Hydrocarbon middle distillates composition containing nitrogen-containing additives for decreasing its cloud point
This is a continuation of application Ser. No. 659,922 filed Oct. 11, 1985, which is a continuation of Ser. No. 404,090, filed July 30, 1982, now abandoned. 
    
    
     BACKGROUND OF THE INVENTION 
     The invention relates to new nitrogen additives which can be used as agents for decreasing the cloud point of hydrocarbon middle distillates (fues oils, gas oils), as well as to compositions of middle distillates containing said additives. 
     The oil distillates of interest in the invention are middle distillates (fuel oils, gas oils) whose distillation range (standard ASTM D 86-87) is between 150° C. and 450° C. Gas oils which are of more particular interest distill between an initial temperature from 160° C. to 190° C. and a final temperature from 350° C. to 390° C. 
     A great number of products sold on the market are designed to improve the limit filtrability temperature and the pour point of oil cuts of high paraffin content, for example: 
     polymers based on long chain olefins, 
     copolymers based on alpha-olefins, 
     ethylene-vinyl acetate copolymers, 
     N-acylaminoethylesters of acid-containing polymers, or 
     halocarbon compounds. 
     These products act on the kinetic crystallization phenomena and change the crystal size, thus allowing the use of the suspension at a lower temperature without plugging of the pipes and the filters. The above products do not modify the temperature at which the first paraffin crystals appear. As a matter of fact, it has been considered, up to now, that this temperature was dependent on the molecular weight and the composition of the paraffins and on the nature of the solvent. 
     A decrease of the cloud point of middle distillates (particularly gas oils) by means of an additive would be highly beneficial to the refiners, since it would make it possible, without changing the distillation diagram, to comply with the standards which are presently subject to an increasing severity. 
     SUMMARY OF THE INVENTION 
     It has now been discovered that certain chemicals, whose definition is given hereinafter, when added to middle distillates, have the ability to make the first paraffin crystals appear at a lower temperature than that observed in the absence of these additives. This property is the more unobvious as it is still maintained after several cycles of heating and cooling and operates according to a mechanism which has not yet been explained. 
     This class of chemical compounds also has an action on other properties of middle distillates (particularly gas oils), by modifying the behavior of the medium which contains the precipitated paraffins. 
     Thus, the compounds proposed in this invention have a substantial affect on the limit filterability temperature and the pour point. 
     When paraffin crystals have formed by cooling, their normal tendency is to assemble by gravity at the bottom. This phenomenon, generally called settling, results in the plugging of ducts and filters and is detrimental to a safe use of middle distillates, particularly gas oils. The chemicals proposed in the invention can decrease substantially the settling rate of the paraffins formed by cooling of gas oils and other middle distillates. 
     Finally, the proposed products for having the above mentioned properties, also confer to the gas oils and middle distillates, to which they are added, anti-corrosion properties with respect to metal surfaces. 
     DETAILED DISCUSSION 
     As a general rule, the additives of the invention can be defined as products having an average molecular weight of about 300 to 10,000, obtained by condensation of at least one compound comprising a primary amine function, complying with one of the following general formulas (I) and (II): 
     
         R--Z--(CH.sub.2).sub.n NH].sub.m H                         (I) 
    
     and 
     
         HO--CH.sub.2 --R.sup.5 --NH.sub.2                          (II) 
    
     with at least one dicarboxylic compound as hereinafter defined. 
     In formula (I), R is generally a monovalent saturated aliphatic radical comprising from 1 to 30 carbon atoms; Z can be, depending on the case, an oxygen atom or a divalent group of the type --NR&#39;--, R&#39; being either a hydrogen atom or a monovalent aliphatic radical; n is an integer from 2 to 4 and m may be zero or an integer from 1 to 4. 
     The compounds of the above formula (I) may consist of primary amines of the formula R 1  --NH 2  (in that case, in formula (I), Z represents a --NH-- group and the value of m is zero). 
     The radical R 1  is preferably linear and comprises from 12 to 30, particularly from 16 to 25 carbon atoms. 
     Specific examples of these amines are: dodecylamine, tetradecylamine, hexadecylamine, octadecylamine, eicosylamine and docosylamine, hexadecylamine and octadecylamine being preferred. 
     The compounds of the formula (I) may also consist of polyamines obtained from saturated aliphatic amines of the formula: 
     
