Heat-curable composition
FIELD OF THE INVENTION 
     The present invention is directed to a heat-curable composition comprising a polyepoxide, an unsaturated monomer, an amine, a trialkylsulfonium salt of an anion of low nucleophilicity, and a free-radical curing agent. 
     RELATED APPLICATION 
     The present application is related to patent application Serial Number 635,984 filed July 30, 1984, having a common inventor and common assignee. 
     BACKGROUND OF THE INVENTION 
     A large number of curing agents are known for epoxy resins, as, for example, amines, anhydrides, mercaptans, etc. Each curing agent has advantages and disadvantages that make it acceptable or unusable for some applications. Also, each curing agent, or combination thereof, may be employed with one or more curing accelerators. Examples include the inorganic and organic metal salts such as lithium chloride and stannous octoate; onium salts such as ammonium chloride, alkyl phosphonium halides, etc; and BF 3  complexes. 
     There is a need to develop curable epoxy resin compositions which cure very rapidly at moderably elevated temperatures yet have very long pot life at room temperature. 
     Accordingly, it has now been disclosed that certain trialkylsulfonium salts containing anions of low nucleophilicity function as excellent accelerators for the amine cure of epoxy resins. These accelerators are much more thermally latent than prior art accelerators such as BF 3  complexes and give a much longer room temperature pot life at equivalent 150° C. gel time. These systems have further been modified with additional monomers to give lower viscosity products. 
     SUMMARY OF THE INVENTION 
     The present invention is directed to heat-curable epoxy resin compositions exhibiting improved thermal latency and pot life, which when cured, yield compositions exhibiting improved physical properties. More particularly, the invention provides a heat-curable composition comprising (1) a polyepoxide, (2) a curing amount of an amine, especially an aromatic amine, (3) a catalytic amount of a trihydrocarbyl sulfonium salt, particularly a trialkyl sulfonium salt containing an anion of low nucleophilicity, (4) at least one unsaturated monomer selected from the group consisting of alkyl esters or amides of ethylenically unsaturated monocarboxylic acids, cyano-containing compounds, vinyl esters, N-vinyl amides and allyl compounds and (5) a curing amount of a free radical curing agent. These compositions are suitable for use in sheet molding compositions (SMC), in structural applications such as automotive parts, oil well parts (sucker rods), as well as in resin transfer molding (RTM) applications. In addition to the above, these compositions also give reduced viscosity combined with excellent heat resistance, factors which make them leading candidates for a number of pultrusion, filament winding, and resin transfer molding applications. 
     DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     It has now been found that heat-curable compositions exhibiting improved thermal latency are obtained from epoxy compositions comprising (1) a polyepoxide, (2) an aromatic (or possibly aliphatic) amine, (3) a trialkyl sulfonium salt, (4) at least one unsaturated monomer selected from the group consisting of alkyl esters or amides of ethylenically unsaturated monocarboxylic acids, cyano-containing compounds, vinyl esters, N-vinyl amides and allyl compounds and (5) a curing amount of a free radical curing agent. 
     Preferably, the composition comprises (1) a glycidyl polyether of a polyhydric phenol, (2) from about 0.5 to about 1.5 chemical equivalents of an aromatic or aliphatic amine based on the glycidyl polyether, (3) a catalytic amount of a trialkyl sulfonium salt, preferably from about 0.001% to about 10% by weight of the glycidyl polyether, (4) at least one unsaturated monomer selected from the group consisting of alkyl esters or amides of ethylenically unsaturated monocarboxylic acids, cyano-containing compounds, vinyl esters, N-vinyl amides and allyl compounds and (5) a curing amount of a free radical curing agent, wherein the relative amounts of component (1) to component (4) is about 25 to about 99 percent by weight component (1) to about 75 to about 1 percent by weight component (4). 
