Single package ambient curing polymers
FIELD OF THE INVENTION 
     The present invention relates to the preparation of aqueous-based polymers bearing reactive functional groups. More particularly, this invention relates to waterborne or water dispersed polymers that are equivalent in performance in applications formerly dominated by solvent based polymers. 
     Polymers of the present invention have many uses including adhesives, saturant applications, solutions or dispersions in water or water-cosolvent mixtures, and are most useful as coatings and sealants for wood, glass, metal, concrete and binders for mortars and non-wovens. 
     More specifically, surface coatings produced from polymers of the present invention exhibit improved properties such as, for example, durability, toughness, solvent resistance, dirt pickup resistance, print and block resistance and mar resistance. 
     BACKGROUND OF THE INVENTION 
     In applications where the development of a high degree of durability and toughness under ambient conditions-are important, polymers dispersed in organic solvent have traditionally been employed or used. Additionally, solvent based polymers allow the formulator to produce coatings with all the necessary formulation ingredients in a single package. However, more recently, solvent based coatings have come under extreme pressure because of health, safety and environmental concerns. In an attempt to address these concerns, formulators are demanding from raw material suppliers polymers which give equivalent performance with decreasing levels of volatile organic solvents. In response to health, safety and environmental concerns, formulators have increased their use of aqueous based polymers. 
     However, aqueous based polymers, when cured under ambient conditions, have inherent shortcomings with respect to durability and to toughness when compared to solvent based polymers. Consequently, waterborne coatings have not found wide acceptance in applications where strength and durability are important. Another shortcoming of aqueous based polymers is the need for multiple package systems for equivalent performance of solvent based systems. Multiple package systems require the end-user to mix at least two components prior to the coating application. However, there are instances where the use of multiple package systems are impractical and inconvenient. 
     What we have found to be novel and unanticipated is a waterborne or water dispersed polymer which cures at ambient temperature and can be formulated into a single package coating, and has the durability and toughness of solvent based polymer systems. This is accomplished by post-reacting an acetoacetoxy functional polymer with an amine-functional silane. 
     PRIOR RELATED ART 
     It is well known that incorporation of silane functionality into a polymer can yield compositions which can self-crosslink at about 25° Centigrade. Crosslinking occurs due to the facile hydrolysis of alkoxysilane groups to silanols and their subsequent condensation to form Si-O-Si linkages in the presence of water (See e.g., Feasibility of Using Alkoxy Silane Functional Monomers for the Development of Crosslinking Emulsions, T. R. Bourne, B. G. Bufkin, G. C. Wildman and J. R. Grave in the Journal of Coatings Technology, Vol. 54, No. 684, Jan. 1982). However, because of the ease of hydrolysis and subsequent condensation of the silane functionality, it is difficult to produce stable and useful silicone-modified waterborne polymers in a single package. This is particularly problematic for applications where high levels of crosslinking and therefore high levels of silane modification are required. 
     We have found that many of the problems associated with developing a single package, self-crosslinking waterborne polymer are avoided by the postreaction of an acetoacetoxy functional polymer with an amine functional silane. 
     Therefore, while it is generally known to modify the properties of polymers by incorporating functional groups, none of the related art discloses the preparation of polymers containing functional acetoacetate groups with post-polymerization reaction of the acetoacetate group with an amine functional silane. 
     European Patent Application EP 0 442 653 A2 discloses a process for the production of a polymer having desired functional group(s). The functional group(s) can be adhesion promoters, silicones, olefinically unsaturated groups, etc. The desired groups(s ) are incorporated into the composition by producing a precursor polymer having --NH-- and/or --NH2-bound functionality which is further reacted with a molecule which contains at least one enolic carbonyl capable of forming an enamine with the --NH-- or --NH2- functionality, and at least one of the desirable groups. Acetoacetoxy ethyl methacrylate is an example of a species which contains both the enolic carbonyl and a desirable, in this case, an olefinic unsaturation, group. The --NH-- and/or --NH2- functional precursor is produced, for example, from the reaction of a carboxylic acid functional polymer and an aziridine-containing species. 
     European Patent Application EP 0 483 583 A2 discloses a use for an aminosilane as a hardener or an acetoacetate and/or acetoacetamide functional polymer. Cure of this composition results from the hydrolysis and subsequent condensation of the alkoxy silane groups from the presence of water liberated during enamine formation from atmospheric moisture. This is a two package system in that the silane and acetoacetate functional polymer must be mixed or blended just prior to use. 
     Serial No. 091,489 (Rohm and Haas) discloses the functionalization of a polymer with various desirable groups such as adhesion promoters, steric stabilizers, etc., by reacting an enolic carbonyl containing precursor polymer with a species which contains at least one of the desired functional groups and at least one amine capable of forming an enamine with the enolic carbonyl. However, Serial No. 091,489 does not disclose the use of amino functional silanes. 
     SUMMARY OF THE INVENTION 
     The present invention provides a process for the polymerization of polymers containing functional acetoacetate groups and then following the polymerization post-reacting the acetoacetate functional polymer with an amino functional silane to produce self-crosslinking, ambient curing, film-forming polymers. 
     DETAILED DESCRIPTION 
     The present invention provides for self-crosslinking, ambient curing, aqueous-based, film-forming polymers containing functional acetoacetate groups which are post-reacted with an amino functional silane. 
     Coatings produced from polymers of the present invention exhibit improved properties such as solvent resistance, dirt pickup resistance, print and block resistance, mar resistance, adhesion and tensile properties, such as impact resistance, and tensile strength. 
     Polymers 
     The preferred polymers for use in this invention are vinyl polymers with pendant acetoacetate groups, alternately known as beta-ketoesters. The term &#34;pendant&#34; is used in the specification to mean &#34;attached to the polymer backbone and available for further reaction.&#34; Pendant should not be read in the strict sense which would exclude the attachment of such groups at the termini of a polymer chain. Thus, polymer having acetoacetate functionality introduced on the chain end by an acetoacetate functional mercaptan, as taught in U.S. Pat. No. 4,960,924, would be useful in this invention. Generally, the pendant acetoacetate groups are attached to the polymer backbone via an organic divalent radical R 1  which in turn is attached to the acetoacetate moiety or by a trivalent organic radical R 2  bearing two acetoacetate groups. ##STR1## 
     The acetoacetate functional polymers can be prepared by means known in the art. A preferred method is polymerization through incorporation, which includes an acetoacetate functional monomer. A preferred monomer is acetoacetoxyethyl methacrylate which is conveniently referred to throughout this specification as AAEM, shown below. ##STR2## 
     Examples of other monomers useful for introduction of acetoacetate functionality are acetoacetoxyethyl acrylate, acetoacetoxypropyl methacrylate, allyl acetoacetate, acetoacetoxybutyl methacrylate, 2,3-di(acetoacetoxy)propyl methacrylate, and the like. In general, any polymerizable hydroxy functional monomer can be converted to the corresponding acetoacetate by reaction with diketene or other suitable acetoacetylating agent (See e.g. Comparison of Methods for the Preparation of Acetoacetylated Coating Resins, Witzeman, J. S.; Dell Nottingham, W.; Del Rector, F. J. Coatings Technology; Vol. 62, 1990, 101. (and references contained therein)). 
     The vinyl polymers of this invention are most often copolymers of the acetoacetate functional monomer and other monomers. Examples of useful comonomers are simple olefins such as ethylene, alkyl acrylates and methacrylates where the alkyl group has 1 to 20 carbon atoms (more preferably 1 to 8 carbon atoms), vinyl acetate, acrylic acid, methacrylic acid, acrylonitrile, styrene, isobornyl methacrylate, acrylamide, hydroxyethyl acrylate and methacrylate, hydroxypropyl methacrylate and acrylate, N-vinyl pyrolidinone, butadiene, isoprene, vinyl halides such as vinyl chloride and vinylidene chloride, alkyl maleates, alkyl fumarates, fumaric acid, maleic acid, itaconic acid, and the like. It is also possible, and sometimes desirable, to include low levels of divinyl or polyvinyl monomers such as glycol polyacrylates, allyl methacrylate, divinyl benzene, and the like, to introduce a controlled amount of gel in the latex particle. It is important, however, to be sure that when this is done, the quality of the film formation is not seriously impaired. Additionally, one may wish to include chain transfer agents to control molecular weight of the polymer. 
