Piezoelectric ceramic composition
BACKGROUND OF THE INVENTION 
     1. FIELD OF THE INVENTION 
     The present invention relates to a piezoelectric ceramic composition, and in particular to a piezoelectric ceramic composition suitable for use in a ceramic oscillator, ceramic discriminator, ceramic filter or surface wave elastic element. 
     2. BACKGROUND ART 
     The parts used in conventional electronic equipment and devices are lead-type resin molded products. Soldering is performed by inserting the lead wires of the parts into a printed circuit board and immersing in a molten solder bath the surface with no parts mounted on it. Thus, the mounted parts are not exposed to temperatures of 200° C. or higher. 
     With the progress made in recent years in the miniaturization of electronic equipment and devices, the use of surface packaging and mounting is increasing. To solder parts in surface packaging, chip parts with no lead wires on them are provisionally mounted on a printed circuit board and the entire printed circuit board is heated in a reflow furnace. As a result, the chip parts mounted on the printed circuit board are exposed during soldering to temperatures in the reflow furnace of around 250° C. 
     The materials used in conventional type piezoelectric elements include: a piezoelectric ceramic composition in which a piezoelectric property is improved by adding Cr 2  O 3 , MnO 2 , Fe 2  O 3 , Bi 2  O 3 , etc. to a two-component ceramic composition of PbTiO 3  --PbZrO 3  to make a three-component composition; a piezoelectric ceramic composition in which a piezoelectric property is improved by adding Pb(Co1/3Nb 2/3 )O 3 , Pb(Mg 1/3  Nb 2/3 )O 3 , Pb(Mn 1/3  Nb 2/3 )O 3 , Pb(Ni 1/3  Nb 2/3 )O 3 , etc. to a two-component ceramic composition of PbTiO 3  --PbZrO 3  to make a three-component composition; or a three-component ceramic composition of PbTiO 3  --PbZrO 3  --Pb(Yb1/2Nb1/2)O 3  as disclosed in Japanese laid-open publication No. 3-36773. 
     However, conventional piezoelectric elements having lead wires are usually not exposed to temperatures of 200° C. or higher, and the ceramic compositions used in these piezoelectric elements are not designed to be exposed to temperatures of 200° C. or higher. 
     For this reason, when these conventional piezoelectric elements are mounted on electronic devices and are exposed for soldering to temperatures around 250° C. in the reflow furnace, the mechanical quality factor (Qm) and electromechanical coupling factor (kp) decrease. It is difficult to obtain piezoelectric element chip parts with reliable heat-resistance properties. 
     Also, polarization occurs in conventional piezoelectric ceramic materials when they are exposed to temperatures of 200° C. even when the material has a Curie point of 300° C. or more. Further, piezoelectric properties, such as electromechanical coupling factor, decrease. In a ceramic oscillator using conventional piezoelectric material, the resonance frequency deviates extensively from the initial frequency over time. 
     SUMMARY OF THE INVENTION 
     It is an object of the present invention to provide a piezoelectric ceramic composition that solves the above problems, does not deteriorate even when exposed to temperatures of 200° C. or higher, exhibits less change over time, has a resonance frequency that does not deviate extensively from an initial frequency due to change over time, and causes no problems due to depolarization. 
     To attain the above object, the present invention limits the range of product composition in each of the following compositions: (1) a first piezoelectric ceramic composition, in which (Mg 1/3  Nb 2/3 )O 3  is solubilized as a third component and (Yb 1/2  Nb 1/2 )O 3  as a fourth component to PbTiO 3  --PbZrO 3  ; (2) a second piezoelectric ceramic composition, which is obtained by substituting a part of Pb in the first piezoelectric ceramic composition with at least one element selected from Ba, Sr and Ca; (3) a third piezoelectric ceramic composition, in which Yb is treated as bivalent while it is treated as trivalent in the first piezoelectric ceramic composition; (4) a fourth piezoelectric ceramic composition, which is obtained by adding at least one element selected from Cr and Mn to the third piezoelectric ceramic composition as a secondary component; and (5) a fifth piezoelectric ceramic composition obtained by substituting a part of Pb in the third piezoelectric ceramic composition with at least one element selected from Ba, Sr and Ca. 
     By the use of a piezoelectric ceramic element using the piezoelectric ceramic compositions of (1) to (3) and (5) above, it is possible to obtain a piezoelectric ceramic composition which has a high electromechanical coupling factor and high heat-resistance property, and exhibits a low temperature coefficient of resonance frequency and less change over time. By the use of a piezoelectric ceramic composition of (4) above, it is possible to obtain the mechanical quality factor desired due to the secondary component without decreasing the piezoelectric property, and while still maintaining the heat-resistance property and low change over time. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     FIG. 1 is a manufacturing process chart illustrating the use a piezoelectric ceramic composition of the present invention for piezoelectric chip parts. 
     FIG. 2 is a graph illustrating the resonance frequency change ratio over time for the piezoelectric ceramic composition of the present invention and a conventional type piezoelectric ceramic composition. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     The following is a description of the embodiments of the present invention in connection with the drawings and the tables as attached. 
     A piezoelectric ceramic disk using the piezoelectric ceramic composition of the present invention is manufactured through the following manufacturing processes, as given in FIG. 1: 
     (1) Raw materials are weighed. 
     (2) The weighed materials are processed by wet mixing in a ball mill. 
     (3) The mixture processed by wet mixing is dried. 
     (4) The dried material is calcinated at 750° C. to 950° C. 
     (5) The calcinated material is processed by wet crushing in a ball mill. 
     (6) To the powder thus obtained, a proper amount of an organic binder is added to granulate it. 
     (7) The material thus granulated is processed by pressure forming under pressure of 4 tons/cm 2 . 
     (8) The formed material is sintered at 1130° C. to 1250° C. 
     (9) On both surfaces of the sintered product, silver electrodes are baked and mounted. 
     (10) In silicone oil kept at 50° C. to 120° C., a DC electric field of 2 to 3 MV/m is applied for one hour for polarizing. 
     PbO, MgCO 3 , Yb 2  O 3 , Nb 2  O 5 , TiO 2  and ZrO 2  are used as the starting materials. Pb is represented by y, a mixture of MgCO 3  and Nb 2  O 5  in molar ratio of 1:1 is represented by a, a mixture of Yb 2  O 3  and Nb 2  O 5  in molar ratio of 1:1 is represented by b, Ti is represented by c, and Zr is represented by d. This piezoelectric ceramic composition can be represented by a general formula: 
     
         Pb.sub.y [(Mg.sub.1/3 Nb.sub.2/3).sub.a (Yb.sub.1/2 Nb.sub.1/2).sub.b Ti.sub.c Zr.sub.d ]O.sub.3 
    
     (where a+b+c+d=1). These are weighed to make up a product composition as shown in Table 1. In accordance with the processes already described, a piezoelectric ceramic disk of 14.3 mm in diameter and 0.6 mm in thickness was manufactured. 
     
