High impact thermoplastic polyamide molding compositions
This invention relates to thermoplastic molding compositions having improved impact strength at low temperatures comprising polyamides and grafted, at least partially cross-linked diene rubbers and/or acrylate rubbers having a bimodal rubber particle sizes distribution. 
     Moldings of polyamides have been successful because of their mechanical strength, such as their rigidity, abrasion resistance, hardness, dynamic and thermal stability, and the ease with which they can be produced. Their main disadvantage is unsatisfactory toughness. 
     Numerous proposals have been made towards improviding the toughness of polyamide molding compositions by the addition of other polymers Thus, polyolefins (DE-OS Nos. 16 94 802, 20 38 317 and 30 22 295) and ethylene ionomers (EP-A Nos. 34 704, 69 200, and 72 480) have been proposed. Grafted acrylate rubbers and grafted diene rubbers which have a specific graft structure and which have been produced by specific processes have also been proposed (EP-A No. 3 126 and DE-OS Nos. 27 58 615, 31 01 771 and 31 20 803). 
     The proposed molding compositions generally show improved toughness. However, it has been found that molding compositions of this type are not always totally satisfactory for certain applications, for example in the automotive field, where strong deformation forces occur in the event of collisions, affecting for example bodywork, fenders and spoilers, steering wheel and steering column. Molding compositions intended for applications such as these have to meet particular requirements, even at low temperatures of the order of -20° C. or even -30° C. 
     Accordingly, the present invention provides thermoplastic molding compositions comprising: 
     A. from 65 to 97% by weight, preferably from 70 to 95% by weight and, more preferably from 75 to 90% by weight (based on components A+B) of polyamide and 
     B. from 3 to 35% by weight, preferably from 5 to 30% by weight and, more preferably, from 10 to 25% by weight (based on components A+B) of graft product 
     of at least one vinyl monomer selected from styrene, acrylonitrile and methyl methacrylate on particulate, at least partially crosslinked diene rubbers and/or alkyl acrylate rubbers having average rubber particle diameters of from 0.05 to 1 μm and the graft products having a rubber content of from 60 to 85% by weight, preferably from 65 to 80% by weight and, more preferably, from 70 to 75% by weight, characterised in that the graft product B is produced on the basis of a mixture of 
     (a) from 20 to 80% by weight, preferably from 30 to 70% by weight and, more preferably, from 35 to 60% by weight (based on a+b) of a rubber latex having a particle diameter d 50  of from 0.05 to 0.19 μm and preferably from 0.08 to 0.15 μm and 
     (b) from 80 to 20% by weight, preferably from 70 to 30% by weight and, more preferably, from 65 to 40% by weight (based on a+b) of a rubber latex having a particle diameter d 50  of from 0.2 to 1 μm, preferably from 0.25 to 0.8 μm and, more preferably from 0.3 to 0.6 μm 
     with the limitation that 
     (1) d 50  (b) is larger than d 50  (a) by a factor of from 1.5 to 8, preferably from 2.7 to 5, in particular from 3 to 4.5, 
     (2) the quotient Q=(d 90  -d 10 )/d 50  of the particular rubbers is at most 2, preferably at most 1.8, in particular at most 0.8, and 
     (3) the difference d 10  (b)-d 90  (a) is from 0.01 to -0.10, preferably from 0 to -0.08 and in particular from 0 to -0.05. 
     The percentage by weight above are referred to the solids content. 
     The graft product B may be produced either by mixing a rubber latex corresponding to (a) and a rubber latex corresponding to (b) in the required quantitative ratio and graft polymerizing the vinyl monomer onto the resulting mixture or by separately graft polymerizing the vinyl monomers onto a rubber latex corresponding to (a) and onto a rubber latex corresponding to (b) and then mixing the two graft products (either in the form of latices, followed by co-precipitation or in the form of the solids already present). The second method is preferred. 
     These molding compositions are more suitable for the above-mentioned applications than known molding compositions and, moreover, they do not have any significant disadvantages. 
     It is essential to use at least partially cross-linked diene rubbers and/or alkyl acrylate rubbers having rubber particle diameters d 50  of from 0.05 to 1 μm and a &#34;bimodal&#34; particle diameter distribution. 
     This means that by combining particular coarsely-divided rubbers with particular finely divided rubbers in the form of graft polymers B molding compositions according to the invention having considerably improved properties are obtained; for this purpose, the particle size distribution of the rubbers which are used for the preparation of component B has to be bimodal and should exhibit two pronounced maxima. In order to obtain the effect associated with these specific particle size distribution, it is, however, necessary to start with rubber having a particle size distribution conforming to specific parameters: 
     These include a critical width of the distribution curve (expressed by the quotient Q), a critical distance between the maxima of the distribution curve (expressed by the difference d 50  (b)-d 50  (a)) and a critical overlapping of the distribution curves (expressed by the difference d 10  (b)-d 90  (a)). 
     The molding compositions according to the invention are distinguished by the fact that, irrespective of their modifier content, they remain impact-resistant at temperatures down to -20° C. and, in some cases, down to -30° C. and by the fact that their toughness properties only begin to deteriorate at temperatures below those levels. 
     This effect according to the invention is all the more surprising insofar as finely particulate rubber only improves the impact strength of thermoplastic polyamides whilst coarsely divided rubbers result in a continuous deterioration in toughness with decreasing temperature. 
     The effect according to the invention was not foreseeable because known ABS-plastics, which contain both coarsely and finely divided graft rubbers together (cf. DE-AS No. 24 20 358), undergo a continuous deterioration in toughness with decreasing temperature, which is what had been expected to occur here also. 
     The graft products B include graft polymers having elastomeric properties of the type obtained by grafting vinyl monomers from the group consisting of styrene, acrylonitrile and methyl methacrylate onto particulate, at least partially crosslinked diene rubbers and/or alkyl acrylate rubbers. 
     Preferred graft monomers are methyl methacrylate and also mixtures of styrene and methyl methacrylate or styrene and acrylonitrile. 
     Diene rubbers are particulate, crosslinked homo-and/or copolymers of conjugated C 4  -C 6  -dienes. The preferred diene is 1,3-butadiene. In addition to the diene residues, the diene copolymers may contain up to 30% by weight, based on the copolymer, of residues of other ethylenically unsaturated monomers, for example styrene, acrylonitrile, esters of acrylic or methacrylic acid with monohydric alcohols containing from 1 to 4 C-atoms, for example methyl acrylate, ethyl acrylate, methyl methacrylate and ethyl methacrylate. 
     The production of the diene rubber graft base and of the graft polymers is known and is described, for example, in &#34;Methoden der Organischen Chemie&#34; (Houben-Weyl), Vol. 14/1, Georg Thieme Verlag, Stuttgart 1961, pages 393 to 406 and also in Ullmanns Encyclopadie der technischen Chemie, 4th Edition, Vol. 19, Verlag Chemie 1981, pages 279 to 284. 
     Alkyl acrylate rubbers are particulate, cross-linked alkyl acrylate polymers obtained by the polymerization of esters of acrylic acid and monohydric alcohols containing from 1 to 8 C-atoms. The polymers may also be copolymers of acrylic acid esters with up to 40% by weight of other vinyl monomers, such as styrene, acrylonitrile, methyl methacrylate, vinyl esters and vinyl ethers. 