     The acetoacetate functional polymer may contain from about 0.5 percent to 100 percent of the acetoacetate functional monomer by weight. In any application, the amount of acetoacetate functional monomer required will vary from case to case depending upon the desired degree of post functionalization necessary for the particular end-use application. Generally, however, the acetoacetate monomer concentration will be between 1 percent and 40 percent. Conventional coatings will usually contain from about 0.5 percent to 20 percent acetoacetate monomer by weight. Polymers having a molecular weight of from 1,000 to over one million can be used. The lower molecular weight polymers should contain a sufficiently high level of acetoacetate to maximize the degree of post functionalization. For example, a copolymer of AAEM having a molecular weight under 10,000 would typically contain 30 percent or more of AAEM. 
     Generally, the vinyl polymer is prepared as a dispersion or emulsion polymer in water by a suitable free radical initiated polymerization technique, using a free radical initiator and appropriate heating. Since a film-forming polymer is sometimes desired, useful emulsion polymers will generally have glass transition temperatures under 60 degrees Centigrade, since these polymers with coalescent will form good quality films at ambient temperatures. If soluble polymers are used in the film-formation process, polymers of higher glass transition temperature are readily used since they are film-forming. 
     In certain aspects of the invention, polymerization in an aqueous medium and, in particular, aqueous emulsion polymerization, is used to prepare the polymer. Conventional dispersants can-be used (e.g. anionic and/or nonionic emulsifiers such as alkali or ammonium alkyl sulfates, alkyl sulfonic acids, and fatty acids, oxyethylated alkyl phenyls, and the like). The amount of dispersant used is usually 0.1 percent to 6 percent by weight based on the weight of total monomer. Either thermal or redox initiation processes may be used. Conventional free radical initiators may be used (hydrogen peroxide, organic hydroperoxides such as t-butyl hydroperoxide, cumene hydroperoxide, t-amyl hydroperoxide, ammonium and/or alkali persulfates, organic peroxides such as t-butyl perpivalate, t-butyl perbenzoate, benzoyl peroxide, di(n-propyl) peroxydicarbonate, acetyl cyclo-hexylsulfonyl peroxide, and the like); typically 0.05 percent to 3.0 percent by weight based on the weight of total monomer. Redox systems using the same initiators coupled with a suitable reductant (for example: reducing sugars such as isoascorbic acid, sodium bisulfite, sodium thiosulfate, hydroxyl amine, hydrazine, sodium hydrosulfite) can be used at similar levels, oftentimes in conjunction with a metal catalyst such as salts of transition metals, examples of which are iron sulfate, copper sulfate, vanadium sulfate, and the like. Additionally, non-oxidizing thermal initiators such as 2,2&#39;-Azo-bis-isobutyronitrile, 4,4&#39;-Azo-bis(4-cyanopentanoic acid), 2,2&#39;-Azo-bis(2-amidinopropane) dihydrochloride, and the like. Frequently, a low level of chain transfer agent such as a mercaptan (for example: n-octyl mercaptan, n-dodecyl mercaptan, butyl or methyl mercaptopropionate, mercaptopropionic acid at 0.05 percent to 6 percent by weight based on total weight of monomer) is employed to control molecular weight. 
     The invention may also be practiced using a solvent-soluble or water-soluble polymer. When this is desired, the polymer may be prepared directly in water if the monomer mix is water-soluble or, as is most often the case, the polymerization solvent is a water miscible solvent such as isopropanol, butyl cellosolve, propylene glycol, and the like. In this case, water may be included in the polymerization mixture or post added after the polymerization is complete. In some cases, the polymer is prepared in a conventional organic solvent such as xylene, butyl acetate, methyl ethyl ketone, methyl tertiary butyl ether, and the like. When organic solvent is employed with or without water, it is convenient to use organic soluble-free radical initiators such as azo-bis-isobutyronitrile, t-butyl-peroctoate, or benzoyl peroxide and whatever heat is convenient to assure smooth copolymerization. Another route to preparation of a water-soluble polymer for this invention is to prepare a vinyl dispersion polymer having enough acrylic or methacrylic acid or other polymerizable acid monomer (usually greater than 10 percent) so that the emulsion polymer can be solubilized by addition of ammonia or other base. Watersoluble polymers of this type are advantageously used as blends with conventional dispersion polymers, preferably those which also have pendant acetoacetate functionality. The blend of alkali-soluble resin and latex polymer has a particularly advantageous property combination of gloss and rheology and is useful in coatings and printing ink applications. 
     In another embodiment of this invention, an aqueous dispersion contains copolymer particles made up of at least two mutually incompatible copolymers. These mutually incompatible copolymers may be present in the following morphological configurations, for example, core/shell, core/shell particles with shell phases incompletely encapsulating the core, core/shell particles with a multiplicity of cores, interpenetrating network particles, and the like. In all of these cases, the majority of the surface area of the particle will be occupied by at least one outer phase and the interior of the particle will be occupied by at least one inner phase. The mutual incompatibility of the two polymer compositions may be determined in various ways known in the art. The use of scanning electron microscopy using staining techniques to emphasize the difference between the appearance of the phases, for example, is such a technique. 
     The emulsion polymerization techniques used to prepare such dispersions are well known in the art. It is sometimes advantageous to introduce some crosslinking or gel structure by the sequential polymerization process in the core via low levels of a crosslinking monomer such as allyl methacrylate, diallylphthalate, diallyl maleate, butylene glycol dimethacrylate, divinyl benzene, triallyl isocyanurate, ethylene glycol diacrylate, and the like. The lightly crosslinked core does not adversely affect film formation and does in some cases result in better coatings, particularly when tile pendant acetoacetate is concentrated in the shell. 
     As indicated above, a major use for this technology is for functionalizing vinyl polymers dispersed or dissolved in aqueous solvents. Unfortunately, vinyl polymers containing pendant acetoacetate are prone to hydrolysis in water, particularly on heat aging. The hydrolysis occurs at nearly any pH and yields acetoacetic acid, ##STR3## which in turn decomposes to acetone and carbon dioxide. 
     In an earlier application, U.S. Ser. No. 632,302, the solution to this problem was provided by treating the aqueous acetoacetate polymer after preparation with one molar equivalent of ammonia or a primary amine such as ethanolamine, methyl amine, or isopropyl amine. As described in that application, typically, the polymer is neutralized to a basic pH with one of the aforementioned amines, preferably to a pH greater than 9. Under these conditions, the enamine is formed. The reaction to form the enamine is generally rapid with the rate of formation increasing with temperature. In general, enamine formation is complete within 8 hours. An alternative approach is to raise the pH to about 9, allow the system to equilibrate, and readjust the pH to about 9 to replace the amine consumed by enamine formation. The enamine is stable to hydrolysis at pH&#39;s typically greater than 7. 
     Another approach to preparation of vinyl polymers containing equivalent pendant enamine functionally is to use preformed enamine monomers derived from the appropriate amine and the acetoacetate monomer. In this case, the pH must be kept on the alkaline side during polymerization to avoid hydrolysis of the enamine back to the acetoacetate. 
     Amino Functional Silanes 
     Aminosilane-modified polymers of this invention are prepared by adding an effective amount of an aminosilane to a polymer having acetoacetate functionality introduced on the polymer chain by an acetoacetate functional monomer such as, for example, acetoacetoxy ethyl methacrylate. The quantity of aminosilane that is added to the polymer is a function of the acetoacetate functionality content of the polymer. As mentioned above, the level of acetoacetoxy functional monomer is generally from about 1 weight percent to about 40 weight percent, based on the weight of the polymer. The level of aminosilane to modify the polymer is from about 0.10 to about 1.0 moles of amine moiety to one mole of acetoacetoxy group. 
     If insufficient aminosilane is used in relation to the acetoacetate functional vinyl polymer, properties, such as, for example, solvent resistance, dirt pickup resistance, print and block resistance, and mar resistance of the dried coating may be compromised. Whereas, on the other hand, if the ratio of the moles of aminosilane to the moles of acetoacetate functionality is much greater than 1 of the vinyl polymer, coating properties such as film formation may become imparted do to excessive precrosslinking of the silicone groups. This may also lead to increased water sensitivity as well as discoloration of some substrates such as, for example, wooden substrates. 
     Aminosilanes of various molecular weights and structures may be used to modify the acetoacetate function polymer in practicing the invention. The general structure of the aminosilanes useful for the invention is 
     
