Molding compositions
BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     This invention relates to modified unsaturated polyester compositions which have improved physical properties when used as molding compositions. In particular, the modified unsaturated polyester compositions exhibit highly advantageous hydrolytic stability and resistance to chemical degradation. 
     2. Description of the Prior Art 
     Unsaturated polyesters are industrially important materials which have broad application in the manufacture of products such as automotive parts, boats, appliance parts, and furniture. Unsaturated polyester compositions have also been applied to the fabricating of pipes, tanks and fume ducts used for handling materials in waste water treatment, selected chemicals, and gas and oil. 
     One problem which has been encountered in the past with such compositions is that of high polymerization shrinkage of the polyester resin. Shrinkage results in poor surface smoothness and low gloss of molded parts. Polymerization shrinkage also results in poor dimensional agreement between the mold surface and the fabricated part. Another problem encountered is that crosslinked unsaturated polyester matrix is a brittle glassy phase that has low chip and crack resistance at high stress areas such as corners and molded edges. In addition, conventionally formulated unsaturated polyester compositions generally exhibit poor resistance to strong aqueous caustic and acid solutions and can readily degrade in polar organic media. 
     A method that has been applied for reducing the polymerization shrinkage, and for modifying the final physical properties of the crosslinked compositions, involves the addition of various high molecular weight thermoplastics such as homopolymers of various acrylates, methacrylates, styrene, and vinyl acetate; copolymers of styrene; copolymers of vinyl chloride and vinyl acetate; cellulose esters; saturated polyesters and polycaprolactone. These materials, however, increase the viscosity of the unsaturated polyester resin to such an extent that formulation of other components such as fillers and fiberglass with the resin becomes difficult or impossible. The high viscosity results in poor wet-out of fiber reinforcement and filler, and can impart undesirable physical properties to the final molded product. 
     Micropulverized polyethylene powder has also been reported as a shrink-control agent in unsaturated polyester molding compounds. The conventional procedure involves mechanically blending polyethylene powder with the polyestermonomer resin syrup along with fillers and fiberglass. A major problem associated with combining polyethylene powder with the resin in this fashion is the extreme difficulty in properly dispersing the powder in the resin phase. Poor dispersion causes porosity and craters which subsequently cause problems of poor physical properties and problems on painting. 
     U.S. Pat. No. 3,207,816 discloses that modification of reactive, essentially linear ethylenically unsaturated polyester resins, prior to cross-linking, by the addition thereto of an interpolymer of an α,β-ethylenically unsaturated dicarboxylic acid or anhydride with a monoolefin having a terminal methylene group, results in linear alkyd resins having higher molecular weights than are readily obtainable by conventional procedures. The resulting linear alkyd, due to its improved viscosity, is said to impart many outstanding advantages to polyester resinous compositions prepared therefrom. This patent further discloses, however, that the amount of interpolymer or mixture of interpolymers employed may be from about 0.05% to about 10%, preferably about 0.2% to about 3%, by weight based on the total weight of resin forming components. 
     SUMMARY OF THE INVENTION 
     According to the present invention, modified unsaturated polyester compositions are provided which have improved physical properties and exhibit unexpected compatibility with high molecular weight polymers. The modified unsaturated polyester compositions comprise the reaction product of 
     (a) from about 50 to about 90% by weight (preferably about 50-85%), based on the weight of the reaction product, of an ethylenically unsaturated polyester derived from an α,β-ethylenically unsaturated dicarboxylic acid with a saturated aliphatic polyol, and 
     (b) from about 50 to greater than about 10% by weight (preferably about 50-15%), based on the weight of said reaction product, of a modified polyolefin derived by peroxide grafting of an α,β-ethylenically unsaturated dicarboxylic acid or anhydride and a polyolefin. 
     Preferably, the compositions comprise from about 75 to about 99% by weight of the modified unsaturated polyester and from about 25 to about 1% by weight of a polymer or copolymer of an olefin in the above reaction product, the polymer or copolymer having a molecular weight of from about 500 to about 50,000. The modified, unsaturated polyester compositions are suitable for combining with conventional polymerizable, ethenically unsaturated monomeric cross-linking agents such as styrene. 
     DETAILED DESCRIPTION OF THE INVENTION 
     According to the present invention, polymeric compositions having an improved balance of physical properties, including enhanced resistance to water absorption and chemical attack are provided. Also, because of low shrinkage during polymerization, greater dimensional stability and a smooth, crack-free surface of molded parts is realized. 
     The present invention provides compositions comprising unsaturated polyesters with carboxylated polyolefins, prepared by carrying out the esterification reaction in the presence of the polyolefin. Preferably, the compositions are then melt blended with one or more high molecular weight polymers to form a solid product which may then be combined with a polymerizable, ethylenically unsaturated monomeric cross-linking agent containing a CH 2  ═C&lt; group having a boiling point, at atmospheric pressure, of 60° C. or greater such as styrene. Surprisingly, the esterification product has good tolerance for the high molecular weight polymer and forms a stable mixture, thus avoiding the usual formation of a separate biphase mixture. 
     Polyester-General 
     As is well known, essentially linear, ethylenically unsaturated polyester resins of the type employed in the practice of this invention are conventionally prepared by esterifying an α,β-ethylenically unsaturated polycarboxylic acid or anhydride, alone or together with a non-polymerizable polycarboxylic acid or anhydride, with a saturated aliphatic polyhydric alcohol. In preparing these polyester resinous compositions, it is preferred that there be present at least a stoichiometric amount of the polyhydric alcohol, preferably 5 to 25% excess hydroxy groups as represented by the polyol over the carboxyl groups of the polycarboxylic acid component of the esterification mixture. It will be understood that the term polyester as used herein includes copolymers as well as homopolymers. 
     Polyester-Acid Reactant 
     Among the α,β-ethylenically unsaturated polycarboxylic acids that may be used are maleic, fumaric, substituted fumaric, citraconic, mesaconic, teraconic, glutaconic, muconic, and the like, as well as mixtures thereof. Non-polymerizable polycarboxylic acids, i.e., those which do not contain polymerizable α,β-ethylenic unsaturation, may also be used if employed in combination with one or more of the aforementioned α,β-ethylenically unsaturated polycarboxylic acids. Where such non-polymerizable polycarboxylic acids are employed, the amount thereof should not constitute more than about 80% of the total equivalents of carboxyl groups in the esterification mixture. Preferably, such nonpolymerizable polycarboxylic acids will be employed in amounts varying between about 35% and 75% of the above-indicated equivalence basis. Among the non-polymerizable polycarboxylic acids that may be used are such as oxalic, malonic, succinic, glutaric, sebacic, adipic, phthalic, isophthalic, terephthalic, substituted phthalic, such as tetrachlorophthalic, suberic, azelaic, tricarballylic, citric, tartaric, cyclopropanedicarboxylic, cylohexanedicarboxylic, and the like, as well as mixtures thereof. 
     Polyester-Glycol Reactant 
     With respect to the saturated aliphatic polyhydric alcohols which may be employed in the preparation of the modified linear alkyds or polyesters, it is preferred that those containing only two hydroxyl groups be used. Among such diols are included ethylene glycol, propylene glycol, butylene glycol, diethylene glycol, dipropylene glycol, triethylene glycol, tetraethylene glycol, butanediol-1,2, butanediol-1,3, butanediol-1,4, pentanediol-1,2, pentanediol-1,4, pentanediol-1,5, hexanediol-1,6, neopentyl glycol, 2,2,4-trimethyl-1,3-pentanediol and the like, as well as mixtures thereof. However, saturated aliphatic polyhydric alcohols containing more than two hydroxyl groups may also be employed. Among such polyols are included glycerol, trimethylol ethane, trimethylol propane, pentaerythritol, sorbitol and the like, as well as mixtures thereof. It is usually desirable that such polyols containing more than two hydroxyl groups be employed in minor proportions relative to the diol or diols used. 
     Carboxylated Polyolefin Modifier 
     The carboxylated polyolefins useful in the present invention are commercially available or may be prepared by reacting poly-α-olefins with an unsaturated polycarboxylic component such as unsaturated polycarboxylic acids, anhydrides or esters thereof. Generally, the reaction is carried out in the presence of a free radical source. These poly-α-olefins include homopolymers prepared from alpha-olefin monomers containing 3 to 12 carbon atoms, copolymers of such monomers with each other or copolymers of such monomers and ethylene. The poly-α-olefins also include polyethylenes such as high, medium and low density polyethylenes. One such suitable poly-α-olefin is highly crystalline polypropylene prepared according to U.S. Pat. No. 2,969,345. Commercially available materials include, for example, Epolene C-16 maleated polyethylene and Epolene E-43 maleated polypropylene, products of Eastman Chemical Products, Inc. 
     The poly-α-olefins are reacted with unsaturated poly-carboxylic components such as unsaturated polycarboxylic acids, anhydrides or esters thereof at temperatures generally less than 300° C., preferably from about 130°-240° C., in the presence of free radical sources. Suitable free radical sources are, for example, peroxides such as ditertiary butyl peroxide, t-butyl peracetate, t-butyl perbenzoate, or 2,5-dimethyl-2,5-di(tertiarybutylperoxy)hexane. Suitable irradiation sources also include, for example, ultraviolet light. Preferably, about 1 to 25% of the unsaturated polycarboxylic component, such as unsaturated polycarboxylic acids, anhydrides or esters thereof, based on the weight of the polyolefin, is used in preparing the carboxylated polyolefin used in the invention. 
     The carboxylated polyolefins useful in the present invention can be prepared either in solution, in solvents such as xylene, mineral spirits and the like, at temperatures of about 130°-200° C. or in the melt phase at temperatures of about 180°-240° C. When the carboxylated polyolefins are prepared in solution, the polyolefin is generally dissolved in refluxing solvent, for example xylene at 140° C., and the unsaturated polycarboxylic component, maleic anhydride, and peroxide initiator dissolved in solvent are added dropwise to the reaction mixture. 
     The amount of unsaturated component used is determined by the reaction process employed. For example, in a solution process, the unsaturated component may be present in an amount of about 1 to 25 weight percent. However, in a melt phase reaction, the unsaturated component is preferably present in an amount of about 1 weight percent. The amount of peroxide or free radical agent used is generally quite low being of the order of about 0.01 to about 0.5% based on the weight of the poly-α-olefin. 
