Pin heterojunction photovoltaic elements with polycrystal AlP(H,F) semiconductor film
FIELD OF THE INVENTION 
     The present invention relates to an improved photovoltaic element usable as a power source not only in commercial and home appliances but also in power supply systems. More particularly, it is concerned with a pin heterojunction photovoltaic element, at least the n-type or p-type semiconductor layer of which comprises an n-type or p-type polycrystal AlP:H(F) semiconductor film which exhibits a high photoelectric conversion efficiency. 
     BACKGROUND OF THE INVENTION 
     There have been proposed a variety of photovoltaic elements such as solar cells and power sources for commercial and home appliances. They utilize pn junctions formed by ion implantation or thermal diffusion of impurities into a single crystal substrate of silicon (Si) or gallium arsenide (GaAs), or by epitaxial growth of an impurity-doped layer on such single crystal substrate. However, there is a disadvantage for any of these photovoltaic elements that they are still costly because of using an expensive specific single crystal substrate. Hence, they have not yet come into general use as solar cells or power sources in commercial and home appliances used by the general public. In order to solve this problem, there have been proposed a photovoltaic element in which there is utilized a pin junction formed by amorphous silicon (hereinafter referred to as &#34;a-Si&#34;) semiconductor films laminated on an inexpensive substrate of a non-single crystal material such as glass, metal, ceramic, synthetic resin, etc. by way of a glow discharge decomposition method. This photovoltaic element does not provide a photoelectric conversion efficiency as high as that provided by the foregoing pn junction photovoltaic element in which a single crystal substrate is used. However, this photovoltaic element can be relatively easily produced and is of low production cost, and because of this, it is used as a power source in some kinds of appliances with very small power consumption such as electronic calculators and wrist watches. 
     In this pin junction amorphous silicon photovoltaic element, the Fermi level of the a-Si semiconductor having a good photoconductive property lies a little toward the conduction band from the center of the band gap and the electric field strength at the interface of the p-i junction is greater than that at the interface of the n-i junction. In this respect, it is advantageous to impinge light from the side of the p-type semiconductor layer in order to provide a desirable photoelectric conversion efficiency. 
     For the p-type semiconductor layer, it is desired to be formed of such a semiconductor film that does not absorb light and does not have defects since the light to be absorbed within the p-type semiconductor layer does not contribute to generation of photoelectric current in the case where defects acting as recombination centers are present therein. In view of this, for the semiconductor film to constitute the p-type semiconductor layer in the pin junction a-Si photovoltaic element, studies have been made on amorphous silicon carbide films (hereafter referred to as &#34;a-SiC film&#34;) which are of wide band gap and also on microcrystalline silicon films (hereinafter referred to as &#34;μC-Si film&#34;) which are known as indirect semiconductor films having small absorption coefficients and which are considered to hardly absorb light when they are of 100 to 200 Å in thickness even in the case where they are of narrow band gap. As for the a-SiC semiconductor film, there is an advantage that its band gap can be widened by increasing the composition ratio of the constituent carbon atoms. However, there is a disadvantage that when its band gap is more than 2.1 eV, its film quality is markedly worsened. Therefore, there is a limit for the a-SiC semiconductor film to be used as the p-type semiconductor layer in a pin heterojunction photovoltaic element. 
     As for the μC-Si semiconductor film, there is still a disadvantage that its band gap is narrow in any case and the quantity of light absorbed thereby is remarkable. Particularly, when the incident light is such that it contains short-wavelength light in a large proportion, the quantity of light absorbed becomes great. 
     In view of this, in order to provide a desirable pin heterojunction photovoltaic element of the type wherein light is impinged from the side of the p-type semiconductor layer, it necessitates the use of a p-type semiconductor film having a desirably wide band gap and a minimized defect density as the p-type semiconductor layer. 
     The same situation is present also in the case of a pin heterojunction photovoltaic element of the type wherein light is impinged from the side of the n-type semiconductor layer. That is, the n-type semiconductor layer is required to be constituted by such an n-type semiconductor film having a desirably wide band gap and with a minimized defect density. 
     Further, in the case of a so-called tandem stacked type photovoltaic element or a triple cell tandem stacked type photovoltaic element comprising a plurality of stacked cells, each cell of which comprises a pin heterojunction photovoltaic element in which the residual components of light which are left not absorbed by the upper cell are absorbed by the lower cell to obtain a sufficient photoelectric conversion, both the p-type semiconductor layer and the n-type semiconductor layer of each of the cells are required to have a desirably wide band gap and a minimized defect density. 
     Further, for any of the foregoing photovoltaic elements, it is required for the material to constitute the p-type or n-type semiconductor layer to be such that it can be directly deposited on a non-single crystal substrate of glass, metal, ceramic or synthetic resin in a desired state and does not give any negative effect to the i-type semiconductor layer laminated thereon. 
     As a semiconductor film capable of providing a wide band which satisfy the foregoing requirements, AlP semiconductor films have been proposed by Japanese Patent Laid-open No. 116673/1981 (called &#34;literature 1&#34; hereinafter), Japanese Patent Laid-open No. 6874/1986 (called &#34;literature 2&#34; hereinafter), Japanese Patent Laid-open No. 189629/1986 (called &#34;literature 3&#34; hereinafter) or Japanese Patent Laid-open No. 189630/1986 (called &#34;literature 4&#34; hereinafter). 
     That is, literature 1 mentions a pin heterojunction solar cell in which either the p-type or n-type semiconductor layer is comprised of a p-type or n-type amorphous AlP semiconductor film (that is, a-AlP semiconductor film) prepared by the glow discharge decomposition method and the i-type semiconductor layer is comprised of a a-Si semiconductor film containing fluorine atoms (F). Literature 1 does not mention anything about a crystalline AlP semiconductor film (that is, poly-AlP semiconductor film) which is to be distinguished from said a-AlP semiconductor film. In addition, literature 1 does not describe anything about the characteristics required for a solar cell for the said pin heterojunction photovoltaic element. Literature 2 describes an improvement in the photovoltaic characteristics of a pin junction solar cell in which a compound semiconductor film and an amorphous silicon semiconductor film are used in combination by the use of a doped compound semiconductor film. However, literature 2 does not teach anything about AlP semiconductor films. Literatures 3 and 4 are concerned with methods of forming semiconductor films containing group III-V elements of the Periodic Table by way of the HR-CVD method (Hydrogen Radical Assisted CVD method). But neither of literatures 3 and 4 mentions anything about AlP semiconductor films. 
     Further, none of literatures 1 to 4 mentions anything about a tandem type photovoltaic element or a triple type photovoltaic element. 
     Against this background, there is an increased social demand to provide an inexpensive photovoltaic element which exhibits a high photoelectric conversion efficiency particularly for short wavelength light and which is practically usable as a solar cell and also as a power source in various appliances. 
     SUMMARY OF THE INVENTION 
     The present invention is aimed at solving the foregoing problems relating to photovoltaic elements for use in solar cells and other appliances and satisfying the foregoing social demand. 
     It is therefore an object of the present invention to provide an improved pin heterojunction photovoltaic element usable in devices typified by a solar cell with the use of an improved AlP semiconductor film which may be desirably formed even on a commercially available inexpensive nonsingle crystal substrate of glass, metal, ceramics or synthetic resin and which may form a desired pin junction with other films formed on such substrate. 
     Another object of the present invention is to provide an improved pin heterojunction photovoltaic element based on the improved AlP semiconductor film which provides a high photoelectric conversion efficiency particularly for short-wavelength light and which is usable in devices typified by a solar cell. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     FIG. 1(A) is a schematic representation showing a typical layer structure of a pin heterojunction photovoltaic element according to the present invention. 
     FIG. 1(B) is a schematic representation showing another typical layer structure of a pin heterojunction photovoltaic element according to the present invention. 
     FIG. 1(C) is a schematic representation showing a typical multi-cell tandem stacked structure of a pin heterojunction photovoltaic element according to the present invention. 
     FIG. 2 is a schematic diagram showing the apparatus for forming a deposited film by way of a HR-CVD method of the present invention. 
     FIG. 3 is a schematic diagram showing the apparatus for forming a deposited film by way of a reactive sputtering method of the present invention. 
     FIG. 4 is a schematic diagram showing the apparatus for forming a deposited film by way of a plasma CVD method of the present invention. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     The present inventors have made extensive studies for overcoming the foregoing problems of the known AlP semiconductor films for use in various devices such as solar cells and attaining the objects as described above and as a result, have accomplished the present invention based on the findings obtained through various experiments as below described. 
     That is, as a result of preparing a polycrystal AlP semiconductor film in which a specific amount of hydrogen atoms was incorporated, optionally a specific amount of fluorine atoms was additionally incorporated, and the average size of crystal grains is controlled to a specific value (this deposited film is hereinafter referred to as &#34;poly-AlP:H(F) film&#34;), the present inventors have found that (a) the poly-AlP:H(F) film may be formed in a desired state even on a non-single crystal substrate of glass, metal, ceramics or synthetic resin: (b) the poly-AlP:H(F) film formed on such non-single crystal substrate is accompanied with very few defects: (c) it can be easily and efficiently doped with a dopant of p-type or n-type: and (d) when doped with such dopant, there is afforded a desirable high quality p-type or n-type poly-AlP:H(F) semiconductor film having many practically applicable semiconductor characteristics. 
     The present inventors have further found that in the case of using the foregoing poly-AlP:H(F) film as a member of a pin heterojunction photovoltaic element, there is afforded a pin heterojunction photovoltaic element which efficiently and stably generates a desired photoelectromotive force. 
     The present invention has been completed on the basis of these findings, and it provides pin heterojunction photovoltaic elements as are below mentiond. (1) A pin heterojunction photovoltaic element which generates photoelectromotive force by the junction of a p-type semiconductor layer, an i-type semiconductor layer and an n-type semiconductor layer, characterized in that at least one of said p-type and n-type semiconductor layers comprises a polycrystal semiconductor film comprised of aluminum atoms (Al), phosphorus atoms (P), hydrogen atoms (H), optionally fluorine atoms (F), and atoms (M) of a p-type or n-type dopant element: said semiconductor film contains crystal grains of an average size in the range of 50 to 1000 Å: and said semiconductor film contains the hydrogen atoms (H) in an amount of 0.5 to 5 atomic % (this polycrystal semiconductor film will be hereinafter referred to as &#34;poly-AlP:H(F):M film&#34;): and said i-type layer comprises a non-single crystal semiconductor film containing silicon atoms (Si) as a matrix and at least one kind of atoms selected from the group consisting of hydrogen atoms (H) and fluorine atoms (F). Said non-single crystal semiconductor film includes amorphous semiconductor films including microcrystal semiconductor films, and polycrystal semiconductor films, and it will be hereinafter referred to as &#34;Non-Si(H,F) film&#34;. (2) A pin heterojunction photovoltaic element which generates photoelectromotive force by the juction of a p-type semiconductor layer, an i-type semiconductor layer and an n-type semicondeuctor layer, characterized in that at least one of said p-type and n-type semiconductor layers comprises the foregoing poly-AlP:H(F):M semiconductor film: and said i-type semiconductor layer comprises a non-single crystal semiconductor film containing silicon atoms (Si) as a matrix, at least one kind of atoms selected from the group consisting of carbon atoms (C) and germanium atoms (Ge) at least one kind of atoms selected from the group consisting of hydrogen atoms (H) and fluorine atoms (F) (this film will be hereinafter referred to as &#34;Non-Si(C,Ge)(H,F) semiconductor film&#34;). This Non-Si(C,Ge)(H,F) semiconductor film includes a-Si(C,Ge)(H,F) semiconductor films, uC-Si(C,Ge)(H,F) semiconductor films, and poly-Si(C,Ge)(H,F) semiconductor films. 
     Any of the foregoing pin heterojunction photovoltaic elements (1) and (2) according to the present invention stably provides a high photoelectric conversion efficiency particularly for short-wavelength light and enables the obtainment of a large Isc at a high Voc. In addition, any of the foregoing pin heterojunction photovoltaic elements (1) and (2) according to the present invention may be a multi-cell tandem stacked photovoltaic element, each cell comprising the foregoing pin heterojunction photovoltaic element (1) or (2). The pin heterojunction photovoltaic element according to the present invention always exhibits its functions even upon repeated use for a long period of time without deterioration and thus, it can be practically used as a power source to supply electric power. 
     The experiments carried out by the present inventors will be detailed in the following. 
     Experiment A 
     Studies on the method of forming a poly-AlP:H(F) film. 
     The present inventors have prepared poly-AlP:H(F) films by each of the following three processes (1) to (3). 
     Process (1) by HR-CVD method 
     This process (1) forms a poly-AlP:H(F) film by using an Al-containing precursor from an Al-containing raw material gas, a P-containing precursor from a P-containing raw material gas, hydrogen radicals from hydrogen gas (H 2 ), optionally fluorine radicals from a F-containing raw material gas and chemically reacting them in a film-forming space containing a substrate on which a film is to be deposited to form a poly-AlP:H(F) film on the substrate maintained at a desired temperature. 
     This process (1) is practiced by using an appropriate HR-CVD apparatus having a structure as shown in FIG. 2. 
     The HR-CVD apparatus shown in FIG. 2 comprises a film-forming chamber 201 in which is installed a substrate holder 202. There is shown a substrate 203 which is fixed onto the substrate holder 202. The substrate 203 is heated by radiation from an infrared heater 205, while being monitored by a thermo-couple 204. 
     The substrate holder 202 is transferred to the other film-forming chamber 222 or a load lock chamber 212 through a gate valve 207 by a substrate transfer unit 206. Reference numeral 208 stands for a first activation chamber connected through a transport conduit 217 to the film-forming chamber 201. 
     To the activation chamber 208, a gas supply pipe 214 extending from a gas reservoir containing, for example, an Al-containing raw material gas (not shown) is connected. The first activation chamber 208 is provided with an activation energy generation means 211 to apply an activation energy such as an electric energy of direct current, high-frequency or microwave, heat energy or light energy to said Al-containing raw material gas supplied into the first activation chamber 208, to thereby produce Al-containing precursors, which are successively transported through the transport conduit 217 into the film-forming chamber 201. 
     Likewise, reference numeral 209 stands for a second activation chamber connected through a transport conduit 218 to the film-forming chamber 201. To the second activation chamber 209, a gas supply pipe 215 extending from a gas reservoir containing, for example, H 2  gas (not shown) is connected. 
     The second activation chamber 209 is provided with an activation energy generation means 212 to apply an activation energy such as an electric energy of direct current, high-frequency or microwave, heat energy or light energy to said H 2  gas supplied into the second activation chamber 209, to thereby produce hydrogen radicals, which are successively transported through the transport conduit 218 into the film-forming chamber 201. 
     Further, reference numeral 210 stands for a third activation chamber connected through a transport conduit 219 to the film-forming chamber 201. Reference numeral 216 stands for a gas supply pipe extending from a gas reservoir containing, for example, a P-containing raw material gas (not shown) which is connected to the third activation chamber 210. The third activation chamber 210 is provided with an activation energy generation means 213 to apply an activation energy such as an electric energy of direct current, high-frequency or microwave, heat energy or light energy to said P-containing raw material gas supplied into the third activation chamber 210, to thereby produce P-containing precursors, which are successively transported through the transport conduit 219 into the film-forming chamber 201. 
     The foregoing Al-containing precursors, P-containing precursors and hydrogen radicals thus introduced into the film-forming chamber 201 are mixed and chemically reacted to form a semiconductor film on the substrate 203 maintained at a desired temperature. The film-forming chamber 201 is provided with an exhaust pipe connected through an exhaust valve 220 to a vacuum pump 221. Reference numeral 223 stands for a pressure gage provided with the film-forming chamber 201, which serves to monitor the inner pressure of the film-forming chamber 201. 
     Now, by the HR-CVD method to be practiced in the foregoing HR-CVD apparatus shown in FIG. 2, there were prepared ten kinds of semiconductor films containing Al and P (Samples Nos. 1 to 10) under the conditions shown in Table 1. In each case, there was used a Corning No. 7059 glass plate of 2 (inch) by 2 (inch) in size and 0.8 mm in thickness (product by Corning Glass Works Co.) as the substrate 203. As for Al(C 2  H 5 ) 3  (raw material gas (A) in Table 1). it was gasified by introducing He gas as a carrier gas thereinto in a bubbling vessel (not shown) and supplied through the gas supply pipe 214 into the first activation chamber 208. PF 5  gas (raw material gas B in Table 1) was supplied through the gas supply pipe 216 into the third activation chamber 210. And H 2  gas and He gas (raw material gas (C) in Table 1) were supplied through the gas supply pipe 215 into the second activation chamber 209. 
     For each of the resultant semiconductor film samples Nos. 1 to 10, the film sample was cut into six equal parts. 
     The first cut part was subject to measurement of the hydrogen content in the film by a SIMS apparatus (trade name: IMS-3f, product by CAMEA Co., Ltd.). The second cut part was supplied to a X-ray microanalyzer EPM-810Q (product by Shimazu Seisakusho K.K.) to determine the distributed states and the composition ratio of Al to P in the film. The third cut part was supplied to an X-ray diffractometer RAD IIB (product by Rigaku Denki K.K.) to determine the crystal orientation and the size of the crystal grains in the film. 
     The results obtained are collectively shown in Table 2. 
     From the results shown in Table 2, there have been obtained the following findings. That is, it has been firstly recognized that the hydrogen content, the fluorine content and the sizes of crystal grains in the film can be properly controlled by regulating the flow rate of H 2  gas to be introduced into the second activation chamber 209. 
     Then, in the case of each of the film samples Nos. 1 and 2 which were prepared with the respective flow rates of 0 sccm and 0.2 sccm for the H 2  gas, it has been found that since supply of the hydrogen radicals into the reaction system is zero or small, the hydrogen content in the film is zero or small but the fluorine content therein is relatively large, Al and P are distributed in localized states and the film structure is random and does not have a crystal orientation. 
     As for the film samples Nos. 3 to 7, it has been found that the composition ratio of Al to P in the film satisfies the stoichiometric ratio with the flow rate of H 2  gas being increased wherein a crystal orientation is caused and the sizes of crystal grains are enlarged accordingly. 
     As for the film samples Nos. 8 to 10 which were prepared with an increased flow rate of the H 2  gas, a tendency has been found that supply of hydrogen radicals into the reaction system becomes excessive and causes negative influences for the film to be deposited such as etching and because of this, the sizes of crystal grains is reduced and the hydrogen content also is reduced. 
     In consequence, it has been recognized that the amount of hydrogen radicals supplied to the reaction system plays an important role in forming the film. 
     In addition to the above, other facts have also found through further experiments by the present inventors. That is, changes in the film-forming parameters i.e. the substrate temperature, the inner pressure, the activation energy power (microwave power) to be applied, the flow rate of a dilution gas (He gas), the distance between the substrate and the outlet of the transportation conduit, the kinds of the raw material gases to be used also contribute somewhat to control of the hydrogen content, the fluorine content and the sizes of crystal grains in the film. 
     Process (2) by reactive sputtering method 
     This process (2) is to form a poly-AlP:H(F) film by introducing Ar gas and H 2  gas, and optionally F 2  gas or HF gas in combination into a film-forming chamber in which a substrate is placed and a cathode electrode having a target comprising a single crystal AlP wafer plate thereon is placed at a position opposite to the substrate, applying a high frequency voltage to the cathode to form a plasma atmosphere in the space between the substrate and the aluminum wafer plate, sputtering the AlP wafer plate with the plasma to release aluminum atoms (Al) and phosphorus atoms (P) and chemically reacting the aluminum atoms (Al) with phosphorus atoms (P), hydrogen atoms (H) and optional fluorine atoms (F) present in the plasma to cause the formation of said film on the substrate maintained at a desired temperature. 
     This process (2) is practiced by using an appropriate reactive sputtering apparatus having such a structure as shown in FIG. 3. 
     The reactive sputtering apparatus shown in FIG. 3 comprises a film-forming chamber 301 in which is installed a substrate holder 302. There is shown a substrate 303 which is fixed onto the substrate holder 302. The substrate 303 is heated by radiation from an infrared heater 305, while being monitored by a thermo-couple 304. The substrate holder 302 is transferred to the other film-forming chamber 317 or a load lock chamber 313 through a gate valve 307 by a substrate transfer unit 306. The substrate 303 is electrically grounded through the substrate holder 302 as shown in FIG. 3. Reference numeral 312 stands for a cathode electrode having a target 316 comprising, for example, a single crystal AlP wafer plate, placed thereon. The cathode electrode 312 is connected through a matching box 311 to a high frequency power source 310. The film-forming chamber 301 is provided with a gas supply pipe 308 for introducing sputtering gases such as Ar gas, H 2  gas. F 2  gas, etc. into the film-forming chamber. The film-forming chamber 301 is further provided with an exhaust pipe connected through a exhaust valve 314 to a vacuum pump 315. Numeral reference 309 stands for a pressure gage provided with the film-forming chamber 301, which serves to monitor the inner pressure of the film-forming chamber 301. 
     Now, by the reactive sputtering method to be practiced in the foregoing sputtering apparatus shown in FIG. 3, there were prepared ten kinds of semiconductor films containing Al and P (Samples Nos. 11 to 20) under the conditions shown in Table 3. 
     In each case, there was used a Corning No. 7059 glass plate of 2 (inch) by 2 (inch) in size and 0.8 mm in thickness as the substrate 303. 
     For each of the resultant film samples Nos. 11 to 20, the film sample was cut into six equal parts; three of them were subjected to the evaluations in the same manners as in the above case. 
     The results obtained are collectively shown in Table 4. 
     From the results shown in Table 4, there have been obtained the following findings. That is, it has been firstly recognized that the hydrogen content, the fluorine content and the sizes of crystal grains in the film can be properly controlled by regulating the flow rate of H 2  gas or/and HF gas introduced into the film-forming chamber 301. 
     Then, for the case of the film sample No. 11 which was prepared with introduction of neither H 2  gas nor HF gas, it has been recognized that neither hydrogen radicals nor fluorine radicals are present in the plasma atmosphere formed in the film-forming chamber 301 and because of this, the resultant film contains neither hydrogen atoms nor fluorine atoms, the composition ratio of Al to P does not satisfy the stoichiometric ratio and the Al and the P are distributed in localized states in the film, and the film structure is random and does not have a crystal orientation. 
     Likewise, in the case of the film sample No. 12 which was prepared with introduction of H 2  gas but with no introduction of HF gas, it has been recognized that hydrogen radicals are not present in a sufficient amount in the plasma atmosphere formed in the film-forming chamber 301 and because of this, although the resultant film contains a certain amount of hydrogen atoms, the composition ratio of the Al to the P does not satisfy the stoichiometric ratio and the Al and the P are distributed in localized states in the film, and the film structure is random and does not have a crystal orientation. 
     On the other hand, for the film samples Nos. 13 to 18, it has been recognized that the more the flow rate of H 2  gas is increased, the more the composition ratio of the Al to the P satisfies the stoichiometric ratio and the distributed states of the Al and the P are improved, and in addition, the average size of crystal grains is desirably enlarged and the film contains desired amounts of hydrogen atoms and optional fluorine atoms. 
     However, for the film samples Nos. 19 and 20 which were prepared with excessive flow rates of H 2  gas and HF gas, a tendency has been recognized that excessive amounts of hydrogen radicals and fluorine radicals are present in the plasma atmosphere formed in the film-forming chamber 301 and because of this, the average size of crystal grains is undesirably reduced, and both the hydrogen content and the fluorine content are undesirably increased. 
     In consequence, it has been recognized that the amount of hydrogen radicals present in the plasma atmosphere formed in the reaction system plays an important role and the chemical reactions to cause the formation of the film are enhanced when fluorine radicals are present together with the hydrogen radicals in the above plasma atmosphere formed in the reaction system, thereby resulting in forming desired poly-AlP:H(F) films 
     In addition to the above, other facts have been also found through further experiments by the present inventors. That is, changes in the film-forming parameters i.e. the substrate temperature, the inner pressure, the high frequency power to be applied, the flow rates of sputtering gases to be used, the distance between the target and the substrate and the like also contribute somewhat to control the hydrogen content, the fluorine content and the average size of crystal grains in the film. 
     Process (3) by plasma CVD method 
     This process (3) is to form a poly-AlP:H(F) film by introducing an Al-containing raw material gas (A), a P-containing raw material gas (B), H 2  gas (C), and optionally a further gas such as HF gas or F 2  gas into a film-forming chamber in which a substrate on which a film is to be formed is placed and a cathode electrode is installed, applying a high frequency voltage to the cathode to cause glow discharge plasmas by which the raw material gases ar decomposed to cause the formation of said film on the substrate maintained at a desired temperature. 
     This process (3) is practiced by using an appropriate plasma CVD apparatus having such a structure as shown in FIG. 4. 
     The plasma CVD apparatus shown in FIG. 4 comprises a film-forming chamber 401 in which is installed a substrate holder 402. There is shown a substrate 403 which is fixed onto the substrate holder 402. The substrate 403 is heated by radiation from an infrared heater 405, while being monitored by a thermo-couple 404. The substrate holder 402 is transferred to the other film-forming chamber 416 or a load lock chamber 413 through a gate valve 407 by a substrate transfer unit 406. Reference numeral 412 stands for a cathode electrode which is placed at the position opposite to the substrate 403. The cathode electrode 412 is connected through a matching box 411 to a high frequency power source 410. The film-forming chamber 401 is provided with a gas supply pipe which is connected through a plurality of feed pipes 408, 409 to a plurality of gas reservoirs (not shown). The film-forming chamber 401 is further provided with an exhaust pipe connected through an exhaust valve 414 to a vacuum pump 415. Reference numeral 417 stands for a pressure gage provided with the film-forming chamber 401, which serves to monitor the inner pressure of the film-forming chamber 401. 
     Now, by the plasma CVD method to be practiced in the foregoing plasma CVD apparatus shown in FIG. 4, there were prepared ten kinds of AlP system semiconductor films (Samples Nos. 21 to 30) under the conditions shown in Table 5. In each case, there was used a Corning No. 7059 glass plate of 2 (inch) by 2 (inch) in size and 0.8 mm in thickness as the substrate 403. 
     As for Al(C 2  H 5 ) 3  (raw material gas (A) in Table 5), it was gasified by introducing He gas as a carrier gas thereinto in a bubbling vessel (not shown) to produce a raw material gas containing said Al(C 2  H 5 ) 3 , which was supplied into the film-forming chamber 401 through the feed pipe 408. Other raw material gases, i.e. PH 3  gas (raw material gas (B) in Table 5) and H 2  gas and HF gas (raw material gas (C) in Table 5) were supplied into the film-forming chamber 401 through the feed pipe 409. 
     For each of the resultant film samples Nos. 21 to 30, the film sample was cut into six equal parts, the three parts of which were subjected to the evaluations in the same manners as in the foregoing case of the process (1). 
     The results obtained are collectively shown in Table 6. 
     From the results shown in Table 6, there have obtained the following findings. 
     That is, it has been firstly recognized that the hydrogen content, the fluorine content and the average size of crystal grains in the film can be properly controlled by regulating the flow rate of the raw material gas (C) i.e. principally H 2  gas and also HF gas introduced into the film-forming chamber 401. 
     Then, for the case of the film sample No. 21 which was prepared without introduction of H 2  gas and HF gas, it has been recognized that because neither H 2  gas nor HF gas is used, the resultant film is amorphous, the Al and the P are distributed in localized states and the film contains an undesirably large amount of hydrogen atoms due to the influence caused by the residual --C 2  H 5  group in the reaction system. 
     Likewise, for the case of the film sample No. 22 which was prepared with introduction of H 2  gas only at a flow rate of 5 sccm, it has been recognized that because the amount of hydrogen radicals present in the plasma atmosphere formed in the reaction system is insufficient, the resultant film is amorphous, Al and P are distributed in localized states and the film contains an undesirably large amount of hydrogen atoms due to the influence caused by the residual --C 2  H 5  group in the reaction system. Further, for the case of the film sample No. 23 which was prepared by introducing H 2  gas and HF gas into the film-forming chamber 401 at respective flow rates of 5 sccm, it has been recognized that because the amount of hydrogen radicals present in the plasma atmosphere formed in the reaction system is still insufficient, the resultant film is still amorphous and although the hydrogen content in the film is desirable, the distributed states of the Al and the P are not desirably even but uneven. 
     On the other hand, for the film samples Nos. 24 to 28 which were prepared by introducing H 2  gas at respective flow rates of 50, 100, 100, 300 and 500 and HF gas at respective flow rates of 50, 50, 100, 50 and 50 into the film-forming chamber 401, each of the films contains desirable amounts of hydrogen atoms and fluorine atoms, the composition ratio of the Al to the P satisfies the stoichiometric ratio, the Al and the P are evenly distributed in the film, the film has a desirable crystal orientation and contains a desirable average size of crystal grains. However, for the film samples Nos. 29 and 30 which were prepared with excessive flow rates of H 2  gas, a tendency has been recognized that there ar present an excessive amount of hydrogen radicals in the plasma atmosphere formed in the reaction system and because of this, reduction in the average size of crystal grains in the film is caused. 
     In consequence, it has been recognized that the amount of hydrogen radicals present in the plasma atmosphere upon forming the poly-AlP: H(F) films plays an important role and the chemical reactions to cause the formation of said film are enhanced when fluorine radicals are present together with the hydrogen radicals in the plasma atmosphere formed in the reaction system, thereby resulting in forming a desired poly-AlP: H(F) film. 
     In addition to the above, other facts have been also found through further experiments by the present inventors. That is, changes in the film-forming parameters, i.e. the substrate temperature, the inner pressure, the high frequency power to be applied, the flow rates and the kinds of the raw material gases (A),(B) and (C), the distance between the substrate and cathode, and the like also contribute somewhat to control the hydrogen content, the fluorine content and the average size of crystal grains in the film. 
     Experiment B 
     Observations of the interrelations among various characteristics, the content of hydrogen atoms, the content of optional fluorine atoms, and the average size of crystal grains for the deposited film 
     Each of the foregoing film samples Nos. 1 to 30 was examined for deterioration in its characteristics under light irradiation. 
     The examination was carried out using one of the remaining cut three parts. 
