Method for doping a melt
FIELD OF THE INVENTION 
     The present invention relates to methods for doping a melt, specifically a silicon melt used for growing silicon dendritic web crystals, and the crystals grown from the doped melt. 
     BACKGROUND OF THE INVENTION 
     Dendritic web crystals are grown according to known methods by withdrawing (growing) a continuous ribbon or web from a pool of molten silicon. See, for example, U.S. Pat. No. 4,389,377. Generally, the method involves placing a silicon charge in a quartz crucible which is housed in a susceptor, placing heat shields over the crucible, melting the silicon using an inductive coil heater or other known heating methods, placing a seed dendrite in the melt, undercooling to form a button and pulling the button from the melt to drop dendrites from each end of the button. The dendrites grow into the melt and on continued pulling of the button from the melt, the dendrites support a liquid film of silicon that freezes as the material passes through a slot in the shields, thereby growing a single crystal silicon ribbon (also known as silicon dendritic web), between the dendrites. 
     In the standard growth process, precise amounts of boron or phosphorous are added to the molten silicon so that as the ribbon is growing, boron or phosphorous atoms are included in the ribbon structure to form a p-type or n-type crystal, respectively. N-type crystals are those having an excess of electrons, while p-type crystals are those having an excess of holes. The concentration of these &#34;impurity&#34; atoms in the silicon ribbon determines the base resistivity of the crystal, a key parameter in the efficiency of photovoltaic cells produced from a silicon ribbon crystal. 
     However, the use of phosphorus as a dopant has certain drawbacks. Dendritic web crystals are generally grown according to a semi-continuous process, whereby silicon feedstock is injected into the growth furnace as the ribbon crystals are being withdrawn. Maintaining uniform resistivity in an n-type phosphorous doped web requires that the dopant be replenished continuously along with the silicon to maintain a constant dopant concentration in the melt. However, it is extremely difficult to control the addition of phosphorus to the melt in order to obtain a uniform resistivity along the entire length of a ribbon crystal which is typically five to fifteen meters long and requires 5 to 15 hours of growing time. Thus, it would be useful to develop a doping method whereby the resistivity of the crystal could be controlled to be more uniform. It would also be useful to develop a method of doping in which there would be no need to replenish the dopant added after the initial charge. 
     Although the inventors are aware of no publications to this effect, it is believed that antimony may have been used as a dopant in the Czochralski crystal growth process, in the growth of n-type boules. However, antimony, if used at all, is not used as a dopant for any specific reason in Czochralski growth other than in order to conduct certain tests. Normally, n-type Czochralski boules are grown with phosphorus doping. 
     SUMMARY OF THE INVENTION 
     The present invention solves the problems of prior doping schemes by providing a doping method which includes the addition of antimony as a dopant, which results in crystals having a nearly uniform resistivity over the entire length of the crystal. The method of the present invention does not require the addition of antimony dopant after the initial charge, thereby significantly simplifying the crystal growing process. Crystals grown from melts doped according to the present invention exhibit superior properties relative to prior art methods, such as unexpectedly high photovoltaic cell efficiencies. 
     Processing of photovoltaic cells fabricated from web crystals which were lightly doped (5×10 14  atoms Sb per cm 3  Si web) with antimony was performed. These cells had measured efficiencies as high as 16.8%, were quite thin (117 μm) and had no surface passivation or texturing. Measurements of internal quantum efficiency showed a strong red response, with a minority carrier diffusion length of 272 μm, indicating superior quality material. These measurements were corroborated by measurements at Sandia National Laboratories. Sandia measurements gave efficiencies as high as 16.7% (AM 1.5, global, 25° C.), with internal quantum efficiencies very similar to those measured by the inventors. 
