Water treatment polymers and methods of use thereof
This is a continuation of application Ser. No. 864,049 filed on May 16, 1986, now U.S. Pat. No. 4,659,481, which is a divisional of application Ser. No. 545,563 filed Oct. 26, 1983, now abandoned. 
    
    
     FIELD OF THE INVENTION 
     The present invention pertains to a composition and method of utilization of same to inhibit corrosion and control the formation and deposition of scale imparting compounds in water systems such as cooling, boiler and gas scrubbing systems. 
     BACKGROUND OF THE INVENTION 
     The problems of corrosion and scale formation and attendant effects have troubled water systems for years. For instance, scale tends to accumulate on internal walls of various water systems, such as boiler and cooling systems, and thereby materially lessens the operational efficiency of the system. 
     Deposits in lines, heat exchange equipment, etc., may originate from several causes. For example, precipitation of calcium carbonate, calcium sulfate and calcium phosphate in the water system leads to an accumulation of these scale imparting compounds along or around the metal surfaces which contact the flowing water circulating through the system. In this manner, heat transfer functions of the particular system are severely impeded. 
     Corrosion, on the other hand, is a degradative electrochemical reaction of a metal with its environment. Simply stated, it is the reversion of refined metals to their natural state. For example, iron ore is iron oxide. Iron oxide is refined into steel. When the steel corrodes, it forms iron oxide which, if unattended, may result in failure or destruction of the metal, causing the particular water system to shut down until the necessary repairs can be made. 
     Typically, in cooling water systems, the formation of calcium sulfate, calcium phosphate and calcium carbonate, among others, has proven deleterious to the overall efficiency of the cooling water system. Recently, due to the popularity of cooling treatments using high levels of orthophosphate to promote passivation of the metal surfaces in contact with the system water, it has become critically important to control calcium phosphate crystallization so that relatively high levels of orthophosphate may be maintained in the system to achieve the desired passivation without resulting in fouling or impeded heat transfer functions which would normally be caused by calcium phosphate deposition. 
     Although steam generating systems are somewhat different from cooling water systems, they share a common problem in regard to deposit formation. 
     As detailed in the Betz Handbook of Industrial Water Conditioning, 8th Edition, 1980, Betz Laboratories, Inc., Trevose, PA Pages 85-96, the formation of scale and sludge deposits on boiler heating surfaces is a serious problem encountered in steam generation. Although current industrial steam producing systems make use of sophisticated external treatments of the boiler feedwater, e.g., coagulation, filtration, softening of water prior to its feed into the boiler system, these operations are only moderately effective. In all cases, external treatment does not in itself provide adequate treatment since muds, sludge, silts and hardness-imparting ions escape the treatment, and eventually are introduced into the steam generating system. 
     In addition to the problems caused by mud, sludge or silts, the industry has also had to contend with boiler scale. Although external treatment is utilized specifically in an attempt to remove calcium and magnesium from the feedwater, scale formation due to residual hardness, i.e., calcium and magnesium salts, is always experienced. Accordingly, internal treatment, i.e., treatment of the water fed to the system, is necessary to prevent, reduce and/or retard formation of the scale imparting compounds and their resultant deposition. The carbonates of magnesium and calcium are not the only problem compounds as regards scale, but also waters having high contents of phosphate, sulfate and silicate ions either occurring naturally or added for other purposes cause problems since calcium and magnesium, and any iron or copper present, react with each and deposit as boiler scale. As is obvious, the deposition of scale on the structural parts of a steam generating system causes poorer circulation and lower heat transfer capacity, resulting accordingly in an overall loss in efficiency. 
     DETAILED DESCRIPTION OF THE INVENTION 
     In accordance with the invention, it has been surprisingly discovered that water soluble copolymers, as shown in Formula I hereinafter, are effective in controlling the formation of mineral deposits and in inhibiting corrosion in various water systems. 
     The water soluble copolymers of the invention have the structure: ##STR2## wherein R 1  is H or lower alkyl (C 1  -C 3 ); R 2  is OH or OM, or NH 2  ; M is a water soluble cation; R 3  is a hydroxy substituted alkyl or alkylene radical having from 1 to 6 carbon atoms or a non-substituted alkyl or alkylene radical having from 1 to about 6 carbon atoms; X, when present, is an anionic radical selected from the group consisting of SO 3 , PO 3 , PO 4 , and COO; Z, when present, is H or hydrogens or any water soluble cation or cations which together counterbalance the valence of the anionic radical; P is 0 or 1. 
     The number average molecular weight of the water soluble copolymers of FORMULA I may fall within the range of 1,000 to 1,000,000. Preferably the number average molecular weight will be within the range of from about 1,500 to 500,000, with the range of about 1,500 to about 10,000 being even more highly desirable. The key criterion is that the polymer be water soluble. 
     The molar ratio A:b of the monomers of FORMULA I may fall within the range of between about 30:1 to 1:20, with the A:b molar ratio range of from about 10:1 to 1:5 being preferred. 
     At present, the water soluble polymer preferred for use in cooling water systems is: ##STR3## wherein M is the same as given in FORMULA I. This polymer (FORMULA II) is referred to as acrylic acid/allyl hydroxy propyl sulfonate ether (AA/AHPSE). The IUPAC nomenclature for AHPSE is 1-propane sulfonic acid, 2-hydroxy-3-(2-propenyl oxy)-mono sodium salt. Heretofore, the AHPSE monomer has been used in the emulsion polymerization of acrylate esters, vinyl acetate and styrene for the manufacture of latex paints. However, to my knowledge, my invention involves the first time this monomer has been polymerized into a water soluble polymer under aqueous solution polymerization techniques. 
     With respect to both repeat units of the polymers of the present invention, they may exist is acid or water soluble salt form when used in the desired water system. 
     As to preparation of the monomer designated as a above, in FORMULA I, acrylic acid is well known. It may be produced by hydrolysis of acrylonitrile or via oxidation of acrolein. Other well known vinyl containing monomers such as methacrylic acid and acrylamide may also be utilized as monomer a of FORMULA I in accordance with the invention. 
     Turning to the allyl containing monomer, monomer b, in the FORMULA I above, these may be produced by reacting allyl alcohol with a non-tertiary alcohol in the temperature range of about 25°-150° C. as is detailed in U.S. Pat. No. 2,847,477 (the entire disclosure of which is hereby incorporated by reference) followed by, if desired, sulfonation, phosphorylation, phosphonation or carboxylation of the monomer via well-known techniques. 
     The preferred allyl hydroxyl propyl sulfonate ether monomers (monomer b FORMULA II) may conveniently be prepared via a ring opening reaction of the epoxy group of an allyl glycidyl ether precursor. Sulfonation of the epoxy group with sodium sulfite in the presence of a phase transfer catalyst such as tetra-n-butylammonium bisulfite or with fuming sulfuric acid containing sulfur trioxide will produce the sulfonic acid group and hydroxy group of the AHPSE. The resulting monomer can be further neutralized with caustic or other basic material. The reaction is illustrated by the following mechanism: ##STR4## 
     Similar ring opening reactions can be carried out by using phosphorus acid and its derivatives including phosphorous trichloride to obtain the phosphonic acid substituents. 
     If orthophosphoric acid (H 3  PO 4 ) and its derivatives are used in the ring opening reaction, phosphoric acid ester substituents may be formed in accordance with the mechanism: ##STR5## 
     Such reaction is described in U.S. Pat. No. 2,723,971. 
     Carboxylate functions can be provided on the allyl hydroxy propyl ether monomer via the reaction of allyl alcohol and chloro-β hydroxy butanoic acid according to the mechanism: ##STR6## 
     It should be noted that the monomer b (FORMULA I) may itself be allyl glycidyl ether which is commercially available from several sources. 