     The reaction may be carried out either in a batchwise or in a continuous manner with contact times in the order of about 1 minute to about 2 hours. The reaction of polyethylenes should be carried out in the absence of oxygen, preferably in an inert nitrogen atmosphere. The reaction of polypropylene and higher α-olefins preferably is carried out in an inert atmosphere. Suitable unsaturated polycarboxylic component such as acids and anhydrides are, for example, maleic acid, maleic anhydride, fumaric acid, citraconic anhydride, aconitic anhydride and itaconic anhydride. Suitable esters are, for example, the half or full esters derived from maleic and fumaric acid such as methyl ethyl fumarate, dimethyl maleate, dimethyl fumarate, methyl ethyl maleate, dibutyl maleate, dipropyl maleate, and the like, maleic acid or anhydride is preferred. The carboxylated polypropylene, higher-α-olefin homopolymers and copolymer compositions have a melt viscosity of 100 to 40,000 at 175° C. and a saponification number of 1 to 200 preferably about 20-80. The carboxylated polyethylene compositions have a melt viscosity of 100 to 40,000 at 175°  C. and a saponification number of 1 to 30. 
     Production of Modified Unsaturated Polyester 
     The components may be reacted in the manner customarily used in preparing ethylenically unsaturated polyester resins, i.e., at elevated temperatures and atmospheric pressure, although pressures slightly above or below atmospheric may be employed if desired. The reaction temperature is not critical. The preferred temperature will usually be just below the boiling point of the most volatile component of the reaction mixture which is generally the polyol. However, temperatures in excess of the boiling point of the most volatile constituent may be employed if the reaction vessel has been equipped with a steam-heated reflux condenser, which permits water of esterification to escape from the reaction vessel while condensing volatilized reaction components and returning them to the reaction sphere. 
     As indicated previously, the composition of this invention comprise (1) the unsaturated polyester chemically modified with the carboxylated polyolefin, or (2) the unsaturated polyester modified with the carboxylated polyolefin and melt blended with a high molecular weight polymer. In either case, it is preferred to add the carboxylated polyolefin when the acid number of the esterification mixture is between about 40 and about 60, preferably between about 43 and about 57. The amount of carboxylated polyolefin added to the polyester melt is usually in the range of 10-50 wt % based on the total reactant weight of polyester components. The selected carboxylated polyolefin is added to the reaction mixture and the polymerization is continued at a temperature of 190°-200° C. until the acid number reaches 30±5. 
     High Molecular Weight Polymer Additive 
     In (2) above, after a homogeneous reaction product is obtained, the appropriate amount of high molecular weight polymer is similarly added to the melt. After 10-30 minutes of stirring, a stable, homogeneous polymer blend is obtained. 
     The composition according to (2) above preferably contains about 75 to about 99% by weight of modified unsaturated polyester and from about 25 to about 1% by weight of the high molecular weight polymer. The term polymer as used in this regard includes homopolymer, copolymer and mixtures thereof. The high molecular weight polymer is normally in powder or pellet form and comprises a polymer of an olefin having a molecular weight of from about 500 to about 50,000. The melt phase advantageously produces an intimate polymer blend with a dispersed phase size between about 1 to about 30 microns. In contrast with previous art, this process produces a nonsetting, homogeneous, resinous product, which on crosslinking with styrene produces a homogeneous thermoset composition in contrast with the bulk, phase separation of components that results from conventional mixture of the reactants. 
     Preparation of Molding Composition 
     In preparing polyester resinous compositions from the modified unsaturated polyesters, they are combined with a polymerizable, ethylenically unsaturated monomeric crosslinking agent containing a CH 2  ═C&lt; group and desirably having a boiling point, at atmospheric pressure of 60° C. or greater. 
     Among such polymerizable compounds there are included styrene, side chain substituted styrenes such as the α-methyl styrene, α-ethyl styrene, and the like, ring substiuted styrenes, such as alkyl styrenes, e.g., ortho-, meta- and para-alkyl styrenes, e.g., o-methyl styrene, p-ethyl styrene, meta-propyl styrene, 2,4-dimethyl styrene, 2,5-diethyl styrene, and the like, halostyrenes, e.g., o-bromostyrene, p-chlorostyrene, 2,4-dichlorostyrene, and the like. Alkyl esters of acrylic and methacrylic acid, e.g., methyl, ethyl or butyl acrylate, methyl methacrylate, and the like, may also be employed. In addition, one may also use aliphatic vinyl esters such as vinyl acetate, vinyl butyrate, vinyl laurate, acrylonitrile, methacrylonitrile, vinyl chloride, and the like. Further, acrylamide, methacrylamide and their derivatives may be employed. Still further, one can make use of the allyl compounds such as diallyl phthalate, allyl acetate, allyl methacrylate, diallyl carbonate, allyl lactate, allyl α-hydroxyisobutyrate, allyl trichlorosilane, allyl acrylate, diallyl malonate, diallyl oxalate, diallyl gluconate, diallyl methyl gluconate, diallyl adipate, diallyl sebacate, diallyl tartronate, diallyl tartrate, diallyl mesaconate, diallyl citraconate, the diallyl ester of muconic acid, diallyl itaconate, diallyl chlorophthalate, diallyl dichlorosilane, the diallyl ester of endomethylenetetrahydrophthalic anhydride, triallyl tricarballylate, triallyltrimesate, triallyl aconitate, triallyl cyanurate, triallyl citrate, triallyl phosphate, trimethallyl phosphate, tetraalyl silane, tetraalyl silicate, hexallyl disiloxane and the like. These polymerizable, ethylenically unsaturated monomeric cross-linking agents may be used singly or in combination with one another. 
     The ratio of the unsaturated polyester to the monomeric crosslinking agent may be varied over a wide range and, therefore, this ratio is not critical. For example, the unsaturated reactive resin content may range from about 10 to about 90% of the total weight of this copolymerizable mixture. For most purposes, however, the polyester resinous compositions will comprise from about 30 to 60 parts of the unsaturated resin and correspondingly from about 70 to 40 parts of the polymerizable monomer. 
     In order to facilitate the copolymerization of the monomeric cross-linking agent with the reactive resin, it is preferred that a polymerization catalyst be incorporated in the composition at the time of its curing. The type and amounts of these catalytic materials which may be used are well known and the art, and any material which normally induces polymerization of polyester resinous compositions can be utilized. The optimum reaction conditions are modified to some extent by the choice of the particular catalyst used in the process. A very active catalyst should be used in lower concentrations, and preferably at lower temperatures, than a less reactive material. The catalysts that are preferably employed comprise a wide variety of organic superoxides, i.e., organic peroxides (&#34;acidic peroxides&#34;) and hydroperoxides (&#34;alcoholic peroxides&#34;). Mixtures of peroxides and hydroperoxides, including commercially available mixtures such as methyl ethyl ketone peroxide, cyclohexanone peroxide, and the like, are especially effective as catalysts. Among the organic peroxide catalysts that may be employed are such as acetyl peroxide, benzoyl peroxide, substituted benzoyl peroxides, and particularly halogenated benzoyl peroxides such as p-bromobenzoyl peroxide, 2,4-dichlorobenzoyl peroxide, etc., benzoyl acetyl peroxide, phthalyl peroxide succinyl peroxide, fatty oil acid peroxides, such as coconut oil peroxide, lauryl peroxide, stearyl peroxide, oleyl peroxide, anisoyl peroxide, toluyl peroxide, and the like. Organic peracids, such as peracetic acid and perbenzoic acid, may also be employed. Among the organic hydroperoxide catalysts that may be employed are such as tertiary butyl hydroperoxide, cumene hydroperoxide, diisopropyl benzene hydroperoxide, 1-hydroxycyclohexyl hydroperoxide, the terepene oxides, such as ascaridole, 1-p-methane hydroperoxide, etc., and the like. Various other types of polymerization catalyst may also be employed, for example, compounds such as aluminum chloride, stannic chloride, boron trifluoride, or the azo-type catalysts such as α,α&#39;-azobisisobutyronitrile. 
     Since the polyester constituents of the resinous compositions mentioned above contain a high degree of polymerizable unsaturation, it is often desirable to incorporate a polymerization inhibitor therewith. The inhibitor, i.e., a material whose primary function is to retard internal polymerization of the polyester constiuent of the resinous composition, effects stabilization of the composition during any storage period encountered prior to curing. However, once the resinous composition is contacted with a sufficient amount of a polymerization catalyst, the effect of the inhibitor will be overcome. Among the inhibitors that may be used are such as phenol; the monoalkyl phenols, such as ortho-, meta-, and para-cresol, as well as mixtures of such isomers; polyalkyl phenols having a plurality of the same or different substituents, e.g., ethyl, propyl, butyl, and higher alkyl radicals attached to their nuclei; catechol, tertiary butyl catechol, hydroquinone, tertiary butyl hydroquinone, resorcinol, eugenol guaiacol, pyrogallol, benzaldehyde, tannic acid, ascorbic acid, isoascorbic acid, phenylene diamine, sym-di-β-naphthyl-p-phenylene diamine, aniline, and the like. The amount of polymerization inhibitor employed depends on the nature of the polyester resinous composition as well as the period of storage stability required. Generally, from about 0.001% to 0.3% by weight, based on the total weight of polymerizable reactive components present, will be sufficient. 
     Inhibitors of this type may be added to the reactive resin during the preparation thereof or optionally added later to the compounded polyester resinous composition. In addition, other known additives may be employed such as promoters used in conjunction with the catalyst, mold lubricants, fillers and reinforcements, colorants, flow promoters, ultraviolet absorbing compounds, and the like. 
     The conditions necessary for curing the polyester resinous compositions of this invention do not depart from the practice ordinarily observed in curing this type of composition. They may be cured in contact with air or in enclosed molds at temperatures ranging from about 10° C. to about 160° C. or even higher as long as they are kept below the point at which the particular resinous composition employed begins to decompose. Where it is convenient, it is especially desirable to cure the resinous compositions by heating the catalyzed, resin-forming mass to between 90° C. and about 150° C. for a period of about 3 to 90 minutes. 
     The following examples are submitted for a better understanding of the invention. 
     The following abbreviations, tradenames or trademarks are used herein: 
     Epolene® C-16 resin--maleated polyethylene having a saponification number of 4.0 and a melt viscosity of 4180 cp at 175° C. 
     Epolene® E-43 resin--maleated polypropylene having a saponification number of 60 and a melt viscosity of &lt;1000 cp at 175° C. 
     Maleated Epolene® N-14 resin--maleated polyethylene having a saponification number of 72 and a melt viscosity of 2600 cp at 175° C. 
     Maleated Epolene® C-15 resin--maleated polyethylene having a saponification number of 43 and a melt viscosity of 12,000 cp at 175° C. 
     Tenite® 424S resin--polypropylene having a melt flow rate at 230° C. of 9. 
     EG--ethylene glycol. 
     IPA--isophthalic acid. 
     TPA--terephthalic acid 
     TMPD® glycol chemical--2,2,4-trimethyl-1,3-pentanediol. 
     MA--maleic anhydride. 
     DMT--dimethyl terephthalate. 
     PG--propylene glycol. 
     In the examples, Tensile Strength and Elongation are measured in accordance with ASTM D638; Impact Strength in accordance with ASTM D256-56; and Flexural Stress (Flex. Str.) and Flexural Modulus (Flex. Mod.) in accordance with D671. 
    
