Method of making magnetic devices including amorphous alloys
BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     The invention is in the field of electromagnetic devices using soft magnetic materials. 
     2. Brief Description of the Prior Art 
     Many metallic alloys have been produced in amorphous (non-crystalline) form by such methods as rapid cooling from the melt. These amorphous alloys have markedly different magnetic and mechanical properties from crystalline alloys of similar composition. Among these amorphous alloys are various nickel containing, iron containing and cobalt containing alloys, which include glass formers such as phosphorous and boron. (See, for example, Journal of Non-Crystalline Solids, 15 (1974) 165-178, &#34;Amorphous Magnetism&#34; H. O. Hooper and A. M. de Graaf, 1973, Plenum Press, New York, pp. 313-320; U.S. Pat. No. 3,838,365, Sept. 24, 1974 issued to M. Dutoit.) Various workers have studied the mechanical, electrical, magnetic, and acoustic properties of such amorphous materials. The characterization of these materials as amorphous is borne out by X-ray scattering measurements which do not show the sharp scattering peaks characteristic of crystalline materials. This characterization is particularly appropriate when considering the magnetic properties of these materials since the X-ray characteristic length is much smaller than distances characteristic of magnetic ordering phenomena. These materials have also been found to possess many of the thermodynamic properties of glasses. Many investigators are currently searching to find amorphous alloys with useful properties. 
     SUMMARY OF THE INVENTION 
     It has been found that certain cobalt rich amorphous alloys possess low magnetostriction along with high electrical resistance and excellent soft magnetic properties. These materials are produced directly in the filamentary form needed for the fabrication of many classes of magnetic devices so that it is not necessary to go through the many metallurgical processing steps needed to reduce ingots to the wire or tape form required for these devices. When the wire or tape is wound to final geometry, raised to a temperature below its crystallization temperature but above its Curie temperature and immediately quenched in a high heat of vaporization liquid (e.g., water), the permeability is greatly improved. An exemplary alloy was shown to possess properties, in some respects, equivalent to those of Supermalloy, an alloy of much more complex manufacture. 
     The subject materials are cobalt rich, cobalt-iron based alloys including a total of from 10 to 30 atomic percent of &#34;glass formers&#34;, the glass forming group consisting of P, Si, B, C, As, Ge, Al, Ga, In, Sb, Bi and Sn. The cobalt-iron &#34;metallic&#34; portion can also include up to approximately 25 percent of a species selected from Ni, Cr, Mn, V, Ti, Mo, W, Nb, Zr, Pd, Pt, Cu, Ag, Au. For each value of the total proportion of &#34;metallic&#34; constituents there is a narrow band of compositions which defines the range of low magnetostriction compositions. This band may vary as the amount of &#34;metallic&#34; constituent varies with respect to the amount of glass forming constituent. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     FIG. 1 is a ternary composition diagram showing the cobalt, iron, and nickel composition range within which exemplary low magnetostriction amorphous alloys fall; and 
     FIG. 2 is a perspective view of an exemplary electromagnetic device. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION THE MATERIALS 
     A class of low magnetostrictive amorphous alloys of excellent soft magnetic properties has been found within the composition range represented by (Co a  Fe b  T c ) i  X j  ; with 0.7 ≦ a ≦ 0.97, 0.03 ≦ b ≦ 0.25 and a + b + c = 1. The elements within the parenthesis can be called the &#34;metallic&#34; constituents which make up from 70 to 90 atomic percent of the alloy (0.7 ≦ i ≦ 0.9) and X is the &#34;glass former&#34; group, which make up the remainder. X is selected from P, Si, B, C, As, Ge, Al, Ga, In, Sb, Bi and Sn or a combination of these. T is selected from Ni, Cr, Mn, V, Ti, Mo, V, W, Nb, Zr, Pd, Pt, Cu, Ag, and Au or a combination of these. The subscripts i and j sum to 1. The limits on the content of &#34;metallic&#34; constituents approximately delimit the composition range within which low magnetostriction is obtainable. From 10 to 30 atomic percent of glass formers is needed to achieve sufficiently stable amorphous alloys. 
     The above materials can be produced in amorphous form, for example, by extremely rapid cooling from the melt, usually as thin foils or tapes. Glass formers specified above are known to be so operative in nickel-iron alloys (Journal of Non-Crystalline Solids, 15 (1974) 165-178). It has been found that similar proportions are effective as glass formers in the alloys considered here. Improved stability results from inclusion of at least one atomic percent of at least one element selected from P, Si, B, C, As and Ge together with at least one atomic percent of at least one element selected from Al, Ga, In, Sb, Bi and Sn. 