     Z in the allyl monomer, (monomer b of FORMULA I) if present, may be hydrogen, hydrogens or any soluble cation or cations which together counterbalance the valence of the anionic moiety X. Suitable cations include Na, NH 4   + , Ca, and K. X, when present, may be chosen from the group consisting of SO 3 , PO 3 , PO 4 , and COO. 
     After the desired monomers have been obtained, free radical chain addition polymerization may proceed in accordance with conventional solution polymerization techniques. Polymerization initiators such as persulfate initiators, peroxide initiators, etc. may be used. Preferably the requisite monomers are mixed with water and alcohol (preferably isopropanol). The resulting polymer may be isolated by well-known methods such as distillation, etc. or the polymer may simply by used in its aqueous solution. 
     It should be mentioned that water soluble terpolymers comprising monomers a and b of FORMULAE I or II may also be prepared for use as deposit control agents and/or corrosion control agents. For instance, AHPSE monomers may be incorporated into a water soluble terpolymer backbone having other repeat units including acrylic acid monomers, alkyl acrylate monomers, methacrylic acid monomers, acrylamide monomers, etc. 
     The polymers should be added to the aqueous system, for which corrosion inhibiting, and/or deposit control activity is desired, in an amount effective for the purpose. This amount will vary depending upon the particular system for which treatment is desired and will be influenced by factors such as, the area subject to corrosion, pH, temperature, water quantity and the respective concentrations in the water of the potential scale and deposit forming species. For the most part, the polymers will be effective when used at levels of about 0.1-500 parts per million parts of water, and preferably from about 1.0 to 100 parts per million of water contained in the aqueous system to be treated. The polymers may be added directly into the desired water system in a fixed quantity and in the state of an aqueous solution, continuously or intermittently. 
     The polymers of the present invention are not limited to use in any specific category of water system. For instance, in addition to boiler and cooling water systems, the polymers may also be effectively utilized in scrubber systems and the like wherein corrosion and/or the formation and deposition of scale forming salts is a problem. Other possible environments in which the inventive polymers may be used include heat distribution type sea water desalting apparatus and dust collection systems in iron and steel manufacturing industries and as a dispersant in the pulp and paper processing industries. Also the polymers could be used as mineral beneficiation aids such as in iron ore, phosphate, and potash recovery. 
     The water soluble polymers of the present invention can also be used with topping agent components in order to enhance the corrosion inhibition and scale controlling properties thereof. For instance the polymers may be used in combination with one or more kinds of compounds selected from the group consisting of inorganic phosphoric acids, phosphonic acid salts, organic phosphoric acid esters, and polyvalent metal salts. Such topping agents may be added to the system in an amount of from about 1 to 500 ppm. 
     Examples of such inorganic phosphoric acids include condensed phosphoric acids and water soluble salts thereof. The phosphoric acids include an orthophosphoric acid, a primary phosphoric acid and a secondary phosphoric acid. Inorganic condensed phosphoric acids include polyphosphoric acids such as pyrophosphoric acid, tripolyphosphoric acid and the like, metaphosphoric acids such as trimetaphosphoric acid, and tetrametaphosphoric acid. 
     As to the other phosphonic acid derivatives which are to be added in addition to the polymers of the present invention, there may be mentioned aminopolyphosphonic acids such as aminotrimethylene phosphonic acid, ethylene diaminetetramethylene phosphonic acid and the like, methylene diphosphonic acid, hydroxyethylidene diphosphonic acid, 2-phosphonobutane 1,2,4, tricarboxylic acid, etc. 
     Exemplary organic phosphoric acid esters which may be combined with the polymers of the present invention include phosphoric acid esters of alkyl alcohols such as methyl phosphoric acid ester, ethyl phosphoric acid ester, etc., phosphoric acid esters of methyl cellosolve and ethyl cellosolve, and phosphoric acid esters of polyoxyalkylated polyhydroxy compounds obtained by adding ethylene oxide to polyhydroxy compounds such as glycerol, mannitol, sorbitol, etc. Other suitable organic phosphoric esters are the phosphoric acid esters of amino alcohols such as mono, di, and tri-ethanol amines. 
     Inorganic phosphoric acid, phosphonic acid, and organic phosphoric acid esters may be salts, preferably salts of alkali metal, ammonia, amine and so forth. 
     Exemplary polyvalent metal salts which may be combined with the water soluble polymers of the invention include those capable of dissociating polyvalent metal cations in water such as Zn ++ , Ni ++ , etc., which include zinc chloride, zinc sulfate, nickel sulfate, nickel chloride and so forth. 
     The water soluble polymers of the present invention may also be used in conjunction with water soluble chromate compounds that are adapted to provide chromate radicals in water solutions. Illustrative water soluble chromate compounds include sodium chromate dihydrate, sodium chromate anhydrous, sodium chromate tetrahydrate, sodium chromate hexahydrate, sodium chromate decahydrate, potassium dichromate, potassium chromate, ammonium dichromate and chromic acid. 
     In addition, water soluble azole compounds can be used in combination with the water soluble polymers herein disclosed. Such azoles have the formula ##STR7## Included within the scope of the invention are N-alkyl substituted 1,2,3-triazole, or a substituted water soluble 1,2,3-triazole where substitution occurs at the 4 and/or 5 position of the ring. The preferred 1,2,3-triazole is 1,2,3-tolyltriazole of the formula ##STR8## Other exemplary 1,2,3-triazoles include benzotriazole, 4-phenol-1,2,3-triazole, 4-methyl-1,2,3-triazole, 4-ethyl-1,2,3-triazole, 5 methyl-1,2,3-triazole, 5-ethyl-1,2,3-triazole, 5-propyl-1,2,3-triazole, and 5-butyl-1,2,3-triazole. Alkali metal or ammonium salts of these compounds may be used. 
     Other azole compounds include thiazole compounds of the formula: ##STR9## Suitable thiazoles include thiazole, 2-mercaptothiazole, 2-mercaptobenzothiazole, benzothiazole and the like. 
     The water soluble polymers may also be used in conjunction with molybdates such as, inter alia, sodium molybdate, potassium molybdate, lithium molybdate, ammonium molybdate, etc. 
     When the water soluble polymer of the invention (FORMULA I) is added to the aqueous system in combination with a topping agent component selected from the group consisting of inorganic phosphoric acids, phosphonic acids, organic phosphoric acids esters, their water-soluble salts (all being referred to hereinafter as phosphoric compounds), polyvalent metal salts, chromates, molybdates, and azoles, a fixed quantity of said polymer may be added separately and in the state of aqueous solution into the system. The water soluble polymers may be added either continuously or intermittently. Alternatively, the polymer may be blended with the above noted topping agent compounds and then added in the state of aqueous solution into the water system either continuously or intermittently. The topping agents are utilized in the usual manner for corrosion and scale preventing purposes. For instance, the phosphoric compounds or polyvalent metal salts may be added to a water system continuously or intermittently to maintain their necessary concentrations. 
     Generally, the phosphoric compounds should be present in the aqueous system in an amount of about 1-100 ppm (as PO 4 ) or the polyvalent metal salts should be present in an amount of about 1 to 50 ppm (as metal cation). 
     As is conventional in the art, the phosphoric compounds or polyvalent metal salts may be added, as pretreatment dosages, to the water system in an amount of about 20 to about 500 ppm, and thereafter a small quantity of chemicals may be added, as maintenance dosages. 
     The polymers may be used in combination with yet other topping agents including corrosion inhibitors for iron, steel, copper, copper alloys or other metals, conventional scale and contamination inhibitors, metal ion sequestering agents, and other conventional water treating agents. Other corrosion inhibitors comprise tungstate, nitrites, borates, silicates, oxycarboxylic acids, amino acids, catechols, aliphatic amino surface active agents, benzotriazole, and mercaptobenzothiazole. Other scale and contamination inhibitors include lignin derivatives, tannic acids, starch, polyacrylic soda, polyacrylic amide, etc. Metal ion sequestering agents include polyamines, such as ethylene diamine, diethylene triamine and the like and polyamino carboxylic acids, such as nitrilo triacetic acid, ethylene diamine tetraacetic acid, and diethylene triamine pentaacetic acid. 
    
