High temperature compressor oil
FIELD OF THE INVENTION 
     The invention relates to a synthetic lubricating oil composition. The invention also relates to lubricating oil comprising antioxidants and rust inhibitors. The invention particularly relates to lubricating oils which are free of sulfur, phosphorous and metals. 
     DESCRIPTION OF OTHER RELATED METHODS IN THE FIELD 
     Lubricating oils are characterized by resistance to oxidation and corrosion inhibition. Typical compressor lubricants include amino, phenolic and other antioxidants. Amino and phenolic antioxidants contain no sulfur and phosphorous, while dithiocarbamates, zinc dialkyldithiophosphates and many other antioxidants contain sulphur, phosphorous and metals such as zinc. Phosphates, phosphites and essentially all extreme pressure and antiwear additives contain sulfur and/or phosphorous. A variety of components may be used to provide rust protection, corrosion protection and metal passivation. Since lubricating oils used in gas compressors, such as in the manufacture of ethylene oxide and propylene oxide are subject to unique conditions of operation, special attention must be directed to the problems encountered by the inevitable contacting of process streams with these lubricating oils. The effect these lubricating oils have on the process will be determined by the formulation which will contain anti-wear additives, oxidation inhibitors, demulsifying agents, rust-inhibitors, etc. 
     In particular, it has been found that conventional rust-inhibited and oxidation stabilized compressor lubricants are unsuitable in the manufacture of ethylene oxide and propylene oxide. Conventional lubricants contain sulfur, phosphorous and metal salt additives to improve their operating properties. The smallest amounts of these additives finding their way into the process have been found to poison oxidation catalysts, shortening the run length. 
     There is a need in the art for a compressor lubricant which is rust-inhibited and oxidation stable and provides good lubricity at high temperatures in the absence of sulfur, phosphorous and metals such as zinc. 
     SUMMARY OF THE INVENTION 
     The invention is a lubricating oil composition comprising a major proportion of a synthetic base lubricating oil. Incorporated in minor proportion are an additive solubilizer, an antioxidant and a rust inhibitor/metal passivator. 
     The additive solubilizer is an ester synthetic lubricating oil incorporated in an additive solubilizing amount of at least 5 wt %. The antioxidant comprises 0.1 to 3 wt % of phenolic and/or amino antioxidants. The rust inhibitor/metal passivator comprises 0.01 to 0.5 wt % of triazole and/or alkenyl succinic acid rust inhibitors. 
     The lubricating oil composition is characterized as free of sulfur, phosphorous and metals. This is particularly beneficial in the use of the oil to lubricate gas compressors used in the manufacture of chemicals. 
    
