Selective hydroformylation process
SUMMARY OF THE INVENTION 
     This invention relates to the use of novel hybrid platinum catalysts suitable for the catalytic hydroformylation of α-olefin substrates to predominantly linear, terminally substituted aldehydes. 
     More specifically, this invention concerns the use of certain novel platinum halide, Group IVA metal halide catalyst complexes bonded or anchored to nitrogen-containing organic or inorganic supports which are useful in the selective hydroformylation of linear α-olefin to predominantly linear aldehydes under moderate conditions of temperature and pressure. 
     Hydroformylation, as used throughout this disclosure and claims refers to the process of preparing aldehydic products from linear α-olefins through the addition of carbon monoxide and hydrogen to the carbon-to-carbon unsaturated bond of said olefin substrate, in accordance with stoichiometry of equation (1), set forth below: 
     
         RCH═CH.sub.2 + CO+ H.sub.2 → RCH.sub.2 --CH.sub.2 --CHO (1) 
    
     where R in this invention may be hydrogen or an alkyl, aryl, alkaryl, aralkyl or cycloalkyl group containing 1 to 28 carbon atoms. 
     BACKGROUND OF THE INVENTION 
     Over the past decade many highly active and selective catalysts for hydrocarbon reactions have been derived from transition-metal complexes. These homogeneous complex catalysts have several advantages over conventional heterogeneous catalysts in that the active centers are readily accessible and reactions involving their use characterized by a high degree of selectivity and reproducibility. However, the use of homogeneous catalysts on an industrial scale can lead to numerous practical problems, including corrosion, deposition of the catalyst on the reactor walls and recovery of the catalyst from reaction products. One way of overcoming these problems while retaining the advantages of the transition-metal complex catalyst is to attach the complex to the surface of a solid support. In particular, increased attention has been given recently to anchoring homogeneous transition metal catalysts to polymeric supports through the formation of one or more chemical bonds between the surface of the support and a ligand group involved in the metal complex. The transition-metal complexes may be attached to the surfaces of both organic and inorganic solids. Generally, these hybrid or &#34;heterogenized&#34; catalysts have certain intrinsic advantages over their homogeneous counterparts, particularly: (1) ease of separation from products, (2) enhanced size and positional selectivity, (3) ability to carry out sequential catalytic reactions and (4) ease of catalyst recycle. A number of research groups have, in recent years, demonstrated that a variety of transition-metal organometallic species possess excellent activity and selectivity for hydrogenation, isomerization and hydroformylation when bonded to macroreticular polymeric resins. However, olefinic hydroformylation stuties have, to our knowledge, been carried out only with polymer anchored cobalt* and rhodium** catalyst complexes. The normal/iso aldehyde ratio with these catalysts is typically 1/3-3/1, hydroformylation being accompanied by concurrent isomerization of the unreacted olefin and reduction to alkanes. 
    
    
     In the broadest contemplated practice of this invention, aldehydes are produced from α-olefins substrates by the catalytically directed addition of hydrogen and carbon monoxide to said α-olefins in the presence of a catalytic quantity of a supported hydroformylation catalyst consisting of one or more platinum halides, in combination with one or more Group IVA metal halides (such as tin and germanium halides) bonded to nitrogen containing organic and or inorganic supports to form a reaction mixture, and heating the pressurized reaction mixture until substantial amounts of the desired aldehydes are produced. 
     In a narrower practice of this invention, aldehydic products containing from 3 to 31 carbon atoms are prepared by the catalytic addition of carbon monoxide and hydrogen to an α-olefin substrate containing from 2 to 30 carbon atoms by a process of: 
     (a) Admixing each mole of said α-olefin to be hydroformylated, in a deoxygenated reaction medium with at least a catalytic quantity of a supported hydroformylation catalyst consisting of one or more platinum halides, bonded to or anchored to one or more nitrogen containing organic and inorganic supports, to form a reaction mixture. 
     (b) Pressurizing said reaction mixture with at least sufficient carbon monoxide and hydrogen to satisfy the stoichiometry of the hydroformylation reaction described supra (Eq. 1); 
     (c) Heating said pressurized reaction mixture to temperatures of from about 20° to 130° C. until substantial formation of the predominantly linear alkyl aldehyde product is formed, and 
     (d) Isolating said aldehyde products contained therein. 
     In a yet narrower embodiment of this invention, aldehydic products containing 3 to 31 carbon atoms are prepared by the catalytic addition of hydrogen and carbon monoxide to an alpha-olefin substrate containing 2 to 30 carbon atoms by the following steps: 
     (a) Mixing the catalyst, comprising an insoluble, macroreticular nitrogen-containing organic polymer or silica supported, amine-stabilized platinum-tin halide complex, containing a tin to platinum atomic ratio of 0.5 to 30:1, in a deoxygenated inert solvent and pretreating with carbon monoxide at 250 to 4000 psig for 15 to 90 minutes at temperatures of 20° to 90° centigrade, to form a pretreated reaction mixture. 
     (b) Dispersing the alpha-olefin, in the ratio of one mole per 0.001 to 0.1 mole of platinum catalyst used, then pressurizing to at least 250 psig with carbon monoxide and additional sufficient hydrogen to satisfy the stoichiometry of the hydroformylation reaction referred to above (Eq. 1), to form a pretreated reaction mixture. 
     (c) Heating said pressurized reaction mixture to temperatures of 20° to 130° centigrade until substantial formation of the aldehydic product is achieved, and 
     (d) Isolating said aldehydic products contained therein. 
