Ceramic green sheets
BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     This invention relates to ceramic green sheets, and more particularly to a ceramic green sheet used for laminating a plurality of ceramic green sheets one upon the other. 
     2. Related Art Statement 
     Heretofore, the IC package, printed circuit board or the like has been frequently manufactured by laminating a plurality of ceramic green sheets one upon the other. This lamination is usually carried out by piling the ceramic green sheets one upon the other and bonding them through pressing at a heated state by means of a pressing machine or the like. 
     As the lamination through heating and pressing, there is a method of laminating a plurality ceramic green sheets at the piled state. However, in order to increase the bonding property and achieve the stable lamination, there has been proposed a method wherein the lamination is carried out after an organic solvent, a solvent dissolving a binder, a plasticizer or the like is applied to a surface of the ceramic green sheet, a method of heating and pressing a laminate of ceramic green sheets in an atmosphere of an organic solvent gas, and the like. 
     In the method of applying the organic solvent or the like, however, the stability is lost with the lapse of time due to the evaporation of the applied solvent. On the other hand, it is difficult to perform the method of laminating in the solvent gas atmosphere from a viewpoint of the equipment. 
     Further, a metallized paste for the formation of electric conductor is frequently formed on the green sheet to be laminated through printing or the like. Particularly, it is required to make the metallized pattern fine and highly dense. For example, when the pattern has line a width/spacing of about 100 μm/80 μm, it is difficult to conduct the bonding without forming a gap between the metallized lines. In this case, it is possible to remove the gap by raising the lamination pressure, but such a high pressure increases the density of the green sheet and generates scattering of the green sheet density to deform the laminated assembly at the green state, which causes problems such as change of shrinkage during firing, shape warp of the fired product and the like, and consequently products can not be produced with high accuracy. 
     SUMMARY OF THE INVENTION 
     It is, therefore, an object of the invention to provide a ceramic green sheet which can easily and stably perform the lamination without forming the gap even in the formation of a fine metallized pattern under a pressure not changing the density of the green sheet nor deforming the green sheet. 
     According to the invention, there is the provision of a ceramic green sheet comprising a green sheet as a core for maintaining a shape thereof and a surface layer formed on a surface of said green sheet as a lamination assisting layer. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     FIGS. 1a and 1b are conceptionally schematically sectional views of embodiments of the ceramic green sheet printed with a metallized pattern according to the invention, respectively; 
     FIG. 2 is a plan view of an embodiment of the green sheet according to the invention; 
     FIG. 3 is a sectional view showing a lamination state of green sheets according to the invention; 
     FIG. 4 is a sectional view showing a lamination state of the conventional green sheets; 
     FIGS. 5a and 5b are plan and sectional views of another embodiment of the green sheet according to the invention, respectively; and 
     FIGS. 6a and 6b are plan and sectional views showing deformation amounts to be measured, respectively. 
    
