Partially dehydrated vermiculite flakes and method of making same
BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     This invention relates to intumescent vermiculite flakes which resist combustion and expand when subjected to high temperatures and are suitable for mounting a monolithic catalytic element in the casing of a catalytic converter. This invention also relates to a method of making the intumescent vermiculite flakes. 
     2. Description of the Related Art 
     Intumescent minerals such as flakes of vermiculite ore resist combustion and expand when subjected to high temperatures, and are used in catalytic converter mountings, caulks and putties for fire barriers, and in high-temperature gaskets. In a catalytic converter, a monolithic catalytic element (usually ceramic and herein referred to as a &#34;monolith&#34;) can be mounted in a metallic casing by mounting material containing vermiculite flakes that expand when heated, thus compensating for the greater thermal expansion of a metallic casing as compared to a ceramic monolith. The mounting typically is in the form of a flexible mat which is wrapped around the monolith. The mat preferably incorporates inorganic fibrous material plus inorganic binder and/or organic binder which improves the integrity of the mat and thus makes it easier for the mat to be wound onto a monolith and to remain in place in the metallic casing. 
     Intumescent vermiculite mats are disclosed in co-assigned U.S. Pat. Nos. 3,916,057 (Hatch et al.) and U.K. Pat. No. 1,513,808 (issued Jun. 7, 1978). However, as is explained in co-assigned U.S. Pat. No. 4,305,992 (Langer et al.), the intumescent vermiculite has a region of negative expansion (contraction) between about 100° and 400° C. that can cause problems in each of the aforementioned uses. In a catalytic converter, this can cause the monolith to become loose from the casing during warm-up of the catalytic converter. To guard against such loosening, the initial expansion temperature of the intumescent vermiculite should be as low as possible, and the intumescent vermiculite should not experience any negative expansion. 
     The Langer patent subjects flakes of vermiculite ore to an ammonium cationic exchange, both to reduce the degree of negative expansion and to reduce the temperature at which the intumescent mats begin to expand. U S. Pat. No. 4,746,570 (Suzaki et al.) likewise subjects flakes of vermiculite ore to a cationic exchange plus a subsequent amine treatment in order to improve heat resistance and resiliency after repeated flexing at the high temperatures to which catalytic converters are subjected in use. 
     As explained in co-assigned U.S. Pat. No. 4,617,176 (Merry), pressure exerted against the monolith by intumescent vermiculite ore can be so high that, when combined with other factors, the monolith can experience &#34;ring-off&#34; cracks. In severe cases, the monolith is completely severed into two pieces. The Merry patent solves the ring-off problem by employing a flexible intumescent planar mat or sheet that is corrugated, i.e., it has a generally sinusoidal wave pattern along both its lengthwise edges, thus reducing forces exerted against the monolith. However, the corrugations of the intumescent sheet leave gaps that tend to allow heat to escape to the casing. 
     The Merry patent treats monolithic diesel particulate filters in the same manner as monolithic catalytic converters (herein, the term &#34;catalytic converter&#34; is meant to encompass monolithic diesel particulate filters). Like ordinary catalytic converters, many diesel monolithic particulate filters have a ceramic monolith mounted in a metallic casing, and the mounting can be a sheet of intumescent material. 
     In addition to the above-discussed problems, flakes of intumescent vermiculite ore experience greater expansion when first heated to high temperatures than in subsequent heating cycles. This thermal degradation results in gradually reduced holding forces at operating temperatures and, in mountings of catalytic converters, may also result in gradual erosion of the vermiculite by exhaust gases. 
     SUMMARY OF THE INVENTION 
     The invention provides intumescent vermiculite flakes that, when used in mounting a monolithic catalytic element in the casing of a catalytic converter, provides all the advantages of prior intumescent vermiculite materials, plus additional advantages including elimination of the ring-off problem and no significant reduction in expansion in the second cycle of thermal expansion as compared to the first thermal expansion. The novel intumescent vermiculite flakes are characterized by: 
     a) from about 1.0 to 3.2% by weight of &#34;chemically bound water,&#34; and 
     b) a uniform bulk density from about 0.2 to 0.9 g/cm 3 . 
