                                
__________________________________________________________________________
          1  2    3  4  5  6  7  8  9                                     
__________________________________________________________________________
Chlorinated butyl                                                         
rubber    100                                                             
             100  100                                                     
                     100                                                  
                        100                                               
                           100                                            
                              100                                         
                                 100                                      
                                    100                                   
Zinc Oxide                                                                
          5  5    5  5  5  5  5  5  5                                     
Stearic Acid                                                              
          1  1    1  1  1  1  1  1  1                                     
E1255 VII -- 2    4                                                       
E1221 VIII           1.3                                                  
                        2.6                                               
E1260 VI                   2.3                                            
E1262 VII                     2.5                                         
E1263 VIII                       9.4                                      
Thiokol LP3                         5.0                                   
0 Megarad - 100%                                                          
          Sol.                                                            
             Sol. Sol.                                                    
                     Sol.                                                 
                        Sol.                                              
                           Sol. Sol.                                      
                              Sol.                                        
                                 Sol.                                     
Co.sup.60 Irradiation                                                     
          0.01                                                            
             MR/min.                                                      
XL/cc × 10.sup.-19                                                  
 4.2 MR   0.5                                                             
             2.30    2.02  1.68                                           
                              1.70                                        
                                 0.75                                     
                                    1.0                                   
 7.5 MR              2.53           1.30                                  
 9.4 MR   1.15                                                            
             2.92          2.59                                           
                              2.27                                        
                                 1.38                                     
12.4 MR   1.40                                                            
             3.25    3.26  3.0                                            
                              2.51                                        
                                 1.67                                     
                                    1.82                                  
Irradiation by the                                                        
Electron Beam                                                             
          30 MR/min.                                                      
XL/cc × 10.sup.-19                                                  
 5 MR     0.31                                                            
             1.35 2.34                                                    
                     1.22                                                 
                        2.14                                              
                           0.66                                           
                              0.72                                        
                                 0.52                                     
                                    0.43                                  
10 MR     0.60                                                            
             1.80 3.07                                                    
                     1.61                                                 
                        3.05                                              
                           1.27                                           
                              1.18                                        
                                 0.84                                     
                                    0.79                                  
15 MR     0.77                                                            
             2.0  3.17                                                    
                     1.92                                                 
                        3.94                                              
                           1.70                                           
                              1.46 1.12                                   
                                 0.88                                     
__________________________________________________________________________
 
    
     It is evident that the presence of polythioether polythiols increase the crosslinking response of chlorinated butyl rubber three- to fourfold. The tri- and tetrathiols are superior to the dithiol represented by E1263 VIII. The tetra functional E1221 VIII as shown in columns 4 and 5 is especially noteworthy because of its ability to promote the crosslinking response at quite low concentration levels. The commercial Thiokol rubber has only a mildly activating effect under Cobalt 60 radiation which appears to be further reduced under the higher dose rates of the electron beam. 
     EXAMPLE 6 
     The polythioether polythiols of this invention will promote the radiation crosslinking of chlorinated butyl rubber in the absence of zinc oxide and stearic acid as demonstrated by the results in Table X. 
     
                       TABLE X                                                     
______________________________________                                    
Component.sup.(1)                                                         
               1         2         3                                      
______________________________________                                    
Chlorinated butyl                                                         
rubber HT 10-68                                                           
               100       100       100                                    
Zinc Oxide     --        5         5                                      
Stearic Acid   --        1         1                                      
E1255 VII      2         2         --                                     
Crosslinked density after Co.sup.60 and electron                          
beam exposure is expressed as XL/cc × 10.sup.-19                    
on the basis of the original polymer volume.                              
Co.sup.60 Radiation                                                       
 4.2 MR        2.54      2.30      .5                                     
 9.4 MR        2.47      2.92      1.15                                   
12.4 MR        2.41      3.25      1.40                                   
Electron Beam                                                             
 5 MR          1.50      1.35      0.3                                    
10 MR          1.63      1.80      0.6                                    
15 MR          1.63      2.10      0.77                                   
______________________________________                                    
 .sup.(1) Parts per 100 parts of elastomer by weight.?                    
 