    
     DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     In the ceramic green sheet of the aforementioned structure according to the invention, when laminating the green sheets, the very fine and high density metallized pattern can be embedded in the surface layer formed on the green sheet surface without forming the gap even under a relatively low pressure. 
     As the ceramic component of the ceramic green sheet, there are alumina usually used in the manufacture of IC package, printed circuit board or the like; glass filler, crystallized glass, mullite and other ceramic mixture for the purpose of reducing the dielectricity or conducting low temperature firing; aluminum nitride having a high thermal conductivity and the like, which are applicable to the green sheet according to the invention. Such a ceramic component is mixed with a resin as a binder to form a green sheet as a core. As a method of forming the green sheet, a doctor blade method is usual and preferable, but an extrusion method, roll coater method and the like may be used. Moreover, the thickness of the green sheet capable of being formed by the doctor blade method is usually about 100-1200 μm, which is frequently applied to the green sheet used in the production of the IC package, printed circuit board or the like. 
     Then, a surface layer is formed on the surface of the green sheet as a core. The formation of the surface layer is carried out by mixing a ceramic component with a resin as a binder and then applying it to the surface of the green sheet as a core. As the application means, a roll coater is preferable because of uniform application, and particularly the use of a reverse roll coater is favorable because the uniform application can be achieved without being influenced by the scattering of the thickness of the green sheet as the core. And also, the doctor blade process is favorable because the application can be carried out under a tension somewhat applied to the green sheet. Further, a screen printing process, spraying process, process of penetrating slurry and the like may be used. In any case, the surface layer may be formed on one-side surface or both-side surfaces of the green sheet as the core. Moreover, in order to stably and surely conduct the lamination with sandwiching the fine metallized pattern, it is preferable to form the surface layer on both-side surfaces of the green sheet. 
     The metallized pattern is formed on the green sheet by using a paste containing metallic powder such as W, Mo, Cu, Ni, Ag or the like through a screen printing process or the like. In this case, the metallized pattern may be formed on the green sheet as a core or the surface layer. The metallized pattern has usually a thickness of about 5-30 μm, so that the thickness of the surface layer is desirable to be 5-80 μm for completely absorbing the thickness of the metallized pattern in the lamination. When the green sheets are laminated so as to sandwich the metallized pattern therebetween, it is important that the thickness of the metallized pattern is absorbed by the deformation of the surface layer and the deformation is not affected to the green sheet as the core. For this end, it is favorable that the surface layer having a rich flexibility is formed at a thickness larger than that of the metallized pattern. On the other hand, when the thickness of the surface layer is too thick, the properties of the surface layer badly affects the flexibility of the ceramic green sheet, the deformation state of the sheets in the lamination and the like. 
     Moreover, it is desirable that the ceramic component in the ceramic green sheet as a core is substantially the same as the ceramic component of the surface layer for the uniformization of the product composition. The term &#34;substantially the same&#34; used herein means that both the ceramic components are prepared by the same composition system and may not completely be the same. On the other hand, a material having different properties is able to be formed in the laminate, and in this case, both ceramic components may be different. For example, a material having different dielectricity, thermal conductivity, mechanical strength or the like may be formed in the middle or surface portion of the laminate. 
     As the organic binder used in the shaping, use may be made of resins for shaping the green sheet as a core and/or resins for shaping the surface layer, such as polyvinyl butyral (PVB), ethylcellulose, acrylic resin, hydrocarbon resin and the like. Among them, the use of acrylic resin is preferable because it can adjust the flexibility of the green sheet and/or surface layer without a plasticizer and is good in the binder burnout property during the firing. The acrylic resin is a polymer consisting mainly of acrylic acid and/or methacrylic acid series monomer such as acrylic acid, methyl acrylate, ethyl acrylate, methacrylic acid, methyl methacrylate, ethyl methacrylate or the like. 
     When the combination of the resin for the green sheet and the resin for the surface layer is a combination of organic solvent soluble resin and water soluble resin, it is advantageous that these resins are not influenced by each other when the surface layer is formed on the green sheet as the core. In any case, the resin for the green sheet and the resin for the surface layer can properly be used in accordance with the properties required in these resins. 
     In the green sheet as a core, the resin is added in an amount of about 3-30 parts by weight per 100 parts by weight of the ceramic component. When the green sheet is formed by the doctor blade process, the amount of resin added is about 3-15 parts by weight. On the other hand, in the formation of the surface layer, the resin is added in an amount of 3-50 parts by weight per 100 parts by weight of the ceramic component. In order to improve the adhesion property in the lamination, it is preferable that the amount of the resin in the surface layer is made larger than that in the green sheet, or that the plasticizer is added in the surface layer when the plasticizer is not included in the green sheet or the amount of the plasticizer added to the surface layer is increased when the plasticizer is included in the green sheet. Thus, the flexibility is increased in the surface layer rather than in the green sheet as a core to facilitate the adhesion as well as embedding of gaps in fine metallized pattern. Similarly, in order to make the surface layer more flexible than the green sheet, the resin used in the surface layer is effective to have a glass transition temperature (Tg) lower than that of the resin used in the green sheet, or the glass transition temperature may be substantially reduced by adding the plasticizer when using the resin having the same glass transition temperature. Particularly, it is more effective to form the surface layer by mixing the resin having a low glass transition temperature with the plasticizer. Further, the resin used in the surface layer is effective to have a molecular weight lower than that in the green sheet. In any case, it is considered that when using the resin having a low glass transition temperature or a low molecular weight, the movement of the resin as a binder is easy in the lamination to develop the adhesion property. 
     Moreover, the plasticizer may be applied to the surface layer having the above composition after the formation of the metallized pattern on the surface layer through printing process or the like, if necessary, and before the lamination. In this case, the amount of the plasticizer included in the surface layer can previously be reduced or be made zero, and consequently it is prevented to cause a problem of lowering the strength of the green sheet by the influence of the plasticizer included in the surface layer. 
     The green sheet provided with the surface layer may advantageously be subjected to a working for microhole formation by simultaneously punching plural micro through-holes having, for example, a hole diameter of 150 μm and a pitch of 300 μm with a mold. That is, even when cracks are formed between the holes in the green sheet having no surface layer, the presence of the surface layer prevents the formation of cracks. 
     The following examples are given in illustration of the invention and are not intended as limitations thereof. 
     EXAMPLE 1 
     A resin as a binder, a plasticizer and a solvent were added to a ceramic mixture powder consisting of 90% by weight of alumina, 7% by weight of a mixture of clay mineral, silica sand, magnesium carbonate and calcium carbonate and 3% by weight in total of chromium oxide and titanium oxide, which were mixed in a pot mill to form a slurry. After the viscosity of the slurry was adjusted by defoaming under vacuum, the slurry was cast into a green sheet as a core by the doctor blade process. The kind and amount of the resin and the kind and amount of the solvent are shown in the following Table 1. 
     To the same ceramic mixture powder as mentioned above were added a resin as a binder, a plasticizer and a solvent, which were mixed in a pot mill to form a slurry for the formation of a surface layer. The kind and amount of the resin and the kind and amount of the solvent are shown in the following Table 2. 
     
