Process for producing closed-cell polyurethane foam compositions expanded with mixtures of blowing agents
This application is a continuation of application Ser. No. 158,442 filed Feb. 2, 1988, now abandoned. 
    
    
     FIELD OF THE INVENTION 
     This invention relates to closed-cell polyurethane foams expanded with mixtures of blowing agents comprising the two-carbon hydrogen-containing halocarbons HCFC-123, HCFC-123a and HCFC-141b and selected shrinkage-minimizing halocarbons to produce minimal shrinkage polyurethane foams. 
     BACKGROUND OF THE INVENTION 
     In 1985, about 140 MM lbs. of blowing agents (primarily CFC-11 and CFC-12) were used in the U.S. to produce all types of insulation foams. Of this total volume, about 70% or 100 MM lbs. were used to make polyurethane foam. Closed-cell polyurethane foam is the most energy efficient insulating material available, having an R value of approximately 7.2 per inch; whereas fiberglass has an R value of approximately 3.1 per inch. 
     Closed-cell polyurethane foams are widely used for insulation purposes in building construction and in the manufacture of energy efficient electrical appliances. In the construction industry, polyurethane (polyisocyanurate) board stock is used in roofing and siding for its insulation and load-carrying capabilities. Poured and sprayed polyurethane foams are also used in construction. Sprayed polyurethane foams are widely used for insulating large structures such as storage tanks, etc. Pour-in-place urethane foams are used, for example, in appliances such as refrigerators and freezers plus they are used in making refrigerated trucks and rail cars. 
     In the early 1970s, concern began to be expressed that the stratospheric ozone layer (which provides protection against penetration of the earth&#39;s atmosphere by ultraviolet radiation) was being depleted by chlorine atoms introduced to the atmosphere from the release of fully halogenated chlorofluorocarbons. These chlorofluorocarbons are widely used as propellants in aerosols, as blowing agents for foams, as refrigerants and as cleaning/drying solvent systems. Because of the great chemical stability of fully halogenated chlorofluorocarbons, according to the ozone depletion theory, these compounds do not decompose in the earth&#39;s atmosphere but reach the stratosphere where they slowly degrade liberating chlorine atoms which in turn react with the ozone. 
     Concern reached such a level that in 1978 the U.S. Environmental Protection Agency (EPA) placed a ban on nonessential uses of fully halogenated chlorofluorocarbons as aerosol propellants. This ban resulted in a dramatic shift in the U.S. away from chlorofluorocarbon propellants (except for exempted uses) to primarily hydrocarbon propellants. However, since the rest of the world did not join the U.S. in this aerosol ban, the net result has been to shift the uses of chlorofluorocarbons in aerosols out of the U.S., but not to permanently reduce the world-wide total chlorofluorocarbon production, as sought. In fact, in the last few years the total amount of chlorofluorocarbons manufactured has exceeded the level produced in 1978 (before the U.S. ban). 
     During the period of 1978-1987, much research was conducted to study the ozone depletion theory. Because of the complexity of atmospheric chemistry, many questions relating to this theory remain unanswered. However, if the theory is valid, the health risks which would result from depletion of the ozone layer are significant. This, coupled with the fact that world-wide production of chlorofluorocarbons has increased has resulted in international efforts to reduce chlorofluorocarbon use. Particularly, in Sept. 1987, the United Nations through its Environment Programme (UNEP) issued a tentative proposal calling for a 50 percent reduction in world-wide production of fully halogenated chlorofluorocarbons by the year 2000. 
     Because of this proposed reduction in availability of fully halogenated chlorofluorocarbons such as CFC-11 and CFC-12, alternative, more environmentally acceptable, products are urgently needed. 
     As early as the 1970s with the initial emergence of the ozone depletion theory, it was known that the introduction of hydrogen into previously fully halogenated chlorofluorocarbons markedly reduced the chemical stability of these compounds. Hence, these now destabilized compounds would be expected to degrade in the atmosphere and not reach the stratosphere and the ozone layer. The accompanying Table lists the ozone depletion potential for a variety of fully and partially halogenated halocarbons. Greenhouse potential data (potential for reflecting infrared radiation (heat) back to earth and thereby raising the earth&#39;s surface temperature) are also shown. 
