Foamed ink composition and method of making the same
REFERENCE TO RELATED APPLICATION 
     This application is a continuation-in-part of U.S. Ser. No. 360,757 filed Mar. 22, 1982, now abandoned. 
    
    
     BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     This invention relates generally to the printing of moving webs and is concerned in particular with water-based foamable ink printing composition and a method of making the same. 
     2. Description of the Prior Art 
     The invention is especially useful in, although not limited to, the rotogravure printing of paper webs. Since its inception in the late 1800&#39;s, rotogravure printing has been carried out primarily with solvent based inks. The solvents are toxic and highly flammable, and consequently printing plant personnel are exposed continuously to potentially serious health, fire and explosion hazards. As a result, in spite of the implementation of elaborate and expensive protective measures such as for example solvent recovery and air pollution abatement systems, electrically grounded presses, shielded electric motors, etc., insurance costs remain extremely high. Moreover, because solvents are extracted from petroleum, their costs have increased dramatically during the last decade, as has the cost of the energy consumed by the dryers required to dry solvent inks after printing. 
     It has been suggested to coat or print a web of cloth, paper or the like with a water-based foamed ink. U.S. Pat. No. 2,971,458, Kumins, is believed to be the most relevant prior art. This reference teaches the foaming of water-based inks by conventional foaming devices such as mechanical mixers, followed by transfer of the foamed ink into the cells of a gravure cylinder and subsequent transfer of the foamed ink from the cells of the cylinder to a web to be printed. Further in this reference, the disclosed compositions include additives to enhance stability, but no additive is taught which is used both to enhance the mixing of the composition during foaming and to control the fluidity and stability of the ink once foamed. 
     Although this reference suggests the use of a water-based foamed ink for the printing of a moving web of paper, there presently is no economically successful commercial implementation of this suggestion. 
     SUMMARY OF THE INVENTION 
     The present invention is directed to a water-based foamable ink composition and more particularly, to a composition having physical properties which make it especially suitable for foaming and subsequent application to a gravure-type cylinder where it is doctored to convert the foam bubbles into thin discrete membranes overlying the gravure cells, with the cell volumes underlying the membranes as well as the cylinder and areas separating the cells being subsequently free of ink, thus facilitating the subsequent transfer of the membranes onto a moving paper web. The foaming step does not require the use of mechanical agitation. 
     In a preferred embodiment, the composition prior to foaming is a water-based liquid, which comprises: a pigment, a resin, a foaming agent or a blended foaming agent and a wetting agent, and, optionally, a `stabilizer` as hereinafter defined, and most importantly, a psuedoplastic additive. Additives such as fungistats, bacteriostats, etc. which impart to the web desired characteristics also may be used. 
     Broadly, the pseudoplastic additive will impart to the composition a viscosity which is reduced by a factor of between about 10 to 20,000 when mixed with a compressed gas and which imparts to the foamed ink a desired fluidity. Preferably, the pseudoplastic additive is a polysaccharride. 
     The foamable composition is mixed with a compressed gas, such as air in an expansion ratio (gas-to-formulation-ratio) of from 3 to 20, say for example, an expansion ratio of between 6 to 12 by volume. The mixing of the composition and air is effected in a chamber devoid of mechanical agitation. The gas is discharged from a nozzle. The discharge of the nozzle is in communication with a chamber and a receiver. The composition is introduced into the chamber. The gas mixes with and carries the composition from the chamber and into the receiver; the composition in the receiver nozzle having the gas dispersed therein to form a mixture. The mixture is discharged from the receiver into a foam refining tube ultimately forming a foamed ink. The foamed ink is coated onto a gravure type cylinder where it is doctored, causing the foam to be converted into thin discrete membranes of ink composition spanning the gravure cells. These membranes are ultimately brought into contact with either a moving web or another roll, causing the pigment in the ink membranes to be transferred to the web or other roll. The membrane may or may not include microbubbles, however, it is believed to be essentially a liquid film. 
     The foamed ink composition has a surface tension of between about 15 to 40 dynes cm -1  and a 25% drainage time (NFPA Std 11, 1978, p. 11-98) of between about 12 minutes to 4 hours. 
     In a particularly preferred embodiment where no `stabilizer` is used, the composition has marked fluidity with a 25% drainage time of between about 8 minutes to 1 hour. The composition on drying does not dry to a ghost foam; but rather, the foam collapses holding the liquid ink interstitially. The collapsed foam can be refoamed simply by mechanical agitation. 
    
