Shrinkage compensated mortar material
CROSS REFERENCE TO RELATED APPLICATION 
     This application claims foreign priority based on Japanese Patent Application No. 58-84692, filed May 14, 1983. 
     BACKGROUND OF THE INVENTION 
     This invention is concerned with a mortar material composed of all materials, except water, of which the mortar is composed. The desired mortar may be produced by adding water to the referenced mortar material. 
     During installation of machinery, the installation of foundations for bridges, or during the installation of inverse castings of concrete, an opening is temporarily formed between the structures, and mortar (also called grout) is later poured into the referenced opening. The referenced mortar should have high flowability in order to fill the void completely. In addition, it is critical that there be no shrinkage. If the mortar shrinks at the time of hardening, adhesion between the hardened mortar and the structure will not occur. Moreover, the referenced mortar must be able to withstand the conditions of use. 
     Utility of cement products such as mortar and concrete is usually evaluated by means of 28-day strength tests. The referenced mortar is also evaluated by 28-day strength tests. However, the use of mortar as referenced is merely one of the procedures of the total construction process. If the mortar does not harden to certain standards of strength, the next stage of construction cannot be started. The strength required of the mortar differs depending upon the type of work and processes involved. However, in general the mortar of this invention attains adequate strength within 2 or 3 days at normal temperatures. During the winter additional time is required. Consequently, there is a problem of waiting before the next step in construction can be commenced. 
     If a shrinkage compensated, fast hardening mortar which achieves compressive strength of 100 to 150 kg/cm 2  within a few hours of placement could be produced, it could reduce the total construction time. However, there has been no mortar with both accelerated hardening characteristics and characteristics of strength and durability, while at the same time providing practicality and total balance in terms of high flowability, shrinkage compensation, high strength, accelerated time of set, and early utility. For example, normal mortars with accelerated setting time hardening characteristics are often deficient in 28-day strength, creating an imbalance of the desired characteristics, resulting in a lack of utility of the product. 
     SUMMARY OF THE INVENTION 
     The purpose of this invention is to produce a better and more practical shrinkage compensated mortar which has both accelerated hardening characteristics and good strength characteristics. A wide range of experiments were performed with the material components of the referenced mortar, with the ratios of the component materials used, and with the performance of the mortar. The result was the discovery of components which achieved the objectives of this invention. 
     The composition of the shrinkage compensated mortar used by this invention is as follows: 
     a. Cement composed of 60 to 80% by weight of fast hardening cement, and the balance of portland cement; 
     b. Lime 5 to 8% by weight; 
     c. Silica Powder 5 to 8% by weight; 
     d. Hydroxylated carboxylic acid or the equivalent sodium salt 0.2 to 0.4% by weight; 
     e. Super plasticizing agent 2 to 3% by weight. 
     This material is characteristic of mortars in that it is composed of 40 to 60% by weight hydraulic material and 40 to 60% by weight of fine aggregate. 
     DETAILED DESCRIPTION OF THE INVENTION 
     The fast hardening cement of the above mentioned components is primarily portland cement produced, however, with bauxite or kaolin as the alumina source. In addition, fluosilicate is used as the source of fluorine. The components are calcined to produce the fast hardening component of the mortar material. The clinker is primarily made of solid solution of 3CaO.SiO 2 , the solid solution of 11CaO.7Al 2  O 3 .CaF 2 , small amounts of the solid solution of CaO.SiO 2 , a solid solution of 2CaO-Fe 2  O 3  -6CaO.2Al 2  O 3 .Fe 2  O 3  and CaO. In addition, anhydrous gypsum is added to the ground clinker. This mixture is generally referred to as &#34;Jet Cement&#34;. The shrinkage compensated mortar which contains this fast hardening cement has both fast hardening characteristics and good strength characteristics. However, the placement time is limited and 28-day strength is low. In order to overcome these shortcomings, this fast hardening cement and portland cement are blended in the above-mentioned proportions. 
     The lime expansion material is a baked clinker powder containing a large amount of CaO crystal grains of which the primary components are the 3 components of 3CaO.SiO 2 ,CaO,CaSO 4 . When water is added, CaO hydrates to Ca(OH) 2  and expands. This component is added to the mortar in order to obtain shrinkage compensation characteristics. The amount added should be within the range given above. When the amount added is less than given, adequate shrinkage compensation characteristics cannot be obtained. On the other hand, if the amount added is too much, undesirable excessive expansion is obtained. 