    
     EXAMPLES 1-11 
     In examples 1-11, an unsaturated polyester is prepared from 75 mole percent TMPD, 25 mole percent EG, 50 mole percent IPA and 50 mole percent MA. Unsaturated polyester is modified as indicated. The resin is dissolved in styrene monomer, test samples cast, and after crosslinking, the physical properties are as indicated. 
     
         __________________________________________________________________________
                          Izod                                            
               Tensile                                                    
                    Elong.                                                
                          Impact                                          
     Polyolefin                                                           
               Strength                                                   
                    to    Strength                                        
                                Flex. Flex.                               
Example                                                                   
     Modifier  (psi)                                                      
                    Break(%)                                              
                          Ft-Lb/In.                                       
                                Str. (psi)                                
                                      Mod. (psi)                          
__________________________________________________________________________
(Control)      2168 4     0.72  6.84 × 10.sup.3                     
                                      4.61 × 10.sup.5               
2    10% Epolene C-16                                                     
               4275 4     1.03  8.77 × 10.sup.3                     
                                      4.57 × 10.sup.5               
3    10% Epolene E-43                                                     
               3495 4     1.07  7.13 × 10.sup.3                     
                                      4.03 × 10.sup.5               
__________________________________________________________________________
 
    
     The above table of physical properties illustrates the tensile strength, impact strength, and flexural strength of thermoset compositions prepared with 10 wt % maleated polyethylene and maleated polypropylene, respectively. 
     
         ______________________________________                                    
Polyolefin Modifier  % Retention                                          
in Unsaturated       of Flexural Strength                                 
Example Polyester        3 Days  6 Days                                   
                                       12 Days                            
______________________________________                                    
(Control)                87.5%   66.5% 37%                                
5       30% Epolene C-16 88.9%   68.4% 56%                                
6       30% Epolene E-43 64.4%   65.2% 16%                                
7       30% Maleated Epolene                                              
                         61.2%   40.9% 13%                                
        N-14                                                              
______________________________________                                    
 
    
     Examples 4-7 illustrate the significant improvement in retention of flexural strength of thermoset samples containing Epolene C-16, compared with the control, on exposure to hot caustic solution over a period of 12 days. The caustic is 10% NaOH solution. The cycle is 8 hours per day at 100° C. and 16 hours per day at 70° C. 
     
         ______________________________________                                    
       Polyolefin                                                         
       Modifier in Unsaturated                                            
Example                                                                   
       Polyester       % Shrinkage of Thermoset                           
______________________________________                                    
 8                                                                        
(Control)              3.50%                                              
 9     10% Maleated Epolene                                               
                       3.43%                                              
       C-15                                                               
10     10% Epolene E-43                                                   
                       3.24%                                              
11     10% Epolene C-16                                                   
                       2.88%                                              
______________________________________                                    
 
    
     The ability of the unsaturated polyester/polyolefin compositions to reduce thermoset shrinkage of an unsaturated polyester resin is shown in Examples 8-11. Resin samples are prepared with the following resin composition: 
     59.5% unsaturated polyester resin 
     39.5% styrene monomer 
     1.0% benzoyl peroxide 
     The resin samples are degassed and decanted into the cavity of a precision machined stainless-steel mold. The crosslinking reaction is initiated by heating the mold in a water bath at 100° C. for 15 min. After cooling, the diameter of the thermoset sample is measured with a micrometer and the shrinkage is calculated relative to the inside diameter of the mold. 
     EXAMPLES 12-39 
     Into a three-neck flask is added 241.3 g (1.65 moles) of TMPD, 166.1 g (1.00 mole) of isophthalic acid, 0.54 g of dibutyltin oxide and 0.54 g of sodium tetraborate. The reaction is heated under nitrogen at 195°-205° C. This first-stage is reacted for about 15 hr., at which time the acid number of the polymer is less than 20. The polymer is cooled and 34.1 g (0.55 mole) of ethylene glycol, 98.1 g (1.0 mole) of maleic anhydride and 0.05 g of toluhydroquinone are added. The reaction is heated and the reaction continued at a temperature of 190°-200° C. until the acid number is about 30. Then 53.9 g of maleated polypropylene (Epolene E-43 resin, 10 wt. % based on the total reactant charge weight) is added. Within a few minutes the maleated polypropylene melts and becomes homogeneous with the polyester melt. The reaction is continued until the acid number is about 20. The polyester/maleated polypropylene resin is decanted from the flask, cooled and dissolved in 30 wt. % styrene monomer. The styreneated resin is homogeneous in apperance and remains as a single phase after standing for several days. The thermoset casting is prepared by further addition of styrene monomer until 40 wt. % styrene is present. Then 1% benzoyl peroxide is added and the resin is poured between two glass plates, sealed around three sides by a 1/8 in. thick spacer gasket. The casting is heated especially at 70° C. for 2 hr., 100° C. for 1 hr., 125° C. for 1 hr. and 150° C. for 1 hr. to crosslink the polyester/maleated polypropylene composition. The crosslinked casting is then cut into flexural bars (1/8 in.×1/2 in.×4 in.) for physical property measurement. The physical property data are shown in Examples 12-17. 
     The evaluation of the corrosion resistance of the crosslinked composition is carried out by placing the flexural bars in boiling 10% sodium hydroxide in Examples 18-23. Samples are removed after 3, 6 and 12 days and the flexural strength is determined. Examples 19 clearly shows the higher retention of flexural strength for the polyester/polypropylene compositions compared with the polyester control. 
     Tests are repeated using different levels of carboxylated polyolefin additive. The results are included in Examples 12-39. In all the examples except 17 and 23, the polyester is 75/25 TMPD/EG, 1/1 IPA/MA. In Examples 17 and 23 a bisphenol-A-fumarate is used. 
     
