Piezoelectric ceramic compounds
BACKGROUND OF THE INVENTION 
     This invention relates to piezoelectric ceramic compounds consisting of ternary system piezoelectric ceramic compounds PbTiO 3  -PbZrO 3  -La(Mn 1-1 α Ni 3 α W.sub.α)O 3  in which lanthanum manganate-nickelate-tungstate La(Mn 1-4 α Ni 3 α W.sub.α) O 3  is solid-soluted in a binary system piezoelectric ceramic compound of lead titanate-zirconate PbTiO 3  -PbZrO 3 . 
     In the prior art of piezoelectric ceramic compounds, compounds consisting of a binary system piezoelectric ceramic compound of lead titanate-zirconate PbTiO 3  -PbZrO 3  and niobium added thereto are known. Although these compounds have a relatively high specific resistivity of 10 13  to 10 14  Ω cm, secular variation of the electrical properties of these compounds is not small enough. In general, it is recognized that the secular variation of the electrical properties of a piezoelectric ceramic compound depends upon an absolute amount of inner space charge and the manner of transmission of inner space charge of the piezeoelectric compound. In a piezoelectric ceramic compound having a large specific resistivity, since the transmission of inner space charge is effected slowly, it is difficult to realize a stable distribution of a charge in a short period of time. Thus, piezoelectric ceramic compounds having a high specific resistivity do not have a satisfactory property from the viewpoint of secular variation. Accordingly, it is not always advantageous that a piezoelectric ceramic compound has a high specific resistivity. However, there has been a problem in that it is difficult to realize simultaneously a reduction of specific resistivity, a reduction of secular variation of electrical properties, and an improvement of piezoelectric properties such as the mechanical quality factor Q M  of a piezoelectric ceramic compound, because the reduction of specific resistivity and inner specific charge cause to deteriorate the mechanical quality factor Q M . 
     Also, in another prior art of piezoelectric ceramic compounds, compounds consisting of a binary system piezoelectric ceramic compound of lead titanate-zirconate PbTiO 3  -PbZrO 3  and chromium added thereto are known. Although these compounds have a relatively small specific resistivity and have a satisfactory property from the viewpoint of secular variation, it is difficult to obtain a compound having high mechanical quality factor Q M . Also in the case of these compounds, there have been problems in that it is difficult to realize simultaneously a reduction of specific resistivity, a reduction of secular variation of electrical properties, and an increase of the mechanical quality factor Q M  of a piezoelectric ceramic compound. 
     SUMMARY OF THE INVENTION 
     It is an object of the present invention to provide piezoelectric ceramic compounds, the theoretical density ratio of which is large, crystal structure of which is dense, the secular change of electrical properties such as resonance frequency is small, the mechanical factor Q M  is above a predetermined value, and the temperature coefficient of resonance frequency of which is small over a wide range of temperature, by selecting the composition of piezoelectric ceramic compounds having the molecular formula La(Mn 1-4 α -Ni 3 α W.sub.α)O 3  -PbTiO 3  -PbZrO 3 . 
     The piezoelectric ceramic compounds in accordance with the present invention are suitable for piezoelectric filters, particularly piezoelectric filters in communication devices and filters of the elastic surface wave type, as well as for ultrasonic devices and sensing devices. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     FIG. 1 shows a ternary diagram explaining the range of composition of piezoelectric ceramic compounds in accordance with the present invention, 
     FIG. 2 shows a graph explaining the changes of lattice constant of a crystal, 
     FIGS. 3A, 3B and 3C illustrate electron microscopic photographs revealing the difference of crystal grain growth by changing the α value in the formula, 
     FIGS. 4A and 4B illustrate electron microscopic photographs revealing the surfaces of compounds in accordance with a prior art and the present invention, respectively, 
     FIG. 5 is a graph showing the changes of density of piezoelectric ceramic compounds in accordance with the present invention, 
     FIG. 6 is a graph showing the changes of dielectric constant and electro-mechanical coupling coefficient of piezoelectric ceramic compounds in accordance with the present invention, 
     FIG. 7 is a graph showing the changes of mechanical quality factor of the piezoelectric ceramic compounds in accordance with the present invention, 
     FIG. 8 is a graph showing the changes of specific resistivity, electro-mechanical coupling coefficient, relative dielectric constant and mechanical quality factor, and, 
     FIG. 9 is a graph showing the changes of temperature coefficient of piezoelectric ceramic compounds. 
