Transparent, impact-resistant molding compositions based on polyvinyl chloride
BACKGROUND OF THE INVENTION 
     The present invention relates to impact-resistant, transparent molding compositions based on polyvinyl chloride or on copolymers comprising at least about 80% by weight of vinyl chloride units. 
     It is known to improve the impact resistance of polyvinyl chloride by polymerizing vinyl chloride in the presence of an elastomer or by blending polyvinyl chloride with elastomer proportions. The resultant products are generally opaque. 
     Molding compositions of modified polyvinyl chloride having both impact resistance and a certain transparency have, however, also been described in the literature. Thus, DAS No. 2,013,020 describes transparent graft copolymers. In their manufacture, first of all a monomer blend of styrene or α-methylstyrene is graft-polymerized, in the presnce of comonomers having crosslinking effect and in the presence of acrylic and methacrylic acid nitrile or of acrylic and methacrylic acid esters, onto a butyl or 2-ethylhexyl acrylate polymer. Subsequently, polymerization of the vinyl chloride in suspension is carried out in the presence of the thus-produced graft polymer. Apart from the fact that the aforedescribed mode of operation for producing the rubber-elastic phase is expensive due to the plurality of steps and components, the notched impact resistance values demonstrated in the examples are comparatively low. 
     Transparent, impact-resistant polyvinyl chloride molding compositions have also been disclosed in German Patent No. 2,621,522. These molding compositions consist of three components, namely a vinyl chloride homo- or copolymer, a graft copolymer wherein methyl methacrylate and styrene are grafted on a butadiene rubber, and finally a copolymer of α-methylstyrene, methyl methacrylate, acrylonitrile, and optionally a further, copolymerizable monomer. On the one hand, this involves an expensive multistage process whose sequence of addition of the numerous components is disclosed as extraordinarily critical, even during the preparation of the elastomer proportion; on the other hand, a large number of components is employed; and, finally, the resultant molding compositions are not weatherable on account of the butadiene proportion (cf. DAS No. 2,013,020, column 1, lines 60 et seq.). 
     This disadvantage of lack of weatherability is eliminated in molding compositions wherein chlorinated polyethylene is added to raise the impact resistance of polyvinyl chloride, as described, for example, in German Pat. No. 2,456,278. Here, there is the drawback of the narrow limits for the chlorine content (38-42%), which can be maintained only with difficulty in performing the process; additionally, only low impact resistance values can be attained. Thus, for example, with the addition of 10% by weight of the special chlorinated polyethylene, impact resistances of only 7-8 kJ/m 2  are produced. 
     SUMMARY OF THE INVENTION 
     Accordingly, it is an object of this invention to eliminate or ameliorate the above-discussed disadvantages of the state of the art, e.g., to provide transparent and weatherable molding compositions having improved impact resistance requiring only a comparatively low expense for their manufacture. 
     Upon further study of the specification and appended claims, further objects and advantages of this invention will become apparent to those skilled in the art. 
     It has now been found, surprisingly, that these objects are attained by providing transparent, impact-resistant molding compositions based on polyvinyl chloride or on copolymers containing at least about 80% by weight of vinyl chloride units, containing as the component imparting impact resistance, homo- and/or copolymers of monomers having the following formula ##STR1## wherein x is 1-4 and 
     R is H, CH 3 , or Cl, 
     wherein the difference of the indices of refraction n D   20  (at 20° C., measured with the Na D line) of the basic polymer and that of the component imparting impact resistance is at most ±0.01; and, optionally, including other acrylic acid ester monomers. 
     DETAILED DESCRIPTION 
     Suitable amounts of the component imparting impact resistance in the molding compositions are 3-30%, preferably 6-15%, especially 8-12% by weight, based on the total weight of the mixture of polyvinyl chloride and/or vinyl chloride mixed or co-polymer and the component imparting impact resistance. 
     Preferably, the difference of the indices of refraction n D   20  (at 20° C., measured with the Na D line) between that of the basic polymer per se and the component imparting impact resistance per se is especially to be limited to ±0.005, especially to ±0.002, thereby minimizing refractive and scattering effects and maintaining the desired transparency e.g., transmittances of 93-100% or more of the value of that of pure bulk PVC, e.g., at wavelengths in the visible region, e.g., about 600 nm. 