     To determine the percentage of &#34;chemically bound water,&#34; the vermiculite flakes are heated to 100° C. to drive off free water and then to 900° C. while measuring the amount of water that evolves between 100° and 900° C. This measurement indicates the amount of &#34;chemically bound water.&#34; After being heated to 900° C., the vermiculite flakes may contain some water, but this has no practical significance when the vermiculite flakes are to be used in a catalytic converter, because they would rarely be exposed in such use to temperatures above 900° C. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     The invention may be more easily understood in reference to the drawings in which: 
     FIG. 1 is a plan view of a catalytic converter with half of its casing removed, showing a mounting based on intumescent vermiculite flakes of the invention; 
     FIG. 2 shows a thermal expansion curve of intumescent vermiculite flakes of the invention; and 
     FIG. 3 shows, for purposes of comparison, a thermal expansion curve of prior art vermiculite ore. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     The intumescent vermiculite flakes of the invention preferably are produced by partially dehydrating vermiculite ore at a temperature between 350° and 800° C., more preferably between 450° and 650° C. The partial dehydration is complete within three hours. The preferred percent of chemically bound water liberated in the process of heating to 900° C. is from about 1 to 3.2% by weight of the ore. Ore is herein defined as unexpanded vermiculite flakes. The most preferred is from about 1.5 to 3.2% by weight of the ore. The desired water content and bulk density can also be achieved by heating the flakes for shorter periods of time at somewhat higher temperatures up to about 1000° C., but this makes it more difficult to attain the precisely desired water content and bulk density. The intumescent vermiculite flakes of the invention can alternatively be produced by chemically treating vermiculite ore, e.g., with acids, to achieve the desired degree of partial dehydration. However, this method is not preferred due to the cost of the acid and waste disposal problems. 
     Preferably when heating to partially dehydrate the vermiculite ore, its normal volume expansion is restricted in order to produce flakes having a lower initial expansion temperature and also a higher bulk density. 
     The novel intumescent vermiculite flakes of the present invention, as compared to known intumescent vermiculite flakes, 
     1) have a substantially lower initial expansion temperature; 
     2) undergo substantially reduced or no negative expansion at moderately elevated temperatures; 
     3) when used in a catalytic converter mounting, exert adequate, lower holding forces at high operating temperatures (thus affording good support for a monolith without danger of ring-off cracking); and 
     4) experience substantially no thermal degradation when repeatedly heated to about 750° C. and cooled to room temperature, in contrast to significant thermal degradation experienced by known intumescent vermiculite flakes. 
     Preferably the bulk density of the intumescent vermiculite flakes of the invention is from about 0.2 to 0.9 g/cm 3 . Below this preferred range, the holding forces in a catalytic converter might be lower than required for some uses. A most preferred range is from about 0.5 to 0.9 g/cm 3 . At a bulk density substantially above about 0.9 g/cm 3 , the holding forces might produce ring-off cracks. If necessary, the bulk density of the partially dehydrated vermiculite flakes can be increased by calendering iso-static pressing, or other compressing means. 
     The intumescent vermiculite flakes of the invention have average particle sizes from about 0.05 to 5 mm. Flakes of substantially smaller average sizes might afford inferior holding forces in a catalytic converter. Flakes of substantially larger average particle sizes would be more difficult to cut cleanly to shapes useful for such purposes as mats for catalytic converters or as gaskets. Preferably, the average particle size of the novel flakes is from about 0.1 to 1.0 mm. 
