Novel solid solution, heat-resistant sintered body and method of producing the same
BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     This invention relates to a solid solution of R y  Zr 4  Si x  P 6-x  O 24  system (wherein R is at least one bivalent or trivalent element, x is a numerical value of 0 to 2, and y is a numerical value of 2/3 to 2 satisfying an electrically neutral condition of the chemical formula), a heat-resistant sintered body and a heat-resistant phosphate based compound sintered body each comprising the above solid solution, and a method of producing the same. More particularly, the present invention relates to a solid solution of R y  Zr 4  Si x  P 6-x  O 24  system having excellent heat resistance and high temperature stability, a heat-resistant high strength sintered body comprising the above solid solution and having low expansion and improved high temperature stability, a phosphate based compound sintered body comprising the solid solution and having excellent heat resistance and high temperature stability and low expansion, and a method of producing the same. 
     RELATED ART STATEMENT 
     Recently, it has been strongly demanded to develop materials having excellent heat resistance and low expansion with the advance of industrial technologies. 
     Under such demands, it has been recognized that zirconyl phosphate [(ZrO) 2  P 2  O 7  ] is promising as a material having improved heat resistance and low expansion. 
     Lately, zirconium phosphates of alkali metals such as sodium and the like have been proposed as a material having good heat resistance and a low thermal expansion coefficient [Mat. Res. Bull., Vol. 19, pp. 1451-1456 (1984); Journal of Materials Science, 16, 1633-1642 (1981); and Yogyo Kyokai-shi, 95(5), pp. 531-537 (1987)]. 
     Furthermore, phosphate compounds of alkaline earth metals having a particular composition are proposed to have a low expansion [Mat. Res. Bull, Vol. 20, pp. 99-106 (1985); and J. Am, Ceram. Soc., 70[10] C-232˜C-236 (1987)]. 
     Moreover, U.S. Pat. No. 4,675,302 discloses that ceramic materials having a basic composition of Ca 0 .5 Ti 2  P 3  O 12  are excellent in low expansion. 
     However, although the above phosphate compounds such as zirconyl phosphate and so on have a merit of excellent low expansion, these phosphate compounds have a common problem that they are thermally decomposed at high temperatures above 1,200° C. to evaporate the phosphorus component. For instance, when the heat treatment is carried out at 1,400° C. for 100 hours, zirconyl phosphate reduces the weight of the sintered body by 19%, while sodium zirconium phosphate reduces the weight of the sintered body by 36%. 
     Further, the ceramic material disclosed in U.S. Pat. No. 4,675,302 is mainly used as a substrate for a low expansion optical reflector in a man-made satellite causing no deformation or the like even under a temperature change. As shown in FIG. 2 of this patent, the temperature change is about 500° C. at most, so that there is no care on the stability, heat resistance and the like at an elevated temperature of, for example, not lower than 1,200° C. 
     The phosphate compounds of CaZr 4  P 6  O 24 , SrZr 4  P 6  O 24 , BaZr 4  P 6  O 24  and the like are excellent in high temperature stability as compared with zirconyl phosphate and their weight loss is not more than 10% after the heat treatment at 1,400° C. for 100 hours. However, CaZr 4  P 6  O 24  has a negative thermal expansion coefficient and is low in strength, while SrZr 4  P 6  O 24  has high strength but has a relatively high expansion owing to a thermal expansion coefficient of 25×10 -7  /°C. Therefore, it is desired to develop heat resistant ceramics which have high strength and low expansion. 
     On the other hand, a method using a combination of substances selected from Na 2  CO 3 , ZrO 2 , ZrOCl 2 .8H 2  O, SiO 2 , (NH 4 ) 2  HPO 4 , H 3  PO 4 , Nb 2  O 5 , Y 2  O 3 , SrCO 3 , K 2  CO 3 , CaCO 3   and the like is known as a method for the production of a phosphate compound [T. Oota and I. Yamai, Journal of the American Ceramic Society, 69, 1, (1986)]. 
     In this method, however, the P 2  O 5  component is produced alone during the decomposition of ammonium phosphate or H 3  PO 4  to locally form portions having a high phosphorus concentration, resulting in the formation of a low melting compound during sintering. Consequently, large pores (spaces) are formed in the sintered body, thereby causing serious defects. 
     SUMMARY OF THE INVENTION 
     The inventors have made various studies in order to solve the aforementioned problems of the conventional techniques and found that firing under an addition of a certain additive is effective for restraining the weight reduction due to the evaporation of the phosphorus component and in this case a given crystalline phase is formed in the sintered body. Furthermore, it has been found that the heat resistance and high temperature stability of the crystalline phase are excellent when R in the R y  Zr 4  Si x  P 6-x  O 24  system is at least one bivalent or trivalent element such as Ca, Sr, Ba, Y or the like, and further various compounds of R y  Zr 4  P 6  O 24  (2/3≦y≦1, and R is at least one bivalent or trivalent element) such as CaZr 4  P 6  O 24 , SrZr 4  P 6  O 24 , BaZr 4  P 6  O 24  and the like form a whole solid solution, and also high strength and low expansion sintered bodies having heat resistance and high temperature stability can be obtained by controlling the properties of R y  Zr 4  P 6  O 24  itself such as thermal expansion behavior, thermal properties and the like through solid solubilization. In addition, it has been found that it is possible to form a solid solution wherein a part of the P ion is simultaneously replaced with an Si ion and an R ion as shown in the following reaction formula (1): 
     
         R.sub.y Zr.sub.4 P.sub.6 O.sub.24 +xSi.sup.4+ +1/nR&#39;.sup.n+ -xP.sup.6+ →R.sub.y R&#39;.sub.1/n ZrSi.sub.x P.sub.6-x O.sub.24  ( 1) 
    
     (where n is a valance number of R), and heat-resistant low expansion materials having high heat resistance and high strength and high temperature stability can be obtained by controlling the properties of R y  Zr 4  Si x  P 6-x  O 24  itself such as thermal expansion behavior, thermal properties and the like through solid solubilization. As a result, the invention has been accomplished. 
     That is, the invention provides a solid solution having a composition of R y  Zr 4  Si x  P 6-x  O 24 , wherein R is at least one bivalent or trivalent element, x is a numerical value of 0 to 2; and y is a numerical value of 2/3 to 2 satisfying an electrically neutral condition of the chemical formula, a heat-resistant sintered body comprising the above solid solution; a heat-resistant phosphate based compound sintered body containing not less than 10% by weight of the above solid solution and having a weight-reduced percentage of not more than 10% after the heat treatment at 1,400° C. for 100 hours; a method of producing a heat-resistant sintered body comprising a solid solution of R y  Zr 4  Si x  P 6-x  O 24  system, which comprises molding and firing a batch mixture of materials selected from ZrP 2  O 7 , (ZrO) 2  P 2  O 7 , ZrO 2 , Zr(OH) 4 , ZrSiO 4 , SiO 2 , a phosphate of R, a silicate of R, and RO (R is an element capable of forming bivalent or trivalent cation); and a method of producing a heat-resistant phosphate based compound sintered body, which comprises molding and firing a batch mixture of materials selected from ZrP 2  O 7 , (ZrO) 2  P 2  O 7 , ZrO 2 , ZrSiO 4 , SiO 2 , a phosphate of R, a silicate of R, and RO (R is an element capable of forming a bivalent or trivalent cation). 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     The invention will be described with reference to the accompanying drawings, wherein: 
     FIG. 1 is a graph showing a relationship between chemical composition and lattice constant in solid solutions of the CaZr 4  P 6  O 24  --SrZr 4  P 6  O 24  system and the CaZr 4  P 6  O 24  --BaZr 4  P 6  O 24  system; 
     FIG. 2 is a graph showing a relationship among chemical composition in a sintered body composed of a solid solution of the CaZr 4  P 6  O 24  --SrZr 4  P 6  O 24  system, thermal expansion coefficient within a range of room temperature to 1,400° C. and four-point flexural strength; 
     FIG. 3 is a graph showing a relationship among chemical composition in a sintered body composed of a solid solution of the CaZr 4  P 6  O 24  --BaZr 4  P 6  O 24  system, thermal expansion coefficient within a range of room temperature to 1,400° C. and four-point flexural strength; 
     FIG. 4 is a bar chart showing the weight-reduced percentage in Examples 1-10 and 14-18 and Comparative Examples 21-25 after heat treatment at 1,400° C. for 100 hours; 
     FIG. 5 is a graph showing a relationship between chemical composition of a sintered body composed of a solid solution of the R y  Zr 4  Si x  P 6-x  O 24  system and thermal expansion coefficient over a temperature range of room temperature to 1,400° C.; 
     FIG. 6 is a graph showing a relation between open porosity and four-point flexural strength in the sintered body composed of a solid solution of R y  Zr 4  Si x  P 6-x  O 24  system; 
     FIG. 7 is a graph showing a powder X-ray diffraction pattern at room temperature in Example 16; 
     FIG. 8 is a graph showing a weight-reduced percentage in the heat treatment at 1,400° C. for 100 hours when various additives are added to the phosphate based compound sintered body; 
     FIG. 9 is a graph showing a relationship between amount of R y  Zr 4  Si x  P 6-x  O 24  crystalline phase in the phosphate based compound sintered body and weight-reduced percentage in the heat treatment at 1,400° C. for 100 hours; 
     FIG. 10 is a graph showing a relationship between amount of R y  Zr 4  Si x  P 6-x  O 24  crystalline phase in the phosphate based compound sintered body and dimensional change percentage in the heat treatment at 1,400° C. for 100 hours; 
     FIG. 11 is a graph showing a relationship between open porosity and four-point flexural strength in the phosphate based compound sintered body; 
     FIG. 12 is a graph showing an X-ray diffraction pattern in the phosphate compound of Example 33; and 
     FIG. 13 is a view illustrating a method of measuring a self-weight softening percentage. 
    