     
         ______________________________________                                    
OZONE DEPLETION AND GREENHOUSE POTENTIALS                                 
                 Ozone Depletion                                          
                             Greenhouse                                   
Blowing Agent    Potential*  Potential**                                  
______________________________________                                    
CFC-11 (CFCl.sub.3)                                                       
                 1.0         0.4                                          
CFC-12 (CF.sub.2 Cl.sub.2)                                                
                 0.9         1.0                                          
HCFC-22 (CHF.sub.2 Cl)                                                    
                 0.05        0.07                                         
HCFC-123 (CF.sub.3 CHCl.sub.2)                                            
                 less than 0.05                                           
                             less than 0.1                                
HCFC-124 (CF.sub.3 CHFCl)                                                 
                 less than 0.05                                           
                             less than 0.1                                
HFC-134a (CF.sub.3 CH.sub.2 F)                                            
                 0           less than 0.1                                
HCFC-141b (CFCl.sub.2 CH.sub.3)                                           
                 less than 0.05                                           
                             less than 0.1                                
HCFC-142b (CF.sub.2 ClCH.sub.3)                                           
                 less than 0.5                                            
                             less than 0.2                                
HFC-152a (CHF.sub.2 CH.sub.3)                                             
                 0           less than 0.1                                
______________________________________                                    
 *Calculated relative to CFC11.                                           
 **Calculated relative to CFC12.                                          
 
    
     Halocarbons such as HCFC-123, HCFC 123a and HCFC-141b are environmentally acceptable in that they theoretically have minimal effect on ozone depletion. However, these halocarbons cause cell shrinkage or collapse when used as blowing agents for closed-cell polyurethane foams. This shrinkage is particularly apt to occur with relatively flexible polymers such as those prepared from polyether polyols and when the closed-cell polyurethane foam is a low density foam, e.g., less than about 2.0 lbs./cu. ft., particularly about 1.5 lbs./cu.ft. As compared to higher density foams, the production of lower density foams generally requires a larger quantity of blowing agent and a smaller amount of polymer which results in thinner and, consequently, weaker cell walls. In addition, the halocarbon blowing agents may migrate from the cell cavities to the bulk polymer and soften or plasticize the already thin cell walls. 
     Finally, foam cells are most fragile just after preparation as the temperature of the foamed polyurethane returns to ambient. At the temperature at which foams are made, which normally reaches about 200°-300° F. because of the exothermic reaction between polyol and isocyanate, the cells contain blowing agent at one atmosphere pressure. However, after cooling to ambient temperature, foams typically contain blowing agent at less than atmospheric pressure. Since this creates a partial vacuum in the cells, they will shrink to smaller volumes if the cell walls are weak, soft or very thin. Generally, this shrinkage occurs within 72 hours of preparation and before the polymer in the cell walls fully cures and hardens. This shrinkage or collapse of foams is undesirable and results in: 
     (a) loss of insulation value; 
     (b) loss of structural strength; 
     (c) pulling away of foam from walls, e.g., walls of a refrigerator. 
     Such shrinkage or collapse of polyurethane insulation foam makes these halocarbons unattractive as blowing agents. It might be possible, however, to reformulate the polyurethane foam formulations to be more compatible with these halocarbons. Such a solution would require a complete study of the preparation/properties/uses of new formulations and would require a considerable period of time for development. Long term, new or modified polymer systems designed for use with these halocarbons and other more polymer-soluble blowing agents will most likely be developed; however, what is needed, as fully halogenated chlorofluorocarbon blowing agents face regulation and usage restriction, are blowing agent systems which can be used in present, essentially unmodified, polyurethane foam formulations. 
     SUMMARY OF THE INVENTION 
     A Process has been discovered comprising 
     mixing at least 1 wt. percent and less than about 60 wt. percent of a shrinkage-minimizing halocarbon selected from the group consisting of CFC-11, CFC-12, HCFC-22, HFC-32, CFC-113, CFC-114, HCFC-124, HCFC-133a, HFC-134a, HCFC-142b and HFC-152a and a minimum of about 40 wt. percent of a two-carbon hydrogen-containing halocarbon selected from the group consisting of HCFC-123, HCFC-123a and HCFC-141b, to form a mixture, and, thereafter, 
     using the mixture to produce a minimal shrinkage closed-cell polyurethane foam. 