     Other details, objects and advantages of the invention will become apparent as the following description of the presently preferred embodiments and presently preferred methods of practicing the invention proceeds. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     The invention will become more readily apparent from the following description of preferred embodiments thereof shown, by way of example only, in the accompanying drawings, wherein: 
     FIGS. 1-3 are graphs showing the resistivity of web crystals grown from melts doped according to the present invention versus the cumulative weight of all crystals grown from the melt. 
     FIG. 4 is a graph which compares the calculated depletion of dopant atoms of phosphorus and antimony in a charge. 
     FIG. 5 is a graph which illustrates the average resistivity of crystals grown from melts doped according to the present invention versus the number of antimony dopant atoms in the initial charge. 
     FIG. 6 is a graph illustrating internal quantum efficiency versus wavelength for a thin web photovoltaic cell produced from web crystal grown from a melt doped according to the present invention. 
     FIG. 7 is a graph used to determine hole diffusion length from quantum efficiency data for a web photovoltaic cell produced from web crystal grown from a melt doped according to the present invention. 
     FIG. 8 is a graph illustrating the internal quantum efficiency versus wavelength for a photovoltaic cell produced from web crystal grown from a melt doped according to the present invention. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     According to the present invention, a silicon melt used for growing silicon dendritic web crystals is doped with antimony, preferably in quantities of at least 1.8×10 15  atoms of antimony/gram of silicon melt. The antimony may be added directly to the melt in pellet form, or may be diffused into a silicon substrate, such as a silicon wafer, on a heavily doped silicon wafer. These dopant sources are added to the melt prior to starting the crystal growth process. The antimony may either be added before or after the silicon is melted. In either case, the antimony is allowed to melt and diffuse throughout the silicon melt before commencing crystal growth. 
     Antimony (Sb) is an n-type dopant with a low segregation coefficient in silicon. The segregation coefficient is the ratio of dopant concentration in a molten solution to the dopant concentration in the solidified crystal produced from that molten solution. The segregation coefficient of antimony in silicon is 0.023 as compared to 0.35 for phosphorous in silicon. It is preferable, in order to achieve acceptable photovoltaic cell efficiencies, for dendritic web crystals to have resistivities in the 4-50 Ωcm range. In order to achieve this range of resistivity, the antimony concentration must be 15 times greater than the phosphorous concentration in the molten silicon used to produce similar crystals having similar resistivities. During the growth process, the concentration of antimony in the molten silicon drops 15 times more slowly as compared to phosphorous. Extremely long crystals have been grown with substantially uniform resistivity and with no replenishment of the antimony dopant. In fact, entire growth runs (5 days) with a total grown crystal weight of 600 grams have been made with no dopant additions during growth. In these runs, the web resistivity varied within the above 4-50 Ωcm specification limits. 
     FIGS. 1-3 show the resistivity of web crystals grown in three growth runs from melts doped with antimony according to the present invention. In these figures, the resistivity of a given crystal is plotted against the cumulative weight of all crystals grown up to that time, in other words, the total amount of silicon removed from the charge. 
     The initial resistivity was controlled by the amount of antimony added to the charge. FIG. 1 shows the data for a run of crystals grown from a melt having 1.8×10 18  antimony atoms in the charge, in which the resistivity varied from 20 Ωcm to 27 Ωcm over the course of the run. FIG. 2 shows data for a run having 2.44×10 18  antimony atoms in the charge, in which the resistivity varied from 6 Ωcm to 13 Ωcm. Similarly, FIG. 3 shows data on yet another run having 7.4×10 18  atoms of antimony in the charge, in which the resistivity varied from 1.2 Ωcm to 2.2 Ωcm. In all cases the silicon charge was 280 grams, which was replenished with silicon as needed, however, no further antimony dopant was added over the course of each respective run. These variations for FIGS. 1, 2 and 3 are within specification limits of the grown web. FIGS. 1-3 indicate that uniform resistivity material over a wide range of resistivities can be grown using antimony doping in the initial charge and with no further doping required, even though silicon is added to the charge during the run to replace the silicon used in the grown web. As used herein, the term &#34;uniform resistivity&#34; is defined to mean a resistivity falling within the specified range of 4-50 Ωcm. 
