Coating compositions
This invention relates to an aqueous coating composition which can form films having high hydrophilicity and excellent physical properties such as water resistance, adhesion to substrates, transparency, smoothness, surface hardness, resistance to scuffing, and the like. The coating composition of the present invention can provide substrates such as glass, metals, plastics, fibers, and the like with various functions such as nonfogging, antistatic properties, resistance to stains, suitability as medical supplies, and the like, by forming films on the substrates. 
     Heretofore various hydrophilic coating compositions have been proposed, but no composition can provide the above-mentioned physical properties at the same time (U.S. Pat. Nos. 3,597,384 and 3,488,215). Even if the hydrophilic nature is sufficient, the film formed is poor in water resistance or adhesion to substrates or sometimes brittle in the dry state or insufficient in smoothness, surface hardness, and the like (German Offenlengungsschrift No. 2,009,296). In any case, such a composition has various problems in practical applications. On the other hand, most coating compositions which have been provided contain organic solvents, which give various problems from viewpoints of public health, safety, as well as saving of resources. Therefore, an aqueous coating composition having excellent hydrophilic nature and the physical properties as mentioned above has long been desired. 
     The present inventors have accomplished the present invention based on the finding that an aqueous composition containing a hydrophilic copolymer having units of ethylene satisfies the requirements for practical applications as mentioned above. 
     It is an object of the present invention to provide an aqueous coating composition having excellent hydrophilic nature and the physical properties as mentioned above. 
     The present invention provides a coating composition comprising 
     A. A HYDROPHILIC COPOLYMER OF 60 TO 20% BY MOLE OF ETHYLENE, 20 TO 1% BY MOLE OF ALPHA,BETA-ETHYLENICALLY UNSATURATED CARBOXYLIC ACID AND 20 TO 79% BY MOLE OF POLYVALENT ALCOHOL MONOESTER OF ALPHA,BETA-ETHYLENICALLY UNSATURATED CARBOXYLIC ACID, 
     B. A WATER-SOLUBLE BASE, 
     C. WATER, AND, IF NECESSARY, 
     D. ONE OR MORE COMPOUNDING AGENTS. 
     The components of the coating composition are explained below. 
     A. The hydrophilic copolymer is a copolymer of (i) ethylene, (ii) an alpha,beta-ethylenically unsaturated carboxylic acid and (iii) a polyvalent alcohol monoester of alpha,beta-ethylenically unsaturated carboxylic acid. 
     i. The monomeric units derived from ethylene are the most important ones which give maximum effect at low concentration compared with other comonomers, on improving water resistance, adhesion to substrates, and brittleness in the dry state, which are most important defects of the conventional hydrophilic polymers. Introduction of the monomeric units of ethylene, which has smallest molecular weight, in the copolymer makes the decrease of hydrophilic nature of the copolymer minimum and improves not only water resistance and brittleness in the dry state which are necessary for practical use, but also adhesion to substrates, beyond any expectation. The proportion of ethylene in the copolymer is 60 to 20% by mole. If the proportion is more than 60% by mole, although water resistance and brittleness in the dry state may be improved remarkably, hydrophilic nature is unfavorably lowered. If the proportion is less than 20% by mole, improvement in the physical properties is insufficient. 
     ii. The monomeric units derived from alpha,beta-ethylenically unsaturated carboxylic acid have effects on making the hydrophilic copolymer water-soluble by reacting the latter with a water-soluble base and forming a film insoluble in water with excellent surface hardness by cross-linking the functional groups utilizing thermal treatment, and the like. 
     As the alpha,beta-ethylenically unsaturated carboxylic acids, those having 3 to 9 carbon atoms such as acrylic acid, methacrylic acid, crotonic acid, itaconic acid, maleic acid, fumaric acid, cinnamic acid, and the like are preferable. Among them, methacrylic acid and acrylic acid are more preferable industrially. 
     The proportion of the alpha,beta-ethylenically unsaturated carboxylic acid in the copolymer is 20 to 1% by mole, preferably 15 to 2% by mole. If the proportion is more than 20% by mole, hydrophilic nature is lowered and if the proportion is less than 1% by mole, it is difficult to make the copolymer water-soluble. 
     iii. The monomeric units derived from polyvalent alcohol monoester of alpha,beta-ethylenically unsaturated carboxylic acid have an effect on controlling hydrophilic nature of the copolymer. Said component is derived from an alpha,beta-ethylenically unsaturated carboxylic acid as described in the above item (ii) and from a polyvalent alcohol, which form a monoester structure. As the polyvalent alcohol, those having 2 to 6 carbon atoms such as ethylene glycol, propylene glycol, glycerin, diethylene glycol, triethylene glycol, dipropylene glycol, and the like are preferable. Among them, ethylene glycol is most preferable industrially. 
     The proportion of the polyvalent alcohol monoester of alpha,beta-ethylenically unsaturated carboxylic acid in the copolymer is 20 to 79% by mole, preferably 25 to 78% by mole. 
