Method for producing color filter
BACKGROUND OF THE INVENTION 
     This invention relates to a method for producing a color filter and more particularly to a color filter advantageously employed as a color liquid crystal display device. 
     Among the currently employed methods for preparing a color filter, there are a dyeing method consisting in dyeing a transparent substrate with a binder containing dyes and pigments, a printing method and a pigment dispersion method. 
     Since the dyeing method consists in selectively forming a thin resin film on a substrate with dyes, a resist printing process and a photolithographic process need to be performed each time the color is changed. Although resist printing is unnecessary with the printing method, there is a limit to the refinement, of color patterns and, the larger is the number of colors, the printing position becomes the worse. Although the fine color pattern is possible with the pigment dispersion method, a high precision photolithographic process needs to be performed each time the color is changed, resulting in a complicated process. 
     For overcoming the deficiency, there is proposed in Japanese Laid-open Patent Application No. 59-114572 (1984) a method for producing a color filter by an electrodeposition coating method. With this method, a transparent electrode is prepared by patterning a transparent electrically conductive film deposited on the substrate, the substrate is immersed in a colored electrodeposition bath for forming a colored layer by electrodeposition, and electrical voltage is applied only to a portion of the patterned transparent electrode which is to be dyed in the same color. The substrate is then immersed in a colored electrodeposition bath for forming a different color layer by electrodeposition, and electric voltage is then applied only to a portion of the substrate which is to be dyed in a different color. However, it is necessary with this method to perform a high precision patterning of the transparent electrode, and to pay meticulous care during the subsequent process not to break the fine pattern, because otherwise the subsequent coloring process is rendered difficult. Besides, the patterned transparent electrode needs to be electrically continuous, even in fine pattern sections, so that limitations are imposed on the degree of freedom of the pattern shape. 
     In Japanese Laid-open Patent Application No. 63-210901 (1988), there is proposed a method consisting in forming colored layers by light exposure, development and electrodeposition, using a mask having patterns only in areas to be dyed in the same colors and a positive type photosensitive resin composition, and repeating the steps of light exposure, development and electrodeposition a desired number of times. This method is inferior in stability because it makes use of a compound containing unstable quinone diazido groups. Besides, if the quinone diazido compound is brought into contact with an aqueous alkali solution, the quinone diazido compound in the unexposed part is also reacted with an aqueous alkali solution so that photosensitivity is markedly changed to present difficulties in the subsequent light exposure and development steps. 
     In the aforementioned electrodeposition methods, the transparent electrode for forming colored layers thereon is also employed as an electrode for driving a liquid crystal display device. However, the colored layers formed on the transparent electrode are of dielectric nature so that voltage for driving the liquid crystal device is extremely high. Accordingly, on the practical application another transparent electrode for driving the liquid crystal device is further provided on the colored layers produced in accordance with the aforementioned methods so as to lower the driving voltage. In the meanwhile, as the transparent electrode employed in the aforementioned methods has light transmittance of 80 to 85%, the provision of two transparent electrodes poses another disadvantage in that light transmittance is lowered, leading to inferior performance of a colored display liquid crystal device. To solve such a problem, there is proposed in Japanese Laid-open Patent Application No. 1-22379 a method for forming colored layers on an original plate and transferring the colored layers on a transparent substrate. In the method, however, the transferring is performed for each color, thus necessitating high precision of alignment at respective transferring steps. 
     On the other hand, in order to meet the demand for high performance of the device provided with a color filter, it has been desired to improve contrast and to prevent color purity from being lowered. In order to solve this problem, a method of forming a non-light transmitting film in a region of the color filter defined between neighboring pixels has been proposed. For forming the non-light transmitting film, there are known a method comprising Forming pixels with alignment on a substrate on which a non-tight transmitting film pattern is formed previously, and a method comprising forming a non-light transmitting Film pattern with alignment on a substrate on which a pixel pattern is formed previously. 
     However, since it is necessary with these methods to effect an alignment operation between the pixel pattern and the non-light transmitting pattern, it is difficult with this precision to Form a pattern of non-light transmitting pattern of a coincident size free of the light transmitting sections between the pixel patterns. If overlapped portions are produced, step differences are produced on a color filter, so that it becomes difficult to produce a color filter excellent in planarity. 
     With any of the above methods, high precision processing is required for alignment so that it is difficult to cope with the demand for a larger work size, that is a larger picture size with reduced costs. 
     It is a principal object of the present invention to provide a method for producing a color filter which is not in need of high precision fine processing and which has a large degree of freedom in selecting any kind of patterns of the colored layers and non-light transmitting layers can be arrayed without gaps between the color filter pixels. 
     It is another object of the present invention to provide a method for preparing a color filter which can be adapted easily for larger picture size and which can be mass-produced easily. 
     It is a further object of the present invention to provide a method for producing a color filter which can lower the driving voltage without light transmission being lowered and which do not require an additional step of forming transparent electrodes. 
     It is a further object of the present invention to provide a method for producing a color filter having light-intercepting layers patterned with high precision. 
     The above and other objects of the invention will become apparent from the following description. 
     The present invention provides a method for producing a color filter comprising the steps of: 
     (A) forming a photosensitive coating film on at least a transparent electrically conductive layer of a substrate selected from the group consisting of a first substrate having both the transparent electrically conductive layer and a light-intercepting layer on its surface and a second substrate having the transparent electrically conductive layer on its outermost surface and a light-intercepting layer between the second substrate and the transparent electrically conductive layer and exposing the photosensitive coating film through a mask having patterns of at least three different degrees of light transmittances; and 
     (B) developing and removing a photosensitive coating film region corresponding to a pattern selected from the group consisting of a pattern having smallest degree of light transmittance and a pattern having largest degree of light transmittance for exposing the transparent electrically conductive layer and electrodepositing a colored coating on the exposed transparent electrically conductive layer for forming a colored layer thereon, operation of developing and removing the photosensitive coating film and electrodepositing the colored coating being sequentially repeated for the respective patterns having different degrees of light transmittances where the sequence of repetition is selected from the group consisting of increasing light transmittance and decreasing light transmittance to form different colored layers, respectively. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     FIG. 1 is a diagram showing step by step a process for producing a color filter according to an embodiment of the present invention. 
     FIG. 2 is a diagramatic view showing the steps of producing a transparent substrate having both a light-intercepting layer and a transparent electrically conductive layer shown in FIG. 1 according to one embodiment of the present invention. 
     FIG. 3 is an enlarged schematic view showing a mask for producing a light-intercepting layer partially on the transparent electrically conductive layer. 
     FIG. 4 is an enlarged schematic view showing the transparent substrate having both the light-intercepting layer and the transparent electrically conductive layer produced by using the mask shown in FIG. 3. 
     FIG. 5 is an enlarged schematic view showing a negative mask having four different degrees of light transmittances used in the present invention. 
     FIG. 6 is an enlarged schematic view showing a mask for producing a light-intercepting layer. 
     FIG. 7 is an enlarged schematic view showing a positive mask having four different degrees of light transmittances used in the present invention. 
     FIG. 8 is an enlarged schematic view showing a negative mask having three different degrees of light transmittances used in the present invention. 
    
    
     PREFERRED EMBODIMENTS OF THE INVENTION 
     The present invention will be explained in more detail hereinbelow. 
     According to the present invention, a photosensitive coating film is formed on at least a transparent electrically conductive layer of a substrate having both the transparent electrically conductive layer and a light-intercepting layer on its surface or a substrate having the electrically conductive layer on its outermost surface and a light-intercepting layer between the substrate and the transparent electrically conductive layer, and light exposure is performed via a mask having patterns of at least three different degrees of light transmittances (the step is referred to hereinafter as step A). 
     There is no particular limitation to the substrate, if the substrate has both a transparent electrically conductive layer and a light-intercepting layer on its surface or has a transparent electrically conductive layer on its outermost surface and a light-intercepting layer between the substrate and the transparent electrically conductive layer. As for the substrate having both the transparent electrically conductive layer and the light-intercepting layer on its surface, the transparent electrically conductive layer and the light-intercepting layer may be separately formed on the outmost surface of the substrate. Alternatively, the light-intercepting layer may be formed partially on the transparent electrically conductive layer. Conversely, the transparent electrically conductive layer may be formed partially on the light-intercepting layer. To improve the smoothness of the objective color filter, it is preferred to employ the substrate in which the light-intercepting layer is formed partially on the transparent electrically conductive layer. Examples of the substrate may include a glass plate, a laminated plate, a plastic plate, or a plate having a transparent electrically conductive layer and a light-intercepting layer formed on its surface as described above. The substrate preferably has a smooth surface in view of the performance desired of a color filter. The surface of the substrate may be ground if so required. 
     The transparent electrically conductive layer may be formed of such materials as tin oxide, indium oxide, antimony oxide and mixtures thereof. There is no particular limitation to the methods for forming an electrically conductive layer and any of the known methods such as spraying, chemical vapor deposition (CVD), sputtering or vacuum evaporation, may be employed. A commercially available transparent substrate having a transparent electrically conductive layer may be employed. The substrate is preferably of higher transparency in view of the performance desired of the color filter. 
     The materials for making the light-intercepting layer to be formed on the substrate and the method for forming the light-intercepting layer are not particularly limited. The known light-intercepting layer materials ordinarily employed such as resin dispersants in which light-intercepting materials such as chromium, chromium oxide, dyes, pigments, or carbon black are dispersed in resins may be used by the known methods. When the light-intercepting layer is formed partially on the transparent electrically conductive layer and the light-intercepting layer is made of materials having low electrical conductance, a color filter excellent in smoothness is readily available. 