     Also included are minimal shrinkage closed-cell polyurethane foams which have been formed using the mixture of the instant invention. 
     DETAILED DESCRIPTION OF THE INVENTION 
     By minimal shrinkage closed-cell polyurethane foam is meant a closed-cell polyurethane foam which is formed using the mixture of the instant invention which foam decreases in volume by less than ten (10) percent after it is allowed to stand at atmospheric pressure for at least seventy-two (72) hours after formation as compared to the foam&#39;s original volume. 
     The closed-cell polyurethane foams of the instant invention include all types of closed-cell polyurethane foams including: 
     1. pour-in-place appliance foams, normally made by the reaction of a polyether polyol with an isocyanate, approximately on a 1/1 isocyanate equivalent/hydroxyl equivalent basis. An isocyanate index of 105 is common. The isocyanate chosen may be of the toluene diisocyanate (TDI) or polymethylene polyphenyl isocyanate (MDI) type. The polyether polyols may be various polyhydroxy compounds which may be polyethylene glycols, polypropylene glycols, mixed PEO-PPO-based glycols, reaction products of sugars or aminoalcohols and ethylene oxide and/or propylene oxide, etc. 
     2. board stock (isocyanurate) foams, normally made by the reaction of an aromatic polyester polyol (may be a mixture of polyester/polyether polyols) with an isocyanate (MDI) in the ratio of isocyanate equivalent to hydroxyl equivalent of 1.5-6.0. Aromatic polyester polyols may differ considerably in structure. For example, a polyester polyol may be made by the transesterification of polyethylene terephthalate (PET) scrap with a glycol such as diethylene glycol or a polyester polyol may be made from phthalic anhydride plus a glycol. 
     Unexpectedly, the two-carbon hydrogen-containing halocarbons of this invention, 1,1-dichloro-2,2,2-trifluoroethane (HCFC-123), 1,2-dichloro-1,1,2-trifluoroethane (HCFC-123a) and 1,1-dichloro-1-fluoroethane (HCFC-141b), in combination with selected shrinkage-minimizing halocarbons, trichloromonofluoromethane (CFC-11), dichlorodifluoromethane (CFC-12), monochlorodifluoromethane (HCFC-22), difluoromethane (HFC-32), 1,1,2-trichlorotrifluoroethane (CFC-113), 1,2-dichlorotetrafluoroethane (CFC-114), 1-chloro-1,2,2,2-tetrafluoroethane (HCFC-124), 1-chloro-2,2,2-trifluoroethane (HCFC-133a), 1,1,1,2-tetrafluoroethane (HFC-134a), 1-chloro-1,1-difluoroethane (HCFC-142b) and 1,1-difluoroethane (HFC-152a), form blowing agent mixtures which can produce minimal shrinkage closed-cell polyurethane foams. The use of the two-carbon hydrogen-containing halocarbons as the sole blowing agents produce closed-cell polyurethane foams which have much greater shrinkage. The mixtures of the instant invention produce closed-cell polyurethane foams which, unexpectedly, shrink less than one would expect from a simple mixing of the two-carbon hydrogen-containing halocarbons with the selected shrinkage-minimizing halocarbons. 
     The two-carbon hydrogen-containing halocarbons of the instant invention, HCFC-123, HCFC-123a and HCFC-141b, are known in the art and can be prepared by known methods. The shrinkage-minimizing halocarbons of the instant invention, CFC-11, CFC-12, HCFC-22, HFC-32, CFC-113, CFC-114, HCFC-124, HCFC-133a, HFC-134a, HCFC-142b and HFC-152a, are also known in the art and can be prepared by known methods. 
     It has been found that at least 1 wt. percent and less than about 60 wt. percent of the shrinkage-minimizing halocarbons of this invention can be combined with a minimum of about 40 wt. percent of the two-carbon hydrogen-containing halocarbons of the instant invention to form the mixtures of this invention. 