     Prior to the examination, a comb-shaped Cr electrode was formed on each specimen by vacuum deposition. The resultant was exposed to AM-1 light (100 mW/cm 2 ) for 8 hours to examine the ratio of change Δσ in the electric conductivity (σ) after irradiation with the AM-1 light for 8 hours versus the initial value (σ i ), that is Δσ=σ e  /σ i , where σ e  is the value after irradiation with the AM-1 light for 8 hours. 
     The results for the ratio of change Δσ are collectively shown in Table 7. For this evaluation item in Table 7, the symbol &#34;0&#34; means the case where Δσ≧0.95, the symbol &#34;Δ&#34; means the case where 0.9&lt;Δσ≦0.95 and the symbol &#34;X&#34; means the case where Δσ&lt;0.9. 
     Then, each of the foregoing film samples Nos. 1 to 30 was examined for the content of an impurity in the following way. That is, in each case, one of the remaining two cut parts was placed in a cryostat and irradiated with light from a UV lamp (1KW) at a temperature of 7.7K to examine photoluminescence. 
     This evaluation was made based on the ratio ΔI between the intensity I R  of a spectrum from the film sample No. 11 as the control and the intensity Is of a spectrum from the other film sample (that is, ΔI=Is/I R ) and the number of the spectra. The results for the photoluminescence are collectively shown in Table 7. For this evaluation item in Table 7, the symbol &#34;0&#34; means the case where ΔI≦0.3, the symbol &#34;Δ&#34; means the case where 0.3≦I≦0.7, and the symbol &#34;X&#34; means the case where ΔI&gt;0.7. 
     Finally, each of the foregoing film samples Nos. 1 to 30 was examined for surface smoothness in the following way. That is, in each case, the remaining last cut part was placed in a FE-SEM (trade name: field-emission scanning electron microscope S-900, produced by Hitachi Seisakusho K.K.) to examine the minute structure of the surface of the film. The results are collectively shown in Table 7. 
     For this evaluation item in Table 7, the symbol &#34;0&#34; means the case where crystal grains are uniformly distributed, and surface roughness and pin holes are not present, and the symbol &#34;X&#34; means the case where crystal grains are not observed, or crystal grains are unevenly distributed, and/or roughness and pin holes are observed. 
     In addition, the above results were combined to totally evaluate each of the film samples Nos. 1 to 30. The totally evaluated results are collectively shown in the column &#34;total evaluation&#34; of Table 7. For this evaluation in Table 7, the symbol &#34; ⊚ &#34; means the case where the total evaluation was concluded to be excellent, the symbol &#34; ○ &#34; means the case where the total evaluation was concluded to be good, the symbol &#34;Δ&#34; means the case where the total evaluation was concluded to be fairly good, and the symbol &#34;X&#34; means the case where the total evaluation was concluded to be not good. 
     From the results shown in Table 7, it has been considered that the film samples which were evaluated as being excellent or good in the total evaluation are desirably usable as constituent element members in various electronic devices including photovoltaic devices. And it has been confirmed that each of these film samples contains hydrogen atoms in an amount of 0.5 to 5 atomic %, optional fluorine atoms in an amount of 0 to 5 atomic %, and crystal grains of an average size in the range of 50 to 1000 Å. 
     Experiment C 
     Observations of the doping properties of the AlP:H(F) film (1) n-type doping properties 
     The foregoing procedures for preparing the film samples No. 1 to 10 by the HR-CVD method were repeated, except that liquid Se(CH 3 ) 2  was gasified by feeding He gas (as a carrier gas) into said liquid Se(CH 3 ) 2  in a bubbling vessel (not shown) to generate a gas comprising Se(CH 3 ) 2  saturated with He gas (hereinafter referred to as &#34;Se(CH 3 ) 2  /He gas&#34;) and this Se(CH 3 ) 2  /He gas was used as an n-type dopant-imparting raw material gas together with the raw material gas (A) in Table 1 and said Se(CH 3 ) 2  /He gas was introduced into the first activation chamber 208 at a flow rate of 30×10 -10  mol/min together with the raw material gas (A), to thereby obtain ten AlP:H(F):Se film samples (Samples Nos. 31 to 40). 
     Likewise, ten AlP:H(F):Se film samples (Samples Nos. 41 to 50) were prepared by repeating the foregoing procedures for preparing the film samples Nos. 11 to 20 by the reactive sputtering method, except for using said Se(CH 3 ) 2  /He gas in addition to the sputtering gases shown in Table 3 and introducing said Se(CH 3 ) 2  /He gas at a flow rate of 5×10 -11  mol/min together with the sputtering gases into the film-forming chamber 301. 
     Further, ten AlP:H(F): Se film samples (Samples Nos. 51 to 60) were prepared by repeating the foregoing procedures for preparing the film samples 21 to 30 by the plasma CVD method, except for using said Se(CH 3 ) 2  /He gas in addition to the raw material gas (A) shown in Table 5 and introducing said Se(CH 3 ) 2  /He gas at a flow rate of 1.7×10 -10  mol/min together with the raw material gas (A) into the film-forming chamber 401. 
     Each of the film samples Nos. 31 to 60 thus obtained was examined with respect to various evaluation items in the same manners as in the above Experiments A and B. Each was also examined for conduction type by a conventional thermo-electric power measuring method. 
     As a result, the film samples Nos. 34 to 39 (which correspond to the foregoing film samples Nos. 4 to 9), the film samples Nos. 43 to 48 (which correspond to the foregoing film samples Nos. 13 to 18), and the film samples Nos. 55 to 58 (which correspond to the foregoing film samples Nos. 25 to 28) were found to be excellent or good in the total evaluation. Specifically, each of these film samples was very satisfactory, with the hydrogen content in the range of 0.5 to 5 atomic %, the fluorine content in the range of 0 to 5 atomic %, the average size of crystal grains, the ratio of change in the electric conductivity and the photoluminescence, and each had a desirable crystal orientation. And each of these films samples exhibited a desirable n-type conductivity. 
     The average size of crystal grains contained in these film samples was found to be in the range of 50 to 1000 Å. Separately, as a result of examining the quality of each of these film samples doped with an n-type dopant (Se), it has been found that each of the film samples containing fluorine atoms (F) exhibits an improved heat resistance. 
     (2) p-type doping properties 
     The foregoing procedures for preparing the film samples Nos. 1 to 10 by the HR-CVD method were repeated, except that there was used Zn(CH 3 ) 2  (hereinafter referred to as &#34;DMZn&#34;) as a p-type dopant-imparting raw material gas. It was gasified by introducing He gas as a carrier gas into the DMZn contained in a bubbling vessel (not shown) and the resultant gas was introduced at a flow rate of 4.5×10 -10  mol/min into the activation chamber 208 together with the raw material gas (A) in Table 1, to thereby obtain ten AlP:H(F):Zn film samples (Samples Nos. 61 to 70). 
     Likewise, ten AlP:H(F):Zn film samples (Samples Nos. 71 to 80) were prepared by repeating the foregoing procedures for preparing the film samples Nos. 11 to 20 by the reactive sputtering method, except for using DMZn, gasifying it with the use of He gas and introducing the resultant gas containing DMZn at a flow rate of 6.0×10 -11  mol/min into the film-forming chamber 301 together with the sputtering gases shown in Table 3. 
     Further, ten AlP:H(F):Zn film samples (Sample Nos. 81 to 90) were prepared by repeating the foregoing procedures for preparing the film samples Nos. 21 to 30 by the plasma CVD method, except for using DMZn, gasifying it with the use of He gas and introducing the resultant gas containing DMZn at a flow rate of 2.5×10 -10  mol/min into the film-forming chamber 401 together with the raw material gas (A) shown in Table 5. 
     Each of the film samples Nos. 61 to 90 thus obtained was examined with respect to various evaluation items in the same manners as in the above Experiments A and B. It was also examined for conduction type by a conventional thermo-eletric power measuring method. 
     As a result, the film samples No. 64 to 69 (which correspond to the foregoing film samples Nos. 4 to 9), the film samples Nos. 73 to 78 (which correspond to the foregoing film samples Nos. 13 to 18), and the film samples Nos. 85 to 88 (which correspond to the foregoing film samples Nos. 25 to 28) were found to be excellent or good in the total evaluation. Specifically, each of these film samples was very satisfactory with the hydrogen content in the range of 0.5 to 5 atomic %, the fluorine content in the range of 0 to 5 atomic %, the average size of crystal grains, the ratio of change in the electric conductivity and the photoluminescence, and it had a desirable crystal orientation. Each of these film samples exhibited a desirable p-type conductivity. The average size of crystal grains contained in each of these film samples was found to be in the range of 50 to 1000 Å. Separately, as a result of examining the quality of each of these film samples doped with a p-type dopant (Zn), it has been found that each of the film samples containing fluorine atoms (F) exhibits an improved heat resistance. 
     Not only from the above results obtained through the above experiments but also from the results obtained through further studies, it has been recognized that a desirable poly-AlP:H(F):M semiconductor film (where M is a dopant of n-type or p-type) in which the Al and the P are evenly distributed and the composition ratio of the Al to the P satisfies the stoichiometric ratio and which contains crystal grains of a desired average size and has a desired crystal orientation can be effectively obtained by the foregoing HR-CVD method, reactive sputtering method or plasma CVD method in which the amount of hydrogen radicals present in the plasma atmosphere formed in the reaction system is properly controlled. And in the case where fluorine radicals are present together with hydrogen radicals in the plasma atmosphere, the chemical reaction causing the formation of said semiconductor film is further enhanced. Further, the presence of the hydrogen radicals in a controlled amount in the plasma atmosphere formed in the reaction system causes significant effects such as promoting the chemical reaction to cause the formation of said semiconductor film without localization of atoms of the constituent elements of the film from the raw material gases and to incorporating a desired amount of hydrogen atoms into the film to be formed so that the resulting film has practically applicable desired characteristics. This situation is improved in the case where fluorine radicals are present together with the hydrogen radicals in the plasma atmosphere formed in the reaction system. 
     It has been found that in the case of an AlP film which contains neither hydrogen atoms nor fluorine atoms or contains hydrogen atoms only in a slight amount or contains both hydrogen atoms and fluorine atoms only in slight amounts, when it is irradiated with light of a strong intensity for a long period of time, changes in the film structure or in the film composition due to promotion of by-reactions caused by external factors such as dissociation or hydrolysis of the unstable bonds in the film, in increase in the dangling bonds in the film caused by release of , hydrogen atoms and/or fluorine atoms often occurs, thereby causing deterioration in the initial film structure. However, in the case of the poly-AlP:H(F):M semiconductor film according to the present invention which contains hydrogen atoms in an amount of 0.5 to 5 atomic % and optionally fluorine atoms in an amount of 0 to 5 atomic %, it has been confirmed that these atoms terminate dangling bonds when they are present in the crystal grains and also terminate dangling bonds when they are present at the grain boundaries and thus the film is accompanied with an extremely reduced crystal defect level, excellent structural stress relaxation and excellent electrical, optical and mechanical properties. Thus, the poly AlP:H(F):M semiconductor film according to the present invention can be desirably used as a constituent element in various electronic devices including photovoltaic devices. 
     The n-type poly-AlP:H(F):Mn semiconductor film (where Mn is an n-type dopant) according to the present invention contains an n-type dopant (represented by Mn) which is selected from the group consisting of Group VI A elements i.e. O, S, Se and Te. Preferable among these elements are Se and Te. 
     The p-type poly-AlP:H(F):M p  semiconductor film (where Mp is a p-type dopant) according to the present invention contains a p-type dopant (represented by M p ) which is selected from the group consisting of Group II B elements i.e. Zn, Cd and Hg. Preferable among these elements are Zn and Cd. 
     As the starting material to impart the n-type dopant to be used in order to obtain the poly-AlP:H(F):Mn semiconductor film, there can be mentioned, for example, NO, N 2  O, CO 2 , CO, H 2  S, SCl 2 , S 2  Cl 2 , SOCl 2 , SO 2  Cl 2 , SeCl 4 , Se 2  Cl 2 , Se 2  Br 2 , SeOCl 2 , Se(CH 3 ) 2 , Se(C 2  H 5 ) 2 , TeCl 2 , Te(CH 3 ) 2  and Te(C 2  H 5 ) 2 . 
     These compound can be used alone or in combination of two or more of them. In the case where the compound is in the liquid state at ordinary temperatures and at atmospheric pressure, it is desired that the compound is gasified by feeding an inert gas such as Ar gas or He gas into the liquid compound contained in a bubbling vessel while heating and the gas generated is introduced into the film-forming chamber. In the case where the compound is in the solid state at ordinary temperatures and at atmospheric pressure, it is desired that the compound is gasified by passing an inert gas such as Ar gas or He gas over the solid compound contained in a heat sublimation furnace while heating and the gas generated is introduced into the film-forming chamber. 
     As the starting material to impart the p-type dopant to be used in order to obtain the poly-AlAslH(F):M p  semiconductor film, there can be mentioned, for example, Zn(CH 3 ) 2 , Zn(C 2  H 5 ) 2 , Zn(OCH 3 ) 2 , Zn(OC 2  H 5 ) 2 , Cd(CH 3 ) 2 , Cd(C 2  H 5 ) 2 , Cd(C 3  H 7 ) 2 , Cd(C 4  H 9 ) 2 , Hg(CH 3 ) 2 , Hg(C 2  H 5 ) 2 , Hg(C 6  H 5 ) 2  and HG[C=(C 6  H 5 )] 2 . 
     These compounds can be used alone or in combination of two or more of them. In the case where the compound is in the liquid state at ordinary temperatures and at atmospheric pressure, it is desired that the compound is gasified by feeding an inert gas such as Ar gas or He gas into the liquid compound contained in a bubbling vessel while heating and the gas generated is introduced into the film-forming chamber. 
     In the case where the compound is in the solid state at ordinary temperatures and at atmospheric pressure, it is desired that the compound is gasified by passing an inert gas such as Ar gas or He gas over the solid compound contained in a heat sublimation furnace while heating and the gas generated is introduced into the film-forming chamber. 
     Alternatively, the poly-AlP:H(F):Mn semiconductor film or the poly-AlP:H(F):Mp semiconductor film according to the present invention may be obtained by substituting part of the aluminum atoms (Al) or part of the phosphorous atoms (P) of a poly-AlP:H(F) semiconductor film by an element belonging to Group IV A of the Periodic Table. Specific examples of such element are C, Si Ge, Sn and Pb. Preferable along these elements are Si, Ge and Sn. That is, in the case where part of the aluminum [toms (Al) of the poly-AlP:H(F) semiconductor film is substituted by said element, there is afforded an n-type poly-AlP:H(F) semiconductor film. In the case where part of the phosphorous atoms (P) of the poly-AlP:H(F) semiconductor film is substituted by said element, there is afforded a p-type poly-AlP:H(F) semiconductor film. It is possible to substitute both part of the aluminum atoms and part of the phosphorous atoms by said element. In this case, when both parts are equally substituted by said element, the resulting semiconductor film sometimes becomes intrinsic. When both parts are substituted by said element, the resulting film will be of n-type or p-type depending upon which atoms are excessively substituted by said element. 
     Specific examples of starting materials to impart C are CH 4 , C 2  H 6 , C 2  H 4 , C 2  H 2 , C 2  H 8 , C 3  H 6 , C 3  H 4 , CF 4 , (CF 2 ) 5 , (CF 2 ) 6 , (CF 2 ) 4 , C 2  F 6 , C 3  F 8 , CHF 3 , CH 2  F 2 , CCl 4 , (CCl 2 ) 5 , CBr 4 , (CBr 2 ) 5 , C 2  Cl 6 , C 2  Br 6 , CHCl 3 , CH 2  Cl 2 , CHI 3 , CH 2  I 2 , C 2  Cl 3  F 3 , C 2  H 3  F 3  and C 2  H 2  F 4 . 
     Specific example of starting materials to impart Si are SiH 4 , Si 2  H 6 , Si 3  H 8 , (SiH 2 ) 4 , (SiH 2 ) 5 , (SiH 2 ) 6 , SiF 4 , (SiF 2 ) 5 , (SiF 2 ) 6 , (SiF 2 ) 4 , Si 2  F 6 , Si 3  F 8 , SiHF 3 , SiH 2  F 2 , SiCl 4 , (SiCl 2 ) 5 , SiBr 4 , (SiBr 2 ) 5 , Si 2  Cl 6 , Si 2  Br 6 , SiHCl 3 , SiH 2  Cl 2 , SiHBr 3 , SiHI 3 , Si 2  Cl 3  F 3 , Si 2  H 3  F 3 , Si 2  H 2  F 4 , Si 2  H 3  Cl 3  and Si 2  H 2  Cl 4 . 
     Specific examples of starting materials to impart Ge are GeH 4 , Ge 2  H 6 , GeF 4 , (GeF 2 ) 5 , (GeF 2 ) 6 , (GeF 2 ) 4 , Ge 2  F 6 , Ge 3  F 8 , GeHF 3 , GeH 2  F 2 , GeCl 4 , (GeCl 2 ) 5 , GeBr 4 , (GeBr 2 ) 5 , Ge 2  Cl 6 , Ge 2  Br 6 , GeHCl 3 , GeH 2  Cl 2 , GeHBr 3 , GeHI 3 , Ge 2  Cl 3  F 3 , Ge 2  H 3  F 3 , Ge 2  H 3  Cl 3 , Ge 2  H 2  F 4  and Ge 2  H 2  Cl 4 . 
     Specific examples of starting materials to impart Sn are SnH 4 , SnCl 4 , SnBr 4 , Sn(CH 3 ) 4 , Sn(C 2  H 5 ) 4 , Sn(C 3  H 7 ) 4 , Sn(C 4  H 9 ) 4 , Sn(OCH 3 ) 4 , Sn(OC 2  H 5 ) 4 , Sn(i-OC 3  H 7 ) 4  and Sn(tOC 4  H 9 ) 4 . 
     Specific examples of startoing materials to impart Pb are Pb(CH 3 ) 4 , Pb(C 2  H 5 ) 4  and Pb(C 4  H 9 ) 4 . 
     As for these compounds, a single compound is generally used. But two or more compounds can be used together where necessary. 
     In the case where the compound to be used is in the gaseous state at ordinary temperature and at atmospheric pressure, it is introduced into the activation space or the film-forming chamber while controlling its flow rate to a desired valve, for example, by means of a mass flow controller. In the case where the compound to be used is in the liquid state at ordinary temperature and at atmospheric pressure, it is desired that the liquid compound is gasified by feeding an inert gas such as Ar gas or He gas into it contained in a bubbling vessel while heating and the gas generated is introduced into the activation chamber or the film-forming chamber while controlling its flow rate to a desired value. In the case where the compound to be used is in the solid state at ordinary temperature and at atmospheric pressure, it is desired that the solid compound is gasified by passing an inert gas such as Ar gas or He gas over it contained in a heat sublimation furnace while heating and the gas generated is introduced into the activation chamber or the film-forming chamber while controlling its flow rate to a desired value. 
     As the Al-containing raw material to be used in any of the foregoing processes (1) to (3) in the present invention, there can be mentioned, for example, Al(CH 3 ) 3 , Al(C 2  H 5 ) 3 , Al(i-C 4  H 9 ) 3 , AlCl(C 2  H 5 ) 2 , Al(OC 2  H 5 )(C 2  H 5 ) 2  and AlH(i-C 4  H 9 ) 2 . 
     As for these Al-containing raw materials, they can be used alone or in combination of two or more of them. 
     In the case where the compound to be used is in the gaseous state at ordinary temperatures and at atmospheric pressure, it is introduced into the activation space or the film-forming chamber while controlling its flow rate to a desired value, for example, by means of a mass flow controller. In the case where the compound to be used is in the liquid state at ordinary temperatures and at atmospheric pressure, it is desired that the liquid compound is gasified by feeding an inert gas such as Ar gas or He gas into it contained in a bubbling vessel while heating and the gas generated is introduced into the activation chamber or the film-forming chamber while controlling its flow rate to a desired value. In the case where the compound to be used is in the solid state at ordinary temperatures and at atmospheric pressure, it is desired that the solid compound is gasified by passing an inert gas such as Ar gas or He gas over it contained in a heat sublimation furnace while heating and the gas generated is introduced into the activation chamber or the film-forming chamber while controlling its flow rate to a 
     As the P-containing raw materials to be used in the present invention, there can be mentioned, for example, PH 3 , P 2  H 4 , PF 3 , PF 5 , PCl 3 , PCl 5 , PBr 3 , PBr 5 , P(CH 3 ) 3 , P(C 2  H 5 ) 3 , P(C 3  H 7 ) 3 , P(C 4  H 9 ) 3 , P(OCH 3 ) 3 , P(OC 2  H 5 ) 3 , P(OC 3  H 7 ) 3 , P(OC 4  H 9 ) 3 , P 2  O 5 , POCl 3 , PO(OCH 3 ) 3 , PO(OC 2  H 5 ) 3 , PO(OC 3  H 7 ) 3  and PO(OC 4  H 9 ) 3 . 
     As for these P-containing raw materials, they can be used alone or in combination of two or more of them. 
     In the case where the compound to be used is in the gaseous state at ordinary temperatures and at atmospheric pressure, it is introduced into the activation space or the film-forming chamber while controlling its flow rate to a desired value, for example, by means of a mass flow controller. In the case where the compound to be used is in the liquid state at ordinary temperatures and at atmospheric pressure, it is desired that the liquid compound is gasified by feeding an inert gas such as Ar gas or He gas into it contained in a bubbling vessel while heating and the gas generated is introduced into the activation chamber or the film-forming chamber while controlling its flow rate to a desired value. In the case where the compound to be used is in the solid state at ordinary temperatures and at atmospheric pressure, it is desired that the solid compound is gasified by passing an inert gas such as Ar gas or He gas over it contained in a heat sublimation furnace while heating and the gas generated is introduced into the activation chamber or the film-forming chamber while controlling its flow rate to a desired value. 
     The substrate temperature during forming the foregoing poly-AlP:H(F):M semiconductor film (where M is a dopant of n-type or n-type) by any of the foregoing processes (1) to (3) is desired to be controlled to a temperature preferably in the range of from 50° to 600° C., more preferably in the range of from 50° to 450° C., most preferably in the range of from 100° to 400° C. 
     The inner pressure of the film-forming chamber during forming said poly-AlP:H(F):M semiconductor film by the foregoing process (1) or the foregoing process (3) is desired to be controlled to a value preferably in the range of from 1×10 -4  to 50 Torr, more preferably in the range of from 5×10 -3  to 10 Torr, most preferably in the range of from 1×10 -3  to 5 Torr. As for the inner pressure of the film-forming chamber during forming said poly-AlP:H(F):M semiconductor film by the foregoing process (2), it is desired to be controlled to a value preferably in the range of from 1×10 -5  to 1×10 -1  Torr, more preferably in the range of from 1×10 -4  to 1×10 -2  Torr. 
     In the following, explanation will be given concerning the structures of the photovoltaic elements according to the present invention. 
     When a pin heterojunction photovoltaic element is so designed that the p-type semiconductor layer made thin so as to impinge light from the side thereof can be theoretically expected that the light will be slightly absorbed in the p-type semiconductor layer but mostly absorbed in the i-type semiconductor layer to thereby obtain a desirable current. 
     However, in practice, there is a limit to how thin the p-type semiconductor layer can be not only because of the physical and electrical properties but also is commonly required to have a thickness of some tens of angstroms to some hundreds of angstroms and due consideration should be made for its band gap in order to prevent the light impinged from being absorbed by the p-type semiconductor layer. 
     In the case where the i-type semiconductor layer is formed of an a-Si:H film or a-SiC:H film which is capable of absorbing relatively short wavelength light and generating photocarriers, absorption of the light by the p-type semiconductor layer is reduced to provide a marked improvement in the current to be outputed. Because of this, it is necessary for the p-type semiconductor layer to be formed of a semiconductor film having a wide band gap. 
     In the case of a pin heterojunction photovoltaic element, when its p-type semiconductor layer or/and its n-type semiconductor layer is formed of a semiconductor film having a wide band gap, it generates a high open-circuit voltage (Voc) and exhibits a high photoelectric conversion efficiency. 
     Thus, as above described, the poly-AlP:H(F):M semiconductor film (where M is a dopant of n-type or p-type) according to the present invention is indeed a desirable semiconductor film of p-type or n-type which can be effectively used as the p-type semiconductor layer or n-type layer of the pin heterojunction photovoltaic element since said semiconductor film contains aluminum atoms (Al) and phosphorous atoms (P) uniformly distributed while satisfying the stoichiometric ratio, hydrogen atoms (H) in a specific amount and optionally fluorine atoms (F) in a specific amount, further contains crystal grains of a desired average size, has a desired crystal orientation, is accompanied with very few defects, has a desirably wide band gap and exhibits markedly improved characteristics and thus, it surpasses the known AlP semiconductor film. 
     What has been stated above for the p-type semiconductor layer through which light is impinged is applicable in the case where light is impinged from the side of the n-type semiconductor layer. Further, in the case of a multi-cell stacked tandem type or triple type pin heterojunction photovoltaic elements each cell comprising a pin heterojunction photovoltaic element, when the p-type or n-type semiconductor layer of the cell situated on the side from which light is impinged is formed of the foregoing poly-AlP:H(F):M film, marked effects are also provided. 
     In addition, the poly-AlP:H(F):M semiconductor film according to the present invention is capable of also absorbing relatively long wavelength light. Because of this, even in the case where the i-type semiconductor layer is formed of a-SiGe:H film or uC-Si:H film having a narrow band gap which makes it possible to obtain a large photocurrent, as long as the p-type semiconductor layer through which light is impinged is formed of the poly-AlP:H(F):Mp semiconductor film having a wide band gap (where Mp is a p-type dopant) according to the present invention, there is desirably caused a so-called backsurface field effect due to a gap of the conduction band between the p-type semiconductor layer and the i-type semiconductor layer to thereby present electrons generated in the i-type semiconductor layer from being back-diffused at the interface between the p-type semiconductor layer and the i-type semiconductor layer, thereby providing a significant improvement in the photocurrent to be obtained. 
     Thus, for the pin heterojunction photovoltaic element, a large photocurrent is afforded and a markedly improved photoelectric conversion efficiency is provided. In fact, the pin heterojunction photovoltaic element according to the present invention stably provides an excellent photoelectric conversion efficiency not only for a light, source having a relatively large quantity of short wavelength components such as a fluorescent lamp but also for a light source having a large quantity of long wavelength components such as an incandescent lamp. In view of this, the pin heterojunction photovoltaic element according to the present invention can be desirably used also as a power source in various electric applicants 
     Further, the tandem type pin heterojunction photovoltaic element and the triple type pin heterojunction photovoltaic element according to the present invention provide excellent photelectric conversion efficiency, excellent durability and stably exhibit their functions without being deteriorated even upon repeated use for a long period of time and they can be desirably used as solar cells in power supply systems by sunlight power generation. 
     The following describes typical examples of the pin heterojunction photovoltaic element to be provided according to the present invention. 
     The following description, however, is not intended to limit the scope of the present invention. 
     FIG. 1(A) and FIG. 1(B) schematically show typical embodiments of the pin heterojunction photovoltaic element according to the present invention which has a layer structure based on the foregoing poly-AlP:H(F):M semiconductor film. 
     FIG. 1(A) is a schematic cross-sectional view of a first representative embodiment of the pin heterojunction photovoltaic element according to the present invention. In FIG. 1(A), there is shown a pin heterojunction photovoltaic element 100 having a structure comprising a lower electrode 102, an n-type semiconductor layer 103, an i-type semiconductor layer 104, a p-type semiconductor layer 105, a transparent electrode 106 and a collecting electrode 107 disposed in this order on a substrate 101. 
     In the pin heterojunction photovoltaic element shown in FIG. 1(A), light is impinged from the side of the transparent electrode 106. 
     FIG. 1(B) is a schematic cross-sectional view of a second representative embodiment of the pin heterojunction photovoltaic element according to the present invention. 
     In FIG. 1(B), there is shown a pin heterojunction photovoltaic element 100 comprising a transparent electrode 106, a p-type semiconductor layer 105, an i-type semiconductor layer 104, an n-type semiconductor layer 103 and a lower electrode 102 disposed in this order on a transmissive substrate 101. In the pin heterojunction photovoltaic element shown in FIG. 1(B), light is impinged from the side of the transmissive substrate 101. 
     For each of the above pin heterojunction photovoltaic elements shown in FIG. 1(A) and FIG. 1(B). it is possible to transpose each of the n-type semiconductor layer and the p-type semiconductor layer in accordance with the desired use requirements. 
     FIG. 1(C) is a schematic cross-sectional view of a representative embodiment of the triple cell tandem stacked type pin heterojunction photovoltaic element 120 according to the present invention which comprises three cells 111, 112 and 113 stacked on a lower electrode 102 disposed on a substrate 101, each cell comprising a pin heterojunction photovoltaic element. 
     The lower cell 111 comprises an n-type semiconductor layer 103, an i-type semiconductor layer 104 and a p-type semiconductor layer 105 which are laminated in this order from the side of the substrate 101. The middle cell 112 comprises an n-type semiconductor layer 114, an i-type semiconductor layer 115 and a p-type semiconductor layer 116 which are laminated in this order from the side of the substrate 101. 
     The top cell 113 comprises an n-type semiconductor layer 117, an i-type semiconductor layer 118 and a p-type semiconductor layer 119 which are laminated in this order from the side of the substrate 101. 
     Reference numeral 106 stands for a transparent electrode disposed on the p-type semiconductor layer 119 of the top cell 113. On the transparent electrode 106, there is provided a collecting electrode 107. 
     In the triple cell tandem stacked type pin heterojunction photovoltaic element 120 shown in FIG. 1(C), light is impinged from the side of the transparent electrode 106. 
     For this pin heterojunction photovoltaic element, it is also possible to transpose the n-type semiconductor layer and the p-type semiconductor layer in accordance with the desired use requirements. 
     Explanation will be made for the substrate, each constituent semiconductor layer and each constituent electrode in the pin heterojunction photovoltaic element of the present invention. 
     Substrate 
     The substrate 101 used in the pin heterojunction photovoltaic element according to the present invention may be of single crystal material or non-single crystal material. It may be electroconductive or electrically insulating, and it may be transparent or opaque. Usable as such substrate are, for example, Fe, Ni, Cr, Al, Mo, Au, Nb, Ta, V, Ti, Pt, and Pb and alloys thereof such as brass and stainless steel. Other than these there can be mentioned films or sheets of synthetic resin such as polyester, polyethylene, polycarbonate, cellulose acetate, polypropylene, polyvinyl chloride, polyvinylidene chloride, polystyrene, polyamide, polyimide and the like, and glass or ceramics. 
     Examples of the substrate comprising a single crystal material are, for example, wafer-like shaped members obtained by slicing an appropriate single crystal of Si, Ge, C, NaCl, KCl, LiF, GaSb, InAs, InSb, GaP, MgO, CaF 2 , BaF 2 , α-Al 2  O 3  or the like. The surface of any of said wafer-like shaped members may be provided with an epitaxially grown layer of the same constituent(s) as the member or of a material whose lattice constant is close to that of the constituent(s) of the member. 
     The shape of the substrate may be optionally determined in accordance with the end use purpose. Examples are plate, belt, drum and suitable like shapes having a plane or uneven surface. The thickness of the substrate is properly determined so that the layer structure of the photovoltaic member can be formed as desired. In the case where flexibility is required for the photovoltaic element to be prepared, it can be made as thin as possible within a range capable of sufficiently providing the functions as the substrate. However, the thickness of the substrate is usually not less than 10 microns from the view points of its manufacturing and handling conveniences and its strength. 
     Electrodes 
     In the photovoltaic element according to the present invention, appropriate electrodes are used in accordance with the configuration of the photovoltaic element to be prepared. As such electrodes, there can be mentioned the lower electrode, upper electrode (transparent electrode) and collecting electrode. Said upper electrode denotes the one to be placed at the side on which light is impinged, and said lower electrode denotes the one to be placed opposite to the upper electrode through the semiconductor layers to be arranged between the two electrodes. 
     These electrodes will be explained in the following. 
     (i) Lower electrode 
     For the pin heterojunction photovoltaic element according to the present invention, the side through which light is impinged is determined depending upon whether there is used a transmissive member or an opaque member as the substrate 101. 
     In this connection, the position where the lower electrode 102 is to be placed is properly determined by the kind the substrate 101 to be used. For example, in the case where an opaque member such as a metal member is used as the substrate 101, light for the generation of a photoelectromotive force is impinged from the side of the transparent electrode 106. 
     Now, in the case where the pin heterojunction photovoltaic element is of the configuration as shown in FIG. 1(A) or FIG. 1(C), the lower electrode 102 is desired to be placed between the substrate 101 and the n-type semiconductor layer 103. In this case, if the substrate 101 comprises an electroconductive member, it can function also as the lower electrode. However, in the case where the substrate 101 is electroconductive but is of a high sheet resistance, the lower electrode may be disposed as a lower resistance electrode serving to output the current or in order to heighten the reflectivity of the incident light at the surface of the substrate 101 so as to make it utilized more efficiently. 
     In the case of FIG. 1(B), there is used a transmissive member as the substrate 101 and light is impinged from the side of the substrate 101. In this connection, the lower electrode 102 serving to output a current is placed on the surface of the top semiconductor layer over the substrate 101. However, in the case where there is used an electrically insulating member as the substrate 101 as in the case of 1(B), the lower electrode 102 serving to output the current is placed between the substrate 101 and the n-type semiconductor layer 103. 