                                           TABLE 1                                 
__________________________________________________________________________
        Tg of                                                             
            Molecular                                                     
                  Amount of resin                                         
                                 Amount of plas-                          
   Kind of                                                                
        resin                                                             
            weight                                                        
                  added (1)                                               
                           Kind of                                        
                                 ticizer added (1)                        
No.                                                                       
   resin                                                                  
        (°C.)                                                      
            of resin                                                      
                  (part by weight)                                        
                           plasticizer                                    
                                 (part by weight)                         
                                          Kind of solvent                 
__________________________________________________________________________
1-1                                                                       
   polyvinyl                                                              
        +65  80000                                                        
                  7        DOP   3        mixture of toluene              
   butyral                                and butanol                     
1-2                                                                       
   acrylic                                                                
        +5  300000                                                        
                  8        --    --       mixture of toluene              
   resin                                  and ethyl acetate               
1-3                                                                       
   acrylic                                                                
        +30 200000                                                        
                  6        DBP     1.5    mixture of xylene               
   resin                                  and ethyl acetate               
1-4                                                                       
   acrylic                                                                
        +40 250000                                                        
                  7        PEG   2        water                           
   resin                                                                  
__________________________________________________________________________
 (1) part by weight per 100 parts by weight of powdery ceramic component  
 
    
     
                                           TABLE 2                                 
__________________________________________________________________________
        Tg of                                                             
            Molecular                                                     
                  Amount of resin                                         
                                 Amount of plas-                          
   Kind of                                                                
        resin                                                             
            weight                                                        
                  added (1)                                               
                           Kind of                                        
                                 ticizer added (1)                        
No.                                                                       
   resin                                                                  
        (°C.)                                                      
            of resin                                                      
                  (part by weight)                                        
                           plasticizer                                    
                                 (part by weight)                         
                                          Kind of solvent                 
__________________________________________________________________________
2-1                                                                       
   polyvinyl                                                              
        +65  50000                                                        
                  15       DOP   6        mixture of toluene              
   butyral                                and ethanol                     
2-2                                                                       
   acrylic                                                                
        +5  300000                                                        
                  40       --    --       mixture of toluene              
   resin                                  and butanol                     
2-3                                                                       
   acrylic                                                                
        +5  300000                                                        
                   8       DOP   10       mixture of toluene              
   resin                                  and butanol                     
2-4                                                                       
   acrylic                                                                
        -10 300000                                                        
                  25       DBP   3        mixture of toluene              
   resin                                  and ethyl acetate               
2-5                                                                       
   acrylic                                                                
        -20 200000                                                        
                  15       --    --       mixture of xylene               
   resin                                  and butyl acetate               
2-6                                                                       
   acrylic                                                                
        +40  50000                                                        
                  20       DBS   5        mixture of toluene              
   resin                                  and ethanol                     
2-7                                                                       
   acrylic                                                                
        +40 250000                                                        
                  20       PEG   15       water                           
   resin                                                                  
__________________________________________________________________________
 (1) part by weight per 100 parts by weight of powdery ceramic component  
 