         R.sup.1 --NH--(CH.sub.2).sub.n NH].sub.m H 
    
     corresponding to the general formula (I) wherein Z is a --NH-- group; m may have a value from 1 to 4 and n a value from 2 to 4, preferably 3. 
     Preferably, the radical R 1  is linear and comprises from 12 to 30 and particularly from 16 to 25 carbon atoms. 
     Specific compounds are: N-dodecyl 1,3-diaminopropane N-tetradecyl 1,3-diamino propane, N-hexadecyl 1,3-diaminopropane, N-octadecyl 1,3-diamino propane, N-eicosyl 1,3-diaminopropane, N-docsyl 1,3-diaminopropane, N-hexadecyldipropylenetriamine, N-octadecyl dipropylenetriamine, N-eicosyldipropylenetriamine and N-docosyl dipropylenetramine. There are more advantageously used N-docosyl-, N-eicosyl-, N-octadecyl-, N-hexadecyl- or N-dodecyl 1,3-diamino propane, as well as N-hexadecyl- and N-octadecyl-dipropylenetriamine. 
     The compounds of formula (I) may also consist of polyamines of the formula: ##STR1## wherein R 2  and R 3 , identical or different, are each an alkyl radical with 1 to 24 and preferably 8 to 22 carbon atoms, R 2  and R 3  preferably comprising together from 16 to 32 carbon atoms; n has a value from 2 to 4 and m a value from 1 to 4. 
     Specific compounds are: N,N-diethyl 1,2-diaminoethane, N,N-diisopropyl 1,2-diamino ethane, N,N-dibutyl 1,2-diaminoethane, N,N-diethyl 1,4-diaminobutane, N,N-dimethyl 1,3-diaminoethane, N,N-diethyl 1,3-diaminobutane, N,N-dioctyl 1,3-diaminobutane, N,N-didecyl 1,3-diaminobutane, N,N-didodecyl 1,3-diaminobutane, N,N-ditetradecyl 1,3-diaminobutane, N,N-dihexadecyl 1,3-diaminobutane, N,N-dioctadecyl 1,3-diamino propane, N,N-didodecyldipropylenetriamine, N,N-ditetradecyldipropylenetriamine, N,N-dihexadecyldipropylenetriamine and N,N-dioctadecyldipropylenetriamine. 
     Finally the compounds of formula (I) contemplated in this invention may consist of ether-amines, more particularly those complying with the formula: 
     
         R.sup.4 --O(CH.sub.2).sub.n NH].sub.m H 
    
     corresponding to the general formula (I) wherein Z is an oxygen atom; the radical R 4  comprises 1 to 24, preferably 8 to 22 carbon atoms, m is an integer from 1 to 24 and n an integer from 1 to 4, preferably 2 or 3. 
     Specific compounds of the ether-amine type are: 2-methoxy ethylamine, 3-methoxy propylamine, 4-methoxy butylamine, 3-ethoxy propylamine, 3-octyloxy propylamine, 3-decyloxy propylamine, 3-hexadecyloxy propylamine, 3-eicosyloxy propylamine, 3-docosyloxy propylamine, N-(3-octyloxy propyl) 1,3-diaminopropane, N-(3-decyloxy propyl) 1,3-diaminopropane, 3-(2,4,6-trimethyldecyloxy)propylamine and N-[3-(2,4,6-trimethyldecyloxy)-propyl]-1,3-diaminopropane. 
     The compound with a primary amine function which is used for preparing additives conforming to the invention may also consist of an aminoalcohol of formula (II): 
     