    
     Although zinc oxide and stearic acid are not essential for radiation cure, they enhance the effect of the polythiols on radiation cure. 
     EXAMPLE 7 
     A series of experiments were conducted to determine whether other smaller molecular structures containing active hydrogen species would enhance the radiation crosslinking response of chlorinated butyl rubber. Included in these studies were mono-, di- and trithiols as shown in Table XI. 
     
                       TABLE XI                                                    
______________________________________                                    
Components.sup.(1)                                                        
               1      2      3    4    5    6                             
______________________________________                                    
Chlorinated Butyl                                                         
rubber HT-10-68                                                           
               100    100    100  100  100  100                           
Zinc Oxide     5      5      5    5    5    5                             
Stearic Acid   1      1      1    1    1    1                             
1-butane thiol (.011                                                      
SH/gm)                .95                                                 
1,4-butane dithiol                                                        
(0.16 SH/gm)                 .7                                           
1,2,3-propane trithiol                                                    
(.021 SH/gm)                      .5                                      
Phenyl Phosphine                                                          
(.0091 F/gm)                           1.1                                
Diphenyl Silane                                                           
(.0054 F/gm)                                1.85                          
______________________________________                                    
 .sup.(1) Parts per 100 parts of elastomer by weight.                     
 
    
     Functionalities per gram are shown adjacent to each additive and the amounts added would be comparable to the functionality of 2 parts of E1255 VII added to 100 parts of chlorinated butyl rubber. These obnoxious and sometimes toxic chemicals were added to chlorinated butyl rubber, zinc oxide, stearic acid masterbatch by solution mixing. Solutions were made in n-pentane and solid films recovered by room temperature evaporation in a hood followed by vacuum drying at room temperature. All films prior to irradiation with Co 60  source were soluble in cyclohexane. Crosslinking densities of the networks were obtained as a function of dose levels and are shown below in Table XII. 
     
                       TABLE XII                                                   
______________________________________                                    
           1    2        3      4    5    6                               
______________________________________                                    
XL/cc × 10.sup.-19 Orig.                                            
Polymer Volume after                                                      
0 MR         All    Soluble                                               
3.8 MR       .33    Loose    .98  2.3  .63  .62                           
                    Gel                                                   
7.4 MR       1.36   .6       1.55 2.0  1.39 1.28                          
12.3 MR      1.55   .81      1.59 2.2  1.82 1.40                          
______________________________________                                    
 
    
     A comparison of the data in Table XII shows that the monothiol of column 2 has a retarding effect upon radiation-induced crosslinking over the control column 1. The dithiol has a very modest activating effect, as do the phosphine and to a lesser extent, the silane as shown in columns 3, 5 and 6. The trithiol reflecting some of the activity of the polythioether polythiols has a more pronounced activating effect, although it does not appear to progress as radiant energy absorbed is increased. On a functionality basis, it can be considered inferior to the several types of polythioether polythiols evaluated. 
     EXAMPLE 8 
     Prior experiences have shown that radiation precure of chlorinated butyl rubber subsequently compounded with ingredients that promote chemical thermal curing, generally detracted from the subsequent thermal cure. 
     Table XIV shows the effect of polythiol E1255 VII on thermal cure after a precure by electron beam exposure. 
     