    
     The slurry of Table 2 was applied to the green sheet of Table 1 according to a combination shown in the following Table 3. The application of the slurry onto the green sheet was carried out by means of a reverse roll coater. Immediately after the application, the green sheet coated with the slurry was placed in a dryer held at a temperature of 100°-150° C. and dried for 2-10 minutes. The &#34;both-side surfaces&#34; in Table 3 means that the front and rear side surfaces of the green sheet were coated with the slurry by repeating the above application method two times. The coated thickness is also shown in Table 3. Moreover, an example of the green sheet having no surface layer is shown as a comparative example in Table 3. 
     
                                           TABLE 3                                 
__________________________________________________________________________
                            Coated thickness                              
   No. of green             per one-side                                  
   sheet as                                                               
          Slurry used as    surface                                       
No.                                                                       
   a core surface layer                                                   
                   Applied surface                                        
                            (μm)                                       
__________________________________________________________________________
3-1                                                                       
   1-1    2-1      one-side surface                                       
                            40                                            
3-2                                                                       
   1-1    2-4      one-side surface                                       
                            20                                            
3-3                                                                       
   1-2    2-1      both-side surfaces                                     
                            40                                            
3-4                                                                       
   1-2    2-2      both-side surfaces                                     
                            30                                            
3-5                                                                       
   1-2    2-3      both-side surfaces                                     
                            25                                            
3-6                                                                       
   1-2    2-3      one-side surface                                       
                            100                                           
3-7                                                                       
   1-2    2-4      both-side surfaces                                     
                            20                                            
3-8                                                                       
   1-2    2-4      one-side surface                                       
                            40                                            
3-9                                                                       
   1-2    2-5      both-side surfaces                                     
                            30                                            
3-10                                                                      
   1-2    2-6      both-side surfaces                                     
                            30                                            
3-11                                                                      
   1-2    2-7      both-side surfaces                                     
                            30                                            
3-12                                                                      
   1-3    2-3      both-side surfaces                                     
                            30                                            
3-13                                                                      
   1-3    2-4      both-side surfaces                                     
                            20                                            
3-14                                                                      
   1-3    2-4      both-side surfaces                                     
                             5                                            
3-15                                                                      
   1-3    2-4      one-side surface                                       
                            10                                            
3-16                                                                      
   1-4    2-4      both-side surfaces                                     
                            40                                            
3-17                                                                      
   1-4    2-7      both-side surfaces                                     
                            40                                            
3-18                                                                      
   1-1    --       --       --                                            
3-19                                                                      
   1-2    --       --       --                                            
__________________________________________________________________________
 
    
     The green sheet of Table 3 was punched out into a square having a side of 70 mm, onto which was printed a W paste through screen printing into a pattern of 101 lines having a line width of 120 μm and a spacing of 80 μm as shown in FIG. 2. Then the green sheet not printed having the same size was piled on the printed surface of the green sheet and then laminated by heating and pressing under lamination conditions as shown in the following Table 4, and the resulting laminate was fired at 1,550° C. in a mixed gas of N 2  and H 2  having a dew point of 35° C. to form a ceramic substrate. Moreover, the conceptionally sectional view of the green sheet printed in the metallized pattern according to the invention is shown in FIG. 1a, and the conceptionally sectional view of the ceramic sheet obtained by laminating the green sheets of FIG. 1a is shown in FIG. 1b. In FIG. 1, the surface layer is formed on both-side surfaces of the green sheet. 
     When the resulting ceramic sheet or porcelain was cut to observe lines of the W metallized pattern by means of a microscope, the ceramic substrate made from the green sheets according to the invention exhibits a good lamination state that gaps are completely embedded between the metallized lines as shown in FIG. 3, while the ceramic sheet made from the green sheets outside the invention has many gaps between the metallized lines as shown in FIG. 4. 
     