    
     BRIEF DESCRIPTION OF THE DRAWING 
     The drawing is a side sectional view of a nozzle-mixing chamber assembly. 
    
    
     DESCRIPTION OF THE PREFERRED EMBODIMENT 
     The foamable ink composition broadly comprises a printing ink, a resin, a foaming agent and a pseudoplastic additive. Optionally foam stabilizers and/or wetting agents may be used. 
     Specific suitable and utilizable aqueous pigment dispersions are: Super Imperse Phthalo blue 2663-Ciba-Geigy, Aurasperse Diarylide Yellow W-1041, Aurasperse Barium Lithol Red W-3161, and Aurasperse Carbon Black W-7012, Harshaw Chemical Co.; Flexo PLUS Diarylide Yellow WY-7714, Flexo PLUS Barium Lithol Red WR-7749, and Flexo PLUS Phthalo Blue WB-7715, Mobay Chemical Corp.; Flexiverse Diarylide Yellow TFD-1123, Flexiverse Barium Lithol Red RFD-1135, and Flexiverse Phthalo Blue BFD-1121, Sun Chemical Corp. These pigment dispersions may be used as is, or various combinations thereof may be employed to obtain various color and shade possibilities. 
     Aqueous pigment dispersions which are commercially available with pH ranges of from about 8 to about 12 are preferred, inasmuch as such will obviate the necessity of adjusting their pH values to such a range, prior to their use. Also, the dispersions may have 30-60% solids by weight. 
     Resins that may be successfully employed in the invention are water soluble or water dispersable with the appropriate vehicle. 
     Specific utilizable resins include: Joncryl 678SC, S. C. Johnson &amp; Sons Co. (acrylic); SC 5011, Stanchem Corp. (acrylic); Rhoplex AC 33, Rohm and Haas (acrylic); CL 202, Celanese Plastic Company (polyvinylacetate latex); and Vinac ASB, Air Products &amp; Chemical Co. (pva); Cymel 200, 300, 400, 500 Series, American Cyanamide (melamine resins). These resins may be supplied as emulsions or solutions and vary from 20 to 60% solids, or in some instances may be 100% solids. 
     The foaming agent used is selected to produce a foamable ink composition which will retain its stability until coating of the foamed ink is doctored after being applied to a gravure-type cylinder, at which time the foam bubbles are converted to discrete membranes spanning the cells of the gravure cylinder. After this conversion, the cell volumes underlying the membranes as well as the cylinder land areas separating the cells are substantially free of ink, and the membranes are readily transferrable to any other surface brought into contact therewith. In rotogravure printing, this other surface will comprise one face of a moving web, whereas in flexographic printing, the other surface can comprise the surface of an intermediate transfer roll. 
     For a foaming agent any surface active agent can be used which will produce a foam having the characteristics herein described. The composition is foamed in a foaming apparatus to produce the novel foams of this invention, using air or any inert gaseous material. The amount of gas that is used to foam the composition can be as much as 20 times or as little as 3 times and is generally about 8 to 12 times the volume of the liquid formulation that is to be foamed. 
     Suitable foaming agents include the ethylene oxide adducts of the mixed C 11  to C 15  linear secondary alcohols which contain from about 10 to 50 ethyleneoxy units, preferably from about 12 to 20 ethyleneoxy units in the molecule. Also, the ethylene oxide adducts of the linear primary alcohols having from 10 to 16 carbon atoms in the alcohol moiety, or of the alkyl phenols wherein the alkyl group has from 8 to 12 carbon atoms, wherein the adducts can have from about 10 to about 50, preferably from about 12 to 20 ethyleneoxy units in the molecule. Also useful are the fatty acid alkanolamides such as coconut fatty acid monoethanolamide. Another suitable class of foaming agents is the group of sulfosuccinate ester salts, such as disodium N-octadecylsulfosuccinate, tetrasodium N-(1,2-dicarboxyethyl)-N-octadecylsulfonsuccinate, diamyl ester of sodium sulfoccinic acid, dihexylester of sodium sulfosuccinic acid, dioctyl ester sodium sulfosuccinic acid, and the like. In addition to the above nonionic and anionic surfactants one can also use a cationic surfactant or an amphoteric surfactant, N-coco-beta-aminopropionic acid (of the N-tallow or N-lauryl derivatives) or the sodium salts thereof, stearyl dimethyl benzyl ammonium chloride, the betaines or quaternized tertiary alkylamines. These are well known and any similar surfactant can be used in addition to those specifically identified above. Blends of one or more surfactants are often used to advantage. Particularly preferred foaming agents are sodium lauryl sulfate and sodium lauryl ether sulfate in a range of 0.1 to 6% solids by weight. 
