Polyarylate containing blends
BACKGROUND OF THE INVENTION 
     This invention is directed to a molding composition comprising a blend of a polyarylate, a polyester, and at least one thermoplastic polymer selected from the group consisting of an aromatic polycarbonate, a styrene resin, an alkyl acrylate resin, a polyurethane, a vinyl chloride polymer, a poly(aryl ether), a copolyetherester block polymer or a polyhydroxyether. 
     Polyarylates are aromatic polyesters derived from a dihydric phenol, particularly 2,2-bis-(4-hydroxyphenyl)propane (also identified as Bisphenol-A) and an aromatic dicarboxylic acid, particularly mixtures of terephthalic and isophthalic acids. 
     Polyarylates are high temperature, high performance thermoplastic polymers with a good combination of thermal and mechanical properties. They have a high continuous use temperature of about 130° C., and good unnotched toughness, with a pendulum impact value of greater than 300 ft. lbs./in. 3 . Additionally, polyarylates have inherent flammability and combustion resistance as well as good weatherability. The polyarylates have good melt stability at high temperatures and good color retention. They also have good processability which allows them to be molded into a variety of articles. 
     Polyarylates have been blended with other resin systems such as ABS resin (U.S. Pat. No. 3,792,118), polycarbonate resins (U.S. Pat. No. 3,792,115), polyurethane resins, methyl methacrylate resins, etc. The blending of resins is often used to cover a defect of one resin with another resin. For example, a resin having a low heat distortion temperature may be blended with a resin having a high heat distortion temperature. However, this method is generally accompanied by unfavorable effects on other properties such as deterioration of mechanical properties or an inferior surface of the resulting injection molded resin. 
     Specifically, when polyarylates are blended with resins such as thermoplastic polyurethanes, vinyl chloride polymers, methyl methacrylate resins, etc. several problems result. Polyarylates have high viscosities which require a high molding temperature which exceeds the temperature stability limit of the other resin which is blended with the polyarylate. Thus, when this blend is molded deterioration of the resin occurs. This is observed particularly with blends of polyarylate and vinyl chloride polymers. Additionally, when there is an extreme viscosity difference between the high viscosity polyarylate and the other polymer severe surface irregularities (e.g. jetting) are observed when these blends are injection molded. This is observed especially when polyarylate is blended with, for example, ABS resins and poly(methyl methacrylate) resins. Further, the extremely high viscosity of polyarylates prevents a uniform product from being obtained when the polyarylate is blended with a resin having a lower viscosity by conventional polymer mixing techniques, i.e., extrusion or Banbury type melt mixing. The non-uniform blend will not weather as well as a uniform blend of the resins nor will it have an acceptable balance of properties. 
     It has now been found that the addition of a polyester derived from an aliphatic or cycloaliphatic diol, or mixtures thereof, and an aromatic dicarboxylic acid to a blend of a polyarylate and at least one thermoplastic polymer selected from the group consisting of an aromatic polycarbonate, a styrene resin, an alkyl acrylate resin, a vinyl chloride polymer, a poly(aryl ether), a copolyetherester block polymer or a polyhydroxyether, produces a blend which has excellent surface appearance and can be easily molded without deterioration. 
     Additionally, it has been found that the addition of polyarylate to a blend of the polyester and the thermoplastic polymer improves the weatherability of the blend, i.e., the mechanical properties of the blends are retained after exposure to conditions of ultraviolet light and moisture. The presence of the polyester resin in the blend provides a uniform blend and the resins can be blended using conventional polymer mixing techniques. The presence of the polyester resin in the blend does not interfere with the improving effect the polyarylate has on the weatherability of the blend. 
     The blends of the present invention have excellent mechanical properties, better than the properties of a binary blend of polyarylate and a thermoplastic polymer. This is unexpected and allows heretofore unusable binary systems of polyarylate resin and thermoplastic polymer to be molded into articles. 
     DESCRIPTION OF THE INVENTION 
     According to the present invention there is provided a molding composition comprising a blend of: 
     (a) a polyarylate derived from at least one dihydric phenol and at least one aromatic dicarboxylic acid, 
     (b) a polyester derived from an aliphatic or cycloaliphatic diol, or mixtures thereof, and at least one aromatic dicarboxylic acid, and 
     (c) at least one thermoplastic polymer selected from the group consisting of an aromatic polycarbonate, a styrene resin, an alkyl acrylate resin, a polyurethane, a vinyl chloride polymer, a poly(aryl ether), a copolyetherester block polymer or a polyhydroxyether. 
     Polyarylates 
     The polyarylates of this invention are derived from a dihydric phenol and an aromatic dicarboxylic acid. 
     A particularly desirable dihydric phenol is of the following formula: ##STR1## wherein Y is selected from alkyl groups of 1 to 4 carbon atoms, chlorine or bromine, z has a value of from 0 to 4, inclusive, and R&#39; is a divalent saturated aliphatic hydrocarbon radical, particularly alkylene and alkylidene radicals having from 1 to 3 carbon atoms, and cycloalkylene radicals having up to and including 9 carbon atoms. The preferred dihydric phenol is Bisphenol-A. The dihydric phenols may be used individually or in combination. 
     Additionally, said dihydric phenols can be used in combination with a dihydric phenol of the following formula: ##STR2## wherein Y and z are as previously defined. 
     Suitable aromatic dicarboxylic acids include terephthalic acid, isophthalic acid, naphthalene dicarboxylic acids, and mixtures thereof, as well as alkyl substituted homologs of these carboxylic acids wherein the alkyl groups contain from 1 to about 4 carbon atoms, and acids containing other inert substituents such as halides, alkyl or aryl ethers, and the like. 
     The polyarylates contain from about 95 to 0 mole percent of terephthalic acid and from about 5 to 100 mole percent of isopthalic acid. More preferably, the polyarylates contain a mixture of from about 30 to about 70 mole percent of terephthalic acid and from about 70 to about 30 mole percent of isophthalic acid. A polyarylate containing a mixture of 50 mole percent of terephthalic acid and 50 mole percent of isophthalic acid is most preferred. 
     The polyarylates of the present invention can be prepared by any of the well known prior art polyester forming reactions, such as the reaction of the acid chlorides of the aromatic dicarboxylic acids with the dihydric phenol, the reaction of the diaryl esters of the aromatic dicarboxylic acids with the dihydric phenols, and the reaction of the aromatic diacids with diester derivatives of the dihydric phenol. These processes are described in, for example, U.S. Pat. Nos. 3,317,464; 3,948,856; 3,780,148; 3,824,213 and 3,133,898. 
     These polyarylates have a reduced viscosity of from about 0.4 to about 1.0 as measured in p-chlorophenol at 49° C. (0.2 g/100 ml.). 
     Polyesters 
     The polyesters which are suitable for use herein are derived from an aliphatic or cycloaliphatic diol, or mixtures thereof, containing from 2 to about 10 carbon atoms and at least one aromatic dicarboxylic acid. The polyesters which are derived from an aliphatic diol and an aromatic dicarboxylic acid have repeating units of the following general formula: ##STR3## wherein n is an integer of from 2 to 4. 
     The preferred polyester is poly(ethylene terephthalate). 
     Also contemplated herein are the above polyesters with minor amounts, e.g., from 0.5 to about 2 percent by weight, of units derived from aliphatic acids and/or aliphatic polyols, to form copolyesters. The aliphatic polyols include glycols such as poly(ethylene glycol). These can be made following the teachings of, for example, U.S. Pat. Nos. 2,465,319 and 3,047,539. 
     Among the units which can be present in the copolyesters are those derived from aliphatic dicarboxylic acids, e.g., of up to about 50 carbon atoms, including cycloaliphatic straight and branched chain acids, such as adipic acid, cyclohexanediacetic acid, dimerized C 16  -C 18  unsaturated acids (which have 32 to 36 carbon atoms), trimerized acids, and the like. In addition, there can be minor amounts of units derived from aliphatic glycols and polyols, e.g., of up to about 50 carbon atoms preferably from 2 to about 20 carbon atoms and these include, among others, propylene glycol, glycerol, diethylene glycol, triethylene glycol and the like. 
     The polyesters which are derived from a cycloaliphatic diol and an aromatic dicarboxylic acid are prepared by condensing either the cis- or trans-isomer (or mixtures thereof) of, for example, 1,4-cyclohexanedimethanol with the aromatic dicarboxylic acid so as to produce a polyester having recurring units having the following formula: ##STR4## wherein the cyclohexane ring is selected from the cis- and trans-isomers thereof and R represents an aryl radical containing 6 to 20 carbon atoms and which is the decarboxylated residue derived from an aromatic dicarboxylic acid. 
     Examples of aromatic dicarboxylic acids indicated by R in formula II, include isophthalic or terephthalic acid, 1,2-di(p-carboxyphenyl) ethane, 4,4&#39;-dicarboxydiphenyl ether, etc., and mixtures of these. All of these acids contain at least one aromatic nucleus. Fused rings can also be present such as in 1,4- or 1,5-naphthalene-dicarboxylic acids. The preferred dicarboxylic acid is terephthalic acid or mixtures of terephthalic and isophthalic acid. 
     A preferred polyester may be derived from the reaction of either the cis- or trans-isomer (or a mixture thereof) of 1,4-cyclohexanedimethanol with a mixture of iso- and terephthalic acids. These polyesters have repeating units of the formula: ##STR5## 
     Another preferred polyester is a copolyester derived from a cyclohexane dimethanol, an alkylene glycol and an aromatic dicarboxylic acid. These copolyesters are prepared by condensing either the cis- or trans-isomer (or mixtures thereof) of, for example, 1,4-cyclohexanedimethanol and an alkylene glycol with an aromatic dicarboxylic acid so as to produce a copolyester having repeating units of the following formula: ##STR6## wherein the cyclohexane ring is selected from the cis- and trans-isomers thereof, R is as previously defined, n is an integer of 2 to 4, the x units comprise from about 10 to about 90 percent by weight and the y units comprise from about 10 to about 90 percent by weight. 
     The preferred copolyester may be derived from the reaction of either the cis- or trans-isomer (or mixtures thereof) of 1,4-cyclohexanedimethanol and ethylene glycol with terephthalic acid in a molar ratio of 1:2:3. These copolyesters have repeating units of the following formula: ##STR7## wherein x and y are as previously defined. 
     Blends of said copolyesters and polyarylates are described in U.S. Pat. application Ser. No. (12,396) of L. M. Robeson, titled &#34;Polyarylate Blends with Copolyesters&#34; and filed on June 18, 1979. 
     This Patent Application Ser. No. (12,396) describes blends of polyarylates derived from a dihydric phenol and an aromatic dicarboxylic acid and a copolyester derived from a cyclohexanedimethanol, an alkylene glycol and an aromatic dicarboxylic acid, as having improved processability, weatherability and impact properties. 
     The polyesters as described herein are either commercially available or can be produced by methods well known in the art such as those set forth in, for example, U.S. Pat. No. 2,901,466. 
     The preferred polyesters are poly(1,4-cyclohexanedimethanol tere/iso-phthalate) and a copolyester of 1,4-cyclohexanedimethanol, ethylene glycol and terephthalic acid and poly(ethylene terephthalate) as previously described. 
     The polyesters used herein have an intrinsic viscosity of at least about 0.4 to about 2.0 dl/g. measured in a 60:40 phenol/tetrachloroethane mixture or similar solvent at 23°-30° C. The intrinsic viscosity is defined by the following relationship: ##EQU1## wherein ηSP=specific viscosity, and C=the concentration in dl/g. 
     Thermoplastic Polymers 
     The thermoplastic polymers suitable for use in this invention are selected from the group consisting of an aromatic polycarbonate, a styrene resin, an alkyl acrylate resin, a polyurethane, a vinyl chloride polymer, a poly(aryl ether), a copolyetherester block polymer, a polyhydroxyether, or mixtures thereof. 
     A. Polycarbonate 
     The thermoplastic aromatic polycarbonates that can be employed herein are homopolymers and copolymers and mixtures thereof which have an intrinsic viscosity of 0.40 to 1.0 dl./g. as measured in methylene chloride at 25° C. that are prepared by reacting a dihydric phenol with a carbonate precursor. Typical of some of the dihydric phenols that may be employed in the practice of this invention are bisphenol-A (2,2-bis(4-hydroxyphenyl) propane), bis(4-hydroxyphenyl) methane, 2,2-bis(4-hydroxy-3-methylphenyl) propane, 4,4-bis(4-hydroxyphenyl) heptane, 2,2-(3,5,3&#39;,5&#39;-tetrachloro-4,4&#39;-dihydroxydiphenyl) propane, 2,2-(3,5,3&#39;,5&#39;-tetrabromo-4,4&#39;-dihydroxydiphenyl)-propane, (3,3&#39;-dichloro-4,4&#39;-dihydroxydiphenyl) methane. Other dihydric phenols of the bisphenol type are also available and are disclosed in U.S. Pat. Nos. 2,999,835, 3,028,365 and 3,334,154. 
     It is, of course, possible to employ two or more different dihydric phenols or a copolymer of a dihydric phenol with a glycol or with hydroxy or acid terminated polyester, or with a dibasic acid in the event a carbonate copolymer or inter-polymer rather than a homopolymer is desired for use in the preparation of the aromatic carbonate polymers of this invention. 
     The carbonate precursor may be either a carbonyl halide, a carbonate ester or a haloformate. The carbonyl halides which can be employed herein are carbonyl bromide, carbonyl chloride and mixtures thereof. Typical of the carbonate esters which may be employed herein are diphenyl carbonate, di-(halophenyl) carbonates such as di-(chlorophenyl) carbonate, di-(bromophenyl) carbonate, di-(trichlorophenyl) carbonate, di-(tribromophenyl) carbonate, etc., di-(alkylphenyl) carbonates such as di(tolyl) carbonate, etc., di-(naphthyl) carbonate, di-(chloronaphthyl) carbonate, phenyl tolyl carbonate, chlorophenyl chloronaphthyl carbonate, etc. or mixtures thereof. The haloformates suitable for use herein include bis-haloformates of dihydric phenols (for example, bischloroformates of bisphenol-A, of hydroquinone, etc.) or glycols (for example, bishaloformates of ethylene glycol, neopentyl glycol, polyethylene glycol, etc.). While other carbonate precursors will occur to those skilled in the art, carbonyl chloride, also known as phosgene, is preferred. 
     The aromatic carbonate polymers of this invention may be prepared by using phosgene or a haloformate and by employing a molecular weight regulator, an acid acceptor and a catalyst. The molecular weight regulators which can be employed in carrying out the process of this invention include monohydric phenols such as phenol, para-tertiarybutylphenol, para-bromophenol, primary and secondary amines, etc. Preferably, a phenol is employed as the molecular weight regulator. 