                                           TABLE 1                                 
__________________________________________________________________________
                              E-mechl                                     
                      Di- Mechl                                           
                              coupl&#39;g                                     
                                   KP                                     
Composition       Dens&#39;y                                                  
                      elect.                                              
                          qual&#39;y                                          
                              factor                                      
                                   change                                 
(molar ratio)     (ρ)                                                 
                      Const.                                              
                          factor                                          
                              (kp) ratio                                  
No.                                                                       
   y  a  b  c  d  g/cm.sup.3                                              
                      (ε)                                         
                          (Qm)                                            
                              %    %                                      
__________________________________________________________________________
 *1A                                                                      
   0.94                                                                   
      0.05                                                                
         0.05                                                             
            0.45                                                          
               0.45                                                       
                  7.0 910 113 34.4 -20.2                                  
  2A                                                                      
   0.95                                                                   
      0.05                                                                
         0.05                                                             
            0.45                                                          
               0.45                                                       
                  7.6 1508                                                
                          96  60.1 -2.6                                   
  3A                                                                      
   1  0.05                                                                
         0.05                                                             
            0.45                                                          
               0.45                                                       
                  7.7 1017                                                
                          83  67.4 -2.0                                   
  4A                                                                      
   1.05                                                                   
      0.05                                                                
         0.05                                                             
            0.45                                                          
               0.45                                                       
                  7.7 866 83  61.2 -2.4                                   
 *5A                                                                      
   1.06                                                                   
      0.05                                                                
         0.05                                                             
            0.45                                                          
               0.45                                                       
                  7.6 753 88  34.8 -22.8                                  
 *6A                                                                      
   1  0.005                                                               
         0.055                                                            
            0.47                                                          
               0.47                                                       
                  7.8 840 101 45.3 -18.2                                  
  7A                                                                      
   I  0.01                                                                
         0.05                                                             
            0.47                                                          
               0.47                                                       
                  7.7 1084                                                
                          85  60.7 -2.9                                   
  8A                                                                      
   1  0.15                                                                
         0.05                                                             
            0.40                                                          
               0.40                                                       
                  7.8 725 100 61.0 -3.0                                   
 *9A                                                                      
   1  0.16                                                                
         0.04                                                             
            0.40                                                          
               0.40                                                       
                  7.8 782 112 52.5 -16.1                                  
*10A                                                                      
   1  0.095                                                               
         0.005                                                            
            0.45                                                          
               0.45                                                       
                  7.8 2045                                                
                          79  75.0 -16.0                                  
 11A                                                                      
   1  0.09                                                                
         0.01                                                             
            0.45                                                          
               0.45                                                       
                  7.9 2009                                                
                          78  76.3 -2.9                                   
 12A                                                                      
   1  0.05                                                                
         0.10                                                             
            0.43                                                          
               0.42                                                       
                  7.7 866 95  60.5 -3.0                                   
*13A                                                                      
   1  0.04                                                                
         0.11                                                             
            0.43                                                          
               0.42                                                       
                  7.6 839 91  50.0 -18.2                                  
*14A                                                                      
   1  0.10                                                                
         0.05                                                             
            0.29                                                          
               0.55                                                       
                  7.6 317 392 37.4 -21.3                                  
 15A                                                                      
   1  0.10                                                                
         0.05                                                             
            0.30                                                          
               0.55                                                       
                  7.9 439 165 60.2 -2.7                                   
*16A                                                                      
   1  0.15                                                                
         0.05                                                             
            0.56                                                          
               0.24                                                       
                  7.7 730 95  37.7 -8.5                                   
 17A                                                                      
   1  0.15                                                                
         0.05                                                             
            0.55                                                          
               0.25                                                       
                  7.7 725 100 61.0 -2.8                                   
 18A                                                                      
   1  0.05                                                                
         0.05                                                             
            0.60                                                          
               0.30                                                       
                  7.7 524 197 60.3 -3.0                                   
*19A                                                                      
   1  0.05                                                                
         0.05                                                             
            0.61                                                          
               0.29                                                       
                  7.6 406 252 20.2 -7.0                                   
 20A                                                                      
   1  0.10                                                                
         0  0.45                                                          
               0.45                                                       
                  7.7 1881                                                
                          44  58.1 -20.8                                  
__________________________________________________________________________
 
    
     Sample No. 20A is a piezoelectric ceramic disk manufactured using a conventional piezoelectric ceramic composition, and appears for reference. 
     Table 1 also summarizes the results of measurements for density (ρ), dielectric constant (ε), mechanical quality factor (Qm), electromechanical coupling factor (kp), and kp change ratio of the piezoelectric ceramic disk thus manufactured. 
     The piezoelectric property (i.e. dielectric constant (ε)), mechanical quality factor (Qm) and electromechanical coupling factor (kp) were calculated from the results of measurements of resonance and anti-resonance frequencies using an impedance analyzer. 
     The kp change ratio is used to evaluate the heat-resistance property. It is obtained by immersing the disk element in a solder bath at 250° C. for one minute and measuring the change of kp. The kp change ratio is given by the following formula: 
     
         kp change ratio (%)=[(kp-kp.sub.i)/kp.sub.i ]* 100 
    
     where kp i  is the electromechanical coupling factor before immersion in the solder bath, and kp is the electromechanical coupling factor after immersion in the solder bath for one hour. 
     The results of the measurements were evaluated for the electromechanical coupling factor (kp) and the change ratio of electromechanical coupling factor. The materials were regarded as acceptable when the electromechanical coupling factor was 60% or more and the change ratio of the electromechanical coupling factor was within ±3%. The other values were regarded as defective. 
     As a result, samples 1A, 5A, 6A, 9A, 13A, 14A, 16A and 19A were judged as defective based on the electromechanical coupling factor. Samples 1A, 5A, 6A, 9A, 10A, 13A, 14A, 16A and 19A were judged as defective based on the change ratio of the electromechanical coupling factor. 
     In the overall evaluation, samples 2A, 3A, 4A, 7A, 8A, 11A, 12A, 15A, 17A, and 18A were judged as acceptable (In the table, the samples judged as defective are marked with an asterisk). 
     In summarizing the composition range of the samples according to the results of evaluation, a sample is defective if it is within the composition range of: 
     y&lt;0.95 or y&gt;1.05 for y; 
     a&lt;0.01 or a&gt;0.15 for a; 
     b&lt;0.01 or b&gt;0.10 for b; 
     c&lt;0.30 or c&gt;0.60 for c; and 
     d&lt;0.25 or d&gt;0.55 for d. Therefore, a sample is acceptable if it is within the composition range of: 
     0.95≦y≦1.05 for y: 
     0.01≦a≦0.15 for a; 
     0.01≦b≦0.10 for b; 
     0.30≦c≦0.60 for c; and 
     0.25≦d≦0.55 for d. 
     As is evident from Table 1, in the conventional type piezoelectric ceramic composition, the change ratio of the electromechanical coupling factor due to soldering heat at 250° C. is around -20%, while in the piezoelectric ceramic composition of the present invention, it can be greatly improved to -3.0% to -2.0% or less by simultaneously solubilizing (Mg 1/3  Nb 2/3 )O 3  and (Yb 1/2  Nb 1/2 )O 3  as the third and the fourth components respectively to PbTiO 3  --PbZrO 3 . 
     FIG. 2 shows the change of resonance frequency over time of sample 3A, which is an embodiment of the present invention, and a conventional example, i.e. sample No. 20A. 
     The change ratio of the resonance frequency is given by the following formula: 
     