     Suitable foam stabilizers are used in some of the formulas and include the higher fatty alcohols such as decyl alcohol, lauryl alcohol, tetradecyl alcohol, cetyl alcohol, oleyl alcohol and stearyl alcohol, the higher alkyl mono-ethers of etylene glycol, diethylene glycol, propylene glycol, and dipropylene glycol (such as cetyl diethylene glycol ether), fatty monoglycerides such as glycerol monolaurate and clycerol monostearate, amides such as stearic acid amide and stearic acid ethanolamide, amines such as alkyldimethylamine oxide, N-higher alkyl hydroxyalkyl carbamates such as N-dodecylhydroxyethyl carbamate, and SULFOBETAINES® such as alkyl amino propyl sulfonic acids. Preferred stabilizers are ammonium salts of the higher saturated fatty acids such as ammonium stearate, ammonium palmitate, ammonium myristate and the like. The stabilizer used may comprise from 0.1 to 10.0% by weight of the liquid composition, preferably 0.4 to 7.0%. 
     In some embodiments, a wetting agent may be used. Suitable wetting agents are the adduct of 6 moles of ethylene oxide with trimethyl nonanol, the adducts of about 7 or 9 moles of ethylene oxide with the mixed C 11  to C 15  linear secondary alcohols or with the C 11  to C 16  primary alcohols, the adduct of 9 moles of ethylene oxide with nonylphenol; the silicone wetting agents of the structure ##STR1## Also useful are the commercially available fluorocarbon wetting agents such as the known perfluoroalkyl surfactants. In some formulations, the foaming agent may also serve as the wetting agent. 
     The amount of such wetting agent to be added to provide properties of the foams will vary depending upon the particular wetting agent selected. The wetting agent used may comprise from 0.01 to 5.0 weight, preferably 0.06 to 1%. 
     An essential aspect of the invention is the use of a pseudoplastic additive such as a polysaccharide. The preferred pseudoplastic additive is heteropolysaccharride-7. This compound is disclosed in U.S. Pat. No. 3,915,800 to Kang, which patent is hereby incorporated by reference in its entirety in this disclosure. The pseudoplastic additive increases the viscosity of the liquid in the foam bubble walls thereby allowing control of drainage and foam collapse (fluidity). However, when the composition passes through a foaming device where the liquid composition is subjected to shear, the apparent viscosity of the liquid is greatly reduced due to the presence of the pseudoplastic additive. This makes possible the good flow characteristics necessary for proper foam formation. Other materials useful as pseudoplastic additives include scleroglucan gums and xantham gums. 
     The pseudoplastic material may comprise from 0.02 to 0.5% by weight of the liquid composition, preferably 0.06 to 0.20%. 
     In lieu of separate foaming agents, stabilizers and wetting agents, blended foaming agents may be used in lieu thereof, such as High Expansion Foam Concentrates of National Foam Systems, Inc. 
     The following examples of specific formulas serve to further illustrate the invention. All formulas (foamable ink compositions) were foamed with the mixing device described hereafter and illustrated in the drawing. Where indicated each foamed ink was introduced into a press fountain. The foamed ink was transferred from the press fountain and applied as a coating on the surface of a gravure-type cylinder with a rotating brush being employed to insure uniform foam application. The foam coating was doctored in order to convert the foam bubbles into thin discrete membranes of ink composition covering or spanning the cells of the cylinder while allowing the land areas between cells as well as the air volumes underlying the membranes to remain substantially free of ink. The cylinder was then brought into contact either with a moving web of paper, as in a conventional rotogravure printing process, or a transfer roll forming part of a flexographic printing apparatus, and upon contact the pigment was transferred to the paper or transfer roll, 
     Except as otherwise noted, the foamed ink was coated on a modified Helioengraved solvent cylinder. The cylinder was modified by reducing the cells 35% in depth. The details of the specific cylinder and method of application need not be described in detail in this application. 
     Certain processes and apparatus for employing the foamable ink composition of the present invention are the subject of separate applications assigned to the same assignee as that of the present invention, and such applications are hereby incorporated by reference in their entireties in this disclosure. 
     In the following examples, the phrase &#34;successfully coated&#34; means that the specific foamed ink composition was transferred either directly or indirectly onto a moving web to produce a desired pattern or coating free of streaks or skips. 
     EXAMPLE I 
     