     The novel intumescent vermiculite flakes can be converted into a flexible, coherent mat useful for mounting a monolith in a catalytic converter by standard papermaking techniques, preferably by employing from about 10 to 70% by weight of the vermiculite flakes, from about 25 to 85% by weight of inorganic fibrous material, and from about 2 to 20% by weight of organic and/or inorganic binder. Useful inorganic fibrous materials include alumina-silicate fibers commercially available under the tradenames &#34;Cerafiber&#34; from Manville Corporation, &#34;Kaowool&#34; from Thermal Ceramics, and &#34;Fiberfrax&#34; from Carborundum Company, soft glass fibers commercially available under the tradename &#34;E-glass&#34; from Manville Corporation, mineral wool, and refractory filaments such as zirconia-silica fibers and crystalline alumina whiskers. Suitable organic binders include rubber latexes such as natural rubber, styrene-butadiene, butadiene-acrylonitrile, acrylates, and methacrylates. Suitable inorganic binders include bentonite and colloidal silica. Small amounts of surfactants, foaming agents, and flocculating agents may also be used as necessary. 
     Instead of being used as a mat for mounting a monolith in a catalytic converter, the novel intumescent vermiculite flakes can be converted into a paste by admixture with water and clays, colloids, or thixotropic agents. The paste can be injected into the space between the monolith and the casing, thus assuring complete filling of that space as well as uniform mount density. However, a mat may be easier to produce because of problems encountered, such as holding and sealing of the paste during the injection. 
     In addition to being useful in mountings of catalytic converters, the novel intumescent vermiculite flakes can be put to other uses requiring a material that resists combustion and expands when subjected to high temperatures. For example, the novel intumescent vermiculite flakes can be used in caulks and putties for fire barriers, and may be superior to flakes of vermiculite ore in such use, in that the flakes of the instant invention begin to expand at lower temperatures and experience substantially reduced or no negative expansion at moderately elevated temperatures when compared to vermiculite ore flakes. Because of these improved properties, fire barriers based on the novel intumescent vermiculite flakes of the present invention, as compared to those based on flakes of vermiculite ore, may more quickly and surely seal off openings against the spread of a fire. When the novel intumescent vermiculite flakes are used in high-temperature gaskets, those improved properties can better assure against leakage of the gaskets at temperatures at which flakes of intumescent vermiculite ore experience negative expansion. 
     Testing 
     Bulk Density 
     Bulk volume measurements are performed by packing vermiculite flakes in a 100-ml graduated cylinder and tapping the cylinder on a hard surface 40-50 times before reading the volume. Bulk densities are calculated using bulk volume measurements. 
     Thermogravimetric Analysis to Determine Bound Water (TGA) 
     Using a sample of approximately 12 mg, TGA (plotting percent weight loss vs. temperature rise) is performed using a 1090B thermal analyzer and a 951 thermogravimetric analyzer, both from E. I. duPont. Chemically bound water is irreversibly lost in this test. 
     Thermal Expansion Test 
     This test uses a Theta Dilatronic II Thermal Analyzer, Model MFE-715. With 0.2 g of vermiculite flakes in a 7.2-mm-diameter quartz crucible in a furnace, an end of a 7.0-mm-diameter quartz rod rests on the vermiculite flakes under a 1350 g dead weight applying a force of 0.345 N/mm 2 . While recording the displacement of the rod as a function of vermiculite temperature using a pen writer, the temperature is increased 20° C. per minute from room temperature to about 750° C., and the furnace is allowed to cool to room temperature. From the heating portion of the first cycle, the &#34;% Expansion&#34; is calculated at various temperatures. 
     The sample then undergoes a second, identical heating cycle. When the maximum thermal expansion in the second cycle is less than that during the first cycle, this indicates that the vermiculite flakes have been thermally degraded. The degraded vermiculite flakes, when employed in a catalytic converter mounting, would exert gradually reduced holding forces at operating temperatures. 
     Push-out Force 
     To determine how securely a mounting holds a monolith in place in a catalytic converter, a mounting mat, cut to fit the monolith, is employed to mount a cylindrical ceramic monolith, 11.84 cm in diameter by 15.24 cm in length in a metal casing, 12.34 cm I. D. by 17.78 cm in length. The peak force required to move the monolith relative to the canister is measured at room temperature, 300° C., 600° C., and again after cooling to room temperature. The applied force is measured on an MTS tensile tester (MTS Systems Corp.). 
     DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     In FIG. 1, a catalytic converter 10 includes a metal casing 12, one half of which is shown. The casing has generally frusto-conical inlet and outlets 14 and 15, respectively. Disposed within the casing 12 is a monolithic catalytic element (or monolith) of a refractory material such as ceramic having internal gas flow channels (not shown). Wrapped around the monolith is a mat 18 containing intumescent vermiculite flakes. The mat 18 mounts the monolith snugly within the casing 12 and seals the space between the monolith and casing 12 to prevent exhaust from bypassing the monolith. 
     Curve 20 of FIG. 2 shows thermal expansion characteristics of intumescent vermiculite flakes of the present invention as described in Example 4 below; and curve 30 of FIG. 3 shows, for purposes of comparison, thermal expansion characteristics of the flakes of vermiculite ore of the prior art described in comparative Example A below. During the initial heat-up portion 32 of curve 30 of FIG. 3, negative expansion begins at about 175° C. and reaches -8% at point 33, i.e., at about 340° C. Upon being heated to 370° C., the expansion returns to zero, and continual heat-up produces a maximum expansion at about 750° C. (point 35). 
     The negative expansion is contrasted with curve 20 of FIG. 2, which shows no negative expansion. The initial heat-up portion 22 of curve 20 shows expansion beginning at about 235° C. In the second heat-up portion 24 of curve 20, the intumescent vermiculite flakes of the present invention reach the same maximum positive expansion at about 750° C. (point 26) as and the cooling portion 28 of curve 20 during the second cycle retraces that of the first cycle. 
     In the second heat-up portion 34 of curve 30 of FIG. 3, the vermiculite ore reaches a maximum positive expansion at point 36 which is appreciably reduced from the maximum attained in the first cycle (point 35), thus indicating thermal degradation. The cooling portion 38 of the second cycle of curve 30 lies well below the cooling portion 39 of the first cycle. 
     Testing various intumescent vermiculite flakes has demonstrated that whenever there is thermal degradation, it is most obvious in the second cycle. Testing of some partially dehydrated intumescent vermiculite flakes of the invention has shown progressively higher maximum thermal expansions at about 750° C. through the first few cycles and no reduction in expansion in any cycle as compared to earlier cycles, even when tested over 50 cycles. 
     In the following examples, all parts are given by weight. 
     EXAMPLES 1-8 
     Partially dehydrating vermiculite ore while restricting expansion 
     Several 2.4-mm vent holes were drilled through the 9-mm-thick wall and lid of a cylindrical stainless steel canister having internal dimensions of 5.4 cm long×5.7 cm diameter. A centrally placed thermocouple was wired through a vent. Into the cavity of this canister was placed vermiculite ore (VCX-104 from W. R. Grace Co.) in amounts between about 75% to 125% of its natural packing density (about 1.2 g/cm 3 ). The canister was closed and placed in an oven that was pre-heated to and maintained at a given temperature. The thermocouple reached that temperature after about 2.5 hours, and that temperature was maintained an additional half hour before removing the canister. After allowing it to cool to room temperature, the lid was detached to remove the resulting partially dehydrated intumescent vermiculite flakes. 
     EXAMPLES 9-14 
     Partially dehydrating vermiculite ore while allowing free expansion 
     About 75 g of loose vermiculite ore was held for three hours in a 250-ml porcelain crucible in an oven that had been pre-heated to and was maintained at a given temperature, thus producing partially dehydrated intumescent vermiculite flakes of the invention. A thermocouple had been centrally buried in the sample to record the highest temperature to which it was heated. 
     Table I reports in sequence for Examples 1-14  the highest temperature to which each was heated (&#34;Exposure Temp.&#34;), the &#34;Packing Density&#34; (Examples 1-8 only), and the &#34;Fired Bulk Density&#34; of the partially dehydrated vermiculite flakes. Table I next reports results of the Thermal Expansion Test, including the &#34;% Expansion&#34; at various temperatures and the temperatures at which the sample begins to expand (&#34;Begins&#34;) and at which its expansion is zero (&#34;0%&#34;). When the &#34;Begins&#34; and &#34;0%&#34; temperatures are equal, there is no negative expansion. Table I also reports under &#34;% Expansion&#34; the expansion of the sample in the second cycle of the Thermal Expansion Test at various temperatures. Desirably, the &#34;% Expansion&#34; in the second cycle is equal to or greater than that in the first cycle. 
