Vinyl-type interpolymers and uses thereof
This is a continuation of application Ser. No. 527,069, filed Aug. 29, 1983, now abandoned, which is a division of Ser. No. 435,859, filed Oct. 21, 1982, now abandoned, which is a continuation-in-part of U.S. patent application Ser. No. 055,661 filed July 9, 1979, now abandoned. 
    
    
     This invention relates to unique novel demulsifying agents useful in preventing breaking or resolving emulsions of the water-in-oil type and particularly petroleum emulsions. Their use provides an economical and rapid process for resolving petroleum emulsions of the water-in-oil type that are commonly referred to as &#34;cut oil,&#34; &#34;roily oil,&#34; &#34;emulsified oil,&#34; etc. and which comprises fine droplets of naturally-occurring waters or brines dispersed in a more or less permanent state throughout the oil which constitutes the continuous phase of the emulsion. 
     These novel demulsifying agents also provide an economical and rapid process for breaking and separating emulsions which have been prepared under controlled conditions from mineral oil, such as crude oil and relatively soft waters or weak brines. Controlled emulsification and subsequent demulsification under the conditions just mentioned, are of significant value in removing impurities, particularly inorganic salts from pipeline oil, (i.e., desalting). 
     Demulsification as contemplated herein includes the preventive step of commingling the demulsifier with the hydrocarbon phase. Similarly, such demulsifiers may be mixed, emulsified, suspended, etc. in the aqueous component. 
     Heretofore, a wide variety of chemical agents have been employed in the demulsification of such W/O emulsions. Most of the demulsifiers currently in commercial use are oxyalkylated chemical agents. 
     We have now discovered a new class of agents which are effective in the demulsification of W/O emulsions, particularly petroleum W/O emulsions. 
     These novel demulsifiers are in general water insoluble, oil soluble, vinyl-type interpolymers derived from one or more hydrophilic vinyl-type monomers and one or more hydrophobic vinyl-type monomers. Any pair or combination of vinyl-type monomers can be used to prepare these interpolymers provided the following three requirements are met: 
     (1) At least one monomer (referred to as the &#34;hydrophilic&#34; monomer) containing, aside from the vinyl function, only aliphatic carbon atoms and oxygen atoms in such a fashion that the overall carbon atom to oxygen atom ratio in the monomer is about 3.0 or less. (e.g., vinyl acetate, vinyl formate, methyl acrylate, dimethyl maleate, ethyl methacrylate, methyl vinylether, etc.) 
     (2) At least one monomer (referred to as the &#34;hydrophobic&#34; monomer) containing, aside from the vinyl function, only aliphatic carbon atoms or aliphatic carbon atoms and oxygen atoms in such a fashion that the overall carbon atom to oxygen atom ratio in the monomer is about 3.0 or more (e.g., vinyl stearate, dodecyl acrylate, butyl methacrylate, dioctyl maleate, 1-octene, 1-dodecene, dodecyl vinyl ether, etc.). 
     (3) The interpolymers are derived from at least 50 mole % of &#34;hydrophilic&#34; monomer and 50 mole % or less of &#34;hydrophobic&#34; monomer in such a manner that the overall carbon atom to oxygen atom ratio of the interpolymer is between about 2 and about 4. The hydrophilic to hydrophobic mole percent ratios of the monomers can vary widely, such as from about 50/50 to about 95/5, for example from about 75/25 to about 90/10 with an optimum of about 80/20 to 90/10. However, the optimum ratio employed will, of course, depend on the particular monomers employed. They preferably have a random composition and a relatively low molecular weight. 
     The interpolymers of this invention can be viewed as substituted polyethylenes of the following generalized structure: ##STR1## in which A, B, C, D, E, F, etc. may be the same or different functional groups chosen from among: ##STR2## in which R designates --C n  H 2n+1  with n being a whole number, e.g., 0, 1, 2, 3, 4, etc. and wherein a, b, c, d, e, etc. indicate numbers of units of any particular kind, as specified above, incorporated into the random interpolymer. 
     As an indication of the variety of types of interpolymers fitting the above general description, some non-limiting examples of such interpolymers are methyl acrylate/octadecene copolymers, vinyl acetate/distearyl maleate interpolymers, methyl vinylether/dodecyl vinylether copolymers, vinyl acetate/vinyl decanoate copolymers, etc. In this invention these interpolymers are sometimes exemplified by vinyl acetate/vinyl fatty ester copolymers. 
     They are essentially water insoluble, oil soluble interpolymers at room temperature. This indicates that these interpolymers are only soluble to the extent of less than about 0.1% by weight in water and essentially solvent soluble in aromatic type solvents, for example having solubilities of at least about 1% by weight, but preferably at least about 5% in an aromatic solvent. These solubilities may be in an aromatic hydrocarbon solvent alone (toluene, xylene, etc.) or in conjunction with other solvents, for example, lower alkanols (1-50% alkanol in aromatic solvent) such as methanol, propanol, butanol, etc. 