         R.sub.1 --Si(R.sub.2).sub.3-n (OR.sub.3)n, 
    
     where n is the greater or equal to 1 but less than or equal to 3, R 1  is an alkyl or phenyl group or combinations thereof and contains at least one amine group capable of forming an enamine with the acetoacetoxy group, R 3  is alkyl, phenyl or hydrogen atom or combinations thereof, and R 2  is a hydrogen atom phenyl or alkyl group or combinations thereof. The group R 2  may also be oligomers of silane, which may or may not contain OR 3  groups and may or may not include amine functionality capable of undergoing enamine formation with acetoacetoxy groups. Preferably, however, the aminosilanes have an average molecular weight, as may be determined by gel permeation chromatography, of from about 140 to about 500, most preferably from about 150 to about 250. Practical considerations such as solubility, hydrolysis rate, compatibility with the acetoacetate precursor polymer, polymer stability, and the like, are the only limitations placed upon the structure and molecular weight of the aminosilane. Although for convenience purposes, it is most preferred that the molecular weight not exceed a maximum of about 190 to about 250, that n is equal to 1 or 2, that R 2  is a methyloxy or ethyloxy group and that R 1  is an alkyl group of 3 to 6 carbon atoms and contains no more than one amine group capable of forming an enamine with the acetoacetoxy group. 
     Amino silanes found to be effective modifiers of acetoacetate functional vinyl polymer polymers may be selected from the group consisting of trimethoxysilylpropyldiethylenetriamine, N-methylaminopropyltrimethoxysilane aminoethylaminopropylmethyldimethoxysilane, aminoethylaminopropyltrimethoxysilane (Dow Corning Z-6020), aminopropylmethyldimethoxysilane, aminopropyltrimethoxysilane, polymeric aminoalkylsilicone, aminoethylaminoethylaminopropyl-trimethoxysilane, N-methylaminopropyltrimethoxysilane, methylamino-propyltrimethoxysilane, aminopropylmethyldimethoxysilane, aminopropyltriethoxysilane, 4-aminobutyltriethoxysilane, oligomeric aminoalkylsilane and the like, which are available from Dow Corning, Midland, Mich., Union Carbide Specialty Chemicals Division, Danbury Connecticut and Huls of America, Piscataway, N.J., Wacker Silicones Corporation of Adrian, Mich. 
     In the practice of the invention, aminosilane-modified coatings are prepared by adding a specific quantity of aminosilane to acetoacetate functional vinyl polymer. The quantity of silane added should be in specific proportion, for reasons stated earlier, to the acetoacetate content of the polymer. The amino-functional silane is preferably added after the polymerization of the acetoacetate functional vinyl emulsion polymer. 
     In general, the aminosilane can be added directly to the acetoacetate functional precursor polymer. However, for optimum performance and processing of the final silicone-modified polymer, an auxiliary surfactant may be required. This is particularly true, for example, in some cases where the precursor polymer is produced by emulsion polymerization in this case, the surfactant can provide, for example, enhanced stability, as well as enhanced desirable properties such as mar resistance when used in conjunction with aminosilane. 
     The auxiliary surfactant can be added preferably before or after the addition of the aminosilane, or as part of the preparation of the precursor, as in the case, for example, of emulsion polymerization. 
     Surfactants may be characterized by their &#34;Hydrophilic-Lipophilic Balance&#34; (HLB) value. Surfactants with HLB values of less than 10 are considered to possess more lipophilic character, while surfactants with HLB values greater than 10 are considered to possess more hydrophilic character. In the context of the preferred surfactants, non-ionic surfactants with HLB values with more hydrophilic character, HLB&gt;(greater than) 10 are desirable. More preferably, the HLB value should be greater than 15. 
     Surfactant levels of up to 10 percent of the weight of the precursor can be used. The more preferable level of surfactant is between 3 percent and 6 percent of the weight of the precursor. The only limitations on the surfactant level are, for example, poor water resistance, instability, and the like. 
     Examples of surfactants which may be used in the practice of the present invention are selected from the group consisting of non-ionics, such as octylphenoxypolyethoxyethanols, nonylphenoxypolyethoxyethanols, polypropyloxyethoxy alcohols, and the like, and ionics, such as sodium lauryl sulfate, sodium stearate, and the like. 
     Additives 
     The acetoacetate functional vinyl polymer-modified with aminosilanes of this invention may be formulated for the chosen end use. Additives such as thickeners, dispersants, pigment, extenders, fillers, anti-freeze agents, plasticizers, adhesion promoters, coalescents, wetting agents, defoamers, colorants, nona-aldehyde based biocides, soaps and slip agents may be incorporated. 
     TEST METHODS 
     Evaluating the Performance of Clear Coatings Based on Silicon-Modified Lattices 
     Mar Resistance 
     This test is based on striking the coating at a shallow angle with a hard object; in the examples provided, the object was the fingernail of the individual performing the test. This test gives an indication of how the coating will resist marring, which leads to gloss reduction of the coating. 
     After the coating is applied to the substrate and allowed to cure, the coated substrate is placed on a solid surface such as a table top and struck with the operator&#39;s fingernail. The operator&#39;s fingernail is kept parallel to the coated surface and the impact angle is greater than 45° from the normal of the surface, to increase the likelihood of marking the coating. 
     When comparing coatings, it is important that the same operator perform the test. This test is designed to distinguish relative differences. 
     We used the following rating system: 
     
         ______________________________________                                    
Rating       Appearance                                                   
______________________________________                                    
1-Excellent  No perceptible marks                                         
3-Good       Marks which appear as thin scratches                         
5-Poor       Marks which are wide                                         
______________________________________                                    
 
    
     Black Heel Mark and Scuff Resistance 
     The method for determining black heel and scuff resistance is described in Chemical Specialty Manufacturers Association Bulletin No. 9-73, except commercially available rubber shoe heels were used in place of the recommended 2&#34; rubber cubes and the substrates were wood (maple) panels rather than vinyl tile. 
     We determined the percentage of the coated substrate area which was covered by black heel and scuff marks; this is conveniently performed with transparent graph paper. Black heel marks are an actual deposition of rubber onto or into the coating. Black heel marks can be temporary and may be removed with dry cheesecloth, for example, or with cheesecloth and an appropriate solvent such as odorless mineral spirits. 
     A scuff mark, on the other hand, results from a physical displacement of the coating and appears as an area of reduced gloss. Scuff and black heel marks can occur simultaneously at the point where the heel impacts the substrate; i.e., upon removal of a black heel mark, a scuff may be present. 
     Floor Wear Test 
     Coatings were applied to wood panels, and cured at 25° centigrade for a specific time prior to their placement in a heavily traveled corridor. The corridor used experienced foot traffic as well as wheeled traffic from maintenance carts, sample trays etc. The gloss at 60 and 20 degrees as well as scuffing and scratching before and after a sufficient exposure time were measured. 
     Black Mark Removal with a Dry Cloth 
     After the test panels were exposed to rubber heels as described above, the coatings were tested for ease of rubber mark removal with a dry cloth. Cheesecloth was rubbed over the black rubber marks with moderate pressure after which removal was rated as &#34;complete&#34; meaning all black rubber marks were removed; &#34;partial&#34; meaning less than all of the black rubber marks were removed; and &#34;none&#34; meaning all of the black rubber marks were present after wiping. 
     The following examples are provided to illustrate some embodiments of the invention. They should not be read as limiting the scope of the invention which is more fully described in the specification and claims. 
     Unless otherwise indicated, percentages are by weight based on the total solids. 
    