     Comparative Examples A-B 
     Table I also reports testing of vermiculites that are representative of the prior art, namely, 
     
                                           TABLE I                                 
__________________________________________________________________________
               Fired                                                      
Exposure  Packing                                                         
               Bulk                         Expansion                     
Temp.     Density                                                         
               Density                                                    
                    % Expansion at °C.                             
                                            Temp (°C.)             
Example                                                                   
     (°C.)                                                         
          (g/cm)                                                          
               (g/cm)                                                     
                    100°                                           
                        200°                                       
                            300°                                   
                                400°                               
                                   500°                            
                                      600°                         
                                         700°                      
                                            Begins                        
                                                @ 0%                      
__________________________________________________________________________
1    300  1.11 1.10 -1.0                                                  
                        -5.9                                              
                            -6.9                                          
                                28.7                                      
                                   71.3                                   
                                      78.2                                
                                         82.2                             
                                            345 375                       
2    400  1.14 0.78 -0.9                                                  
                        -3.0                                              
                            -2.6                                          
                                6.0                                       
                                   34.5                                   
                                      45.7                                
                                         54.3                             
                                            285 345                       
3    478  1.08 0.66 0   -0.7                                              
                            2.6 8.1                                       
                                   14.1                                   
                                      19.6                                
                                         27.4                             
                                            235 260                       
4    581  1.20 0.62 0   0   2.2 6.7                                       
                                   9.6                                    
                                      12.2                                
                                         16.3                             
                                            235 235                       
                                         18.1*                            
5    703  1.09 0.63 0   0   2.0 4.3                                       
                                   5.8                                    
                                      7.1                                 
                                         8.6                              
                                            220 220                       
6    789  1.21 0.67 0   0   1.7 3.8                                       
                                   5.0                                    
                                      6.0                                 
                                         7.5                              
                                            215 215                       
7    585  0.90 0.56 0   0   1.5 5.3                                       
                                   7.0                                    
                                      9.0                                 
                                         13.0                             
                                            235 235                       
8    585  1.56 0.77 0   0   6.0 14.5                                      
                                   18.8                                   
                                      22.5                                
                                         27.8                             
                                            215 215                       
9    340  --   1.21 0   -0.5                                              
                            -0.5                                          
                                12.7                                      
                                   53.1                                   
                                      62.0                                
                                         66.2                             
                                            365 370                       
                                         56.8*                            
10   390  --   .45  0   -0.9                                              
                            -0.9                                          
                                0  12.9                                   
                                      22.4                                
                                         31.9                             
                                            365 400                       
                                         33.6*                            
11   437  --   .37  0   0   0   0.4                                       
                                   2.9                                    
                                      6.2                                 
                                         11.3                             
                                            350 385                       
                                         13.5*                            
12   490  --   .31  -0.3                                                  
                        -0.3                                              
                            -0.3                                          
                                0.2                                       
                                   1.0                                    
                                      3.6                                 
                                         5.1                              
                                            300 380                       
                                         6.3*                             
13   590  --   .25  0   -0.4                                              
                            -0.4                                          
                                0  0.7                                    
                                      0.8                                 
                                         1.4                              
                                            300 400                       
                                         2.1*                             
14   690  --   .25  0   0   0   0.3                                       
                                   0.6                                    
                                      0.6                                 
                                         0.6                              
                                            400 400                       
                                         0.0*                             
A                   -0.5                                                  
                        -6.1                                              
                            -8.3                                          
                                29.3                                      
                                   63.5                                   
                                      70.7                                
                                         74.0                             
                                            340 370                       
                                         64.1*                            
B                   -0.5                                                  
                        -2.1                                              
                            25.7                                          
                                50.8                                      
                                   63.9                                   
                                      71.2                                
                                         76.4                             
                                            265 275                       
__________________________________________________________________________
 A = VCX104 of W.R. Grace Co.                                             
 B = Example 1 of abovecited U.S. Pat. No. 4,305,992                      
 
    
     Table I illustrates, for Examples 1-8, that the exposure temperature for restricted expansion should be above about 450° C. to ensure low negative expansion and lower initial expansion temperature. Examples 4-8 show no negative expansion for exposure temperature above 478° C., which is desirable. Examples 9-14, for free expansion, illustrate that the exposure temperature should be about 400° to 600° C. to insure similar expansion properties as the restricted expansion samples. A negative thermal expansion of less than about 1% is preferred for most applications. Controls A and B illustrate expansion properties which are undesirable for mats encasing monolithic catalytic elements. 