     b. The water-soluble base is a component necessary for making the hydrophilic copolymer water-soluble. As the water-soluble bases, ammonia and amines are principally used and sometimes basic alkali metal compounds can be used. As the amines, aliphatic amines such as monoethylamine, diethylamine, triethylamine, propylamine, butylamine, ethylenediamine, and the like, and aliphatic hydroxy amines such as ethanolamine, dimethylethanolamine, and the like are mainly used. However, if required, other amines such as pyridine, morpholine, benzylamine, aniline, and the like may be used. Examples of the basic alkali metal compounds are sodium hydroxide, potassium hydroxide, sodium carbonate, potassium carbonate, sodium bicarbonate, and the like. 
     The amount of the water-soluble base to be used is that necessary for neutralizing a part or the whole of the carboxyl groups in the hydrophilic coplymer. In general, 0.01 to 50 parts by weight, preferably 0.1 to 25 parts by weight, of the water-soluble base per 100 parts by weight of the hydrophilic copolymer is used. 
     The water-soluble base has effects not only on making the hydrophilic copolymer water-soluble but also, to our surprise, if some kinds of the bases are used, on greatly improving surface hardness of the film while maintaining excellent hydrophilic nature and other good physical properties. In this sense, amines are particularly preferable. 
     c. Water is used as a solvent in the coating composition of the present invention. It is preferable from viewpoints of economics, public health and safety. The amount of water to be used changes widely depending on purposes of applications but in general 100 to 1000 parts by weight of water are preferably used per 100 parts by weight of the hydrophilic copolymer. 
     In some cases, depending on coating conditions, a part of the water, and in special cases almost all the water containing the water-soluble base may be replaced by a water-soluble organic solvent such as methanol, ethanol, isopropanol, dimethylformamide, and the like. 
     d. The coating composition may contain one or more compounding agents or additives such as curing catalysts, cross-linking agents, surface active agents, flow control agents, pigments, coloring agents, other polymeric solutions, and the like. 
     As the curing catalysts, conventional ones such as sulfonic acids and the like may be used. If ammonia is used as the water-soluble base in the coating composition, since surface hardness of the formed film is inferior to that of the film formed by using an amine, it is preferable to use water-soluble sulfonic acids such as benzenesulfonic acid, p-toluenesulfonic acid, and the like, as the curing catalyst in an amount of preferably 0.1 to 2 parts by weight per 100 parts by weight of the hydrophilic copolymer. By using such a curing catalyst, a film excellent in surface hardness and resistance to scuffing while maintaining excellent hydrophilic nature can be obtained. This is one of features of the present invention. 
     As the cross-linking agents, aminoplasts such as condensation products of formaldehyde with urea, melamine, benzoguanamine, and the like, epoxy compounds such as bisphenol A epichlorhidrin, vinyl cyclohexene diepoxide, butadiene diepoxide, and the like, polyvalent block isocyanates such as a reaction product of phenol with prepolymer obtained from trimethylol propane and tolylene diisocyanate, and the like can be used in order to improve the surface hardness. The amount of the cross-linking agent to be used is preferably 1 to 10 parts by weight per 100 parts by weight of the hydrophilic copolymer. 
     Surface active agents are used in the coating composition in order to increase wettability of the surface of the formed film and to prevent fogging which appears after the moisture absorption attains to the saturated state and lowers reflection or transparency of the substrate. In the case of preventing fogging, it is necessary and more effective that the coating film has hydrophilic nature and greater surface hardness from the aspect of durability of the surface active agent. As the surface active agents, water-soluble and nonionic surface active agents are preferable. Examples of such surface active agents are polyoxyethylene alkylphenyl ether, polyoxyethylene alkyl ether, polyoxyethylene sorbitane ester, and the like. In general, the surface active agent is used in an amount of preferably 1 to 10 parts by weight per 100 parts by weight of the hydrophilic copolymer. 
     As the polymeric solutions, polymeric emulsions of acrylic polymers, vinyl acetate polymers and the like, or polymeric aqueous solutions of polyvinyl alcohol, acrylic polymers, cellulose derivatives and the like may be used. 
     The compounding agents or additives can be used alone or as a mixture of two or more kinds of additives. For example, if a mixture of a surface active agent and a curing catalyst is added to the coating composition, a film having remarkable hydrophilic nature and excellent surface hardness can be formed on the substrate. 
     The hydrophilic copolymer used in the coating composition can be prepared as follows: 
     A. Direct copolymerization of each monomer corresponding to ethylene, an alpha, beta-ethylenically unsaturated carboxylic acid and a polyvalent alcohol monoester of alpha, beta-ethylenically unsaturated carboxylic acid; and 
     B. Stepwise preparation comprising copolymerization of ethylene and an alpha,beta-ethylenically unsaturated carboxylic acid and the subsequent reaction of the resulting copolymer with (I) a polyvalent alcohol, (II) a 1,2-epoxy compound or (III) an alkylene carbonate in order to convert the desired amount of the carboxyl groups to polyvalent alcohol monoesters. 
     The direct copolymerization method as mentioned in above (A) has the following disadvantages. Since a polyvalent alcohol monoester, for example, ethylene glycol methacrylate, inevitably accompanies such a by-product as ethylene glycol dimethacrylate which has a crosslinking function and which can only be removed with great difficulty, the use of such a polyvalent alcohol monester accompanying the by-product would give unfavorable gel insolbule in the solvent, etc. 