     The alkyl acrylate rubbers are crosslinked, for example, by the copolymerization of polyfunctional, copolymerizable, ethylenically unsaturated comonomers, having a crosslinking effect. Monomers containing more than one polymerizable double bond may be copolymerized for crosslinking. Preferred examples of crosslinking monomers are esters of unsaturated monocarboxylic acids containing from 3 to 8 C-atoms and unsaturated monohydric alcohols containing from 3 to 12 C-atoms or saturated polyols containing from 2 to 4 OH-groups and from 2 to 20 C-atoms, for example ethylene glycol dimethacrylate, allyl methacrylate; polyunsaturated heterocyclic compounds, for example trivinyl and triallyl cyanurate and isocyanurate, tris-acryloyl-s-triazines; more particularly triallyl cyanurate; polyfunctional vinyl compounds, such as di- and tri-vinyl benzenes; and also triallyl phosphate and diallyl phthalate. 
     Preferred crosslinking monomers are allylmethacrylate, ethylene glycol dimethacrylate, diallyl phthalate and heterocyclic compounds containing at least three ethylenically unsaturated groups. 
     Particularly preferred crosslinking monomers are the cyclic monomers triallyl cyanurate, triallyl isocyanurate, trivinyl cyanurate, triacryloyl hexahydro-s-triazine and triallyl benzenes. 
     The crosslinking monomers are preferably used in quantities of from 0.02 to 5% by weight and, more preferably, in quantities of from 0.05 to 2% by weight, based on the rubber graft base. 
     In the case of cyclic crosslinking monomers containing at least three ethylenically unsaturated groups, it is advantageous to use no more than 1% by weight, based on the rubber graft base. 
     Alkyl acrylate rubbers may also be multiple-shell products which contain a crosslinked diene rubber of one or more conjugated dienes, such as polybutadiene, or a copolymer of a conjugated diene with an ethylenically unsaturated monomer, such as styrene and/or acrylonitrile, as the core and poly(meth)acrylate graft-polymerized as a shell onto that core. 
     The percentage of polydiene core in multiple-shell rubber graft bases of this type may amount to between 0.1 and 80% by weight and preferably to between 10 and 50% by weight. Shell(s) and core may be partially crosslinked or highly crosslinked independently of one another. 
     The diene rubbers and the alkyl acrylate rubbers are in the form of particles having an average diameter of d 50  of from 0.05 to 1 μm and are at least partially crosslinked. They have gel contents of ≧50% by weight, preferably ≧80% by weight and, more preferably ≧90% by weight. 
     The advantageous particle diameter d may be determined by ultracentrifuge measurements (W. Scholtan, H. Lange, Kolloid Z. and Z. Polymere 250 (1972), 782-796) or by electron microscopy, followed by particle counting (G. Kaempf, H. Schuster, Angew. Makromolekulare Chemie 14, (1970) 111-129). 
     If the particle size distributions are determined by means of electron microcopy and subsequent counting of the particles, number averages (and not weight averages) are obtained. Number averages thus determined do then, however, have to be converted into weight averages to make them comparable with the values d 10 , d 50 , d 90  given herein. This conversion can be carried out, for instance, by the method of W. Scholtan and H. Lange and provides the same or nearly the same values for both methods. Furthermore, reference is made to DIN (German Industrial Standard) 53 206 in which conversions of particle size distributions are defined. 
     The average particle sizes given in this application are in all cases the weight averages of the particle size as determined by means of an analytical ultracentrifuge according to the method of W. Scholtan and H. Lange, Kolloid-Z. and Z. Polymere 250 (1972), pages 782-796. The ultracentrifuge determination provides the integral mass distribution of the particle diameter of the specimen. From this it is possible to conclude which percentage by weight of the particles have a diameter equal to or smaller than a particular size. The average particle diameter which is also termed the d 50  value of the integral mass distribution is defined as that particle diameter at which 50% by weight of the particles have a diameter equal to or smaller than the diameter eualling the d 50  value. In order to characterise the width of the size distribution of the rubber particles, the d 10  and d 90  values taken from the integral mass distribution are used in addition to the d 50  value (average particle diameter). The d 10  and d 90  values of the integral mass distribution are defined in the same same way as the d 50  value, but with the difference that they refer to 10 and 90%, by weight, of the particles. The quotient ##EQU1## is a criterion for the width of the distribution of the particle size: 
     The difference d 10  (b)-d 90  (a) is a criterion for the overlapping of the curves: If the difference is positive, there is no or only a slight overlapping of the curves; if the difference is negativ, a curve overlapping exists, the extent of which is given by the size of the negative value. 
     As already stated, it is also possible to determine the number average distribution of the rubber particles and then to convert these into weight averages. The microscopic counting method according to Kampf et al. is the more exact, the greater the number of particles counted; usually, at least 10 4  particles should be measured which then, after statistical evaluation, provide a particle size number average distribution curve. It is, for instance, possible in this procedure to select the particle size classes to be of such a size that 90% of the particles are distributed over not less, but not more than 20 classes. 
     It must, however, be added that the rubber particles in the moulding compositions are in a grafted state; it could, therefore, be assumed that the grafting has changed the rubber particle size compared with the rubber particles present in the rubber latices (for the preparation of B). It has, however, been found that the grafting as well as the quantity of the graft shell, according to the characteristics described herein, hardly influence the rubber particle size so that distribution curves determined from molding compositions can be compared with distribution curves determined from latices. 
     The gel content of the diene rubbers is determined in toluene at 25° C. and the gel content of the alkyl acrylate rubber is determined in dimethyl formamide at 25° C. (M. Hoffmann, H. Kroemer, R. Kuhn, Polymeranalytik I and II, Georg Thieme Verlag Stuttgart, 1977). 
     Preferred grafted alkyl acrylate rubbers are those which 
     a. are crosslinked with cyclic trifunctional comonomers, such as triallyl cyanurate and triallyl isocyanurate (as described in DE-OS No. 30 39 114), 
     b. contain a polybutadiene core (as described in DE-OS No. 30 39 115), 
     c. have been produced in the &#34;absence of suspending agents&#34; (as described in DE-OS No. 31 17 052). 
     The rubber content which is most favourable for the production of the molding compositions according to the present invention depends, among other things, on the rubber particle diameter in each case and on the graft density. 
     Rubbers having the particle diameters according to the invention may be obtained by the emulsion polymerization of suitable monomers. In the emulsion polymerization processes known for that purpose, the latex particle diameters may be adjusted in dependence upon the process conditions selected, for example in dependence upon the type and concentration of the emulsifier, particle agglomeration, electrolytes, temperatures and monomer/polymer concentration. 
