Emollient durability enhancing siloxanes
BACKGROUND OF THE INVENTION 
     This invention relates to the enhancement of the durability of emollient materials with certain organosilicon compounds. More particularly, the durability of mineral oil, for example, on human skin is enhanced by mixing the emollient with one of aminofunctional, amidofunctional, or carboxyfunctional, polysiloxanes. 
     Mineral oil is a highly refined, colorless, tasteless, and odorless, liquid mixture of hydrocarbons obtained from petroleum, that has been used medicinally as an internal lubricant and in the manufacture of various salves and ointments. It is also known as medicinal oil, white mineral oil, heavy mineral oil, light mineral oil, liquid paraffin, and paraffin oil. Mineral oil has long been the emollient of choice in creams and lotions. It is second only to water as a moisturizer ingredient. Mineral oil acts as a moisturizer primarily through the functioning of the ingredient as an occlusive barrier. The water content of the outer layers of the stratum corneum of the human skin is a controlling factor in the appearance of dry skin symptoms. When the stratum corneum contains an adequate amount of water within the range of ten to twenty percent, the skin remains flexible. However, when the water content falls below ten percent, the stratum corneum often becomes brittle and rough, and can exhibit scaling and cracking. 
     The stratum corneum receives its water from the deep layers of the epidermis by diffusion or when it is brought into direct contact with water. The diffusion process is controlled by the water content of the skin, as well as the concentration gradient. In a very dry environment, the water loss from the external skin layers can be significant and often exceeds the rate of replacement by diffusion. An occlusive barrier of mineral oil, for example, placed onto the surface of the skin acts to retard the water loss to the environment and allows the skin surface to rehydrate by the diffusion process. Due to the effectiveness, low cost, and safety, of petroleum derivatives such as mineral oil, it serves as a useful occlusive moisturizer and contributes to dry skin prevention by protection and moisture retention, as well as dry skin repair by emolliency, lubricity, and moisture restoration. 
     While mineral oil has been found to be an effective and economical emollient for skin care applications, and provides softening, smoothing, and a protective action on skin, it nevertheless suffers from the disadvantage that it is easily removed from the skin by washing the skin with soap. Thus, the effectiveness and long term benefits of mineral oil enumerated above are of a limited duration. However, in accordance with the present invention, it has been discovered that certain aminofunctional, amidofunctional, and carboxyfunctional, organosilicon compounds act as durability enhancers when mixed with mineral oil, and therefore provide skin care formulations that a consumer can perceive as being longer lasting and more aesthetically pleasing. 
     It is not new, as noted above, to employ mineral oil in skin conditioning formulations. For example, this feature is clearly taught, for example, in U.S. Pat. No. 3,818,105, issued June 18, 1974, and in U.S. Pat. No. 4,246,285, issued Jan. 20, 1981. Aminofunctional, amidofunctional, and carboxyfunctional, organosilicon compounds are also not new, and certain of such siloxanes are shown, for example, in U.S. Pat. No. 4,271,215, issued June 2, 1981; U.S. Pat. No. 4,477,514, issued Oct. 16, 1984; U.S. Pat. No. 4,559,227, issued Dec. 17, 1985; U.S. Pat. No. 4,563,347, issued Jan. 7, 1986; U.S. Pat. No. 4,749,732, issued June 7, 1988; U.S. Pat. No. 4,810,253, issued Mar. 7, 1989; U.S. Pat. No. 4,848,981, issued July 18, 1989; and in U.S. Pat. No. 4,857,212, issued Aug. 15, 1989. However, none of these references teach the combination of mineral oil with such siloxanes and there use on the skin as durability enhancers. Formulations containing mineral oil and an aminofunctional siloxane are know as exemplified by U.S. Pat. No. 3,852,075, issued Dec. 3, 1974, and U.S. Pat. No. 4,113,677, issued Sept. 12, 1978, but such formulations are employed to clean and polish automotive vehicles rather than as personal skin care applications. 