     In order to further aid in the understanding of this invention, the following additional disclosure is submitted: 
     A. Process Sequence and Variations 
     In general, the components of the hydroformylation reaction mixture, including optional inert solvent, olefin and catalyst may be added in any sequence as long as good agitation is employed to provide a good dispersion of the heterogeneous reaction mixture. For example, the following represent some variations insofar as the addition of catalyst components, inert solvents and olefin addition that may be made without departing from the inventive process. These modifications include: 
     (1) The catalyst may be preformed and added preformed to the reactor prior to the addition of the olefin and other inert solvent components. 
     (2) Preferably, to maximize the specific activity of said platinum catalyst, the catalyst is suspended in an inert solvent, under an inert atmosphere, prior to addition of the α-olefin substrate and the other components of the hydroformylation reaction mix. 
     (3) To minimize induction periods and to further maximize the specific activity of the supported platinum halide, tin(II) halide catalyst, a particularly preferred modification is that the suspension of said catalyst in an inert solvent is pretreated with superatmospheric pressures of carbon monoxide prior to the addition of the α-olefin substrate, and the other components of the hydroformylation reaction mix. 
     B. Supported Platinum Halide, Group IVA Metal Halide Catalyst 
     The catalysts of this invention consist essentially of platinum-tin halides complexed or anchored to five types of nitrogen-containing supports shown below: 
     (a) Polyvinylpyridine homopolymers derived from 4-vinylpyridine and 2-vinylpyridine 
     (b) Vinylpyridine polymers crosslinked with divinylbenzene 
     (c) Vinylpyridine-styrene-divinylbenzene terpolymers 
     (d) Styrne based polymers having appended tertiary amine groups 
     (e) Silica supports having chemically bonded to them organic nitrogen groups. 
     The supported platinum halide, Group IVA metal halide catalysts of this invention may be prepared by a number of methods. One convenient mode of preparation is to suspend the nitrogen-containing polymer or silica support in a suitable inert organic solvent or solvents used alone or with water. Illustrative of water-organic solvent mixtures are water-alkanol solutions. The procedure generally followed is to stir the polymer of silica support, the solvent or solvent mixture, Group IVA and platinum salt until the platinum is anchored to the polymer, or silica support. The platinum anchored-support or polymer is filtered and washed to resuspend said platinum support in a suitable inert solvent with the Group IVA halide salt. 
     Illustrative of suitable Group IVA metal halides which may be utilized in combination with a platinum halide to form an active hydroformylation catalyst are: tin(II) chloride, tin(II) bromide, tin(II) iodide, tin(IV) chloride and germanium(II) chloride. A preferred class of Group IVA metal halides to be used in the hydroformylation process of this invention are tin(II) halides selected from the group consisting of tin(II) chloride, tin(IV) chloride and tin(II) bromide. 
     The class of platinum halides which are utilizable in the presence of a Group IVA metal halide to form an active hydroformylation catalyst include platinum(II) bromide, potassium tetrachloroplatinate(II), potassium hexachloroplatinate(IV) and chloroplatinic acid. 
     The transition-metal catalysts of this invention are employed for the hydroformylation process when bonded to suitable macroreticular organic polymers are support. Illustrative of suitable organic polymer supports for this class of catalyst include poly-2-vinylpyridine, poly-4-vinylpyridine, 2-vinylpyridine-divinylbenzene copolymer, 4-vinylpyridine-divinylbenzene copolymer and vinylpyridine-styrene-divinylbenzene terpolymers. Also included are polystyrenes, styrene-divinylbenzene copolymers, polyethylenes, polypropylenes and styrene-butadiene polymers having attached or appended organic amine groups. The amine groups appended to the oganic polymeric supports useful in this invention may be directly bonded to the carbon chain of the polymer or they may be attached through a methylene group or groups. Furthermore, said appended amine may also possess alkyl radicals containing 1 to 12 carbon atoms or a cycloalkyl radical of 4 to 7 carbon atoms. A particularly preferred class of catalyst support consists of styrene-divinylbenzene copolymers with appended dimethylaminomethyl or pyrrolinylmethyl groups. A typical synthesis of such a support is illustrated in Example 8, below. 
     The transition metal catalysts of this invention are also employed for hydroformylation when bonded to silica which has organic amine containing groups chemically attached to it. Illustrative of suitable organic amines which can chemically be attached to dehydrated silica are hydroxypyridine, 2- and 4-methylolpyridine, beta-pyridinethanol, N,N-dimethylaminoethanol and dimethylaminomethylphenol. A particularly preferred catalyst support consists of 4-hydroxypyridine chemically attached to dehydrated silica through the formation of a pyridinoxy-silicon bond. Synthesis of such a transition metal complex of 4-hydroxypyridine bonded to silica is shown in Example 12, below. Other organic amines which can be chemically bonded to dry silica are those which also possess the trimethoxysilane moiety. Illustrative of this type amine are dimethylaminopropyltrimethoxysilane, 3-(2-aminoethylaminopropyl)trimethoxysilane and 3-(4-pyridinyl)propyltrimethoxysilane. A typical synthesis of such a support is illustrated in Example 13, below. 
     Still another type of nitrogen containing silica support can be obtained by copolymerizing mixtures of vinylpyridines and vinyltriacetoxysilane and reacting the resultant copolymer with silica. A typical synthesis of such an amine-polymer coated silica is illustrated in Example 11. 