     Antimony is also advantageous as an n-type dopant because of its low diffusion constant. Dopant atoms in the vicinity of the web surface can diffuse out of the material when the web is at high temperatures in the growth furnace. Because of its low diffusion constant in silicon, antimony tends to remain in the web material while other dopants, such as phosphorous, diffuse out. When antimony is used, the dopant profile through the thickness of the web remains uniform, even for light doping. This is not necessarily the case when phosphorous is used as the dopant. 
     In addition, the doping along the length of the web crystals (and even from crystal to crystal) remains nearly constant because of the low segregation coefficient (0.023) of antimony in crystalline silicon as compared to 0.35 for phosphorous. This has the important practical benefit that the antimony dopant need only be added to the starting silicon charge at the beginning of the growth run. The furnace can then produce web crystals over its full operating cycle (five days) without the need to add additional dopant to the melt, despite the fact that silicon is replenished to maintain a constant melt level as the crystal is withdrawn. 
     FIG. 4 illustrates a graphical comparison of the calculated depletion of dopant atoms in a silicon charge. The graph plots number of dopant atoms in the charge (× 10 18 ) versus the weight of web grown in grams. As illustrated, the amount of phosphorous in the charge (symbolized by +) is depleted by nearly 25% after growth of 600 grams of web, while the amount of antimony in the charge (symbolized by □) is depleted by less than 5% over the same amount of web growth. 
     FIG. 5 illustrates the average resistivity (ohm-cm) of all crystals grown from a melt doped with antimony according to the present invention versus the number of antimony dopant atoms (×10 18 ) added to the initial charge. The solid line shown in this figure is the calculated resistivity based on the original dopant concentration in the charge. There is good agreement between the calculated curve and the experimental data. As seen in this figure, runs of antimony doped web with resistivities ranging from 2 Ωcm to 40 Ωcm have been grown with similar results; that is, the resistivity remained relatively constant without any dopant being added during the runs. 
     A number of photovoltaic cells have been fabricated on crystals produced in the antimony doped growth runs discussed above. In addition to obtaining uniform dopant profiles with antimony, cell data indicates that antimony may be responsible for increasing hole diffusion lengths in web material. The mechanism by which this occurs is not readily understood at this time, but it may be related to the fact that the antimony has a strong affinity for oxygen. It is conceivable that the antimony is affecting the oxygen content or the oxygen distribution in web material and is proving to be beneficial to its electrical quality. What has been shown recently is that superior web cells with a conventional p +  nn +  structure can be made with thin (.sup.˜ 100 μm) material which is lightly doped (5×10 14  atoms Sb per cm 3  of Si web) with antimony. 
     In the fabrication of these cells, a boron diffusion (BBr 3 ) was used to create the front p +  n junction, and a phosphorous diffusion (POCl 3 ) was used for the back n +  n high-low junction. An aluminum layer was deposited on the back of the cell for a back surface reflector (BSR), but no surface passivation or texturing was employed. 
     Table 1 shows lighted IV and diffusion length data recorded for a number of web strips produced throughout a 5 day growth run. The cell data are remarkably uniform considering that more than 35 meters of web crystal were grown between the first crystal (4-413-1.2) and the last (4-413-13.8). The resistivity only varied from 9 Ωcm to 15 Ωcm from the beginning to the end of the run with no dopant added during the run. 
