Latent, curable, catalyzed mixtures of epoxy-containing and phenolic hydroxyl-containing compounds
CROSS-REFERENCE TO RELATED APPLICATIONS 
     This application is a continuation-in-part of application Ser. No. 155,381 filed Feb. 12, 1988 (now abandoned), which is a continuation-in-part of application Ser. No. 021,837 filed Mar. 4, 1987 (now U.S. Pat. No. 4,725,652), which is a continuation-in-part of application Ser. No. 849,087 filed Apr. 7, 1986 (now abandoned), which is a continuation-in-part of application Ser. No. 716,279 filed Mar. 25, 1985, (now U.S. Pat. No. 4,594,291), which is a continuation-in-part of application Ser. No. 631,676, filed Jul. 17, 1984 (now abandoned); all of which are incorporated herein by reference. 
    
    
     FIELD OF THE INVENTION 
     The present invention concerns latent, curable, catalyzed mixtures of epoxy-containing compounds and aromatic hydroxyl-containing compounds. The present invention also concerns latent catalysts and epoxy resin compositions containing them. 
     BACKGROUND OF THE INVENTION 
     Epoxy resins have been precatalyzed with phosphonium and other compounds to provide latent compositions which form advanced, higher molecular weight epoxy resins when admixed with an aromatic hydroxyl-containing compound as disclosed by Perry in U.S. Pat. No. 3,948,855 and Can. No. 893,191; by Dante et al. in U.S. Pat. No. 3,477,990; by Mueller et al. in U.S. Pat. No. 3,547,881; by Tyler, Jr. et al. in U.S. Pat. No. 4,366,295; and by Cragar in Can. No. 858,648. 
     While compositions containing these catalysts and an epoxy resin are somewhat stable, such compositions which also contain an aromatic hydroxyl-containing compound are lacking in stability. 
     Curable compositions containing epoxy resins and aromatic hydroxyl-containing compounds and a catalyst therefor would be highly desirable in the preparation of storage stable coatings, storage stable electrical encapsulants, storage stable formulations for preparing mechanical and electrical laminates and composites, storage stable one package molding compositions, storage stable curable compositions for use in resin transfer molding (RTM) and reaction injection molding (RIM) applications and the like. 
     SUMMARY OF THE INVENTION 
     The present invention pertains to compositions comprising (A) at least one compound containing an average of more than one epoxide group per molecule; (B) at least one compound containing an average of more than one aromatic hydroxyl group per molecule, other than an alkenylphenol polymer; and (C) at least one of (1) the product resulting from contacting (a) at least one onium compound of the element nitrogen, phosphorus, sulfur or arsenic with (b) an inorganic acid or metal salt of an inorganic acid, said acid having a weak-nucleophilic anion or a combination of such acids or metal salts; (2) the product resulting from contacting (a) at least one amine compound with (b) at least one inorganic acid having a weak-nucleophilic anion; or (3) the product resulting from contacting (a) at least one adduct of an acid having a relatively strong-nucleophilic anion and an amine compound with (b) an inorganic acid or metal salt of an inorganic acid, said acid having a weak-nucleophilic anion or a combination of such acids or metal salts; wherein (i) components (a) and (b) are contacted in quantities which permit the composition to satisfy the viscosity requirements of the composition after storage at 50° C. for 14 days; (ii) components (A) and (B) are present in quantities which provide a ratio of aromatic hydroxyl groups to epoxide group of from about 0.05:1 to about 20:1; and (iii) a mixture of components (A), (B), and (C), when dissolved in 20 to 40 percent by weight of a suitable solvent or solvent mixture, has a viscosity measured at 25° C. of 75% or less than the viscosity of a like composition except that the catalyst consists only of component (a), said viscosity being determined after storage for 14 days at 50° C. 
     The term weak-nucleophilic as employed herein means that the material has a nucleophilicity value &#34;n&#34; from about zero to less than about 2.5 as described by C. G. Swain and C. B. Scott in J. Am. Chem. Soc., Vol. 75, p. 141 (1953) which is incorporated herein by reference. 
     The term relatively strong-nucleophilic as employed herein means that the material has a nucleophilicity value &#34;n&#34; of 2.5 or greater as described by C. G. Swain and C. B. Scott in J. Am. Chem. Soc., Vol. 75, p. 141 (1953) which is incorporated herein by reference. 
     DETAILED DESCRIPTION OF THE INVENTION 
     The catalysts employed in the present invention are prepared by simply mixing in the desired proportions and stirring to insure intimate contact the onium, amine or nitrogen-containing compound with the acid or salt of an acid having a weak-nucleophilic anion and which acid or acid salt is free of any organic substituent. The contact can be conducted at temperatures of from about 0° C. to about 100° C., preferably from about 20° C. to about 60° C. for a time sufficient to complete any reaction which occurs. The time depends upon the temperature, but usually from about 1 to about 120, preferably from about 5 to about 60 minutes is sufficient. 
     The components from which the catalysts are prepared are mixed in proportions which provide from about 0.6 to about 1.4, usually from about 0.75 to about 1.35, moles of acid per mole of onium, amine or heterocyclic nitrogen-containing compound. The preferred ratios depend upon which onium, amine or heterocyclic amine compound is mixed with the acid or acid salt. For example, the preferred ratio of moles of acid or acid salt per mole of imidazole compound is from about 0.85:1 to about 1.12:1 while the most preferred ratio is in the range of from about 0.93:1 to about 1.1:1. For phosphonium compounds, the preferred ratio is from about 0.95:1 to about 1.35:1, more preferably from about 1.1:1 to about 1.25:1 moles of acid per mole of phosphonium compound. For other catalysts, it is easy to determine the optimum ratios of acid or acid salt to onium, amine or heterocyclic amine compound by mixing the components together in various ratios and conducting simple, routine experiments such as those described in examples 1-9, 18-26 and 39-45. When the amount of acid or acid salt is less than about 0.6 mole per mole of imidazole the catalyst is less latent and begins to approach the reactivity of the original imidazole prior to reaction with the acid or acid salt. When the amount of acid or acid salt is more than about 1.4 moles per mole of phosphonium, the catalyst becomes less latent to the point that at a ratio of about 1.5:1 the catalyst becomes an accelerator as compared to the original onium-containing compound prior to reaction with the acid. When the amount of acid or acid salt is more than about 1.14 moles per mole of imidazole, the catalyst becomes less latent to the point that at a ratio of about 1.17:1 the catalyst becomes an accelerator as compared to the original imidazole compound prior to reaction with the acid or acid salt. 
     The catalyst is employed in amounts sufficient to catalyze the reaction between components (A) and (B) when heated to a temperature of at least about 75° C. In most instances, the quantity of catalyst is from about 0.05 to about 100, suitably from about 0.1 to about 50, more suitably from about 0.5 to about 20, most suitably from about 1 to about 10 millimoles of catalyst per epoxide equivalent. 
     Suitable onium compounds which can be employed herein include, ammonium, phosphonium, sulfonium and arsonium compounds. Particularly suitable such compounds include, those represented by the following formulas IA or IB ##STR1## wherein each R, R 1 , R 2  and R 3  is independently a hydrocarbyl group having from 1 to about 18, preferably from about 1 to about 9, carbon atoms, or a hydrocarbyl group having from 1 to about 18, preferably from 1 to about 9 carbon atoms which group also contains one or more oxygen, sulfur, halogen, or nitrogen atoms or two of such R, R 1 , R 2  and R 3  groups can combine to form a heterocyclic ring containing one or more atoms other than carbon atoms; each X is the anion portion of an acid of a relatively strong nucleophilic acid; Z is phosphorus, nitrogen, sulfur or arsenic; m has a value equal to the valence of the anion X; and z has a value of zero or 1 depending on the valence of Z. Particularly suitable onium or amine compounds which can be reacted or complexed with the inorganic acids having a weak-nucleophilic anion to form the catalysts of the present invention include, for example, ethyltriphenyl phosphonium acetate, ethyltriphenyl phosphonium acetate•acetic acid complex, tetrabutyl phosphonium acetate, tetrabutyl phosphonium acetate•acetic acid complex, ethyltriphenyl phosphonium chloride, ethyl triphenyl phosphonium iodide, tetrabutyl phosphonium chloride, tetrabutyl phosphonium iodide, tetrabutylphosphonium hydroxide, tetrabutylammonium hydroxide, tetraethylammonium hydroxide, tetramethylammonium hydroxide, N-methylmorpholine, 2-methylimidazole, triethylamine, N,N,N&#39;,N&#39;-tetramethylethylenediamine, ethyltri(2-hydroxyethyl)-ammonium hydroxide, ethyltri(2-ethoxyethyl)ammonium hydroxide, triethyl(2-thioethylethyl)ammonium hydroxide, N-methyl-N-methylenemethanaminium acetate, N-methyl-N-methylenemethanaminium acetate•acetic acid complex, N-methyl-N-methylenemethanaminium chloride, N-methyl-N-methylenemethanaminium iodide, N-methylpyridinium acetate, N-methylpyridinium acetate•acetic acid complex, N-methylpyridinium chloride, N-methylpyridinium iodide, 1-ethyl-2,3-dimethylimidazolium acetate, 1-ethyl-2,3-dimethyl-imidazolium acetate•acetic acid complex, 1-ethyl-2,3-dimethylimidazolium chloride, 1-ethyl-2,3-dimethyl-imidazolium iodide, N-methylquinolinium acetate, N-methylquinolinium acetatee•acetic acid complex, N-methylquinolinium chloride, N-methylquinolinium iodide, N-methyl-1,3,5-triazinium acetate, N-methyl-1,3,5-triazinium acetate•acetic acid complex, N-methyl-1,3,5-triazinium chloride, N-methyl-1,3,5-triazinium iodide, combinations thereof and the like. 
     Suitable relatively strong-nucleophilic acid anions include, for example, carboxylates, halides, phosphates, phosphites, carbonates, bicarbonates, hydroxide, cyanide, thiol, sulfate, thiosulfate, and the like. Particularly suitable such nucleophilic acid anions include, for example, acetate, acetate•acetic acid complex, propionate, chloride, iodide, and the like. 
     Particularly suitable onium or amine-acid complexes which can be reacted with the salt of inorganic acids having a weak-nucleophilic anion to form the catalysts employed in the present invention include, for example, tetrabutylphosphonium chloride, tetrabutylammonium chloride, tetraethylammonium chloride, tetramethylammonium chloride, triethylamine hydrochloride, 2-methylimidazole hydrochloride, N-methylmorpholine hydrochloride, ethyltri(2-hydroxyethyl)ammonium chloride, triethyl(2-thioethylethyl)ammonium chloride, mixtures thereof and the like. 
     The amine compounds which can be suitably employed herein include, for example, primary, secondary, tertiary, aliphatic, cycloaliphatic or heterocyclic amines. 
     Suitable non-heterocyclic amines which can be employed herein include, those containing suitably from 1 to about 60, more suitably from about 2 to about 27, most suitably from about 2 to about 18, carbon atoms. Particularly suitable such amines include, for example, ethylamine, diethylamine, triethylamine, n-propylamine, di-n-propylamine, tri-n-propylamine, isopropylamine, diisopropylamine, triisopropylamine, butylamine, dibutylamine, tributylamine, methyldibutylamine, combinations thereof and the like. 
     Suitable heterocyclic secondary and tertiary amines or nitrogen-containing compounds which can be employed herein include, for example, imidazoles, imidazolidines, imidazolines, oxazoles, pyrroles, thiazoles, pyridines, pyrazines, morpholines, pyridazines, pyrimidines, pyrrolidines, pyrazoles, quinoxalines, quinazolines, phthalozines, quinolines, purines, indazoles, indoles, indolazines, phenazines, phenarsazines, phenothiazines, pyrrolines, indolines, piperidines, piperazines, combinations thereof and the like. 
     Suitable imidazole compounds which can be employed herein include, for example, those represented by the following formula II ##STR2## wherein each R a , R b , R c  and R d  is independently hydrogen, halogen, cyano or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur or halogen or the like substitutent, or R b  and R c  can combine to form a 5 or 6 membered ring with the carbon and nitrogen atoms from the imidazole ring to which they are attached or R c  and R d  can combine to form a 5 or 6 membered ring with the two carbon atoms from the imidazole ring to which they are attached. Particularly suitable imidazole compounds include, for example, 2-methylimidazole, 2-ethylimidazole, 2-propylimidazole, 2-butylimidazole, 2-pentylimidazole, 2-hexylimidazole, 2-cyclohexylimidazole, 2-phenylimidazole, 2-nonylimidazole, 2-undecylimidazole, 2-heptadecylimidazole, 2-ethyl-4-methylimidazole, 2-phenyl-4-methylimidazole, 1-benzylimidazole, 1-ethyl-2-methylbenzimidazole, 2-methyl-5,6-benzimidazole, 1-vinylimidazole, 1-allyl-2-methylimidazole, 2-cyanoimidazole, 2-chloroimidazole, 2-bromoimidazole, combinations thereof and the like. Suitable imidazoles wherein one or more of the R a , R b , R c , or R d  group contain oxygen, sulfur or halogen or the like substitutents include, for example, 1-(2-hydroxypropyl)-2-methylimidazole, 2-phenyl-4,5-dimethylolimidazole, 2-phenyl-4-methyl-5-hydroxymethylimidazole, 2-chloromethylbenzimidazole, 2-hydroxybenzimidazole, any combination thereof and the like. Most particularly suitable are 2-methylimidazole, 2-ethyl-4-methylimidazole, 1,2-dimethylimidazole and 2-phenylimidazole. 