     The light-intercepting layer may be formed by, for example Cr-photolithographic method, black organic photosensitive material method, black ink printing method, dyeing method and electrodeposition method. Particularly, the Cr-photolithographic method excellent in thermal resistance is preferred. The Cr-photolithographic method involves, for example vacuum-evaporating or sputtering chromium alone or both chromium and chromium oxide on a glass substrate to form a film, and patterning the film by photolithography with the use of a photosensitive resist. The black organic photosensitive material method involves dispersing a light-intercepting material such as dyes, pigments or carbon black into a photosensitive resin to prepare a black organic photosensitive material, and forming a patterned light-intercepting layer with the use of the black organic photosensitive material. In the black ink printing method, for example a light-intercepting material such as dyes, pigments or carbon black is dispersed into a vehicle containing ink materials such as oil, solvents, resins, waxes and plasticizers to prepare a black ink. A patterned light-intercepting layer is formed by printing the black ink by offset printing method, intaglio printing method or screen printing method. In the dyeing method, a patterned light-intercepting layer may be formed by dyeing a coloring base such as gelatin, casein, PVA, PVA/vinylpyrrolidone copolymer through a masking layer with the use of black acidic dyes or reactive dyes. In the electrodeposition method, for example where a positive type photosensitive coating film is formed on the surface of a transparent electrically conductive layer by, e.g. spin-coating method or electrodeposition method, exposure is effected through a mask so that the positive type photosensitive coating film portion corresponding to a light-intercepting layer is exposed. The positive type photosensitive coating film of the exposed portions, i.e. corresponding to the light-intercepting layer are removed with an alkali aqueous solution to expose the transparent electrically conductive layer corresponding to the light-intercepting layer. An electrodeposition coating having black-hue and alkali resistance after curing is electrodeposited on the exposed transparent electrically conductive layer followed by drying, curing and exposure of light to the overall surface of the layer. The remaining positive type photosensitive coating film is removed with an alkali aqueous solution. The black coating film thus obtained may be further heated, if necessary. On the other hand, for example where a negative type photosensitive coating film is formed on the surface of a transparent electrically conductive layer by, e.g. spin-coating method or electrodeposition method, exposure is effected through a mask so that the negative type photosensitive coating film portion corresponding to a light-intercepting layer is not exposed. The negative type photosensitive coating film of the unexposed portions, i.e. corresponding to the light-intercepting layer are removed with a developing liquid to expose the transparent electrically conductive layer corresponding to the light-intercepting layer. An electrodeposition coating having black-hue and resistance against a removing agent after curing is electrodeposited on the exposed transparent electrically conductive layer followed by drying, and curing. The remaining negative type photosensitive coating film is removed with a removing agent. The black coating film thus obtained may be further heated, if necessary. The positive type or negative type photosensitive coating film later described may be employed. As the black-hued electrodeposition coating, a coating mixed with black pigments or dyes such as carbon black may preferably be used. Particularly, if the black-hued coating film is dried, e.g. at 80° to 140° C. for 10 to 30 minutes, the electrical conductance of the light-intercepting layer may preferably be lowered. 
     Although there is no particular limitation to the method of forming the photosensitive coating film on the transparent electrically conductive layer formed on at least the transparent electrically conductive layer, a negative or positive type photosensitive coating may be applied on the substrate by the known methods, such as electrodeposition, spraying, dip coating, roll coating, screen printing or spin coating. 
     As the negative type photosensitive coating for forming the negative type photosensitive coating film, a negative type photosensitive coating resin exhibiting film forming capabilities and photosensitivity and a photopolymerization initiator may be dispersed or dissolved in a solvent such as an organic solvent or water so as to be used as a coating material. As the positive type photosensitive coating for forming the positive type photosensitive coating film, a positive type photosensitive coating resin exhibiting film forming capabilities and photosensitivity may be dispersed or dissolved in water or in an organic solvent so as to be used as a coating material. Dyes and/or pigments may be contained in the negative or positive type coatings. 
     The negative type photosensitive coating resin preferably employed in the present invention may be a resin into which ethylenic double bonds crosslinkable by light are introduced and may include a prepolymer or resin having photosensitive groups such as (meth)acryloyl groups, e.g. acryloyl or methacryloyl group, cinnamoyl groups or mixtures thereof at a terminal and/or side chain of the molecule, an onium group-containing cationic resin or a carboxylic group-containing anionic resin. The negative type photosensitive coating resin may have a molecular weight ranging between 500 and 10,000 
     The prepolymer may preferably be formed from epoxy (meth)acrylate, urethane (meth)acrylate, polyester (meth)acrylate, or mixtures thereof. 
     The onium group-containing cationic resins may be composed of a main resin, such as acrylic resin, polyester resin, maleinated oil resin, polybutadiene resin, epoxy resin, urethane resin, polyamide resin or mixtures thereof, and the photosensitive groups and onium groups, such as amino group, ammonium group, sulfonium group or mixtures thereof, introduced therein. These resins may preferably be neutralized with an acidic susbstance such as formic acid, acetic acid, propionic acid, lactic acid or mixtures thereof, and solubilized and/or dispersed in water. 
     The carboxyl group-containing anionic resins may be composed of the above mentioned main resin into which carboxylic groups and the aforementioned photosensitive groups are introduced. These resins may preferably be solubilized and/or dispersed in basic substances, such as triethylamine, diethylamine, dimethylethanol amine, ammonia or mixtures thereof. 
     There is no particular limitation to the positive type photosensitive coating resin, if exposed portions of the resin are dissolved in a developing solution on light exposure, and may be enumerated by resins including quinone diazido groups, resins including diazomeldrum&#39;s acid or nitrobenzyl ester, or resin compositions including these resins. Specific examples of these resins include a quinone diazido group-containing cationic resin in which the onium groups and hydroxyl groups are introduced into the above main resins, to which a quinone diazido sulfonic acid compound is added further by esterification reaction followed by being neutralized with an acidic substance such as formic acid, acetic acid, propionic acid, lactic acid or mixtures thereof and solubilized and/or dispersed in water; a quinone diazido group-containing anionic resin in which carboxyl groups and hydroxyl groups are introduced into the above mentioned main resins, to which a quinone diazido sulfonic acid compound is further added by an esterificiation reaction followed by being neutralized with basic substances e.g. triethylamine, diethylamine, dimethylethanol a, mine, ammonia or mixtures thereof, and solubilized and/or dispersed in water; a quinone diazido group-containing resin obtained by reacting a resin having Film-forming capability and a hydroxyl group-compound with a quinone diazido compound including a quinone diazido sulfonic acid derivative or an isocyanate group; and resin compositions containing these resins. The mixing ratio for the resin compositions may be optionally selected depending on light exposure and development conditions. 
     As the negative type photosensitive coating resin and the positive type photosensitive coating resin, prepolymers or resins that may be solubilized and/or dispersed in water are most preferred for simplifying the process and combating the pollution. 
     The negative type photosensitive coating resins may also be admixed with low molecular (meth)acrylates for controlling photosensitive properties and viscosity of the coating film. Examples of such (meth)acrylates include 2-hydroxyethyl (meth)acrylate, 2-phenoxyethyl (meth)acrylate, 3-phenoxy-2-hydroxypropyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, tricyclodecane (meth)acrylate, hexanediol-di(meth)acrylate, trimethylolpropane triacrylate, pentaerythritol triacrylate, dipentaerythritol hexacrylate, tris(acryloyl oxyethyl) isocyanurate, and mixtures thereof. The proportion of these (meth) acrylates is preferably up to 50 and most preferably up to 30 parts by weight to 100 parts by weight of the negative type photosensitive coating resin. If the proportion of the (meth)acrylates exceeds 50 parts by weight, the coating becomes undesirably tacky. 
     The photopolymerization initiator employed in the negative type photosensitive coating may be any of those known in the art and may be enumerated by benzoins, benzoin ethers, benzilalkyl ketals, benzophenone derivatives, anthraquinone derivatives, thioxanthone derivatives or mixtures thereof. Sensitizers may be added thereto if so desired. The photopolymerization initiator may be added in an amount of 0.1 to 30 parts and preferably 0.5 to 20 parts by weight to 100 parts by weight of the negative type photosensitive coating resin. If the amount of the initiator is less than 0.1 part by weight, photocuring properties fall short, whereas if it exceeds 30 parts by weight, curing proceeds excessively and hence the coating film becomes poor in strength, while economic advantages are also lost. 
     The organic solvent used for dispersing or dissolving the components of the negative and positive type photosensitive coating resins may be any of those capable of dispersing or dissolving the above mentioned prepolymers or resins. Examples of the solvents include glycol ethers, such as ethyleneglycol monobutyl ether, ethyleneglycol monohexyl ether, ethyleneglycol monophenyl ether, propyleneglycol monomethyl ether, propyleneglycol monophenyl ether, diethyleneglycol dimethyl ether or triethyleneglycol dimethyl ether; ketones such as acetone, methylethyl ketone, methylisobutyl ketone, cyclohexanone, N-methyl pyrrolidone or isophorone; ethers such as dibutyl ether, dioxane or tetrahydrofuran; alcohols such as methoxy butanol, diacetone alcohol, butanol, octanol or isopropanol; hydrocarbons such as toluene, xylene, cyclohexane or hexane; esters such as ethyl acetate, butyl acetate, 2-methoxyethyl acetate, 2-methoxypropyl acetate or ethyl benzoate; acid amides such as dimethyl formamide, N,N-dimethyl acetoamide or dimethyl sulfoxide, and mixtures thereof. 
