Wet adhesion emulsions of polymer resins systems employed in water-based paint and coating compositions comprising as a component thereof monomer containing an ethylenic double bond and a ureido group polymerized therein
CROSS REFERENCE TO RELATED APPLICATION 
     The present application is a continuation-in-part of our application Ser. No. 709,677 filed July 29, 1976 now U.S. Pat. No. 4,111,877 which issued September 5, 1978 . Novel monomeric compounds useful in enhancing wet adhesion and syntheses of such compounds are disclosed and claimed in copending application Serial No. 883,554 having a filing date of March 6, 1978, and entitled &#34;Monomeric Compounds Having Vinyl and Ureido Terminal Groups.&#34; 
    
    
     BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     This invention relates generally to resin polymer emulsions used in formulation of water-based paints and coating compositions and is concerned particularly with improving the useful properties, more particularly the wet adhesion properties, of such paints and coating compositions. Such improvements are brought about by incorporation into the polymer resin emulsion certain monomeric compounds, as hereinafter described, which have at one end thereof a terminal ureido group and at the opposite terminal end, an unsaturated ethylenic group. 
     2. Prior Art 
     In U.S. Pat. No. 3,300,429 there are disclosed emulsions for water-based paints and coating compositions comprising addition polymers of (1 ) vinyl esters, (2 ) acrylic acid esters, and (3 ) mono- and di-ethylenically unsaturated hydrocarbons, stated to impart improved adhesion properties, including wet adhesion. The disclosed compositions of the patent comprise (1 ) the said water-insoluble addition polymer together with (2 ) a low molecular weight water-soluble ammonium salt of a copolymer of an alpha-beta unsaturated acid, said water insoluble addition polymer (1 ) or said soluble copolymer (2 ) having copolymerized therein a monomer having a cyclic or acyclic ureido group. A number of such ureido compounds are listed in the patent, and a wide variety of uses are indicated for the described compositions. 
     Various polymerizable compounds containing a terminal ureido group are disclosed in the prior art for a wide variety of different uses. Thus, in U.S. Pat. Nos. 2,881,155 and 2,881,171 there are disclosed cyclic ureido compounds terminated at the opposite end in an acrylic or methacrylic acid group. In U.S. Pat. No. 3,369,008, polymerization of N-(cyclic ureido-alkyl) crotonamides is disclosed, stated to be useful in adhesives, coating and textile finishing compositions. U.S. Pat. Nos. 2,980,652 and 3,194,792 disclose cyclic ureido compounds terminated at the opposite end by the residue of an unsaturated dicarboxylic acid. The ureido compounds of U.S. Pat. No. 3,024,246 terminate at the opposite end in an acrylamido group, and are stated to be useful as textile softening agents. 
     In our copending application Ser. No. 709,677 there are described novel cyclic ureido monomers terminating at the opposite end in the residue of an allyl or methallyl ester of a carboxylic acid ##STR2## The compounds of said copending application, in contrast to the known cyclic ureido derivatives of the prior art, are characterized in that the carbonyl group in the chain linking the amino nitrogen of the N-amino alkyl urea to the terminal ethylene group is not directly attached to an ethylenic carbon atom. 
     In copending U.S. patent application, Ser. No. 709,916  filed July 29, 1976, now Pat. No. 4,104,220 the synthesis of novel allyl succinamic ureido compounds is described. These compounds as well as those described in the companion copending application Ser. No. 709,677 are shown to be particularly useful as functional comonomers for imparting improved wet adhesion properties to emulsion systems containing vinyl ester polymers, employed in paints and coating compositions. 
     SUMMARY OF THE INVENTION 
     It has now been found that the monomeric ureido compounds previously disclosed in our copending application Ser. No. 709,677 for improving the wet adhesion properties of waterbased paints comprising polymer emulsion systems containing vinyl ester polymers are also effective in improving the wet adhesion properties of such compositions employiing emulsions of other resin polymers, such as those containing acrylate and/or methacrylate esters. It has also been found that such enhancement of wet adhesion can be effected with other selected acyclic and cyclic ureido compounds including not only the new synthesized compounds disclosed in our companion copending application U.S. Ser. No. 883,554 and having a filing date of March 6, 1978 discussed previously, but also by use of certain relatively simple ethylenically unsaturated urea compounds, such as allyl urea. 
     Accordingly, the present invention is directed to polymer emulsion systems for incorporation in formulations for water-based paints and coating compositions, which emulsions contain, in addition to the usual polymer resin, a monomeric ureido compound corresponding to the formula ##STR3## wherein R is H or CH 3 , U designates a cyclic or acyclic ureido or thioureido group and L designates a selected linking chain connecting a ureido nitrogen to the vinylic ##STR4## terminal group at the opposite end of the chain. The linking chain L may be a single methylene group --CH 2  --or a polymethylene chain or such chain may contain one or more oxy (ether), amino, amido or carbonyl groups, provided that any carbonyl group (CO) present is not directly attached to U or to an ethylenic carbon atom nor is an ethylenic carbon directly attached to a nitrogen atom. The ureido terminal group U may be acyclic corresponding to the structure ##STR5## in which B is an oxygen or sulfur atom, and R 1  R 2  and R 3  each separately is hydrogen, alkyl, aryl, hydroxyalkyl or alkoxyalkyl or R 2  and R 3  may form a cyclic structure by being part of a piperidine, pyrrolidine or morpholine structure; or the ureido group may be cyclic, corresponding to the structure ##STR6## wherein B is as above defined, 
     R 4  is hydrogen, alkyl, aryl, hydroxyalkyl or alkoxyalkyl, and A is ah alkylene group of 2 to 3 carbon atoms, such as 
     
