Method of removing plastic material from optical fiber cable
BACKGROUND 
     This invention relates to a unique gel composition, composed of either ethyl acetate or butyl acetate, or a mixture of both ethyl acetate and butyl acetate, and method of using same to remove matrix material from matrix enclosed optical fibers, e.g., ribbon cable. 
     Optical fibers, in the form they are received from the manufacturer, usually comprise a glass core circumscribed by a glass cladding. Circumscribing this glass portion is a first and then a second plastic coating usually made from polyurethane acrylate, the first and inner layer having a lower modulus than the outer layer. See U.S. Pat. No. 5,181,268 for an example, the contents of which are incorporated herein by reference. From such fibers either a loose tube, a ribbon, or a tight buffered cable can be made. 
     In the case of ribbon cable, a plurality of as received fibers are aligned, one to another, and are circumscribed by what is called a matrix. The matrix bonds the fibers one to another in a planer or ribbon configuration. Usually the matrix is UV-cured polyurethane acrylate. In the field there comes a time when the terminal ends and/or mid-span portion of the ribbon cable must be stripped of its matrix so that fiber ends of the optical fibers are exposed and made accessible for splicing to a fiber end of another cable. 
     Stripping the matrix of optical fiber cables, such as ribbon cable, has in the past been accomplished by soaking the terminal or mid-span portion of a cable sought to be stripped in either ethyl alcohol or acetone. Acetone has been objected to because of its strong odor and propensity to chemically attack other cable components and ethyl alcohol is not effective on most ribbon matrix materials presently used. Customers such as the Regional Bell Operating Companies, when faced with use of these compounds, have required an alternative. This invention is directed towards a solution to this problem. 
     BRIEF DESCRIPTION OF THE INVENTION 
     The invention comprises the use of a gel comprising: (a) ethyl and/or butyl acetate; (b) a filler, which acts as a thickening agent, and optionally (c) a fragrance enhancer. A fragrance enhancer is generally not necessary if butyl acetate is employed. Such a mixture causes the matrix of a ribbon or other tight buffered optical fiber cable to soften, swell and break up. Removing the matrix material with a fibrous scouring pad, exposing optic fibers in their as-received state, is the last step. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     FIGS. 1-8 show a typical procedure for access to a given fiber or fibers at mid-span of a fiber optic ribbon cable. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     Shown by FIGS. 1-8 are the mechanical steps used to access a given fiber at mid-span. Matrix material may be removed from a ribbon cable terminal portion in much the same fashion. 
     Shown by element 10 of FIG. 1 is a cross-section of a typical prior art ribbon cable, with optical fibers 11 circumscribed by ribbon matrix 12. It is the removal of matrix 12 that is the result of the following described steps. In FIG. 2, there is shown a splice closure or splice tray 13 in which ribbon cable 10 enters and exits leaving a loop or slack as shown by element 14. Near the center 15 of loop 14 access to one or more fibers is desired. Taping the loop 14 at position 16 delimits the portion of loop 14 desired to be accessed. 
     As shown in FIG. 3, a marked section of ribbon to be accessed (between tapes 16) is placed on top of scrub pad strip 18, impregnated with the ethyl and/or butyl acetate gel as hereafter described. Both sides of loop 14 are coated with the ethyl and/or butyl acetate gel. After thoroughly applying the gel to ribbon loop 14, the coated section is placed on the scrub pad strip 18 and allowed to sit for 5 to 10 minutes. Optionally, the coated section can be wrapped in a non-absorbent plastic or treated paper sheet to reduce evaporation of the ethyl acetate and/or butyl acetate from the gel. This period of time has been found appropriate for most matrix materials (for example, polyurethane acrylate) having a matrix thickness between 20-50 microns. The acetate gel causes the plastic matrix to swell and soften. After the above described waiting period, the scrub pad is used as shown in FIG. 4. Pad 18 is folded over the gel coated area of ribbon cable 10 and wiped over such area by starting from the same end each time and sliding the folded plastic pad 18 in the same direction until the ribbon matrix 12 has been removed. 
     Working from an outside edge, one fiber at a time is grasped and broken out along the entire length of loop 14. See FIGS. 5 and 6. Any remnants of ribbon matrix 14 can be removed by a wiping action as shown in FIG. 7. Verification that all of the matrix material has been removed can be made by running fingers along the fibers. If they feel and appear uniform in dimension and texture, then the matrix material has been removed and fibers are ready for splicing as desired. Scrub pad 18 can be made from any plastic or animal fiber content not soluble in ethyl or butyl acetate. A pad of plastic fibers sold in grocery stores under the mark &#34;Scotch Brite&#34; has proven satisfactory. 
     Various percentages of the gel components have been used and found to be sufficient. Examples of such are as follows: 
     
         ______________________________________                                    
          % By Volume                                                     
______________________________________                                    
Ethyl Acetate                                                             
             0    10           20  30                                     
Butyl Acetate                                                             
            30    20           10   0                                     
Filler      70    70           70  70                                     
______________________________________                                    
Gel Mixture                                                               
           % By Volume                                                    
______________________________________                                    
Solvent    30    32       34  36     38  40                               
Filler     70    68       66  64     62  60                               
______________________________________                                    
Solvent Mixture                                                           
            % By Volume                                                   
______________________________________                                    
Ethyl Acetate                                                             
            100    80      60  40     20   0                              
Butyl Acetate                                                             
             0     20      40  60     80  100                             
______________________________________                                    
Preferred Embodiments                                                     
              % By Volume                                                 
______________________________________                                    
Ethyl Acetate  0       10    20     30  40                                
Butyl Acetate 40       30    20     10   0                                
Filler        60       60    60     60  60                                
______________________________________                                    
 Solvent is butyl acetate or ethyl acetate or mixtures thereof.           
 See Table below.                                                         
 Filler is fumed silica or cornstarch.                                    
 
    
     The example formulations were prepared and applied as set forth in the above explanation of FIGS. 1-8. Instead of applying the gel by a plastic pad 18 the gel may be packaged in a tube, foil packet, or a syringe and applied like applying toothpaste to the cable matrix. It is obvious that the applying medium must be essentially insoluble in butyl and/or ethyl acetate, either per se or in gel form. 
     Ethyl acetate has a disagreeable odor and may be used with a fragrance enhancer (up to 14% by volume), which can be obtained from Atlanta Fragrance, Inc. or Aromatics Flavors, Inc., both of Atlanta, Ga. A fragrance can be used with butyl acetate but ordinarily is not necessary. Fumed silica can be obtained from Degussa Corp of Richfield Park, N.J. and has a particle size in the range of 7 to 40 nanometers, and the ethyl and butyl acetate can be secured from Fisher Scientific, Inc. of Atlanta, Ga. 
     A variety of modifications which do not depart from the scope and spirit of the invention will be evident to persons or ordinary skill in the art from the disclosure herein. The following claims are intended to cover the specfic embodiments set forth herein as well as modifications, variations, and equivalents.