     SUMMARY OF THE INVENTION 
     This invention relates to a method of enhancing the durability of an emollient material on a substrate by forming a mixture of an emollient material and an effective amount of an organosilicon compound, and applying the mixture to the substrate to be treated. The organosilicon compound is either an aminofunctional, amidofunctional, or carboxyfunctional, polysiloxane. 
     Preferred embodiments of the present invention include an aminofunctional polysiloxane having the formula Me 3  SiO(Me 2  SiO) x  (MeRSiO) y  SiMe 3  in which Me is methyl; R is the functional group --(C 4  H 8 )NH(CH 2 ) 2  NH 2  ; x is an integer from fifty to one thousand; and y is an integer from one to fifty preferably one to twenty. The amidofunctional polysiloxane preferably has the formula Me 3  SiO(Me 2  SiO) x  (MeRSiO) y  SiMe 3  in which Me is methyl; R is the functional group --(C 4  H 8 )NH(CH 2 ) 2  NHCOCH 3  ; x is an integer from fifty to one thousand preferably fifty to one hundred; and y is an integer from one to fifty preferably one to ten. Preferably, the carboxyfunctional polysiloxane compound has the formula Me 3  SiO(Me 2  SiO) x  (MeRSiO) y  SiMe 3  in which Me is methyl; R is the functional group --(C 3  H 6 )COOH; x is an integer from fifty to one thousand preferably one hundred to three hundred; and y is an integer from one to fifty. 
     The emollient and the polysiloxane may be present in the mixture in the ratio of four to one, more preferably two to one. The mixture of the emollient and the polysiloxane may, if desired, include a volatile cyclic siloxane solvent, and the solvent can be a low viscosity polydimethylcyclosiloxane fluid, for example, which is a mixture of cyclic tetramers and pentamers and having a viscosity of about 2.5 centistokes measured at twenty-five degrees Centigrade. The mixture should contain about five to ten percent by weight of the emollient and the polysiloxane in the volatile cyclic siloxane solvent. The emollient may be a material such as mineral oil, mink oil, lanolin oil, and petrolatum. 
     The invention also relates to a skin conditioning composition of enhanced durability which is a mixture of an emollient material and an effective amount of an organosilicon compound. The organosilicon compound, as noted above, is either an aminofunctional, amidofunctional, or carboxyfunctional, polysiloxane. 
     These and other features, objects, and advantages, of the herein described present invention will become more apparent from a consideration of the following detailed description thereof. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     In accordance with the present invention, there is provided a concept which relates to the enhancement of the durability of emollient materials with certain organosilicon compounds. The durability on human skin is enhanced by mixing an emollient with either one of an aminofunctional, amidofunctional or carboxyfunctional, polysiloxanes. These aminofunctional amidofunctional, and carboxyfunctional, organosilicon compounds are well known in the prior art, and such compounds as well as methods for preparing these compounds can be found in U.S. Pat. No. 4,477,514, issued Oct. 16, 1984, which shows carboxyfunctional siloxanes; U.S. Pat. No. 4,559,227, issued Dec. 17, 1985, which shows aminofunctional siloxanes; and U.S. Pat. No. 4,848,981, issued July 18, 1989, which shows the amidofunctional siloxanes, of the present invention. In the interest of providing a full and complete disclosure of the present invention, these patents are considered incorporated herein by reference. However, a brief description of these functional siloxanes is set forth hereinbelow. 
     The amine functional siloxane polymer has the formula 
     