         --CH.sub.2 CH.sub.2 --, --CH.sub.2 --CH.sub.2 --CH.sub.2 -- or 
    
     
         --CH.sub.2 --CH(CH.sub.3 )--. 
    
    
    
     description of preferred embodiments 
     compounds corresponding to formula I above, in their simplest form, are those in which the linking chain L is a --CH 2  -- group as in ##STR7## A simple example of such compounds is allyl urea of the formula ##STR8## 
     The useful compounds described in our copending application Ser. No. 709,677 contain as the linking chain L the group ##STR9## wherein m is zero or one. Illustrative specific compounds corresponding to the above are ##STR10## and 
     Other related specific compounds containing the linking group III above and analogs thereof include those in which R is CH 3  and those in which ##STR11## is replaced by oxygen, respectively as in ##STR12## and 
     Compounds of the type IIIa and IIIb may be synthesized by the methods described in our copending application Ser. No. 709,677; respectively by (a) reaction of 2-aminoethyl ethyleneurea with diallyl carbonate or with allyl chloroformate and (b) by reaction of the 2 -aminoethyl ethyleneurea with diallyl oxalate. 
     Among further types of compounds useful in practice of the invention are those corresponding to the general formula ##STR13## wherein n is an integer from 1 to 9, T is oxygen or ##STR14## and the other designations being as hereinbefore defined. A specific compound corresponding to the above formula IV are illustrated by ##STR15## 
     Also useful in practice of the invention are compounds represented by the general formula ##STR16## wherein 
     
         G is CH.sub.2 NR.sup.1 -- or CH.sub.2 O, 
    
     t is oxygen or ##STR17## and the other symbols are as above defined. Specific examples of such compounds are those corresponding to the formulae ##STR18## 
     A further type of useful compound is represented by the general formula ##STR19## wherein D is -- (CH 2  )  n  -- or --CH 2  -- T -- (CH 2  ) n  --. 
     Particular examples of such compounds are those represented by the formulae: ##STR20## 
     A further group of useful compounds is represented by the general formula ##STR21## wherein E represents an alkylene group of 1 to 10 carbon atoms and J is --CH 2  O --, --CH 2  NR 1  -- or an oxygen atom. Illustrative examples of such compounds include those represented by the formulae ##STR22## 
     Another group of useful compounds is that represented by the general formula ##STR23## 
     Illustrative examples of such compounds are ##STR24## 
     A further group of such compounds is that represented by the general formula ##STR25## 
     A specific example of compounds coming within this group is that represented by the formula ##STR26## 
     SYNTHESIS OF HC1 SALT N-β  - (ALLYLAMINO) ETHYL ETHYLENE UREA (FORMULA IVa) 
     To a reaction vessel containing 285.5 parts by weight of allylamine, there were added 148.04 parts of N-(β-chloroethyl)-N,N&#39;  ethylene urea and 750 parts distilled water. A slight exotherm was observed (temperature rise about 16° C.). 
     Heating was commenced with stirring, and an initial reflux temperature of 87.5° C. was observed. The reactants were permitted to reflux overnight, after which the contents were transferred to a concentrating vessel and heated at about 75° C. to remove water and excess allyl amine. 
     A mass of yellow waxy material was obtained. This product was taken up in absolute ethanol (350 parts product per 237 parts alcohol and to the resulting hot mixture there was added 630 parts by weight of ethyl acetate and the mixture set aside to cool slowly. Crystals of the hydrochloride salt of compound IVA were filtered off from the cooled mixture and dried in a vacuum oven at room temperature. 
     Actual yield obtained was 85.11% of theory. The crystalline product had a melting point of 151.5°-152.5° C. 
     