         HO--CH.sub.2 --R.sup.5 --NH.sub.2                          (II) 
    
     wherein R 5  is a divalent saturated aliphatic radical, linear or branched, preferably linear, comprising 1 to 18 and preferably 10 to 18 carbon atoms. 
     Specific examples are: monoethanolamine, 1-amino 3-propanol, 1-amino 4-butanol, 1-amino 5-pentanol, 1-amino 6-hexanol, 1-amino 7-heptanol, 1-amino 8-octanol, 1-amino 10-decanol, 1-amino 11-undecanol, 1-amino 13-tridecanol, 1-amino 14-tetradecanol, 1-amino 16-hexadecanol, 2-amino 2-methyl 1-propanol, 2-amino 1-butanol and 2-amino 1-pentanol. 
     It must be understood that, without departing from the invention, it is possible to operate with one or more compounds of formula (I) and/or one or more compounds of formula (II). 
     The dicarboxylic compounds on which is effected the condensation of a compound of formula (I) or a compound of formula (II) such as described hereinbefore are more particularly selected from the anhydrides of aliphatic, preferably unsaturated, α,β-dicarboxylic acids, such as, for example, maleic anhydride, alkylmaleic anhydrides, for example methylmaleic (or citraconic) anhydride, or from the alkenyl-succinic anhydrides, for example those obtained by reacting at least one α-olefin, preferably linear, (having, for example, 10 to 30 carbon atoms) with maleic anhydride. Specific examples are n-octadecenyl succinic anhydride or dodecenyl succinic anhydride. It is obviously possible to use mixtures of two (or more) of these compounds. 
     It is also possible, according to the invention, to use polyalkenyl-succinic anhydrides, for example polyisobutenyl-succinic anhydrides, whose molecular weight is selected between 500 and 2000 and preferentially between 1000 and 1700. The manufacture of anhydrides of this type is well known in the prior art. 
     The above mentioned anhydrides may be replaced by the corresponding dicarboxylic acids, or by the lower alkyl diesters thereof (such as, for example, methyl, ethyl, propyl and butyl esters). 
     The compounds with a primary amine function of the formulas (I) and (II) are commonly used in a proportion of 1.02 to 1.2 mole, preferably 1.05 to 1.1 mole, per mole of the dicarboxylic compound. The compound with a primary amine function (I) or (II) may also be used in slight deficiency, down to 0.9 mole per mole of the dicarboxylic compound. The proportion is thus generally from 0.9 to 1.2 mole/mole. 
     The condensation of the compounds of formula (I) and/or (II) with the dicarboxylic compounds (for example dicarboxylic acids, esters or preferably anhydrides) may be effected without solvent; but preferably with a solvent, consisting more particularly of an aromatic or napheno-aromatic hydrocarbon having a boiling point of for example, from 70° to 250° C.: toluene, xylenes, diisopropylbenzene or an oil cut having the appropriate distillation range. 
     The additive compositions of the invention can be prepared, in practice, as follows: the compound of formula (I) and/or (II) is introduced progressively into a reactor containing the dicarboxylic compound, while maintaining the temperature between 30° and 80° C. The temperature is then raised to 120°-200° C. while eliminating the resultant volatile products (water or alcohols), either stripping with a stream of inert gas or by azeotropic distillation with the selected solvent; the content of dry substance is, for example, from 40 to 70% more often about 60%. 
     The reaction time, after addition of the reactants, is, for example, from 1 to 8 hours, preferably 3 to 6 hours. 
     The additives contemplated in this invention are particularly efficient for improving the cloud point of oil middle distillates (particularly gas oils), thus decreasing the temperature at which appear the first crystals of paraffin contained therein. 
     Although the action of these additives on the temperature at which the paraffin crystals appear in the middle distillates has not yet been clearly elucidated, a positive improvement i.e., a significant lowering of the cloud point of the middle distillates treated with these additives is observed, when the latter are added in a proportion of, for example, from 20 to 2000 g per ton of middle distillate. The preferred concentrations range from 100 to 2000 g/t. The decrease of the cloud point may reach, for example, 5° C., sometimes more. 
     It is also noteworthy that the additives of the invention, which improve efficiently the cloud point of middle distillates, also have the properties of inhibiting the settling of n-paraffins contained in middle distillates, also at rest, of improving the limit filterability temperature and the pour temperature and of inhibiting the corrosion of metal surfaces in contact with these distillates. 
     Thus, in the range of additive concentrations, from 20 to 2000 g per ton, it is possible to observe a decrease in the filterability temperature of, for example, up to 12° C. a decrease of the pour point of up to 20° C., a decrease of the proportion of settled paraffins and a clear anticorrosion effect particularly on ferrous metals. 
     The middle distillate compositions according to the invention may be prepared by directly admixing additives with the middle distillate. 
     It is however often advantageous to introduce them in the form of &#34;mother-solutions&#34; previously prepared in the above-mentioned solvents. 
     The &#34;mother-solutions&#34; can contain, for example, from 20 to 60% by weight of additive. 
     The following examples illustrate the invention and must not be considered as limitative thereof in any respect. 
    
