N-2,2-dimethyl-2-(2-hydroxy-alkylphenyl) heterocycles and stabilized compositions
The present invention is directed to compounds having alkylhydroxyphenol groups bonded to a heterocyclic nitrogen atom via a dimethylethyl group and stabilized polymer resins containing them. It is also directed to resins containing the novel stabilizers and co-stabilizing antioxidant sulfur-containing compounds. 
     The compounds of this invention contain alkylhydroxyphenyl group sbonded to a heterocyclic nitrogen atom through a dimethylethyl bridging group. At least one nitrogen atom is located between two carbonyl or thiocarbonyl groups in the ring. The hetercyclic nucleus of the present compound will contain one or more imidocarbonyl or imidothiocarbonyl groups. The compounds of the present invention are represented by the general formula: ##STR1## wherein R 1 , R 2 , R 3 , R 4  are independently selected from H or alkyl groups having 1-12 carbon stoms. X is oxygen or sulfur, and A is a bivlant molecular grouping having a chain of 2--3 atoms. The bivalent radical A may be a hydrocarbon radical, such as alkylene having 2-3C atoms or ortho phenylene, or may contain at least one C atom and one or two atoms selected from N, O, S in functional groups such as &gt;NH, &gt;C═S, and &gt;C═O as represented by the following divalent structural configurations: --C 2  H 2  --; --C 2  H 4  --; ##STR2## Heterocyclic compounds containing nitrogen atoms for substitution with alkylhydroxyphenyl groups include isocyanuric acid, uric acid, hydantoins, alloxan, uracil, thymine, barbituric acid, succinimide and maleimide and derivatives thereof, phthalimide and derivatives thereof. 
     A preferred class of compounds are derivatives of s-triazine-2,4,6-trione (isocyanurates), having the general formula: ##STR3## where Y is as defined above. 
     It is known that organic materials deteriorate upon exposure to air. The compounds of this invention are stabilizers for such organic materials normally subject to oxidative deterioration. Materials which are thus stabilized include synthetic organic polymer substances such as vinyl resins formed from the polymerization of vinyl halides or from the copolymerization of vinyl halides with unsaturated polymerizable compounds, for example vinylesters, β-unsaturated ketones, β-unsaturated aldehydes, and unsaturated hydrocarbons such as butadienes and styrene; poly-α-olefins such as polyethylene, polypropylene, polybutylene, and the like including copolymers of poly-α-olefins, polyurethanes and polyamides such as polyhexamethylene adipamide and polycaprolactam; polyesters such as polyethylene terephthalates; polycarbonate; polyacetals, polystyrene; polyethyleneoxide; polyisoprene; polybutadiene and copolymers such as those of high impact polystyrene containing copolymers of butadiene and styrene and those formed by the copolymerization of acrylonitrile, butadiene and/or styrene. 
     In general one or more of the stabilizers of the present invention are employed in amounts based on the total weight of the resin of from about 0.005 to about 5% by weight of the composition to be stabilized. A particularly advantageous range of the present stabilizers is from about 0.05% to about 2%. The preferred range is particularly effective in polyolefins such as polypropylene. 
     The compounds of the invention may be incorporated in the polymer substrate during the usual processing operations, for example, by milling or extrusion. The stabilized polymer can be fabricated into films, fibers, filaments, hollowspheres and the like. The heat stabilizing properties of these compounds advantageously stabilize the polymer against degradation during such processing at the high temperatures generally employed. 
     The stabilizers employed in this invention can also be used in combination with other stabilizers or additives. In general these co-stabilizers are represented by those having the following general formula: [ROCO(C m  H 2m )CH 2  ] 2  S wherein R is an alkyl group having from 6-24 carbon atoms; and m is an integer from 1-6. Especially useful co-stabilizers are di-lauryl-β-thiodipropionate and distearyl-β-thiodipropionate (DSTDP). These co-stabilizers are used in an amount ranging from 0.01-2% by weight of the organic material and preferably from 0.1-% by weight. 