     These organic solvents may be added during solubilization or dispersion in water of the above mentioned cationic or anionic resins for improving bath stability or smoothing coating films. 
     The hue of the dyes and/or pigments mixed with the positive type or negative type photosensitive coating may be selected freely depending on objects, if so desired. For example, in order to improve resolution of the photosensitive coating, it is preferred to incorporate dyes absorbing light having wavelength of 400 to 500 nm such as oil yellow or ultraviolet ray absorber, e.g. trihydroxy benzophenone to remove light having broad wavelength which exhibits large diffraction upon exposure. Two or more dyes and/or pigments may be mixed to obtain desired hue unless their characteristics are impaired. 
     The dyes and/or the pigments are preferably so selected as not to lower the stability and occasionally electrodeposition properties as well as durability of the coating. For this reason, oil soluble or dispersible dyes, such as azo, anthraquinone, benzodifuranone, condensed methine series dyes, or mixtures thereof, are preferred. The pigments may be exemplified by organic pigments, such as azo lake organic pigments, quinacridone organic pigments, phthalocyanine organic pigments, isoindolinone organic pigments, anthraquinone organic pigments or thioindigo organic pigments; chrome yellow, iron oxide, chrome vermilion, chrome green, ultramarine, prussian blue, cobalt blue, cobalt green, emerald green, titanium white, carbon black or mixtures thereof. As for the color hue of the dyes and pigments, reference is had to &#34;COLOUR INDEX&#34; whenever necessity arises. 
     The amount of the dyes and/or the pigments is suitably selected depending on the application, color hue, the type of the dyes and/or the pigments or the film thickness of the photosensitive coating. The amount may preferably be 0.1 to 10 wt. % and more preferably 0.5 to 5.0 wt. % based on the total photosensitive coating. 
     For producing the negative type photosensitive coating, the negative type photosensitive coating resins, the photopolymerization initiator and the solvent are sufficiently dispersed, using a dispersion apparatus, such as customary sand mills, roll mills or attriters. The positive type photosensitive coating may be prepared by mixing and dispersing the resins for the positive type photosensitive coating and the solvent in the same manner as for the negative type coating. The dyes, pigments, acidic or basic substances, dispersants, levelling agents for improving smoothness of the coating film, viscosity adjustment agents or defoaming agents may be mixed and dispersed as needed. There is no limitation to the film thickness of the photosensitive coating films formed by the photosensitive coating and the film thickness may be suitably selected depending on the performance desired of the color filter. The dry film thickness may be usually 0.3 to 20 μm and preferably 1 to 15 μm. The film thickness may be adjusted by controlling, for example electrodeposition conditions, such as electric current, voltage, electrodeposition time and bath temperature. However, film thickness adjustment may be usually made under the same conditions as those for electrodeposition coating of colored coatings, as will be explained subsequently. In case where the negative type photosensitive coating film is used, the film thickness may usually be as thick as approximately 5 to 15 μm or may be formed to have a thickness of approximately 0.3 to 10 μm followed by forming an oxygen-barrier film such as polyvinyl alcohol to reduce hardening prevention action due to oxygen and to prevent contamination of the mask or formation of pinholes. 
     According to the present invention, exposure of the photosensitive coating film is to be performed by using a mask having patterns of at least three different degrees of light transmittances. The light transmittance means an intensity ratio before and after transmission of the exposure light through the mask. At least three different light transmittance degrees of the mask patterns will suffice depending on the number of types of the colored coatings. The difference in the light transmittance degrees may be optionally determined depending on the conditions of light exposure and development. In general, the larger the relative difference in the respective light transmittances, the easier becomes the adjustment of light exposure time, which is more desirable. However, even if the difference in the light transmittances is small, the same objective may be achieved by enhancing the volume of light exposure or prolonging the light exposure time. Thus, a significant difference of 5% or more is desirable, although no imitations are placed on the relative difference in the light transmittances. 
     Light exposure may be usually achieved using a system radiating a large quantity of ultraviolet rays. For example, a high pressure mercury lamp, an ultra high pressure mercury lamp or a metal halide lamp may be used as a light source. If necessary, other radiation rays may also be employed. Light exposure conditions may be selected suitably depending on photosensitive coatings employed, light exposure devices and masks. 
     In the step A of the present invention, by effecting light exposure through a mask having patterns of at least three different degrees of light transmittances, a number of different exposure states which is the same as that of the different light transmittance degrees of the patterns may be provided in the photosensitive coating film. 
     In the method of the present invention, the step of forming a colored layer by applying a colored coating by electrodeposition on the transparent electrically conductive layer exposed after developing and removing the photosensitive coating film is repeated, next to the step A, in the order of the increasing light transmittance degrees of the patterns with use of the negative type photosensitive coating and in the order of the decreasing light transmittance degrees of the patterns with use of the positive type photosensitive coating, for producing the respective colored layers. That is, if the negative type photosensitive coating is employed, the portion of the photosensitive coating film corresponding to a pattern of the smallest degree of light transmittance of the patterns is selectively developed and removed, and the colored coating is electrodeposited on the exposed transparent electrically conductive layer to form a colored layer (step B). The portion of the coating film corresponding to the second smallest light transmittance degree of the patterns is then selectively developed and removed and the colored coating is electrodeposited on the exposed electrically conductive layer to form a colored layer. This sequence of operations is repeated to produce the colored layers, respectively (step B). If the positive type photosensitive coating is employed, the portion of the photosensitive coating film corresponding to a pattern of the largest light transmittance of the mask is selectively developed and removed and a colored coating is electrodeposited on the exposed transparent electrically conductive layer to form a colored layer (step B). The portion of the coating film corresponding to the second largest light transmittance degree of the patterns is then selectively developed and removed and a colored coating is electrodeposited on the exposed electrically conductive layer to form a colored layer. This sequence is repeated to produce the respective colored layers (step B). 
     The conditions for selectively developing and removing the photosensitive coating film may be changed depending on the volume of light exposure, solubility of the photosensitive coating in the developing solution, the types and the concentrations of the developing solution, development time and temperatures. Thus, the conditions may be suitably selected for the resin used for the preparation of the photosensitive coating. Specifically, aqueous solutions containing dissolved acidic materials may be used as a developing solution when the cationic resin is used as a component of the negative photosensitive coating. The acidic materials include organic acids, such as formic acid, acetic acid, propionic acid or lactic acid; inorganic acids, such as hydrochloric acid or phosphoric acid; and mixtures thereof. If lactic acid is used as a developing solution, it may be used at a concentration usually of 0.01 to 50 wt. % and preferably 0.05 to 25 wt. %. The developing temperature is usually 10° to 70° C. and preferably 15° to 50° C. and the developing time is usually 2 to 600 seconds and preferably 30 to 300 seconds. As a developing solution in case of employing an anionic resin as a component of the negative type photosensitive coating and as a developing solution for the positive type photosensitive coating, an aqueous solution containing basic substances dissolved therein, may be employed. The basic substances may include sodium carbonate, sodium hydrogen carbonate, sodium metasilicate, tetraalkyl ammonium hydroxide, sodium hydroxide, potassium hydroxide and mixtures thereof. If an aqueous solution of sodium carbonate is used as a developing solution, sodium carbonate may be used in a concentration range of 0.01 to 25 wt. % and preferably 0.05 to 20 wt. % for development. The development time usually is selected within a range of 2 to 600 and preferably 30 to 300 seconds generally at 10° to 70° C. and preferably 15° to 50° C. A developing solution when the positive type photosensitive coating is employed may usually be an aqueous solution in which a basic material is dissolved. The basic material includes sodium carbonate, sodium hydrogen carbonate, sodium metasilicate, tetraalkyl ammonium hydroxide, sodium hydroxide, potassium hydroxide and mixtures thereof. For example, where an aqueous solution of sodium metasilicate is employed as a developing solution, development may be effected at the concentration of sodium metasilicate of 0.01 to 25 wt. % and preferably 0.05 to 20 wt. %. The developing temperature may usually be 10 ° to 70° C. and preferably be 15° to 50° C. and the developing time may be 2 to 600 seconds and preferably 30 to 300 seconds. For the developing solutions, organic solvents such as alcohols, glycol ethers, ketones, chlorinated hydrocarbons or mixtures thereof, may be employed. Surfactants or defoaming agents may also be added to these developing solutions for improving wettability or anti-foaming properties. Aqueous developing solutions are preferably employed in view of non-toxicity and sanitation in working environments. 
     Where the oxygen-barrier film is formed on the negative type photosensitive coating film, the oxygen-barrier film should be removed in advance of the aforementioned development. The removal of the oxygen-barrier film may be effected in any way depending upon the kinds of the films used. For example, if polyvinyl alcohol is used for forming the film, deionized water or an aqueous solution in which a surface active agent is added to deionized water may be employed as a removing agent. To effect the removal promptly, the removing agent may be heated to 30° to 60° C. 
     After the development, colored coatings are electrodeposited on the exposed transparent electrically conductive layer for forming a colored layer in step B. 
     In preparing the colored coating, cationic resins or anionic resins or photocurable resins are used as a film-forming component, and dyes and/or pigments are added as a colorant component. Acidic or basic substances may also be employed for dissolving and/or dispersing these components in water. Organic solvents may be added for facilitating dissolution and/or dispersion of the resins in the colored coating for improving bath stability or for producing smooth coating films. If the positive type photosensitive coating film is used in step A, a cationic resin is preferably used for preparation of the colored coating used in step B. On the other hand, if the negative type photosensitive coating film used in step A is composed of a cationic resin, an anionic resin is preferably used for preparation of the colored coating used in step B, whereas if the negative type photosensitive coating film used in step A is composed of an anionic resin, a cationic resin is preferably used for preparation of the colored coating employed in step B although not limited to such combinations. 