                                           TABLE XIV                               
__________________________________________________________________________
EFFECT OF RADIATION PRECURE UPON SUBSEQUENT                               
THERMAL CURE AT 20&#39;-307° F COMPARED TO A THERMAL CURE              
        Composition:                                                      
               Chlorinated Butyl HT 10-68 - 100                           
               Zinc Oxide-  5                                             
               Stearic Acid-  1                                           
               PTEPT (E1255 VII) as indicated                             
        Crosslinks Generated on Basis of Original                         
        Polymer Volume XL/cc × 10.sup.-19                           
Parts of Polythiol                                                        
              After Electron                                              
per 100 parts of Chlorinated Butyl Rubber                                 
              Beam Exposure (RC) 5 MR10 MR15 MR                           
                          AfterThermal Cure (TC) Only                     
                                     After TC+RC                          
                                           ##STR13##                      
__________________________________________________________________________
0 pt. E1255 Control                                                       
               .29                                                        
                  --  --  1.57       1.15  72%                            
              --   .50                                                    
                      --  1.57       1.06 68                              
              --  --   .62                                                
                          1.57       1.12 71                              
1 pt. E1255    .55                                                        
                  --  --  2.12       1.97  93%                            
              --   .79                                                    
                      --  2.12       1.65 78                              
              --  --  1.13                                                
                          2.12       1.59 75                              
2 pt. E1255   1.35                                                        
                  --  --  2.65       2.42  91%                            
              --  1.78                                                    
                      --  2.65       2.37 90                              
              --  --  2.06                                                
                          2.65       2.30 87                              
4 pt. E1255   2.34                                                        
                  --  --  3.39       3.90  115%                           
              --  3.07                                                    
                      --  3.39       3.73 110                             
              --  --  3.17                                                
                          3.39       3.48 103                             
__________________________________________________________________________
 
    
     These results show that at 1 pt. per 100 of polythiol there is a subtractive effect on the thermal cure; however, at higher levels the effect is additive. 
     EXAMPLE 9 
     Various polythiols were compared for their effectiveness with E1221 VIII polythiol. The three thiols tested in these experiments are as follows: 
     
         ______________________________________                                    
98-1 Trimethylol propane tris-thioglycolate                               
C.sub.2 H.sub.5 C(CH.sub.2 OCOCH.sub.2 SH).sub.3                          
                  Formula weight = 398                                    
                  Molar equiv. SH/gm = 3/398                              
                  = 0.0076                                                
98-2 Pentaerythritol tetra 3 mercaptoproprionate                          
C(CH.sub.2 OCOCH.sub.2 CH.sub.2 SH).sub.4                                 
                  Formula weight = 488                                    
                  Molar equiv. SH/gm = 4/488                              
                  = 0.0082                                                
______________________________________                                    
 
    
     These two thiol containing ester structures were compared with a polythioether polythiol of similar molecular weight and functionality per gram. ##STR14## Formulations were prepared and exposed to electron beam irradiation. The results are shown in Table XV. 
     
                       TABLE XV                                                    
______________________________________                                    
POLYTHIOL COMPOUNDS AS RADIATION CURE                                     
PROMOTERS OF CHLORINATED BUTYL RUBBER -                                   
EXPOSURE TO ELECTRON BEAM                                                 
AT 30 MEGARADS PER MINUTE                                                 
          Parts by Weight                                                 
Component   1      2      3    4    5    6    7                           
______________________________________                                    
Chlorinated Butyl                                                         
            100    100    100  100  100  100  100                         
Rubber HT 10-66                                                           
Zinc Oxide  5      5      5    5    5    5    5                           
Stearic Acid                                                              
            1      1      1    1    1    1    1                           
Polythiol 98-1                                                            
            --     1.45   2.89                                            
98-2        --                 1.34 2.68                                  
98-3        --                           1.37 2.75                        
______________________________________                                    
 Sample films molded between mylar film at 175° F. - 1 minute.     
 Exposed to 5, 10, 15 megarads at 30 MR/minute. Networks characterized by 
 volume swell in cyclohexane: at 0 megarads samples were soluble.         
 