     In general, all of the homo and copolymers of the foregoing formula will be useful in most, if not all, polyvinyl chloride compositions, i.e., will have the necessary small refractive index difference with the PVC component. In the rare case where a given homo- or copolymer of the foregoing formula does not satisfy the refractive index requirement described above, there will always be another polymer of this formula which will satisfy the requirements for all PVC compositions. When this happens, only routine experimentation will be required to determine the relative refractive indices and only routine experimentation will be required to determine the structure of an alternative homo- or copolymer of the foregoing formula which will satisfy the refractive index difference requirement. For example the refractive index decreases if x of polymers according to the foregoing formula increases and vice versa. The refractive index of polymers according to the foregoing formula increases by changing R from CH 3  to H to C1. Furthermore the refractive index decreases in a given copolymer of the foregoing formula with increasing amount of the aliphatic acrylic ester. 
     Homo- and copolymeric acrylic acid esters of oxethylates of phenol are preferred as the component imparting impact resistance. Especially preferred are those wherein x is 2 or 3, respectively. The component imparting impact resistance should have an average molecular weight of M w  =5×10 4  to 10 7 , preferably 5×10 4  to 5×10 6 , and can contain 0-30% by weight, preferably 0-10% by weight, of acrylic ester(s) of aliphatic unbranched alcohols of 4-10 carbon atoms and/or aliphatic branched alcohols of 6-10 carbon atoms as the comonomers incorporated by polymerization. When included in the impact resistance component, these optional comonomers are usually included in an amount of at least 0-30%. 
     Such added polymers can have the formula ##STR2## wherein x is 1-3 
     R is H, CH 3 , or C1, and 
     n is a number in the range of 50 to 50,000. 
     The component imparting impact resistance can also have been produced in the presence of 0.1-2.0% by weight, preferably 0.5-1.0% by weight of crosslinking agents, or they can have been reacted prior to their incorporation into the molding compositions of this invention with crosslinking agents. Examples of suitable conventional crosslinking agents include diallyl phthalate, maleic acid diallyl ester, divinylbenzene, etc. 
     The polymerization of vinyl chloride to form homo or copolymers can be accomplished in fully conventional manner. Any of the methods of bulk, emulsion, or suspension polymerization can be utilized, as described, for example, on pages 1-59 of the monograph by Kainer, &#34;Polyvinylchlorid und Vinylchlorid-Mischpolymerisate&#34; [Polyvinyl Chloride and Vinyl Chloride Copolymers], Springer Publishers, Berlin/Heidelberg/New York (1965) whose disclosure is incorporated herein. Similarly, the copolymers of vinyl chloride with comonomers are made conventionally. Suitable comonomers include the usual olefinic compounds, e.g., vinyl esters, such as vinyl acetate, vinylidene halogenides, such as vinylidene chloride, acrylic acid and methacrylic acid alkyl esters of 1-18 carbon atoms in the alkyl group, such as the methyl, n-butyl, and lauryl esters, esters of maleic acid, such as diethyl, dipropyl maleate, and monoolefins, such as ethylene or propylene, etc. The comonomers are included up to an extent of 30 wt. % as long as the weight of vinyl chloride units in the total amount of polyvinyl chloride component in the molding composition is maintained at a level of at least 80 wt. %. Mixtures of polyvinyl chlorides can be used, e.g., homo PVC and one or more co-PVC&#39;s, or two or more co-PVC&#39;s. 
     By using the polymers imparting impact resistance, made up of acrylic esters of oxethylates of phenol and/or of substituted phenols, the polyvinyl chloride molding compositions of this invention not only have good transparency and considerably improved notched impact resistances, e.g., values of about 13-27 kJ/m 2  (DIN 53453; 4 mm) but also are obtained in a simpler way than using prior art methods. The latter require the utilization of polymers built up of several components and produced accordingly only with considerable expense and difficulty. 