         ______________________________________                                    
ELEMENTAL ANALYSIS                                                        
          C       H         N                                             
______________________________________                                    
Actual %    45.95     7.99      19.94                                     
Theor. %    46.74     7.78      20.44                                     
______________________________________                                    
 
    
     Instead of reacting the chloroethyl urea compound with the allylamine, the same product can be obtained by reacting the 2 -amino ethyl ethylene urea with allyl halide. If one employs as reactant with the ureido amine, the isomeric 1 -halo-2-methyl-2 -propene compound, corresponding compounds are obtained terminating in the ##STR27## group. 
     PREPARATION OF ALLYL (B-1 -ETHYLENEUREIDO) ETHYL CARBONATE (FORMULA IIId) 
     In a reaction vessel there were mixed 
     
         ______________________________________                                    
                       pbw                                                
______________________________________                                    
N-β-hydroxyethyl-N,N&#39;-ethylene urea                                  
                         130                                              
Methylene chloride       1325.5                                           
Triethylamine            126.31                                           
______________________________________                                    
 
    
     To the resulting mixture there was added dropwise 150.6  parts allyl chloroformate while maintaining the temperature at 10°-15° C. The addition took about 1.5 hours. 
     The mixture began to reflux at about 45° C., and was continued overnight. It was then filtered with suction and the filtrate containing the product was concentrated under vacuum. The last traces of solvent were removed by vacuum pumping overnight with heating to 50° C.; and then dried. Actual yield was 88.7% of theory. 
     
         ______________________________________                                    
ELEMENTAL ANALYSIS                                                        
          C       H         N                                             
______________________________________                                    
% theory    50.49      7.51     13.08                                     
% actual    51.54     6.53      12.63                                     
______________________________________                                    
 
    
     SYNTHESIS OF n-[B-1-ETHYLENEUREIDO] ETHYL ALLYLOXYACETAMIDE (FORMULA VIc) 
     The reactants comprised: 
     
         ______________________________________                                    
                       pbw                                                
______________________________________                                    
N-(β-aminoethyl)-N,N&#39;-ethylene urea                                  
                         71                                               
Allyl allyloxyacetate    86.23                                            
Acetonitrile             157.14                                           
______________________________________                                    
 
    
     These were added one after another to a reaction vessel and the mixture stirred for about 2 hours at room temperature. A TLC (thin layer chromotography) plate was run on the mixture which indicated that some product was formed. 
     The reaction was maintained at 50° C. for about 17  hours. The TLC plate was again run on the mixture which indicated further product formation. 
     The reaction was heated for an additional three hours, then cooled and filtered to remove the precipitated impurities. The filtrate was stripped of acetonitrile and allyl alcohol by rotary evaporation. A clear yellow oil remained which solidified on standing at room temperature. The obtained solid material was recrystallized from ethanol/ethyl ether and had a melting point of 73°-74° C. The actual yield of recrystallized product was 45.16% of theory. 
     PRODUCTION OF ALLYL N-METHYL-N-β-(1 -ETHYLENE UREIDO) ETHYL CARBAMATE (FORMULA IIIc) 
     In a reaction vessel there were mixed 
     
         ______________________________________                                    
                        pbw                                               
______________________________________                                    
N(B-Methylaminoethyl)-N,N&#39; ethylene urea                                  
                          18                                              
Methylene chloride        99.4                                            
Sodium hydroxide (30% solution in water)                                  
                          143.                                            
______________________________________                                    
 
    
     To this stirred solution there was added dropwise with cooling 12 parts of allyl chloroformate, keeping the temperature between 15°-20° C. 
     The reaction mixture was then stirred at room temperature for about an hour and let stand to permit the product to separate into layers. The bottom layer comprising the methylene chloride solution was dried over anhydrous magnesium sulfate. Following filtration to remove the magnesium sulfate, the methylene chloride solvent was stripped off at about 30° C. under vacuum. The product was obtained at 87.27% of theoretical yield. 
     It was confirmed by TLC that there was only one component in the reaction product and the structure was confirmed by NMR (nuclear magnetic resomance spectroscopy). 
     