     A suitable acid acceptor may be either an organic or an inorganic acid acceptor. A suitable organic acid acceptor is a tertiary amine and includes such materials as pyridine, triethylamine, dimethylaniline, tributylamine, etc. The inorganic acid acceptor may be one which can be either a hydroxide, a carbonate, a bicarbonate, or a phosphate of an alkali or alkaline earth metal. 
     The catalysts which are employed herein can be any of the suitable catalysts that aid the polymerization of bisphenol-A with phosgene. Suitable catalysts include tertiary amines such as, for example, triethylamine, tripropylamine, N,N-dimethylaniline, quaternary ammonium compounds such as, for example, tetraethylammonium bromide, cetyl triethyl ammonium bromide, tetra-n-heptylammonium iodide, tetra-n-propyl ammonium bromide, tetramethylammonium chloride, tetra-methyl ammonium hydroxide, tetra-n-butyl ammonium iodide, benzyltrimethyl ammonium chloride and quaternary phosphonium compounds such as, for example, n-butyltriphenyl phosphonium bromide and methyl-triphenyl phosphonium bromide. 
     The polycarbonates can be prepared in a one-phase (homogeneous solution) or two-phase (interfacial) systems when phosgene or a haloformate are used. Bulk reactions are possible with the diarylcarbonate precursors. 
     B. Styrene Resin 
     The styrene resins suitable for use herein are ABS type polymers, the molecules of which consist of two or more polymeric parts of different compositions that are bonded chemically. The polymer is preferably prepared by polymerizing a conjugated diene such as butadiene or a conjugated diene with a monomer copolymerizable therewith such as styrene to provide a polymeric backbone. After formation of the backbone, at least one grafting monomer and preferably two are polymerized in the presence of the prepolymerized backbone to obtain the graft polymer. 
     The backbone polymer, as mentioned, is preferably a conjugated diene polymer such as polybutadiene polyisoprene, or a copolymer such as butadiene-styrene, butadiene-acrylonitrile, or the like. 
     The specific conjugated diene monomers normally utilized in preparing the backbone of the graft polymer portion of the blends of this invention are generically described by the formula: ##STR8## wherein X may be selected from the group consisting of hydrogen, alkyl groups containing from one to five carbon atoms, chloro and bromo. Examples of dienes that may be used are butadiene; isoprene; 1,3-heptadiene; methyl-1,3-pentadiene; 2,3-dimethyl-1,3-butadiene; 1,3-pentadiene; 2-methyl-3-ethyl-1,3-butadiene; 2-ethyl-1,3-pentadiene; 1,3- and 2,4-hexadienes, chloro and bromo substituted butadienes such as dichlorobutadiene, bromobutadiene, dibromobutadiene, mixtures thereof, and the like. The preferred conjugated diene utilized herein is butadiene. 
     One monomer of group of monomers that may be polymerized in the presence of the prepolymerized backbone are preferably monovinylaromatic hydrocarbons. The monovinyl-aromatic monomers utilized are generically described by the formula: ##STR9## wherein X may be selected from the group consisting of hydrogen, alkyl groups containing from one to five carbon atoms, chloro and bromo. Examples of the monovinylaromatic compounds and substituted monovinylaromatic compounds that may be used are styrene and other vinyl substituted aromatic compounds including alkyl-, cycloalkyl-, aryl-, alkaryl-, aralkyl-, alkoxy-, aryloxy-, and other substituted vinylaromatic compounds. Examples of such compounds are 3-methylstyrene; 3,5-diethylstyrene and 4-n-propylstyrene, α-methylstyrene, α-methyl vinyltoluene, α-chlorostyrene, α-bromo-styrene, dichlorostyrene, dibromostyrene, tetra-chlorostyrene, mixtures thereof, and the like. The preferred monovinylaromatic hydrocarbons used herein are styrene and/or α-methylstyrene. 
     A second group of monomers that may be polymerized in the presence of the prepolymerized backbone are acrylonitrile, substituted acrylonitrile and/or acrylic acid esters exemplified by acrylonitrile and alkyl acrylates such as methyl methacrylate. The acrylonitrile, substituted acrylonitrile, or acrylic acid esters are described generically by the formula: ##STR10## wherein X may be selected from the group consisting of hydrogen, alkyl groups containing from one to five carbon atoms, chloro and bromo and Y is selected from the group consisting of cyano and carbalkoxy wherein the alkyl group of the carbalkoxy group contains from one to about twelve carbon atoms. Examples of monomers of this description are acrylonitrile, ethacrylonitrile, methacrylonitrile, α-chloroacrylonitrile, β-chloroacrylonitrile, α-bromoacrylonitrile, and β-bromoacrylonitrile, methyl acrylate, methyl methacrylate, ethyl acrylate, butyl acrylate, propyl acrylate, isopropyl acrylate, isobutyl acrylate, mixtures thereof and the like. The preferred acrylic monomer used herein is acrylonitrile and the preferred acrylic acid esters are ethyl acrylate and methyl methacrylate. 
     In the preparation of the graft polymer, the conjugated diolefin polymer or copolymer exemplified by 1,3-butadiene polymer or copolymer comprises from about 50% by weight to about 5% by weight of the total graft polymer composition and the monomers polymerized in the presence of the backbone exemplified by styrene and acrylonitrile comprise from about 40 to about 95% by weight of the total graft polymer composition. 
     The second group of grafting monomers, exemplified by acrylonitrile, ethyl acrylate or methyl methacrylate, of the graft polymer composition, preferably comprise from about 10% to about 40% by weight of the total graft copolymer composition and the monovinylaromatic hydrocarbon exemplified by styrene comprise from about 30 to about 70% by weight of the total graft polymer composition. 
     In preparing the polymer, it is normal to have a certain percentage of the polymerizing monomers that are grafted on the backbone combine with each other and occur as free copolymer. If styrene is utilized as one of the grafting monomers and acrylonitrile as the second grafting monomer, a certain portion of the composition will copolymerize as free styrene-acrylonitrile copolymer. In the case where α-methylstyrene (or other monomer) is substituted for the styrene in the compositions used in preparing the graft polymer, a certain percentage of the composition may be an α-methylstyrene-acrylonitrile copolymer. Also, there are occasions where a copolymer, such as α-methylstyrene-acrylonitrile, is added to the graft polymer copolymer blend. When the graft polymer-copolymer blend is referred to herein, it is meant optionally to include at least one copolymer blended with the graft polymer. It is contemplated in this invention that the graft polymer composition may contain up to 90% of free copolymer. 
     Optionally, the elastomeric backbone may be an acrylate rubber such as one based on n-butyl acrylate, ethylacrylate, 2-ethylhexylacrylate, and the like. Additionally, minor amounts of a diene may be copolymerized in the acrylate rubber backbone to yield improved grafting with the matrix polymer. 
     C. Alkyl Acrylate Resin 
     The alkyl acrylate resin used in the present invention includes a homopolymer of methyl methacrylate (i.e. polymethyl methacrylate) or a copolymer of methyl methacrylate with a vinyl monomer (e.g. acrylonitrile, N-allylmaleimide, N-vinyl maleimide, or an alkyl acrylate or methacrylate in which the alkyl group contains from 1 to 8 carbon atoms such as methyl acrylate, ethyl acrylate, butyl acrylate, ethyl methacrylate and butyl methacrylate). The amount of methyl methacrylate is not less than 70% by weight of this copolymer resin. The methyl methacrylate resin may have a reduced viscosity of from 0.1 to 2.0 dl/g in a 1% chloroform solution at 25° C. 
     The alkyl acrylate resin may be grafted onto an unsaturated elastomeric backbone such as polybutadiene, polyisoprene, and/or butadiene or isoprene copolymers. In the case of the graft copolymer, the alkyl acrylate resin comprises greater than 50 weight percent of the graft copolymers. 
     D. Polyurethanes 
     These thermoplastic polyurethanes may be synthesized by methods disclosed in U.S. Pat. No. 3,214,411 incorporated herein by reference. A particularly useful polyester resin used as a starting material for the thermoplastic polyurethane are those produced from adipic acid and a glycol having at least one primary hydroxyl group. The adipic acid is condensed with a suitable glycol or mixture of glycols which have at least one primary hydroxyl group. The condensation is stopped when an acid number of from about 0.5 to about 2.0 is reached. The water formed during the reaction is removed simultaneously therewith or subsequently thereto such that the final water content is from about 0.01 to about 0.2%, preferably from about 0.01 to 0.05%. 
     Any suitable glycol may be used in reaction with the adipic acid such, as, for example, ethylene glycol, propylene glycol, butylene glycol, hexanediol, bis- (hydroxymethylcyclohexane), 1,4-butanediol, diethylene glycol, 2,2-dimethyl propylene glycol, 1,3-propylene glycol and the like. In addition to the glycols, a small amount of trihydric alcohol of up to about 1% may be used along with the glycols such as, for example, trimethylolpropane, glycerol, hexanetriol and the like. The resulting hydroxyl polyester has a molecular weight of at least about 600, a hydroxyl number of about 25 to about 190 and preferably between about 40 and about 60, and acid number of between about 0.5 and about 2 and a water content of 0.01 to about 0.2%. 
     The organic diisocyanate to be used in the preparation of the elastomer is preferably 4,4&#39;-diphenylmethane diisocyanate. It is desired that the 4,4&#39;-diphenylmethane diisocyanate contain less than 5% of 2,4&#39;-diphenylmethane diisocyanate and less than 2% of the dimer of diphenylmethane diisocyanate. It is further desired that the acidity calculated as HCl is from about 0.0001 to about 0.02%. The acidity calculated as percent HCl is determined by extracting the chloride from the isocyanate in a hot aqueous methanol solution or by liberating the chloride on hydrolysis with water and titrating the extract with a standard silver nitrate solution to obtain the chloride ion concentration present. 
     Other diisocyanates may be used in preparing the thermoplastic processable polyurethanes such as ethylene diisocyanate, ethylidene diisocyanate, propylene diisocyanate, butylene diisocyanate, cyclopentylene-1,3-diisocyanate, cyclohexylene-1,4-diisocyanate, cyclohexylene-1,2-diisocyanate, 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, 2,2-diphenylpropane-4,4&#39;-diisocyanate, p-phenylene diisocyanate, m-phenylene diisocyanate, xylylene diisocyanate, 1,4-naphthylene diisocyanate, 1,5-naphthylene diisocyanate, diphenyl-4,4&#39;-diisocyanate, azobenzene-4,4&#39;-diisocyanate, diphenyl sulfone-4,4&#39;-diisocyanate, dichlorohexamethylene diisocyanate, pentamethylene diisocyanate, hexamethylene diisocyanate, 1-chlorobenzene-2,4-diisocyanate, furfurylidene diisocyanate and the like. 
     Any suitable chain extending agent having active hydrogen containing groups reactive with isocyanate groups may be used such as, for example, diols including ethylene glycol, propylene glycol, 1,4-butanediol, butenediol, butynediol, xylylene glycols, amylene glycols, 1,4-phenylene-bis-β-hydroxy ethyl ether, 1,3-phenylene-bis-β-hydroxy ethyl ether, bis-(hydroxy-methyl-cyclohexane), hexanediol, thiodiglycol and the like; diamines including ethylene diamine, propylene diamine, butylene diamine, hexamethylene diamine, cyclohexylene diamine, phenylene diamine, tolylene diamine, xylylene diamine, 3,3&#39;-dichlorobenzidine, 3,3&#39;-dinitrobenzidine and the like; alkanol amines such as, for example, ethanol amine, aminopropyl alcohol, 2,2-dimethyl propanol amine, 3-aminocyclohexyl alcohol, p-aminobenzyl alcohol and the like. The difunctional chain extenders mentioned in U.S. Pat. Nos. 2,620,516, 2,621,166 and 2,729,618 incorporated herein by reference may be used. If desirable, a small amount of polyfunctional material may be utilized. This polyfunctional chain extender, however, should not be present in an amount greater than about 1% by weight. Any suitable polyfunctional compound may be used in this application such as, for example, glycerol, trimethylolpropane, hexanetriol, pentaerythritol and the like. 
     In accordance with the process of this invention, the polyester, the organic diisocyanate and the chain extender may be individually heated preferably to a temperature of from about 60° to about 135° C. and then the polyester and chain extender are substantially simultaneously mixed with the diisocyanate. Of course, to increase the rate of reaction, any suitable catalyst may be added to the reaction mixture such as tertiary amines and the like as set forth in U.S. Pat. Nos. 2,620,516, 2,621,166 and 2,729,618. Although adipate polyesters are preferred, polyesters may be used which are based on succinic acid, suberic acid, sebacic acid, oxalic acid, methyl adipic acid, glutaric acid, pimelic acid, azelaic acid, phthalic acid, terephthalic acid, isophthalic acid and the like. Polyesters based on ε-caprolactone are also preferred. 
     A polyether may be used instead of the polyester in the preparation of the thermoplastic polyurethane and preferably polytetramethylene glycol having an average molecular weight between about 600 and 2000 and preferably about 1000. Other polyethers such as polypropylene glycol, polyethylene glycol and the like may be used providing their molecular weight is above about 600. The above and other thermoplastic polyurethanes such as disclosed in U.S. Pat. Nos. 2,621,166, 2,729,618, 3,214,411, 2,778,810, 3,012,992 Canadian Pat. Nos. 754,233, 733,577 and 842,325 all incorporated herein by reference may be used to produce the thermoplastic polyurethanes. 
     E. Vinyl Chloride Polymers 
     Vinyl chloride polymers for the purpose of this invention are polyvinyl chloride and copolymers of vinyl chloride with olefinically unsaturated polymerisable compounds which contain at least 80 percent by weight of vinyl chloride incorporated therein. Olefinically unsaturated compounds which are suitable for copolymerisation are, for example, vinylidene halides such as vinylidene chloride and vinylidene fluoride, vinyl esters such as vinyl acetate, vinyl propionate, vinyl butyrate, vinyl chloroacetate, vinyl benzoate, acrylic and α-alkyl-acrylic acids and their alkyl esters, amides and nitriles, methacrylic acid, methyl methacrylate, ethyl acrylate, 2-ethyl-hexylacrylate, butyl methacrylate, acrylamide, N-methyl acrylamide, acrylonitrile and methacrylonitrile, aromatic vinyl compounds such as styrene and vinyl naphthalene and olefinically unsaturated hydrocarbons such as ethylene, bicyclo-[2,2,1]-hept-2-ene and bicyclo-[2,2,1]-hepta-2,5-dienes. These vinyl chloride polymers are known and can be prepared by the usual methods of emulsion, suspension, bulk or mass polymerisation. Vinyl chloride polymers which have molecular weights of 40,000 to 60,000 are preferred. 
     F. Poly(aryl ether)s 
     The poly(aryl ether) resin component of the blend of this invention may be described as a linear, thermoplastic polyarylene polyether polysulfone, wherein the arylene units are interspersed with ether and sulfone linkages. These resins may be obtained by reaction of an alkali metal double salt of a dihydric phenol and a dihalobenzenoid compound, either or both of which contain a sulfone linkage --SO 2  -- between arylene groupings, to provide sulfone units in the polymer chain in addition to arylene units and ether units. The polysulfone polymer has a basic structure composed of recurring units of the formula 
     