     Where the graft products B are produced by graft copolymerization, which is normally carried out in the presence of radical initiators, for example water, soluble initiators, emulsifiers or complexing agents/ graft activators, and also regulators, free polymers or copolymers of the graft monomers forming the graft shell are also generally formed to a certain extent in addition to the actual graft copolymer. The quantity of this ungrafted polymer may be characterized by the degree of grafting or by the grafting yield which depends inter alia upon the polymerization conditions, upon the composition of the rubber graft base, upon the size of the particles to be grafted and upon the quantity of grafted rubber graft base. 
     Accordingly, graft product B in the context of the present invention is the product obtained by the polymerization of vinyl monomers in the presence of the rubber latices which, strictly speaking, is generally a mixture of graft copolymer and free (co)polymer of the graft monomers. 
     The molding compositions according to the invention show optimal properties when the quantity of free (co)polymer of the graft monomers does not exceed certain limits. This upper limit is generally set at 15% by weight, preferably at 10% by weight and, more preferably of A+B. In addition, the Staudinger Index [η] of these free (co)polymers is usually ≦0.6 dl/g and preferably ≦0.4 dl/g, as measured in dimethyl formamide at 25° C. 
     To obtain certain technological properties, it may even be advantageous separately to produce the polymers of the graft monomers and then to incorporate them in the molding compositions by mixing during their production. However, the separately produced polymer of the graft monomers may also be present during the graft (co)polymerization process. It is also possible to separate any excess polymer of the graft monomers from the graft products B. The particular procedure adopted will depend upon the polymerization process selected, upon the particular type of rubber graft base, upon the type and quantity of graft monomers and upon the required technological properties of the molding compositions. 
     The preferred procedure is that in which the graft polymerization of the graft monomers onto the rubber particles is carried out and controlled in such a way that the graft product compositions required in accordance with the invention are formed and, at the same time, the graft monomer polymer contents optionally required are also obtained. 
     Special polymers such as these, consisting of graft polymers in admixture with suitable graft monomer polymers, may then be directly used for producing the molding compositions. In such cases, the graft branch polymers may of course be largely indentical in chemical terms with the graft monomer polymers. However, it is also possible in accordance with the present invention for the graft monomer polymers to differ chemically from the graft monomers used for grafting. For example, a polymethyl methacrylate may be used as the graft monomer polymer and, at the same time, a styrene-acrylonitrile-grafted rubber as graft product B. Combinations such as these may afford certain advantages in regard to practical application. 
     The &#34;bimodal&#34; graft products B may be produced by any one of various methods. Thus, they may be produced by grafting a dispersion of finely divided rubber particles (corresponding to a) with monomers, subsequently mixing this graft polymer emulsion with a separately prepared graft polymer dispersion of coarsely divided rubber particles and subsequently working up the resulting mixture. 
     The rubber particle dispersions (latices) may also be mixed and the graft monomers subsequently graft-polymerized onto the resulting mixture, particularly in aqueous emulsion, by means of radical-forming systems, followed by working up in known manner. However, it is also possible separately to produce finely diVided and coarsely divided graft products and to mix then with the thermoplastic polyamides for producing the molding compositions according to the invention. 
     In the processes comprising separate grafting and common working up of the graft product on the one hand and in the separate production of finely divided and coarsely divided graft product on the other hand, it is also possible to use graft products in which the finely divided and coarsely divided components differ structurally from one another. Accordingly, these processes are preferred. 
     Suitable polyamides A are any thermoplastic polyamides, preferably partially crystalline polyamides. Thus polyamide-6, polyamide-6,6 and copolymers of these two components may be used as partially crystalline polyamides for the molding compositions according to the invention. In addition, it is possible to use partially crystalline polyamides of which the acid component consists completely or partly of terephthalic acid and/or isophthalic acid and/or suberic acid and/or sebacic acid and/or azelaic acid and/or adipic acid and/or cyclohexane dicarboxylic acid; of which the diamine component consists completely or partially of m- and/or p-xylene diamine and/or hexamethylene diamine and/or 2,2,4-trimethyl hexamethylene diamine and/or 2,4,4-trimethyl hexamethylene diamine and/or isophorone diamine and of which the composition is known from the prior art. 
     Other suitable polyamides are those of the type produced completely or partly from C 6  -C 12  -lactams, optionally in conjunction with one or more of the starting components previously mentioned. 
     Particularly preferred partially crystalline polyamides are polyamide-6 and polyamide-6,6. 
     The polyamides should have a relative viscosity (as measured on 1% by weight solution in m-cresol at 25° C.) of preferably from 2.0 to 5.0 and, more preferably, from 2.5 to 4.5. 
     The molding compositions according to the present invention may contain standard additives, such as lubricants and mold release agents, nucleating agents, stabilizers, fillers and reinforcing materials, flameproofing agents and dyes. 
     The fillers or reinforced molding compositions may contain up to 60% by weight, based on the reinforced molding composition, of fillers and/or reinforcing materials. Preferred reinforcing materials are glass fibers. Preferred fillers, which may also have a reinforcing effect, are glass beads, mica, silicates, feldspar, quartz, talcum, titanium dioxide and wollastonite. 
     The flameproofed molding compositions contain flameproofing agents generally in a concentration of less than 30% by weight, based on the flameproofed molding compositions. 
     Any known flameproofing agents may be used, including, for example, cyclic chlorine compounds, melamine and its salts, such as melamine cyanurate or melamine sulfate, and red phosphorus. 
     The molding compositions may be produced in the usual mixing units, such as mixing rolls, kneaders, single-screw and multiple-screw extruders. 
     Although, in most cases, all the resin components are best mixed in a single step, it may also be advisable in some cases initially to omit one or even two components and to add them at a later stage. 
     Thus, the molding compositions according to the invention may be produced in the above-mentioned mixing units by melting and homogenizing the two components A and B together or by incorporating the graft product B into a melt of the polyamide A. 
     The temperature prevailing during the preparation of the mixtures is generally at least 10 ° C. and best at most 80° C. above the melting point of the polyamide. The molding compositions according to the invention are distinguished by improved toughness. An outstanding feature is the improvement in toughness at low temperatures. 
     Commensurate with their property spectrum, the molding compositions according to the invention may be used anywhere in the injection molding and extrusion field where moldings are exposed to severe impact stressing, for example in the automotive field for fenders, spoilers, buffer strips, body components, steering wheels and steering columns. 
     The invention is illustrated by the following Examples. 
    