     The electrode 102 may be a thin film of a metal selected from the group consisting of Ag, Au, Pt, Ni, Cr, Cu, Al, Ti, Zn, Mo and W. Said metallic thin film may be formed by way of the known vacuum deposition technique, electron-beam deposition technique or sputtering technique. However, due consideration should by given that the metallic thin film to be thus formed is not a resistive component for the photovoltaic element. In this respect, the metallic thin film constituting the electrode 102 preferably has a sheet resistance of 50 Ω or less, more preferably, 10 Ω or less. 
     In the alternative, it is possible to place a diffusion preventive layer comprising an electroconductive material such as zinc oxide between the lower electrode 102 and the n-type semiconductor layer 103. (This is not shown in the figures). 
     In the case where such diffusion preventive layer is used as mentioned above, the following advantages will be expected: (a) it prevents the metal elements constituting the electrode 102 from diffusing into the n-type semiconductor layer 103; (b) being provided with a certain resistance value, it prevents the occurrence of shorts, which would otherwise occur between the lower electrode 102 and the transparent electrode 106 through the semiconductor layers arranged between them due to pinholes and the like; and (c) it serves to generate multiple interference effects with the thin film and confine the impinged light within the photovoltaic element. 
     (ii) Upper electrode (transparent electrode) 
     The transparent electrode 106 is desired to have a light transmittance of more than 85% so that it serves to make the semiconductor layer efficiently absorb sunlight or fluorescent light. In addition to this, it is desired to have a sheet resistance of 100 Ω or less from the viewpoint of preventing the internal resistance of the photovoltaic element from becoming great thereby impairing the performance. 
     In view of the above, the transparent electrode 106 is desired to comprise a thin film of a metal oxide selected from the group consisting of SnO 2 , In 2  O 3 , ZnO, CdO, Cd 2  SnO 2  and ITO (In 2  O 3  +SnO 2 ) or a semitransparent thin film of a metal selected from the group consisting of Au, Al and Cu. 
     The transparent electrode 106 is disposed on the p type semiconductor layer in the case of the photovoltaic element shown in FIG. 1(A) or FIG. 1(C), and it is disposed on the substrate 101 in the case of the photovoltaic element shown in FIG. 1(B). 
     In any of these cases, it is necessary to constitute the transparent electrode 106 with a thin film member selected from the foregoing which is good in adhesion with the layer or the substrate. 
     The transparent electrode 106 comprising such thin film may be formed by way of the known resistance heating deposition technique, electron beam heating deposition technique, reactive sputtering technique or spraying technique. 
     (iii) Collecting electrode 
     The collecting electrode 107 in the photovoltaic element according to the present invention is disposed on the transparent electrode 106 for the purpose of reducing the surface resistance of said transparent electrode. 
     The collecting electrode 107 is desired to comprise a metallic thin film of Ag, Cr, Ni, Al, Au, Ti, Pt, Cu, Mo, W or an alloy of these metals. It is possible for the collecting electrode 107 to be constituted with a member comprising a stacked plurality of such metallic thin films. 
     The shape and the area of the collecting electrode 107 are properly designed so that a sufficient quantity of light can be received by the semiconductor layer. 
     Specifically as for the shape, it is desired to be such that it extends uniformly all over the light receiving face of the photovoltaic element. As for the area, it is desired to cover 15% or less of said light receiving face in a preferred embodiment or 10% or less in a more preferred embodiment. 
     The member constituting the collecting electrode 107 preferably has a sheet resistance of 50 Ω or less, more preferably, 10 Ω or less. 
     i-type semiconductor layer 
     In a preferred embodiment, the i-type semiconductor layer in any of the pin heterojunction photovoltaic elements shown in FIGS. 1(A) to 1(C) according to the present invention is formed of an i-type semiconductor film selected from the group consisting of a-Si:H film, a-Si:F film, a-Si:H:F film, a-SiC:H film, a-SiC:F film, a-siC:H:F film, a-SiGe:H film, a-SiGe:F film, a-SiGe:H:F film, poly-Si:H film, poly-Si:F film and poly-Si:H:F film. 
     The pin heterojunction photovoltaic element according present invention is based on the combined use of this i-type semiconductor layer and the p-type or/and n-type semiconductor layer formed of the foregoing poly-AlP:H(F):M semiconductor film and because of this, it provides the foregoing various significant effects. 
     This situation will be made further apparent from the results obtained through the following experiment. 
     Experiment D 
     There were prepared nineteen pin heterojunction photovoltaic element samples (Samples Nos. 91 to 109) of the configuration shown in FIG. 1(B) by using the foregoing i-type semiconductor films to form their i-type or n-type semiconductor layers, the known p-type AlAs semiconductor film to form their p-type semiconductor layers and the foregoing poly-AlP:H(F):M semiconductor films according to the present invention to form their p-type and/or n-type semiconductor layers. 
     In each of the pin heterojunction photovoltaic element samples Nos. 91 to 109, as the substrate 101 there was used a quartz glass plate. As the transparent electrode 106, there was formed a ITO thin film on the substrate 101 by means of a conventional reactive sputtering deposition technique. As the electrode 102, there was used a Ag thin film formed by a conventional electron-beam deposition technique. 
     Each of the pin heterojunction photovoltaic element samples Nos. 91 to 109 was made such that light is impinged from the side of the substrate 101. 
     In the case of the pin heterojunction photovoltaic element sample having the p-type semiconductor layer comprised of the foregoing poly-AlP:H(F):Mp semiconductor film according to the present invention, said p-type semiconductor layer was formed by repeating the foregoing procedures for preparing the film sample No. 76 (by the reactive sputtering method). 
     Likewise, in the case of the pin heterojunction photovoltaic element sample having the n-type semiconductor layer comprised of the foregoing poly-AlP:H(F):Mn semiconductor film according to the present invention, said n-type semiconductor layer was formed by repeating the foregoing procedures for preparing the film sample No. 36 (by the HR-CVD method). 
     The known i-type semiconductor film, n-type semiconductor film, or p-type semiconductor film in any of the pin heterojunction photovoltaic elements was formed in the known manner. 
     In the case of the pin heterojunction photovoltaic element sample having the p-type semiconductor layer comprised of a known p-type AlP semiconductor film, said p-type semiconductor layer was formed by a conventional sputtering deposition method. 
     The layer constitution of each of the pin heterojunction photovoltaic element samples Nos. 91 to 109 prepared was shown in Table 8. 
     For each of the pin heterojunction photovoltaic element samples Nos. 91 to 109 thus obtained, there were evaluated a short-circuit current (Isc) under irradiation of AM-1 light (100 mW/cm 2 ) and an open-circuit voltage (Voc). 
     The results obtained are collectively shown in Table 8. 
     From the results obtained through the experiment, the following findings have been obtained. That is, it has been found that in each of the cases (Samples Nos. 91-93 and 97-99) where the n-type and i-type layers are formed of the same kind of a semiconductor film and the p-type layer is formed of the poly-AlP:H(F):Mp semiconductor film according to the present invention, the Isc and the Voc exhibited surpass those exhibited by any of the pin heterojunction photovoltaic elements (Samples Nos. 104-109) in which the p-type semiconductor layer is formed of the known p-type AlP semiconductor film, and the n-type and i-type semiconductor layers are formed of those silicon-containing non-single crystal semiconductor films used in Samples Nos. 91-99. It has been also found that in any of the cases (Samples Nos. 94-96) where the p-type and n-type semiconductor layers are formed of the poly-AlP:H(F):M semiconductor film according to the present invention and the i-type semiconductor layer is formed of a a-Si:H film, a-Si:F film or a-Si:H:F film, the Voc is markedly improved. 
     On the other hand, in any of the cases (Samples Nos. 100-103) where the p-type semiconductor layer is formed of the poly-AlP:H(F):Mp semiconductor film, the n-type semiconductor layer is formed of an n-type a-Si:H film, and the i-type semiconductor layer is formed of an a-Si film, a-SiC film, a-SiGe film or poly-Si film, it has been found that there are not provided desirable Isc and Voc and thus, each of them is not practically acceptable. 
     In view of the above, it has been recognized that for the pin heterojunction photovoltaic element according to the present invention, it is necessary for the i-type semiconductor layer to be formed of a silicon-containing semiconductor film containing hydrogen atoms (H) or/and fluorine atoms (F) selected from the group consisting of a-Si:H film, a-Si:F film, a-Si:H:F film, a-SiC:H film, a-SiC:F film, a-SiC:H:F film, a-SiGe:H film, a-SiGe:F film, a-SiGe:H:F film, poly-Si:H film, poly-Si:F film and poly-Si:H:F film. 
     In order to form a desirable pin heterojunction in the preparation of the pin heterojunction photovoltaic element according to the present invention, it is desired to continuously form the n-type semiconductor layer, the i-type semiconductor layer and the p-type semiconductor layer under an enclosed vacuum condition. In a preferred embodiment in this respect, the formation of said pin heterojunction is carried out in a single film-forming apparatus. In the alternative, it is possible to form one semiconductor layer in a film-forming apparatus, to transfer the substrate having the semiconductor layer formed thereon through a gate valve into an other film forming apparatus and to form a successive semiconductor layer on the previously formed semiconductor layer therein. 
     DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     The present invention will be described more specifically while referring to Examples, but the present invention is not intended to limit the scope only to these examples. 
     EXAMPLE 1 
     There was prepared a pin heterojunction photovoltaic element of the configuration shown in FIG. 1(A) by the foregoing process (1) (HR-CVD method) practiced in the HR-CVD apparatus shown in FIG. 2 in the following way. 
     As the substrate 101, there was used a stainless steel plate of 50 mm by 50 mm in size. 
     Firstly, the substrate was placed in a known sputtering apparatus (not shown). The sputtering apparatus was evacuated to a vacuum of about 1×10 -5  Torr or below. On the substrate was deposited a Ag thin film of about 1000 Å in thickness as the lower electrode 102 by sputtering Ag in Ar gas. The substrate was taken out from the sputtering apparatus and then fixed, with the lower electrode 102 facing downward, onto the substrate holder 202 on the substrate transfer unit 206 positioned in the load lock chamber 212. The load lock chamber 212 was evacuated to 10 -5  Torr or below by means of a vacuum pump (not shown). During evacuation, the film-forming chamber 201 was evacuated to 10 -5  Torr or below by means of the vacuum pump 221. When the pressures in the two chambers became almost balanced, the two chambers were opened and the substrate transfer unit 206 was moved through the gate valve 207 to the film forming chamber 201. Then, the gate valve 207 was closed. The substrate (203 in FIG. 2) was heated to 220°  C. by actuating the heater 205 and it was maintained at this temperature. Thereafter, Si 2  F 6  gas and PH 3  gas diluted with SiF 4  gas to 3500 ppm (hereinafter referred to as &#34;PH 3  /SiF 4  gas&#34;) were introduced through the gas supply pipe 214 into the activation chamber 208 maintained at 700° C. by the activation energy generation means 211 at respective flow rates of 25 sccm and 12 sccm while being mixed. At the same time, He gas and H 2  gas were introduced through the gas supply pipe 215 into the activation chamber 209 at respective flow rates of 100 sccm and 55 sccm while being mixed. The inner pressure of the film-forming chamber 201 was kept at 0.3 Torr by regulating the exhaust valve 220. Film-forming was started by applying microwave power (2.45 GHz) of 300W from the activation energy generation means 212 into the activation chamber 209. Precursors generated in the activation chamber 208 and hydrogen radicals generated in the activation chamber 209 were successively transported respectively through the transport conduits 217 and 218 into the film-forming chamber 201, where they were chemically reacted to form a 400 Å thick n-type a-Si:H:F:P semiconductor film as the n-type semiconductor layer 103 on the Ag thin film as the lower electrode 102. The application of microwave power and the introduction of gases were suspended, and the film-forming chamber 201 was evacuated to 10 -5  Torr or below by the vacuum pump. 
     Then, the substrate (203) was moved through the gate valve 207 into the film-forming chamber 222 having the same constitution as that of the film-forming chamber 201 which had been evacuated to 10 -5  Torr or below by means of the substrate transfer unit 206. Then, the above film-forming procedures were repeated, except that only Si 2  F 6  gas was introduced at a flow rate of 30 sccm without using the PH 3  /SiF 4  gas and the microwave power was changed to 400W, to thereby form a 3500 Å thick non-doped a-Si:H:F film as the i-type semiconductor layer 104 on the previously formed n-type semiconductor layer 103. 
     The application of microwave power and the introduction of gases were suspended, and the film-forming chamber 222 was evacuated to 10 -5  Torr or below. Then, the substrate (203) was moved through the gate valve into a film-forming chamber (not shown) have the same constitution as that of the film-forming chamber 201 which had been evacuated to 10 -5  Torr or below. 
     Then a liquid mixture composed of Al(C 2  H 5 ) 3  and Zn(CH 3 ) 2  with the quantitative ratio of 10 4  :1 in a bubbling vessel (not shown) was gasified by bubbling it with He gas (as a carrier gas) supplied at a flow rate of 20 sccm to generate a raw material gas containing said two compounds. The resultant raw material gas was successively introduced through the gas supply pipe 214 into the activation chamber 208 at a flow rate of 2.7×10 -4  mol/min, into which microwave power (2.45 GHz) of 60W from the activation energy generation means 211 was applied. At the same time, PF 5  gas was introduced at a flow rate of 5 sccm through the gas supply pipe 216 into the activation chamber 210 maintained at 500° C. by the activation energy generation means 213. Concurrently, H 2  gas and He gas were introduced through the gas supply pipe 215 into the activation chamber 209 at respective flow rates of 15 sccm and 40 sccm while being mixed, into which microwave power (2.45 GHz) of 300W from the activation energy generation means 212 was applied. At this time, the inner pressure of the film-forming chamber was controlled to 60 m Torr. Precursors generated in the activation chamber 208, other precursors generated in the activation chamber 210 and hydrogen radicals generated in the activation chamber 209 were successively introduced into the film-forming chamber respectively through the transport conduits 217, 219 and 218, where they were chemically reacted to form a 200 Å thick p-type poly-AlP:H:F:Zn semiconductor film as the p-type semiconductor layer 105 on the previously formed i-type semiconductor layer on the substrate maintained at 210° C., the substrate being placed at a position 8 cm distant from the outlet of the transport conduit 218. 
     Thereafter, the substrate transfer unit was moved to the load lock chamber through the gate valve. After cooling therein, the substrate on which were deposited the n-type, i-type and p-type semiconductor layers was taken out. Then, the substrate was placed in a known vacuum deposition apparatus, which was evacuated to 10 -5  Torr or below. On the foregoing p-type semiconductor layer 105 on the substrate was deposited an ITO thin film of about 700 Å in thickness in an oxygen atmosphere at about 1×10 -3  Torr. The source of deposition was a 1:1 (by weight) mixture of In and Sn placed in a crucible which was heated by the resistance heating method. The substrate temperature was 170° C. In this way the transparent electrode 106 was formed. After cooling, the substrate was removed. With a permalloy mask placed on the transparent electrode 106, the substrate was placed in another known vacuum deposition apparatus, which was evacuated to 1×10 -5  Torr or below. A Ag thin film of about 0.8 μm in thickness was deposited by the resistance heating method to form an about 0.8 μm thick comb-shaped collecting electrode 107. Thus there was obtained Element Sample No. 1. The characteristics of Element Sample No. 1 as a solar cell were evaluated in the following manner. 
     The open-circuit voltage (Voc) and the short-circuit current (Isc) which are produced when the transparent electrode is irradiated with AM-1 light (100 mW/cm 2 ) were measured. The relative value of output obtained when AM-1 light is irradiated through an interference filter of 400 nm was also measured. Said relative value is a value obtained when the value obtained when the comparative element sample prepared in the later described Comparative Example 1 was measured under the same conditions as in the above was made to be the control (1). 
     The measured results were shown in Table 9. 
     Besides the foregoing, using a quartz glass plate, there was formed a p-type poly-AlP:H:F:Zn semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the p-type semiconductor layer 105. 
     The resultant film was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 9. 
     EXAMPLE 2 
     There was prepared a pin heterojunction photovoltaic element (Element Sample No. 2) of the configuration shown in FIG. 1(A) by repeating the procedures of Example 1, except that the p-type semiconductor layer 105 was formed by the foregoing process (2)(reactive sputtering method) practiced in the reactive sputtering apparatus shown in FIG. 3 in the following manner. 
     That is, the substrate having the lower electrode 102, the n-type semiconductor layer 103 and the i-type semiconductor layer 104 thereon which were formed respectively in the same manner as in Example 1 was moved by the substrate transfer unit into the other film-forming chamber comprising the reactive sputtering film-forming chamber 301 shown in FIG. 3. The film-forming chamber 301 was evacuated to 1×10 -5  Torr or below. The substrate was heated to 220° C. by actuating the heater 305 and it was maintained at this temperature. Film-forming was conducted under the conditions shown in Table 10 to thereby form a 200 Å thick p-type poly-AlP:H:F:Zn semiconductor film as the p-type semiconductor layer 105 on the previously formed i-type semiconductor layer 104. Thereafter, the substrate was moved to the load lock chamber and it was cooled therein. 
     The substrate was taken out therefrom, and on the foregoing p-type semiconductor layer 105 was formed an about 700 Å thick ITO film as the transparent electrode 106 and then an about 0.8 μm thick comb-shaped collecting electrode 107 comprising an 0.8 μm thick Ag thin film in the same manner as in Example 1. 
     Thus there was obtained Element Sample No. 2. 
     The characteristics of Element Sample No. 2 as a solar cell were evaluated in the same manner as in Example 1. 
     The results obtained are shown in Table 9. 
     Besides the foregoing, using a quartz glass plate, there was formed a p-type poly-AlP:H:F:Zn semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the p-type semiconductor layer 105. 
     The resultant film was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 9. 
     EXAMPLE 3 
     There was prepared a pin heterojunction photovoltaic element of the configuration shown in FIG. 1(A) (Element Sample No. 3) by repeating the procedures of Example 1, except that the p-type semiconductor layer 105 was formed by the foregoing process (3) (plasma CVD method) practiced in the plasma CVD apparatus shown in FIG. 4 in the following manner. 
     That is, the substrate having the lower electrode 102, the n-type semiconductor layer 103 and the i-type semiconductor layer 104 thereon which were formed respectively in the same manner as in Example 1 was moved by the substrate transfer unit into the other film-forming chamber comprising the plasma CVD film-forming chamber 401 shown in FIG. 4. The film-forming chamber 401 was evacuated to 1×10 -5  or below. The substrate was heated to 230° C. by the heater 405 and it was maintained at this temperature. Then, raw material gas (A), raw material gas (B) and raw material gas (C) shown in Table 11 were introduced through the respective gas supply pipes 408 and 409 into the film-forming chamber 401 under the respective conditions shown in Table 11. The inner pressure of the film-forming chamber 401 was controlled to and maintained at 0.8 Torr by regulating the exhaust valve 414 and while monitoring by the pressure gage 417. High frequency power (13.56 MHz) of 70W from the high frequency power source 410 was applied through the cathode 412 into the film-forming chamber 401 to thereby form a 200 Å thick p-type poly-AlP:H:F:Zn semiconductor film as the p-type semiconductor layer 105 on the previously formed i-type semiconductor layer. Thereafter, the substrate transfer unit was moved to the load lock chamber and it was cooled therein. 
     The substrate was taken out therefrom, and on the foregoing p-type semiconductor layer 105 was formed an about 700 Å ITO film as the transparent electrode 106 and then an about 0.8 μm thick comb-shaped collecting electrode 107 comprising an 0.8 μm thick Ag thin film in the same manner as in Example 1. 
     Thus there was obtained Element Sample No. 3. 
     The characteristics of Element Sample No. 3 as a solar cell were evaluated in the same manner as in Example 1. The results obtained are shown in Table 9. 
     Besides the foregoing, using a quartz glass plate, there was formed a p-type poly-AlP:H:F:Zn semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the p-type semiconductor layer 105. 
     The resultant film was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The results are were shown in Table 9. 
     EXAMPLE 4 
     There was prepared a pin heterojunction photovoltaic element of the configuration shown in FIG. 1(A) (Element Sample No. 4) by repeating the procedures of Example 1, except that the i-type semiconductor layer 104 was formed of a non-doped i-type a-SiC:H:F film which was prepared in the following manner. 
     That is, after the n-type semiconductor layer 103 was formed, the substrate was moved by the substrate transfer unit through the gate valve to the other film-forming chamber having the same constitution as that of the film forming chamber 201. 
     The gate valve was closed and the film-forming chamber was evacuated to and maintained at 1×10 -5  Torr or below. The substrate was then heated to 220° C. by actuating the heater 205 and it was maintained at this temperature. Thereafter, raw material gas (A), raw material gas (B) and raw material gas (C) shown in Table 12 were introduced into the respective activation chambers 208, 209 and 210, wherein they were separately activated under the respective activation conditions shown in Table 12 to generate respective active species. The respective active species were separately introduced through the respective transport conduits 217, 218 and 219 into the film-forming chamber, wherein they were chemically reacted to form a 3500 Å thick non-doped i-type a-SiC:H:F film as the i-type semiconductor layer 104 on the previously formed n-type semiconductor layer 103 comprising a 400 Å thick n-type a-Si:H:F:P semiconductor film. 
     On the thus formed i-type semiconductor layer 104 was formed a 200 Å thick p-type poly-AlP:H:F:Zn semiconductor film as the p-type semiconductor layer 105 in the same manner as in Example 1. Thereafter, the substrate transfer unit was moved to the load lock chamber and it was cooled therein. 
     The substrate was taken out therefrom, and on the foregoing p-type semiconductor layer 105 was formed an about 700 Å thick ITO film as the transparent electrode 106 and then an about 0.8 μm thick comb-shaped collecting electrode 107 comprising an 0.8 μm thick Ag thin film in the same manner as in Example 1. 
     Thus there was obtained Element Sample No. 4. 
     The characteristics of Element Sample No. 4 as a solar cell were evaluated in the same manner as in Example 1. The results obtained are shown in Table 9. 
     Besides the foregoing, using a quartz glass plate, there was formed a p-type poly-AlP:H:F:Zn semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the p-type semiconductor layer 105. 
     The resultant film was examined for the hydrogen content, the fluorine content and the average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 9. 
     EXAMPLE 5 
     There was prepared a pin heterojunction photovoltaic element of the configuration shown in FIG. 1(A) (Element Sample No. 5) by repeating the procedures of Example 1, except that the i-type semiconductor layer 104 was formed of a non-doped i-type a-SiGe:H:F film which was prepared in the following manner. 
     That is, after the n-type semiconductor layer 103 was formed, the substrate was moved by the substrate transfer unit through the gate valve to the other film-forming chamber having the same constitution as that of the film-forming chamber 201. 
     The gate valve was closed and the film-forming chamber was evacuated to and maintained at 1×10 -5  Torr or below. The substrate was then heated to 220° C. by actuating the heater 205 and it was maintained at this temperature. Thereafter, raw material gas (A), raw material gas (B) and raw material gas (C) shown in Table 13 were introduced into the respective activation chambers 208, 209 and 210, wherein they were separately activated under the respective activation conditions shown in Table 13 to generate respective active species. The respective active species were separately introduced through the respective transport conduits 217, 218 and 219 into the film-forming chamber, wherein they were chemically reacted to form a 3500 Å thick non-doped i-type a-SiGe:H:F film as the i-type semiconductor layer 104 on the previously formed n-type semiconductor layer 103 comprising a 400 Å thick n-type a-Si:H:F:P semiconductor film. 
     On the thus formed i-type semiconductor layer 104 was formed a 200 Å thick p-type poly-AlP:H:F:Zn semiconductor film as the p-type semiconductor layer 105 in the same manner as in Example 1. Thereafter, the substrate transfer unit was moved to the load lock chamber and it was cooled therein. 
     The substrate was taken out therefrom, and on the foregoing p-type semiconductor layer 105 was formed at about 700 Å thick ITO film as the transparent electrode 106 and then at about 0.8 μm thick comb-shaped collecting electrode 107 comprising a 0.8 μm thick Ag thin film in the same manner as in Example 1. 
     Thus there was obtained Element Sample No. 5. 
     The characteristics of Element Sample No. 5 as a solar cell were evaluated in the same manner as in Example 1. The results obtained are shown in Table 9. 
     Besides the foregoing using a quartz glass plate there was formed a p-type poly-AlP:H:F:Zn semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the p-type semiconductor layer 105. 
     The resultant film was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 9. 
     EXAMPLE 6 
     There was prepared a pin heterojunction photovoltaic element of the configuration shown in FIG. 1(A) (Element Sample No. 6) by repeating the procedures of Example 1, except that the i-type semiconductor layer 104 was formed of a non-doped i-type poly-Si:H:F film which was prepared in the following manner. 
     That is, after the n-type semiconductor layer 103 was formed, the substrate was moved by the substrate transfer unit through the gate valve to the other film-forming chamber having the same constitution as that of the film-forming chamber 201. 
     The gate valve was closed and the film-forming chamber was evacuated to and maintained at 1×10 -5  Torr or below. The substrate was then heated to 220° C. by actuating the heater 205 and it was maintained at this temperature. 
     Thereafter, raw material gas (A) and raw material gas (B) shown in Table 14 were introduced into the respective activation chambers 208 and 209, wherein they were separately activated under the respective activation conditions shown in Table 14 to generate respective active species. The respective active species were separately introduced through the respective transport conduits 217 and 218 into the film-forming chamber, wherein they were chemically reacted to form a 8000 Å thick non-doped i-type poly-Si:H:F film as the i-type semiconductor layer 104 on the previously formed n-type semiconductor layer comprising a 400 Å thick n-type a-Si:H:F:P semiconductor film. 
     On the thus formed i-type semiconductor layer 104 was formed a 200 Å thick p-type poly-AlP:H:F:Zn semiconductor film as the p type semiconductor layer 105 in the same manner as in Example 1. Thereafter, the substrate transfer unit was moved to the load lock chamber and it was cooled therein. 
     The substrate was taken out therefrom, and on the foregoing p-type semiconductor layer 105 was formed at about 700 Å thick ITO film as the transparent electrode 106 and then at about 0.8 μm thick comb-shaped collecting electrode 107 comprising an 0.8 μm thick Ag thin film in the same manner as in Example 1. 
     Thus there was obtained Element Sample No. 6. 
     The characteristics of Element Sample No. 6 as a solar cell were evaluated in the same manner as in Example 1. The results obtained are shown in Table 9. 
     Besides the foregoing, using a quartz glass plate, there was formed a p-type poly-AlP:H:F:Zn semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the p-type semiconductor layer 105. 
     The resultant film was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 9. 
     EXAMPLE 7 
     There was prepared a pin heterojunction photovoltaic element of the configuration shown in FIG. 1(B) (Element Sample No. 7) in accordance with the manner of Example 1. 
     That is, as the substrate 101, there was used a Corning glass plate No. 7059 of 50 mm by 50 mm in size. On the substrate was formed at ITO thin film of about 500 Å in thickness as the transparent electrode 106 by the resistance heating method. The procedures of forming the p-type semiconductor layer in Example 1 were repeated to form a 200 Å thick p-type poly-AlP:H:F:Zn semiconductor film as the p-type semiconductor layer 105 on the transparent electrode. Then, the procedures for forming the i-type semiconductor layer in Example 1 were repeated to form a 3500 Å thick non-doped i-type a-Si:H:F film as the i-type semiconductor layer 104 on the p-type semiconductor layer. Successively, there was formed a 400 Å thick n-type a-Si:H:F:P semiconductor film as the n-type semiconductor layer 103 on the i type semiconductor layer 104 by repeating the procedures of forming the n-type semiconductor layer in Example 1. On this n-type semiconductor was formed a 0.5 μm thick Ag film as the electrode 102 by repeating the procedures of forming the comb-shaped collecting electrode in Example 1. Thus there was obtained Element Sample No. 7. The characteristics of Element Sample No. 7 as a solar cell were evaluated in the same manner as in Example 1. 
     The results obtained are shown in Table 9. 
     Besides the foregoing, using a quartz glass plate, there was formed a p-type poly-AlP:H:F:Zn semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the p-type semiconductor layer 105. 
     The resultant film was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 9. 
     EXAMPLE 8 
     There was prepared a pin heterojunction photovoltaic element of the configuration shown in FIG. 1(A) (Element Sample No. 8) by repeating the procedures of Example 1, except that the n-type semiconductor layer 104 was formed of an n-type poly-AlAs:H:F:Se semiconductor film which was prepared in the following manner. 
     That is, after the lower electrode 102 was formed, he substrate was moved by the substrate transfer unit through the gate valve to the other film-forming chamber having the same constitution as that of the film-forming chamber 201. 
     The gate valve was closed and the film-forming chamber was evacuated to and maintained at 1×10 -5  Torr or below. The substrate was then heated to 220° C. by actuating the heater 205 and it was maintained at this temperature. Then, liquid Al(C 2  H 5 ) 3  in a bubbling vessel (not shown) was gasified by bubbling it with He gas (as a carrier gas) being supplied at a flow rate of 20 sccm to generate at Al-containing raw material gas. The resultant raw material gas was successively introduced through the gas supply pipe 214 into the activation chamber 208 at a flow rate of 4.0×10 -4  mol/min. 
     At the same time, H 2  Se gas diluted with He gas to 1000 ppm (hereinafter referred to as &#34;H 2  Se/He gas&#34;) was introduced through the gas supply pipe 214 into the activation chamber 208 at a flow rate of 85 sccm. High frequency power (13.56 MHz) of 100 W from the activation energy generation means 211 was applied into the activation chamber 208 to generate precursors which were successively introduced through the transport conduit 217 into the film-forming chamber 201. At the same time, PF 5  gas was introduced through the gas supply pipe 216 into the activation chamber 210 maintained at 500° C. by the activation energy generation means 213 at a flow rate of 7 sccm, to thereby generate precursors containing fluorine radicals, which were successively introduced through the transport conduit 219 into the film-forming chamber 201. Concurrently, H 2  gas and He gas were introduced through the gas supply pipe 215 into the activation chamber 209 at respective flow rates of 7 sccm and 60 sccm while being mixed, into which microwave power (2.45 GHz) of 50 W from the activation energy generation means 212 was applied to generate hydrogen radicals, which were successively introduced through the transport conduit 218 (the outlet of which is 7 cm distant from the substrate) into the film-forming chamber 201. 
     At this time, the inner pressure was maintained at 70 m Torr. 
     The foregoing precursors and hydrogen radicals thus introduced into the film-forming chamber 201 were chemically reacted to form a 400 Å thick n-type poly-AlP:H:F:Se semiconductor film as the n-type semiconductor layer 103 on the lower electrode 102. The film-forming conditions used in this case are shown in Table 15. On this n-type semiconductor layer was formed a 3500 Å thick non-doped i-type a-Si:H:F film as the i-type semiconductor layer 104 by repeating the procedures of forming the i-type semiconductor layer in Example 1. Then, on this i-type semiconductor layer was formed a 200 Å thick p-type poly-AlP:H:F:Zn semiconductor film as the p-type semiconductor layer 105 by repeating the procedures of forming the p-type semiconductor layer in Example 1. On this p-type semiconductor layer were successively formed a 700 Å thick ITO film as the transparent electrode 106 and an 0.8 μm thick comb-shaped film comprising an 0.8 μm thick Ag film as the collecting electrode 107 respectively in the same manner as in Example 1. 
     Thus there was obtained Element Example No 8. 
     The characteristics of Element Sample No. 8 as a solar cell were evaluated in the same manner as in Example 1. 
     The results obtained are shown in Table 9. 
     Besides the foregoing, using a quartz glass plate, there was formed a p-type poly-AlP:H F:Zn semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the p-type semiconductor layer 105. 
     The resulting film was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 9. 
     EXAMPLE 9 