    
    
     PREFERRED EMBODIMENTS OF THE INVENTION 
     Piezoelectric ceramic compounds in accordance with the present invention are produced by means of a powder metallurgical process from oxide materials and the like. An example of such process is described in the following. PbO or Pb 3  O 4 , La 2  O 3 , NiO, WO 3 , MnO 2 , TiO 2 , ZrO 2  ; a hydroxide, or; a carbonate and the like weighed and mixed in water in a ball-mill for 24 hours so as to produce one of the compositions of sample Nos. 1 through 85 of List 1. The mixed material is calcinated at a temperature range of from 800° C. to 850° C. for 2 hours, then is powdered by means of a ball-mill for a period of from 20 hours to 30 hour with a predetermined amount of organic binding agents which are dissolved in water, then is dried, and then meshed through grade 60 Mesh. The product as produced in accordance with the above described process is pressed and shaped into a disc 20 mm in diameter and 2 mm in thickness, and sintered into a piezoelectric ceramic compound at a temperature range of from 1110° C. to 1230° C. for a period of from 2 hours to 4 hours. This sintering temperature is lower than the prior art sintering temperature of approximately 1300° C. Accordingly, the vaporization of lead oxide in the composition is reduced. The piezoelectric ceramic compound disc thus produced is ground into the thickness of 1 mm, then a pair of silver electrodes is printed on both planes of the disc, and then the disc is polarized by a direct current voltage gradient of 3 KV/mm through 4 KV/mm in silicone oil in a temperature range of from 80° C. to 150° C. 
     List 1 shows the main properties of Sample Nos. 1 through 85, each of which is produced with a predetermined composition under appropriate conditions in the production process. The main properties include a sintering temperature in °C, electro-mechanical coupling coefficient Kp in %, relative dielectric constant ε 33   T  /εo and mechanical quality factor Q M . 
     
                                           List 1                                  
__________________________________________________________________________
                          Electro-                                        
                          Mechanical                                      
                                Relative                                  
                                      Mechanical                          
Sample                                                                    
    Composition (Molar Fraction)                                          
                   Sintering                                              
                          Coupling                                        
                                Dielectric                                
                                      Quality                             
No. x   y   z  α                                                    
                   Temperature                                            
                          Coefficient                                     
                                Constant                                  
                                      Factor                              
__________________________________________________________________________
1   0.005                                                                 
        0.565                                                             
            0.43                                                          
               3/40                                                       
                   1180   30    450   1650                                
(A)                                                                       
2   0.005                                                                 
        0.295                                                             
            0.70                                                          
               3/40                                                       
                   1180   25    230   1880                                
(B)                                                                       
3   0.05                                                                  
        0.25                                                              
            0.70                                                          
               3/40                                                       
                   1140   29.5  430   1850                                
(C)                                                                       
4   0.10                                                                  
        0.30                                                              
            0.60                                                          
               3/40                                                       
                   1120   27    850   680                                 
(D)                                                                       
5   0.10                                                                  
        0.45                                                              
            0.45                                                          
               3/40                                                       
                   1120   31    1750  780                                 
(E)                                                                       
6   0.08                                                                  
        0.51                                                              
            0.41                                                          
               3/40                                                       
                   1140   30    1470  1050                                
(F)                                                                       
7   0.05                                                                  
        0.55                                                              
            0.40                                                          
               3/40                                                       
                   1150   35.5  880   1330                                
(G)                                                                       
8   0.05                                                                  
        0.47                                                              
            0.48                                                          
               3/40                                                       
                   1130   48    1400  1200                                
9   0.05                                                                  
        0.47                                                              
            0.48                                                          
               4/40                                                       
                   1150   49.5  1410  1225                                
10  0.05                                                                  
        0.47                                                              
            0.48                                                          
               5/40                                                       
                   1150   51    1420  1165                                
11  0.05                                                                  
        0.47                                                              
            0.48                                                          
               8/40                                                       
                   1180   53.5  1680  1000                                
12  0.05                                                                  
        0.47                                                              
            0.48                                                          
               10/40                                                      
                   1210   48.5  1250  300                                 
13  0.04                                                                  
        0.49                                                              
            0.47                                                          
               3/40                                                       
                   1160   46.5  1200  1350                                
14  0.04                                                                  
        0.49                                                              
            0.47                                                          
               4/40                                                       
                   1160   48.5  1250  1450                                
15  0.04                                                                  
        0.49                                                              
            0.47                                                          
               5/40                                                       