     The specific demulsification agents of this invention are essentially water insoluble, oil soluble interpolymers produced by free radical initiated interpolymerization of at least one &#34;hydrophilic&#34; monomer, e.g. vinyl acetate, and at least one &#34;hydrophobic&#34; monomer, e.g. a vinyl ester. Vinyl acetate (the &#34;hydrophilic&#34; vinyl ester; C/O=2.0, soluble to the extent of 1% or more in water) must constitute at least about 50 mole % of the interpolymer. The &#34;hydrophobic&#34; monomer, e.g. vinylester(s) constituting the remaining less than about 50 mole % of the interpolymer, can in general be any hydrophobic monomer, e.g. vinyl ester CpH 2p-2  O 2 , provided p represents a number equal to or greater than 6 (to meet the required C/O ratio of 3 or higher). Examples of &#34;hydrophobic&#34; monomers according to this definition are: 
     vinyl hexanoate 
     vinyl octanoate 
     vinyl decanoate 
     vinyl laurate 
     vinyl stearate 
     di(stearyl) maleate 
     vinyl palmitate, etc. 
     Methods for the preparation of interpolymers based on combinations of vinyl esters by free radical polymerization are well known to the art. For our purpose any suitable method that will result in the formation of such interpolymers can be used, provided that the resulting interpolymer has the &#34;desired composition&#34; and a relatively low molecular weight (≦200,000). Solutions containing from 25-50% of such materials are generally fluid and easy to handle. 
     Although all compositions within this range exhibit at least some slight demulsifier activity, it should be understood that specific ones among these show much higher activity than others. In general, the more active materials are usually found in interpolymers based upon monomer combinations between &#34;hydrophilic&#34; monomers with low C/O ratios (like vinyl acetate, methylacrylate, etc.) and &#34;hydrophobic&#34; monomers with high C/O ratios (like vinyl stearate, dioctyl maleate, etc.), rather than in interpolymers based on monomer pairs, both with C/O ratios close to 3.0. Those familiar with the art and the general surfactant theory may appreciate this observation in the general context of the HLB principle. 
     As stated in the introduction, only those interpolymers are considered to have &#34;the desired composition&#34; in which the overall carbon to oxygen ratio falls in the specified range from about 2 to about 4. 
     A substantial number of vinyl ester interpolymers were prepared. As stated before, general methods for the preparation of vinyl ester interpolymers by free radical polymerization are well known to the art. With few exceptions all interpolymers of the present invention were prepared according to the following general procedure: To a pressure reactor, 64 parts of the desired molar combination of monomers is charged, followed by 96 parts of solvent (aromatic, e.g., benzene, toluene, xylene, etc.) and initiator (2,2&#39;-azobis(-methylpropionitrile), &#34;VAZO&#34;), 1-3% of the total monomer weight, to give a 40 percent active monomer solution. Before sealing the reactor, its content is purged with nitrogen for 15 minutes. Upon completion of the oxygen removal the reactor is sealed and heated to 65° C. The reaction is maintained at this temperature for 16-24 hours. A small part of the reaction product is then stripped in vacuo to determine conversion of monomers to polymer and to obtain a sample for further analyses. The bulk of the sample is kept as such. 
     Normally the polymer solutions obtained from this procedure were moderately viscous, nicely fluid products with a polymer content of 35-40%. To those familiar with the art of vinyl interpolymerization and the concept of interpolymerization parameters, it will be clear that, even though all monomers are vinyl esters, the desired random interpolymer composition could not in all cases directly be customized by choosing that same ratio in the monomer mixture. It sometimes became necessary to devise a special monomer addition scheme to prepare an interpolymer with the desired composition. In other instances fractionation of polymer batches resulted in samples with a well defined much narrow monomer ratio. 
     Special emphasis was placed on the synthesis of the commercially most attractive interpolymers, namely those copolymers based on vinyl acetate (as the &#34;hydrophilic&#34; monomer) and vinyl-tertiary decanoate (&#34;Versatic-10&#34; monomer Shell) (as the &#34;hydrophobic&#34; monomer). Altogether several hundred interpolymers were prepared and subsequently evaluated for demulsification activity. 
     These interpolymers were evaluated by the method generally referred to as the &#34;Bottle Test&#34; described in &#34;Treating Oil Field Emulsions&#34; second edition, issued by Petroleum Extension Service and the Texas Education Agency in cooperation with the American Petroleum Institute, 1955, (revised 1962) pages 39-44. These evaluations were carried out at wells at various locations as listed below in the following States: 
     
