Process for producing blocked, urea group-containing polyisocyanates
BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     The invention relates to a process for manufacturing blocked, urea group-containing polyisocyanates from semi-blocked polyisocyanates and polyamines. 
     2. Discussion of Background 
     The reaction of polyisocyanates with polyamines is so violent that &#34;it has priority over all other isocyanate reactions&#34; (cf. Houben-Weyl, Methoden der Organischen Chemie. Vol. XIII, p. 132). This high reactivity may also be the reason for the fact that for a long time little research has been done on the direct reaction between polyamines and polyisocyanates to the corresponding urea derivatives. 
     Of course, in principle symmetrical urea derivatives can be obtained through direct conversion of polyisocyanates and water according to the process designated in DE-OS No. 23 41 065, but with this process one must accept the fact that gaseous reaction products, which must be carefully removed, are produced during the formation of urea. Furthermore, the reaction between water and isocyanate has the drawback that there is limited variability and in using the stoichiometric method, oligomeric urea will form, leaving monomeric polyisocyanate. In addition to this, DE-OS No. 23 41 065 teaches that frequently an excess of polyisocyanate-isophorone-diisocyanate is added or that due to viscosity reasons, solvents must be used. 
     Another disadvantage is that the high reactivity of the reaction between a polyamine and polyisocyanate results in a reaction that can be controlled only with difficulty, and results in a wide range of molecular weights. 
     This reaction is also observed in the preparation of biuret polyisocyanates and represents there an undesired secondary reaction (cf. DE-OS No. 22 61 065, OS No. 26 09 995 and U.S. Pat. No. 3,903,126). 
     Finally, in the DE-OS No. 31 43 060 a process for preparing blocked, urea group-containing isophoronediisocyanate adducts is described. Such compounds are obtained by converting 3-isocyanatomethyl-3,5,5-trimethylcyclohexylisocyanate, also called isophorone diisocyanate (IPDI), that are partially blocked with epsilon-caprolactam, and diamines having two sterically feasible primary and/or secondary amino nitrogens. The reaction is performed neat and, for viscosity reasons, must occur above 130° C. and, as demonstrated in the examples, even at 160° C. If the partial blocking of IPDI is carried out according to the directives in DE-OS No. 31 43 060, then as the reaction equation shows and it would be desirable, ##STR1## not only the partially-blocked IPDI adduct but also completely blocked IPDI is obtained while retaining from 15 to 17% by weight non-reacted, thus unblocked monomeric IPDI. This high monomer content has a very grave disadvantage, since during the reaction with diamines, it is responsible for the formation of undesired polymeric urea compounds. 
     According to DE-OS No. 31 43 60, further reactions of the partially blocked polyisocyanates with polyamines are unsuitable for producing urea compounds that are interesting for polyurethane chemistry. 
     SUMMARY OF THE INVENTION 
     Therefore, one object of the present invention is a process for producing blocked urea group-containing polyisocyanates from partially-blocked polyisocyanates and polyamines. 
     This and other objects which will become apparent from the following specification have been achieved by the process for the production of blocked urea group-containing polyisocyanates from a partially blocked polyisocyanate and a polyamine, comprising the steps of: 
     (i) reacting a partially blocked polyisocyanate, said polyisocyanate being made substantially free of monomeric polyisocyanate, by vacuum thin layers evaporation with a primary polyamine, secondary polyamine, or mixtures thereof, in relative proportions such that the ratio of isocyanate groups to amino groups is in the range from about 1:1 to 1.3:1, and 
     (ii) isolating said urea group-containing polyisocyanate by wherein the vacuum boiling point of said polyisocyanate is lower than the deblocking temperature of said urea group-containing polyisocyanate. 
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     Formulas I and II illustrate the type of polyamines that may be used in the present process: ##STR2## in which R is --(CH 2 )-- 2-36 , or C 2-36  branched alkyl, ##STR3## in which R 1  is the same as or different from R 3  =H, straight chain or branched alkyl, cycloalkyl-, aryl-, aralkyl, R 2  is --CH 2  -- or if desired, a branched alkyl group, in which the polyamine contains from 2 to 36 carbon atoms, and m=2 to 8, X=0 to 6, and n=2 to 8. 
     The polyisocyanates to be added according to the invention are described for example in &#34;Methoden der Organischen Chemie,&#34; Houben-Weyl, Vol. 14/2, 4th edition, Georg Thieme Verlag Stuttgart, 1963, pp. 61-70 and in W. Siefken, Liebigs Ann. Chem. 562, pp. 75-136. 
     By using a partially blocked polyisocyanate containing 6.5% by weight of monomeric polyisocyanate, preferably up to 3.5% by weight and in particular up to 2.5% by weight, it is possible to obtain an additional reaction. These partially blocked polyisocyanates may be produced by reacting a large excess of polyisocyanate (5 to 20 mole) with the blocking agent (1 mole) at temperatures ranging from 50° C. to 130° C., preferably from 70° C. to 100° C., and subsequently separating the excess polyisocyanate by means of conventional thin-layer evaporation. This process is disclosed in U.S. application Ser. No. 07/243,605, filed Sept. 13, 1988 incorporated herein by reference. 
     Only those polyisocyanates whose boiling points under vacuum are below the deblocking temperature of the blocking agent added are suitable and thus those which can be separated by means of thin-layer evaporation. 
     Particularly preferred aliphatic, (cyclo)aliphatic and aromatic polyisocyanates are those which are technically readily accessible such as 1,6-hexamethylene diisocyanate (HDI), 2,2,4,(2,4,4)-trimethylhexamethylene diisocyanate (TMDI), 2-methylpentane-1,5-diisocyanate (DI51), and 2,4- or 2,6-toluylene diisocyanate, and in particular 3-isocyanatomethyl-3,5,5-trimethylcyclohexylisocyanate (IPDI) and their mixtures of isomers. 
     For manufacturing polyisocyanate-urea-adducts according to the invention, polyamines having primary and/or secondary amino groups are suitable. They preferably have from 2 to 36 carbon atoms and can be aliphatic or have one or more cycloaliphatic, aromatic or heterocyclic rings having from 5 to 8 substituents. The polyamines that can be added can also carry tertiary amino groups. Non-limiting examples of suitable polyamines include: 
