Thermal cell non-deflagration design
BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     This invention relates to electrochemical cells. More particularly, this invention relates to electrochemical cells for use in thermal batteries. In particular, this invention relates to thermal battery cells employing calcium anodes and oxidizing molten nitrate and perchlorate salts. 
     2. Description of the Prior Art 
     Calcium anodes have been used with molten nitrate electrolytes in thermal battery cells to obtain high voltage outputs. A problem with this combination has been flashing. Flashing refers to the rapid, self-sustaining reaction of depassivated calcium with nitrate, yielding a flash of light. This problem was avoided in U.S. Pat. No. 4,184,018 by the use of a non-flashing electrolyte containing potassium, nitrate and chloride ions. When thermal battery cells containing lithium perchlorate and lithium nitrate were scaled up in size, the problem of the calcium anode flashing or deflagrating returned. 
     Previous thermal battery systems have utilized homogeneous mixtures as the electrolyte. The use of additives to the electrolyte has been found to improve performance of the cathode and the anode. U.S. Pat. No. 4,190,704 describes the use of chloride ion to improve the calcium anode performance. AgNO 3  has been used as an additive to improve cathode performance and allow a higher current density. The use of homogeneous mixtures has not effectively utilized the additives in increasing power density. 
     OBJECTS OF THE INVENTION 
     One object of the present invention is to eliminate the flashing problem of the scaled up thermal battery cells. 
     Another object of the invention is to more efficiently utilize the electrolyte additives used to increase power density. 
     These and other objects, advantages and novel features of the present invention will become apparent from the following detailed description of the invention. 
     SUMMARY OF THE INVENTION 
     The present invention achieves the above objects by providing an electrochemical cell having a calcium anode, a cathode, electrolyte disposed between the cathode and the anode, and means for wetting the edges of the anode with the electrolyte. Further, the present invention can include a separator between the cathode and the anode to separate the additives to different portions of the cell. 
    
    
     BRIEF DESCRIPTION OF THE DRAWING 
     The FIGURE shows the components of the thermal battery cell. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     Referring to the FIGURE, the optional cell configuration of a thermal battery cell 10 includes a stack of elements surrounded by a sleeve 12 and pressed together by spring washers 14. Sleeve 12 can be glass or fiberglass. The enclosed stack of elements includes a current collector 16, an anode 18, an electrolyte layer 20, a separator 22, an electrolyte layer 24, and a cathode 26. Current collector 16 adjacent to anode 18 is connected to the negative lead and cathode 26 is connected to the positive lead. 
     Anode 18 is made of calcium. Either nickel or iron is suitable for current collector 16. In one particular embodiment, electrolyte layer 20 comprises a mixture of LiNO 3  and LiCl and electrolyte layer 24 comprises a mixture of LiNO 3  and AgNO 3 . These two layers of electrolyte are divided by separator 22, which can be a fiberglass binder containing LiNO 3 . This design results in a non-homogeneous electrolyte mixture throughout the cell. 
     Lithium nitrate (LiNO 3 ) is a strong oxidizing agent (m.p. 261° C.). The calcium anode in contact with molten LiNO 3  during cell operation rapidly forms a non-stoichiometric calcium oxide film and can limit the passage of large current densities. The chloride ion attacks the film allowing for high rate discharge at useful potentials. The present design concentrates the chloride ion in the vicinity of the anode by use of separator 22. 
     On the cathode side of separator 22, the electrolyte layer includes LiNO 3  and AgNO 3 . Although nitrate species are reducible, the electrode product of insoluble Li 2  O precipitates on cathode 26 and can prevent high rate discharge due to film resistivity. The inclusion of the silver nitrate (AgNO 3 ) additive in the LiNO 3  electrolyte allows for the reduction of silver ions to be utilized as the cathodic reaction as well as the reduction of nitrate ions. The silver ion reduction in molten LiNO 3  has been shown to sustain current densities of 100 mA/cm 2  without severe polarization. The fiberglass with LiNO 3  separator 22 effectively prevents the formation of a dense insoluble resistive AgCl layer. 
     In another embodiment, electrolyte layer 20 and electrolyte layer 24 include a mixture of LiClO 4  and AgNO 3 . In contrast to LiNO 3 , no added LiCl is required since the LiClO 4  will react with calcium at temperatures above 250° C. to produce LiCl to depassivate the film upon anode 18. 
     A problem with the cells utilizing LiClO 4  was a tendency for thermal runaway followed by anode deflagration or flashing at temperatures above 350° C. The autocatalytic decomposition of LiClO 4  can produce LiCl and hot O 2  gas at the temperatures above 350° C. The hot gases react with calcium anode 18 and will flash or deflagrate. In the LiNO 3  electrolyte cells, deflagrations were attributed to reaction with O 2  generation from the thermal decomposition of LiNO 3  to give off oxygen at high temperatures. 
     The design of the present invention includes a means for wetting the edges of the anode with the electrolyte of the cell. A glass or fiberglass sleeve 12 can serve as a means for wetting the anode edges. The molten electrolyte will be contained by sleeve 12 and coat or wet the anode edges preventing contact between anode 18 and any hot oxygen gas. The means for wetting additionally can include the application of moderate facial pressure which can be supplied by spring washers 14. This further prevents the calcium metal from reacting with any hot oxygen gas. The use of the above means of wetting the edges of the anode has effectively eliminated deflagration problems in cells with calcium anodes and LiNO 3  or LiClO 4  electrolyte melts. 
     The electrolyte layers of the present invention are constructed as electrolyte wafers. The desired electrolyte is mixed with silica (Cab-O-Sil) as a binder and pressed at high pressures of around 80,000 psi for over ten minutes to obtain the wafer or electrolyte layer. 
     Obviously, many modifications and variations of the present invention are possible in light of the above teachings. It is therefore to be understood that within the scope of the appended claims the invention may be practiced otherwise than as specifically described.