         ______________________________________                                    
ELEMENTAL ANALYSIS                                                        
          C       H         N                                             
______________________________________                                    
Theoretical %                                                             
            52.88     7.48      18.5                                      
Actual %    51.61     7.78      18.14                                     
______________________________________                                    
 
    
     The compounds of the invention may be incorporated in emulsion systems containing acrylic, vinyl ester or other pigmented or non-pigmented aqueous emulsion systems useful in paints and coatings in the manner described in the aforesaid copending applications. The following specific example illustrates the polymerization of a ureido compound of the type described to form an interpolymer within a commercial interpolymer system comprising vinyl acetate, vinyl chloride, ethylene and maleic acid. 
     EXAMPLE 1 
     To a pressure vessel, there was charged: 
     
         ______________________________________                                    
                    parts by weight                                       
                    (p.b.w.)                                              
______________________________________                                    
     Vinyl acetate        4540                                            
a)   Triton X-301 (20%)   1040                                            
b)   Igepal CO-730        416                                             
c)   Siponate DS-10       208                                             
     Sodium vinyl sulfonate (25%)                                         
                          98                                              
     Potassium persulfate 300                                             
     Ferrous salt         1.5                                             
     Water                8170                                            
______________________________________                                    
 
    
     The agitated vessel contents initially showed a pH of 3.2. 
     The kettle contents were purged with N 2  and agitated at 150 rpm. Upon heating to 46° C., the charge was pressurized to 900  psi (63.28 kg/cm 2  ) with ethylene. Polymerization was initiated with a 2.0% Discolite solution and there were simultaneously added to the kettle the following compositions in 5 delays. 
     In the first delay, the initiator was introduced over a period of eight hours and was composed of: 
     
         ______________________________________                                    
        Delay 1     p.b.w.                                                
______________________________________                                    
(d)       Discolite     200                                               
          water         4600                                              
          NH.sub.4 OH (28%)                                               
                        200                                               
______________________________________                                    
 
    
     The second and third delays were introduced during a three hour period. These comprised: 
     
         ______________________________________                                    
Delay 2          Delay 3                                                  
______________________________________                                    
4540 parts vinyl 9090 parts vinyl                                         
acetate          chloride                                                 
______________________________________                                    
 
    
     The fourth and fith delays were introduced during a four hour period. These comprised: 
     
         ______________________________________                                    
Delay 4      p.b.w.   Delay 5       p.b.w.                                
______________________________________                                    
Maleic acid (29% sol)                                                     
             664      ureido cmpd.III(a)                                  
                                     363                                  
sodium vinyl sulfonate                                                    
             293      water         1816                                  
water        2227                                                         
______________________________________                                    
 
    
     (a) Anionic surfactant-sodium salt of an alkaryl polyether sulfate. 
     (b) Nonionic surfactant; nonylphenoxy ethanol comprising 75% ethylene oxide. 
     (c) Anionic surfactant; purified dodecyl benzene sodium sulfonate. 
     (d) Sodium formaldehyde sulfoxylate. 
     The polymerization temperature was maintained at 50° C. with a jacket temperature of 23°-50° C. The kettle pressure was maintained at 960 psi (67.5 kg/cm 2  ) throughout the delays. At the end of the delays, the vinyl acetate free monomer content was less than 0.5%. The final emulsion had a solids content of 53.4% and the final pH was adjusted to 5.0. This emulsion when incorporated into a semi-gloss paint had outstanding wet adhesion. 
     An example for preparation of another emulsion system comprising a copolymer of vinyl acetate with ethylene and maleic acid is as follows. 
     EXAMPLE 2 
     There was charged to a pressure vessel 
     