         O--E--O--E&#39;-- 
    
     wherein E is the residuum of the dihydric phenol and E&#39; is the residuum of the benzenoid compound having an inert electron withdrawing group in at least one of the positions ortho and para to the valence bonds; both of said residua are valently bonded to the ether oxygens through aromatic carbon atoms. Such polysulfones are included within the class of polyarylene polyether resins described in U.S. Pat. No. 3,264,536, the disclosure of which is hereby incorporated herein by reference, for the purpose of describing and exemplifying E and E&#39; in more detail, including the preferred forms of E derived from dinuclear phenols having the structure: ##STR11## Aris an aromatic group and preferably is a phenylene group. A and A 1  can be the same or different inert substituent groups as alkyl groups having from 1 to 4 carbon atoms, halogen atoms, i.e., fluorine, chloride, bromine or iodine, or alkoxy radicals having from 1 to 4 carbon atoms, r and r 1  are integers having a value of from 0 to 4, inclusive, and R 1  is representative of a bond between aromatic carbon atoms as in dihydroxydiphenyl, or is a divalent radical, including, for example, CO, O, S, S--S, SO 2  and divalent organic hydrocarbon radicals such as alkylene, alkylidene, cycloalkylene, or the halogen, alkyl, aryl or like substituted alkylene, alkylidene and cycloalkylene radicals as well as alkarylene and aromatic radicals and a ring fused to both Ar groups. Typical preferred polyners are composed of recurring units having the formula: ##STR12## as described in the Robinson et al. patent. In the foregoing formula A and A 1  can be the same or different inert substituent groups as alkyl groups having from 1 to 4 carbon atoms, halogen atoms (e.g., fluorine, chlorine, bromine or iodine) or alkoxy radicals having from 1 to 4 carbon atoms, r and r 1  are integers having a value of from 0 to 4, inclusive. Typically, R 1  is representative of a bond between aromatic carbon atoms or a divalent connecting radical and R 2  represents sulfone, carbonyl, sulfoxide. Preferably, R 1  represents a bond between aromatic carbon atoms. Even more preferred are the thermoplastic polyarylene polysulfones of the above formula wherein r and r 1  are zero. R 1  is a divalent connecting radical of the formula ##STR13## wherein R&#34; represents, as exemplified in Robinson et al., a member of the group consisting of alkyl, lower aryl, and the halogen substituted groups thereof, and R 2  is a sulfone group. 
     Typical examples are the reaction products prepared from 2,2-bis-(4-hydroxyphenyl) propane (source of E residue) with 4,4&#39;-dichlorodiphenylsulfone (source of E&#39; residue) and equivalent reaction products such as those from 4,4&#39;-dichlorodiphenylsulfone with bisphenol of benzophenone (4,4&#39;-dihydroxydiphenyl ketone), or the bisphenol of acetophenone [1,1-bis(4-hydroxyphenyl) ethane], or the bisphenol of vinyl cyclohexane [1-ethyl-1-(4-hydroxyphenyl)-3-(4-hydroxyphenylcyclohexane)], or 4,4&#39;-dihydroxydiphenyl sulfone or alpha, alpha&#39;-bis(4-hydroxyphenyl)-p-diisopropylbenzene. 
     Further useful discussion of the polysulfone resins which may be used is to be found in British Pat. No. 1,060,546. 
     G. Copolyetherester Block Copolymer 
     The polyetheresters consist essentially of a multiplicity of recurring intralinear long chain and short chain ester units connected head-to-tail through ester linkages, said long chain ester units being represented by the following structure: ##STR14## and said short chain ester units being represented by the following structure ##STR15## wherein: G is a divalent radical remaining after removal of terminal hydroxy groups from a poly(alkylene oxide) glycol having a molecular weight of about 400-3500; D is a divalent radical remaining after removal of hydroxyl groups from a low molecular weight diol having a molecular weight less than about 250; and R 2  is a divalent radical remaining after removal of carboxyl groups from a dicarboxylic acid having a molecular weight less than about 300; with the provisos that the short chain ester units constitute about 25-65% by weight of the copolyester, at least about 70% of the R 2  groups must be 1,4-phenylene radicals, at least about 70% of the D groups must be the 1,4-butylene radicals, and the sum of the percentages of the R 2  groups which are not 1,4-phenylene radicals and of the D groups which are not 1,4-butylene radicals cannot exceed about 30%. 
     The term &#34;long chain ester units&#34; as applied to units in a polymer chain refers to the reaction product of a long chain glycol with a dicarboxylic acid. Such &#34;long chain ester units&#34;, which are a repeating unit in the copolyesters of this invention correspond to the Formula a above. The long chain glycols of the instant invention are poly(alkylene oxide) glycols having a molecular weight between about 400 and 3500, preferably between about 600 and 2000. Copolyesters prepared from poly(alkylene oxide) glycols having a molecular weight of about 600-2000 are preferred because they exhibit useful properties over a wide range of temperature, combined with limited water swell. Copolyesters prepared from poly(alkylene oxide) glycols having a molecular weight in excess of about 3500 may crystallize and lose their elastomeric character and good low temperature properties. Copolyester prepared from glycols having molecular weights below about 400 have useful properties only within a narrow temperature range and are less suited for injection molding and extrusion because of a slower rate of crystallization of the resultant block copolymer. The long chain glycols contain a major proportion of tetramethylene oxide units. In a preferred embodiment of the instant invention the long chain glycols will be entirely poly(tetramethylene oxide) glycol. In some instances it may be desirable to use random or block copolymers of tetramethylene oxide containing minor proportions of a second alkylene oxide. Typically the second monomer will constitute less than about 40 mole percent of the poly(alkylene oxide) glycols and preferably less than 20 mole percent. Representative examples of the second monomer include 1,2- and 1,3-propylene oxides, 1,2-butylene oxide and ethylene oxide. 
     The term &#34;short chain ester units&#34; as applied to units in a polymer chain refers to low molecular weight compounds or polymer chain units having molecular weights less than about 550. They are made by reacting a low molecular weight diol (below about 250) with a dicarboxylic acid to form ester units represented by Formula (b) above. 
     Included among the low molecular weight diols (other than 1,4-butanediol) which react to form short chain ester units are acyclic, alicyclic and aromatic dihydroxy compounds. Preferred are diols with 2-15 carbon atoms such as ethylene, propylene, isobutylene, tetramethylene, pentamethylene, 2,2-dimethyltrimethylene, hexamethylene and decamethylene glycols, dihydroxy cyclohexane, cyclohexane dimethanol, resorcinol, hydroquinone, 1,5-dihydroxy naphthalene, etc. Especially preferred are aliphatic diols containing 2-8 carbon atoms. Included among the bisphenols which can be used are bis(p-hydroxy) diphenyl, bis(p-hydroxyphenyl) methane, and bis(p-hydroxyphenyl) propane. Equivalent esterforming derivatives of diols are also useful (e.g., ethylene oxide or ethylene carbonate can be used in place of ethylene glycol). The term &#34;low molecular weight diols&#34; as used herein should be construed to include such equivalent ester-forming derivatives: provided, however, that the molecular weight requirement pertains to the diol only and not to its derivatives. 
     Dicarboxylic acids (other than terephthalic acid) which are reacted with the foregoing long chain glycols or low molecular weight diols to produce the copolyesters of this invention are aliphatic, cycloaliphatic or aromatic dicarboxylic acids of a low molecular weight. The term &#34;dicarboxylic acids&#34; as used herein, includes acid equivalents of dicarboxylic acids having two functional carboxyl groups which perform substantially like dicarboxylic acids in reaction with glycols and diols in forming copolyester polymers. These equivalents include esters and ester-forming derivatives, such as acid halides and anhydrides. The molecular weight requirement pertains to the acid and not to its equivalent ester or ester-forming derivative. Thus, an ester of a dicarboxylic acid having a molecular weight greater than 300 or an acid equivalent of a dicarboxylic acid having a molecular weight greater than 300 are included provided the acid has a molecular weight below about 300. The dicarboxylic acids can contain any substituent groups or combinations which do not substantially interfere with the copolyester polymer formation and use of the polymer in the elastomeric compositions of this invention. 
     Aliphatic dicarboxylic acids, as the term is used herein, refers to carboxylic acids having two carboxyl groups each attached to a saturated carbon atom. If the carbon atom to which the carboxyl group is attached is saturated and is in a ring, the acid is cycloaliphatic. Aliphatic or cycloaliphatic acids having conjugated unsaturation often can not be used because of homopolymerization. However, some unsaturated acids, such as maleic acid, can be used. 
     Aromatic dicarboxylic acids, as the term is used herein, are dicarboxylic acids having two carboxyl groups attached to a carbon atom in an isolated or fused benzene ring. It is not necessary that both functional carboxyl groups be attached to the same aromatic ring and where more than one ring is present, they can be joined by aliphatic or aromatic divalent radicals such as --O-- or --SO 2  --, alkylene, alkylidene, etc. 
     Representative aliphatic and cycloaliphatic acids which can be used for this invention are sebacic acid, 1,3-cyclohexane dicarboxylic acid, 1,4-cyclohexane dicarboxylic acid, adipic acid, glutaric acid, succinic acid, carbonic acid, oxalic acid, azelaic acid, diethylmalonic acid, allylmalonic acid, 4-cyclohexane-1,2-dicarboxylic acid, 2-ethylsuberic acid, 2,2,3,3-tetramethylsuccinic acid, cyclopentanedicarboxylic acid, decahydro-1,5-naphthylene dicarboxylic acid, 4,4-bicyclohexyl dicarboxylic acid, decahydro-2,6-naphthylene dicarboxylic acid, 4,4-methylenebis-(cyclohexyl) carboxylic acid, 3,4-furan dicarboxylic acid, and 1,1-cyclobutane dicarboxylic acid. Preferred aliphatic acids are cyclohexane-dicarboxylic acids and adipic acid. 
     Representative aromatic dicarboxylic acids which can be used include phthalic, terephthalic and isophthalic acids, substituted dicarboxy compounds with two benzene nuclei such as bis(p-carboxyphenyl) methane, p-carboxyphenyl/oxybenzoic acid, ethylene-bis (p-oxybenzoic acid) 1,5-naphthalene dicarboxylic acid, 2,6-naphthalene dicarboxylic acid, 2,7-naphthalene dicarboxylic acid, phenanthrene dicarboxylic acid, anthracene dicarboxylic acid, 4,4&#39;-sulfonyl dibenzoic acid and C 1  -C 12   alkyl and ring substituted derivatives thereof, such as halo, alkoxy, and aryl derivatives. Hydroxy acids such as p(β-hydroxyethoxy) benzoic acid can also be used providing an aromatic dicarboxylic acid is also present. 
     Aromatic dicarboxylic acids are a preferred class for preparing the copolyester polymers useful for compositions of this invention. Among the aromatic acids, those with 8-16 carbon atoms are preferred, particularly the phenylene dicarboxylic acids, i.e., terephthalic and isophthalic acids. 
     It is essential that at least about 70 mole percent of the dicarboxylic acid incorporated into the polymer be terephthalic acid and at least about 70 mole percent of the low molecular weight diol incorporated into the polymer be 1,4-butanediol. Thus, at least 70% of the R 2  groups in Formulae a and b above are 1,4-phenylene radicals and at least about 70% of the D groups in Formula b above are 1,4-butylene radicals. A further requirement in making the polymers of this invention is that the sum of the percentages of the R 2  groups which are not 1,4-phenylene radicals and of the D groups which are not 1,4-butylene radicals cannot exceed about 30%. For example, if 30% of the low molecular weight diol molecules incorporated into the polymer are other than 1,4-butanediol, then all of the dicarboxylic acid used must be terephthalic acid, or if 10% of the low molecular weight diol molecules are other than 1,4-butanediol, then at least about 80% of the dicarboxylic acid used must be terephthalic acid. The D and R units which are not 1,4-butylene and 1,4-phenylene, respectively, can be derived from any of the low molecular weight diols or dicarboxylic acids named above. 
     The dicarboxylic acids or their derivatives and the polymeric glycol are incorporated into the final product in the same molar proportions as are present in the reaction mixture. The amount of low molecular weight diol actually incorporated corresponds to the difference between the moles of diacid and polymeric glycol present in the reaction mixture. When mixtures of low molecular weight diols are employed, the amounts of each diol incorporated is largely a function of the amounts of the diols present, and relative reactivities. The total amount of glycol incorporated is still the difference between moles of diacid and polymeric glycol. 
     The copolyesters of this invention contain about 25-65% by weight of short chain ester units corresponding to Formula (b) above, the remainder being long chain ester units corresponding to Formula a above. When the copolyesters contain less than about 25% by weight short chain units, the tear strength and solvent resistance of the copolyesters fall to undesirably low levels and when the copolyesters contain more than about 65% short chain units, the low temperature properties worsen and the copolyesters become less elastomeric. The preferred balance of properties is obtained when the short chain ester content is about 55-62%. 
     The most preferred copolyesters of this invention are those prepared from dimethylterephthalate, 1,4-butanediol and poly (tetramethylene oxide) glycol having a molecular weight from about 600-1500. 
     The polymers described herein can be made conveniently by a conventional ester interchange reaction. A preferred procedure involves heating the dimethyl ester of terephthalic acid with a long chain glycol and a molar excess of a butanediol in the presence of a catalyst at 150° to 260° C. followed by distilling off methanol formed by the interchange. Heating is continued until methanol evolution is complete. Depending on temperature, catalyst and glycol excess, this polymerization is complete within a few minutes to a few hours. The procedure results in the preparation of a low molecular weight prepolymer which can be carried to a high molecular weight copolyester of this invention by the procedure described below. Such prepolymers can also be prepared by a number of alternate esterification or ester interchange processes; for example, the long chain glycol can be reacted with a high or low molecular weight short chain ester homopolymer or copolymer is the presence of catalyst until randomization occurs. The short chain ester homopolymer or copolymer can be prepared by ester interchange from either the dimethyl esters and low molecular weight diols, as above, or from the free acids with the diol acetates. Alternatively, the short chain ester copolymer can be prepared by direct esterification from appropriate acids, anhydrides or acid chlorides, for example, with diols or by other processes such as reaction of the acids with cyclic ethers or carbonates. Obviously the prepolymer might also be prepared by running these processes in the presence of the long chain glycol. 
     The resulting prepolymer is then carried to high molecular weight by distillation of the excess of short chain diol. This process is known as &#34;polycondensation&#34;. Additional ester interchange occurs during the distillation to increase the molecular weight and to randomize the arrangement of the copolyester units. Best results are usually obtained if this final distillation or polycondensation is run at less than 1 mm. Hg pressure and 240°-260° C. for less than 2 hours in the presence of antioxidants such as sym-di-beta-naphthyl-phenylene-diamine and 1,3,5-trimethyl-2,4,6-tris[3,5-ditertiary butyl-4-hydroxybenzyl]benzene. Most practical polymerization techniques rely upon ester interchange to complete the polymerization reaction. In order to avoid excessive hold time at high temperatures with possible irreversible thermal degradation, it is advantageous to employ a catalyst for ester interchange reactions. While a wider variety of catalysts can be used, organic titanates such as tetrabutyl titanate used alone or in combination with magnesium or calcium acetates are preferred. Complex titanates, such as 
     
         Mg[HTi(OR.sub.3).sub.6 ].sub.2&#39; 
    
     derived from alkali or alkaline earth metal alkoxides and titanate esters are also very effective. Inorganic titanates, such as lanthanum titanate, calcium acetate/antimony trioxide mixtures and lithium and magnesium alkoxides are representative of other catalysts which can be used. 
     These polyetheresters are described in, for example, U.S. Pat. Nos. 3,784,520 and 3,766,146. 
     H. Polyhydroxyether 
     The thermoplastic polyhydroxyethers in the present invention have the general formula 
     