                       TABLE 4                                                     
______________________________________                                    
           Lamination conditions                                          
             temperature                                                  
                        pressure                                          
No.          (° C.)                                                
                        (kg/cm.sup.2)                                     
______________________________________                                    
3-1          80         15                                                
3-2          80         20                                                
3-3          80         15                                                
3-4          80         20                                                
3-5          70         10                                                
3-6          70         20                                                
3-7          60          5                                                
3-8          60         10                                                
3-9          50         10                                                
3-10         70         10                                                
3-11         90         30                                                
3-12         70         10                                                
3-13         60          5                                                
3-14         60         15                                                
3-15         60         15                                                
3-16         60         10                                                
3-17         90         20                                                
3-18         110        80                                                
3-19         120        100                                               
______________________________________                                    
 
    
     EXAMPLE 2 
     A resin as a binder, a plasticizer and a solvent as shown in the following Table 5 were added to 100 parts by weight of a ceramic powder consisting of 40% by weight of alumina, 40% by weight of borosilicate glass and 20% by weight of quartz glass, which were mixed in a pot mill, defoamed under vacuum, and then casted into a green sheet as a core by the doctor blade process. Separately, the ceramic powder having the same composition as mentioned above was added with a resin as a binder, a plasticizer and a solvent as shown in the following Table 6 and mixed in a pot mill to form a slurry for the formation of a surface layer. Then, the slurry was applied to the surface of the green sheet with a doctor blade. The combination of the green sheet as a core and the slurry for the formation of surface layer, the applied surface and the coated thickness are shown in the following Table 7. In Table 7 is also shown an example of the green sheet having no surface layer as a comparative example. 
     
                                           TABLE 5                                 
__________________________________________________________________________
           Tg of                                                          
               Amount of resin                                            
                              Amount of plas-                             
           resin                                                          
               added (1)                                                  
                        Kind of                                           
                              ticizer added (1)                           
No.                                                                       
   Kind of resin                                                          
           (°C.)                                                   
               (part by weight)                                           
                        plasticizer                                       
                              (part by weight)                            
                                       Kind of solvent                    
__________________________________________________________________________
5-1                                                                       
   polystyrene                                                            
           +20 8        DOP   1        mixture of toluene                 
                                       and methyl ethyl                   
                                       ketone                             
5-2                                                                       
   polynorbornene                                                         
           +15 7        --    --       toluene                            
5-3                                                                       
   acrylic resin                                                          
           +20 7        DBS   2        mixture of toluene                 
                                       and ethyl acetate                  
__________________________________________________________________________
 (1) part by weight per 100 parts by weight of powdery ceramic component  
 
    
     
                                           TABLE 6                                 
__________________________________________________________________________
           Tg of                                                          
               Amount of resin                                            
                              Amount of plas-                             
           resin                                                          
               added (1)                                                  
                        Kind of                                           
                              ticizer added (1)                           
No.                                                                       
   Kind of resin                                                          
           (°C.)                                                   
               (part by weight)                                           
                        plasticizer                                       
                              (part by weight)                            
                                       Kind of solvent                    
__________________________________________________________________________
6-1                                                                       
   polystyrene                                                            
           +20 20       DOP   5        mixture of toluene                 
                                       and ethyl acetate                  
6-2                                                                       
   polynorbornene                                                         
           +15 25       DOP   10       xylene                             
6-3                                                                       
   acrylic resin                                                          
           +20 15       DBS   7        mixture of toluene                 
                                       and ethyl acetate                  
6-4                                                                       
   acrylic resin                                                          
           -10 20       --    --       mixture of toluene                 
                                       and butanol                        
__________________________________________________________________________
 (1) part by weight per 100 parts by weight of powdery ceramic component  
 
    
     
