Heimd-containing polyetheramine curative for flexible, toughened products
CROSS-REFERENCE 
     This application is related to U.S. application Ser. No. 07/928,582, filed of even date. 
     BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     This invention relates to polyetherdiamines and, more particularly, this invention relates to novel curing compositions comprising aminated, alkoxylated derivatives of hydroxyalkyl-2-imidazolidones, prepared as described in copending application Ser. No. 07/928,582 incorporated herein by reference in its entirety. The hydroxyalkyl-2-imidazolidone initiator is reacted with an alkylene oxide and the resulting polyol subsequently undergoes reductive amination. 
     These novel polyetherdiamines, termed HEIMD-containing polyetheramines, exhibit improved elastomeric properties and can be used alone or combined with known polyoxyalkyleneamine curing agents and reacted with multifunctional epoxy resins to produce systems which possess a level of flexibility and toughness not usually achieved. Due to the unique structure of these amines, which contain cyclic urea, cured systems are more resistant to impact and are more extensible than are systems cured with blends of other polyetheramines of equivalent weight. 
     2. Related Art 
     It is known in the art that compounds with primary and secondary amine functions can be used as reactive hardeners in epoxy resin formulations employed for protective coatings, electrical embodiments, adhesives, etc. Many of the known polyethylenediamines have been used for such applications. Grayson et al., ed., Kirk-Othmer Encyclopedia of Chemical Technology, Third Edition, Vol 7, p. 593. 
     It is also known in the art that the utility of the polyethylenepolyamines as curing agents or hardeners for epoxy resin compositions can be extended through the use of numerous derivatives. For example, hydroxy-substituted amines can be prepared by the reaction of a pclyethylenepolyamine with ethylene oxide or propylene oxide. Cyancethylated polyethylenepolyamines represent another useful class cf derivatives. 
     Substituted imidazolines prepared by the condensation of polyethylenepolyamines with carboxylic acids or carboxylic acid derivatives have also been employed as epoxy curing agents. These curing agents are proposed for use in aqueous emulsion systems and to provide coatings with improved hydrolytic stability. 
     Polyethylenepolyamines can be condensed with di- and trifunctional fatty carboxylic acids obtained from the thermal polymerization of vegetable oil fatty acids to produce liquid, reactive polyamide resins. Various polyethylenepolyamines may be used in the preparation of polyamides, which may be characterized as low molecular weight, highly branched, highly viscous polymers with high amine functionality. The liquid polyamides often provide substantial improvements in flexibility of cured composites, leading to higher impact resistance and flexural strength. 
     Other derivatives of polyethylenepolyamines can be prepared by reaction with α,β-unsaturated esters to reduce viscosities. Viscosity reduction can also be effected by blending the polyamides with the higher polyethylenepolyamines. 
     Other derivatives are prepared by reacting polyethylenepolyamines with an aliphatic, hydroxyl-containing carboxylic acid, with tall oil fatty acids and with keto-acids. 
     The products of polyethylenepolyamines and aromatic monoisocyanates, lower aliphatic aldehydes, epoxidized fatty nitriles and propylene sulfide are also useful as epoxy curing agents. 
     There is always a need in the field of epoxy curing agent for compounds which provide improvements in toughness (resistance to impact) and flexibility (elongation) of cured compositions, as measured by tests which are well-known in the art. 
     It would represent a substantial advance in the art if a curing agent were commercially available which had distinct, measurable improvements in strength properties, i.e., resistance to impact and elongation. 
     It would also be very useful in the art if such a curing agent could be used alone or blended with other curing agents in a predictable way to modify properties of cured systems. 
     SUMMARY OF THE INVENTION 
     In accordance with the foregoing the present invention is directed to an epoxy resin curative which comprises an aminated, alkoxylated derivative of 1-2&#39;-hydroxyethyl-2-imidazolidone. The amine is represented by the formula: ##STR2## wherein R is H or an alkyl group of from 1 to 16 carbon atoms, and a+b=n, wherein n is from about 2 to 80. These HEIMD-containing polyetheramines are prepared as described in copending Ser. No. 07/928,582. 
     The HEIMD-containing polyetheramines may be reacted with multifunctional epoxy resins to produce materials having a degree of toughness and flexibility substantially improved over anything available in the art. 
     The level of toughness and flexibility developed in systems using these HEIMD derivatives has previously been quite difficult to attain. The significant improvements are believed to be due in part to the unique structure of these compounds, which comprises the incorporation of the cyclic urea group(s). Systems cured with these aminated alkoxylated HEIMDs are more resistant to impact and more extensible than are systems cured with blends of polyetheramines of equivalent weight as will be demonstrated in the examples. They are also efficient modifiers of less flexible epoxy systems. 
     These HEIMD-containing polyetheramine curatives will provide many new possibilities in epoxy, polyurea RIM and polyamide applications. 
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT 
     In the instant invention it has been discovered that the aminated alkoxylated 1-2&#39;-hydroxyethyl-2-imidazolidone (HEIMD) derivatives having the structure identified in FIG. have properties which make them particularly valuable as curing agents. 
     They can be used in epoxy resin compositions, such as films, castings, adhesives, etc., comprising a vicinal polyepoxide having an epoxide equivalency greater than about 1.8 and a curing amount of a curing agent such as the HEIMD amine curing agent of this invention. 
     These HEIMD amine derivatives may be used as the sole epoxy curative or blended with other known curatives, such as, for example, polyoxyalkyleneamines to modify resin properties. 
     As mentioned above, the aminated, alkoxylated derivative of HEIMD may be used as a curing agent alone or in combination with a polyoxyalkyleneamine, for example, including, but not limited to polyoxyalkylenediamines of the JEFFAMINE® D-series as exemplified by the structural formula: ##STR3## where x is a number from about 2 to 35 and includes, for example, JEFFAMINE® D-230, JEFFAMINE® D-400 and JEFFAMINE® D-2000. The HEIMD derivative may also be used in combination with a polyoxyalkylenediamine of the EDR-series represented by the formula: 
     