         Change ratio of resonance frequency (%)=[(fr-fr.sub.i)/fr.sub.i ]*100 
    
     where fr i  represents the resonance frequency in the initial stage (one hour after polarization), and fr represents the resonance frequency at a certain period of time after polarization. 
     As it is evident from FIG. 2, compared with the conventional type piezoelectric ceramic composition, the change ratio of the resonance frequency of the piezoelectric ceramic composition of the present invention can be reduced to 0.1%/time decade or lower. 
     Next, a description is given for a piezoelectric ceramic composition obtained by substituting a part of Pb in the starting materials with Me, i.e. Ba, Sr or Ca. The composition ratio of Pb and Me is represented by (1-x) and x respectively. This piezoelectric ceramic composition can be represented by a general formula: 
     
         (Pb.sub.1-x Me.sub.x)[(Mg.sub.1/3 Nb.sub.2/3).sub.a (Yb.sub.1/2 Nb.sub.1/2).sub.b Ti.sub.c Zr.sub.d ]O.sub.3 
    
     (where Me represents at least one element selected from Ba, Sr, and Ca, a +b+c+d=1). 
     Using the piezoelectric ceramic composition obtained by substituting a part of Pb with Me as shown in Table 2, a piezoelectric ceramic disk of the same shape, i.e. 14.3 mm in diameter and 0.6 mm in thickness, was produced by the manufacturing processes described above. For this piezoelectric ceramic disk, density (ρ), dielectric constant (ε), mechanical quality factor (Qm) and electromechanical coupling factor (kp) were determined by the same measuring procedure. Further, the temperature coefficient of resonance frequency (frTC) was measured. 
     The temperature coefficient of resonance frequency (frTC) is given by the following formula: 
     
         frTC(ppm/° C.)=[(fr.sub.1 -fr.sub.2)/(fr.sub.3 *125)]10.sup.6 
    
     where fr 1  and fr 2  represent the maximum and minimum values of the resonance frequency in the temperature range from -40° C. to 85° C. respectively, and fr 3  represents resonance frequency at 25° C. 
     Sample No. 25B in Table 2 is a piezoelectric ceramic disk obtained by the use of a conventional piezoelectric ceramic composition, and appears for reference. 
     Table 2 summarizes the product composition of the piezoelectric ceramic compositions thus obtained and the results of measurements on the piezoelectric ceramic disk. 
     The results of the measurements were evaluated for the temperature coefficient of resonance frequency (frTC). Similarly to the case of the piezoelectric ceramic disk of Table 1, the materials were regarded as acceptable when kp was 60% or more and the kp change ratio was within ±3%. It was further required that the temperature coefficient of resonance frequency be 200 ppm or less. The materials with other values were regarded as defective. 
     As a result, samples 5B, 11B, 18B, 19B, 21B and 24B were judged as defective based on the electromechanical coupling factor. Samples 5B, 11B, 14B, 15B, 18B, 19B, 21B and 24B were judged as defective based on the change ratio of the electromechanical coupling factor, and sample 1B was judged as defective based on the temperature coefficient of resonance frequency. 
     