     C. Ratio of Stannous Chloride to Polymer-Ligand Stabilized Platinum Chloride in Supported Catalysts 
     While any molar ratio greater than 0.1 mole of stannous chloride per mole of ligand-stabilized platinum chloride will produce active catalysts, the experimental work performed indicates that at least one mole of stannous chloride for each mole of platinum chloride is required for good catalyst activity, reproducibility and stability. The preferred ratio is from one to 2.5 moles of stannous chloride per mole of platinum chloride. Less than a 1:1 Sn/Pt ratio leads to poorer catalyst reproducibility and catalyst deactivation. Mole ratios appreciably greater than 2.5 to 1 of tin and platinum generally produce less active catalysts. Within the range of 1:1 to 2.5:1 Sn/Pt ratios, only moderate differences in catalyst activity and stability were observed. This preferred ratio is based upon the hydroformylation of hexene-1. 
     D. Ratio of Supported, Ligand Stabilized Platinum Catalyst to Olefin Substrate 
     The quantity of catalyst employed in this process is normally not critical and a wide range of concentrations may be employed. In general, the process is desirably conducted in the presence of catalytically effective quantities of active platinum halide-Group IVA metal halide catalysts which yield the desired aldehydic product. 
     Molar ratios of 100 to 1500 moles of olefin per mole of platinum complex can be employed where alpha olefins such as hexene-1 are used as the substrate. Much lower ratios are not harmful but are economically unattractive. The favored mole ratio used for the examples in Tables I through IV were 200 to 500 moles of olefin per gram atom of platinum in the polymer or supported complex. 
     E. Olefins as Substrates 
     Alpha olefins ranging in carbon content from 2 to 30 carbon atoms can be employed as substrates for the hydroformylation reactions. Illustrative alpha olefins would be propene-1, butene-1, pentene-1, hexene-1, octene-1, nonene-1, decene-1, undecene-1, dodecene-1 as well as their higher homologues. Illustrative branched chain alpha olefins would be 4-methylpentene-1 and 3-methylpentene-1. 
     The olefins can be used as single discrete compounds, in the form of mixtures of olefins, with or without large quantities of saturated hydrocarbons. 
     F. Inert Solvent 
     The hydroformylation may be run in the presence of an inert diluent when operating in batch processes. Solvents such as methylisobutylketone, benzene, toluene, tetrahydrofuran, dimethoxyethane, and paraffins such as hexane, isooctane and cyclohexane. Highly polar solvents are not required but good solvents for the product aldehydes are best used. 
     G. Temperature Required for Hydroformulation 
     The temperature range which can be employed for the hydroformylation will depend upon the olefin employed, the total pressure, the mole ratio of hydrogen to carbon monoxide used, the concentration of reactants and the amount of catalyst and choice of support used for the platinum catalyst. Using hexane-1 as a typical alpha olefin and a 4-vinylpyridine-divinylbenzene copolymer as a ligand-support for a 2:1 mole ratio complex of tin/platinum chlorides, an operating temperature range is from 25° to 130° C. when using H 2  /CO mixtures having CO partial pressures of 250 psig or greater. Below 250 psig partial pressures of CO, the catalytically active platinum-tin complex deactivates and at temperatures above 130° C., decomposition of the polymeric support can occur. A preferred temperature range is 70° to 120° C. when the aforementioned olefin is hydroformylated at 1500 to 3500 psig of CO and H 2  using the catalyst system also described above. 
     H. Pressures Required for Hydroformylation 
     The pressures which can be employed for hydroformylation are variable and are dependent on the factors mentioned above. Using hexene-1 as a representative olefin and again, a 4-vinylpyridine-divinylbenzene copolymer as a ligand support for a 2:1 and 1:1 molar tin/platinum chlorides complex, an operable pressure range is from 500 to 4000 psig when a 1:1 mole ratio of H 2  to CO and temperatures of 25° to 130° C. are employed. Pressures of 1500 psig or greater are preferred when operating within the preferred temperature range of 70° to 120° C. in order to reduce reaction times. 
     I. Hydrogen to Carbon Monoxide Ratio 
     The H 2  /CO mole ratio may be varied over a range of from 10/1 to 1/10 when suitable temperatures and total pressures are employed. A preferred narrower range is from 2/1 to 1/2 of hydrogen and carbon monoxide. The effect of differing ratios on yields and selectivities to aldehydic products is shown in Examples 15 and 42 to 48 in Table IV. 
     J. Effect of Hydroformylation Conditions 
     As shown by Examples 39-41 in Table IV, reducing the total gas pressure from 3400 to 1700 psig (1:1 CO/H 2 ) occasioned a diminution in conversion and yields over an eighteen hour period but selectivity to linear heptaldehyde rose to 68 percent. In Example 45, operating at 120° C. and 2000 psig total pressure (2:1 H 2  /CO), the hydroformylation rate was faster than Example 40 and selectivity to linear heptaldehyde was higher still. Reversing the hydrogen to carbon monoxide ratio to 1:2.5 slowed the rate of hydroformylation as shown in Examples 46 and 47, Table IV but again increased the selectivity to linear aldehyde. We conclude that generally slower hydroformylation rates associated with lower total pressures and particularly lower hydrogen partial pressures favor increased product linearity. The predominent side reactions were found to be hexene-1 isomerization to hexenes-2,3 and reduction to n-hexane. 
     K. Reaction Times Required 
     As previously indicated in the discussions of temperatures, pressures and effects of reaction conditions on the hydroformylation reaction, experimental variables are important in arriving at reaction times. Generally, substantial conversions (50% or higher) of the olefin to aldehyde can be accomplished within eight hours when operating at or above 90° C. and at or above 2000 psig total pressure and 1000 psig partial pressure of hydrogen and using a catalyst having a Sn/Pt atomic ratio between 1:1 and 2.5:1. Frequently, at 3000 to 3500 psig of 1:1 CO and H 2 , the hydroformylation was more than 95% complete within 150 minutes of reaching the reaction temperature of 90° C. 