                   1160   50.5  1300  1520                                
16  0.04                                                                  
        0.49                                                              
            0.47                                                          
               8/40                                                       
                   1180   47    1260  1280                                
17  0.04                                                                  
        0.49                                                              
            0.47                                                          
               10/40                                                      
                   1230   44    1190  355                                 
18  0.025                                                                 
        0.495                                                             
            0.48                                                          
               0   1160   40    950   900                                 
19  0.025                                                                 
        0.495                                                             
            0.48                                                          
               1/40                                                       
                   1160   42    980   1100                                
20  0.025                                                                 
        0.495                                                             
            0.48                                                          
               2/40                                                       
                   1170   44    1070  1300                                
21  0.025                                                                 
        0.495                                                             
            0.48                                                          
               3/40                                                       
                   1170   45.5  1110  1600                                
22  0.025                                                                 
        0.495                                                             
            0.48                                                          
               4/40                                                       
                   1170   47.5  1150  1730                                
23  0.025                                                                 
        0.495                                                             
            0.48                                                          
               5/40                                                       
                   1170   49.5  1200  1680                                
24  0.025                                                                 
        0.495                                                             
            0.48                                                          
               6/40                                                       
                   1170   52    1230  1580                                
25  0.025                                                                 
        0.495                                                             
            0.48                                                          
               7/40                                                       
                   1170   54    1250  1500                                
26  0.025                                                                 
        0.495                                                             
            0.48                                                          
               8/40                                                       
                   1190   52    1200  1380                                
27  0.025                                                                 
        0.495                                                             
            0.48                                                          
               9/40                                                       
                   1190   48    1100  900                                 
28  0.025                                                                 
        0.495                                                             
            0.48                                                          
               10/40                                                      
                   1230   46    950   400                                 
29  0.05                                                                  
        0.45                                                              
            0.50                                                          
               3/40                                                       
                   1140   53.5  1400  665                                 
30  0.05                                                                  
        0.45                                                              
            0.50                                                          
               4/40                                                       
                   1150   57    1500  720                                 
31  0.05                                                                  
        0.45                                                              
            0.50                                                          
               5/40                                                       
                   1150   60    1650  790                                 
32  0.05                                                                  
        0.45                                                              
            0.50                                                          
               8/40                                                       
                   1160   60    1900  1000                                
33  0.05                                                                  
        0.45                                                              
            0.50                                                          
               10/40                                                      
                   1180   57    1700  250                                 
34  0.07                                                                  
        0.43                                                              
            0.50                                                          
               3/40                                                       
                   1110   46    1800  600                                 
35  0.07                                                                  
        0.43                                                              
            0.50                                                          
               4/40                                                       
                   1130   46.5  1700  680                                 
36  0.07                                                                  
        0.43                                                              
            0.50                                                          
               5/40                                                       
                   1130   46.5  1550  780                                 
37  0.07                                                                  
        0.43                                                              
            0.50                                                          
               8/40                                                       
                   1150   51.5  1800  970                                 
38  0.07                                                                  
        0.43                                                              
            0.50                                                          
               10/40                                                      
                   1170   47    1550  400                                 
39  0.02                                                                  
        0.47                                                              
            0.51                                                          
               3/40                                                       
                   1170   61    1260  1200                                
40  0.02                                                                  
        0.47                                                              
            0.51                                                          
               4/40                                                       
                   1170   65    1275  1350                                
41  0.02                                                                  