     
                       TABLE 1                                                     
______________________________________                                    
HIGH QUALITY CELLS (NO AR COATING) FROM                                   
LIGHTLY DOPED N-TYPE WEB CRYSTALS                                         
FROM A SINGLE GROWTH RUN (RUN SBWEB-1)                                    
       Web       J.sub.sc  V.sub.oc  η                                
                                          L.sub.p (SPV)                   
Cell ID                                                                   
       Crystal   (mA/cm.sup.2)                                            
                           (V)  FF   (%)  (μm)                         
______________________________________                                    
1.2-1  4-413-1.2 24.0      0.580                                          
                                0.777                                     
                                     10.82                                
                                          197                             
1.2-2  4-413-1.2 24.4      0.581                                          
                                0.776                                     
                                     11.03                                
                                          191                             
1.2-3  4-413-1.2 24.2      0.580                                          
                                0.774                                     
                                     10.90                                
1.2-4  4-413-1.2 24.2      0.579                                          
                                0.774                                     
                                     10.85                                
1.3-1  4-413-1.3 23.5      0.558                                          
                                0.692                                     
                                      9.09                                
1.3-2  4-413-1.3 23.6      0.567                                          
                                0.731                                     
                                      9.78                                
1.3-3  4-413-1.3 23.6      0.572                                          
                                0.753                                     
                                     10.16                                
1.3-4  4-413-1.3 23.4      0.567                                          
                                0.766                                     
                                     10.18                                
3.5-1  4-413-3.5 23.0      0.556                                          
                                0.778                                     
                                      9.96                                
3.5-2  4-413-3.5 23.2      0.558                                          
                                0.781                                     
                                     10.12                                
3.5-3  4-413-3.5 23.2      0.558                                          
                                0.775                                     
                                     10.06                                
3.5-4  4-413-3.5 23.3      0.561                                          
                                0.782                                     
                                     10.20                                
3.6-1  4-413-3.6 23.3      0.552                                          
                                0.780                                     
                                     10.05                                
3.6-2  4-413-3.6 23.4      0.548                                          
                                0.778                                     
                                      9.97                                
3.6-3  4-413-3.6 22.6      0.553                                          
                                0.778                                     
                                      9.71                                
6.4-1  4-413-6.4 23.8      0.558                                          
                                0.783                                     
                                     10.43                                
6.4-2  4-413-6.4 23.6      0.555                                          
                                0.778                                     
                                     10.20                                
6.4-3  4-413-6.4 23.6      0.555                                          
                                0.779                                     
                                     10.22                                
6.4-4  4-413-6.4 23.4      0.553                                          
                                0.773                                     
                                     10.00                                
6.5-1  4-413-6.5 23.6      0.553                                          
                                0.763                                     
                                      9.96                                
6.5-2  4-413-6.5 23.8      0.553                                          
                                0.776                                     
                                     10.20                                
6.5-3  4-413-6.5 23.7      0.550                                          
                                0.776                                     
                                     10.11                                
6.5-4  4-413-6.5 23.5      0.553                                          
                                0.780                                     
                                     10.13                                
10.5-1 4-413-10.5                                                         
                 23.7      0.557                                          
                                0.699                                     
                                      9.21                                
10.5-2 4-413-10.5                                                         
                 24.0      0.562                                          
                                0.765                                     
                                     10.30                                
10.5-3 4-413-10.5                                                         
                 24.0      0.561                                          
                                0.774                                     
                                     10.42                                
10.5-4 4-413-10.5                                                         
                 23.8      0.561                                          
                                0.774                                     
                                     10.31                                
10.6-2 4-413-10.6                                                         
                 21.9      0.521                                          
                                0.775                                     
                                      8.84                                
10.6-3 4-413-10.6                                                         
                 22.9      0.533                                          
                                0.778                                     
                                      9.48                                
10.6-4 4-413-10.6                                                         
                 23.0      0.536                                          
                                0.777                                     
                                      9.60                                
12.2-1 4-413-12.2                                                         
                 23.8      0.565                                          
                                0.772                                     
                                     10.34                                
                                          243                             
12.2-2 4-413-12.2                                                         
                 24.0      0.567                                          
                                0.773                                     
                                     10.53                                
                                          210                             
12.2-3 4-413-12.2                                                         
                 24.0      0.562                                          
                                0.761                                     
                                     10.27                                
12.2-4 4-413-12.2                                                         
                 23.7      0.566                                          
                                0.775                                     
                                     10.40                                
13.8-1 4-413-13.8                                                         
                 22.6      0.545                                          
                                0.785                                     
                                      9.66                                
13.8-2 4-413-13.8                                                         
                 22.7      0.553                                          
                                0.783                                     
                                      9.82                                
FZ-3   Float Zone                                                         
                 25.2      0.593                                          
                                0.785                                     
                                     11.73                                
                                          451                             
______________________________________                                    
 Notes to Table 1:                                                        