    
     EXAMPLES 
     Example I 
     Example I shows the enhancement of coating performance aminosilane modification brings to the AAEM containing latex. We also show the effect of aminosilane level and aminosilane type on coating performance. 
     Preparation of Precursor Latex 
     The details for the preparation of the precursor lattices I-A and I-B are described below. Both Precursors are identical in their preparation except the monomer acetoacetoxy ethyl methacrylate (AAEM) was omitted from I-B. Table I-A shows the composition of the precursors as well as some characteristics. 
     To a glass vessel add 121.3 g deionized water (DIW) and 6.1 g of ALIPAL CO436. To this 4.8 g of sodium lauryl sulphate followed by 326.3 g butyl acrylate (BA), 386.8 g methyl methacrylate (MMA), 7.25 allyl methacrylate (ALMA) and 3.65 g methacrylic acid was added and then stirred to emulsify. This is monomer emulsion 1 (ME-1). 
     To another glass vessel 260 g DIW and 14.2 g of ALlPAL CO436 was added. To this 380.9 g BA, 515 g MMA, 167.8 g AAEM and 27.5 g of MAA was added and then stirred to emulsify. This is monomer emulsion 2 (ME-2). 
     To a polymerization Vessel 1282.3 g DIW was charged under dry nitrogen followed by 18.6 g of ALIPAL CO436. This mixture was stirred and then heated to 85° C. Next, 100 g of ME-1 was added. Two minutes later, 3.6 g of sodium persulphate (SP) in DIW was added. After ten minutes, 7.2 g of sodium carbonate in DIW was added. Five minutes later, ME-1 was cofed with 0.90 g of SP in DIW over 90 minutes. After the addition of ME-1 was complete, the ME-1 vessel was rinsed with 40 g of DIW. The polymerization vessel was held at 85° C. for an additional 15 minutes. Next, the cofed of ME-2 was started with 0.90 g SP in DIW. This cofeed was carried over a 90 minute period. Following the addition of ME-2, the ME-2 vessel was rinsed with 40 g DIW. The polymerization vessel was held for 30 minutes at 85° C. 
     After the 30 minute hold at 85° C., the vessel was cooled to 55° C. and the monomers were &#34;chased&#34; by, in the order, 5 g of 0.15% FeSO4, 5 g of 1% versene and 0.5 g of 70% t-BHP all in DIW. After one minute, 0.30 g of isoascorbic acid in DIW was added. After an additional 30 minute hold at 55° C., 62.5 g of 28% aqueous ammonia was added. The resulting polymer was cooled to room temperature before modification with the aminosilane. 
     Precursors I-A and I-B are identical in their preparation, two-stage process, and composition except AAEM was omitted from I-B. 
     Preparation of Silicon-Modified Latex 
     Into a mixing vessel, precursor I-A, whose preparation is described above, was charged. With stirring, TRITON X405 (70%) was added to the stirring precursor over the course of about 5 minutes. Approximately 10 minutes after the X405 addition, the aminosilane was added drop-wise over the course of about 5 minutes. The mixture was allowed to stir for about one hour after the addition of the aminosilane was complete. The amounts of materials used are shown in Table I-2. The silane-modified latex was allowed to stand for about 16 hours before it was formulated into a sealer. 
     Preparation of Aqueous Wood Sealers Based on Silane-Modified Lattices 
     Table I-3 gives the sealer formulation used to evaluate compositions I-1 through I-9. A general formulation is shown as well as a specific example based on composition I4. To a mixing vessel, all materials except the latex were added. With stirring, the silane-modified latex was added and stirred for at least an additional hour and allowed to stand for at least 16 hours before use. 
     Testing of Sealers Based on Compositions I-1 to I-9 
     To maple wood panels, 3 coats of sealers based on compositions I-1 to I-9 were applied with about one to two hours between coats. After the final coat, the sealed panels were allowed to cure at 25° C. for 72 hours before testing. The test results are displayed in Table I-4. 
     
                       TABLE I-1                                                   
______________________________________                                    
Characteristics of AAEM Containing Precursors                             
AAEM Precursor                                                            
            Solids (wt %)                                                 
                        Meq. AAEM/gram-solid                              
______________________________________                                    
IA          46.0        0.42                                              
IB          46.1        0.00                                              
______________________________________                                    
 Composition of Precursor IA:                                             
 1st Stage 40% of 45 BA/53.5 MMA/1 ALMA/0.5 MAA                           
 2nd Stage 60% of 35 BA/47.5 MMA/2.5 MAA/15 AAEM                          
 Composition of Precursor IB: Same as IA except AAEM was omitted.         
 
    
     
                                           TABLE I-2                               
__________________________________________________________________________
Formulations of Silicone Modified Lattices                                
(Quantities in parts by weight)                                           
Composition                                                               
(In order of addition)                                                    
           I1  I2  I3  I4  I5  I6  I7  I8  I9                             
__________________________________________________________________________
Material                                                                  
Precursor IA                                                              
           100 100 100 100 100 100 100                                    
Precursor IB                           100 100                            
Triton X405.sup.1                                                         
           3.4 3.4 3.4 3.4 3.4 3.4 3.4 3.4 3.4                            
A0700.sup.2                                                               
           0.0 1.5 2.9 4.3 5.8         4.3 0.0                            
A0800.sup.3                    3.5 1.2                                    
Meq. Silane/                                                              
           0.00                                                           
               0.33                                                       
                   0.66                                                   
                       1.00                                               
                           1.33                                           
                               0.33                                       
                                   1.00                                   
                                       1.00                               
                                           0.00                           
Meq. AAEM                                                                 
__________________________________________________________________________
 Footnotes:                                                               
 .sup.1 70% concentration                                                 
 .sup.2 Aminoethyl aminopropyl trimethoxysilane                           
 .sup.3 Aminopropyl Trimethoxysilane                                      
 
    
     
                       TABLE I-3                                                   
______________________________________                                    
Aqueous Wood Sealer                                                       
Formulations for Latex Compositions I1 to I9                              
Material          Amount (parts by weight)                                
______________________________________                                    
General Formulation                                                       
(25% Solids, Order of addition shown                                      
Silane modified Latex                                                     
                  25 pph.sup.1 (solids)                                   
DE.sup.2          35% on latex solids                                     
FC-120.sup.3      1.2 pph                                                 
SWS-211.sup.4     0.02 pph                                                
Water             Dilute to 25% Solids                                    
Specific Example of Aqueous                                               
Wood Sealer Based on Composition I-4                                      
Latex Composition I4                                                      
                  53.87                                                   
DE                8.14                                                    
FC-120            1.2                                                     
SWS-211           0.02                                                    
Water             40.60                                                   
______________________________________                                    
 Footnotes:                                                               
 .sup.1 pph = parts per hundred parts of sealer.                          
 .sup.2 Diethylene glycol mono ethyl ether.                               
 .sup.3 Fluorad 120 wetting aid at 1% active in water/dipropylene glycol  
 methyl ether: 47/1.                                                      
 .sup.4 Silicone defoamer from Wacker.                                    
 
    
     
                       TABLE 1-4                                                   
______________________________________                                    
Properties of Aqueous Wood Sealers Based on Composition 1 to 9            
Latex    Mar       % Black Heel                                           
                               Black Heel Mark                            
Composition                                                               
         Resistance                                                       
                   marks       Removal (dry cloth)                        
______________________________________                                    
I1       5         2.3         none                                       
I2       2         1.5         partial                                    
I3       I         1.1         complete                                   
I4       1         1.6         complete                                   
I5       1         1.5         complete                                   
I6       4         1.5         none                                       
I7       4         2.0         partial                                    
I8       5         2.6         none                                       
I9       5         2.9         none                                       
______________________________________                                    
 
    
     EXAMPLE II 
     Example II shows the enhancement of coating performance aminosilane modification brings to the precursor AAEM containing latex. We also show the effect of aminosilane level and aminosilane type on coating performance. 
     Preparation of Precursor Latex 
     A monomer emulsion (ME) was prepared by adding 475 g DIW, 20 g of sodium lauryl sulphate (SLS), 600 g ethyl acrylate, 335 g MMA, 15 g MAA and 50 g AAEM followed by stirring. 
     To a polymerization vessel, under nitrogen, 800 g DIW and 25 g SLS was added. After the temperature was increased to 85° C., 4.2 g of ammonium persulfate (ASP) in DIW was added. After the addition of the APS, add ME along with a feed of 2.1 APS in DIW at approximately 12.5 g/minute and 0.88 cc/minute respectively was initiated. After the addition of the ME was completed, the emulsion jar was rinsed with 30 g of DIW. The vessel was cooled to 56° C. over a 1 hour period after which 1 g of t-BHP in DIW and 0.5 g isoascorbic acid in DIW was added. The vessel was cooled to room temperature and filtered before modification with aminosilanes. Table II displays some characteristics of precursor IIA. 
     Preparation of Silicon-Modified Latex 
     The procedure for the preparation of a silicone-modified latex based on precursor II-A was the same as described in Example I, except the materials and proportions used are shown in Table II-2. The silane-modified latex was allowed to stand for 4 days before it is formulated into a sealer. 
     Preparation of Aqueous Wood Sealers Based on Silane-Modified Lattices 
     Table II-3 gives the sealer formulation used to evaluate compositions II-1 through II-4. A general formulation is shown as well as a specific example based on composition II-4. To a mixing vessel, all materials except the latex were added. With stirring, the silane-modified latex was added. The mixture was stirred for at least an additional hour and allowed to stand for at least 16 hours before use. 
     Testing of Sealers Based on Compositions II-1 to II-4 
     To maple wood panels, 3 coats of sealers based on compositions II-1 to II-4 were applied with about one to two hours between coats. After the final coat, the sealed panels were allowed to cure at 25° C. for 72 hours before testing. The test results are displayed in Table II-4. 
     
