Adhesive-coating composition for organic or mineral filaments
The present invention relates to a new adhesive-coating composition which is very easy to use and makes it possible to increase the adhesion of continuous yarns based on polyester, heat-stable, high-modulus polymers, &#34;modal&#34; yarn and glass fibres intended for the reinforcement of articles made of compounded rubber based on natural rubber and on synthetic rubber. 
     In the text, the term &#34;yarns&#34; denotes: continuous filaments and assemblies formed when such filaments are assembled in one and the same operation, yarns and cords formed by twisting, doubling or interlacing a certain number of these filaments, and the woven and non-woven fabrics which are formed from such filaments, yarns or cords, discontinuous fibres and spun yarns consisting of the said discontinuous fibres, and woven and nonwoven fabrics formed from such discontinuous or spun fibres, and combinations of continuous and discontinuous fibres in the form of yarns, cords or fabrics. 
     By &#34;compounded rubbers based on natural rubber&#34; there are understood compounded rubbers containing from 40 to 100% of natural rubber, in which the other constituents can be, for example, synthetic polyisoprene, polybutadiene or a butadiene/styrene copolymer and the like. 
     By &#34;compounded rubbers based on synthetic rubber&#34; there are understood those consisting, for example, of polychloroprene, polyisoprene, polybutadiene, butadiene/styrene copolymers and the like. 
     It is also possible to use mixtures of two types of compounded rubbers in varying percentages depending on the use to be made of them and depending on their compatibility. 
     From French Application No. 2,182,993 there are already known compositions for treating glass fibres, which compositions comprise an aqueous system having a solids content of 2 to 10 parts by weight of resorcinol/aldehyde resin, 20 to 60 parts by weight of a butadiene/styrene/vinylpyridine terpolymer, 20 to 30 parts by weight of a dicarboxylated butadiene/styrene resin and 4 to 20 parts by weight of an incompatible wax. 
     However, such a composition does not make it possible to obtain adhesive-coated glass fibres having sufficient flexibility for the fibres to be used for the production of articles of great flexibility. 
     U.S. Pat. No. 3,533,830 proposes adhesive-coating baths for glass fibres which contain, in addition to the resorcinol/formaldehyde resin, a vinylpyridine/butadiene/styrene terpolymer, a polychloroprene latex, a butadiene/styrene latex and carbon black. 
     U.S. Pat. No. 3,876,024 proposes the use of adhesive-coating compositions containing a polymer produced by grafting vinyl chlorine, vinylidene chloride or chloroprene on a vinylpyridine/butadiene/styrene terpolymer, and a microcrystalline paraffin wax. 
     However, the adhesive-coating compositions of these two U.S. patents do not make it possible to obtain adhesive-coated yarns which are sufficiently flexible for the uses in the rubber industry and which possess the necessary &#34;tack&#34; for easy handling. 
     The present invention relates to a new adhesive-coating composition which makes it possible to increase the adhesion of heat-stable yarns &#34;high-modulus&#34; yarns, yarns based on polyesters, yarns of the modal type, as well as glass fibres, towards compounded rubbers based on natural rubber and synthetic rubber, which composition consists of: 
     
         ______________________________________                                    
 a resin solution A containing:                                           
softened water     547 to 8,954 parts by weight                           
sodium hydroxide   1 to 2 parts by weight                                 
precondensed resorcinol/                                                  
formaldehyde resin 48 to 57 parts by weight                               
40% strength formaldehyde                                                 
                   14.75 to 17.5 parts by weight                          
 a latex solution B containing:                                           
latex based on vinylpyridine                                              
                   805 to 875 parts by weight                             
polychloroprene latex                                                     
                   46 to 92 parts by weight                               
28% strength ammonium hydroxide                                           
                   80 parts by weight                                     
 a latex solution C containing:                                           
softened water     200 parts by weight                                    
28% strength ammonium hydroxide                                           
                   15 parts by weight                                     
dicarboxylated butadiene                                                  
styrene resin      350 parts by weight                                    
______________________________________                                    
 