 1. Cell area is 1.00 cm.sup.2 and cells had no antireflective coating.   
 2. Measurement conditions: AM 1.5, 100 mW/cm.sup.2, 25° C.        
 3. Web growth run 4413 produced 14 crystals.                             
 4. Web growth crystals were ntype, 9 to 15 ohmcm, with thicknesses rangin
 from 111 to 146 μm.                                                   
 5. Floatzone wafer (J88412) had a (100) surface, was doped ntype to 5-8  
 ohmcm, and was 280 μm thick.                                          
 
    
     Two sections of web crystals were chosen for deposition of an evaporated double layer antireflective coating (600 angstroms of ZnS and 1000 angstroms of MgF 2 ). One section was from a crystal grown at the beginning of the run (4-413-1.2), and the other section was from a crystal grown near the end of the five-day run (4-413-12.2). 
     Pertinent data measured for these cells are given in Table 2. The highest efficiency obtained was 16.8% (AM 1.5, 1000 mW/cm 2 , 25° C.), with a J sc  of 36.5 mA/cm 2 , a V oc  of 0.589 V, and a FF of 0.781. The hole diffusion length in the base of these cells is typically 200 μm, as measured by the surface photovoltage technique; and the thickness is approximately 115 μm. It is noteworthy that such high efficiencies can be obtained from material produced near the end of a five-day growth run, indicating that the electrical quality of the web material remains high throughout the entire run. 
     
                       TABLE 2                                                     
______________________________________                                    
LIGHTLY-DOPED, THIN, HIGH EFFICIENCY                                      
DENDRITIC WEB SILICON SOLAR CELLS                                         
        J.sub.sc   V.sub.oc      η L.sub.p (SPV)                      
Cell ID (mA/cm.sup.2)                                                     
                   (V)     FF    (%)   (μm)                            
______________________________________                                    
A. Cells Produced from First Web Crystal of Growth Run                    
4-413-1.2 (117 μm thick)                                               
1.2-1   36.1       0.589   0.784 16.6  197                                
1.2-3   36.4       0.589   0.777 16.7  191                                
1.2-4   36.5       0.589   0.781 16.8  --                                 
B. Cells Produced From Twelfth Web Crystal                                
of Growth Run 4-413-12.2 (110 μm thick)                                
12.2-1  35.9       0.580   0.774 16.1  243                                
12.2-2  36.1       0.580   0.772 16.1  210                                
12.2-4  35.8       0.581   0.773 16.1  --                                 
______________________________________                                    
 Notes to Table 2:                                                        
 1. Web Crystals are doped ntype with antimony at a concentration of 5    
 × 10.sup.14 atoms Sb per cm.sup.3 of silicon web.                  