     The monomers used to produce the soft components to be added according to this invention to the polyvinyl chloride composition are, in contrast to the above, obtainable readily and thus economically from oxethylates (accessible by simple ethylene oxide addition to the corresponding phenols), by converting the oxethylates, by direct esterification or by ester interchange with acrylic acid and/or the esters thereof, into the desired monomers of the foregoing formula. Reference is had to the pertinent literature with respect to oxethylation of phenols as well as production of monomeric acrylic esters; typical, in this connection, are, for example, the review articles in M. J. Schick, &#34;Nonionic Surfactant&#34; Vol. I (1967) and in J. K. Haken, &#34;Synthesis of Acrylic Esters by Transesterification&#34; (1967), Noyes Development Co., whose disclosures are incorporated by reference herein. 
     The acrylate monomers and the polymers obtainable therefrom have been disclosed, in part. Thus, phenoxyethyl acrylate and phenoxyethoxyethyl acrylate have been synthesized before and have been polymerized in various ways (cf. U.S. Pat. Nos. 2,396,434, 2,458,888, as well as J. Org. Chem. 14 [1949] 1094, all of whose disclosures are incorporated by reference herein). The suitability of such polymers for use as the soft component of impact-resistant, transparent PVC molding compositions has not heretofore been recognized. Even in German Pat. No. 2,846,573, describing a process for producing heat-curable synthetic resin compositions as a substitute for polyvinyl chloride plastisols, the range of utilization according to this invention has not been perceived. In the past, the inducement for using 2-phenoxy(polyethoxy)ethyl acrylates was in all cases their low vapor pressure under the processing conditions of the prior art compositions, or the desire of purposely influencing the end use properties (such as, for example, dyeability) by using polar molecular components. 
     The polymers to be used according to this invention as the component imparting impact resistance can be produced by customary polymerization in bulk, in solution, or in emulsion from the afore-mentioned monomers, analogously as has been disclosed in the monograph &#34;Acrylic Resins&#34; by Horn, Reinhold Publishing Corp. (1960), pages 26-29, or in Houben-Weyl, &#34;Methoden der Organischen Chemie&#34; [Methods of Organic Chemistry], 4th edition (1961), vol. 14, part 1, pp. 1010 et seq., whose disclosures are incorporated by reference herein. 
     The polymers can be prepared especially advantageously by emulsion polymerization. Suitable emulsifiers are the conventional types. Especially suitable are ionic emulsifiers, e.g., alkyl sulfonates such as sodium stearyl sulfonate, sodium oleyl sulfonate, etc. Furthermore suitable are alkyl sulfates, e.g., sodium lauryl sulfate, sodium stearyl sulfate, and sodium oleyl sulfate, etc., as well as salts of carboxylic acids, such as sodium caprate, sodium laurate, sodium myristate, sodium palmitate, etc. It is also possible to use the above-mentioned classes of compounds with statistical distributions of the aliphatic chain lengths of C 12  -C 18 . Also suitable are arylalkyl sulfonates, for example the sodium salt of p-n-dodecylbenzenesulfonic acid; mixtures of emulsifiers can likewise be employed. The concentration of the emulsifiers is 0.3-3% by weight, preferably 0.5-2.0% by weight, based on the amount of monomer. 
     Suitable catalysts include the water-soluble compounds usually employed in emulsion polymerization, such as water-soluble azo initiators, e.g., 2,2&#39;-azobis [2-amidinopropane] hydrochloride, or similar compounds disclosed in the literature (see, for example, Nuyken and Kerber, &#34;Makromol. Chem.&#34; [Macromolecular Chemistry] 179 : 2845-2857 [1978]); also persulfates, optionally combined with a reducing component such as water-soluble bisulfite, hydrogen peroxide combined with reducing components such as bisulfite, hydrazine, or ascorbic acid; also, combinations of the aforementioned catalysts can be used, optionally in the presence of activating components, such as, for example, copper salts. The usual concentrations are employed. Among the listed initiators, water-soluble azo initiators are preferred. Especially preferred is 2,2&#39;-azobis[2-amidinopropane] dihydrochloride. 
     Suitable temperatures in the emulsion polymerization are usually 40°-90° C., preferably 50°-70° C. The temperature that is optimum for individual initiators can routinely be determined from the initiator decomposition data known from the literature. The same applies for the phase ratio of monomer/water, which usually should range from 1/10 to 1/1. 