     L. Catalyst Recycle 
     Empirically selected catalysts with platinum-tin chloride complexes anchored to different classes of nitrogen containing supports are active for hydroformylation upon recycle one or more times with fresh hexene-1 charge. Evidental recycle capability of selected catalysts are found in Tables II and IV. Samples of active catalysts derived from vinylpyridine polymers, having 1:1 to 2:1  tin to platinum atomic ratios were recovered and reused repeatedly for hexene-1 hydroformylation with no evident loss in activity, heptaldehyde yields remaining 85-98% when hydroformylation conditions were held at 90° C. and about 3000 psig of 1:1 CO and H 2 . A platinum-tin chloride complex anchored to silica silylized by reaction with 3-(2-aminoethyl)aminopropyltrimethoxysilane also showed continued activity upon recycle (Examples 25-28, Table II). This property is very desirable in a commercial process, reducing the frequency of catalyst regeneration and lowering operating costs. 
     M. By-Products 
     As far as can be determined, without limiting the invention thereby, hydroformylation of olefins, catalyzed by the supported ligand-stabilized platinum-tin chloride complexes, leads to the formation of only three minor classes of by-products. These are isomerized olefins, hydrogenated olefins and high boiling materials formed via condensation reactions of the initially produced aldehydes. 
     N. Identification Procedures 
     Where applicable, the aldehydic products of this invention are identified by one or more of the following analytical procedures - gas chromatography (gc) infrared, elemental and nuclear magnetic resonance analyses. Unless otherwise specified all percentages are by mole rather than weight or volume, and all temperatures are in centrigrade rather than fahrenheit. 
     O. Conversion 
     As defined herein, conversion is the efficiency in transforming the α-olefin substrate to non α-olefinic products. Conversion is expressed in mole percent, and is calculated by dividing the amount of α-olefin substrate consumed during hydroformylation by the amount of α-olefin originally charged, and multiplying the quotient by 100. 
     P. Selectivity 
     Selectivity as defined herein, represents the efficiency in catalyzing the desired hydroformylation reaction relative to other undesired reactions or lack of reaction. In this instance hydroformylation to paraffinic aldehyde is the desired conversion. Selectivity is expressed as a percentile, and is calculated by determining the amount of paraffinic aldehyde product formed, divided by the amount of olefin converted and multiplying the quotient obtained by 100. 
     Q. Product Linearity 
     Product linearity, as defined herein, is the efficiency in catalyzing the desired hydroformylation relative to other undesired hydroformylation reactions. When α-olefins are to be hydroformylated, hydroformylation to the linear paraffinic aldehyde is the desired conversion. Linearity is expressed as a percentile, and is calculated by determining the amount of linear aldehyde product formed, divided by the total amount of aldehyde products formed and multiplying the quotient obtained by 100. 
     Having described the inventive process in general terms, the following examples are submitted to supply specific and illustrative embodiments. 
    
    
     EXAMPLES 1 to 9 
     Preparation of Nitrogen Containing Polymeric Supports and Ligand-Stabilized Platinum-Tin Chloride Complexes 
     EXAMPLE 1. 4-Vinylpyridine-divinylbenzene copolymer 
     4-Vinylpyridine (98 grams), dinvinylbenzene (4 grams), 600 ml of water and 0.2 grams of Natrasol 250H were charged to a one-liter stainless steel autoclave reactor. Azobisisobutyronitrile (0.5 grams) was added, the reactor sealed and flushed with nitrogen and heated to 80° C. at 2500 RPM stirring. After three hours the reactor was cooled to 30° C., an additional 0.5 grams of the butyronitrile added and the reactor heated to 80° C. with stirring for another 20 hours. 
     The reactor was cooled and the contents removed by water washing. The white solids were then washed with methanol and water and dried over solid KOH. Obtained 91 grams (82% yield) of copolymer calculated 6% crosslinked. 
     Example 2. 4-Vinylpyridine-styrene-divinylbenzene terpolymer 
     Styrene (73 grams), 4-vinylpyridine (24 grams), 600 ml of water, divinylbenzene (4 grams), Natrasol 250H and azobisisobutyronitrile reacted as in Example 1. Obtained 88 grams of fine white solids, 3.3% nitrogen. 
     Example 3. 2-Vinylpyridine-styrene-divinylbenzene terpolymer 
     Styrene (73 grams), 2-vinylpyridine (24 grams), dinvinylbenzene (4 grams), Natrasol 250H (0.3 grams) and 600 ml of water were reacted as in Example 1. There were obtained 90 grams of white solids containing 3.4% nitrogen. 
     Example 4. 2-Vinylpyridine-styrene-dinvinylbenzene terpolymer 
     Styrene (40 grams), 2-vinylpyridine (40 grams), dinvinylbenzene (1.6 grams), Natrasol 250H (0.3 grams) and azobisisobutyronitrile in 600 ml of water were reacted as described previously. There were obtained 67 grams of terpolymer containing 6.7 % nitrogen. 
     Example 5.2 -Vinylpyridine-dinvinylbenzene copolymer 
     2-Vinylpyridine (50 grams), divinylbenzene (2 grams), water (350 ml), Natrasol 250HH (0.1 gram) and azobisisobutyronitrile were reacted at 80° C. for 6 hours. The mixture was cooled and filtered and 39 grams of white polymer were obtained. After drying over solid KOH elemental analysis showed it contained 10.7% nitrogen. 