    
     EXAMPLES 
     I. Polyamide-6 having a relative viscosity of 3.5 (as measured on a 1% by weight solution in m-cresol at 25° C.). 
     II. Polyamide-6,6 having a relative viscosity (measured in the same way as for I) of 3.0. 
     III. Grafted polybutadiene rubber 
     III.1. Production of polybutadiene latices 
     III.1.1 The following emulsion was polymerized with stirring in a reactor at 65° C. until the monomer conversion was substantially complete (approx. 22 hours): 
     
         ______________________________________                                    
100.0       parts by weight of butadiene;                                 
1.8         parts by weight of the sodium                                 
            salt of disproportionated abietic                             
            acid;                                                         
0.257       part by weight of sodium hydroxide;                           
0.3         part by weight of n-dodecyl mer-                              
            captan;                                                       
1.029       parts by weight of Na--ethylene                               
            diamine tetra-acetate;                                        
0.023       part by weight of potassium per-                              
            sulfate; and                                                  
176.0       parts by weight of water.                                     
______________________________________                                    
 
    
     A latex is obtained, containing butadiene polymer particles with an average diameter (d 50 ) of 0.1 μm in a concentration of approximately 35-36%, by weight. The polybutadiene particles have gel contents of 90-95% by weight (as measured in toluene at 23° C.). 
     III 1.2. The following emulsion was polymerized for about 110 hours at 60°-68° C. by the procedure according to III.1.1: 
     