    
     in which the proportion by weight of solids relative to the weight of the bath varies between 6 and 30%, the proportion by weight of dry resin relative to the total weight of solids varies from 8% to 10%, the ratio of dry latex to the weight of dry resin varies from 8/1 to 11/1, the proportion by weight of dry chlorinated latex relative to the total weight of dry latex varies from 5 to 10%, the proportion by weight of dry latex relative to the total amount of solids varies from 86 to 87% and the final pH is 9.6±0.3. 
     The present invention also relates to the yarns which have been adhesive-coated by means of the above composition. 
     By yarns based on &#34;polyester&#34; there are understood yarns based on polyesters and copolyesters produced from at least one aromatic diacid or one of its esters and, optionally, a small amount of an aliphatic diacid, and at least one aliphatic, or cycloalkane possessing 2 to 10 carbon atoms in the molecule. Preferably, the aromatic diacid is terephthalic acid, the aliphatic diacid is adipic acid or sebacic acid and the diol is ethylene glycol, 1,4-butane diol or 1,4-cyclohexanedimethanol. 
     The yarns of the &#34;modal&#34; type are those defined by &#34;BISFA&#34;, the international bureau for the standardisation of rayon and synthetic fibres. 
     By &#34;high modulus&#34; there is to be understood here a modulus of elasticity or Young&#39;s modulus greater, on average, than 250 g/1.1 dtex (1 denier), this modulus being measured in accordance with Standard specification ASTM D 2IOI, part 25, 1968. 
     The invention is more particularly applicable to the high modulus yarns which furthermore have a high tenacity and/or a high breaking energy, that is to say of at least 50 g/tex, and preferably of at least 100 g/tex. The high modulus yarns are obtained by spinning polymers of inorganic origin such as boron or of organic origin, or are obtained by carbonisation or graphitisation of filaments of polymers based on acrylonitrile; as filaments of organic origin there may be mentioned those produced from polymers which generally contain aromatic nuclei to which rigid radicals are fixed. As an example of these polymers there may be mentioned the aromatic polyamides and more particularly those having a parastructure, of the type of poly-para-phenylene terephthalamide or poly-para-benzamide, the arylaliphatic polyamides or copolyamides of the poly-hexamethylene terephthalamide type or copolyamides which contain aromatic diacids or aliphatic saturated, unsaturated and/or cyclic diacids and aromatic or aliphatic diamines, the copolyamides derived more particularly from terephthalic acid, adipic acid and tetramethylene diamines or para-phenylene diamines, such as those described in French Application No. 2,272,118, published on Dec. 19, 1975, the polyoxadiazoles such as polyarylene-1,3,4-oxadiazole, the copolyoxadiazoles produced from mixtures of isophthalic and terephthalic acids or one of these and aliphatic or cycloalkane acids, and the PVA-based polymers having a high tenacity and high modulus. 
     The invention is also applicable to industrial yarns of the heat-stable type, that is to say yarns which have a high heat resistance (350°-500° C.) and which are based on polymers either of the polyamide-imide type produced by the reaction of a diamine or of one of its derivatives with an acid anhydride or one of its derivatives, or of the aromatic polyamide type obtained by reaction of an aromatic diacid or of one of its derivatives with a diamine or one of its derivatives, it being possible for these polymers to be modified by the introduction of acid groups. 
     Finally, the expression &#34;glass fibres&#34; frequently used throughout the present application comprises all the yarns, fibres and filaments, as defined above, formed by rapid thinning-down of streams of molten glass, in a manner known to those skilled in the art, as well as all the articles obtained from these yarns. 
     By a latex base of vinylpyridine there is understood a styrene/butadiene/vinylpyridine terpolymer known under the trade mark &#34;GEN-TAC&#34; (GENERAL TIRE &amp; RUBBER CO) or UGITEX V.P. (RHONE-POULENC). 
     The precondensed resorcinol/formaldehyde resin used is preferably the resin known under the trade mark &#34;PENACOLITE B 1  A&#34; and the dicarboxylated butadiene/styrene resin used is preferably the resin known under the trade mark &#34;PLIOLITE 4121&#34; of Messrs. GOODYEAR TIRE &amp; RUBBER CO. 