         --D--O--E&#34;--O].sub.n 
    
     wherein D is the radical residuum of a dihydric phenol, E&#34; is a radical residuum of an epoxide selected from mono- and diepoxides and contains from 1 to 2 hydroxyl groups and n is an integer which represents the degree of polymerization and is at least 30 and preferably is above about 80. 
     In general, thermoplastic polyhydroxyethers are prepared by contacting under polymerization conditions a dihydric phenol and an epoxide containing from 1 to 2 epoxide groups in substantially equimolar amounts. 
     The product produced by the reaction between bisphenol-A and epichlorohydrin has the repeating unit ##STR16## and can be termed a poly(monohydroxyether) of bisphenol-A. 
     The product produced by the reaction between hydroquinone and butadiene dioxide has the repeating unit ##STR17## and can be termed a poly(dihydroxyether) of hydroquinone. 
     By the use of both a monoepoxide and a diepoxide poly(hydroxy-dihydroxyethers) can be obtained, the relative amounts of mono- and diepoxide determining the final concentration of the mono- and dihydroxy containing repeating units E&#34; in the polymer. 
     Any dihydric phenol can be used in forming polyhydroxyethers. Illustrative dihydric phenols are mononuclear dihydric phenols such as hydroquinone, resorcinol, and the like as well as the polynuclear phenols which are preferred. The dihydric polynuclear phenols have the general formula: ##STR18## wherein: Ar is an aromatic divalent hydrocarbon radical such as naphthylene and phenylene with phenylene being preferred for the thermoplastic polyhydroxyethers used in this invention; B and B 1  which can be the same or different are alkyl radicals such as methyl, n-propyl, n-butyl, n-hexyl, n-octyl and the like, preferably alkyl radicals having a maximum of 4 carbon atoms; or halogen atoms, i.e., chlorine, bromine, iodine, or fluorine; or alkoxy radicals such as methoxy, methoxymethyl, ethoxy, ethoxyethyl, n-butyloxy, amyloxy and the like, preferably an alkoxy radical having a maximum of 4 carbon atoms, a and a 1  are independently integers of 0 to 4, R&#39; is alkylene, alkylidene, cycloalkylene or a saturated divalent group. Particularly preferred are dihydric polynuclear phenols having the general formula: ##STR19## wherein B, B 1 , a and a 1  are as previously defined, and R 3  is an alkylene or alkylidene group, preferably having from 1 to 3 carbon atoms inclusive or cycloalkylene or R 3  is a saturated divalent group such as is obtained from compounds such as vinylcyclohexane and dipentene or its isomers by reaction with two moles of phenol per mole of the compound. R 3  preferably contains from 1 to 9 carbon atoms. 
     Diepoxides useful for the preparation of polyhydroxyethers can be represented by the formula ##STR20## wherein R 4  is representative of a bond between adjacent carbon atoms or a divalent inorganic or organic radical such as an aliphatic, aromatic, homocyclic, heterocyclic or acyclic arrangement of atoms. 
     By the term &#34;diepoxide&#34; is meant a compound containing two epoxide groups i.e. groups containing an oxirane oxygen atom bonded to two vicinal aliphatic carbon atoms. Saturated diepoxides in which both the oxirane oxygen atoms are bonded to carbon atoms of a saturated aliphatic hydrocarbon chain are particularly preferred. The term &#34;saturated diepoxides&#34; refers to diepoxides which are free of ethylenic unsaturation, i.e. --C═C-- and acetylenic unsaturation, i.e. --C.tbd.C--. Diepoxides which contain solely carbon, hydrogen and oxygen atoms are especially preferred. The oxygen atoms can be (in addition to oxirane oxygen), ether oxygen, i.e. --O-- oxacarbonyl oxygen, i.e. ##STR21## carbonyl oxygen, i.e. ##STR22## and the like. A single diepoxide or a mixture of at least two diepoxides can be employed in preparing the polydihydroxyethers of the present invention and the term &#34;diepoxide&#34; is intended to include a mixture of at least two diepoxides. 
     Other diepoxides which can be mentioned include those wherein the two oxirane groups are linked through an aromatic ether i.e. compounds having the grouping ##STR23## wherein R 4  is a divalent organic radical, W is a divalent aromatic radical residuum of a dihydric phenol such as those listed above in the description of dihydric phenols, and d is an integer from 0 to 1 inclusive. 
     Still other diepoxides include ethers wherein the oxirane groups are connected to vicinal carbon atoms at least one pair of which is a part of a cycloaliphatic hydrocarbon. 
     These polyhydroxy ethers are prepared by methods well known in the art such as those detailed in, for example, U.S. Pat. Nos. 3,238,087; 3,305,528; 3,294,747 and 3,277,051. 
     Ordinarily from 0.985 to 1.015 moles and preferably one mole of the epoxide is employed per mole of dihydric phenol. Polymerization occurs at room temperature (25° C.) and lower but only slowly, hence ordinarily, an elevated temperature e.g. 40° C. to 250° C. or more preferably from 80° to 125° C. is used to ensure a rapid rate of polymerization. Pressure is not at all critical, with polymerization being successfully effected at atmospheric, subatmospheric, or superatmospheric pressure with or without an inert gas such as nitrogen in the reaction vessel. 
     The polyarylate is used in amounts of from about 4 to about 80, preferably from about 40 to about 60 weight percent. The polyester is used in amounts of from about 4 to about 60, preferably from about 10 to about 45 weight percent. The thermoplastic polymer is used in amounts of from about 10 to about 92, preferably from about 30 to 60 weight percent. 
     The compositions of this invention are prepared by any conventional mixing methods. For example, a preferred method comprises mixing the polyarylate, polyester, and thermoplastic polymer in powder or granular form in an extruder and extruding the mixture into strands, chopping the strands into pellets and molding the pellets into the desired article. 
     It should, of course, be obvious to those skilled in the art that other additives may be included in the present compositions. These additives include plasticizers; pigments; flame retardant additives, particularly, decabromodiphenyl ether and triarylphosphates, such as triphenylphosphate; reinforcing agents, such as glass fibers; thermal stabilizers; ultraviolet light stabilizers processing aids, impact modifiers and the like. The impact modifiers which can be used are described in U.S. Patent application Ser. No. 049,131 of L. M. Robeson, titled &#34;Impact Modified Polyarylate Blends&#34;, filed June 18, 1979. These impact modifiers are a graft copolymer of a vinyl aromatic, an acrylate, an unsaturated nitrile, or mixtures thereof, grafted onto an unsaturated elastomeric backbone and having a tensile modulus (as measured by ASTM D-638, except that the test piece is compression molded to a 20 mil thickness) of less than about 100,000 psi, and preferably from about 15,000 to less than about 100,000 psi. 
     The unsaturated elastomeric backbone may be polybutadiene, poly(butadiene-co-styrene), poly(butadiene-co-acrylonitrile), or poly(isoprene). In each of the polymers there is sufficient butadiene to give the polymer a rubbery character. 
     The constituents which are grafted onto the unsaturated elastomeric backbone are selected from a vinyl aromatic, such as styrene, α-methylstyrene, alkylstyrene, or mixtures thereof; an acrylate such as the acrylic ester monomers, such as methyl acrylate, ethyl acrylate, butyl acrylate, methyl methacrylate, or mixtures thereof; an unsaturated nitrile such as acrylonitrile, methacrylonitrile, or mixtures thereof. It will be understood that the vinyl aromatic, acrylate and acrylonitrile may be used individually or in any combinations in grafting onto the unsaturated elastomeric backbone. 
     These impact modifiers are free-flowing powders and are commercially available as impact modifiers for poly(vinyl chloride) as described in, for example, V. Shakaypal, in &#34;Developments in PVC Technology&#34;, edited by J. H. L. Hensen and A. Whelan, Applied Science Publishers Ltd., New York, 1973. 
     The grafted constituents of the impact modifier will comprise from about 20 to about 60 percent by weight of said constituents such that their tensile modulus does not exceed about 100,000 psi, and is preferably, between about 15,000 to less than about 100,000 psi. 
    
    
     EXAMPLES 
     The following examples serve to give specific illustrations of the practice of this invention but they are not intended in any way to limit the scope of this invention. 
     CONTROL A 
     60 weight percent of poly(ethylene terephthalate) having an intrinsic viscosity of 1.04 as measured in 60:40 phenol/tetrachloroethane mixture at 23° C. was blended with 40 weight percent of an aromatic bisphenol-A polycarbonate (Lexan 101 sold by General Electric Company) having a reduced viscosity of 0.64 as measured in chloroform at 25° C. 
     This blend was prepared by extrusion blending the components at about 275° C. in a single screw 1-inch diameter extruder with L/D=36/1. The extrudate was chopped into pellets. The pelletized product was then injection molded into ASTM test specimens (at 270°-300° C.) using a Newbury 11/4 ounce screw injection molding machine. The test specimens were measured for the following properties: tensile strength and modulus according to ASTM D-638; elongation at break according to ASTM D-638; notched izod impact strength according to ASTM D-256; tensile impact strength according to ASTM D-1822: heat distortion temperature measured at 264 psi on a 1/8 inch thick unannealed test bar according to ASTM D-635. Also, the clarity of the test specimen as molded was observed. 
     The results are shown in Table I. 
     EXAMPLE 1 
     80 weight percent of the poly(ethylene terephthalate) described in Control A was blended with 10 weight percent of the polycarbonate described in Control A and 10 weight percent of polyarylate (Ardel D-100, sold by Union Carbide Corporation and prepared from, Bisphenol-A and a mixture of 50 mole percent each of terephthalic and isophthalic acid chlorides, by conventional methods) having a reduced viscosity of 0.66 as measured in p-chlorophenol at 49° C. (0.2 g/100 ml.). 
     The blend was prepared in an extruder by the procedure as described in Control A. The extrudate was chopped into pellets, molded into test bars and tested by the procedures as described in Control A. 
     EXAMPLE 2 
     60 weight percent of the poly(ethylene terephthalate) described in Control A was blended with 20 weight percent of the polycarbonate described in Control A and 20 weight percent of the polyarylate described in Example 1. 
     The blend was prepared in an extruder by the procedure as described in Control A. The extrudate was chopped into pellets, molded into test bars and tested by the procedures as described in Control A. 
     The results are shown in Table I. 
     EXAMPLE 3 
     40 weight percent of the poly(ethylene terephthalate) described in Control A was blended with 30 weight percent of the polycarbonate described in Control A and 30 weight percent of the polyarylate described in Example 1. 
     The blend was prepared in an extruder by the procedure as described in Control A. The extrudate was chopped into pellets, molded into test bars and tested by the procedures as described in Control A. 
     The results are shown in Table I. 
     CONTROL B 
     The procedure of Control A was exactly repeated except that the blend was prepared by extrusion blending the components at about 310° C. instead of about 275° C. 
     The results are shown in Table I. 
     EXAMPLE 4 
     The procedure of Example 1 was exactly repeated except that the blend was prepared by extrusion blending the components at about 310° C. instead of about 275° C. 
     The results are shown in Table I. 
     EXAMPLE 5 
     The procedure of Example 2 was exactly repeated except that the blend was prepared by extrusion blending the components at about 310° C. instead of about 275° C. 
     The results are shown in Table I. 
     EXAMPLE 6 
     The procedure of Example 3 was exactly repeated except that the blend was prepared by extrusion blending the components at about 310° C. instead of about 275° C. 
     The results are shown in Table I. 
     The data of Table I show that a ternary blend of a polyarylate, a polyester and a polycarbonate, according to the present invention, has excellent mechanical properties. Additionally, two component mixtures are rarely transparent and transparency in three component systems is unique. Example 5 shows that the addition of polyarylate to a polycarbonate/poly(ethyleneterephthalate) blend (control B) improves the transparency. 
     
                                           TABLE I                                 
__________________________________________________________________________
                                       Notched Izod                       
Description of Clarity After                                              
                       Tensile                                            
                            Tensile    Impact Strength                    
                                               Tensile Impact             
                                                       Heat               
the Composition.sup.1                                                     
               Molding at                                                 
                       Modulus                                            
                            Strength                                      
                                 Elongaton                                
                                       ft.-lbs./                          
                                               Strength                   
                                                       Distortion         
Example                                                                   
      Polymer                                                             
           (wt.%)                                                         
               275° C.                                             
                   310° C.                                         
                       (psi)                                              
                            (psi)                                         
                                 (percent)                                
                                       in. of Notch)                      
                                                (ft.-lbs./in..sup.2       
                                                       Temp.              
__________________________________________________________________________
                                                       (°C.)       
Control A                                                                 
      PE   60  opaque                                                     
                   --  358,000                                            
                            8,850                                         
                                 150   1.09    187     76                 
      PC   40                                                             
1     PE   80  trans-                                                     
                   --  366,000                                            
                            8,410                                         
                                 98    0.93    149     73                 
      PC   10  parent                                                     
      PA   10                                                             
2     PE   60  opaque                                                     
                   --  366,000                                            
                            8,700                                         
                                 90    1.26    160     76                 
      PC   20                                                             
      PA   20                                                             
3     PE   40  trans-                                                     
                   --  370,000                                            
                            9,450                                         
                                 48    1.19    114     94                 
      PC   30  parent                                                     
      PA   30                                                             
Control B                                                                 
      PE   60  --  opaque                                                 
                       363,000                                            
                            9,120                                         
                                 198   1.09    179     78                 
      PC   40                                                             
4     PE   80  --  trans-                                                 
                       351,000                                            
                            8,430                                         
                                 133   0.80    136     71                 
      PC   10      parent                                                 
      PA   10                                                             
5     PE   60  --  trans-                                                 
                       362,000                                            
                            9,020                                         
                                 162   0.78    148     82                 
      PC   20      parent                                                 
      PA   20                                                             
6     PE   40  --  trans-                                                 
                       366,000                                            
                            9,490                                         
                                 87    1.04    --      97                 
      PC   30      parent                                                 
      PA   30                                                             
__________________________________________________________________________
 PE = poly(ethylene terephthalate)                                        
 PC = polycarbonate                                                       
 PA = polyarylate                                                         
 
    
     CONTROL C 
     The polyarylate (Ardel D-100) described in Example 1 was injection molded into ASTM test specimens (at 270°-300° C.) using a Newbury 11/4 ounce screw injection molding machine. The test specimens were measured for the following properties: tensile strength and modulus according to ASTM D-638; elongation at break according to ASTM D-638; notched izod impact strength according to ASTM D-256; tensile impact strength according to ASTM D-1822; heat distortion temperature measured at 264 psi on a 1/4 inch thick unannealed test bar according to ASTM D-635. Also, the minimum melt temperature required for injection molding, was determined using a 3 ounce Van Dorn injection molding machine with a four cavity ASTM test specimen mold. The minimum melt temperature is the lowest polymer melt temperature, determined by a pyrometer, to fill the four cavity mold. 
     The results are shown in Table 2. 
     CONTROL D 
     The polycarbonate (Lexan 101) described in Control A was injection molded into test bars and tested by the procedure as described in Control C. 
     The results are shown in Table 2. 
     CONTROL E 
     67 weight percent of the polyarylate (Ardel D-100) described in Control C was blended with 33 weight percent of a copolyester, PETG-6763, (a copolyester prepared by the reaction of cyclohexanedimethanol and ethylene glycol with terephthalic acid, in a molar ratio of 1:2:3. This polyester has a M n  of about 26,000 and is sold by Tennessee Eastman Company). 
     This blend was prepared by extrusion blending the components at about 270° C. in a single screw 1-inch diameter extruder with L/D=36/1. The extrudate was chopped into pellets. The pelletized product was then injection molded into ASTM test specimens and tested by the procedure as described in Control C. 
     The results are shown in Table 2. 
     CONTROL F 
     50 weight percent of the polyarylate (Ardel D-100) described in Control C was blended with 50 weight percent of the polycarbonate (Lexan 101) described in Control A. The blend was prepared by extrusion blending the components by the procedure described in Control E. The pelletized product was injection molded into ASTM test specimens and tested by the procedure as described in Control C. 
     The results are shown in Table 2. 
     EXAMPLE 7 
     33.3 weight percent of the polyarylate (Ardel D-100) described in Control C was blended with 16.7 weight percent of a copolyester, PETG-6763, described in Control E and 50 weight percent of the polycarbonate (Lexan 101) described in Control A. The blend was prepared by extrusion blending the components by the procedure described in Control E. The pelletized product was injection molded into ASTM test specimens and tested by the procedures as described in Control C. 
     The results are shown in Table 2. 
     The data of Table 2 shows that the addition of a copolyester to blends of polyarylate and polycarbonate results in excellent compatability with the polyarylate and a polycarbonate. Also, the addition of a copolyester to a blend of a polyarylate and a polycarbonate improves the processability as shown by the minimum melt temperature required for injection molding. 
     
