Quaternary ammonium and benzothiazole microbicidal preservative composition
FIELD OF THE INVENTION 
     The present invention relates generally to a composition and more particularly, to a microbicidal preservative composition comprising a quaternary ammonium compound and 2-(thiocyanomethylthio)benzothiazole (hereafter TCMTB). 
     BACKGROUND OF THE INVENTION 
     Various chemicals such as organomercury compounds, organotin compounds and chlorinated phenols have been used as industrial preservative fungicides. However, the toxicity of these compounds and environmental contamination caused by these compounds are known problems. 
     The quaternary ammonium compounds and TCMTB used in the present invention are known individually as low toxicity antimicrobials. However, these compounds each possess a narrow antibacterial spectrum and, when used alone, have limited ability to completely prevent the growth of microorganisms. Thus, it was not possible to effectively prevent the development of microorganisms. 
     SUMMARY OF THE INVENTION 
     The present invention can overcome the problems and disadvantages of the prior art by providing a composition comprising a quaternary ammonium compound and TCMTB which has improved microbicidal and preservative effects at lower concentrations than the prior art, has low toxicity and is effective against a wider spectrum of microorganisms. The instant inventors discovered that the combined use of a quaternary ammonium compound and 2-(thiocyanomethylthio)benzothiazole achieve superior microbicidal preservative activity at low concentrations against a wide range of microorganisms. 
     The present invention also provides a method for inhibiting the growth of a microorganism which comprises the step of contacting the microorganism with the composition of the invention in an amount synergistically effective to inhibit the growth of the microorganism. The invention also provides a method of preventing decay or deterioration of a material capable of supporting growth of a microorganism comprising the step of contacting the material with the composition of the invention in an amount synergistically effective to prevent the decay or deterioration of the material. The effective amount varies in accordance with the material or product to be treated and can readily be determined, without undue experimentation, by one skilled in the art. 
     The microbicidal preservative composition of the invention is useful in preventing the deterioration of various types of industrial raw materials and products such as dyes, glues, lumber, leather, textiles and pulp by microorganisms such as bacteria, mold and fungi. 
     Additional advantages of the invention will be set forth in part in the description which follows, and in part will be obvious from the description, or may be learned by practice of the invention. The objects and advantages of the invention may be realized and obtained by means of instrumentalities and combinations particularly pointed out in the appended claims. 
     The present invention provides a composition comprising a quaternary ammonium compound (hereinafter &#34;QAC&#34;) and TCMTB. The QAC is represented by the formula (I): ##STR1## wherein R 1  is an alkyl group having from 8 to 18 carbon atoms, or an alkenyl group having from 8 to 18 carbon atoms, R 2  is a alkyl group having from 1 to 5 carbon atoms, an alkyl group having from 8 to 18 carbon atoms or an alkenyl group having from 8 to 18 carbon atoms or an aralkyl group; R 3  and R 4  are independently alkyl groups having from 1 to 5 carbon atoms; and X is a halogen atom. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     The accompanying drawings, which are incorporated in and constitute a part of this specification, illustrate several exemplary embodiments of the invention and together with the description, serve to explain the principles of the invention. 
     FIG. 1 is a graph showing the evaluation standards of the synergistic effects of the composition of the invention against microorganisms by the TDMIC curve in the binary dilution method. 
     FIG. 2 sets forth the TDMIC curve of the composition of the invention against Bacillus subtilis. 
     FIG. 3 sets forth the TDMIC curves of the composition of the invention against Aspergillus niger. 
     The foregoing and other features and advantages of the present invention will be made more apparent from the following description of the preferred embodiments. 
    