     The resin solution A is prepared by introducing the starting products, in the stated order, whilst stirring at ambient temperature. This solution undergoes a ripening process for a few minutes, whilst stirring, at ambient temperature. 
     The latex solutions B and C are separately prepared in an identical manner, whilst stirring and at ambient temperature. 
     The latex solution C is poured, whilst stirring at ambient temperature, into the latex solution B, and the resin solution A is then poured into the mixture of the latex solutions B and C whilst stirring at ambient temperature. 
     The adhesive-coating composition according to the present invention is preferably left standing for about 24 hours so as to give, after the subsequent treatments, adhesive-coated yarns which have optimum mechanical and physical characteristics. 
     The final pH of the said compositions is generally 9.6±0.3. 
     The adhesive-coating bath thus obtained has a viscosity which is stable over a period of time, and also has good mechanical stability when the filaments are passed over draining rollers; this means that no coagulation of the adhesive-coating bath takes place on the draining devices. 
     It is possible to vary the proportion by weight of dry resorcinol/formaldehyde resin relative to the total amount of all the solids contained in the bath; this ratio varies between 8% and 10%. 
     The proportion of dry latex relative to the total amount of solids can vary between 86% and 87% and the dry latex/dry resin ratio between 8 and 11/1. 
     Equally, the proportion of the amount of dry latex based on polychloroprene relative to the total amount of dry latex can vary between 5 and 10%. 
     The ratio of total solids to the weight of the bath can vary from 6 to 30%. 
     The adhesive-coating treatment by means of the composition according to the present invention is carried out on each of the various types of yarns described above, which have in general been sized and coated with an adhesive primer beforehand in accordance with any process known to those skilled in the art. 
     After passing through the adhesive-coating bath, which is kept at ambient temperature, the yarns are drained to render the layer of coating uniform and are dried at a temperature which depends on the speed of forward travel of the yarn (but at least 100° C.), using any appropriate device such as an oven and the like, after which they are again heat-treated at a high temperature, generally above 130° C., in order to cross-link the resin. 
     The cords treated in this way are generally wound up or doubled directly after the cross-linking treatment. 
     The adhesive-coating compositions according to the present invention have properties which are very valuable to the user. They make it possible to obtain yarns having great flexibility and good adhesion (BISFA static adhesion-test H), whilst the tensometric properties (breaking load, tenacity and elongation at break) remain unchanged. 
     The yarns adhesive-coated in this way possess both good &#34;tack&#34; and good &#34;slip&#34;. The &#34;tack&#34; is the property which the adhesive-coated yarns possess of sticking slightly to one another and to the unvulcanised compounded rubber used, which, inter alia, permits easy winding up and unwinding, as well as good hold of the yarn on the bobbins, by keeping the turns contiguous in a given layer and causing them to stick to one another from one layer to the next. 
     At the same time, the adhesive-coated yarns possess good &#34;slip&#34;, that is to say they are also not subject to drag on passing over working devices in the course of being processed. 
     Furthermore, it is well known to those skilled in the art that in order to achieve a good level of adhesion between the adhesive-coated yarns, regardless of their nature and of the compounded rubber used, the same elastomer or elastomers must be present both in the adhesive-coating bath formulation and in the compounded rubber used. Surprisingly, it has been found, according to the present invention, that it is possible to obtain acceptable levels of adhesion by introducing latex based on polychloroprene into adhesive-coating baths used to impregnate yarns intended to reinforce both compounded rubbers based on natural rubber and based on synthetic rubber as defined above, but also to achieve flexibility and tack of the adhesive-coated yarns by virtue of the carefully chosen ratios of the various constituents. 
     The adhesive-coated yarns thus obtained are of great value for all applications in the rubber industry and in particular for the manufacture of cords for tyres, conveyor belts, conveyors, hoses and the like. 
    