     There was prepared a pin heterojunction photovoltaic element of the configuration shown in FIG. 1(A) (Element Sample No. 9) by repeating the procedures of Example 1, except that the n-type semiconductor layer 103 was formed of a 400 Å thick n-type AlP:Se semiconductor which was prepared in accordance with a known sputtering method under the conditions shown in Table 16. 
     The characteristics of Element Sample No. 9 as a solar cell were evaluated in the same manner as in Example 1. 
     The results obtained are shown in Table 17. 
     Besides the foregoing, using a quartz glass plate, there was formed a p-type poly-AlP:H:F:Zn semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the p-type semiconductor layer 105. 
     The resultant film was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The examined results are shown in Table 17. 
     EXAMPLE 10 
     There was prepared a pin heterojunction photovoltaic element of the configuration shown in FIG. 1(A) (Element Sample No. 10) by repeating the procedures of Example 1, except that the n-type semiconductor layer 103 was formed of a 400 Å thick n-type a-SiGe:H:F:P semiconductor film which was prepared by the foregoing process (3) by the plasma CVD method practiced in the plasma CVD apparatus shown in FIG. 4 under the conditions shown in Table 18. 
     The characteristics of Element Sample 10 as a solar cell were evaluated in the same manner as in Example 1. 
     The results obtained are shown in Table 17. 
     Besides the foregoing, using a quartz glass plate, there was formed a p-type poly-AlP:H:F:Zn semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the p-type semiconductor layer 105. 
     The resultant film was examined for hydrogen content, fluorine content and average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 17. 
     EXAMPLE 11 
     There was prepared a pin heterojunction photovoltaic element of the configuration shown in FIG. 1(A) (Element Sample No. 11) by repeating the procedures of Example 1, except that the n-type semiconductor layer 103 was formed of a 400 Å thick n-type a-SiC:H:F:P semiconductor film which was prepared by the foregoing process (3) by the plasma CVD method practiced in the plasma CVD apparatus shown in FIG. 4 under the conditions shown in Table 19. 
     The characteristics of Element Sample 11 as a solar cell were evaluated in the same manner as in Example 1. 
     The results obtained are shown in Table 17. 
     Besides the foregoing, using a quartz glass plate, there was formed a p-type poly-AlP:H:F:Zn semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the p-type semiconductor layer 105. 
     The resultant film was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 17. 
     EXAMPLE 12 
     There was prepared a pin heterojunction photovoltaic element of the configuration shown in FIG. 1(A) (Element Sample No. 12) by repeating the procedures of Example 1, except that the n-type semiconductor layer 103 was formed of a 400 Å thick n-type GaAs:Si semiconductor film which was prepared by the foregoing process (2) by the reactive sputtering method practiced in the reactive sputtering apparatus shown in FIG. 3 under the conditions shown in Table 20. 
     The characteristics of Element Sample 12 as a solar cell were evaluated in the same manner as in Example 1. 
     The results obtained are shown in Table 17. 
     Besides the foregoing, using a quartz glass plate, there was formed a p-type poly-AlP:H:F:Zn semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the p-type semiconductor layer 105. 
     The resultant film was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 17. 
     EXAMPLE 13 
     There was prepared a pin heterojunction photovoltaic element of the configuration shown in FIG. 1(A) (Element Sample No. 13) by repeating the procedures of Example 8, except that the i-type semiconductor layer 104 was formed of a 3500 Å thick non-doped i-type a-Si:H semiconductor film which was prepared by the foregoing process (3) by the plasma CVD method practiced in the plasma CVD apparatus shown in FIG. 4 under the conditions shown in Table 21. 
     The characteristics of Element Sample 13 as a solar cell were evaluated in the same manner as in Example 1. 
     The results obtained are shown in Table 17. 
     Besides the foregoing, using a quartz glass plate, there was formed a p-type poly-AlP:H:F:Zn semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the p-type semiconductor layer 105. 
     The resultant film was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 17. 
     EXAMPLE 14 
     There was prepared a pin heterojunction photovoltaic element of the configuration shown in FIG. 1(A) (Element Sample No. 14) by repeating the procedures of Example 8, except that the i-type semiconductor layer 104 was formed of a 3500 Å thick non-doped i-type a-SiGe:H semiconductor film which was prepared by the foregoing process (3) by the plasma CVD method practiced in the plasma CVD apparatus shown in FIG. 4 under the conditions shown in Table 22. 
     The characteristics of Element Sample 14 as a solar cell were evaluated in the same manner as in Example 1. 
     The results obtained are shown in Table 17. 
     Besides the foregoing, using a quartz glass plate, there was formed a p-type poly-AlP:H:F:Zn semiconductor film on the quartz glass plate by repeating the foregoing procedure for the formation of the p-type semiconductor layer 105. 
     The resultant film was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 17. 
     EXAMPLE 15 
     There was prepared a pin heterojunction photovoltaic element of the configuration shown in FIG. 1(A) (Element Sample No. 15) by repeating the procedures of Example 8, except that the i-type semiconductor layer 104 was formed of a 3500 Å thick non-doped i-type a-SiC:H semiconductor film which was prepared by the foregoing process (3) by the plasma CVD method practiced in the plasma CVD apparatus shown in FIG. 4 under the conditions shown in Table 23. 
     The characteristics of Element Sample 15 as a solar cell were evaluated in the same manner as in Example 1. 
     The results obtained are shown in Table 17. 
     Besides the foregoing, using a quartz glass plate, there was formed a p-type poly-AlP:H:F:Zn semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the p-type semiconductor layer 105. 
     The resultant film was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 17. 
     EXAMPLE 16 
     There was prepared a pin heterojunction photovoltaic element of the configuration shown in FIG. 1(A) (Element Sample No. 16) by repeating the procedures of Example 8, except that the i-type semiconductor layer 104 was formed of a 3500 Å thick non-doped i-type a-Si:F semiconductor film which was prepared by the foregoing process (2) by the the reactive sputtering method practiced in the reactive sputtering apparatus shown in FIG. 3 under the conditions shown in Table 24. 
     The characteristics of Element Sample 16 as a solar cell were evaluated in the same manner as in Example 1. 
     The results obtained are shown in Table 17. 
     Besides the foregoing, using a quartz glass plate, there was formed a p-type poly-AlP:H:F:Zn semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the p-type semiconductor layer 105. 
     The resultant film was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 17. 
     EXAMPLE 17 
     There was prepared a pin heterojunction photovoltaic element of the configuration shown in FIG. 1(A) (Element Sample No. 17) by repeating the procedures of Example 8, except that the i-type semiconductor layer 104 was formed of a 3500 Å thick non-doped i-type a-Si:GeC:H semiconductor film which was prepared by the foregoing process (3) by the the plasma CVD method practiced in the plasma CVD apparatus shown in FIG. 4 under the conditions shown in Table 25. 
     The characteristics of Element Sample 17 as a solar cell were evaluated in the same manner as in Example 1. 
     The results obtained are shown in Table 17. 
     Besides the foregoing, using a quartz glass plate, there was formed a p type poly-AlP:H:F:Zn semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the p-type semiconductor layer 105. 
     The resultant film was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 17. 
     EXAMPLE 18 
     There was prepared a pin heterojunction photovoltaic element of the configuration shown in FIG. 1(A) (Element Sample No. 18) by repeating the procedures of Example 8, except that the i-type semiconductor layer 104 was formed of a 3500 Å thick non-doped i-type poly-Si:H semiconductor film which was prepared by the foregoing process (2) by the the reactive sputtering method practiced in the reactive sputtering apparatus shown in FIG. 3 under the conditions shown in Table 26. 
     The characteristics of Element Sample 18 as a solar cell were evaluated in the same manner as in Example 1. 
     The results obtained are shown in Table 17. 
     Besides the foregoing, using a quartz glass plate, there was formed a p-type poly-AlP:H:F:Zn semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the p-type semiconductor layer 105. 
     The resultant film was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 17. 
     EXAMPLE 19 
     There was prepared a pin heterojunction photovoltaic element of the configuration shown in FIG. 1(B) (Element Sample No. 19) in accordance with the manner of Example 1 and the manner of Example 8. 
     That is, as the substrate 101, there was used a Corning glass plate No. 7059 of 50 mm by 50 mm in size. On the substrate and ITO thin film of about 500 Å in thickness as the transparent electrode 106 was formed by the resistance heating method. 
     On the foregoing transparent electrode was formed a 200 Å thick p-type a-Si:H:F:B semiconductor film as the p-type semiconductor layer 105 by repeating the procedures of forming the n-type layer in Example 1, except that BF 3  gas diluted with H 2  gas to 4000 ppm (BF 3  /H 2  gas) was introduced into the film-forming chamber at a flow rate of 35 sccm instead of the PH 3  /SiF 4  gas. On this p-type semiconductor layer was formed a 3500 Å thick non-doped i-type a-Si:H:F film as the i-type semiconductor layer 104 by repeating the procedures of forming the i-type semiconductor layer in Example 1. There was then formed a 400 Å thick n-type poly-AlP:H:F:Se semiconductor film as the n-type semiconductor layer 103 on the i-type semiconductor layer 104 by repeating the procedures of forming the n-type semiconductor layer in Example 8. On this n-type semiconductor was formed a 0.5 μm thick Ag film as the electrode 102. Thus there was obtained Element Sample No. 19. The characteristics of Element Sample No. 19 as a solar cell were evaluated in the same manner as in Example 1. 
     The results obtained are shown in Table 27. 
     Besides the foregoing, using a quartz glass plate, there was formed an n-type poly-AlP:H:F:Se semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the n-type semiconductor layer 103. 
     The resultant film was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 27. 
     EXAMPLE 20 
     There was prepared a pin heterojunction photovoltaic element of the configuration shown in FIG. 1(B) (Element Sample No. 20) basically in accordance with the manner of Example 8. 
     That is, as the substrate 101, there was used a Corning glass plate No. 7059 of 50 mm by 50 mm in size. On the substrate at ITO thin film of about 500 Å in thickness as the transparent electrode 106 was formed by the resistance heating method. The procedures of forming the n-type semiconductor layer in Example 11 were repeated to form a 200 Å thick p-type a-SiC:H:F:B semiconductor film as the p-type semiconductor layer 105 on the transparent electrode, except that BF 3  gas diluted with H 2  gas to 4000 ppm (BF 3  /H 2  gas) was introduced into the film-forming chamber at a flow rate of 30 sccm instead of the PH 3  /H 2  gas. Then, the procedures for forming the i-type semiconductor layer in Example 1 were repeated to form a 3500 Å thick non-doped i-type a-Si:H:F film as the i-type semiconductor layer 104 on the p-type semiconductor layer. Successively, there was formed a 400 Å thick n-type poly-AlP:H:F:Se semiconductor film as the n-type semiconductor layer 103 on the i-type semiconductor layer 104 by repeating the procedures of forming the n-type semiconductor layer in Example 8. On this n-type semiconductor was formed a 0.5 μm thick Ag film as the electrode 102. Thus thee was obtained Element Sample No. 20. The characteristics of Element Sample No. 20 as a solar cell were evaluated in the same manner as in Example 1. 
     The results obtained are shown in Table 27. 
     Besides the foregoing, using a quartz glass plate, there was formed an n-type poly-AlP:H:F:Se semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the n-type semiconductor layer 103. 
     The resultant film was examined for hydrogen content, fluorine content, and the average size of crystal, grains in the film in the same as above described. 
     The results are shown in Table 27. 
     EXAMPLE 21 
     There was prepared a pin heterojunction photovoltaic element of the configuration shown in FIG. 1(B) (Element Sample No. 21) basically in accordance with the manner of Example 1 and the manner of Example 8. 
     That is, as the substrate 101 there was used a Corning glass plate No. 7059 of 50 mm by 50 mm in size. On the substrate at ITO thin film of about 500 Å in thickness as the transparent electrode 106 was formed by the heating method. On the transparent electrode was a 200 Å thick p-type ZnTe:P semiconductor film as the p-type semiconductor layer 105 by the foregoing (2) by the reactive sputtering method practiced in the reactive sputtering apparatus shown in FIG. 3 under the conditions shown in Table 28. Then, the procedures forming the i-type semiconductor layer in Example 1 were repeated to form a 3500 Å thick non-doped i-type a-Si:H:F as the i-type semiconductor layer 104 on the p-type semiconductor layer. Successively, there was formed a 400 Å n-type poly-AlP:H:F:Se semiconductor film as the n-type semiconductor layer 103 on the i-type semiconductor layer 104 by repeating the procedures of forming the n-type semiconductor layer in Example 8. On this n-type semiconductor formed a 0.5 μm thick Ag film as the electrode 102. Thus, there was obtained Element Sample No. 21. The characteristics of Element Sample No. 21 as a solar cell were in the same manner as in Example 1. 
     The results obtained are shown in Table 27. 
     Besides the foregoing, using a quartz glass plate, there was formed an n-type poly-AlP:H:F:SE semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the n-type semiconductor layer 103. 
     The resultant film was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 27. 
     EXAMPLE 22 
     There was prepared a pin heterojunction photovoltaic element of the configuration shown in FIG. 1(B) (Element Sample No. 22) basically in accordance with the manner of Example 1 and the manner of Example 8. 
     That is, as the substrate 101, there was used a Corning glass plate No. 7059 of 50 mm by 50 mm in size. On the substrate an ITO thin film of about 500 Å in thickness was formed as the transparent electrode 106 by the resistance heating method. 
     On the transparent electrode was formed a 200 Å thick p-type AlP:Zn semiconductor film as the p-type semiconductor layer by the foregoing process (2) by the reacting sputtering method practiced in the reactive sputtering apparatus shown in FIG. 3 under the conditions shown in Table 29. Then, the procedures for forming the i-type semiconductor layer in Example 1 were repeated to form a 3500 Å thick non-doped i-type a-Si:H:F film as the i-type semiconductor layer 104 on the p-type semiconductor layer. Successively, there was formed a 400 Å thick n-type poly-AlP:H:F:Se semiconductor film as the n-type semiconductor layer 103 on the i-type semiconductor layer 104 by repeating the procedures of forming the n-type semiconductor layer in Example 8. On this n-type semiconductor was formed a 0.5 um thick Ag film as the electrode 102. Thus there was obtained Element Sample No. 22. The characteristics of Element Sample No. 22 as a solar cell were evaluated in the same manner as in Example 1. 
     The results obtained are shown in Table 27. 
     Besides the foregoing, using a quartz glass plate, there was formed an n-type poly-AlP:H:F:Se semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the n-type semiconductor layer 103. 
     The resultant film was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 27. 
     EXAMPLE 23 
     There was prepared a multi-cell tandem stacked pin heterojunction photovoltaic element of the configuration shown in FIG. 1(C) (Element Sample 23) which comprises three cells stacked in the following manner. 
     As the substrate 101, there was used a stainless plate of 50 mm by 50 mm in size. 
     Firstly, on the substrate was formed a 1000 Å thick Ag thin film as the lower electrode 102 in the same manner as in Example 1. 
     On the lower electrode was then formed a pin heterojunction photovoltaic element as the first cell 111 comprising a 400 Å thick n-type a-Si:H:F:P semiconductor film as the n-type semiconductor layer, a 3500 Å thick non-doped i-type a-SiGe:H:F semiconductor film as the i-type semiconductor layer 104 and a 200 Å thick p-type poly-AlP:H:F:Zn semiconductor film as the p-type semiconductor layer 105 by repeating the procedures of Example 5. Then, a second pin heterojunction photovoltaic element as the second cell 112 comprising a 400 Å thick n-type a-Si:H:F:P semiconductor film as the n-type semiconductor layer 114, a 3000 Å thick i-type non-doped a-Si:H:F film as the i-type semiconductor layer 115 and a 200 Å thick p-type poly-AlP:H:F:Zn semiconductor film as the p-type semiconductor layer 116 was formed on the first cell 111 by repeating the procedures of Example, 1. On the second cell 112 there was formed a pin heterojunction photovoltaic element as the third cell 113 comprising a 400 Å thick n-type a-Si:H:F:P semiconductor film as the n-type semiconductor layer 117, a 2500 Å thick non-doped i-type a-SiC:H:F semiconductor film as the i-type semiconductor layer 118 and a 200 Å thick p-type poly-AlP:H:F:Zn semiconductor film as the p-type semiconductor layer 119 by repeating the procedures of Example 4.  On the p type semiconductor layer 119 of the third cell 113 was formed a 700 Å ITO film as the transparent electrode 106 in the same manner in Example 1. On the transparent electrode, there was formed a comb-shaped film comprising an Ag thin film of 0.8 μm in thickness as the collecting electrode 107 by repeating the procedures of forming the comb-shaped collecting electrode in Example 1. Thus there was obtained Element Sample No. 23. The characteristics of Element Sample No. 23 as a solar cell were evaluated in the same manner as in Example 1. 
     The results obtained are shown in Table 30. 
     COMPARATIVE EXAMPLE 1 
     There was prepared a comparative pin heterojunction photovoltaic element of the configuration shown in FIG. 1(A) (Element Sample No. 24) by repeating the procedures of Example 1, except that the p-type semiconductor layer 105 was formed of a 200 Å thick p-type a-Si:H:F:B semiconductor film which was prepared in the following manner. 
     That is, after the i-type semiconductor layer 104 was formed, the substrate was moved by the substrate transfer unit through the gate valve to the other film-forming chamber having the same constitution as that of the film-forming chamber 201. The gate valve was closed and the film-forming chamber was evacuated to and maintained at 1×10 -5  Torr or below. The substrate was then heated to 220° C. by actuating the heater 205 and it was maintained at this temperature. Thereafter, Si 2  F 6  gas and BF 3  gas diluted with SiF 4  gas to 4000 ppm (BF 3  /SiF 4  gas) were introduced through the gas supply pipe 214 into the activation chamber 208 maintained at 700° C. by the activation energy generation means 211 at respective flow rates of 30 sccm and 8 sccm while being mixed to generate precursors containing fluorine radicals, which were successively introduced through the transportation conduit 217 into the film-forming chamber 201. 
     At the same time, He gas and H 2  gas were introduced through the gas supply pipe 215 into the activation chamber 209 at respective flow rates of 120 sccm and 60 sccm while being mixed, into which microwave power (2.45 GHz) of 320 W was applied to generate hydrogen radicals which were successively introduced through the transport conduit 218 into the film-forming chamber 201. At this time, the inner pressure of the film-forming chamber 201 was maintained at 0.35 Torr. The foregoing precursors and hydrogen radicals thus introduced into the film-forming chamber 201 were chemically reacted to form a 200 Å thick p-type a-Si:H:F:B semiconductor film as the p-type semiconductor layer 105 on the i-type semiconductor layer 104. On this p-type semiconductor were successively formed a 700 Å thick ITO film as the transparent electrode 106 and an 0.8 μm thick comb-shaped film comprising an 0.8 μm thick Ag film as the collecting electrode 107 respectively in the same manner as in Example 1. 
     Thus there was obtained Element Example No. 24 for comparison purposes. 
     The characteristics of Element Sample No. 24 as a solar cell were evaluated in the same manner as in Example 1. 
     The results obtained are shown in Table 31. 
     COMPARATIVE EXAMPLE 2 
     There was prepared a comparative pin heterojunction photovoltaic element of the configuration shown in FIG. 1(A) (Element Sample No. 25) by repeating the procedures of Example 1, except that the p-type semiconductor layer 105 was formed of a 200 Å thick p type poly-AlP:F:Zn semiconductor film which was prepared by repeating the procedures of forming the p type semiconductor layer in Example 1, except that H 2  gas was not used. 
     Likewise, there was separately prepared another comparative pin heterojunction photovoltaic element of the configuration shown in FIG. 1(A) (Element Sample No. 26) by repeating the procedures of Example 1, except that the p-type semiconductor layer 105 was formed of a 200 Å thick p-type poly-AlP:H:F:Zn semiconductor film (wherein the hydrogen content is slight) which was prepared by repeating the procedures of Example 1, except for changing the flow rate of the H 2  gas to 0.5 sccm. 
     The characteristics of each of Element Samples Nos. 25 and 26 as a solar cell were evaluated in the same manner as in Example 1. 
     The results obtained are shown in Table 31. 
     Besides the foregoing, using a quartz glass plate, there was formed each of the foregoing two p-type semiconductor films on the quartz glass plate by repeating the respective foregoing procedures for the formation of the p-type semiconductor layer 105. 
     Each of the resultant films was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 31. 
     COMPARATIVE EXAMPLE 3 
     There was prepared a comparative pin heterojunction photovoltaic element of the configuration shown in FIG. 1(A) (Element Sample No. 27) by repeating the procedures of Example 1, except that the flow rate of the raw material gas containing Al(C 2  H 5 ) 3  /Zn(CH 3 ) 2  =10 4  :1 and the flow rate of the PF 5  gas at the time of forming the p-type semiconductor layer were changed respectively to 5.0×10 -4  mol/min and 15 sccm. 
     The characteristics of Element Sample No. 27 as a solar cell were evaluated in the same manner as in Example 1. 
     The results obtained are shown in Table 31. 
     Besides the foregoing, using a quartz glass plate, there was formed the foregoing p-type semiconductor film on the quartz glass plate by repeating the foregoing procedures for the formation of the p-type semiconductor layer 105. 
     The resultant film was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 31. 
     COMPARATIVE EXAMPLE 4 
     There were prepared three kinds of comparative pin heterojunction photovoltaic elements of the configuration shown in FIG. 1(A) (Element Samples Nos. 28, 29 and 30) by repeating the procedures of Example 1, except that the i-type semiconductor layer 104 was formed of a 3500 Å thick non-doped i-type a-Si film, a-SiC film or a-SiGe film prepared by the foregoing process (2) by the reactive sputtering apparatus shown in FIG. 2 under the conditions shown in Table 32. 
     The characteristics of each of Element Samples Nos. 28, 29 and 30 as a solar cell were evaluated in the same manner as in Example 1. 
     The results obtained are shown in Table 31. 
     Other than the foregoing, using a quartz glass plate, each of the p-type poly-AlP:H:F:Zn semiconductor conductor films was formed on the quartz glass plate by repeating the foregoing procedures for the formation of the p-type semiconductor layer 105. 
     Each of the resultant films was examined for hydrogen content, fluorine content, and the average size of crystal grains in the film in the same manner as above described. 
     The results are shown in Table 31. 
     COMPARATIVE EXAMPLE 5 
     There was prepared a comparative multi-cell tandem stacked pin heterojunction photovoltaic element of the configuration shown in FIG. 1(C) (Element Sample 31) by repeating the procedures of Example 23, except that the p-type semiconductor layer 119 of the third cell 113 was formed of a 200 Å thick p-type a-Si:H:F:B film by repeating the procedures of forming the p-type semiconductor layer in Comparative Example 1. 
     The characteristics of Element Sample 31 were evaluated, in the same manner as in Example 1. The results obtained are shown in Table 30. 
     Observations on the Results Shown in Tables 9, 17, 27, 30 and 31 
     In each of Tables 9, 17, 27, 30 and 31, with respect to characteristic properties required for a pin heterojunction photovoltaic element, there are indicated the following evaluation items: (a) open circuit voltage (Voc) which is generated when the element is irradiated with AM-1 light (100 mW/cm 2 ), (b) short-circuit current (Isc) which is generated when the element is irradiated with AM-1 light (100 mW/cm 2 ), and (c) the relative value of the output which is obtained when the element is irradiated with AM-1 light through a 400 nm interference filter versus the output which is obtained when the pin heterojunction photovoltaic element prepared in Comparative Example 1 is irradiated through the interference filter. 
     In each of Tables 9, 17, 27 and 31, there are also shown the content of hydrogen atoms (H), the content of optional fluorine atoms (F), the average grain size, and the composition ratio of the Al to the P with respect to each of the poly-AlP:H(F):M semiconductor films used. 
     The results indicate the following. It has been recognized that each of the pin heterojunction photovoltaic elements of the configuration shown in FIG. 1(A) or FIG. 1(B) (Element Samples Nos. 1-22 obtained in Examples 1 to 22) having the p-type semiconductor layer or/and the n-type semiconductor layer formed of a specific poly-AlP:H(F):M semiconductor film of wide band gap (where M is a dopant of p-type or n-type) according to the present invention which contains aluminum atoms (Al) and phosphorous atoms (P) in uniformly distributed states with the composition ratio of the Al to the P to satisfy the stoichiometric ratio, hydrogen atoms (H) in an amount of 0.5 to 5 atomic %, optionally fluorine atoms (F) in an amount of 0 to 5 atomic %, and crystal grains of an average size in the range of from 50 to 1000 Å and the i-type semiconductor layer of a specific silicon (Si)-containing non-single crystal film containing at least hydrogen atoms (H) and/or fluorine atoms (F) excels in any of the evaluation items required for a solar cell. It has been also recognized that the specific poly-AlP:H(F):M semiconductor film according to the present invention makes it possible to form a desirable junction with a specific silicon(Si)-containing non-single crystal semiconductor film regardless of its band gap whether it is wide or narrow and thus, it makes possible to provide a desirable pin heterojunction photovoltaic element excelling in the characteristics required for a solar cell. This situation is apparent when the characteristics of each of these pin heterojunction photovoltaic elements (Element Samples Nos. 1 to 22) as a solar cell are compared with those of each of the comparative shown in FIG. 1(A) (Element Samples Nos. 24 to 30 obtained in Comparative Examples 1 to 4). More particularly in this respect, it has been recognized that the pin heterojunction photovoltaic elements (Element Samples, 1 to 3 prepared in Examples 1 to 3, respectively) in which the p-type semiconductor layer comprising the foregoing specific poly-AlP:H(F):Mp semiconductor film (where Mp is a p-type dopant) is prepared by a different film-forming method, the i-type semiconductor layer comprises the foregoing selected Si-containing non-single crystal film (a Si:H:F film) and the n-type semiconductor layer comprises an n-type non-single crystal Si containing film (n-type a-Si:H:F film) markedly surpass the comparative pin photovoltaic element (Element Sample No. 24 prepared in Comparative Example 1) which has the p-type semiconductor layer comprising a p-type a-Si:H:F film, the i-type semiconductor layer comprising an i-type a-Si:H:F film and the n-type semiconductor layer comprising an n-type a-Si:H:F film, with respect to any of the foregoing evaluation items (a) to (c) without depending upon the kind of the method employed for forming said poly-AlP:H(F):Mp semiconductor film. 
     For the pin heterojunction photovoltaic elements (Element Samples Nos. 4, 5 and 6 prepared respectively in Examples 4, 5 and 6) respectively comprising a p-type semiconductor layer formed of the foregoing poly-AlP:H(F):Mp semiconductor film, an i-type semiconductor layer formed of an i-type a-SiC:H:F film, an i-type a-SiGe:H:F film or an i-type poly-Si:H:F film and an n-type semiconductor layer formed of an n-type a-Si:H:F film, it has been recognized that each of them still excels in each of the evaluation items (a) to (c) although the i-type semiconductor layer is formed of a Si-containing non-single crystal, film other than the i-type a-Si:H:F film, i.e. said i-type a-SiC:H:F film, i-type a-SiGe:H:F film or i-type poly-Si:H:F film. 
     From the results of the pin heterojunction photovoltaic element (Element Sample No. 7 prepared in Example 7), it has been recognized that the present invention is markedly effective also in the case of pin heterojunction photovoltaic elements of the type wherein light is impinged from the side of the substrate. In fact, as Table 9 illustrates, the pin heterojunction photovoltaic element of the configuration shown in FIG. 1(B) which comprises the p-type semiconductor layer formed of p-type a-Si:H:F, the i-type semiconductor layer formed of i-type a-Si:H:F film and the n-type semiconductor layer formed of the foregoing poly-AlP:H(F):Mn film (where Mn is an n-type dopant) markedly excels in each of the foregoing evaluation items (a) to (c). 
     From the results shown in Table 9 for the pin heterojunction photovoltaic element (Element Sample No. 8 prepared in Example 8) which comprises a p-type semiconductor layer formed of the foregoing poly-AlP:H(F):Mp semiconductor film, an i-type semiconductor layer formed of an i-type a-Si:H:F film and an n-type semiconductor layer formed of the foregoing poly-AlP:H(F):Mn semiconductor film, it has been recognized that Element Sample No. 8 surpasses any of Element Samples 1 to 3 with respect to all the foregoing evaluation items (a) to (c). 
     On the other hand, for the two comparative pin heterojunction photovoltaic elements (Element Samples Nos. 25-26 prepared in Comparative Example 2), it has been recognized that each of them apparently is inferior to each of Element Samples Nos. 1-3 chiefly because each of them has a p-type semiconductor layer formed of a p-type poly-AlP:F semiconductor film not containing hydrogen atoms or a p-type poly-AlP:H:F semiconductor film containing hydrogen atoms only in a slight amount. 
     Likewise, for the comparative pin heterojunction photovoltaic element (Element Sample No. 27 prepared in Comparative Example 3), it has been recognized that it is apparently inferior to each of Element Samples Nos. 1 to 3 chiefly because of having a p-type semiconductor layer formed of a p-type poly-AlP:H:F film containing aluminum atoms (Al) and phosphorus atoms (P) with a composition ratio which does not satisfy the stoichiometric ratio. 
     For the three comparative pin heterojunction photovoltaic elements (Element Samples Nos. 28-30), it has been recognized that each of them is apparently inferior to each of Element Samples Nos. 3-5 although each of them has a p-type semiconductor layer formed of the foregoing poly-AlP:H:F:Mp semiconductor film but each has an i-type semiconductor layer formed of an i-type a-Si film, a-SiC film or a-SiGe film containing neither hydrogen atoms (H) nor fluorine atoms (F). 
     For the pin heterojunction photovoltaic elements (Element Samples Nos. 9-12 prepared in Examples 9-12) respectively having a p-type semiconductor layer formed of the foregoing poly-AlP:H(F):Mp semiconductor film, an i-type semiconductor layer formed of an i-type a-Si:H:F film and an n-type semiconductor layer formed of an n-type non-single crystal film other than the n-type a-Si:H:F film, i.e. an n-type AlP film of wide band gap an n-type a-SiGe:H:F film of narrow band gap, an n-type a SiC:H:F film of wide band gap or an n-type GaAs film of narrow band gap, it has been recognized that each of them provides a high Voc and a desirable Isc, and exhibits good, practically applicable solar cell characteristics. 
     For the pin heterojunction photovoltaic elements (Element Samples Nos. 13-18 prepared in Examples 13-18) respectively having a p-type semiconductor layer formed of the foregoing poly-AlP:H(F):Mp semiconductor film, an i-type semiconductor layer formed of an i-type Si-containing non-single crystal film other than the i-type a-Si:H:F film, i.e. an i-type a-Si:H film, an i-typo a-SiGe:H film of narrow band gap, an i-type a-SiC:H film of wide band gap, an i-type a-Si:F film, an i-type a-Si:Ge:C:H film of wide band gap or an i-type poly-Si:H film of narrow band gap, and an n-type semiconductor layer formed of the foregoing poly-AlP:H(F): Mn semiconductor film, it has been recognized that each of them provides a high Voc and a desirable Isc, and exhibits good, practically applicable solar cell characteristics. 
     For the pin heterojunction photovoltaic elements (Element Samples Nos. 19-22 prepared in Examples 19-22) of the configuration shown in FIG. 1(B) respectively having a p-type semiconductor layer formed of a p-type a-Si:H:F film, a p-type a-SiC:H:F film of wide band gap, a p-type ZnTe film of wide band gap or a p-type AlP film of wide band gap, an i-type semiconductor layer formed of an i-type a-Si:H:F film and an n-type semiconductor layer formed of the foregoing poly-AlP:H(F):Mn semiconductor film, it has been recognized that each of them provides a high Voc and a desirable Isc, and exhibits good, practically applicable solar cell characteristics. 
     For each of the multi-cell tandem stacked pin heterojunction photovoltaic elements of the configuration shown in FIG. 1(c) (Element Samples Nos. 23 and 31 prepared in Examples 21 and Comparative Example 5), evaluations were made of the Voc and the Isc and in addition, for the change in photoelectric conversion efficiency that takes place after continuous irradiation with AM-1 light for 10 hours: the change is expressed by Δ.sub.η /η o  in percentage, where Δ.sub.η  is the amount of change in photoelectric conversion efficiency and η o  is the initial photoelectric conversion efficiency as shown in Table 30. 
     From the results shown in Table 30, it has been recognized that (1) the multi-cells tandem stacked pin heterojunction photovoltaic element in which the p-type semiconductor layer of each cell is formed of the foregoing poly-AlP:H(F):Mp semiconductor film (Element Sample No. 23) is superior to the comparative multi-cell tandem stacked pin heterojunction photovoltaic element (Element Sample No. 31) in which the p-type semiconductor layer of each cell is formed of a p-type a-Si:H:F film with respect to Voc and the Isc. It has been also recognized that the change in photoelectric conversion efficiency of Element Sample No. 23 is significantly smaller than that of Element Sample No. 31. This means that Element Sample No. 23 not only excels in the initial solar cell characteristics but also can be continuously used as a solar cell for a long period of time without being deteriorated. 
     