     (i) non-branched primary alkylene diamines, such as ethylene diamine, trimethylene diamine, tetramethylene diamine, hexamethylene diamine, octamethylene diamine, dodecamethylene diamine and the C 36  -diamine, 
     (ii) branched primary alkylene diamines, such as 2-methyl-pentamethylene diamine, 2,2,4(2,4,4)-trimethylhexamethylene diamine and 5-methylnonamethylene diamine, 
     (iii) cycloaliphatic primary diamines such as 1,4(1,2)-diaminocyclohexane, 2,4(2,6)-diamino-1-methylcyclohexane, 4,4&#39;-diaminodicyclohexylmethane, 4,4&#39;-diamino-3,3&#39;-dimethyldicyclohexylmethane, and 4,4&#39;-diamino-3,3&#39;5,5&#39;-tetramethyldicyclohexylmethane, 
     (iv) cycloaliphatic/aliphatic primary or secondary diamines, such as N-cyclohexyl-1,3-propylene diamine, bis-(1,4-aminomethyl)-cyclohexane and 3-aminomethyl-3,5,5-trimethylcyclohexylamine (isophorone diamine IPD), 
     (v) aliphatic primary and secondary polyamines such as diethylene triamine, triethylene tetramine, tetraethylene pentamine, pentaethylene hexamine, dipropylene triamine, dihexamethylene triamine, dioctamethylene triamine, and bis-(3-aminopropyl)ethylene diamine, 
     (vi) aromatic primary diamines such as 3,5-diethyl-toluylene diamine, 2,4(2,6)-toluylene diamine, 1,4-diamino-2,3,5,6-tetramethylbenzene and 4,4-diaminodiphenylmethane, 
     (vii) aliphatic secondary diamines such as 1,1,6,6-tetraisopropyl-2,5-diazahexane and N,N&#39;-diisobutyl isophorone diamine, 
     (viii) heterocyclic diamines such as 4-(3-aminopropyl-amino)- 2,2,6,6-tetramethylpiperidine and 4[(bis-3-aminopropyl)amino]-2,2,6,6-tetramethylpiperidine, 
     (ix) and their mixtures. 
     Melamine and water may also be used. 
     The addition of the aforementioned heterocyclic compounds is of a great interest since the manufacture of permanent ultraviolet-stable plastics, and in particular paint systems, are then feasible. In this method they function not only as an additive but rather they are incorporated directly into the macromolecule. 
     According to the invention, suitable blocking agents are those which deblock at curing conditions, i.e. between 140° and 220° C. This includes alcohols, e.g. methanol, ethanol, ispropanol, cyclohexanol; oximes such as acetone oxime, methylisobutyl ketoxime; mercaptans; lactams, for example lauryl lactam, acetoacetic ester, malonic ester, and especially epsilon-caprolactam and methyl ethyl ketoxime (cf. &#34;Methoden der Organischen Chemie,&#34; Houben-Weyl, Vol. 14/2, 4th edition, Georg Thieme Verlag Stuttgart, 1963, p. 61 ff.). 
     In the process of the invention, the curing agent is manufactured in the solvent and in particular such that the partially blocked polyisocyanate is present in the solvent and the polyamine is added dropwise either neat or also dissolved in a solvent. Suitable solvents are, on the one hand, those that can be readily removed such as toluene, xylene, cyclohexane, special benzene with less than 1% by vol. of aromatics (a mixture of mainly aliphatic, cycloaliphatic and aromatic hydrocarbons with a boiling point between 60°-96° C.), acetic ester and acetone, in order to isolate the polyisocyanate-urea-adducts of the invention; on the other hand, such solvents as toluene, xylene, SOLVESSO® 100 and 150 (mixture of aromatics produced by Esso), tetraline, cumene, methylisobutyl- and diisobutyl ketone, hexyl acetate, butyl acetate, ethylene glycol diacetate (EGA), methoxypropyl acetate (MOP-acetate), butylene glycol diacetate etc., which in industry are added for solvent-containing paint systems. 
     The aforementioned compounds can also be used as mixtures. The concentrations of polyisocyanate-urea-adducts can vary widely. Concentrations ranging from 30 to 70% by weight have proven to be advantageous. 
     According to the invention, the reaction takes place between room temperature and 80° C., preferably between room temperature and 70° C. Following successful addition of polyamine it is preferable to heat the reaction mixture to, if desired, a temperature ranging from 100° to 120° C. If the reaction product is to be liberated from the solvent, this can be done by simply applying a vacuum. Melt extrusion in an evaporation screw is especially suitable for removing the solvent. 
     The use of special benzenes having less than 1% by vol. of aromatics or cyclohexane as solvent has proven to be an especially advantageous process for manufacturing permanent, blocked polyisocyanate-urea-adducts according to the invention. In this process the reaction is carried out at room temperature, and in particular such that the partially-blocked polyisocyanate is dissolved in special benzene or cyclohexane and with intensive stirring, the polyamine is added dropwise in such a manner that the reaction temperature does not exceed 70° C. The reaction product precipitates out during the dropwise addition. Following completion of the amine addition, stirring is continued from 30 to 45 minutes and the solvent is subsequently removed. 
     In the conversion process of the invention, the reaction partners--polyisocyanate and polyamine--are added in such proportions as to give a ratio of isocyanate groups to amino groups of 1-1.3:1, preferably one isocyanate group per primary and/or secondary amino group. In general, the adducts of the invention have an NCO content ranging from 4 to 20%, preferably from 6 to 15% by weight. The free isocyanate content ranges from about 0.7% by weight to 5% by weight. The polyisocyanate addition products have a melting range from 90° to 210° C. They are especially suitable as curing agents for highly functional compounds having Zerewitinoff active hydrogen atoms. Combined with such compounds having Zerewitinoff active hydrogen atoms, above 140° C., preferably from 180° to 220° C., the polyaddition products result in systems that cure to high-grade plastics. Probably the most important application area for such systems is their use as linkers for PUR powder paint and solvent-containing single component-PUR-varnish. 
     The compounds of the invention are suitable as intermediate products for manufacturing plastics, in particular paints. Therefore, they are especially valuable because they also facilitate, in a simple manner, the manufacture of PUR varnish having a reduced degree of gloss. 
     Other features of the invention will become apparent according to the following descriptions of the exemplary embodiments which are given for illustration of the invention and are not intended to be limiting thereof. 
    