         ______________________________________                                    
                     parts by weight                                      
______________________________________                                    
     Vinyl acetate         1,907                                          
(e)  Igepal CO 887         1,218                                          
(f)  Igepal CO 630         426                                            
     Sodium vinyl sulfonate (25%)                                         
                           158                                            
     Polysodium vinyl sulfonate (25%)                                     
                           171                                            
     Potassium persulfate  80                                             
     Fe.sup.++             0.3                                            
     Water                 18,160                                         
______________________________________                                    
 
    
     The stirred mixture had an initial pH of 3.2. 
     The kettle contents were stirred at 150 rpm, purged with nitrogen, and then pressurized to 570 psi (=40 kg/cm 2  ) while heating to 50° C. Polymerization was initiated with a 50% solution of Discolite and there were added to the kettle simultaneously over a four hour period, four delays as follows: 
     
         ______________________________________                                    
Delay 1          Delay 2                                                  
______________________________________                                    
            pbw                       pbw                                 
Vinyl acetate                                                             
            19,749   Maleic anhyd.    115                                 
Triallyl cyanurate                                                        
            8,898    Sodium vinyl sulfonate                               
                                      173                                 
                     (25%)                                                
                     Pot. persulfate  58                                  
                     Water            922                                 
Delay 3          Delay 4                                                  
______________________________________                                    
Discolite   250      Ureido compound III(a)                               
                                      363                                 
NH.sub.4 OH (28%)                                                         
            150      Water            4631                                
Water       5,000                                                         
______________________________________                                    
 
    
     (e) Nonyl phenoxypoly (ethyleneoxy) ethanol comprising 86 % ethylene oxide. 
     (f) Nonyl phenoxypoly (ethyleneoxy) ethanol comprising 65 % ethylene oxide. 
     The polymerization temperature was maintained at 50° C. with a jacket temperature of 43° C. and ethylene pressure of 570  psi (=30  kg/cm 2  ) during the course of the delays. At the end of the delays, and when the vinyl acetate free monomer content was less than 0.5%, the emulsion was cooled to ambient temperature and transferred to a degasser. The emulsion contained 50% solids and imparted outstanding wet adhesion to semi-gloss paints. 
     A further example of an emulsion system comprising a copolymer of vinyl acetate and butyl acrylate made up for a semigloss paint which showed particularly good wet adhesion properties with addition of selected ureido compounds, was formulated as follows: 
     EXAMPLE 3 
     Into a jacketed reaction vessel there was charged 
     
         ______________________________________                                    
                       pbw                                                
______________________________________                                    
Hydroxyethyl cellulose   0.45                                             
Alkyl phenoxy poly(oxyethylene)ethanols                                   
                         13.7                                             
Ferrous salt             (trace)                                          
De-ionized water         380                                              
______________________________________                                    
 
    
     The vessel and contents were purged with nitrogen while heated at 65° C. and stirred. There were then added to the vessel at delayed intervals the following three mixtures 
     
         ______________________________________                                    
Mixture 1               pbw                                               
______________________________________                                    
Vinyl acetate           415.2                                             
Butyl acrylate          67.5                                              
*Pluronics              15.6                                              
t-Butyl peroxide (70%)  0.7                                               
 *Pluronics are non-ionic block polymers comprising polyalkylene          
 derivatives of propylene glycol terminating in hydroxyl.                 
Mixture 2               pbw                                               
______________________________________                                    
Sodium formaldehyde bisulfite                                             
                        0.2                                               
Sodium benzoate         0.6                                               
De-ionized water        8.2                                               
Mixture 3               pbw                                               
______________________________________                                    
Ureido compound III(a)  2.4                                               
De-ionized water        72.0                                              
______________________________________                                    
 
    
     The first and third mixtures were added over a two hour period while the second was added during a fifteen minute period. The polymerization mixture was maintained at 65° C. After addition of the second mixture was completd, there was further added a solution of 0.6 parts of sodium formaldehyde bisulfite in 18.1  parts de-ionized water until polymerization was completed. The emulsion was then cooled to ambient temperature. It had a pH of 5.2 and contained 55.4% solids. Addition of a pigment dispersion to the emulsion provided a semigloss paint having outstanding wet adhesion. 
     An example of an all acrylic emulsion to which improved wet adhesion properties is conferred by incorporation of the selected ureido compounds is formulated as follows. 
     EXAMPLE 4 
     To a reaction vessel there were added: 
     