                       TABLE 1                                                     
______________________________________                                    
substrate temperature                                                     
             220° C.                                               
inner pressure                                                            
             80 mTorr                                                     
raw material gas (A)                                                      
             gasified Al(CH.sub.3).sub.3 at                               
                           decomposed with                                
(introduced into                                                          
             3.0 × 10.sup.-4 mol/min                                
                           microwave (2.45                                
the activation                                                            
             He gas at 15 sccm                                            
                           GHz) of 50 W                                   
chamber 208)                                                              
raw material gas (B)                                                      
             PF.sub.5 gas at 5 sccm                                       
                           thermally de-                                  
(introduced into           composed at 500° C.                     
the activation                                                            
chamber 210)                                                              
raw material gas (C)                                                      
             H.sub.2 gas* at 0˜800                                  
                           decomposed with                                
(introduced into                                                          
             sccm,         microwave (2.45                                
the activation                                                            
             He gas at 50 sccm                                            
                           GHz) of 200 W                                  
chamber 209)                                                              
the distance between the substrate and the                                
                       8 cm                                               
outlet of the transportation conduit for H                                
radicals                                                                  
______________________________________                                    
*Sample No. and the flow rate of H.sub.2 gas                              
Sample No. 1                                                              
          0      sccm                                                     
Sample No. 2                                                              
          0.2    sccm                                                     
Sample No. 3                                                              
          1.0    sccm                                                     
Sample No. 4                                                              
          3.0    sccm                                                     
Sample No. 5                                                              
          10     sccm                                                     
Sample No. 6                                                              
          20     sccm                                                     
Sample No. 7                                                              
          50     sccm                                                     
Sample No. 8                                                              
          100    sccm                                                     
Sample No. 9                                                              
          400    sccm                                                     
Sample No. 10                                                             
          800    sccm                                                     
 