         R.sub.3-z &#39;Q.sub.z SiO[R.sub.2 &#39;SiO].sub.x [R&#39;QSiO].sub.y SiQ.sub.z R.sub.3-z &#39; 
    
     wherein R&#39; denotes an alkyl group of 1 to 4 carbons or a phenyl group, with the proviso that at least 50 percent of the total R&#39; groups are methyl; Q denotes an amine functional substituent of the formula --R&#39;&#39;Z, wherein R&#39;&#39; is a divalent alkylene radical of 3 to 6 carbon atoms or a radical of the formulation --CH 2  CH 2  CH 2  OCH 2  --CHOHCH 2  -- and Z is a monovalent radical selected from the group consisting of NR 2  &#39;&#39;&#39;, NR&#39;&#39;&#39;(CH 2 ) n  NR 2  &#39;&#39;&#39;; and ##STR1## wherein R&#39;&#39;&#39; denotes hydrogen or an alkyl group of 1 to 4 carbons, R&#39;&#39;&#39;&#39; denotes an alkyl group of 1 to 4 carbons and n is a positive integer from 2 to 6; z has a value of 0 or 1; x has an average value of 25 to 3000; y has an average value of 0 to 100 when z is 1, and y has an average value of 1 to 100 when z is 0. 
     The amidofunctional polysiloxane is a triorganosiloxane-endblocked polydiorganosiloxane having an average of 50 to 1000 siloxane units per molecule with an average of 1 to 50 of the siloxane unites per molecule being amide-containing siloxane units. The amide-containing siloxane units bear a substituent of the formula ##STR2## wherein n is 0 or 1, R&#39; denotes an alkylene radical of 3 to 6 carbon atoms, and R&#39;&#39; denotes a hydrogen radical or an alkyl radical of 1 to 6 carbon atoms, X denotes an acyl radical of the formula ##STR3## X&#39; denotes a hydrogen radical or X, and R&#39;&#39;&#39; denotes an alkyl radical of 1 to 4 carbon atoms and substantially all other organic substituents in the polydiorganosiloxane being methyl groups. 
     The amidofunctional silicone component in accordance with this invention consists essentially of a triorganosiloxane-endblocked polydiorganosiloxane which contains amidoalkyl substituents. Triorganosiloxane-endblocked polydiorganosiloxanes (amidofunctional silicone) consist essentially of terminal triorganosiloxane units of the formula R 3  SiO 1/2  and backbone diorganosiloxane units of the formula R 2  SiO 2/2 . Trace amounts of other siloxane units in amidofunctional silicone, such as SiO 4/2  and RSiO 3/2 , which are normally present as impurities in commercial polydiorganosiloxanes may be present. Preferably there are no SiO 4/2  units or RSiO 3/2  units in the amidofunctional silicones. 
     The R radicals of the above siloxane units are substantially either amide-containing radicals of the formula ##STR4## or methyl radicals. Minor amounts of other organic substituents which are normally present as impurities in commercial polydiorganosiloxanes may be present. It should be understood, for example, that the amidofunctional silicones of this invention are often prepared by acylation of corresponding aminofunctional silicones. Consequently, the amidofunctional silicones may also contain residual aminofunctional siloxane units. For example, siloxane unites such as H 2  NCH 2  CH 2  NHCH 2  CH(CH 3 )CH 2  SiO 2/2  or H 2  NCH 2  CH 2  CH 2  SiO 2/2  may also be present in the amidofunctional silicones useful in this invention. However, for the purposes of this invention it is preferred to employ silicone oils that do not contain significant levels (more than 25 percent of the number of amidofunctional substituents) of the unmodified aminofunctional siloxane units. 
     In the formula for the amide-containing radicals, R&#39; denotes an alkylene radical of 3 to 6 carbon atoms, such as --CH 2  CH 2  CH 2  --, --CH 2  CH 2  CH 2  CH 2  --, --CH 2  CH(CH 3 )CH 2  --, --CH 2  CH 2  CH 2  CH 2  CH 2  --, and --CH 2  CH(CH 2  CH 3 )CH 2  --. Amidofunctional silicones wherein the silicon bonded, amide-containing radicals have a trimethylene radical or an alkylated trimethylene radical, such as --CH 2  CH(CH 3 )CH 2  --, as the R&#39; radical are preferred because of ease of synthesis and availability. 
     R&#39;&#39; denotes a hydrogen radical, which is a preferred R&#39;&#39; radical, or an alkyl radical of 1 to 6 carbon atoms, such as methyl, ethyl, propyl, butyl, and isobutyl. 
     In the formula for the amide-containing radicals, n has a value of 0 or 1, so that the radical may contain one or two nitrogen atoms. X denotes an acyl radical of the formula ##STR5## and X&#39; denotes a hydrogen radical or X. In the acyl radical, R&#39;&#39;&#39; denotes an alkyl radical of 1 to 4 carbon atoms such as methyl, ethyl, propyl, isopropyl, or butyl. 
     In accordance with the above, triorganosiloxane-endblocked polydiorganosiloxanes preferred for use in the method of this invention consists essentially of siloxane units selected from the following: ##STR6## (CH 3 ) 3  SiO 1/2 , and (CH 3 ) 2  SiO 2/2  where R&#39;, R&#39;&#39;, and R&#39;&#39;&#39; have the same meanings as described above. It should be understood that any of the siloxane units having non-acylated nitrogen atoms can also be present in their salt form. It is well known that the salt form occurs when such polymers are neutralized by acids such as mineral acids or carboxylic acids. 
     The silicone polymers of this invention may contain amide-containing siloxane units of the formula ##STR7## wherein R&#39;, R&#39;&#39;, and R&#39;&#39;&#39; have the same meanings as described above. These amide-containing units have a ratio of acyl groups to nitrogen atoms of about 0.5. 
     The carboxyfunctional silicones of the invention have the formula 
     