     In solution polymerization, the following solvents can be utilized, for example: aliphatic saturated carboxylic acid esters, e.g., ethyl acetate, butyl acetate, or similar compounds, aromatic hydrocarbons, e.g., toluene, xylene, etc., ethers, e.g., tetrahydrofuran, diethyl esters, or similar compounds. The amount should be chosen to achieve perfect intermixing and also removal of the heat of polymerization without problems. 
     Examples of suitable catalysts for solution polymerization include: organic peroxides, e.g., benzoyl peroxide, lauroyl peroxide, or similar compounds; percarbonates, e.g., isopropyl percarbonate, cyclohexyl percarbonate, etc., azo compounds, e.g., azobisisobutyronitrile, etc. Azo initiators are preferred. The polymerization temperature is usually 30° to 110° C. 
     The copolymers of mixtures of 2-phenoxy (ethoxy) ethyl acrylates as monomers are also prepared in this fashion. Such copolymers can contain very little amounts of each different monomer but the widest latitude in composition is possible. The production of the co-polymers of such monomers with up to 30% by weight of aliphatic acrylic acid esters of 4-10 carbon atoms in the alcohol component likewise proceeds according to the above-described methods. Suitable aliphatic acrylic acid esters of 4-10 carbon atoms in the alcohol portion include: n-butyl acrylate, n-hexyl acrylate, isohexyl acrylate, n-octyl acrylate, 2-ethylhexyl acrylate, n-decyl acrylate, isodecyl acrylate, etc. Preferred are n-butyl acrylate and 2-ethylhexyl acrylate. 
     The introduction of the component imparting impact resistance into the polyvinyl chloride can take place by all per se conventional methods of modification, e.g., by graft polymerization of vinyl chloride onto the component imparting impact resistance or vice versa, or by any desired kind of blending of polyvinyl chloride with the component imparting impact resistance, for example by mixing in the solid phase on a mixing roll, a Banbury mixer, a plastograph, a compounder-extruder, or the like. If desired, the components can also be premixed by means of a finned-agitator mixer or a powder mixer with rotor. The polyvinyl chloride and the component imparting impact resistance can also be blended in latex form. The latex can then be dried conventionally, for example by passing it through nozzles. Graft polymerization is preferred. 
     Customary additives, in the usual amounts, e.g., 4-8 wt. %, including stabilizers, plasticizers, mold release agents, pigments, fillers, and the like after being blended with the component imparting impact resistance, can be added to the polyvinyl chloride. These additives can also be mixed in immediately during the blending of the polyvinyl chloride with the component imparting impact resistance or in any other applicable manner. Greater details can be seen from the pertinent technical literature, for example the monograph by Gachter-Muller, &#34;Handbuch der Kunststoff-Additive&#34; [Manual of Plastics Additives], Hanser Publishers, 1979, whose disclosure is incorporated by reference herein. 
     When evaluating transparency, it must be kept in mind that polyvinyl chloride, as compared with other thermoplastics, must be stabilized in a special way on account of its tendency toward decomposition during the processing operation. Thereby, its transparency is impaired as compared with other thermoplastics. Bulk polyvinyl chloride, being the purest polyvinyl chloride, should exhibit the maximum transparency possible for the composition of this invention. Therefore, if an impact-resistant, i.e., modified, polyvinyl chloride exhibits transparencies closely approaching the transparency of pure bulk polyvinyl chloride, these transparencies will represent the highest possible in this area. 
     In this connection, consideration must further be given to the fact that transparency, even in the case of bulk polyvinyl chloride, is dependent on the individual formulation, e.g., the addition (absolutely necessary for processing) of mold release agents, stabilizers, and the like, and comparisons may be made only for absolutely identical formulations and, of course, identical layer thicknesses. 
     Without further elaboration, it is believed that one skilled in the art can, using the preceding description, utilize the present invention to its fullest extent. The following preferred specific embodiments are, therefore, to be construed as merely illustrative, and not limitative of the remainder of the disclosure in any way whatsoever. In the following examples, all temperatures are set forth uncorrected in degrees Celsius; unless otherwise indicated, all parts and percentages are by weight. 