                       TABLE I                                                     
______________________________________                                    
Field                 State                                               
______________________________________                                    
Dixie Pool            Oklahoma                                            
Oregon Basin          Wyoming                                             
Weyburn               Canada                                              
Brookhaven            Mississippi                                         
Manvel                Texas                                               
Thompson              Texas                                               
Pine                  Montana                                             
Crawar                Oklahoma                                            
Fort Zarah            Kansas                                              
Richfield             California                                          
Weeks Island          Louisiana                                           
Elk Basin             Wyoming                                             
Huntington Beach      California                                          
Port Barre            Louisiana                                           
Fruitvale             California                                          
______________________________________                                    
 
    
     It should be understood that specific responses by a particular crude to a specific composition, as determined by this bottle test will vary widely due to the great variety in the nature, composition, character, production method, temperature, etc., etc. of the crude oil in question and the specific interpolymer under evaluation. In order to establish a reliable method to evaluate the relative performance of these vinyl ester interpolymers compared to the activity of commercially available demulsifying agents, as used at different locations, an average overall performance rating was devised as follows: 
     
         ______________________________________                                    
no, or very little, activity                                              
                 0                                                        
little activity  p (poor)                                                 
substantial activity                                                      
                 f (fair)       indicating good,                          
                                commercially sig-                         
excellent activity                                                        
                 g (good)       nificant activity.                        
______________________________________                                    
 
    
     In this rating scheme the field standard, the commercial material actually in use at the particular location is given a g rating, while all experimental materials are judged relatively to this standard. 
     The following Table II describes a cross section of vinyl ester copolymers prepared and evaluated during the course of this invention, (the following abbreviations were used:) 
     VA=vinyl acetate 
     VV-10=vinyl ester of &#34;Versatic-10&#34; (Shell trade name) acid: 
     
         R.sub.1 R.sub.2 R.sub.3 C--CO.sub.2 --CH═CH.sub.2 
    
     
         R.sub.1 +R.sub.2 +R.sub.3 =C.sub.8 H.sub.18 -- 
    
     ViBut=vinyl isobutyrate 
     V-n-Dec=Vinyl normal decanoate 
     V-Stear=Vinyl stearate 
     VF=Vinylformate 
     VP=Vinyl propionate. 
     
                       TABLE II                                                    
______________________________________                                    
                                 Aver-                                    
                                 age                                      
                                 Perfor-                                  
Exam-                      C/O   mance                                    
ple No.                                                                   
      Copolymer  Mole Ratio                                               
                           Ratio Rating                                   
                                       Remarks                            
______________________________________                                    
 1    VA/VV10    100/0     2.0   0     As made                            
 2     &#34;         90/10     2.4   p     &#34;                                  
 3     &#34;         80/20     2.8   f     &#34;                                  
 4     &#34;         70/30     3.2   g     &#34;                                  
 5     &#34;         60/40     3.6   f     &#34;                                  
 6     &#34;         50/50     4.0   p     &#34;                                  
 7     &#34;         40/60     4.4   0     &#34;                                  
 8     &#34;         30/70     4.8   0     &#34;                                  
 9     &#34;         20/80     5.2   0     &#34;                                  
10     &#34;         10/90     5.6   0     &#34;                                  
11    VA/VV10    95.4/4.6   2.18 p     &#34;                                  
12     &#34;         92.9/7.1   2.28 p     &#34;                                  
13     &#34;         90.2/9.8   2.38 p     &#34;                                  
14     &#34;         87.4/12.8  2.50 p     &#34;                                  
15     &#34;         84.3/15.7  2.63 f     &#34;                                  
16     &#34;         81.1/18.9   2.76                                         
                                 g     &#34;                                  
17     &#34;         77.6/22.4  2.90 f     &#34;                                  
18    VA/VV10    87/13      2.52 p     &#34;                                  
19     &#34;         88.6/13.4  2.54 p     Fraction-                          
                                       ated From                          
                                       Ex. 3                              
                                       above*                             
20     &#34;         85.5/14.5  2.58 f     Fraction-                          
                                       ated From                          
                                       Ex. 3                              
                                       above*                             
21     &#34;         83.3/16.7  2.67 f     Fraction-                          
                                       ated From                          
                                       Ex. 3                              
                                       above*                             
22     &#34;         80.1/19.9  2.80 g     Fraction-                          
                                       ated From                          
                                       Ex. 3                              
                                       above*                             
23     &#34;         78.4/21.6  2.86 g     Fraction-                          
                                       ated From                          
                                       Ex. 3                              
                                       above*                             
24     &#34;         74.6/25.4  3.02 f     Fraction-                          
                                       ated From                          
                                       Ex. 3                              
                                       above*                             
25     &#34;         73.6/26.4  3.06 f     Fraction-                          
                                       ated From                          
                                       Ex. 3                              
                                       above*                             
26    VA/ViBut   80/20     2.2   0     As made                            
27     &#34;         60/40     2.4   0     &#34;                                  
28     &#34;         40/60     2.6   0     &#34;                                  
29     &#34;         20/80     2.8   p     &#34;                                  
30     &#34;          0/100    3.0   p     &#34;                                  
31    VA/V-n-    90/10     2.4   0     &#34;                                  
      Dec                                                                 
32    VA/V-n-    85/15     2.6   0     &#34;                                  
      Dec                                                                 
33    VA/V-n-    80/20     2.8   p     &#34;                                  
      Dec                                                                 
34    VA/V-n-    75/25     3.0   f     &#34;                                  
      Dec                                                                 
35    VA/V-n-    70/30     3.2   f     &#34;                                  
      Dec                                                                 
36    VA/V-n-    65/35     3.4   p     &#34;                                  
      Dec                                                                 
37    VA/V-n-    60/40     3.6   0     &#34;                                  
      Dec                                                                 
38    VA/V-Stear 95/5      2.4   0     &#34;                                  
39     &#34;         92.5/7.5  2.6   p     &#34;                                  
40     &#34;         90/10     2.8   p     &#34;                                  
41     &#34;         87.5/12.5 3.0   p     &#34;                                  
42     &#34;         85/15     3.2   p     &#34;                                  
43     &#34;         82.5/17.5 3.4   p     &#34;                                  
44     &#34;         80/20     3.6   0     &#34;                                  
45    VT/VV10    77.8/22.2 2.5   0     &#34;                                  
46     &#34;         72.2/27.8  2.75 p     &#34;                                  
47     &#34;         66.4/33.3 3.0   0     &#34;                                  
48     &#34;         61.1/38.9  3.25 0     &#34;                                  
49     &#34;         55.6/44.4 3.5   0     &#34;                                  
50     &#34;         50/50      3.75 0     &#34;                                  
51    VP/V-Stear 96.7/3.3   2.75 0     &#34;                                  
52     &#34;         93.3/6.7  3.0   0     &#34;                                  
53     &#34;         90/10      3.25 0     &#34;                                  
54     &#34;         86.7/13.3 3.5   0     &#34;                                  
55     &#34;         83.3/16.7  3.75 0     &#34;                                  
56     &#34;         80/20     4.0   0     &#34;                                  
______________________________________                                    
 *Examples 19 through 25 contain copolymers fractionated from Example 3 of
 Table II (mole ratio 80/20) to yield the mole ratio shown in the specific
 examples 19 through 25.                                                  
 