    
     DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     The solid solution of the R y  Zr 4  Si x  P 6-x  O 24  system according to the invention can be used not only as a sintered body alone but also as a compound constituting a composite body with a heat-resistant compound such as zircon, zirconia or the like. 
     In the solid solution of R y  Zr 4  Si x  P 6-x  O 24  system according to the invention, it is necessary that R is at least one bivalent or trivalent element, and x is a numerical value of 0 to 2, and y is a numerical value of 2/3 to 2. Particularly, R is at least one element in Group IIa of the Periodic Table, (for example, barium (Ba), strontium (Sr) and calcium (Ca)). When R contains a monovalent cation, the high temperature stability is poor, while when x is more than 2, the heat resistance is poor. 
     When the above system satisfies the aforementioned requirements, a solid solution having improved heat resistance and high temperature stability, and a sintered body comprising this solid solution, are obtained. 
     In the phosphate based compound sintered body according to the invention, it is necessary to include a substance having the general formula of R y  Zr 4  Si x  P 6-x  O 24  as a crystalline phase. The heat stability at high temperature becomes largely different due to the presence or absence of this crystalline phase as mentioned later. 
     According to the sintered body of the invention, the weight-reduced percentage due to the evaporation of phosphorus component and the four-point flexural strength can be made to not more than 10% and not less than 100 kg/cm 2  at an open porosity of not more than 50% after the heat treatment at 1,400° C. for 100 hours. That is, when the open porosity exceeds 50%, the four-point flexural strength becomes less than 100 kg/cm 2  and the strength required as a practical ceramic material is not satisfied. Furthermore, the self-weight softening percentage of the sintered body after the heat treatment at 1,400° C. for 5 hours is not more than 0.3%, which satisfies the requirement as a heat-resistant material. 
     Moreover, the above sintered body is small in dimensional change percentage. That is, the dimensional change percentage is not more than 1% after a heat treatment at 1,400° C. for 100 hours, which also satisfies the requirement as a heat-resistant material. And also, the thermal expansion coefficient of the sintered body over a temperature range of room temperature to 1,400° C. is as low as not higher than 25×10 -7  /°C., which shows the excellent thermal shock resistance. Therefore, the sintered bodies according to the invention having the above properties are favorably applied to materials requiring the heat resistance and heat stability at high temperature such as ceramic honeycomb structural bodies, for instance, catalyst carrier for the purification of automobile exhaust gas and the like; rotary heat regenerating type ceramic heat exchangers, heat recuperative type ceramic heat exchangers, housings for a turbocharger rotor, heat insulation materials for an engine manifold, diesel particulate filters and so on. 
     In the method of producing the heat-resistant sintered body according to the invention, the starting material lies in a batch mixture of powdery materials selected from ZrP 2  O 7 , (ZrO) 2  P 2  O 7 , ZrO 2 , Zr(OH) 4 , ZrSiO 4 , SiO 2 , a phosphate of R, a silicate of R and RO (R is at least one bivalent or trivalent element). 
     Furthermore, in the method of producing the phosphate based compound sintered body according to the invention, the starting material lies in a batch mixture of powdery materials selected from ZrP 2  O 7 , (ZrO) 2  P 2  O 7 , ZrO 2 , ZrSiO 4 , SiO 2 , a phosphate of R, a silicate of R and RO (R is at least one bivalent or trivalent element). 
     These powdery materials of ZrP 2  O 7 , (ZrO) 2  P 2  O 7 , ZrO 2 , Zr(OH) 4 , ZrSiO 4 , SiO 2 , a phosphate of R, a silicate of R and RO are stable compounds and hardly produce the non-uniformity at the molding and firing step and are firable at the high temperature and can provide ceramics having excellent heat resistance. 
     On the other hand, if the conventionally used phosphoric acid is used as a P 2  O 5  source, since phosphoric acid is liquid, non-uniformity is caused during the mixing to locally form portions having a high phosphorus concentration and to thereby produce a compound having a low melting point. Further, when the honeycomb structural body is obtained by extruding a body containing phosphoric acid, an extrusion die or a cylinder in an extruder rusts or corrodes due to corrosiveness of phosphoric acid, and consequently the extrusion molding becomes considerably difficult. Moreover, when such a body is used in the pressing, it is essentially impossible to mold the body as a powder due to the presence of phosphoric acid. 
     In the method of producing the heat-resistant sintered body according to the invention, the batch mixture usually comprises 0-82.9% by weight of ZrP 2  O 7 , 0-79.5% by weight of (ZrO) 2  P 2  O 7 , 0-50.4% by weight of ZrO 2 , 0-56.8% by weight of Zr(OH) 4 , 0-38.0% by weight of ZrSiO 4 , 0-12.5% by weight of SiO 2 , 0-44.9% by weight of a phosphate of R, 0-35.5% by weight of a silicate of R, and 0-37.3% by weight of RO. In this case, it is necessary that the batch mixture contains at least one of ZrP 2  O 7 , (ZrO) 2  P 2  O 7  and the phosphate of R as well as RO, the silicate of R and the phosphate of R. 
     In the method of producing the heat-resistant phosphate based compound sintered body according to the invention, the batch mixture usually comprises 0-84.2% by weight of ZrP 2  O 7 , 0-82.3% by weight of (ZrO) 2  P 2  O 7 , 0-51.7% by weight of ZrO 2 , 0-77.2% by weight of ZrSiO 4 , 0-37.8% by weight of SiO 2 , 0-44.6% by weight of a phosphate of R, 0-53.0% by weight of a silicate of R, and 0-42.1% by weight of RO. In this case, it is necessary that the batch mixture contains at least one of ZrP 2  O 7 , (ZrO) 2  P 2  O 7  and the phosphate of R as well as RO, the silicate of R and the phosphate of R. 
     The RO as a starting component may be used by selecting from stable compounds such as hydroxides, carbonates, sulfates and the like converting into RO or an oxide during the firing. 
     Moreover, the starting material usually used has an average particle size of not more than 50 μm, preferably not more than 10 μm. 
     As the firing conditions for the sintered body according to the invention, the firing temperature is not lower than 1,400° C., preferably 1,400°-1,800° C., and the firing time is 1-24 hours, preferably 2-10 hours. When the firing temperature is restricted to not lower than 1,400° C., the phosphate based compound sintered body containing not less than 10% by weight of R y  Zr 4  Si x  P 6-x  O 24  as a crystalline phase according to the invention can be obtained. Further, when the firing time is less than 1 hour, the sintering is insufficient, while when it exceeds 24 hours, the strength lowers due to abnormal grain growth and also the precipitate of a different phase occurs due to the evaporation of the phosphorus component. 
     As mentioned above, the preferred embodiments of the invention will be summarized as follows: 
     (a) a solid solution of R y  Zr 4  P 6  O 24 , wherein R is at least two bivalent or trivalent elements and y is a numerical value of 2/3 to 2 satisfying an electrically neutral condition of the chemical formula, and a heat-resistant sintered body and heat-resistant phosphate based compound sintered body comprising the above solid solution; 
     (b) a solid solution of R y  Zr 4  Si x  P 6-x  O 24 , wherein R is at least one element of Ba, Sr and Ca, and x is a numerical value of 0 to 2 and y is a numerical value of 1 to 2, and a heat-resistant sintered body and heat-resistant phosphate based compound sintered body comprising the above solid solution; 
     (c) a heat-resistant sintered body comprising a solid solution of the R y  Zr 4  Si x  P 6-x  O 24  system and having a weight-reduced percentage of not more than 10% after a heat treatment at 1,400° C. for 100 hours; 
     (d) a heat-resistant sintered body and a heat-resistant phosphate based compound sintered body each comprising a solid solution of the R y  Zr 4  Si x  P 6-x  O 24  system and having an open porosity of not more than 50% and a four-point flexural strength of 100 kg/cm 2  ; 
     (e) a heat-resistant sintered body and a heat-resistant phosphate based compound sintered body each comprising a solid solution of R y  Zr 4  Si x  P 6-x  O 24  system and having a self-weight softening percentage of not more than 0.3% after the heat treatment at 1,400° C. for 5 hours; 
     (f) a heat-resistant sintered body and a heat-resistant phosphate based compound sintered body each comprising a solid solution of the R y  Zr 4  Si x  P 6-x  O 24  system and having a dimensional change percentage of not more than 1% after the heat treatment at 1,400° C. for 100 hours; 
     (g) a heat-resistant sintered body and a heat-resistant phosphate based compound sintered body each comprising a solid solution of the R y  Zr 4  Si x  P 6-x  O 24  system and having a thermal expansion coefficient over a temperature range of room temperature to 1,400° C. of not higher than 25×10 -7  /°C.; 
     (h) a heat-resistant sintered body and a heat-resistant phosphate based compound sintered body each comprising a solid solution of the R y  Zr 4  Si x  P 6-x  O 24  system for use in a honeycomb structural body; 
     (i) a heat-resistant composite body containing a solid solution of the R y  Zr 4  Si x  P 6-x  O 24  system as a main crystalline phase and a heat-resistant compound such as zircon, zirconia or the like as a second crystalline phase; 
     (j) a method of producing a heat-resistant sintered body and heat-resistant phosphate based compound sintered body comprising a solid solution of the R y  Zr 4  Si x  P 6-x  O 24  system, wherein R is at least one element of Ba, Sr and Ca; 
     (k) a method of producing a heat-resistant sintered body and heat-resistant phosphate based compound sintered body comprising a solid solution of the R y  Zr 4  Si x  P 6-x  O 24  system, wherein RO is selected from hydroxides, carbonates and sulfates converting into RO during the firing; 
     (l) a method of producing a heat-resistant sintered body and heat-resistant phosphate based compound sintered body comprising a solid solution of the R y  Zr 4  Si x  P 6-x  O 24  system, wherein the firing temperature is not lower than 1,400° C. and the firing time is 1-24 hours. 
     The following examples are given in illustration of the invention and are not intended as limitations thereof. 
     According to a formulating recipe as shown in the following Tables 1 and 2 zirconyl phosphate [(ZrO) 2  P 2  O 7  ], ZrP 2  O 7 , calcium carbonate, strontium carbonate, barium carbonate, yttria, nickel oxide, zircon, sodium carbonate, ammonium dihydrogen phosphate, ceria, titania, silica, calcium phosphate and zirconia, which were previously adjusted to a given particle size, were mixed to form a mixture. In Comparative Example 25, a mixture shown in Table 1 was charged into an alumina crucible, held in an electric furnace in air at 1,000° C. for 12 hours and pulverized to form a batch mixture. The adjustment of grain size in zirconyl phosphate was carried out by using a vibration mill filled with pebbles of ZrO 2  sintered body having a diameter of about 5 mm, but it may be carried out in a pot mill or an attriter. The pebbles of ZrO 2  sintered body were used by stabilizing with MgO and Y 2  O 3 . The chemical composition of the pebble used is shown in the following Table 3. Further, the chemical analysis values of the starting materials used are shown in the following Table 4. 
     One hundred parts by weight of the batch mixture shown in Tables 1 and 2 was added and throughly mixed with 5 parts by weight of a 10% PVA aqueous solution, which was pressed in a mold of 25×80×6 mm at a pressure of 100 kg/cm 2 , rubber-pressed at a pressure of 2 tons/cm 2  and then dried. After the drying, the molded body was fired in an electric furnace in air under conditions shown in Tables 1 and 2. The heating rate was 5°-1,700° C./hr. After the firing, the resulting sintered body was worked into a test specimen of 3×4×40 mm defined in JIS R1601 (1981), which was then measured with respect to weight-reduced percentage and dimensional change percentage after heat treatment at 1,400° C. for 100 hours, thermal expansion coefficient over a temperature range of room temperature (RT) to 1,400° C., four-point flexural strength, self-weight softening percentage, open porosity, and melting point. The measurement of the thermal expansion coefficient was carried out by means of a push rod type differential dilatometer using a high purity alumina sintered body over a measuring temperature range of room temperature to 1,400° C. The four-point flexural strength was measured according to a method shown in JIS R1601. The self-weight softening percentage was determined by the following equation through placing the above test specimen on supports at a span of 30 mm shown in FIG. 13, heat-treating it in air at 1,400° C. for 5 hours and measuring a self-weight deformation amount Δx: 
     