         ______________________________________                                    
                 pbw                                                      
______________________________________                                    
Igepal CO 887      61                                                     
Igepal CO 630      31.3                                                   
Fe.sup.++          trace                                                  
Water              935.8                                                  
______________________________________                                    
 
    
     The contents of the vessel were stirred at 120 rpm and heated to 65° C. under a nitrogen purge. There were then added to the reaction vessel over a two hour period, three delays, as follows: 
     
         ______________________________________                                    
Delay 1                pbw                                                
______________________________________                                    
Ethyl acrylate         480                                                
Methyl Methacrylate    320                                                
t-butyl hydroperoxide (70%)                                               
                       1.4                                                
Delay 2                                                                   
Sodium formaldehyde sulfoxylate                                           
                       1.5                                                
Sodium benzoate        1.1                                                
Deionized water        48.5                                               
Delay 3                                                                   
Ureido compound III(a) 8.0                                                
Deionized water        92                                                 
______________________________________                                    
 
    
     The polymerization temperature was maintained at 65°- 66° C. with a cooling jacket temperature of 60° C. At the end of the delays, there was added to the emulsion 2.0 parts of sodium formaldehyde sulfoxylate and 1 part of t-butyl hydroperoxide mixed with 10 parts water. The obtained emulsion had 44.4% solids and a pH of 5.1. 
     The foregoing emulsion put into a standard semi-gloss paint formulation, passed the cut film wet adhesion test described below. 
     The cut film test employed is a standard procedure for testing wet adhesion to a surface of semi-gloss paint as set out in Federal Specification TT-P-001511, paragraph 4.3.9 (GSA-FSS). In this test a panel is painted with an alkyd enamel of specified composition and permitted to dry under specified conditions. The test paint is then applied over the alkyd surface and dried. A cut is then made longitudinally through the center of the test film and the panel scrubbed under water at a specified rate of brush travel. To pass this test, there must be no loss of adhesion between the test paint and the alkyd undercoat and no wearing through to the undercoat in fewer than 5,000 cycles. 
     In the recut test, a second cut is made perpendicular to the first on the test film. The board is subject to an additional 1000 cycles of under water brushing. 
     In the &#34;floating board&#34; the composition to be tested is applied over a dry glossy alkyd-painted plane board surface and dried. A one-inch section of the surface is scored by cross-hatching with parallel cuts vertical and horizontal 1/10-1/8 inch apart. An adhesive tape is applied to the dry scored surface and the relative amounts of the surface film peeled off by the adhesive observed. The board is again similarly scored and then floated face down on a water bath to wet the scored surface and the adhesive tape procedure repeated, again observing the amount of painted surface removed. 
     A representative number of ureido compounds were each incorporated into an emulsion system for testing of wet adhesion properties. The systems tested contained 0.75% of the ureido compound. Other amido compounds were also included in these tests as well as a control free of additive. 
     The results of the tests are shown in Tables 1 and 2  below, respectively, on the cut film and floating board tests. 
     The emulsion systems employed in all of the tests reported in Tables 1 and 2 were similarly prepared except for the particular ureido or amido compound employed to determine its properties for conferring improved wet adhesion to the paint composition into which the emulsion was incorporated. 
     The emulsion systems were prepared by mixing in a reaction vessel, a seed emulsion composed of: 
     
         ______________________________________                                    
                         pbw                                              
______________________________________                                    
(g)  FLEXBOND.sup.® 325 (55% solids)                                  
                               91.                                        
     Natrosal 25.0 LR (hydroxy-ethyl cellulose)                           
                               0.89                                       
     Fe.sup.++                 trace                                      
     Deionized water           539.                                       
______________________________________                                    
 (g) A copolymer emulsion prepared from 86 parts vinyl acetate, 14 parts  
 butyl acrylate, stabilized with hydroxyethyl cellulose.                  
 