         ______________________________________                                    
100.0       parts by weight of butadiene;                                 
70.0        parts by weight of water;                                     
1.146       parts by weight of the sodium                                 
            salt of disproportionated abietic                             
            acid;                                                         
0.055       part by weight of Na--ethylene                                
            diamine tetra-acetate;                                        
0.137       part by weight of sodium hydroxide;                           
0.028       part by weight of sodium hydrogen                             
            carbonate; and                                                
0.282       part by weight of potassium                                   
            persulfate.                                                   
______________________________________                                    
 
    
     A latex is obtained, containing polybutadiene particles with an average diameter (d 50 ) of 0.4 μm in a concentration of approximately 58% by weight. The polybutadiene particles have gel contents of 90 to 91% by weight (as measured in toluene at 23° C.). 
     III.2 Production of graft products 
     (a) Parts by weight of polydiene latex and (b) parts by weight of water are initially introduced with stirring into a reactor at 65° C. After initiation with (c) parts by weight of potassium persulfate, 100 parts by weight of methyl methacrylate and, separately therefrom, a mixture of (d) parts by weight of water, (e) parts by weight of the sodium salt of disproportionated abietic acid and (f) parts by weight of 1N aqueous sodium hydroxide are metered thereto over a period of several hours. The mixture is then left to polymerize at 65°-75° C. to a final conversion of 98% by weight. The quantitative data of these graft polymerization reactions are shown in the following Table. 
     