     The cationic resins may for example be resins composed of the main resins used in the photosensitive coating into which onium groups such as ammonium, sulfonium groups or amino groups are introduced, such as resins solubilized or dispersed in water with an acidic substance, such as formic acid, acetic acid, propionic acid, lactic acid or mixtures thereof. 
     The anionic resins may for example be resins composed of the main resins used in the photosensitive coating into which carboxyl groups, etc. are introduced, and may for example be resins solubilized or dispersed in water with basic substances such as triethylamine, diethylamine, dimethylethanol amine, ammonia or mixtures thereof. 
     As the photocurable resins, those prepolymers or resins containing acryloyl groups, methacryloyl groups, cinnamoyl groups or mixtures thereof, that are used in the photosensitive coating film in the step A and that are suited for electrodeposition, may be employed. The above mentioned photopolymerization initiators may also be employed in combination. Resin components for preparation of the colored coating may include highly thermosetting electrodeposition resins such as a mixed resin of acrylic resin and a melamine resin. 
     The colored coatings employed in step B may be different in type, color hue, color concentration or color brightness in the regions exhibiting different light transmittances. Alternatively, the same colored coatings may be used in common for these regions. 
     The color hue of the colored coating may be selected depending on the objects. For example, the colored coatings having different color hue may be employed for the photosensitive coating used in the step A, the colored coating used in step B and the plural colored coatings used in step B, respectively. 
     The dyes and/or pigments used in the colored coatings may be suitably selected depending on the targeted color hue. It is, however, preferred to use those dyes and/or pigments which are not unsatisfactory in transparency, stability, electrodeposition properties and durability of the coating film. Those dyes or pigments may be mixed as the occasion may demand if their properties are not impaired. 
     In the preparation of the colored coatings, resins, dyes and/or pigments, acidic or basic substances, organic solvents, dispersants for the dyes or pigments, levelling agents for improving smoothness of the coating films, viscosity controlling agents or anti-foaming agents are mixed together and dispersed sufficiently in a conventional dispersion device such as sand mill, roll mill or attriter. The resulting dispersion is diluted in water to a predetermined concentration of about 4 to 25 wt. % and preferably to 7 to 20 wt. % of solid content to produce a coating suitable for electrodeposition. The so-produced coating may be applied on the electrically conductive layer by electrodeposition for providing a colored layer. 
     There is no particular limitation to the film thickness of the colored layer, which may be suitably selected depending on the performance required of a color filter. However, the dry thickness is usually 0.3 to 5 μm and preferably 1 to 3 μm. 
     Although the conditions of electrodeposition may be suitably selected depending on the types of the colored coatings and film thickness of the colored coating films, the electrical voltage is usually 5 to 500 V dc and preferably 10 to 300 V dc, the electrodeposition time is usually 5 to 300 sec and preferably 10 to 200 sec and the liquid temperature is usually 10°to 35° C. and preferably 15° to 30° C. After lapse of the electrodeposition time sufficient to produce a desired film thickness, current conduction is discontinued and the substrate is taken out of the bath. The substrate is freed of excess bath liquid by washing with water and dried to produce the colored layer. 
     Although the drying conditions may be selected suitably depending on the conditions of the subsequent process steps, it is usually preferred that the conditions be such that surface moisture is dried, for example, the drying time be of the order of 0.5 to 60 minutes and preferably 5 to 30 minutes at a temperature of 150° C. or lower and preferably 60° to 120° C. If the drying temperature is higher than 150° C., the photosensitive coating film is occasionally cured under heat to raise difficulties in the subsequent development process. 
     Although the desired color filter may be produced by the above described steps (A) and (B), heating, curing or photocuring may be effected, if needed, for further improving weatherability or resistance to chemicals. If heating or curing is effected, the temperature is usually 100° to 250° C. and preferably 150° to 250° C. and the processing time is usually 5 minutes to one hour and preferably 15 to 40 minutes. 
     The process according to embodiments of the present invention will be hereinafter explained by referring to FIGS. 1 to 5. It should be noted that the present invention is not limited to this merely illustrative embodiments. 
     FIG. 1 shows one embodiment of the present process step by step. FIG. 2 is a diagramatic view showing the steps of producing a transparent substrate having both a light-intercepting layer and a transparent electrically conductive layer shown in FIG. 1 according to one embodiment of the present invention. FIG. 3 is an enlarged schematic view showing a mask for producing a light-intercepting layer partially or, the transparent electrically conductive layer. FIG. 4 is an enlarged schematic view showing the transparent substrate having both the light-intercepting layer and the transparent electrically conductive layer produced by using the mask shown in FIG. 3. FIG. 5 shows, in an enlarged schematic view, a mask having four different degrees of light transmittances according to an embodiment of the present invention, wherein 5 is a mask region having a 100% light transmittance, 6 is a mask region having a 5% light transmittance corresponding to a first color region, 7 is a 25% light transmittance mask region corresponding to a second color region and 8 is a 80% light transmittance mask region corresponding to a third color region. 
     First, a positive type photosensitive coating film is formed of a transparent substrate having a transparent electrically conductive layer thereon. A mask for producing a light-intercepting layer shown in FIG. 3 is placed on the thus formed substrate and exposed to light. Through the ask shown in FIG. 3, a positive type photosensitive coating film portion corresponding to a light-intercepting layer portion 1 is exposed, while a positive type photosensitive coating film portion corresponding to a transparent electrically conductive layer portion 2 is not exposed to light. After exposure, the exposed photosensitive coating film portion (portion 4 in FIG. 4) is developed and removed to expose a transparent electrically conductive layer portion correspond to the light-intercepting layer portion 1. Next, an electrodeposition black coating insoluble into a developing liquid is electrodeposited onto the substrate and dried followed by light exposure on the overall surface. The electrodeposited film is heated to obtain a substrate (hereinafter referred as &#34;substrate 1&#34;) in which a black light-intercepting layer 4 is formed partially on the transparent electrically conductive layer. 
     Then, a negative type photosensitive coating film is formed on the surface of the substrate 1. The substrate is then dried and exposed to light through, for example a mask shown in FIG. 5. A first development operation is then performed for exposing or laying to outside a region of the electrically conductive layer which is in register with the 5% transmittance mask region 6 and which corresponds to the first color region. The substrate 1 is then dipped in an electrodeposition bath containing a first colored coating for electrodeposition coating followed by washing with water. 
     A second development operation is then carried out under conditions different from those employed in the first development operation, for exposing or laying to outside a region of the electrically conductive layer which is in register with the 25% light transmittance mask region 7 and which corresponds to the second color region. The substrate is then dipped in an electrodeposition bath containing a second colored coating for electrodeposition coating followed by washing with water. 
     A third developing operation is then carried out under conditions different from those employed in the first or second developing operations for exposing or laying to outside a region of the electrically conductive layer which is in register with the 80% light transmittance mask region 8 and which corresponds to the third color region. The substrate is then subjected to electrodeposition coating in an electrodeposition bath containing a third colored coating followed by washing with water and drying for forming colored layer. 
     A fourth developing operation is then carried out under conditions different from those of the first to third developing operation, for removing a negative type photosensitive coating film region which is in register with the 100% transmittance mask region 5 to expose the light-intercepting layer. 
     With the present, method for producing a color filter, patterning may be achieved by one light exposure operation with an increased degree of freedom in the patterned shapes of the colored layers without the necessity of highly advanced fine processing techniques while increased color filter size can be coped with. Thus, the color filter may be mass-produced relatively easily. Besides, according to the present invention a color filter having a highly precision light-intercepting layer can be produced. 
     EXAMPLES OF THE INVENTION 
     The present invention will be explained hereinbelow with reference to Synthesis Examples and Examples which are given only for illustration and are not intended for limiting the invention. In these examples, parts are shown in terms of parts by weight. 
     Synthesis Example 1 
     Synthesis of Cationic Positive Type Photosensitive Coating (X-1) 
     Synthesis of Unsaturated Compound (x-1) 
     148 parts of glycidol, 0.8 part of dibutyl tin dilaurylate, 0.2 part of hydroquinone monomethyl ether and 82 parts of 2-ethoxyethyl acetate were charged into a 1-lit separable flask fitted with a thermometer, an agitator, a reflux cooling tube, a gas inlet pipe and a dropping funnel, and the temperature was raised to 50° C. 319 parts of methacryloyloxyethyl isocyanate were added dropwise over an hour as air was blown into the system and reaction was carried out until absorption of the isocyanate groups in absorption spectrum substantially disappeared. 276 parts of 4-hydroxybenzoic acid were added, and the temperature was raised to 110° C. After it was confirmed that the acid value was not more than 5 and the epoxide equivalent weight was not less than 11,000, the reaction was discontinued to produce an unsaturated compound (x-1). 