    
     DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     Compressor lubricants must protect rotating bearing and/or sliding screws, pistons, crankcase components and other parts. Depending on the compressor design and type, high temperatures may be generated from adiabatic compression or friction of moving parts. Adequate thermal and oxidative stability is therefore a requirement for compressor lubricants. Rust and oxidation inhibited lubricants also provide rust protection, corrosion protection and metal passivation. Antiwear protection is sometimes needed. 
     Typical base fluids for compressor lubricants include mineral oils and a variety of synthetic base fluids. Mineral oil products are cost effective for applications where excellent high temperature stability is not required. Mineral oils may be processed to reduce sulfur content but generally will contain residual sulfur in amounts of 0.1 to 0.5 wt %. For this reason, synthetic base lubricating oils are used in the instant composition because they are free of residual sulfur. Synthetic base lubricating oils may include polyalphaolefin (PAO) oils, ester (diester and polyolester) oils, polyalkylene glycol oils or mixtures having a kinematic viscosity of 2 cSt to 10 cSt at 100° C. These synthetic base oils are inherently free of sulfur, phosphorus and metals. 
     Polyalphaolefin oils are prepared by the oligomerization of 1-decene or other lower olefin to produce high viscosity index lubricant range hydrocarbons in the C 20  to C 60  range. Other lower olefin polymers include polypropylene, polybutylenes, propylene-butylene copolymers, chlorinated polybutylenes, poly(1-hexenes), poly(1-octenes), alkylbenzenes (e.g., dodecylbenzenes, tetradecylbenzenes, dinonylbenzenes, di(2-ethylhexyl)benzenes); polyphenyls (e.g., biphenyls, terphenyls, alkylated polyphenols); and alkylated diphenyl ethers and the derivatives, analogs and homologs thereof. 
     Polyalkyleneglycol oils are prepared by polymerization of alkylene oxide polymers and interpolymers and derivatives wherein the terminal hydroxyl groups have been modified by esterification, etherification, etc. Examples include polyoxyalkylene polymers prepared by polymerization of ethylene oxide or propylene oxide, the alkyl and aryl ethers of these polyoxyalkylene polymers (e.g., methyl-polyisopropylene glycol ether having an average molecular weight of 1000, diphenyl ether of polyethylene glycol having a molecular weight of 500-1000, diethyl ether of polypropylene glycol having a molecular weight of 1000-1500); and mono- and polycarboxylic esters thereof, for example, the acetic acid esters, mixed C 3  -C 8  fatty acid esters and C 13  Oxo acid diester of tetraethylene glycol. 
     The ester oil serves as the solubilizing medium between the synthetic lubricating base oil and the additive composition. Ester oil may comprise an aliphatic diester of an aliphatic dicarboxylic acid. These include esters of phthalic acid, succinic acid, alkyl succinic acids and alkenyl succinic acids, maleic acid, azelaic acid, suberic acid, sebasic acid, fumaric acid, adipic acid, linoleic acid dimer, malonic acid, alkylmalonic acids, alkenyl malonic acids with a variety of alcohols (e.g., butyl alcohol, hexyl alcohol, dodecyl alcohol, 2-ethylhexyl alcohol, ethylene glycol, diethylene glycol monoether, propylene glycol). Specific examples of these esters include dibutyl adipate, di(2-ethylhexyl)sebacate, di-n-hexyl fumarate, dioctyl sebacate, diisooctyl azelate, diisodecyl azelate, dioctyl phthalate, didecyl phthalate, dieicosyl sebacate, the 2-ethylhexyl diester of linoleic acid dimer, and the complex ester formed by reacting 1 mole of sebacic acid with two moles of tetraethylene glycol and 2 moles of 2-ethylhexanoic acid. 
     Esters useful as synthetic oils also include those made from C 5  to C 12  monocarboxylic acids and polyols and polyol esters such as neopentyl glycol, trimethylolpropane, pentaerythritol, dipentaerythritol and tripentaerythritol. 
     The additive composition comprises an antioxidant comprising a phenolic antioxidant, an amino antioxidant and mixtures thereof. 
     Phenols which are useful for this purpose include various alkylated phenols, hindered phenols and phenol derivatives such as t-butyl hydroquinone, butylated hydroxyanisole, polybutylated bisphenol A, butylated hydroxy toluene, alkylated hydroquinone, 2,5-ditert-aryl hydroquinone 2,6-ditert-butyl-para-cresol, 2,2&#39;-methylenebis(6-tert-butyl-p-cresol); 1,5-naphthalenediol; 4,4&#39;-thiobis(t-tert-butyl-m-cresol); p,p-biphenol; butylated hydroxy toluene; 4,4&#39;-butylidenebis(6-tert-butyl-m-cresol); 4-methoxy-2,6-di-tert-butyl phenol; and the like. 
     Amino antioxidants include aldehyde amines, ketone amines, ketone-diarylamines, alkylated diphenylamines, phenylenediamines and the phenolic amines. 
     The additive composition comprises a rust inhibitor/metal passivator. These are selected from triazole derivatives and alkenyl succinic acid esters which are known for this purpose. 
     Triazole derivatives may be the reaction product of a substantially aliphatic, substantially saturated hydrocarbon substituted carboxylic acid wherein the hydrocarbon group contains at least about 20 aliphatic carbons, with an aminoguanidine derivative of the formula: ##STR1## wherein R 1  is hydrogen or a C 1  to C 15  hydrocarbyl radical, and R 2  and R 3  are independently hydrogen or a C 1  to C 20  hydrocarbyl radical, or salts thereof. Reaction is with reactants and under conditions to form a hydrocarbon substituted 1,2,4-triazole, preferably the 1,2,4-triazole-3-amine. 
     Suitable triazoles also include tolyltriazole, benzotriazole and aminotriazole. 
     The alkenyl succinic acid or anhydride structural unit employable in the instant invention is represented by the formula: ##STR2## in which R is an alkenyl group having from 10 to 35 carbon atoms. Preferably R is an alkenyl group having 14 to 20 carbon atoms. Examples of suitable alkenyl groups include decenyl, dodecenyl, tetradecenyl, octadecenyl and tricosenyl. For the purposes of this invention the alkenyl succinic acid and the alkenyl succinic anhydride function as reaction equivalents, that is, the same products are formed with either the acid or anhydride reactant. 
     Either one or both of the carboxyl functionalities is esterified, preferably with an amino alcohol represented by the formula: 
     