         QMe.sub.2 SiO(Me.sub.2 SiO).sub.x (MeRSiO).sub.y SiMe.sub.2 Q 
    
     wherein Me is a methyl radical, R is a carboxyfunctional radical, said carboxyfunctional radical being selected from the group consisting of carboxyalkyl radicals and carboxythioalkyl radicals, Q is selected from the group consisting of R, Me and OH groups, x has a value of 1 to 1000, and y has a value of 1 to 100. 
     As referred to herein, a carboxyfunctional radical is a monovalent radical which contains the --COOH radical, and is attached to a silicon atom of the main molecular chain by a divalent linking group. Direct attachment to the silicon atom is through a silicon to carbon bond. 
     Divalent linking groups contemplated for use in the present invention are either alkylene groups containing from 2 to 9 carbon atoms, or thioalkylene groups, containing 2 to 8 carbon atoms and one sulfur atom present as a thioether group. 
     Those carboxyfunctional radicals wherein the divalent linking group is an alkylene group are referred to herein as carboxyalkyl radicals; those carboxyfunctional radicals wherein the divalent linking group is a thioalkylene group are referred to herein as carboxythioalkyl radicals. 
     Specific examples of carboxyalkyl radicals include, but are not limited to --CH 2  CH 2  COOH, --CH 2  CH(CH 3 )COOH, --CH 2  CH(C 2  H 5 )CH 2  COOH, --CH 2  CH(CH 3 )CH(CH 3 )CH 2  COOH, and the like. The --CH 2  CH(CH 3 ) COOH radical is a preferred carboxyalkyl radical for the practice of the present invention. 
     Specific examples of carboxythioalkyl radicals include, but are not limited to --CH 2  CH 2  SCOOH, --(CH 2 ) 3  SCOOH, --CH 2  CH(CH 3 )SCH 2  COOH, --CH 2  CH 2  SCH 2  COOH, --CH 2  CH(C 2  H 5 )SCH 2  COOH, and the like. The --CH 2  CH 2  SCH 2  COOH radical is a preferred carboxythioalkyl radical for the practice of the present invention. 
     Examples of emollients and moisturizers which may be used in this invention include straight, branched or cyclic hydroxy compounds such as alcohols containing 1 to 30 carbon atoms; straight, branched, or cyclic carboxylic acids containing 1 to 31 carbon atoms; acid esters containing C 1  to C 30  carboxylic acids esterfied with C 1  to C 30  alcohols; alcohol ethers containing 1 to 30 carbon atoms; alkanes of the formula H--(CH 2 )n--H, wherein n is 5 to 30; and siloxanes. Examples of such functional materials include 2-ethylhexyl oxystearate; arachidyl propionate; 2-ethylhexyl adipate; isopropyl myristate; ethanol; stearyl alcohol; propylene glycol; propionic acid; stearic acid; polyoxypropylene cetyl alcohol; polyoxypropylene lanolin alcohol; Carbowax® 300; petroleum jelly; mineral oil; aliphatic hydrocarbons such as mineral spirits; lanolin and lanolin derivatives such a acetylated lanolin and isopropyl lanolate; hexamethyldisiloxane; cyclic polydimethylsiloxane ; linear polydimethylsiloxane; polypheylmethylsiloxane; and poly dimethyl/trimethylsiloxane. Other phenyl, ethyl and vinyl substituted polysilanes may also be included in the products of this invention. 
     In order to illustrate the durability enhancement of the siloxanes of the present invention, durability enhancement data was collected for a variety of emollients. A soap washing test procedure was used in order to measure the influence of the silicones on the durability of the various emollients. The emollients considered were mineral oil, mink oil lanolin oil, and petrolatum. The test procedure was used to measure silicone substantivity on human skin. Specifically, the method was based on Attenuated Total Reflectance/Fourier Transform Infrared Spectrophotometric (ATR/FTIR) analysis, in which prism skin studies were conducted and analyzed based on the reflection of energy at the interface. Instrumentation included a NICOLET Model 20DX FTIR system, and a HARRICK Scientific Skin Analyzer. The ATR studies involved contact of the skin sample and prism. A hydration procedure was employed in order to increase the softness and flexibility of the skin surface which resulted in a less variable contact between the skin and prism. This hydration procedure included placing a water soaked towel against the skin test site for one minute