                                           TABLE 2                                 
__________________________________________________________________________
                               Notched Izod                               
Description of Tensile                                                    
                    Tensile    Impact Strength                            
                                       Tensile Impact                     
                                               Heat   Minimum Inject-     
the Composition.sup.1                                                     
               Modulus                                                    
                    Strength                                              
                         Elongation                                       
                               (ft.-lbs./                                 
                                       Strength                           
                                               Distortion                 
                                                      ion Molding         
Example                                                                   
      Polymer                                                             
           (wt.%)                                                         
               (psi)                                                      
                    (psi)                                                 
                         (percent)                                        
                               in. of Notch)                              
                                       (ft.-lbs./in..sup.2)               
                                               Temp. (°C.)         
                                                      Temp.               
__________________________________________________________________________
                                                      (°F.)        
Control C                                                                 
      PA   100 280,000                                                    
                    9,500                                                 
                         48    4.2     132     174                        
Control D                                                                 
      PC   100 325,000                                                    
                    9,000                                                 
                         50-100                                           
                               18      --      128                        
Control E                                                                 
      PA   67  330,000                                                    
                    9,800                                                 
                         74    2.3     166     118                        
      PETG 33                                                             
Control F                                                                 
      PA   50  320,000                                                    
                    10,000                                                
                         80    8.8     170     147    630° F.      
      PC   50                                                             
7     PA   33.3                                                           
               330,000                                                    
                    9,600                                                 
                         80    6.8     150     128    560° F.      
      PETG 16.7                                                           
      PC   50                                                             
__________________________________________________________________________
 .sup.1 PA = polyarylate                                                  
 PC = polycarbonate                                                       
 PETG = copolyester PETG 6763                                             
 
    
     CONTROL G 
     A polyarylate (prepared from Bisphenol-A and a mixture of 25 mole percent terephthalic acid chloride and 75 mole percent isophthalic acid chloride, by conventional methods, having a reduced viscosity of 0.77 as measured in p-chlorophenol at 49° C., 0.2 g/100 ml.) was injection molded into ASTM test specimens (at 270°-300° C.) using a Newbury 11/4 ounce screw injection molding machine. The test specimens were measured for the following properties: tensile strength and modulus according to ASTM D-638; elongation at break according to ASTM D-638; and notched izod impact strength according to ASTM D-256. 
     The results are shown in Table 3. 
     CONTROL H 
     A styrene/acrylonitrile grafted onto a butylacrylate based elastomeric backbone, an ABS type resin, (Luran S described in Table 3 and sold by BASF) was molded into test specimens and tested by the procedures as described in Control G. 
     The results are shown in Table 3. 
     CONTROL I 
     A poly(butylene terephthalate) resin (6PRO sold by Tennessee Eastman Co.) having an R.V. of 1.83 as measured in 60/40 phenol/tetrachloroethane (1 g/1000 ml) at 25° C., was molded into test specimens and tested by the procedures as described in Control G. 
     The results are shown in Table 3. 
     CONTROL J 
     60 weight percent of the polyarylate described in Control G was blended with 40 weight percent of the poly butylene terephthalate) described in Control I. 
     This blend was prepared by extrusion blending the components at about 270° C. in a single screw 1-inch diameter extruder with L/D=36/1. The extrudate was chopped into pellets. The pelletized product was then injection molded into ASTM test specimens (at 270°-300° C.) using a Newbury 11/4 ounce screw injection molding machine. The test specimens were tested as described in Control G. 
     The results are shown in Table 3. 
     EXAMPLE 8 
     36 weight percent of the polyarylate described in Control G was blended with 24 weight percent of the poly(butylene terephthalate) described in Control I and 40 weight percent of the ABS resin described in Control H. 
     The blend was prepared by the procedure described in Control J. The pelletized product was injection molded into test specimens and tested by the procedures described in Control G. 
     The results are shown in Table 3. 
     The data of Table 3 shows that the ternary blend of this invention exhibits a notched izod impact strength higher than the individual components. 
     
                                           TABLE 3                                 
__________________________________________________________________________
Description of Tensile                                                    
                    Tensile    Notched Izod                               
the Composition.sup.1                                                     
               Modulus                                                    
                    Strength                                              
                         Elongation                                       
                               Impact Strength                            
Example                                                                   
      Polymer                                                             
           (wt.%)                                                         
               (psi)                                                      
                    (psi)                                                 
                         (percent)                                        
                               (ft.-lbs./in. of Notch)                    
__________________________________________________________________________
Control G                                                                 
      PA   100 305,000                                                    
                    10,400                                                
                         20    2.6                                        
Control H                                                                 
      ABS  100 297,000                                                    
                    5,840                                                 
                         29    1.53                                       
Control I                                                                 
      PBT  100 404,000                                                    
                    7,710                                                 
                         295   1.1                                        
Control J                                                                 
      PA   60  335,000                                                    
                    9,430                                                 
                         138   0.9                                        
      PBT  40                                                             
8     PA   36  319,000                                                    
                    7,870                                                 
                         68    13.7                                       
      PBT  24                                                             
      ABS  40                                                             
__________________________________________________________________________
 .sup.1 PA = polyarylate                                                  
 PBT = poly(butylene terephthalate)                                       
 ABS = styrene/acrylonitrile/grafted into a butyl acrylate based          
 elastomeric backbone, Luran S.                                           
 
    
     CONTROL K 
     60 weight percent of a polyarylate, Ardel D-100, described in Example 1 was blended with 40 weight percent of poly(1,4-cyclohexanedimethanol tere/isophthalate) (commercially available from Tennessee Eastman Co. under the designation 7-DRO, the terephthalate to isophthalate ratio is 1:1). 
     This blend was prepared by extrusion blending the components at about 270° C. in a single screw 1-inch diameter extruder with L/D=36/1. The extrudate was chopped into pellets. The pelletized product was then injection molded into ASTM test specimens (at 270°-300° C.) using a Newbury 11/4 ounce screw injection molding machine. The test specimens were measured for the following properties: tensile strength and modulus according to ASTM D-638; elongation at break according to ASTM D-638; flexural strength and modulus according to ASTM D-790; notched izod impact strength according to ASTM D-256; tensile impact strength according to ASTM D-1822; heat distortion temperature measured at 264 psi on a 1/8 inch thick unannealed test bar according to ASTM D-635. 
     The results are shown in Table 4. 
     EXAMPLE 9 
     40 weight percent of the polyarylate (Ardel D-100) described in Example 1 was blended with 20 weight percent of the copolyester (7 DRO) described in Control K and 40 weight percent of the ABS resin, Luran S, described in Control H. 
     The blend was prepared by extrusion blending the components as described in Control K. The pelletized product was injection molded into test bars and tested by the procedures described in Control K. 
     The results are set forth in Table 4. 
     The data in Table 4 shows that the copolyester is compatible with the blend of polyarylate and ABS as seen by the good mechanical properties. 
     
                                           TABLE 4                                 
__________________________________________________________________________
                                        Notched Izod                      
Description of Tensile                                                    
                    Tensile                                               
                         Elonga-                                          
                              Flexural                                    
                                   Flexural                               
                                        Impact Strength                   
                                                Tensile                   
                                                        Heatct            
the Composition.sup.1                                                     
               Modulus                                                    
                    Strength                                              
                         tion Modulus                                     
                                   Strength                               
                                        (ft.-lbs./                        
                                                Strength                  
                                                        Distortion        
Example                                                                   
      Polymer                                                             
           (wt.%)                                                         
               (psi)                                                      
                    (psi)                                                 
                         (percent)                                        
                              (psi)                                       
                                   (psi)                                  
                                        in. of Notch)                     
                                                (ft.-lbs./in..sup.2)      
                                                        Temp.             
__________________________________________________________________________
                                                        (°C.)      
Control H                                                                 
      ABS  100 297,000                                                    
                    3,840                                                 
                         29   --   --    1.53   218      76               
Control K                                                                 
      PA   60  348,000                                                    
                    9,450                                                 
                         83   328,000                                     
                                   13,200                                 
                                        1.2      80     103               
      PE   40                                                             
9     PA   40  347,000                                                    
                    7,520                                                 
                         96   309,000                                     
                                   11,800                                 
                                        2.0     196     --                
      PE   20                                                             
      ABS  40                                                             
__________________________________________________________________________
 .sup.1 ABS = styrene/acrylonitrile resin grated onto butyl acrylate      
 rubber.                                                                  
 PA = polyarylate                                                         
 PE = copolyester 7DRO                                                    
 
    
     CONTROL L 
     A blend of α-methylstyrene/acrylonitrile copolymer and styrene/acrylonitrile grafted onto a butadiene based elastomeric backbone (Kralastic K-2938 sold by Uniroyal Company and having the mechanical properties listed in Table 5) was injection molded into ASTM test specimens (at 270°-300° C.) using a Newbury 11/4 ounce screw injection molding machine. The test specimens were measured for the following properties: tensile strength and modulus according to ASTM D-638; elongation at break according to ASTM D-638; flexural strength and modulus according to ASTM D-790; notched izod impact strength according to ASTM D-256; heat distortion temperature measured at 264 psi on a 1/8 inch thick unannealed test bar according to ASTM D-635 and tensile impact strength according to ASTM-D-1822. 
     The results are shown in Table 5. 
     CONTROL M 
     A styrene/acrylonitrile grafted onto a butadiene based elastomer (Kralastic MV sold by Uniroyal Company and having the mechanical properties listed in Table 5) was injection molded into test bars and tested as described in Control L. 
     The results are shown in Table 5. 
     CONTROL N 
     A styrene/acrylonitrile grafted onto a butadiene based elastomer (Cycolac T-100 sold by Borg Warner Company, and having the mechanical properties listed in Table 5) was injection molded into test bars and tested as described in Control L. 
     The results are shown in Table 5. 
     CONTROL O 
     67 weight percent of a polyarylate, Ardel D-100 described in Example 1 was blended with 33 weight percent of a copolyester, PETG-6763, described in Control E. 
     This blend was prepared by extrusion blending the components at about 270° C. in a single screw 1-inch diameter extruder with L/D=36/1. The extrudate was chopped into pellets. The pelletized product was then injection molded into ASTM test specimens and tested as described in Control L. 
     The results are shown in Table 5. 
     EXAMPLE 10 
     40 weight percent of a polyarylate, Ardel D-100, was blended with 20 weight percent of a copolyester, PETG-6763, and 40 weight percent of Kralastic 2938, described in Control L. 
     The blend was prepared as described in Control O. The product was injection molded into test specimens and tested as described in Control L. 
     The results are shown in Table 5. 
     EXAMPLE 11 
     40 weight percent of polyarylate, Ardel D-100, was blended with 20 weight percent of a copolyester, PETG-6763, and 40 weight percent of Kralastic MV, described in Control M. 
     The blend was prepared as described in Control O. The product was injection molded into test specimens and tested as described in Control L. 
     The results are shown in Table 5. 
     EXAMPLE 12 
     40 weight percent of a polyarylate, Ardel D-100, was blended with 20 weight percent of a copolyester, PETG-6763, and 40 weight percent of Cyclolac T-1000 described in Control N. 
     The blend was prepared as described in Control O. The product was injection molded into test specimens and tested as described in Control L. 
     The results are shown in Table 5. 
     EXAMPLE 13 
     40 weight percent of a polyarylate, Ardel D-100 was blended with 20 weight percent of a copolyester, PETG-6763 and 40 weight percent of Luran S described in Control H. 
     The blend was prepared as described in Control O. The product was injection molded into test specimens and tested as described in Control L. 
     The results are shown in Table 5. 
     The data in the Table shows that the ternary blends of polyarylate/copolyester/ABS, of the present invention, exhibit excellent compatibility as shown by the tensile strength values which are intermediate between those of the component values. Also, the addition of the polyarylate/copolyester binary blend to ABS increases the heat distortion temperature of ABS. 
     
                                           TABLE 5                                 
__________________________________________________________________________
                                        Notched Izod                      
Description of Tensile                                                    
                    Tensile                                               
                         Elonga-                                          
                              Flexural                                    
                                   Flexural                               
                                        Impact Strength                   
                                                Tensile                   
                                                        Heatct            
the Composition.sup.1                                                     
               Modulus                                                    
                    Strength                                              
                         tion Modulus                                     
                                   Strength                               
                                        (ft.-lbs./                        
                                                Strength                  
                                                        Distortion        
Example                                                                   
      Polymer                                                             
           (wt.%)                                                         
               (psi)                                                      
                    (psi)                                                 
                         (percent)                                        
                              (psi)                                       
                                   (psi)                                  
                                        in. of Notch)                     
                                                (ft.- lbs./in..sup.2)     
                                                        Temp.             
__________________________________________________________________________
                                                        (°C.)      
Control L                                                                 
      K-2938                                                              
           100 307,000                                                    
                    6,080                                                 
                         28.6 --   --   5.2     59      85                
Control M                                                                 
      KMV  100 263,000                                                    
                    4,850                                                 
                         18   310,000                                     
                                    9,330                                 
                                        6.1     --      73                
Control N                                                                 
      T-1000                                                              
           100 296,000                                                    
                    5,790                                                 
                         11.7 344,000                                     
                                   10,500                                 
                                        6.2     --      75                
Control O                                                                 
      PA   67  321,000                                                    
                    9,710                                                 
                         33   335,000                                     
                                   15,800                                 
                                        2.5     133     113               
      PE   33                                                             
10    PA   40  378,000                                                    
                    8,320                                                 
                         13.3 --   --   2.1     92      93                
      PE   20                                                             
      K-2938                                                              
           40                                                             
11    PA   40  314,000                                                    
                    7,650                                                 
                         13   371,000                                     
                                   13,800                                 
                                        1.5     89      91                
      PE   20                                                             
      K-MV 40                                                             
12    PA   40  287,000                                                    
                    8,290                                                 
                         17   --   --   1.2     113     93                
      PE   20                                                             
      T-1000                                                              
           40                                                             
13    PA   40  263,000                                                    
                    7,310                                                 
                         55   --   --   2.1     176     96                
      PE   20                                                             
      Luran-S                                                             
           40                                                             
__________________________________________________________________________
 .sup.1 K2938 = Kralastic K2938                                           
 PA = polyarylate                                                         
 KMV = Kralastic MV                                                       
 PE = copolyester PETG6763                                                
 T1000 = Cycolac T1000                                                    
 
    
     CONTROL P 
     A styrene/acrylonitrile copolymer grafted onto a butyl acrylate rubber (Luran S 776 sold by BASF) was compression molded at 250° C. into 20 mil thick samples. These samples were exposed in an artificial weathering unit for 500, 1000, 2000, and 3000 hours, by the procedure and equipment as described in ASTM D-1499. From the exposed specimens, 1/8 inch wide specimens were shear cut to determine the tensile strength according to ASTM-D-638. The initial tensile strength of the sample after molding is shown in Table 6 and the percent of the retention of the tensile strength of the samples is reported after 500, 1000, 2000 and 3000 hours of exposure in the weathering unit (XW-Weatherometer). 
     The results are shown in Table 6. 
     EXAMPLE 14 
     90 weight percent of the ABS described in Control P (Luran S 776), was blended with 6 weight percent of polyarylate, Ardel D-100, and 4 weight percent of poly(ethylene terephthalate) having an intrinsic viscosity of 0.64 as measured in 60:40 phenol/tetrachloroethane mixture at 23° C. 
     The blend was prepared by blending the materials in a Brabender blender at 250°-270° C. The blend was then compression molded into test samples and tested by the procedures as described in Control P. 
     The results are shown in Table 6. 
     EXAMPLE 15 
     80 weight percent of the ABS described in Control P (Luran S 776) was blended with 12 weight percent of polyarylate, Ardel D-100, and 8 weight percent of the poly(ethylene terephthalate) described in Example 14. 
     The blend was prepared by blending the materials in a Brabender blender at 250°-270° C. The blend was then compression molded into test samples and tested by the procedure as described in Control P. 
     The results are shown in Table 6. 
     The data of Table 6 show that the addition of a polyarylate/poly(ethylene terephthalate) blend to an ABS polymer improves the resistance to accelerated weathering. Even when the polyarylate is added at low levels (6% and 12%) an excellent improvement in the retention of tensile strength of the ABS after accelerated weathering is observed. 
     