         ______________________________________                                    
% Solids                                                                  
______________________________________                                    
10.00      pigment (1123)                                                 
10.00      resin (5011)                                                   
0.45       high expansion foam concentrate (FOAM)                         
5.00       stabilizer (STAB)                                              
0.08       wetting agent (L-7129)                                         
0.10       pseudoplastic (PP)                                             
______________________________________                                    
 pigment 1123: 100% Sunsperse Yellow YFD1123 (35% solids) Sun Chemical    
 Corp.                                                                    
 resin 5011: vinyl acrylic latex emulsion Stanchem, Inc. 5011 (55% solids)
 high expansion foam concentrate: High Expansion Foam, National Foam      
 Systems, Inc.                                                            
 stabilizer: 100%, ammonium stearate Diamond Shamrock (33% solids)        
 wetting agent: silicon surfactant L7129 Union Carbide                    
 pseudoplastic: 50% by weight Kelco K8A13 (heteropolysaccharride7) slurrie
 in 150% by weight Butyl Carbitol ® Union Carbide Corp.               
 
    
     The listed components were mixed with water resulting in a water-based formulation which was part solution, part emulsion and part slurry. The formula was foamed and successfully coated on a paper web. 
     EXAMPLE II 
     
         ______________________________________                                    
% by Weight                                                               
______________________________________                                    
38.93               water                                                 
0.07                PP                                                    
24.00               resin 5011                                            
0.30                NH.sub.4 OH                                           
28.60               pigment 1123                                          
5.00                STAB                                                  
0.40                FOAM                                                  
______________________________________                                    
 
    
     3.30% NH 4  OH was added to the above formula to adjust the pH to 10.0 and the formula foamed and successfully coated on a paper web. 
     Expansion ratio: 6.3 
     25% drainage: 41 minutes 
     EXAMPLE III 
     The formula of Example II was used except the NH 4  OH was 0.30% resulting in a pH of 9.3. The formula was successfully coated on a paper web in two runs. 
     
         ______________________________________                                    
          Expansion ratio                                                 
                    25% drainage                                          
______________________________________                                    
Run 1       8.1         82 min                                            
Run 2       6.8         73 min                                            
______________________________________                                    
 
    
     One liter of the formula of Example III had dilute HCl 10N added to bring the pH to 7.0. 
     Expansion ratio: 6.0 
     25% drainage: 56 min 
     The formula was successfully coated on a paper web. 
     EXAMPLE V 
     The formula of Example II was used except that 0.75% HCl 10N was initially used in lieu of NH 4  OH. The pH was 6.5 and NH 4  OH was added to bring the pH to 7.5. 
     Expansion ratio: 6.0 
     25% drainage: 57 min 
     The formula was successfully coated on a paper web. 
     EXAMPLE VI 
     The formula of Example II was used except no NH 4  OH was used and the water % was 41.93%. 
     pH: 8.9 
     Expansion ratio: 9.5 
     25% drainage: 146 min 
     The formula was successfully coated on a paper web. 
     EXAMPLE VII 
     The formula of Example II was used except no NH 4  OH was used and 0.6% HCl 10N was used. The formula was successfully coated on a paper web in two runs. 
     