                       TABLE 1                                                     
______________________________________                                    
Production of graft products                                              
      Latex   Latex                                                       
Type  III 1.1 III 1.2  b    c     d     e    f                            
______________________________________                                    
A     --      690      100  0.50  100   4.0  3.0                          
B     228     551      100  0.52  100   4.2  3.1                          
C     --      517      150  0.58  100   4.8  3.5                          
D     171     414      100  0.52  100   4.8  3.5                          
E     --      402      233  0.67  100   5    3.66                         
F     666     --       134  0.66  100   6.25 4.37                         
G     133     322      190  0.66  100   5.1  3.8                          
H     200     281      170  0.66  100   5.3  3.9                          
I     266     241      135  0.66  100   5.4  3.0                          
J     333     201      100  0.66  100   5.5  4.0                          
K     400     161       80  0.66  100   5.6  4.1                          
L     533      81       29  0.66  100   5.6  4.5                          
M     333     201       80  0.50  100   4.0  3.5                          
______________________________________                                    
 
    
     For the above graft products and for the rubber bases thereof, the following relations exist (as far as rubber mixtures are concerned): ##EQU2## 
     
                       TABLE 2                                                     
______________________________________                                    
Composition of the graft products                                         
                                    Ungrafted                             
                                    MMA-resin.sup.1                       
                                    parts by                              
                           Graft    weight in                             
                           monomer  100 parts                             
     Polybutadiene                                                        
                 Graft base                                               
                           methyl meth-                                   
                                    by weight                             
     III.1.1 % by                                                         
                 III.1.2 % acrylate %                                     
                                    of graft                              
Type weight.sup.2                                                         
                 by weight.sup.2                                          
                           by weight.sup.2                                
                                    polymer                               
______________________________________                                    
A    --          80        20        9                                    
B    16          64        20        8                                    
C    --          75        25       11                                    
D    15          60        25       10                                    
E    --          70        30       15                                    
F    70          --        30       13                                    
G    14          56        30       15                                    
H    21          49        30       15                                    
I    28          42        30       15                                    
J    35          35        30       15                                    
K    42          28        30       15                                    
L    56          14        30       15                                    
M    39          39        22       .sup. ./..sup.3                       
______________________________________                                    
 .sup.1 [η]DMF = 0.18-0.31 dl/g, as measured at 25° C.         
 .sup.2 Total composition of the graft product disregarding the ungrafted 
 resin present                                                            
 .sup.3 The graft product M does not contain any free MMAresin (free      
 MMAresin in the graft product was removed by extraction with methylene   
 chloride).    IV. Grafted polyacrylate rubber                            
 
    
     IV. 1 Finely divided acrylate rubber 
     The following components were initially introduced into a reactor: 
     1030 parts by weight of water and 
     5 parts by weight of sodium salt of C 14  -C 16  - alkyl sulfonic acids. 
     80 parts by weight of solution 1 (see below) are run in at 70° C. Polymerization is the initiated by the addition of 5 parts by weight of potassium peroxydisulfate in 100 parts by weight of water. The following solutions are then run in: 
     
         ______________________________________                                    
Solution 1:  995 parts by weight of  -n-butyl                             
             acrylate; and                                                
             5 parts by weight of triallyl                                
             cyanurate (80 parts by weight of                             
             this solution were introduced before                         
             and the rest after initiation).                              
Solution 2:  20 parts by weight of the sodium                             
             salts of C.sub.14 -C.sub.18 --alkyl sulfonic acids           
             and 700 parts by weight of water.                            
______________________________________                                    
 
    
     After the addition of solutions 1) and 2) over a period of 5 hours at 70° C., polymerization is continued for 4 hours at 70° C. A latex having a solids content of 35% by weight is formed. The latex particle size is 0.09 μm (latex IV.1). 
     IV.2 Coarsely divided acrylate rubber 
     The following solutions are used: 
     
         ______________________________________                                    
Starting solution 1:                                                      
                12.4 parts by weight of                                   
                latex IV.1; and                                           
                313 parts by weight of water;                             
Starting solution 2:                                                      
                0.82 part by weight of                                    
                potassium peroxy disulfate;                               
                and                                                       
                20 parts by weight of water;                              
Addition 1:     629 parts by weight of  -n-                               
                butyl acrylate; and                                       
                1 part by weight of triallyl                              
                cyanurate;                                                
Addition 2:     700 parts by weight of the                                
                sodium salts of C.sub.14 -C.sub.16 --alkyl                
                sulfonic acids.                                           
______________________________________                                    
 
    
     Starting solution 1 is heated at 65°-68° C., after which 24 parts by weight of addition 1 are introduced. After initiation with starting solution 2, the rest of addition 1 and addition 2 are run in over a period of 5 hours, followed by stirring over a period of 4 hours. The latex has a solids content of 37% by weight. The latex particle size is 0.5 μm. The polymer has a gel content of 93% by weight and a swelling index (1) of 8, as measured in DMF at 23° C. (latex IV.2). 
    