    
     EXAMPLE 1 
     2,700 g of a polyamine of the trade (containing, in admixture, about 27% of palmityl 1,3 -propanediamine and 70% of stearyl 1,3 propanediamine, with a 370 g equivalent of primary amine) and 2,700 g of xylene are introduced into a 20 liter reactor provided with an efficient stirrer; the amine is dissolved at 50° C.; after cooling to 30° C., a solution of 699 g of maleic anhydride in 1,050 g of xylene is added, while maintaining the inner temperature at 40° C. The addition lasts one hour; heating at xylene reflux is then performed for 3 hours, the inner temperature being 144° C.; 157 g of water, corresponding to 128 g of reaction water and 29 g of water contained in the amine, are removed by distillation; once the reaction is complete, 500 g of xylene are distilled to obtain a 50% b.w. solution of additive I in xylene. 
     Additive I has been analyzed after evaporation of the solvent. Its molecular weight, by number, measured by tonometry, amounts to 1800. The thin layer infra-red spectrum shows the presence of imide bands at 1700 and 1780 cm -1 , secondary amide bands at 1635 and 1560 cm -1  and a secondary amine band at 3300 cm -1 . 
     Additives II to VII have the same bands as additive I. Their molecular weights range between 1500 and 3000. 
     The activity of additive I is determined with two gas oil cuts of Aramco origin, whose characteristics are given in Table I below: 
     
                       TABLE I                                                     
______________________________________                                    
       DISTILLA-             DENSITY                                      
       TION ASTM                                                          
                % DISTILLED  15° C. IN                             
       IP.sub.°C.                                                  
            FP.sub.°C.                                             
                    AT 350° C.                                     
                                 (Kg/l)                                   
______________________________________                                    
Gas oil No. 1                                                             
         181    382     89         0.846                                  
Gas oil No. 2                                                             
         186    385     87         0.847                                  
______________________________________                                    
 
    
     The effect of additive I on the decrease of the cloud point of each of the two gas oil cuts, in relation with the additive concentration, determined according to standard NF T 60105, is shown in Table II below. 
     
                       TABLE II                                                    
______________________________________                                    
ADDITIVE     CLOUD POINT    CLOUD POINT                                   
CONCENTRATION                                                             
             (°C.)   (°C.)                                  
(% b.w.)     GAS OIL No. 1  GAS OIL No. 2                                 
______________________________________                                    
0            +2             +6                                            
0.01         +1             +5                                            
0.05          0             +4                                            
0.1          -1             +2                                            
0.15         -1             +2                                            
0.2          -2             +1                                            
______________________________________                                    
 
    
     EXAMPLE 2 
     Additives differing mainly by the starting amine are used in an amount of 0.1% b.w. in the two gas oil cuts of example 1, the method of manufacture being the same as in example 1. 
     Additive I: product used in example 1; 
     Additive II: product obtained by condensing N-stearyl-dipropylene triamine with maleic anhydride: 
     Additive III: product obtained by condensing stearyl amine with maleic anhydride. 
     The results are given in Table III below: 
     