         H.sub.2 N--CH.sub.2 CH.sub.2( --O--CH.sub.2 CH.sub.2)n --NH.sub.2 
    
     where n=2 or 3, represented by JEFFAMINE® EDR-148 or EDR-192. 
     Generally, the JEFFAMINE® polyoxyalkylenepolyamines employed in conjunction with the curing agents of this invention will have molecular weights of about 148 or more and, preferably will have molecular weights ranging from about 230 to about 2000. All of the above JEFFAMINE® products are marketed by the Texaco Chemical Company, Houston, Tex. 
     The HEIMD-containing polyetheramines can be combined, not only with polyoxyalkyleneamines such as those of the JEFFAMINE® series mentioned above, but with a variety of commercially available amines. Suitable examples are ethyleneamines, including, but not limited to diethylenetriamines, triethylenetetramine, etc., and aromatic or cycloaliphatic amines and catalytic amines such as imidazoles. 
     Examples 2, 2a, 2b, 2c, 3 and 3a compare properties of systems cured with the HEIMD-containing polyetheramine with properties of systems cured with JEFFAMINE® amines or blends of commercially available amines. The data confirms significant improvements in strength and flexibility. 
     When the curing agent comprises a blend of the HEIMD-containing polyetheramine of this invention and another polyoxyalkylenepolyamine, usually the polyetherdiamine will comprise from about 15 to about 100 wt% of the compound with the balance being the polyoxyalkylenepolyamine. 
     Generally, the amine-cured vicinal polyepoxide-containing compositions are organic materials having an average of at least 1.8 reactive 1,2-epoxy groups per molecule. These polyepoxide materials can be monomeric or polymeric, saturated or unsaturated, aliphatic, cycloaliphatic, aromatic or heterocyclic, and may be substituted if desired with other substituents besides the epoxy groups, e.g., hydroxyl groups, ether radicals, aromatic halogen atoms and the like. These vicinal polyepoxide-containing compounds typically are of an epoxy equivalent weight (EEW) of 150 to 250. Preferably the base resin, which has an epoxy equivalent weight of from 175 to 195, is derived from condensing epichlorohydrin with 4,4&#39;-isopropylidenediphenol or 2,2-bis(p-hydroxyphenyl)propane to form 2,2-bis(p-2,3 epoxy propoxyphenyl)propane, a derivative of Bisphenol A. 
     Preferred polyepoxides are those of glycidyl ethers prepared by epoxidizing the corresponding allyl ethers or reacting, by known procedures, a molar excess of epichlorohydrin and an aromatic polyhydroxy compound; i.e., isopropylidene bisphenol, novolak, resorcinol, etc. The epoxy derivatives of ethylene or isopropylidene bisphenols are especially preferred. 
     A widely-used class of polyepoxides which are useful according to the instant invention includes the resinous epoxy polyethers obtained by reacting an epihalohydrin, such as epichlorohydrin, etc., with either a polyhydric phenol or a polyhydric alcohol. An illustrative, but by no means exhaustive, listing of suitable dihydric phenols includes 4,4&#39;-isopropylidene bisphenol, 2,4&#39;-dihydroxydiphenylethylmethane, 3,3&#39;-dihydroxydiphenyldiethylmethane, 3,4&#39;-diphenylmethylpropylmethane, etc. 
     Among the polyhydric alcohols which can be coreacted with an epihalohydrin to provide these resinous epoxy polyethers are such compounds as ethylene glycol, propylene glycols, butylene glycols, pentane diols, bis(4-hydroxycyclohexyl)dimethylmethane, 1,4-dimethylolbenzene, glycerol, 1,2,6-hexanetriol, trimethylolpropane, mannitol, sorbitol, erythritol, pentaerythritol, their dimers, trimers and higher polymers, e.g., polyethylene glycols, polypropylene glycols, triglycerol, dipentaerythritol and the like, polyallyl alcohol, polyhydric thioethers, etc. 