    
     EXAMPLES 
     Example 1 
     A. Preparation of partially blocked polyisocyanates General preparation 
     One mole of blocking agent was added in proportions of from 5 to 20 moles of polyisocyanate at temperatures ranging from 70° to 80° C. with stirring. After the completed addition of the blocking agent, the reaction mixture was then heated at 100° C. for another hour and subsequently the non-reacted polyisocyanate was removed via thin-layer evaporation at temperatures ranging from 90° to 140° C. and at 0.0133 mbar. The chemical and physical characteristic values of the reaction product (=residue) were determined and compiled in the following table. 
     
         __________________________________________________________________________
Partially blocked polyisocyanates                                         
Starting Materials                                                        
                 NCO content                                              
                         Polyisocyanate                                   
Examples                                                                  
     polyiso-                                                             
          blocking                                                        
                 in % by weight                                           
                         monomer Viscosity in mPa&#39;s                       
A    cyanate                                                              
          agent  free                                                     
                     total                                                
                         % by wt.                                         
                                 25° C.                            
                                      30° C.                       
                                          40° C.                   
                                              50° C.               
                                                  70° C.           
__________________________________________________________________________
1    IPDI caprolactam                                                     
                 12.4                                                     
                     24.8                                                 
                         &lt;1.0    1250000                                  
                                      410000                              
                                          63500                           
                                              13700                       
                                                  1250                    
2    IPDI caprolactam                                                     
                 11.5                                                     
                     24.5                                                 
                         2.2     1145000                                  
                                      397000                              
                                          61250                           
                                              12530                       
                                                  1070                    
3    IPDI caprolactam                                                     
                 11.6                                                     
                     24.4                                                 
                         3.5     1120000                                  
                                      360000                              
                                          59500                           
                                              11500                       
                                                  980                     
4    IPDI caprolactam                                                     
                 11.8                                                     
                     24.5                                                 
                         4.6     660000                                   
                                      194000                              
                                          34000                           
                                              8550                        
                                                  680                     
5    IPDI caprolactam                                                     
                 11.85                                                    
                     24.6                                                 
                         6.4     451000                                   
                                      101000                              
                                          22000                           
                                              4500                        
                                                  450                     
6    IPDI MEK-oxime                                                       
                 12.8                                                     
                     26.5                                                 
                         2.8     571000                                   
                                      152000                              
                                          27500                           
                                              5500                        
                                                  420                     
7    HDI  caprolactam                                                     
                 15.3                                                     
                     29.4                                                 
                         0.5     100  80  50  30  &lt;30                     
8    HDI  MEK-oxime                                                       
                 15.8                                                     
                     32.4                                                 
                         2.5     70   60  50  30  &lt;30                     
9    DI51 caprolactam                                                     
                 14.8                                                     
                     29.3                                                 
                         0.7     160  120 60  45  &lt;30                     
10   DI51 MEK-oxime                                                       
                 15.7                                                     
                     31.5                                                 
                         0.8     190  150 80  60  30                      
11   DI51 MEK-oxime                                                       
                 16.5                                                     
                     32.9                                                 
                         7.5     110  70  40  &lt;30 &lt;30                     
__________________________________________________________________________
 