    
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     Reference will now be made in detail to the preferred embodiments of the invention. 
     In accordance with the invention, the present invention can provide a low toxicity microbicidal preservative composition comprising a QAC of the formula (I): ##STR2## wherein R 1 , R 2 , R 3  and R 4  are defined as set forth above, and TCMTB. The combination of QAC and TCMTB is employed in an amount effective to synergistically inhibit the growth of a microorganism and prevent the decay or deterioration of the material or product to which the composition is applied. When R 2  is an aralkyl group, it is preferably a benzyl or phenethyl group. X may be chlorine, bromine, iodine, etc. but is preferably chlorine. 
     The weight ratio of the QAC:TCMTB is from 30:1 to 1:10, preferably from 20:1 to 1:10, and more preferably from 10:1 to 1:2, although the ratio varies depending upon the intended use, and the microorganism, material or product to which it is applied. 
     The microbicidal preservative composition of the invention which combines the QAC and TCMTB can demonstrate an unexpected synergistic antimicrobial effect between the respective components and achieves superior, i.e. greater than additive, microbicidal preservative activity at low concentrations against a wide range of microorganisms. 
     Preferably, the QAC is an alkyl C 8  -C 18  trimethylammonium halide such as octyltrimethylammonium chloride, decyltrimethylammonium chloride, dodecyltrimethylammonium chloride, hexadecyltrimethylammonium chloride, stearyltrimethylammonium chloride, a dialkyl C 8  -C 18  dimethylammonium halide such as dioctyldecyldimethylammonium chloride, dioctyldimethylammonium chloride, didecyldimethylammonium chloride, dioctyldodecyldimethylammonium chloride, dihexadecyldimethylammonium chloride, dioctadecyldimethylammonium chloride, an alkyl C 8  -C 18  benzyldimethylammonium halide such as dodecyldimethylbenzylammonium chloride, hexadecyldimethylbenzylammonium chloride, octadecyldimethylbenzylammonium chloride. The QAC may be used in mixtures, particularly mixtures having mixed alkyl groups derived from common fats and oils such as C 8  -C 18  alkyltrimethylammonium chloride, C 8  -C 18  dialkyldimethylammonium chloride, and C 8  -C 18  alkyldimethylbenzylammonium chloride. Preferably, dioctyldimethylammomium chloride, didecyldimethylammonium chloride, dodecyldimethylbenzylammonium chloride, hexadecyldimethylbenzylammonium chloride or octadecyltrimethylammonium chloride is employed. 
     Depending upon the specific application, the composition of the present invention may be prepared in various forms. It may be prepared in liquid form in which it is useful to prevent the decay and molding of starch paste solution, wet pulp and lumber. The composition may be dissolved in solvents such as for example, N,N-dimethylformamide, monochlorobenzene, cyclohexanone, tetrahydrofuran, diethylene glycol monomethyl ether and ethylene glycol monophenyl ether. An emulsion can be prepared by adding a surfactant, if necessary, and emulsifying in water. Preferably, nonionic surfactants are employed such as polyoxyethylene alkylphenol ether, polyoxyethylene-polyoxypropylene block copolymer, polyoxyethylene alkyl ether and polyoxyethylene fatty acid ester. The composition of the present invention can also be used as a powder when the subject to be treated is a powder, in which case the composition is preferably deposited on a carrier such as diatomaceous earth or kaolin. The composition can also be prepared in paste form by dissolving it in an organic solvent and adding a surfactant. The paste can be applied to lumber for microbicidal and preservative treatment. Other microbicidal preservatives such as dithiocyanomethane and 2-(4-thiazolyl)-1H-benzimidazole, or other chemicals, such as insecticides, can be added to the present composition. 
     The concentrations of the components of the composition of the present invention vary depending on the intended use and the microorganism, material or product to which it is applied. For example, from 5 to 100 mg/kg of QAC and from 1 to 100 mg/kg of TCMTB can be added to prevent decay of glues such as starch paste and to prevent molding of wet pulp. In lumber, from 0.1 to 10 g/m 2  of QAC and from 0.5 to 1 g/m 2  of TCMTB should be absorbed when the intent is to prevent molding, and from 1 to 10 g/m 2  of QAC and from 0.2 to 5 g/m 2  of TCMTB should be applied when the intent is to prevent decay. 
     The invention will be further clarified by the following examples, which are intended to be merely illustrative of the invention. 
     EXAMPLE 1 
     Synergistic Effect of the Combined Use of QAC and TCMTB Against Microorganisms 
     The synergistic effects of the combined use of QAC and TCMTB against microorganisms were measured by the binary dilution method. The two components were diluted to specific concentrations and then added to culture medium. The medium was then inoculated with microorganisms and cultured under designated conditions. The concentrations at which no growth of microorganisms was found were taken as the minimal inhibitory concentrations by the binary dilution method. 
     FIG. 1 is a graph of the minimal inhibitory concentrations of each component (TCMTB: Component A, QAC: Component B) using common scale coordinates. The curve of this graph, i.e. the region above the TDMIC curve, shows the proliferation inhibition region. The area below the TDMIC curve shows the proliferation region. Agreement of the diagonal and TDMIC curve shows additive effects. The fact that the curve is lower than the diagonal demonstrates synergistic effects. 
     EXAMPLE 2 
     Synergistic Effect of the Combined Use of QAC and TCMTB Against Bacteria 
     The synergistic effects of the combined use of QAC and TCMTB were evaluated against Bacillus subtilis of the genus Bacillus, a bacteria detected frequently in decayed latex, starch paste, starch slurry and coating color. 
     Bouillon medium was used as the medium. It was inoculated with a set quantity of a bacterial solution that had been precultured overnight. After shake culturing for 24 hours at 37° C., the concentration at which the medium was not turbid was determined. 
     Didecyldimethylammonium chloride (hereafter &#34;DDAC&#34;) was used as the QAC. 
     The results are set forth in FIG. 2. 
     As shown in FIG. 2, the TDMIC curve against Bacillus subtilis demonstrates clear synergistic effects. The concentrations at which the combination of DDAC and TCMTB completely inhibited bacterial growth were 1 μg/ml and 1.5 μg/ml respectively. Since bacterial growth was inhibited individually by 6 μg/ml of TCMTB and 4 μg/ml of DDAC, the composition of the present invention manifested marked synergistic effects because it was capable of suppression at 1/4 the sum of the quantities used alone. Examples of other concentration combinations that demonstrated synergistic effects are set forth in Table 1. 
     
