Preparation of epoxy resin-rubber-glass mixture and mixture produced
BACKGROUND OF THE INVENTION 
     This invention relates to the utilization of rubber and glass materials and, more particularly, to the utilization of used rubber and glass materials to form a new composition. 
     Industrialized societies produce large quantities of waste materials which are typically incinerated and then used as landfill. However, in recent years there have been increased efforts to recover the valuable products from this waste. In particular ferrous metals have been separated from the waste by magnetic attraction and have been melted, combined with new metal and used to form new metallic products. Rubber from tires has been reused to form new tires. Attempts have also been made to convert animal and vegetable wastes into sugars, alcohol and even hydrocarbons, e.g. methane gas, which can be used in other processes. 
     The glass material found in waste is typically not reused because there are more than 500 different types of glass made each year and each must be made with certain critical parameters. It would be extremely difficult to separate the various types of glass in the waste material into the type needed for a particular process. 
     Plastics are used to produce a number of inexpensive items. Usually, plastic objects are made from previously unused raw materials, e.g. crude oil products. If it were possible to replace these plastic objects with objects made from waste materials, there would be a saving of raw materials, particularly precious crude oil. 
     SUMMARY OF THE INVENTION 
     The present invention is directed to the formation of a rubber-glass material useful for many for the applications to which plastics are put. 
     In an illustrative embodiment of the invention waste rubber, e.g. from automobile tires, is reduced to a melt and is mixed with a melt of discarded glass. Small quantities of epoxy, sand and water are added. The mixture is stirred until a homogeneous mass is obtained and is then allowed to solidify in a mold. The result is a rather tough and relatively inflexible object that can replace typical plastic objects used for industrial and household applications. 
     DESCRIPTION OF A PREFERRED EMBODIMENT 
     In forming the rubber-glass material for the present invention, rubber, e.g. newly formed or from automobile tires, is ground to a sand-like consistency and is heated to about 400° F. to form a melt. At the same time, new glass or discarded glass is ground and heated to a temperature of about 2,600° F. in a separate kiln in order to form a melt. The two substances, while still in the molten state, are mixed together in a cylindrical vessel in a range of proportions, i.e. 20-80% by volume of the glass is added to the rubber. Minute quantities of an epoxy resin (approximately 0.5-1.5%), sand and water are also added at a later point. The epoxy and sand act as binders and the water is added to increase the liquidity and homogeneity of the mixture. While cooling the mixture is stirred to an even consistency and then poured into a suitable mould. 
    
    
     EXAMPLE 
     Portions of disposed ground glass and ground rubber from automobile tires were melted in separate vessels at temperatures of 2,600° F. and 400° F. respectively. The two portions were then mixed in equal proportions by volume. An epoxy resin in an amount equal to 1% of the volume of the mixture and approximately 1% by volume of sand were also added. The mixture was stirred until homogenous. Over the course of one hour the temperature dropped, but the mixture did not immediately solidify. Therefore it was possible to add small quantities of water to the mixture as it was being mixed in order to assure a uniform consistency. Before the mixture solidified it was poured into a mold and then allowed to harden over the course of another two hours. 
     The result was a molded object that had the following approximate quantitive properties: 
     
         ______________________________________                                    
 Specific Gravity     2.8                                                 
Tensile Strength      12,000 psi                                          
Compressive Strength  40,000 psi                                          
Modulus of Elasticity 8 × 10.sup.6 psi                              
______________________________________                                    
 
    
     Qualitatively the molded object had excellent resistance to solvents and cold flow. Its resistance to abrasion and heat was very good. The object even had good resistance to oils. 
     When the mixture has a larger precentage of rubber it is more elastic and has much the same properties as hard rubber. If the mixture has more glass, the end product is somewhat like thin sheet metal. Naturally the thickness of the cast product affects its final properties. 
     Because of its properties the mixture can be used to replace many plastic objects formerly prepared from crude oil products. In particular it can be molded into household products, farm implements, toys, food and beverage containers, oil and gasoline containers, paint containers, coat hangers etc. Also, if mixed with asphalt, it can be used for filling pot holes. 
     While the invention has been particularly shown and described with reference to a preferred embodiment thereof, it will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention. In particular, new glass and rubber, and not discarded materials, may be employed.