                                           TABLE 6                                 
__________________________________________________________________________
                       Retention of Initial Tensile                       
Description of         Strength (%) after Exposure                        
the Composition.sup.1                                                     
                Initial Tensile                                           
                       in Weatherometer for:                              
Example                                                                   
      Polymer                                                             
           (wt. %)                                                        
                Strength (psi)                                            
                       500                                                
                          1000                                            
                             2000                                         
                                3000 (hrs.)                               
__________________________________________________________________________
Control P                                                                 
      ABS  100  3460   86 79 75 59                                        
14    ABS  90   3470   101                                                
                          86 91 88                                        
      PA   6                                                              
      PET  4                                                              
15    ABS  80   3710   109                                                
                          98 99 95                                        
      PA   12                                                             
      PET  8                                                              
__________________________________________________________________________
 .sup.1 ABS = Luran S 776                                                 
 PA = polyarylate                                                         
 PET = poly(ethylene terephthalate)                                       
 
    
     CONTROL Q 
     Samples of a polyarylate, Ardel D-100, were compression molded into 20 to 30 mil thick samples. Samples 1/8 inch wide and 20 to 30 mils thick were placed under the stress shown in Table 7. A cotton swab saturated with the chemical environment, as identified in Table 7, is attached to the center of the test specimen. The time for the specimen to rupture is then recorded. 
     The results are shown in Table 7. 
     CONTROL R 
     75 weight percent of polyarylate, Ardel D-100, was blended with 25 weight percent of poly(ethylene-terephthalate) having an intrinsic viscosity of 0.64 as measured in 60:40 phenol/tetrachloroethane mixture at 23° C. 
     The blend was prepared by blending the materials in a Brabender blender at 250°-270° C. The blend was compression molded and tested as described in Control Q. 
     The results are shown in Table 7. 
     EXAMPLE 16 
     60 weight percent of the blend of polyarylate and poly(ethylene terephthalate) of Control R was blended with 40 weight percent of an ABS resin (Kralastic K-2938 described in Control L). 
     The blend was prepared by blending the materials in a Brabender blender at 250°-270° C. The blend was compression molded and tested as described in Control Q. 
     The results are shown in Table 7. 
     The data in the Table show that the environmental stress crack resistance of polyarylate and a blend of polyarylate and poly(ethylene terephthalate) is quite poor in several organic environments. The addition of ABS to the polyarylate/poly(ethylene terephthalate) blend yields improved stress crack resistance. 
     
                                           TABLE 7                                 
__________________________________________________________________________
Description of                                                            
the Composition.sup.1                                                     
                 Chemical  Stress                                         
                               Time to Rupture                            
Example                                                                   
      Polymer                                                             
             wt. %                                                        
                 Environment                                              
                           (psi)                                          
                               (sec)                                      
__________________________________________________________________________
Control Q                                                                 
      PA     100 acetone   500 1                                          
Control R                                                                 
      PA     75                                                           
      PET    25  acetone   500 1                                          
16    PA (75)                                                             
             60  acetone   500 108                                        
      PET (25)                                                            
      ABS    40                                                           
Control Q                                                                 
      PA     100 methyl ethyl ketone                                      
                           500 2                                          
Control R                                                                 
      PA     75                                                           
      PET    25  methyl ethyl ketone                                      
                           500 1                                          
16    PA (75)                                                             
             60  methyl ethyl ketone                                      
                           500 234                                        
      PET (25)                                                            
      ABS    40                                                           
Control Q                                                                 
      PA     100 carbon tetrachloride                                     
                           1000                                           
                               15                                         
Control R                                                                 
      PA     75                                                           
      PET    25  carbon tetrachloride                                     
                           1000                                           
                               5                                          
16    PA (75)                                                             
             60  carbon tetrachloride                                     
                           1000                                           
                               153                                        
      PET (25)                                                            
      ABS    40                                                           
__________________________________________________________________________
 .sup.1 PA = polyarylate                                                  
 PET = poly(ethylene terephthalate)                                       
 ABS = K2938                                                              
 
    
     CONTROL S 
     60 weight percent of a polyarylate, Ardel D-100, described in Example 1, was blended with 40 weight percent of an impact modified poly(methyl methacrylate) grafted onto a butadiene based elastomeric backbone (Implex R sold by Rohm &amp; Haas Company). 
     This blend was prepared by extrusion blending the components at about 270° C. in a single screw 1-inch diameter extruder with L/D=36/1. The extrudate was chopped into pellets. The pelletized product was then injection molded into ASTM test specimens (at 270°-300° C.) using a Newbury 11/4 ounce screw injection molding machine. The test specimens were measured for the following properties: tensile strength and modulus according to ASTM D-638; elongation at break according to ASTM D-638; flexural strength and modulus according to ASTM-790; notched izod impact strength according to ASTM D-256; tensile impact strength according to ASTM D-1822; heat distortion temperature measured at 264 psi on a 1/8 inch thick unannealed test bar according to ASTM D-635. Also, the surface appearance of the molded article is described. 
     The results are shown in Table 8. 
     EXAMPLE 17 
     40 weight percent of a polyarylate, Ardel D-100, was blended with 40 weight percent of poly(methyl methacrylate) as described in Control S and 20 weight percent of a copolyester, 7-DRO, described in Control K. 
     The blend was prepared, molded into test bars and tested as described in Control S. 
     The results are shown in Table 8. 
     
                       TABLE 8                                                     
______________________________________                                    
Example                                                                   
Description of the                                                        
Composition.sup.1                                                         
                 Control S   17                                           
______________________________________                                    
Polymer (wt.%)   PA (60)     PA (40)                                      
                 PMMA (40)   PE (20)                                      
                             PMMA (40)                                    
Tensile modulus (psi)                                                     
                 306,000     314,000                                      
Tensile strength (psi)                                                    
                 7,830       7,640                                        
Elongation (percent)                                                      
                 34          76                                           
Flexural modulus (psi)                                                    
                 315,000     317,000                                      
Flexural strength (psi)                                                   
                 11,800      12,100                                       
Notched Izod Impact Strength                                              
(ft.-lbs./in. of notch)                                                   
                 0.90        1.2                                          
Tensile impact strength                                                   
(ft.-lbs./in..sup.3)                                                      
                 62          102                                          
Surface appearance of                                                     
                 Rough irregu-                                            
                             Glossy, smooth                               
injection molded bars                                                     
                 lar surface surface                                      
______________________________________                                    
 .sup.1 PA = polyarylate                                                  
 PMMA = poly(methyl methacrylate)                                         
 PE = copolyester, 7DRO                                                   
 
    
     The data in the Table shows that the addition of poly(1,4-cyclohexanedimethanol tere/isophthalate) to a polyarylate/poly(methyl methacrylate) blend shows an improvement in the surface characteristics of injection molded articles and also provides improvement in mechanical properties. 
     CONTROL T 
     Poly(methyl methacrylate) grafted onto butadiene based rubber (Plexiglas DR sold by Rohm &amp; Haas Co. and having the properties described in Table 9) was injection molded into ASTM test specimens (at 240° C.) using a Newbury 11/4 ounce screw injection molding machine. The test specimens were measured for the following properties: tensile strength and modulus according to ASTM D-638; flexural strength and modulus according to ASTM D-790; elongation at break according to ASTM D-638; notched izod impact strength according to ASTM D-256; tensile impact strength according to ASTM D-1822; heat distortion temperature measured at 264 psi on a 1/8 inch thick unannealed test bar according to ASTM D-635. The appearance of the molded surface after molding into test bars is described. 
     The results are shown in Table 9. 
     CONTROL U 
     67 weight percent of a polyarylate, Ardel D-100, described in Example 1 was blended with 33 weight percent of a copolyester, PETG-6763, described in Control E. 
     This blend was prepared by extrusion blending the components at about 270° C. in a single screw 1-inch diameter extruder with L/D=36/1. The extrudate was chopped into pellets. The pelletized product was then injection molded into ASTM test specimens and tested as described in Control T. 
     The results are shown in Table 9. 
     CONTROL V 
     60 weight percent of a polyarylate, Ardel D-100, was blended with 40 weight percent of a poly(methyl methacrylate) resin (Plexiglas DR) described in Control T. 
     The blend was prepared as described in Control U. The product was molded into test bars and tested as described in Control T. 
     The results are shown in Table 9. 
     EXAMPLE 18 
     40 weight percent of a polyarylate, Ardel-D-100, was blended with 20 weight percent of a copolyester, PETG-6763, and 40 weight percent of a poly(methyl methacrylate) resin (Plexiglas DR) described in Control T. 
     The blend was prepared as described in Control U. The product was molded into test bars and tested as described in Control T. 
     The results are shown in Table 9. 
     The data in the Table show that when a ternary blend of polyarylate, copolyester, and poly(methyl methacrylate), according to this invention, is molded it has a surface which is uniform and smooth in comparison to a blend of polyarylate and poly(methyl methacrylate) where the the resultant molded article has a surface which is irregular and rough. The ternary blend of this invention also has an acceptable combination of mechanical properties. 
     
                                           TABLE 9                                 
__________________________________________________________________________
                                    Notched                               
                           Flex-    Izod   Tensile                        
                                                Heat                      
             Tensile       ural     Impact Impact                         
                                                Distor-                   
    Description of                                                        
             Mod-                                                         
                 Tensile                                                  
                      Elonga-                                             
                           Mod-                                           
                               Flexural                                   
                                    Strength                              
                                           Strength                       
                                                tion                      
                                                    Appearance of         
Ex- the Composition.sup.1                                                 
             ulus                                                         
                 Strength                                                 
                      tion ulus                                           
                               Strength                                   
                                    (ft.-lbs./                            
                                           (ft.-lbs./                     
                                                Temp.                     
                                                    molded                
ample                                                                     
    Polymer                                                               
         (wt. %)                                                          
             (psi)                                                        
                 (psi)                                                    
                      (percent)                                           
                           (psi)                                          
                               (psi)                                      
                                    (in. of Notch)                        
                                           in..sup.2)                     
                                                (°C.)              
                                                    Surface               
__________________________________________________________________________
Con-                                                                      
    PMMA 100 242,000                                                      
                 5,780                                                    
                      48   277,000                                        
                                9,390                                     
                                    1.17   42    70 Uniform and Smooth    
trol T                                                                    
Con-                                                                      
    PA   67  321,000                                                      
                 9,710                                                    
                      33   335,000                                        
                               15,800                                     
                                    2.5    133  113 Uniform and Smooth    
trol U                                                                    
    PE   33                                                               
Con-                                                                      
    PA   60  268,000                                                      
                 8,250                                                    
                      78   --  --   0.90   17   104 Irregular and         
trol V                                                                    
    PMMA 40                                         Rough                 
18  PA   40  297,000                                                      
                 8,440                                                    
                      47   --  --   1.0    94   98  Uniform and Smooth    
    PE   20                                                               
    PMMA 40                                                               
__________________________________________________________________________
 .sup.1 PMMA = poly(methyl methacrylate), Plexiglas DR                    
 PA = polyarylate                                                         
 PE = copolyester, PETG6763-                                              
 
    
     CONTROL W 
     A polyurethane (Pellethane 2102-80A sold by Upjohn Company and having the mechanical properties described in Table 10) was injection molded into ASTM test bars (at 200° C.) using a Newbury 1 1/4 ounce screw injection molding machine. The test bars were measured for the following properties: tensile strength and modulus according to ASTM D-638, and elongation at break according to ASTM D-638. 
     The results are shown in Table 10. 
     Preparation of blend of polyarylate and poly(ethylene-terephthalate): 60 weight percent of polyarylate (Ardel D-100 sold by Union Carbide Corporation and prepared from Bisphenol-A and a mixture of 50 mole percent each of terephthalic and isophthalic acid chlorides, by conventional methods, having a reduced viscosity of 0.66 as measured in p-chlorophenol at 49° C., 0.2 g/100 ml.) was blended with 40 weight percent of poly(ethylene terephthalate) having an intrinsic visosity of 0.64 as measured in a 60/40 1,1,2,2-tetrachloroethane/phenol mixture at 25° C. 
     This blend was prepared by extrusion blending the components at about 270° C. in a single screw 1-inch diameter extruder with L/D=36/1. 
     EXAMPLE 19 
     20 weight percent of the blend of polyarylate and poly(ethylene terephthalate) described above was blended with 80 weight percent of the polyurethane, Pellethane 2102-80A, described in Control W. 
     The blend was prepared by extrusion blending the components at about 210°-220° C. in a single screw 1-inch diameter extruder with L/D=36/1. The extrudate was chopped into pellets. The pelletized product was molded into test bars and tested by the procedures as described in Control W. 
     The results are shown in Table 10. 
     EXAMPLE 20 
     The procedure of Example 19 was exactly repeated except that 40 weight percent of the blend of polyarylate and poly(ethylene terephthalate) and 60 weight percent of the polyurethane were used. 
     The results are shown in Table 10. 
     CONTROL X 
     A polyurethane (Texin 355 DXH sold by Mobay Chemical Co. and having the mechanical properties described in Table 10) was injection molded into test bars and tested by the procedures as described in Control W. 
     The results are shown in Table 10. 
     EXAMPLE 21 
     20 weight percent of the blend of polyarylate and poly(ethylene terephthalate) described above was blended with 80 weight percent of the polyurethane, Texin 355 DXH, described in Control X. 
     The blend was prepared by extrusion blending the components at about 210°-220° C. in a single screw 1-inch diameter extruder with L/D=36/1. The extrudate was chopped into pellets. The pelletized product was molded into test bars and tested by the procedures as described in Control W. 
     The results are shown in Table 10. 
     EXAMPLE 22 
     The procedure of Example 21 was exactly repeated except that 40 weight percent of the blend of polyarylate and poly(ethylene terephthalate) and 60 weight percent of the polyurethane were used. 
     The results are shown in Table 10. 
     CONTROL Y 
     A thermoplastic polyurethane (Pellethane 2102-55D sold by Upjohn Company and having the mechanical properties described in Table 10) was injection molded into test bars and tested by the procedures as described in Control W. 
     The results are shown in Table 10. 
     EXAMPLE 23 
     40 weight percent of the blend of polyarylate and poly(ethylene terephthalate) described above was blended with 60 weight percent of the polyurethane, Pellethane 2102-55D, described in Control Y. 
     The blend was prepared by extrusion blending the components at about 200°-210° C. in a single screw 1-inch diameter extruder with L/D=36/1. The extrudate was chopped into pellets. The pelletized product was molded into test bars and tested by the procedures as described in Control W. 
     The results are shown in Table 10. 
     The data in Table 10 shows that the addition of polyarylate/poly(ethylene terephthalate) blends to thermoplastic polyurethanes yields higher modulus products while retaining good strength and ultimate elongation. This method of polymeric reinforcement offers distinct advantages over inorganic filler or fiber reinforcement. Commercially, the maximum tensile modulus of unreinforced thermoplastic polyurethanes is 20,000 psi. The terpolymer of this invention yields improved load bearing properties including lower creep and lower deformation under load. 
     
