Fusion adhesive which can comprise an isocyanate prepolymer, a thermoplastic polymer and/or a lower molecular weight ketone resin
Fusion adhesives are known. They consist of thermoplastic polymers which are in general modified with synthetic or natural resins, waxes, organic fillers etc. When heated to 100°-200° C. they liquefy. After application of the fusion adhesive on the substrates to be bonded, the adhesive rapidly solidifies and forms a solid bond. 
     The main advantages of fusion adhesives with respect to other adhesive systems are the rapid binding and the absence of water and solvents. The main drawback is their thermoplastic behaviour. At increased temperatures they become soft to liquid, but at low temperatures they become hard and brittle so that the adhesive bonds are only resistent in a more or less narrow temperature range. 
     The same applies also to known polyurethane fusion adhesives. They are costly and do not offer the advantages found with the adhesives based on ethylene vinyl acetae polymers, polyamides and polyterephthalic acid. 
     Polyurethane fusion products are highly viscous. At the necessary processing temperature their stability is poor. Starting resistance and heat resistance are low. They provide good bonding only on very few materials. 
     There are also known solvent-free wet-hardening NCO-prepolymers. At room temperature they are liquid or soft as wax. Due to the low starting resistance and the long reaction time their possible application is limited. 
     From DE-PS 24 01 320 are known fusion adhesives consisting of NCO-prepolymers which are combined with ethylene vinyl acetate, ethylene acrylate copolymers, atactic polypropylene and saturated thermoplastic polyesters such as for instance polyethylene terephtalate polymers as well as tackifying resins such as resin derivatives or terpenephenolic copolymers. 
     But said component containing compositions tend at certain composition ratios to make such fusion products incompatible or instable. In many cases their shelf life is not sufficient. 
     The present invention addresses the problems associated with the prior art and provides for compatible, fusion-stable and, in the absence of ambient humidity, storable fusion adhesives presenting a high initial bonding resistance and high thermostability. 
     Accordingly, the present invention provides for fusion adhesives comprising the following: 
     (a) 20 to 90% by weight isocyanate prepolymer, and 
     (b) 5 to 50% by weight of a lower molecular weight synthetic resin selected from a group consisting of ketone resins, hydrogenation products of acetophenone condensation resins, and mixtures thereof. 
     The composition may also comprise up to 75% by weight thermoplastic polyurethane. 
     Instead of thermoplastic polyurethane, the composition may comprise 10 to 70% by weight of a thermally stable or stabilized thermoplastic polyester preferably comprising an ester based on terephthalic acid, dicarboxylic acid and diols resulting in as few hydroxyl groups as possible in the polyester. When polyester is used, the composition of the fusion adhesive need not comprise lower molecular weight synthetic resin. 
     Not all polyesters are appropriate for the inventive fusion adhesives. Appropriate are such polyesters which comprise as few hydroxyl groups as possible. Polyester having a higher portion of hydroxyl groups results in highly viscous to unfusable products and therefore is not appropriate for fusion adhesives. 
     When using crystalline thermoplastic polyester instead of thermoplastic polyurethane there are rapidly obtained fast binding fusion adhesives having higher initial resistance. 
     Such fusion adhesives are particularly appropriate for bonding inorganic and organic substrates. But they are also similarly appropriate for bonding thermoplastic and thermosetting synthetic materials, foam materials, varnished surfaces, wood and wooden materials, paper, leather, synthetic leather, rubber, textiles, non-woven materials and metals. 
     A further subject matter of the invention relates to fusion adhesives consisting of a composition of 
     (a) 50 to 80% by weight isocyanate prepolymer, 
     (b) 0-2% by weight of a thermoplastic polyurethane or polyester, and 
     (c) 20-70% by weight of a lower molecular weight synthetic resin. 
     Due to their low viscosity such adhesive formulations are appropriate for spraying application and can advantageously be used for bonding foam materials or foam materials with non-woven materials, textiles, synthetic leather, leather, etc. 
     MANUFACTURE OF THE ISOCYANATE PREPOLYMER (A) 
     The reactive polyurethane prepolymers used in the inventive adhesive may consist of 
     1. aromatic diisocyantes such as 4.4&#39;-diphenyl methane diisocyanate or cycloaliphatic diisocyanates such as for instance diisocyanato hexane or diisocyanatoisophoron or mixtures of said compounds and/or of 