                                           TABLE 7                                 
__________________________________________________________________________
                            Coated thickness                              
   No. of green             per one-side                                  
   sheet as                                                               
          Slurry used as    surface                                       
No.                                                                       
   a core surface layer                                                   
                   Applied surface                                        
                            (μm)                                       
__________________________________________________________________________
7-1                                                                       
   5-1    6-1      both-side surfaces                                     
                            25                                            
7-2                                                                       
   5-2    6-2      both-side surfaces                                     
                            30                                            
7-3                                                                       
   5-2    6-2      one-side surface                                       
                            50                                            
7-4                                                                       
   5-3    6-3      both-side surfaces                                     
                            15                                            
7-5                                                                       
   5-3    6-3      one-side surface                                       
                            40                                            
7-6                                                                       
   5-3    6-4      both-side surfaces                                     
                            20                                            
7-7                                                                       
   5-2    --       --       --                                            
__________________________________________________________________________
 
    
     The green sheet of Table 7 was punched out into a square having a side of 70 mm, onto which was printed a Cu paste in the same pattern as in Example 1 through screen printing and further piled an unprinted green sheet. The resulting assembly was laminated by heating and pressing under lamination conditions as shown in the following Table 8. The resulting laminate was fired at 1,000° C. in an atmosphere of N 2  gas having a dew point of 30° C. The thus obtained ceramic substrate was cut to observe the Cu metallized pattern. As a result, the ceramic substrate made from the green sheets according to the invention has no gap between the metallized lines likewise Example 1, while many gaps are existent between the metallized lines in the substrate made from the green sheet outside the invention. 
     
                       TABLE 8                                                     
______________________________________                                    
           Lamination conditions                                          
             temperature                                                  
                        pressure                                          
No.          (° C.)                                                
                        (kg/cm.sup.2)                                     
______________________________________                                    
7-1          80         20                                                
7-2          70         10                                                
7-3          70         20                                                
7-4          60          5                                                
7-5          60         10                                                
7-6          50         10                                                
7-7          120        150                                               
______________________________________                                    
 
    
     EXAMPLE 3 
     A resin as a binder, a plasticizer and a solvent as shown in the following Table 9 were added to 100 parts by weight of a ceramic powder consisting of 99% by weight of aluminum nitride and 1% by weight of calcium carbonate, which were mixed in a pot mill, defoamed and cast into a green sheet as a core through the doctor blade process. Separately, the ceramic powder having the same composition as mentioned above was added with a resin as a binder, a plasticizer and a solvent as shown in the following Table 10, which were mixed in a pot mill to form a slurry for the formation of a surface layer. This slurry was applied to the green sheet as a core by means of a reverse roll coater. The combination of the green sheet and the slurry for the formation of surface layer, the applied surface and the coated thickness are shown in the following Table 11. 
     
                                           TABLE 9                                 
__________________________________________________________________________
           Tg of                                                          
                Amount of resin                                           
                               Amount of plas-                            
           resin                                                          
                added (1)                                                 
                         Kind of                                          
                               ticizer added (1)                          
No.                                                                       
   Kind of resin                                                          
           (°C.)                                                   
                (part by weight)                                          
                         plasticizer                                      
                               (part by weight)                           
                                        Kind of solvent                   
__________________________________________________________________________
9-1                                                                       
   polynorbornene                                                         
           +15  8        --    --       mixture of toluene                
                                        and methyl ethyl                  
                                        ketone                            
9-2                                                                       
   acrylic resin                                                          
           0    7        --    --       mixture of xylene                 
                                        and ethanol                       
__________________________________________________________________________
 (1) part by weight per 100 parts by weight of powdery ceramic component  
 
    
     
                                           TABLE 10                                
__________________________________________________________________________
           Tg of                                                          
               Amount of resin                                            
                              Amount of plas-                             
           resin                                                          
               added (1)                                                  
                        Kind of                                           
                              ticizer added (1)                           
No.                                                                       
   Kind of resin                                                          
           (°C.)                                                   
               (part by weight)                                           
                        plasticizer                                       
                              (part by weight)                            
                                       Kind of solvent                    
__________________________________________________________________________
10-1                                                                      
   polynorbornene                                                         
           +15 30       DOP   3        toluene                            
10-2                                                                      
   acrylic resin                                                          
           -10 20       DBP   5        mixture of toluene                 
                                       and ethanol                        
__________________________________________________________________________
 (1) part by weight per 100 parts by weight of powdery ceramic component  
 