    
     B. Preparation of blocked polyisocyanate-urea-adducts according to the invention 
     With respect to the free NCO content, the equivalent quantities of a 50 to 70% solution in toulene of a diamine or polyamine or their mixtures were added in such a manner to a 50 to 70% solution in toluene of a partially blocked polyisocyanate, with intensive stirring, at a temperature ranging from 55° to 65° C. such that the reaction temperature does not exceed 70° C. Following completion of amine addition, the reaction mixture was then heated for a period ranging from 30 to 45 minutes. During this time, the temperature was slowly increased to from 100° to 120° C. Then the toluene was removed from the reaction product under vacuum at 0.133 mbar. The following table lists the chemical and physical characteristics of the reaction products. 
     (a) IPDI-urea-adducts according to A 2 and amine component 
     (b) IPDI-urea-adducts according to A 1 and amine component 
     (c) HDI-urea-adduct according to A 7 and amine component 
     (d) DI51-urea-adducts according to A 9 and amine component 
     (e) IPDI-urea-adducts according to A 3, A 4, A 5 and amine component 
     (f) IPDI-urea-adducts according to A 2 in such proportions as to give a ratio of NCO to NH 2  ranging from 1.05 to 1.3:1 and amine component 
     (g) IPDI-urea-adducts according to A 2 and amine component, prepared at a temperature ranging from 40° and 110° C. 
     (h) IPDI-urea-adducts according to A 2 and amine component, prepared in acetone or acetic ester 
     (i) IPDI-urea-adducts according to A 2 and water 
     (j) IPDI-urea-adducts according to A 2 and amine component, prepared in special benzene and cyclohexane 
     