     2. Prepolymers of the diisocyanates cited under 1. with short chain diols and end group primary or secondary OH-groups such as ethylene glycol to hexanediol 1.6, propylene glycol to hexapropylene glycol, or diethylene glycol to hexaethylene glycol, or of compositions of said compounds, and 
     3. linear or slightly branched polyesters with end-group primary or secondary OH-groups in the molecular weight range of 1,000-3,000, or with linear or slightly branched polyesters in the molecular weight range of 1,000-3,000, or polycaprolactodiols in the molecular weight range of 1,000-3,000, and of 
     4. short-chained diols with end-group primary or secondary OH-groups as cited under 2. 
     The reactive polyurethane prepolymer used in the inventive adhesive ranges within a viscosity range of about 50 Pa.s to about 40,000 Pa.s, in particular in the range of 5,000 to 40,000 Pa.s, at 20° C. for NCO % contents of about 1.0 to about 7.5%, in particular 2-5%. 
     The preparation is carried out in the following manner: 
     The diisocyanate and/or diisocyanate prepolymer are heated to 50°-70° C. and mixed with the desired amount of one of the polyol components indicated under A 3. One of the short-chained diols indicated under A 4 is then added, and the composition is maintained for 1-3 hours at 80° to 120° C. 
     The molar ratios of the components are the following: 
     1 mole of diisocyanate component 
     0.05-0.5 moles of polyol component 
     0.1-0.4 moles of short-chained diol component 
     PREPARATION EXAMPLE 
     410 g. of a diisocyanate prepolymer based on 4.4-diphenyl methane diisocyanate and tripropylene glycol (commercial product: Desmodur PF of Messrs. Bayer AG) are heated to 60° C. and then 
     516 g. of a polyester diol based on adipinic acid, ethylene glycol and butane diol 1.4 (molecular weight of about 2,000 and an OH number of about 55) are admixed under stirring and the mixture is heated to 90° C. Then 74 g. of tripropylene glycol are added drop by drop. Care must be taken that the temperature does not rise above 110° C. Said preparation is kept under stirring for 11/2 hours at 110° C. 
     NCO: 2.7 to 3.2%. 
     Viscosity at 20° C.: 31,000 Pa.s (Brookfield HBT). 
     MANUFACTURE OF A THERMOPLASTIC POLYURETHANE (B) 
     The polyurethane used in the inventive adhesive consists of the following individual components: 
     1. Diisocyanates such as for instance 4.4&#39;-diphenyl methane-diisocyanate, 2.4 toluol diisocyanate, 2.6 toluol-diisocyanate, isophorondiisocyanate, 1.6 diisocyanatohexane, and mixtures of said components, and 
     2. Polyols such as for instance linear or slightly branched polyesterdiols with end group primary OH-groups having a molecular weight of 1,000-3,000, linear or slightly branched polyethers with end group primary or secondary OH-groups having a molecular weight ranging from 1,000-3,000, or polycaprolactodiols having a molecular weight ranging from 1,000-3,000, and 
     3. short-chained diols with end group primary or secondary OH-groups such as for instance ethylene glycol to hexanediol 1.6, propylene glycol to hexapropylene glycol, diethylene glycol to hexaethylene glycol, and mixtures of said compounds. 
     The thermoplastic polyurethane used in the inventive adhesive therefore consists of one or several diisocyanate components cited under 1., one or several of the polyol components cited under 2., and additionally one or several of the short-chained diols cited under 3. 
     The molar ratios of the cited components may be as follows: 
     B 1. 1 mole of diisocyanate 
     B 2. 0.2-1.0 mole of longer chained diol 
     B 3. 0.8-0.0 mole of short-chained diol 
     the molar ratios of components B 1-B 3 being selected such that the thermoplastic polyurethane practically contains no more free OH- and NCO-groups. 
     At room temperature, thermoplastic polyurethane (B) is a solid block-shaped composition presenting high cohesion. The melting point is 70°-170° C., in particular 130°-135° C. The polyol component of the thermoplastic polyurethane (B) should be composed similarly to prepolymer (A) in order to obtain good compatibility with prepolymer (A) in all temperature ranges (from about -30° to +170° C.). The thermoplastic urethane (B) must not comprise any NCO-reactive groups in the molecule in order to ensure the storability of the hotmelt. 
     The thermoplastic polyurethane (B) provides the fusion adhesive with high resistance at room temperature. Furthermore, it is possible to adjust the melting or softening points and thereby the processing temperatures of the inventive fusion adhesive compositions due to the proportion of thermoplastic urethane (B) as desired. 
     In compliance with said proportion the surface of the fusion adhesive composition is slightly adhesive or blocking at room temperature. 
     PREPARATION EXAMPLE FOR A THERMOPLASTIC POLYURETHANE 
     