         Self-weight softening percentage=Δx/l×100(%) 
    
     The open porosity was measured according to an Archemedian process. The melting point was determined by visually observing whether or not a cut sample of the sintered body of 3×4×5 mm was melted by the heat treatment in an electric furnace at 1,700° C. for 10 minutes. Further, amounts of crystalline phases in the sintered body were quantitatively determined by using a reflection peak value at (200) plane of zirconyl phosphate (β-(ZrO) 2  P 2  O 7 ) [Communications of the American Ceramic Society, C-80(1984)], a reflection peak value at (113) plane of R y  Zr 4  Si x  P 6-x  O 24  [after the index of the above crystalline phase composition was numbered according to JCPDS 33-321 of CaZr 4  (PO 4 ) 6 , JCPDS 33-1360 of SrZr 4  (PO 4 ) 6  and JCPDS 34-95 of BaZr 4  (PO 4 ) 6 , a possible case for index numbering was judged to form a solid solution], a reflection peak value at (312) plane of JCPDS 6-266 of zircon, and a reflection peak value at (011) plane of JCPDS 34-95 of m-ZrO 2 , provided that since a relative intensity of the reflection at (011) plane of m-ZrO 2  is as low as 18/100, a value of 5.6 times of the intensity was used as a peak value. With respect to the other different crystalline phases, presence or absence thereof was only identified by the X-ray diffraction pattern. The lattice constant of the solid solution was determined by calculating a and c according to the following simultaneous equations after interplanar spacings d 018  and d 208  were measured from a reflection peak angle 2θ at (018) plane and a reflection peak angle at (208) plane of R y  Zr 4  Si x  P 6-x  O 24  : 
     