    
     
         Additive                                                                  
          Con-                                                            
          trol 98-1      98-2      98-3                                   
            1      2      3    4    5    6    7                           
______________________________________                                    
Exposure 5 MR:                                                            
% Volume Increase                                                         
            1545   1295   1196 1334 1282 670  634                         
% Soluble Polymer                                                         
            16.3   13.3   12.4 14.0 13.7 5.6  4.2                         
Mc × 10.sup.-3                                                      
            64     48     42   51   47   16.5 15                          
XL/cc × 10.sup.-19                                                  
            0.37   0.52   0.59 0.48 0.53 1.56 1.78                        
(O.P.V.)                                                                  
Exposure 10 MR:                                                           
% Volume Increase                                                         
            1168   915    834  897  877  597  495                         
% Soluble Polymer                                                         
            12.9   14.0   12.5 13.3 12.8 6.1  5.7                         
Mc × 10.sup.-3                                                      
            41     27.5   23.4 27   25.5 13.6 10                          
XL/cc × 10.sup.-19                                                  
            0.45   0.90   1.05 0.95 0.98 1.88 2.51                        
Exposure 15 MR:                                                           
% Volume Increase                                                         
            1040   817    724  738  712  553  446                         
% Soluble Polymer                                                         
            12.8   14.3   12.1 12.5 12.2 6.8  4.8                         
Mc × 10.sup.-3                                                      
            39     23     18.2 19.5 18.2 12   8.4                         
XL × 10.sup.-19                                                     
            0.73   1.07   1.32 1.26 1.36 2.06 3.05                        
______________________________________                                    
 
    
     With column 1 as the control, the greater effectiveness of polythiol 98-3 can be observed in columns 6 and 7, as compared to 2 through 5. At the 5 MR exposure level, the ester structures (98-1; 98-2) on the basis of generated crosslinks (XL/cc) provide a response only marginally better than the control, while 98-3 provides an increase in crosslinking response of 5 to 6 times. This advantage is maintained at the higher dose levels. 
     Under Co 60  gamma radiation, at 0.01 MR/minute, the ester structures 98-1, 98-2 displayed a three-fold advantage in crosslinking response when compared to the control with 98-3 providing a further advantage. 
     EXAMPLE 10 
     Conventional butyl rubber will degrade under gamma ray irradiation through main chain scission while in contrast a chlorinated butyl rubber possesses considerable crosslinking potential. The addition of the polythiols of this invention do not change the response of unhalogenated butyl rubber to radiation exposure. The samples irradiated are described in Table XVI. 
     
                       TABLE XVI                                                   
______________________________________                                    
EFFECT OF IRRADIATION UPON                                                
REGULAR BUTYL RUBBER IN THE PRESENCE                                      
AND ABSENCE OF POLYTHIOETHER POLYTHIOL                                    
             1       2         3                                          
______________________________________                                    
Butyl Rubber 268.sup.(1)                                                  
               100       100       100                                    
Zinc Oxide     5         5         5                                      
Stearic Acid   1         1         1                                      
E2323III Polythiol                                                        
               --        2.25      4.5                                    
______________________________________                                    
 .sup.(1) Butyl rubber of 450,000 viscosity average molecular weight havin
 about 1.5 mole % unsaturation and a Mooney Viscosity at 260° F. of
 about 55.                                                                
 
    
     After irradiation, the polymers were still completely soluble in cyclohexane whereas the halogenated butyl rubbers cured under similar circumstances showed improved crosslink density. 
     EXAMPLE 11 
     Thiol structures that are not polythioether polythiols also have utility as coagents capable of accelerating the radiation-induced crosslinking of chlorinated butyl rubber as was demonstrated in Example 9. The experiments of Example 9 were repeated using Cobalt 60 irradiation instead of electron beam irradiation. These results are shown in Table XVII. 
     