     The method of reacting a copolymer of ethylene and alpha,beta-ethylenically unsaturated carboxylic acid with a polyvalent alcohol as mentioned above (B) (I) is also not preferable, since gel is easily produced. On the other hand, the methods of reacting a copolymer of ethylene and alpha, alpha,beta-ethylenically unsaturated carboxylic acid with a 1,2-epoxy compound or an alkylene carbonate as mentioned above (B) (I) and (III) are most preferable, since the hydrophilic copolymers containing no gel can easily be produced. 
     The copolymerization of ethylene and alpha,beta-ethylenically unsaturated carboxylic acid can be carried out by using conventional solution polymerization, emulsion polymerization or the like. In general, ethylene pressure of 10 to 200 kg/cm 2  and reaction temperature of 50° to 100° C may be employed. As polymerization catalyst, there may be used azobisisobutyronitrile, benzoyl peroxide, potassium persulfate, and the like. As a solvent, benzene, hexane, butanol, ethanol, water, and the like, alone or as a mixture thereof, may be used. 
     Degree of polymerization of the resulting ethylene copolymer can be controlled by the kind of solvent, polymerization temperature, the amount of catalyst, and the like, and in general, it is preferably 0.1 to 1.0 in terms of reduced viscosity (η sp  /c) measured in methanol at 30° C with concentration of 0.1 g/dl. 
     The reaction of the resulting ethylene-alpha,beta-ethylenically unsaturated carboxylic acid copolymer with a 1,2-epoxy compound or an alkylene carbonate can be carried out as follows. As the 1,2-epoxy compounds, ethylene oxide, propylene oxide, and the like may be used. As the alkylene carbonates, ethylene carbonate, propylene carbonate, and the like may be used. The reaction can generally be carried out in a autoclave or a conventional vessel. As a solvent, in general, an aliphatic alcohol such as methanol, ethylene glycol, or the like may be used alone, or a mixture of an aliphatic alcohol with an aromatic compound such as benzene, toluene, xylene or the like, or a mixture of an aliphatic alcohol with water may be used. As a reaction catalyst, a basic catalyst such as sodium hydroxide, sodium carbonate, or the like is mainly used. Reaction temperature of 30° to 180° C may generally be used. 
     The thus obtained hydrophilic copolymer consists of three monomeric units of ethylene, alpha,beta-ethylenically unsaturated carboxylic acid and polyvalent alcohol monoester of alpha,beta-ethylenically unsaturated carboxylic acid; this is identified by analyses using NMR and IR spectra. Reduced viscosity of the hydrophilic copolymer is generally 0.1 to 0.6 measured in methanol at 30° C with concentration of 0.1 g/dl. However, since the hydrophilic copolymer can form a water-insoluble film by cross-linking with thermal treatment and the like, it is not necessary to limit the degree of polymerization. In an extreme case, so-called prepolymer having very low molecular weight may be used. 
     The coating composition is prepared by adding the water-soluble base and water, and if required, one or more compounding agent to the hydrophilic copolymer thus prepared. 
     The coating composition of the present invention can be coated on substrates by using conventional coating methods such as dip, spray, roll, flow coatings and the like, and subsequently dried and baked with heated air, far infrared rays, and the like to form a film. Drying and baking temperature is about 50° to 260° C, preferably 100° to 200° C. In special cases, films can be formed by irradiation of ultraviolet rays, gamms rays, electron rays, and the like. 
     Thickness of the film formed is usually 10 - 50 microns. The film is generally formed by one or several coatings with the same coating composition solution and drying, but in some cases, laminated films can be formed by using different coating composition solutions. 
     As mentioned above, the films formed by coating, drying and baking the coating compositions of the present invention are excellent not only in hydrophilic nature but also in water resistance, adhesion to substrates, surfaces hardness and the like without becoming brittle in the dry state. Further since the coating composition is an aqueous solution, the films formed are excellent in surface appearance such as smoothness, transparency, gloss and the like, so that it is very difficult to distinguish a substrate not coated from that coated with the coating composition. 
     In addition, the formed films have other excellent physical properties, which are necessary for practical applications, such as resistance to weathering, heat, cold, and chemicals, as well as excellent nonfogging, antistatic properties, resistance to stains, and the like. Semiconducting properties are also observed in the wet state. 
     As the substrates, glass, metals, plastics, and fibers, and in some cases, paper, wood, stone, cement, and the like can be used. As glass, transparent glass used mainly in windows, vehicles, and the like, or mirrors, lenses, and the like can be used. As the metals, aluminum, iron, steel, stainless steel, and the like can mainly be used. Films can be formed directly on the metals or on paint coated metals. As the plastics, stretched or nonstretched shaped articles of poly(methyl methacrylate), polycarbonates, polyesters, nylons, styrene, resins, vinyl chloride or vinylidene chloride resins, polyolefin resins, cellulosic derivatives including cellophane and the like can be used. As the fibers, polyesters, nylons, polyacrylonitrile, polyvinyl chloride, polyvinylidene chloride, polyolefins, cellulosic fibers and the like can be used. 
    