     Polyepoxides 
     The polyepoxides used to prepare the present compositions comprise those compounds containing at least one vicinal epoxy group; i.e., at least one ##STR1## group. These polyepoxides may be saturated or unsaturated, aliphatic, cycloaliphatic, aromatic or heterocyclic and may be substituted if desired with non-interfering substituents such as halogen atoms, hydroxyl groups, ether linkages, and the like. They may also be monomeric or polymeric. 
     For clarity, many of the polyepoxides and particularly those of the polymeric type are described in terms of epoxy equivalent values. The meaning of this expression is described in U.S. Pat. No. 2,633,458. The polyepoxides used in the present process are preferably those having an epoxy equivalency greater than 1.0. 
     Various examples of liquid polyepoxides that may be used in the process of the invention are given in U.S. Pat. No. 2,633,458 and it is to be understood that the disclosure of that patent relative to examples of polyepoxides is incorporated by reference into this specification. 
     Other suitable polyepoxides are disclosed in U.S. Pat. Nos. 3,356,624, 3,408,219, 3,446,762, and 3,637,618 and the disclosure of these patents relevant to examples of epoxy compounds is incorporated by reference into this specification. 
     Preferred polyepoxides are the glycidyl polyethers of polyhydric phenols and polyhydric alcohols, especially the glycidyl polyethers of 2,2-bis(4-hydroxyphenyl)propane having an average molecular weight between about 300 and 3,000 and an epoxide equivalent weight between about 140 and 2,000 and more preferably an average molecular weight of from about 300 to about 1000 and an epoxide equivalent weight of from about 140 to about 650. 
     Other suitable epoxy compounds include those compounds derived from polyhydric phenols and having at least one vicinal epoxy group wherein the carbon-to-carbon bonds within the six-membered ring are saturated. Such epoxy resins may be obtained by at least two well-known techniques, i.e., by the hydrogenation of glycidyl polyethers of polyhydric phenols or by the reaction of hydrogenated polyhydric phenols with epichlorohydrin in the presence of a suitable catalyst such as a Lewis acid, e.g., boron trihalides and complexes thereof, and subsequent dehydrochlorination in an alkaline medium. The method of preparation form no part of the present invention and the resulting saturated epoxy resins derived by either method are suitable in the present compositions. 
     Briefly, the first method comprises the hydrogenation of glycidyl polyethers of polyhydric phenols with hydrogen in the presence of a catalyst consisting of rhodium and/or ruthenium supported on an inert carrier at a temperature below about 50° C. This method is thoroughly disclosed and described in U.S. Pat. No. 3,336,241, issued Aug. 15, 1967. 
     The hydrogenated epoxy compounds prepared by the process disclosed in U.S. Pat. No. 3,336,241 are suitable for use in the present compositions. Accordingly, the relevant disclosure of U.S. Pat. No. 3,336,241 is incorporated herein by reference. 
     The second method comprises the condensation of a hydrogenated polyphenol with an epihalohydrin, such as epichlorohydrin, in the presence of a suitable catalyst such as BF 3 , followed by dehydrohalogenation in the presence of caustic. When the hydrogenated phenol is hydrogenated Bisphenol A, the resulting saturated epoxy compound is sometimes referred to as &#34;diepoxidized hydrogenated Bisphenol A&#34;, or more properly as the diglycidyl ether of 2,2bis(4-cyclohexanol)propane. 
     In any event, the term &#34;saturated epoxy resin&#34;, as used herein shall be deemed to mean the glycidyl ethers of polyhydric phenols wherein the aromatic rings of the phenols have been or are saturated. 
     Preferred saturated epoxy resins are the hydrogenated resins prepared by the process described in U.S. Pat. No. 3,336,241. Especially preferred are the hydrogenated glycidyl ethers of 2,2-bis(4-hydroxyphenyl)propane, sometimes called the diglycidyl ethers of 2,2-bis(4-cyclohexanol)propane. 
     Other examples of suitable polyepoxides include the glycidyl ethers of novolac resins, i.e., phenol-aldehyde condensates. Preferred resins of this type are those disclosed in U.S. Pat. No. 2,658,885. 