         ______________________________________                                    
404.0 g. of polyester diol based on adipinic acid,                        
         butane diol 1.4 and ethylene glycol with an                      
         OH-number of about 55 and a molecular weight                     
         of about 2,000                                                   
 20.0 g. of butane diol 1.4                                               
109.5 g. of 4.4&#39;-diisocyanatodiphenyl methane                             
533.5 g.                                                                  
______________________________________                                    
 
    
     The preparation is made as follows: 
     The 4.4-diisocyanatodiphenyl methane is heated to 50°-70° C. and mixed with the polyester diol. The mixture is heated with stirring to 80° C. while the butane diol 1.4 is added drop by drop. 
     The preparation is kept under stirring at 80° C. Thereby is obtained a solid white thermoplastic polyurethane having a melting point of 130° C. 
     The proportion of lower molecular weight synthetic resin (C) is provided for further modification of the characteristics of the fusion adhesive. The softening point should range from about 60° to 120° C. The resin has to be compatible with both main components of the inventive fusion adhesive and must not react with the isocyanate-groups of the prepolymer. The lower molecular weight synthetic resins permit control or modification of characteristics such as hottack, initial resistance and viscosity. 
     MANUFACTURE OF THE LOWER MOLECULAR WEIGHT SYNTHETIC RESIN (C) 
     The lower molecular weight synthetic resins are products which are generally prepared from: 
     (a) aliphatic ketones such as acetone or methyl ethyl ketone, aliphatic aromatic ketones such as acetophenone, methylnaphthyl ketone, propiophenone, or nucleus alkylized acetophenones such as methyl-, ethyl, tert. butyl and cyclohexanone or methylcyclohexanone, or mixtures thereof, under catalytic influence of neutral basic or acid condensation products, and/or 
     (b) ketones comprised of (a) and aldehydes such as for instance formaldehyde, acetaldehyde, propionaldehyde, butylaldehyde, crotonaldehyde, β-oxybutyraldehyde at molar ratios of ketones to aldehyde of 1:1 to 2:1. 
     The lower molecular weight synthetic resin may further be 
     (c) a hydrogenation product of acetonephenone condensation resins. 
     Synthetic resins as they may be used according to the invention are disclosed by 
     1. H. Wagner, H. F. Starx 
     Lack-Kunstharze (4th ed. 1959) 
     Karl Hanser, editors, Munich 
     pages 79-83 
     2. Houben-Weyl, vol. XIV 
     Part 2 
     Georg Thieme editors, Stuttgart, 1963 
     pages 416-424. 
     With particular advantage is used a light neutral unsaponifiable ketone aldehyde condensation resin. Said resin has a density of about 1.19, an iodine colour number in a 50% toluol solution of about 1.5, an acid number of about 0.1 and a softening point of about 79° C. 
     According to the above citation (2) said synthetic resin may be manufactured from acetophenone and formaldehyde in a molar ratio of 1:1. 
     The inventive fusion adhesive comprising the above described components, remains stable and storable over a long period of time (more than 8 months) and is solid at room temperature. 
     Processing characteristics and binding behaviour substantially conform with usual fusion adhesives. Initial resistance is satisfactory to good. With progressing reaction of the NCO-groups with ambient humidity the binding resistance increases. The thermoplastic hotmelt film becomes more and more flexible and reaches an elastic final condition. The finished reacted fusion adhesive films are unmeltable, their elasticity and resistance are maintained in a broad temperature range. The latter as well as the bondings are resistant against fats, oils, softeners, diluted acids and lye solutions and are insoluble in most solvents and water. By varying the quantity ratios of prepolymer, thermoplastic polyurethane or polyester and lower molecular resin it is possible to vary processing and utilisation characteristics in the desired direction. The softening range (melting point), viscosity and processing temperature of the hotmelt depend on the molecular weight and composition of the prepolymer isocyanate (A), the thermoplastic polyurethane (B) or polyester and the melting point of the lower molecular weight synthetic resin (C). 