    
     The examples which follow, in which the parts are to be understood as being by weight, are given by way of indication but without implying a limitation, in order to illustrate the invention. 
     In these examples, the adhesive-coating tests are carried out in the manner described below, firstly on compounded rubber based on natural rubber and secondly on compounded rubber based on synthetic rubber. 
     Adhesion test or test H 
     This evaluates the adhesion of the adhesive-coated cords to the rubber. The two ends of the cord to be examined are embedded in two blocks of natural rubber which is then vulcanised. The sample is in the shape of a H. 
     A sample of compounded rubber based on natural rubber, of the following composition by weight, is vulcanised at 145° C. for 30 minutes: 
     
         ______________________________________                                    
smoked sheets         100    parts by weight                              
EPC carbon black      43     parts by weight                              
zinc oxide            5      parts by weight                              
stearic acid          2      parts by weight                              
pine tar              2      parts by weight                              
antioxidant MC (phenyl-β-naphthylamine)                              
                      1      parts by weight                              
&#34;201 RP&#34; rapid accelerator (dibenzo-                                      
thiazyl disulphide)   1      parts by weight                              
sulphur               3      parts by weight                              
______________________________________                                    
 
    
     The compounded rubber thus prepared has the following characteristics: 
     
         ______________________________________                                    
tenacity in kg/cm.sup.2  220                                              
elongation at break, %   554                                              
modulus at 300% in kg/cm.sup.2                                            
                          76                                              
Shore hardness            61                                              
______________________________________                                    
 
    
     and after being left at rest for 24 hours, the adhesion H is determined. 
     The adhesion test H is also carried out on compounded rubber based on synthetic rubber, in the following manner: 
     A sample of compounded rubber of the following composition is vulcanised at 153° C. for 30 minutes: 
     
         ______________________________________                                    
chloroprene (trade mark Neoprene                                          
                      100    parts by weight                              
G N A)                                                                    
SRF carbon black      30     parts by weight                              
FT carbon black       20     parts by weight                              
treated chalk         10     parts by weight                              
plasticiser known under the trade mark                                    
&#34;Circolight Oil&#34;      15     parts by weight                              
anti-ozone agent known under the trade                                    
mark &#34;Heliozone&#34;      2      parts by weight                              
zinc oxide            5      parts by weight                              
magnesia              4      parts by weight                              
antioxidant known under the trade                                         
mark &#34;Permanax 49 HV&#34; 2      parts by weight                              
the product has the following characteristics:                            
breaking load         135    kg                                           
elongation at break   592    %                                            
modulus at 300 %      35.75  kg/cm.sup.2                                  
Shore hardness        60                                                  
______________________________________                                    
 
    
     EXAMPLE 1 
     A yarn based on poly(ethylene glycol terephthalate) having a gauge of 1,100 dtex/200 strands is sized, then twisted at 500 turns/meter in the Z-direction and then doubled at 500 turns/meter in the S-direction (1100/1/2 500 Z/S). It is adhesive-coated, for comparison purposes, on the one hand with a comparison bath and on the other hand with a bath according to the present invention. 
     1A. Experiment with the bath according to the invention 
     
         ______________________________________                                    
softened water       956.5   parts by weight                              
sodium hydroxide     1       parts by weight                              
precondensed resorcinol/formal-                                           
dehyde resin known under the trade                                        
mark &#34;Penacolite B.sub.1 A&#34;                                               
                     57      parts by weight                              
40 % strength formaldehyde                                                
                     15.5    parts by weight                              
whilst stirring and at ambient temperature to give solution               
______________________________________                                    
A.                                                                        
 