                       TABLE 1                                                     
______________________________________                                    
       TCMTB  DDAC                                                        
       (μg/ml)                                                         
              (μg/ml)                                                  
______________________________________                                    
       4.5    0.5                                                         
       3.0    0.5                                                         
       3.0    1.0                                                         
       1.5    2.0                                                         
       0.75   2.0                                                         
       0.75   3.0                                                         
______________________________________                                    
 
    
     EXAMPLE 3 
     Synergistic Effects of the Combined Use of TCMTB and QAC Against Molds 
     The synergistic effects of the combined use of TCMTB and QAC were evaluated against Aspergillus niger of the species Asperqillus, a mold that develops frequently in wet pulp, starch paste and coating color. 
     Czapek medium was used as the medium. Spores were collected from a previous slant cultured stock strain. The medium was inoculated with a set amount of a solution of spores suspended in sterilized water. After shake culturing for 72 hours at 27° C., the concentration at which no mycelia developed in the medium was determined. The results are set forth in FIG. 3. 
     As shown in FIG. 3, the TDMIC curve against Asperqillus niger demonstrated clear synergistic effects. The synergistic effects of the combination of the two components that completely inhibited growth of the organisms appeared at, for example, a TCMTB concentration of 0.75 μg/ml and a DDAC concentration of 10 μg/ml. Since growth of the organisms was inhibited individually by 3.0 μg/ml of TCMTB and 80 μg/ml of DDAC, the composition of the present invention permitted inhibition at 1/4 and 1/8 the quantities of the individual components when used alone, demonstrating strong synergistic effects. Examples of concentration combinations of TCMTB and DDAC that demonstrate synergistic effects are given in Table 2. 
     