     The fusion viscosity of the fusion adhesive, measured at 150° C. with the Epprecht Rheomat 15 with viscotemp. ranges from about 0.1 to about 800 Pa.s. 
     The wetting velocity depends on construction and type of the isocyanate prepolymer (A) selected. 
     The polyisocyanate prepolymer (A) should be the main component of the inventive fusion adhesive. It conditions the high flexibility of the finished reacted film, the good resistance against cold and heat, high resistance against numerous agents such as solvents, fat etc. as well as excellent adhesion on many substrates. 
     When the proportion of prepolymer (A) drops below 20% by weight, the characteristics of the thermoplastic polymer or synthetic resin portion dominate. Heat and cold resistance are poorer. Resistance against softeners, fats and solvents decreases. At prepolymer (A) proportions of more than 90% by weight the prepolymer characteristics dominate. In this case the initial resistance of the incompletely reacted adhesive composition is very low and the film surface does not form a solid block. According to the invention the preferred proportions are 50 to 75% by weight of (A). 
     Even very low proportions of thermoplastic polyurethane (B) or ester influence the rheologic behaviour of the prepolymer fusion so that even on porous substrates it does not diffuse. This effect occurs already at proportions of 2% by weight of (B). It is an important characteristic of the thermoplastic polyurethane or polyester (B) that proportions in the range of 5-10% by weight may increase essentially the softening and melting point of the adhesive composition. The composition comprising the viscous to waxy prepolymers (A) becomes firm and the fusion rapidly solidifies. Thus is obtained the main requirement for hotmelts, i.e. to bind rapidly when cooling. With an increasing proportion of (B) fusion viscosity increases and thus the processing temperature of the adhesive composition increases and open time is shortened. 
     For adhesives requiring high initial resistances and for which penetration on porous materials is to be avoided, the thermoplastic polymer (B) is used in proportions ranging from 2-75% by weight, preferably 5-55% by weight. 
     If the application purpose requires low fusion viscosity of the adhesive the thermoplastic polymer (B) may either be left out completely or be used in proportions of less than 2%. 
     The proportion of lower molecular synthetic resin (C) improves the hottack, the wetting capacity and the binding velocity of the not cross-linked adhesive composition. In particular it causes a viscosity decrease. Consequently, there should be used at least 5% by weight of resin (C). At higher proportions than 50% by weight the utilization characteristics of the adhesive film become less good, for instance cold resistance and resistance against fat, softener and solvents, although cohesion and elasticity may still be sufficient. The proportions preferred according to the invention (component (C)) range between 10-40% by weight. 
     In the absence of humidity the inventive adhesive composition has good storing stability. Processing is carried out at temperatures ranging between 90° C. and 160° C. depending on the composition of the adhesive mixture and the temperature sensitivity of the substrate to be bonded. 
     For bonding thin synthetic films, for instance polyethylene films, there are preferably used low viscosity adjustments with low melting points (example 1, adhesive (a) which may be processed at temperatures ranging from 90° to 100° C. Conventional thermoplastic fusion adhesives with sufficient heat resistance necessitate substantially higher processing temperatures such that film damage may occur. For commercial fusion adhesives with low processing temperatures heat resistance of the bonding is poorer. 
     For bonding porous materials, or in cases in which the bonding is immediately stressed, high viscosity adjustments with higher softening or melting points are advantageous (example 2, adhesives (b) and (c)). 
     Processing of the fusion adhesive may be carried out with a wiper, rollers or spray devices. Particularly appropriate are drum melting installations. 
     The inventive fusion adhesives adheres to many organic or inorganic substrates, for instance to thermoplastic and thermosetting synthetic materials including foam materials, different varnishes, rubber, textiles, non-woven materials, leather, wood, metal and paper. 
    