         __________________________________________________________________________
                                                        IMPACT            
                                                        STRENGTH          
                   Appearance                                             
                          FLEXURAL PROPERTIES                             
                                          TENSILE PROPERTIES              
                                                        Unnotched         
           Melt    of     Flexural                                        
                                  Flexural                                
                                          Tensile                         
                                                 Elongation               
                                                        Izod              
   Polyolefin                                                             
           Dispersibility                                                 
                   Thermoset                                              
                          Strength                                        
                                  Modulus Strength                        
                                                 to     Strength          
Ex.                                                                       
   Additive                                                               
           of Additive                                                    
                   Casting                                                
                          (PSI)   (PSI)   (PSI)  Break(%)                 
                                                        (Ft-Lb/In.)       
__________________________________________________________________________
12                                                                        
Control    --      Clear  10.59 × 10.sup.3                          
                                  4.82 × 10.sup.5                   
                                          3553   5      2.18              
13 10% Epolene                                                            
           Homogeneous                                                    
                   Nearly Clear,                                          
                          8.93 × 10.sup.2                           
                                  4.67 × 10.sup.5                   
                                          4161   7      1.01              
   E-43            Homogeneous                                            
14 20% Epolene                                                            
           &#34;       Sl. Opaque,                                            
                          7.00 × 10.sup.3                           
                                  4.48 × 10.sup.5                   
                                          3743   5      0.70              
   E-43            Homogeneous                                            
15 30% Epolene                                                            
           &#34;       Sl. Opaque,                                            
                          5.85 × 10.sup.3                           
                                  4.49 × 10.sup.5                   
                                          3457   5      0.89              
   E-43            Homogeneous                                            
16 40% Epolene                                                            
           &#34;       Sl. Opaque,                                            
                          6.70 × 10.sup.3                           
                                  4.42 × 10.sup.5                   
                                          3272   4      0.82              
   E-43                                                                   
17                                                                        
Commercial Clear   11.47 × 10.sup.3                                 
                          4.42 × 10.sup.5                           
                                  4009    7      1.19                     
   Control                                                                
__________________________________________________________________________
 
    
     
         __________________________________________________________________________
                 Exposure to Boiling 10% NaOH                             
                 Flexural Strength &amp; % Retention of Flexural Strength     
          Initial                                                         
                 After 3 Days                                             
                           132 After 6 Days                               
                                     After 12 Days                        
          Flexural                                                        
                 Flexural                                                 
                       % Ret.                                             
                           Flexural                                       
                                 % Ret.                                   
                                     Flexural                             
                                           % Ret.                         
                                               Appearance                 
   Polyolefin                                                             
          Strength                                                        
                 Strength                                                 
                       Flex.                                              
                           Strength                                       
                                 Flex.                                    
                                     Strength                             
                                           Flex.                          
                                               After                      
Ex.                                                                       
   Additive                                                               
          (PSI)  (PSI) Str.                                               
                           (PSI) Str.                                     
                                     (PSI) Str.                           
                                               12 Days                    
__________________________________________________________________________
18                                                                        
Control   10.59 × 10.sup.3                                          
                 3.75 × 10.sup.3                                    
                       35% 4.03 × 103                               
                                 38% 2.79 × 10.sup.3                
                                           26% Pitted, hazy               
                                               surface                    
19 10% Epolene                                                            
          8.73 × 10.sup.3                                           
                 7.78 × 10.sup.3                                    
                       89% 6.72 × 10.sup.3                          
                                 77% 6.08 × 10.sup.3                
                                           70% Hazy surface               
   E-43                                                                   
20 20% Epolene                                                            
          7.00 × 10.sup.3                                           
                 7.58 × 10.sup.3                                    
                       108%                                               
                           7.10 × 10.sup.3                          
                                 102%                                     
                                     5.60 × 10.sup.3                
                                           80% Hazy surface               
   E-43                                                                   
21 30% Epolene                                                            
          5.85 × 10.sup.3                                           
                 3.95 × 10.sup.3                                    
                       68% 4.18 × 10.sup.3                          
                                 71% 3.73 × 10.sup.3                
                                           64% Hazy surface               
   E-43                                                                   
22 40% Epolene                                                            
          6.70 × 10.sup.3                                           
                 2.91 × 10.sup.3                                    
                       43% 3.70 × 10.sup.3                          
                                 55% 2.13 × 10.sup.3                
                                           32% Hazy surface               
   E-43                                                                   
23                                                                        
Commercial                                                                
   11.47 × 10.sup.3                                                 
          9.99 × 10.sup.3                                           
                 87%   8.94 × 10.sup.3                              
                           78%   9.51 × 10.sup.3                    
                                     83% Smooth, Glossy                   
   Control                                     surface                    
__________________________________________________________________________
 
    
     
         __________________________________________________________________________
                                                   Impact Strength        
                  Appearance                                              
                         Flexural Properties                              
                                       Tensile Properties                 
                                                   Unnotched              
          Melt    of     Flexural                                         
                                 Flexural                                 
                                       Tensile                            
                                           Elongation                     
                                                   Izod  Standard         
   Polyolefin                                                             
          Dispersibility                                                  
                  Thermoset                                               
                         Strength                                         
                                 Modulus                                  
                                       Str.                               
                                           to Break                       
                                                   Strength               
                                                         Deviation        
Ex.                                                                       
   Additive                                                               
          of Additive                                                     
                  Casting                                                 
                         (PSI)   (PSI) (PSI)                              
                                           (%)     (Ft-Lb/In.)            
                                                         (Ft-Lb/In.)      
__________________________________________________________________________
24                                                                        
Control - --      Clear  10.59 × 10.sup.3                           
                                 4.82 × 10.sup.5                    
                                       3553                               
                                           5       2.18  0.04             
25 5% Epolene                                                             
          Homogeneous                                                     
                  Opaque,                                                 
                         6.76 × 10.sup.3                            
                                 3.61 × 10.sup.5                    
                                       1870                               
                                           2       0.95  0.05             
   C-16           White                                                   
26 10% Epolene                                                            
          Homogeneous                                                     
                  Opaque,                                                 
                         7.61 × 10.sup.3                            
                                 4.24 × 10.sup.5                    
                                       2240                               
                                           3       1.12  0.02             
   C-16           White                                                   
27 15% Epolene                                                            
          Homogeneous                                                     
                  Opaque,                                                 
                         6.97 × 10.sup.3                            
                                 3.42 × 10.sup.5                    
                                       2162                               
                                           2       0.74  0.01             
   C-16           White                                                   
28 20% Epolene                                                            
          Homogeneous                                                     
                  Opaque,                                                 
                         7.20 × 10.sup.3                            
                                 3.42 × 10.sup.5                    
                                       1708                               
                                           2       1.21  0.02             
   C-16           White                                                   
29 25% Epolene                                                            
          Homogeneous                                                     
                  Opaque,                                                 
                         7.03 × 10.sup.3                            
                                 2.75 × 10.sup. 5                   
                                       1924                               
                                           2       0.68  0.01             
   C-16           White                                                   
30 30% Epolene                                                            
          Homogeneous                                                     
                  Opaque,                                                 
                         5.55 × 10.sup.3                            
                                 2.73 × 10.sup.5                    
                                       1912                               
                                           3       0.78  0.01             
   C-16           White                                                   
31 40% Epolene                                                            
          Homogeneous                                                     
                  Opaque,                                                 
                         5.13 × 10.sup.3                            
                                 2.58 × 10.sup.3                    
                                       1651                               
                                           3       0.46  0.01             
   C-16           White                                                   
__________________________________________________________________________
 
    
     
         __________________________________________________________________________
                    After 12 Days in                                      
                    Boiling 10% NaOH                                      
                    Flexural Strength                                     
                    and % Retention                                       
             Initial                                                      
                    Flexural Strength                                     
             Flexural                                                     
                    Flexural                                              
                          % Retention                                     
                                 Appearance After                         
   Polyolefin                                                             
             Strength                                                     
                    Strength                                              
                          Flexural                                        
                                 12 Days in                               
Ex.                                                                       
   Additive  (PSI)  (PSI) Strength                                        
                                 Boiling 10% NaOH                         
__________________________________________________________________________
32                                                                        
Control      10.59 × 10.sup.3                                       
                    2.79 × 10.sup.3                                 
                          26%    Pitted, Hazy Surface                     
33 5% Epolene C-16                                                        
             6.76 × 10.sup.3                                        
                    3.93 × 10.sup.3                                 
                          58%                                             
34 10% Epolene C-16                                                       
             7.61 × 10.sup.3                                        
                    4.98 × 10.sup.3                                 
                          65%    Smooth, Semi-Dull                        
35 15% Epolene C-16                                                       
             6.97 × 10.sup.3                                        
                    3.67 × 10.sup.3                                 
                          53%    Smooth, Semi-Dull                        
36 20% Epolene C-16                                                       
             7.20 × 10.sup.3                                        
                    2.42 × 10.sup.3                                 
                          32%    Pitted, Dull                             
37 25% Epolene C-16                                                       
             7.03 × 10.sup.3                                        
                    3.66 × 10.sup.3                                 
                          52%    Smooth, Semi-Dull                        
38 30% Epolene C-16                                                       
             5.55 × 10.sup.3                                        
                    3.11 × 10.sup.3                                 
                          56%    Smooth, Semi-Dull                        
39 40% Epolene C-16                                                       
             5.13 × 10.sup.3                                        
                    2.79 × 10.sup.3                                 
                          55%    Smooth, Semi-Dull                        
__________________________________________________________________________
 
    
     EXAMPLES 40-55 
     Polyolefins with selected levels of maleation (saponification no.) and melt viscosity are added to the 2nd stage melt phase polycondensation of unsaturated polyesters. The polyester is again 75/25 TMPD/EG, 1/1 IPA/MA except bisphenol-A-fumarate is used in Examples 47 and 55. The polyester/polyolefin resin products are dissolved in 40% styrene and crosslinked in the usual manner. Flexural bar specimens (1/8 in.×1/2 in.×4 in.) are evaluated for physical properties and also placed in boiling 10% NaOH. Specimens are removed after 3, 6, 12 and 30 days and the retention of flexural strength is determined (Examples 48-55). It is found that the polyester/polyolefin compositions overall exhibit excellent hydrolytic resistance compared to the unmodified resin control. The composition containing maleated Epolene C-10 also shows corrosion resistance comparable to a commercial high performance bisphenol-A fumarate material. Thermoset compositions prepared with polyolefins of high melt viscosity and high maleation give the best overall balance of physical properties and exhibit excellent corrosion resistance. 
     