     The stabilizers described in this invention can also be used in combination with di- and trialkyl and alkylphenyl phosphites such as tris-nonylphenyl phosphite, tris(2,4-di-tert-butylphenyl)phosphite, bis(2,4-di-t-butylphenyl)pentaerythritol disphosphite, tetrakis(2,4-di-t-butylphenyl)-4,4&#39;-biphenylene diphosphonite, and disearyl pentaerythritol disphosphite. 
     Other antioxidants, antiozonants, thermal stabilizers, ultraviolet light absorbers, coloring materials, dyes, pigments, metal chelating agents, etc., may also be used in compositions in combination with the stabilizers of the invention. 
     The compounds of the invention may be synthesized by addition of trimethallylisocyanurate (TMI), prepared according to a procedure outlined in U.S. Pat. No. 3,075,979, to the appropriate phenol in the presence of a suitable Lewis acid catalyst such as BF 3  ET 2  O. A preferred process involves reacting trimethallylisocyanurate with a 3-100 mol excess of an alkyl phenol such as 2,4-xylenol, p-cresol, 4-ethyl phenol, 4-sec butyl phenol, in the presence of BF 3  ET 2  O catalyst at 50-150° C. 
     Similar hindered hydroxyphenyl isocyanate derivatives are described in U.S. Pat. Nos. 3,531,483 and 3,723,427 wherein the hydroxyphenyl group is linked directly to the isocyanurate nitrogen through a methylene group at the meta and para positions. 
     The following examples serve to illustrate but not limit the invention wherein all proportions expressed by weight unless other specified. 
    
    
     EXAMPLE 1 
     1,3,5-Tris[2,2-dimethyl-2-(2-hydroxy-3,5-dimethylphenyl)ethyl]-s-triazine-2,4,6-(1H,3H,5H)trione. 
     Trimethylallyl isocyanurate (10 g, 0.035 mol) and 2,4-xylenol (25 g, 0.205 mol) are stirred under nitrogen in a 50 ml 3-neck flask. To this suspension is added 0.25 ml BF 3  ET 2 ). The reaction is heated at 100° C. for 16 hours. At this time, a white precipitate has formed. The product is separated from unreacted xylenol by filtration. The solids are washed with petroleum ether (BP 35°-50° C.) to yield 23 g white solid containing a small amount of 2,4-xylenol. The product can be further purified by dissolving in 150-200 ml acetone and pouring into 400 ml hexane. Concentration of the resulting solution to 300 ml results in isolation of 14.1 g (66%) of product, mp 210°-211° C. Calc. for C 39  H 51  N 3  O 6  : C, 71.19; H, 78.83; N, 6.39; 
     Found: C, 71.18; H, 7.95; N, 6.22. 
     EXAMPLE 2 
     1,3,5-Tris[2,2-dimethyl-2-(2-hydroxy-5-methylphenyl)ethyl]-s-triazine-2,4,6-(1H,3H,5H)trione. 
     TMI (10 g, 0.035 mol) and p-cresol (70 g, 0.66 mol) are stirred under N 2  in a 100 ml 3-neck flask. To this suspension is added 0.25 ml BF 3  ET 2  0. The reaction is heated for 16 hours at 100° C. The resulting white precipitate is recovered by filtration and washed with petroleum ether to give 21.4 g white solid, contaminated with p-cresol. The product can be purified by recrystallization from acetonitrile to give 16.8 g (80.3%) of product, mp 248°-250° C. Calc. for C 36  H 45  N 3  O 6  : C,70.21; H, 7.38; N, 6.82; 
     Found: C, 69.83; H, 7.44; N, 6.53. 
     EXAMPLE 3 
     1,3,5-Tris[2,2-dimethyl-2-(2-hydroxy-5-methyl-3-t-butylphenyl)ethyl]-s-triazine-2,4,6-(1H,3H,5H)trione. 