    
     Although specific interpolymers may end up with a low average overall rating (o,p) in the above table, such products may well score high at another particular location, or vice versa, as can be seen from the specific examples that follow. 
     It is also often observed that specific types of materials perform exceptionally well in one particular phase of the demulsification process, although blending with components contributing complementary activity is required to form a &#34;complete&#34; compound. So these &#34;single component&#34; vinyl ester interpolymers for this reason may score less than the field standards which are always blends of several ingredients. 
    
    
     The following examples of bottle tests are presented for purposes of illustration and not of limitation. 
     EXAMPLE 57 
     A crude oil emulsion, produced in the Oregon Basin, Wyo., contained 34% water. The demulsifier to be tested was added, as a 1% solution, to 100 ml of the emulsion. After shaking for 4 minutes (at 200 shakes per minute) the treated emulsion was allowed to quietly settle for two hours. The resultant top oil was then sampled at about half-way total liquid depth and analyzed for water content with the following results (Table III). 
     
                       TABLE III                                                   
______________________________________                                    
                           Residual H.sub.2 O in                          
Product of Example:                                                       
               ml of 1% Soln.                                             
                           treated oil                                    
______________________________________                                    
Commercial blend A                                                        
               .25         1.2%                                           
In use at location                                                        
               .20          .7%                                           
Commercial blend B                                                        
               .15         1.4%                                           
In use at location                                                        
               .20         1.0%                                           
Example No. 26 .20         4.8%                                           
Example No. 27 .20         4.4%                                           
Example No. 28 .20         1.2%                                           
Example No. 29 .20         0.5%                                           
Example No. 30 .20         0.9%                                           
Example No. 32 .20         8.8%                                           
Example No. 33 .20         3.4%                                           
Example No. 34 .20         1.2%                                           
Example No. 35 .20         1.2%                                           
Example No. 36 .20         5.3%                                           
______________________________________                                    
 
    
     EXAMPLE 58 
     An emulsion sample was taken from the production in the Twining Field in Alberta, Canada. This emulsion contained 50% water. It was treated with a 1% solution of chemical per 100 ml., shaken for 200 shakes and analyzed after a quiet settling period of 45 minutes with the following results (Table IV). 
     