     An epoxy resin which may be cured by the process of this invention, the use of which is demonstrated in Examples 1-6, is one prepared, for example, by the reaction of Bisphenol A with epichlorohydrin in the presence of sodium hydroxide. After condensation is complete, the crude resin is freed of residual epichlorohydrin, washed well to remove salt and soluble by-products and recovered. Among those which have been employed to demonstrate the effectiveness of the instant invention are diglycidyl ethers of Bisphenol A, such as liquid epoxy resin which has a molecular weight of approximately 380, a functionality of approximately 2, and an equivalent weight of approximately 185-192. 
     Optionally, the epoxy resin formulations of the instant invention can include an &#34;accelerator&#34; to speed the amine cure of the epoxy resin, especially at ambient temperatures. In several applications, such acceleration is beneficial, especially when an epoxy resin is used as an adhesive in a flammable environment, thus making elevated temperature cure inconvenient or even hazardous. Lee, H. and Neville, K., HANDBOOK OF EPOXY RESINS, pp. 7-14, describes the use of certain amine-containing compounds as epoxy curing agent accelerators. 
     Many accelerators are known in the art which can be utilized in accordance with the instant invention. Examples include salts of phenols, salicylic acids, amine salts of fatty acids, such as those disclosed in U.S. Pat. No. 2,681,901, and tertiary amines such as those disclosed in U.S. Pat. No. 2,839,480, incorporated herein by reference. 
     It will further be realized that various conveniently employed additives can be admixed with the polyepoxide-containing composition of the instant invention prior to final cure. For example, in certain instances it may be desirable to add minor amounts of hardeners along with various other accelerators and curing agent systems well-known in the art. Additionally, conventional pigments, dyes, fillers, flame-retarding agents and the like which are compatible and natural or synthetic resins can be added. 
     The preparation of a cured epoxy resin is carried out in the following manner: 
     Epoxy resin is normally used without dilution and without other additives. 
     A solvent may be used where components are very viscous. 
     To a component containing the epoxy resin is added an equivalent amount of HEIMD-containing polyetherdiamine alone or in combination with a polyoxyalkylenediamine. The mixture is then mixed, degassed and poured into molds. 
     The HEIMD-containing polyetherdiamines or blends, where mixed with other amine curatives, should be present in the epoxy resin in an amount sufficient to provide about 0.8 to 1.2 amino (NH 2 ) groups per oxirane group of the epoxy resin. 
     In the various Examples the following terms are used to describe properties measured: 
     HDT--(ASTM D648-72) Heat distortion temperature is the temperature at which a polymer sample distorts under load upon heating under specified conditions. HDTs can also be used to indicate the degree of cross-linking or extent of cure of an epoxy resin. 
     Shore D hardness--(ASTM D-2240-81) Measured at 0 and at 10 seconds indentation hardness with durometer. 
     Izod impact strength (ft-lb/in) (ASTM D256-81)--Izod impact testing is carried out with the pendulum-type device where the test specimen is positioned as a cantilever beam with the notched side facing the striker. Five samples are tested for impact with each formulation with the average being recorded as IZOD impact strength. 
     Tensile Strength, psi (ASTM D638-80)--The rupture strength (stress/strain product at break) per unit area of material subjected to a specified dynamic load. &#34;Ultimate tensile strength&#34; is the force, at break, when a sample is pulled apart. 
     Tensile Modulus, psi--Stress/strain 
     Flexural Strength, psi (ASTM D790-80)--A measure of the ability of a material to withstand failure due to bending. ##EQU1## 
     Elongated at break, % 
     All parts are measured by weight. 
    