    
     The present invention is explained more in detail by the following examples, in which parts and percentages are by weight unless otherwise specified. 
     EXAMPLE 1 
     i. Preparation of ethylene-methacrylic acid copolymer 
     In an autoclave, 100 g of methacrylic acid and 1.0 g of benzoyl peroxide were dissolved in 900 g of tert-butanol. Then ethylene is fed to the autoclave, and the copolymerization was carried out at 70° C for 3 hours under ethylene pressure of 50 kg/cm 2 . After adding n-hexane to the reaction mixture, the product was deposited and separated to give 78 g of an acid copolymer (A). In the same manner as mentioned above except for employing ethylene at a pressure of 20 kg/cm 2 , an acid copolymer (B) was obtained. For comparison, an acid polymer (C) was obtained by polymerizing methacrylic acid in solution without using ethylene. Ethylene content and reduced viscosity of each acid copolymer are as set forth in Table 1. 
     
                       Table 1                                                     
______________________________________                                    
              Ethylene                                                    
              content *1  Reduced                                         
Acid copolymer                                                            
              (% by mole) viscosity *2                                    
______________________________________                                    
(A)           51.9        0.58                                            
(B)           36.9        0.52                                            
(C)           0           0.60                                            
______________________________________                                    
*1  Ethylene content was measured by N.M.R.                               
    analysis as follows:                                                  
    Apparatus: Nippon Denshi MH 100                                       
    Solvent: Heavy hydrogenated methanol                                  
    Concentration: 10%                                                    
    Temperature at measuring: Room temperature                            
    R.F. level: 0.1                                                       
    A.F. level: 0.5                                                       
    Analysis was based on the following                                   
    assignment.                                                           
______________________________________                                    
Chemical shifts (ppm)                                                     
                Assignment                                                
______________________________________                                    
a: 0.6 - 1.6 b: 1.90                                                      
                 ##STR1##                                                 
                (TMS standard)                                            
______________________________________                                    
*2  Solvent: Methanol                                                     
    Concentration: 0.1 g/dl                                               
    Temperature at measuring: 30° C                                
 