        0.47                                                              
            0.51                                                          
               5/40                                                       
                   1170   61    1290  1280                                
42  0.02                                                                  
        0.47                                                              
            0.51                                                          
               8/40                                                       
                   1190   59.5  1320  1250                                
43  0.02                                                                  
        0.47                                                              
            0.51                                                          
               10/40                                                      
                   1230   57    1300  200                                 
44  0.03                                                                  
        0.45                                                              
            0.52                                                          
               3/40                                                       
                   1170   68    800   750                                 
45  0.03                                                                  
        0.45                                                              
            0.52                                                          
               4/40                                                       
                   1170   70    935   700                                 
46  0.03                                                                  
        0.45                                                              
            0.52                                                          
               5/40                                                       
                   1170   71    990   650                                 
47  0.03                                                                  
        0.45                                                              
            0.52                                                          
               8/40                                                       
                   1190   72.5  1170  450                                 
48  0.03                                                                  
        0.45                                                              
            0.52                                                          
               10/40                                                      
                   1230   69    1050  180                                 
49  0.02                                                                  
        0.52                                                              
            0.46                                                          
               3/40                                                       
                   1170   43    800   2350                                
50  0.02                                                                  
        0.52                                                              
            0.46                                                          
               4/40                                                       
                   1170   47.5  820   2400                                
51  0.02                                                                  
        0.52                                                              
            0.46                                                          
               5/40                                                       
                   1180   49.5  850   2300                                
52  0.02                                                                  
        0.52                                                              
            0.46                                                          
               8/40                                                       
                   1180   41.5  885   1760                                
53  0.02                                                                  
        0.52                                                              
            0.46                                                          
               10/40                                                      
                   1210   37    790   350                                 
54  0.03                                                                  
        0.35                                                              
            0.62                                                          
               3/40                                                       
                   1150   38    400   2500                                
55  0.03                                                                  
        0.35                                                              
            0.62                                                          
               4/40                                                       
                   1160   39.5  390   2650                                
56  0.03                                                                  
        0.35                                                              
            0.62                                                          
               5/40                                                       
                   1160   42    385   2650                                
57  0.03                                                                  
        0.35                                                              
            0.62                                                          
               8/40                                                       
                   1160   38.5  380   2300                                
58  0.03                                                                  
        0.35                                                              
            0.62                                                          
               10/40                                                      
                   1180   36    370   550                                 
59  0.03                                                                  
        0.53                                                              
            0.44                                                          
               3/40                                                       
                   1170   42.5  800   1900                                
60  0.03                                                                  
        0.51                                                              
            0.46                                                          
               3/40                                                       
                   1170   44.5  890   1850                                
61  0.03                                                                  
        0.50                                                              
            0.47                                                          
               3/40                                                       
                   1170   50    995   1750                                
62  0.03                                                                  
        0.49                                                              
            0.48                                                          
               3/40                                                       
                   1170   52.5  1110  1600                                
63  0.03                                                                  
        0.47                                                              
            0.50                                                          
               3/40                                                       
                   1170   65    1380  1280                                
64  0.03                                                                  
        0.46                                                              
            0.51                                                          
               3/40                                                       
                   1170   70    1510  1050                                
65  0.02                                                                  
        0.54                                                              
            0.44                                                          
               3/40                                                       
                   1170   40    640   2150                                
66  0.01                                                                  