                                           TABLE 2                                 
__________________________________________________________________________
Subs&#39;te                                                                   
Comp&#39;n                           E-mechl  Temp&#39;re                         
element                  Di- Mechl                                        
                                 coupl&#39;g                                  
                                      kp  co-                             
(molar   Basic Composition                                                
                     Dens&#39;y                                               
                         elect.                                           
                             qual&#39;y                                       
                                 factor                                   
                                      change                              
                                          effic&#39;t                         
ratio)   (molar ratio)                                                    
                     (ρ)                                              
                         Const.                                           
                             factor                                       
                                 (kp) ratio                               
                                          (frTC)                          
No.                                                                       
   Me x  a  b  c  d  g/cm.sup.3                                           
                         (ε)                                      
                             (Qm)                                         
                                 %    %   ppm/°C.                  
__________________________________________________________________________
 *1B                                                                      
   -- 0  0.05                                                             
            0.05                                                          
               0.45                                                       
                  0.45                                                    
                     7.7 1017                                             
                             83  67.4 -2.0                                
                                          356                             
  2B                                                                      
   Ba 0.01                                                                
         0.05                                                             
            0.05                                                          
               0.45                                                       
                  0.45                                                    
                     7.7 1161                                             
                             82  64.1 -2.1                                
                                          150                             
  3B                                                                      
   Ba 0.05                                                                
         0.05                                                             
            0.05                                                          
               0.45                                                       
                  0.45                                                    
                     7.7 1180                                             
                             80  63.8 -2.0                                
                                          149                             
  4B                                                                      
   Ba 0.12                                                                
         0.05                                                             
            0.05                                                          
               0.45                                                       
                  0.45                                                    
                     7.6 1204                                             
                             61  63.3 -2.4                                
                                          141                             
 *5B                                                                      
   Ba 0.13                                                                
         0.05                                                             
            0.05                                                          
               0.45                                                       
                  0.45                                                    
                     7.2 1364                                             
                             70  50.4 -21.8                               
                                          132                             
  6B                                                                      
   Sr 0.05                                                                
         0.05                                                             
            0.05                                                          
               0.45                                                       
                  0.45                                                    
                     7.6 1233                                             
                             92  63.1 -2.2                                
                                          125                             
  7B                                                                      
   Ca 0.05                                                                
         0.05                                                             
            0.05                                                          
               0.45                                                       
                  0.45                                                    
                     7.6 1256                                             
                             90  60.1 -2.1                                
                                          126                             
  8B                                                                      
   Ba 0.08                                                                
         0.05                                                             
            0.05                                                          
               0.45                                                       
                  0.45                                                    
                     7.7 1204                                             
                             87  63.7 -2.2                                
                                          143                             
  9B                                                                      
   Sr 0.08                                                                
         0.05                                                             
            0.05                                                          
               0.45                                                       
                  0.45                                                    
                     7.6 1301                                             
                             101 62.5 -2.3                                
                                          121                             
 10B                                                                      
   Ca 0.08                                                                
         0.05                                                             
            0.05                                                          
               0.45                                                       
                  0.45                                                    
                     7.6 1398                                             
                             91  60.3 -2.1                                
                                          120                             
*11B                                                                      
   Ba 0.05                                                                
         0.005                                                            
            0.055                                                         
               0.47                                                       
                  0.47                                                    
                     7.7 821 98  44.8 -20.4                               
                                          155                             
 12B                                                                      
   Ba 0.05                                                                
         0.01                                                             
            0.05                                                          
               0.47                                                       
                  0.47                                                    
                     7.7 1197                                             
                             88  60.2 -2.8                                
                                          150                             
 13B                                                                      
   Ba 0.05                                                                
         0.15                                                             
            0.05                                                          
               0.40                                                       
                  0.40                                                    
                     7.7 833 95  61.0 -2.9                                
                                          148                             
*14B                                                                      
   Ba 0.05                                                                
         0.16                                                             
            0.04                                                          
               0.40                                                       
                  0.40                                                    
                     7.7 801 104 50.1 -19.6                               
                                          153                             
*15B                                                                      
   Ba 0.05                                                                
         0.095                                                            
            0.005                                                         
               0.45                                                       
                  0.45                                                    
                     7.7 2095                                             
                             81  66.6 -17.3                               
                                          154                             
 16B                                                                      
   Ba 0.05                                                                
         0.09                                                             
            0.01                                                          
               0.45                                                       
                  0.45                                                    
                     7.7 2012                                             
                             84  67.8 -3.0                                
                                          150                             
 17B                                                                      
   Ba 0.05                                                                
         0.05                                                             
            0.10                                                          
               0.43                                                       
                  0.42                                                    
                     7.6 866 95  60.5 -2.9                                
                                          151                             
*18B                                                                      
   Ba 0.05                                                                
         0.04                                                             
            0.11                                                          
               0.43                                                       
                  0.42                                                    
                     7.5 855 106 48.7 -22.9                               
                                          147                             
*19B                                                                      
   Ba 0.05                                                                
         0.10                                                             
            0.05                                                          
               0.29                                                       
                  0.56                                                    
                     7.5 423 341 32.6 -22.4                               
                                          135                             
 20B                                                                      
   Ba 0.05                                                                
         0.10                                                             
            0.05                                                          
               0.30                                                       
                  0.55                                                    
                     7.6 595 121 60.2 -2.8                                
                                          137                             
*21B                                                                      
   Ba 0.05                                                                
         0.15                                                             
            0.05                                                          
               0.56                                                       
                  0.24                                                    
                     7.6 780 99  35.4 -9.6                                
                                          145                             
 22B                                                                      
   Ba 0.05                                                                
         0.15                                                             
            0.05                                                          
               0.55                                                       
                  0.25                                                    
                     7.6 820 103 61.1 -2.9                                
                                          144                             
 23B                                                                      
   Ba 0.05                                                                
         0.05                                                             
            0.05                                                          
               0.60                                                       
                  0.30                                                    
                     7.6 650 154 60.5 -2.7                                
                                          149                             
*24B                                                                      
   Ba 0.05                                                                
         0.05                                                             
            0.05                                                          
               0.61                                                       
                  0.29                                                    
                     7.5 488 264 30.3 -8.4                                
                                          156                             
 25B                                                                      
   -- 0  0.10                                                             
            0  0.45                                                       
                  0.45                                                    
                     7.7 1881                                             
                             44  56.1 -20.8                               
                                          368                             
__________________________________________________________________________
 
    
     In the overall evaluation, samples 2B, 3B, 4B, 6B, 7B, 8B, 9B, 10B, 12B, 13B, 16B, 17B, 20B, 22B and 23B were judged as acceptable. 
     In summarizing the composition range of the samples according to the results of the evaluation, a sample is defective if it is within the composition range of: 
     x&gt;0.12 for x; 
     a&lt;0.01 or a&gt;0.15 for a; 
     b&lt;0.01 or b&gt;0.10 for b; 
     c&lt;0.30 or c&gt;0.60 for c; and 
     d&lt;0.25 or d&gt;0.55 for d. 
     Therefore, a sample is acceptable if it is within the composition range of: 
     0&lt;x≦0.12 for x; 
     0.01≦a≦0.15 for a; 
     0.01≦b≦0.10 for b; 
     0.30≦c≦0.60 for c; and 
     0.25≦d≦0.55 for d. 
     As is evident from Table 2, by substituting a part of Pb with at least one element selected from Ba, Sr and Ca, it is possible to greatly improve the temperature coefficient of resonance frequency (frTC) without decreasing the heat-resistance property and the resistance to change over time. 
     When the change of resonance frequency over time was determined for sample No. 3B, the value was as low as 0.1%/time decade or less as in the case of the sample No. 3A in Table 1. 
     In general, in producing a piezoelectric ceramic composition, it is widely known that it is possible to blend the materials to match the stable valence of the element used in case a plurality of stable valence states are present, i.e. in case it is possible to constitute oxides in a plurality of oxidation states. 
     For example, in a three-component type piezoelectric material using Mn and Nb as the third components, PbTiO 3  --PbZrO 3  --Pb(Mn 1/3  Nb 2/3 )O 3  having Mn as bivalent and PbTiO 3  --PbZrO 3  Pb(Mn 1/2  Nb 1/2 )O 3  having Mn as trivalent are both used in practical application. 
     The present inventors have found that Yb used in the above embodiment is an element that may be bivalent or trivalent for stable valence, while, even when it is treated as bivalent, the effect of the present invention can be attained. 
     A description will now be given on a piezoelectric ceramic disk using a piezoelectric ceramic composition, which has Yb as bivalent. 
     This piezoelectric ceramic disk is produced by the same procedure as described above, except that the materials are sintered at 1100° C. to 1260° C. 
     As the starting materials, PbO, MgCO 3 , Yb 2  O 3 , Nb 2  O 5 , TiO 2  and ZrO 2  were used. Mg 1/3 .Nb 2/3   was represented by e, Yb 1/3 .Nb 2/3  was represent by f, Pb.Ti was represented by g, and Pb.Zr was represented by h. This piezoelectric ceramic composition can be represented by a general formula: 
     
         Pb[(Mg.sub.1/3 Nb.sub.2/3).sub.e (Yb.sub.1/3 Nb.sub.2/3).sub.f Ti.sub.g Zr.sub.h ]O.sub.3 
    
     (where e+f+g+H=1). These materials were weighed to make up a product composition shown in Table 3. In accordance with the processes described above, a piezoelectric ceramic disk of 15 mm in diameter and 1 mm in thickness was manufactured. On each of the piezoelectric ceramic disks thus obtained, density, electromechanical coupling factor, dielectric constant and mechanical quality factor were determined. 
     Table 3 summarizes the composition of the piezoelectric ceramic compositions thus obtained and the results of measurement on the piezoelectric ceramic disks. 
     The results of the measurement were evaluated by the same procedure as the piezoelectric ceramic disks shown in Table 1. The materials were regarded as acceptable when kp was 60% or more and the kp change ratio was within ±3%. The materials with other values were regarded as defective. 
     