     Suitable pyrazole compounds which can be employed herein include, for example, those represented by the following formula III ##STR3## wherein each R a , R b , R c  and R d  is independently hydrogen, halogen, cyano or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent, or R b  and R c  can combine to form a 5 or 6 membered ring with the carbon and nitrogen atoms from the imidazole ring to which they are attached or R c  and R d  can combine to form a 5 or 6 membered ring with the two carbon atoms from the pyrazole ring to which they are attached. Particularly suitable pyrazole compounds include, for example, pyrazole, 1-methylpyrazole, 3-methylpyrazole, 4-butylpyrazole, 1-methyl-3-propylpyrazole, 3-ethyl-5-methylpyrazole, 1-(3-hydroxypropyl)pyrazole, 5-phenylpyrazole, 5-benzylpyrazole, 1-phenyl-3-methylpyrazole, 1-cyanopyrazole, 3-chloropyrazole, 4-bromo-1-methylpyrazole, any combination thereof and the like. 
     Suitable oxazole compounds which can be employed herein include, for example, those represented by the following formula IV ##STR4## wherein each R a , R b , and R c  is independently hydrogen, halogen, cyano or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Particularly suitable oxazole compounds include, for example, oxazole, 4-methyloxazole, 2-methyloxazole, 4-butyloxazole, 2-methyl-5-propyloxazole, 2-ethyl-4-methyloxazole, 2-(3-hydroxypropyl)oxazole, 4-phenyloxazole, 5-benzyloxazole, 2-phenyl-5-methyloxazole, 2-cyanooxazole, 4-chlorooxazole, 4-bromo-2-methyloxazole, any combination thereof and the like. 
     Suitable imidazolidine compounds which can be employed herein include, for example, those represented by the following formula V ##STR5## wherein each R a , R b , R c , R d , R e , R f , R g  and R h  is independently hydrogen, halogen, cyano or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Particularly suitable imidazolidine compounds include, for example, imidazolidine, 1-methylimidazolidine, 2-methylimidazolidine, 4-butylimidazolidine, 1-methyl-3-propylimidazolidine, 1-ethyl-4-methylimidazolidine, 1-(3-hydroxypropyl)imidazolidine, 2-phenylimidazolidine, 1-benzylimidazolidine, 2-phenyl-1-methylimidazolidine, 4-cyanoimidazolidine, 4-chloroimidazolidine, 4-bromo-1-methylimidazolidine, any combination thereof and the like. 
     Suitable imidazoline compounds which can be employed herein include, for example, those represented by the following formula VI ##STR6## wherein each R a , R b , R c , R d , R e  and R f  is independently hydrogen, halogen, cyano or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Particularly suitable imidazoline compounds include, for example, imidazoline, 1-methylimidazolidine, 2-methylimidazolidine, 4-butylimidazolidine, 1-methyl-2-propylimidazolidine, 1-ethyl-4-methylimidazolidine, 1-(3-hydroxypropyl)imidazolidine, 2-phenylimidazolidine, 1-benzylimidazolidine, 2-phenyl-1-methylimidazolidine, 4-cyanoimidazolidine, 5-chloroimidazolidine, 5-bromo-1-methylimidazolidine, any combination thereof and the like. 
     Suitable thiazole compounds which can be employed herein include, for example, those represented by the following formula VII ##STR7## wherein each R a , R b , and R c  is independently hydrogen, halogen, cyano or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Particularly suitable thiazole compounds include, for example, thiazole, 2-methylthiazole, 5-methylthiazole, 4-butylthiazole, 2-methyl-4-propylthiazole, 4-ethyl-5-methylthiazole, 2-(3-hydroxypropyl)thiazole, 2-phenylthiazole, 2-benzylthiazole, 4-phenyl-5-methylthiazole, 2-cyanothiazole, 5-chlorothiazole, 5-bromo-2-methylthiazole, any combination thereof and the like. 
     Suitable pyrrole compounds which can be employed herein include, for example, those represented by the following formula VIII ##STR8## wherein each R a , R b , R c , R d  and R e  is independently hydrogen, halogen, cyano or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Particularly suitable pyrrole compounds include, for example, pyrrole, 1-methylpyrrole, 2-methylpyrrole, 3-butylpyrrole, 1-methyl-2-propylpyrrole, 2-ethyl-3-methylpyrrole, 1-(3-hydroxypropyl)pyrrole, 2-phenylpyrrole, 1-benzylpyrrole, 2-phenyl-1-methylpyrrole, 3-cyanopyrrole, 3-chloropyrrole, 2-bromo-1-methylpyrrole, any combination thereof and the like. 
     Suitable pyridine compounds which can be employed herein include, for example, those represented by the following formula IX ##STR9## wherein each R a , R b , R c , R d  and R e  is independently hydrogen, halogen, cyano or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Particularly suitable pyridine compounds include, for example, pyridine, 2-methylpyridine, 3-methylpyridine, 4-butylpyridine, 2-methyl-3-propylpyridine, 3-ethyl-4-methylpyridine, 4-(3-hydroxypropyl)pyridine, 2-phenylpyridine, 3-benzylpyridine, 4-phenyl-2-methylpyridine, 3-cyanopyridine, 2-chloropyridine, 3-bromo-5-methylpyridine, any combination thereof and the like. 
     Suitable pyrazine compounds which can be employed herein include, for example, those represented by the following formula X ##STR10## wherein each R a , R b , R c  and R d  is independently hydrogen, or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Particularly suitable pyrazine compounds include, for example, pyrazine, 2-methylpyrazine, 3-methylpyrazine, 2-butylpyrazine, 2-methyl-5-propylpyrazine, 2-ethyl-6-methylpyrazine, 2-(3-hydroxypropyl)pyrazine, 2-phenylpyrazine, 2-benzylpyrazine, 2-phenyl-3-methylpyrazine, 2-cyanopyrazine, 2-chloropyrazine, 2-bromo-5-methylpyrazine, any combination thereof and the like. 
     Suitable pyridazine compounds which can be employed herein include, for example, those represented by the following formula XI ##STR11## wherein each R a , R b , R c , and R d  is independently hydrogen, hydrogen, halogen, cyano or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Particularly suitable pyridazine compounds include, for example, pyridazine, 3-methylpyridazine, 4-methylpyridazine, 3-butylpyridazine, 3-methyl-4-propylpyridazine, 3-ethyl-6-methylpyridazine, 4-(3-hydroxypropyl)pyridazine, 3-phenylpyridazine, 4-benzylpyridazine, 4-phenyl-5-methylpyridazine, 4-cyanopyridazine, 4-chloropyridazine, 3-bromo-5-methylpyridazine, any combination thereof and the like. 
     Suitable pyrrolidine compounds which can be employed herein include, for example, those represented by the following formula XII ##STR12## wherein each R a , R b , R c , R d , R e , R f , R g , R h  and R i  is independently hydrogen, halogen, cyano or a hydrocarbyl group having from 1 to about 18 carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Particularly suitable compounds include, for example, pyrrolidine, 1-methyl-pyrrolidine, 4-phenylpyrrolidine, 2-methylpyrrolidine, 3-methylpyrrolidine, 1-butylpyrrolidine, 1-methyl-2-propylpyrrolidine, 3-ethyl-4-methyl-pyrrolidine, 2-(3-hydroxypropyl)pyrrolidine, 1-phenyl-2-methylpyrrolidine, 2-cyanopyrrolidine, 2-chloropyrrolidine, 2-bromo-1-methylpyrrolidine, any combination thereof and the like. 
     Suitable morpholine compounds which can be employed herein include, for example, those represented by the following formula XIII ##STR13## wherein each R a , R b , R c , R d , R e , R f , R g , R h  and R i  is independently hydrogen, or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Particularly suitable morpholine compounds include, for example, morpholine, 4-methylmorpholine, 3-methylmorpholine, 4-butylmorpholine, 4-methyl-3-propylmorpholine, 2-ethyl-3-methylmorpholine, 4-(3-hydroxypropyl)morpholine, 2-phenylmorpholine, 4-benzylmorpholine, 3-phenyl-1-methylmorpholine, 3-cyanomorpholine, 3-chloromorpholine, 3-bromo-4-methylmorpholine, any combination thereof and the like. 
     Suitable pyrimidine compounds which can be employed herein include, for example, those represented by the following formula XIV ##STR14## wherein each R a , R b , R c  and R d  is independently hydrogen, or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Particularly suitable pyrimidine compounds which can be employed herein include, for example, pyrimidine, 2-methylpyrimidine, 4-methylpyrimidine, 2-butylpyrimidine, 2-methyl-4-propylpyrimidine, 4-ethyl-5-methylpyrimidine, 2-(3-hydroxypropyl)pyrimidine, 2-phenylpyrimidine, 2-benzylpyrimidine, 4-phenyl-2-methylpyrimidine, 4-cyanopyrimidine, 2-chloropyrimidine, 4-bromo-2-methylpyrimidine, any combination thereof and the like. 
     Suitable quinoxaline compounds which can be employed herein include, for example, those represented by the following formula XV ##STR15## wherein each R a , R b , R c , R d , R e , and R f  is independently hydrogen, or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Particularly suitable quinoxaline compounds include, for example, quinoxaline, 2-methylquinoxaline, 5-methylquinoxaline, 2-butylquinoxaline, 2-methyl-3-propylquinoxaline, 5-ethyl-6-methylquinoxaline, 2-(3-hydroxypropyl)quinoxaline, 2-phenylquinoxaline, 5-benzylquinoxaline, 2-phenyl-5-methylquinoxaline, 2-cyanoquinoxaline, 2-chloroquinoxaline, 2-bromo-5-methylquinoxaline, any combination thereof and the like. 
     Suitable quinazoline compounds which can be employed herein include, for example, those represented by the following formula XVI ##STR16## wherein each R a , R b , R c , R d , R e , and R f  is independently hydrogen, or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Suitable quinazoline compounds include, for example, quinazoline, 2-methylquinazoline, 4-methylquinazoline, 2-butylquinazoline, 2-methyl-4-propylquinazoline, 5-ethyl-6-methylquinazoline, 2-(3-hydroxypropyl)quinazoline, 2-phenylquinazoline, 2-benzylquinazoline, 2-phenyl-4-methylquinazoline, 4-cyanoquinazoline, 4-chloroquinazoline, 2-bromo-4-methylquinazoline, any combination thereof and the like. 
     Suitable phthalazine compounds which can be employed herein include, for example, those represented by the following formula XVII ##STR17## wherein each R a , R b , R c , R d , R e , and R f  is independently hydrogen, or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Suitable phthalazine compounds include, for example, phthalazine, 1-methylphthalazine, 6-methylphthalazine, 1-butylphthalazine, 1-methyl-4-propylphthalazine, 1-ethyl-6-methylphthalazine, 1-(3-hydroxypropyl)phthalazine, 5-phenylphthalazine, 1-benzylphthalazine, 1-phenyl-4-methylphthalazine, 1-cyanophthalazine, 1-chlorophthalazine, 1-bromo-4-methylphthalazine, any combination thereof and the like. 
     Suitable quinoline compounds which can be employed herein include, for example, those represented by the following formula XVIII ##STR18## wherein each R a , R b , R c , R d , R e , R f  and R g  is independently hydrogen, or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Suitable quinoline compounds which can be employed herein include, for example, quinoline, 2-methylquinoline, 3-methylquinoline, 4-butylquinoline, 5-methyl-2-propylquinoline, 2-ethyl-3-methylquinoline, 3-(3-hydroxypropyl)quinoline, 3-phenylquinoline, 4-benzylquinoline, 3-phenyl-2-methylquinoline, 3-cyanoquinoline, 4-chloroquinoline, 2-bromo-3-methylquinoline, any combination thereof and the like. 
     Suitable purine compounds which can be employed herein include, for example, those represented by the following formula XIX ##STR19## wherein each R a , R b , and R c  is independently hydrogen, or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Suitable purine compounds include, for example, purine, 2-methylpurine, 8-methylpurine, 6-butylpurine, 2-methyl-8-propylpurine, 6-ethyl-8-methylpurine, 8-(3-hydroxypropyl)purine, 2-phenylpurine, 2-benzylpurine, 6-phenyl-2-methylpurine, 8-cyanopurine, 2-chloropurine, 8-bromo-2-methylpurine, any combination thereof and the like. 
     Suitable indazole compounds which can be employed herein include, for example, those represented by the following formula XX ##STR20## wherein each R a , R b , R c , R d , R e  and R f  is independently hydrogen, or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Suitable indazole compounds include, for example, indazole, 1-methylindazole, 3-methylindazole, 1-butylindazole, 1-methyl-3-propylindazole, 1-ethyl-5-methylindazole, 3-(3-hydroxypropyl)indazole, 3-phenylindazole, 6-benzylindazole, 6-phenyl-1-methylindazole, 3-cyanoindazole, 5-chloroindazole, 3-bromo-1-methylindazole, any combination thereof and the like. 
     Suitable indole compounds which can be employed herein include, for example, those represented by the following formula XXI ##STR21## wherein each R a , R b , R c , R d , R e , R f  and R g  is independently hydrogen, or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Suitable indole compounds which can be employed herein include, for example, indole, 1-methylindole, 2-methylindole, 3-butylindole, 1-methyl-2-propylindole, 2-ethyl-3-methylindole, 1-(3-hydroxypropyl)indole, 2-phenylindole, 1-benzylindole, 2-phenyl-1-methylindole, 2-cyanoindole, 5-chloroindole, 3-bromo-1-methylindole, any combination thereof and the like. 