        0.51                                                              
            0.48                                                          
               3/40                                                       
                   1190   41.5  855   1550                                
67  0.05                                                                  
        0.50                                                              
            0.45                                                          
               3/40                                                       
                   1150   43    1175  1280                                
68  0.07                                                                  
        0.47                                                              
            0.46                                                          
               3/40                                                       
                   1130   39.5  1580  1050                                
69  0.02                                                                  
        0.46                                                              
            0.52                                                          
               3/40                                                       
                   1180   64.5  720   1200                                
70  0.03                                                                  
        0.42                                                              
            0.55                                                          
               3/40                                                       
                   1170   53.5  690   1280                                
71  0.03                                                                  
        0.39                                                              
            0.58                                                          
               3/40                                                       
                   1170   46    475   1590                                
72  0.05                                                                  
        0.43                                                              
            0.52                                                          
               3/40                                                       
                   1150   63.5  1500  650                                 
73  0.05                                                                  
        0.43                                                              
            0.52                                                          
               5/40                                                       
                   1150   64.5  1950  530                                 
74  0.05                                                                  
        0.43                                                              
            0.52                                                          
               8/40                                                       
                   1160   63.5  1800  620                                 
75  0.05                                                                  
        0.43                                                              
            0.52                                                          
               10/40                                                      
                   1170   62    1700  750                                 
76  0.03                                                                  
        0.33                                                              
            0.64                                                          
               3/40                                                       
                   1170   36    375   2850                                
77  0.03                                                                  
        0.31                                                              
            0.66                                                          
               3/40                                                       
                   1170   34    360   3150                                
78  0.03                                                                  
        0.29                                                              
            0.68                                                          
               3/40                                                       
                   1170   32    350   3500                                
79  0.05                                                                  
        0.35                                                              
            0.60                                                          
               3/40                                                       
                   1160   38.5  495   1480                                
80  0.05                                                                  
        0.30                                                              
            0.65                                                          
               3/40                                                       
                   1150   32    450   2000                                
81  0.07                                                                  
        0.38                                                              
            0.55                                                          
               3/40                                                       
                   1130   44    870   1050                                
82  0.07                                                                  
        0.35                                                              
            0.58                                                          
               3/40                                                       
                   1130   38.5  720   1250                                
83  0.07                                                                  
        0.40                                                              
            0.53                                                          
               3/40                                                       
                   1130   47    1250  730                                 
84  0.09                                                                  
        0.39                                                              
            0.52                                                          
               3/40                                                       
                   1110   39.5  2050  480                                 
85  0.09                                                                  
        0.36                                                              
            0.55                                                          
               3/40                                                       
                   1110   39.5  1100  650                                 
__________________________________________________________________________
 
    
     The range defined by the points A, B, C, D, E, F and G, is illustrated in the ternary diagram of FIG. 1. The points A, B, C, D, E, F and G correspond to Sample Nos. 1, 2, 3, 4, 5, 6 and 7, respectively. 
     It has been confirmed that La(Mn 1-4 α Ni 3 α W.sub.α)O 3 , which is the third component of piezoelectric ceramic compounds in accordance with the present invention, has a cubic perovskite structure of a crystal where α is 10/40 to 2/40 and is easily synthesized by means of sintering in the air. As shown in FIG. 2 which illustrates the changes of the lattice constant of a crystal of A +3  B +3  O 3  type in the B site of which an appropriate amount of Mn is solid-soluted, the change of the lattice constant is small and the structure of the crystal is dense when the value of α is approximately from 7/40 to 2/40. In addition, when the value of α is in the above mentioned range, it has been found the crystalization is excellent by means of X-ray diffraction, and it is easy to effect the solid-solution into PbTiO 3  -PbZrO 3 . However, when the value of α is below 2/40, it is difficult to effect the sintering in air, and the crystal is in the state of mixed crystal, and accordingly, is not in perfect form. In FIG. 2, it should be noted that the value corresponding to α=0 is obtained in accordance with a vacuum sintering process at 1020° C. 
     It has been found that, if La(Mn 1-4 α Ni 3 α W.sub.α)O 3  having a semiconductive cubic perovskite type structure is solid-soluted with PbTiO 3  -PbZrO 3 , the solid-solution is effected at a relatively low temperature range of approximately from 1110° C. to 1230° C., and a product having an excellent crystalising property, a high sintering property, and a tight structure is produced. Therefore, it has been found that it is possible to realize the mass production of stable piezoelectric ceramic compounds in which the vaporization of lead oxide is small. 