                                           TABLE XVII                              
__________________________________________________________________________
EFFECT OF OTHER POLYTHIOLS ON THE Co.sup.60 IRRADIATION                   
INDUCED CROSSLINKING OF CHLORINATED BUTYL RUBBER                          
           (parts by weight)                                              
           1    2   3   4   5   6   7                                     
__________________________________________________________________________
Chlorinated butyl                                                         
rubber HT-10-68                                                           
           100  100 100 100 100 100 100                                   
Zinc Oxide 5    5   5   5   5   5   5                                     
Stearic Acid                                                              
           1    1   1   1   1   1   1                                     
98-1       --   1.45                                                      
                    2.89                                                  
98-2       --           1.34                                              
                            2.68                                          
98-3 (E1221)                                                              
           --               1.37                                          
                                2.75                                      
__________________________________________________________________________
 Test samples molder for 1 minute at 175° F. were soluble in       
 cyclohexane (mylar film protected). These films were exposed to Co.sup.60
 radiation at 0.01 megarads per minute followed by crosslinked network    
 analysis by volume swelling in cyclohexane with the following listed     
 results.                                                                 
Physical Properties                                                       
after Co.sup.60 Irradia-                                                  
           Control                                                        
                98-1    98-2    E1221                                     
tion at:   1    2   3   4   5   6   7                                     
__________________________________________________________________________
5.1 MR                                                                    
% Vol. Increase                                                           
           1110 627 500 621 583 469 381                                   
% Soluble Polymer*                                                        
           8.8  3.3 1.9 3.1 2.5 0.7 0                                     
Mc × 370.sup.-3                                                     
                15  10.3                                                  
                        14.8                                              
                            13.0                                          
                                9.4 6.7                                   
XL/cc × 10.sup.-19                                                  
           0.69 1.79                                                      
                    2.57                                                  
                        1.84                                              
                            2.05                                          
                                2.87                                      
                                    4.0                                   
(Orig. Pol. Vol.)                                                         
8.7 MR                                                                    
% Vol. Increase                                                           
           764  506 397 492 399 409 305                                   
% Soluble Polymer                                                         
           5.4  3.3 1.5 1.7 1.7 2.2 0.3                                   
Mc × 10.sup.-3                                                      
           21   10.5                                                      
                    7.2 10  7.2 7.3 4.7                                   
XL/cc × 10.sup.-19                                                  
           1.28 2.49                                                      
                    3.64                                                  
                        2.65                                              
                            3.64                                          
                                3.52                                      
                                    5.67                                  
13.0 MR                                                                   
% Vol. Increase                                                           
           684  450     450     366                                       
% Soluble Polymer                                                         
           7.1  4.5     4.0     3.1                                       
Mc × 10.sup.-3                                                      
           17   8.7     8.7     6.1                                       
XL/cc × 10.sup.-19                                                  
           1.49 3.0     3.01    4.25                                      
__________________________________________________________________________
 *Including polythiols.                                                   
 
    
     Although the thioether polythiol provides the greatest degree of radiation cure enhancement (based upon generated crosslinks per cc) on an equivalent functionality basis, the polythiols with ester structures were also effective as accelerating coagents. At the lowest megarad dose of 5.1, the E1221 additive enhanced generated crosslinks up to sixfold while the other additives registered a threefold improvement. The difference may be associated with coagent solubility in the hydrocarbon polymer medium. These data also illustrate that the sample E1221 additive would be one of the preferred structures from the standpoint effectiveness per unit weight. 
     EXAMPLE 12 
     The radiation cure of polybutadiene is well known in the art. Two typical polybutadienes were radiation cured using the method of this invention by preparing compositions which were molded into test samples of 0.025 thick films by press molding at 175° F for five minutes between Mylar film. All samples were hydrocarbon-soluble prior to radiation treatment. Exposures were made under a 30 MR/min. electron beam accelerator for various dose levels. The results are shown in Table XVIII. 
     
                                           TABLE XVIII                             
__________________________________________________________________________
                1   2   3   4   5   6                                     
__________________________________________________________________________
Firestone Diene 55.sup.(1)                                                
                100 100 100                                               
Phillips Cis 4 PB.sup.(2)   100 100 100                                   
E1262 VII           3   3       3   3                                     
Zinc Oxide              5           5                                     
Stearic Acid            1           1                                     
__________________________________________________________________________
 .sup.(1) a butyl lithium polymerized polybutadiene which has an          
 approximate structure: 45% 1,4 cis, 45% 1,4 trans. 10% 1,2 (vinyl pendant
 groups) butadiene addition.                                              
 .sup.(2) polybutadiene which has an approximate structure: 92% 1,4 cis   
 with some 1,4 trans and 2% 1,2 addition of butadiene.                    
 