    
     EXAMPLES 
     The invention will now be further described with reference to a number of specific examples which are to be regarded solely as illustrative, and not as restricting the scope of the invention. 
     EXAMPLE 1 
     Preparation of Acrylic Acid/Allyl Hydroxylpropyl Sulfonate Ether Copolymer 
     A suitable reaction flask was equipped with a mechanical agitator, a thermometer, a reflux condenser, a nitrogen inlet and two addition inlets for the initiator and monomer solutions. The flask was charged with 200 g of deionized water and 26 g of isopropanol. The resulting solution was then heated to reflux under a nitrogen blanket. 72 g of acrylic acid (1 mole) and 136 g of 1-propane sulfonic acid, 2-hydroxy-3-(2-propenyl oxy) mono sodium salt [AHPSE] (40%, 0.25 mole) were mixed in a separate flask so as to provide a mixed monomer solution. The mixed monomer solution was then transferred to an addition funnel. An initiator solution containing 27.3% of sodium persulfate in deionized water was prepared separately and sparged with nitrogen. The initiator solution (20 ml) was then added to the reaction flask along with the mixed monomer solution over a period of 2 hours. After this addition, the resulting mixture was heated for 2 more hours at 85 C. and subsequently, 66.5  g of the isopropanol/water solution was stripped off. The reaction mixture was then cooled to less than 40 C. and 60 g of 50% caustic solution was then added. 
     The structure of the resulting copolymer was verified by Carbon 13 NMR. The polymer solution, after being diluted to 25% solids with water, had a Brookfield viscosity of 14.5 cps at 25 C. It was a stable solution with a slightly yellow color. 
     EXAMPLE 2 
     Utilizing both apparatus and procedure similar to that described in Example 1, 200 g of deionized water and 13 g of isopropanol were charged to a reaction flask. The solution was then heated to reflux temperature under a nitrogen blanket. 72 g of acrylic acid and 136 g of AHPSE (40%) were added to a separate flask so as to provide a mixed monomer solution. The mixed monomer solution was then added to the reaction flask along with an initiator solution comprising sodium persulfate over a 2 hour period. The reaction mixture was heated for 2 more hours and subsequently, 36.4 g of isopropanol/water solution was stripped off. The mixture was cooled to lower than 40 C. and 60 g of 50% caustic solution was added. 
     The resulting polymer solution, after being diluted to 25% with water, had a Brookfield viscosity of 19.8 cps (at 25° C.). 
     EXAMPLE 3 
     Utilizing both apparatus and procedure similar to that described in Example 1, 15 g of isopropanol and 228 g of water were added to a reaction flask. 72 g of acrylic acid (1 mole) and 180 g of AHPSE (40% solution, 0.33 mole) were added to an addition funnel so as to provide a mixed monomer solution. The mixed monomer solution was then added to the reaction flask along with a sodium persulfate containing initiator solution over a 2 hour period. One hour after this addition, a solution of t-butyl hydroperoxide (0.2 g in 10 ml of water) was added to the reaction mixture. The mixture was heated for 1 more hour and subsequently, 39.4 g of isopropanol/water solution was stripped off. The mixture was cooled to lower than 40 C. and 60 g of 50% caustic was added. 
     The resulting copolymer solution, after being diluted to 25% solids, had a Brookfield viscosity of 15.9 cps at 25 C. 
     EXAMPLE 4 
     Utilizing the apparatus and procedure described in Example 1, 72 g of acrylic acid (1 mole) and 90.8 g of AHPSE (40%, 0.167 mole) were used for copolymerization. The resulting polymer solution, after being diluted to 25%, had a Brookfield viscosity of 14.5 cps (at 25° C.). The structure of the copolymer was verified by Carbon 13 NMR. 
     EXAMPLE 5 
     Utilizing the apparatus and procedure as described in Example 1, 72 g of acrylic acid (1 mole) and 68.1 g of AHPSE (40%, 0.125 mole) were used for copolymerization. The resulting polymer solution, after being diluted to 25% had a Brookfield viscosity of 15.1 cps (at 25° C.). 
     EXAMPLE 6 
     Apparatus, procedure and reagent charge similar to that described in Example 3 were used, except that this time, AHPSE (180 g, 40% solution) was initially charged into a reaction flask along with isopropanol and water. Acrylic acid (72 g) and sodium persulfate solution were then added to the reaction flask over a 2 hour period. The resulting copolymer solution, after isopropanol distillation, caustic addition and water dilution (to 25% solids) had a Brookfield viscosity of 22.5 cps at 25 C. 
     EXAMPLE 7 
     Apparatus, procedure and reagent charge similar to that described in Example 4 were used except that this time AHPSE (90.8 g, 40% solution) was charged initially into the reaction flask along with isopropanol and water. Acrylic acid (72 g) and sodium persulfate solution were then added to the reaction mixture over a 2 hour period. The resulting copolymer solution, after isopropanol distillation, caustic addition, and water dilution, (to 25% solids) had a Brookfield viscosity of 15.4 cps (at 25 C.). 
     Table I hereinbelow presents a summary of the physical properties of the copolymers produced in accordance with Examples 1 through 6. 
     