     For most applications it is desirable to utilize an epoxy resin which is liquid or semi-liquid under the conditions of application. Accordingly, a blend of a liquid and solid epoxy resin may be employed. For some applications, a solid resin may be employed. 
     Amines 
     Suitable aromatic amines include, among others, methylenedianiline, metaphenylenediamine, 2,4-bis[p-aminobenzyl]aniline, diaminodiphenyl sulfone, 2,4-toluenediamine, 1,3-diamino-2,4-diethyl-6-methylbenzene, 4,4&#39;-oxydianiline, methylenebis(ortho-chloroaniline), 2,6-diaminopyridine, 4-bromo-1,3-diaminobenzene, etc. Aliphatic amines such as bis(4-aminocyclohexyl)methane, 1,8-diamino-p-menthane, or 1,2-diaminocyclohexane may also be used, although aromatic amines constitute a preferred class. 
     In general, a curing amount of amine is used. Operable amounts range from about 0.5 to about 2.0 chemical equivalents of amine to epoxy resin, with from about 0.75 to 1.25 being preferred. As used herein, a chemical equivalent is the amount which furnishes one amino hydrogen per epoxy group. 
     Trialkylsulfonium Salts 
     In general, the trialkylsulfonium salts containing anions of low nucleophilicity are preferred. Suitable tri(hydrocarbyl)sulfonium salts have the following general formula: ##STR2## wherein R 1 , R 2 , and R 3  each represent the same or different alkyl or aryl radicals of from about 1 to about 18 carbon atoms; and X is selected from the group: BF 4 , PF 6 , AsF 6 , SbF 6 , CF 3  SO 3 , FSO 3 , CH 3  SO 3 , 2,4,6-trinitrobenzenesulfonate, p-toluenesulfonate, etc. The alkyl or aryl radicals R 1 , R 2  and R 3  may contain various substituents such as oxygen, sulfur, halogens, etc. 
     Suitable triorgano-sulfonium salts include, among others, triethylsulfonium tetrafluoroborate, methyldiphenylsulfonium tetrafluoroborate, ethyldiphenylsulfonium tetrafluoroborate, allyldimethylsulfonium tetrafluoroborate, allyl bis(2-(allyloxy)ethyl)-sulfonium tetrafluoroborate, trimethylsulfonium hexafluorophosphate, ethyl(2-hydroxyethyl)(2-(ethylthio)ethyl)sulfonium tetrafluoroborate, etc. 
     Briefly, these triorgano-sulfonium salts can be prepared by a number of processes. One process involves reaction of a sulfonium halide with the silver salt of a nonnucleophilic anion such as tetrafluoroborate. In a second process, an alcohol such as allyl alcohol, a sulfide such as dimethyl sulfide, and an acid such as tetrafluoroboric acid containing an anion of low nucleophilicity, are mixed and refluxed. In some cases a thiol may be used instead of a sulfide. Water is removed by azeotropic distillation and entrained in a Dean-Stark trap and the sulfonium salt is left in the pot (in this case, allyldimethylsulfonium tetrafluoroborate). In a third process, a β-hydroxyalkyl sulfide, such as 2,2&#39;-thiodiethanol, is mixed with an acid containing an ion of low nucleophilicity and water is removed by vacuum distillation, leaving a sulfonium salt mixture. 
     In general, a catalytic amount of triorgano-sulfonium salts are used; i.e. 0.001% to about 10% by weight of the polyepoxide, preferably about 0.3% to about 5% by weight. 
     Monomers 
     As noted hereinbefore, the polyepoxide is blended with up to 75% by weight of one or more monomers selected from the group consisting of (1) esters or amides of ethylenically unsaturated carboxylic acids, (2) cyano-containing compounds, (3) vinyl esters, (4) N-vinyl amides or (5) allyl-containing compounds. 