         ______________________________________                                    
          pH                                                              
          Expansion ratio                                                 
                    25% drainage                                          
______________________________________                                    
Run 1       5.2         35 min                                            
Run 2       5.2         36 min                                            
______________________________________                                    
 
    
     In examples II-VIII, the pH of a basic formulation was varied. Although all formulas were successfully coated, the foam characteristics varied. Example II was most satisfactory with uniform foam. The foams of Examples III-VII commenced to grow, i.e. became less fluid. Additionally, the foams of Examples IV, V and VII were characterized by large blow through bubbles. 
     EXAMPLE VIII 
     The formula of Example VI was extended with the following base, equal amounts by weight. 
     
         ______________________________________                                    
Base                                                                      
% by Weight                                                               
______________________________________                                    
67.53%              H.sub.2 O                                             
0.07%               PP                                                    
24.00%              resin 5011                                            
5.00%               STAB                                                  
0.40%               FOAM                                                  
______________________________________                                    
 
    
     The formula of Example VII was mixed with the following thinner, equal amounts by weight 
     
         ______________________________________                                    
Thinner                                                                   
% by Weight                                                               
______________________________________                                    
94.5%               H.sub.2 O                                             
0.1%                pseudoplastic                                         
5.0%                stabilizer                                            
0.4%                FOAM                                                  
______________________________________                                    
 
    
     The color intensity of the coated web was varied by extending the pigment with the base and the thinner, respectively. Both formulas were successfully coated on a paper web. 
     EXAMPLE IX 
     The formula of Example II was used except that H 2  O was 60.93% and the resin was reduced from 24% to 5%. 
     pH: 9.6 
     Expansion ratio: 7.3 
     25% drainage: 183 min 
     After several runs with foams of high resin content as in Example II, it was found that resin was beginning to plug the cells of the cylinder. This formula with low resin content was successfully coated on a paper web. 
     EXAMPLE X 
     The formula of Example II was used. To 48 lbs of this formula was added 2 lbs of NH 4  OH. The formula was foamed and the expansion ratio increased from 5.1 to 7.0 which was not objectional. 
     EXAMPLE XI 
     The following formula (low resin) was compared with the formula of Example X to compare growth of the respective foams. 
     
         ______________________________________                                    
Pounds                                                                    
______________________________________                                    
28.00              H.sub.2 O                                              
0.03               PP                                                     
2.00               resin 5011                                             
2.00               STAB                                                   
8.00               pigment 1123                                           
______________________________________                                    
 
    
     The expansion ratio increased from 6.3 to 8.9 and the foam was not as satisfactory as the foam of Example X. In regard to growth, neither formula was tranferred to a paper web or transfer roll. 
     EXAMPLE XII 
     
         ______________________________________                                    
% by Weight                                                               
______________________________________                                    
61.0      H.sub.2 O                                                       
 5.0      resin 5011                                                      
28.6      pigment F-122                                                   
 0.4      FOAM                                                            
pigment:  F-122 35% carbon black pigment/5.6% Nitrile                     
          Resin (Atromax-Vivitone)/59.4% water                            
pH:       9.4                                                             
Expansion ratio:                                                          
          6.8                                                             
25% drainage:                                                             
          less than 10 minutes                                            
______________________________________                                    
 
    
     This formula did not incorporate the psuedoplastic (PP). The 25% drainage time of 10 minutes was unacceptable. Once the foam collapsed in the fountain, it could not be refoamed in the fountain to embody the properties of the original foam. 
     EXAMPLE XIII 
     The formula of Example XI was used except water was 60.93% and the pseudoplastic additive PP was 0.07%. 
     