                       TABLE II-I                                                  
______________________________________                                    
Characteristics of AAEM Containing Precursor IIA                          
Solids (wt %)                                                             
             Meq. AAEM/gram-solid                                         
______________________________________                                    
40.1         0.23                                                         
Composition of precursor IIA:                                             
60 EA/33.5 MMA/1.5 MAA/5 AAEM                                             
______________________________________                                    
 
    
     
                       TABLE II-2                                                  
______________________________________                                    
Formulations of Silicone-Modified Lattices                                
(Quantities in parts by weight)                                           
Composition                                                               
(In order of addition)                                                    
              II1     II2      II3    II4                                 
______________________________________                                    
Material                                                                  
Precursor IIA 100     100      100    100                                 
Triton X405.sup.1                                                         
              2.9     2.9      2.9    2.9                                 
A0700.sup.2   0.0     0.7      2.1                                        
A0699.sup.3                           1.9                                 
Meq. Silane/  0.00    0.33     1.00   1.00                                
Meq. AAEM                                                                 
______________________________________                                    
 Footnotes:                                                               
 .sup.1 70% concentration                                                 
 .sup.2 Aminoethyl aminopropyl trimethoxysilane                           
 .sup.3 Aminoethyl aminopropyl methyl dimethoxysilane                     
 
    
     
                       TABLE II-3                                                  
______________________________________                                    
Aqueous Wood Sealer                                                       
Formulations for Latex Compositions II-1 to II-4                          
Material          Amount (parts by weight)                                
______________________________________                                    
General Formulation                                                       
(25% Solids, Order of Addition Shown)                                     
Silane-Modified Latex                                                     
                  25 pph.sup.1 (solids)                                   
DE.sup.2          35% on latex solids                                     
FC-120.sup.3      1.2 pph                                                 
SWS-211.sup.4     0.02 pph                                                
Water             Dilute to 25% Solids                                    
Specific Example of Aqueous                                               
Wood Sealer Based on Composition II-4                                     
Latex Composition II-4                                                    
                  64.18                                                   
DE                9.98                                                    
FC-170C           0.20                                                    
SWS-211           0.02                                                    
Water             25.63                                                   
______________________________________                                    
 Footnotes:                                                               
 .sup.1 pph = parts per hundred parts of sealer.                          
 .sup.2 Diethylene glycol mono ethyl ether.                               
 .sup.3 3M Fluorad 170C wetting aid.                                      
 .sup.4 Silicone defoamer from Wacker.                                    
 
    
     
                       TABLE II-4                                                  
______________________________________                                    
Properties of Aqueous                                                     
Wood Sealers Based on Composition II-1 to II-4                            
Latex          Black Heel                                                 
Composition    (Relative.sup.1)                                           
                         % Scuffing                                       
______________________________________                                    
II1            3         3.3                                              
II2            2         1.6                                              
II3            2         0.0                                              
II4            1         0.0                                              
______________________________________                                    
 Footnotes:                                                               
 .sup.1 1 = best at about 2.5% coverage. Increasing number implies        
 decreasing performance.                                                  
 
    
     EXAMPLE III 
     Example III shows that coating performance is effected by the structure of the aminosilane. 
     Preparation of Precursor Latex 
     Precursor latex, IA, described above in Example I, was used. 
     Preparation of Silicone-Modified Latex 
     The procedure for the preparation of a silicone-modified latex based on precursor IA was the same as described above in Example I, except the materials and proportions used are shown in Table III-1 and a common preblend of precursor/Triton 405 (70%) was used. The silane-modified lattices were allowed to stand for 1 day before they were formulated into sealers. 
     Preparation of Aqueous Wood Sealers Based on Silane-Modified Lattices 
     Table III-2 gives the sealer formulation used to evaluate compositions III-1 through III-4. A general formulation is shown as well as a specific example based on composition III-1. Coating preparation is described in Example I. 
     Testing of Sealers Based on Compositions II-1 to II-4 
     To maple wood panels, 4 coats of sealers based on compositions III-1 to III-5 were applied with about one to two hours between coats. After the final coat, the sealed panels were allowed to cure at 25° C. for 4 days before testing. The test results are displayed in Table III-3. 
     
                       TABLE III-1                                                 
______________________________________                                    
Formulations of Silicone-Modified Lattices                                
(Quantities in parts by weight)                                           
Preblend = 100 Precursor latex IA                                         
    3.3 Triton X405 (70%)                                                 
Composition                                                               
(In order of addition)                                                    
             III1    III2    III3  III4  III5                             
______________________________________                                    
Material                                                                  
Preblend             103.3   103.3 103.3 103.3                            
Precursor IA 100                                                          
Triton X405.sup.1                                                         
             3.3                                                          
A0700.sup.2          3.4                                                  
A0699.sup.3                  3.2                                          
A0800.sup.4                        2.8                                    
A0742.sup.5                              2.9                              
Meq. Silane/ 0.00    0.80    0.80  0.80  0.80                             
Meq. AAEM                                                                 
______________________________________                                    
 Footnotes:                                                               
 .sup.1 70% concentration                                                 
 .sup.2 Aminoethyl aminopropyl trimethoxysilane                           
 .sup.3 Aminoethyl aminopropyl methyl dimethoxysilane                     
 .sup.4 Aminopropyl trimethoxysilane                                      
 .sup.5 Aminopropyl methyl diethoxysilane                                 
 
    
     
                       TABLE III-2                                                 
______________________________________                                    
Aqueous Wood Sealer                                                       
Formulations for Latex Compositions III-1 to III-5                        
Material           Amount (parts by weight)                               
______________________________________                                    
General Formulation                                                       
(25% Solids, Order of Addition Shown)                                     
Silane-modified Latex                                                     
                   25 pph.sup.1 (solids)                                  
DE.sup.2           35% on latex solids                                    
FC-120.sup.3       1.2 pph                                                
SWS-211.sup.4      0.02 pph                                               
Water              Dilute to 25% Solids                                   
Specific Example of Aqueous                                               
Wood Sealer Based on Composition III-2                                    
Latex Composition III-2                                                   
                   54.19                                                  
DE                 8.14                                                   
FC-120             1.2                                                    
SWS-211            0.02                                                   
Water              36.30                                                  
______________________________________                                    
 Footnotes:                                                               
 .sup.1 pph = parts per hundred parts of sealer.                          
 .sup.2 Diethylene glycol mono ethyl ether.                               
 .sup.3 Fluorad 120 wetting aid at 1% active in water/dipropylene glycol  
 methyl ether: 47/1.                                                      
 .sup.4 Silicone defoamer from Wacker.                                    
 
    
     
                       TABLE III-3                                                 
______________________________________                                    
Properties of Aqueous Wood                                                
Sealers Based on Composition III-1 to III-5                               
Latex     % Black Heel            Mar                                     
Composition                                                               
          Marks        % Scuffing Resistance                              
______________________________________                                    
III-1     3.8          2.2        5    (Poor)                             
III-2     2.2          0.0        1    (Exc.)                             
III-3     1.0          0.0        1    (Exc.)                             
III-4     1.7          1.0        4    (Fair)                             
III-5     1.2          0.0        1    (Exc.)                             
______________________________________                                    
 
    
     EXAMPLE IV 
     Example IV shows that silicone modification improves the performance of a coating based on a room temperature film-forming precursor latex. 
     Preparation of Precursor Latex IV 
     The preparation and characteristics of the precursor latex, IVA, is described above in Example I, except the ratio of BA/MMA in ME-I (Monomer Emulsion I) was changed from 35/47.5 to 69.8/12.7, giving a softer, lower glass transition temperature, first stage. The solids of precursor IVA was 45.3. 
     Preparation of Silicone-Modified Latex 
     The procedure for the preparation of a silicone-modified latex based on precursor IVA was the same as described above in Example I, except the materials and proportions used are shown in Table IV-1. 
     Preparation of Aqueous Wood Sealers Based on Silane-Modified Lattices 
     Table IV-2 gives the sealer formulation used to evaluate composition IV-1. The procedure is the same as previous examples. Note no cosolvent (DE) was used as both composition IV1 and precursor IVA form films below room temperature. 
     Testing of Sealers based on Compositions IV-1 and Precursor IV 
     To maple wood panels, 4 coats of sealers based on compositions IV1 and precursor IVA were: applied with about one to two hours between coats. After the final coat, the sealed panels were allowed to cure at 25 ° C. for 3 days before testing. The test results are displayed in Table IV-3. 
     