         __________________________________________________________________________
                                                        Impact            
                                                        Strength          
                   Appearance                                             
                           Flexural Properties                            
                                           Tensile Properties             
                                                        Unnotched         
           Melt    of      Flexural                                       
                                   Flexural                               
                                           Tensile                        
                                                 Elongation               
                                                        Izod              
   Polyolefin                                                             
           Dispersibility                                                 
                   Thermoset                                              
                           Strength                                       
                                   Modulus Strength                       
                                                 to Break                 
                                                        Strength          
Ex.                                                                       
   Additive                                                               
           of Additive                                                    
                   Casting (PSI)   (PSI)   (PSI) %      (Ft-Lb/In)        
__________________________________________________________________________
40                                                                        
Control    --      Clear   10.59 × 10.sup.3                         
                                   4.82 × 10.sup.5                  
                                           3553  5      2.18              
41 10% Epolene                                                            
           Homogeneous,                                                   
                   Homogeneous,                                           
                           8.73 × 10.sup.3                          
                                   4.67 × 10.sup.5                  
                                           4161  7      1.01              
   E-43            Nearly Clear                                           
42 10% Epolene                                                            
           Homogeneous                                                    
                   Homogeneous,                                           
                           9.40 × 10.sup.3                          
                                   4.02 × 10.sup.5                  
   C-16            White                                                  
43 10% Maleated                                                           
           Homogeneous                                                    
                   Uniform 6.60 × 10.sup.3                          
                                   4.30 × 10.sup.5                  
                                           3583  6      0.68              
   Epolene C-10    Dispersion                                             
                   Sl. Yellow                                             
44 10% Maleated                                                           
           Homogeneous                                                    
                   Uniform 6.69 × 10.sup.3                          
                                   4.16 × 10.sup.5                  
                                           3123  4      0.97              
   Epolene N-14    Dispersion                                             
                   Sl. Yellow                                             
45 5% Maleated                                                            
           Homogeneous                                                    
                   Uniform 8.89 × 10.sup.3                          
                                   4.63 × 10.sup.5                  
                                           4111  8      1.38              
   Epolene C-15    Dispersion                                             
                   Sl. Yellow                                             
46 20% Maleated                                                           
           Homogeneous                                                    
                   Uniform 9.67 × 10.sup.3                          
                                   3.46 × 10.sup.5                  
                                           4638  8      1.86              
   Epolene C-15    Dispersion                                             
                   Sl. Yellow                                             
47                                                                        
Commercial                                                                
   --      Clear   11.47 × 10.sup.3                                 
                           4.42 × 10.sup.5                          
                                   4009    7     1.19                     
   Control                                                                
__________________________________________________________________________
 
    
     
         __________________________________________________________________________
                 Exposure to Boiling 10% NaOH                             
           Initial                                                        
                 Flexural Strength and % Retention of lexural Strength    
           Flrxural                      Appearance     Appearance        
   Polyolefin                                                             
           Strength                                                       
                 After   After   After   After                            
                                           After        After             
Ex.                                                                       
   Additive                                                               
           (PSI) 3 Days  6 Days  12 Days 12 Days                          
                                           30 Days      30Days            
__________________________________________________________________________
48 --Control                                                              
           10.59 × 10.sup.3                                         
                  ##STR1##                                                
                          ##STR2##                                        
                                  ##STR3##                                
                                         Pitted, hazy surface             
                                            --           --               
49 10% Epolene E-43                                                       
           8.73 × 10.sup.3                                          
                  ##STR4##                                                
                          ##STR5##                                        
                                  ##STR6##                                
                                         Slight hazy surface              
                                            --           --               
50 10% Epolene C-16                                                       
           9.40 × 10.sup.3                                          
                  ##STR7##                                                
                          ##STR8##                                        
                                  ##STR9##                                
                                         Smooth, glossy surface           
                                            --           --               
51 10% Maleated Epolene C-10                                              
           6.60 × 10.sup.3                                          
                 --                                                       
                          ##STR10##                                       
                                  ##STR11##                               
                                         Smooth, glossy surface           
                                            ##STR12##   Smooth, glossy    
                                                        surface           
52 10% Maleated Epolene N-14                                              
           6.69 × 10.sup.3                                          
                  ##STR13##                                               
                          ##STR14##                                       
                                  ##STR15##                               
                                         Blister on Surface               
                                            --           --               
53 5% Maleated Epolene C-15                                               
           8.89 × 10.sup.3                                          
                 --                                                       
                          ##STR16##                                       
                                  ##STR17##                               
                                         Smooth, glossy surface           
                                            ##STR18##   Some pitting      
                                                        surface erosion   
54 20% Maleated Epolene C-15                                              
           9.67 × 10.sup.3                                          
                 --                                                       
                          ##STR19##                                       
                                  ##STR20##                               
                                         Some pittingsurface erosion      
                                            ##STR21##   pitted with       
                                                        surface erosion   
55 --Commercial Control                                                   
           11.47 × 10.sup.3                                         
                  ##STR22##                                               
                          ##STR23##                                       
                                  ##STR24##                               
                                         Smooth, glossy surface           
                                            --           --               
__________________________________________________________________________
 
    
     These examples demonstrate the preparation, properties and corrosion resistance of polyester/polyolefin compositions fabricated with 30 wt. % glass fiber reinforcement. The polyester/polyolefin resins shown in Examples 56-79 are prepared in the same manner as described in the previous examples. The resins are dissolved in 40% styrene and combined with 30 wt. % three-ply glass fiber mats and crosslinked at room temperature with 0.5% cobalt naphthenate and 1% methylethylketone peroxide. The laminates are then post-cured in an air oven at 70° C. for 2 hr., cooled, and cut into flexural bars (1/8 in.×1/2 in.×4 in.). The initial physical properties are shown in Examples 56-63. The flexural bars are placed in boiling 10% NaOH, boiling 25% acetic acid, boiling 5% nitric acid and boiling distilled water. After 12 days exposure the samples are removed and evaluated for retention of flexural strength (Examples 64-71) and flexural modulus (Examples 72-79). It is found that the DMT-based resin prepared with 20% Epolene E-43 and 5% Tenite 424S shows excellent corrosion resistance compared with the conventional polyester control. The polyester compositions for Examples 56-79 are given in the following table. 
     
         ______________________________________                                    
Code Polyester       Polyolefin Modifier                                  
______________________________________                                    
A    TMPD/EG/ISO/MA  Control                                              
B    TMPD/EG/ISO/MA  10% Epolene C-16                                     
C    TMPD/EG/ISO/MA  20% Epolene C-16                                     
D    TMPD/EG/ISO/MA  20% Epolene E-43 + 5% Tenite                         
                     424S                                                 
E    TMPD/PG/DMT/MA  Control                                              
F    TMPD/PG/DMT/MA  20% Epolene E-43                                     
G    TMPD/PG/DMT/MA  20% Epolene E-43 + 5% Tenite                         
                     424S                                                 
H    ATLAC 382 (Bisphenol-A fumarate) Commercial Control                  
______________________________________                                    
 
    
     
         __________________________________________________________________________
                                 Izod                                     
          Tensile                                                         
               Elongation                                                 
                     Flexural                                             
                           Flexural                                       
                                 Impact                                   
   Composition                                                            
          Strength                                                        
               to Break                                                   
                     Strength                                             
                           Modulus                                        
                                 Strength                                 
Ex.                                                                       
   Code   (PSI)                                                           
               (%)   (× 10.sup.5 PSI)                               
                           (× 10.sup.5 PSI)                         
                                 (Ft-Lb/In.)                              
__________________________________________________________________________
56 A      13,651                                                          
               14    28.5  12.8  12.1                                     
57 B      14,569                                                          
                9    26.7  11.5  12.8                                     
58 C      15,314                                                          
                9    25.1  10.6  13.2                                     
59 D      15,901                                                          
               10    24.0  10.2  10.6                                     
60 E      13,324                                                          
               13    21.8  10.6  13.4                                     
61 F      14,323                                                          
               12    24.9  10.5  10.7                                     
62 G      13,068                                                          
               13    18.5  8.0   13.5                                     
63 H      17,420                                                          
               10    30.2  12.4  14.4                                     
__________________________________________________________________________
 
    
     
         __________________________________________________________________________
Corrosion Resistance Testing                                              
Initial          % Retention of Flexural Strength                         
Flexural         12 Days Exposure                                         
   Composition                                                            
          Strength                                                        
                 Boiling                                                  
                        Boiling Boiling Boiling                           
Ex.                                                                       
   Code   (× 10.sup.3 PSI)                                          
                 10% NaOH                                                 
                        5% HNO.sub.3                                      
                                25% HOAC                                  
                                        Dist. H.sub.2 O                   
__________________________________________________________________________
64 A      28.5   73%                                                      
                    (20.71)                                               
                        3%  (0.71)                                        
                                76% (21.59)                               
                                        106%                              
                                            (30.30)                       
65 B      26.7   53%                                                      
                    (14.20) 0   69% (18.36)                               
                                        74% (19.62)                       
66 C      25.1   63%                                                      
                    (15.79)                                               
                        11% (2.67)                                        
                                85% (21.40)                               
                                        125%                              
                                            (31.50)                       
67 D      24.0   53%                                                      
                    (12.59)                                               
                        67% (16.00) 0   70% (16.64)                       
68 E      21.8   4% (0.76)                                                
                        93% (20.27)                                       
                                81% (17.76)                               
                                        104%                              
                                            (22.65)                       
69 F      24.9   6% (1.44)                                                
                        78% (19.36)                                       
                                113%                                      
                                    (27.96)                               
                                        96% (23.94)                       
70 G      18.5   34%                                                      
                    (6.21)                                                
                        132%                                              
                            (24.40)                                       
                                117%                                      
                                    (21.71)                               
                                        124%                              
                                            (22.93)                       
71 H      30.2   29%                                                      
                    (8.80)                                                
                        98% (29.77)                                       
                                97% (29.20)                               
                                        83% (24.93)                       
__________________________________________________________________________
 
    
     