     FIG. 3A, 3B and 3C illustrate photographs revealing the surface status of a crystal of 0.03La(Mn 1-4 α Ni 3 α W.sub.α)O 3  +0.96Pb(Ti y  Zr 1-y )O 3  dependent on the value of α. FIGS. 3A, 3B and 3C correspond to α=10/40, α=5/40 and α=0, respectively. Although photographs of FIGS. 3A, 3B and 3C were taken under the condition y=50, similar photographs have been taken even in the case where the value of y is changed. It is observed in FIGS. 3A, 3B and 3C that: a piezoelectric ceramic compound having a uniformity in structure and high density property is formed where the value of α is approximately 5/40; that an anomalous growth appears in the crystal and the density of the ceramics is decreased in accordance with the reduction of the value of α, and; that although no anomalous growth appears in the crystal, the sintering property is deteriorated, the pore eliminating effect is decreased and accordingly pores become distinguished where the value of α is approximately  10/40. It should be noted that the properties of the structures illustrated in FIGS. 3A are superior to those of the prior art structure of PbTiO 3  -PbZrO 3 , though they are more or less inferior to those illustrated in FIG. 3B. As a result, the value of the molar fraction α of (Mn 1-4 α Ni 3 α W.sub.α) ion should be selected in the range of 3/40≦α≦10/40. 
     FIGS. 4A and 4B illustrate photographs of the structure of: 
     
         0.10Pb(Fe.sub.1/5 Ni.sub.1/5 Nb.sub.3/5)O.sub.3 +0.90Pb(Ti.sub.y Zr.sub.1-y)O.sub.3 
    
     which is a prior art ternery system piezoelectric ceramic compound and the structure of: 
     
         0.03La(Mn.sub.1/2 Ni.sub.3/8 W.sub.1/8)O.sub.3 +0.97Pb(Ti.sub.y Zr.sub.1-y)O.sub.3 
    
     which is an example of the structure in accordance with the present invention, respectively. Although photographs of FIGS. 4A and 4B were taken under the condition y=50, similar photographs have been taken even in the case where the value of y is changed. It is observed in FIGS. 4A and 4B that pores are eminently decreased, and the sintering property is excellent in the structure in accordance with the present invention. 
     FIG. 5 shows the apparent density of 0.025 La (Mn 1-4 α Ni 3 α W.sub.α)O 3  +0.495PbTiO 3  +0.48PbZrO 3  which is an example of the composition in accordance with the present invention. In FIG. 5, De shows the experimental value density and Dt shows the theoretical value density calculated from the lattice constant obtained by means of the X-ray diffraction. The experimental value density De is 7.93 g/cm 3 , and the theoretical density ratio De/Dt is 98% where the value of α is approximately 7/40. It has been very difficult to gain such a high value of the theoretical density ratio by means of the normal sintering process for ternary system piezoelectric ceramic compounds. In accordance with the present invention, the compounds having the theoretical density ratio of greater than 97% are easily obtained in the range of 3/40≦α≦10/40. These values of the theoretical density ratio in accordance with the present invention are better than either the value from 93% to 95% for the prior art PbTiO 3  -PbZrO 3  structure or the value from 94% to 96% for another prior art PbTiO 3  -PbZrO 3  structure having the solid-soluted third component. Samples, which are used for density measurement shown in FIG. 5, are produced in accordance with the above described production process without a polarizing treatment and are formed in the shape of a plate, the plane of which is a square of 20 mm and the thickness of which is 2 mm. The measurements are conducted in accordance with Archimedes method at 23° C. 
     In order to explain the electro-mechanical coupling coefficient Kp in connection with the present invention, List 1 is again referred to. Within the range defined by the points A, B, C, D, E, F and G, said points A, B, C, D, E, F and G corresponding to Sample Nos. 1, 2, 3, 4, 5, 6 and 7 of List 1, respectively, the compounds have satisfactory values of the electro-mechanical coupling coefficient Kp which are not less than 25%. It is required that, in the case of the contour vibrations in general, the Kp should be at least not less than 20%. In addition, the inventors have confirmed by experiments that the values of Kp do not reach to 25% outside of the range defined by A, B, C, D, E, F and G in List 1. 