    
     It is understood the following examples are only intended to illustrate the invention and that the invention is not meant to be limited thereby. 
     EXAMPLE 1 
     
         __________________________________________________________________________
Properties of Epoxy Resin Systems Cured with Various Aminated             
Alkoxylated 1-2&#39;-Hydroxyethyl-2-Imidazolidones (HEIMD)                    
Formulation       6913-31A                                                
                       6913-31B                                           
                             6913-31A                                     
                                  6913-76C                                
__________________________________________________________________________
Liquid epoxy resin (EEW 185-192)                                          
                  100  100   100  100                                     
Aminated alkoxylated HEIMD                                                
                  73   --    --   --                                      
4 EO/2 PRO; eq. wt. ˜135                                            
Aminated propoxylated HEIMD                                               
                  --   57    --   --                                      
5 PRO; eq. wt. ˜105                                                 
Aminated propoxylated HEIMD                                               
                  --   --    92   --                                      
10 PRO; eq. wt. ˜170                                                
Aminated alkoxylated HEIMD                                                
                  --   --    --   100                                     
10 EO/3 PRO; eq. wt. ˜185                                           
Properties: Cured 1/8-inch Castings                                       
cured: 2 hours 80°, 3 hours 125° C.                         
Shore D hardness, 0-10 sec.                                               
                  65-46                                                   
                       85-83 72-60                                        
                                  38-25                                   
HDT, °C., 264 psi                                                  
                  22.1 68.8  26.2 --                                      
Izod impact strength, ft-lb/in                                            
                  13.5 2.2   11.6 --                                      
Tensile strength, psi                                                     
                  730  9500  1420 430                                     
Tensile modulus, psi                                                      
                  2730 460000                                             
                             46100                                        
                                  --                                      
Elongation at break, %                                                    
                  163  7.1   140  71                                      
Flexural strength, psi                                                    
                  97   16300 230  --                                      
Flexural modulus, psi                                                     
                  1420 448000                                             
                             1420 --                                      
__________________________________________________________________________
 
    
     Comments: Variations in structure and molecular weight of the subject polyetheramines result in cured epoxy resin systems with quite variable physical properties. An epoxy resin cured with any of the subject polyetheramines developed variable properties dependent largely on amine molecular weight. Properties varied in the degree of flexibility and resistance to applied tensile and flexural forces. A degree of toughness (resistance to impact) and flexibility (elongation; modulus) that are not normally achieved with epoxy systems were demonstrated with several of the subject polyetheramine cured systems. EO represents ethylene oxide and PRO represents propylene oxide. The polyetheramine prepared solely from propylene oxide (6913-31B), although of higher equivalent weight than an amine containing both propylene and ethylene oxide (6913-31A), produced a cured resin with considerably higher modulus, indicating that better physical properties might be expected with polyetheramines prepared solely from propylene oxide rather than those containing both propylene and ethylene oxide. 
     EXAMPLE 2 
     