    
     
                                           TABLE 2                                 
__________________________________________________________________________
Sample                                                                    
    hydrogen content                                                      
             fluorine content                                             
                     composition ratio of                                 
                               distributed state                          
                                         crystal                          
                                               average crystal            
No. (atomic %)                                                            
             (atomic %)                                                   
                     Al to P   of crystal grain                           
                                         orientation                      
                                               grain size                 
__________________________________________________________________________
                                               (Å)                    
1   not detected                                                          
             6.3     33:67     uneven (localized)                         
                                         random                           
                                               --                         
2   0.2      5.6     44:56     &#34;         &#34;     --                         
3   1.3      5.2     47:53     even      &lt;111&gt;  50                        
4   2.1      5.0     49:51     &#34;         &#34;     250                        
5   3.2      2.8     50:50     &#34;         &#34;     550                        
6   4.3      1.6     50:50     &#34;         &#34;     900                        
7   4.8      1.3     51:49     &#34;         &#34;     1000                       
8   4.0      0.8     52:48     &#34;         &#34;     850                        
9   3.4      0.5     52:48     &#34;         &#34;     800                        
10  2.6       0.08   54:46     &#34;         &#34;     650                        
__________________________________________________________________________
 
    
     
                       TABLE 3                                                     
______________________________________                                    
target material  non-doped polycrystal AlP wafer                          
sputtering gas used                                                       
                 Ar gas at 40 sccm                                        
and its flow rate                                                         
                 H.sub.2 gas* at 0˜500 sccm                         
                 HF gas* at 0˜100 sccm                              
the distance between the target                                           
                 35 mm                                                    
and the substrate                                                         
high frequency power                                                      
                 400 W (13.56 MHz)                                        
substrate temperature                                                     
                 220° C.                                           
inner pressure   6 mTorr                                                  
______________________________________                                    
*Sample No. and the flow rates of H.sub.2 gas and HF gas                  
        H.sub.2 HF                                                        
Sample No. 11                                                             
          0      sccm   0    sccm                                         
Sample No. 12                                                             
          1      sccm   1    sccm                                         
Sample No. 13                                                             
          5      sccm   0    sccm                                         
Sample No. 14                                                             
          5      sccm   5    sccm                                         
Sample No. 15                                                             
          10     sccm   5    sccm                                         
Sample No. 16                                                             
          50     sccm   10   sccm                                         
Sample No. 17                                                             
          50     sccm   50   sccm                                         
Sample No. 18                                                             
          100    sccm   50   sccm                                         
Sample No. 19                                                             
          100    sccm   100  sccm                                         
Sample No. 20                                                             
          500    sccm   50   sccm                                         
 