                       TABLE IV                                                    
______________________________________                                    
                           Percent residual                               
Product of Example                                                        
               ml of 1% soln.                                             
                           H.sub.2 O in treated oil                       
______________________________________                                    
Commercial compound                                                       
               1.8 ml.     0.5%                                           
in use                                                                    
Example 33      &#34;          0.6%                                           
Example 34      &#34;          0.4%                                           
Example 35      &#34;          0.4%                                           
______________________________________                                    
 
    
     EXAMPLE 59 
     An emulsion, containing 30-35% water was sampled while hot from the Fruitvale Field, Bakersfield, Cal. The sample was heated, 5% solution of chemical was added and shaken hot (≈96° C.) for five minutes at 150 shakes per minute. After quietly settling at 96° C. for four hours, the top oil was sampled, close to the interphase, and analyzed for residual water with the following results: 
     
                       TABLE V                                                     
______________________________________                                    
                           % residual water                               
Product of Example:                                                       
               ml 5% soln. in treated oil                                 
______________________________________                                    
Standard in use                                                           
               .5 ml       1.8%                                           
Commercial C    &#34;           .8%                                           
Example 46      &#34;          12.0%                                          
Example 47      &#34;          17.0%                                          
Example 11      &#34;          1.6%                                           
Example 12      &#34;          1.8%                                           
Example 13      &#34;           .8%                                           
Example 14      &#34;          1.0%                                           
Example 15      &#34;           .4%                                           
Example 16      &#34;           .2%                                           
Example 17      &#34;          1.6%                                           
Example 56      &#34;          34.0%                                          
______________________________________                                    
 
    
     A preferred embodiment of this invention pertains to interpolymers of a hydrophilic monomer and a hydrophobic dialkyl maleate monomer, e.g., vinyl acetate/dialkyl maleate interpolymers having an overall C/O atom ratio of between about 2 and about 4 and having about 50 mole % or more hydrophilic monomer and 50 mole % or less dialkyl maleate, e.g. 50-99 mole % vinyl acetate and, correspondingly, 50-1 mole % dialkyl maleate, preferably 65-97 mole % vinyl acetate and, correspondingly, 35-3 mole % dialkyl maleate. Especially useful is a copolymer of about 75-95 mole % vinyl acetate and, correspondingly, about 25-5 mole % dialkyl maleate. 
     The hydrophobic dialkyl maleate constituting 50 mole % or less of the copolymer can in general be any dialkyl maleate characterized by the general formula: 
     
         C.sub.p H.sub.2P-4 O.sub.4 
    
     provided p represents a number equal to or greater than 12 (to meet the required C/O ratio of 3 or higher). 
     Examples of dialkyl maleate monomers according to the above definition are dibutyl maleate, dihexyl maleate, dioctyl maleate, di-(2-ethylhexyl) maleate, di-dodecyl maleate, di-octadecyl maleate, ethylhexyl maleate, octadecyl maleate, mixed dialkyl maleates and the like. 
     A substantial number of dialkyl maleate-containing interpolymers were prepared. General methods for the preparation of copolymers of hydrophilic esters like vinyl acetate with hydrophobic maleate esters by free radical polymerization are known. The dialkyl maleate-containing interpolymers were prepared according to the following general procedure: 
     To a pressure reactor are charged vinyl acetate, aromatic solvent and part of the dialkyl maleate. After purging with nitrogen, 1-3% benzoyl peroxide (based on combined monomer weight) is added and the polymerization started by heating to 50°-55° C. An exotherm carries the reaction to 70°-75° C. After 6-8 hours at this temperature additional dialkyl maleate is added according to a special co-monomer addition scheme in order to prepare copolymers with the desired composition. 
     Normally the polymer solutions obtained from this procedure were moderately viscous, nicely fluid products with a polymer content of 40-60%. To those familiar with the art of vinyl copolymerization and the concept of copolymerization parameters, it will be clear that the desired random copolymer composition could not in all cases directly be customized by choosing that same ratio in the monomer mixture. It sometimes became necessary to devise special co-monomer addition schemes to prepare copolymers with the desired composition. In other instances fractionation of polymer batches resulted in samples with a well defined much narrower co-monomer ratio. 
     Special emphasis was placed on the synthesis of the commercially most attractive copolymers, namely those based on vinyl acetate (as the &#34;hydrophilic&#34; monomer) and di-(2-ethylhexyl) maleate (as the &#34;hydrophobic&#34; monomer). Altogether several hundred copolymers were prepared and subsequently evaluated for demulsification activity. 
     These copolymers were evaluated by the method generally referred to as the &#34;Bottle Test&#34; described in &#34;Treating Oil Field Emulsions&#34; second edition, issued by Petroleum Extension Service and the Texas Education Agency in cooperation with the American Petroleum Institute, 1955, (revised 1962) pages 39-44. These evaluations were carried out at wells at various locations. A cross section of many of these is listed below: 
     
                       TABLE VI                                                    
______________________________________                                    
Field                 Location                                            
______________________________________                                    
Huntington Beach      California                                          
Heidelberg            Mississipi                                          
Elk Basin             Wyoming                                             
Thompsons             Texas                                               
Three Hills           Canada                                              
Port Barre            Louisiana                                           
Dixie Pool            Oklahoma                                            
Sand Flats            Texas                                               
Baxterville           Mississippi                                         
Tyler                 Texas                                               
Oregon Basin          Wyoming                                             
Notrees               Texas                                               
Stafford              Kansas                                              
Twining               Canada                                              
Fruitvale             California                                          
______________________________________                                    
 