                       TABLE IV-1                                                  
______________________________________                                    
Preparation of Silicone-Modified Latex IV1                                
(Quantities in parts by weight)                                           
(In order of addition)                                                    
Material                                                                  
______________________________________                                    
Precursor IVA       100.0                                                 
Triton X405.sup.1   3.2                                                   
A0700.sup.2         4.3                                                   
Meq. Silane/Meq. AAEM                                                     
                    1.00                                                  
______________________________________                                    
 Footnotes:                                                               
 .sup.1 70% concentration                                                 
 .sup.2 Aminoethyl aminopropyl trimethoxysilane                           
 
    
     
                       TABLE IV-2                                                  
______________________________________                                    
Aqueous Wood Sealer formulations for Composition IV1                      
(25% Solids, Order of Addition Shown)                                     
                  Amount                                                  
Material          (parts by weight)                                       
______________________________________                                    
Water             45.65    39.85                                          
FC-120            0.93     0.93                                           
SWS-211           0.02     0.02                                           
Composition IV1   50.00                                                   
Precursor IVA              50.00                                          
______________________________________                                    
 
    
     
                       TABLE IV-3                                                  
______________________________________                                    
Properties of Aqueous Wood Sealers Based on Composition IV1               
Latex    % Black Heel             Mar                                     
Composition                                                               
         Marks          % Scuffing                                        
                                  Resistance                              
______________________________________                                    
IV1      2.0            0         1    (exc)                              
Precursor IV                                                              
         3.5            2.2       5    (poor)                             
______________________________________                                    
 
    
     EXAMPLE V 
     Floor Wear Test 
     In this example, composition III-5 was prepared and formulated as described in Example III. The control (precursor not modified with aminosilane) was composition III-1 of Example III, except X405 was omitted and formulated into a sealer according to Example III. Five coats of each coating were applied to maple panels and cured at 25° C. for one week prior to placement on the floor of the exposure area. 
     Table V-1 shows the effects of 26 days of wear. 
     
                       TABLE V-1                                                   
______________________________________                                    
Comparison of Silane-Modified                                             
and Unmodified Precursor I-1 in a Wear Test                               
Latex    % Gloss     % Gloss                                              
Composition                                                               
         Retained at 20°                                           
                     Retained at 60°                               
                                 Appearance                               
______________________________________                                    
Precursor I-1                                                             
         62          72          Highly scuffed                           
(unmodified)                     and scratched                            
III-5    91          82          Few minor                                
                                 scuffs and                               
                                 scratches                                
______________________________________                                    
 Footnotes:                                                               
 .sup.1 Gloss retained = (final gloss/initial gloss) × 100          
 
    
     EXAMPLE VI 
     In Example VI, we show neutralization with potassium hydroxide rather than ammonia. 
     Preparation of Precursor Lattices 
     The preparation and characteristics of precursor lattices VI-A and VI-B are described above in Example I, except neither latex was neutralized with NH 3  and VI-B was prepared by a homogeneous process where all monomers were introduced from a single monomer emulsion. The solids of precursor VI-A and VI-B were 47.6% and 47.8% respectively. 
     Preparation of Silicon-Modified Latex 
     The procedure for the preparation of silicone-modified lattices based on precursors VI-A and VI-B is described in Example I, except the materials and proportions used are shown in Table VI-1. Also, the pH of the precursor lattices was increased to about 7.5 with aqueous potassium hydroxide before the addition of the other materials. 
     Preparation of Aqueous Wood Sealers Based on Silane-Modified Lattices 
     Table VI-2 gives the sealer formulation used to evaluate compositions VI-1 to VI-5. The procedure was the same as previous examples. 
     Testing of Sealers Based on Compositions IV-1 and Precursor IV 
     To maple wood panels, 4 coats of sealers based on compositions IV1 and precursor IV were applied with about one to two hours between coats. After the final coat, the sealed panels were allowed to cure at 25° C. for 3 days before testing. The test results are displayed in Table VI-3. 
     
                       TABLE VI-1                                                  
______________________________________                                    
Formulations of Silicone-Modified Lattices                                
(Quantities in parts by weight)                                           
Composition                                                               
(In order of addition)                                                    
             VI1     VI2     VI3   VI4   VI5                              
______________________________________                                    
Material                                                                  
Precursor VI-A                                                            
             100     100                                                  
Precursor VI-B               100   100   100                              
KOH (2.1 N)  1.70    1.70    1.50  1.50  1.50                             
Water        5.08    11.36   5.52  11.20 11.72                            
Triton X405.sup.1            3.40  3.4   3.4                              
A0700.sup.2                              3.6                              
A0742.sup.3          3.06          3.1                                    
Meq. Silane/ 0.00    0.80    0.00  0.80  0.80                             
Meq. AAEM                                                                 
______________________________________                                    
 Footnotes:                                                               
 .sup.1 70% concentration                                                 
 .sup.2 Aminoethyl aminopropyl trimethoxysilane                           
 .sup.3 Aminoethyl aminopropyl methyl dimethoxysilane                     
 
    
     
                       TABLE VI-2                                                  
______________________________________                                    
Material           Amount (parts by weight)                               
______________________________________                                    
General Formulation                                                       
(25% Solids, Order of Addition Shown)                                     
Silane-modified Latex                                                     
                   25 pph.sup.1 (solids)                                  
DE.sup.2           35% on latex solids                                    
FC-120.sup.3       1.2 pph                                                
SWS-211.sup.4      0.02 pph                                               
Water              Dilute to 25% Solids                                   
Specific Example of Aqueous                                               
Wood Sealer Based on Composition VI-2                                     
Latex Composition VI-1                                                    
                   35.00                                                  
DE                 3.80                                                   
FC-120             0.94                                                   
SWS-211            0.02                                                   
Water              22.70                                                  
______________________________________                                    
 Footnotes:                                                               
 .sup.1 pph = parts per hundred parts of sealer.                          
 .sup.2 Diethylene glycol mono ethyl ether.                               
 .sup.3 Fluorad 120 wetting aid at 1% active in water/dipropylene glycol  
 methyl ether: 47/1.                                                      
 .sup.4 Silicone defoamer from Wacker.                                    
 
    
     
                       TABLE VI-3                                                  
______________________________________                                    
Properties of Aqueous Wood Sealers Based on Composition IV1               
Latex                                                                     
Composition                                                               
          % Black Heel % Scuffing Mar                                     
______________________________________                                    
VI1       2.4          2.5        5    (poor)                             
VI2       1.6          &lt;0.1%      1    (exc)                              
VI3       1.6          1.7        5    (poor)                             
VI4       1.3          &lt;0.1%      1    (exc)                              
VI5       1.5          0.0        1    (exc)                              
______________________________________                                    
 
    
     EXAMPLE VII 
     Effect of Neutralization and Process 
     Example VII shows the silicon-modified latex can be prepared by adding a preblend of aminosilane and surfactant to the precursor rather than added individually. This gives an improved mode for preparation since the addition of diluted materials are less likely to &#34;shock&#34; the latex and cause latex flocculated. We also show neutralization by potassium hydroxide can be eliminated. 
     Preparation of Precursor Lattices 
     The latex, precursor VIIA, described in Example I, was prepared without NH 3  neutralization. The solids level was 46.5%. 
     Preparation of Silicon-Modified Latex 
     The silicon-modified lattices were prepared as described in Example VI, except a preblend of the aminosilane, surfactant and water was used in two of the compositions (see Table VII-1). 
     Preparation of Aqueous Wood Sealers Based on Silane-Modified Lattices 
     Aqueous sealers, based on precursors VII1 to VII4, were prepared as described in Example VI, except adjustments were made for precursor solids. The sealers were applied to wood panels and cured as described in the previous examples. The test results are displayed in Table VI-3. 
     