         __________________________________________________________________________
Comparison of Properties: Epoxy Resin Systems Cured with Aminated         
Alkoxylated 1-2&#39;-                                                         
Hydroxyethyl-2-Imidazolidone (HEIMD) vs. Commercial Polyetheramine        
Formulation                  6913-94A                                     
                                   6914-32C                               
__________________________________________________________________________
Liquid epoxy resin (EEW 185-192)                                          
                             100   100                                    
Aminated propoxylated HEIMD.sup.1) 5 PRO; eq. wt. ˜105              
                             57    --                                     
JEFFAMINE ® D-400.sup.2) Eq. wt. ˜102                           
                             --    55                                     
Properties:                                                               
          Cured 1/8-inch Castings                                         
cured:    2 hours 80°, 3 hours 125° C.                      
Shore D hardness, 0-10 sec.  85-83 81-79                                  
HDT, °C., 264 psi     68.8  42.2                                   
Izod impact strength, ft-lb/in                                            
                             2.2   1.1                                    
Tensile strength, psi        9500  7500                                   
Tensile modulus, psi         460000                                       
                                   479000                                 
Elongation at break, %       7.1   4.1                                    
Flexural strength, psi       16300 13400                                  
Flexural modulus, psi        448000                                       
                                   434000                                 
% wt gain,                                                                
24-hr water boil             4.3   3.0                                    
3-hr acetone boil            9.6   31.3                                   
__________________________________________________________________________
 ##STR4##                                                                 
 .sup.2) Structure: H.sub.2 NCH(CH.sub.3)CH.sub.2 [OCH.sub.2              
 CH(CH.sub.3)].sub.x NH.sub.2 (x = 5.6)                                   
 
    
     Comments: Comparison of physical properties obtained on curing with the HEIMD-containing polyetheramine and a polyetheramine of quite similar equivalent weight, JEFFAMINE D-400, are shown. Cured properties obtained with the HEIMD-containing amine are clearly superior in a number of significant properties. HDT, impact, tensile and flexural strength and elongation values were higher for the HEIMD-containing polyether. The system cured with the HEIMD-amine was slightly less resistant to boiling water but was considerably improved in resistance to boiling acetone, a measure of solvent or chemical resistance. These improvements in properties also were noted in systems cured with variable amounts of curative. Results are shown in Examples 2a.-2c. 
     EXAMPLE 2a 
     
         ______________________________________                                    
Heat Deflection Temperature vs. Stoichiometry: HEIMD                      
Amine vs. JEFFAMINE ® D-400 (AHEW˜102-105)                      
             Percent of Stoichiometry                                     
             80    90     100     110  120                                
______________________________________                                    
Amin. propoxyl. HEIMD                                                     
               53.2    61.8   68.0  63.3 55.0                             
(5 PRO; eq. wt ˜105)                                                
JEFFAMINE D-400                                                           
               27.6    35.3   42.2  44.1 39.6                             
(eq. wt. ˜102)                                                      
______________________________________                                    
 
    
     Comments. The HEIMD-containing polyetheramine as an epoxy resin curative, provided cured systems over a wide concentration range that were considerably improved in heat resistance over those cured with a commercial polyetheramine. 
     EXAMPLE 2b 
     
         ______________________________________                                    
Tensile Strength vs. Stoichiometry: HEIMD                                 
Amine vs. JEFFAMINE ® D-400 (AHEW˜102-105)                      
             Percent of Stoichiometry                                     
             80    90      100    110  120                                
______________________________________                                    
Amin. propoxyl. HEIMD                                                     
               10150   10100   9600 9300 9000                             
(5 PRO; eq. wt ˜105)                                                
JEFFAMINE D-400                                                           
                2100    5900   7500 6900 6300                             
(eq. wt. ˜102)                                                      
______________________________________                                    
 
    
     Comment: Systems cured with HEIMD-containing amine exhibited considerably higher tensile strength over a wide concentration range than did a similar commercial polyetheramine. 
     EXAMPLE 2c 
     