     Of the total blowing agent mixture, the effective quantity of CFC-11, CFC-12, HCFC-22, HFC-32, CFC-113, CFC-114, HCFC-124, HCFC-133a, HFC-134a, HCFC-142b and HFC-152a can be at least 1 wt. percent and less than about 60 wt. %, preferably, about 5 to 59 wt. percent, and more preferably, about 10 to 40 wt. percent. The remainder of the mixture is two-carbon hydrogen-containing halocarbons, such as HCFC-123. 
     Concentrations of CFC-11 in HCFC-123/CFC-11 mixtures of less than about 5 wt. percent up to about 40 wt. percent function unexpectedly to prevent foam shrinkage associated with the presence of HCFC-123. In addition, this concentration range permits making lower density foams, 1.5-2.5 lbs./cu.ft. (lower density gives lower K-factor and better insulation) than would be possible with HCFC-123 alone, since low density foams shrink most when HCFC-123 is used as the sole blowing agent. 
     Concentrations of CFC-11 in HCFC-123/CFC-11 blends of 40 to 60 wt. percent function to permit preparation of very low density foams (density of 1.2-1.5 lbs./cu.ft.) without shrinkage, which are the best insulating foams and which would be difficult or impossible to produce with HCFC-123 alone. 
     The use of the preferred blend of HCFC-123/HCFC-11 in the ratio of about 80/20 wt. percent, for example, limits shrinkage of a polyurethane foam to less than one percent compared to the foam&#39;s original volume. This compares to a shrinkage of about 35% for a foam which is formed using HCFC-123 as the sole blowing agent. CFC-12, HCFC-22, HFC-32, CFC-113, CFC-114, HCFC-124, HCFC-133a, HFC-134a, HCFC-142b and HFC-152a also unexpectedly reduce/prevent appreciable cell collapse/shrinkage as compared to a polyurethane foam which has been formed using HCFC-123 as the sole blowing agent. 
     HCFC-123a and HCFC-141b, used alone, also cause excessive foam cell shrinkage. Mixtures of the two-carbon hydrogen-containing halocarbons can also be used. When up to but less than 60 wt. percent of CFC-11, CFC-12, HCFC-22, HFC-32, CFC-113, CFC-114, HCFC-124, HCFC-133a, HFC-134a, HCFC-142b and/or HFC-152a, either individually or together, are blended with the two-carbon hydrogen-containing halocarbons, either individually or together, minimal shrinkage closed-cell polyurethane foams can be produced. 
     The mixtures of the instant invention can be prepared in any manner convenient to the preparer including simply weighing desired quantities of each component and, thereafter, combining them in an appropriate container. 
     Polyurethane foams are generally prepared by combining a polyol, an isocyanate, a blowing or expanding agent, and other materials such as catalysts and surfactants, to form a polyurethane reaction formulation. Thereafter, the polyurethane reaction formulation is allowed to expand either into an enclosed space or to expand unrestricted. For example, polyurethane foams using the mixture of the instant invention can be prepared by methods described in U.S. Pat. No. 4,411,949, which patent is incorporated herein by reference. 
     Based on the weight of the total polyurethane reaction formulation, the effective concentration of CFC-11, CFC-12, HCFC-22, HFC-32, CFC-113, CFC-114, HCFC-124, HCFC-133a, HFC-134a, HCFC-142b and HFC-152a can be about 0.1 to 25 wt. percent, preferably about 0.5 to 15 wt. percent. 
     The useful concentration range for the mixtures of the instant invention based on the weight of the polyurethane reaction formulation can be about 1 to 30 wt. percent based on the total polyurethane reaction formulation, with the preferred range being about 5 to 20 wt. percent. Since blowing agents are often dissolved (for handling convenience) in the polyol portion of the polyurethane reaction formulation to prepare &#34;B-side systems&#34;, the useful concentration range of the mixture of the instant invention in the polyol may be about 2-60 wt. percent with the preferred range being about 10-40 wt. percent of the polyol. 
    
    
     EXAMPLES 
     In order to determine the amount of foam shrinkage which occurs in polyurethane foams using different blowing or expanding agents, samples of foams were prepared by hand mixing and aging, using the three basic polyurethane reaction formulations described in Table I. 
     Foams were prepared by mixing the indicated quantities of polyol and isocyanate as outlined in Table I for each of the three foam systems studied. 