    
     A latex solution B, which is left to ripen for 3 to 4 minutes, and a latex solution C, are prepared separately, whilst stirring and at ambient temperature; these solutions respectively contain: 
     
         ______________________________________                                    
latex solution B:                                                         
latex based on vinylpyridine                                              
                      805    parts by weight                              
polychloroprene       92     parts by weight                              
28 % strength ammonium hydroxide                                          
                      80     parts by weight                              
latex solution C:                                                         
softened water        200    parts by weight                              
28 % strength ammonium hydroxide                                          
                      15     parts by weight                              
&#34;Pliolite 4121&#34; dicarboxylated butadiene/                                 
styrene resin         350    parts by weight                              
______________________________________                                    
 
    
     Latex solution C is poured into solution B whilst stirring, and solution A is then poured into the mixture thus obtained, whilst stirring at ambient temperature. 
     
         ______________________________________                                    
Solids content of the composition                                         
                           25 %                                           
Dry weight of resin/solids content                                        
                           9.8 %                                          
Dry weight of latex/solids content                                        
                           86 %                                           
Dry weight of latex/dry weight of resin                                   
                           8.7/1                                          
Dry weight of chlorinated latex/total of the                              
latices                    10 %                                           
______________________________________                                    
 
    
     The bath is left to stand for 24 hours. 
     The adhesive-coating composition thus obtained, of pH 9.6, has a stable viscosity and good mechanical stability. 
     The yarns are adhesive-coated at a speed of 18 m/minute and drained on rollers to remove the excess bath, dried continuously in an oven at a temperature of 145° C. and then heat-treated at a temperature of 225° C. to cross-link the resin, during which treatment the yarn is stretched by an amount of about 5% of its initial length and is then relaxed by about 2%. 
     Amount of deposit on the yarn: 6.5% ##EQU1## 
     The adhesion results are shown in the table below. 
     1B. Comparative experiment with a comparison bath of the following composition: 
     
         ______________________________________                                    
Solution A                                                                
______________________________________                                    
resorcinol            27     parts by weight                              
water                 305    parts by weight                              
The resorcinol is dissolved in water and the following                    
are then added:                                                           
NaOH (28 % strength)  2.5    parts by weight                              
followed by formaldehyde (30% strength)                                   
                      48.5   parts by weight                              
______________________________________                                    
 
    
     Solution A is left to ripen for 6 hours at 15° C. and the following is added: NaOH (28% strength) 6 parts by weight 
     
         ______________________________________                                    
Solution B                                                                
______________________________________                                    
styrene/butadiene/vinylpyridine                                           
copolymer latex    361      parts by weight                               
natural latex      68.5     parts by weight                               
styrene/butadiene latex (S.B.R.)                                          
40% strength       51.5     parts by weight                               
water              130      parts by weight                               
______________________________________                                    
 
    
     Solution A is poured into Solution B. 
     The adhesive-coating solution thus prepared has the following characteristics: 
     
         ______________________________________                                    
solids content             25 %                                           
molar ratio formaldehyde/resorcinol                                       
                           2                                              
proportion by weight of dry resin/solids content                          
                           16.6%                                          
proportion by weight of latex/solids content                              
                           82.5% -weight ratio latex/resin 5/1            
______________________________________                                    
 
    
     The yarns are then treated with this bath in the same way as they were treated with the bath according to the invention in experiment 1A. 
     