         ______________________________________                                    
Solvent Resistance.sup.1) vs. Stoichiometry: HEIMD                        
Amine vs. JEFFAMINE ® D-400 (AHEW˜102-105)                      
             Percent of Stoichiometry                                     
             80    90     100     110  120                                
______________________________________                                    
Amin. propoxyl. HEIMD                                                     
               28.47   15.03   9.38 10.67                                 
                                         16.00                            
(5 PRO; eq. wt ˜105)                                                
JEFFAMINE D-400                                                           
               56.62   46.26  31.31 23.32                                 
                                         27.68                            
(eq. wt. ˜102)                                                      
______________________________________                                    
 .sup.1) Measured by weight gain of 2.5 × 0.5 × 0.125 in.     
 samples after boiling in acetone for three hours.                        
 
    
     Comment: The epoxy resin system cured with HEIMD-containing polyetheramine was considerably more resistant to attack by boiling acetone than were formulations cured with a commercial polyetheramine. This was shown throughout a wide curative concentration range. 
     EXAMPLE 3 
     
         ______________________________________                                    
Comparison of Properties: Epoxy Resin Systems Cured with                  
Aminated Alkoxylated 1-2&#39;-Hydroxyethyl-2-Imidazolidones                   
(HEIMD) vs. Commercial Polyetheramine Blend                               
Formulation           6913-59A  6913-60A                                  
______________________________________                                    
Liquid epoxy resin (EEW 185-192)                                          
                      100       100                                       
Aminated alkoxylated HEIMD                                                
                      92        --                                        
10 PRO; eq. wt. ˜170                                                
JEFFAMINE ® D-400/D-2000 Blend                                        
                      --        94                                        
50/50 pbw.; eq. wt. ˜174                                            
Properties: Cured 1/8-inch Castings                                       
cured: 2 hours 80°, 3 hours 125° C.                         
Shore D hardness, 0-10 sec.                                               
                      69-60     47-30                                     
HDT, °C., 264 psi                                                  
                      22.7      23.1                                      
Izod impact strength, ft-lb/in                                            
                      11.3      8.7                                       
Tensile strength, psi 1330      430                                       
Tensile modulus, psi  16700     1030                                      
Elongation at break, %                                                    
                      141       54.5                                      
Flexural strength, psi                                                    
                      350       120                                       
Flexural modulus, psi 29200     1480                                      
% wt gain, 24-hr water boil                                               
                      4.6       3.2                                       
       .sup. 3-hr acetone boil                                            
                      38.6      46.4                                      
Tear strength, pli    162       38                                        
______________________________________                                    
 
    
     Comment: When compared with a system cured with a blend of commercial polyetheramines (JEFFAMINE D-400/D-2000) of matching equivalent weight, the formulation cured with the HEIMD-containing polyetheramine was clearly superior in strength and flexibility. Higher impact strength, elongation and resistance to acetone boil (chemical resistance) were features of the HEIMD-amine cure. 
     EXAMPLE 3a 
     
         ______________________________________                                    
Total Impact Energy vs. Stoichiometry: HEIMD Amine                        
vs. JEFFAMINE ® D-400/D-2000 (AHEW˜102-105)                     
             Percent of Stoichiometry                                     
             80   90     100    110  120  130                             
______________________________________                                    
Amin. propoxyl. HEIMD                                                     
               152    166    180  192  174  136                           
(10 PRO; eq. wt ˜170)                                               
JEFFAMINE D-400/                                                          
                66    105    124  114  --   --                            
D-2000 blend (50/50                                                       
pbw; eq. wt. ˜174)                                                  
______________________________________                                    
 
    
     Comment: Values for total energy required for catastrophic failure as measured by the Dynatap falling dart impact test (ASTM D-3763) were considerably higher for the HEIMD-containing polyetheramine than for the system cured with a blend of commercial polyetheramines or equivalent weight. This is an indication of a higher degree of toughness of the system cured with the HEIMD-amine. Although values maximized at 100-110% of stoichiometry, impact values were quite high over the total range tested. 
     EXAMPLE 4 
     