     Suitable indolizine compounds which can be employed herein include, for example, those represented by the following formula XXII ##STR22## wherein each R a , R b , R c , R d , R e , R f  and R g  is independently hydrogen, or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Suitable indolizine compounds include, for example, indolazine, 1-methylindolizine, 2-methylindolizine, 3-butylindolizine, 5-methyl-1-propylindolizine, 2-ethyl-1-methylindolizine, 6-(3-hydroxypropyl)indolizine, 3-phenylindolizine, 7-benzylindolizine, 2-phenyl-3-methylindolizine, 5-cyanoindolizine, 7-chloroindolizine, 3-bromo-5-methylindolizine, any combination thereof and the like. 
     Suitable phenazine compounds which can be employed herein include, for example, those represented by the following formula XXIII ##STR23## wherein each R a , R b , R c , R d , R e , R f , R g  and R h  is independently hydrogen, or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Suitable phenazine compounds which can be employed herein include, for example, phenazine, 1-methylphenazine, 2-methylphenazine, 2-butylphenazine, 1-methyl-7-propylphenazine, 1-ethyl-4-methylphenazine, 2-(3-hydroxypropyl)phenazine, 1-phenylphenazine, 1-benzylphenazine, 1-phenyl-7-methylphenazine, 2-cyanophenazine, 1-chlorophenazine, 1-bromo-2-methylphenazine, any combination thereof and the like. 
     Suitable phenarsazine compounds which can be employed herein include, for example, those represented by the following formula XXIV ##STR24## wherein each R a , R b , R c , R d , R e , R f , R g  and R h  is independently hydrogen, or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Suitable phenarsazine compounds which can be employed herein include, for example, phenarsazine, 1-methylphenarsazine, 2-methylphenarsazine, 4-butylphenarsazine, 1-methyl-6-propylphenarsazine, 2-ethyl-3-methylphenarsazine, 1-(3-hydroxypropyl)phenarsazine, 4-phenylphenarsazine, 3-benzylphenarsazine, 2-phenyl-7-methylphenarsazine, 3-cyanophenarsazine, 1-chlorophenarsazine, 1-bromo-8-methylphenarsazine, any combination thereof and the like. 
     Suitable phenothiazine compounds can be employed herein include, for example, those represented by the following formula XXV ##STR25## wherein each R a , R b , R c , R d , R e , R f , R g , R h  and R i  is independently hydrogen, or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Suitable phenothiazine compounds include, for example, phenothiazine, 10-methylphenothiazine, 1-methylphenothiazine, 2-butylphenothiazine, 10-methyl-4-propylphenothiazine, 2-ethyl-3-methylphenothiazine, 4-(3-hydroxypropyl)phenothiazine, 10-phenylphenothiazine, 1-benzylphenothiazine, 10-phenyl-4-methylphenothiazine, 7-cyanophenothiazine, 4-chlorophenothiazine, 4-bromo-10-methylphenothiazine, any combination thereof and the like. 
     Suitable pyrroline compounds which can be employed herein include, for example, those represented by the following formula XXVI ##STR26## wherein each R a , R b , R c , R d , R e , R f  and R g  is independently hydrogen, or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Suitable pyrroline compounds include, for example, pyrroline, 2-methylpyrroline, 4-methyl-pyrroline, 5-butylpyrroline, 5-methyl-1-propyl-pyrroline, 1-ethyl-3-methylpyrroline, 1-(3-hydroxy-propyl)pyrroline, 5-phenylpyrroline, 1-benzylpyrroline, 1-phenyl-4-methylpyrroline, 3-cyanopyrroline, 5-chloropyrroline, 2-bromo-1-methylpyrroline, any combination thereof and the like. 
     Suitable indoline compounds which can be employed herein include, for example, those represented by the following formula XXVII ##STR27## wherein each R a , R b , R c , R d , R e , R f , R g , R h  and R i  is independently hydrogen, or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Particularly suitable indoline compounds include, for example, indoline, 1-methylindoline, 2-methylindoline, 3-butylindoline, 1-methyl-2-propyl-indoline, 2-ethyl-2-methylindoline, 1-(3-hydroxy-propyl)indoline, 1-phenylindoline, 1-benzylindoline, 1-phenyl-2-methylindoline, 1-benzylindoline, 1-phenyl-2-methylindoline, 5-cyanoindoline, 7-chloroindoline, 5-bromo-1-methylindoline, any combination thereof and the like. 
     Suitable piperidine compounds which can be employed herein include, for example, those represented by the following formula XXVIII ##STR28## wherein each R a , R b , R c , R d , R e , R f , R g , R h , R i , R j  and R k  is independently hydrogen, or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent,. Suitable piperidine compounds which can be employed herein include, for example, piperidine, 1-methylpiperidine, 2-methylpiperidine, 3-butylpiperidine, 1-methyl-2-propypiperidine, 2-ethyl-4-methylpiperidine, 1-(3-hydroxypropyl)piperdine, 1-phenylpiperidine, 1-benzylpiperidine, 1-phenyl-2-methylpiperidine, 4-cyanopiperdine, 3-chloropiperidine, 4-bromo-1-methylpiperidine, any combination thereof and the like. 
     Suitable piperazine compounds which can be employed herein include, for example, those represented by the following formula XXIX ##STR29## wherein each R a , R b , R c , R d , R e , R f , R g , R h , R i  and R j  is independently hydrogen, or a hydrocarbyl group having suitably from 1 to about 18, more suitably from 1 to about 9, carbon atoms or such hydrocarbyl groups containing an oxygen, sulfur, cyano or halogen or the like substitutent. Particularly suitable piperazine compounds which can be employed herein include, for example, piperazine, 1-methylpiperazine, 2-methylpiperazine, 3-butylpiperazine, 1-methyl-4-propylpiperazine, 1-ethyl-3-methylpiperazine, 1(3-hydroxypropyl)-piperazine, 2-phenylpiperazine, 1-benzylpiperazine, 1-methyl-3-phenylpiperazine, 2-cyanopiperazine, 2-chloropiperazine, 1,4-dimethyl-2-bromopiperazine, any combination thereof and the like. 
     Particularly suitable inorganic acids having a weak nucleophilic anion include, for example, fluoboric acid, fluoarsenic acid, fluoantimonic acid, fluophosphoric acid, chloroboric acid, chloroarsenic acid, chloroantimonic acid, chlorophosphoric acid, perchloric acid, chloric acid, bromic acid, iodic acid and any combination thereof and the like. Most particularly suitable such acid is fluoboric acid. 
     Fluoboric acid is sometimes referred to as fluoroboric acid or hydrogen tetrafluoroborate. Any of these expressions refer to the chemical represented by the formula, HBF 4 . 
     Suitable metal salts of inorganic acids free from any organic substituents and having a weak nucleophilic anion include, for example those sets of metals of Groups I and II of the Periodic Table of the Elements published by Sargent-Welch Scientific Company as catalog number S-18806. Particularly such salts include, for example, the sodium, potassium, lithium, calcium, barium, magnesium and silver salts of such inorganic acids. 
     Suitable compounds having an average of more than one epoxide group per molecule which can be employed herein include, epoxy resins such as, for example, the glycidyl ethers of polyhydric phenols such as dihydroxy phenols, biphenols, bisphenols, halogenated bisphenols, alkylated bisphenols, trisphenols, phenol-aldehyde novolac resins, substituted phenol-aldehyde novolac resins, phenol-hydrocarbon resins, substituted phenol-hydrocarbon resins, any combination thereof and the like. Suitable such epoxy resins include, for example, those represented by the following formulas XXX-XXXIV ##STR30## wherein each A is independently a divalent hydrocarbyl group having from 1 to about 9, preferably from 1 to about 4, carbon atoms, --O--, --S--, --S--S--, --SO--, --SO 2  --, or --CO--; each A&#39; is independently a divalent hydrocarbyl group having from 1 to about 9, preferably from 1 to about 4 carbon atoms; Q is a hydrocarbyl group having from 1 to about 10 carbon atoms; Q&#39; is hydrogen, halogen, cyano or an alkyl group having from 1 to about 4 carbon atoms; each R is independently hydrogen, halogen, cyano or an alkyl group having from 1 to about 4 carbon atoms; each X is independently hydrogen, bromine, chlorine, or a hydrocarbyl or hydrocarbyloxy group having from 1 to about 9, preferably from 1 to about 4 carbon atoms; m has an average value from zero to about 12, preferably from about zero to about 9, most preferably from about 0.03 to about 3; m&#39; has an average value from about 0.01 to about 8, preferably from about 0.2 to about 6, more preferably from about 0.5 to about 4; n has a value of zero or 1; n&#39; has an average value of from zero to about 12, preferably from zero to about 9, most preferably from about 0.03 to about 3; each p suitably has a value from zero to about 10, more suitably from zero to about  6, most suitably from about 1 to about 3; and each p&#39; suitably has a value from zero to about 8, more suitably from about 1 to about 6, most suitably from about 2 to about 4. Also suitable are the oligomers of the epoxy resin represented by formula XXXIV. 
     The term hydrocarbyl as employed herein means any aliphatic, cycloaliphatic, aromatic, aryl substituted aliphatic or cycloaliphatic, or aliphatic or cycloaliphatic substituted aromatic groups. The aliphatic groups can be saturated or unsaturated. Likewise, the term hydrocarbyloxy means a hydrocarbyl group having an oxygen linkage between it and the carbon atom to which it is attached. 
     Particularly suitable such epoxy resins include, for example, the diglycidyl ethers of resorcinol, catechol, hydroquinone, biphenol, bisphenol A, bisphenol F, bisphenol K, tetrabromobisphenol A, phenol-formaldehyde novolac resins, alkyl substituted phenol-formaldehyde resins, phenol-hydroxybenzaldehyde resins, cresol-hydroxybenzaldehyde resins, dicylopentadiene-phenol resins, dicyclopentadiene-substituted phenol resins tetramethylbiphenol, tetramethyl-tetrabromobiphenol, tetramethyltribromobiphenol, tetrachlorobisphenol A, any combination thereof and the like. 
     Also suitable as the epoxide compound which can be employed in the present invention include those partially advanced epoxy resins disclosed by Bertram et al. in U.S. Pat. No. 4,594,291 which is incorporated herein by reference. 
     Also suitable as the epoxide compound are the glycidyl ethers of compounds having an average of more than one aliphatic hydroxyl group per molecule such as, for example, aliphatic diols, polyether diols, polyether triols, polyether tetrols, any combination thereof and the like. Also suitable are the alkylene oxide adducts of compounds containing an average of more than one aromatic hydroxyl group per molecule such as, for example, the ethylene oxide, propylene oxide, or butylene oxide adducts of dihydroxy phenols, biphenols, bisphenols, halogenated bisphenols, alkylated bisphenols, trisphenols, phenol-aldehyde novolac resins, halogenated phenol-aldehyde novolac resins, alkylated phenol-aldehyde novolac resins, hydrocarbon-phenol resins, hydrocarbon-halogenated phenol resins, or hydrocarbon-alkylated phenol resins, or any combination thereof and the like. 
     Suitable aromatic hydroxyl containing compounds which can be employed herein include, for example, compounds having an average of more than one phenolic hydroxyl group per molecule. Suitable such compounds include, for example, dihydroxy phenols, biphenols, bisphenols, halogenated bisphenols, alkylated bisphenols, trisphenols, phenol-aldehyde resins, halogenated phenol-aldehyde novolac resins, alkylated phenol-aldehyde novolac resins, phenolhydroxybenzaldehyde resins, alkylated phenolhydroxybenzaldehyde resins, hydrocarbon-phenol resins, hydrocarbon-halogenated phenol resins, hydrocarbon-alkylated phenol resins, any combination thereof and the like. Particularly suitable aromatic hydroxyl containing compounds include, for example, those represented by the following formulas XXXV-XXXVIII ##STR31## wherein A, A&#39;, Q, Q&#39; X, n and m are as defined above in formulas XII-XVI. Particularly suitable aromatic hydroxyl-containing materials include, for example, biphenol, bisphenol A, bisphenol K, tetrabromobisphenol A, tetrabromobisphenol K, resorcinol, phenol-aldehyde novolac resins, cresol-aldehyde novolac resins, phenolhydroxybenzaldehyde resins, cresol-hydroxybenzaldehyde resins, tetramethylbiphenol, tetramethyltribromobiphenol, tetramethyltetrabromobiphenol, tetrachorobisphenol A, any combination thereof and the like. Also suitable are the oligomers of the multifunctional phenolic compounds represented by the formula X. 
     These and other suitable aromatic hydroxyl-containing compounds are disclosed in U.S. Pat. No. 4,594,291 issued Jun. 10, 1986 by Bertram et al which is incorporated herein by reference in its entirety. 
     The aromatic hydroxyl-containing compounds are employed in amounts which provide a ratio of aromatic hydroxyl groups to epoxy groups suitably from about 0.05:1 to about 20:1, more suitably from about 0.1:1 to about 10:1, most suitably from about 0.2:1 to about 5:1. 
     The precatalyzed compositions of the present invention can contain, if desired, pigments, fillers, dyes, diluents, solvents, stabilizers, epoxy resin curing agents, any combination thereof and the like. 
     Suitable stabilizer materials and curing agents which can be employed herein include, for example, those disclosed in the aforementioned U.S. Pat. No. 4,594,291 by Bertram et al which is incorporated herein by reference in its entirety. 
     The compositions of the present invention are useful in the preparation of formulations for use in the preparation of electrical and structural laminates and composites, coatings, castings, moldings, encapsulants and the like. They can be employed in the conventional methods or the newer reaction transfer molding (RTM) and reaction injection molding (RIM) techniques. 
    