prior to actual spectra collection. A skin test site selected was an area of about eighty square centimeters, and about ten to twelve milligrams of each solution tested was applied to the skin test site area in the form of a thin film using a small paint brush. From the data collected, it was possible to calculate percentages of ingredients remaining on the skin following various soap wash sequences. The soap employed was a 0.5 weight percent solution of IVORY bar soap, and a soap rub is defined as two passes over the test area with the soap solution cupped in the palm of the hand. One soap wash procedure included fifteen soap rubs and ten rinse rubs under cool running tap water. The test site was the volar forearm. The test solutions were applied to the skin test site on the forearm in the form of a mixture of the various silicones and emollients, dissolved in a volatile silicone fluid of low viscosity, such as polydimethylcyclosiloxane which is a mixture of tetramer and pentamer having a viscosity of about 2.5 centistokes measured at twenty-five degrees Centigrade. The solution contained five to ten percent by weight of the mixture in the solvent. The solvent was allowed to evaporate from the volar forearm region for fifteen to thirty minutes prior to the institution of the measurement procedures. The site was hydrated as noted above and initial spectrum was collected. The data included tests conducted with and without the presence of the various silicones in the test mixture, and at least two test runs were conducted for each mixture. 
     A simplified test procedure is illustrated as follows. A test area on the forearm was marked, and the test area was washed with the soap solution using fifteen rubs, followed by rinsing with ten rubs under cool running water. Excess moisture was blotted from the forearm with a towel. After one minute, the skin was hydrated for one minute using a towel saturated with water which was held loosely over the test area. Excess moisture was blotted, and at the end of thirty seconds a background scan was run. The lest mixture was applied to the skin test area and the solvent allowed to evaporate. The skin was again hydrated for one minute and excess moisture was blotted off. After thirty seconds, a scan was run of the test area which represented an Initial using fifteen rubs followed by ten rinses, and the excess moisture was blotted off. After one minute, the skin was hydrated for one minute, blotted, and at the end of thirty seconds, a scan was run of the test area which represented a First Soap Wash Condition. Similar steps were repeated for second, third, and fourth, soap wash conditions. Baselines for infrared bands were defined and band heights were measured. The percent ingredient remaining on the skin was calculated using this data. 
     The following tables set forth the results of the foregoing procedures, and illustrate the concept of the present invention of enhancing the durability of various emollients with certain functional silicones. The tables indicate that the functional silicones enhance emollient durability and therefore provide a viable solution to dry, chapped, and rough skin, which results when the emollients are removed by washing. The siloxanes are soap wash resistant and have shown minimal or no dermal irritation The carboxyfunctional siloxane is known to possess the least dermal irritation of the siloxane types tested. The functional silicones used in the tables conform to the formula Me 3  SiO(Me 2  SiO) x  (MeRSiO) y  SiMe 3  in which Me is methyl and R is the functional group. Specifics of the R group and values of the integers x and y are set forth in the tables where appropriate. Unless otherwise indicated, the mixtures of emollient and silicone were in a ratio of four to one, and the mixtures were delivered in form of mixtures including a volatile cyclic siloxane. The compositions of the present invention may contain other adjuvants such as perfumes, fragrances, and preservatives, provided the addition of the adjuvant to the composition would not materially affect the basic and novel characteristics of the composition and would not materially change its fundamental characteristics. 
     
