Ampoule for crystal-growing furnace
FIELD OF THE INVENTION 
     The present invention relates to a crystal-growth ampoule for use in a multi-zone furnace, and more particularly to such an ampoule particularly suited for withstanding the stress and vibration of space flight. 
     BACKGROUND OF THE INVENTION 
     A gradient-type furnace for growing semiconductor crystals is illustrated in U.S. Pat. No. 4,086,424 which issued Apr. 25, 1978. In this patented furnace a temperature profile having 21 zones is achieved by sequentially powering the heating elements in each zone. An improved furnace is disclosed in U.S. patent application Ser. No. 132,224, filed Dec. 14, 1987, and assigned to the present assigned. Other gradient-type furnaces of the type employed with the present invention are disclosed in U.S. patent applications No. 264,341, filed Oct. 31, 1988; and No. 264,378, filed Oct. 31, 1988. 
     The process for fabricating a semiconductor crystal, such as gallium arsenide, starts with an ampoule which contains a raw gallium arsenide charge which is not of single crystal composition. A seed of single crystalline structure is positioned within the ampoule and adjacent the ingot. The ampoule containing the charge is then subjected to a sequence of carefully controlled temperature changes which result in the melting and solidification of the charge. The presence of the seed adjacent the charge causes the solidification of the charge as a single crystal structure. 
     In order to achieve high uniformity and homogeneity of the grown crystal, it is desirable to have the crystal grown in space where it is not subjected to normal gravitational forces. However, due to the excessive vibration during lift-off and re-entry, the seed and charge are often disturbed upon lift-off so that crystal growth is not possible in space or the grown crystal is damaged when encountering vibrational and impact forces upon re-entry and landing. 
     BRIEF DESCRIPTION OF THE INVENTION 
     The ampoule of the present invention incorporates structural and functional requirements for use in a crystal-growing space flight furnace. Namely, the ampoule is designed to withstand the structural stresses, vibrations, etc., of launch as well as landing, and must be able to provide for the thermal conditions of growing semiconductor crystals in space. 
     In a preferred embodiment of the present invention, a 5 mm quartz wall is fabricated to be approximately 18 inches long and about 2 inches in diameter. Within the wall are included a multiple quartz assembly which is used to support a semiconductor ingot. The multiple quartz assembly includes a small diameter projection for supporting the ampoule in a furnace and for minimizing the interface between the ampoule and the furnace thereby minimizing vibration transmission to the ampoule. 
     The ampoule of the present invention includes a segment for holding a single crystal seed while enclosing a charge of semiconductor material. A quartz tube is positioned within the ampoule wall and bears against the charge so that it is held in place during space flight, launching, and transport, as well as maintaining the grown crystal during the recovery phase of a space flight. 
     The ampoule of the present invention is also unique in that it provides a large space adjacent the charge which can be used for vapor control, such as an arsenic zone in a gallium arsenide ampoule. 
    
    
     BRIEF DESCRIPTION OF THE FIGURE 
     The above-mentioned objects and advantages of the present invention will be more clearly understood when considered in conjunction with the accompanying drawing, in which: 
     The FIGURE is a diagrammatic view of an ampoule in accordance with the present invention which illustrates the disposition of a semiconductor charge and seed therein. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     Referring to the FIGURE, the ampoule of the present invention is generally indicated by reference numeral 10. It is seen to include an outer wall 12 having end projections 14 and 16 which fit into complementary supports within a furnace. By supporting the ampoule at both ends, as opposed to along the entire length of the ampoule, vibration transfer to the ampoule is minimized. In a preferred embodiment, the ampoule wall is approximately 18 inches long and the thickness of wall 12 is 5 mm. 
     Within the wall is a containment member 16A. The containment member is likewise fabricated from quartz and includes a hollow projection 18 at one end thereof for holding a semiconductor seed 20 having a single crystal composition. The seed may be composed of gallium arsenide. The containment member 16A extends to a larger cylindrical section 22 which contains the semiconductor charge 24 which, in a preferred embodiment of the invention, is a raw gallium arsenide crystalline material. 
     A quartz tube 26 is positioned between the right illustrated end 30 of ampoule 10 and the right illustrated end of charge 24. The purpose of the tube is twofold. In the first place, the tube acts as an abutment for maintaining the charge 24 against the left illustrated end 30 of cylindrical section 22. Further, it serves the function of creating a vapor space for vapor during the transformation of the charge between the various phases of crystal growth. The existence of this space allows for the overpressurization within the containment member 16A. Since such overpressurization becomes possible by virtue of the present ampoule design, a final single crystal may be grown having considerable homogeneity and uniformity. 
     As an additional means for snugly containing the seed 20 within hollow projection 18, the seed 20 may be covered with commercially available BETA cloth 32. Similarly, the charge 24 may be covered with BETA cloth 34 which helps contain the charge within the cylindrical section 22. 
     The foregoing describes an ampoule design which is capable of withstanding the stresses and vibrational forces of space vehicle launch and recovery. Further, the inclusion of quartz tube 26 creates a vapor space that enables a homogeneous and uniform single crystal to be grown in space. 
     It should be understood that the invention is not limited to the exact details of construction shown and described herein for obvious modifications will occur to persons skilled in the art.