         1/d.sup.2.sub.018 =4/3a.sup.2 +64/c.sup.2 
    
     
         1/d.sup.2.sub.208 =16/3a.sup.2 +64/c.sup.2 
    
     
                                           TABLE 1(a)                              
__________________________________________________________________________
           Example                                                        
           1      2      3      4       5       6       7                 
__________________________________________________________________________
Formulating                                                               
proportions (wt %)                                                        
(ZrO).sub.2 P.sub.2 O.sub.7                                               
           37.1   36.8   36.5   36.1    36.8    36.1    35.4              
ZrP.sub.2 O.sub.7                                                         
           52.3   51.8   51.3   50.9    51.8    50.8    49.9              
CaCO.sub.3 7.7    5.7    3.8    1.9     7.5     5.6     3.7               
SrCO.sub.3 2.9    5.7    0.4    11.1                                      
BaCO.sub.3                              3.8     7.5     11.0              
ZrO.sub.2                                                                 
Ca.sub.3 P.sub.2 O.sub.8                                                  
NiO                                                                       
Y.sub.2 O.sub.3                                                           
SiO.sub.2                                                                 
Chemical                                                                  
composition (mol %)                                                       
CaZr.sub.4 P.sub.6 O.sub.24                                               
           80     60     40     20      80      60      40                
SrZr.sub.4 P.sub.6 O.sub.24                                               
           20     40     60     80                                        
BaZr.sub.4 P.sub.6 O.sub.24             20      40      60                
NiZr.sub.4 P.sub.6 O.sub.24                                               
Y.sub.2/3 Zr.sub.4 P.sub.6 O.sub.24                                       
Sr.sub.4 Zr.sub.4 Si.sub.6 O.sub.24                                       
Ba.sub.4 Zr.sub.4 Si.sub.6 O.sub.24                                       
Crystalline phase                                                         
           CaZr.sub.4 P.sub.6 O.sub.24                                    
                  CaZr.sub.4 P.sub.6 O.sub.24                             
                         CaZr.sub.4 P.sub.6 O.sub.24                      
                                CaZr.sub.4 P.sub.6 O.sub.24               
                                        CaZr.sub.4 P.sub.6 O.sub.24       
                                                SrZr.sub.4 P.sub.6        
                                                O.sub.24                  
                                                        SrZr.sub.4        
                                                        P.sub.6 O.sub.24  
main crystal-                                                             
SrZr.sub.4 P.sub.6 O.sub.24                                               
BaZr.sub.4 P.sub.6 O.sub.24                                               
BaZr.sub.4 P.sub.6 O.sub.24                                               
BaZr.sub.4 P.sub.6 O.sub.24                                               
BaZr.sub.4 P.sub.6 O.sub.24                                               
BaZr.sub.4 P.sub.6 O.sub.24                                               
BaZr.sub.4 P.sub.6 O.sub.24                                               
line phase solid  solid  solid  solid   solid   solid   solid             
           solution                                                       
                  solution                                                
                         solution                                         
                                solution                                  
                                        solution                          
                                                solution                  
                                                        solution          
second crystal-                                                           
           --     --     --     --      --      --      --                
line phase                                                                
__________________________________________________________________________
 
    
     
                                           TABLE 1(b)                              
__________________________________________________________________________
                    Example                                               
                    1   2   3   4   5   6   7                             
__________________________________________________________________________
Lattice constant of crystalline phase a (Å)                           
                    8.73                                                  
                        8.75                                              
                            8.71                                          
                                8.71                                      
                                    8.75                                  
                                        8.67                              
                                            8.73                          
c (Å)           22.86                                                 
                        23.00                                             
                            23.25                                         
                                23.29                                     
                                    22.96                                 
                                        23.31                             
                                            23.42                         
Firing conditions firing temperature (°C.)                         
                    1,600                                                 
                        1,600                                             
                            1,600                                         
                                1,600                                     
                                    1,600                                 
                                        1,600                             
                                            1,600                         
keeping time (h)    5   5   5   5   5   5   5                             
Firing shrinkage (%)                                                      
                    10.6                                                  
                        16.2                                              
                            16.8                                          
                                16.7                                      
                                    14.7                                  
                                        14.3                              
                                            13.8                          
Characteristics of sintered body                                          
open porosity (%)   16.3                                                  
                        14.8                                              
                            11.9                                          
                                14.0                                      
                                    15.6                                  
                                        14.0                              
                                            15.7                          
four-point bending strength (kg/cm.sup.2)                                 
                    250 520 660 720 170 370 570                           
weight-reduced percentage                                                 
                    1.2 1.0 0.9 0.6 2.4 2.1 1.7                           
(%, 1400° C. × 100 h)                                        
dimensional change percentage                                             
                    -0.8                                                  
                        -0.96                                             
                            -0.9                                          
                                -0.8                                      
                                    -0.7                                  
                                        -0.96                             
                                            -0.7                          
(%, 1400° C. × 100 h)                                        
self-weight softening percentage                                          
                    0.03                                                  
                        0.02                                              
                            0.02                                          
                                0.01                                      
                                    0.03                                  
                                        0.01                              
                                            0.01                          
(%, 1400° C. × 5 h)                                          
thermal expansion coefficient                                             
                    -3  13  21  24  -8  8   19                            
(×10.sup.-7 /°C., RT-1400° C.)                        
melting point (°C.)                                                
                    &gt;1,700                                                
                        &gt;1,700                                            
                            &gt;1,700                                        
                                &gt;1,700                                    
                                    &gt;1,700                                
                                        &gt;1,700                            
                                            &gt;1,700                        
__________________________________________________________________________
 
    
     
                                           TABLE 1(c)                              
__________________________________________________________________________
           Example                                                        
           8      9      10      11      12     13      14                
__________________________________________________________________________
Formulating                                                               
proportions (wt %)                                                        
(ZrO).sub.2 P.sub.2 O.sub.7                                               
           34.8          43.9    37.1    34.5   34.8                      
ZrP.sub.2 O.sub.7                                                         
           49.0   73.7   42.8    52.3    48.6   49.0    78.2              
CaCO.sub.3 1.8                   7.7            1.8                       
SrCO.sub.3        6.7    3.5     2.9     2.6            7.1               
BaCO.sub.3 14.4   9.1    4.8             14.3   14.4                      
ZrO.sub.2         10.5                                  11.1              
Ca.sub.3 P.sub.2 O.sub.8 5.0                                              
NiO                                                     3.6               
Y.sub.2 O.sub.3                                                           
SiO.sub.2                                                                 
Chemical                                                                  
composition(mol %)                                                        
CaZr.sub.4 P.sub.6 O.sub.24                                               
           20            50      80             20                        
SrZr.sub.4 P.sub.6 O.sub.24                                               
                  50     25      20      20             50                
BaZr.sub.4 P.sub.6 O.sub.24                                               
           80     50     25              80     80                        
NiZr.sub.4 P.sub.6 O.sub.24                             50                
Y.sub.2/3 Zr.sub.4 P.sub.6 O.sub.24                                       
Sr.sub.4 Zr.sub.4 Si.sub.6 O.sub.24                                       
Ba.sub.4 Zr.sub.4 Si.sub.6 O.sub.24                                       
 Crystalline phase                                                        
           CaZr.sub.4 P.sub.6 O.sub.24                                    
                  SrZr.sub.4 P.sub.6 O.sub.24                             
                         CaZr.sub.4 P.sub.6 O.sub.24                      
                                 CaZr.sub.4 P.sub.6 O.sub.24              
                                         SrZr.sub.4 P.sub.6 O.sub.24      
                                                CaZr.sub.4 P.sub.6        
                                                O.sub.24                  
                                                        SrZr.sub.4        
                                                        P.sub.6 O.sub.24  
main crsytal-                                                             
BaZr.sub.4 P.sub.6 O.sub.24                                               
BaZr.sub.4 P.sub.6 O.sub.24                                               
SrZr.sub.4 P.sub.6 O.sub.24                                               
SrZr.sub.4 P.sub.6 O.sub.24                                               
BaZr.sub.4 P.sub.6 O.sub.24                                               
BaZr.sub.4 P.sub.6 O.sub.24                                               
NiZr.sub.4 P.sub.6 O.sub.24                                               
line phase solid  solid  BaZr.sub.4 P.sub.6 O.sub.24                      
                                 solid   solid  solid   solid             
           solution                                                       
                  solution                                                
                         solid   solution                                 
                                         solution                         
                                                solution                  
                                                        solution          
                         solution                                         
second crystal-                                                           
           --     --     --      --      --     --      ZrP.sub.2         
                                                        O.sub.7           
line phase                                                                
__________________________________________________________________________
 