         ______________________________________                                    
Adhesion results                                                          
               Test 1 B  Test 1 A                                         
______________________________________                                    
Adhesion to synthetic rubber                                              
(compounded rubber defined                                                
above)           8.4 kg/5 mm 9 kg/5 mm                                    
Coefficient of variation                                                  
                 conventional                                             
                 base: 100   75                                           
Adhesion to natural rubber                                                
(compounded rubber defined                                                
above)           9 kg/5 mm   10.1 kg/5 mm                                 
Coefficient of variation                                                  
                 conventional                                             
                 base: 100   80                                           
______________________________________                                    
 
    
     EXAMPLE 2 
     A yarn based on poly(para-phenylene terephthalamide), having a gauge of 1,650 dtex/1,000 strands (gauge per strand 1.65 dtex) is sized, then twisted at 340 turns/meter in the Z-direction and then doubled at 340 turns/meter in the S-direction to give the final construction 1650/1/2 340 Z/S, and is treated with a preadhering agent. 
     It is then adhesion-coated, by way of comparison, with a comparison bath and a bath according to the present invention. 
     2A. Experiment with the bath according to the invention 
     identical to that prepared in Example 1, Experiment 1A. 
     The yarn is then drained on rollers to remove the excess bath, dried continuously to a temperature of 225° C. and then heat-treated at a temperature of 225° C. to cross-link the resin during which treatment the yarn is stretched by 0.36% of its initial length. 
     Proportion of deposit: 9.5% 
     The adhesion results are given in the table below. 
     2B. Comparative experiment with comparison bath 
     
         ______________________________________                                    
Solution A                                                                
______________________________________                                    
resorcinol       27     parts by weight                                   
water            305    parts by weight                                   
______________________________________                                    
 
    
     The resorcinol is dissolved in water and the following are then added: 
     
         ______________________________________                                    
NaOH (28% strength)   2.5    parts by weight                              
followed by formaldehyde                                                  
 (30 % strength)      48.5   parts by weight                              
______________________________________                                    
 
    
     Solution A is left to ripen for 6 hours at 15° C. and the following is added: 
     NaOH (28% strength): 6 parts by weight 
     
         ______________________________________                                    
Solution B                                                                
______________________________________                                    
styrene/butadiene/vinylpyridine                                           
copolymer latex    361      parts by weight                               
natural latex      68.5     parts by weight                               
styrene/butadiene latex (S.B.R.)                                          
40% strength       51.5     parts by weight                               
water              130      parts by weight                               
______________________________________                                    
 
    
     Solution A is then poured into solution B. 
     The adhesion-coating composition thus prepared has the following characteristics: 
     
         ______________________________________                                    
solids content             25 %                                           
molar ratio formaldehyde/resorcinol                                       
                           2                                              
proportion by weight of dry resin/solids content                          
                           16.6%                                          
proportion by weight of latex/solids content                              
                           82.5% -weight ratio latex/resin 5/1            
______________________________________                                    
 
    
     The yarn is treated with this bath in the same manner as in the above experiment 2A according to the invention. 
     Proportion of deposit on the yarn: 9.5% 
     
         ______________________________________                                    
Adhesion results                                                          
               Experiment                                                 
                         Experiment                                       
               2 B       2 A                                              
______________________________________                                    
Adhesion to synthetic rubber                                              
                 8 kg/5 mm   11 kg/5 mm                                   
Coefficient of variation                                                  
                 conventional                                             
                 base: 100   80                                           
Adhesion to natural rubber                                                
                 8 kg/5 mm   8.8 kg/5 mm                                  
Coefficient of variation                                                  
                 conventional                                             
                 base: 100   60                                           
______________________________________                                    
 
    
     EXAMPLE 3 
     A yarn of the modal type known commercially by the name of &#34;continuous polynosic yarn BX&#34;, having a gauge of 1,400 dtx/3,125 strands (gauge per strand 0.45 dtex) is sized, then twisted at 200 turns/m in the Z-direction and then doubled at 150 turns/m in the S-direction, so as to give the final construction of 1400/1/3 200/150 Z/S. It is adhesive-coated, by way of comparison, with a comparison bath and the bath according to the invention. 
     3A. Experiment with the bath according to the invention 
     The bath as described in Example 1A, but having a solids content of 7.5%, the other ratios being identical, is used. 
     The yarn is adhesive-coated at a speed of 40 m/minute, then drained on rollers to remove the excess bath, dried continuously at a temperature of 185° C. and heat-treated in an oven at 135° C. to cross-link the resin, and is then wound up directly. 
     Proportion of deposit on the yarn: 4%. 
     The adhesion results are given in the table below. 
     3B. Comparative experiment with a bath of the following composition: 
     