    
     ii. Hydroxyethylation 
     In a flask, 60 g of the acid copolymer (A) was dissolved in 600 g of ethylene glycol and then 240 g of ethylene carbonate and 0.6 g of sodium carbonate were added thereto. The reaction was carried out at 130° C for 5 hours. After addition of aqueous solution of sulfuric acid, the reaction product was deposited and separated to give 68 g of a hydrophilic copolymer A. In the same manner, the hydrophilic copolymer B was obtained from the acid copolymer (B) and the hydrophilic copolymer C (comparison) was obtained from the acid polymer (C). Components and their proportions of each hydrophilic copolymer are as set forth in Table 2. 
     
                       Table 2                                                     
______________________________________                                    
Hydrophilic copolymer                                                     
                     A       B       C                                    
______________________________________                                    
           Ethylene      51.9    36.9  0                                  
Component *1                                                              
           Methacrylic acid                                               
                         4.8     6.3   10.0                               
(% by mole)                                                               
             [a]                                                          
           Hydroxyethyl  43.3    56.8  90.0                               
           methacrylate [b]                                               
Degree of                                                                 
hydroxyethylation (%) *2                                                  
                     90      90      90                                   
[b/(a + b) × 100]                                                   
Reduced                                                                   
viscosity *3         0.34    0.27    0.34                                 
______________________________________                                    
 Note)-                                                                   
 *1 The hydrophilic copolymers were treated with an aqueous solution of   
 sodium hydroxide and analyzed by infrared absorption spectra. There were 
 observed absorptions of a sodium salt moiety of carboxylic acid (1500 -  
 1600 cm.sup.-1), an ester group of carboxylic acid (1725 cm.sup.-1) and a
 hydroxyl group (3400 cm.sup.-1). Absorbance ratio of the ester group and 
 the hydroxyl group was in agreement with those of the hydroxyethyl       
 methacrylate monomer. Thus it was identified that the hydrophilic        
 copolymers contained monomeric units of methacrylic acid and hydroxyethyl
 methacrylate.                                                            
 *2 It was calculated from the absorbance ratio of the ester group (1725  
 cm.sup.-1) and the salt moiety of carboxylic acid (1500 - 1600 cm.sup.-1)
 obtained from the infrared spectra.                                      
 *3 Solvent: Methanol                                                     
  Concentration: 0.1 g/dl                                                 
  Temperature at measuring: 30° C                                  
 
    
     iii. Preparation of coating compositions 
     The hydrophilic copolymer A (30 g) was dissolved in 170 g of water containing 0.65 g of ammonia to give a transparent aqueous composition A containing 15% by weight of the hydrophilic copolymer A. In the same manner a composition B and a composition C (comparison) were obtained from the hydrophilic copolymers B and C, respectively. 
     EXAMPLE 2 
     The compositions A and B obtained in Example 1 were coated on a surface of a glass plate and dried and baked with heated air at 180° C for 30 minutes to give Samples A and B. The formed films of Samples A and B were excellent in smoothness, transparency and gloss, so that it was impossible to distinguish the coated glass plates from untreated one. For comparison, the composition C was coated on a glass plate and dried and baked in the same manner to give Sample C. Thickness of each coated film was 30 ± 5 microns. 
     Physical properties of each coated film are as set forth in Table 3. 
     
                                           Table 3                                 
__________________________________________________________________________
                   Sample                                                 
                                 C                                        
Physical properties                                                       
                   A      B      (comparison)                             
__________________________________________________________________________
Hydrophilic                                                               
        Nonfogging effect *1                                              
nature  (sec)      53     71     75                                       
        Water resistance *2                                               
                   No change                                              
                          No change                                       
                                 Swollen in                               
                                 part                                     
Resistance to                                                             
        Resistance to hot                                                 
                   No change                                              
                          No change                                       
                                 Peeled in                                
water   water *3                 part                                     
        Resistance to                                                     
                   &gt;1 hour                                                
                          &gt;1 hour                                         
                                 Peeled within                            
        boiling water *4                                                  
                   No change                                              
                          No change                                       
                                 30 minutes                               
        Cross cut test *5                                                 
                   100/100                                                
                          90/100 40/100                                   
Adhesion to                                                               
substrate                                                                 
        Drawing test *6                                                   
                   10     10     6                                        
        (points)                                                          
Brittleness                                                               
        Cutting test *7                                                   
                   Not peeled                                             
                          Not peeled                                      
                                 Peeled                                   
Hardness                                                                  
        Pencil hardness *8                                                
                   H - 2H 2H     2H                                       
__________________________________________________________________________
 Note)                                                                    
 *1 Time (in seconds) required for producing fogging when nitrogen gas of 
 40° C containing saturated vapor is blown at the rate of 52 cc/min
 . cm.sup.2 to the film to be tested kept at 35° C was measured.   
 When an untreated glass plate was used, it took 3 - 4 seconds.           
 *2 Surface appearance of the sample was observed after dipping it in wate
 at 23° C for 100 hours.                                           
 *3 Surface appearance of the sample was observed after dipping it in hot 
 water at 60° C for 24 hours.                                      
 *4 The sample was dipped in boiling water and its surface appearance was 
 observed.                                                                
 *5 100 squares (10 × 10), each side being 1 mm long, were made usin
 a razor blade on the surface of the film formed sample at the dry state  
 and the number of squares retained on the surface after removing peeled  
 squares with an adhesive tape was counted. There is a detailed descriptio
 on page 255 of &#34;Toso-gizyutsu Binran&#34; (Manual of Coating Techniques)     
 published by Nikkan Kogyo Shinbun Sha, Japan, in 1972.                   
 *6 Spirals (having doubling parts) were drawn with a sharp pointed needle
 loading 200 g thereon on the surface of the film formed sample at the dry
 state and the state of peeling was evaluated according to the standard of
 Japanese Association of Paint Industries. (10 points is the best and 0   
 point is the worst.) There is a detailed description on page 255 of      
 &#34;Toso-gizyutsu Binran&#34; mentioned above.                                  
 *7 The film was cut with a razor blade and peeling of the surrounding    
 parts was observed. The sample was tested at dry state.                  
 *8 The sample was tested at a temperature of 23° C and relative   
 humidity of 50%.                                                         
 