    
     
                                           TABLE 1(d)                              
__________________________________________________________________________
                    Example                                               
                    8   9 10    11  12  13  14                            
__________________________________________________________________________
Lattice constant of crystalline phase a (Å)                           
                    8.70                                                  
                        8.70                                              
                            8.68                                          
                                8.74                                      
                                    8.72                                  
                                        --  8.74                          
c (Å)           23.72                                                 
                        23.69                                             
                            22.91                                         
                                22.85                                     
                                    23.81                                 
                                        --  23.28                         
Firing conditions firing termperature (°C.)                        
                    1,600                                                 
                        1,600                                             
                            1,600                                         
                                1,400                                     
                                    1,800                                 
                                        1,800                             
                                            1,400                         
keeping time (h)    5   5   5   24  1   1   1                             
Firing shrinkage (%)                                                      
                    14.1                                                  
                        10.0                                              
                            17.2                                          
                                7.2 15  20.7                              
                                            23.1                          
Characteristics of sintered body                                          
open porosity (%)   13.8                                                  
                        20.2                                              
                            12.0                                          
                                18.1                                      
                                    14.9                                  
                                        5.0 5.4                           
four-point bending strength (kg/cm.sup.2)                                 
                    580 320 460 300 410 650 280                           
weight-reduced percentage                                                 
                    1.7 1.6 2.3 1.3 1.6 1.3 9.5                           
(%, 1400° C. × 100 h)                                        
dimensional change percentage                                             
                    -0.6                                                  
                        0.00                                              
                            -0.02                                         
                                -1.0                                      
                                    -0.05                                 
                                        --  -1.8                          
(%, 1400° C. × 100 h)                                        
self-weight softening percentage                                          
                    0.00                                                  
                        0.01                                              
                            0.02                                          
                                --  0.00                                  
                                        --  --                            
(%, 1400° C. × 5 h)                                          
thermal expansion coefficient                                             
                    21  22  19  1   23  --  --                            
(×10.sup.-7 /°C., RT-1400° C.)                        
melting point (°C.)                                                
                    &gt;1,700                                                
                        &gt;1,700                                            
                            &gt;1,700                                        
                                &gt;1,700                                    
                                    &gt;1,700                                
                                        &gt;1,700                            
                                            --                            
__________________________________________________________________________
 
    
     
                                           TABLE 1(e)                              
__________________________________________________________________________
           Example                                                        
           15     16     17     18     19                                 
__________________________________________________________________________
Formulating                                                               
proportions (wt %)                                                        
(ZrO).sub.2 P.sub.2 O.sub.7                                               
           35.8   52.5          63.1   49.2                               
ZrP.sub.2 O.sub.7                                                         
           50.4   22.8   40.7   10.5   21.3                               
CaCO.sub.3                             24.6                               
SrCO.sub.3 6.9    19.5   31.7   13.3                                      
BaCO.sub.3                                                                
ZrO.sub.2                                                                 
Ca.sub.3 P.sub.2 O.sub.8                                                  
NiO                                                                       
Y.sub.2 O.sub.3                                                           
           6.9                  5.0                                       
SiO.sub.2         5.2    ZrSiO.sub.4 27.6                                 
                                8.1    4.9                                
Chemical                                                                  
composition(mol %)                                                        
CaZr.sub.4 P.sub.6 O.sub.24                                               
SrZr.sub.4 P.sub.6 O.sub.24                                               
           50     83     67                                               
BaZr.sub.4 P.sub.6 O.sub.24            83                                 
NiZr.sub.4 P.sub.6 O.sub.24                                               
Y.sub.2/3 Zr.sub.4 P.sub.6 O.sub.24                                       
           50                   75                                        
Sr.sub.4 Zr.sub.4 Si.sub.6 O.sub.24                                       
                  17     33     25                                        
Ba.sub.4 Zr.sub.4 Si.sub.6 O.sub.24    17                                 
Crystalline phase                                                         
           SrZr.sub.4 P.sub.6 O.sub.24                                    
                  SrZr.sub.4 P.sub.6 O.sub.24                             
                         SrZr.sub.4 P.sub.6 O.sub.24                      
                                Y.sub.2/3 Zr.sub.4 P.sub.6 O.sub.24       
                                       Ba.sub. 4 Zr.sub.4 P.sub.6         
                                       O.sub.24                           
main crystal-                                                             
           Y.sub.2/3 Zr.sub.4 P.sub.6 O.sub.24                            
                  SrZr.sub.4 P.sub.6 O.sub.24                             
                         SrZr.sub.4 P.sub.6 O.sub.24                      
                                SrZr.sub.4 P.sub.6 O.sub.24               
                                       Ba.sub.4 Zr.sub.4 P.sub.6 O.sub.24 
                                       3                                  
line phase solid solution                                                 
                  solid solution                                          
                         solid solution                                   
                                solid solution                            
                                       solid solution                     
second crystal-                                                           
           ZrP.sub.2 O.sub.7                                              
                  --     zircon zircon --                                 
line phase                                                                
__________________________________________________________________________
 
    
     
                                           TABLE 1(f)                              
__________________________________________________________________________
                    Example                                               
                    15  16  17 18  19                                     
__________________________________________________________________________
Lattice constant of crystalline phase a (Å)                           
                    8.70                                                  
                        8.74                                              
                            8.77                                          
                               8.69                                       
                                   8.69                                   
c (Å)           23.30                                                 
                        23.34                                             
                            23.41                                         
                               23.32                                      
                                   24.00                                  
Firing conditions firing temperature (°C.)                         
                    1,400                                                 
                        1,600                                             
                            1,500                                         
                               1,600                                      
                                   1,600                                  
keeping time (h)    10  5   20 5   5                                      
Firing shrinkage (%)                                                      
                    7.6 21  23.1                                          
                               12.9                                       
                                   5.6                                    
Characteristics of sintered body                                          
open porosity (%)   38.3                                                  
                        4.7 6.4                                           
                               35.2                                       
                                   41.2                                   
four-point bending strength (kg/cm.sup.2)                                 
                    140 200 270                                           
                               160 130                                    
weight-reduced percentage                                                 
                    8.0 0.3 0.4                                           
                               1.2 0.7                                    
(%, 1400° C. × 100 h)                                        
dimensional change percentage                                             
                    -0.08                                                 
                        +0.20                                             
                            -0.3                                          
                               -0.8                                       
                                   -0.9                                   
(%, 1400° C. × 100 h)                                        
self-weight softening percentage                                          
                    0.24                                                  
                        0.10                                              
                            -- 0.13                                       
                                   0.26                                   
(%, 1400° C. × 5 h)                                          
thermal expansion coefficient                                             
                    37  -20 -- 11  -5                                     
(×10.sup.-7 /°C., RT-1400° C.)                        
melting point (°C.)                                                
                    &gt;1,700                                                
                        &gt;1,700                                            
                            -- &gt;1,700                                     
                                   &gt;1,700                                 
__________________________________________________________________________
 
    
     