                       TABLE I                                                     
______________________________________                                    
EMOLLIENTS - NO SILICONE                                                  
PERCENT REMAINING                                                         
Test      Mink   Lanolin    Mineral                                       
Condition Oil    Oil        Oil    Petrolatum                             
______________________________________                                    
Initial   100    100        100    100                                    
1st wash  32     33         32     44                                     
2nd wash  19     21         16     34                                     
3rd wash  14     15         6      19                                     
4th wash  --     --         4      16                                     
5th wash  --     --         2      13                                     
______________________________________                                    
 
    
     
                       TABLE II                                                    
______________________________________                                    
COMPOUNDS USED                                                            
AMINE AND AMIDE FUNCTIONAL SILICONES                                      
Sili-                                                                     
cone R-Group          M % R    x    y    x/y                              
______________________________________                                    
A    iBuNH(CH.sub.2).sub.2 NH.sub.2                                       
                      1        97   1    91/1                             
B    iBuNH(CH.sub.2).sub.2 NH.sub.2                                       
                      2        96   2    48/1                             
C    iBuNH(CH.sub.2).sub.2 NH.sub.2                                       
                      5        188  10   19/1                             
D    iBuNH(CH.sub.2).sub.2 NH.sub.2                                       
                        0.7    296  2    148/1                            
E    iBuNH(CH.sub.2).sub.2 NH.sub.2                                       
                        0.5    445.8                                      
                                      2.2                                 
                                         203/1                            
F    iBuNH(CH.sub.2).sub.2 NH.sub.2                                       
                        1.7    440.4                                      
                                      7.6                                 
                                         58/1                             
G    iBuNH(CH.sub.2).sub.2 NH.sub.2                                       
                        0.25   796  2    398/1                            
H    iBuNH(CH.sub.2).sub.2 NHCOCH.sub.3                                   
                      2        96   2    48/1                             
______________________________________                                    
 
    
     
                       TABLE III                                                   
______________________________________                                    
PERCENT REMAINING                                                         
MINERAL OIL AND SILICONES                                                 
Test     SILICONES                                                        
Condition                                                                 
         H      A      B    C    D    E    F    G                         
______________________________________                                    
INITIAL  100    100    100  100  100  100  100  100                       
1st wash 46     56     53   47   46   46   50   52                        
2nd wash 28     38     35   35   40   32   34   41                        
3rd wash 22     32     28   30   32   32   28   32                        
4th wash 20     30     24   27   26   26   21   30                        
5th wash 17     25     20   24   22   25   20   19                        
______________________________________                                    
 
    
     
                       TABLE IV                                                    
______________________________________                                    
PERCENT REMAINING                                                         
MINERAL OIL AND SILICONES                                                 
Test    Polydimethylsiloxane (1)   Average                                
Condition                                                                 
        100 DP   550 DP  6800 DP  H    A-G                                
______________________________________                                    
INITIAL 100      100     100      100  100                                
1st wash                                                                  
        35       35      45       46   50                                 
2nd wash                                                                  
        24       20      37       28   36                                 
3rd wash                                                                  
        20       18      31       22   31                                 
4th wash                                                                  
        18       16      27       20   26                                 
5th wash                                                                  
        14       --      24       17   22                                 
______________________________________                                    
 (1): 100 DP is 350 Centistoke fluid.                                     
 550 DP is hydroxy endblocked fluid with partial trimethyl capping.       
 6800 DP is a siloxane gum.                                               
 
    
     