    
     It should be understood that specific responses by a particular crude to a specific composition, as determined by this bottle test will vary widely due to the great variety in the nature, composition, character, production method, temperature, etc., etc. of the crude oil in question and the specific interpolymer under evaluation. In order to establish a reliable method to evaluate the relative performance of these interpolymers compared to the activity of commercially available demulsifying agents, as used at different locations, an average overall performance rating was devised as follows: 
     
         ______________________________________                                    
no, or very little, activity                                              
                 0                                                        
little activity  P (poor)                                                 
substantial activity                                                      
                 F (fair)       indicating good                           
                                commercially sig-                         
excellent activity                                                        
                 G (good)       nificant activity.                        
______________________________________                                    
 
    
     In this rating scheme the field standard, the commercial material actually in use at the particular location is given a G rating, while all experimental materials are judged relatively to this standard. 
     The following Table VII describes a cross section of copolymers prepared and evaluated during the course of this invention, (the following abbreviations were used:) 
     VA=Vinyl acetate 
     DBM=Dibutyl maleate 
     DDM=Didecyl maleate 
     DEHM=Di(2-ethylhexyl) maleate 
     DDOM=Didodecyl maleate 
     DA 1218  M=Di(&#34;Alfol&#34;-1218) maleate 
     DODM=Dioctadecyl maleate 
     DMM=Dimethyl maleate 
     
                       TABLE VII                                                   
______________________________________                                    
                                 Average                                  
Ex-                              Perfor-                                  
am-                        C/O   mance                                    
ple  Copolymer   Mole Ratio                                               
                           Ratio Rating Remarks                           
______________________________________                                    
60   VA/DBM      95/5      2.09  0      As made                           
61               90/10     2.18  P      &#34;                                 
62               80/20     2.33  0      &#34;                                 
63               65/35     2.52  0      &#34;                                 
64               50/50     2.66  0      &#34;                                 
65   VA/DDM      95/5      2.38  F      &#34;                                 
66               92.5/7.5  2.55  G      &#34;                                 
67               90/10     2.72  F      &#34;                                 
68               87.5/12.5 2.88  P      &#34;                                 
69               85/15     3.04  P      &#34;                                 
70               82.5/17.5 3.19  P      &#34;                                 
71               80/20     3.33  P      &#34;                                 
72   VA/DEHM     95/5      2.28  F      &#34;                                 
73               90/10     2.55  G      &#34;                                 
74               80/20     3.0   G      &#34;                                 
75               65/35     3.55  P      &#34;                                 
76               50/50     4     0      &#34;                                 
 77* VA/DEHM     98/2      2.11  0      Isolated                          
                                        fractions                         
78               95/5      2.28  0      Isolated                          
                                        fractions                         
79               93/7      2.39  P      Isolated                          
                                        fractions                         
80               90/10     2.55  F      Isolated                          
                                        fractions                         
81               87/13     2.69  F      Isolated                          
                                        fractions                         
82               83/7      2.87  G      Isolated                          
                                        fractions                         
83               79/21     3.04  G      Isolated                          
                                        fractions                         
84               74/26     3.23  F      Isolated                          
                                        fractions                         
85               70/30     3.38  F      Isolated                          
                                        fractions                         
 86*             60/40     3.71  P      Isolated                          
                                        fractions                         
87   VA/DDOM     97.5/2.5  2.24  P      As made                           
88               95/5      2.47  F      &#34;                                 
89               92.5/7.5  2.69  P      &#34;                                 
90               90/10     2.90  P      &#34;                                 
91               87.5/12.5 3.11  P      &#34;                                 
92               85/15     3.30  P      &#34;                                 
93   VA/DA.sub.1218 M                                                     
                 98/2      2.10  0      &#34;                                 
94               97/3      2.16  P      &#34;                                 
95               96/4      2.21  F      &#34;                                 
96               95/5      2.26  F      &#34;                                 
97               94/6      2.31  G      &#34;                                 
98               92/8      2.40  F      &#34;                                 
99               90/10     2.50  P      &#34;                                 
100              87.5/12.5 2.61  P      &#34;                                 
101  VA/DODM     95/5      2.76  P      &#34;                                 
102              92.5/7.5  3.11  P      &#34;                                 
103              90/10     3.45  F      &#34;                                 
104              87.5/12.5 3.77  P      &#34;                                 
105              85/15     4.08  0      As made                           
106              80/20     4.66  0      &#34;                                 
107  VA/DMM      95/5      1.95  0      &#34;                                 
108              90/10     1.90  0      &#34;                                 
109              85/15     1.86  0      &#34;                                 
110              75/25     1.80  0      &#34;                                 
111              65/35     1.74  0      &#34;                                 
112              50/50     1.66  0      &#34;                                 
______________________________________                                    
 *Examples 77 through 86 contain copolymer fractions from Example 74 (mole
 ratio 80/20) to yield narrower compositions with the mole ratio shown.   
 