                       TABLE III                                                   
______________________________________                                    
CLOUD POINT (°C.)                                                  
              GAS OIL No. 1 GAS OIL No. 2                                 
______________________________________                                    
Additive-free +2            +6                                            
+0.1% additive I                                                          
              -1            +2                                            
+0.1% additive II                                                         
               0            +3                                            
+0.1% additive III                                                        
              +1            +5                                            
______________________________________                                    
 
    
     It is found that the effect of decreasing the cloud point is maximum in the case of additive I, wherein the starting amine is a mixture of two N-alkyl 1,3 propanediamines. 
     EXAMPLE 3 
     Additives differing essentially by the length of the alkyl chain of the starting amine are used in this example, in an amount of 0.1% b.w. in the same two gas oils as above. 
     There are thus used: 
     Additive I: product used in example 1: 
     Additive IV: product obtained by condensing N-behenyl 1,3 propane with maleic anhydride (benhenyl=C 22 ) 
     Additive V: product obtained by condensing N-lauryl 1,3 propane with maleic anhydride (lauryl=C 12 ) 
     The results of the determinations of the cloud point are given in Table IV below 
     
                       TABLE IV                                                    
______________________________________                                    
CLOUD POINT (°C.)                                                  
              GAS OIL No. 1 GAS OIL No. 2                                 
______________________________________                                    
Additive-free +2            +6                                            
+0.1% additive I                                                          
              -1            +2                                            
+0.1% additive IV                                                         
              -1            +2                                            
+0.1% additive V                                                          
              +1            +5                                            
______________________________________                                    
 
    
     It can be observed that the additive obtained from a diamine with an alkyl chain of 12 carbon atoms has a lower efficiency than the additives obtained from a diamine with a longer chain of 16, 18 or 22 carbon atoms. 
     EXAMPLE 4 
     Additives differing essentially by the nature of the starting dicarboxylic compound are used in this example, in a proportion of 0.1% b.w. in the same two gas oils as above. 
     There are thus used: 
     Additive I: product used in example 1, obtained from maleic anhydride. 
     Additive VI: product obtained by condensing N-stearyl 1,3 propane with methylmaleic (citraconic)anhydride. 
     Additive VII: product obtained by condensing N-stearyl 1,3 propane with n-octadecenyl succinic anhydride. 
     The determined cloud points are shown in Table V below: 
     
                       TABLE V                                                     
______________________________________                                    
CLOUD POINT (°C.)                                                  
              GAS OIL No. 1 GAS OIL No. 2                                 
______________________________________                                    
Additive-free +2            +6                                            
+0.1% additive I                                                          
              -1            +2                                            
+0.1% additive VI                                                         
               0            +3                                            
+0.1% additive VII                                                        
               0            +3                                            
______________________________________                                    
 
    
     EXAMPLE 5 
     The inhibiting effect of an additive conforming to the invention on the settling of n-paraffins crystallizing in a gas oil cut maintained at rest at low temperature is determined in this example. 
     The additive is additive I already used above. 
     Two 100 cc test tubes are filled with the already used gas oil No. 2 (distillation range: IP=186° C., FP=385° C.). 
     No additive is introduced into the first test tube. 
     0.1% b.w. of additive is introduced into the second test tube. 
     The two test tubes are closed hermetically, then left at rest in a cold room at -10° C. for one week. 
     After one week, the settling rate of the settled paraffins expressed as the volume of the upper limpid phase, is reported in the following Table: 
     
                       TABLE VI                                                    
______________________________________                                    
TEST TUBE No. 1   TEST TUBE No. 2                                         
ADDITIVE-FREE GAS OIL                                                     
                  GAS OIL + ADDITIVE I                                    
______________________________________                                    
50% vol           15% vol                                                 
______________________________________                                    
 