    
     The following examples are illustrative of the invention but are not to be construed as to limiting the scope thereof in any manner. 
     EXAMPLE 1 
     PREPARATION OF 2-METHYLIMIDAZOLIUM FLUOBORATE COMPLEX 
     A glass flask fitted with a stirrer, thermometer, and reflux condenser is charged with 15.37 grams (0.098 mole) of a 55.9% aqueous solution by weight, of fluoboric acid. To this stirred solution, 8.2 grams (0.100 mole) of 2-methylimidazole are slowly added during about five minutes. The heat from the reaction warmed the solution to approximately 50° C. as the 2-methylimidazole dissolves. The solution is stirred for an additional 30 minutes as it cools to near ambient temperature. Methanol is then added, 19.98 grams, to dilute the solution to 38.6% solids based on the weight of the 2-methylimidazole and fluoboric acid. 
     The concentration of the aqueous fluoboric acid was determined by potentiometric titration to the first inflection point with 0.100N potassium hydroxide in methanol. An MCI GT-05 automatic titrator and a combination silver/silver chloride electrode (Curtain Matheson Scientific No. 201-947) were used to measure the pH changes during the course of the titration. 
     EXAMPLES 2-12 
     PREPARATION OF 2-METHYLIMIDAZOLIUM FLUOBORATE COMPLEXES 
     The procedure described in Example 1 is repeated using the same procedure and amount of 2-methylimidazole (2-MI), however the weight of fluoboric acid (55.9% aqueous solution) is varied as shown in Table I. All experiments are diluted with methanol to 38.5% solids based on the combined weights of 2-MI and fluoboric acid. The results are given in Table I. 
     