                       TABLE I                                                     
______________________________________                                    
                     Viscosity                                            
                     (Brookfield                                          
Example   AA/AHPSE   25% Soln.                                            
Number    Molar Ratio                                                     
                     25° C.)                                       
                                 --Mn pH                                  
______________________________________                                    
1         4:1        14.5        2,550                                    
                                      5.9                                 
2         4:1        19.8        3,600                                    
                                      5.5                                 
3         3:1        15.9        2,900                                    
                                      5.7                                 
4         6:1        14.5        2,080                                    
                                      6.1                                 
5         8:1        15.1        2,260                                    
                                      6.7                                 
6         3:1        22.5        3,760                                    
                                      6.1                                 
7         6:1        15.4        2,217                                    
                                      6.2                                 
______________________________________                                    
 AA = acrylic acid                                                        
 AHPSE = allyl hydroxypropyl sulfonate ether; IUPAC 1propane sulfonic acid
 2hydroxy-3-(2-propenyloxy)-mono sodium salt.                             
 
    
     DEPOSIT CONTROL ACTIVITY 
     One method of evaluating deposit control activity of a material consists of measuring its ability to prevent bulk phase precipitation of a salt at conditions for which the salt would normally precipitate. It is additionally important to recognize that the material being evaluated is tested at &#34;substoichiometric&#34; concentrations. That is, typical molar ratios of precipitating cation to the material being evaluated are on the order of 20:1 and much greater. Consequently, stoichiometric sequestration is not the route through which bulk phase precipitation is prevented. This well known phenomenon is also called &#34;threshold&#34; treatment and is widely practiced in water treatment technology for the prevention of scale (salt) deposits from forming on various surfaces. In the results that follow calcium phosphate, calcium carbonate, and calcium sulfate salts commonly found in industrial water systems under various conditions have been selected as precipitants. The polymers of the present invention has been evaluated for their ability to prevent precipitation (i.e., inhibit crystallization) of these salts. Zinc hydroxide and calcium phosphonate precipitation studies were also undertaken as these particular deposit forming species are also commonly encountered as a result of the use of zinc based corrosion prevention treatments and phosphonate containing deposit control treatments. The results are expressed as &#34;percent inhibition&#34;, positive values indicate that the stated percentage of precipitate was prevented from being formed. Except as where noted to the contrary, the following conditions, solutions, and testing procedure were utilized to perform the inhibition tests, the results of which are reported herein in Tables II to VIII. 
     
         ______________________________________                                    
CALCIUM CARBONATE INHIBITION                                              
Conditions      Solutions                                                 
______________________________________                                    
pH = 9.0, 8.5   3.25 g CaCl.sub.2.2H.sub.2 O/liter DI H.sub.2 O           
T = 70° C.                                                         
                2.48 g Na.sub.2 CO.sub.3 /liter DI H.sub.2 O2O            
5 hour equilibrium                                                        
105 ppm Ca.sup.+2 as CaCO.sub.3                                           
702 ppm CO.sub.3.sup.-2                                                   
______________________________________                                    
 
    
     Procedure 
     (1) Add 50 ml CaCl 2 .2H 2  O pre-adjusted to pH 9.0. 
     (2) Add 40 ml of Na 2  HPO 4  solution. 
     (3) Add 50 ml Na 2  CO 3  pre-adjusted to pH 9.0. 
     (4) Heat 5 hours at 70° C. water bath. Remove and cool to room temperature. 
     (5) Filter 5 mls through 0.2u filters. 
     (6) Adjust samples to pH 1.0 with conc. HCl (≈1 g Conc. HCl). 
     (7) Allow to stand at least 15 minutes. 
     (8) Dilute to 50 mls with DI H 2  O. 
     (9) Bring pH to 12.0 with NaOH. 
     (10) Add Ca +2  indicator (1 level). 
     (11) Titrate with EDTA to purple-violet endpoint. 
     Calculation ##EQU1## 
     
         ______________________________________                                    
CALCIUM PHOSPHATE INHIBITION PROCEDURE                                    
Conditions       Solutions                                                
______________________________________                                    
T = 70° C.                                                         
                 36.76 CaCl.sub.2.2H.sub.2 O/liter DIH.sub.2 O            
pH = 8.5         0.4482 g Na.sub.2 HPO.sub.4 /liter DIH.sub.2 O           
17 hour equilibration                                                     
Ca.sup.+2 = 250 ppm as CaCO.sub.3                                         
PO.sub.4.sup.-3 = 6 ppm                                                   
______________________________________                                    
 
    
     Procedure 
     (1) To about 1800 ml DIH 2  O in a 2 liter volumetric flask, add 20 ml of CaCl 2 .2H 2  O solution followed by 2 drops of conc. HCl. 
     (2) Add 40 ml of Na 2  HPO 4  solution. 
     (3) Bring volume to 2 liters with DI water. 
     (4) Place 100 ml aliquots of solution in 4 oz glass bottles. 
     (5) Add treatment. 
     (6) Adjust pH as desired. 
     (7) Place in 70° C. water bath and equilibrate for 17 hours. 
     (8) Remove samples and filter while hot through 0.2u filters. 
     (9) Cool to room temperature and take Absorbance measurements using Leitz photometer (640 nm). 
     Preparation for Leitz 
     a. 5 mls filtrate 
     b. 10 mls Molybdate Reagent 
     c. 1 dipper Stannous Reagent 
     d. Swirl 1 minute, pour into Leitz cuvette; wait 1 minute before reading. 
     (10) Using current calibration curve (Absorbance vs ppm PO 4   -3 ) find ppm PO 4   -3  of each sample. 
     Calculation ##EQU2## 
     
         ______________________________________                                    
CALCIUM SULFATE INHIBITION PROCEDURE                                      
Conditions        Chemicals                                               
______________________________________                                    
pH = 7.0          1 × 10.sup.-1 M CaCl.sub.2.2H.sub.2 O             
T = 50° C. 1 × 10.sup.-1 M Na.sub.2 SO.sub.4                 
24 hour equilibration                                                     
Ca.sup.+2 = 2000 ppm                                                      
SO.sub.4.sup.-2 = 4800 ppm                                                
______________________________________                                    
 