    
     
         Physical Properties after                                                 
                Firestone Diene 55                                        
                            Phillips Cis 4 PB                             
     irradiation at:                                                      
                1   2   3   4   5   6                                     
__________________________________________________________________________
 5 MR -                                                                   
     % Volume Increase                                                    
                1002                                                      
                    353 258 1115                                          
                                594 522                                   
     % Soluble  9.0 2.2 1.7 11.1                                          
                                7.4 7.1                                   
     Mc × 10.sup.-3 (gel)                                           
                24  5   3.1 29  11  9.1                                   
     XL/cc × 10.sup.-19                                             
                1.06                                                      
                    5.57                                                  
                        9.25                                              
                            0.96                                          
                                2.41                                      
                                    2.97                                  
     (Orig. Poly. Vol.)                                                   
10 MR -                                                                   
     % Volume Increase                                                    
                505 271 221 576 361 328                                   
     % Soluble  3.3 1.1 1.3 5.5 4.3 4.5                                   
     Mc × 10.sup.-3                                                 
                8.4 3.3 2.5 10.4                                          
                                5.2 4.5                                   
     XL/cc × 10.sup.-19                                             
                3.19                                                      
                    8.3 11.35                                             
                            2.55                                          
                                5.3 6.11                                  
15 MR -                                                                   
     % Volume Increase                                                    
                395 256 209 445 298 274                                   
     % Soluble  1.8 0.9 1.3 4.3 3.6                                       
     Mc × 10.sup.-3                                                 
                6.0 3.1 2.3 7.2 3.9 3.4                                   
     XL/cc × 10.sup.-19                                             
                4.71                                                      
                    9.51                                                  
                        12.6                                              
                            3.92                                          
                                7.14                                      
                                    8.1                                   
__________________________________________________________________________
 
    
     Columns 1 and 4 are the respective polymer controls with no additives, columns 2 and 5 have just the 3% of added E1262 VII and columns 3 and 6 are further supported with zinc oxide and stearic acid. The accelerating effect for either elastomer by the PTEPT is marked with further enhancement by zinc oxide, stearic acid on the basis of any network parameter. This is shown by a reduction in volume swelling and soluble polymer as well as by a smaller molecular weight between effective crosslinks. Crosslink density is increased manyfold, as much as nine times for the Diene 55 at 5 MR exposure. The Diene 55 is more responsive presumably due to its larger amount of vinyl pendant groups. Data of this nature reveal the tremendous potential for the precuring of polydiene elastomers at markedly reduced radiation dose levels. 
     EXAMPLE 13 
     The chemistry of thioetherpolythiol acceleration of Chlorobutyl radiation curing was followed using a pilot plant prepared sample of the trivinylcyclohexane - H 2  S reaction product. This material, designated 5188, possessed the following analytical specifications. 
     Thiol sulfur - 21.0% by wt. 
     Total sulfur - 29.3% by wt. 
     Molecular Wt. - 413 by vapor pressure osmometry 
     Thiol sulfur is thus 71.7% of the total sulfur, and the difference between these sulfur analyses attests to the thioether structure of the polythiol. 
     The polythiol accelerator, 5188, was mixed with Chlorobutyl, zinc oxide and stearic acid at the two concentration levels shown in Table XIX. The acceleration of radiation cure, exposed to a 1.4 Mev electron beam, was compared to an elastomer system with no polythiol. The course and chemistry of the crosslinking reaction was followed by four parameters. 
     1. Reduction of soluble polymer. 
     2. Increase in crosslink concentration. 
     3. Reduction of reactive elastomer chlorine. 
     4. Increase in the combined thiol sulfur in the crosslinked network. 
     In order to obtain crosslinked samples free of inorganic residues (ZnO and ZnCl 2 ) as well as unreacted polythiol, an elaborate extraction process was performed to obtain transparent crosslinked films. 
     (a) Crosslinked films were digested in a solution of 1/3 naphthenic acid and 2/3 normal hexane at a refluxing temperature of 74° C for 10 hours to remove zinc oxide as soluble zinc naphthenate. 
     (b) Extracted samples with chloroform to remove ZnCl 2  and uncombined polythiol. 
     (c) Final extraction with fresh hexane to displace CHCl 3 . 
     (d) Dry to constant weight under high vacuum at 60°-70° C. 
     The levels of crosslinking desired can be varied by changes in the polythiol concentration. If a radiation process was designed to give only an initial precure to a rubber composition (for example to reduce viscous flow) lower levels of polythiol and reduced radiation exposures (down to 1-2 megarads) could be employed. To obtain highest levels of crosslinking, comparable to the best thermal cure formulations, the molar thiol content of the polythiol should equal the halogen functionality of the Chlorobutyl and up to 15 megarads of radiation energy could be used. 
     Examination of the data show that the presence of the polythiol markedly enhances the state of radiation crosslinking over the control. These increases in crosslink density and reductions in soluble polymer are accompanied by greater amounts of chlorine removal (for a given radiation dose level) and the presence of increasing amounts of combined thiol sulfur in the network. The polythiol is thus contributing to the network formation, probably via addition to double bonds as well as accelerating hydrogen chloride removal as chloride salts during the process. 
     