                       TABLE 2                                                     
______________________________________                                    
       TCMTB  DDAC                                                        
       (μg/ml)                                                         
              (μg/ml)                                                  
______________________________________                                    
       2.25   10                                                          
       1.5    10                                                          
       1.5    20                                                          
       0.75   20                                                          
       0.75   40                                                          
       0.375  40                                                          
       0.375  60                                                          
______________________________________                                    
 
    
     EXAMPLE 4 
     Preservative Effect of the Composition of the Invention In Starch Paste Solution 
     Cornstarch was dispersed in water in a weight ratio of 5%, and paste solution was prepared by heating to 90-95° C. while stirring. After cooling, 1% already decayed paste solution was added and 100 g portions were poured into 140 ml glass bottles. DDAC, TCMTB and a mixture of DDAC:TCMTB=1:1 were dissolved in N,N-dimethylformamide and added to make the concentrations set forth in Table 3. Culture was conducted at 37° C. and the bacterial counts were measured over time. The results are set forth in Table 3. 
     
                       TABLE 3                                                     
______________________________________                                    
Chemical                                                                  
Name      Blank    DDAC      TCMTB  1:1 Mixture                           
______________________________________                                    
Added Con-                                                                
          0 μg/ml                                                      
                   15 μg/ml                                            
                             15 μg/ml                                  
                                    30 μg/ml                           
centration                                                                
Days                                                                      
Elapsed                                                                   
0         1.9 × 10.sup.4                                            
                   --        --     --                                    
2         7.9 × 10.sup.5                                            
                   &lt;10.sup.2 8.8 × 10.sup.3                         
                                    &lt;10.sup.2                             
4         7.7 × 10.sup.6                                            
                   &lt;10.sup.2 9.3 × 10.sup.4                         
                                    &lt;10.sup.2                             
6         3.8 × 10.sup.7                                            
                     5 × 10.sup.2                                   
                             8.6 × 10.sup.5                         
                                    &lt;10.sup.2                             
8         6.9 × 10.sup.7                                            
                   2.0 × 10.sup.3                                   
                             1.4 × 10.sup.6                         
                                    &lt;10.sup.2                             
10        7.6 × 10.sup.7                                            
                   5.9 × 10.sup.4                                   
                             4.3 × 10.sup.6                         
                                    &lt;10.sup.2                             
______________________________________                                    
 
    
     The figures in the table represent the live bacterial counts (cells/ml). As shown in Table 3, the DDAC:TCMTB=1:1 mixture demonstrated clearly superior preservative activity in comparison to the same concentrations of the chemicals alone. Synergistic effects demonstrating enhanced preservative activity were thus obtained. 
     EXAMPLE 5 
     Microbicidal Activity of the Composition of the Invention In Wet Pulp 
     Test sheets were produced by punching wet pulp (LBKP) into 5 cm diameter pieces. DDAC, TCMTB and DDAC:TCMTB=10:1 mixture were dissolved in N,N-dimethylformamide and applied uniformly by pipette to prepare the concentrations set forth in Table 4 in relation to the dry weight of the pulp. 0.1 ml of the various concentrations were applied to the test sheets. Sheets containing 0.1 ml of N,N-dimethylformamide were used as the controls. The test sheets were placed in petri dishes 9 cm in diameter into which culture medium of the following composition had previously been poured and solidified. 
     To 1 liter of deionized water, 3.0 g NH 4  NO 3 , 1.0 g KH 2  PO 4 , 0.5 g MgSO 4 .7H 2  O, 0.25 g KCl, pb 0.002 g FeSO 4  and 25 g agar were added. Spores of the genus Aspergillus, Penicillium and Trichoderma that appear frequently in wet pulp, and are among the molds separated and stored from wet pulp, were suspended in sterilized water and the designated quantities were uniformly applied on top of the aforementioned sheets. Culture was conducted at 27° C. and the growth of the molds was observed visually over time. The results are shown in Table 4. 
     