    
     All the precipitated paraffins are thus present in 50% by volume of the additive-free gas oil, which makes the lower portion more difficult to use as the result of the plugging of the pumps, filters and pipes. 
     As concerns the additive-containing gas oil, the upper limpid phase amounts to only 15%. The paraffins are thus in 85% of the total volume. They are in a state of better dispersion and can be transported more easily. 
     EXAMPLE 6 
     The effect of an additive conforming to the invention is tested, in this example, on the limit filterability temperature (LFT) of the two gas oil cuts described above. 
     The LFT values are determined according to standard NF M 07-042. 
     
                       TABLE VII                                                   
______________________________________                                    
CONCENTRATION OF                                                          
               TLF          TLF                                           
ADDITIVE I (% b.w.)                                                       
               GAS OIL No. 1                                              
                            GAS OIL No. 2                                 
______________________________________                                    
0               0° C.                                              
                            +3° C.                                 
0.15           -8° C.                                              
                            -5° C.                                 
0.20           -9° C.                                              
                            -9° C.                                 
______________________________________                                    
 
    
     EXAMPLE 7 
     The anti-corrosion effect of additive I of example 1 is tested in this example. 
     Product I has been used in the two gas oils No. 1 and No. 2, as hereinbefore described, at a concentration of 0.01% by weight. 
     The corrosion test consists of determining the rate of corrosion, by synthetic sea water, of cylindrical test pieces of polished steel or iron, according to the ASTM standard D 665 modified in the following manner: 
     The temperature is 32.2° C.; the test time is 20 hours. 
     The additive-free gas oils No. 1 and No. 2 cause 100% of the surface of the test pieces to rust; the two gas oils containing 0.01% b.w. of additive do not cause any rusting of the test pieces. 
     EXAMPLE 8 
     In this example, the effect of additive I, according to the invention, on the pour point of gas oil cuts is tested. The pour points are determined according to the French standard NFT 60105;  The additive is tested in an amount of 0.1% by weight. The results are given in Table VIII below. 
     
                                           TABLE VIII                              
__________________________________________________________________________
DISTILLATION   %      DENSITY                                             
                             POUR POINT                                   
ASTM           DISTILLED                                                  
                      kg/l AT                                             
                             WITHOUT                                      
                                    WITH                                  
GAS OIL                                                                   
      IP° C.                                                       
          FP° C.                                                   
               AT 350°                                             
                      15° C.                                       
                             ADDITIVE                                     
                                    ADDITIVE                              
__________________________________________________________________________
No. 1 181 382  89     0.846  -6° C.                                
                                     -9° C.                        
No. 2 186 385  87     0.847  -3° C.                                
                                     -9° C.                        
No. 3 201 366  93     0.833  -3° C.                                
                                    -15° C.                        
No. 4 186 386  89     0.833  -3° C.                                
                                    -21° C.                        
__________________________________________________________________________
 
    
     EXAMPLE 9 
     A solution consisting of 294 g (3 moles) of maleic anhydride dissolved in 500 g of xylene is introduced into a 3 liter reactor provided with a Dean and Stark water-separation system and an efficient stirrer. While maintaining the temperature of the solution between 30° and 40° C., a solution of 1230 g (3 moles) of N,N-didodecyl 1,3-diaminopropane in 1000 g of xylene is added thereto in 1.5 h. The whole is heated for 3 hours at xylene reflux, during time 55 g of water discharged from the reaction medium are collected. The reaction product constitutes additive VIII which is present as a solution is xylene at a concentration very close to 50% b.w. 
     EXAMPLE 10 
     Although operating as in example 9, 532 g (2 moles) of dodecenylsuccinic anhydride are condensed with 820 g (2 moles) of N,N-didodecyl 1,3-diaminopropane. The condensation product constitutes additive IX whose concentration in xylene is so adjusted as to attain 50% b.w. 
     EXAMPLE 11 
     In this example, use is made of a polyisobutenyl-succinic anhydride with a weight of 1200, corresponding to 0.90 anhydride group per 1000 g. According to the operating mode of example 9, 1200 g (1 mole) of this polyisobutenyl-succinic anhydride are condensed with a mixture of products consisting of 289 g (0.5 mole) of N,N dioctadecyl 1,3-diaminopropane and 40.8 g (0.4 mole) of N,N dimethyl 1,3-diaminopropane as a solution in xylene. The reaction product constitutes additive X; its xylene concentration is adjusted to 50% b.w. 
     The effect of the so-obtained additives VIII, IX and X has been tested on the cloud point (determined according to standard NF T 60-105), the limit filterability temperature (determined according to standard NF M 07-042) and the pour point (determined according to standard NF T 60-105) of the two gas oils No. 1 and No. 2, the concentration of the additive being 0.1% b.w. in each case. 
     The results are given in Table IX below: 
     