     The silica powder in the formula reacts with the Ca(OH) 2  produced by the hydration of lime expansion material, and produces the crystalline calcium silicate. This compound is blended into the shrinkage compensating mortar in order to increase strength at later ages, and to control the expansion. Among the various silica powders, silica flour or silica fume, an extremely fine crystal of silica powder, with an average diameter less than 1 micron, seems to be the most suitable material to obtain the objectives of this invention. This extremely fine crystalline silica fume does not require as large an amount of water as some other types of silica powders in order to obtain the effects cited. Optimum results are obtained when the amount of the silica fume is the same as that of the lime expansive material. 
     The hydroxycarboxylic acid or sodium salt is used to remedy the problem of early setting times, caused by the use of the fast hardening cement. When the amount added is below the above cited range, its retarding effect is inadequate. On the other hand, when the amount added is greater than that of the range cited, there is a delay in the time required to achieve setting time and early strength characteristics. Gluconic acid or sodium gluconate produces the best results. 
     The referenced water reducing agent is a product possessing low air-entraining characteristics in concrete, with little or no retardation. This includes a sodium salt of a condensate of naphthalene sulfonic acid and formaldehyde, and a sodium salt of a condensate of sulfonated melamine and formaldehyde. The water reducing agent is added to the mix in order to reduce the amount of water necessary to produce an adequate degree of flowability in the shrinkage compensated mortar. As the amount of mixing water is reduced, the compressive strength is increased. At the same time &#34;bleeding&#34;, which destroys some of the characteristics of shrinkage compensated mortars is controlled. In general, about 0.5% by weight of cement of this type of water reducing agent is used for ordinary concrete materials. However, in this invention, greater amounts of this agent are used. The exact amount of water reducing agent in the mortar is determined relative to the amounts of the other compounds needed to produce high flowability, high strength, and shrinkage compensation. 
     The mortar material of this invention is composed of 40 to 60% by weight of fine aggregate, as cited in sections (a) to (e). This fine aggregate should be hard and clean (such as with quartz sand or silica sand). The shape of the grains should be well formed, and able to pass through a 2.5 mm sieve. The aggregate should not contain too much fine sand. The range for the hydraulic material and the aggregate is appropriate for this use. When the amount of fine aggregate is reduced below the limits given, the characteristics of shrinkage compensation and working time are also reduced significantly. 
     Water is added to the mortar material of this invention and mixed well. This produces a mortar having the necessary characteristics of flowability. The required degree of flowability varies according to the shape of the space which should be filled, and the method of placing the mortar. However, flowability is standardized in &#34;Test Methods for Quality Control of Non-Shrink Mortar&#34; by the Japan Highway Corporation. Flowability is the flow time measured by the designated and improved J funnel, equivalent to 8+/-3 seconds. The mortar material of this invention achieved high flowability, above the referenced 8+/-3 seconds, by adding less than 40% by weight of water per 100% by weight of hydraulic material. 
     It takes about 3 hours at normal ambient temperatures of 22° C. to reach a compressive strength of 150 kg/cm 2 . It takes about 7 hours at 5° C. Later 28-day strength is more than 600 kg/cm 2 . Normal working time for the mortar is more than 15 minutes, and is practical. This invention has demonstrated for the first time a shrinkage compensated mortar with superior characteristics of an accelerated setting time, long term strength, and practical working time. Of course, desired characteristics of good flowability and shrinkage compensation are also present. In addition, it is appropriate often to add 0.5 to 1.5% by weight of sodium carbonate to the 100% by weight of the cement component in order to increase the fast setting characteristics. 
     In the manner of this invention, it is possible to reduce the period of time required for machinery installation by using the shrinkage compensating mortar composed of the materials specified. During the winter, in periods of low temperature, ordinary mortar does not gain strength quickly. For this reason any processes following the pouring of the mortar may be delayed for several days. However, the mortar described by this invention, as previously mentioned, achieves the designated strength at the low temperature of 5° C., although a few hours later than at ordinary temperatures. For this reason, construction time during the winter can be greatly reduced. 
     In addition, the mortar material of this invention can be used in a special way for installation of machinery. Prior to the installation of the base plate, the pads which support the base plate are usually constructed on a concrete base. The material used is different from the shrinkage compensating mortar. However, small amounts of water can be added to the mortar of this invention, producing a fairly dry mixture. Pads can be made of this mixture, by tamping it down. 
    