         ______________________________________                                    
Solution A                                                                
______________________________________                                    
water                 93.9   parts by weight                              
NaOH (28 % strength)  0.18   parts by weight                              
formaldehyde          2.2    parts by weight                              
precondensed resorcinol/formaldehyde                                      
resin (&#34;Miplacol 730&#34; from Kleber                                         
Colombes)             2.2    parts by weight                              
______________________________________                                    
 
    
     Solution A is prepared by introducing the resin into the water containing the sodium hydroxide and then adding the formaldehyde. 
     
         ______________________________________                                    
Latex solution B                                                          
______________________________________                                    
polychloroprene latex                                                     
(&#34;Neoprene 650&#34; of Du Pont)                                               
                   27.7    parts by weight                                
natural latex      11.9    parts by weight                                
water              227.9   parts by weight                                
Characteristics of the bath:                                              
solids content          7.5%                                              
proportion by weight of dry resin/solids content                          
                       11.6 %                                             
proportion by weight of latex/solids content                              
                       88  %                                              
latex/resin ratio       7.6/1                                             
proportion by weight of chlorinated latex/                                
total latex            70  %                                              
______________________________________                                    
 
    
     Solution A is poured into solution B at 20° C. 
     This yarn is then treated with the same manner as according to Experiment 3A. 
     Proportion of deposit on the yarn: 4%. 
     
         ______________________________________                                    
Adhesion results                                                          
               Experiment                                                 
                         Experiment                                       
               3 B       3 A                                              
______________________________________                                    
Adhesion to synthetic rubber                                              
                 6.8 kg/5 mm 8 kg/5 mm                                    
Coefficient of variation                                                  
                 conventional                                             
                 base: 100   30                                           
Adhesion to natural rubber                                                
                 7.5 kg/5 mm 7.5 kg/5 mm                                  
Coefficient of variation                                                  
                 conventional                                             
                 base: 100   100                                          
______________________________________                                    
 
    
     In the above examples, the comparison between the comparison bath and the bath of the invention shows a marked improvement of the adhesion and in the majority of cases better uniformity of the adhesion levels (shown by the values of the coefficient of variation), this being true for different types of yarns having a different construction, and for compounded rubber based either on natural rubber or on synthetic rubber. 
     EXAMPLE 4 
     An adhesive-coating bath according to the invention, consisting of a resin solution A containing: 
     
         ______________________________________                                    
softened water        547    parts by weight                              
sodium hydroxide      1      parts by weight                              
precondensed resorcinol/formaldehyde                                      
resin known by the trade mark                                             
&#34;Penacolite B.sub.1 A&#34;                                                    
                      57     parts by weight                              
40 % strength formaldehyde                                                
                      15.5   parts by weight                              
is prepared whilst stirring at ambient temperature.                       
______________________________________                                    
 
    
     A latex solution B, which is left to ripen for 3 to 4 minutes, and a latex solution C, are prepared separately, whilst stirring and at ambient temperature; these solutions respectively contain: 
     
         ______________________________________                                    
latex solution B:                                                         
latex based on vinylpyridine                                              
                      805    parts by weight                              
polychloroprene       92     parts by weight                              
28 % strength ammonium hydroxide                                          
                      80     parts by weight                              
latex solution C:                                                         
softened water        200    parts by weight                              
28 % strength ammonium hydroxide                                          
                      15     parts by weight                              
&#34;Pliolite 4121&#34; dicarboxylated/butadiene                                  
styrene resin         350    parts by weight                              
______________________________________                                    
 
    
     Latex solution C is poured into solution B whilst stirring, and solution A is then poured into the mixture thus obtained, whilst stirring at ambient temperature. 
     