    
     Procedure 
     (1) Add 50 ml of 10 -1  M CaCl 2 .2H 2  O pre-adjusted to pH 7.0 to a 4 oz. bottle. 
     (2) Add treatment. 
     (3) Add 50 ml of 10 -1  M Na 2  SO 4  preadjusted to 7.0. 
     (4) Heat samples for 24 hours in a 50° C. water bath. 
     (5) Cool for 30 minutes, at least. 
     (6) Filter 5 ml through 0.45u filters. 
     (7) Add NaOH to pH 12.0 and dilute to 50 ml with DI H 2  O. 
     (8) Add Ca +2  indicator (1 level). 
     (9) Titrate to purple-violet endpoint with EDTA. 
     Calculation ##EQU3## 
     CALCIUM PHOSPHONATE PRECIPITATION INHIBITION PROCEDURE 
     Conditions 
     Static Beaker Study; 750 ppm Ca +2  as CaCO 3  ; pH=8.7; T=158° F.; 18 hour Equilibration Time; 10 ppm 1-hydroxyethylidene 1,1-diphosphonic acid (HEDP) 
     Experimental 
     Prepare following solutions: 
     Stock Sol&#39;n--2.206 g CaCl 2 .2H 2  O+0.033 g HEDP/2 liters. 
     Treatment--1,000 ppm active solutions 
     Procedure 
     (1) To clean 4 oz bottle add 100 ml of stock solution. 
     (2) Add treatment with stirring. 
     (3) Adjust pH to 8.7 with a dilute NaOH sol&#39;n. 
     (4) Place samples in water bath at T=158° F., for 18 hours, after which time filter aliquot through 0.2u filter paper. 
     (5) Analyze filtrate for organic phosphate (TP). 
     Calculation of % Inhibition ##EQU4## 
     ZINC HYDROXIDE INHIBITION PROCEDURE 
     Conditions 
     T=120° F.; Static Beaker Study; Equilibration Time=18 hours; Ca +2  =170 ppm as CaCO 3  ; Mg +2  =110 ppm as CaCO 3  ; SiO 2  =15 ppm; Zn +2  =5 ppm; treatment level=5 ppm active. 
     Solutions 
     1000 ppm Treatment Solution 
     Stock Solution 
     Preparation of Stock Solution 
     (1) To approximately 9 liters DI water, add 0.5357 g Na 2  SiO 3 .5H 2  O. 
     (2) Adjust pH 6 with concentrated HCl. 
     (3) Add 2.4996 g CaCl 2 .2H 2  O. 
     (4) Add 2.7114 g MgSO 4 .7H 2  O. 
     (5) Add 0.1374 g ZnSO 4 .H 2  O. 
     (6) Bring volume to 10 liters with DI water. 
     Procedure 
     (1) To 800 ml stock solution, add 4 ml treatment solution. 
     (2) Adjust pH with dilute NaOH. 
     (3) As each desired pH is reached, place 100 ml of solution in clean 4 oz. bottle. 
     (4) Place in water bath at 120° F. and equilibrate for 18 hours. 
     (5) Remove samples and filter through 0.2u filter. 
     (6) Analyze filtrate for soluble zinc. 
     (7) Measure and record pH of cooled unfiltered solution. 
     
                       TABLE II                                                    
______________________________________                                    
CaCO.sub.3 Precipitation Inhibition                                       
              % Inhibition                                                
              Treatment Concentrations                                    
              (ppm active)                                                
Treatment       1      3       5    7.5   10                              
______________________________________                                    
Polyacrylic acid                                                          
                30.0   63.2    73.7 77.9  78.9                            
MW ≈ 5,000                                                        
Acrylic acid/2-hydroxy                                                    
                1.7    45.1    56.6 65.3  42.2                            
propylacrylate copolymer                                                  
--Mn ≈ 2,000                                                      
AA/HPA molar ratio                                                        
3:1                                                                       
Example 1 Copolymer                                                       
                0.0    36.4    45.1 56.6  62.4                            
Example 2 Copolymer                                                       
                1.7    38.2    50.9 53.8  57.8                            
Example 3 Copolymer                                                       
                1.7    30.6    42.2 48.0  45.1                            
Polyacrylic acid                                                          
                12.4   71.4    75.7 84.9  86.5                            
MW ≈ 5,000                                                        
Example 4 Copolymer                                                       
                10.8   56.8    68.6 75.7  75.7                            
Example 5 Copolymer                                                       
                8.1    54.1    67.6 73.0  78.4                            
______________________________________                                    
 
    
     
                       TABLE III                                                   
______________________________________                                    
Ca.sub.3 (PO.sub.4).sub.2 Precipitation Inhibition                        
             % Inhibition                                                 
             Treatment Concentrations                                     
             (ppm active)                                                 
Treatment      5          10      15                                      
______________________________________                                    
Acrylic acid/2-hydroxy                                                    
               59.3       88.9    90.7                                    
propylacrylate copolymer                                                  
--Mn ≈ 2,000; AA/HPA                                              
Molar ratio 3:1                                                           
Sulfonated styrene/                                                       
               50.0       81.5    90.7                                    
maleic anhydride                                                          
copolymer                                                                 
MW ≈ 1,500                                                        
SS/MA molar                                                               
ratio 3:1                                                                 
Example 1 Copolymer                                                       
               42.6       90.7    94.4                                    
Example 2 Copolymer                                                       
               48.1       90.7    100.0                                   
Example 3 Copolymer                                                       
               53.7       92.6    100.0                                   
Acrylic acid/2-hydroxy                                                    
               31.7       87.3    87.3                                    
propylacrylate copolymer                                                  
--Mn ≈ 2,000, AA/HPA                                              
molar ratio 3:1                                                           
Example 4 Copolymer                                                       
               22.2       84.1    93.7                                    
Example 5 Copolymer                                                       
               12.7       84.1    90.5                                    
______________________________________                                    
 
    
     
                       TABLE IV                                                    
______________________________________                                    
Calcium Phosphonate Inhibition                                            
            % Inhibition                                                  
            Treatment Concentration (ppm active)                          
Treatment     5        10      15     20                                  
______________________________________                                    
Sulfonated styrene/                                                       
              2.9      4.4     26.5   72.1                                
maleic anhydride                                                          
copolymer                                                                 
MW ≈ 1,500                                                        
SS/MA molar ratio                                                         
3:1                                                                       
Example 1 Copolymer                                                       
              0.0      0.0     17.6   76.5                                
Example 2 Copolymer                                                       
              0.0      0.0     33.8   69.1                                
Example 3 Copolymer                                                       
              0.0      2.9     51.5   82.4                                
Sulfonated styrene/                                                       
              4.2      5.6     25.4   69.0                                
maleic anhydride                                                          
copolymer                                                                 
MW ≈ 1,500                                                        
SS/MA molar ratio 3:1                                                     
Example 4 Copolymer                                                       
              0.0      0.0     0.0    2.8                                 
Example 5 Copolymer                                                       
              0.0      0.0     0.0    0.0                                 
______________________________________                                    
 