                                           TABLE 1(g)                              
__________________________________________________________________________
           Example                                                        
           21     22     23     24     25     26                          
__________________________________________________________________________
Formulating                                                               
proportions (wt %)                                                        
(ZrO).sub.2 P.sub.2 O.sub.7                                               
           37.5   35.8   34.2   100                                       
ZrP.sub.2 O.sub.7                                                         
           52.8   50.4   48.1                                             
CaCO.sub.3 9.7                                                            
SrCO.sub.3        13.8                        40.9                        
BaCO.sub.3               17.7                                             
ZrO.sub.2                              38.4   34.2                        
Ca.sub.3 P.sub.2 O.sub.8                                                  
SiO.sub.2                                     24.8                        
NaCO.sub.3                             8.1                                
NH.sub.4 H.sub.2 PO.sub.4              53.5                               
Chemical                                                                  
composition (mol %)                                                       
CaZr.sub.4 (PO.sub.4).sub.6                                               
           100                                                            
SrZr.sub.4 (PO.sub.4).sub.6                                               
                  100                                                     
BaZr.sub.4 (PO.sub.4).sub.6                                               
                         100                                              
NiZr.sub.4 (PO.sub.4).sub.6                                               
Y.sub.2/3 Zr.sub.4 (PO.sub.4).sub.6                                       
(ZrO).sub.2 P.sub.2 O.sub.7     100                                       
Sr.sub.4 Zr.sub.4 Si.sub.6 O.sub.24    100                                
Ba.sub.4 Zr.sub.4 Si.sub.6 O.sub.24           100                         
Crystalline phase                                                         
main crystal-                                                             
           CaZr.sub.4 P.sub.6 O.sub.24                                    
                  SrZr.sub.4 P.sub.6 O.sub.24                             
                         BaZr.sub.4 P.sub.6 O.sub.24                      
                                (ZrO).sub.2 P.sub.2 O.sub.7               
                                       NaZr.sub.2 P.sub.3 O.sub.12        
                                              unknown                     
line phase                                                                
second crystal-                                                           
           --     --     --     --     --     m-ZrO.sub.2                 
line phase                                                                
__________________________________________________________________________
 
    
     
                                           TABLE 1(h)                              
__________________________________________________________________________
                    Example                                               
                    21  22  23  24  25 26                                 
__________________________________________________________________________
Lattice constant of crystalline phase a (Å)                           
                    8.79                                                  
                        8.72                                              
                            8.68                                          
                                --  -- --                                 
c (Å)           22.72                                                 
                        23.36                                             
                            23.95                                         
                                --  -- --                                 
Firing conditions firing temperature (°C.)                         
                    1,550                                                 
                        1,600                                             
                            1,600                                         
                                1,600                                     
                                    1,400                                 
                                       1,400                              
keeping time (h)    5   5   5   5   2  5                                  
Firing shrinkage (%)                                                      
                    14.6                                                  
                        16.2                                              
                            10.4                                          
                                18.5                                      
                                    13.0                                  
                                       melt                               
Characteristics of sintered body                                          
open porosity (%)   16.1                                                  
                        17.2                                              
                            26.5                                          
                                4.1 23 --                                 
four-point bending strength (kg/cm.sup.2)                                 
                    110 640 320 500 490                                   
                                       --                                 
weight-reduced percentage                                                 
                    3.0 0.6 2.4 18.5                                      
                                    36 --                                 
(%, 1400° C. × 100 h)                                        
dimensional change percentage                                             
                    -1.8                                                  
                        -0.25                                             
                            -0.2                                          
                                -1.4                                      
                                    -3.0                                  
                                       --                                 
(%, 1400° C. × 100 h)                                        
self-weight softening percentage                                          
                    0.03                                                  
                        0.01                                              
                            0.00                                          
                                0.01                                      
                                    0.09                                  
                                       --                                 
(%, 1400° C. × 5 h)                                          
thermal expansion coefficient                                             
                    -15 25  23  4   -22                                   
                                       --                                 
( × 10.sup.-7 /°C., RT-1400° C.)                      
melting point (°C.)                                                
                    &gt;1,700                                                
                        &gt;1,700                                            
                            &gt;1,700                                        
                                &gt;1,700                                    
                                    -- --                                 
__________________________________________________________________________
 
    
     
                                           TABLE 2(a)                              
__________________________________________________________________________
                              Example                                     
                              31  32  33  34  35  36   37                 
__________________________________________________________________________
formulating                                                               
           (ZrO).sub.2 P.sub.2 O.sub.7                                    
                              98.0                                        
                                  95.0                                    
                                      98.0                                
                                          95.0                            
                                              95.0                        
                                                  86   66.6               
proportions                                                               
           ZrP.sub.2 O.sub.7                           7.0                
(wt. %)    CaCO.sub.3                 2.0 5.0                             
           SrCO.sub.3         2.0 5.0                  13.3               
           BaCO.sub.3                         5.0                         
           ZrO.sub.2                                                      
           Ca.sub.3 P.sub.2 O.sub.6                                       
           ZrSiO.sub.4                            9                       
           SiO.sub.2                                   8.0                
           Y.sub.2 O.sub.3                        5    5.1                
Crystalline phase                                                         
           CaZr.sub.4 (PO.sub.4).sub.6                                    
                                      20  47                              
(wt. %)    SrZr.sub.4 (PO.sub.4).sub.6                                    
                              13  32                                      
           BaZr.sub.4 (PO.sub.4).sub.6        24                          
           R.sub.y Zr.sub.4 P.sub.6-x Si.sub.x O.sub.24 solid             
                                                  21lution                
                                                       97                 
                                                  (YZr.sub.4 P.sub.5      
                                                       (SrY.sub.0.5       
                                                       Zr.sub.4           
                                                  SiO.sub.24)             
                                                       P.sub.4.5 Si.sub.1.
                                                       5 O.sub.24)        
           (ZrO).sub.2 P.sub.2 O.sub.7                                    
                              87  62  80  44  68  65                      
           m-ZrO.sub.2            6       9   8   9                       
           others                                 zircon                  
                                                       zircon 3           
Firing     fireing temperature (°C.)                               
                              1,600                                       
                                  1,500                                   
                                      1,600                               
                                          1,400                           
                                              1,800                       
                                                  1,600                   
                                                       1,600              
conditions keeping time (h)   5   10  5   24  1   5    5                  
Firing shrinkage (%)          19.2                                        
                                  18.1                                    
                                      19.1                                
                                          13.8                            
                                              18.7                        
                                                  17.4 12.9               
Characteristics of                                                        
           open porosity (%)  2.5 8.1 3.7 19.5                            
                                              3.3 6.7  35.2               
sintered body                                                             
           four-point bending strength (kg/cm.sup.2)                      
                              750 650 450 320 550 680  300                
           weight-reduced percentage                                      
                              8.6 6.0 7.0 6.2 7.2 8.3  8.6                
           (%, 1400° C. × 100 h)                             
           dimensional change percentage                                  
                              -0.77                                       
                                  -0.35                                   
                                      -0.29                               
                                          -0.25                           
                                              -0.17                       
                                                  -0.98                   
                                                       -0.4               
           (%, 1400° C. × 100 h)                             
           self-weight softening percentage                               
                              --  --  --  --  --  --   --                 
           (%, 1400° C. × 5 h)                               
           thermal expansion coefficient                                  
                              11  --  2   --  5   --   14                 
           (× 10.sup.-7 /°C., RT-1400°  C.)           
           melting point (°C.)                                     
                              --  &gt;1,700                                  
                                      --  --  --  --   &gt;1,700             
__________________________________________________________________________
 
    
     