     The reason for the limitation of molar fraction of the third component within 10 mol.% is explained as follows. If the molar fraction of the third component is greater than 10 mol%, i.e. if the composition is in the range over the line D-E in FIG. 1, an anomalous growth of crystal grains takes place, the Curie Temperature is lowered, the realization of uniformity in structures and high density property becomes difficult, and accordingly, the practicality of compounds is reduced. 
     In FIG. 6, the relative dielectric constant (ε 33hu  T /εo) is shown in broken lines and the electro-mechanical coupling coefficient is shown in solid lines with respect to the range A-B-C-D-E-F-G in FIG. 1. In FIG. 6, it is observed that the morphotrophic phase boundary (MP B) inclines to the rhombohedral (Rhomb) side and electro-mechanical coupling coefficients (Kp) in the region of the rhombohedral system show a relatively large value, though relative dielectric constants (ε 33   T  /εo) show reduced values in the same region. Since there is a need for piezoelectric ceramic compounds having a low relative dielectric constant and a high electro-mechanical coupling coefficient for high frequency piezoelectric filters such as energy trapped type high frequency piezoelectric filters and elastic surface wave devices, the compositions in the region of the rhombohedral system in accordance with the present invention are useful for high frequency piezoelectric filters and elastic surface wave devices. 
     In FIG. 7, the mechanical quality factor Q M  is shown with respect to the range A-B-C-D-E-F-G in FIG. 1. In FIG. 7, it is observed that the values of the mechanical quality factors are high in a wide range within the regions of the rhombohedral system and tetragonal system. 
     In FIG. 8, the changes of the relative dielectric constant ε 33   %  /εo, electromechanical coupling coefficient Kp, mechanical quality factor Q M  and specific resistivity ρ of Sample Nos. 18 through 28 in accordance with the change of molar fraction α of the third component La (Mn 1-4 α Ni 3 α W.sub.α)O 3  at a point in the region of tetragonal system which is 3 mol.% apart from the morphotrophic phase boundary (MPB) point are shown. In FIG. 8, it is observed that the electro-mechanical coupling coefficient Kp shows its maximum value at α=7/40 at which point the theoretical density ratio also shows its maximum values as explained hereinbefore with reference to FIG. 5. Thus, the electro-mechanical coupling coefficient and the theoretical density ratio are quite high where the value of α is around 7/40. In addition, in FIG. 8, it is observed that the mechanical quality factor Q M  is greater than 1700 and the electro-mechanical coupling coefficient Kp is greater than 47%, though the specific resistivity ρ is decreased to not greater than 10 11  Ωcm, at α=4/40. Thus, the compound also has the properties suitable for piezoelectric filters where the value of α is around 4/40. 
     
                                           List 2                                  
__________________________________________________________________________
                  Theoretical                                             
                        Density                                           
                  Density                                                 
                        of    Theoretical                                 
                                    Mechanical                            
Sample                                                                    
    Specific Secular                                                      
                  by X-ray                                                
                        Sintered                                          
                              Density                                     
                                    Quality                               
No. Resistivity                                                           
          tan δ                                                     
             Variation                                                    
                  Diffraction                                             
                        Compound                                          
                              Ratio Factor                                
__________________________________________________________________________
18  1.3   1.2                                                             
             0.03 8.078 7.65  94.7  900                                   
19  3.5   0.9                                                             
             0.03 8.080 7.70  95.3  1100                                  
20  5.4   0.7                                                             
             0.04 8.082 7.77  96.1  1300                                  
21  7.5   0.6                                                             
             0.06 8.084 7.82  96.7  1600                                  
22  11.0  0.4                                                             
             0.12 8.087 7.88  97.4  1730                                  
23  18.0  0.3                                                             
             0.25 8.089 7.90  97.7  1680                                  
24  19.5  0.2                                                             
             0.38 8.091 7.91  97.8  1580                                  
25  18.2  0.3                                                             
             0.45 8.093 7.935 98.0  1500                                  
26  16.7  0.3                                                             
             0.40 8.095 7.90  97.6  1380                                  
27  15.8  0.5                                                             
             0.37 8.097 7.88  97.3  900                                   
28  14.9  0.7                                                             
             0.27 8.10  7.85  96.9  400                                   
__________________________________________________________________________
 
    
     List 2 shows the secular variation of properties of Sample Nos. 18 through 28 which are calculated as change per 10 years in %. The columns of List 2 are arranged by Sample Number, specific resistivity (×10 11  Ωcm), tan ρ (%), change per 10 years (%) of resonance frequency the initial value of which is the value at 24 hours after polarizing treatment (fr), tehoretical density by X-ray diffraction (g/cm 3 ), density of the sintered compound (g/cm 3 ), theoretical density ratio (%) and mechanical quality factor. 