    
     
                       TABLE V                                                     
______________________________________                                    
Zinc Hydroxide Inhibition                                                 
                           ppm Soluble                                    
                           Zinc after 18                                  
Treatment         Final pH Hours                                          
______________________________________                                    
No treatment      7.42     3.3                                            
                  7.60     1.5                                            
                  8.10     0.3                                            
                  8.47     0.1                                            
                  8.79     0.1                                            
                  9.09     0.1                                            
Acrylic acid/2-hydroxy                                                    
                  7.12     4.3                                            
propylacrylate copolymer                                                  
                  7.55     3.8                                            
--Mn ≈ 2,000; AA/HPA                                              
                  7.93     3.7                                            
molar ratio 3:1   8.15     3.8                                            
                  8.64     3.8                                            
                  9.04     3.6                                            
Sulfonated styrene/                                                       
                  7.40     4.0                                            
maleic anhydride  7.68     3.8                                            
copolymer MW ≈ 1,500                                              
                  8.06     3.9                                            
SS/MA molar ratio 8.35     4.2                                            
3:1               8.77     4.0                                            
                  9.08     3.5                                            
Example 1 Copolymer                                                       
                  7.03     4.3                                            
                  7.62     4.6                                            
                  7.96     4.6                                            
                  8.29     4.2                                            
                  8.64     4.2                                            
                  8.96     4.0                                            
Example 2 Copolymer                                                       
                  7.12     4.2                                            
                  7.64     4.6                                            
                  7.90     4.0                                            
                  8.29     4.5                                            
                  8.57     4.0                                            
                  9.10     3.7                                            
Example 3 Copolymer                                                       
                  7.20     4.2                                            
                  7.64     4.6                                            
                  7.94     4.6                                            
                  8.33     4.3                                            
                  8.67     4.4                                            
                  9.06     4.2                                            
No treatment      7.27     3.5                                            
                  7.63     1.6                                            
                  8.03     0.3                                            
                  8.48     0.1                                            
                  8.73     0.1                                            
                  9.05     0.1                                            
Example 4 Copolymer                                                       
                  7.22     3.7                                            
                  7.65     3.8                                            
                  8.02     3.7                                            
                  8.43     3.4                                            
                  8.73     4.1                                            
                  9.05     4.1                                            
Example 5 Copolymer                                                       
                  7.24     3.8                                            
                  7.60     3.3                                            
                  8.01     3.6                                            
                  8.37     3.9                                            
                  8.72     3.5                                            
                  9.03     4.1                                            
______________________________________                                    
 
    
     
                       TABLE VI                                                    
______________________________________                                    
Ca.sub.3 (PO.sub.4).sub.2 Precipitation Inhibition                        
              % Inhibition                                                
              Treatment Concentration (ppm active)                        
Treatment     10 ppm                                                      
______________________________________                                    
Acrylic       70.4                                                        
acid/2-hydroxy                                                            
propylacrylate                                                            
--Mn ≈ 2,000; AA/HPA                                              
molar ratio 3:1                                                           
Example 1 Copolymer                                                       
              90.7                                                        
Example 2 Copolymer                                                       
              94.4                                                        
Example 3 Copolymer                                                       
              94.4                                                        
______________________________________                                    
 
    
     
                       TABLE VIa                                                   
______________________________________                                    
Ca.sub.3 (PO.sub.4).sub.2 Precipitation Inhibition                        
                 Treatment                                                
Treatment        Level (ppm)                                              
                            % Inhibition                                  
______________________________________                                    
Example 1 Copolymer                                                       
                 2.5        25.9                                          
Example 1 Copolymer                                                       
                 5.0        46.3                                          
                 10.0       90.7                                          
                 20.0       100.0                                         
Example 2 Copolymer                                                       
                 2.5        18.5                                          
                 5.0        44.4                                          
                 10.0       94.4                                          
                 20.0       100.0                                         
Example 3 Copolymer                                                       
                 2.5        38.9                                          
                 5.0        42.6                                          
                 10.0       94.4                                          
                 20.0       100.0                                         
Acrylic acid/    2.5        31.5                                          
2-hydroxypropyl  5.0        44.4                                          
acrylate copolymer                                                        
                 10.0       70.4                                          
--Mn ≈ 2,000; AA:HPA                                              
                 20.0       98.1                                          
molar ratio = 3:1                                                         
______________________________________                                    
 
    
     
                       TABLE VII                                                   
______________________________________                                    
Calcium Carbonate Precipitation Inhibition                                
                Treatment                                                 
Treatment       Level (ppm)                                               
                           % Inhibition                                   
______________________________________                                    
Example 1 Copolymer                                                       
                0.5        25.0                                           
                1.0        53.6                                           
                3.0        70.3                                           
                5.0        74.5                                           
Example 2 Copolymer                                                       
                0.5        27.1                                           
                1.0        55.7                                           
                3.0        63.0                                           
                5.0        71.4                                           
Example 3 Copolymer                                                       
                0.5        26.6                                           
                1.0        47.9                                           
                3.0        66.7                                           
                5.0        65.6                                           
Polyacrylic acid                                                          
                1.0        31.0                                           
MW ≈ 5,000                                                        
                3.0        61.0                                           
                5.0        59.7                                           
                10.0       66.7                                           
______________________________________                                    
 
    
     
                       TABLE VIII                                                  
______________________________________                                    
Calcium Sulfate Inhibition                                                
                Treatment                                                 
Treatment       Level (ppm)                                               
                           % Inhibition                                   
______________________________________                                    
Example 1 Copolymer                                                       
                0.5        10.4                                           
                1.0        24.3                                           
                3.0        88.4                                           
                5.0        98.6                                           
Example 2 Copolymer                                                       
                0.5        8.1                                            
                1.0        18.9                                           
                3.0        97.3                                           
                5.0        97.5                                           
Example 3 Copolymer                                                       
                0.5        7.5                                            
                1.0        16.5                                           
                3.0        92.9                                           
                5.0        97.2                                           
Polyacrylic acid                                                          
                1.0        97.0                                           
MW ≈ 5,000                                                        
                3.0        98.0                                           
                5.0        98.0                                           
______________________________________                                    
 
    
     Ferric Oxide Dispersion 
     In order to demonstrate the effectiveness of the polymers of the invention in dispersing suspended particulate matter, the following procedure, using Fe 2  O 3  as suspended solids, was undertaken. Results appear in Table IX. In the results, it is noted that increasing Δ%T values indicate better treatment as more particles remain suspended in the aqueous medium. 
     