         ______________________________________                                    
Solids content of the composition                                         
                            30 %                                          
Dry weight of resin/solids content                                        
                             9.8 %                                        
Dry weight of latex/solids content                                        
                            86 %                                          
Dry weight of latex/dry weight of resin                                   
                             8.7/1                                        
Dry weight of chlorinated latex/total of the latices                      
                            10 %                                          
______________________________________                                    
 
    
     The bath is left to stand for 24 hours. 
     The adhesive-coating composition thus obtained, of pH 9.6, has a stable viscosity and a good mechanical stability. 
     3 cords of glass fibres each of 340 dtex, with each strand having a diameter of 9μ, are impregnated by means of the composition thus prepared. 
     Each cord is drained on a roller equipped with a wiper blade to remove the excess bath, and is then dried continuously at a speed of 45 m/minute in a 12 meter long oven maintained at 270° C.; the treatment of cross-linking the resin is then carried out continuously in a 12 meter long oven at 270° C. at a speed of 45 m/minute. 
     Each cord adhesive-coated in this way is twisted at 140 turns/m in the Z-direction and the 3 cords are then twisted together at 140 turns/m in the S-direction. 
     Apart from very great flexibility, the twisted cord thus prepared has the following characteristics: 
     
         ______________________________________                                    
Adhesion H towards compounded rubber                                      
based on polychloroprene, of the                                          
composition given above                                                   
                      8.5 kg/5 mm (mean of                                
                      20 measurements)                                    
Proportion                                                                
 ##STR1##                                                                 
Breaking load:        26.4 kg                                             
______________________________________                                    
 
    
     EXAMPLE 5 
     An adhesive-coating composition composed of the following is prepared in the same manner as according to Example 4: 
     
         ______________________________________                                    
Solution A                                                                
softened water       732     parts by weight                              
sodium hydroxide     1       parts by weight                              
&#34;Penacolite B.sub.1 A&#34; precondensed                                       
resorcinol/formaldehyde resin                                             
                     48      parts by weight                              
40 % strength formaldehyde                                                
                     12      parts by weight                              
Solution B                                                                
latex based on vinylpyridine                                              
                     805     parts by weight                              
polychloroprene      92      parts by weight                              
28 % strength ammonium hydroxide                                          
                     80      parts by weight                              
Solution C                                                                
softened water       200     parts by weight                              
28 % strength ammonium hydroxide                                          
                     15      parts by weight                              
&#34;Pliolite 4121&#34; dicarboxylated/butadiene                                  
styrene resin        350     parts by weight                              
Solids content of the composition                                         
                      27 %                                                
Weight of dry latex/solids content                                        
                      87 %                                                
Weight of dry resin/solids content                                        
                       8 %                                                
Dry weight of latex/resin                                                 
                      10.5/1                                              
Dry weight of chlorinated latex/latex                                     
                      10 %                                                
______________________________________                                    
 
    
     The composition is left to stand for 24 hours. It has a pH of 9.6, a viscosity which is stable over a period of time, and good mechanical stability. 
     3 Cords of 340 dtex (9μ) are treated in exactly the same manner as according to Example 4, the cords being twisted together in this case also. 
     The final cord has great flexibility and possesses the following characteristics: 
     
         ______________________________________                                    
Adhesion H towards compounded rubber                                      
based on polychloroprene                                                  
                      8.1 kg/5 mm (mean of                                
                      20 measurements)                                    
Proportion of deposit: 20 %                                               
                      (measured as in Ex. 1)                              
Adhesion H towards compounded rubber                                      
based on natural rubber                                                   
                      7.5 kg/5mm (mean of                                 
                      20 measurements)                                    
Proportion of deposit: 20.4 %.                                            
______________________________________