                       TABLE I                                                     
______________________________________                                    
2-METHYLIMIDAZOLE WITH VARYING                                            
RATIOS OF FLUOBORIC ACID                                                  
                        Moles of                                          
              Fluoboric Fluoboric                                         
              Acid      Acid Per                                          
Example       Solution  Mole of                                           
Number        (grams)   2-MI                                              
______________________________________                                    
2             11.71     0.75                                              
3             13.17     0.84                                              
4             13.90     0.89                                              
5             14.63     0.93                                              
1             15.37     0.98                                              
6             16.10     1.03                                              
7             16.83     1.07                                              
8             17.56     1.12                                              
9             17.88     1.14                                              
10            18.35     1.17                                              
11            20.39     1.30                                              
12            21.17     1.35                                              
______________________________________                                    
 
    
     EXAMPLE 13 
     PREPARATION OF 2-PHENYLIMIDAZOLIUM FLUOBORATE 
     A glass flask fitted with a stirrer, thermometer, and a reflux condenser is charged with 15.37 grams (0.098 mole) of a 55.9% aqueous solution, by weight, of fluoboric acid and 29.3 grams of methanol. To this stirred solution, 14.4 grams (0.100 mole) of 2-phenylimidazole (2-PI) are slowly added during about five minutes. The heat from the reaction warms the solution to approximately 50° C. as the 2-phenylimidazole dissolves. The solution is stirred for an additional 30 minutes as it cools to near ambient. The product is a clear solution containing 38.9% by weight of the 2-phenylimidazolium fluoborate adduct/complex. 
     EXAMPLE 14 
     PREPARATION OF 4-METHYLIMIDAZOLIUM FLUOBORATE COMPLEX 
     The procedure of Example 13 is followed using the following reagents: 
     4.00 g (0.0487 mole) of 4-methylimidazole (4-MI) 
     7.84 g (0.0500 mole) of fluoboric acid (55.9% aqueous) 
     9.92 g of methanol 
     The resultant product is a clear solution containing 38.5% by weight of the 4-methylimidazolium fluoborate adduct/complex. 
     EXAMPLE 15 
     PREPARATION OF 1,2-DIMETHYLIMIDAZOLIUM FLUOBORATE COMPLEX 
     The procedure of Example 13 is followed using the following reagents: 
     4.68 g (0.0487 mole) of 1,2-dimethylimidazole (1,2-DMI) 
     7.84 g (0.0500 mole) of fluoboric acid (55.9% aqueous) 
     10.95 g of methanol 
     The resultant product is a clear solution containing 38.6% by weight of the 1,2-dimethylimidazolium fluoborate adduct/complex. 
     EXAMPLE 16 
     PREPARATION OF 2-ETHYL-4-METHYLIMIDAZOLIUM FLUOBORATE COMPLEX 
     The procedure of Example 13 is followed using the following reagents: 
     5.36 g (0.0487 mole) of 2-ethyl-4-methylimidazole (2-E-4-MI) 
     7.84 g (0.0500 mole) of fluoboric acid (55.9% aqueous) 
     11.98 g of methanol 
     The resultant product is a clear solution containing 38.7% by weight of the 2-ethyl-4-methylimidazolium fluoborate adduct/complex. 
     EXAMPLE 17 
     Preparation of 4,5-Diphenylimidazolium Fluoborate Complex 
     The procedure of Example 13 is followed using the following reagents: 
     4.00 g (0.0182 mole) of 4,5-diphenylimidazole (4,5-DPI) 
     2.92 g (0.0166 mole) of fluoboric acid (55.9% aqueous) 
     7.47 g of methanol 
     After the above reactants are added together, the mixture is not homogeneous, therefore an additional 35.4 grams of the monomethyl ether of propylene glycol monoacetate is added to give a clear solution containing 11.3% by weight of the 4,5-diphenylimidazolium fluoborate adduct/complex. 
     EXAMPLE 18-34 
     Imidazolium Fluoborate Complex Catalyzed Epoxy/Phenolic Systems 
     The catalysts described in Examples 1-17 are mixed with a 1:1 molar ratio of a diglycidyl ether of bisphenol A having an epoxy equivalent weight of 181.5 (D.E.R.™383 Epoxy Resin commercially available from The Dow Chemical Co.) and bisphenol A (2,2-bis(4,4&#39;-hydroxyphenyl)propane), commercially available from The Dow Chemical Co. as PARABIS™) dissolved in the monomethylether of propylene glycol monoacetate (PMA). The epoxy resin (181.5 grams, 1 equiv.), bisphenol A (114 grams, 1 equiv.) and 73.88 grams of PMA are heated between 80° C. and 100° C. under a nitrogen atmosphere until homogeneous, cooled to ambient temperature and the appropriate amount of catalyst added as described in Table II. Portions of these solutions are then stored at 50° C. and the 25° C. viscosity monitored as shown in Table III. 
     