     IV.3 Production of the graft products of acrylate rubber and methyl methacrylate 
     General procedure: 
     The following solutions or latices are polymerized in a reactor: 
     
         ______________________________________                                    
Starting solution 1:                                                      
               latex IV.1 or latex IV.2:                                  
               A parts by weight;                                         
Starting Solution 2:                                                      
               potassium peroxydisulfate:                                 
               2 parts by weight;                                         
Water:         120 parts by weight;                                       
Addition 1:    methyl methacrylate: 304 parts by                          
               weight;                                                    
Addition 2:    sodium salts of C.sub.14 -C.sub.16 --alkyl sul-            
               fonic acids: 6 parts by weight;                            
Water:         396 parts by weight.                                       
______________________________________                                    
 
    
     Starting solution 1 is introduced into starting solution 2 at 65° C., followed by the introduction of addition 1 and addition 2 over a period of 4 hours at 65° C. The mixture is then left to polymerize to completion at 65° C. (4 h) (latex IV.3). The graft polymer latices are further treated as follows: 
     
         ______________________________________                                    
Starting solution 3:                                                      
               Water: 5525 parts by weight;                               
               MgSO.sub.4 × H.sub.2 O (Epsom salt):                 
               107 parts by weight;                                       
Addition 3:    latex IV.3: B parts by weight;                             
Addition 4:    methyl methacrylate: 156 parts by                          
               weight;                                                    
Activator:     potassium peroxydisulfate:                                 
               1.3 parts by weight;                                       
               Water: 78 parts by weight.                                 
______________________________________                                    
 
    
     Starting solution 3 is heated with thorough stirring to 70°-73° C. Addition 3 is then introduced over a period of 1 hour. Thereafter addition 4 is introduced over a period of 30 minutes, followed by activation with the activator solution. After heating to 80° C., the mixture is stirred for 2 hours, hours. After stabilization with 2 parts by weight of phenolic oxidation inhibitor, the reaction mixture is worked up by filtration, washing and drying to form a powder. 
     
                       TABLE 3                                                     
______________________________________                                    
Production of the graft products                                          
A parts by weight    B parts by weight                                    
Type    latex IV.2 latex IV.1                                             
                             latex IV.3                                   
______________________________________                                    
N       3286.4     ./.       3795                                         
O       ./.        3474.3    4011                                         
P       1643       1737      3900                                         
______________________________________                                    
 
    
     
                       TABLE 4                                                     
______________________________________                                    
Composition of the graft products                                         
Polyacrylate graft base                                                   
                     Graft Shell                                          
parts by weight.sup.1                                                     
                     methyl methacrylate                                  
Type   latex IV.1  latex IV.2                                             
                             parts by weight                              
______________________________________                                    
N      ./.         70        30                                           
O      70          ./.       30                                           
P      35          35        30                                           
______________________________________                                    
 .sup.1 based on solids content                                           
 
    
     The graft products N, O and P contain approximately 12% by weight of non-grafted MMA-resin with an intrinsic viscosity (Staudinger Index [η] of 0.3 dl/g, as measured in DMF at 25° C. 
     B. Production and testing of the molding compositions 
     EXAMPLES 1-24 
     The components were melted and homogenized in a continuous-action twin-screw extruder. The barrel temperatures were selected such that the melt temperatures indicated in Tables 5 to 7 were maintained. The melt strand was degassed before issuing from the nozzle, cooled in water, granulated and dried. 
     Standard small test bars were produced from the molding compositions in an injection molding machine. Notched impact strength was tested at the temperatures indicated (in accordance with DIN 53 453). 
     EXAMPLES 25-27 
     As in Examples 1 to 24, the graft polymer was mixed with molten polyamide in the extruder. Chopped glass fibers 6 mm long were then introduced into and homogeneously distributed in the molten mixture. 
     After the melt had been degassed before issuing from the nozzle and the melt strand discharged into water, granulated and dried, standard small test bars were produced in the same way as described above. Impact strength and nothced impact strength were tested at various temperatures (in accordance with DIN 53 453). The results are shown in Table 8. 
     