                       TABLE IX                                                    
______________________________________                                    
        CLOUD POINT          POUR POINT                                   
        (°C.)                                                      
                   T.L.F. (°C.)                                    
                             (°C.)                                 
ADDITIVES G.sub.1  G.sub.2 G.sub.1                                        
                                G.sub.2                                   
                                     G.sub.1                              
                                           G.sub.2                        
______________________________________                                    
0.1% VIII -1       +3      -4    0   -9    -9                             
0.1% IX   -2       +2      -5   -3   -12   -9                             
0.1% X    -3       +1      -7   -5   -12   -9                             
Without   +2       +6       0   +3   -6    -3                             
______________________________________                                    
 
    
     EXAMPLE 12 
     294 g (3 moles) of maleic anhydride dissolved in 500 g of xylene are introduced into a stirred 3 l reactor, and the temperature is decreased to 30° C. A solution of 797 g (3.1 moles) of 3-(2,4,6-trimethyldecyloxy)propylamine in 324 g of xylene is added, while maintaining the temperature below 40° C. The addition lasts one hour, and heating is then performed for 3 hours at xylene reflux. The inner temperature is 144° C. 67 g of water are removed by distillation, corresponding to 54 g of reaction water and 13 g of water contained in the amine; after completion of the reaction, 200 g of dilution xylene are added to obtain a 50% b.w. solution of additive XI in xylene. 
     Additive XI has been analyzed after evaporation of the solvent. Its molecular weight by number, determined by tonometry, is 500. The thin layer infra-red spectrum shows imide bands at 1700 and 1780 cm -1 , secondary amide bands at 1635 and 1560 cm -1  and an ether band at 1100 cm -1 . 
     The additives XII to XVI, whose manufacture is described in the following examples, show the same I.R. absorption bands as those of additive XI; their molecular weights are between 600 and 3000. 
     EXAMPLES 13 AND 14 
     The method of manufacture is the same as in example 12, with similar molar ratios, but the amine compounds differ. 
     EXAMPLE 13 
     Additive XII is obtained by condensing maleic anhydride with N-[3-(2,4,6-trimethyldecyloxy)propyl]-1,3-diaminopropane. 
     EXAMPLE 14 
     Additive XIII is obtained from the condensation product of maleic anhydride on a mixture comprising, by mole, 55% of ethanolamine and 45% of a N-alkyl propylenediamine cut of the trade, whose alkyl chains consist of about 27% of C 16  chain and 72% of C 18  chain (equivalent molecular weight: 370 per primary amine function). 
     EXAMPLES 15 TO 17 
     These examples are conducted according to the operating mode of example 12, the molar ratios of the reactants being the same as in example 12. 
     EXAMPLE 15 
     3-(2,4,6-trimethyldecyloxy)propylamine is condensed with a polyisobutenyl succinic anhydride whose weight is about 1000 and which has 0.675 anhydride function per 1000 g, thus producing additive XIV. 
     EXAMPLE 16 
     3-(2,4,6-trimethyldecyloxy)propylamine is condensed with an alkenyl succinic anhydride obtained by reacting equimolecular proportions of maleic anhydride and of a cut of linear α-olefins containing approximately 49% of C 20  olefin, 42% of C 22  olefin and 9% of C 24  olefin. 
     The result of this condensation is additive XV. 
     EXAMPLE 17 
     Ethanolamine is condensed with the alkenylsuccinic anhydride of example 16, the molar ratio of the ethanolamine to the anhydride content of the alkenylsuccinic anhydride being 1/1. Additive XVI is obtained. 
     In the above examples, the additives are obtained as a solution in xylene whose concentration is adjusted, so as to obtain 50% b.w. solutions of additive in xylene. 
     The activity of these additive compositions is tested by incorporating them, in a proportion of 0.1% b.w. of additive with respect to the gas oil, into the two gas oils cuts of ARAMCO origin, designated as G 1  and G 2 , whose properties have been given above. 
     Three determinations have been performed on each of the so-formed compositions: 
     cloud point according to standard NF T 60-105 
     limit filterability temperature (LFT) according to standard NF M 07-042 
     pour point according to method NF T 60-105. 
     The results of these determinations are given in Table X below: 
     