     The following stabilizing formulation was utilized for the examples set forth below for explanatory purposes: 
     
         ______________________________________                                    
Polyvinyl chloride (or modified                                           
                     100    parts by weight                               
polyvinyl chloride)                                                       
Ba--Cd Stabilizer    2.5    parts by weight                               
Polyethylene mold    0.15   part by weight                                
release agent                                                             
Polymethyl methacrylate                                                   
                     1.2    parts by weight                               
processing aid                                                            
Liquid partial fatty acid                                                 
                     0.4    part by weight                                
ester of glycerol                                                         
Solid neutral glycerol                                                    
                     0.4    part by weight                                
ester wax                                                                 
______________________________________                                    
 
    
     In order to produce the test specimens, rolled sheets were first produced at a roll temperature of 185° C. and with a rolling period of 5 minutes. After pressing into plates having a thickness of 2 mm and 4 mm, respectively, the transmission, haze, and notched resistance measurements were conducted as indicated in Table 1. 
     As borne out by the examples below, the mixtures of this invention show high impact resistance with high transparency. In the following, FD water means fully demineralized water. 
     (A) PREPARATION OF POLYACRYLIC ACID ESTER 
     Example 1 
     The ingredients set out below are charged into a 2-liter steel autoclave with agitator, temperature control, as well as devices for evacuation, feeding of gaseous N 2 , charging and metered feed of reactants (manufacturer, for example, SFS/Buechi, Uster, Switzerland): 
     20 parts (250 g) phenoxyethoxyethyl acrylate 
     76 parts (950 g) FD water 
     0.24 part (3 g) sodium dodecyl sulfonate 
     The receiver of the metered feeding device is charged with 
     0.04 part ( 0.5 g) of 2,2&#39;-azobis[2-amidinopropane] hydrochloride 
     4 parts (50 g) of FD water 
     After degasifying and purging with N 2 , the content of the reactor is heated to 60° C. under 2 bar of excess N 2  pressure. During the heating up step, 5 ml of the initiator solution is added; the remainder is uniformly added in metered amounts during the course of 120 minutes after the end of the heating step, and the reaction temperature is maintained at 60° C. After another 30 minutes, the reaction is completed. The reaction mixture is allowed to cool, thus obtaining a white, stable acrylate latex with 19.6% by weight of solid matter, i.e. conversion is about 98% by weight. Gel content in tetrahydrofuran ranges between 50 and 65% by weight. 
     Example 1a 
     Example 1 is repeated, additionally charging 0.2 part (2.5 g) of diallyl phthalate into the reactor. Solid content: 19.7% by weight corresponding to about 98% by weight conversion. The gel content in tetrahydrofuran is between 70 and 85% by weight. 
     Example 2 
     The following ingredients are charged into the apparatus described in Example 1: 
     20 parts (250 g) of phenoxyethoxyethyl acrylate 
     76 parts (950 g) of FD water 
     0.24 part (3 g) of sodium laurate 
     The following materials are charged into two receivers of the metering device: 
     Receiver 1 
     0.002 part (0.025 g) of ascorbic acid dissolved in 
     2 parts (25 g) of FD water 
     Receiver 2 
     0.002 part (0.025 g) of H 2  O 2  dissolved in 
     2 parts (25 g) of FD water 
     After degasifying and purging with N 2 , the reactor content is heated to 60° C. under 2 bar excess N 2  pressure. During heating, respectively 2 ml of the initiator components from receiver 1 and receiver 2 are added, the remainder being added uniformly in metered quantities after the termination of the heating step during the course of 120 minutes, and the reaction temperature is kept at 60° C. After another 30 minutes, the reaction is completed. The reaction mixture is allowed to cool, thus obtaining a white, stable acrylate latex with 19.6% by weight of solids, i.e. conversion is about 98% by weight. Gel content in tetrahydrofuran ranges between 50 and 65% by weight. 