                       TABLE II                                                    
______________________________________                                    
CATALYZED EPOXY/PHENOLIC FORMULATIONS                                     
Example               Catalyst Millimoles of                              
or Comp. Catalyst     Solution Catalyst per                               
Expt.    (Ex.         Weight   Equivalent of                              
No.      Number)      (grams)  Epoxide                                    
______________________________________                                    
18       1            3.92     9.0                                        
19       2            3.47     9.0                                        
20       3            3.67     9.0                                        
21       4            3.75     9.0                                        
22       5            3.82     9.0                                        
23       6            4.02     9.0                                        
24       7            4.12     9.0                                        
25       8            4.22     9.0                                        
26       9            4.24     9.0                                        
 27*     10           4.31     9.0                                        
 28*     11           4.59     9.0                                        
 29*     12           4.67     9.0                                        
30       13           5.31     9.0                                        
31       14           4.00     9.0                                        
32       15           4.33     9.0                                        
33       16           4.65     9.0                                        
34       17           24.65    9.0                                        
C. E..sup.a A*                                                            
         No Cat.      --       --                                         
C. E..sup.a B*                                                            
         2-MI.sup.b   1.85     9.0                                        
C. E..sup.a C*                                                            
         2-PI.sup.c   3.24     9.0                                        
C. E..sup.a D*                                                            
         1,2-DMI.sup.d                                                    
                      2.16     9.0                                        
______________________________________                                    
 *Not an example of the present invention.                                
 .sup.a C. E. is Comparative Experiment.                                  
 .sup.b 2methyl imidazole alone as catalyst. (40% by wt. solution in      
 methanol)                                                                
 .sup.c 2phenylimidazole alone as catalyst. (40% by wt. solution in       
 methanol)                                                                
  .sup.d 1,2dimethylimidazole alone as catalyst. (40% by wt. solution in  
 methanol)                                                                
 
    
     
                                           TABLE III                               
__________________________________________________________________________
50° C. Stability Study                                             
         Mol.                                                             
         of                                                               
         HBF.sub.4                                                        
Nitrogen per                             % of Control                     
or       Mol.                            Viscosity.sup.d                  
Ex.                                                                       
   Phosporus                                                              
         of N-                                                            
             Viscosity                       After                        
or Cont. Cont.                                                            
             Initial After 1 Day                                          
                               After 14 Days                              
                                         After                            
                                             14                           
CE.sup.a                                                                  
   Compound                                                               
         Cmpd.                                                            
             Cps                                                          
                Pa.s Cps   Pa.s                                           
                               Cps   Pa.s                                 
                                         1 Day                            
                                             Days                         
__________________________________________________________________________
18 2-MI  0.98                                                             
             885                                                          
                .885 1054  1.054                                          
                               1385  1.385                                
                                         10.5                             
                                             &lt;0.7                         
19 2-MI  0.75                                                             
             914                                                          
                .914 1361  1.361                                          
                               N.D.  N.D.                                 
                                         13.6                             
                                             N.D.                         
20 2-MI  0.84                                                             
             904                                                          
                .904 1211  1.211                                          
                               24150 24.150                               
                                         12.1                             
                                             &lt;12.1                        
21 2-MI  0.89                                                             
             891                                                          
                .891 1144  1.144                                          
                               8890  8.890                                
                                         11.4                             
                                             &lt;4.4                         
22 2-MI  0.93                                                             
             887                                                          
                .887 1085  1.085                                          
                               3120  3.120                                
                                         10.8                             
                                             &lt;1.6                         
23 2-MI  1.03                                                             
             877                                                          
                .887 1032  1.032                                          
                               1251  1.251                                
                                         10.3                             
                                             &lt;0.6                         
24 2-MI  1.07                                                             
             840                                                          
                .840 957   .957                                           
                               1168  1.168                                
                                         9.6 &lt;0.6                         
25 2-MI  1.12                                                             
             836                                                          
                .836 987   .987                                           
                               2919  2.919                                
                                         9.9 &lt; 1.5                        
 26*                                                                      
   2-MI  1.14                                                             
             1360                                                         
                1.360                                                     
                     &gt;200,000.sup.b                                       
                           &gt;200.sup.b                                     
                               N.D.  N.D.                                 
                                         N/A N.D.                         
 27*                                                                      
   2-MI  1.17                                                             
             1243                                                         
                1.243                                                     
                     &gt;200,000.sup.b                                       
                           &gt;200.sup.b                                     
                               --    --  &gt;1999                            
                                             --                           
 28*                                                                      
   2-MI  1.30                                                             
             1715                                                         
                1.715                                                     
                     &gt;200,000.sup.b                                       
                           &gt;200.sup.b                                     
                               --    --  &gt;1999                            
                                             --                           
 29*                                                                      
   2-MI  1.35                                                             
             2000.sup.e                                                   
                2.000.sup.e                                               
                     &gt;200,000.sup.b                                       
                           &gt;200.sup.b                                     
                               --    --  &gt;1999                            
                                             --                           
30 2-PI  0.98                                                             
             820                                                          
                .820 980   .980                                           
                               1404  1.404                                
                                         7.0 --                           
31 4-MI  1.02                                                             
             867                                                          
                .867 1020  1.020                                          
                               1179  1.179                                
                                         --  --                           
32 1,2-DMI                                                                
         1.03                                                             
             836                                                          
                .836 932   .932                                           
                               1260  1.260                                
                                         7.6 &lt;0.6                         
33 2-E-4-MI                                                               
         1.02                                                             
             828                                                          
                .828 897   .897                                           
                               1140  1.140                                
                                         --  --                           
34 4,5-DPI                                                                
         1.03                                                             
             417                                                          
                .417 576   .576                                           
                               742   .742                                 
                                         --  --                           
A* None  0   1079                                                         
                1.079                                                     
                     1081  1.081                                          
                               1256  1.256                                
                                         --  --                           
B* 2-MI.sup.c                                                             
         0   1006                                                         
                1.006                                                     
                     10,006                                               
                           10.006                                         
                               &gt;200,000.sup.b                             
                                     &gt;200.sup.b                           
                                         --  --                           
C* 2-PI.sup.c                                                             
         0   1042                                                         
                1.042                                                     
                     14,000                                               
                           14.000                                         
                               --    --  --  --                           
D* 1,2-DMI.sup.c                                                          
         0   1171                                                         
                1.171                                                     
                     12,228                                               
                           12,228                                         
                               &gt;200,000.sup.b                             
                                     &gt;200.sup.b                           
                                         --  --                           
__________________________________________________________________________
 FOOTNOTES TO TABLE III                                                   
 *Not an example of the present invention.                                
 .sup.a Examples are designated by numerals whereas comparative experiment
 are designated by letters.                                               
 .sup.b Viscosity of the composition exceeded the test method (&gt;200,000   
 cps).                                                                    
 .sup.c 2Methylimidazole, 2phenylimidazole and 1,2dimethylimidazole       
 employed alone as catalyst.                                              
 .sup.d This value is determined by dividing the viscosity obtained in the
 appropriate example by the viscosity of a comparable formulation employin
 as the catalyst the same nitrogen or phosphorus compound except that it  
 has not been reacted with HBF.sub.4.                                     
 .sup.e The viscosity was increasing during measurement.                  
 
    
     EXAMPLE 35 
     Coating Properties with 2-Methyl-Imidazolium Fluoborate Catalyst 
     The formulations described in Example 18 and Comparative Experiment B are applied to 24 gauge Bonderite™ R 90 treated steel panels available from Parker Chemical Co. via a wire wound steel draw down rod. The coatings are allowed to air dry for approximately five minutes, then placed in a forced air oven preset at 200° C. for 10 minutes. The panels are removed from the oven, cooled to ambient temperature, and tested as shown in Table IV. 
     Resistance to methyl ethyl ketone is determined in the following manner. The ball end of a ball peen hammer weighing about 1.5 lbs. (0.6804 kg) is covered with 8 plys of gauze, which is then wet with methyl ethyl ketone (MEK). The ball end of the hammer is applied to the coated surface and rubbed back and forth until the coating is removed. One double rub corresponds to one back and forth movement of the hammer. The number of double rubs required to remove or mar the coating is recorded. 
     Flexibility is determined by a 1/8 in. wedge test using a Gardner Falling Dart Impact Tester (available from the Gardner Laboratory, Inc., Bethesda, Md.) configured for 0 to 1/8 in. (0 to 3.175 mm) wedge bend test. The bottom 3/4 in. (19.05 mm) of the panel is bent 180° over itself, exposing the coating to the outer surface, then sandwiched between two nonparallel steel plates that are hinged such that when completely together, they form a zero to 1/8 in. (0 to 3.175 mm) gap. The top plate is then impacted with the blunt end of the falling dart until the panel is bent from a zero to 1/8 in. (0 to 3.175 mm) wedge. The coated area over the bend is then wiped for approximately one minute with a 10% CuSO 4  /1N HCl solution which turns a copper-red color where the coating has failed and exposed steel metal. The percent pass value given in Table IV is calculated as the number of inches from the 1/8 in. (0 to 3.175 mm) end to the point of failure, as evidenced by the copper-red color, divided by the total 4 in. (101.6 mm) total length times 100. 
     