     FIG. 1 shows the composition range of magnetic constituents within which exemplary nickel containing low magnetostrictive amorphous alloys lie. The magnetostriction is observed to be positive in the upper portion 11 of this range and negative in the lower portion 12. The dashed line 13 indicates the approximate position of optimum low magnetostrictive amorphous alloys for nickel containing alloys with approximately 25 atomic percent of glass forming constituents and 75 atomic percent &#34;metallic&#34; constituents. Within plus or minus one-half atomic percent in iron composition, the magnetostrictive effect is less than 10 percent of the magnetostrictive effect observed well away from the line. Variation of cobalt or nickel composition is at constant iron content somewhat less restricted since the change produced is nearly parallel to the line 13. For a composition made with an iron content within 0.1 atomic percent of the line, no magnetostrictive effect was observed on the same apparatus as was used to make the other measurements. This line 13 approximately describes the position of low magnetostriction for alloys &#34;metallic&#34; material content within plus or minus 5 atomic percent of the above mentioned 75 atomic percent quantity. The location of this line 13 was determined by experimental data reported in Table 1. The alloys measured can be represented by the formula (Co a  Fe b  Ni c ) 0 .75 P 0 .16 B 0 .06 Al 0 .03. 
     
                                           TABLE I                                 
__________________________________________________________________________
                     Glass transition or                                  
                              Change of                                   
                     crystallization                                      
                              magnetization                               
                                      Amorphous                           
                                            Curie                         
Sample                                                                    
     Composition     temperature                                          
                              for given stress                            
                                      to x-ray                            
                                            temperature                   
__________________________________________________________________________
1    (Co.sub..9 Fe.sub.0.1).sub..75 P.sub..16 B.sub..06 Al.sub..03        
                     ˜760° K                                 
                              +15%    yes   657° K                 
2    (Co.sub..95 Fe.sub..05).sub..75 P.sub..16 B.sub..06 Al.sub..03       
                     ˜756° K                                 
                              +7%     yes   642° K                 
3    (Co.sub..96 Fe.sub..04).sub..75 P.sub..16 B.sub..06 Al.sub..03       
                     ˜757° K                                 
                              0       yes   640° K                 
4    (Co.sub..98 Fe.sub..02).sub..75 P.sub..16 B.sub..06 Al.sub..03       
                     ˜759° K                                 
                              -18.5%  yes   633° K                 
5    Co.sub..75 P.sub..16 B.sub..06 Al.sub..03                            
                     ˜763°  K                                
                              -35%    yes   630° K                 
6    (Co.sub..72 Fe.sub..08 Ni.sub..2).sub..75 P.sub..16 B.sub..06        
     Al.sub..03      ˜743° K                                 
                              +8%     yes   565° K                 
7    (Co.sub..76 Fe.sub..04 Ni.sub..2).sub..75 P.sub..16 B.sub..06        
     Al.sub..03      ˜743°  K                                
                              -29%    yes   560° K                 
__________________________________________________________________________
 
    
     PRODUCTION OF AMORPHOUS ALLOYS 
     Amorphous alloys have been produced by several methods involving rapid cooling of thin sections of the molten material. Some techniques involve the injection of a thin stream of liquid into a cooling bath, others involve contact of a thin portion of liquid with a cool solid. The latter techniques have been characterized under the general description of &#34;splat cooling.&#34; Among these techniques are the piston and anvil technique and techniques involving the dropping of a portion of liquid between two counterrotating rollers (H. S. Chen and C. E. Miller, Reviews of Scientific Instruments, 41 (1970) 1237) or the injection of a thin stream of liquid between counterrotating rollers, such as in the apparatus pictured in U.S. Pat. No. 3,732,349 issued May 8, 1973 to Ho-Sou Chen et al. Amorphous metals have also been produced by vapor deposition or electrolytic deposition on a cooled surface. 
     In materials produced by the techniques described above, the extent or absence of crystalline ordering is investigated by such techniques as X-ray and electron beam scattering. These techniques, applied to the materials under consideration here, have shown no significant crystalline ordering over a greater than approximately 20 Angstroms range. Since magnetic ordering takes place with a characteristic length of the order of 1000 Angstroms, these materials show no crystalline ordering which can be seen by the magnetic system and, thus, can be classified as amorphous for purposes of magnetic description. 
     MATERIAL PROPERTIES 
     Soft magnetic materials with high electrical resistivity are required for the production of electromagnetic devices, such as inductors or transformers as pictured in FIG. 2. In FIG. 2 a transformer consists of a magnetic core 20 and conducting windings 22. The core 20 is wound from a long thin wire or tape 21 of an amorphous magnetic alloy. 