     To a 50 ml 3-neck round bottom flask is charged 2 g product of Example 2 in 10 ml nitrobenzene. 0.1 ml H 2  SO 4  is added and isobutylene is bubbled through the solution while warming to 90° C. After TLC shows the reaction to be complete, the mixture is diluted with an equal volume of ethyl acetate and washed 2 times with 50 ml 5% sodium bicarbonate. The organic layer is dried and concentrated in vacuo. The residue is purified by dry column chromatography (ET 2  O/hexane) to yield 1.3 g of product, mp 215°-217° C. Calc. for C 48  H 69  N 3  O 6  : C, 73.51; H, 8.89; N, 5.56; 
     Found: C,73.12; H, 8.94; N, 5.04. 
     EXAMPLE 4 
     1,3,5-Tris[2,2-dimethyl-2-(2-hydroxy-5-ethylphenyl)ethyl]-s-triazine-2,4,6-(1H,3H,5H)trione. 
     To a 100 ml 3-neck flask round bottom flask is charged 50 g 4-ethylphenol. The contents are warmed to 60° C. and 10 g TMI is added, followed by 0.2 ml BF 3  ET 2  O. The contents are heated to 100°-120° C. for 16 hours. The resulting solids are isolated by filtration, yielding 15.6 g of white solid containing unreacted ethylphenol. The solids are recrystallized from acetone to yield 4.9 g of product, mp 202°-205° C. Calc. for C 39  H 51  N 3  O 6  : C, 71.19; H, 4.83; N, 6.39; 
     Found: C, 71.01; H, 4.63; N, 6.27. 
     EXAMPLE 5 
     1,3,5-Tris[2,2-dimethyl-2-(2-hydroxy-5-sec-butylphenyl)ethyl]-s-triazine-2,4,6-(1H,3H,5H)trione. 
     To a 100 3-neck round bottom flask is charged 50 g 4-sec-butylphenol. The contents are heated to a molten state and 10 g TMI is added, followed by 0.2 ml BF 3  ET 2  O. The contents are warmed to 100°-120° C. for 16 hours. The excess 4-sec-butylphenol is removed by vacuum stripping. The pot residue is transferred to 350 ml hexane while stirring. The resulting white powder is collected by filtration yielding 19.6 g. white powder. The product can be purified by recrystallization from hexane/acetone to yield 6.1 g white solid, mp 185° C. 
     EXAMPLE 6 
     1,3,5-Tris[2,2-dimethyl-2-(2-hydroxy-5-ethyl-3-t-butylphenyl)ethyl]-s-triazine-2,4,6-(1H,3H,5H)trione. 
     To a 100 ml 3-neck round bottom flask is charged 8.9 g product of Example 4 in 30 ml toluene. To this is added 0.8 g p-toluenesulfonic acid. Isobutylene is passed through the solution while warming to 90° C. When TLC shows the reaction to be complete, the contents are diluted with an equal volume to ethyl acetate and washed 2 times with 50 ml of 5% sodium bicarbonate. The organic layer is dried, and stirpped under vacuu. The residue is purified by dry column chromatography to give 3.3 g white solids. Further purification by precipitation from a water/methanol solution gives 2.4 g of product. Calc. for C 57  H 87  N 3  O 6  : C, 75.19; H, 9.65; N, 4.62; 
     Found: C, 75.06; H, 9.55; N, 4.75. 
     EXAMPLE 7 
     1,3,5-Tris[2,2-dimethyl-2-(2-hydroxy-4-methylphenyl)ethyl]-s-triazine-2,4,6-(1H,3H,5H)trione. 
     To a 100 ml 3-neck round bottom flask is charged 62 g m-cresol and 10 g TMI. To this is added 0.2 ml BF 3  ET 2  O. The contents are stirred at 100° C. under N 2  for 16 hours. The contents are cooled and solids isolated by filtration and washing with petroleum ether to give 13.2 g of white solid. The product can be purified by recrystallization from acetonitrile to yield 7.9 g product. Calc. for C 36  H 45  N 3  O 6  : C, 70.21; H, 7.38; N, 6.82; 
     Found: C 70.03; H, 7.74; N, 6.89. 