     The blowing agents used were generally premixed with the polyol portion of the formulation for convenience. Blowing agents CFC-11, HCFC-123 and HCFC-141b were blended with the appropriate polyol in one pint glass jars; however, because of the higher pressures (and tendency for blowing agent loss if blended at atmospheric pressure), the other blowing agents evaluated were combined with the appropriate polyol in 8-ounce aerosol cans. 
     To allow time for a 15 sec. blending of the polyol containing the blowing agent and the isocyanate prior to the start of the reaction exotherm, the polyol and the isocyanate were separately cooled to -10° C. prior to mixing. 
     After cooling to -10° C., the polyol (containing the blowing agent, surfactant and catalyst) was added to the isocyanate and blended for 15 seconds using a high speed air driven mixer. 
     Foams were prepared by two techniques: 
     (1) After the 15 sec. mixing, the appliance foam reaction formulation was poured into a 2-1/2&#34;×13&#34;×15&#34; mold (heated to 140° F.) and allowed to expand and fill the closed mold. 
     (2) After the 15 sec. mixing, the board stock reaction formulation was poured into a 5-qt. paint can liner and allowed to rise freely. 
     After allowing the foam samples to cure and cool to ambient temperature, the amount of shrinkage was determined as described below. 
     In the free rise samples, a center section (3&#34;×3&#34;×4&#34;) was removed for observation. All shrinkage measurements were made a minimum of 72 hours after foam formation. 
     Table II shows typical quantities of ingredients required for preparing a foam sample in the 21/2&#34;×13&#34;×15&#34; closed mold. 
     Table III shows shrinkage DATA. 
     Shrinkage Measurement 
     (A) 21/2&#34;×13&#34;×15&#34; Closed Mold: Because foam shrinkage can be non-uniform, varying from irregular concave areas on sides of the foam blocks to significant volume contractions at the tops of the foam blocks, estimation of volume is difficult. Thus, a water immersion technique was developed. In this technique, the increased amount of water required to fill a plastic chamber containing the shrunken foam block versus the foam block exhibiting no shrinkage is a measure of the volume loss or shrinkage occurring after a given period of time. 
     The amount of shrinkage was calculated using the following formula: ##EQU1## where A=Volume of chamber to overflow 
     B=Original Volume of foam block before shrinkage occurs 
     C=Volume of water required to fill chamber to overflow with shrunken block in place 
     D=A-C=Volume of shrunken block 
     The following is the Result of sample calculation with the indicated values: ##EQU2## 
     (B) 3&#34;×3&#34;×4&#34; Free Rise: Just as with the closed mold tests, the water immersion technique was used for determining shrinkage of the center sections (3&#34;×3&#34;×4&#34;) for free rise foam samples after a given period of time. 
     The amount of shrinkage was calculated using the following formula: ##EQU3## where A=Volume of chamber to overflow 
     B=Original Volume of foam block before shrinkage occurs 
     C=Volume of water required to fill chamber to overflow with shrunken block in place 
     D=A-C=Volume of shrunken block 
     The following is the result of a sample calculation with the indicated values: ##EQU4## 
     
                                           TABLE I                                 
__________________________________________________________________________
POLYURETHANE SYSTEMS                                                      
               Iso-            Iso-  Iso-                                 
Polyurethane                                                              
       Foam    cyanate                                                    
                    Polyol                                                
                          Polyol                                          
                               cyanate                                    
                                     cyanate                              
System Application                                                        
               Index*                                                     
                    Type  Eq. Wt.                                         
                               Type  Eq. Wt.                              