         ______________________________________                                    
pH                 9.6                                                    
Expansion ratio    7.4                                                    
25% drainage       less than 94 minutes                                   
______________________________________                                    
 
    
     The formula of Example XII was successfully coated on a paper web. 
     EXAMPLE XIV 
     
         ______________________________________                                    
% by Weight                                                               
______________________________________                                    
54.93               H.sub.2 O                                             
0.07                PP                                                    
5.00                STAB                                                  
28.00               pigment 1123                                          
0.40                FOAM                                                  
11.00               resin (678)                                           
______________________________________                                    
 
    
     Initially, some resin settled out. NH 4  OH added to redissolve the resin. 
     pH: 10.3 
     Expansion ratio: 7.2 
     25% drainage: 24 minutes 
     The formula was successfully coated on a paper web. 
     EXAMPLE XV 
     
         ______________________________________                                    
Grams                                                                     
______________________________________                                    
23,153.0            H.sub.2 O                                             
26.6                PP                                                    
1900.0              resin 5011                                            
1900.0              STAB                                                  
10,868.0            pigment F-122                                         
152.0               FOAM                                                  
______________________________________                                    
 
    
     pH 9.6 originally; NH 4  OH added to bring pH to 10.6. The formula was successfully coated on a transfer roll. 
     EXAMPLE XVI 
     In the aforementioned successful runs, it was found that after approximately 30 minutes, the color tended to lose its intensity. The following three runs were conducted to determine if resin content affected the color intensity. 
     
         ______________________________________                                    
         % by Weight                                                      
Formula    A          B          C (Extender)                             
______________________________________                                    
water      19.93          19.93      40.53                                
PP         0.07           0.07       0.07                                 
STAB       7.00           7.00       7.00                                 
resin      44.00  (C55)   52.00                                           
                               (C55) 52.00                                
                                          (C55)                           
FOAM       0.40           0.40       0.40                                 
pigment (1123)                                                            
           28.60          28.60      --                                   
______________________________________                                    
 
    
     Formulas A &amp; B were run as shown. Formula A was extended 50% by weight with Formula C. The formulas A, B and A/C were coated successfully on a paper web. However color intensity faded over extended periods of time. 
     EXAMPLE XVII 
     
         ______________________________________                                    
Weight %                                                                  
______________________________________                                    
54.8               H.sub.2 O                                              
0.2                PP                                                     
11.0               resin FJC-55                                           
28.6               pigment 1123                                           
0.4                FOAM                                                   
5.0                ethylene glycol                                        
pH                 10.0                                                   
surface tension:   36.9 dynes cm.sup.-1                                   
Expansion ratio:   12.4                                                   
25% drainage:      35 minutes                                             
______________________________________                                    
 
    
     The ammonium stearate (STAB) used in prior formulations was deleted. Ethylene glycol was added as a foam conditioner and the amount of pseudoplastic material was increased to 0.20%. Although the foam lacked consistency, the formula was coated successfully on a paper web. No change in color intensity was noted after a run of 11/2 hours. No indication of growth was noticed. 
     EXAMPLE XVIII 
     1% silicone surfactant (L-7129) was added to the formula of Example XVII. The addition of the surfactant resulted in a uniform foam. The formula was successfully coated on a paper web. No change in color intensity or growth in one hour. 
     