                                           TABLE 3                                 
__________________________________________________________________________
                             E-mechl                                      
                    Di- Mechl                                             
                             coupl&#39;g                                      
                                  KP                                      
Composition    Dens&#39;y                                                     
                    elect.                                                
                        qual&#39;y                                            
                             factor                                       
                                  change                                  
(molar ratio)  (ρ)                                                    
                    const.                                                
                        factor                                            
                             (kp) ratio                                   
No.                                                                       
   e  f  g  h  g/cm.sup.3                                                 
                    (ε)                                           
                        (Qm) %    %                                       
__________________________________________________________________________
  1C                                                                      
   0.06                                                                   
      0.06                                                                
         0.44                                                             
            0.44                                                          
               7.8  1150                                                  
                        85   62.5 -2.0                                    
 *2C                                                                      
   0.005                                                                  
      0.065                                                               
         0.47                                                             
            0.46                                                          
               7.5  950 90   46.0 -19.5                                   
  3C                                                                      
   0.01                                                                   
      0.06                                                                
         0.47                                                             
            0.46                                                          
               7.7  1100                                                  
                        85   60.5 -3.0                                    
  4C                                                                      
   0.15                                                                   
      0.05                                                                
         0.42                                                             
            0.38                                                          
               7.7  1020                                                  
                        90   61.0 -3.0                                    
 *5C                                                                      
   0.16                                                                   
      0.04                                                                
         0.42                                                             
            0.38                                                          
               7.5  850 100  45.5 -18.5                                   
 *6C                                                                      
   0.095                                                                  
      0.005                                                               
         0.44                                                             
            0.46                                                          
               7.5  1250                                                  
                        85   60.0 -18.0                                   
  7C                                                                      
   0.09                                                                   
      0.01                                                                
         0.44                                                             
            0.46                                                          
               7.8  1300                                                  
                        100  65.0 -2.5                                    
  8C                                                                      
   0.05                                                                   
      0.15                                                                
         0.42                                                             
            0.38                                                          
               7.7  1010                                                  
                        90   60.5 -3.0                                    
 *9C                                                                      
   0.04                                                                   
      0.16                                                                
         0.42                                                             
            0.38                                                          
               7.3  890 95   48.0 -19.0                                   
*10C                                                                      
   0.11                                                                   
      0.06                                                                
         0.25                                                             
            0.58                                                          
               7.4  750 300  40.0 -22.0                                   
 11C                                                                      
   0.11                                                                   
      0.06                                                                
         0.30                                                             
            0.53                                                          
               7.7  1000                                                  
                        100  60.0 -3.0                                    
*12C                                                                      
   0.15                                                                   
      0.06                                                                
         0.56                                                             
            0.23                                                          
               7.4  780 90   38.0 -12.0                                   
 13C                                                                      
   0.15                                                                   
      0.06                                                                
         0.54                                                             
            0.25                                                          
               7.7  1010                                                  
                        95   60.5 -2.7                                    
 14C                                                                      
   0.07                                                                   
      0.03                                                                
         0.60                                                             
            0.30                                                          
               7.7  1000                                                  
                        110  60.2 -3.0                                    
*15C                                                                      
   0.07                                                                   
      0.03                                                                
         0. 7.4                                                           
               730  200 30.5 -9.5                                         
__________________________________________________________________________
 
    
     As a result, samples 2C, 5C, 9C, 10C, 12C and 15C were judged as defective based on the electromechanical coupling factor. Samples 2C, 5C, 6C, 9C, 10C, 12C and 15C were judged as defective based on the change ratio of the electromechanical coupling factor. 
     In the overall evaluation, samples 1C, 3C, 4C, 7C, 8C, 11C, 13C and 14C were judged as acceptable. 
     In summarizing the composition range of the samples according to the results of evaluation, a sample is defective if it is within the composition range of: 
     e&lt;0.01 or e&gt;0.15 for e; 
     f&lt;0.01 or f&gt;0.15 for f; 
     g&lt;0.30 or g&gt;0.60 for g; and 
     h&lt;0.25 or h≧0.58 for h. 
     Therefore, a sample is acceptable if it is within the composition range of: 
     0.01≦e≦0.15 for e; 
     0.01≦f≦0.15 for f; 
     0.30≦g≦0.60 for g; and 
     0.25≦h&lt;0.58 for h. 
     Specifically, 
     1. In the case where e&lt;0.01, the sintering property of the element is aggravated, and the high electromechanical coupling factor desired is not obtained. Also, the heat-resistance property decreases. The heat-resistance property also decreases when e&gt;0.15. 
     2. In the case where f&lt;0.01, the heat-resistance property decreases. Where f&gt;0.15, the sintering property decreases, the high electromechanical coupling factor desired is not obtained, and the heat-resistance property is aggravated. 
     3. Where g&lt;0.30 or g&gt;0.60, the desired high electromechanical coupling factor is not obtained and the heat-resistance property decreases. 
     4. In a composition with h&lt;0.25, the desired high electromechanical coupling factor is not obtained. Further, where d&gt;0.58, the desired improvement of the heat-resistance property is not obtained. 
     As is evident from Table 3, in the conventional piezoelectric ceramic composition, the change ratio of the electromechanical coupling factor due to soldering heat at 250° C. is around -20%, while in the piezoelectric ceramic composition of the present invention, it can be greatly improved to -3% or less by simultaneously solubilizing (Mg 1/3  Nb 2/3 )O 3  and (Yb 1/3  Nb 2/3 )O 3  as the third and the fourth components respectively to PbTiO 3  --PbZrO 3 . 
     When the change of resonance frequency over time was determined for sample No. 1E, the value was as low as 0.1%/time decade or less as in the case of sample No. 3A in FIG. 2. 
     Next, a description is given on a piezoelectric ceramic disk using the piezoelectric ceramic composition containing Cr 2  O 3  and MnO 2  added as secondary components to the piezoelectric composition having Yb as bivalent, referring to Table 4. 
     The piezoelectric ceramic composition used for this piezoelectric ceramic disk is produced through the manufacturing processes shown in FIG. 1 except that Cr 3  O 3  and MnCO 3  are added as the starting materials to the piezoelectric ceramic composition shown in Table 3 to make up the product composition shown in Table 3. 
     Table 4 also summarizes the results of the measurements of density (ρ), dielectric constant (ε), mechanical quality factor (Qm), electromechanical coupling factor (kp) and change ratio of electromechanical coupling factor (kp) of each of the piezoelectric ceramic disks. 
     The results of the measurements were evaluated for kp and kp change ratio by the same procedure as the piezoelectric ceramic disks of Table 1. The materials were regarded as acceptable when kp was 60% or more and the kp change ratio was within ±3%. The materials with other values were regarded as defective. 
     