 2. Cell size is 1 × 1 cm, defined by a mesa.                       
 3. Cell structure is p.sup.+ nn.sup.+ with a DLAR (600 angstrom ZnS and  
 1000 angstrom MgF.sub.2) and aluminum BSR. No surface passivation or     
 texturing was used. (Run SBWEB1).                                        
 4. Measurement conditions: AM1.5, 100 mW/cm.sup.2, 25° C. (measure
 at Westinghouse R &amp; D Center).                                           
 
    
     The cells listed in Table 2 were sent to Sandia National Laboratories for an independent measurement of cell parameters, courtesy of Dr. D. Arvizu. The values given in Table 2 were corroborated at Sandia, with the efficiencies measured at Sandia generally .sup.˜ 0.2% (absolute) lower than those given in Table 2. The Sandia measurements included a correction for the small difference between their illumination source and the true AM 1.5 global spectrum (spectral mismatch). The global spectrum is appropriate for cells intended for use in flat plate arrays rather than concentrator arraYs. The cell (1.2-4) with the highest efficiency (16.7%) had a J sc  of 36.7 mA/cm 2 , a V oc  of 0.586 V, and a FF of 0.774 according to the Sandia measurements (AM 1.5 global, 100 mW/cm 2 , 25° C.). This efficiency represents the highest independently-measured value for any web photovoltaic cell yet produced. 
     Measurements of internal quantum efficiency for cells 1.2-1 and 12.2-4 were also made at Sandia from 0.35 μm to 1.10 μm. These measurements were in agreement with similar measurements made by the inventors, as given in FIG. 6 for cell 1.2-4. FIG. 6 plots the internal quantum efficiency (%) versus wavelength (μm) for web cell 4-413-1.2-4 having a thickness of 117 μm, a p +  nn +  structure, a base doping with antimony of 5×10 14  atoms Sb/cm 3  of silicon web, and an efficiency of 16.8%. The measurement of internal quantum efficiency showed a strong red response of the cell, as expected for material in which the diffusion length significantly exceeds the thickness, but only a modest blue response. This is consistent with a long diffusion length in the cell base and the absence of surface passivation, respectively. If surface passivation (thin thermal oxide) improves the blue response, then cell efficiencies exceeding 17% may be obtained. 
     An estimate of the hole diffusion length in the base of cell 1.2-4 can be made from the quantum efficiency data. The reciprocal of the spectral absorption coefficiency (β) is plotted against X-1, where X is the ratio of the number of photons absorbed in the base per unit time to the number of electrons diffused from the base into the emitter per unit time. The slope of such a plot is a measure of the hole diffusion length. From FIG. 7, the value of diffusion length is determined to be 272 μm for web cell 4-413-1.2-4 having a thickness of 117 μm. 
     The hole lifetime in the base of antimony doped web cells was also measured by the OCD open circuit decay) technique. These cells were fully processed, including the double layer antireflective coating. The results are summarized in Table 3 for cells fabricated from web crystals grown near the beginning (4-413-1.2) and near the end (4-413-12.2) of a five day run. The cell area is 1.00 cm 2 , and an injection current of approximately 30 mA was used in the measurement. Lifetimes as high as 66.5 μs were measured. The corresponding hole diffusion lengths were calculated from the measured lifetimes, assuming the diffusion constant for holes is 11.9 cm 2/  V-sec, for the web material doped with antimony to 5×10 14  atoms Sb cm -3  of silicon web. Such calculated diffusion lengths ranged from 226 to 281 μm, which considerably exceed the thickness of the cells (110 and 117 μm) (see note 3 to Table 3). These diffusion lengths are in good agreement with values obtained from quantum efficiency measurements. The efficiencies measured for the cells prior to the application of the antireflective coating are also listed in Table 3. 