                                           TABLE 2(b)                              
__________________________________________________________________________
                     Example                                              
                     41 42      43 44   45   46   47   48                 
__________________________________________________________________________
Formulating                                                               
        (ZrO).sub.2 P.sub.2 O.sub.7                                       
                     98.0                                                 
                        88      37.5                                      
                                   95.0 95.0 95.0 95.0 95.0               
proportions                                                               
        ZrP.sub.2 O.sub.7       52.8              5.0                     
(wt. %) CaCO.sub.3              9.7                                       
        SrCO.sub.3                                                        
        BaCO.sub.3   2                                                    
        ZrO.sub.2                                                         
        Ca.sub.3 P.sub.2 O.sub.6                                          
        ZrSiO.sub.4                                                       
        SiO.sub.2       Y.sub.2 O.sub.3 :2.0                              
                                   CeO.sub.2 :5.0                         
                                        SiO.sub.2 :5.0                    
                                             TiO.sub.2 :5.0               
                                                       Na.sub.2 CO.sub.3  
                                                       :5.0               
        Y.sub.2 O.sub.3 zircon 10.0                                       
Crystalline                                                               
        CaZr.sub.4 (PO.sub.4).sub.6                                       
                        solid   100                                       
phase   SrZr.sub.4 (PO.sub.4).sub.6                                       
                        solution 8                                        
(wt. %) BaZr.sub.4 (PO.sub.4).sub.6                                       
                     9  (YZr.sub.4 P.sub.5 SiO.sub.24)                    
        R.sub.y Zr.sub.4 P.sub.6-x Si.sub.x O.sub.24                      
                        8                              45                 
        solid solution  (YZr.sub.4 P.sub.5 SiO.sub.24) (Na.sub.2 Zr.sub.4 
                                                       P.sub.6 O.sub.24)  
        (ZrO).sub.2 P.sub.2 O.sub.7                                       
                     91 77         S    S    S    S    40                 
        m-ZrO.sub.2     7                              15                 
        others          zircon 8   CePO.sub.4                             
                                        ZrP.sub.2 O.sub.7                 
                                             TiO.sub.2                    
                                                  ZrP.sub.2 O.sub.7       
Firing  firing temperature (°C.)                                   
                     1,600                                                
                        1,600   1,350                                     
                                   1,600                                  
                                        1,600                             
                                             1,600                        
                                                  1,600                   
                                                       1,600              
conditions                                                                
        keeping time (h)                                                  
                     5  5       5  5    5    5    5    5                  
Firing               19.1                                                 
                        21.0    12.8                                      
                                   20.2 18.0 18.2 19.4 15.0               
shrinkage (%)                                                             
Characteristics                                                           
        open porosity (%)                                                 
                     2.1                                                  
                        5.6     21.7                                      
                                   --   --   --   --   21.3               
of sintered                                                               
        four-point bending strength                                       
                     610                                                  
                        710     260                                       
                                   --   --   --   --   360                
body    (kg/cm.sup.2)                                                     
        weight-reduced percentage                                         
                     15.5                                                 
                        12.3    11.4                                      
                                   14.5 16.5 23.6 13.8 23                 
        (%, 1400° C. × 100 h)                                
        dimensional change                                                
                     -1.10                                                
                        -1.00   -5.62                                     
                                   -1.14                                  
                                        -1.55                             
                                             -2.67                        
                                                  -1.35                   
                                                       -1.20              
        percentage                                                        
        (%, 1400° C. × 100 h)                                
        self-weight softening                                             
                     -- --      0.01                                      
                                   --   --   --   --   --                 
        percentage                                                        
        (%, 1400° C. × 5 h)                                  
        thermal expansion                                                 
                     -- --      -- --   --   --   --   --                 
        coefficient                                                       
        (× 10.sup.-7 /°C., RT-1400° C.)               
        melting point (°C.)                                        
                     -- --      -- --   --   --   --   &gt;1,700             
__________________________________________________________________________
 
    
     
                       TABLE 3                                                     
______________________________________                                    
         MgO stabilized                                                   
                   Y.sub.2 O.sub.3 stabilized                             
         ZrO.sub.2 pebbles                                                
                   ZrO.sub.2 pebbles                                      
______________________________________                                    
SiO.sub.2  0.28        &lt;0.05                                              
Al.sub.2 O.sub.3                                                          
           0.037       &lt;0.02                                              
Fe.sub.2 O.sub.3                                                          
           0.14        0.10                                               
TiO.sub.2  0.12        &lt;0.01                                              
CaO        0.29        &lt;0.005                                             
MgO        3.37        0.007                                              
K.sub.2 O  0.010       &lt;0.005                                             
Na.sub.2 O 0.047       &lt;0.01                                              
Y.sub.2 O.sub.3                                                           
           --          5.04                                               
ZrO.sub.2  94.19       92.90                                              
HfO.sub.2  1.65        2.11                                               
Total      100.13      100.16                                             
______________________________________                                    
 
    
     
                                           TABLE 4                                 
__________________________________________________________________________
       Chemical analysis values                                           
       ZrO.sub.2                                                          
           P.sub.2 O.sub.5                                                
              SiO.sub.2                                                   
                  Al.sub.2 O.sub.3                                        
                      MgO CaO NaKO  Ig loss                               
                                        Fe.sub.2 O.sub.3                  
                                             SrO                          
                                                BaO                       
__________________________________________________________________________
(ZrO).sub.2 P.sub.2 O.sub.7                                               
       61.85                                                              
           36.38                                                          
              &lt;0.2                                                        
                  0.01                                                    
                      0.45                                                
                          0.02                                            
                              0.01  3.20                                  
                                        &lt;0.01                             
                                             -- --                        
ZrP.sub.2 O.sub.7                                                         
       46.44                                                              
           52.24                                                          
              0.02                                                        
                  &lt;0.01                                                   
                      &lt;0.01                                               
                          &lt;0.01                                           
                              &lt;0.01 2.86                                  
                                        &lt;0.01                             
                                             -- --                        
CaCO.sub.3                                                                
       --  -- --  --  --  55.72                                           
                              &lt;0.01 43.78                                 
                                        &lt;0.01                             
                                             -- --                        
SrCO.sub.3                                                                
       --  -- 0.001                                                       
                  &lt;0.001                                                  
                      0.001                                               
                          0.11                                            
                              0.012 30.15                                 
                                        0.018                             
                                             69.61                        
                                                --                        
BaCO.sub.3                                                                
       --  -- --  --  --  --  --    22.30                                 
                                        &lt;0.01                             
                                             -- 76.50                     
CeO.sub.2                                                                 
       --  -- 0.01                                                        
                  0.001                                                   
                      &lt;0.001                                              
                          0.005                                           
                              --    0.06                                  
                                        &lt;0.001                            
                                             -- --                        
SiO.sub.2                                                                 
       --  -- 99.68                                                       
                  0.07                                                    
                      0.018                                               
                          &lt;0.002                                          
                              0.005 0.07                                  
                                        0.038                             
                                             -- --                        
TiO.sub.2                                                                 
       --  -- 0.07                                                        
                  2.10                                                    
                      &lt;0.01                                               
                          &lt;0.01                                           
                              &lt;0.01 0.66                                  
                                        &lt;0.01                             
                                             -- --                        
Ca.sub.3 (PO.sub.4).sub.2                                                 
       --  45.53                                                          
              0.01                                                        
                  0.02                                                    
                      --  53.97                                           
                              0.01  0.10                                  
                                        &lt;0.01                             
                                             -- --                        
ZrO.sub.2                                                                 
       98.65                                                              
           -- 0.06                                                        
                  0.01                                                    
                      0.01                                                
                          0.04                                            
                              0.02  0.38                                  
                                        &lt;0.01                             
                                             -- --                        
Y.sub.2 O.sub.3                                                           
       --  -- &lt;0.01                                                       
                  --  --  &lt;0.01                                           
                              --    --  &lt;0.01                             
                                             -- --                        
ZrSiO.sub.4                                                               
       66.63                                                              
           -- 32.62                                                       
                  0.35                                                    
                      0.002                                               
                          0.001                                           
                              0.06  0.21                                  
                                        0.054                             
                                             -- --                        
Na.sub.2 CO.sub.3                                                         
       --  -- --  --  --  --  Na.sub.2 O 58.47                            
                                    41.51                                 
                                        &lt;0.0005                           
                                             -- --                        
NH.sub.4 H.sub.2 PO.sub.4                                                 
       --  61.08                                                          
              --  --  --  --  --    37.92                                 
                                        --   -- --                        
NiO    --  -- --  --  --  --  --    0.2 --   -- --                        
__________________________________________________________________________
                                              Average                     
                                              particle                    
                            Chemical analysis values                      
                                              size                        
                            CeO.sub.2                                     
                                Gd.sub.2 O.sub. 3                         
                                    TiO.sub.2                             
                                       Y.sub.2 O.sub.3                    
                                           NiO                            
                                              (μm)                     
__________________________________________________________________________
                     (ZrO).sub.2 P.sub.2 O.sub.7                          
                            --  --  -- --  -- 0.9                         
                     ZrP.sub.2 O.sub.7                                    
                            --  --  -- --  -- 1.0                         
                     CaCO.sub.3                                           
                            --  --  -- --  -- 2.2                         
                     SrCO.sub.3                                           
                            --  --  -- --  -- 0.6                         
                     BaCO.sub.3                                           
                            --  --  -- --  -- 10.0                        
                     CeO.sub.2                                            
                            99.62                                         
                                --  -- --  -- 1.6                         
                     SiO.sub.2                                            
                            --  --  0.004                                 
                                       --  -- 1.0                         
                     TiO.sub.2                                            
                            --  --  97.09                                 
                                       --  -- &lt;1.0                        
                     Ca.sub.3 (PO.sub.4).sub.2                            
                            --  --  -- --  -- 2.0                         
                     ZrO.sub.2                                            
                            --  --  0.15                                  
                                       --  -- 0.9                         
                     Y.sub.2 O.sub.3                                      
                            --  --  -- &gt;99.9                              
                                           -- 1.0                         
                     ZrSiO.sub.4                                          
                            --  --  0.095                                 
                                       --  -- 1.0                         
                     Na.sub.2 CO.sub.3                                    
                            --  --  -- --  -- 10                          
                     NH.sub.4 H.sub.2 PO.sub.4                            
                            --  --  -- --  -- 20                          
                     NiO    --  --  -- --  99 0.8                         
__________________________________________________________________________
 