                       TABLE VII-1                                                 
______________________________________                                    
Formulations of Silicone-Modified Lattices                                
(Quantities in parts by weight)                                           
Composition                                                               
(In order of addition)                                                    
              VII1     VII2    VII3   VII4                                
______________________________________                                    
Material                                                                  
Precursor VII-A                                                           
              100.00   100.00  100.00 100.00                              
KOH (2.1 N)   0.70     0.60           0.60                                
Premix.sup.1           8.1     8.4                                        
Water                                 1.76                                
Triton X405.sup.2                     3.20                                
A0742.sup.3                           2.97                                
Meq. Silane/  0.00     0.80    0.83   0.80                                
Meq. AAEM                                                                 
______________________________________                                    
 Footnotes:                                                               
 .sup.1 Premix = 36.9 A0742/41.2 X405/21.8 water. After preparation, the  
 premix was immediately added to the precursor as shown.                  
 .sup.2 70% concentration                                                 
 .sup.3 Aminoethyl aminopropyl methyl dimethoxysilane                     
 
    
     
                       TABLE VII-2                                                 
______________________________________                                    
Properties of Aqueous Wood Sealers Based on Composition IV1               
Latex     Flocculate                                                      
Composition                                                               
          (Sedimentation)                                                 
                      % Black Heel                                        
                                  Mar                                     
______________________________________                                    
VII1      None        1.4         5    (poor)                             
VII2      None        1.0         1    (exc)                              
VII3      None        0.90        1    (exc)                              
VII4      Slight      1.0         1    (exc)                              
______________________________________                                    
 
    
     Example VIII 
     Example VIII shows the importance of the surfactant for optimum sealer performance. 
     Preparation of Precursor Latex 
     To a polymerization vessel, 812.5 g of DIW was heated to 85° C., after which 20.4 g of SIPONATE DS-4 was added under a nitrogen atmosphere. In a separate vessel, a monomer emulsion (ME) was prepared by mixing 12 g of DS-4, 150 g DIW, 110 g BA, 355 MMA and 10 g MAA. To the polymerization vessel, 31 g of the ME and 10 g of DIW followed by 1.5 g ammonium persulphate (APS) in water and 1.5 g of sodium carbonate in water was added. To the ME vessel, 25 g of ALMA was added. The ME was then added to the polymerization vessel over a 90 minute period along with a cofeed of 1.5 g APS in 150 g of DIW at a rate of 0.84 g/min. After the addition of ME was complete, the APSDIW feed was terminated. The polymerization vessel was then held for an additional 30 minutes at 85° C. 
     A second ME was prepared as above but used 12 g DS-4, 150 g DIW, 212.5 ethyl hexyl acrylate, 67.5 styrene, 125 g acrylonitrile, 75 g AAEM and 20 g MAA. This ME was added to the polymerization vessel over a 90 minute period along with the resumption of the APS/DIW cofeed. After the addition of the ME was complete, the emulsion vessel was rinsed with 25 g DIW. The polymerization vessel was held for an additional 30 minutes at 85° C., after which it was cooled to 60° C. and chased in a similar manner as described in Example I. 
     Preparation of Silicon-Modified Latex 
     Precursor VIII-A, described in Example I, was prepared without NH 3  neutralization at a solids level of 45.9%. The preparation of Precursor VIIIB is described in Attachment VIII and has the following characteristics. 
     Composition: 
     1st Stage: 50% of 22 BA/71 MMA/5 ALMA/2 MAA 
     2nd Stage: 50% of 42.5 EHA/13.5 STY/25 AN/15 AAEM 
     Solids: 39.7% 
     Preparation of Aqueous Wood Sealers Based on Silane-Modified Lattices 
     Aqueous sealers, based on precursors VIII1 to VIII6, were prepared according to Table VIII-2. The sealers were applied to wood panels and cured as described in the previous examples. The test results are displayed in Table VIII-3. 
     
                                           TABLE VIII-I                            
__________________________________________________________________________
Formulations of Silicone-Modified Lattices                                
(Quantities in parts by weight)                                           
Composition                                                               
(In order of addition)                                                    
            VIII1                                                         
                VIII2                                                     
                    VIII3                                                 
                        VIII4                                             
                            VIII5                                         
                                VIII6                                     
__________________________________________________________________________
Material                                                                  
Precursor VIIIA                                                           
            100.00                                                        
                100.00                                                    
                    100.00                                                
Precursor VIIIB         100.00                                            
                            100.00                                        
                                100.00.sup.1                              
Premix.sup.2                                                              
            5.67                                                          
                6.82                                                      
                    7.96                                                  
                        3.44                                              
                            2.45                                          
                                0.0                                       
Characteristics                                                           
X405 Level.sup.3                                                          
            0.0 2.5%                                                      
                    5.0%                                                  
                        5.0%                                              
                            0.0 0.0                                       
Meq. Silane/                                                              
            0.80                                                          
                0.80                                                      
                    0.80                                                  
                        0.80                                              
                            0.80                                          
                                0.0                                       
Meq. AAEM                                                                 
__________________________________________________________________________
 Footnotes:                                                               
 1. Neutralized with NH.sub.3 (aq.) to pH = 7.5.                          
 2. Premixes were prepared as follows:                                    
 Composition 1: 3.56 water + 3.85 A0742.                                  
 Composition 2: 3.92 water + 2.41 X405 (70%) + 4.32 A0742                 
 Composition 3: 4.38 water + 8.23 X405 (70%) + 7.39 A0742                 
 Composition 4: 1.27 water + 2.38 X405 (70%) + 2.14 A0742                 
 Composition 5: 1.98 water + 2.14 A0742                                   
 3. Percent on precursor solids.                                          
 
    
     
                       TABLE VIII-2                                                
______________________________________                                    
Aqueous Sealer Formulations for Compositions VIII                         
(30% Solids)                                                              
Material                                                                  
(in order of addition)                                                    
______________________________________                                    
Water         23.09  24.09  25.04                                         
                                 15.88                                    
                                      13.50                               
                                           11.89                          
DE            7.05   6.89   6.73 6.73 7.05 7.50                           
FC120 (1%)    1.50   1.50   1.50 1.50 1.50 1.50                           
KP-140.sup.1  1.41   1.38   1.35 1.35 1.41 1.50                           
EG.sup.2      2.00   2.00   2.00 2.00 2.00 2.00                           
Defoamer.sup.3                                                            
              0.02   0.02   0.02 0.04 0.04 0.04                           
Charge the above into mixing vessel.                                      
With stirring add the following:                                          
VIII1         64.91                                                       
VIII2                64.10                                                
VIII3                       63.34                                         
VIII4                            72.50                                    
VIII5                                 74.50                               
VIII6                                      75.57                          
______________________________________                                    
 Footnotes:                                                               
 1. Tributoxy ethyl phosphate                                             
 2. Ethylene glycol                                                       
 3. Silicone defoamer                                                     
 
    
     
                       TABLE VIII-3                                                
______________________________________                                    
Performance of Aqueous Sealers Based on Compositions VIII                 
             Mar                                                          
Latex Composition                                                         
             Resistance  % Black Heel Marks                               
______________________________________                                    
VIII-I       5      (poor)   0.8                                          
VIII-2       3      (good)   1.1                                          
VIII-3       1      (exc)    1.2                                          
VIII-4       1      (exc)    0.9                                          
VIII-5       5      (poor)   0.5                                          
VIII-6       5      (poor)   1.2                                          
______________________________________                                    
 
    
     EXAMPLE IX 
     Example IX shows that the surfactant does not have to be present for optimum performance of the silicone-modified latex. 
     Preparation of Silicon-Modified Latex 
     The precursor described in Example VI was used to prepare silicon-modified latex compositions IX-1 to IX-4 (see Table IX). Composition IX3 was prepared by post-addition of X405 to a portion of IX1, which was 24 hours old. 
     Preparation of Aqueous Wood Sealers Based on Silane-Modified Lattices 
     Aqueous sealers, based on precursors IX1 to IX4, were prepared according to Table VIII-2. The sealers were applied to wood panels and cured as described in the previous examples. 
     Properties of Aqueous Sealers Based on Compositions IX 
     Testing of the sealers was the same as in Examples I through VIII with the exceptions that the Snell capsule used was smaller, the heels in the capsule were larger and the time of exposure of the panels was 10 minutes rather than 5 minutes. This gave testing conditions more rigorous than in the previous examples. The results are shown in Table IX-3. 
     