     EXAMPLE 8 
     N,N&#39;-Bis 2,2-dimethyl-2-(2-hydroxy-3,5-dimethylphenyl)-ethyl-5,5-dimethylhydantoin. 
     (A) Prep of N,N&#39;-bismethallyl-5,5-dimethylhydantoin 
     In a 100 ml three necked flask is placed 10 g (0.055 mol) of N-methallyl-5,5-dimethylhydantoin in 100 ml DMF under nitrogen. The solution is cooled to 15° C. and 2.7 g of sodium hydride/mineral oil is added. The reaction is stirred for 2 hours at 15° C. and then warmed to 25°C. Methallyl chloride (5.1 g, 0.056 mol) is added dropwise over 10 minutes, keeping the temperature at 30° C. The reaction is stirred overnight, then poured into 200 ml water, extracted with 2 X 100 ml ether and dried over magnesium sulfate. After removing the ether in vacuo, the residue is distilled under vacuum (BP 100°-105°0 C. 0.3 mm Hg) to give 11.9 g N,N&#39;-bismethallyl-5,5-dimethylhydantoin. 
     (B) Prep of N,N&#39;-bis 2,2-dimethallyl-2-(2-hydroxy-3,5 dimethylphenyl)ethyl-5,5-dimethylhydantoin 
     In a 100 ml three-necked flask is placed 10 g N,N&#39;-bismethallyl hydantoin in 65 ml 2,4-xylenol. To this solution is added 0.5 ml BF 3  ETO 2  and the reaction is warmed to 100° C. for 16 hours. The excess xylenol is removed by distillation and the residue purified by dry column chromatography to give the product as a white solid, mp 150°-152° C. Calc. for C 29  H 40  N 2  O 4  : C, 72.45; H, 8.40; N, 5.83; 
     Found: C, 72.71; H, 8.46; N, 5.90. 
     EXAMPLE 9 
     1,3-Bis-2,2-dimethyl-2-(2-hydroxy-3,5-dimethylphenyl)ethylpyrimidine-2,4,6-(1H,3H,5H)trione 
     (A) Prep of bis-methallylbarbiturate 
     Barbituric acid (11.4 g, 0.1 mol) methallyl chloride (22.6 g, 0.25 mol), triethylamine (32 g, 0.32 mol) and o-dichlorobenzene (80 ml) are heated at reflux for 16 hours. The triethylamine hydrochloride is filtered off from the hot reaction mass and washed with ether. The ether washings are combined with the mother liquor, washed 2 times with 100 ml water, dried over magnesium sulfate and concentrated in vacuo to produce crude bis-methallyl barbiturate. 
     (B) Prep of 1,3-bis-2,2-dimethyl-2-(2-hydroxy-3,5-dimethylphenyl)ethylpyrimidine-2,4,6-(1H, 3H,5H)trione 
     Bis-methallyl barbiturate prepared in part A is treated with a ten fold excess of 2,4-xylenol in the presence of catalytic amount of BF 3  ETO 2 . The reaction contents are heated to 100° C. for 16 hours. The excess xylenol is removed by vacuum distillation and the product isolated by dry column chromatography. 
     EXAMPLE 10 
     The following data show the stabilization imparted to organic polymers on addition of compound in the examples. 
     This example shows the usefulness of the invention for stabilization of polypropylene. The stabilizers were incorporated into Profax 6301 polypropylene resin by solvent blending (methylene chloride) followed by extrusion at 200° C. Twenty-five mil plaques were prepared by compression molding at 6,000 psi and 188° C. Samples were tested in a forced draft oven at 150°. Failure was determined when the first signs of decomposition were observed. Tests were run in quadruplicate and an average value was determined. Results are shown in Table I. 