                                           TABLE 10                                
__________________________________________________________________________
                      Testing Rate                                        
                      Two inch/min.                                       
                                 Twenty inch/min.                         
Description of   Tensile                                                  
                      Tensile    Tensile                                  
the Composition.sup.1                                                     
                 Modulus                                                  
                      Strength                                            
                           Elongation                                     
                                 Strength                                 
                                      Elongation                          
Example                                                                   
      Polymer                                                             
             (wt.%)                                                       
                 (psi)                                                    
                      (psi)                                               
                           (percent)                                      
                                 (psi)                                    
                                      (percent)                           
__________________________________________________________________________
Control W                                                                 
      PU.sup.(a)                                                          
             100  6,900                                                   
                      7,240                                               
                           465   4,850                                    
                                      563                                 
19    PA (60)                                                             
             20   8,900                                                   
                      6,010                                               
                           455   3,480                                    
                                      520                                 
      PE (40)                                                             
      PU.sup.(a)                                                          
             80                                                           
20    PA (60)                                                             
             40  24,200                                                   
                      4,710                                               
                           300   3,570                                    
                                      268                                 
      PE (40)                                                             
      PU.sup.(a)                                                          
           60                                                             
Control X                                                                 
      PU.sup.(b)                                                          
             100 10,900                                                   
                      4,550                                               
                           298   3,010                                    
                                      342                                 
21    PA (60)                                                             
             20  19,500                                                   
                      5,630                                               
                           288   4,060                                    
                                      305                                 
      PE (40)                                                             
      PU.sup.(b)                                                          
             80                                                           
22    PA (60)                                                             
             40  53,300                                                   
                      5,110                                               
                           212   4,320                                    
                                      200                                 
      PE (40)                                                             
      PU.sup.(b)                                                          
             60                                                           
Control Y                                                                 
      PU.sup.(c)                                                          
             100 14,800                                                   
                      8,780                                               
                           372   7,210                                    
                                      437                                 
23    PA (60)                                                             
             40  63,100                                                   
                      7,050                                               
                           268   5,150                                    
                                      257                                 
      PE (40)                                                             
      PU.sup.(c)                                                          
             60                                                           
__________________________________________________________________________
 .sup.1 PA = polyarylate?                                                 
 .sup.(a) = Pellethane 210280A                                            
 PE = poly(ethylene terephthalate)                                        
 .sup.(b) = Texin 355 DXH                                                 
 PU = polyurethane                                                        
 .sup.(c) = Pellethane 210255D                                            
 
    
     CONTROL Z 
     A thermoplastic polyurethane (Pellethane 2102-55D sold by Upjohn Company and having the mechanical properties described in Table 11) was compression molded into samples at 210° C. in a 4×4×0.20 inch mold cavity into test samples. These samples were exposed in an artificial weathering unit for 500, 1000 and 2000 hours by the procedure as described in ASTM-D-1499. From the exposed specimens, 1/8 inch wide specimens were shear cut to determine the tensile strength according to a procedure similar to ASTM D-638. The initial tensile strength after molding is shown in Table II and the percent of the retention of the tensile strength of the samples is reported after 500, 1000 and 2000 hours of exposure in the weathering unit (Weatherometer). 
     The results are shown in Table 11. 
     Preparation of blend of polyarylate and poly(ethylene terephthalate): 60 weight percent of polyarylate, Ardel-D-100, was blended with 40 weight percent of poly(ethylene terephthalate) having an intrinsic viscosity of 0.64 as measured in a 60/40 1,1,2,2-tetrachlorethane/phenol mixture at 25° C. 
     The blend was prepared by extrusion blending the components at 270° C. into pellets in a single screw 1-inch diameter extruder with L/D=36/1. 
     EXAMPLE 24 
     10 weight percent of the blend of polyarylate and poly(ethylene terephthalate) described above was blended with 90 weight percent of the polyurethane, Pellethane 55D, described in Control Z. 
     The blend was prepared by mixing the components in a Brabender blender at about 210°-230° C. The product was tested by the procedure of Control Z. 
     The results are shown in Table 11. 
     EXAMPLE 25 
     The procedure of Example 24 was exactly repeated except that 20 weight percent of the blend of polyarylate and poly(ethylene terephthalate) and 80 weight percent of the polyurethane were used. 
     The results are shown in Table 11. 
     The data in the Table show improved retention of tensile strength after artificial weathering exposure with addition of low levels of polyarylate. The addition of the polyarylate/poly(ethylene terephthalate) blend to the thermoplastic polyurethane did not detract from the excellent tensile strength exhibited by the thermoplastic polyurethane. 
     
                                           TABLE 11                                
__________________________________________________________________________
                       Testing Rate                 Retention of Initial  
                       Two inch/min.                                      
                                  Twenty inch/min.  Tensile Strength (%)  
Description of    Tensile                                                 
                       Tensile    Tensile    Initial Tensile              
                                                     after Exposure in    
Composition.sup.1 Modulus                                                 
                       Strength                                           
                            Elongaton                                     
                                  Strength                                
                                       Elongation                         
                                             Strength                     
                                                    Weatherometer for:    
Example                                                                   
      Polymer                                                             
             (wt.%)                                                       
                  (psi)                                                   
                       (psi)                                              
                            (percent)                                     
                                  (psi)                                   
                                       (percent)                          
                                             (psi)  500                   
                                                       1000               
                                                          2000(hrs)       
__________________________________________________________________________
Control Z                                                                 
      PU     100  14,800                                                  
                       10,500                                             
                            528   8,860                                   
                                       427   10,500 44 35 22              
24    PA (60)                                                             
             10   20,300                                                  
                       10,200                                             
                            502   9,190                                   
                                       431   10,200 66 49 24              
      PET (40)                                                            
      PU     90                                                           
25    PA (60)                                                             
             20   26,800                                                  
                       10,200                                             
                            658   7,990                                   
                                       372   10,200 73 39 31              
      PET (40)                                                            
      PU     80                                                           
__________________________________________________________________________
 .sup.1 PU = polyurethane                                                 
 PA = polyarylate                                                         
 PET = poly(ethylene terephthalate)                                       
 
    
     CONTROL AA 
     A poly(ether-ester) (AB) n  block copolymer (Hytrel 5555 sold by E. I. du Pont Company and having the mechanical properties listed in Table 12) was injection molded into ASTM test bars (at 220°-230° C.) using a Newbury 1 1/4 ounce screw injection molding machine. The test bars were measured for the following properties: tensile strength and modulus according to ASTM D-638, and elongation at break according to ASTM D-638. 
     The results are shown in Table 12. 
     Preparation of Blend of Polyarylate and Poly(ethylene terephthalate) 
     60 weight percent of polyarylate, Ardel D-100 was blended with 40 weight percent of poly(ethylene terephthalate) having an intrinsic viscosity of 0.64 as measured in a 60/40 1,1,2,2-tetrachloroethane/phenol mixture at 25° C. 
     The blend was prepared by extrusion blending the components into pellets at 270° C. in a single screw 1-inch diameter extruder with L/D=36/1. 
     EXAMPLE 26 
     20 weight percent of the polyarylate/poly(ethylene terephthalate) blend prepared above was blended with 80 weight percent of the block copolymer (Hytrel 5555) described in Control AA. 
     The blend was prepared by extrusion blending the components into pellets at 220°-230° C. in a single screw 1-inch diameter extruder with L/D=36/1. The pellets were injection molded into ASTM test bars and tested by the procedures described in Control AA. 
     The results are shown in Table 12. 
     EXAMPLE 27 
     Example 26 was exactly repeated except that 40 weight percent of the polyarylate/poly(ethylene terephthalate) blend and 60 weight percent of the block copolymer (Hytrel 5555) was used. 
     The results are shown in Table 12. 
     CONTROL BB 
     A poly(butylene terephthalate)-polytetrahydrofuran (AB) n  block copolymer (Hytrel 6345 sold by E. I. du Pont Company and having the mechanical properties listed in Table 12) was injection molded into ASTM test bars and tested by the procedures described in Control AA. 
     The results are shown in Table 12. 
     EXAMPLE 28 
     20 weight percent of the polyarylate/poly(ethylene terephthalate) blend prepared above was blended with the block copolymer (Hytrel 6345) described in Control BB. 
     The blend was prepared by extrusion blending the components into pellets at 220°-230° C. in a single screw 1-inch diameter extruder with L/D=36/1. The pellets were injection molded into ASTM bars and tested by the procedures described in Control AA. 
     The results are shown in Table 12. 
     EXAMPLE 29 
     Example 28 was exactly repeated except that 40 weight percent of the polyarylate/poly(ethylene terephthlate blend and 60 weight percent of the block copolymer (Hytrel 6345) were used. 
     The results are shown in Table 12. 
     The data in the Table show that addition of the polyarylate/poly(ethylene terephthalate) blend to the block copolymer results in a significant increase in modulus while maintaining the excellent tensile strength inherent in these block copolymers. The increased modulus will improve the resistance to deformation under load. 
     
                                           TABLE 12                                
__________________________________________________________________________
                        Testing Rate                                      
                        Two inch/min                                      
                                   Twenty inch/min                        
       Description of the                                                 
                   Tensile                                                
                        Tensile    Tensile                                
       Composition Modulus                                                
                        Strength                                          
                             Elongation                                   
                                   Strength                               
                                        Elongation                        
Example                                                                   
       Polymer                                                            
              (wt. %)                                                     
                   (psi)                                                  
                        (psi)                                             
                             (percent)                                    
                                   (psi)                                  
                                        (percent)                         
__________________________________________________________________________
Control AA                                                                
       BC.sup.(a)                                                         
              100  29,600                                                 
                        5,800                                             
                             537   5,090                                  
                                        607                               
26     BC.sup.(a)                                                         
              80   50,600                                                 
                        5,010                                             
                             397   4,480                                  
                                        430                               
       PA(60)                                                             
              20                                                          
       PET(40)                                                            
27     BC.sup.(a)                                                         
              60   97,600                                                 
                        4,910                                             
                             243   4,530                                  
                                        270                               
       PA(60)                                                             
              40                                                          
       PET(40)                                                            
Control BB                                                                
       BC.sup.(b)  50,900                                                 
                        5,600                                             
                             455   4,720                                  
                                        440                               
28     BC.sup.(b)                                                         
              80   107,000                                                
                        5,650                                             
                             322   4,920                                  
                                        485                               
       PA(60)                                                             
              20                                                          
       PET(40)                                                            
29     BC.sup.(b)                                                         
              60                                                          
       PA(60)                                                             
              40   202,000                                                
                        5,570                                             
                             265   4,750                                  
                                         60                               
       PET(40)                                                            
 .sup.1 BC = block copolymer                                              
 .sup.(a) = Hytrel 5555                                                   
 PA = polyarylate                                                         
 .sup.(b) = Hytrel 6345                                                   
 PET = poly(ethylene terephthalate)                                       
 
    
     CONTROL CC 
     A poly(ether-ester) (AB) n  block copolymer, Hytrel 5555, described in Control AA was compression molded at 230° C. in a 4×4×0.20 inch mold cavity to form 20 mil samples. These samples were exposed in an artificial weathering unit for 500 and 1000 hours by the procedure as described in ASTM D-1499. From the exposed specimens, 1/8 inch wide specimens were shear cut to determine the tensile strength according the procedure of ASTM D-638. The initial tensile strength after molding is shown in Table 13 and the percent of the retention of the tensile strength of the samples is reported after 500 and 1000 hours of exposure in the weathering unit (Weathermometer). 
     The results are shown in Table 13. 
     PREPARATION OF A BLEND OF POLYARYLATE AND POLY(ETHYLENE TEREPHTHALATE) 
     60 weight of polyarylate, Ardel-D-100, was blended with 40 weight percent of poly(ethylene terephthalate) having an intrinsic viscosity of 0.64 as measured in a 60/40 1,1,2,2-tetrachloroethane/phenol mixture at 25° C. 
     The blend was prepared by extrusion blending the components at 270° C. into pellets in a single screw 1-inch diameter extruder with L/D=36/1. 
     EXAMPLE 30 
     10 weight percent of the polyarylate/poly(ethylene terephthalate) blend prepared above was blended with 90 weight percent of the block copolymer (Hytrel 5555) described in Control CC. 
     The blend was prepared by mixing the components in a Brabender blender at 220°-230° C. The blend was then tested by the procedures described in Control CC. 
     The results are shown in Table 13. 
     EXAMPLE 31 
     Example 31 was exactly repeated except that 20 weight percent of the polyarylate/poly(ethylene-terephthalate) blend and 80 weight percent of the block copolymer (Hytrel 5555) was used. 
     The results are shown in Table 13. 
     CONTROL DD 
     A poly(butylene terephthalate)-polytetrahydrofuran (AB) n  block copolymer, Hytrel 6345, described in Control BB was compression molded and tested by the procedure described in Control CC. 
     The results are shown in Table 13. 
     EXAMPLE 32 
     10 weight percent of the polyarylate/polyethylene terephthalate) blend prepared above was blended with 90 weight percent of the block copolymer (Hytrel 6345) described in Control DD. 
     The blend was prepared by mixing the components in a Brabender blender at 220°-230° C. the blend was then tested by the procedure described in Control CC. 
     The results are shown in Table 13. 
     EXAMPLE 33 
     Example 32 was exactly repeated except that 20 weight percent of the polyarylate/poly(ethylene-terephthalate) blend and 80 weight percent of the block copolymer (Hytrel 6345) was used. 
     The results are shown in Table 13. 
     The results in the Table show that the block copolymers degrade very rapidly under the test conditions. The addition of a blend of polyarylate/poly(ethylene-terephthalate) to the block copolymer results in improved tensile strength retention of the poly(ether-ester) block copolymer after weathering. 
     
                                           TABLE 13                                
__________________________________________________________________________
                      Initial tensile                                     
                             Retention of Initial Tensile Strength (%)    
       Description of the Composition                                     
                      strength                                            
                             After Exposure in Weatherometer for          
Example                                                                   
       Polymer (wt. %)                                                    
                      (psi)  500    1000   (hrs)                          
__________________________________________________________________________
Control CC                                                                
       BC.sup.(a)                                                         
               100    7710    8.3   0                                     
30     BC.sup.(a)                                                         
               90     5750   18.4   14.6                                  
       PA(60)  10                                                         
       pET(40)                                                            
31     BC.sup.(a)                                                         
               80     5160   37.0   22.7                                  
       PA(60)  20                                                         
       PET(40)                                                            
Control DD                                                                
       BC.sup.(b)                                                         
               100    7790   25.6   11.8                                  
32     BC.sup.(b)                                                         
               90     6790   17.2   17.4                                  
       PA(60)  10                                                         
       PET(40)                                                            
33     BC.sup.(b)                                                         
               80     6940   27.8   21.8                                  
       PA(60)  20                                                         
       PET(40)                                                            
__________________________________________________________________________
 .sup.1 BC = block copolymer                                              
 .sup.(a) = Hytrel 5555                                                   
 PA = polyarylate                                                         
 .sup.(b) = Hytrel 6345                                                   
 PET = poly(ethylene terephthalate)                                       
 
    
     CONTROL EE 
     100 weight percent of poly(vinyl chloride) having an inherent viscosity of 0.78 (as measured by ASTM-D1243, Method A) (QSAH-7 sold by Union Carbide Corporation) was mixed with 4 parts by weight of an organo tin thermal stabilizer (TM-181 sold by Cincinnati Milacron). This mixture was compression molded at 180° C. in a 4×4×0.20 inch mold cavity to form 20 mil samples. These samples were exposed to an artificial weathering unit for 500 and 1000 hours by the procedure as described in ASTM D-1499. From the exposed specimens, 1/8 inch wide specimens were shear cut to determine the tensile strength according to the procedure of ASTM D-638. The initial tensile strength after molding is shown in Table 14 and the percent of the retention of the tensile strength of the samples is reported after 500 and 1000 hours of exposure in the weathering unit (Weatherometer). The color of the sample after 1000 hours of exposure is also shown. 
     The results are shown in Table 14. 
     PREPARATION OF A BLEND OF POLYARYLATE AND POLY(ETHYLENE TEREPHTHALATE) 
     60 weight percent of polyarylate, Ardel D-100, was blended with 40 weight percent of poly(ethylene terephthalate) having an intrinsic viscosity of 0.64 as measured in a 60/40 1,1,2,2-tetrachloroethane/phenol mixture at 25° C. 
     The blend was prepared by extrusion blending the components at 270° C. into pellets in a single screw 1-inch diameter extruded with L/D=36/1. 
     EXAMPLE 34 
     10 parts by weight of the polyarylate/poly(ethylene terephthalate) blend prepared above was blended with the mixture of 100 parts by weight of the poly(vinyl chloride) and 4 parts by weight of the stabilizer as described in Control EE. 
     The blend was prepared by blending the two premixed blends on a two roll mill at 170°-180° C. roll temperature. The blend was then tested by the procedure described in Control EE. 
     The results are shown in Table 14. 
     EXAMPLE 35 
     Example 34 was exactly repeated except that 20 parts by weight of the polyarylate/poly(ethylene terephthalate) blend was used. 
     The results are shown in Table 14. 
     CONTROL FF 
     100 parts by weight of the poly(vinyl chloride) (QYSA sold by Union Carbide Corporation) having an inherent viscosity of 0.63 (as measured by ASTM D-1243, Method A) was mixed with 4 parts by weight of a thermal stabilizer (TM-181) described in Control EE. The mixture was compression molded and tested by the procedure described in Control EE. 
     The results are shown in Table 14. 
     EXAMPLE 36 
     20 parts by weight of the polyarylate/poly(ethylene terephthalate) blended prepared above was blended with a mixture of 100 parts by weight of poly(vinyl chloride) and 4 parts by weight of the stabilizer as described in Control EE. 
     The blend was prepared by blending the two premixed blends on a two roll mill at 170°-180° C. roll temperature. The blend was then tested by the procedure described in Control EE. 
     The results are shown in Table 14. 
     The results in the Table show that the ternary blends of polyarylate/poly(ethylene terephthalate) and poly(vinyl chloride), according to this invention have improved retention of tensile strength and also exhibit lower discoloration after exposure of 1000 hours in comparison to the poly(vinyl chloride). 
     