                       TABLE 4                                                     
______________________________________                                    
Chemical                                                                  
Name      Subject  DDAC     TCMTB  10:1 Mixture                           
______________________________________                                    
Added Con-                                                                
          0 mg/kg  20 mg/kg 2 mg/kg                                       
                                   22 mg/kg                               
centration                                                                
Days                                                                      
Elapsed                                                                   
 5        +        -        -      -                                      
10        ++       +        -      -                                      
15        +++      +        -      -                                      
20        +++      ++       +      -                                      
25        +++      ++       +      -                                      
30        +++      ++       ++     -                                      
______________________________________                                    
 The evaluation standards in Table 4 are as follows:                      
 -: No growth of mold found on the sheets                                 
 +: Growth of mold found on less than 1/3 of the sheet                    
 ++: Growth of mold found on from 1/3 to 2/3 of the sheet                 
 +++: Growth of mold found on 2/3 or more of the sheet                    
 
    
     As shown in Table 4, mold development was completely inhibited by addition of 22 mg/kg of the DDAC:TCMTB=10:1 mixture. The microbicidal activity was clearly superior to that obtained by the same concentration of the chemicals alone and synergistic effects were thus obtained. 
     EXAMPLE 6 
     Microbicidal Activity of the Composition of the Invention Against Fungi in Wood 
     A microbicidal test using DDAC and TCMTB alone and a mixture of DDAC:TCMTB=10:3 was conducted against molds that frequently grow in wood. The test method was in accordance with regulation No. 2 &#34;Fungicidal test methods of fungicides for wood&#34; of the Japan Wood Preservation Association (abbreviated JWPA). The concentrations shown in Table 5 were tested. 
     The chemicals tested are shown in Table 5. The numbers in the table represent the respective parts by weight of each component. 
     
                       TABLE 5                                                     
______________________________________                                    
           Preparation                                                    
                    Preparation                                           
                              Preparation                                 
           1        2         3                                           
______________________________________                                    
DDAC         10         --        10                                      
TCMTB        --         3          3                                      
Ethanol       2         --         2                                      
Diethylene   --         --        50                                      
glycol monomethyl                                                         
ether                                                                     
Diethylene   --         92        27                                      
glycol                                                                    
Nonylphenol  --         5         --                                      
ethylene oxide                                                            
adduct                                                                    
Tap Water    88         --         8                                      
______________________________________                                    
 
    
     The molds tested were: 
     A 1  : Aspergillus niger 
     A 2  : Penicillium funiculosum 
     A 3  : Aureobasidium pullulans 
     A 4  : Gliocladium riruns 
     A 5  : Rhizopus javanicus 
     The test sheets were prepared as follows. Rectangular sheets of Japanese beech (20×3×50 mm) were immersed for 3 minutes in solutions of Preparations 1, 2 and 3 diluted to 2.0%, 4.0% and 6.0% by weight by tap water. These were subsequently dried for 2 days and taken as treated test pieces. 
     2% agar solution steam sterilized under high pressure was poured and solidified in sterilized petri dishes (90 mm in diameter). A polypropylene mesh was placed on top of the agar as a stand so that the test pieces and agar would not come into direct contact. Three test pieces were placed on the stand and spore suspensions of the various test molds were poured on top. Six treated pieces (2 per petri dish) were used for each concentration. Culture was conducted for 4 weeks at 26° C. The effects were evaluated by examining the mold development in each individual test sheet after 4 weeks for each type of mold and each concentration. The evaluation values were determined according to the following standards. 
     