         ______________________________________                                    
Fe.sub.2 O.sub.3 Dispersion Procedure                                     
Conditions:    Solutions:                                                 
______________________________________                                    
T = 25° C.                                                         
               0.1% solution Fe.sub.2 O.sub.3 in D.I. H.sub.2 O           
pH = 7.5       3.68 g CaCl.sub.2.2H.sub.2 O/100 ml DI H.sub.2 O           
200 ppm Ca.sup.+2 as CaCO.sub.3                                           
______________________________________                                    
 
    
     Procedure 
     (1) Prepare a suspension of 0.1% Fe 2  O 3  in DI H 2  O. 
     (2) Adjust hardness to 200 ppm Ca +2  as CaCO 3  using CaCl 2 .2H 2  O solution--8 ml/1000 ml of Fe 2  O 3  solution. 
     (3) Using overhead mixer, mix suspension 1/2 hour at 1000 rpms. 
     (4) Remove solution to magnetic stirrer and adjust to pH 7.5 (about 20 minutes to stabilize pH). 
     (5) Return solution to overhead mixer. 
     (6) Take 90 ml aliquots of suspension and place 4 oz. glass bottle. 
     (7) Add treatment and DI water to bring total volume to 100 ml. 
     (8) Cap bottle, invert several times and place on reciprocating shaker at a moderate speed of about 40 spm for 1/2 hour. 
     (9) Place on vibration-proof surface and allow to stand 18 hours. 
     (10) Without disturbing settled phase, pipet the top 40 mls off the sample. Place in a cell and read %T (at 415 nm). 
     Calculation 
     
         Δ%T=%T (control)-%T (treated) 
    
     
                       TABLE IX                                                    
______________________________________                                    
                   Treatment                                              
Treatment          Level (ppm)                                            
                              Δ% T                                  
______________________________________                                    
Example 1 Copolymer                                                       
                   2.5        7.5                                         
                   5.0        20.7                                        
                   10.0       21.2                                        
                   20.0       20.7                                        
Example 2 Copolymer                                                       
                   2.5        12.0                                        
                   5.0        10.0                                        
                   10.0       10.2                                        
                   20.0       10.7                                        
Example 3 Copolymer                                                       
                   2.5        15.1                                        
                   5.0        23.1                                        
                   10.0       25.9                                        
                   20.0       25.4                                        
Acrylic acid/2-hydroxy                                                    
                   2.5        9.3                                         
propyl acrylate --Mn ≈ 2,000                                      
                   5.0        15.4                                        
molar ratio AA:HPA =                                                      
                   10.0       15.1                                        
3:1                20.0       16.4                                        
                   30.0       16.9                                        
______________________________________                                    
 
    
     Recirculator Studies 
     In order to approximate those conditions experienced in a cooling tower, tests were conducted under recirculatory conditions with heat transfer provided. 
     These conditions closely simulate the environment in a field cooling system. In this test system treated water is circulated by a centrifugal pump through a corrosion coupon by-pass into which corrosion coupons are inserted, and past a mild steel (AISI-1010) heat exchanger tube contained in a plexiglass block. The inside of the exchanger tube is filled with silicone oil and heated with an electric heater. The temperature of the silicone oil can be regulated. The water velocity past the corrosion coupons and heat exchanger tube can be controlled anywhere from 0 to 4.5 ft/sec. 
     The pH and temperature of the bulk water are automatically controlled. The treated water is prepared by chemical addition to deionized water. Provisions for continuous make-up and blowdown are made by pumping fresh treated water from supply tanks to the sump, with overflow from the sump serving as blowdown. 
     Corrosion rates are determined by exposing precleaned and weighed metal specimens for a specified period of time, after which they are removed, cleaned and reweighed. Corrosion rates are calculated by dividing the total coupon weight loss by the number of days of exposure. 
     The conditions used were: Heat Flux 8000 BTU/ft 2  /hr; Water Velocity=3 ft/sec; Water Temperature=120° F.; Retention Time=1.3 days; Mild Steel Heat Transfer Surface. 
     Water Chemistry: 600 ppm Ca as CaCO 3  ; 300 ppm Mg +2  as CaCO 3  ; 83 ppm NaHCO 3  ; pH=7.3±0.2. 
     Treatment: 12.5 ppm active polymer; 3.0 ppm tolyltriazole; 10.5 ppm tetrapotassium pyrophosphate; 15.2 ppm monosodium phosphate; HEDP 4.0 ppm. 
     The following results were obtained: 
     
                       TABLE X                                                     
______________________________________                                    
                  Pretreated                                              
        Mild Steel                                                        
                  Mild Steel                                              
                            Admiralty                                     
Treatment                                                                 
        Corrosion Corrosion Corrosion                                     
                                    Remarks                               
______________________________________                                    
Example 4                                                                 
        1.2 mpy   0.1 mpy   0.1 mpy No significant                        
Copolymer                           corrosion or                          
                                    deposition on                         
                                    steel sur-                            
                                    faces.                                
Example 2                                                                 
        1.2 mpy   0.9 mpy   0.5 mpy No significant                        
Copolymer                           corrosion or                          
                                    deposition on                         
                                    mild steel                            
                                    surfaces.                             
Example 5                                                                 
        1.1 mpy   0.8 mpy   0.5 mpy Heat transfer                         
Copolymer                           surface covered                       
                                    with uniform                          
                                    white                                 
                                    deposits.                             
______________________________________                                    
 
    
     EXAMPLE 8 
     Copolymer of Methacrylic Acid and AHPSE 
     Utilizing both apparatus and procedure similar to that described in Example 1, 228 g. of water and 180 g of AHPSE (40% solution, 0.33 mole) were added to a reaction flask, 86 g. of methacrylic acid (1 mole) and sodium persulfate solution were then separately added to the reaction mixture over a two hour period at 85° C. The resulting polymer solution was further neutralized with 70 g of caustic (50%) and diluted to a 25% solids solution. The final solution had a Brookfield viscosity of 28.2 cps at 25° C. The molecular weight Mn of the copolymer was 3,400. 
     Boiler Studies 
     In order to assess the efficacy of the polymers of the present invention in inhibiting scale formation in steam generating systems, research boilers were fitted with two 4,000 watt electrical heater probes, giving 185,000 BTU/ft 2  /hr and about 8 Kg/hr steam. The boiler feedwater contained the contaminants and treatment agents given hereinbelow. The boilers were operated for 44 hours per run at an average of 15 cycles of concentration. At the conclusion of each run, the deposits were cleaned from the probes with an acid solution and the deposit densities were then calculated. 
     Boiler Test Conditions 
     Condition &#34;A&#34;=sodium sulfite oxygen scavenger, 900 psig, contaminants 4/1/1 ppm Ca/Mg/Fe in feedwater, stoichiometric amount of EDTA added--chelant/polymer program. 
     Condition &#34;B&#34;=sodium sulfite oxygen scavenger, 900 psig, contaminants 4/1 ppm Ca/Mg in feedwater, phosphate added to produce 30 ppm PO 4  as Ca--phosphate precipitation/polymer program. 
     Condition &#34;C&#34;=hydrazine oxygen scavenger, 1450 psig, contaminant 5 ppm Fe in feedwater, phosphate added to produce 7 ppm PO 4  as Ca--coordinated phosphate/pH/polymer. 
     The results appear hereinbelow in Table XI. 
     