     Properties of importance in such devices include high initial permeability, high remanence and low coercivity. Amorphous magnetic material in the above-described composition range has been produced whose properties approach or meet the properties of conventional crystalline Supermalloy. The achievement of low coercivity is usually related to the achievement of a material possessing low magnetostriction. In addition, low magnetostriction is desirable for the production of devices whose properties are insensitive to mechanical stress during fabrication and varying thermomechanical stress during use. These materials have resistivities of the order of 200μ ohm centimeters which is an order of magnitude higher than the resistivities of permalloy materials. 
     It is known that the initial permeability of many magnetic materials is critically dependent on the thermal history of the materials during various stages of manufacture. In particular, Supermalloy, a material known and used for its high initial permeability, undergoes a closely controlled program of final cooling to develop its excellent magnetic properties. The materials of the invention, by contrast, have been shown to develop their high initial permeability properties upon a final quenching treatment. The material is fabricated to its final geometry (e.g., by winding the desired length of material on a bobbin to form an inductor or transformer core), raised to a temperature above the Curie temperature but below the glass transition temperature and quenched in a high heat of vaporization liquid, such as water. 
     The required residence time at the heat treatment temperature is somewhat temperature dependent, since the suggested physical phenomenon is diffusion related. Higher temperatures require shorter times. However, the difference between the Curie temperature and the glass transition temperature for these materials (See Table I), is small relative to the activation energy for ionic diffusion, so that over the composition range of interest, a residence time of 10 minutes is sufficient. Times as short as 1 minute are sufficient for most of the materials. The temperature must not be above the glass transition temperature so as not to destroy the amorphous nature of the alloy. 
     The requirement that a liquid possessing a high heat of vaporization be used for the quench is related to the need to rapidly cool the material down through the temperature range between the Curie temperature and that lower temperature, below which diffusion is so slow as to be insignificant (typically 100° C) so that there can be no preferential atomic ordering as the material cools. Water is particularly advantageous because of its high heat of vaporization and because it is otherwise easy to handle. Generally, liquids with at least half of the heat of vaporization of water are necessary in order to achieve the required rapid cooling rate in all but the smallest of devices. 
     EXAMPLES 
     The samples reported in Table I were produced by injecting a stream of molten metal of the desired composition into the contact area of two counterrotating cool rollers, from a fused silica tube with a 200 micrometer diameter opening. The liquid was forced from the tube by imposing a ˜ 1/2 atmosphere overpressure of Ar gas on the upper surface of the liquid. The apparatus was similar to the apparatus pictured in U.S. Pat. No. 3,732,349 issued May 8, l973 to Ho-Sou Chen et al. The rollers were 5 cm in diameter and rotating at a rate of 1000 revolutions per minute. The amorphous alloy was produced in the form of a tape 3 millimeters wide and approximately of 50 micrometers thick. 
     Metallic glass tapes approximately 25μm thick were produced by a spinning apparatus as described in Ho-Sou Chen et al, Material Research Bulletin, 11 (1976) 49 from two molten compositions. Composition I was (Co 0 .96 Fe 0 .04) 0 .75 P 0 .16 B 0 .06 Al 0 .03. Composition II was (Co 0 .74 Fe 0 .06 Ni 0 .2) 0 .75 P 0 .16 B 0 .06 Al 0 .03. Samples of both compositions were wound on bobbins, heat treated for approximately 10 minutes and quenched in water at room temperature. Composition I was heat treated at 700° K. Composition II was heat treated at 640° K. Table II shows the results of measurements of initial permeability of the two glass alloys both before and after heat treatment and the initial permeability of Supermalloy. The measurements were made at the indicated frequencies and magnetic fields. The Table indicates an improvement of initial permeability of, typically, more than a factor of four and results that approach or exceed those for Supermalloy. 
     
                                           TABLE II                                
__________________________________________________________________________
           Permeability                                                   
Magnetic   Alloy I   Alloy II                                             
Frequency                                                                 
      Field                                                               
           As   Rapid                                                     
                     As   Rapid                                           
(Hz)  (Gauss)                                                             
           Produced                                                       
                Cool Produced                                             
                          Cool  Supermalloy                               
__________________________________________________________________________
100   20   3.2 × 10.sup.3                                           
                15 × 10.sup.3                                       
                     2.8 × 10.sup.3                                 
                          12.5 × 10.sup.3                           
                                67.5 × 10.sup.3                     
100   100       19   6.6  23.4  72.0                                      
100   1000      68   20.8 89.3  120.0                                     
1000  20             3.0  12.7  63.0                                      
1000  100            5.8  18.8  65.0                                      
1000  1000           14.2 89.3  89.0                                      
10000 20             3.0  12.9  42.0                                      
10000 100            4.3  15.0  43.0                                      
10000 1000           --   --    45.0                                      
__________________________________________________________________________