     Synthesis of Cationic Positive Type Photosenstive Resin (x-2) 
     238 parts of diethyleneglycol monoethyl ether were charged into a 1-lit separable flask fitted with a thermometer, an agitator, a reflux cooling tube and a dropping funnel, and the temperature was raised to 130° C. Into this mixture, a mixed solution composed of 145 parts of (x-1), 83 parts of isobutyl methacrylate, 167 parts of ethyl acrylate, 78 parts of ethyl methacrylate, 41 parts of dimethylaminoethyl methacrylate and 12 parts of t-butyperoxy-2-ethyl hexanoate were added dropwise over three hours. After lapse of 30 minutes, a mixed solution of 25 parts of diethylene glycol monoethyl ether and 2 parts of t-butylperoxy-2-ethyl hexanoate was added dropwise over 30 minutes. The resulting mixture was maintained at this temperature for two hours to terminate the reaction. 500 parts of the produced acrylic resin solution were taken into a 3-lit separable flask fitted with a thermometer, an agitator, a reflux cooling tube, a nitrogen inlet pipe and a dropping funnel Into this mixture 1570 parts of acetone and 60.1 parts of 1,2-naphthoquinonediazido-5-sulfonyl chloride were added, and the resulting mixture was agitated throughly at room temperature. Into the resulting mixture, 26.7 parts of triethylamine were added dropwise over an hour, and reaction was continued for further two hours. The produced solution was filtered to remove impurities. The resulting mixture was added dropwise over about one hour into a 20-fold quantity of well-agitated water and precipitated resins were recovered. After removal of the moisture under reduced pressure, a brownish cationic positive type photosensitive resin (x-2) was produced. 
     Synthesis of Cationic Positive Type Photosenstive Coating (X-1) 
     500 g of a cationic positive type photosensitive resin (x-2) were dissolved in 333.3 g of methyl ethyl ketone. 11.7 g of acetic acid were added as a neutralizer and the resulting mixture was agitated sufficiently and homogenized. As deionized water was added gradually, the resulting mixture was agitated vigorously by a high-speed mixer to effect dispersion in water to prepare an aqueous solution (X-1) of a cationic positive type photosensitive coating (cationic electrodeposition type). 
     Synthesis Example 2 
     Synthesis of Anionic Positive Type Photosensitive Coating (X-2) 
     Synthesis of Anionic Resin (x-3) 
     1,000 g of &#34;NISSEKI POLYBUTADIENE B-1000&#34; (manufactured by NIPPON PETROCHEMICALS CO., LTD.; number average molecular weight, 1,000; iodine value, 430; content of 1,2-linkage, 85%), 751 g of maleic anhydride, 10 g of xylene and 5.0 g of trimethylhydroquinone, were charged into a 3-lit separable flask fitted with a thermometer, an agitator, a reflux cooling tube and a nitrogen blowing pipe, and reaction was carried out at 190° C. for 5 hours under nitrogen. After non-reacted maleic anhydride and xylene were distilled off, maleinated polybutadiene with a total acid value of 480 mg KOH/g was produced. 
     Then, 500 g of the maleinated polybutadiene, 218 g of phenoxyethanol and 205 g of diethyleneglycol dimethyl ether were charged into a 2-lit separable flask fitted with a reflux cooling tube, and dissolved homogeneously. Reaction was then carried out under nitrogen at 130° C. for three hours. Then, 61 g of benzylamine were added dropwise for 30 minutes at the same temperature and the temperature was raised to 165° C. Reaction was carried out at this temperature for seven hours to produce a solution of an anionic resin (x-3) containing hemi-ester and imide groups. 
     Synthesis of Photosensitive Resin (x-4) 
     1000 g of &#34;NISSEKI POLYBUTADIENE B-1000&#34; (manufactures by NIPPON PETROCHEMICALS CO., LTD.; number average molecular weight, 1,000; iodine value, 430; content of 1,2-linkage, 65%), 388 g of maleic anhydride, 10 g of xylene and 3.0 g of trimethyl hydroquinone were charged into a 3-lit separable flask fitted with a thermometer, an agitator, a reflux cooling tube and a nitrogen blowing pipe, and reaction was carried out at 190° C. for 5 hours under nitrogen. After non-reacted maleic anhydride and xylene were distilled off, maleinated polybutadiene with a total acid value of 320 mg KOH/g was produced. 
     Then, 500 g of the maleinated polybutadiene and 300 g of phenoxyethanol were charged into a 2-lit separable Flask fitted with a thermometer, an agitator, a reflux cooling tube and a nitrogen blowing tube and dissolved homogeneously. Reaction was then carried out under nitrogen at 130° C. for three hours. After cooling to room temperature, 149 g of 2-(2-aminoethylamino)ethanol were added dropwise over an hour. The temperature was then raised to 125° C., at which temperature the reaction was carried out for four hours to produce a solution of polyamine resin containing imido groups. 
     Into a 5-lit separable flask fitted with a reflux cooling tube were charged 269 g of 1,2-naphthoquinoneazidosulfonyl chloride, 1900 g of dioxane and 300 g of &#34;KYOWARD 1000&#34; manufactured by KYOUWA CHEMICAL INDUSTRY CO., LTD. Then, 645 g of the polyamine resin solution were added dropwise at 30° C. over two hours and reaction was carried out at this temperature further for five hours. After the produced solution was filtered, 440 g of phenoxy ethanol was added and dioxane was removed under reduced pressure to produce a photosensitive resin (x-4). 
     The produced resin (x-4) in solution contained 150 mg equivalent of naphthoquinone diazido groups per 100 g of resin, and the non-volatile content amounted to 60.0 wt. %. 
     Synthesis of Anionic Positive Type Photosensitive Resin (x-5) 
     750 g of the (x-3) resin solution and 670 g of the (x-4) photosensitive resin were mixed thoroughly followed by adding 60 g of triethylamine for sufficient neutralization to produce an anionic positive type photosensitive resin (x-5) in solution, 
     Synthesis of Anionic Positive Type Photosensitive Coating (X-2) 
     Deionized water was added gradually to 500 g of a solution of an anionic positive type photosensitive resin (x-5) and the resulting mixture was agitated vigorously with a high-speed mixer to effect dispersion in water for preparing an aqueous solution of an anionic positive type photosensitive coating (X-2) (an anionic electrodeposition type.) 
     Synthesis Example 3 
     Synthesis of Cationic Negative Type Photosensitive Coating (X-3) 
     Synthesis of Amine-added Expoxidated Polybutadiene (x-6) 
     1,000 g of epoxidated liquid polybutadiene (manufactured by NIPPON PETROCHEMICALS CO., LTD. under the trade name of &#34;E-1000-8&#34;, with a number average molecular weight of 1,000 and an oxirane oxygen content of 8%), were charged into a 2 lit separable flask, fitted with a thermometer, a stirrer and a reflux cooling pipe. After replacing the atmosphere within the system by nitrogen, 231.2 g of methylethanolamine were added and reaction was carried out at 170° C. for five hours. Non-reacted methylethanolamine was then distilled off under reduced pressure to produce amine-added epoxidated polybutadiene (x-6) with an amine value of 230.4 mmol/100 g. 
     Synthesis of Unsaturated Groups--Containing Isocyanate Compound (x-7) 
     435.5 g of 2,4-tolylene diisocyanate and 266.1 g of diethylene glycol dimethyl ether were charged into a 2-lit round-bottom flask, which might be heated and cooled and which was fitted with a thermometer, a stirrer, a reflux cooling pipe and a dropping funnel. After heating to 40° C., 362.8 g of 2-hydroxyethyl acrylate were added dropwise from the dropping funnel. 200 ppm of p-benzoquinone was also added at this time. Since some heat was evolved due to dropwise addition of 2-hydroxyethyl acrylate, the system was occasionally cooled for maintaining the constant temperature. After the end of the dropwise addition of 2-hydroxyethyl acrylate, the temperature was raised to 70° C., at which temperature the reaction was carried out for three hours. After the IR absorption spectral analyses revealed that the absorption intensity of the isocyanate groups was decreased to about one half that before start of the reaction, the reaction system was cooled to produce an unsaturated group-containing isocyanate compound (x-7). 
     Synthesis of Cationic Resin (x-8) 
     500 g of (x-6) were dissolved in 166.7 g of diethylene glycol dimethyl ether in a 2 lit separable flask. 713.4 g of (x-7), in which isocyanate groups are contained in an amount of 0.8 equivalent to 1 equivalent of hydroxyl groups in (x-6) , were added dropwise at 40° C., at which temperature the reaction was carried out for one hour. The IR absorption spectral analyses indicated that the isocyanate groups had disappeared. A cationic resin (x-8), in which (x-7) was added to (x-6), was produced. 
     Synthesis of Cationic Negative Type Photosensitive Coating (X-3) 
     To 500 g of the cationic resin (x-8) were added 27.0 g of &#34;IRGACURE 907&#34; (manufactured by CIBA-GEIGY INC.) and 3.0 g of &#34;KAYACURE DETX&#34; (manufactured by NIPPON KAYAKU (CO. LTD.) , as photopolymerization initiators, under agitation, and 16.7 g of acetic acid were added to the resulting mass as a neutralizer. The resulting mixture was agitated thoroughly and re-homogenized. Deionized water was added gradually to the homogenized mass and the resulting mixture was agitated vigorously by a high-speed mixer to effect dispersion in water to prepare an aqueous solution of the cationic negative type photosensitive coating (X-3) (the cationic electrodeposition type). 
     Synthesis Example 4 
     Synthesis of Anionic Negative Type Photosensitive Coating (X-4) 
     Synthesis of Hemi-Ester Product (x-9) Solution 
     1,000 g of &#34;NISSEKI POLYBUTADIENE B-1000&#34; (trade name of a product manufactured by NIPPON PETROCHEMICALS CO., LTD., with a number average molecular weight of 1,000, an iodine value of 430, and 1,2-linkage of 65 percent), 554 g of maleic anhydride, 10 g of xylene and 8.0 g of trimethyl-hydroquinone were charged into a 8 lit separable flask, fitted with a thermometer, a stirrer, a reflux cooling pipe and a nitrogen blowing tube, and reaction was carried out under nitrogen at 190° C. for five hours. After non-reacted maleic anhydride and xylene were distilled off, maleinated polybutadiene with a total acid value of 400 mg KOH/g was produced. 