     Suitable unsaturated monocarboxylic acid esters include the alkyl esters of ethylenically unsaturated acids such as acrylic acid, methacrylic acid, crotonic acid, alpha-phenylacrylic acid, alpha-cyclohexylacrylic acid, maleic acid, cyanoacrylic acid, methoxyacrylic acid, and the like. Very preferred acids are acrylic acid and methacrylic acid. Accordingly, suitable such esters include, methyl methacrylate, ethyl acrylate, butyl acrylate, butyl methacrylate, isobutyl methacrylate, and the like wherein side chains may contain halogen, e.g., 2,3-dibromopropyl acrylate, pentachlorophenyl methacrylate, etc. 
     Very preferred comonomers include the polycrylate and polymethacrylate esters of polyols containing more than one terminal acrylate or methacrylate group. These esters are the acrylic and methacrylic acid esters of aliphatic polyhydric alcohols such as, for example, the di- and polyacrylates and the di- and polymethacrylates of alkylene glycols, polyoxyalkylene glycols, alicyclic glycols and higher polyols, such as ethylene glycol, triethylene glycol, tetraethylene glycol, tetramethylene glycol, hexanediol, trimethylolethane, trimethylolpropane, pentaerythritol, dipentaerythritol, tripentaerythritol and the like, or mixtures of these with each other or with their partially esterified analogs. 
     Typical compounds include but are not limited to trimethylolpropane triacrylate, trimethylolethane triacrylate, trimethylolpropane trimethacrylate, trimethylolethane trimethacrylate, tetramethylene glycol dimethacrylate, ethylene glycol dimethacrylate, triethylene glycol dimethacrylate, pentaerythritol triacrylate, pentaerythritol tetraacrylate, 1,6-hexanediol diacrylate, 1,6-hexanediol dimethacrylate, dipentaerythritol tetraacrylate, dipentaerythritol pentaacrylate, and the like. Particularly preferred esters are neopentyl glycol dimethacrylate, trimethylolpropane trimethacrylate, trimethylolpropane triacrylate, pentaerythritol triacrylate, and 1,3-butylene dimethacrylate. 
     Additional acrylate or methacrylate esters of polyols are the acrylate or methacrylate esters of epoxide resins, wherein epoxide resins as used herein are considered to be polyols. The epoxide resins useful in reacting with acrylic or methacrylic acid are those epoxide resins described hereinbefore. The procedures for preparing these acrylate and methacrylate esters of epoxide resins are described in U.S. Pat. No. 3,377,406 which is hereby incorporated by reference. 
     Suitable unsaturated carboxylic acid amides include acrylamide, N,N&#39;-dimethylacrylamide, diacetone acrylamide, N-isopropylacrylamide, N,N&#39;-dimethyl methacrylamide, etc. 
     Suitable cyano-compounds are acrylontrile, methacrylonitrile, and halogenated acrylontrile, etc. 
     Suitable vinyl esters include vinyl acetate, vinyl benzoate, divinyl adipate, etc. Suitable N-vinyl amides include N-vinylpyrrolidone, N-vinylacetamide, N,N-divinyladipamide, etc. 
     Suitable allyl monomers include diallyl phthalate, triallyl isocyanurate, diallyl isophthalate, allyl diglycol carbonate, etc. 
     Epoxy Monomer Blends 
     Usable blends of the polyepoxide and other monomers will range from about 99% to 25% polyepoxide and from about 1% to about 75% other monomers as a weight basis. An especially preferred range is from about 95% to about 65% polyepoxide and from about 5% to about 35% other monomers. 