                                           TABLE 14                                
__________________________________________________________________________
       Description of the                                                 
                     Initial Tensile                                      
                            Retention of Initial Impact Strength          
                                               Color of Sample            
       Composition   strength                                             
                            After Exposure in Weatherometer               
                                               After 1000 hrs             
Example                                                                   
       Polymer                                                            
              (Parts by wt.)                                              
                     (psi)  500      1000 (hrs)                           
                                               Exposure                   
__________________________________________________________________________
                                               1                          
Control EE                                                                
       PVC.sup.(a)                                                        
              100    7620   104      93        Brown                      
34     PVC.sup.(a)                                                        
              100    6990   109      109       Light yellow               
       PA(60)                                                             
               10                                                         
       PET(40)                                                            
35     PVC.sup.(a)                                                        
              100    7040   108      118       Light yellow               
       PA(60)                                                             
               20                                                         
       PET(40)                                                            
Control FF                                                                
       PVC.sup.(b)                                                        
              100    6980   114      65        Brown                      
36     PVC.sup.(b)                                                        
              100    6440    97      89        Light yellow               
       PA(60)                                                             
               20                                                         
       PET(40)                                                            
__________________________________________________________________________
 .sup.1 PVC = poly(vinyl chloride)                                        
 .sup.(a) = QSAH7 poly(vinyl chloride)                                    
 PA = polyarylate                                                         
 .sup.(b) QYSA poly(vinyl chloride)                                       
 PET = poly(ethylene terephthalate)                                       
 
    
     EXAMPLE 37 
     50 weight percent of poly(hydroxy ether) having a reduced viscosity of 0.41 as measured in methylene chloride (Phenoxy PKHH sold by Union Carbide Corporation) was blended with 33.5 weight percent of polyarylate, Ardel D-100, and 16.5 weight percent of a copolyester, PETG-6763 (a copolyester prepared by the reaction of cyclohexanedimethanol and ethylene glycol with terephthalic acid, in a molar ratio of 1:2:3. This polyester has a M n  of about 26,000 and is sold by Tennessee Eastman Company). 
     The blend was prepared by extrusion blending the components at 265° C. in a single screw 1-inch diameter extruder with L/D=36/1. The extrudate was chopped into pellets. The pelletized product was injected molded into ASTM test specimens (250°-265° C.) using a Newbury 11/4 ounce screw injection molding machine. The test specimens were measured for the following properties: tensile strength and modulus according to ASTM D-638; elongation at break according to ASTM D-638; and notched izod impact strength according to ASTM D-256. The results are shown in Table 15 as follows: 
     
                       TABLE 15                                                    
______________________________________                                    
Tensile modulus (psi)    409,000                                          
Tensile strength (psi)   10,100                                           
Elongation (%)           45                                               
Notched Izod Impact Strength                                              
                         1.1                                              
(ft. lbs./in. of notch)                                                   
______________________________________                                    
 
    
     Blends of poly(hydroxy ether) and polyarylate are very difficult to prepare and injection mold due to the potential of crosslinking due to transesterification. However, the addition of a copolyester to the poly(hydroxy ether) and polyarylate allows for sufficient blending and fabrication lattitude for forming injection molded articles. The ternary blend has good mechanical properties. 
     CONTROL GG 
     A polyarylate, Ardel D-100, was tested for melt flow by the apparatus and procedure as described in ASTM-D-1238. 
     The results are shown in Table 16. 
     CONTROL HH 
     75 weight percent of polyarylate, Ardel D-100, was blended with 25 weight percent of poly(ethylene terephthalate) having an intrinsic viscosity of 0.64 as measured in a 60/40 1,1,2,2-tetrachloroethane/phenol mixture at 25° C. 
     The blend was prepared by extrusion blending the components into pellets at 270° C. in a single screw 1-inch diameter extruder with L/D=36/1. The blend was tested for melt flow according to the procedure described in Control GG. 
     The results are shown in Table 16. 
     In the following Controls and Examples the materials identified therein were blended together by extrusion blending the components into pellets at 260°-280° C. in a single screw 1-inch diameter extruder with L/D=36/1. The blends were then tested for melt flow according to the procedure described in Control GG. 
     CONTROL II 
     70 weight percent of polyarylate, Ardel D-100 was blended with 30 weight percent of K-2938 described in Control L. 
     EXAMPLE 38 
     70 weight percent of the polyarylate/poly(ethylene terephthalate) blend of Control HH was blended with 30 weight percent of the ABS (K-2938) of Control II. 
     CONTROL JJ 
     60 weight percent of polyarylate; Ardel D-100 was blended with 40 weight percent of the ABS (K-2938) of Control II. 
     EXAMPLE 39 
     60 weight percent of the polyarylate/poly(ethylene terephthalate) blend of Control HH was blended with 40 weight percent of the ABS (K-2938) of Control II. 
     CONTROL KK 
     70 weight percent of polyarylate, Ardel D-100, was blended with 30 weight percent of poly(methyl methacrylate) grated onto a butadiene based rubber (Plexiglas DR described in Control T). 
     EXAMPLE 40 
     70 weight percent of the polyarylate/poly(ethylene terephthalate) blend of Control HH was blended with 30 weight percent of poly(methyl methacrylate) described in Control KK. 
     CONTROL LL 
     60 weight percent of polyarylate, Ardel D-100, was blended with 40 weight percent of poly(methyl methacrylate) described in Control KK. 
     EXAMPLE 41 
     60 weight percent of the polyarylate/poly(ethylene terephthalate) blend of Control HH was blended with 40 weight percent of poly/methyl methacrylate) described in Control KK. 
     CONTROL MM 
     50 weight percent of polyarylate, Ardel D-100, was blended with 50 weight percent of polysulfone having a reduced viscosity of 0.48 as measured in chloroform at 25° C. (0.2 g/dl) (P-1700 sold by Union Carbide Corporation). 
     EXAMPLE 42 
     50 weight percent of the polyarylate/poly(ethylene terephthalate) blend of Control HH was blended with 50 weight percent of the polysulfone of Control MM. 
     The results are shown in Table 16. 
     The data in the Table shows that the ternary blends of this invention have improved processability as shown by the increased melt flow. Increased melt flow results in a lower injection molding temperature. 
     
                       TABLE 16                                                    
______________________________________                                    
       Description of the                                                 
       Composition   Melt Flow (dg./min) at                               
Example  Polymer     (wt %)  300° C.                               
______________________________________                                    
Control GG                                                                
         PA              100   0.38                                       
Control HH                                                                
         PA              75    3.4                                        
         PET             25                                               
Control II                                                                
         PA              70    2.8                                        
         ABS             30                                               
38       PA(75)                                                           
                         70    8.9                                        
         PET(25)                                                          
         ABS             30                                               
Control JJ                                                                
         PA              60    3.1                                        
         ABS             40                                               
39       PA(75)                                                           
                         60    13.3                                       
         PET(25)                                                          
         ABS             40                                               
Control KK                                                                
         PA              70    3.6                                        
         PMMA            30                                               
40       PA(75)                                                           
                         70    36.8                                       
         PET(25)                                                          
         PMMA            30                                               
Control LL                                                                
         PA              60    13.1                                       
         PMMA            40                                               
41       PA(75)                                                           
                         60    42.6                                       
         PET(25)                                                          
         PMMA            40                                               
Control MM                                                                
         PA              50    1.4                                        
         PS              50                                               
42       PA(75)                                                           
                         50    4.5                                        
         PET(25)                                                          
         PS              50                                               
______________________________________                                    
 .sup.1 PA = polyarylate                                                  
 PET = poly(ethylene terephthalate)                                       
 ABS = K2938                                                              
 PMMA = poly(methyl methacrylate)                                         
 PS = polysulfone                                                         
 
    
     PREPARATION OF A BLEND OF POLYCARBONATE, POLY(ETHYLENE TEREPHTHALATE) AND POLYARYLATE 
     33 weight percent of polycarbonate (Lexan 101 described in Control A) was blended with 33 weight percent of poly(ethylene terephthalate) having an intrinsic viscosity of 1.04 as measured in 60:40 phenol/tetrachloromethane mixture at 23° C., and 34 weight percent of polyarylate, Ardel D-100. 
     The blend was prepared by extrusion blending the components at 290° C. in a single screw 1-inch diameter extruder with L/D=36/1. The extrudate was chopped into pellets. 
     EXAMPLE 43 
     55 weight percent of the blend of polycarbonate, polyarylate and poly(ethylene terephthalate) prepared above was blended with 45 weight percent of ABS (K-2938 described in Control L). 
     The blend was prepared by extrusion blending the components at 270° C. in a single screw 1-inch diameter extruder with L/D=36/1. The extrudate was chopped into pellets. The pelletized product was then injection molded into ASTM test specimens (at 270° C.) using a Newbury 11/4 ounce screw injection molding machine. The test specimens were measured for the following properties: tensile strength and modulus according to ASTM D-638, elongation at break according to ASTM D-638; tensile impact strength according to ASTM D-1822 and notched izod impact strength according to ASTM D-256. 
     The results are shown in Table 17. 
     EXAMPLE 44 
     55 weight percent of the blend of polycarbonate, polyarylate and poly(ethylene terephthalate) prepared above was blended with 45 weight percent of poly(methyl methacrylate) grafted onto a butadiene based rubber (Plexiglas DR as described in Control T). The blend was prepared by the procedure described in Example 43. The product was pelletized, molded into test bars and tested by the procedures described in Example 43. 
     The results are shown in Table 17. 
     EXAMPLE 45 
     90 weight percent of the blend of polycarbonate, polyarylate, and poly(ethylene terephthalate) prepared above was blended with 10 weight percent of KM-611 (a styrene/acrylate/butadiene terpolymer having a tensile modulus of 43,600 psi and sold by Rohm and Haas Company). The blend was prepared by the procedure described in Example 43. The product was pelletized, molded into test bars and tested by the procedures described in Example 43. 
     The results are shown in Table 17. 
     
                                           TABLE 17                                
__________________________________________________________________________
Description of the                                                        
                 Tensile                                                  
                      Tensile    Tensile Impact                           
                                         Notched Izod                     
Composition      Modulus                                                  
                      Strength                                            
                           Elongation                                     
                                 Strength                                 
                                         Impact Strength                  
Example                                                                   
     Polymer                                                              
            (wt. %)                                                       
                 (psi)                                                    
                      (psi)                                               
                           (percent)                                      
                                 (ft. lbs/in.sup.2)                       
                                         (ft. lbs/in. of                  
__________________________________________________________________________
                                         Notch                            
43   PC (33)                                                              
     PET(33)                                                              
            55   315,000                                                  
                      7310 42    72      1.2                              
     PA (34)                                                              
     ABS    45                                                            
44   PC (33)                                                              
     PET(33)                                                              
            55   287,000                                                  
                      7560 45    49      1.1                              
     PA (34)                                                              
     PMMA   45                                                            
45   PC (33)                                                              
     PET(33)                                                              
            90   303,000                                                  
                      8360 93    128     13.6                             
     PA (34)                                                              
     KM-611 10                                                            
__________________________________________________________________________
 .sup.1 ABS = K2938                                                       
 PMMA = Plexiglas DR                                                      
 PC = polycarbonate                                                       
 PET = poly(ethylene terephthalate)                                       
 PA = polyarylate                                                         
 
    
     EXAMPLE 46 
     40 weight percent of a polyacrylate, Ardel D-100 was blended with 20 weight percent of a copolyester of cyclohexanedimethanol, ethylene glycol and terephthalic acid (PETG-6763 described in Control E), 30 weight percent of a poly (methyl methacrylate) grafted onto butadiene based rubber (Pexiglas DR described in Control T and Table 9) and 10 weight percent of a styrene/acrylate/butadiene terpolymer (KM-611 described in Example 47) 
     This blend was prepared by extrusion blending the components at about 270° C. in a 1-inch diameter extruder with L/D=36/1. The extrudate was chopped into pellets. The pellets were molded into ASTM test specimens (at 270°-300° C.) using a Newbury 11/4 ounce screw injection molding machine. The test specimens were measured for the following properties: tensile strength and modulus according to ASTM D-638; elongation at break according to ASTM D-638; notched izod impact strength according to ASTM D-256; tensile impact strength according to ASTM-D-1822; heat distortion temperature measured at 264 psi on a 1/8 inch thick unannealed test bar according to ASTM D-635. 
     The results are shown in Table 18 
     EXAMPLE 47 
     52.5 weight percent of a polyarylate, Ardel D-100, 17.5 weight percent of a copolyester, PETG-6763 (described in Example 46), 10 weight percent of a styrene/acrylate/butadiene terpolymer (KM-611 described in Example 48) and 20 weight percent of a poly(methyl methacrylate) (XT-375 sold by American Cyanamid). 
     The blend was prepared as in Example 46 molded into test samples and tested by the procedures as described in Example 46. 
     The results are shown in Table 18. 
     EXAMPLE 48 
     Example 47 was exactly repeated except that 20 weight percent of a poly (methyl methacrylate) (XT-250 sold by American Cyanamid) was substituted for the XT-375 poly (methyl methacrylate). 
     The results are shown in Table 18. 
     
                                           TABLE 18                                
__________________________________________________________________________
                                                Heat                      
Description of the                                                        
              Tensile                                                     
                   Tensile    Tensile Impact                              
                                      Notched Izod                        
                                                Distortion                
Composition   Modulus                                                     
                   Strength                                               
                        Elongation                                        
                              Strength                                    
                                      Impact Strength                     
                                                Distortion                
Example                                                                   
     Polymer                                                              
          Wt. %                                                           
              (psi)                                                       
                   (psi)                                                  
                        (percent)                                         
                              (ft. lbs/in.sup.2)                          
                                      (ft. lbs/in of notch)               
                                                (°C.)              
__________________________________________________________________________
46   PA   40                                                              
     PE   20  280,000                                                     
                   7930 58    137     4.2       98                        
     DR   30                                                              
     KM-611                                                               
          10                                                              
47   PA   52.5                                                            
     PE   17.5                                                            
              285,000                                                     
                   7730 23    75      1.21      99                        
     XT-375                                                               
          20                                                              
     KM-611                                                               
          10                                                              
48   PA 52.5                                                              
     PE   17.5                                                            
              297,000                                                     
                   7930 33    85      1.53      100                       
     XT-250                                                               
          20                                                              
     KM-611                                                               
          10                                                              
__________________________________________________________________________
 .sup.1 PA = polyarylate                                                  
 PE = copolyester, PETG6763                                               
 DR = Plexiglas DR