         H.sub.2 N(CH.sub.2).sub.n OH 
    
     in which n is an integer from 2 to 6. Preferably n is an integer from 2 to 5 and more preferably an integer from 2 to 3. Examples of suitable alkanolamine reactants are monoethanolamine, 1,2-propanolamine, 1,3-propanolamine, 1,2-butanolamine, 1,3-butanolamine and 1,4-butanolamine. 
     Examples of succinamic acid products are 
     N-(2-hydroxyethyl)-n-tetradecenyl succinamic acid, 
     N-(3-hydroxypropyl)-n-tetradecenyl succinamic acid, 
     N-(2-hydroxypropyl)-n-tetradecenyl succinamic acid, 
     N-(4-hydroxybutyl)-n-dodecenyl succinamic acid, 
     N-(3-hydroxybutyl)-n-octadecenyl succinamic acid, 
     N-(2-hydroxybutyl)-n-dodecenyl succinamic acid, 
     N-(2-hydroxyethyl)-n-decenyl succinamic acid, and 
     N-(2-hydroxyethyl)-n-octadecenyl succinamic acid. 
     Examples of the succinimide products are 
     N-(2-hydroxyethyl)-n-tetradecenyl succinimide, 
     N-(2-hydroxypropyl)-n-tetradecenyl succinimide, 
     N-(3-hydroxypropyl)-n-tetradecenyl succinimide, 
     N-(4-hydroxybutyl)-n-dodecenyl succinimide, 
     N-(2-hydroxybutyl)-n-octadecenyl succinimide, 
     N-(2-hydroxyethyl)-n-octadecenyl succinimide, and 
     N-(2-hydroxyalkyl)-n-tricosenyl succinimide. 
     Examples of succinamide products are 
     N,N&#39;-di(2-hydroxyethyl)-n-tetradecenyl succinamide, 
     N,N&#39;-di(2-hydroxypropyl)-n-tetradecenyl succinamide, 
     N,N&#39;-di(2-hydroxypropyl)-n-tetradecenyl succinamide, 
     N,N&#39;-(3-hydroxypropyl)-n-tetradecenyl succinamide, 
     N,N&#39;-di(4-hydroxybutyl)-n-dodecenyl succinamide, and 
     N,N&#39;-di(2-hydroxybutyl)-n-octadecenyl succinamide. 
     The alkenyl succinic acid (anhydride) and alkanolamine reaction products are described in U.S. Pat. No. 4,505,832 to Whiteman et al. incorporated herein by reference. 
     The lubricating compositions are formulated by methods well-known in the art. That is, the formulation is carried out continuously at the cannery. In the alternative, the compositions can be formulated in a semi works by hand. The additive composition substituents are weighed individually on a scale and added to an amount of ester oil in a steam jacketed stainless steel kettle at ambient temperature to 120° F., with stirring. When a homogeneous mixture is achieved, the base lubricating is added gradually, with continuous stirring. The result is the final lubricating oil composition. This composition is canned and shipped to point of use. At the point of use, the crankcase of a gas compressor is drained and then refilled with the lubricating oil composition of the invention. 
     This invention is shown by way of example. 
     Four lubricating oils were formulated according to the invention to replace a commercial mineral oil. The compositions and test results follow: 
     