     
                       TABLE I                                                     
______________________________________                                    
                            Hours to                                      
Stabilizer    Concentration (%)                                           
                            Failure                                       
______________________________________                                    
none          --             24                                           
Ex. 1         0.10           510                                          
Ex. 2         0.10           126                                          
Ex. 3         0.10           672                                          
Ex. 4         0.10           150                                          
Ex. 5         0.10           156                                          
Ex. 6         0.10           72                                           
Ex. 7         0.10           90                                           
Ex. 1/DSTDP   0.1/0.25      2364                                          
Ex. 2/DSTDP   0.1/0.25      2412                                          
Ex. 3/DSTDP   0.1/0.25      1932                                          
Ex. 4/DSTDP   0.1/0.25      1242                                          
Ex. 5/DSTDP   0.1/0.25      1494                                          
Ex. 6/DSTDP   0.1/0.25      1140                                          
Ex. 7/DSTDP   0.1/0.25      1410                                          
______________________________________                                    
 
    
     COMPARISON EXAMPLE A 
     Tris(3,5-di-t-butyl-4-hydroxybenzyl)isocyanurate was incorporated in polypropylene as stabilizer by dissolving in acetone, suspending the polypropylene in the solvent solution and thereafter removing the acetone in a rotary evaporator. The polypropylene was hot milled (290°-300° F.) for 5 minutes and placed in a hot mold, skimmed to a thickness of 25 mils. The mold was closed and heated to 400° F. at 4000 psi for 2 minutes. Samples were aged in an air-circulating oven at 140° C. Samples were deemed to have failed at the first sign of crazing. 
     COMPARISON EXAMPLE B 
     (3,5-di-t-butyl-4-hydroxybenzyl) bis(3-t-butyl-5-methyl-2-hydroxybenzyl)isocyanurate was tested as described in Example A at 0.1% and in admixture with 0.2% β-dilaurylthiopropionate (DLTP) at 125° C. Samples were deemed to have failed as determined by carbonyl development. 
     COMPARISON EXAMPLE G 
     N,N&#39;,N&#34;tris(4-t-butyl-3-hydroxy-2,6-dimethylbenzyl)isocyanurate (Cyanox 1790) was tested as described in Example A at 1% and in admixture with 0.2% distearyl-β-thiodipropionate (DSTDP) in 50 mil and 25 mil polypropylene plaques at 150° C. The comparison of this commercially available stabilizer with the product of this invention indicates an improvement in stabilization over 350° C. at the 0.1% level and a 45% improvement with 0.2% DSTDP. 
     
                       TABLE II                                                    
______________________________________                                    
                       Hours to   Temperature                             
Stabilizer Concentration                                                  
                       Failure    ° C.                             
______________________________________                                    
Ex. A      0.1          120       140                                     
Ex. B      0.1          120       125                                     
Ex. B/DLTP 0.1/.2      1194       125                                     
Ex. C      0.1          144       150                                     
Ex. C/DSTDP                                                               
           0.1/.2      1488       150                                     
Ex. 1      0.1          520       150                                     
Ex. 1/DSTDP                                                               
           0.1/.2      2256       150                                     
______________________________________                                    
 
    
     EXAMPLE 11 
     This example shows the usefulness of the invention for stabilization of high impact polystyrene. The stabilizers were incorporated into high impact polystyrene by milling at 188° C. Twenty mil plaques were prepared by compression molding at 6,000 psi and 188° C. Samples were tested in a forced draft oven at 90° C. Failure was determined when cracking was observed after flexing the plaque over a one-inch mandrel. Tests were run in quadruplicate and an average value was determined. Results are shown in Table III. 
     
                       TABLE III                                                   
______________________________________                                    
                           Hours to                                       
Stabilizer   Concentration (%)                                            
                           Failure                                        
______________________________________                                    
none         --             48                                            
Ex. 1        0.10          192                                            
Ex. 2        0.10           72                                            
Ex. 4        0.10          186                                            
Ex. 5        0.10          246                                            
______________________________________