     EXAMPLE 6. Poly-4-vinylpyridine 
     4-Vinylpyridine (49 grams) and benzoylperoxide (0.5 grams) were refluxed in 300 ml of benzene solution with rapid stirring. The solid polymer which formed was collected and washed repeatedly with benzene and finally dissolved in methanol. The methanol was evaporated leaving 40 grams of a hard, brittle polymer which remained methanol soluble. 
     Example 7. Chloromethylation of a styrene-divinylbenzene copolymer 
     Gaseous hydrogen chloride was rapidly passed into a stirred mixture of 300 grams of paraformaldehyde and 350 ml of methanol maintained at 0°-5° C. When all the paraformaldehyde had dissolved, the product was separated from the lower methanol layer, dried over CaCl 2  and distilled. Refractionation afforded 210 grams of chloromethyl ether, b.p. 58°-60° C. 
     Styrene-(2%) divinylbenzene copolymer (25 grams, 20-200 mesh) was dispersed in 150 ml of the above chloromethyl ether and allowed to swell at ambient temperature. After the cautious addition of stannic chloride (8 grams) the mixture was refluxed one hour and the polymer removed by filtration, washed with aqueous dioxane containig 10% (V/V) of concentrated hydrochloric acid and repeatedly with methanol. Upon drying there was obtained 36 grams of polymer containing 19% chlorine. 
     Example 8. Preparation of a styrene-divinylbenzene coplymer having appended pyrrolinylmethyl groups. 
     A sample of the above product (20 grams, Example 7) was dispersed in diethyl ether containing 30 grams of pyrrolidone and the mixture stirred three days at ambient conditions. The polymer was then separated by filtration, washed repeated with methanol and dried. The product consisted of 23 grams of a free-flowing material containig 6.2% nitrogen. 
     EXAMPLES 9-13 
     Preparation of Platinum-Tin Complexes of Nitrogen Containing Polymers 
     Example 9. Polymer Complexes Obtained using Chloroplatinic Acid 
     A sample of 4-vinylpyridine-divinylbenzene copolymer (2.0 rams) was dispersed in 50 ml of water and allowed to soak two hours whereupon chloropatinic acid (H 2  PtCl 6 , 0.1 gram) was added and the mixture stirred 6-18 hours by which time all the yellow color of the platinic acid had been absorbed by the polymer. The mixture was filtered and the solids dried. 
     The resin containing the absorbed platinum was soaked two hours in dry tetrahydrofuran, 0.2 grams of anhhydrous SnCl 2  were added and the mixture stirred overnight. After filtering, the yellow to yellow-orange solids to 2.08 grams (4.0% Pt, 2.6% Sn, Sn/Pt 1). 
     Variations of the above procedures used 1 and 2 grams of polymer, 0.1 to 0.4 grams of SnCl 2  or 0.12 to 0.24 grams of SnCl 2 .H 2  O per 0.1 gram of chloroplatinic acid. 
     Poly-4-vinylpyridine, in water-methanol solutions, was also reacted with H 2  PtCl 6  to form the insoluble platinum salts which were subsequently reacted with stannous chloride as illustrated above. 
     As an example, 1.0 gram of poly-4-vinylpyridine gave 1.3 grams of resinous product containing 5.9% Pt and 5.8% Sn, Sn/Pt 1.6. 
     EXAMPLE 10. Polymer Complexes Obtained using Potassium Tetrachloroplatinite. 
     A 2.0 gram sample of a 4-vinylpyridine-dinvinylbenzene copolymer was stirred overnight in 75 ml of water containing 0.21 gram of K 2  PtCl 4 . The pale yellow solids were collected, dried and again dispersed in 35 ml of tetrahydrofuran containing 0.22 grams of SnCl 2 . 
     Example 11. Preparation of a Vinylpyridine Ligand Attached to Silica 
     Vinyltriacetoxysilane (4.5 grams) and 4-vinylpyridine (19.7 grams) in 200 ml of benzene was treated with 0.2 gram of benzoyl peroxide and the solution heated under nitrogen to 80° C. with rapid stirring. After 35 minutes an additional 0.3 gram of peroxide was added and heating continued for 90 minutes by which time some gummy polymer began to form on the flask walls. 
     Silica (20 grams, 240 mesh), wet with 1 ml of water was added to the above mixture and the reaction continued for an additional 3 hours. Xylene (200 ml) was then added to the stirred mixture and the benzene distilled off until a head temperature of 120° C. was reached. 
     After a further 5-hour reflux the mixture was filtered, the gummy solids collected and continuously extracted with methanol for 24 hours. The solids were removed and dried over KOH, to give 16.2 grams of solid containing 2.2% nitrogen. 
     Platinum-tin chloride complexes of the above support were prepared by the procedure outlined in Example 10, above. 
     Example 12. Preparation of a Platinum-Tin Chloride Complex of 4-Hydroxypyridine Sorbed on Silica 
     4-Hydroxypyridine (0.7 gram) dissolved in 50 ml of methanol was reacted with 0.1 gram of chloroplatinic acid. Silica (10 grams, 240 mesh) and 125 ml of xylene and the thick mixture rapidly stirred and heated. As the methanol distilled off, an additional 500 ml of xylene were slowly introduced, then removed by slow distillation. The semi-solid residue was then stripped to dryness at 100° C. and 15-20 mm of pressure. 
     The dry residue (10.2 grams) was added to a solution of 0.20 gram of stannous chloride in 130 ml of tetrahydrofuran, the mixture stirred overnight and the solids recovered by filtration. Obtained were 10.1 grams of catalyst containing 0.66% platinum, 0.95% tin and having a Pt/Sn of 2.36. 