     Then, 400 g of the maleinated polybutadiene and 188.5 g of diethyleneglycol dimethyl ether and 0.4 g of hydroquinone were charged into a 2-lit flask fitted with a reflux cooling tube and the temperature was raised to 80° C. After the mixture was dissolved uniformly, 165.6 g of 2-hydroxyethyl acrylate and 20 g of triethylamine were added and reaction was carried out at 80° C. for two hours to produce a hemi-esterified product (x-9) in solution. The total acid value of the produced hemi-esterified product (x-9) in solution was 105 mg KOH/g and the non-volatile content amounted to 75.0 wt. %. 
     Synthesis of Anionic Negative Type Photosensitive Coating (X-4) 
     To 500 g of the produced solution of the hemi-ester (x-9) were added 27.0 g of &#34;IRGACURE 907&#34; (manufactured by CIBA GEIGY INC. and 3.0 g of &#34;KAYACURE DETX&#34;, manufactured by NIPPON KAYAKU CO. LTD.), as photopolymerization initiators. To the resulting mass were added 33.7 g of triethylamine as a neutralizer and the resulting mass was agitated thoroughly and re-homogenized. Deionized water was added gradually to the resulting mass and the resulting mixture was agitated vigorously with a high-speed mixture to effect dispersion in water to prepare an aqueous solution of an anionic negative type photosensitive coating (X-4) (anionic electrodeposition type). 
     Synthesis Example 5 
     Preparation of Colored Coatings (Y-1, Y-2 and Y-3) 
     A solution of the cationic resin (x-8), a photopolymerization initiator and pigments were mixed under agitation and dispersed by a laboratory type three-roll roll mill (produced by KODAIRA SEISAKUSHO KK) until the pigment reached a particle size of 0.2 μm or less. The particle size was measured using a COULTER counter N4 (produced by COULTER INC). To each resulting dispersion mixture was added acetic acid as a neutralizer and each of the mixtures was agitated thoroughly for re-homogenization. Each of the resulting masses was dispersed in water under gradual addition of deionized water and under agitation vigorously with a high-speed mixer, to produce each colored coating (Y-1, Y-2 and Y-3) having a solid concentration of 10 wt. %. The compositions of the aqueous solutions of the three-color colored coatings (cationic electrodeposition type) are shown in Table 1. (In Table 1 the numerical figures denote parts by weight). 
     
                       TABLE 1                                                     
______________________________________                                    
Coating No.          Y-1     Y-2     Y-3                                  
Color                Red     Green   Blue                                 
Cationic resin (x-8) solution                                             
                     213.3   213.3   213.3                                
IRGACURE 907 (*)     11.5    11.5    11.5                                 
KAYACURE DETX (**)   1.3     1.3     1.3                                  
Acetic acid (Neutralizer)                                                 
                     19.8    19.8    19.8                                 
Phthalocyanine Blue (***)                                                 
                     --      --      20                                   
Phthalocyanine Green (****)                                               
                     --      20      --                                   
Azo Metal Salt Red Pigment (*****)                                        
                     20      --      --                                   
______________________________________                                    
 (*) &#34;IRGACURE 907&#34; mfd. by CIBAGEIGY INC.                                
 (**) &#34;KAYACURE DETX&#34; mfd. by NIPPON KAYAKU CO., LTD.)                    
 (***) Phthalocyanine Blue &#34;SR150C&#34; (mfd. by SANYO SHIKISO KK)            
 (****) Phthalocyanine Green &#34;SAX&#34; (mfd. by SANYO SHIKISO KK)             
 (*****) &#34;PIGMENT RED 4BS&#34; (mfd. by SANYO SHIKISO KK)                     
 
    
     Synthesis Example 6 
     Preparation of Colored Coatings (Y-4, Y-5 and Y-6) 
     The solution of the hemi-ester (x-9) and a pigment were mixed under agitation and dispersed by a laboratory type three-roll roll mill (manufactured by KODAIRA SEISAKUSHO KK), until the pigment particle size of 0.2 μm or less was reached. The particle size was measured using a COULTER counter N4 (manufactured by COULTER INC). To each resulting dispersion mixture was added triethylamine as a neutralizer and the resulting mixture was agitated sufficiently and re-homogenized. Deionized water was added gradually and each resulting mixture was agitated vigorously by a high-speed mixer to effect dispersion in water to prepare each of colored coatings (Y-4, Y-5 and Y-6) having a solid concentration of 10 wt. %. The compositions of the aqueous solutions of the three-color colored coatings of the anionic electrodeposition type are shown in Table 2. (In Table 2, the numerical values in Table 2 represent parts by weight). 
     
                       TABLE 2                                                     
______________________________________                                    
Coating No.         Y-4     Y-5     Y-6                                   
Color               Red     Green   Blue                                  
Hemi-Ester Product  213.3   213.3   213.3                                 
(x-9) Solution                                                            
Triethylamine (Neutralizer)                                               
                    21.0    21.0    21.0                                  
Phthalocyanine Blue (*)                                                   
                    --      --      20                                    
Phthalocyanine Green (**)                                                 
                    --      20      --                                    
Azo Metal Salt Red Pigment (***)                                          
                    20      --      --                                    
______________________________________                                    
 (*) &#34;SR150C&#34; manufactured by SANYO SHIKISO KK                            
 (**) &#34;SAX&#34; manufactured by SANYO SHIKISO KK                              
 (***) &#34;Pigment Red 4BS&#34; manufactured by SANYO SHIKISO                    
 
    
     Synthesis Example 7 
     Preparation of Colored Coating (Y-7) 
     To 500 g of a solution of the cationic resin (x-8) were added 27.0 g of &#34;IRGACURE 907&#34; (produced by CIBA GEIGY INC.) as a photopolymerization initiator, 3.0 g of &#34;KAYACURE DETX&#34; (produced by NIPPON KAYAKU CO., LTD.), and 37.5 g of &#34;CARBON BLACK #5B&#34; (produced by MITSUBISHI KASEI CORPORATION), under agitation and the resulting mass was dispersed by a laboratory three-roll roll mill (produced by KODAIRA SEISAKUSHO KK), until the carbon black reached a particle size of 0.2 μm or less. The particle size was measured using a COULTER counter N4 (produced by a COULTER INC.). To the resulting dispersion mixture were added 16.7 g of acetic acid as a neutralizer and agitated thoroughly for re-homogenization. The resulting mixture was dispersed in water under gradual addition of deionized water and agitated vigorously by a high-speed mixer to produce a black-hued coating material (Y-7) (cationic electrodeposition type) having a solid concentration of 15 wt. %. 
     Synthesis Example 8 
     Preparation of Colored Coating (Y-8) 
     To 500 g of a solution of the hemi-ester (x-9) were added, under agitation, 27.0 g of &#34;IRGACURE 907&#34; produced by CIBA GEIGY INC. as a photopolymerization initiator, 3.0 g of &#34;KAYACURE DETX&#34;, produced by NIPPON KAYAKU CO., LTD. and 37.5 g of &#34;CARBON BLACK #5B&#34; for mixing and the resulting mixture was dispersed by a laboratory three-roll roll mill, produced by KODAIRA SEISAKUSHO KK until the carbon black reached the particle size of 0.2 μm or less. The particle size was measured using a COULTER counter N4 produced by COULTER INC. To the resulting dispersion mixture were added 33.7 g of triethylamine as a neutralizer and agitated thoroughly for re-homogenization. The resulting mixture was agitated vigorously by a high-speed mixer under gradual addition of deionized water For dispersion in water to produce a colored coating (Y-8) having a solid concentration of 15 wt. %. 
     Synthesis Example 9 
     Preparation of Plate (P-1) Having Light-Intercepting Layer 
     The cathionic positive type photosensitive coating (x-1) was applied by spin coating on a Pyrex glass plate of a thickness of 1.1 mm (hereinafter referred to as &#34;master plate G-1&#34;) having an ITO film (indium-tin oxide) of 80 nm in film thickness followed by drying at 80° C. for 5 minutes. After cooling, a non-tacky positive type photosensitive coating film of 3.0 μm in film thickness was formed. 
     Through a mask for producing the light-intercepting layer shown in FIG. 3, i.e. a mask for exposing the positive type photosensitive coating film corresponding to the light-intercepting layer portion 1, UV rays of 500 mJ/cm 2  were irradiated using a UV exposure device having a high pressure mercury lamp manufactured by ORC MANUFACTURING CO., LTD. under the trade name of &#34;JL-3300&#34;. When developing with a 0.3 wt. % aqueous solution of sodium metasilicate, the positive type photosensitive coating film corresponding to the light-intercepting layer portion 1 (Portion 4 in FIG. 4) was removed to expose the transparent electrically conductive layer. After washing with water and drying, electrodeposition was carried out at 25° C. for 3 minutes with a dc voltage of 25 V with the use of the master plate (G-1) as a cathode and a stainless steel beaker as an anode containing the black-hued coating (Y-7). After washing the master plate (G-1) with ion-exchanged water, the master plate (G-1) was dried for 5 minutes at 80° C. UV rays of 500 mJ/cm 2  were irradiated to the overall master plate (G-1) followed by heating the whole plate to 50° C. for 10 minutes. When developing with a 0.3 wt. % aqueous solution of sodium metasilicate, the remaining positive type photosensitive coating film was all removed so that there remained a black-hued light-intercepting layer 4 non-tacky at room temperature having a film thickness of 2μm, while a transparent electrically conductive layer 3 was exposed in the region on the surface of the master plate (G-1) where there was no light-intercepting layer. With the above steps, a plate (P-1) (FIG. 4) in which the black-hued light-intercepting layer 4 was formed partially on the transparent electrically conductive layer was obtained. 