    
     As is clear from Table 3, introduction of the monomeric units of ethylene into the hydrophilic copolymer only lowers hydrophilic nature of the formed film to the minimum and improves not only water resistance and brittle at the dry state but also adhesion to substrates greatly, these physical properties being necessary for practical applications. 
     The coated films formed from the compositions A and B also showed excellent results in resistance to weathering, heat, and cold. 
     EXAMPLE 3 
     Five coating compositions containing 15% of the hydrophilic copolymer were prepared by adding water-soluble bases as set forth in Table 4 to the hydrophilic copolymer B obtained in Example 1. The water-soluble bases were used two times as much as required for neutralizing the carboxyl groups of the hydrophilic copolymer B. Each composition was coated on a surface of a glass plate and dried and baked with heated air at 180° C for 30 minutes. Thickness of each coated film was 30 ± 5 microns. 
     Physical properties of each coated film measured in the same manner as in Example 2 are set forth in Table 4. 
     
                       Table 4                                                     
______________________________________                                    
             Physical properties                                          
                            Nonfogging                                    
Run  Water-soluble Pencil   effect   Water                                
No.  base          hardness (sec)    resistance                           
______________________________________                                    
1    Ammonia       2H       71       No change                            
2    Monoethylamine                                                       
                   4H       68       &#34;                                    
3    Diethylamine  4H       60       &#34;                                    
4    Ethylenediamine                                                      
                   3H - 4H  75       &#34;                                    
5    Ethanolamine  3H       88       &#34;                                    
______________________________________                                    
 
    
     As is clear from Table 4, the use of amines as the water-soluble base improves surface hardness remarkably while maintaining good hydrophilic nature. 
     EXAMPLE 4 
     A composition was prepared by adding paratoluenesulfonic acid (hereinafter referred to as PTS) to the composition B obtained in Example 1. 0.3 part of PTS per 100 parts of the hydrophilic copolymer B was added to the composition B. The resulting composition was coated on a surface of a glass plate and dried and baked with heated air at 180° C for  30 minutes. Thickness of the coated film was 30 ± 5 microns. 
     Physical properties of the coated film measured in the same manner as in Example 2 together with the data of the composition B obtained in Example 2 are set forth in Table 5. 
     
                       Table 5                                                     
______________________________________                                    
        Physical properties                                               
                     Nonfogging                                           
Proportion                                                                
          Pencil     effect      Water                                    
of PTS    hardness   (sec)       resistance                               
______________________________________                                    
0 %       2H         71          No change                                
0.3 %     3H - 4H    69          &#34;                                        
______________________________________                                    
 
    
     As is clear from Table 5, when a curing catalyst of PTS is added to the composition containing ammonia as the water-soluble base, surface hardness of the coated film can be improved remarkably while maintaining good hydrophilic nature. Further resistance to scuffing of the coated film is also excellent. 
     Resistance to scuffing is measured as follows. 
     The coated surface of the sample was rubbed with wiping cloth for glasses or gauze with load of 100 g/cm 2  1000 times in reciprocating motion and the presence of scuffing was evaluated. 
     EXAMPLE 5 
     To the composition A obtained in Example 1, 2 or 5 parts of aminoplast of urea type (a ureafolmaldehyde condensate manufactured by Sanwa Chemical Co., Ltd., MX201) per 100 parts of the hydrophilic copolymer A was added to give compositions as listed in Table 6. Each composition was coated on a surface of a glass plate and dried and baked with heated air at 180° C for 30 minutes. Thickness of each coated film was 30 ± 5 microns. 
     Physical properties of each coated film measured in the same manner as in Example 2 are set forth in Table 6. 
     