         __________________________________________________________________________
                        NCO content    glass transition                   
                        (% by weight)                                     
                                melting range                             
                                       temperature                        
       amine component  latent                                            
                            Free                                          
                                °C.                                
                                       (DTA) °C.                   
__________________________________________________________________________
Example B a                                                               
 1     1,6-hexamethylene diamine                                          
                        10.8                                              
                            0.15                                          
                                120-122                                   
                                       51-66                              
 2     1,8-octamethylene diamine                                          
                        10.5                                              
                            0.5 101-103                                   
                                       41-61                              
 3     1,12-dodecamethylene diamine                                       
                        9.6 0.3 93-96  32-56                              
 4     2-methyl-pentamethylene-                                           
                        10.5                                              
                            0   106-108                                   
                                       35-47                              
       1,5-diamine                                                        
 5     2,2,4(2,4,4)-trimethyl-                                            
                        10.0                                              
                            0   107-109                                   
                                       30-44                              
       hexamethylene 1,6-diamine (TMD)                                    
 6     1,4-diaminocyclohexane                                             
                        10.3                                              
                            0.3 120-130                                   
                                       53-85                              
 7     4,4&#39;-diamino-dicyclohexyl-                                         
                        9.9 0.25                                          
                                148-150                                   
                                       39-58                              
       methane - solid                                                    
 8     4,4&#39;-diamino-dicyclohexyl-                                         
                        10.0                                              
                            0.3 146-149                                   
                                       40-57                              
       methane - liquid                                                   
 9     3,3&#39;-dimethyl-4,4&#39;-diamino-                                        
                        9.3 0   149-155                                   
                                       37-85                              
       dicyclohexylmethane                                                
10     N-cyclohexyl-propylene                                             
                        10.8                                              
                            0.3 142-145                                   
                                       43-80                              
       1,3-diamine                                                        
11     bis-(1,4-aminomethyl)-                                             
                        10.9                                              
                            0.5 133-140                                   
                                       50-80                              
       cyclohexane                                                        
12     isophorone diamine (IPD)                                           
                        10.5                                              
                            0.1 160-165                                   
                                       60-87                              
13     90 parts by weight IPD                                             
                        9.9 0   146-157                                   
                                       49-72                              
       10 parts by weight TMD                                             
14     70 parts by weight IPD                                             
                        9.9 0   138-148                                   
                                       38-61                              
       30 parts by weight TMD                                             
15     50 parts by weight IPD                                             
                        10.2                                              
                            0.1 125-127                                   
                                       34-58                              
       50 parts by weight TMD                                             
16     diethylene triamine                                                
                        11.1                                              
                            0.4 162-165                                   
                                       45-88                              
17     triethylene tetramine                                              
                        11.5                                              
                            0.5 140-145                                   
                                       40-80                              
18     tetraethylene pentamine                                            
                        12.0                                              
                            0.3 120-123                                   
                                       40-75                              
19     pentamethylene hexamine                                            
                        12.1                                              
                            0.4 113-115                                   
                                       36-70                              
20     dipropylene triamine                                               
                        11.8                                              
                            0.4 153-155                                   
                                       40-65                              
21     bis-(3-aminopropyl)-                                               
                        11.6                                              
                            0.5 152-155                                   
                                       42-68                              
       ethylene diamine                                                   
22     3,5-diethyl-toluylene-                                             
                        10  0   203-205                                   
                                       70-80                              
       diamine                                                            
23     1,4-diamino-2,3,5,6-                                               
                        10  0   175-177                                   
                                       55-72                              
       tetramethyl benzene                                                
24     4,4&#39;-diaminodiphenyl-                                              
                        10  0.3 178-182                                   
                                       58-74                              
       methane                                                            
25     1,1,6,6-tetraisopropyl-                                            
                        9.7 0.45                                          
                                120-122                                   
                                       47-65                              
       2,5-diazahexane                                                    
26     N,N&#39;-diisobutyl-isophorone-                                        
                        9.4 0.3 130-132                                   
                                       45-65                              
       diamine                                                            
27     4-(3-aminopropyl-amino)-                                           
                        10.1                                              
                            0.5 125-129                                   
                                       35-49                              
       2,2,6,6-tetramethylpiperidine                                      
28     4-[(bis-3-aminopropyl)-amino]-                                     
                        9.6 0.5 138-140                                   
                                       40-53                              
       2,2,6,6-tetramethylpiperidine                                      
29     melamine         10.3                                              
                            0.5 197-200                                   
                                       75-90                              
30     N-(3-aminopropyl)glucamine                                         
                        9.5 0   124-126                                   
                                       33-95                              
Example B b                                                               
1      4,4&#39;-diamino-dicyclohexyl-                                         
                        10.2                                              
                            0.1 144-147                                   
                                       41-59                              
       methane - liquid                                                   
2      bis-(1,4-aminomethyl)cyclo-                                        
                        10.8                                              
                            0.3 136-141                                   
                                       53-75                              
       hexane                                                             
Example B c                                                               
1      4,4&#39;-diaminodicyclohexyl-                                          
                        10.7                                              
                            0   124-126                                   
                                       26-52                              
       methane - liquid                                                   
Example B d                                                               
1      4,4&#39;-diaminodicyclohexyl-                                          
                        10.6                                              
                            0.1 105-111                                   
                                       24-52                              
       methane - liquid                                                   
__________________________________________________________________________
 
    
     Example B e 
     According to the general preparation B, the partially blocked IPDI adducts according to A 3, A 4 and A 5 underwent a reaction with 4,4&#39;-diaminodicyclohexylmethane. The following table shows the chemical and physical characteristics of the product: 
     
         ______________________________________                                    
Exam-            NCO content                                              
                            melting                                       
                                   glass transition                       
ple   IPDI adduct                                                         
                 % by weight                                              
                            range  temperature                            
B e   according to                                                        
                 latent  free °C.                                  
                                     (DTA) °C.                     
______________________________________                                    
1     A 3        10.3    0.3  148-150                                     
                                     38-72                                
2     A 4        10.2    0.1  155-161                                     
                                     37-78                                
3     A 5        10.25   0.2  155-157                                     
                                     40-96                                
______________________________________                                    
 
    
     Example B f 
     According to the general preparation B, the partially blocked IPDI adducts according to A 2, were reacted with 4,4&#39;-diaminodicyclohexylamethane, not in equivalent proportions, but rather in such proportions as to give a ratio of NCO to amine of X:1. The following table shows the chemical and physical characteristics for the product: 
     
         ______________________________________                                    
              NCO content                                                 
                         melting                                          
                                glass transition                          
Example       % by weight                                                 
                         range  temperature (DTA)                         
B f    X      latent  free °C.                                     
                                  °C.                              
______________________________________                                    
1      1.05   9.9     0.4  145-148                                        
                                  35-58                                   
2      1.1    10.7    0.8  140-142                                        
                                  33-59                                   
3      1.2    11.5    1.4  138-140                                        
                                  35-58                                   
4      1.3    12.0    1.95 131-136                                        
                                  33-55                                   
______________________________________                                    
 
    
     Example B g 
     According to the general preparation for the blocked polyisocyanate-urea-adducts, at X °C., the partially blocked IPDI adducts according to Example A 2, underwent a reaction with 4,4&#39;-diaminodicyclohexylmethane and in the following table the chemical and physical characteristics of the inventive and comparative reaction products are shown. 
     