         ______________________________________                                    
Properties of Epoxy Resin Systems Cured with HEIMD-                       
Containing Polyetheramine (AHEW.sup.1)˜108) and                     
JEFFAMINE ® D-400 (AHEW˜105)                                    
Formulation           6974 2C   6974-32C                                  
______________________________________                                    
Liquid epoxy resin (EEW 185-192)                                          
                      100       100                                       
Aminated propoxylated HEIMD                                               
                      57        --                                        
(5 PRO)                                                                   
JEFFAMINE ® D-400 --        55                                        
Properties: Cured 1/8-inch Castings                                       
cured: 2 hours 80°, 3 hours 125° C.                         
Shore D hardness, 0-10 sec.                                               
                      85-83     81-79                                     
HDT, °C., 264 psi                                                  
                      68.0      42.2                                      
Izod impact strength, ft-lb/in                                            
                      2.2       1.1                                       
Tensile strength, psi 9600      7500                                      
Tensile modulus, psi  460000    479000                                    
Elongation at break, %                                                    
                      8.0       4.1                                       
Flexural strength, psi                                                    
                      16600     13400                                     
Flexural modulus, psi 453000    434000                                    
% wt gain, 24-hr water boil                                               
                      4.3       3.0                                       
       .sup. 3-hr acetone boil                                            
                      9.4       31.3                                      
______________________________________                                    
 
    
     Comments: A stronger, more flexible cured epoxy system was prepared with the HEIMD-polyetheramine as curative than was possible with JEFFAMINE® D-400. Areas of considerable improvement were shown in heat resistance (HDT) and weight gain with boiling acetone (chemical resistance). The HEIMD-containing system was slightly more sensitive to moisture (weight gain with water boil) than was the formulation cured with JEFFAMINE® D-400. 
     EXAMPLE 5 
     
         ______________________________________                                    
Properties of Epoxy Resin System Cured with HEIMD-                        
Containing Polyetheramine (AHEW˜170), JEFFAMINE ®               
D-400/D-2000 Blend (AHEW˜174) and JEFFAMINE ®                   
DU-700 (AHEW˜219)                                                   
Formulation       6913-59A 6913-60A 6913-45A                              
______________________________________                                    
Liquid epoxy resin (EEW                                                   
                  100      100      100                                   
185-192)                                                                  
Aminated propoxylated HEIMD                                               
                  92       --       --                                    
(10 PRO)                                                                  
JEFFAMINE ® D-400/                                                    
                  --       94       --                                    
D-2000 Blend (50/50 pbw.)-                                                
JEFFAMINE ® DU-700                                                    
                  --       --       118.5                                 
Properties: Cured 1/8-inch                                                
Castings                                                                  
cured: 2 hours 80°, 3 hours 125° C.                         
Shore D hardness, 0-10 sec.                                               
                  69-60    47-30    63-47                                 
HDT, °C., 264 psi                                                  
                  22.7     23.1     --                                    
Izod impact strength, ft-lb/in                                            
                  11.3     8.7      --                                    
Tensile strength, psi                                                     
                  1330     430      780                                   
Tensile modulus, psi                                                      
                  16700    1030     5650                                  
Elongation at break, %                                                    
                  140.9    54.5     94.5                                  
Flexural strength, psi                                                    
                  350      120      --                                    
Flexural modulus, psi                                                     
                  29200    1480     --                                    
% wt gain, 24-hr water boil                                               
                  4.6      3.2      1.2                                   
       .sup. 3-hr acetone boil                                            
                  38.6     46.4     43.8                                  
Tear strength, pli                                                        
                  162      38       88                                    
______________________________________                                    
 
    
     Comments: When compared with a system cured with a blend of JEFFAMINE® D-400 and D-2000 of matching equivalent weight, the formulation cured with the HEIMD-containing polyetheramine was clearly superior in strength and flexibility. Higher impact strength, elongation and resistance to acetone boil (chemical resistance) were features of the HEIMD-amine cure. When compared to a product similar in structure JEFFAMINE® DU-700, again strength properties and elongation favor the HEIMD amine cured system. DU-700 is a type of urea condensate of a polyoxypropylenepolyamine. See Texaco Chemical Company New Product Development Bulletin NPD-005. DU-700 is known to develop tough, impact resistance cured systems.