         __________________________________________________________________________
% Retention of Flexural Modulus                                           
12 Days Exposure                                                          
          Initial                                                         
          Flexural                                                        
   Composition                                                            
          Modulus                                                         
                 Boiling                                                  
                        Boiling Boiling                                   
                                       Boiling                            
Ex.                                                                       
   Code   (× 10.sup.5 PSI)                                          
                 10% NaOH                                                 
                        5% HNO  25% HOAC                                  
                                       Dist. H.sub.2 O                    
__________________________________________________________________________
72 A      12.8   57%                                                      
                    (7.32)                                                
                        23% (2.93)                                        
                                28%                                       
                                   (3.5)                                  
                                       98% (12.6)                         
73 B      11.5   37%                                                      
                    (4.19)  0   56%                                       
                                   (6.38)                                 
                                       66% (7.60)                         
74 C      10.6   50%                                                      
                    (5.28)                                                
                        26% (2.73)                                        
                                79%                                       
                                   (8.40)                                 
                                       93% (9.84)                         
75 D      10.2   29%                                                      
                    (2.95)                                                
                        60% (6.12) 0   65% (6.61)                         
76 E      10.6   2% (0.27)                                                
                        81% (8.51)                                        
                                68%                                       
                                   (7.20)                                 
                                       91% (9.58)                         
77 F      10.5   16%                                                      
                    (1.62)                                                
                        72% (7.54)                                        
                                80%                                       
                                   (8.42)                                 
                                       74% (7.79)                         
78 G      8.0    56%                                                      
                    (4.47)                                                
                        103%                                              
                            (8.28)                                        
                                91%                                       
                                   (7.28)                                 
                                       108%                               
                                           (8.67)                         
79 H      12.4   76%                                                      
                    (9.35)                                                
                        95% (11.7)                                        
                                90%                                       
                                   (11.14)                                
                                       87% (10.77)                        
__________________________________________________________________________
 
    
     EXAMPLES 80-103 
     The examples illustrate the effect of sequence of addition of polyolefins during the melt phase preparation of unsaturated polyester on the physical properties and corrosion resistance of the crosslinked compositions. 
     The unsaturated polyesters are parepared by a conventional 2-stage reaction wherein TMPD and IPA are reacted in the first stage until the acid number is about 20 and then ethylene glycol and maleic anhydride are added and the reaction is continued until the final acid no. was ≦30. This experiment is designed to enable the addition of maleated polypropylene (Epolene E-43) and a high mol. wt. polypropylene (Tenite 424S) at selected intervals during the polyesterification. The first table which follows shows the plan for the designed experiment involving the addition of polyolefins to the unsaturated polyester preparation. 
     Examples 80-91 show the effect of adding the polyolefins at selected times during the polyesterification reaction. Examples 82, 83 and 84 result in unprocessable compositions. Examples 87 and 88 result in thick resins containing gel particles. The other examples result in homogeneous resins and give uniform, translucent thermoset castings. 
     Examples 92-103 show the effect of these processing variables on the corrosion resistance. This example clearly demonstrates the importance of selecting the preferred sequence of polyolefin addition to the polyester melt to obtain compositions with enhanced corrosion resistance. 
     
         __________________________________________________________________________
Experiment No.                                                            
        1  2 3 4  5 6 7 8 9 10                                            
                              11                                          
                                12                                        
__________________________________________________________________________
First-Stage                                                               
Start   A&amp;B                                                               
           A B        A B A     CONTROL                                   
Acid No. 50                 A                                             
Acid No. 20                                                               
           B A                                                            
Second-Stage                                                              
Start          A&amp;B                                                        
                  A B B A                                                 
Acid No. 50                 B A                                           
Acid No. 20       B A     B   B                                           
__________________________________________________________________________
 A = 20 wt. % Epolene E43                                                 
 B = 5 wt. % Tenite 424                                                   
 
    
     
         __________________________________________________________________________
                                               Impact                     
                                               Strength                   
                Appearance                                                
                       Flexural Properties                                
                                    Tensile Properties                    
                                               Unnotched                  
         Melt   of     Flexural                                           
                              Flexural                                    
                                    Tensile                               
                                         Elongation                       
                                               Izod                       
   Experiment                                                             
         Dispersibility                                                   
                Thermoset                                                 
                       Strength                                           
                              Modulus                                     
                                    Strength                              
                                         to Break                         
                                               Strength                   
Ex.                                                                       
   No.   of Polyolefins                                                   
                Casting                                                   
                       (PSI)  (PSI) (PSI)                                 
                                         (%)   (Ft-Lb/In.)                
__________________________________________________________________________
80 1     Homogeneous                                                      
                Translucent                                               
                       7.09 × 10.sup.3                              
                              3.99 × 10.sup.5                       
                                    3742 4     0.70                       
81 2     &#34;      &#34;      5.95 × 10.sup.3                              
                              4.38 × 10.sup.5                       
                                    2629 4     0.65                       
82 3     &#34;      Phase  --     --    --   --    --                         
                Separated                                                 
                No Casting                                                
                Made                                                      
83 4     Gel Particles                                                    
                Phase  --     --    --   --    --                         
                Separated                                                 
                No Casting                                                
                Made                                                      
84 5     Homogeneous                                                      
                Phase  --     --    --   --    --                         
                Separated                                                 
                No Casting                                                
                Made                                                      
85 6     &#34;      Translucent                                               
                       6.39 × 10.sup.3                              
                              4.17 × 10.sup.5                       
                                    2288 2     1.14                       
86 7     &#34;      &#34;      6.94 × 10.sup.3                              
                              4.19 × 10.sup.5                       
                                    36.54                                 
                                         5     0.88                       
87 8     Gel Particles,                                                   
                &#34;      5.00 × 10.sup.3                              
                              4.09 × 10.sup.5                       
                                    3280 5     0.66                       
         thick                                                            
88 9     Gel Particles,                                                   
                &#34;      8.47 × 10.sup.3                              
                              4.27 × 10.sup.5                       
                                    3532 3     1.02                       
         thick                                                            
89 10    Homogeneous,                                                     
                &#34;      8.76 × 10.sup.3                              
                              4.33 × 10.sup.5                       
                                    2954 4     1.11                       
         Low                                                              
         Viscosity                                                        
90 11    Homogeneous,                                                     
                &#34;      6.63 × 10.sup.3                              
                              4.40 × 10.sup.5                       
                                    3125 3     1.02                       
         thick                                                            
91 12    Clear, Low                                                       
                Clear, 12.48 × 10.sup.3                             
                              4.79 × 10.sup.5                       
                                    4014 4     2.34                       
   (Control)                                                              
         Viscosity                                                        
                Transparent                                               
__________________________________________________________________________
 
    
     
         __________________________________________________________________________
                 Exposure to Boiling 10% NaOH Flexural                    
                 Strength and % Retention of Flexural Strength            
                 After 12 Days                                            
                            After 30 Days                                 
                       %          %                                       
          Initial      Retention  Retention                               
          Flexural                                                        
                 Flexural                                                 
                       of   Flexural                                      
                                  of                                      
    Experiment                                                            
          Strength                                                        
                 Strength                                                 
                       Flexural                                           
                            Strength                                      
                                  Flexural                                
Ex. No.   (PSI)  (PSI) Strength                                           
                            (PSI) Strength                                
__________________________________________________________________________
92  1     7.09 × 10.sup.3                                           
                 5.30 × 10.sup.3                                    
                       75%  2.47 × 10.sup.3                         
                                  35%                                     
93  2     5.95 × 10.sup.3                                           
                 5.87 × 10.sup.3                                    
                       99%  2.43 × 10.sup.3                         
                                  42%                                     
94  3     No Casting                                                      
                 --    --   --    --                                      
          Made                                                            
95  4     No Casting                                                      
                 --    --   --    --                                      
          Made                                                            
96  5     No Casting                                                      
                 --    --   --    --                                      
          Made                                                            
97  6     6.39 × 10.sup.3                                           
                 0.44 × 10.sup.3                                    
                        7%  0     0                                       
98  7     6.94 × 10.sup.3                                           
                 1.43 × 10.sup.3                                    
                       21%  2.25 × 10.sup.3                         
                                  32%                                     
99  8     5.00 × 10.sup. 3                                          
                 3.78 × 10.sup.3                                    
                       76%  1.35 × 10.sup.3                         
                                  27%                                     
100 9     8.47 × 10.sup.3                                           
                 5.72 × 10.sup.3                                    
                       67%  2.42 × 10.sup.3                         
                                  29%                                     
101 10    8.76 × 10.sup.3                                           
                 6.14 × 10.sup.3                                    
                       70%  2.52 × 10.sup.3                         
                                  29%                                     
102 11    6.63 × 10.sup.3                                           
                 0.93 × 10.sup.3                                    
                       14%  1.11 × 10.sup.3                         
                                  17%                                     
103 12    12.48 × 10.sup.3                                          
                 4.73 × 10.sup.3                                    
                       38%  1.89 × 10.sup.3                         
                                  13%                                     
    (Control)                                                             
__________________________________________________________________________
 
    
     EXAMPLES 104-115 
     In these examples, the physical properties and corrosion resistance of thermoset polyester containing Epolene E-43 and selected levels of high molecular weight polypropylene are determined. The resins are prepared by addition of 20% Epolene E-43 and 2.5-20% Tenite 424S polypropylene to the second-stage melt polycondensation of TMPD-based unsaturated polyesters. The polyester/polypropylene reaction products are homogeneous in the melt and remain homogeneous after dilution with 30% styrene. The thermoset flexural bars are placed in boiling 10% NaOH for 3, 6 and 12 days (initial physical properties are shown in Examples 104-109). The thermoset composition containing 20% Epolene E-43 and 5% Tenite 424S gives the best retention of flexural strength after 12 days exposure in boiling caustic (Examples 110-115). In Examples 104-115, the polyesters are derived from 75/25 TMPD/EG, 1/1 IPA/MA, except Examples 109 and 115 are bisphenol-A-fumarate. 
     