                       TABLE XIX                                                   
______________________________________                                    
ANALYSIS OF CHLOROBUTYL RADIATION CURE                                    
PROMOTED BY THIOETHERPOLYTHIOLS                                           
Tests by Wt.      1        2        3                                     
______________________________________                                    
Chlorobutyl (a)   100      100      100                                   
Zinc oxide        5        5        5                                     
Stearic acid      1        1        1                                     
5188              --       1.6      3.2                                   
Molar equiv. of SH added                                                  
                  --       .0133    .0267                                 
Ratio of thiol to Cl function                                             
                           0.40     0.80                                  
1.4 Mev electron beam                                                     
exposure for                                                              
0 megarads                                                                
% Soluble Polymer 100      100      100                                   
Xl/CC × 10.sup.-19 (b)                                              
                  0        0        0                                     
gm atoms Cl present                                                       
                  .034     .034     .034                                  
gm. atoms thiol S combined                                                
                  0        0        0                                     
5 Megarads                                                                
% Soluble Polymer 12.99    4.52     3.64                                  
XL/cc × 10.sup.-19 (b)                                              
                  0.38     1.23     1.49                                  
gm. atoms CL eliminated                                                   
                  .0094    .0129    .0134                                 
gm. atoms thiol S combined                                                
                  0        .0093    .0165                                 
10 Megarads                                                               
% Soluble Polymer 12.33    3.47     2.18                                  
XL/cc × 10.sup.-19 (b)                                              
                  0.64     2.02     2.54                                  
gm. atoms Cl eliminated                                                   
                  .0129    .0154    .0174                                 
gm. atoms thiol S combined                                                
                  0        .0117    .0201                                 
______________________________________                                    
 (a) Chlorobutyl had 1.18% allylic Cl by wt. = 0.034 gm. atoms Cl per 100 
 gms. of polymer.                                                         
 (b) XL/CC × 10.sup.-19 = effective crosslinks per cubic centimeter 
 generated by the curing process. To put these values in perspective, a   
 level of 1.50 would be the lower region of a satisfactory technical cure 
 by thermal processes. Special Chlorobutyl zinc oxide - tetramethylthiuram
 disulfide systems, for thermal cure, provide levels of 2.5 + considered t
 be high levels of crosslink density.