         ______________________________________                                    
Evaluation Value                                                          
            Mold Growth                                                   
______________________________________                                    
0           Absolutely no mold growth found on test                       
            sheet                                                         
1           Mold growth found on only sides of test                       
            sheet                                                         
2           Mold growth found on less than 1/3 of the                     
            surface area of the test sheet                                
3           Mold growth found on more than 1/3 of the                     
            surface area of the test sheet                                
______________________________________                                    
 
    
     The damage values (D) in Table 6 were determined by the following equation after determining the total mean evaluation value (S) for each concentration. 
     Total mean evaluation value (S)=A 1  +A 2  +A 3  +A 4  +A 5  (A 1 , A 2  . . . A 5  : Mean evaluation value of each mold species) ##EQU1## S 0  : Total mean evaluation value of untreated test sheet S: Total mean evaluation value of treated test sheet of a certain concentration 
     The results are shown in Table 6. 
     
                       TABLE 6                                                     
______________________________________                                    
Treatment             Mean Evaluation                                     
Concen-      Amount   Value of Each                                       
tration %    Absorbed Organism                                            
Chemical                                                                  
       by weight (g/m.sup.2)                                              
                          A.sub.1                                         
                              A.sub.2                                     
                                  A.sub.3                                 
                                      A.sub.4                             
                                          A.sub.5                         
                                              S    D                      
______________________________________                                    
Prepar-                                                                   
       6.0       6.2      2.2 2.2 0   1.5 1.0 6.9  46                     
ation  4.0       4.1      2.4 2.4 0.7 1.8 2.2 9.5  63                     
1      2.0       2.0      3   2.4 1.3 3   3   12.7 85                     
Prepar-                                                                   
       6.0       6.1      1.0 0   0   2.3 0   3.3  22                     
ation  4.0       4.0      2.4 0.7 0   3   2.4 8.5  57                     
2      2.0       2.0      3   2.4 0.7 3   3   12.1 81                     
Prepar-                                                                   
       6.0       6.2      0   0   0   0   0   0     0                     
ation  4.0       4.1      1.0 0   0   0   0   1.0   7                     
3      2.0       2.0      1.0 0   0   1.0 0   2.0  13                     
______________________________________                                    
 
    
     The damage value (D) at which essential microbicidal effects can be expected is not more than 30. According to Table 5, Preparation 1 exceeds 30 even in a treatment concentration of 6.05 (amount absorbed 6.2 g/m 2 ). Preparation 2 also exceeds 30 in a treatment concentration of 4.0% (amount absorbed 4.0 g/m 2 ). In contrast to this, Preparation 3, in accord with the present invention, is below 30 even in a treatment concentration of 2.0% (amount absorbed 2.0 g/m 2 ). Together with demonstrating superior microbicidal effects, this evidences synergistic effects. 
     The most effective microbicidal activity resulted from the use of Preparation 3 in which the active ingredients are DDAC and TCMTB. Preparation 3 demonstrated superior microbicidal activity even in a low concentration even against A 1 , A 4  and A 5  molds against which Preparation 1 (active ingredient DDAC) and Preparation 2 (active ingredient TCMTB) have little microbicidal activity. 
     Considering that the microbicidal activity against A 4  molds was unsatisfactory even by individual or combined use (not shown in Table 6) of MBTC (methylene bisthiocyanate) and TCMTB, which are representative of commercial fungicides, the effects of the present invention are even more remarkable than anticipated. 
     EXAMPLE 7 
     Preservative Activity of the Composition of the Invention Against Microorganisms in Wood 
     A preservative activity test was conducted against various types of organisms that rot wood using DDAC and TCMTB alone and the two in combination. Preparations 1-3 set forth above in Example 6 were utilized. The test method was according to regulation No. 1 &#34;Wood preservative activity test method&#34; of the JWPA. 
     The same chemicals as in Example 5 were tested. 
     The test organisms employed were: 
     (I) Oouzuratake: Tyromyces palustris 
     (II) Kawaratake: Coriolus versicolor 
     (III) Namidatake: Serpula lacrymans 
     The test sheets were prepared as follows. Rectangular sheets of Japanese cedar, red pine and beech (5×20×40 mm, flat surfaced, known holes sealed with normal temperature curing epoxy type resin) were used as the test sheets. The chemicals of Preparations 1, 2 and 3 were diluted to 15, 20 and 25% by weight by tap water and uniformly applied by brush to the aforementioned test pieces to make a proportion of 110±10 g/m 2 . After drying, the pieces were divided into two groups, one submitted to a weathering test and one not. The former were treated according to the JWPA weathering procedure method. All of the test sheets were then dried until reaching a constant weight at 60° C. and taken as treated test sheets. 
     In the preservative activity test, JIS modified medium (peptone=0.5%, malt extract=1%, glucose=2.5%, KH 2  PO 4  =0.3%, MgSO 4 . 7H 2  O=0.2%) was used as the culture medium. Culture was conducted by combining the test sheets of the three types of wood and the wood rotting organisms as shown in the following table. 
     