     
                       TABLE 3                                                     
______________________________________                                    
MEASURED LIFETIME FOR THIN WEB CELLS                                      
LIGHTLY DOPED WITH ANTIMONY (RUN SBWEB-1)                                 
        τ.sub.p (OCD)                                                 
                    L.sub.p = D.sub.p τ.sub.p                         
                               η (without AR)                         
Cell ID (μs)     (μm)    (%)                                        
______________________________________                                    
4-413-1.2-2                                                               
        66.5        281        11.03                                      
4-413-1.2-3                                                               
        65.7        280        10.90                                      
4-413-1.2-4                                                               
        61.5        271        10.85                                      
4-413-12.2-1                                                              
        43.1        226        10.34                                      
4-413-12.2-2                                                              
        50.3        245        10.53                                      
______________________________________                                    
 Notes to Table 3:                                                        
 1. Lifetime in finished cells measured by open circuit voltage decay (OCD
 with an injected amount of approximately 30 mA (cell area is 1.00        
 cm.sup.2).                                                               
 2. D.sub.p taken to be 11.9 cm.sup.2 /Vsec based on antimony doping of   
 approximately 5 × 10.sup.14 cm.sup.-3 for calculating L.sub.p from 
 τp.                                                                  
 3. Cells from crystal 4413-1.2 are 117 μm thick and from crystal      
 4413-12.2 are 100 μm thick.                                           
 
    
     Large area (24.5 cm 2 ) bifacial cells have been fabricated on crystals produced in the antimony doped growth runs of the present invention. These cells were produced using the Westinghouse baseline process. A single layer of antireflective coating was applied by a standard dipping technique. 
     Table 4 gives data on seven such solar cells, having resistivities from 10-20 Ωcm. The data further demonstrate that high efficiency cells can be fabricated from antimony doped web. The minority carrier diffusion length of representative cells was measured at 100-200 μm which indicates a good quality bulk material with few recombination centers. Therefore, the antimony doped web is at least as high quality as the phosphorous doped material but has the added advantage of producing uniform resistivity throughout the run without requiring dopant additions. The efficiencies given are for illumination on the front surface. When illuminated from the back, the cell efficiency was 95-97% that of the front (after adjustment for the metal coverage on the back). This data confirms that cell diffusion lengths in excess of the 100-150 μm cell thickness have been maintained on full size cells during processing operations using standard processing equipment. 
     
                       TABLE 4                                                     
______________________________________                                    
Test Data On Cells Fabricated On Antimony Doped Web                       
                   Resistivity                                            
                             V.sub.oc                                     
                                  I.sub.sc Eff.                           
Cell ID Growth Run (Ω cm)                                           
                             (V)  (A)  FF  (%)                            
______________________________________                                    
12B     6429       20        .580 .777 .77 14.2                           
16B     6429       20        .596 .774 .79 14.7                           
17A     6429       20        .561 .772 .79 13.9                           
49A     6430       17        .597 .726 .77 13.8                           
53A     6430       16        .597 .744 .79 14.4                           
20      6430       21        .596 .740 .78 14.0                           
10      6434       10        .585 .746 .77 13.7                           
______________________________________                                    
 
    
     Data on front and back surface illumination for three further cells is shown in Table 5. A maximum efficiency of 15.3% was obtained. Since these cells were thin (about 115 μm) and did not have a back surface reflector, about 10% of the incident light in the AM 1.5 spectra passed through the cell without being absorbed. If these transmitted photons were absorbed and collected, the cell efficiency would approach 16%. Of special interest in this table are the high values of the short circuit current and efficiency developed under back surface illumination. This indicates a very high quality bulk material with diffusion lengths well in excess of the cell thickness. 