                       TABLE X                                                     
______________________________________                                    
        CLOUD POINT                                                       
                   TLF       POUR POINT                                   
        (°C.)                                                      
                   (°C.)                                           
                             (°C.)                                 
ADDITIVES G.sub.1  G.sub.2 G.sub.1                                        
                                G.sub.2                                   
                                     G.sub.1                              
                                           G.sub.2                        
______________________________________                                    
Without   +2       +6       0   +3    -6   -3                             
0.1% XI   -1       +3      -6   -2    -9   -6                             
0.1% XII  -1       +3      -3    0   -12   -9                             
0.1% XIII -2       +3      -7   -5   -12   -9                             
0.1% XIV  -1       +3      -3    0    -9   -9                             
0.1% XV   -3       +2      -8   -4   -24   -21                            
0.1% XVI  -2       +2      -8   -5   -21   -18                            
______________________________________                                    
 
    
     EXAMPLE 18 
     The inhibiting effect of an additive according to the invention on the settling of n-paraffins crystallizing in a gas oil cut maintained at rest at low temperature is tested in this example. 
     Two 100 cc test tubes are filled with the previously used gas oil No. 2 (distillation range IP=186° C., FP=385° C.). 
     No additive is introduced into the first test tube. 
     0.1% b.w. of additive XI is introduced into the second test tube. The two test tubes are hermetically closed and left at rest in a cold room at -10° C. for one week. 
     After one week, the settling rate of the settled paraffins, expressed as the volume of the limpid upper phase, is noted in the following Table: 
     
                       TABLE XI                                                    
______________________________________                                    
TEST TUBE No. 1   TEST TUBE No. 2                                         
ADDITIVE-FREE GAS OIL                                                     
                  GAS OIL + ADDITIVE XI                                   
______________________________________                                    
50% vol.          15% vol.                                                
______________________________________                                    
 
    
     All the precipitated paraffins are present in 50% of the volume of the additive-free gas oil, which makes the lower portion thereof more difficult to use, as a result of the pumps, filters and pipes plugging. 
     There is only 15% of limpid upper phase in the additive-containing gas oil. The paraffins are contained in 85% of the total volume. They are better dispersed and can be transported more easily. 
     EXAMPLE 19 
     The anti-corrosion effect of additive XI of example 12 is tested in this example. 
     Product XI has been used in the two already described gas oils G 1  and G 2  at a concentration of 0.01% b.w. 
     The corrosion test consists of examining the corrosion rate of cylindrical polished steel or iron test pieces, caused by synthetic sea water, according to standard ASTM D 665 modified as follows: the temperature is 32.2° C. and the test time is 20 hours. 
     The two additive-free gas oils G 1  and G 2  give test pieces rusted on 100% of their surface, and the two gas oils containing 0.01% b.w. of additive give test pieces totally free of rust.