         ______________________________________                                    
Type of                 Culture                                           
Wood      Organism      Temperature (°C.)                          
______________________________________                                    
Japanese  Tyromyces palustris                                             
                        26 ± 2                                         
Cedar                                                                     
Japanese  Coriolus versicolor                                             
                        26 ± 2                                         
beech                                                                     
Red Pine  Serpula lacrymans                                               
                        20 ± 2                                         
______________________________________                                    
 
    
     After culturing for 56 days, the organisms adhering to the test pieces were removed and the pieces were dried to a constant weight at 60° C. The percentage weight loss was determined and the preservative activity value was calculated by the following equation. ##EQU2## wherein D represents the preservative activity value; S 0  represents the mean weight loss percentage of untreated test sheet and S represents the mean weight loss percentage of chemical treated test sheet. The test results are shown in Table 7. 
     
                                           TABLE 7                                 
__________________________________________________________________________
          Coriolus versicolor-                                            
                          Tyromyces palustris-                            
                                          Serpula lacrymans-              
Treatment Chemical                                                        
          Japanese beech  Japanese cedar  Red Pine                        
Name of                                                                   
     Concen-                                                              
          No Weathering                                                   
                  With Weather-                                           
                          No Weathering                                   
                                  With Weather-                           
                                          No Weathering                   
                                                  With Weather-           
Chemical                                                                  
     tration %                                                            
          Procedure                                                       
                  ing Procedure                                           
                          Procedure                                       
                                  ing Procedure                           
                                          Procedure                       
                                                  ing Procedure           
__________________________________________________________________________
Prepara-                                                                  
     15   21       0      36       0      59      32                      
ation 1                                                                   
     20   54      39      69      43      75      63                      
     25   75      70      72      62      89      71                      
Prepara-                                                                  
     15   26       0      36      22      57      34                      
ation 2                                                                   
     20   52      33      79      47      82      68                      
     25   80      75      99      79      100     87                      
Prepara-                                                                  
     15   51      47      82      69      83      80                      
ation 3                                                                   
     20   85      74      91      88      100     98                      
     25   100     99      100     100     100     100                     
Untreated Weight                                                          
          31.4%           33.2%           27.5%                           
Loss Percentage                                                           
(%)                                                                       
__________________________________________________________________________
 
    
     The preservative activity value at which essential preservative effects can be expected is at least 85. As is evident from Table 7, the effective treatment concentrations for all combinations of woods and rotting organisms were more than 25% by weight for both Preparations 1 and 2, while that of Preparation 3 was from 20 to 25% by weight. Together with demonstrating the superior preservative activity, marked synergistic effects were found. 
     Superior microbicidal preservative effects were manifested by the synergistic antimicrobial and preservative activity of the ingredients of the composition of the present invention. This makes it possible to effectively prevent microbial damage at lower cost. The preparation of the present invention is also advantageous in terms of environmental contamination because both the QAC and TCMTB are of low toxicity. 
     Other embodiments of the invention will be apparent to those skilled in the art from consideration of the specification and practice of the invention disclosed herein. It is intended that the specification and examples be considered as exemplary only, with the true scope and spirit of the invention being indicated by the following claims.