                       TABLE XI                                                    
______________________________________                                    
                         Treatment                                        
                         Dosage     Average                               
Condi-                   ppm polymer                                      
                                    Deposit                               
tion  Polymer            (actives)  (g/ft.sup.2)                          
______________________________________                                    
A     Polymethacrylic acid                                                
                         5          0.18                                  
      --Mw 12,000 (sodium salt)                                           
A     Example 8          5          0.19                                  
      Copolymer                                                           
B     Sulfonated Polystyrene                                              
                         7.5        0.23                                  
      Maleic Anhydride Copolymer                                          
      MW 3,000-5,000 SSMA (3:1)                                           
B     Example 8          7.5        0.23                                  
      Copolymer                                                           
C     Polymethacrylic acid --Mw                                           
                         5          0.93                                  
      12,000 (Sodium Salt)                                                
C     Example 8          5          2.55                                  
      Copolymer                                                           
______________________________________                                    
 
    
     Discussion 
     The examples demonstrate that the copolymers of the present invention are effective in inhibiting the formation of those deposits normally encountered in industrial water systems such as cooling and boiler systems. Further, the copolymers are effective in dispersing iron oxide which is sometimes encountered as a troublesome fouling species. 
     The demonstrated efficacy of the copolymers in inhibiting calcium phosphate, and calcium phosphonate precipitation is very important. For instance, one successfully established cooling water treatment method provides a passivated oxide film on metal surfaces in contact with the aqueous medium via addition of orthophosphate, organo-phosphonate and an acrylic acid/hydroxylated alkyl acrylate copolymer. Details of such method are disclosed in U.S. Pat. No. 4,303,568 (May et al). The entire content of this patent is hereby incorporated by reference. Based upon the deposit control efficacy shown by the instant copolymers, as well as the minimum corrosion rates displayed herein in the recirculator studies, it is thought that the subject copolymers can be substituted for the polymers disclosed in the aforementioned May et al patent so as to provide the important passivated oxide film on the desired metal surfaces. 
     As is stated in that patent, the passive oxide film is provided on metal surfaces in contact with the aqueous medium without substantial attendant deposition formed thereon. A composition containing polymer and orthophosphate and optionally but preferably a phosphonate, polyphosphate and copper corrosion inhibitors is used in order to achieve such passivation. A typical composition contains on a weight ratio basis of polymer to orthophosphate expressed as PO 4   ---  of about 1:8 to about 4:1 and preferably about 1:6 to 2:1. When a polyphosphate* is included, the weight ratio of orthophosphate to polyphosphate on a PO 4   ---  to PO 4   ---  basis is 15:1 to 1:3, and preferably 2.5:1 to 1:1. Similarly, if the organo-phosphonate is included, the ratio of the orthophosphate to the phosphonate expressed as PO 4   ---  to PO 4   ---  is 1:2 to 13:1, and preferably 2:1 to 8:1. Any copper corrosion inhibitor may be included in the composition (0.01 to 5% by weight) in an amount which will be effective for controlling the copper corrosion in a given system: 0.05 to 10 parts per million and preferably 0.5 to 5 parts per million. Similarly, zinc salts may be included if additional protection is needed. 
    
     In treating the aqueous systems to provide such passivation, the following dosages in parts per million parts of water in said aqueous systems of the respective ingredients are desirable, with the dosages, of course, being based upon the severity of the corrosion problem foreseen or experienced: 
     orthophosphate (expressed as PO 4   --- ): 2 to 50 parts per million parts of water (ppm) and preferably 6 to 30 ppm; 
     polymer: 0.3 to 120 ppm and preferably 3 to 25 ppm per million parts of water; 
     polyphosphate (expressed as PO 4   --- ): 0.1 to 30, and preferably 3 to 10, parts per million parts of water; 
     phosphonate (expressed as PO 4   --- ): 0.04 to 20, and preferably 1 to 6, parts per million parts of water. 
     The preferred rate of application of this treatment to cooling water systems and the ratios of various components depends on the calcium concentration of the cooling water. The treatment is preferably applied in waters having between 15 ppm and 1,000 ppm calcium. Within this range the weight ratio of calcium to orthophosphate is varied from 1:1 to 83.3:1, the weight ratio of polymer to orthophosphate is varied from 1:3 to 1.5:1. 
     The orthophosphate which is critical to the passivation aspect of the present invention is generally obtained by direct addition. However, it is understood that the orthophosphate can also arise due to reversion of either inorganic polyphosphates or the organo-phosphonates, or any other appropriate source or precursor thereof. 
     The above dosages represent the most desirable ranges since most systems will be treatable therewith. Higher dosages are permissible when the situation demands, but of course are most costly. The effectiveness of the inventive treatments are dependent upon the aqueous medium having a pH of 5.5 and above, and preferably 6.5 to 9.5, and containing calcium ion concentrations, preferably about 15 parts per million parts of water. Below this range, it may be necessary for overall effectiveness to add metallic ions such as zinc, nickel, chromium, etc. as described in column 3, lines 4 to 24, of U.S. Pat. No. 3,837,803. 
     As the copolymers are effective in inhibiting calcium phosphate formation, they would also be effective in gas scrubbing systems where scrubbing mediums such as sewage treatment effluents contain high phosphate levels. Such systems would have the prerequisite for the formation and deposition of calcium phosphate which is to be avoided. Additional areas of application such as the phosphate production and processing field, fertilizer field, automotive metallic part pretreatment field, etc. will be apparent to those skilled in the art. 
     The fact that the instant copolymers provide for increased soluble zinc concentrations in solution (Table V) is important in that more zinc is left in the system water so as to provide its well known corrosion protection. Without the use of the copolymers of the present invention, more zinc precipitates in the form of zinc hydroxide, thus leaving less zinc available for its all important anti-corrosion protection. As such, it is postulated that the present copolymers can be successfully employed in zinc-based corrosion protection systems such as those disclosed in U.S. Pat. No. 3,510,436 (Silverstein), the content of which is hereby incorporated by reference. 
     The boiler studies demonstrate that a polymethacrylic acid/AHPSE copolymer in accordance with the invention is comparable to the well-known polymethacrylic acid and polysulfonated styrene/maleic anhydride polymeric treatments in inhibiting deposits in boilers. Accordingly, the polymethacrylic acid/AHPSE copolymer of Example 8 is preferred for use in boiler environments. 
     While this invention has been described with respect to particular embodiments thereof, it is apparent that numerous other forms and modifications of this invention will be obvious to those skilled in the art. The appended claims and this invention generally should be construed to cover all such obvious forms and modifications which are within the true spirit and scope of the present invention.