     Example 2a 
     Example 2 is repeated, additionally charging 0.2 part (2.5 g) of diallyl phthalate into the reactor. Solid content: 19.8% by weight, corresponding to approximately 98% by weight conversion. The gel content in tetrahydrofuran is between 70 and 85% by weight. 
     Example 3 
     Example 1 is repeated, using 20 parts (250 g) of phenoxyethoxyethoxyethyl acrylate instead of phenoxyethoxyethyl acrylate. Conversion and gel content correspond to the date indicated for Example 1. 
     Example 3a 
     Example 1 is repeated, employing 20 parts (250 g) of phenoxyethoxyethoxyethyl acrylate instead of phenoxyethoxyethyl acrylate, and additionally charging the reactor with 0.2 part (2.5 g) of diallyl phthalate. Conversion and gel content correspond to the values set forth for Example 1a. 
     Example 4 
     Example 1 is repeated, charging, instead of 20 parts of phenoxyethoxyethyl acrylate, 17 parts (212.5 g) of phenoxyethyl acrylate and 3 parts (37.5 g) of butyl acrylate. The metered feeding device is charged with 0.04 part (0.5 g) of potassium persulfate in place of 0.04 part (0.5 g) of 2,2&#39;-azobis[2-amidinopropane] hydrochloride. Conversion and gel content correspond to the data set forth for Example 1. 
     Example 4a 
     Example 1 is repeated, charging, instead of 20 parts of phenoxyethoxyethyl acrylate, 17 parts (212.5 g) of phenoxyethyl acrylate and 3 parts (37.5 g) of butyl acrylate, as well as additionally 0.2 part (2.5 g) of diallyl phthalate. The metered feeding device receives 0.04 part (0.5 g) of potassium persulfate in place of 0.04 part (0.5 g) of 2,2&#39;-azobis[2-amidinopropane] hydrochloride. Conversion and gel content correspond to the values indicated for Example 1a. 
     Example 5 
     Example 1 is repeated, using, instead of 20 parts of phenoxyethoxyethyl acrylate, a mixture of 18 parts (225 g) of phenoxyethoxyethyl acrylate and 2 parts (25 g) of butyl acrylate. Conversion and gel content correspond to the values set forth for Example 1. 
     Example 5a 
     Example 1 is repeated, using, in place of 20 parts of phenoxyethoxyethyl acrylate, a mixture of 18 parts (225 g) of phenoxyethoxyethyl acrylate and 2 parts (25 g) of butyl acrylate, as well as 0.2 part (2.5 g) of diallyl phthalate. Conversion and gel content correspond to the data set forth under Example 1a. 
     (B) PREPARATION OF THE MIXTURE OF POLYVINYL CHLORIDE AND POLYACRYLIC ACID ESTER 
     (a) Graft Polymerization of Vinyl Chloride with Polyacrylic Acid Ester 
     Examples 6 through 15 
     The following materials are charged into a 2-liter steel autoclave of the type of structure described under (A): 
     50 parts (200 g) of polyacrylate latex, prepared according to Examples 1, 1a, 2, 2a, 3, 3a, 4, 4a, 5, and 5a (corresponding respectively to about 40 g of solid polymer and 160 g of water) 
     160 parts (640 g) of FD water 
     0.03 part (0.12 g) of sorbitan monolaurate 
     0.08 part (0.32 g) of lauroyl peroxide 
     0.06 part (0.24 g) of dicetyl peroxodicarbonate 
     After the introduced mixture has been degasified and purged with nitrogen, 90 parts (360 g) of vinyl chloride is forced into the autoclave under agitation at 200-300 rpm and thereafter the agitator speed is raised to 350 rpm. Then 
     0.4 part (1.6 g) of hydroxyethylcellulose dissolved in 
     50 parts (200 g) of FD water 
     is added, and 2 bar of N 2  pressure is applied. 
     The content of the reactor is heated to 60° C., and polymerization is completed at this temperature within about 6 hours up to a pressure drop by 3 bar. 
     After cooling, residual VC degasification, washing, and drying, pourable powders are obtained, the average grain diameters of which range from 100 to 150 μm. 
     Values determined for impact resistance and transparency can be derived from Table 1. The previously listed stabilizer formulation was utilized. 