     EXAMPLE 13 
     Preparation of a Platinum-Tin Complex of a Silylized Silica 
     Xylene (150 ml) containing silica (5 grams, 240 mesh) was refluxed for 30 minutes with provision for water take-off. 3(2-Aminoethylaminopropyl)trimethoxysilane was then added and the reflux continued for 3 more hours followed by slow distillative removal of most of the xylene. The residue was filtered, washed with benzene and after drying the solids were stirred overnight in a methanolic solution of chloroplatinic acid (0.1 gram). The platinum impregnated silica was separated, washed repeatedly with methanol and dried. It was then dispersed and stirred in tetrahydrofuran containing stannous chloride (0.2 gram) for 12 hours, separated by filtration, washed repeatedly with tetrahydrofuran and dried in vacuo. The dried catalyst amounted to 6.59 grams and contained 1.27% platinum and 0.81% tin (Sn/Pt molecular ratio 1.05). 
     EXAMPLES 14-52 
     Platinum Catalyst Evaluation 
     Hydroformylation studies were carried out in a one-liter Hastelloy autoclave equipped with a magnadrive stirrer, sampling valve and a H 2  CO/N 2  gas supply. The reactor contained water cooling-steam coils and an electric heate with automatic controls to permit rapid heating and cooling as well as constant temperatures during runs. Stirring rates of 700 rpm were usually employed. 
     Platinum-tin catalyst (ca. 2 gm, containing 0.13-0.38 mg Pt) dispersed in solvent, usually benzene (ca. 200 ml) was pretreated for 45-60 minutes with CO at 250-3000 psig, the pressure released and hexen-1 (100 mmoles) and the CO and H 2  mixture charged to the desired pressure. The mixture was brought to temperature and maintaind at temperature with stirring for periods of 2 to 18 hours. Small (0.5 ml) samples were usually withdrawn at regular intervals and the extent of hydroformylation determined by GLC using a 10-ft. 1/4-inch column of 7% loaded SE-30 on Chromasorb &#34;G&#34; or alternatively a 150-ft. 0.01-inch capillary column. Product identification was by IR, NMR and by comparison with authentic samples. After reaction, the autocalve was cooled, disassembled and the product aldehydes isolated by distillation in vacuo. 
     Recovered platinum catalyst in solvent (200 ml) was recycled to the autoclave reactor with fresh hexene (100 mmole) annd hydroformylation to heptaldehydes carried out as described above. 
     Platinum catalysts recovered from hydroformylation reactions were found to be relatively stable at ambient conditions and could be stored for dys in closed vessels without special precautions. Upon reuse, including pretreatment with superatmospheric pressure of CO as described above, no change or loss in catalyst activity was observed. 
     
                                           Table I                                 
__________________________________________________________________________
Hexane-1 Hydroformylation using Supported Platinum-Tin Chlorides          
Catalysts                                                                 
                        mg      Mole percent                              
                        atom                %    Isomerization            
                        Pt Sn/Pt                                          
                                Hexene-1                                  
                                      Aldehyde                            
                                            Product                       
                                                 to     Reduction         
Example                                                                   
      Catalyst composition                                                
                        used                                              
                           ratio                                          
                                conversion                                
                                      Selectivity                         
                                            Linearity                     
                                                 2,3-hexenes              
                                                        to                
__________________________________________________________________________
                                                        hexane            
14    4-VP-(6%)DVB copolymer,                                             
                        0.51                                              
                           1.1  &gt;99.8 90    54   Trace  4.6               
       Pt-tin chlorides complex                                           
15    4-VP-(6%)DVB copolymer                                              
                        0.43                                              
                           2    99    98    55   --     1                 
       Pt-Sn chlorides complex                                            
16    4-VP-(10%)DVB copolymer,                                            
                        0.07                                              
                           1.4  86.5  74.2  61   ND     ND                
       Pt-ton chlorides complex                                           
17    4-VP-(13%)DVB copolymer,                                            
                        0.05                                              
                           0.4  5     20    63   --     Trace             
       Pt-tin chlorides complex                                           
18    4-VP-(6%)DVB copolymer                                              
                        0.46                                              
                           Zero 1     None  --   --     &lt;1                
       containing platinum                                                
       chloride but no tin                                                
19    Poly-4-vinylpyridine,                                               
                        0.39                                              
                           1.6  100   97.9  54   --     2.1               
       Pt-tin chloride complex                                            
20    2-VP-(8%)DVB copolymer,                                             
                        0.45                                              
                           1.9  52.4  78.8  68   --     &lt;1                
       Pt-tin chlorides complex                                           
21    2-VP-styrene(1:3 ratio)-DVB                                         
                        0.35                                              
                           2    53.5  98    60   ND     ND                
       terpolymer, Pt-tin chlorides                                       
22    Styrene-(2%)DVB copolymer                                           
                        0.48                                              
                           2    30    4.3   60   ND     ND                
       with appended CH.sub.2 NC.sub.4 H.sub.8 groups,                    
       Pt-tin chlorides complex                                           
__________________________________________________________________________
 All reactions conducted in a stirred Hastelloy reactor using 100 mmoles  
 hexene-1 in 200 ml of benzene. Reaction conducted at 90° C. and   
 3000-3300 psig of 1:1 CO and H.sub.2 for 8 hours. 4-VP is 4-vinylpyridine
 2-VP is 2-vinylpyridine, DVB is mixed divinylbenzene, ND is not          
 determined.                                                              
 
    
     
                                           Table II                                
__________________________________________________________________________
Hexene-1-Hydroformylation with Silica Supported Platinum-Tin Chloride     
Catalysts.sup.1                                                           
                    mg                                                    
Ex-                 atom    Reaction   Aldehyde  Isomerization            
am-                 Pt  Sn/Pt                                             
                            time Hexene-1                                 
                                       Selec-                             