    
     Although specific interpolymers may end up with a low average overall rating (o,p) in the above table, such products may well score high at another particular location, or vice versa, as can be seen from the specific examples that follow. 
     It is also often observed that specific types of materials perform exceptionally well in one particular phase of the demulsification process, although blending with components contributing complementary activity is required to form a &#34;complete&#34; compound. So these &#34;single component&#34; copolymers for this reason may score less than the field standards which are always blends of several ingredients. 
     The following examples of bottle tests are presented for purposes of illustration and not of limitation. 
     EXAMPLE 113 
     A crude oilfield emulsion, containing 40% water was sampled in the Heidelberg field in Mississippi. The sample was treated at 27° C. by the addition of 1% solution of chemical, to 100 ml emulsion and shaking 100 times to mix in the chemical and observing the results after quiet settling for a one hour period. The resultant top oil was then sampled at half way total liquid depth and analyzed for water content with the following results (Table VIII). 
     
                       TABLE VIII                                                  
______________________________________                                    
                            Residual H.sub.2 O                            
Product of Example                                                        
               ml of 1% Solution                                          
                            in Treated Oil                                
______________________________________                                    
Commercial Blend A                                                        
               1.0          0.4%                                          
In use at location                                                        
               0.3          1.2%                                          
Commercial Blend B                                                        
               0.3          2.1%                                          
Example Number 73                                                         
               1.0          0.2%                                          
Example Number 73                                                         
               0.3          1.4%                                          
 Example Number 109                                                       
               0.3          26.7%                                         
Example Number 66                                                         
               0.3          1.2%                                          
______________________________________                                    
 
    
     EXAMPLE 114 
     An emulsion sample was taken from the production in the Twining Field in Alberta, Canada. This emulsion contained 50% water. It was treated with a 1% solution of chemical per 100 ml, shaken for 200 shakes and analyzed after a quiet settling period of 45 minutes with the following results (Table IX): 
     
                       TABLE IX                                                    
______________________________________                                    
                            Percent Residual                              
Product of Example                                                        
               ml of 1% Solution                                          
                            H.sub.2 O in Oil                              
______________________________________                                    
Commercial Compound                                                       
               1.0          1.1%                                          
In use         .5            .8%                                          
Example No. 84 .5            .1%                                          
Example No. 62 .5           7.4%                                          
Example No. 97 .5           1.9%                                          
 Example No. 112                                                          
               .5           39.0%                                         
______________________________________                                    
 
    
     EXAMPLE 115 
     A crude emulsion sample was taken from production in the Sand Flats Field in Texas. This sample contained 28% highly emulsified water. 100 ml samples of this crude emulsion were treated with 1% solutions of various demulsifiers. After quiescent settling for 90 minutes at 71° C., following 150 shakes to mix in the demulsifier, the top oil was analyzed, close to the oil water interface. Results are listed in Table X: 
     
                       TABLE X                                                     
______________________________________                                    
                             Percentage                                   
Product of Example                                                        
                ml of 1% Solution                                         
                             H.sub.2 O in Oil                             
______________________________________                                    
Commercial Compound                                                       
                1.2          0.6                                          
In use          0.9          0.9                                          
Example No. 84  0.9          2.0                                          
Example No. 82  0.9          1.0                                          
Example No. 98  0.9          1.2                                          
Example No. 64  0.9          19.0                                         
Example No. 70  0.9          4.7                                          
______________________________________                                    
 
    
     Although in all examples given the hydrophilic monomer selected was mainly vinyl acetate, such selection was mainly a matter of convenience and the scope of this invention is much broader and is not to be limited thereby. 
     To illustrate the breadth of this invention, the following examples will illustrate copolymers prepared from hydrophilic monomers other than vinyl acetate, e.g., methyl methacrylate, methyl acrylate, ethyl acrylate, vinyl propionate and vinyl formate. These interpolymers are, in general, prepared by methods discussed above and well-known to those skilled in the art. In some cases (e.g. Examples 126-129) the copolymers were prepared by more elaborate procedures (e.g. polymerization of an MA.BF 3  complex with an olefin, followed by purification and fractionation). 
     Table XI summarizes a small cross-sectional of co- and ter-polymers prepared with hydrophilic monomers other than vinyl acetate. The materials selected for Table XI were especially chosen from those materials which showed good activity when evaluated in demulsification applications. 
     The following abbreviations are used in Table XI: 
     MMA=methyl methacrylate 
     MA=methyl acrylate 
     IBMA=isobutyl methacrylate 
     EA=ethyl acrylate 
     EHMA=2-ethylhexyl methacrylate 
     StMA=stearyl methacrylate 
     LMA=lauryl methacrylate 
     EHA=2-ethylhexyl acrylate 
     HEMA=hydroxyethyl methacrylate 
     HPMA=hydroxypropyl methacrylate 
     C 6  O=C 6  -α olefin (hexene) 
     C 14  O=C 14  -α olefin (tetradecene) 
     C 20  O=C 20  -α olefin (eicosene) 
     VP=vinyl propionate 
     VF=vinyl formate 
     DEHM=di(2-ethylhexyl)maleate 
     