    
     The following examples show the advantages of the crosslinked polyurethane fusion adhesive: 
     Structure of the adhesive compositions in % by weight: 
     
         ______________________________________                                    
                   inventive examples                                     
                   a    b      c      d                                   
______________________________________                                    
A    prepolymer isocyanate accord.                                        
                         65     65   50   40                              
    to example page 6                                                     
B   thermoplastic polyurethane                                            
                          5     20   30   --                              
    according to example page 7                                           
C   lower molecular weight                                                
                         30     15   20    5                              
    synthetic resin (commercial                                           
    ketone-aldehyde condensa-                                             
    tion product) according                                               
    to example page 10                                                    
D   polyester phthalic acid                                               
                         --     --   --   55                              
    ester                                                                 
______________________________________                                    
 
    
     UTILISATION EXAMPLE 1 
     Bonding of polyethylene film 
     Pretreated low density polyethylene film (by corona pretreatment obtained surface tension: 45 dyn/cm) was coated with 20 g/m 2  of fusion adhesive. Application temperature: for fusion adhesive (a) about 90° C.; the conventional EVA based adhesive for synthetic materials necessitated an application temperature of 120° C. On the film coated with adhesive was applied within 10 seconds and pressed thereon a film section of the same dimensions. After 2 hours were cut therefrom the necessary test strips for determining separation, heat and cold resistance. 
     In table I the inventive fusion adhesive (a) has been compared to a specific conventional fusion EVA-based adhesive for synthetic materials. 
     
                       TABLE I                                                     
______________________________________                                    
                     state of art                                         
                     special fusion                                       
                     adhesive e for                                       
                     synthetic mate-                                      
           inventive fusion                                               
                     rials (ISATHERM                                      
           adhesive.sup.(a)                                               
                     S 39/3)                                              
______________________________________                                    
separation resis-                                                         
tance of the coating                                                      
after 2 hours                                                             
             1.1     kp      1.8     kp                                   
after 24 hours                                                            
             1.8     kp      1.9     kp                                   
after 48 hours                                                            
             2.5     kp      1.9     kp                                   
after 1 week film rupture                                                 
                         1.85      kp                                     
             (&gt;3.2 kp)                                                    
heat resistance                                                           
             3 mm after 24                                                
                         1         min.                                   
(after 4 days)                                                            
             hours                                                        
at 50° C.                                                          
at 70° C.                                                          
             66      min     1/2     min                                  
cold resistance of                                                        
             no adhesion breaks off                                       
bonding at - 10° C.                                                
             drop                                                         
at - 20° C.                                                        
             no adhesion breaks off                                       
             drop                                                         
______________________________________                                    
 