     Free Radical Curing Agents 
     Examples of such catalysts include the peroxides, such as benzoyl peroxide, tertiary butyl hydroperoxide, ditertiary butyl peroxide, hydrogen peroxide, potassium persulfate, methyl cyclohexyl peroxide, cumene hydroperoxide, acetyl benzoyl peroxide, Tetralin hydroperoxide, phenylcyclohexane hydroperoxide, tertiary butyl peracetate, dicumyl peroxide, tertiary butyl perbenzoate, ditertiary amyl perphthalate, ditertiary butyl peradipate, tertiary amyl percarbonate, and the like, and mixtures thereof; azo compounds such as 2,2&#39;-azobisisobutyronitrile, dimethyl 2,2&#39;-azobisisobutyrate, 2,2&#39;-azobis(2,4-dimethylvaleronitrile), 2,2&#39;-azobisisobutyramide, and the like. Particularly preferred catalysts include the dialkyl peroxides, tertiary alkyl hydroperoxides, alkyl esters of peroxycarboxylic acids and particularly those of the above noted groups which contain no more than 18 carbon atoms per molecule and which have a half-life of at least one hour at 125° C. 
     An especially useful peroxide is 2,5-dimethyl-2,5-bis(tertiarybutylperoxy)hexane. 
     It will be appreciated that the amount of free-radical catalyst (curing agent) will vary over a broad range depending upon the amount of the particular vinyl monomer used, type of peroxide and end-use properties, etc. In general, an effective or curing amount is employed. One skilled in the art would simply adjust the amounts of a particular peroxide to suit his process conditions. Such adjustments are made in one or two runs knowing the temperatures, half-lives, etc. 
     The present compositions may be utilized in many applications such as for coatings and impregnating compositions in the preparation of adhesives for metals, wood, cement and the like, and in the preparation of reinforced composite products, such as laminated products, filament windings, sheet molding compounds (SMC), electrical laminates, molding powders, fluidized bed powders, potting compounds, etc. A very suitable application is in the preparation of reinforced products and laminates wherein the compositions are applied to fibrous products such as glass fibers or cloth and the material formed in to the desired object and cured. 
     The following examples are given to illustrate the preparation of the instant heat-curable thermosetting compositions. It is understood that the examples are embodiments only and are given for the purpose of illustration and the invention is not to be regarded as limited to any specific components and/or specific conditions recited therein. Unless otherwise indicated, parts and percentages in the examples, are parts and percentages by weight. 
     Epoxy Resin A is a liquid glycidyl polyether of 2,2-bis(4-hydroxyphenyl)propane having an epoxide equivalent weight of 180-195 and an average molecular weight of about 380. 
     Curing Agent A is a liquid aromatic amine having an amine nitrogen content of 14-16% by weight and a viscosity (25° C.) of 15-35 poises, containing about 30% by weight of o-toluenediamine and 70% by weight of a mixture of polymethylene polyanilines. 
     The compositions were tested according to the following test procedures: 
     Heat distortion temperature, °C., ASTM D-648 
     Tg, °C., dynamic mechanical (Rheometrics) 
     R.T. Tensile Strength, MPa, ASTM D-638 
     R.T. Tensile Modulus, MPa, ASTM D-638 
     R.T. Tensile Elongation, %, ASTM D-638 
    
    
     EXAMPLE 1 
     Reaction of 2,2-Thiodiethanol with 48% Aqueous HBF 4   
     6200 (50 moles) of 98.5% 2,2&#39;-thiodiethanol was mixed with 4580 g (25 equivalents) of 48% aqueous tetrafluoroboric acid. This mixture was held in a 5-gallon polyethylene reservoir. A glass wiped-film evaporator with an evaporative surface area of 323 cm 2  was set up with a Teflon intake tube leading to the polyethylene reservoir; intake rate was controlled by a metering valve. The evaporative surface was held at a temperature of 95°-98° C., while water was pumped from an ice bath to cool the condensation surface. The pressure in the evaporator was lowered to 40-130 Pa and the thiodiethanol-tetrafluoroboric acid mixture was introduced slowly. Water was evaporated from the mixture leaaving the desired reaction product as the residue. The intake rate was regulated to give a product output rate of 10-12 mL/min. Karl Fischer titration of the product showed a water level of 2.5% in the product. 