                       TABLE IX-1                                                  
______________________________________                                    
Formulations of Silicone Modified-Lattices                                
(Quantities in parts by weight)                                           
Composition                                                               
(In order of addition)                                                    
              IX1     IX2      IX3.sup.1                                  
                                      IX4.sup.2                           
______________________________________                                    
Material                                                                  
Precursor     100.00  100.00   100.00 100.00                              
Premix.sup.3  5.67    7.96     5.67                                       
X405 (70%)            3.35                                                
Characteristics                                                           
X405 Level.sup.4                                                          
              0.0     5.0%     5.0%   0.0                                 
Meq. Silane/  0.80    0.80     0.80   0.0                                 
Meq. AAEM                                                                 
______________________________________                                    
 Footnotes:                                                               
 1. Prepared by blending X405 (70%) into 24 hour old composition IX1 at a 
 ratio of 100 parts Composition IX1 to 3.1 parts X405 (70%).              
 2. Neutralized with NH3 (aq.) to pH = 8.1.                               
 3. Premixes were prepared as follows:                                    
 Composition 1: 3.56 water + 3.85 A0742.                                  
 Composition 2: 4.38 water + 8.23 X405 (70%) + 7.39 A0742 Composition 4:  
 3.56 water + 3.85 A0742                                                  
 4. Percent on precursor solids.                                          
 
    
     
                       TABLE IX-2                                                  
______________________________________                                    
Aqueous Sealer Formulations for Compositions IX                           
(30% Solids)                                                              
Material                                                                  
(in order of addition)                                                    
______________________________________                                    
Water           20.84  22.77    22.17                                     
                                     19.94                                
DE              7.05   6.73     6.73 7.50                                 
FC120 (1%)      1.50   1.50     1.50 1.50                                 
KP-140.sup.1    1.40   1.40     1.40 1.40                                 
EG.sup.2        2.00   2.00     2.00 2.00                                 
Defoamer.sup.3  0.20   0.20     0.20 0.20                                 
Charge the above into mixing vessel.                                      
With stirring add the following:                                          
IX-1            64.91                                                     
IX-2                   63.30                                              
IX-3                            63.91                                     
IX-4                                 65.36                                
After 30 min. of stirring add the following:                              
Acrysol RM-1020.sup.4                                                     
                2.1    2.1      2.1  2.1                                  
______________________________________                                    
 Footnotes:                                                               
 1. Tributoxy ethyl phosphate                                             
 2. Ethylene glycol                                                       
 3. Foamaster 111                                                         
 4. Rheology modifier                                                     
 
    
     
                       TABLE IX-3                                                  
______________________________________                                    
Performance of Aqueous Sealers Based on Compositions IX                   
Latex     Mar            % Black   % Scuff                                
Composition                                                               
          Resistance.sup.1                                                
                         Heel Marks                                       
                                   Marks                                  
______________________________________                                    
IX-1      3-4     (fair)     1.4     1.2                                  
IX-2      2       (very good)                                             
                             1.1     0.9                                  
IX-3      1       (exc)      1.0     0.7                                  
IX-4      5       (poor)     2.8     1.8                                  
______________________________________                                    
 Footnotes:                                                               
 1. After 3 week cure at 25° C.                                    
 
    
     EXAMPLE X 
     Example X shows the hydrophilic/lipophilic balance (HBL) of the surfactant can effect the performance of the silicon modified latex. 
     Preparation of Silicon-Modified Latex 
     The precursor described in Example VI was used to prepare silicon-modified latex compositions X-1 to X-3. The milliequivalents of surfactant to precursor solids was held constant at 0.25. As described above in Example IX, a premix of surfactant, aminosilane and water was added to the precursor with stirring (see Table X-1). 
     Preparation of Aqueous Wood Sealers Based on Silane-Modified Lattices 
     Aqueous sealers, based on precursors IX1 to IX4, were prepared according to Table X-2. The sealers were applied to wood panels and cured as described in the previous examples. 
     Properties of Aqueous Sealers Based on Compositions IX 
     Testing of the sealers was the same as in Examples I through VIII with the exceptions that the Snell capsule used was smaller, the heels in the capsule were larger. The time in the Snell capsule was 5 minutes. This gave testing conditions more rigorous than in the previous examples. The results are shown in Table X-3. 
     
                       TABLE X-1                                                   
______________________________________                                    
Formulations of Silicone-Modified Lattices                                
(Quantities in parts by weight)                                           
Composition                                                               
(In order of addition)                                                    
               X1         X2      X3                                      
______________________________________                                    
Material                                                                  
Precursor      108.93     108.93  108.93                                  
Premix.sup.1   10.38      8.70    6.94                                    
Characteristics                                                           
Surfactant     X705       X405    X100                                    
Surfactant HBL 13.5       17.9    18.7                                    
Meq. Silane/   0.80       0.80    0.80                                    
Meq. AAEM                                                                 
______________________________________                                    
 Footnotes:                                                               
 1. Premixes were prepared as follows:                                    
 Composition 1: 2.38 water + 11.94 Triton X705 (70%) + 6.43 A0742.        
 Composition 2: 3.82 water + 7.14 Triton X405 (70%) + 6.43 A0742.         
 Composition 3: 5.96 water + 1.49 Triton X100 (100%) + 6.43 A0742.        
 Note in all premixes wt. water/wt. silane = 0.93.                        
 
    
     
                       TABLE X-2                                                   
______________________________________                                    
Aqueous Sealer Formulations for Compositions X                            
(30% Solids)                                                              
Material                                                                  
(in order of addition)                                                    
______________________________________                                    
Water          23.89       22.72  21.63                                   
DE             6.63        6.73   6.83                                    
FC120 (1%)     1.50        1.50   1.50                                    
KP-140.sup.1   1.40        1.40   1.40                                    
EG.sup.2       2.00        2.00   2.00                                    
Defoamer.sup.3 0.15        0.15   0.15                                    
Charge the above into mixing vessel.                                      
With stirring add the following.                                          
IX-1           62.33                                                      
IX-2                       63.30                                          
IX-3                              64.39                                   
After 30 min. of stirring add the following:                              
Acrysol RM-1020.sup.4                                                     
               2.1         2.1    2.1                                     
______________________________________                                    
 Footnotes:                                                               
 1. Tributoxy ethyl phosphate                                             
 2. Ethylene glycol                                                       
 3. Foamaster 111                                                         
 4. Rheology modifier                                                     
 
    
     
                       TABLE X-3                                                   
______________________________________                                    
Performance of Aqueous Sealers Based on Compositions X                    
Latex       Mar            % Black                                        
Composition Resistance.sup.1                                              
                           Heel Marks                                     
                                   Comments                               
______________________________________                                    
X-1         1     (exc)    0.80    Hazy film                              
X-2         1     (exc)    1.2                                            
X-3         4     (fair)   1.4                                            
______________________________________                                    
 
    
     EXAMPLE XI 
     Floor Wear Test 
     In Example XI, the aminosilane-modified composition X-2 of Example X is compared to a commercially available solvent dispersed, oil-modified urethane (OMU). The coating formulation for composition X-2 is given in Table X2. 
     To maple panels, 3 coats of the commercially available OMU, (Hillyard Chemical Company,: St. Joseph, Mo.), was applied. To another maple panel, 2 coats of a clear waterborne primer was applied, followed by 2 coats of the coating based on composition X-2. Both panels were cured for 72 hours at 25° C. before placement in the floor test area. 
     Table XI-I compares the gloss at 20° and 60° as a function of exposure time. The aminosilane-modified polymer exhibits gloss retention superior to the single pack solvent dispersed OMU. 
     
                       TABLE XI-I                                                  
______________________________________                                    
                                After one month                           
60°/20° gloss:                                              
         Initial After 11 day exposure                                    
                                Exposure                                  
______________________________________                                    
Comp X-2 63/27   66/27          64/24                                     
OMU      73/29   63/16          67/15                                     
______________________________________