     Examples 16 through 23 
     The following materials are charged into a 2-liter steel autoclave of the type of structure described under (A): 
     37.5 parts (150 g) of polyacrylate latex, prepared according to Examples 1, 1a, 2, 2a, 3, 3a, 5, and 5a (corresponding to respectively about 30 g of solid polymer and 120 g of water) 
     160 parts (640 g) of FD water 
     0.03 part (0.12 g) of sorbitan monolaurate 
     0.08 part (0.32 g) of lauroyl peroxide 
     0.06 part (0.24 g) of dicetyl peroxodicarbonate 
     After the charged mixture has been degasified and purged with nitrogen, 92.5 parts (370 g) of vinyl chloride is forced into the autoclave under agitation at 200-300 rpm and then the agitator speed is raised to 350 rpm. Then 
     0.4 part (1.6 g) of hydroxyethylcellulose dissolved in 
     50 parts (200 g) of FD water 
     is added, and 2 bar of N 2  pressure is applied. The content of the reactor is heated to 60° C., and polymerization is completed at this temperature within about 6 hours up to a pressure drop by 3 bar. After cooling, residual VC degasification, washing, and drying, pourable powders are obtained, the average grain diameters of which range from 100 to 150 μm. 
     Values determined for impact resistance and transparency can be seen from Table 1. The previously indicated stabilizer formulation was employed. 
     (b) Mixing of PA and Emlusion Polyvinyl Chloride (E PVC) 
     Example 24 
     100 parts (5,000 g) of E PVC latex with 45% PVC (produced, for example according to DOS 2,531,780) and 
     22.5 parts (1,125 g) of PA latex (with 20% by weight polymer proportion, preparation see Example 1a) 
     are spray-dried together in a &#34;Nubilosa&#34; laboratory spray-drying installation, thus obtaining a powder which is pourable within limits. Values determined for impact resistance and transparency can be derived from Table 1. The stabilizing formulation was used as indicated above. 
     
                                           TABLE 1                                 
__________________________________________________________________________
                        Haze H       Notched Impact                       
              Transmission,                                               
                        (Contrast Dimming)                                
                                     Resistance in                        
              Layer Thickness                                             
                        Acc. to ASTM D 1003,                              
                                     kJ/m.sup.2, 4 mm                     
                                               Modifying                  
              2 mm,     Layer Thickness 2 mm,                             
                                     Pressed Plates                       
                                               Component                  
Modified Polyvinyl Chloride                                               
              Wavelength 600 nm                                           
                        Wavelength 600 nm in %                            
                                     Acc. to DIN 53 453                   
                                               in %                       
__________________________________________________________________________
Bulk polyvinyl chloride acc.                                              
              81        8.0           2        0                          
to DOS 1,520,595 (standard                                                
specimen)                                                                 
DAS 2,013,020 --        --            6        10                         
German Patent 2,456,278                                                   
              73        24.4          5        8                          
According to invention                                                    
Example 6     82        8.8          21        10                         
Example 7     82        8.6          23        10                         
Example 8     79        9.3          20        10                         
Example 9     79        9.5          22        10                         
Example 10    78        13.6         24        10                         
Example 11    77        14.2         27        10                         
Example 12    77        15.0         14        10                         
Example 13    78        13.7         15        10                         
Example 14    77        11.9         23        10                         
Example 15    76        10.4         24        10                         
Example 16    84        8.0          14        7.5                        
Example 17    84        8.2          15        7.5                        
Example 18    80        8.7          13        7.5                        
Example 19    81        8.9          16        7.5                        
Example 20    77        14.1         17        7.5                        
Example 21    77        15.6         17        7.5                        
Example 22    78        11.3         14        7.5                        
Example 23    78        10.9         16        7.5                        
Example 24    78        16.0         22        10                         
__________________________________________________________________________
 
    
     The preceding examples can be repeated with similar success by substituting the generically or specifically described reactants and/or operating conditions of this invention for those used in the preceding examples. 
     From the foregoing description, one skilled in the art can easily ascertain the essential characteristics of this invention and, without departing from the spirit and scope thereof, can make various changes and modifications of the invention to adapt it to various usages and conditions.