     EXAMPLE 2 
     Reaction of 2-(Ethylthio)ethanol with 48% Aqueous HBF 4   
     6372 g (60 moles) of 2-(ethylthio)ethanol was mixed with 5487 g (30 equivalents) of 48% aqueous tetrafluoroboric acid. This mixture was held in a 5-gallon polyethylene reservoir. A glass wiped-film evaporator was set up under evaporation conditions identical to those in Example 1. The feed intake rate was regulated to give a product output rate of 5-15 mL/min. Karl Fisher titration showed a water level of 2.5% in the product. Neutron activation analysis gave boron levels in the product of 4.2 and 4.3 weight percent. The  13  C NMR spectrum of the product in acetone-d 6  was consistent with a structure of ##STR3## for 72% of the product, with the product apparently containing 2% of 2-(ethylthio)ethanol and 26% of other components of unknown structure. 
     EXAMPLE 3 
     Preparation of Crude Allyldimethylsulfonium Tetrafluoroborate 
     Into a 3-neck 5-liter flask were weighed 1161.6 g (20 moles) of allyl alcohol, 950 g (15.3 moles) of dimethyl sulfide, and 1829 g (10 moles) of 48% aqueous tetrafluoroboric acid. The flask was attached to a large (1.5 liter) capacity Dean-Stark trap (initially filled with dimethyl sulfide) which was attached to a condenser. Reflux was started and an aqueous phase began to accumulate at the bottom of the Dean-Stark trap, displacing dimethyl sulfide back into the reaction mixture. Reflux was continued for six days. At the end of this period, the rate of accumulation of aqueous phase had become very small. The aqueous phase was drained into a tared bottle and weighed; the net weight of the aqueous phase was 1136.7 g. Excess dimethyl sulfide and allyl alcohol were allowed to distill at atmospheric pressure into the Dean-Stark trap until the temperature in the flask had reached 100° C. At this point, the flask was connected to a dry ice trap and vacuum was applied. The mixture in the flask was evaporated at 70° C. under magnetic stirring for one hour, with the pressure decreasing to a final value of 200 Pa. The yield of nonvolatile product was 1952 g. The nonvolatile product was a viscous liquid containing a small amount of crystals. It showed no signs of further crystallization on standing at room temperature. 
     EXAMPLE 4 
     Use of Sulfonium Salts to Accelerate Aromatic Amine Cure of Epoxy Resins Diluted with Acrylic, Allyl and Vinyl Monomers 
     Epoxy Resin A (100 parts), Curing Agent A (25 parts), and monomers and catalysts in the proportions listed in Table 1 were combined at room temperature in polyethylene beakers and mixed thoroughly with Jiffy mixers. Brookfield viscosity and 150° C. gel time were determined on each mixture shortly after mixing. 
     A portion of each mixture was poured into a mold made of two glass plates held 1/8&#34; (3.2 mm) apart with a polytetrafluoroethylene spacer to make a sheet casting. Another portion of each mixture was poured into two aluminum molds containing a linear cavity 1/2&#34; (12.7 mm) square to form bar castings. The sheet and bar molds were placed in an oven and held for two hours at 80° C. and two hours at 150° C. The sheet and bar castings were then removed from the molds and tested for mechanical properties. Mechanical properties are given in Table 1. 
     A number of salient points can be seen from Table 1. First, all of the monomers tested gave considerable reductions in system viscosity. Room temperature tensile strength, modulus and elongation were good in all systems tested. Heat deflection temperature (HDT) and Tg, however, were depressed in comparison with values for the undiluted systems (control experiments; last two experiments in table). Depression of HDT and Tg was greater for monofunctional diluents than for mixtures of monofunctional and closely related multifunctional diluents. It was also greater for acrylate than for similar methacrylate mixtures. Diluent monomers containing nitrogen (N-vinylpyrrolidone and N,N-dimethylacrylamide) raised the gel time of the catalyzed mixtures somewhat in comparison with other monomers. 
     
                                           TABLE 1                                 
__________________________________________________________________________
USE OF SULFONIUM SALTS TO ACCELERATE AROMATIC AMINE CURE OF EPOXY RESINS  
DILUTED WITH ACRYLIC, ALLYL, AND VINYL MONOMERS                           
                              Brookfield                                  
                         150° C.                                   