                                            Product                       
                                                 to      Reduction        
ple                                                                       
   Catalyst composition                                                   
                    used                                                  
                        ratio                                             
                            (hrs)                                         
                                 conversion                               
                                       tivity                             
                                            linearity                     
                                                 2,3-hexenes              
                                                         to               
__________________________________________________________________________
                                                         hexane           
23 Pt-tin chloride complex of                                             
                    0.49                                                  
                        2   16   100   80   61   1       12               
    4-hydroxypyridine on silica                                           
24 Pt-tin chloride complex of                                             
                    0.27                                                  
                        0.6 16    5    12   56   Undetermined             
                                                         2                
    4-vinylpyridine-triacetoxy-                                           
    vinyl silane copolymer                                                
    reacted with silica                                                   
25 Pt-tin chloride complex of                                             
                    0.425                                                 
                        2   8    100   87.4.sup.a                         
                                            55   Undetermined             
                                                         2.4              
    3-(2-aminoethyl)amino-                                                
    propyl-trimethoxysilane                                               
    silylized silica                                                      
26 Recycled 25      0.37    6    100   97   56   Trace   Trace            
27 Recycled 26.sup.b                                                      
                    0.30    8    26    96   57   1       Trace            
28 Recycle3d 27     0.18    8    70    87   62   22                       
__________________________________________________________________________
 .sup.1 Reactions conducted in a stirred Hastelloy reactor using 100 mmole
 of hexene-1 in 200 ml of benzene. Operating conditions were 3000-3300 psi
 of 1:1 CO and H.sub.2 at 90° C.                                   
 .sup.a 0.5% heptanols also formed                                        
 .sup.b Conducted at 70° C., 3200 psig of 1:1 CO and H.sub.2.      
 
    
     
                                           Table III                               
__________________________________________________________________________
Hexene-1 Hydroformylation using Polymer Supported Platinum-Tin Chloride   
Catalysts                                                                 
                Reaction         %    Isomerization                       
       mg. atom                                                           
            Sn/Pt                                                         
                time Hexene-1                                             
                           Aldehyde                                       
                                 Product                                  
                                      to     Reduction                    
Example.sup.1,2                                                           
       Pt used.sup.3                                                      
            ratio                                                         
                (hrs)                                                     
                     conversion                                           
                           Selectivity                                    
                                 linearity                                
                                      2,3-hexenes                         
                                             to hexane                    
__________________________________________________________________________
29 (a) 0.62 0.6 18   10    43    62   10     40                           
30 (a) 0.43 1.05                                                          
                18   &gt;99.8 86.2  59   Trace  2.5                          
14 (a) 0.51 1.1 18   &gt;99.8 90    54   Trace  4.6                          
15 (a) 0.43 2.0 18   99    97    55   --     1.0                          
31 (a) 0.37 3.0 18   42.5  86.1  62   14     Trace                        
32 (b) 0.49 0.6 8    64    67.1  61   4.5    3.3                          
33 (b) 0.43 1.0 8    8.6   59.3  59   23     Trace                        
34 (a) 0.40 1.0 8    &gt;99.8 98    55   Trace   1                           
(Recycle 27)                                                              
35 (b) 0.46 2.1 8    &gt;99.8 96.6  55   Trace  2.8                          
36 (b) 0.43 2.8 8    38    78.9  61          Trace                        
37 (b) 0.35 4.8 8    12    91.7  60          Trace                        
__________________________________________________________________________
 .sup.1 Catalysts were Pt-tin chloride complexes anchored to a            
 4-vinylpyridine-(6%)divinylbenzene copolymer.                            
 .sup.2 All reactions run in a stirred autoclave at 90° C. and     
 3100-3500 psig of 1:1 CO and H.sub.2.                                    
 .sup.3 Based upon analysis of fresh catalyst and quantity of resin used. 
 (a)Catalyst pretreated with CO at 3000 psig at ambient temperatures,     
 pressure released then repressurized with CO and H.sub.2.                
 (b)Catalyst pretreated with 250 psig of CO at 90° C., then        
 pressured with CO/H.sub.2 mixture.                                       
 
    
     
                                           Table IV                                
__________________________________________________________________________
Hexene-1 Hydroformylation using Supported Platinum-Tin Chlorides          
Catalysts.sup.1                                                           
                                      Mole percent                        
                 mg.                                                      
Ex-              atom Pres-      Reaction                                 
                                      Hexene-1                            
                                           Se-                            
                                              %    Isomeri-               
am-              Pt   sure,                                               
                         H.sub.2 /CO                                      
                             Temp,                                        
                                 time conver-                             
                                           lec-                           
                                              Product                     
                                                   zation                 
                                                         Reduction        
ple                                                                       
   Catalyst composition                                                   
                 used.sup.3                                               
                      psig                                                
                         ratio                                            
                             ° C.                                  