                       Table 6                                                     
______________________________________                                    
          Physical properties                                             
     Proportion           Nonfogging                                      
Run  of amino-  Pencil    effect    Water                                 
No.  plast (%)  hardness  (sec)     resistance                            
______________________________________                                    
1    0           H - 2H   53        No change                             
2    2          2H - 3H   49        &#34;                                     
3    5          3H - 4H   41        &#34;                                     
______________________________________                                    
 
    
     As is clear from Table 6, when an aminoplast is used as a cross-linking agent in the composition, remarkable improvement is obtained in surface hardness but hydrophilic nature is lowered slightly. Further resistance to scuffing was also excellent. 
     EXAMPLE 6 
     Coating compositions were prepared by adding 2.0, 3.5 or 5.0 parts of a surface active agent (hereinafter refered to as SA) to 100 parts of the hydrophilic copolymer A obtained in Example 1 which had been dissolved in an aqueous solution of monoethylamine. Polyoxyethyl nonylphenyl ether (manufactured by Nikko Chemical Co., Ltd., Nikol NP-10) was used as SA. Each composition was coated on a surface of a glass plate and dried and baked with heated air at 170° C for 20 minutes. Thickness of each coated film was 30 ± 5 microns. 
     Physical properties of each coated film measured in the same manner as in Example 2 are set forth in Table 7. 
     
                       Table 7                                                     
______________________________________                                    
          Physical properties                                             
     Proportion           Nonfogging                                      
Run  of SA      Pencil    effect    Water                                 
No.  (%)        hardness  (sec)     resistance                            
______________________________________                                    
1    0          3H - 4H   51        No change                             
2    2.0        4H        &gt;120 *1   &#34;                                     
3    3.5        3H - 4H   &gt;120 *1   &#34;                                     
4    5.0        3H - 4H   &gt;120 *1   &#34;                                     
______________________________________                                    
 Note)                                                                    
 *1 Although a water film was produced on the surface, no fogging was     
 produced after 120 seconds.                                              
 
    
     As is clear from Table 7, when SA is added to the composition containing an amine as the water-soluble base, hydrophilic nature is improved greatly while maintaining excellent surface hardness. 
     EXAMPLE 7 
     To the composition A obtained in Example 1, 0.25 part of PTS and/or 3.5 parts of SA per 100 parts of the hydrophilic copolymer A were added to give compositions as set forth in Table 8. SA was the same one as used in Example 6. Each composition was coated on a surface of a glass plate and dried and baked with heated air at 170° C for 20 minutes. Thickness of each coated film was 30 ± 5 microns. 
     Physical properties of each coated film measured in the same manner as in Example 2 are set forth in Table 8. 
     
                       Table 8                                                     
______________________________________                                    
               Physical properties                                        
     Proportion                                                           
               Proportion       Nonfogging                                
                                        Water                             
Run  of PTS    of SA     Pencil effect  resist-                           
No.  (%)       (%)       hardness                                         
                                (sec)   ance                              
______________________________________                                    
1    0.25      0         3H - 4H                                          
                                51      No                                
                                        change                            
2    0.25      3.5       4H     &gt;120    &#34;                                 
3    0         3.5       2H     &gt;120    &#34;                                 
______________________________________                                    
 
    
     As is clear from Table 8, when both PTS and SA are added to the composition containing ammonia as the water-soluble base, it is possible to improve surface hardness and hydrophilic nature greatly. 
     EXAMPLE 8 
     The composition A obtained in Example 1 was coated on a polyester film and dried and baked with heated air at 180° C for 30 minutes. The formed film was forced to be peeled off to measure electrical properties. Further resistance to stains of Sample A obtained in Example 2 was also measured. 
     The results obtained are shown in Table 9. 
     
                       Table 9                                                     
______________________________________                                    
        Antistatic properties *1                                          
                        Half-life  7 sec                                  
Electrical                                                                
        Volume resistivity                                                
                        Relative hu-                                      
properties                                                                
        at 23° C (Ωcm)                                       
                        midity of 50%                                     
                                   2.1 × 10.sup.14                  
                        Wet state  3 × 10.sup.6                     
______________________________________                                    
        Dirt chamber test *2                                              
                        Relative hu-                                      
        at 20° C midity of 75%                                     
                                   Clean                                  
Resistance              Wet state  Clean                                  
to stains                                                                 
        Prevention of oil                                                 
                        Easily                                            
        stains *3       wiped off                                         
______________________________________                                    
 Note)                                                                    
 *1 Measured by the honet meter at 20° C and relative humidity of  
 65%.                                                                     
 *2 See R.E. Schanzle, Mod. Packaging No. 5, 129 (1964) When a glass plate
 alone was tested, the result was heavy dirt.                             
 *3 The sample was painted with lip-stick and pomade and allowed to stand 
 at 23° C for 24 hours. Then easiness of wiping off the lip-stick  
 and pomade was tested.                                                   
 