    
     As seen from the results of Examples 1-19 and Comparative Examples 21-26 in Table 1, the solid solution of R y  Zr 4  Si x  P 6-x  O 24  system according to the invention and the heat-resistant sintered body comprising the above solid solution are obtained when R is at least one bivalent or trivalent element and x is a numerical value of 0-2. Further, the solid solution and sintered body are obtained by sintering a batch mixture of materials selected from ZrP 2  O 7 , (ZrO) 2  P 2  O 7 , ZrO 2 , Zr(OH) 4 , ZrSiO 4 , SiO 2 , a phosphate of R, a silicate of R and RO (R is at least one bivalent or trivalent element) under firing conditions shown in Table 1. 
     In FIG. 1 is shown a relationship between chemical composition and lattice constant in solid solutions of the CaZr 4  P 6  O 24  --SrZr 4  P 6  O 24  system and the CaZr 4  P 6  O 24  --BaZr 4  P 6  O 24  system. FIG. 2 shows a relationship among chemical composition in a solid solution of the CaZr 4  P 6  O 24  --SrZr 4  P 6  O 24  system, and thermal expansion coefficient and four-point flexural strength of a sintered body thereof. FIG. 3 shows a relationship among chemical composition in a solid solution of the CaZr 4  P 6  O 24  --BaZr 4  P 6  O 24  system, and thermal expansion coefficient and four-point flexural strength of a sintered body thereof. FIG. 4 shows a relationship between chemical composition in a solid solution of the R y  Zr 4  Si x  P 6-x  O 24  system and a weight-reduced percentage when a sintered body comprising this solid solution is held at 1,400° C. for 100 hours. FIG. 5 shows a relationship between chemical composition in a solid solution of the R y  Zr 4  Si x  P 6-x  O 24  system and a thermal expansion coefficient of a sintered body comprising this solid solution. 
     As seen from the above, when R is at least one bivalent or trivalent element, the heat resistance and high temperature stability of the crystalline phase are excellent, and further the characteristics of solid solution of R y  Zr 4  P 6  O 24  (2/3≦y≦1) itself can be maintained through solid solubilization. Additionally, high strength and low expansion sintered bodies having excellent heat resistance and high temperature stability can be obtained. 
     In addition, the solid solution wherein a part of the P ion is simultaneously replaced with an Sr ion and an R ion is more excellent in the high temperature stability and the characteristic of the solid solution of the R y  Zr 4  Si x  P 6-x  O 24  system itself can be controlled, whereby the heat-resistant sintered bodies having a further improved high temperature stability, a high strength and a low expansion are obtained. 
     Further, FIG. 6 shows a relationship between open porosity and four-point flexural strength in the sintered body comprising a solid solution of the R y  Zr 4  Si x  P 6-x  O 24  system. 
     Moreover, FIG. 7 shows a powder X-ray diffraction pattern of the sintered body in Example 16 at room temperature, which indicates that the sintered body consists of only the solid solution of Sr 1 .5 Zr 4  SiP 6  O 24 . 
     As seen from the results of Examples 2, 6, 9, 10, 16 and Comparative Examples 21-24 in Table 1 and Examples 31-37 and Comparative Examples 41-48 in Table 2, when R y  Zr 4  Si x  P 6-x  O 24  (R is at least one capable of forming bivalent or trivalent element) is contained in an amount of not less than 10% by weight as a crystalline phase, the phosphate based compound sintered bodies having a weight-reduced percentage of not more than 10% after heat treatment at 1,400° C. for 100 hours according to the invention are obtained. Further, such sintered bodies are obtained by sintering a batch mixture of materials selected from ZrP 2  O 7 , (ZrO) 2  P 2  O 7 , ZrO 2 , ZrSiO 4 , SiO 2 , a phosphate of R, a silicate of R and RO under firing conditions shown in Tables 1 and 2. FIG. 8 shows a weight-reduced percentage when various additives are added to the phosphate compound. FIG. 9 shows a relationship between weight percentage of R y  Zr 4  Si x  P 6-x  O 24  system contained in the phosphate compound and weight-reduced percentage of the sintered body. FIG. 10 shows a relation between weight percentage of R y  Zr 4  Si x  P 6-x  O 24  crystalline phase and dimensional change percentage in the phosphate based compound sintered body. 
     As seen from the above, when not less than 10% by weight of the R y  Zr 4  Si x  P 6-x  O 24  crystalline phase is included into the phosphate based compound sintered body, the weight-reduced percentage and dimensional change percentage after the heat treatment in air at 1,400° C. for 100 hours are considerably small and the heat resistance is excellent in the phosphate based compound sintered body. 
     Furthermore, FIG. 11 shows a relationship between open porosity and four-point flexural strength in the phosphate based compound sintered body. 
     Moreover, FIG. 12 shows an X-ray diffraction pattern of the phosphate based compound sintered body in Example 33, from which it is apparent that the sintered body contains (ZrO) 2  P 2  O 7  and CaZr 4  (PO 4 ) 6  as a crystalline phase. 
     As mentioned above, according to the invention, there can be obtained a solid solution of the R y  Zr 4  Si x  P 6-x  O 24  system (where R is at least one bivalent or trivalent element, and x is a numerical value of 0-2 and y is a numerical value of 2/3-2 satisfying an electrically neutral condition of the chemical formula), and a heat-resistant sintered body comprising the above solid solution and having high strength, low expansion and excellent high temperature stability, and a heat-resistant phosphate based compound sintered body containing not less than 10% by weight of the above solid solution and having a weight-reduced percentage of not more than 10% after the heat treatment at 1,400° C. for 100 hours. 
     Therefore, the solid solution of the R y  Zr 4  Si x  P 6-x  O 24  system, and the heat-resistant sintered body and phosphate based compound sintered body comprising this solid solution can widely be applied to articles requiring high heat resistance, low expansion and high temperature stability, such as rotary heat regenerating type ceramic heat exchangers and heat recuperative type ceramic heat exchangers when being molded into a honeycomb structural body through extrusion molding, and diesel particulate filters, and housings for ceramic turbocharger rotor or heat insulating materials for engine manifold when being molded through slip casting, pressing, injection molding or the like.