    
     
                                           TABLE 4                                 
__________________________________________________________________________
Sample                                                                    
    hydrogen content                                                      
             fluorine content                                             
                     composition ratio of                                 
                               distributed state                          
                                         crystal                          
                                               average crystal            
No. (atomic %)                                                            
             (atomic %)                                                   
                     Al to P   of crystal grain                           
                                         orientation                      
                                               grain size                 
__________________________________________________________________________
                                               (Å)                    
11  not detected                                                          
             not detected                                                 
                     35:65     fairly uneven                              
                                         random                           
                                               --                         
12  0.1       0.07   43:57     &#34;         &lt;111&gt;  40                        
13  0.5      not detected                                                 
                     45:55     even      &#34;      50                        
14  0.9      0.2     48:52     &#34;         &#34;     250                        
15  1.3      0.6     49:51     &#34;         &#34;     400                        
16  2.8      1.3     50:50     &#34;         &#34;     700                        
17  3.5      2.7     51:49     &#34;         &#34;     950                        
18  4.7      3.7     52:48     &#34;         &#34;     900                        
19  6.3      4.5     55:45     &#34;         &#34;     800                        
20  7.1      2.9     50:50     &#34;         &#34;     750                        
__________________________________________________________________________
 
    
     
                       TABLE 5                                                     
______________________________________                                    
raw material gas (A) gasified Al(CH.sub.3).sub.3 at                       
                     4.0 × 10.sup.-5 mol/min                        
                     He gas at 10 sccm                                    
raw material gas (B) PH.sub.3 gas at 3.5 sccm                             
raw material gas (C) H.sub.2 gas* at 0˜800 sccm                     
                     HF gas* at 0˜100 sccm                          
the distance between the substrate and                                    
                     35 mm                                                
the cathode                                                               
high frequency power 80 W (13.56 MHz)                                     
substrate temperature                                                     
                     230° C.                                       
inner pressure       0.7 Torr                                             
______________________________________                                    
*Sample No. and the flow rates of H.sub.2 gas and HF gas                  
        H.sub.2 HF                                                        
Sample No. 21                                                             
          0      sccm   0    sccm                                         
Sample No. 22                                                             
          5      sccm   0    sccm                                         
Sample No. 23                                                             
          5      sccm   5    sccm                                         
Sample No. 24                                                             
          50     sccm   50   sccm                                         
Sample No. 25                                                             
          100    sccm   50   sccm                                         
Sample No. 26                                                             
          100    sccm   100  sccm                                         
Sample No. 27                                                             
          300    sccm   50   sccm                                         
Sample No. 28                                                             
          500    sccm   50   sccm                                         
Sample No. 29                                                             
          800    sccm   50   sccm                                         
Sample No. 30                                                             
          800    sccm   100  sccm                                         
 
    
     
                                           TABLE 6                                 
__________________________________________________________________________
Sample                                                                    
    hydrogen content                                                      
             fluorine content                                             
                     composition ratio of                                 
                               distributed state                          
                                         crystal                          
                                               average crystal            
No. (atomic %)                                                            
             (atomic %)                                                   
                     Al to P   of crystal grain                           
                                         orientation                      
                                               grain size                 
__________________________________________________________________________
                                               (Å)                    
21  23       not detected                                                 
                     43:57     uneven (localized)                         
                                         amorphous                        
                                               --                         
22  17       not detected                                                 
                     45:55     &#34;         &#34;     --                         
23  11       0.4     46:54     fairly uneven                              
                                         &#34;     --                         
24  6.2      1.3     48:52     even      random                           
                                                40                        
25  5.0      1.0     49:51     &#34;         &lt;111&gt; 150                        
26  4.4      2.3     51:49     &#34;         &#34;     300                        
27  4.2      1.1     50:50     &#34;         &#34;     550                        
28  3.7      1.3     51:49     &#34;         &#34;     850                        
29  2.4      1.1     49:51     &#34;         &#34;     650                        
30  3.1      2.1     49:51     &#34;         &#34;     500                        
__________________________________________________________________________
 
    
     
                       TABLE 7                                                     
______________________________________                                    
      change in                                                           
Sample                                                                    
      the electric                                                        
                  photo-     surface total                                
No.   conductivity                                                        
                  luminescence                                            
                             smoothness                                   
                                     evaluation                           
______________________________________                                    
 1    X           X          X       X                                    
 2    X           X          X       X                                    
 3    Δ     X          X       X                                    
 4    ○    Δ    ○                                     
                                     ○                             
 5    ○    Δ    ○                                     
                                     ○                             
 6    ○    ○   ○                                     
                                     ⊚                     
 7    ○    ○   ○                                     
                                     ⊚                     
 8    ○    ○   ○                                     
                                     ⊚                     
 9    ○    ○   ○                                     
                                     ⊚                     
10    ○    ○   X       X                                    
11    X           X          X       X                                    
12    X           Δ    X       X                                    
13    ○    Δ    ○                                     
                                     ○                             
14    ○    ○   ○                                     
                                     ⊚                     
15    ○    ○   ○                                     
                                     ⊚                     
16    ○    ○   ○                                     
                                     ⊚                     
17    ○    ○   ○                                     
                                     ○                             
18    ○    Δ    ○                                     
                                     ○                             
19    X           Δ    X       X                                    
20    X           Δ    X       X                                    
21    X           X          X       X                                    
22    X           X          X       X                                    
23    X           X          X       X                                    
24    Δ     Δ    X       X                                    
25    ○    ○   ○                                     
                                     ⊚                     
26    ○    Δ    ○                                     
                                     ○                             
27    ○    ○   ○                                     
                                     ⊚                     
28    ○    ○   ○                                     
                                     ⊚                     
29    ○    ○   X       X                                    
30    Δ     Δ    X       X                                    
______________________________________                                    
 Note                                                                     
 ⊚: excellent                                              
  ○ : good                                                         
 Δ: seems practically acceptable                                    
 X: practically not acceptable                                            
 
    
     
                                           TABLE 8                                 
__________________________________________________________________________
Sample                                                                    
     p-type   i-type   n-type                                             
No.  semiconductor                                                        
              semiconductor                                               
                       semiconductor                                      
                                Isc                                       
                                   Voc                                    
__________________________________________________________________________
91   p-type AlP:H(F)                                                      
              A-Si:H   A-Si:H   ○                                  
                                   ○                               
92   according to the                                                     
              A-Si:F            Δ                                   
                                   ○                               
93   present  A-Si:H:F          ○                                  
                                   ○                               
94   invention                                                            
              A-Si:H   n-type AlP:H(F)                                    
                                ○                                  
                                   ⊚                       
95            A-Si:F   according to the                                   
                                ○                                  
                                   ○                               
96            A-Si:H:F present  ○                                  
                                   ⊚                       
                       invention                                          
97            A-SiC:H:F                                                   
                       A-Si:H   Δ                                   
                                   ⊚                       
98            A-SiGe:H:F        ⊚                          
                                   Δ                                
99            poly-Si:H:F       ○                                  
                                   Δ                                
100           A-Si     A-Si:H   x  x                                      
101           A-SiC             x  Δ                                
102           A-SiGe            x  x                                      
103           poly-Si           Δ                                   
                                   x                                      
104  known p-type AlP                                                     
              A-Si:H   A-Si:H   x  Δ                                
105           A-Si:F            x  x                                      
106           A-Si:H:F          Δ                                   
                                   x                                      
107           A-SiC:H:F         x  Δ                                
108           A-SiGe:H:F        x  x                                      
109           poly-Si:H:F       x  Δ                                
__________________________________________________________________________
 Note                                                                     
 ⊚: excellent                                              
  ○ : good                                                         
 Δ: seems practically acceptable                                    
 x: practically not acceptable                                            
 
    
     
                                           TABLE 9                                 
__________________________________________________________________________
                                       open-circuit                       
                                              short-circuit               
                                                     output value under   
Ele-            characteristics of p-type &amp; n-type AlP:H(F)               
                                       voltage under                      
                                              photocurrent                
                                                     irradiation of       
Ex-                                                                       
   ment                     average    irradiation of                     
                                              under irradia-              
                                                     AM-1 light (using    
am-                                                                       
   Sam-         hydrogen                                                  
                      fluorine                                            
                            crystal                                       
                                 composition                              
                                       AM-1 light                         
                                              tion of AM-1                
                                                     400 nm interference  
ple                                                                       
   ple                                                                    
      semiconductor                                                       
                content                                                   
                      content                                             
                            grain size                                    
                                 ratio of Al                              
                                       Voc    light  filter)              
No.                                                                       
   No.                                                                    
      layer     (atomic %)                                                
                      (atomic %)                                          
                            (Å)                                       
                                 to P  [Volt] Isc [mA/cm.sup.2 ]          
                                                     [relative            
__________________________________________________________________________
                                                     value]               
1  1  p-type AlP:H:F (1)                                                  
                4.4   1.3   450  50:50 0.97   17.3   2.0                  
      i-type A-Si:H:F                                                     
      n-type A-Si:H:F                                                     
2  2  p-type AlP:H:F (2)                                                  
                2.4   1.4   600  49:51 0.99   17.1   1.9                  
      i-type A-Si:H:F                                                     
      n-type A-Si:H:F                                                     
3  3  p-type AlP:H:F (3)                                                  
                4.5   2.1   250  50:50 0.96   16.7   1.7                  
      i-type A-Si:H:F                                                     
      n-type A-Si:H:F                                                     
4  4  p-type AlP:H:F                                                      
                4.3   1.2   450  50:50 1.20   12.2   1.6                  
      i-type A-SiC:H:F                                                    
      n-type A-Si:H:F                                                     
5  5  p-type AlP:H:F                                                      
                4.4   1.2   450  50:50 0.62   20.1   1.5                  
      i-type A-SiGe:H:F                                                   
      n-type A-Si:H:F                                                     
6  6  p-type AlP:H:F                                                      
                4.4   1.3   450  51:49 0.58   18.1   1.2                  
      i-type polySi:H:F                                                   
      n-type A-Si:H:F                                                     
7  7  p-type A-Si:H:F                                                     
                4.3   1.3   450  51:49 0.96   17.2   1.9                  
      i-type A-Si:H:F                                                     
      n-type AlP:H:F                                                      
8  8  p-type AlP:H:F                                                      
                4.4   1.1   450  51:49 1.00   18.0   2.2                  
      i-type A-Si:H:F                                                     
                *4.2  1.0   350  49:51                                    
      n-type AlP:H:F                                                      
__________________________________________________________________________
 *n-type AlP:H(F) film                                                    
 
    
     
                       TABLE 10                                                    
______________________________________                                    
target material  non-doped AlP polycrystal wafer                          
substrate temperature                                                     
                 220° C.                                           
flow rate of Ar gas                                                       
                 40 sccm                                                  
flow rate of H.sub.2 gas                                                  
                 25 sccm                                                  
flow rate of HF gas                                                       
                 10 sccm                                                  
flow rate of DMZn gas                                                     
                 3 × 10.sup.-10 mol/min (He 5 sccm)                 
as a carrier gas                                                          
inner pressure   5 mTorr                                                  
high frequency power                                                      
                 400 W (13.56 MHz)                                        
______________________________________                                    
 
    
     
                       TABLE 11                                                    
______________________________________                                    
substrate temperature                                                     
               230° C.                                             
raw material gas (A)                                                      
               gasified Al(CH.sub.3).sub.3 /Zn(CH.sub.3).sub.2 = 10.sup.4 
               :1                                                         
               at 7.0 × 10.sup.-5 mol/min                           
               He gas at 10 sccm                                          
raw material gas (B)                                                      
               PH.sub.3 gas at 3.5 sccm                                   
raw material gas (C)                                                      
               H.sub.2 gas at 150 sccm                                    
               HF gas at 75 sccm                                          
inner pressure 0.8 Torr                                                   
high frequency power                                                      
               75 W (13.56 MHz)                                           
the distance between the                                                  
               35 mm                                                      
substrate and the cathode                                                 
______________________________________                                    
 