         ______________________________________                                    
               Reaction   NCO content                                     
                                   glass transition                       
Example        Temperature                                                
                          % by weight                                     
                                   temperature in                         
B g            X °C.                                               
                          latent                                          
                                free °C. (DTA)                     
______________________________________                                    
1              40         10.27 0.2  36-59                                
2              50         10.25 0.3  38-58                                
3        I     60         10.1  0.2  40-57                                
4              70         10.3  0.25 40-59                                
5              80         10.0  0.15 40-56                                
6              90         10.3  0.1  28-81                                
7        II    100        10.2  0    19-90                                
8              110        10.15 0.2  17-125                               
______________________________________                                    
 Remarks:                                                                 
 I = invention                                                            
 II = comparison                                                          
 
    
     Example B h1 
     With respect to the free NCO content, 210 parts by weight of 4,4&#39;-diamino- dicyclohexylmethane were added to 730 parts by weight of a partially blocked IPDI of a A 2, dissolved in 506 parts by weight of acetone with intensive stirring, at a temperature ranging from 55° to 65° C. in such a manner that the reaction temperature does not exceed 65° C. Following completion of diamine addition, the reaction mixture was then stirred for a period ranging from 30 to 45 minutes urea NCO content has dropped to 0.5% by weight. Then the acetone was removed from reaction product under a vacuum at 0.133 mbar. The reaction product had the following chemical and physical characteristics: 
     NCO content (latent): 10.3% by weight 
     NCO content (free): 0.3% by weight 
     melting range glass transition: 147°-149° C. 
     temperature (DTA) 40°-59° C. 
     Example B h2 
     According to Example B h1, the reaction was carried out in acetic ester. The reaction product had the following chemical and physical characteristics: 
     NCO content (latent): 10.4% by weight 
     NCO content (free): 0% by weight 
     melting range glass transition: 146°-148° C. 
     temperature (DTA) 46°-59° C. 
     EXAMPLE B i 
     With respect to the free NCO content, Z parts by weight of water were added to X parts by weight of a partially blocked IPDI of A 2 and 0.15% by weight of DBTL, with respect to the partially blocked IPDI added, dissolved in Y parts by weight of acetone with intensive stirring, at a temperature ranging from 50° to 60° C. in such a manner that the reaction temperature does not exceed 65° C. Following completion of water addition, the reaction mixture was then heated with stirring until the calculated CO 2  quantity had been evolved. Then the reaction was analyzed by volumetric analysis of NCO by titration and the acetone was removed from the reaction product under a vacuum at 0.133 mbar. The quantities and the corresponding chemical and physical characteristics were compiled in the following table: 
     
         __________________________________________________________________________
                     NCO content                                          
                            melting                                       
Example                                                                   
      in % by wt.    range  DTA*                                          
B i   X  Y  Z  CO.sub.2 (l)                                               
                     total                                                
                         free                                             
                            °C.                                    
                                 °C.                               
__________________________________________________________________________
1     359                                                                 
         146                                                              
            9  11.3-12                                                    
                     12.5                                                 
                         0.3                                              
                            105-107                                       
                                 45-65                                    
2     185                                                                 
         120                                                              
            3.45                                                          
               4.3-4.6                                                    
                     15.2                                                 
                         2.1                                              
                            94-96                                         
                                 38-56                                    
__________________________________________________________________________
 *glass transition temperature                                            
 
    
     Example B j 
     With respect to the free NCO content, the calculated quantity of amine component was added dropwise to 730 parts by weight of a partially blocked IPDI of A 2, dissolved in from 500 to 550 parts by weight of special benzene (contains 3% by vol. of aromatics) or cyclohexane with intensive stirring, at room temperature in such a manner that the reaction temperature does not exceed 70° C. During the addition of diamine the polyisocyanate-urea-adduct precipitated out. Following completion of the diamine addition, the reaction mixture was then stirred for a period ranging from 30 to 45 minutes and then following volumetric analysis of NCO by titration, freed of the solvent. The following table gives the chemical and physical characteristics of the product: 
     