                                          Comments                        
__________________________________________________________________________
I      Appliance                                                          
               105  Polyether                                             
                          133.6                                           
                               MDI   134.0                                
                                          Polyol contains                 
       (pour-in-place)                    1.43 percent water              
II     Appliance                                                          
               100**                                                      
                    Polyether                                             
                          118.0                                           
                               TDI   124.0                                
                                          Polyol contains                 
                               (modified) 0.85 percent water              
III    Insulating                                                         
               250  Polyester                                             
                          140.2                                           
                               MDI   136.0                                
       board stock                                                        
       (isocyanurate)                                                     
__________________________________________________________________________
 *The number of equivalents of isocyanates per equivalent of hydroxyl in  
 the polyol multiplied by 100.                                            
 **Approximate                                                            
 
    
     
                                           TABLE II                                
__________________________________________________________________________
TYPICAL FOAM FORMULATIONS                                                 
Blowing                                                                   
       Quantity                                                           
            Polyurethane                                                  
                   Polyol,                                                
                       Isocyanate,                                        
                             Blowing Agent                                
Agent  g.   System g.  g.    Molecular Weight                             
__________________________________________________________________________
CFC-11 44.0 I      100.0                                                  
                       122.7 137.4                                        
HCFC-123                                                                  
       49.0 I      100.0                                                  
                       122.7 153.0                                        
HCFC-141b                                                                 
       37.4 I      100.0                                                  
                       122.7 116.9                                        
CFC-114                                                                   
       54.7 I      100.0                                                  
                       122.7 170.9                                        
__________________________________________________________________________
 
    
     
                       TABLE III                                                   
______________________________________                                    
POLYURETHANE FOAM PREPARATION                                             
______________________________________                                    
                 FOAM PREPARATION                                         
POLYURETHANE SYSTEM                                                       
                 PROCEDURE -                                              
(TABLE I) - I    CLOSED MOLD                                              
                %        Moles  Foam   %                                  
Blowing % B     A + B    A &amp; B in                                         
                                Den-   Volume                             
Agent   in      in       CWT    sity   Shrink-                            
A    B      A + B   Polymer                                               
                           Polymer                                        
                                  #/cu. ft.                               
                                         age                              
______________________________________                                    
11   --     --      16.5   0.144  1.90   0                                
123  --     --      17.8   0.142  2.13   35                               
123  11      5.0    17.8   0.142  2.11   0.5                              
123  11     10.0    17.7   0.142  2.17   0.25                             
123  11     15.0    17.6   0.142  2.10   0.25*                            
123  11     20.0    17.6   0.142  2.10   0                                
123  11     40.0    17.4   0.142  2.20   0                                
123  11     10.0    19.4   0.160  2.06   0.1**                            
123  11     65.0    17.7   0.151  2.12   0                                
123  --     --      17.8   0.142  2.13   35                               
123  12     5.0     17.7   0.142  2.15   7.2                              
123  12     10.0    17.5   0.142  1.96   5                                
123  12     15.0    17.3   0.142  2.01   2.9                              
123  12     20.0    17.1   0.142  1.95   1.3                              
123  --     --      17.8   0.142  2.13   35                               
123  22     5.0     17.3   0.142  2.01   15                               
123  22     10.0    16.8   0.142  2.10   3                                
123  22     20.0    16.0   0.142  2.23   2.2                              
123  --     --      17.8   0.142  2.13   35                               
123  114    5.0     17.9   0.142  2.15   9                                
123  114    12.0    18.0   0.142  2.13   4.2                              
123  114    15.0    18.1   0.142  2.14   2.3                              
123  114    20.0    18.2   0.142  2.14   1                                
123  --     --      17.8   0.142  2.13   35                               
123  124    20.0    17.5   0.142  2.01   0.3                              
123  134a   20.0    16.5   0.142  1.90   2.4                              
123  142b   20.0    16.4   0.142  2.16   0                                
123  152a   20.0    14.7   0.142  2.15   0.9                              
11   --     --      16.5   0.144  1.90   0                                
11   --     --      24.1   0.231  1.35   0.8                              
141b --     --      20.1   0.215  1.40   44                               
141b 11     20.0    20.6   0.215  1.42   3.2                              
141b --     --      20.1   0.215  1.40   44                               
141b 12     20.0    20.2   0.215  1.31   22                               
141b 12     40.0    20.3   0.215  1.46   3.5                              
141b --     --      20.1   0.215  1.40   44                               
141b 22     5.0     19.8   0.215  1.42   43                               
141b 22     10.0    19.5   0.215  1.33   39                               
141b 22     20.0    19.0   0.215  1.43   16                               
141b 22     40.0    18.0   0.215  1.32   9.4                              
141b --     --      20.1   0.215  1.40   44                               
141b 114    20.0    21.2   0.215  1.44   20                               
141b 114    40.0    21.4   0.215  1.34   2.7                              
141b --     --      20.1   0.215  1.40   44                               
141b 124    20.0    20.6   0.215  1.43   8.8                              
141b 134a   20.0    19.6   0.215  1.36   4.7                              
141b 142b   20.0    19.6   0.215  1.39   2.3                              
141b 152a   20.0    17.9   0.215  1.32   5.3                              
______________________________________                                    
                 FOAM PREPARATION                                         
POLYURETHANE SYSTEM                                                       
                 PROCEDURE -                                              
(TABLE I) - II   CLOSED MOLD                                              
                %        Moles  Foam   %                                  
Blowing % B     A + B    A &amp; B in                                         
                                Den-   Volume                             
Agent   in      in       CWT    sity   Shrink-                            
A    B      A + B   Polymer                                               
                           Polymer                                        
                                  #/cu. ft.                               