         ______________________________________                                    
pH                 9.9                                                    
surface tension    33.0 dynes cm.sup.-1                                   
Expansion ratio    6.4                                                    
25% drainage       32 minutes                                             
______________________________________                                    
 
    
     EXAMPLE XIX 
     The formula of example XVII was modified by increasing the weight percent of the resin from 11.0% to 20.0% and correspondingly decreasing the water content from 54.8% to 45.8%. This formula was successfully coated on a paper web. No change in color intensity was noted. 
     EXAMPLE XX 
     The formula of Example XIX was modified by adding 1% silicone surfactant (L-7129). This formula was successfully coated on a paper web. The foam had the following characteristics: 
     pH: 10.0 
     surface tension: 35.9 dynes cm -1   
     25% drainage: 33 minutes 
     No change in color intensity and very little foam growth. 
     EXAMPLE XXI 
     
         ______________________________________                                    
% by weight                                                               
______________________________________                                    
46.60%            H.sub.2 O                                               
0.20%             PP                                                      
5.00%             ethylene glycol                                         
20.00%            resin FJ-C55                                            
28.60%            pigment 1123                                            
0.60%             FOAM                                                    
0.05%             surfactant L-7129                                       
______________________________________                                    
 
    
     This formula was successfully coated on a paper web. No change in color intensity. 
     EXAMPLE XXII 
     
         ______________________________________                                    
% by Weight                                                               
______________________________________                                    
20.00           pigment F-122                                             
0.20            PP                                                        
2.70            NH.sub.4 OH                                               
10.00           FJC-55                                                    
5.00            ethylene glycol                                           
61.00           H.sub.2 O                                                 
0.60            FOAM                                                      
0.05            surfactant L-7129                                         
0.01            perfluorocarboxylic acid                                  
______________________________________                                    
 
    
     The perfluorocarboxylic acid has the formula: 
     
         C.sub.n F.sub.2n+1 COOH 
    
     where n=5-12. 
     The perfluorocarboxylic acid was added to reduce the surface tension of the foam. The formula was successfully coated on a transfer roll. 
     It was discovered that for the formulas of Examples XVII-XXII (no `stabilizer`) that the color as printed was uniform in intensity for the duration of a run. With ammonium stearate in the formulas, as a run continued, the color would begin to lose its intensity necessitating the addition of pigment periodically during a run. 
     When the foams made with the formulas containing ammonium stearate collapsed they formed a `ghost` foam. When using the formulas with the `stabilizer`, it was desirable to have a long 25% drainage time. 
     It was further discovered with the formulas less the `stabilizer` that as the foam collapsed, the liquid ink was held interstitially and a ghost foam was not formed. These collapsed foams could be refoamed to their original state, i.e. have the same physical and chemical properties including the same 25% drainage time. With these formulas then a long 25% drainage time is not as important as with the formulas containing `stabilizers`. 
     The formulas I-XII were formed in the mixing device illustrated in the drawing. 
     Referring to the drawing, a mixing device is shown at 10  and includes a housing 12 having an inlet conduit 14 and a mixing chamber 16. A nozzle fitting 18 is secured to the housing 12. The fitting 18 has an orifice 20 (1/16&#34; d) which communicates with the chamber 16. A receiver fitting 22 is secured to the housing 12. The fitting 22 has an inlet orifice 24 (3/6&#34; d) which communicates with the chamber 16 and is axially aligned with and spaced-apart from the orifice 20. 
     The exemplary liquid compositions were introduced into the conduit 14 at ambient temperature, a flow rate of between 0.05 to 3.0 gal/min, and under a pressure of between 50-150 psig. Compressed ambient air was introduced into the valve 18 and discharged into the mixing chamber 16. In the mixing chamber turbulence is created due to the venturi effecting good mixing of the liquid with the air. The liquid-air mixture flowed through the valve 22 into a foam refining tube (not shown) and ultimately to a fountain. The flow rate of the compressed air was controlled such that the volume of foamed ink composition to the liquid formulation may vary between 6 to 1 to 12 to 1. 
     The components of the liquid compositions may range between a lower limit of one-fifth to an upper limit of twice the stated amounts of the examples, either alone or in any combination. 
     The liquid compositions of the Examples may have a viscosity unsheared at 1000-20,000 cp; and a sheared viscosity of 1-100 cp measured at a shear rate of 1000 sec -1 . In Example I the viscosities were measured at approximately 2000 cp and 40 cp, respectively. 
     The foams generated had a surface tension of between 15 to 40 dynes/cm and a range of bubble size diameter of between 5-100,000 microns.