         __________________________________________________________________________
                                                Impact                    
                                                Strength                  
                        Flexural Properties                               
                                     Tensile Properties                   
                                                Unnotched                 
          Melt   Appearance                                               
                        Flexural                                          
                               Flexural                                   
                                     Tensile                              
                                          Elongation                      
                                               Izod                       
   Polyolefin                                                             
          Dispersibility                                                  
                 of Thermoset                                             
                        Strength                                          
                               Modulus                                    
                                     Strength                             
                                          to Break                        
                                               Strength                   
Ex.                                                                       
   Additive                                                               
          of Additive                                                     
                 Casting                                                  
                        (PSI)  (PSI) (PSI)                                
                                          (%)  (Ft-Lb/In.)                
__________________________________________________________________________
104                                                                       
Conrol    --     Clear  10.59 × 10.sup.3                            
                               4.82 × 10.sup.5                      
                                     3553 5     2.18                      
105                                                                       
   2.5% Tenite                                                            
          Homogeneous                                                     
                 Translucent                                              
                        7.53 × 10.sup.3                             
                               4.52 × 10.sup.5                      
                                     3538 6     1.26                      
   424                                                                    
   20% Epolene                                                            
   E-43                                                                   
106                                                                       
   5% Tenite                                                              
          &#34;      &#34;      8.42 × 10.sup.3                             
                               4.39 × 10.sup.5                      
                                     3815 7     1.25                      
   424                                                                    
   20% Epolene                                                            
   E-43                                                                   
107                                                                       
   10% Tenite                                                             
          &#34;      &#34;      7.13 × 10.sup.3                             
                               4.34 × 10.sup.5                      
                                     3306 6     0.89                      
   424                                                                    
   20% Epolene                                                            
   E-43                                                                   
108                                                                       
   20% Tenite                                                             
          &#34;      &#34;      8.13 × 10.sup.3                             
                               4.14 × 10.sup.5                      
                                     3592 6 1.18                          
   424                                                                    
   20% Epolene                                                            
   E-43                                                                   
109                                                                       
Commercial                                                                
   &#34;      Clear  11.47 × 10.sup.3                                   
                        4.42 × 10.sup.5                             
                               4009  7    1.19                            
   Control                                                                
__________________________________________________________________________
 
    
     
         __________________________________________________________________________
                 Exposure to Boiling 10% NaOH                             
                 Flexural Strength and % Retention of Flexural Strength   
          After 3 Days      After 6 Days                                  
                                       After 12 Days                      
          Initial      %          %          %                            
          Flexural                                                        
                 Flexural                                                 
                       Retention                                          
                            Flexural                                      
                                  Retention                               
                                       Flexural                           
                                             Retention                    
                                                  Appearance              
   Polyolefin                                                             
          Strength                                                        
                 Strength                                                 
                       Flexural                                           
                            Strength                                      
                                  Flexural                                
                                       Strength                           
                                             Flexural                     
                                                  After                   
Ex.                                                                       
   Additive                                                               
          (PSI)  (PSI) Strength                                           
                            (PSI) Strength                                
                                       (PSI) Strength                     
                                                  12 Days                 
__________________________________________________________________________
110                                                                       
Control   10.59 × 10.sup.3                                          
                 3.75 × 10.sup.3                                    
                       35%  4.03 × 10.sup.3                         
                                  38%  2.79 × 10.sup.3              
                                             26%  Pitted,                 
                                                  hazy                    
                                                  surface                 
111                                                                       
   2.5% Tenite                                                            
          7.53 × 10.sup.3                                           
                 7.66 × 10.sup.3                                    
                       102% 6.43 × 10.sup.3                         
                                  85%  6.20 × 10.sup.3              
                                             82%  Smooth,                 
   424                                            glossy                  
   20% Epolene                                    surface                 
   E-43                                                                   
112                                                                       
   5% Tenite                                                              
          8.42 × 10.sup.3                                           
                 7.05 × 10.sup. 3                                   
                       84%  6.82 × 10.sup.3                         
                                  81%  7.24 × 10.sup.3              
                                             86%  Smooth,                 
   424                                            glossy                  
   20% Epolene                                    surface                 
   E-43                                                                   
113                                                                       
   10% Tenite                                                             
          7.13 × 10.sup.3                                           
                 --    --   --    --   1.59 × 10.sup.3              
                                             22%  Blistered               
   424                                            surface                 
   20% Epolene                                                            
   E-43                                                                   
114                                                                       
   20% Tenite                                                             
          8.13 × 10.sup.3                                           
                 7.12 × 10.sup.3                                    
                       88%  6.22 × 10.sup.3                         
                                  77%  4.63 × 10.sup.3              
                                             57%  Blistered               
   424                                            surface                 
   20% Epolene                                                            
   E-43                                                                   
115                                                                       
Commercial                                                                
   11.47 × 10.sup.3                                                 
          9.99 × 10.sup.3                                           
                 87%   8.94 × 10.sup.3                              
                            78%   9.51 × 10.sup.3                   
                                       83%   Smooth,                      
   Control                                        glossy                  
                                                  surface                 
__________________________________________________________________________
 
    
     EXAMPLE 116-121 
     These examples illustrate the effect of selected glycol structures on the corrosion resistance of polyester/polyolefin compositions. The data show that polyester compositions prepared by the melt-phase reaction with 20% maleated polypropylene (Epolene E-43) show overall enhancement of retention of flexural strength and modulus after exposure to boiling 10% NaOH, compared with the polyester controls. The most significant improvement in corrosion resistance is obtained when the glycol is TMPD. 
     
         __________________________________________________________________________
                     Exposure to Boiling 10% NaOH                         
                           Flexural Strength and % Retention              
                                             Flexural Modulus and %       
                                             Retention                    
                           After 12 Days                                  
                                    After 30 Days                         
                                             After 12 Days                
                                                      After 30 Days       
               Initial                                                    
                     Initial     %        %        %        %             
          Poly-                                                           
               Flexural                                                   
                     Flexural                                             
                           Flexural                                       
                                 Ret.                                     
                                    Flexural                              
                                          Ret.                            
                                             Flexural                     
                                                   Ret.                   
                                                      Flexural            
                                                            Ret.          
   Polyester                                                              
          olefin                                                          
               Strength                                                   
                     Modulus                                              
                           Strength                                       
                                 Flex.                                    
                                    Strength                              
                                          Flex.                           
                                             Modulus                      
                                                   Flex.                  
                                                      Modulus             
                                                            Flex.         
Ex.                                                                       
   Composition                                                            
          Additive                                                        
               (× 10.sup.3 PSI)                                     
                     (× 10.sup.5 PSI)                               
                           (× 10.sup.3 PSI)                         
                                 Str.                                     
                                    (× 10.sup.3 PSI                 
                                          Str.                            
                                             (× 10.sup.3            
                                                   Str.                   
                                                      (× 10.sup.5   
                                                      PSI)  Mod           
__________________________________________________________________________
116                                                                       
   TMPD/ISO/                                                              
          Control                                                         
               12.09 4.51  7.36  61%                                      
                                    4.76  39%                             
                                             4.36  97%                    
                                                      4.37  97% - MA 20%  
117                                                                       
   TMPD/ISO/                                                              
          Epolen                                                          
               7.88  4.38  6.84  87%                                      
                                    4.56  58%                             
                                             4.22  96%                    
                                                      3.53  81%           
   MA     E-43                                                            
118                                                                       
   NPG/ISO/                                                               
          Control                                                         
               15.65 5.47  0.60   4%                                      
                                    0.sup.(1)                             
                                          -- 0.47   9%                    
                                                      0.sup.(1)           
                                                            --            
   MA     20%                                                             
119                                                                       
   NPG/ISO/                                                               
          Epolene                                                         
               8.44  5.20  2.87  34%                                      
                                    0.89  11%                             
                                             3.11  60%                    
                                                      0.70  13%           
   MA     E-43                                                            
120                                                                       
   PG/ISO/                                                                
          Control                                                         
               15.19 5.53  0.53   4%                                      
                                    0.sup.(1)                             
                                          -- 0.32   6%                    
                                                      0.sup.(1)           
                                                            --            
   MA     20%                                                             
121                                                                       
   PG/ISO/                                                                
          Epolene                                                         
               8.67  5.29  0.50   6%                                      
                                    0.sup.(1)                             
                                          -- 0.39   7%                    
                                                      0.sup.(1)           
                                                            --            
   MA     E-43                                                            
__________________________________________________________________________
 .sup.(1) Samples too brittle to test                                     
 
    
     EXAMPLES 122-130 
     These examples demonstrate the significant differences in corrosion-resistant properties of thermoset compositions prepared by the melt phase reaction of polyolefins with an unsaturated polyester, compared with physical blend compositions of the corresponding powdered polyolefin(s) and the styrene-unsaturated polyester solution. 
     The melt-phase prepared polyester/polyolefin compositions in these examples are prepared by methods outlined in the previous ecamples (75/25 TMPD/EG, 1/1 IPA/MA). The physical blends of unsaturated polyester and polyolefins are prepared by the addition of finely powdered polyolefins (3-50 micron particle size range) to the solution of unsaturated polyester dissolved in styrene. The polyolefin powders are dispersed in the unsaturated polyester/styrene solution by placing the materials in a glass jar and rolling the contents for 24 hrs. In each case, thermoset castings are prepared and flexural bar specimens exposed to boiling 10% NaOH. After appropriate exposure times, the specimens are removed from the corrosive medium and tested for retention of flexural strength and modulus. The results clearly show the superior corrosion resistance properties of polyester/polyolefin compositions prepared by the melt phase process compared with the conventional art of physical blends. 
     