     Synthesis Example 10 
     Preparation of Plate (P-2) Having Light-Intercepting Layer 
     Using a Pyrex glass substrate (hereinafter referred to as &#34;master plate G-2&#34;), 1.1 mm in thickness, having an indium-tin oxide (ITO) film, 80 nm in thickness, on its surface, as a cathode, and using a stainless steel beaker containing an aqueous solution of the cationic negative type photosensitive coating (X-3), as an anode, electrodeposition was carried out for three minutes at 25° C. at a dc voltage of 25 V. After washing the master plate (G-2) with ion-exchanged water followed by drying at 80° C. for 5 minutes and cooling, a non-tacky coating film, 3 μm in thickness was formed. 
     Through a mask for producing the light-intercepting layer shown in FIG. 6, i.e. a mask not exposing the negative type photosensitive coating film corresponding to the light-intercepting layer portion 9, UV Fays of 500 mJ/cm 2  were irradiated, using a UV exposure device having a high pressure mercury lamp manufactured by ORC MANUFACTURING CO., LTD. under the trade name of &#34;JL-3300&#34;. When developing with a 0.25 wt. % aqueous solution of lactic acid, the negative type photosensitive coating film corresponding to the light-intercepting layer portion 9 was removed to expose the transparent electrically conductive layer. After washing with water and drying, electrodeposition was carried out at 25° C. for 3 minutes with a dc voltage of 25 V with the use of the master plate (G-2) as an anode and a stainless steel beaker as a cathode containing the black-hued colored coating (Y-8). After washing the master plate (G-2) with ion-exchanged water, the master plate (G-2) was dried for 5 minutes at 80° C. When developing with a 5.0 wt. % aqueous solution of lactic acid, the remaining negative type photosensitive coating film was all removed followed by heating the overall plate (G-2) for 10 minutes at 150° C. so that there remained a black-hued light-intercepting layer non-tacky at room temperature having a film thickness of 2 μm, while a transparent electrically conductive layer 10 was exposed in the region on the surface of the master plate (G-2) where there was no light-intercepting layer. With the above steps, a plate (P-2) in which the black-hued light-intercepting layer was formed partially on the transparent electrically conductive layer was obtained. 
     Synthesis Example 11 
     Preparation of Black-Hued Coating (Y-9) and Colored Coatings (Y-10, Y-11 and Y-12) 
     An acrylic resin available under the trade name &#34;ARON S-4030&#34; from TOAGOSEI CHEMICAL INDUSTRY CO., LTD. was neutralized with triethyl amine to give a solution of pH8, to which deionized water was added to prepare a resin aqueous solution (S). 
     Carbon black, azo metal salt red pigment, phthalocyanine green, and phthalocyanine blue were added under agitation to the resin solution (S), respectively to give pigment dispersions of black-hue, red-hue, green-hue and blue-hue. 
     Separately, a mixture of a melamine resin (tradename &#34;SUMIMAL M-66B&#34; manufactured by SUMITOMO CHEMICAL CO., LTD.) with the aforementioned acrylic resin was neutralized with triethyl amine to have pH8, to which deionized water was added to prepare a resin solution (T). 
     By adding the resin solution (T) to each of the pigment dispersions, a black-hued coating (Y-9) and colored coatings (Y-10, Y-11, and Y-12) were obtained, which were of thermosetting type and of anionic electrodeposition type. 
     The compositions are shown in Table 3. 
     
                       TABLE 3                                                     
______________________________________                                    
               (Parts by weight)                                          
______________________________________                                    
Coating          Y-9     Y-10    Y-11  Y-12                               
Color            Black   Red     Green Blue                               
Acrylic resin (*)                                                         
                 750.0   750.0   750.0 750.0                              
Melamine resin (**)                                                       
                 250.0   250.0   250.0 250.0                              
Triethyl amine (Netralizer)                                               
                 61.8    61.8    61.8  61.8                               
Carbon black     333.0   --      --    --                                 
Phthalocyanine Blue (***)                                                 
                 --      --      --    300.0                              
Phthalocyanine Green (****)                                               
                 --      --      500.0 --                                 
Azo Metal Salt Red Pigment                                                
                 --      500.0   --    --                                 
(*****)                                                                   
______________________________________                                    
 (*) Acrylic resin &#34;ARON S4030&#34; (mfd. by TOAGOSE CHEMICAL INDUSTRY CO.,   
 LTD.)                                                                    
 (**) Melamine Resin &#34;SUMIMAL M66B&#34; (mfd. by SUMITOMO CHEMICAL CO., LTD.) 
 (***) Phthalocyanine Blue &#34;SR150C&#34; (mfd. by SANYO SHIKISO KK)            
 (****) Phthalocyanine Green &#34;SAX&#34; (mfd. by SANYO SHIKISO KK)             
 (*****) Metal Salt Red Pigment &#34;PIGMENT RED 4BS&#34; (mfd. by SANYO SHIKISO  
 KK)                                                                      
 
    
     Example 1 
     With the use, as a cathode, of the plate (P-1) obtained by Synthesis Example 9, referred to hereinafter as a master plate 1, and with the use, as an anode, of a stainless steel beaker, containing an aqueous solution of a cationic positive type photosensitive coating (X-1), electrodeposition was carried out for 60 seconds with a dc voltage of 40 V and a temperature of 25° C. After washing the master plate 1 with ion-exchanged water, the master plate 1 was dried at 80° C. for five minutes and cooled to Form a non-tacky black uniform coating with a film thickness of 2 μm. 
     A positive mask shown in FIG. 7 was intimately contacted with the coating film and irradiated with UV rays of 500 mJ/cm 2  using a UV exposure device having a high pressure mercury lamp manufactured by ORC MANUFACTURING CO., LTD. under trade name of &#34;JL-3300&#34;. On development with a 0.3 wt. % aqueous solution of sodium metasilicate, only the portions of the cationic positive type photosensitive coating film corresponding to the largest light-transmittance portions 11 of the mask were selectively removed to expose the ITO layer. After washing with water and drying, electrodeposition was carried out by applying a d.c. voltage of 25 V was applied across the master plate as a cathode and a stainless steel beaker containing a colored coating (Y-1) as an anode. After washing the master plate 1 with ion-exchanged water, followed by drying at 80° C. for five minutes, a red-hued colored layer, 2 μm in thickness, which was not tacky at room temperature, was produced on the master plate. 
     After development with a 1.3 wt. % aqueous solution of sodium metasilicate, no changes were noticed in the red-hued colored layer, while only the positive type photosensitive coating in register with the portions 12 of the second largest light-transmittance of the mask were selectively removed. After washing with water and drying, the colored coating (Y-2) was electrodeposited for three minutes under conditions of a d.c. voltage of 25 V and a temperature of 25° C., in the same manner as when electrodepositing the colored coating (Y-1), and the resulting substrate was washed with ion-exchanged water. It was found that there were no changes in the previously formed red-hued colored layer, and a greed-hued colored layer was formed on the master plate portions freed of the coating film. After drying at 80° C. for five minutes and development with a 3.0 wt. % aqueous solution of sodium metasilicate, it was found that no changes were produced in the red-hued or green-hued colored layers, and only the positive type photosensitive coating film portions in register with the portions 13 of the third largest light-transmittance of the mask were selectively removed. After washing with water and drying, a colored coating (Y-3) was electrodeposited for three minutes in the same manner as For electrodepositing the colored coating (Y-1), under conditions of a d.c. voltage of 25 V and a temperature of 30° C. After washing the master plate 1 with ion-exchanged water, it was found that no changes were produced in the previously formed red-hued or green-hued colored layers, and a blue-hued colored layer was formed on the master plate. After further drying at 80° C. for five minutes followed by irradiation of UV rays of 500 mJ/cm 2  onto the overall master plate 1 and then heating for 10 minutes at 150° C., development was carried out with a 0.3 wt. % aqueous solution of sodium metasilicate. The residual cationic positive type photosensitive coating film was all removed to obtain a color filter excellent in transparency and uniformity and having a black-hued light-intercepting layer of 2 μm in thickness exhibiting no-tackiness at room temperature and colored layers. 
     Example 2 
     With the use as an anode of the plate (P-1) (hereinafter referred to &#34;master plate 2&#34;) obtained by Synthesis Example 9 and with the use as a cathode of a stainless steel beaker containing an aqueous solution of an anionic positive type photosensitive coating (X-2), electrodeposition was carried out for two minutes at a d.c. voltage of 45 V and a temperature of 25° C. After washing the master plate 2 with ion-exchanged water, followed by drying at 80° C. for five minutes, a uniform non-tacky black coating film, having a film thickness of 1.8 μm, was produced. 
     A positive mask shown in FIG. 7 having four different degrees of light-transmittances was intimately contacted with the coating film and irradiated with UV rays of 500 mJ/cm 2  with the use of a UV exposure device manufactured by ORC MANUFACTURING CO., LTD. under the trade name of &#34;JL-3300&#34;. After development with a 0.5 wt. % aqueous solution of sodium metasilicate, only the anionic positive type photosensitive coating film portions in register with the largest light-transmittance portion 11 of the mask were selectively removed to expose the ITO film thereat. After washing with water and drying, electrodeposition was carried out by applying a d.c. voltage of 30 V at 25° C. for three minutes across the master plate 2 as a cathode and a stainless steel beaker containing the colored coating (Y-1) as an anode. After washing the master plate 2 with ion-exchanged water and drying at 80° for five minutes, a red-hued colored layer, which was not tacky at room temperature, was formed on the master plate portions freed of the coating film. 