         ______________________________________                                    
                   Weight                                                 
Formulation          1       2                                            
______________________________________                                    
Regal R&amp;O 68 (mineral oil)   100                                          
6 cSt PAO            37.95                                                
8 cSt PAO            40.95                                                
TMP Ester w. C.sub.8 -C.sub.10 acids                                      
                     20.0                                                 
Phenolic antioxidant 0.5                                                  
Octylbutylphenylamine antioxidant                                         
                     0.5                                                  
Alkenyl succinic acid half ester                                          
                     0.05                                                 
Triazole derivative  0.05                                                 
Test                 Test Results                                         
Viscosity, cSt @ 40° C.                                            
                     31.9    34.21                                        
Viscosity, cSt @ 100° C.                                           
                     5.98    5.73                                         
Viscosity Index      135     107                                          
Rotary Bomb Oxidation Test, Min.                                          
                     600+    600+                                         
PDSC Temp. Prog., Ext. Onset, °C.                                  
                     227     236                                          
PDSC Isothermal, 180° C., EO, Min.                                 
                     20      14                                           
SSW Rust Test        Pass    Pass                                         
Copper Strip Corrosion                                                    
                     1A      1B                                           
4-Ball Wear, mm      0.48    0.53                                         
Wear Index           18      15                                           
Weld Point, kg       126     126                                          
Formulation          3       4       5                                    
______________________________________                                    
6 cSt PAO            37.9    34.0    37.4                                 
8 cSt PAO            40.9    59.8    40.4                                 
TMP Ester w. C.sub.8 -C.sub.10 acids                                      
                     20.0    --      20                                   
Adipate ester w. C.sub.10 alcohols                                        
                      --     5.0     --                                   
Phenolic antioxidant 0.5     0.5     1.0                                  
Octylbutylphenylamine antioxidant                                         
                     0.5     0.5     1.0                                  
Alkenyl succinic acid half ester                                          
                     0.1     0.1     0.1                                  
Triazole derivative  0.1     0.1     0.1                                  
                   Test Results                                           
Test                 3       4       5                                    
______________________________________                                    
Viscosity, cSt @ 40° C.                                            
                     32.7    36.6    32.6                                 
Viscosity, cSt @ 100° C.                                           
                     6.06    6.62    6.0                                  
Viscosity Index      134     138     133                                  
Rotary Bomb Oxidation Test, Min.                                          
                     600+    600+    1000+                                
PDSC Onset Temp., °C.                                              
                     226     227     232                                  
PDSC Onset Time @ 180° C., Min.                                    
                     18      21      28                                   
SSW Rust Test        Pass    Pass    Pass                                 
Copper Strip Corrosion                                                    
                     1A      1B      1B                                   
4-Ball Wear          0.48    0.44    0.46                                 
Load Wear Index      22      18      18                                   
Weld Point, kg       126     126     126                                  
______________________________________                                    
TABLE OF MATERIALS                                                        
Vanlube 848                                                               
          Octylbutylphenylamine                                           
                             R. T.                                        
                             Vanderbilt                                   
IRGANOX ®                                                             
          Phenolic antioxidant                                            
                             Ciba-Giegy                                   
L-130                                                                     
Reocor 12 Alkenyl succinic acid half ester                                
                             Ciba-Giegy                                   
Reomet 39 Triazole derivative                                             
                             Ciba-Giegy                                   
Mobil SHF-61                                                              
          6 cst PAO          Mobil Chemical                               
Mobil SHF-82                                                              
          8 cst PAO          Mobil Chemical                               
Mobil P-43                                                                
          TMP ester w. C.sub.8 -C.sub.10 acids                            
                             Mobil Chemical                               
Mobil DB-31                                                               
          Adipate ester w. C.sub.10 alcohols                              
                             Mobil Chemical                               
          (Decyl adipate).                                                
Regal R&amp;O 68                                                              
          Also ISO 68, premium grade                                      
                             Texaco                                       
          oil formulated to meet the                                      
          lubrication requirements of                                     
          steam and gas turbines,                                         
          hydraulic systems and air                                       
          compressors. It is                                              
          formulated with high quality                                    
          solvent refined paraffin                                        
          base stocks and contains a                                      
          balanced rust and oxidation                                     
          inhibitor package and an                                        
          anti-foamant.                                                   
______________________________________                                    
 
    
     
         ______________________________________                                    
TABLE OF TEST METHODS                                                     
______________________________________                                    
4-Ball Wear, wear scar                                                    
                ASTM D-2266                                               
diameter, mm.                                                             
(54° C.; 1800 rpm, 20 kg.)                                         
Copper Strip Corrosion                                                    
                ASTM D-4048                                               
4-Ball EP       ASTM D-2596                                               
Load Wear Index ASTM D-2783                                               
Weld Point      ASTM D-2783                                               
SSW Rust Test   ASTM D-665B                                               
Rotary Bomb Oxidation Test                                                
                ASTM D-2272                                               
PDSC Onset Temp., °C.                                              
                Extrapolated Oxidation Onset                              
                Temperature in Temperature                                
                Programmed Pressure Differential                          
                Scanning Calorimetry with a                               
                10° C./min temperature increase                    
                in a 500 psig oxygen atmosphere.                          
PDSC Onset Time, Min.                                                     
                Extrapolated Oxidation Onset Time                         
                in Isothermal Pressure Differential                       
                Scanning Calorimetry with a                               
                180° C. Temperature (after a                       
                40° C./min heat up) in a 500                       
                psig oxygen atmosphere.                                   
______________________________________                                    
 
    
     While particular embodiments of the invention have been described, it will be understood, of course, that the invention is not limited thereto since many modifications may be made, and it is, therefore, contemplated to cover by the appended claims any such modification as fall within the true spirit and scope of the invention.