    
     
                       TABLE 12                                                    
______________________________________                                    
raw material gas (A)                                                      
             Si.sub.2 F.sub.6 gas at 15 sccm                              
                           thermally de-                                  
(introduced into           composed at 700° C.                     
the activation                                                            
chamber 208)                                                              
raw material gas (B)                                                      
             H.sub.2 gas at 150 sccm                                      
                           decomposed with                                
(introduced into                                                          
             He gas at 70 sccm                                            
                           microwave (2.45                                
the activation             GHz) of 400 W                                  
chamber 209)                                                              
raw material gas (C)                                                      
             CH.sub.4 gas at 150 sccm                                     
                           decomposed with                                
(introduced into                                                          
             He gas at 30 sccm                                            
                           microwave (2.45                                
the activation             GHz) of 300 W                                  
chamber 210)                                                              
substrate temperature                                                     
             220° C.                                               
inner pressure                                                            
             0.25 Torr                                                    
the distance between the substrate and the                                
                       8 cm                                               
outlet of the transportation conduit for H                                
radicals                                                                  
______________________________________                                    
 
    
     
                       TABLE 13                                                    
______________________________________                                    
raw material gas (A)                                                      
             Si.sub.2 F.sub.6 gas at 30 sccm                              
                           thermally de-                                  
(introduced into           composed at 700° C.                     
the activation                                                            
chamber 208)                                                              
raw material gas (B)                                                      
             H.sub.2 gas at 100 sccm                                      
                           decomposed with                                
(introduced into                                                          
             He gas at 60 sccm                                            
                           microwave (2.45                                
the activation             GHz) of 400 W                                  
chamber 209)                                                              
raw material gas (C)                                                      
             GeF.sub.4 gas at 8 sccm                                      
                           thermally de-                                  
(introduced into                                                          
             He gas at 25 sccm                                            
                           composed at 450° C.                     
the activation             together with Ge                               
chamber 210)               solid particles                                
substrate temperature                                                     
             220° C.                                               
inner pressure                                                            
             0.15 Torr                                                    
the distance between the substrate and the                                
                       8 cm                                               
outlet of the transportation conduit for H                                
radicals                                                                  
______________________________________                                    
 
    
     
                       TABLE 14                                                    
______________________________________                                    
raw material gas (A)                                                      
             Si.sub.2 F.sub.6 gas at 15 sccm                              
                           thermally de-                                  
(introduced into           composed at 700° C.                     
the activation                                                            
chamber 208)                                                              
raw material gas (B)                                                      
             H.sub.2 gas at 400 sccm                                      
                           decomposed with                                
(introduced into                                                          
             He gas at 150 sccm                                           
                           microwave (2.45                                
the activation             GHz) of 450 W                                  
chamber 209)                                                              
substrate temperature                                                     
             220° C.                                               
inner pressure                                                            
             0.15 Torr                                                    
the distance between the substrate and the                                
                       5 cm                                               
outlet of the transportation conduit for H                                
radicals                                                                  
______________________________________                                    
 
    
     
                       TABLE 15                                                    
______________________________________                                    
raw material gas (A)                                                      
             gasified Al(CH.sub.3).sub.3 /                                
                           decomposed with                                
(introduced into                                                          
             Se(CH.sub.3).sub.2 = 10.sup.4 :1 at                          
                           high frequency                                 
the activation                                                            
             4.5 × 10.sup.-4 mol/min                                
                           power (13.56 MHz)                              
chamber 208) He gas at 15 sccm                                            
                           of 80 W                                        
raw material gas (B)                                                      
             H.sub.2 gas at 7 sccm                                        
                           decomposed with                                
(introduced into                                                          
             He gas at 60 sccm                                            
                           microwave (2.45                                
the activation             GHz) of 50 W                                   
chamber 209)                                                              
raw material gas (C)                                                      
             PF.sub.5 gas at 7 sccm                                       
                           thermally de-                                  
(introduced into           composed at 500° C.                     
the activation                                                            
chamber 210)                                                              
substrate temperature                                                     
             220° C.                                               
inner pressure                                                            
             0.8 Torr                                                     
the distance between the substrate and the                                
                       6 cm                                               
outlet of the transportation conduit for H                                
radicals                                                                  
______________________________________                                    
 
    
     
                       TABLE 16                                                    
______________________________________                                    
target material  non-doped AlP polycrystal wafer                          
substrate temperature                                                     
                 220° C.                                           
flow rate of Ar gas                                                       
                 35 sccm                                                  
flow rate of Se(CH.sub.3).sub.2 saturated                                 
                 4 × 10.sup.-11 mol/min                             
with He gas (as an n-type                                                 
doping raw material gas)                                                  
flow rate of He gas                                                       
                 3 sccm                                                   
inner pressure   4 mTorr                                                  
high frequency power                                                      
                 350 W (13.56 MHz)                                        
______________________________________                                    
 
    
     
                                           TABLE 17                                
__________________________________________________________________________
                                       open-circuit                       
                                              short-circuit               
                                                     output value under   
Ele-            characteristics of p-type &amp; n-type AlP:H(F)               
                                       voltage under                      
                                              photocurrent                
                                                     irradiation of       
Ex-                                                                       
   ment                     average    irradiation of                     
                                              under irradia-              
                                                     AM-1 light (using    
am-                                                                       
   Sam-         hydrogen                                                  
                      fluorine                                            
                            crystal                                       
                                 composition                              
                                       AM-1 light                         
                                              tion of AM-1                
                                                     400 nm interference  
ple                                                                       
   ple                                                                    
      semiconductor                                                       
                content                                                   
                      content                                             
                            grain size                                    
                                 ratio of Al                              
                                       Voc    light  filter)              
No.                                                                       
   No.                                                                    
      layer     (atomic %)                                                
                      (atomic %)                                          
                            (Å)                                       
                                 to P  [Volt] Isc [mA/cm.sup.2 ]          
                                                     [relative            
__________________________________________________________________________
                                                     value]               
9  9  p-type AlP:H:F                                                      
                4.3   1.3   450  50:50 0.94   17.2   1.8                  
      i-type A-Si:H:F                                                     
      n-type AlP                                                          
10 10 p-type AlP:H:F                                                      
                4.4   1.3   450  50:50 0.92   17.1   1.6                  
      i-type A-Si:H:F                                                     
      n-type A-SiGe:H:F                                                   
11 11 p-type AlP:H:F                                                      
                4.4   1.2   450  49:51 0.98   17.9   1.9                  
      i-type A-Si:H:F                                                     
      n-type A-SiC:H:F                                                    
12 12 p-type AlP:H:F                                                      
                4.4   1.2   450  51:49 0.95   16.9   1.6                  
      i-type A-Si:H:F                                                     
      n-type GaAs                                                         
13 13 p-type AlP:H:F                                                      
                *4.3  1.2   450  50:50 0.97   17.7   1.9                  
      i-type A-Si:H                                                       
                **4.3 1.0   350  50:50                                    
      n-type AlP:H:F                                                      
14 14 p-type AlP:H:F                                                      
                *4.4  1.3   450  51:49 0.58   19.4   1.3                  
      i-type A-SiGe:H                                                     
                **4.1 1.0   350  50:50                                    
      n-type AlP:H:F                                                      
15 15 p-type AlP:H:F                                                      
                *4.4  1.2   450  49:51 1.17   11.8   1.5                  
      i-type A-SiC:H                                                      
                **4.3 1.0   350  51:49                                    
      n-type AlP:H:F                                                      
16 16 p-type AlP:H:F                                                      
                *4.3  1.3   450  50:50 0.90   17.0   1.4                  
      i-type A-Si:F                                                       
                **4.2 1.1   350  49:51                                    
      n-type AlP:H:F                                                      
17 17 p-type AlP:H:F                                                      
                *4.3  1.3   450  49:51 0.64   18.7   1.3                  
      i-type A-Si:GeC:H                                                   
                **4.1 1.0   350  50:50                                    
      n-type AlP:H:F                                                      
18 18 p-type AlP:H:F                                                      
                *4.4  1.2   450  50:50 0.57   18.0   1.3                  
      i-type poly-Si:H                                                    
                **4.2 1.0   350  51:49                                    
      n-type AlP:H:F                                                      
__________________________________________________________________________
 *p-type AlP:H(F) film                                                    
 **n-type AlP:H(F) film                                                   
 
    
     
                       TABLE 18                                                    
______________________________________                                    
substrate temperature                                                     
                     220° C.                                       
flow rate of Si.sub.2 H.sub.6 gas                                         
                     8 sccm                                               
flow rate of GeF.sub.4 gas                                                
                     5 sccm                                               
flow rate of PH.sub.3 gas                                                 
                     5 sccm                                               
(diluted by H.sub.2 gas to 3000 ppm)                                      
flow rate of H.sub.2 gas                                                  
                     250 sccm                                             
inner pressure       1.2 Torr                                             
high frequency power 32 W (13.56 MHz)                                     
______________________________________                                    
 
    
     
                       TABLE 19                                                    
______________________________________                                    
substrate temperature                                                     
                     220° C.                                       
flow rate of SiF.sub.4 gas                                                
                     25 sccm                                              
flow rate of CH.sub.4 gas                                                 
                     5 sccm                                               
flow rate of H.sub.2 gas                                                  
                     250 sccm                                             
flow rate of PH.sub.3 gas                                                 
                     21 sccm                                              
(diluted by H.sub.2 gas to 3000 ppm)                                      
inner pressure       1.0 Torr                                             
high frequency power 53 W (13.56 MHz)                                     
______________________________________                                    
 
    
     
                       TABLE 20                                                    
______________________________________                                    
target material      GaAs polycrystal wafer                               
substrate temperature                                                     
                     220° C.                                       
flow rate of Ar gas  60 sccm                                              
flow rate of SiH.sub.4 gas                                                
                     7 sccm                                               
(diluted by Ar gas to 1000 ppm)                                           
inner pressure       4 mTorr                                              
high frequency power 360 W (13.56 MHz)                                    
______________________________________                                    
 
    
     
                       TABLE 21                                                    
______________________________________                                    
substrate temperature                                                     
                    220° C.                                        
flow rate of Si.sub.2 H.sub.6 gas                                         
                    14 sccm                                               
flow rate of H.sub.2 gas                                                  
                    200 sccm                                              
inner pressure      1.3 Torr                                              
high frequency power                                                      
                    36 W (13.56 MHz)                                      
______________________________________                                    
 
    
     
                       TABLE 22                                                    
______________________________________                                    
substrate temperature                                                     
                    220° C.                                        
flow rate of Si.sub.2 H.sub.6 gas                                         
                    10 sccm                                               
flow rate of GeH.sub.4 gas                                                
                    5 sccm                                                
flow rate of H.sub.2 gas                                                  
                    350 sccm                                              
inner pressure      1.4 Torr                                              
high frequency power                                                      
                    30 W (13.56 MHz)                                      
______________________________________                                    
 
    
     
                       TABLE 23                                                    
______________________________________                                    
substrate temperature                                                     
                    220° C.                                        
flow rate of SiH.sub.4 gas                                                
                    60 sccm                                               
flow rate of CH.sub.4 gas                                                 
                    4 sccm                                                
flow rate of H.sub.2 gas                                                  
                    330 sccm                                              
inner pressure      0.7 Torr                                              
high frequency power                                                      
                    40 W (13.56 MHz)                                      
______________________________________                                    
 
    
     
                       TABLE 24                                                    
______________________________________                                    
target material     Si single-crystal wafer                               
substrate temperature                                                     
                    220° C.                                        
flow rate of Ar gas 60 sccm                                               
flow rate of F.sub.2 gas                                                  
                    3 sccm                                                
inner pressure      4 mTorr                                               
high frequency power                                                      
                    360 W (13.56 MHz)                                     
______________________________________                                    
 
    
     
                       TABLE 25                                                    
______________________________________                                    
substrate temperature                                                     
                    220° C.                                        
flow rate of SiH.sub.4 gas                                                
                    40 sccm                                               
flow rate of GeH.sub.4 gas                                                
                    25 sccm                                               
flow rate of CH.sub.4 gas                                                 
                    7 sccm                                                
flow rate of H.sub.2 gas                                                  
                    250 sccm                                              
inner pressure      0.6 mTorr                                             
high frequency power                                                      
                    35 W (13.56 MHz)                                      
______________________________________                                    
 
    
     
                       TABLE 26                                                    
______________________________________                                    
target material    Si single-crystal wafer                                
substrate temperature                                                     
                   220° C.                                         
flow rate of Ar gas                                                       
                   25 sccm                                                
flow rate of H.sub.2 gas                                                  
                   50 sccm                                                
inner pressure     3 mTorr                                                
high frequency power                                                      
                   300 W (13.56 MHz)                                      
______________________________________                                    
 
    
     
                                           TABLE 27                                
__________________________________________________________________________
                                       open-circuit                       
                                              short-circuit               
                                                     output value under   
Ele-            characteristics of n-type AlP:H(F) film                   
                                       voltage under                      
                                              photocurrent                
                                                     irradiation of       
Ex-                                                                       
   ment                     average    irradiation of                     
                                              under irradia-              
                                                     AM-1 light (using    
am-                                                                       
   Sam-         hydrogen                                                  
                      fluorine                                            
                            crystal                                       
                                 composition                              
                                       AM-1 light                         
                                              tion of AM-1                
                                                     400 nm interference  
ple                                                                       
   ple                                                                    
      semiconductor                                                       
                content                                                   
                      content                                             
                            grain size                                    
                                 ratio of Al                              
                                       Voc    light  filter)              
No.                                                                       
   No.                                                                    
      layer     (atomic %)                                                
                      (atomic %)                                          
                            (Å)                                       
                                 to P  [Volt] Isc [mA/cm.sup.2 ]          
                                                     [relative            
__________________________________________________________________________
                                                     value]               
19 19 p-type A-Si:H:F                                                     
                4.2   1.1   350  49:51 0.94   16.9   1.4                  
      i-type A-Si:H:F                                                     
      n-type AlP:H:F                                                      
20 20 p-type A-SiC:H:F                                                    
                4.1   1.1   350  51:49 0.99   17.8   1.8                  
      i-type A-Si:H:F                                                     
      n-type AlP:H:F                                                      
21 21 p-type ZnTe                                                         
                4.2   1.0   350  50:50 0.91   16.8   1.4                  
      i-type A-Si:H:F                                                     
      n-type AlP:H:F                                                      
22 22 p-type AlP                                                          
                4.2   1.1   350  50:50 0.93   17.0   1.6                  
      i-type A-A-Si:H:F                                                   
      n-type AlP:H:F                                                      
__________________________________________________________________________
 
    
     
                       TABLE 28                                                    
______________________________________                                    
target material      ZnTe polycrystal wafer                               
substrate temperature                                                     
                     220° C.                                       
flow rate of Ar gas  80 sccm                                              
flow rate of PH.sub.3 gas                                                 
                     16 sccm                                              
(diluted by Ar gas to 2000 ppm)                                           
inner pressure       3 mTorr                                              
high frequency power 350 W (13.56 MHz)                                    
______________________________________                                    
 
    
     
                       TABLE 29                                                    
______________________________________                                    
target material    AlP polycrystal wafer                                  
substrate temperature                                                     
                   220° C.                                         
flow rate of Ar gas                                                       
                   60 sccm                                                
flow rate of Ar gas                                                       
                   5 sccm                                                 
for bubbling Zn(CH.sub.3).sub.2                                           
inner pressure     4 mTorr                                                
high frequency power                                                      
                   350 W (13.56 MHz)                                      
______________________________________                                    
 
    
     
                                           TABLE 30                                
__________________________________________________________________________
                           open-circuit                                   
                                   short-circuit                          
                                           ratio of change in the         
                           voltage under                                  
                                   photocurrent                           
                                           photoelectric conver-          
                           irradiation of                                 
                                   under irradia-                         
                                           sion efficiency after          
                           AM-1 light                                     
                                   tion of AM-1                           
                                           10 hours irradiation           
                 semiconductor                                            
                           Voc     light   of AM-1 light                  
                 layer     [Volt]  Isc [mM/cm.sup.2 ]                     
                                           [[Δη/η %]        
__________________________________________________________________________
Example No. 23                                                            
         third layer                                                      
                 p-type AlP:H:F                                           
                           2.72    12.0    2.1                            
.                i-type A-SiC:H:F                                         
Element Sample   n-type A-Si:H:F                                          
No. 23   second layer                                                     
                 p-type AlP:H:F                                           
                 i-type A-Si:H:F                                          
                 n-type A-Si:H:F                                          
         first layer                                                      
                 p-type AlP:H:F                                           
                 i-type A-SiGe:H:F                                        
                 n-type A-Si:H:F                                          
Comparative                                                               
         third layer                                                      
                 p-type A-Si:H:F                                          
                           2.45    12.3    3.4                            
example No. 5    i-type A-Si:H:F                                          
.                n-type A-Si:H:F                                          
Element Sample                                                            
         second layer                                                     
                 p-type AlP:H:F                                           
No. 31           i-type A-Si:H:F                                          
                 n-type A-Si:H:F                                          
         first layer                                                      
                 p-type AlP:H:F                                           
                 i-type A-SiGe:H:F                                        
                 n-type A-Si:H:F                                          
__________________________________________________________________________
 
    
     
                                           TABLE 31                                
__________________________________________________________________________
Com-                                   open-circuit                       
                                              short-circuit               
                                                     output value under   
para-                                                                     
    Ele-       characteristics of p-type AlP:H(F) film                    
                                       voltage under                      
                                              photocurrent                
                                                     irradiation of       
tive                                                                      
    ment                   average     irradiation of                     
                                              under irradia-              
                                                     AM-1 light (using    
Exam-                                                                     
    Sam-       hydrogen                                                   
                     fluorine                                             
                           crystal                                        
                                 composition                              
                                       AM-1 light                         
                                              tion of AM-1                
                                                     400 nm interference  
ple ple                                                                   
       semiconductor                                                      
               content                                                    
                     content                                              
                           grain size                                     
                                 ratio of Al                              
                                       Voc    light  filter)              
No. No.                                                                   
       layer   (atomic %)                                                 
                     (atomic %)                                           
                           (Å)                                        
                                 to P  [Volt] Isc [mA/cm.sup.2 ]          
                                                     [relative            
__________________________________________________________________________
                                                     value]               
1   24 p-type A-Si:H:F                                                    
                     --    --    --    0.76   14.1   1.0                  
       i-type A-Si:H:F                                                    
       n-type A-Si:H:F                                                    
2   25 p-type AlP:F                                                       
               --    7.2   --    31:69 0.32   5.8    0.09                 
       i-type A-Si:H:F                                                    
       n-type A-Si:H:F                                                    
    26 p-type AlP:H:F                                                     
               0.3   4.8   --    42:58 0.49   10.0   0.40                 
       i-type A-Si:H:F                                                    
       n-type A-Si:H:F                                                    
3   27 p-type AlP:H:F                                                     
               3.0   4.0   300   33:67 0.63   12.0   0.72                 
       i-type A-Si:H:F                                                    
       n-type A-Si:H:F                                                    
4   28 p-type AlP:H:F                                                     
               4.4   1.3   450   49:51 0.16   2.4    0.04                 
       i-type A-Si                                                        
       n-type A-Si:H:F                                                    
    29 p-type AlP:H:F                                                     
               4.6   1.2   450   49:51 0.04   0.9    0.01                 
       i-type A-SiC                                                       
       n-type A-Si:H:F                                                    
    30 p-type AlP:H:F                                                     
               4.3   1.3   450   50:50 0.05   1.5    0.02                 
       i-type A-SiGe                                                      
       n-type A-Si:H:F                                                    
__________________________________________________________________________
 
    
     
                       TABLE 32                                                    
______________________________________                                    
            Element Sample No.                                            
conditions    28        29         30                                     
______________________________________                                    
target material                                                           
              Si        SiC        SiGe                                   
              polycrystal                                                 
                        polycrystal                                       
                                   polycrystal                            
              wafer     wafer      wafer                                  
substrate temperature                                                     
              220° C.                                              
                        220° C.                                    
                                   220° C.                         
flow rate of Ar gas                                                       
              30 sccm   30 sccm    30 sccm                                
inner pressure                                                            
              4 mTorr   4 mTorr    4 mTorr                                
high frequency power                                                      
              320 W     320 W      320 W                                  
(13.56 MHz)                                                               
______________________________________