         __________________________________________________________________________
                               Exposure to Boiling 10% NaOH               
                               Flexural Strength                          
                                               Flexural Modulus           
                               and % Retention and % Retention            
                       Init.                                              
                           Init.                                          
                               After 12 Days                              
                                       After 30 Days                      
                                               After 12                   
                                                       After 30 Days      
Polyolefine and Method Flex.                                              
                           Flex.                                          
                               Flex.                                      
                                   %   Flex.                              
                                           %   Flex.                      
                                                   %   Flex.              
                                                           %              
of Addition to Polyester                                                  
                       Str.                                               
                           Mod.                                           
                               Str.                                       
                                   Ret.                                   
                                       Str.                               
                                           Ret.                           
                                               Mod.                       
                                                   Ret.                   
                                                       Mod.               
                                                           Ret.           
   Melt Phase Physical (× 10.sup.3                                  
                           (× 10.sup.5                              
                               (× 10.sup.3                          
                                   Flex.                                  
                                       (× 10.sup.3                  
                                           Flex.                          
                                               (× 10.sup.5          
                                                   Flex.                  
                                                       × 10.sup.5   
                                                           Flex.          
Ex.                                                                       
   Reaction   Blend    PSI)                                               
                           PSI)                                           
                               PSI)                                       
                                   Str.                                   
                                       PSI Str.                           
                                               PSI)                       
                                                   Mod.                   
                                                       PSI Mod            
__________________________________________________________________________
122                                                                       
   --         --       12.84                                              
                           4.63                                           
                               2.30                                       
                                   18% 0.sup.(1)                          
                                           --  2.50                       
                                                   54% 0.sup.(1)          
                                                           --             
123                                                                       
   20% Epolene E-43    7.00                                               
                           4.48                                           
                               5.60                                       
                                   80% 1.80                               
                                           26% 4.00                       
                                                   83% 2.54               
                                                           57%            
124           20% Epolene                                                 
                       5.29                                               
                           4.85                                           
                               0.54                                       
                                   10% 0.sup.(1)                          
                                           --  0.57                       
                                                   12% 0.sup.(1)          
                                                           --             
              E-43                                                        
125                                                                       
   20% Epolene E-43    8.76                                               
                           4.33                                           
                               6.14                                       
                                   70% 2.52                               
                                           29% 4.49                       
                                                   104%                   
                                                       3.36               
                                                           75%            
   5% Tenite 424S                                                         
126           20% Epolene                                                 
                       6.51                                               
                           4.86                                           
                               0.sup.(1)                                  
                                   --  0.sup.(1)                          
                                           --  0.sup.(1)                  
                                                   --  0.sup.(1)          
                                                           --             
              E-43                                                        
              5% Tenite 424                                               
127                                                                       
   20% Epolene C-16    7.49                                               
                           3.37                                           
                               4.70                                       
                                   63% 1.72                               
                                           23% 3.12                       
                                                   93% 2.14               
                                                           64%            
128           20% Epolene                                                 
                       8.31                                               
                           5.13                                           
                               3.35                                       
                                   40% 1.33                               
                                           16% 4.18                       
                                                   82% 1.49               
                                                           29%            
              C-16                                                        
129                                                                       
   20% Epolene C-16    7.17                                               
                           3.25                                           
                               5.23                                       
                                   73% 0.sup.(1)                          
                                           --  2.72                       
                                                   84% 0.sup.(1)          
                                                           --             
   5% Tenite 18BOA                                                        
130           20% Epolene                                                 
                       3.01                                               
                           3.09                                           
                               1.71                                       
                                   57% 0.sup.(1)                          
                                           --  2.03                       
                                                   66% 0.sup.(1)          
                                                           --             
              C-16                                                        
              5% Tenite                                                   
__________________________________________________________________________
 .sup.(1) Samples too brittle to test.                                    
 
    
     EXAMPLES 131-138 
     These examples illustrate the effect of a range of dibasic acid structures selected for preparation of unsaturated polyester/polyolefin compositions, and the resulting effect of the acid structure on the corrosion resistance of the thermoset materials. The dibasic acids selected include isophthalic acid 1,4-cyclohexane dicarboxylic acid (CHDA), adipic acid and suberic acid. The polyester/polyolefin compositions are prepared with the indicated acids by the melt phase method previously described. The polyester/polyolefin resins are dissolved in 40% styrene and crosslinked with 1% benzoyl peroxide as 1/8 in. thick sheets. Flexural bar specimens (1/8 in.×1/2 in.×4 in.) are cut from the sheets and placed in 10% boiling NaOH. The bars are removed after 12 and 30 days exposure and evaluated for retention of flexural strength and flexural modulus. The results show that the structure of the dibasic acid used in the preparation of the unsaturated polyester/polyolefin composition have a significant effect on its corrosion resistance. The results show that the aromatic dibasic acid imparts higher corrosion resistance to the polyester/polyolefin composition than aliphatic acids. These examples further demonstrate the enhanced corrosion resistance of compositions containing 20% maleated polypropylene (Epolene E-43) compared with the control samples without Epolene E-43. 
     
         __________________________________________________________________________
                               Exposure to Boiling 10% NaOH               
                               Flexural Strength                          
                                               Flexural Modulus           
                               and % Retention and % Retention            
                       Init.                                              
                           Init.                                          
                               After 12 Days                              
                                       After 30 Days                      
                                               After 12                   
                                                       After 30 Days      
                       Flex.                                              
                           Flex.                                          
                               Flex.                                      
                                   %   Flex.                              
                                           %   Flex.                      
                                                   %   Flex.              
                                                           %              
                       Str.                                               
                           Mod.                                           
                               Str.                                       
                                   Ret.                                   
                                       Str.                               
                                           Ret.                           
                                               Mod.                       
                                                   Ret.                   
                                                       Mod.               
                                                           Ret.           
   Polyester    Polyolefin                                                
                       (× 10.sup.3                                  
                           (× 10.sup.5                              
                               (× 10.sup.3                          
                                   Flex.                                  
                                       (× 10.sup.3                  
                                           Flex.                          
                                               (× 10.sup.5          
                                                   Flex.                  
                                                       (× 10.sup.5  
                                                           Flex.          
Ex.                                                                       
   Composition  Additive                                                  
                       PSI)                                               
                           PSI)                                           
                               PSI Str.                                   
                                       PSI)                               
                                           Str.                           
                                               PSI)                       
                                                   Mod.                   
                                                       PSI Mod.           
__________________________________________________________________________
131                                                                       
   TMPD/EG/ISO/MA                                                         
                Control                                                   
                       12.84                                              
                           4.63                                           
                               2.30                                       
                                   18% 0.sup.(1)                          
                                           --  2.50                       
                                                   54% 0.sup.(1)          
                                                           --             
132                                                                       
   TMPD/EG/ISO/MA                                                         
                20% Epolene                                               
                       7.00                                               
                           4.48                                           
                               5.60                                       
                                   80% 1.80                               
                                           26% 4.00                       
                                                   83% 2.54               
                                                           57%            
                E-43                                                      
133                                                                       
   TMPD/EG/CHDA/MA                                                        
                Control                                                   
                       10.84                                              
                           4.14                                           
                               1.77                                       
                                   16% 0.sup.(1)                          
                                           --  1.87                       
                                                   45% 0.sup.(1)          
                                                           --             
134                                                                       
   TMPD/EG/CHDA/MA                                                        
                20% Epolene                                               
                       7.26                                               
                           3.95                                           
                               2.85                                       
                                   39% 0.60                               
                                           8%  3.23                       
                                                   82% 0.36               
                                                           9%             
                E-43                                                      
135                                                                       
   TMPD/EG/Adipic/MA                                                      
                Control                                                   
                       10.19                                              
                           2.77                                           
                               0.74                                       
                                    7% 0.sup.(1)                          
                                           --  0.42                       
                                                   15% 0.sup.(1)          
                                                           --             
136                                                                       
   TMPD/EG/Adipic/MA                                                      
                20% Epolene                                               
                       8.10                                               
                           3.03                                           
                               1.24                                       
                                   15% 0.sup.(1)                          
                                           --  1.09                       
                                                   36% 0.sup.(1)          
                                                           --             
                E-43                                                      
137                                                                       
   TMPD/EG/Suberic/MA                                                     
                Control                                                   
                       7.35                                               
                           1.93                                           
                               0.57                                       
                                    8% 0.sup.(1)                          
                                           --  0.50                       
                                                   26% O.sup.(1)          
                                                           --             
138                                                                       
   TMPD/EG/Suberic/MA                                                     
                20% Epolene                                               
                       7.52                                               
                           2.81                                           
                               2.52                                       
                                   34% 0.69                               
                                           9%  1.63                       
                                                   58% 0.24               
                                                           95             
                E-43                                                      
__________________________________________________________________________
 .sup.(1) Samples too brittle to test.                                    
 
    
     Unless otherwise specified, all parts, ratios, percentages, etc. are on a weight basis. 
     It will be understood to those skilled in the art that where the term acid is used, the corresponding anhydride may often be used and may sometimes be preferable. 
     The invention has been described in detail with particular reference to preferred embodiments thereof, but it will be understood that variations and modifications can be effected within the spirit and scope of the invention.