    
     EXAMPLES 
     The effects of the mortar material of this invention were tested as follows: 
     (1) The components of the mortar material of this invention were as follows: 
     (a) Fast Hardening Cement (JC). 
     Trademark &#34;Jet Cement&#34; manufactured by Onoda Cement Corporation. 
     (b) Portland Cement (PC) 
     Ordinary Portland Cement manufactured by Asano Cement Corporation. 
     (c) Lime Expansion Material (EX) 
     Trademark &#34;Ekusupsan&#34; manufactured by Onoda Cement Corporation. 
     (d) Silica Powder (SI) 
     Silica powder commercially marketed. Average grain diameter is 0.2 to 0.5 microns, and SiO 2  content is 90.40% by weight or greater 
     (e) Sodium salt of hydroxycarboxylic acid 
     Sodium Gluconic Acid 
     (f) Water-reducing agent 
     Formaldehyde condensate of sulfonated melamine, sodium salt (SMF). Trademark &#34;Merumento F-10&#34; manufactured by Showa Denko Corporation. 
     (g) Fine Aggregate 
     Quartz sand under 2.5 mm. 
     (2) Composition of This Invention 
     (a) The composition of this invention is as shown in the following Table: 
     
         ______________________________________                                    
Cement        % by Weight for 100%                                        
% by Weight   Cement Component                                            
JC      PC        EX       SI    GA     SMF                               
______________________________________                                    
70      30        6        6     0.3    2.7                               
______________________________________                                    
 
    
     (b) Composition of Mortar Materials 
     The shrinkage compensated mortar is made by mixing 50% by weight of the hydraulic material and 50% by weight of the fine aggregate. 
     (3) Mortar Produced by This Invention 
     The mortar produced by this invention is made by adding 18.8% by weight (unspecified) to 100% by weight of the above cited mortar material. The temperature was set at 19° C., and the improved J funnel flow time is 5.7 seconds.* In addition, the usable time for this mortar is 15 minutes. 
    
     (4) Comparison with Other Mortars 
     The required amount of water was added to commercially available calcium sulfoaluminate (CSA) mortar. At a temperature of 21° C. the flow rate was 6.2 seconds. 
     (5) Experimental Results 
     Table 1 shows the experimental results obtained at three different temperatures, i.e. 5° C., 20° C. and 30° C. respectively. No bleeding was observed in any of the test specimens. As seen in Table 1, the mortar made with the material of this invention produced a strength of more than 150 kg/cm 2  within several hours. It showed accelerated hardening characteristics. At the same time, the 28-day compressive strength tests showed more strength than other products. It is clear that the mortar of this invention has characteristics superior to others. 
     In addition, with the exception of when the hydraulic material, to which 1 percent of sodium carbonate was added to 100% by weight of cement components, was used and added to the component structure of our invention, as shown in section (2)(a), the mortar of the same mixing components as this invention showed about 10 percent greater initial strength than that of the mortar of this invention, as shown in the above chart. 
     
                                           TABLE 1                                 
__________________________________________________________________________
Temper-                                                                   
ature     Expansion Ratio (%)                                             
                      Compression Strength (Kg/cm.sup.2)                  
used.     Day Day Day          Day                                        
                                  Day                                     
                                     Day                                  
                                        Day                               
(C)       1   7   28  3 hr                                                
                         6 hr                                             
                            12 hr                                         
                               1  3  7  28                                
__________________________________________________________________________
Products                                                                  
      5   +0.129                                                          
              +0.129                                                      
                  +0.129                                                  
                       61                                                 
                         144                                              
                            195                                           
                               280                                        
                                  410                                     
                                     547                                  
                                        677                               
from this                                                                 
     20   +0.168                                                          
              +0.168                                                      
                  +0.168                                                  
                      155                                                 
                         216                                              
                            297                                           
                               446                                        
                                  579                                     
                                     645                                  
                                        716                               
Invention                                                                 
     30   +0.175                                                          
              +0.175                                                      
                  +0.175                                                  
                      160                                                 
                         244                                              
                            362                                           
                               522                                        
                                  634                                     
                                     691                                  
                                        722                               
Compared                                                                  
      5   +0.080                                                          
              +0.010                                                      
                  +0.010                                                  
                      -- -- --  14                                        
                                  253                                     
                                     480                                  
                                        619                               
Products                                                                  
     20   +0.014                                                          
              +0.014                                                      
                  +0.014                                                  
                      -- -- -- 212                                        
                                  397                                     
                                     545                                  
                                        649                               
     30   +0.015                                                          
              +0.015                                                      
                  +0.015                                                  
                      -- -- -- 396                                        
                                  430                                     
                                     576                                  
                                        664                               
__________________________________________________________________________