                                           TABLE 4                                 
__________________________________________________________________________
                                   E-mechl                                
               Second&#39;y    Di- Mechl                                      
                                   coupl&#39;g                                
                                        KP                                
Composition    element Dens&#39;y                                             
                           elect.                                         
                               qual&#39;y                                     
                                   factor                                 
                                        change                            
(molar ratio)  (Wt %)  (ρ)                                            
                           Const.                                         
                               factor                                     
                                   (kp) ratio                             
No.                                                                       
   e  f  9  h  Cr.sub.2 O.sub.3                                           
                   MnO.sub.2                                              
                       g/cm.sup.3                                         
                           (ε)                                    
                               (Qm)                                       
                                   %    %                                 
__________________________________________________________________________
 *1D                                                                      
   0.06                                                                   
      0.06                                                                
         0.44                                                             
            0.44                                                          
               --  0.005                                                  
                       7.8 1150                                           
                               85  62.3 --                                
  2D                                                                      
   0.06                                                                   
      0.06                                                                
         0.44                                                             
            0.44                                                          
               --  0.02                                                   
                       7.7 1160                                           
                               1000                                       
                                   62.0 -1.9                              
  3D                                                                      
   0.06                                                                   
      0.06                                                                
         0.44                                                             
            0.44                                                          
               --  0.9 7.7 1200                                           
                               1550                                       
                                   64.5 -1.5                              
  4D                                                                      
   0.06                                                                   
      0.06                                                                
         0.44                                                             
            0.44                                                          
               --  1.8 7.7 1250                                           
                               1100                                       
                                   62.2 -3.0                              
 *5D                                                                      
   0.06                                                                   
      0.06                                                                
         0.44                                                             
            0.44                                                          
               --  2.3 7.4 810 400 49.6 -20.0                             
  6D                                                                      
   0.06                                                                   
      0.06                                                                
         0.44                                                             
            0.44                                                          
               0.2 --  7.8 1160                                           
                               510 63.5 -2.0                              
  7D                                                                      
   0.06                                                                   
      0.06                                                                
         0.44                                                             
            0.44                                                          
               0.4 --  7.8 1190                                           
                               760 63.0 -2.0                              
  8D                                                                      
   0.06                                                                   
      0.06                                                                
         0.44                                                             
            0.44                                                          
               0.3 0.5 7.8 1210                                           
                               1400                                       
                                   64.1 -1.8                              
 *9D                                                                      
   0.005                                                                  
      0.065                                                               
         0.47                                                             
            0.46                                                          
               --  0.9 7.5 940 490 47.3 -18.5                             
 10D                                                                      
   0.01                                                                   
      0.06                                                                
         0.47                                                             
            0.46                                                          
               --  0.9 7.7 1110                                           
                               1050                                       
                                   60.4 -2.8                              
 11D                                                                      
   0.15                                                                   
      0.05                                                                
         0.42                                                             
            0.38                                                          
               --  0.9 7.8 1050                                           
                               1250                                       
                                   62.1 -2.5                              
*12D                                                                      
   0.16                                                                   
      0.04                                                                
         0.42                                                             
            0.38                                                          
               --  0.9 7.5 870 900 50.0 -17.9                             
*13D                                                                      
   0.095                                                                  
      0.005                                                               
         0.44                                                             
            0.46                                                          
               --  0.9 7.5 1250                                           
                               1100                                       
                                   60.2 -17.1                             
 14D                                                                      
   0.09                                                                   
      0.01                                                                
         0.44                                                             
            0.46                                                          
               --  0.9 7.8 1340                                           
                               1320                                       
                                   66.4 -2.4                              
 15D                                                                      
   0.05                                                                   
      0.15                                                                
         0.42                                                             
            0.38                                                          
               --  0.9 7.7 1020                                           
                               1370                                       
                                   61.5 -2.8                              
*16D                                                                      
   0.05                                                                   
      0.05                                                                
         0.45                                                             
            0.45                                                          
               0.3 --  7.4 910 1150                                       
                                   48.2 -20.5                             
*17D                                                                      
   0.11                                                                   
      0.06                                                                
         0.25                                                             
            0.58                                                          
               --  0.9 7.4 800 1050                                       
                                   46.1 -21.0                             
 18D                                                                      
   0.11                                                                   
      0.06                                                                
         0.30                                                             
            0.53                                                          
               --  0.9 7.6 1030                                           
                               1300                                       
                                   60.3 -2.5                              
*19D                                                                      
   0.15                                                                   
      0.06                                                                
         0.56                                                             
            0.23                                                          
               --  0.9 7.4 770 950 41.2 -12.5                             
 20D                                                                      
   0.15                                                                   
      0.06                                                                
         0.54                                                             
            0.25                                                          
               --  0.9 7.7 1040                                           
                               1100                                       
                                   61.0 -2.7                              
 21D                                                                      
   0.07                                                                   
      0.03                                                                
         0.60                                                             
            0.30                                                          
               --  0.9 7.6 1010                                           
                               1100                                       
                                   60.4 -2.7                              
*22D                                                                      
   0.07                                                                   
      0.03                                                                
         0.61                                                             
            0.29                                                          
               --  0.9 7.4 750 850 33.3 -11.2                             
__________________________________________________________________________
 