    
     As is clear from Table 9, the composition of the present invention is also effective as antistatic agent and stain resistance agent. 
     EXAMPLE 9 
     The composition obtained in Example 7 Run No. 2 containing 0.25% of PTS and 3.5% of SA was coated on one side of a polymethyl methacrylate resin sheet and dried with air and then baked with far infrared rays for 2 minutes. The formed film had good adhesion to the substrate and surface hardness and showed remarkable preventing effect of fogging. 
     EXAMPLE 10 
     i. Preparation of ethylene-acrylic acid copolymer 
     In the same manner as described in Example 1, ethylene and acrylic acid were copolymerized under ethylene pressure of 50 kg/cm 2  to give the acid copolymer having the ethylene content of 48.0% by mole and reduced viscosity of 0.51. 
     ii. Hydroxyethylation 
     The thus obtained acid copolymer was hydroxyethylated in the same manner as described in Example 1 to give the hydrophilic copolymer having the following components in the following proportions: 
     
         ______________________________________                                    
Ethylene               48.0% by mole                                      
Acrylic acid [a]        5.2% by mole                                      
Hydroxyethyl acrylate  46.8% by mole                                      
 [b]                                                                      
Degree of hydroxyethyla-                                                  
 tion [b/(a + b) × 100]                                             
                       90%                                                
______________________________________                                    
 
    
     iii. Preparation of a composition 
     The resulting hydrophilic copolymer (30 g) was dissolved in 170 g of water containing 0.74 g of ammonia to give a transparent aqueous solution containing 15% by weight of the hydrophilic copolymer. 
     EXAMPLE 11 
     The composition obtained in Example 10 was coated on a surface of a glass plate and dried and baked with heated air at 180° C for 30 minutes. Thickness of the formed film was 30 ± 5 microns. 
     Physical properties of the formed film measured in the same manner as in Example 2 are set forth in Table 10. 
     
                       Table 10                                                    
______________________________________                                    
Nonfogging effect     50 sec.                                             
Water resistance      No change                                           
Cross cut test        100/100                                             
Drawing test          10 points                                           
Cutting test          Not peeled                                          
______________________________________                                    
 
    
     As is clear from Table 10, when acrylic acid is used as the alpha,beta-ethylenically unsaturated carboxylic acid, excellent hydrophilic nature, water resistance and adhesion to the substrate were obtained without showing brittleness in the dry state. 
     EXAMPLE 12 
     The acid copolymer (B) obtained in Example 1 (10 g) was dissolved in 130 g of methanol and 0.2 g of sodium hydroxide was added thereto. After dissolving completely, the resulting solution was placed in an autoclave. Then 7 g of ethylene oxide was charged in the autoclave and the reaction was carried out at 110° C for 6 hours. After the reaction, an aqueous solution of sulfuric acid was added to the reaction mixture to deposit and separate the hydrophilic copolymer having the components as follows: 
     
         ______________________________________                                    
Ethylene             36.9% by mole                                        
Methacrylic acid [a] 11.4% by mole                                        
Hydroxyethyl meth-                                                        
acrylate [b]         51.7% by mole                                        
Degree of hydroxy-                                                        
ethylation           82%                                                  
[b/(a + b) × 100]                                                   
______________________________________                                    
 
    
     The resulting hydrophilic copolymer (5g) was dissolved in 20 g of water containing 0.22 g of ammonia to give a transparent aqueous solution containing 20% of the hydrophilic copolymer. Then the aqueous solution was coated on a surface of a glass plate and dried and baked in the same manner as in Example 2. The formed film showed excellent nonfogging effect, water resistance and adhesion to the substrate. 
     EXAMPLE 13 
     The acid copolymer (B) obtained in Example 1 was hydroxyethylated in the same manner as described in Example 1 except for employing a reaction time of 4 hours in place of 5 hours to give the hydrophilic copolymer having the following components: 
     
         ______________________________________                                    
Ethylene             36.9% by mole                                        
Methacryalic acid [a]                                                     
                     14.5% by mole                                        
Hydroxyethyl meth-                                                        
acrylate [b]         48.6% by mole                                        
Degree of hydroxy-                                                        
ethylation           77%                                                  
[b/(a + b) × 100]                                                   
______________________________________                                    
 
    
     The composition obtained by dissolving the resulting hydrophilic copolymer in ammonia water was coated on a surface of a glass plate and dried and baked with heated air at 180° C for 30 minutes. Thickness of the formed film was 30 ± 5 microns. Nonfogging effect was 49 seconds. The formed film was also excellent in water resistance and adhesion to the substrate.