                                           TABLE V                                 
__________________________________________________________________________
% Mineral Oil Remaining                                                   
Sample                                                                    
     Polymer                                                              
           Initial                                                        
                 1st 2nd 3rd 4th 5th                                      
Number                                                                    
     Description                                                          
           Condition                                                      
                 Wash                                                     
                     Wash                                                 
                         Wash                                             
                             Wash                                         
                                 Wash                                     
__________________________________________________________________________
1    No Silicone                                                          
           100   32  16   6   4   2                                       
2    H     100   56  34  25  20  14                                       
3    A     100   40  26  18  16  14                                       
4    B     100   52  27  18  19  13                                       
5    C     100   40  28  25  18  14                                       
6    D     100   58  36  30  17   8                                       
7    E     100   66  41  34  26  24                                       
8    F     100   58  37  28  17  15                                       
9    G     100   33  30  18  20   5                                       
__________________________________________________________________________
 
    
     
                       TABLE VI                                                    
______________________________________                                    
Compounds Used                                                            
Carboxyfunctional Silicones                                               
Reference                                                                 
        R-Group    M % R    x      y     x/y                              
______________________________________                                    
J       iPr COOH   3          201.7                                       
                                     6.3 32/1                             
K       iPr COOH   0.7      296     2    148/1                            
L       iPr COOH   3.3      288    10    29/1                             
M       iPr COOH   15       253    45     6/1                             
______________________________________                                    
 
    
     
                       TABLE VII                                                   
______________________________________                                    
Percent Remaining                                                         
Mineral Oil and Silicone                                                  
Test                                                                      
Condition  J             K      L                                         
______________________________________                                    
INITIAL    100           100    100                                       
1st Wash   44            42     29                                        
2nd Wash   30            33     19                                        
3rd Wash   24            28     14                                        
4th Wash   21            26     13                                        
5th Wash   19            22     15                                        
______________________________________                                    
 
    
     
                       TABLE VIII                                                  
______________________________________                                    
Mineral Oil and Silicone                                                  
Percent Silicone Remaining                                                
        Polydimethylsiloxane   A-G   J-K                                  
Test                    6800       Amino Carboxylic                       
Condition                                                                 
        100 DP  550 DP  DP    H    Avg.  Acid Avg.                        
______________________________________                                    
INITIAL 100     100     100   100  100   100                              
1st Wash                                                                  
        35      35      45    46   50    43                               
2nd Wash                                                                  
        24      20      37    28   36    32                               
3rd Wash                                                                  
        20      18      31    22   31    26                               
4th Wash                                                                  
        18      16      27    20   26    24                               
5th Wash                                                                  
        14      --      24    17   22    20                               
______________________________________                                    
 
    
     
                       TABLE IX                                                    
______________________________________                                    
Mineral Oil and Silicone                                                  
% Mineral Oil Remaining                                                   
Test        No                                                            
Condition   Sil.    J          K    L                                     
______________________________________                                    
INITIAL     100     100        100  100                                   
1st Wash    32      47         52   32                                    
2nd Wash    16      30         36   20                                    
3rd Wash    6       19         24   13                                    
4th Wash    4       13         22    6                                    
5th Wash    2        8         12    4                                    
______________________________________                                    
 
    
     
                       TABLE X                                                     
______________________________________                                    
Two to One                                                                
Mink Oil and Silicone                                                     
% Mink Oil Remaining                                                      
Test        No      Carboxylic Acid                                       
Condition   Sil.    J          K    L                                     
______________________________________                                    
INITIAL     100     100        100  100                                   
1st Wash    32      46         45   30                                    
2nd Wash    19      28         28   17                                    
3rd Wash    14      26         25   10                                    
______________________________________                                    
 
    
     The mixture of emollient and silicone can be delivered to the skin in the form of emulsions, microemulsions, solutions, dispersions, lotions, gels, aerosols, solid sticks, ointments, and creams. 
     It will be apparent from the foregoing that many other variations and modifications may be made in the compounds, compositions, structures, and methods, described herein, without departing substantially from the essential features and concepts of the present invention. Accordingly, it should be clearly understood that the forms of the invention described herein are exemplary only and are not intended as limitations on the scope of the present invention as defined in the appended claims.