    
     As a result, samples 5D, 9D, 12D, 16D, 17D, 19D and 22D were judged as defective based on the electromechanical coupling factor. Samples 1D, 5D, 9D, 12D, 13D, 16D, 17D, 19D and 22D were judged as defective based on the change ratio of the electromechanical coupling factor. 
     In the overall evaluation, samples 2D, 3D, 4D, 6D, 7D, 8D, 10D, 11D, 14D, 15D, 18D, 20D and 21D were judged as acceptable. 
     In summarizing the composition range of the samples according to the results of evaluation, a sample is defective if it is within the composition range of: 
     e&lt;0.01 or e&gt;0.15 for e; 
     f&lt;0.01 or f&gt;0.15 for f; 
     g&lt;0.30 or g&gt;0.60 for g; and 
     h&lt;0.25 or h≧0.58 for h. Therefore, a sample is acceptable if it is within the composition range of: 
     0.01≦f≦0.15 for f; 
     0.30≦g≦0.60 for g; and 
     0.25≦h&lt;0.58 for h. 
     Specifically, 
     1. Where e&lt;0.01, the sintering property of the element is aggravated, and the desired high electromechanical coupling factor is not obtained. Also, the heat-resistance property decreases. The heat-resistance property also decreases when e&gt;0.15. 
     2. Where f&lt;0.01, the heat-resistance property decreases. Where f&gt;0.15, the sintering property decreases, the high electromechanical coupling factor desired is not obtained and the heat-resistance property is aggravated. 
     3. Where g&lt;0.30 or g&gt;0.60, the desired high electromechanical coupling factor is not obtained and heat-resistance property decreases. 
     4. In a composition with h&lt;0.25, the desired high electromechanical coupling factor is not obtained. Further, where h&gt;0.58, the desired improvement to the heat-resistance property is not obtained. 
     5. In the case where at least one element selected from Cr and Mn is added as a secondary component by 0.02 to 1.8 weight % as converted respectively, it is possible to improve the mechanical quality factor (Qm) without decreasing the piezoelectric property, while improving the heat-resistance property and the change over time. 
     If Cr 2  O 3  and MnO 2  as secondary components are added by less than 0.02 weight %, Qm cannot be improved. If these are added by more than 1.8 weight %, the heat-resistance property decreases. 
     Further, by selecting the composition ratio, it is possible to obtain a piezoelectric ceramic material having a mechanical quality factor of 500 or more without decreasing the piezoelectric property from the materials having an electromechanical coupling factor of 60% or more. 
     Next, a description is given on a piezoelectric ceramic composition obtained by substituting a part of Pb in the piezoelectric ceramic composition having Yb as bivalent with Ba, Sr or Ca. The compositions of Pb and Me are represented by (1-x) and x respectively. 
     Using a piezoelectric ceramic composition of Table 2 obtained by substituting a part of Pb with Me, a piezoelectric ceramic disk of 15 mm in diameter and 1 mm in thickness was manufactured by the manufacturing processes as described above. On each of the piezoelectric ceramic disks, density (ρ), dielectric constant (ε), and electromechanical coupling factor (kp) were determined by the same procedure. Further, the temperature coefficient of resonance frequency (frTC) and mechanical quality factor (Qm) were measured. 
     Table 5 summarizes the composition of the piezoelectric ceramic composition thus obtained and the results of measurement on the piezoelectric ceramic disks. The composition of Me is represented by x. This piezoelectric ceramic composition can be represented by a general formula: 
     
         (Pb.sub.1-x Me.sub.x)[(Mg.sub.1/3 Nb.sub.2/3).sub.e (Yb.sub.1/3 Nb.sub.2/3).sub.f Ti.sub.g Zr.sub.h ]O.sub.3 
    
     (where Me represents at least one element selected from Ba, Sr, and Ca, and e+f+g+h=1). 
     
                                           TABLE 5                                 
__________________________________________________________________________
Subs&#39;te                                                                   
Comp&#39;n                           E-mechl  Temp&#39;re                         
element                  Di- Mechl                                        
                                 coupl&#39;g                                  
                                      kp  co-                             
(molar   Basic Composition                                                
                     Dens&#39;y                                               
                         elect.                                           
                             qual&#39;y                                       
                                 factor                                   
                                      change                              
                                          effic&#39;t                         
ratio)   (molar ratio)                                                    
                     (ρ)                                              
                         Const.                                           
                             factor                                       
                                 (kp) ratio                               
                                          (frTC)                          
No.                                                                       
   Me x  e  f  g  h  g/cm.sup.3                                           
                         (ε)                                      
                             (Qm)                                         
                                 %    %   ppm/°C.                  
__________________________________________________________________________
 *1E                                                                      
   -- 0  0.06                                                             
            0.06                                                          
               0.44                                                       
                  0.44                                                    
                     7.8 1150                                             
                             85  62.5 -2.0                                
                                          340                             
  2E                                                                      
   Sr 0.01                                                                
         0.06                                                             
            0.06                                                          
               0.44                                                       
                  0.44                                                    
                     7.7 1150                                             
                             85  63.0 2.1 130                             
  3E                                                                      
   Sr 0.05                                                                
         0.06                                                             
            0.06                                                          
               0.44                                                       
                  0.44                                                    
                     7.7 1200                                             
                             80  64.1 2.0 120                             
  4E                                                                      
   Sr 0.12                                                                
         0.06                                                             
            0.06                                                          
               0.44                                                       
                  0.44                                                    
                     7.6 1250                                             
                             80  63.0 2.5 120                             
 *5E                                                                      
   Sr 0.15                                                                
         0.06                                                             
            0.06                                                          
               0.44                                                       
                  0.44                                                    
                     7.0 1380                                             
                             75  49.5 -22.0                               
                                          140                             
  6E                                                                      
   Ba 0.05                                                                
         0.06                                                             
            0.06                                                          
               0.44                                                       
                  0.44                                                    
                     7.7 1240                                             
                             95  62.0 -2.3                                
                                          140                             
   7E                                                                     
   Ca 0.05                                                                
         0.06                                                             
            0.06                                                          
               0.44                                                       
                  0.44                                                    
                     7.6 1270                                             
                             90  61.3 -2.2                                
                                          110                             
  8E                                                                      
   Ba 0.08                                                                
         0.05                                                             
            0.06                                                          
               0.44                                                       
                  0.44                                                    
                     7.7 1170                                             
                             90  63.1 -2.4                                
                                          130                             
  9E                                                                      
   Sr 0.08                                                                
         0.06                                                             
            0.06                                                          
               0.44                                                       
                  0.44                                                    
                     7.6 1320                                             
                             95  60.5 -2.2                                
                                          110                             
 10E                                                                      
   Ca 0.08                                                                
         0.06                                                             
            0.06                                                          
               0.44                                                       
                  0.44                                                    
                     7.6 1400                                             
                             90  60.2 -2.3                                
                                          105                             
*11E                                                                      
   Sr 0.05                                                                
         0.005                                                            
            0.065                                                         
               0.47                                                       
                  0.46                                                    
                     7.5 960 95  46.2 -21.5                               
                                          150                             
 12E                                                                      
   Sr 0.05                                                                
         0.01                                                             
            0.06                                                          
               0.47                                                       
                  0.46                                                    
                     7.7 1160                                             
                             85  60.5 -2.9                                
                                          140                             
 13E                                                                      
   Sr 0.05                                                                
         0.15                                                             
            0.05                                                          
               0.42                                                       
                  0.38                                                    
                     7.7 1020                                             
                             95  61.0 -3.0                                
                                          140                             
*14E                                                                      
   Sr 0.05                                                                
         0.16                                                             
            0.04                                                          
               0.42                                                       
                  0.48                                                    
                     7.5 900 100 47.0 -19.5                               
                                          130                             
*15E                                                                      
   Sr 0.05                                                                
         0.095                                                            
            0.005                                                         
               0.44                                                       
                  0.46                                                    
                     7.6 1340                                             
                             90  60.7 -19.0                               
                                          140                             
 16E                                                                      
   Sr 0.05                                                                
         0.09                                                             
            0.01                                                          
               0.44                                                       
                  0.46                                                    
                     7.7 1400                                             
                             100 66.7 -3.0                                
                                          130                             
 17E                                                                      
   Sr 0.05                                                                
         0.05                                                             
            0.15                                                          
               0.42                                                       
                  0.38                                                    
                     7.7 1030                                             
                             95  60.2 -2.9                                
                                          130                             
*18E                                                                      
   Sr 0.05                                                                
         0.04                                                             
            0.16                                                          
               0.42                                                       
                  0.38                                                    
                     7.2 920 95  49.0 -21.9                               
                                          140                             
*19E                                                                      
   Sr 0.05                                                                
         0.11                                                             
            0.06                                                          
               0.25                                                       
                  0.58                                                    
                     7.4 770 305 40.8 -22.5                               
                                          130                             
 20E                                                                      
   Sr 0.05                                                                
         0.11                                                             
            0.06                                                          
               0.30                                                       
                  0.53                                                    
                     7.6 1010                                             
                             100 60.1 -3.0                                
                                          120                             
*21E                                                                      
   Sr 0.05                                                                
         0.15                                                             
            0.06                                                          
               0.56                                                       
                  0.23                                                    
                     7.3 810 95  40.2 -13.5                               
                                          140                             
 22E                                                                      
   Sr 0.05                                                                
         0.15                                                             
            0.06                                                          
               0.54                                                       
                  0.25                                                    
                     7.6 1010                                             
                             100 60.0 -2.9                                
                                          130                             
 23E                                                                      
   Sr 0.05                                                                
         0.07                                                             
            0.03                                                          
               0.60                                                       
                  0.30                                                    
                     7.6 1000                                             
                             115 60.5 -3.0                                
                                          130                             
*24E                                                                      
   Sr 0.05                                                                
         0.07                                                             
            0.03                                                          
               0.61                                                       
                  0.29                                                    
                     7.3 740 210 31.0 -10.5                               
                                          140                             
__________________________________________________________________________
 