    
     
                                           TABLE 11                                
__________________________________________________________________________
   No. of green                                                           
           Slurry used as   Coated thickness per                          
No.                                                                       
   sheet as a core                                                        
           surface layer                                                  
                   Applied surface                                        
                            one-side surface (μm)                      
__________________________________________________________________________
11-1                                                                      
   9-1     10-1    both-side surfaces                                     
                            30                                            
11-2                                                                      
   9-2     10-2    both-side surfaces                                     
                            20                                            
11-3                                                                      
   9-2     --      --       --                                            
__________________________________________________________________________
 
    
     The green sheet of Table 11 was punched out into a square having a side of 70 mm, onto which was printed a W paste in the same pattern as in Example 1 through screen printing and further piled an unprinted green sheet. The resulting assembly was laminated by heating and pressing under lamination conditions as shown in the following Table 12. The resulting laminate was fired at 1,800° C. in an atmosphere of N 2  gas. The thus obtained ceramic substrate was cut to observe the W metallized pattern. As a result, the ceramic substrate made from the green sheets according to the invention has no gap between the metallized lines likewise Example 1, while many gaps are existent between the metallized lines in the substrate made from the green sheet outside the invention. 
     
                       TABLE 12                                                    
______________________________________                                    
           Lamination conditions                                          
             temperature                                                  
                        pressure                                          
No.          (° C.)                                                
                        (kg/cm.sup.2)                                     
______________________________________                                    
12-1         80         15                                                
12-2         60         10                                                
12-3         120        80                                                
______________________________________                                    
 
    
     EXAMPLE 4 
     To the surface of the green sheet made from the ceramic powder as in Example 1 was applied the same slurry for the formation of the surface layer as in Example 1. The thus treated green sheet was used to obtain a laminate composed of three green sheets having a window frame for a package or a chip carriers as shown in FIG. 5. In this case, FIG. 5a is a plan view of the laminate and FIG. 5b is a sectional view thereof, which show a pattern taking 4 chip carrier. The lamination was carried out by piling a first layer on a second layer and then piling a third layer thereon. The combination of the green sheet as a core and the slurry for the formation of surface layer and lamination conditions are shown in the following Table 13. No. described in the column &#34;combination&#34; of Table 13 corresponds to No. of Tables 3 and 4 in Example 1. 
     
                       TABLE 13                                                    
______________________________________                                    
     Combination of green                                                 
                      Deformation Deformation                             
     sheet as a core and slurry                                           
                      amount of   amount of                               
     as a surface layer,                                                  
                      window frame                                        
                                  bottom                                  
No.  and lamination conditions                                            
                      (Δa) (μm)                                  
                                  (Δb) (μm)                      
______________________________________                                    
13-1 3-1              23          56                                      
13-2 3-5              19          40                                      
13-3 3-7               6           8                                      
13-4 3-18             67          121                                     
13-5 3-19             62          107                                     
______________________________________                                    
 
    
     After the lamination, deformation amount of window frame (Δa) as shown in FIG. 6a and deformation amount of bottom (Δb) as shown in FIG. 6b were measured. FIG. 6 shows a one of chip carriers cut out from the pattern shown in FIG. 5, wherein the deformation state in the window frame and the bottom is exaggeratedly shown. The respective deformation amount is also shown in Table 13. As seen from Table 13, when the lamination is carried out by using the green sheet according to the invention, the deformation amounts of the window frame and the bottom are less than those of the case using the conventional green sheet. 
     As mentioned above, the green sheet provided with the surface layer for the lamination according to the invention can fill up gaps between lines of the very fine and high density metallized pattern even when the green sheets are laminated under a relatively low pressure for the manufacture of IC package, printed circuit board or the like. Further, the deformation of IC package or the like at green state or fired state is less and it is effective to prevent the occurrence of cracks when plural fine through-holes are formed in the green sheet through the punching. Therefore, the invention is very valuable in industry.