                              Viscosity,                                  
                                    HDT,                                  
                                        Tg,    R.T. TENSILE               
Run                                                                       
   Monomers, phr                                                          
                Catalysts, phr                                            
                         gel time,                                        
                              24° C.                               
                                    264 psi,                              
                                        Rheometrics                       
                                               Strength,                  
                                                    Modulus,              
                                                         Elongation,      
#  (a)          (b)      Sec. MPa · S                            
                                    °C.                            
                                        °C.                        
                                               MPa  MPa  %                
__________________________________________________________________________
184-1                                                                     
   IBMA (10)             490  1240  135,136                               
                                        157    81   2900 6.2              
   TMPTMA (10)  Lupersol 101 (0.4)                                        
2  IBMA (12)    Catalyst 3 (0.7)                                          
                          97  1390  127,127                               
                                        155    74   2700 5.6              
                Lupersol 101 (0.4)                                        
3  BA (12)      Catalyst 3 (0.7)                                          
                          90  1175   98,102                               
                                        118    64   2500 5.8              
                Lupersol 101 (0.4)                                        
4  IBMA (10)    Catalyst 3 (0.7)                                          
                         110  1225  123,123                               
                                        142    81   2920 6.3              
   TMPTMA (10)  Lupersol 101 (0.4)                                        
5  BA (10)      Catalyst 3 (0.7)                                          
                         115  1125  96,98                                 
                                        120    68   3130 6.6              
   TMPTA (10)   Lupersol 101 (0.4)                                        
6  IBMA (10)    Catalyst 1 (1.0)                                          
                         148  1375  127,129                               
                                        148    78   2800 5.2              
   TMPTMA (10)  Lupersol 101 (0.4)                                        
7  IBMA (10)    Catalyst 2 (1.0)                                          
                         118  1510  125,129                               
                                        147    74   2830 4.6              
   TMPTMA (10)  Lupersol 101 (0.4)                                        
8  Diallyl phthalate (20)                                                 
                Lupersol 101 (2.0)                                        
                         510  1925  87,90                                 
                                        112    72   2900 5.9              
9  Diallyl phthalate (20)                                                 
                Catalyst 3 (0.7)                                          
                         112  2010  82  112    --   --   --               
                Lupersol 101 (2.0)                                        
10 N--Vinylpyrrolidone (15)                                               
                Lupersol 101 (1.0)                                        
                         415  1975  112,113                               
                                        131    84   3120 6.5              
11 N--Vinylpyrrolidone (15)                                               
                Catalyst 3 (0.7)                                          
                         290  1775  89,90                                 
                                        109    79   1600 6.8              
                Lupersol 101 (1.0)                                        
12 N,N--Dimethylacryl-                                                    
                Lupersol 101 (0.4)                                        
                         400  1190  137,117                               
                                        141    82   3040 5.8              
   amide (15)                                                             
13 N,N--Dimethylacryl-                                                    
                Catalyst 3 (0.7)                                          
                         205  1360  95,95                                 
                                        112    74   2950 6.4              
   amide (15)   Lupersol 101 (0.4)                                        
182-1                                                                     
   (none)       Catalyst 3 (0.7)                                          
                          90  --    148,149                               
                                        164    67   2910 3.4              
29-1                                                                      
   (none)       (none)   &gt;300 3850  155,155                               
                                        171    61   2580 4.9              
__________________________________________________________________________
 (a) &#34;IBMA&#34; is isobutyl methacrylate; &#34;TMPTMA&#34; is trimethylolpropane      
 trimethacrylate; &#34;BA&#34; is butyl acrylate; &#34;TMPTA&#34; is trimethylolpropane   
 triacrylate.                                                             
 (b) Catalyst 1 = product of Example 1; Catalyst 2 = product of Example 2;
 Catalyst 3 = product of Example 3 (crude allyldimethylsulfonium          
 tetrafluoroborate).