    
     The results of the measurement were evaluated by the same procedure as in Table 2. Similarly to the piezoelectric ceramic disks shown in Table 1, the disks were regarded as acceptable when kp was 60% or more, the kp change ratio was within ±3%, and further when the temperature coefficient of resonance frequency (frTC) was 200 ppm or less. The materials with other values were regarded as defective. 
     As a result, samples 11E, 14E, 18E, 19E, 21E and 24E were judged as defective based on the electromechanical coupling factor. Samples 5E, 11E, 14E, 15E, 18E, 19E, 21E and 24E were judged as defective based on the change ratio of the electromechanical coupling factor. Sample 1E was judged as defective based on the temperature coefficient of resonance frequency. 
     In the overall evaluation, samples 2E, 3E, 4E, 6E, 7E, 8E, 9E, 10E, 12E, 13E, 16E, 17E, 20E, 22E and 23E were judged as acceptable. 
     In summarizing the composition range of the samples according to the results of evaluation, a sample is defective if it is within the composition range of: 
     x&lt;0.01 or x&gt;0.12 for x; 
     e&lt;0.01 or e&gt;0.15 for e; 
     f&lt;0.01 or f&gt;0.15 for f; 
     g&lt;0.30 or g&gt;0.60 for g; and 
     h&lt;0.25 or h≧0.58 for h. 
     Therefore, a sample is acceptable if it is within the composition range of: 
     021 x≦0.12 for x; 
     0.01≦e≦0.15 for e; 
     0.01≦f≦0.15 for f; 
     0.30≦g≦0.60 for g; and 
     0.25≦h&lt;0.58 for h. 
     Specifically, 
     1. Where e&lt;0.01, the sintering property of the element is aggravated, the high electromechanical coupling factor desired is not obtained and the heat-resistance property decreases. The heat-resistance property also decreases when e&gt;0.15. 
     2. Where f&lt;0.01, the heat-resistance property decreases. Where f&gt;0.15, the sintering property decreases, the high electromechanical coupling factor desired is not obtained, and the heat-resistance property is aggravated. 
     3. In the case where g&lt;0.30 or g&gt;0.60, the desired high electromechanical coupling factor is not obtained and the heat-resistance property decreases. 
     4. In a composition with h&lt;0.25, the desired high electromechanical coupling factor is not obtained. Further, where h&gt;0.58, the desired improvement to the heat-resistance property is not obtained. 
     5. In the case where a part of Pb is substituted with at least one of Ba, Sr or Ca, the temperature coefficient of resonance frequency (fr) increases without decreasing the heat-resistance property and change over time. In the case where Me is 0.0, the temperature coefficient of resonance frequency cannot increase. If Me is more than 0.12, the heat-resistance property decreases. Thus, it is preferred that 0&lt;x≦0.12. 
     As is evident from Table 5, in the conventional piezoelectric ceramic composition, the change ratio of electromechanical coupling factor due to soldering heat at 250° C. is around -20%, while in the piezoelectric ceramic composition of the present invention, it can be greatly improved to -2.0% to -3.0% by simultaneously solubilizing (Mg 1/3  Nb 2/3 )O 3  and (Yb 1/3  Nb 2/3 )O 3  as the third and the fourth components respectively to PbTiO 3  --PbZrO 3 . 
     Further, by substituting a part of Pb with at least one of Ba, Sr, or Ca, it is possible to greatly improve the temperature coefficient of resonance frequency (frTC) without decreasing the heat-resistance property and the change over time. 
     When the change of resonance frequency over time was determined for sample No. 3E, the value was as low as 0.1%/time decade or less, similar to the case of sample No. 3A of FIG. 2. 
     As is self-explanatory from the above description, it is possible by the use of the piezoelectric ceramic composition of the present invention to provide a piezoelectric ceramic element that has a high electromechanical coupling factor (kp) and heat-resistance property, and that exhibits a better temperature coefficient of resonance frequency with an improved heat-resistance property and extremely low change over time. Therefore, it is possible to manufacture chip parts in which the piezoelectric property does not decrease even when exposed to temperatures around 250° C. during surface packaging. 
     In the examples described above, the starting materials are oxides or carbonates. Similar effects can be obtained when carbonates, organic acid salts or hydroxides are used instead of the oxides, and oxides, organic acid salts or hydroxides are used instead of the carbonates.