                       TABLE IV                                                    
______________________________________                                    
COATING PROPERTIES OF CATALYZED SYSTEMS                                   
FORM-                                                                     
ULATIONS                                                                  
FROM                    GARDNER     1/8 in.                               
EXAMPLE       MEK       IMPACT      WEDGE                                 
SAMPLE  OR COMP.  DOUBLE    in.-        BEND                              
NUMBER  EXPT.     RUBS      lbs.  J     % Pass                            
______________________________________                                    
I       18        30-50     &gt;180  &gt;20.34                                  
                                        100                               
II*     C.E..sup.a B                                                      
                  &gt;100      &gt;180  &gt;20.34                                  
                                        100                               
______________________________________                                    
 *Not an example of the present invention.                                
 .sup.a C.E. is Comparative Experiment.                                   
 
    
     EXAMPLE 36 
     Clear Casting Properties with Imidazolium Fluoborate Catalyst 
     Tetrabromobisphenol A 136 grams (0.5 equivalents), 181.5 grams (1.0 equivalent) of D.E.R.™383, 4.3 grams (0.1 equivalent) of sulfanilamide, 24.8 grams (0.4 equivalents) are stirred at 100° C.-130° C. until homogeneous, then 0.871 grams (2.0 millimoles) of the catalyst described in Example 1 is added. The mixture is stirred until homogeneous, degassed via evacuation for approximately one minute, then poured into preheated aluminum molds spaced 1/8 inch apart. The castings are cured for 16 hours at 150° C., followed by three hours at 200° C. The casting is then cooled and removed from the aluminum mold for testing as shown in Table V, Example 36. 
     EXAMPLE 37 
     Clear Casting Properties with Tetrabutylphosphonium Fluoborate Catalyst 
     Example 36 is repeated using 1.84 g (2.0 millimoles) of the catalyst described in Example 52. The testing results are shown in Table V, Example 37. 
     In these experiments, toughness is reported as the stress intensification factor, K q . The method for measuring K q  is an adaptation of ASTM E 399-83 for plastics materials from the original usage with metals. The compact tension test is now widespread in usage and is described in the J. Mater. Sci., Vol., 16, 2657, 1981. An individual test piece is cut as an approximate 1 inch (25.4 mm) square from a flat casting usually of 1/8 inch (3.175 mm) thickness. A dovetail notch is cut into one edge, centered, about 1/4 inch (6.25 mm) in depth. Next, a razor blade is inserted into this notch and tapped to produce a precrack. Tow holes are then drilled adjacent to the dovetail as indicated in ASTM E 399-83, allowing the test piece to be pinned into position in the Instron test machine. Extension of the sample now allows the force required to propagate opening of the precrack to be measured, using a test speed of 0.02 inches/minute (0.0085 mm/sec.). This force is used in the equation given in ASTM E-399, along with the required sample dimensions and actual precrack length, to calculate a &#34;stress intensification factor&#34;, K Q . This method is described by Lee, L. H. in Physicochemical Aspects of Polymer Surfaces, K. L. Mittal, ed., Plenum Press, New York, N.Y., 1983. 
     In these experiments, glass transition temperature (Tg) is measured by differential scanning calorimetry (DSC) using a calibrated DuPont Instrument (Model No. 912 with a 1090 controller). Samples are run under a nitrogen atmosphere with a temperature ramp of 10° C. per minute (0.1667° C./sec.). 
     
                       TABLE V                                                     
______________________________________                                    
CLEAR CASTING PROPERTIES OF CURED                                         
RESIN COMPOSITIONS                                                        
        CATALYST                                                          
        FROM         Glass                                                
EXAM-   EXAMPLE OR   Trans.  Toughness                                    
PLE     COMP.        Temp.   K.sub.q                                      
NUMBER  EXPT.        °C.                                           
                             psi × in.sup.0.5                       
                                     MPa.M.sup.0.5                        
______________________________________                                    
36       1           154     890     0.979                                
37      52           145     990     1.089                                
______________________________________                                    
 
    
     EXAMPLE 38 
     Preparation of Ethyltriphenylphosphonium Fluoborate Complex 
     A glass flask fitted with a stirrer, thermometer, and reflux condenser is charged with 11.4 grams of a 71.9% methanol solution, by weight, of ethyltriphenylphosphonium acetate·acetic acid (ETPPA·HAc) complex (0.0200 moles). To this stirred solution, 3.682 grams (0.0224 moles) of a 53.4% by weight aqueous solution of fluoboric acid (1.12 moles per mole of ETPPA·HAc) are slowly added during about five minutes. The heat from the reaction warms the solution to approximately 50° C. The solution is stirred for an additional 30 minutes as it cooled to near ambient temperature. Methanol is then added, 10.22 grams, to dilute the solution to 40% solids based on the weight of the ethyltriphenylphosphonium fluoborate complex. 
     The weight percent of ETTPA·HAc in methanol was determined by titration of the acetate group with 0.1006N perchloric acid (HClO 4 ) in acetic acid to a crystal violet endpoint (blue to green endpoint). It required 12.80 ml (0.001280 moles) of perchloric acid solution to titrate 0.7295 g of ETPPA·HAc/methanol solution dissolved in 15 ml of dichloromethane, which calculates to 71.9 wt. % of ETPPA·HAc in methanol. 
     EXAMPLES 39-45 
     Preparation of Ethyltriphenylphosphonium Fluoborate Complexes 
     The procedure described in Example 38 is repeated using the same procedure and amount of ETPPA·HAc, however the weight of fluoboric acid (53.4% aqueous solution) is varied as shown in Table IV. All experiments are diluted with methanol to 40% solids based on the combined weights of ETPPA·HAc and fluoboric acid. 
     
                       TABLE IV                                                    
______________________________________                                    
ETHYLTRIPHENYLPHOSPHONIUM FLUOBORATE                                      
COMPLEXES WITH VARYING RATIOS                                             
OF FLUOBORIC ACID                                                         
           FLUOBORIC   MOLES FLUOBORIC                                    
EXAMPLE    ACID SOL.   ACID PER MOLE OF                                   
NUMBER     (grams)     ETPPA.HAc                                          
______________________________________                                    
39         3.123       0.95                                               
40         3.353       1.02                                               
41         3.517       1.07                                               
38         3.682       1.12                                               
42         3.876       1.17                                               
43         4.010       1.22                                               
44         4.175       1.27                                               
45         4.339       1.32                                               
C.E..sup.a E*                                                             
           0.0.sup.b   0.0                                                
______________________________________                                    
 *Not an example of the present invention.                                
 .sup.a C.E. is Comparative Experiment.                                   
 .sup.b Ethyltriphenylphosphonium acetate.acetic acid complex alone as    
 catalyst.                                                                
 
    
     EXAMPLE 46 
     Preparation of Tetrabutylphosphonium Fluoborate Complex 
     A glass flask fitted with a stirrer, thermometer, and reflux condenser is charged with 6.20 grams (0.01 moles) of a 60.9% methanol solution, by weight, of tetrabutylphosphonium acetate·acetic acid complex (TBPA·HAc). To this stirred solution, 2.00 grams (0.0122 moles) of a 53.4% by weight aqueous solution of fluoboric acid (1.22 moles per mole of TBPA·HAc) are slowly added during about five minutes. The heat from the reaction warms the solution to approximately 50° C. The solution is stirred for an additional 30 minutes as it cooled to near ambient temperature. Methanol is then added, 3.916 grams, to dilute the solution to 40% solids based on the weight of the tetrabutylphosphonium fluoborate complex. 
     The weight percent of TBPA·HAc in methanol was determined by titration of the acetate group with 0.1006N perchloric acid (HClO 4 ) in acetic acid to a crystal violet endpoint (blue to green endpoint). It required 10.15 ml (0.001015 moles) of perchloric acid solution to titrate 0.6301 g of TBPA·HAc/methanol dissolved in 15 ml of dichloromethane, which calculates to 60.9 wt. % TBPA·HAc in methanol. 
     EXAMPLES 47-54 
     Preparation of Tetrabutylphosphonium Fluoborate Complexes 
     The procedure described in Example 46 is repeated using the same procedure and amount of tetrabutylphosphonium acetate·acetic acid complex (TBPA·HAc), however the weight of fluoboric acid (53.42% aqueous solution) is varied as shown in Table V. All experiments were diluted with methanol to 40% solids based on the combined weights of TBPA·HAc and fluoboric acid. 
     
                       TABLE V                                                     
______________________________________                                    
TETRABUTYLPHOSPHONIUM FLUOBORATE                                          
COMPLEXES WITH VARYING RATIOS OF                                          
FLUOBORIC ACID                                                            
           FLUOBORIC   MOLES FLUOBORIC                                    
EXAMPLE    ACID SOL.   ACID PER MOLE OF                                   
NUMBER     (grams)     TBPA.HAc                                           
______________________________________                                    
47         1.56        0.95                                               
48         1.67        1.02                                               
49         1.759       1.07                                               
50         1.84        1.12                                               
51         1.923       1.17                                               
46         2.005       1.22                                               
52         2.05        1.25                                               
53         2.087       1.27                                               
54         2.17        1.32                                               
C.E..sup.a F*                                                             
           0.0.sup.b   0.0                                                
______________________________________                                    
 *Not an example of the present invention.                                
 .sup.a C.E. is Comparative Experiment.                                   
 .sup.b Tetrabutylphosphonium acetate.acetic acid complex alone as        
 catalyst.                                                                
 
    
     EXAMPLES 55-63 
     Preparation of Other Fluoborate Complexes 
     The procedure of Example 38 is followed, using a ratio of 1.02 moles of fluoboric acid per equivalent of nitrogen containing compound as described in Table VI. Methanol is added to bring the percent solids based on the amine compound·fluoborate complex to 40% by weight. 
     