                                         age                              
______________________________________                                    
11   --     --      16.4   0.144  1.37   0                                
123  --     --      21.5   0.180  1.77   3                                
123  11     5.0     22.4   0.190  1.80   3                                
123  11     5.0     21.4   0.180  1.77   2.5                              
123  11     10.0    23.3   0.202  1.81   2                                
123  11     15.0    24.4   0.215  1.73   0.6                              
123  11     15.0    21.2   0.180  1.76   0.1                              
123  11     20.0    25.5   0.230  1.65   0.2                              
123  11     20.0    21.1   0.179  1.75   0                                
123  --     --      23.4   0.200  1.59   16.1                             
123  11     10.0    23.2   0.200  1.59   5.4                              
123  12     10.0    22.9   0.200  1.53   3.7                              
123  22     10.0    22.2   0.200  1.53   5.1                              
123  114    10.0    23.6   0.200  1.60   8.8                              
123  124    10.0    23.2   0.200  1.61   0                                
123  134a   10.0    22.6   0.200  1.49   0.8                              
123  142b   10.0    22.5   0.200  1.58   0                                
123  152a   10.0    21.3   0.200  1.50   2.1                              
141b --     --      18.9   0.390  1.41   15                               
141b 11     10.0    19.2   0.391  1.42   4.8                              
141b 12     10.0    19.0   0.391  1.37   9.5                              
141b 22     10.0    18.4   0.391  1.40   3.5                              
141b 114    10.0    19.5   0.391  1.47   2.8                              
141b 124    10.0    19.2   0.391  1.46   1.8                              
141b 134a   10.0    18.7   0.391  1.42   6                                
141b 142b   10.0    18.7   0.391  1.39   5.7                              
______________________________________                                    
                 FOAM PREPARATION                                         
POLYURETHANE SYSTEM                                                       
                 PROCEDURE -                                              
(TABLE I) - III  FREE RISE                                                
                %        Moles  Foam   %                                  
Blowing % B     A + B    A &amp; B in                                         
                                Den-   Volume                             
Agent   in      in       CWT    sity   Shrink-                            
A    B      A + B   Polymer                                               
                           Polymer                                        
                                  #/cu. ft.                               
                                         age                              
______________________________________                                    
11   --     --      19.8   0.180  1.52   0                                
123  --     --      21.6   0.180  1.42   33                               
123  11     5.0     21.5   0.180  1.43   15                               
123  11     10.0    21.4   0.180  1.44   10                               
123  11     15.0    21.3   0.180  1.43   6                                
123  11     20.0    21.2   0.180  1.40   5                                
123  11     25.0    21.1   0.180  1.42   4                                
123  11     30.0    21.0   0.180  1.44   3                                
123  11     65.0    21.6   0.180  1.39   0                                
141b --     --      17.4   0.180  1.54   34                               
141b 11     20.0    17.8   0.180  1.71   0.2                              
141b --     --      17.4   0.180  1.54   34                               
141b 124    20.0    19.4   0.180  1.37   9.1                              
141b 142b   20.0    18.5   0.180  1.38   5.9                              
141b 152a   20.0    16.8   0.180  1.44   10.5                             
______________________________________                                    
 *Less than                                                               
 **Aproximate