         __________________________________________________________________________
                NCO content                                               
                       melting                                            
                            glass transition                              
Example                                                                   
     amine      % by weight                                               
                       range                                              
                            temperature (DTA)                             
B j  component  total                                                     
                    free                                                  
                       °C.                                         
                            °C.                                    
__________________________________________________________________________
Ratio of NCO to amine = 1:1                                               
1    4-4&#39;-diaminodi-                                                      
                9.5 0.4                                                   
                       146-149                                            
                            36-63                                         
     cyclohexylmethane-                                                   
     liquid                                                               
2    bis-(1,4-aminomethyl-                                                
                10.2                                                      
                    0.4                                                   
                       134-136                                            
                            45-95                                         
     cyclohexane                                                          
3    isophorone diamine                                                   
                10.0                                                      
                    0.4                                                   
                       154-159                                            
                            56-84                                         
4    pentaethylene-                                                       
                11.3                                                      
                    0  123-127                                            
                            37-65                                         
     hexane                                                               
Ratio of NCO to amine 1.1:1.2:1.3:1                                       
5    4,4&#39;-diaminodi-                                                      
                10.9                                                      
                    0.8                                                   
                       137-141                                            
                            37-60                                         
     cyclohexylmethane                                                    
6    4,4&#39;-diaminodi-                                                      
                11.2                                                      
                    1.5                                                   
                       140-141                                            
                            33-59                                         
     cyclohexylmethane                                                    
7    4,4&#39;-diaminodi-                                                      
                12.1                                                      
                    1.9                                                   
                       133-135                                            
                            32-56                                         
     cyclohexylmethane                                                    
__________________________________________________________________________
 
    
     C. Preparation of blocked polyisocyanate-urea-adducts according to the invention in conventional paint solvents 
     With respect to the free NCO content, the equivalent quantities (dissolved or neat) of a diamine or polyamine or their mixtures were added to a from 30 to 50% conventional paint solvent solution of a partially blocked polyisocyanate with intensive stirring, at a temperature ranging from 50° to 60° C. in such a manner that the reaction temperature does not exceed 70° C. Following completion of amine addition, the reaction mixture was then heated urea NCO content has dropped to zero. The following table lists the chemical and physical characteristics of the product: 
     
         __________________________________________________________________________
                concentration  NCO content                                
                                      Viscosity                           
Example         of urea        (latent)                                   
                                      DIN-4-cup                           
                                            mPa&#39;s                         
C a  amine component                                                      
                adduct solvent % by weight                                
                                      20° C. (sec)                 
                                            25° C.                 
__________________________________________________________________________
1    2,2,4(2,4,4)-trimethyl-                                              
                40     S* 100  4.2    116   330                           
     hexamethylene-1,6-                                                   
                50     E*/S                                               
                          100                                             
                             1:2                                          
                               5.3    345   1,040                         
     diamine (TMD)                                                        
2    pentaethylene-                                                       
                40     S  100  4.6     32   90                            
     hexamine (PEHA)                                                      
                50     E/S                                                
                          100                                             
                             1:2                                          
                               5.8    200   644                           
3    bis-(1,4-aminomethyl)-                                               
                40     E/S                                                
                          100                                             
                             1:2                                          
                               4.3    --    7,000                         
     cyclohexane (HXDA)                                                   
4    isophorone diamine                                                   
                30     E/S                                                
                          100                                             
                             1:2                                          
                               3.1    151   410                           
                40     E/S                                                
                          100                                             
                             1:2                                          
                               4.1    --    15,600                        
5    HXDA/PEHA 2:1                                                        
                30     E/S                                                
                          100                                             
                             1:2                                          
                               3.4    190   489                           
                40     E/S                                                
                          100                                             
                             1:2                                          
                               4.2    190   490                           
6    IPD/PEHA 2:1                                                         
                40     E/S                                                
                          100                                             
                             1:2                                          
                               4.2    166   472                           
7    HXDA/TMD 1:1                                                         
                30     E/S                                                
                          100                                             
                             1:2                                          
                               3.1     72   177                           
                40     E/S                                                
                          100                                             
                             1:2                                          
                               4.1    754   2,086                         
__________________________________________________________________________
 S* = SOLVESSO ®,                                                     
 E* = EGA                                                                 
 
    
     Example C b 
     With respect to the free NCO content, Z parts by weight of water were added to X parts by weight of a partially blocked IPDI of example A 1 and 0.15% by weight of DBTL, with respect to the partially blocked IPDI added, dissolved in Y parts by weight of conventional paint solvent with intensive stirring, at a temperature ranging from 55° to 60° C. in such a manner that the reaction temperature does not exceed 65° C. Following completion of water addition, the reaction mixture was then heated with stirring urea calculated CO 2  quantity has been evolved. The reaction was then analyzed via volumetric analysis of NCO by titration. The quantities and the corresponding chemical and physical characteristics were listed in the following table: 
     