    
     Measuring methods 
     For determining separation resistance 15 mm large test strips bonded by the inventive adhesive were peeled off on a rupture machine. 
     Feed: 200 mm/min. 
     Heat resistance: 30 mm large bonded test strips were loaded in the air circulation oven at test temperature with a 300 g weight. The heat resistance was determined by measuring the time during which the test strip peels for 60 mm. 
     Cold resistance was verified manually. 30 mm large bonded test strips were stored at low temperatures for 1 hour in a coolant cabinet and then the test sample was loaded abruptly. It was registered whether the test strips delaminate in the bonding joint. 
     Cold rupture temperature: In a coolant cabinet a 10 mm thick, 100 mm large steel plate is set with its narrow edge on a panel. A 30 mm large, 600μ thick fusion adhesive film is fixed by adhesive tape in such a way that it rests for about half its length on the panel. The second half of the fusion adhesive film is bonded vertically to the part fixed on the panel onto the steel plate. After 1 hour the steel plate is pushed over so that the adhesive film is kinked. If the adhesive film does not break the temperature of the coolant cabinet is reduced by 2° and the procedure is repeated until the film breaks. 
     The viscosity of the fusion adhesive was measured by means of the Epprecht Theomat 15 plus Viskotemp. 
     UTILISATION EXAMPLE 2 
     Bonding of rigid substrates (wood). 
     Adhesives b, c and f were compared with a conventional fusion adhesive for binding furniture edges. 
     The test samples made of red beech were manufactured in the manner described in method WPS 68 for determining heat resistance of furniture fusion adhesives. 
     Shear strength was determined in compliance with DIN 53 254. Heat resistance was determined in compliance with WPS 68. 
     Failure load and resistance to rupture were determined by means of 600μ thick and 25 mm large adhesive films on a tearing machine. The gripping length of the films was 30 mm; the feed was 200 mm/min. 
     
                                           TABLE 2                                 
__________________________________________________________________________
                            state of art adhesive.sup.(f)                 
                            commercial furniture                          
inventive                   fusion adhesive                               
adhesive.sup.(b)                                                          
              adhesive.sup.(c)                                            
                     adhesive.sup.(d)                                     
                            (Rakoll K 570)                                
__________________________________________________________________________
shear                                                                     
resistance                                                                
of bonding                                                                
after 2 h                                                                 
      10 kp/4 cm.sup.2                                                    
               23 kp/4 cm.sup.2                                           
                      99 kp/4 cm.sup.2                                    
                            64 kp/4 cm.sup.2                              
after 8 h                                                                 
      38 kp/4 cm.sup.2                                                    
              203 kp/4 cm.sup.2                                           
                     155 kp/4 cm.sup.2                                    
                            68 kp/4 cm.sup.2                              
after 24 h                                                                
      207 kp/4 cm.sup.2                                                   
              213 kp/4 cm.sup.2                                           
                     202 kp/4 cm.sup.2                                    
                            69 kp/4 cm.sup.2                              
heating                                                                   
resistance                                                                
of bonding:                                                               
according                                                                 
to WPS 68:                                                                
after 2 h                                                                 
      35-40° C.                                                    
              45-50° C.                                            
                     50-55° C.                                     
                            65-70° C.                              
after 24 h                                                                
      170-175° C.                                                  
              180-185° C.                                          
                     160-165° C.                                   
                            65-70° C.                              
after 48 h                                                                
      205-210° C.                                                  
              210-215° C.                                          
                     170-175° C.                                   
                            65-70° C.                              
__________________________________________________________________________
 Tables I and 2 show that the bonding resistance of the inventive fusion
 adhesive is superior after complete crosslinking at ambient temperatures
 as well as at very high and low temperatures, as compared to conventional
 fusion adhesives.
 
    
     Table 3 summarizes further physical characteristics. 
     