     EXAMPLE 15 AND COMPARATIVE EXAMPLE C 
     Example 15 used a vermiculite ore which was partially dehydrated while restricting expansion as in Examples 1-8 except that the vermiculite ore was &#34;Strong-Lite,&#34; Micron Grade (0.1 to 0.6 mm) vermiculite from Strong-Lite Products Corp. The exposure temperature was 600° C., the packing density was 1.06 g/cm 3 , and the fired bulk density was 0.68 g/cm 3 . Testing of the resultant intumescent flakes of the invention is reported in Table II together with testing of the &#34;Strong-Lite&#34; ore (Comparative Example C). This demonstrates that the invention applies to alternate sources of ore. 
     
                       TABLE II                                                    
______________________________________                                    
                         Expansion                                        
Ex-                            Temp (°C.)                          
am-  % Expansion at °C. Be-    @                                   
ple  100°                                                          
            200°                                                   
                   300°                                            
                        400°                                       
                             500°                                  
                                  600°                             
                                        700°                       
                                             gins 0%                      
______________________________________                                    
15   0      -3.3   -4.0 -3.7 -2.6 -0.7  4.4  350  515                     
                                        7.4*                              
C    0      -0.8   -6.3 -6.7 -3.6 18.8  26.8 475  515                     
                                        18.8*                             
______________________________________                                    
 *Second heating cycle from 25° C. to 700° C.               
 
    
     It is evident that Example 15 had less negative expansion at low temperatures and did not expand as much at high temperatures as comparative Example C, which was not exposed to 600° C. to reduce the chemically bound water. 
     Table III reports testing for thermogravimetric analysis (TGA) of the partially dehydrated vermiculite flakes of each of Examples 1-6, 9-14, and Comparative Example A. 
     
                       TABLE III                                                   
______________________________________                                    
(Thermogravimetric Analysis (% weight loss @ °C.)                  
Ex-                                                                       
ample 100°                                                         
             200°                                                  
                    300°                                           
                         400°                                      
                              500°                                 
                                   600°                            
                                        700°                       
                                             800°                  
                                                  900°             
______________________________________                                    
1     3.2    3.8    3.9  4.0  4.1  4.2  4.7  5.4  7.0                     
2     0.8    1.0    1.2  1.3  1.3  1.5  2.0  2.6  4.0                     
3     0.3    0.3    0.3  0.3  0.3  0.4  0.7  1.3  2.8                     
4     0.0    0.0    0.0  0.0  0.1  0.0  0.3  0.7  2.0                     
5     0.0    0.0    0.0  0.0  0.0  0.0  0.0  0.3  1.6                     
6     0.0    0.0    0.0  0.0  0.0  0.0  0.0  0.0  1.1                     
9     1.2    1.5    1.5  1.6  1.8  2.0  2.4  3.0  4.0                     
10    0.8    1.0    1.2  1.2  1.2  1.2  1.5  2.0  3.2                     
11    0 7    0.7    0.7  0.7  0.8  1.2  1.4  1.9  2.8                     
12    0.7    0.7    0.7  0.7  0.7  0.8  1.1  1.7  3.1                     
13    0.2    0.2    0.2  0.2  0.2  0.2  0.3  0.8  2.2                     
14    0.2    0.2    0.2  0.2  0.2  0.2  0.3  0.7  1.7                     
A     4.8    6.0    6.5  6.8  6.9  7.2  7.7  8.2  9.6                     
______________________________________                                    
 
    
     Table III illustrates that flakes which have a zero percentage of weight loss at lower temperatures (such as Examples 4-6) do not exhibit negative expansion. Flakes with lower percentage of weight loss tend to have less negative expansion. Flakes having up to about 3.2% chemically bound water have substantially no negative expansion in the second cycle of the Thermal Expansion Test. 