     In List 2, it is observed that the value of the secular variation of the resonance frequency is an excellent value of 0.12% per 10 years with regard to Sample No. 22 where Q M  takes its maximum value and α is 4/40. In addition, the values of the secular variation of the resonance frequency are also advantageous values in the region of the rhombohedral system. For piezoelectric filters, it is required that the secular variation should be smaller than 1% per 10 years. Partiuclarly for piezoelectric filters in communication devices and the elastic surface wave devices, it is requred that the secular variation should be much smaller than in the above described case. In connection with these requirements, in List 2, it is observed that Sample Nos. 21 through 28 have a value greater than 1500 of the mechanical quality factor Q M  and a value smaller than 0.5% per 10 years of secular variation of resonance frequency and are accordingly suitable for the above-mentioned piezoelectric filters, piezoelectric filters in communication devices, and the elastic surface wave devices. 
     List 3 shows temperature coefficients of Sample Nos. 44, and 59 through 64. The temperature coefficient is one of the important properties of piezoelectric ceramic compounds used for piezoelectric filters. In List 3, the variation of resonance frequency Δ fr/fr(%) at -20° C., the variation of resonance frequency Δ fr/fr(%) at 80° C., the temperature coefficient of resonance frequency C f  (ppm/°C.) at -20° C. and the temperature coefficient of resonance frequency C f  (pm/°C.) at 80° C., where fr is the resonance frequency at 25° C., are shown. It should be noted that Δ fr at =20° C. is calculated as fr at 25° C. minus fr at -20° C., while Δ fr at 80° C. is calculated as fr at 80° C. minus fr at 25° C. 
     
                       List 3                                                      
______________________________________                                    
Sample   .increment.fr/fr                                                 
                   .increment.fr/fr                                       
                             C.sub.f C.sub.f                              
No.      (-20° C.)                                                 
                   (80° C.)                                        
                             (-20° C.)                             
                                     (80° C.)                      
______________________________________                                    
59       -0.07     -0.13     -16     -24                                  
60       -0.02     -0.05     -4      -9                                   
61       +0.06     -0.03     +13     -5                                   
62       +0.10     +0.03     +22     +6                                   
63       +0.25     +0.22     +56     +40                                  
64       +0.19     +0.14     +42     +25                                  
44       -0.50     -0.75     -110    -135                                 
______________________________________                                    
 
    
     In List 3, it is observed that the change of resonance frequency due to temperature is relatively small in a wide range of temperatures and the change is linear and has no bend around the range where the temperature coefficient is very close to zero. 
     In FIG. 9 the variation of temperature coefficient both of the compounds in accordance with the present invention and of prior art compounds in response to the mol percent of Ti are shown. In FIG. 9, the Curve Nos. 1, 2 and 3 correspond to the following compounds. 
     
         0.97Pb(Ti.sub.x Zr.sub.1-x)O.sub.3 +0.03La(Mn.sub.7/10 Ni.sub.9/40 W.sub.3/40)O.sub.3                                        (1.) 
    
     
         Pb.sub.0.95 Sr.sub.0.05 (Ti.sub.x Zr.sub.1-x)O.sub.3       2. 
    
     
         0.98Pb(Ti.sub.x Zr.sub.1-x)O.sub.3 -0.02WO.sub.3 +0.75wt% MnO.sub.2 3.