                                           TABLE 5                                 
__________________________________________________________________________
Component                                                                 
I              III                                                        
Polyamide      Graft product                                              
                          Notched impact strength (kJ/m.sup.2)            
Example                                                                   
     Type                                                                 
        % by weight                                                       
               Type                                                       
                   % by weight                                            
                          +20° C.                                  
                               -20° C.                             
                                    -30° C.                        
                                         -40° C.                   
__________________________________________________________________________
.sup.  1.sup.1                                                            
     PA-6                                                                 
        80       A 20     ub.  20        10                               
 2   PA-6                                                                 
        80       B 20     ub.  ub.       12                               
.sup.  3.sup.1                                                            
     PA-6                                                                 
        79       C 21     ub.  22        12                               
 4   PA-6                                                                 
        79       D 21     ub.  ub.       13                               
.sup.  5.sup.1                                                            
     PA-6                                                                 
        78       E 22     ub.   23*  15* 12                               
.sup.  6.sup.1                                                            
     PA-6                                                                 
        78       F 22     50   14   10    8                               
 7   PA-6                                                                 
        78       G 22     ub.  ub.  ub.  14                               
 8   PA-6                                                                 
        78       H 22     ub.  ub.  ub.  16                               
 9   PA-6                                                                 
        78       I 22     ub.  ub.  ub.  17                               
10   PA-6                                                                 
        78       J 22     ub.  ub.  ub.  20                               
11   PA-6                                                                 
        78       K 22     ub.  ub.  ub.  16                               
12   PA-6                                                                 
        78       L 22     ub.  ub.  ub.  12                               
13   PA-6                                                                 
        85       J 15     ub.            10                               
14   PA-6                                                                 
        90       J 10     35              7                               
        78       E 11                                                     
15   PA-6                 ub.  ub.  ub.  19                               
                 F 11                                                     
__________________________________________________________________________
 *The test bars were only cracked in the                                  
 .sup.1 Comparative tests                                                 
 
    
     The melt temperature in the extruder was 280° C. and, in the injection molding machine, 260° C.; the mold temperature was 80° C. The percentage by weight indicated are based on the molding composition. 
     
                                           TABLE 6                                 
__________________________________________________________________________
Component                                                                 
II              III                                                       
Polyamide       Graft product                                             
                           Notched impact strength (kJ/m.sup.2)           
Example                                                                   
     Type                                                                 
         % by weight                                                      
                Type                                                      
                    % by weight                                           
                           +20° C.                                 
                                -20° C.                            
                                     -30° C.                       
                                          -40° C.                  
__________________________________________________________________________
.sup. 16.sup.1                                                            
     PA-6,6                                                               
         78       E 22     ub.  20   15   10                              
.sup. 17.sup.1                                                            
     PA-6,6                                                               
         78       F 22     45*  14   10   6                               
18   PA-6,6                                                               
         78       J 22     ub.  ub.  ub.  15                              
19   PA-6,6                                                               
         85       J 15     ub.            8                               
20   PA-6,6                                                               
         90       J 10     ub.            6                               
                  E 11                                                    
21   AP-6,6                                                               
         78                ub.            6                               
                  F 11                                                    
__________________________________________________________________________
 The melt temperature in the extruder was 280-290° C. and, in the  
 injection molding machine, 270° C.; the mold temperature was      
 80° C. The percentages by weight indicated are based on the moldin
 compositions.                                                            
 *The test bars were only cracked in the                                  
 .sup.1 Comparative tests                                                 
 
    
     
                       TABLE 7                                                     
______________________________________                                    
Component                                                                 
I              IV                                                         
Polyamide      Graft product                                              
                          Notched impact                                  
         % by         % by    strength (kJ/m.sup.2)                       
Example Type   weight  Type weight                                        
                                  +20° C.                          
                                         -20° C.                   
______________________________________                                    
.sup. 22.sup.1                                                            
        PA-6   78      N    22    ub.    10                               
.sup. 23.sup.1                                                            
        PA-6   78      O    22    20     4                                
24      PA-6   78      P    22    ub.    15                               
______________________________________                                    
 The melt temperature in the extruder was 280° C. and, in the      
 injection molding machine, 270° C.; the mold temperature was      
 80° C. The percentages by weight are based on the molding         
 compositions.                                                            
 
    
     
                                           TABLE 8                                 
__________________________________________________________________________
Component                                                                 
I              IV               Impact Strength                           
                                         Notched impact strength          
Polyamide      Graft product                                              
                         Glass fiber                                      
                                kJ/m.sup.2                                
                                         kJ/m.sup.2                       
Example                                                                   
     Type                                                                 
        % by weight                                                       
               Type                                                       
                  % by weight                                             
                         % by weight                                      
                                20° C.                             
                                    -20° C.                        
                                         20° C.                    
                                               -20° C.             
__________________________________________________________________________
25.sup.1                                                                  
     PA-6                                                                 
        60     N  10     30     55  50   18    15                         
26.sup.1                                                                  
     PA-6                                                                 
        60     O  10     30     45  40   14    12                         
27.sup.                                                                   
     PA-6                                                                 
        60     P  10     30     ub. ub.  ub.   ub.                        
__________________________________________________________________________
 The melt temperature in the extruder was 280° C. and, in the      
 injection molding machine, 270° C.; the mold temperature was      
 80° C. The percentages by weight are based on the molding         
 compositions.                                                            
 .sup.1 Comparative tests