     EXAMPLE 16 
     Use of partially dehydrated vermiculite flakes in a catalytic converter mounting 
     A mat was made by mixing 56 parts of the partially dehydrated vermiculite flakes of Example 4, 37 parts of alumina silica fibers, and 7 parts (dry weight) of acrylic latex binder together with a large volume of water, and forming this into a handsheet by a conventional paper-making technique. After being cut to a width of 15.24 cm, the handsheet was wound upon a ceramic monolith 11.84 cm in diameter by 15.24 cm in length and having 62 cells/cm 2 . The wrapped monolith was stuffed into a metallic canister of stainless steel with an I. D. of 12.34 cm. The mounted handsheet had a mount density of 1.0 g/cm 3 . 
     The resulting catalytic converter was connected to an exhaust gas simulator (made by RPS Engineering). This was run at an inlet gas temperature of 954° C. and a flow rate of 39.1 m 3  /hr at standard temperature and pressure. After ten minutes, the propane was shut off, and room air was introduced at 122.3 m 3  /hour at standard temperature and pressure until the canister temperature had dropped to about 38° C. Upon disassembly, no cracks were found in the monolith. 
     COMPARATIVE EXAMPLE D 
     A ceramic monolith was wrapped as in Example 16 except using as the mounting a commercial mat available under the tradename &#34;Interam,&#34; commercially available from Minnesota Mining and Manufacturing Company, employing intumescent vermiculite ore (again at a mount density of 1.0 g/cm 3 ), which is the mat which is currently being used for mounting monoliths in many catalytic converters. After being tested as in Example 16 and disassembled, the monolith was found to be in two pieces. 
     Samples of each of the mats of Example 16 and Comparative Example D were tested for &#34;Push-out Force&#34; at various mount densities and temperatures, with results reported in Table IV. 
     
                       TABLE IV                                                    
______________________________________                                    
Mount      Push-Out Force (Newtons)                                       
Ex-   Density  @ Room   @             Return to                           
ample (g/cm.sup.3)                                                        
               Temp.    300° C.                                    
                              @ 600° C.                            
                                      Room Temp.                          
______________________________________                                    
16    0.71     1260     2350   6140   1400                                
      0.79     2040     3520   7240   2800                                
      0.87     2860     5120  10550   4080                                
      0.95     3650     4900  12880   5220                                
      1.02     4770     6470  13320   5930                                
      1.10     6060     8110  18560   8410                                
D     0.72      240      90    9560   1920                                
      0.80      340      140  15130   2050                                
      0.88     2010      920  24000+  4810                                
      0.96     2700     1410  24000+  7420                                
      1.04     3080     1480  24000+  8540                                
______________________________________                                    
 Capacity of tester was 24,000 N                                          
 
    
     The values for Push-out Force reported in Table IV show that a mounting mat made using the partially dehydrated intumescent vermiculite flakes of the invention (versus the comparative mat at a comparable mount density) desirably exerts less force against the monolith at 600° C. (a typical operating temperature for a catalytic converter) and also desirably exerts greater forces both at room temperature and at 300° C. 
     In view of the foregoing description, it will be apparent that the invention is not limited to the specific details set forth herein for purposes of illustration, and that various other modifications are equivalent for the stated and illustrated functions without departing from the spirit of the invention and the scope thereof as defined in the appended claims.