    
     The reactants were agitated at 200 RPM and heated to 65° C. while purging with nitrogen. There were simultaneously delayed to the emulsion seed over a 2 hour period, the following: 
     
         ______________________________________                                    
                    pbw                                                   
______________________________________                                    
Vinyl acetate         868.                                                
n-Butyl acrylate      97.                                                 
Igepal CO 887         15.                                                 
Igepal CO 630         10.5                                                
Pluronic F 68         15.5                                                
Pluronic L 64         15.5                                                
t-Butyl hydroperoxide (70%)                                               
                      1.4                                                 
______________________________________                                    
 
    
     Followed by a solution composed of 
     
         ______________________________________                                    
Uredio or amide compound                                                  
                   0.75% by weight                                        
being tested       of monomers                                            
Deionized water    200 parts                                              
______________________________________                                    
 
    
     The polymerization temperature was maintained at 65° C. using an activator solution consisting of 
     
         ______________________________________                                    
                  pbw                                                     
______________________________________                                    
Discolite PEA       0.4                                                   
Sodium benzoate     1.1                                                   
Deionized water     16.4                                                  
______________________________________                                    
 
    
     The vinyl acetate free monomer content was kept between 3- 5% throughout the polymerization with a jacket temperature between 53°-65° C. At the end of the delays, and when the vinyl acetate-free monomer content was below 0.5%, the emulsion was cooled. The final pH was 5.1 and solids content were 55.6%. 
     
                       TABLE 1                                                     
______________________________________                                    
               Cut Film                                                   
                 1st cut     Recut                                        
Test Compound    5000 cycles 1000 cycles                                  
______________________________________                                    
N-allyl urea     Pass        Pass                                         
Allyl carbamate  Fails after 250                                          
                             Fails at 340                                 
B-Allyloxy propionamide                                                   
                 Fails at 100                                             
                             Fails at 239                                 
Compound of Formula IIIc                                                  
                 Pass        Pass                                         
Compound of Formula IIId                                                  
                 Fail        Pass                                         
N-carbamyl maleamic acid                                                  
                 Fail        --                                           
Compound of formula IVa                                                   
                 Pass        Pass                                         
Compound of formula IVc                                                   
                 Pass        Pass                                         
3-butenamide     Fail        --                                           
N-carboallyloxy urea                                                      
                 Fail        --                                           
N-carboallyloxy ethylene                                                  
                 Fails       --                                           
urea                                                                      
N-(allyloxyacetyl)ethylene                                                
                 Fails       --                                           
urea                                                                      
Control (no additive)                                                     
                 Completely  Fails at                                     
                 stripped    100 cycles                                   
______________________________________                                    
 
    
     
                       TABLE 2                                                     
______________________________________                                    
               FLOATING BOARD                                             
                 % Removal   % Removal                                    
Test compound    wet         dry                                          
______________________________________                                    
N-allyl urea     0           0                                            
Allyl carbamate  26          4                                            
B-Allyloxy propionamide                                                   
                 98          0                                            
Compound of Formula IIIc                                                  
                 1           0                                            
Compound of Formula IIId                                                  
                 98          7                                            
N-carbamyl maleamic acid                                                  
                 82          1                                            
Compound of Formula IVa                                                   
                 8           10                                           
Compound of Formula VIc                                                   
                 16          4                                            
3-buteneamide    5           1                                            
Control          100         80                                           
______________________________________                                    
 
    
     While the compound of Formula III(d) failed to pass the 5000  cycle wet adhesion test, it did pass the 1000 cycle recut test, and therefore showed significant improvement over the control which failed both of these tests. 
     The novel ureido monomers of the invention can be incorporated into aqueous paint or coating formulations by interpolymerization in emulsions comprising acrylates or methacrylates, or in emulsions comprising vinyl ester systems which may contain one or more other unsaturated monomers. Thus, such systems may comprise vinyl acetate alone or in admixture with one or more monomers from among ethylene, vinyl chloride, maleic acid, and alkyl esters of acrylic, methacrylic and maleic acids. Such emulsion systems generally comprise, in addition to the polymerizable monomer or monomers, free radical initiators and emulsifying, stabilizing, and surface active agents. Preferably, the activator comprises a redox system, typically made up of a peroxide or persulfate catalyst and a reducing component, such as an alkali metal formaldehyde bisulfite or sulfoxylate. The principal emulsifying agent is preferably one of the nonionic type and may also include surface agents of the anionic type. 
     The novel ureido compounds of the invention, added to water-based flat exterior paints also impart improved resistance to blistering.