                                           TABLE 3                                 
__________________________________________________________________________
                        e     f                                           
                        synth.                                            
                              furnit.                                     
                        fusion                                            
                              fusion                                      
a           b     c     adh.  adh. d                                      
__________________________________________________________________________
Viscosity                                                                 
at 120° C.                                                         
        5 Pa · s                                                 
            100 Pa · s                                           
                  2000 Pa · s                                    
                        14.0 Pa · s                              
                              1600 Pa · s                        
                                    3000 Pa · s                  
at 150° C.                                                         
      0.2 Pa · s                                                 
             9 Pa · s                                            
                   160 Pa · s                                    
                         4.5 Pa · s                              
                               490 Pa · s                        
                                     900 Pa · s                  
melting p.                                                                
after 2 h                                                                 
       67° C.                                                      
            90° C.                                                 
                  92°  C.                                          
                        68° C.                                     
                              100° C.                              
                                    115°                           
after 24 h                                                                
      110° C.                                                      
            um.sup.1                                                      
                  um.sup.1          um.sup.1                              
after 48 h                                                                
      um.sup.1                                                            
            um.sup.1                                                      
                  um.sup.1          um.sup.1                              
failure                                                                   
      420%  470%  480%  490%  540%  520%                                  
load                                                                      
tensile                                                                   
      13.6 kp                                                             
            15.0 kp                                                       
                  17.4 kp                                                 
                        1.4 kp                                            
                              6.0 kp                                      
                                    10.64 kp                              
strength                                                                  
cold fail.                                                                
      &lt;-35°  C..sup.2                                              
            &lt;-35° C..sup.2                                         
                  &lt;-35° C..sup.2                                   
                        -15°                                       
                              -28° C.                              
                                    -35° C.                        
temp.                                                                     
__________________________________________________________________________
 .sup.1 um -- unmeltable                                                  
 .sup.2 The fusion adhesive films could not be tested at less than        
 -35° C. The films of adhesives a, b and c are flexible at         
 -35° C. The films of EVA resin adhesives d and e are brittle hard.
 
    
     The cross-linked fusion adhesives are substantially resistant to solvents, oils, fats, softeners, diluted acids and lye solutions. 
     For instance, 14 day old bondings of PE films with adhesive (b) were stored in various solvents (storing time 5 weeks) and after 24 hours of ventilation of the solvents remaining in the bonding joint, the separation resistance was measured on a tension machine. 
     Width of test strips: 15 mm. 
     The following values were obtained: 
     
         ______________________________________                                    
Solvent                                                                   
______________________________________                                    
                   separation resistance of                               
                   PE-bondings after 5 weeks                              
                   storage in the below indi-                             
                   cated solvents                                         
                   3.2 kp/15 mm film rupture                              
special gasoline   2.8 kp/15 mm film rupture                              
toluol             3.2 kp/15 mm film rupture                              
ethylacetate       3.2 kp/15 mm film rupture                              
acetone            2.9 kp/15 mm film rupture                              
trichlorethylene   3.1 kp/15 mm film rupture                              
                   separation resistance of                               
                   PE-bondings after 4 weeks                              
                   storage in the below indi-                             
                   cated media                                            
dibutylphthalate   2.8 kp/15 mm film rupture                              
dioctylphthalate   2.9 kp/15 mm film rupture                              
aqueous sulfuric acid, 2n                                                 
                   3.2 kp/15 mm film rupture                              
aqueous nitric acid, 2n                                                   
                   3.2 kp/15 mm film rupture                              
aqueous potassium hydr., 2n                                               
                   3.2 kp/15 mm film rupture                              
water              2.8 kp/15 mm film rupture                              
______________________________________                                    
 
    
     Softener resistance: 
     Soft PVC film containing 30% of DOP was bonded with adhesive b and the special fusion adhesive d for synthetics. 
     The bonded strips were stored for four days at 50° C. in a drying oven and after cooling to room temperature the separation resistance was measured (width of test strips 30 mm). 
     The samples bonded with adhesive b gave results of 2.8 kp. The samples bonded with special adhesive (d) based on EVA-resins were delaminated. Due to absorption of softener from the PVC the adhesive became soft and smearing.