     
                                           TABLE 5                                 
__________________________________________________________________________
MEASURED PARAMETERS FOR ANTIMONY                                          
DOPED BIFACIAL WEB CELLS                                                  
         Resis-                                                           
         tivity                                                           
             Area                                                         
                 Illumi-                                                  
                     J.sub.sc                                             
                           V.sub.oc                                       
                                 η                                    
                                    J.sub.sc (back)/                      
Cell                                                                      
   Crystal                                                                
         (Ω cm)                                                     
             (cm.sup.2)                                                   
                 nation                                                   
                     (mA/cm.sup.2)                                        
                           (V)                                            
                              FF (%)                                      
                                    J.sub.sc (front)                      
__________________________________________________________________________
75B                                                                       
   6-434-6.6                                                              
         9   24.5                                                         
                 front                                                    
                     31.8  0.593                                          
                              0.809                                       
                                 15.3                                     
                                    0.95                                  
             21.2                                                         
                 back                                                     
                     30.3  0.587                                          
                              0.791                                       
                                 14.1                                     
81B                                                                       
   6-434-7.5                                                              
         9   24.5                                                         
                 front                                                    
                     31.4  0.592                                          
                              0.810                                       
                                 15.1                                     
                                    0.97                                  
             21.2                                                         
                 back                                                     
                     30.5  0.586                                          
                              0.807                                       
                                 14.4                                     
51A                                                                       
   6-430-1.11                                                             
         19  24.5                                                         
                 front                                                    
                     31.4  0.590                                          
                              0.790                                       
                                 14.6                                     
                                    0.97                                  
             21.2                                                         
                 back                                                     
                     30.5  0.587                                          
                              0.814                                       
                                 14.6                                     
__________________________________________________________________________
 Notes to Table 5:                                                        
 1. Under the back illuminated conditions, the cell area was corrected to 
 account for the added metal coverage. A value of 21.2 cm was used rather 
 than 24.5 cm.                                                            
 2. Cells have single layer AR coating and no surface passivation.        
 3. Backto-front ratio of J.sub.sc is nearly unity indicating a hole      
 diffusion length which significantly exceed cell thickness.              
 4. Measurement conditions: AM 1.5, 100 mW/cm.sup.2, 25° C.        
 5. Cells processed in AESD Run 7001.                                     
 
    
     FIG. 8 shows the internal quantum efficiency of cell 75B under front surface illumination as a function of wavelength. THe cell had a p 30  nn +  structure, a base doping of 4×10 14  atoms of antimony per cm 3  of web material, a thickness of 108 μm, and a J sc  (back)/J sc  (front) of 1.00. The cell has an excellent red and blue response. The diffusion length, obtained in the same manner as in FIG. 7, was 333 μm, again indicating a high quality bulk material which results in a high cell efficiency. 
     Table 6 shows a direct comparison between photovoltaic cell efficiencies of dendritic web crystals produced with the conventional phosphorous dopant and dendritic web crystals doped with antimony according to the present invention. The data in Table 6 was generated using identical processing steps, except that the dopants used during growth were different. The cells noted in this table were 25.4 cm 2  in area. 
     
                       TABLE 6                                                     
______________________________________                                    
PROPERTIES OF CELLS FABRICATED OF WEB                                     
DOPED WITH ANTIMONY OR PHOSPHOROUS                                        
PHOSPHOROUS                 ANTIMONY                                      
DOPING                      DOPING                                        
CELL        EFF                 CELL  EFF                                 
ID          %                   ID    %                                   
______________________________________                                    
18          13.9                12    14.2                                
19          13.7                16    13.9                                
17          13.9                17    14.7                                
21          13.6                18    13.9                                
22          13.9                49    13.8                                
77          14.0                53    14.4                                
78          13.9                20    14.0                                
79          13.8                10    13.7                                
86          13.6                75    15.3                                
87          13.6                81    15.3                                
88          13.7                87    14.2                                
89          13.5                51    14.6                                
AVG         13.8       AVG          14.3                                  
______________________________________                                    
 
    
     This data conclusively demonstrates that the use of antimony as a dopant results in a noticeable and unexpected improvement in photovoltaic cell efficiency relative to cells produced from conventional phosphorous doped web. 
     The cell data given in this disclosure confirm that high quality cells can be fabricated on antimony doped web. This data, in addition to the experimental data demonstrating the uniformity of crystal resistivity without need for further doping over the course of the growth run indicate that antimony is an excellent dopant for producing n-type web. 
     Although the invention has been described in detail in the foregoing for the purpose of illustration, it is to be understood that such detail is solely for that purpose and that variations can be made therein by those skilled in the art without departing from the spirit and scope of the invention as described by the claims. For example, it is expected that those skilled in the art would understand that dendritic web crystals may be grown from melts other than silicon, such as qermanium and other Group IV elements, and that the antimony doping of such melts would have similar advantages to those described herein.