                                 (hrs)                                    
                                      sion tivity                         
                                              Linearity                   
                                                   2,3 hexenes            
                                                         to               
__________________________________________________________________________
                                                         hexane           
14 4-VP-(6%)DVB copolymer,.sup.2                                          
                 0.51 3100                                                
                         1   90  18   &gt;99.8                               
                                           90 54   1     4.5              
   Pt-tin chlorides complex                                               
   Sn/Pt ratio: 1.1                                                       
38 Recovered from Example 14                                              
                 0.5  3400                                                
                         1   90  18   98   79.5                           
                                              56   7     10               
39 Recovered from 32                                                      
                 &lt;0.5 3300                                                
                         1   90  18   100  94 54   1     --               
40 Recovered from 33                                                      
                 &lt;0.45                                                    
                      1700                                                
                         1   90  18   12   94.1                           
                                              68   &lt;0.5  --               
41 Recovered from 34                                                      
                 0.42 3000                                                
                         1   90  18   100  92.7                           
                                              55   1     4                
15 4-VP-(6%)DVB copolymer,.sup.2                                          
                 0.43 3100                                                
                         1   90  18   100  97 55   Trace 1                
   Pt-tin chlorides complex,                                              
   Sn/Pt ratio: 2.0                                                       
42 Recovered from Example 15                                              
                 0.41 3100                                                
                         1   90  8    100  93 57   1.5   5                
43 Recovered from 36                                                      
                 0.33 3100                                                
                         1   90  8    20   5  36   ND    ND               
44 Recovered from 37                                                      
                 0.30 3000                                                
                         1   89  8    100  85.7                           
                                              55   Trace 2.9              
45 Recovered from 38                                                      
                 0.26 2000                                                
                         2   120 8    93   34.4                           
                                              71   15.6  42.2             
46 Recovered from 39                                                      
                 0.20 3300                                                
                         1   90  4    100  98 55   Trace 1.8              
47 Recovered from 40                                                      
                 0.195                                                    
                      3500                                                
                         0.4 90  9    75   94.6                           
                                              62   ND    ND               
48 Recovered from 41                                                      
                 0.175                                                    
                      3400                                                
                         1   90  1.25 100  98 55   Trace 1.9              
30 4-VP-(6%)DVB copolymer,.sup.2                                          
                 0.43 3100                                                
                         1   90  20   100  86.1                           
                                              59   Trace 2.5              
   Pt-tin chlorides complex,                                              
   Sn/Pt ratio: 1.05                                                      
49 Recovered from Example 24                                              
                 0.41 3000                                                
                         1   91  4.25 100  97 55   Trace 2.7              
50 Recovered from 43                                                      
                 0.33 3200                                                
                         1   89  4.3  100  97 55   Trace 2.0              
51 Recovered from 44.sup.4                                                
                 0.30 3300                                                
                         1   90  8    4    75 --   --    Trace            
19 Poly-4-vinylpyridine,                                                  
                 0.39 3200                                                
                         1   91  8    100  97.9                           
                                              54   --    2.1              
   Pt-tin chlorides complex,                                              
   Sn/Pt ratio: 1.6                                                       
52 Recovered from Example 19                                              
                 0.34 3200                                                
                         1   90  4.1  100  98 54   Trace 1.8              
__________________________________________________________________________
 .sup.1 Reactions conducted in a stirred Hastelloy autoclave, 100 mmoles  
 hexene-1 in 200 ml of benzene. Example 32 used 200 mmoles hexene-1.      
 Catalysts pretreated with CO at 3000 psig, excpet in Example 37 wherein  
 the recovered catalyst from Example 36 was heated to 90° C. under 
 50 psig of CO immediately prior to use.                                  
 .sup.2 4-VP is 4-vinylpyridine, DVB is divinylbenzene, ND means not      
 determined.                                                              
 .sup.3 Pt used is based upon analysis of fresh catalyst and weight of    
 recycled catalyst charged.                                               
 .sup.4 Hexene-2 was used as the olefin substrate, n-heptane used as      
 solvent.                                                                 
 
    
     EXAMPLES 53 TO 56 
     The Hydroformylation of Various Olefin Substrates Using Supported Platinum Halide-Tin Halide Catalysts 
     Samples of supported platinum chloride-tin chloride catalyst, bonded to nitrogen-containing polymers or amine sorbed or silylized silica, are prepared as described in Examples 9-13. Suspensions of said catalysts in benzene  (200 ml) are then evaluated for hydroformylation activity substantially as described in Examples 14-52, except that in separate runs, the hexene-1 charge in substituted by ethylene, propylene, tetradecene-1,4-methylpentene-1, and dodecene-1. Hydroformylation is achieved in all cases, the major aldehydic products are listed in Table V, below: 
     
                       TABLE V                                                     
______________________________________                                    
Olefin substrate                                                          
              Major aldehydic products                                    
______________________________________                                    
Ethylene      n-Propionaldehyde                                           
Propylene     n-Butyraldehyde and 2-methyl-                               
              propionaldehyde                                             
Tetradecene-1 n-Tetradecanal and 2-methyl-                                
              tetradecanal                                                
4-Methylpentene-1                                                         
              5-Methylhexanal and 2,4-dimethyl-                           
              pentanal                                                    
______________________________________                                    
 
    
     As the examples of this invention indicate, the subject invention is advantageous in several respects compared to the corresponding hydroformylation technology of prior art. For example, the novel supported platinum halide, Group IV metal halide catalysts of this invention can be employed to hydroformylate alpha-olefins to the corresponding aliphatic olefins in high yields, in most cases exceeding 90 mole percent, while competing reduction and aldehyde condensation reactions are kept to a minimum. In addition, the solid catalyst is stable to ambient conditions and atmospheric oxygen and may be treated and reused with no special precautions. 
     Finally, the invention is quite advantageous in that numerous substitutions, modifications and changes can be made without departing from the inventive concept. However, the scope of the subject invention can best be understood by examining the claims which follow, read in conjunction with the preceding specification.