                       TABLE VI                                                    
______________________________________                                    
TETRABUTYLPHOSPHONIUM FLUOBORATE                                          
COMPLEXES WITH VARYING RATIOS OF                                          
FLUOBORIC ACID                                                            
EXAMPLE                                                                   
NUMBER    NITROGEN CONTAINING COMPOUND                                    
______________________________________                                    
55        PYRROLIDINE                                                     
56        N-METHYLMORPHOLINE                                              
57        MORPHOLINE                                                      
58        BUTYLAMINE                                                      
59        DIBUTYLAMINE                                                    
60        TRIBUTYLAMINE                                                   
61        DIETHYLANILINE                                                  
62        1-METHYLPYRROLIDINE                                             
63        PYRIDINE                                                        
______________________________________                                    
 
    
     EXAMPLE 64 
     Fluoborate Complex Via Silver Fluoborate 
     Vacuum dried tetrabutylphosphonium chloride, 1.82 grams (0.0062 moles) is dissolved in 5.84 grams of methanol and added dropwise to 1.20 grams (0.0062 moles) of silver fluoborate dissolved in 3.46 grams of methanol. The suspension is stirred at 25° C. for 30 minutes, and the silver chloride removed by filtration. The tetrabutylphosphonium fluoborate solution is concentrated to 40% solids by weight via vacuum removal of the excess methanol. 
     EXAMPLE 65 
     Fluoborate Complex Catalyzed Epoxy/Phenolic Systems 
     The catalysts described in Examples 38 to 64 are mixed with a 1:1 molar ratio of a diglycidyl ether of bisphenol A having an epoxy equivalent weight of 181.5 (D.E.R.™383 Epoxy Resin commercially available from The Dow Chemical Company) and bisphenol A (2,2-bis(4,4&#39;-hy-droxyphenyl)propane, PARABIS™ commercially available from The Dow Chemical Company) dissolved in the monomethylether of propylene glycol monoacetate (PMA). The epoxy resin (181.5 grams), bisphenol A (114 grams) and 73.88 grams of PMA are heated to 80°-100° C. under a nitrogen atmosphere until homogeneous, cooled to ambient temperature and 9.0 millimoles of catalyst added to 1.00 equivalent of epoxide in a manner that is described previously for Examples 18-34. Portions of these solutions are then stored at 50° C. and the 25° C. viscosity monitored as shown in Table VII. 
     
                                           TABLE VII                               
__________________________________________________________________________
50° C. Stability Study                                             
             Mol.                                                         
             of                                                           
Cat-         HBF.sub.4                                                    
alyst        per                              % of Control                
from         Mol.                             Viscosity.sup.f             
Ex.  Phosporus                                                            
             of P                                                         
                 Viscosity                        After                   
or   Cont.   Cont.                                                        
                 Initial After 1 Day                                      
                                    After 14 Days                         
                                              After                       
                                                  14                      
CE.sup.a                                                                  
     Compound                                                             
             Cmpd.                                                        
                 Cps Pa.s                                                 
                         Cps   Pa.s Cps   Pa.s                            
                                              Day Days                    
__________________________________________________________________________
39   ETPPA.HAc                                                            
             0.95                                                         
                 364 .364                                                 
                         460   .460 --    --  &lt;0.2                        
                                                  --                      
40   ETPPA.HAc                                                            
             1.02                                                         
                 366 .366                                                 
                         408   .408 13565 13.565                          
                                              &lt;0.2                        
                                                  &lt;6.8                    
41   ETPPA.HAc                                                            
             1.07                                                         
                 356 .356                                                 
                         385   .385 1014  1.014                           
                                              &lt;0.2                        
                                                  &lt;0.5                    
38   ETPPA.HAc                                                            
             1.12                                                         
                 348 .348                                                 
                         370   .370 543   .543                            
                                              &lt;0.2                        
                                                  &lt;0.3                    
42   ETPPA.HAc                                                            
             1.17                                                         
                 348 .348                                                 
                         391   .391 623   .623                            
                                              &lt;0.2                        
                                                  &lt;0.3                    
43   ETPPA.HAc                                                            
             1.22                                                         
                 436 .436                                                 
                         749   .749 1352  1.352                           
                                              &lt;0.4                        
                                                  &lt;0.7                    
44   ETPPA.HAc                                                            
             1.27                                                         
                 755 .755                                                 
                         3204  .3204                                      
                                    --    --  &lt;1.6                        
                                                  --                      
45   ETPPA.HAc                                                            
             1.32                                                         
                 2211                                                     
                     2.211                                                
                         10000 10.000                                     
                                    --    --  &lt;5.0                        
                                                  --                      
47   TBPA.HAc                                                             
             0.95                                                         
                 401 .401                                                 
                         570   .570 --    --  1.2 --                      
48   TBPA.HAc                                                             
             1.02                                                         
                 389 .389                                                 
                         460   .460 --    --  1.0 --                      
49   TBPA.HAc                                                             
             1.07                                                         
                 383 .383                                                 
                         444   .444 24378 24.378                          
                                              .9  12.2                    
50   TBPA.HAc                                                             
             1.12                                                         
                 377 .377                                                 
                         430   .430 6490  6.490                           
                                              .9  3.2                     
51   TBPA.HAc                                                             
             1.17                                                         
                 387 .387                                                 
                         407   .407 733   .733                            
                                              .9  .4                      
46   TBPA.HAc                                                             
             1.22                                                         
                 376 .376                                                 
                         393   .393 572   .572                            
                                              .8  .3                      
52   TBPA.HAc                                                             
             1.25                                                         
                 540 0.540                                                
                         1457  1.457                                      
                                    --    --  0.7 --                      
53   TBPA.HAc                                                             
             1.27                                                         
                 385 .385                                                 
                         462   .462 841   .841                            
                                              1.0 .4                      
54   TBPA.HAc                                                             
             1.32                                                         
                 407 .407                                                 
                         936   .936 5900  5.900                           
                                              2.0 3.0                     
55   Pyrrolidine                                                          
             1.03                                                         
                 830 0.830                                                
                         1136  1.136                                      
                                    1416  1.416                           
                                              --  --                      
56   N-methyl                                                             
             1.03                                                         
                 718 0.718                                                
                         845   0.845                                      
                                    1113  1.113                           
                                              3.1 &lt;5.6                    
     morpholine                                                           
57   Morpholine                                                           
             1.03                                                         
                 833 0.833                                                
                         997   0.997                                      
                                    1412  1.412                           
                                              --  --                      
58   Butyl amine                                                          
             1.03                                                         
                 720 .720                                                 
                         889   0.889                                      
                                    1268  1.268                           
                                              --  --                      
59   Dibutyl 1.03                                                         
                 602 .602                                                 
                         684   0.684                                      
                                    1049  1.049                           
                                              3.4 .5                      
     amine                                                                
60   Tributyl                                                             
             1.03                                                         
                 494 .494                                                 
                         580   0.580                                      
                                    849   0.849                           
                                              --  --                      
     amine                                                                
C.E.I                                                                     
     4-Phenyl                                                             
             1.03                                                         
                 688 .688                                                 
                         &gt;2000 g                                          
                               &gt;200 g                                     
                                    --    --  --  --                      
*    morpholine                                                           
61   N,N-Diethyl-                                                         
             1.03                                                         
                 667 .667                                                 
                         865   0.865                                      
                                    --    --  --  --                      
     aniline                                                              
62   1-Methyl                                                             
             1.03                                                         
                 663 .663                                                 
                         810   .810 1193  1.193                           
                                              --  --                      
     pyrrolidine                                                          
63   Pyridine                                                             
             1.03                                                         
                 733 .733                                                 
                         884   .884 1484  1.484                           
                                              --  --                      
C.E..sup.a E*                                                             
     ETPPA.HAc.sup.b                                                      
             0   1053                                                     
                     1.053                                                
                         &gt;200,000 g                                       
                               &gt;200 --    --  --  --                      
C.E..sup.a F*                                                             
     TBPA.HAc.sup.c                                                       
             0   898 .898                                                 
                         47,577                                           
                               47.557                                     
                                    &gt;200,000 g                            
                                          &gt;200                            
                                              --  --                      
C.E..sup.a G*                                                             
     Dibutylamine.sup.d                                                   
             0   1169                                                     
                     1.169                                                
                         20,328                                           
                               20.328                                     
                                    &gt;200,000 g                            
                                          &gt;200                            
                                              --  --                      
C.E..sup.a H*                                                             
     N-Methyl-                                                            
             0   1330                                                     
                     1.330                                                
                         26,999                                           
                               26.999                                     
                                    &gt;200,000 g                            
                                          &gt;200                            
                                              --  --                      
     morpholine.sup.e                                                     
__________________________________________________________________________
 *Not an example of the present invention.                                
 .sup.a Examples are designated by numerals whereas comparative experiment
 are disignated by letters.                                               
 .sup.b Ethyltriphenylphosphonium acetate.acetic acid complex employed    
 alone as catalyst.                                                       
 .sup.c Tetrabutylphosphonium acetate.acetic acid complex employed alone a
 catalyst.                                                                
 .sup.d Dibutylamine employed alone as catalyst.                          
 .sup.e Nmethylmorpholine employed alone as catalyst.                     
 .sup.f This value is determined by dividing the viscosity obtained in the
 appropriate example by the viscosity of a comparable formulation employin
 as the catalyst the same nitrogen or phosphorus compound except that it  
 has not been reacted with HBF.sub.4.                                     
 .sup.g Composition viscosity exceeded the test method (&gt;200,000 cps).