         ______________________________________                                    
                                    time of                               
Exam-              NCO content                                            
                           outflow in                                     
ple   CO.sub.2     in % by wt.                                            
                           DIN-4-cup                                      
C b   X      Y      Z    (l)   total free 20° C. in                
______________________________________                                    
                                          sec                             
1     185    120    3.45 4.2-4.6                                          
                                9.4  1.6  215                             
2     183.3  120    2.3  2.8-3.0                                          
                               10.9  3.4  50                              
3     181.6  120    1.15 4.2-4.5                                          
                               12.8  5.0  20                              
______________________________________                                    
 
    
     D. I. Comparison examples - General preparation (partially blocked polyisocyanates without thin-layer evaporation) 
     One mole of blocking agent was added in such a manner to one mole of polyisocyanate at a temperature ranging from 90° to 110° that the temperature of the reaction mixture does not exceed 120° C. After completion of the addition of blocking agent, the reaction mixture was heated urea NCO content of the reaction mixture has reached the calculated value. The following table shows the chemical and physical characteristics of the reaction products: 
     
         __________________________________________________________________________
                 NCO content                                              
                        Polyisocyanate                                    
Example                                                                   
     polyiso-                                                             
          blocking                                                        
                 % by weight                                              
                        monomer Viscosity in mPa&#39;s at °C.          
DI   cyanate                                                              
          agent  free                                                     
                    total                                                 
                        % by wt.                                          
                                25  30  40  50 70                         
__________________________________________________________________________
1    IPDI caprolactam                                                     
                 12.4                                                     
                    24.85                                                 
                        15.8    381,000                                   
                                    142,000                               
                                        27,800                            
                                            6,650                         
                                               690                        
2    IPDI MEK-oxime                                                       
                 12.4                                                     
                    26.0                                                  
                        15.3    27,000                                    
                                    14,750                                
                                        3,390                             
                                            1,100                         
                                               195                        
3    HDI  caprolactam                                                     
                 14.7                                                     
                    29.75                                                 
                        14.5    90  70  60  40 &lt;30                        
4    HDI  MEK-oxime                                                       
                 16.4                                                     
                    31.5                                                  
                        14.5    75  55  35  30 &lt;30                        
5    DI51 caprolactam                                                     
                 14.5                                                     
                    29.0                                                  
                        14.3    190 140 70  40 &lt;30                        
6    DI51 MEK-oxime                                                       
                 16.2                                                     
                    31.7                                                  
                        17.7    110 85  45  30 &lt;30                        
7    HMDI caprolactam                                                     
                 10.9                                                     
                    21.9                                                  
                        17.0    880,000                                   
                                    300,000                               
                                        60,000                            
                                            9,000                         
                                               1,100                      
__________________________________________________________________________
 
    
     D. II. Comparison examples (polyisocyanate-urea-adducts) 
     According to the general preparation B for the blocked polyisocyanate-urea-adducts, the partially blocked polyisocyanates of D I underwent a reaction with the amine component. The chemical and physical characteristics were compiled in the following table: 
     
         __________________________________________________________________________
                  NCO content                                             
                         melting                                          
                              glass                                       
Example                                                                   
     polyiso-                                                             
           amine  % by weight                                             
                         range                                            
                              transition                                  
D II cyanate                                                              
           component                                                      
                  total                                                   
                      free                                                
                         °C.                                       
                              (DTA) °C.                            
__________________________________________________________________________
1    1     4,4&#39;-diamino-                                                  
                  9.4 0.2                                                 
                         158-160                                          
                               19-110                                     
           dicyclohexyl-                                                  
           methane                                                        
2    3     4,4&#39;-diamino-                                                  
                  10.6                                                    
                      0.1                                                 
                         102-104                                          
                              17-38                                       
           dicyclohexyl-                                                  
           methane                                                        
3    5     4,4&#39;-diamino-                                                  
                  10.8                                                    
                      0  90-92                                            
                              14-34                                       
           dicyclohexyl-                                                  
           methane                                                        
4    7     4,4&#39;-diamino-                                                  
                  8.5 0  160-162                                          
                              26-85                                       
           dicyclohexyl-                                                  
           methane                                                        
5    1     IPD    9.9 0  141-145                                          
                              20-83                                       
__________________________________________________________________________
 
    
     In all of the examples more or less severe incompatibilities (agglomeration) occurred as early as during the amine addition so that the course of the reaction between NCO and amino groups was not without problems. The polyisocyanate-urea-adducts still exhibit weak basicity. 
     D. III Comparison examples (Polyisocyanate-urea-adducts in conventional paint solvents) 
     If according to the general preparation C, the partially blocked polyisocyanates of D I undergo reaction with the amine component, the polyisocyanate-urea-adducts precipitate out already during the amine addition and cannot be used for manufacturing solvent-containing paint systems. 
     Obviously, numerous modifications and variations of the present invention are possible in light of the above teachings. Accordingly, the invention may be practiced otherwise than as specifically described herein.