         ______________________________________                                    
                                  Aver-                                   
                                  age                                     
Ex-                               Perfor-                                 
am-  Co(Ter)                C/O   mance                                   
ple  Polymer     Mole Ratio Ratio Rating                                  
                                        Remarks                           
______________________________________                                    
116  MMA/IBMA    60/40      3.1   0     As made                           
117  MMA/EHMA    85/15      3.0   0     &#34;                                 
118  MMA/StMA    90/10       3.35 P     &#34;                                 
119  MMA/LMA     90/10       3.05 P     &#34;                                 
120  MA/EHMA     75/25      3.0   P     &#34;                                 
121  MA/StMA     92/8        2.72 F     &#34;                                 
122  MA/EHA      70/30       3.05 G     &#34;                                 
123  MA/EHMA     72.5/27.5  3.1   G     &#34;                                 
124  MA/EHMA     70/30      3.2    G-   &#34;                                 
125  MA/EHMA     67.5/32.5  3.3    G-   &#34;                                 
126  MA/C.sub.14 O                                                        
                 81.8/18.2   3.55 G     purified                          
                                        fraction                          
127  MA/C.sub.6 O                                                         
                 62.5/37.5  3.8   P     purified                          
                                        fraction                          
128  MA/C.sub.20 O                                                        
                 81.8/18.2  4.2   0     purified                          
                                        fraction                          
129  EA/C.sub.14 O                                                        
                 85.5/14.5   3.68 F     purified                          
                                        fraction                          
130  VP/DEHM     70/30       3.65 0     As made                           
131  VF/VV-10    77.8/22.2   2.38 0     &#34;                                 
132  MA/EHMA     67.5/32.5  3.3   F     &#34;                                 
133  VA/HEMA/    68/3/29     3.33 G     &#34;                                 
     DEHM                                                                 
134  VA/HPMA/    63.6/9/27.4                                              
                             3.24 G     &#34;                                 
     DEHM                                                                 
135  MA/HEMA/    66.7/4.8/28.5                                            
                             3.11 F     &#34;                                 
     EHMA                                                                 
136  VA/HEMA/    60.8/13.1/26.1                                           
                             3.18 F     &#34;                                 
     DEHM                                                                 
137  MA/EHMA     65/35      3.4   F     &#34;                                 
138  MA/EHMA     90/10      2.4   P     &#34;                                 
139  MA/HEMA/    66.6/4.8/28.6                                            
                             3.11 F     &#34;                                 
     EHMA                                                                 
______________________________________                                    
 
    
     It will be apparent to those skilled in the art from the above description and examples that the demulsification process of this invention can be carried out with numerous interpolymers as defined and especially with the preferred embodiment, i.e., the interpolymers derived from at least one hydrophilic monomer and at least one hydrophobic monomer including a dialkyl maleate. 
     In lieu of a list of several thousand monomer combinations which fall within the scope of the invention, it should suffice to note that those skilled in the art of vinyl polymerization, and in view of the teachings herein, have sufficient guidelines to make and use demulsifiers within the scope of the parameters defined and exemplified above. 
     Although amply illustrated above, the most highly preferred hydrophilic monomers used to prepare the demulsifiers illustrated are vinyl acetate, vinyl formate, vinyl propionate, methyl acrylate, methyl methacrylate, dimethyl maleate and methyl vinyl ether. The most highly preferred hydrophobic monomers are the vinyl esters of &#34;Versatic-10&#34; acid, vinyl isobutyrate, vinyl n-decanoate, vinyl stearate, isobutyl methacrylate, 2-ethylhexyl methacrylate, stearyl methacrylate, lauryl methacrylate, 2-ethylhexyl acrylate, tetradecene, hexene, eicosene, di(2-ethylhexyl)maleate, dibutyl maleate, didodecyl maleate, didecyl maleate and di(&#34;Alfol&#34;-1218) maleate. 
     The foregoing examples represent a cross-section of a far larger group of vinyl-type copolymers that were thoroughly evaluated. No demulsifier activity was observed for compositions outside the claimed compositions. In those cases where apparent activity originally seemed present outside the approximately 2-4 C/O range, further purification and fractionation of the initially obtained crude copolymer led to the final identification of the active fraction as the one with a composition within the claimed composition. To those familiar with the art of vinyl copolymerization and the concept of copolymerization parameters, it will be clear that the desired copolymer compositions can not always be directly obtained from the original ratio as present in the monomer mixture. It is often necessary to devise a special monomer addition scheme to prepare a copolymer with the desired composition. 
     While we have shown and described various embodiments in accordance with the present invention which has described interpolymers and their use in the demulsification of emulsions, it is understood that the same is not limited thereto but is susceptible of various changes and modifications. For example, in addition to copolymers, ter- and higher polymers can also be employed. In addition, the interpolymers may also contain other elements besides carbon, hydrogen and oxygen, provided such elements do not interfere with their function in this invention.