     Then, after development with a 1.5 wt. % aqueous solution of sodium metasilicate, it was found that no changes were produced in the red-hued colored layer, while only the positive type photosensitive coating film portions in register with the portions 12 with the second largest light-transmittance of the mask were selectively removed. After washing with water and drying, a colored coating (Y-2) was electrodeposited for three minutes under conditions of the d.c. voltage of 30 V and a temperature of 25° C., in the same manner as for electrodeposition of the colored coating (Y-1). After subsequent washing with ion-exchanged water, it was found that no changes were produced in the previously formed red-hued colored layer, and a green-hued colored layer was formed on the master plate portions freed of the coating film. After drying at 80° C. for five minutes and development with a 4.0 wt. % aqueous solution of sodium metasilicate, it was found that no changes were produced in the red-hued and green-hued colored layers and only the positive type photosensitive coating portions in register with the portions 13 with the third largest light-transmittance of the mask were selectively removed. After washing with water and drying, the colored coating (Y-3) was electrodeposited for three minutes at a d.c. voltage of 30 V and a temperature of 25° C. in the same manner as for electrodepositing the colored coating (Y-1). After washing the master plate 2 with ion-exchanged water, it was found that no changes were produced in the previously formed red-hued or green-hued colored layers, and a blue-hued colored layer was produced on the master plate portions freed of the coating film. 
     Then, after drying at 80° C. for five minutes, UV rays of 500 mJ/cm 2  were irradiated onto the overall master plate 2 followed by heating the whole master plate 2 for 10 minutes at 150° C. With development with a 0.3 wt. % aqueous solution of sodium metasilicate, the residual anionic positive type photosensitive coating film was all removed. A color filter having transparent and homogeneous colored layers and also having a non-tacky black-hued light-intercepting layer, 2 μm in the thickness, was obtained. 
     Example 3 
     With the use as a cathode of the plate (P-2) obtained by Synthesis Example 10, referred to hereinafter as a master plate 3, and with the use as an anode of a stainless steel beaker containing an aqueous solution of a cationic negative type photosensitive coating (X-3), electrodeposition was carried out for 3 minutes at a d.c. voltage of 30 V and a temperature of 25° C. After washing the master plate 3 with ion-exchanged water, followed by drying at 80° C. for five minutes and subsequent cooling, a non-tacky uniform coating film having a film thickness of 2 μm was produced. 
     The negative mask shown in FIG. 5 having four different degrees of light-transmittance was intimately contacted with the coating film, and irradiated with UV rays of 500 mJ/cm 2 , using a UV exposure device having a high-pressure mercury lamp, manufactured by ORC MANUFACTURING CO., LTD. under the trade name of &#34;JL-3300&#34;. Then, after development with a 0.05 wt. % aqueous solution of lactic acid, the cationic negative type photosensitive coating film portions in register with the portions 6 of the mask with the smallest light-transmittance were selectively removed to expose the ITO film surface thereat. After washing with water and drying, electrodeposition was carried out for 3 minutes by applying a d.c. voltage of 25 V at 25° C. across the master plate 3 as an anode and a stainless steel beaker containing a colored coating (Y-4) as a cathode. After washing the master plate 3 with ion-exchanged water, a red-hued colored layer, 2 μm in thickness, non-tacky at room temperature was formed. 
     Then, after development with a 0.5 wt. % aqueous solution of lactic acid, no changes were noticed in the red-hued colored layer, whilst only the negative type photosensitive coating film portions in register with the portions 7 of the mask with the second smallest light-transmittance were selectively removed. After washing with water and drying, the colored coating (Y-5) was electrodeposited for three minutes under conditions of a d.c. voltage of 25 V and a temperature of 25° C. After washing with ion-exchanged water, it was found that no changes were produced in the previously formed red-hued colored layer, and a green-hued colored layer was formed on the master plate 3. After drying at 80° C. for five minutes and development with a 3.0 wt. % of lactic acid, it was found that no changes were produced in the green-hued or red-hued colored layers, and only the negative type photosensitive coating portions in register with the portions 5 of the mask with the third smallest light-transmittance were selectively removed. After washing with water and drying, the colored coating (Y-6) was electrodeposited for three minutes under conditions of a d.c. voltage of 25 V and a temperature of 25° C. in the same manner as for electrodeposition of the colored coating (Y-4). After washing the master plate 3 with ion-exchanged water, it was found that no changes were produced in the previously formed green-hued or red-hued colored layers, and a blue-hued colored layer was formed on the master plate 3. 
     Then, after drying at 80° C. for five minutes, and development with a 7.0 wt. % aqueous solution of lactic acid, no changes were noticed in the colored layers, and only the residual cationic negative type photosensitive coating film, that is the photosensitive coating film portions in register with the portions 5 irradiated with the largest irradiation amount, were selectively removed. By baking at 170° C. for 30 minutes to complete the curing, a color filter having the colored layers and the light-intercepting layer, each 1.8 μm in thickness and showing excellent transparency and uniformity, could be obtained. 
     Example 4 
     By electrodeposition for three minutes under conditions of a d.c. voltage of 25 V and a temperature of 25° C., with the use as an anode of the plate (P-2) obtained by Synthesis Example 10, hereinafter referred to as a master plate 4, and with the use as a cathode of a stainless steel beaker containing an aqueous solution of an anionic negative type photosensitive coating (X-4), followed by washing of the master plate 4 with ion-exchanged water, drying at 80° C. For five minutes and cooling, a non-tacky uniform coating film with a film thickness of 1.8 μm was produced. 
     The negative mask shown in FIG. 8 was intimately contacted with the coating film and irradiated with UV rays of 600 mJ/cm 2 , using a UV exposure device having a high-pressure mercury lamp, manufactured by ORC MANUFACTURING CO., LTD. under the trade name of &#34;JL-3300&#34;. Then, after development with a 0.1 wt. % aqueous solution of sodium carbonate, the anionic negative type photosensitive coating film portions in register with the portions 5 of the mask with the smallest light-transmittance were selectively removed to expose the ITO film surface. After washing with water and drying followed by electrodeposition at 25° C. for three minutes at a d.c. voltage of 30 V, with the use as a cathode of the master plate 4 and with the use as an anode of a stainless steel beaker containing a colored coating (Y-1), Followed by washing the master plate 4 with ion-exchanged water and drying at 80° C. for five minutes, a red-hued colored layer was formed on the master plate portions freed of the coating film. 
     Then, after development with a 0.75 wt. % aqueous solution of sodium carbonate, no changes were noticed in the red-hued colored layer, and only the negative type photosensitive coating portions in register with the portions 16 of the mask with the second smallest light-transmittance were selectively removed. After washing with water and drying, the colored coating (Y-2) was electrodeposited for three minutes under the conditions of a d.c. voltage of 30 V and a temperature of 25° C., in the same manner as for electrodeposition of the colored coating (Y-1). After washing with ion-exchanged water, no changes were noticed in the previously formed red-hued layer, and a green-hued colored layer was formed on the portions freed of the coating film. After drying at 80° C. for five minutes and development with a 5.0 wt. % aqueous solution of sodium metasilicate, no changes were noticed in the red-hued or green-hued colored layers, and only the negative type photosensitive coating film portions in register with the portions 17 of the mask with the largest light-transmittance were selectively removed. After washing with water and drying, the colored coating (Y-3) was electrodeposited for three minutes under conditions of a d.c. voltage of 30 V and the temperature of 25° C., in the same manner as for electrodeposition of the colored coating (Y-1). After washing the master plate 4 with ion-exchanged water, it was found that no changes were produced in the previously formed red-hued or green-hued colored layers, and a blue-hued colored layer was formed in the portions freed of the coating film. 
     After baking at 160° C. for 20 minutes to complete the curing, a color filter having the colored layers and the light-intercepting layer and having excellent transparency and uniformity was produced. 
     Example 5 
     A positive type photoresist available under the tradename &#34;OFPR-800&#34; from TOKYO OHKA KOGYO KK was applied by a spin coater onto a Pyrex glass plate, 0.7 mm in thickness, having an ITO film of a film thickness of 100 nm on the glass plate followed by drying at 80° C. for 10 minutes to form a photosensitive coating film having a film thickness of 2.5 μm (hereinafter referred to as &#34;a master plate 5&#34;). 
     Through a mask for producing the light-intercepting layer shown in FIG. 3, i.e. a mask for exposing the positive type photosensitive coating film corresponding to the light-intercepting layer portion 1, UV rays of 75 mJ/cm 2  were irradiated using a UV exposure device having a high pressure mercury lamp manufactured by ORC MANUFACTURING CO., LTD. under the trade name of &#34;JL-3300&#34;. When developing with a 2.4 wt. % aqueous solution of tetramethyl ammonium hydroxide, the positive type photosensitive coating film corresponding to the high-intercepting layer portion 1 was removed to expose the transparent electrically conductive layer (ITO film). After washing with water and drying, electrodeposition was carried out at 25° C. For 3 minutes with a dc voltage of 40 V with the use of the master plate 5 as a cathode and a stainless steel beaker as an anode containing the black-hued anionic electrodeposition coating (Y-9). After washing the master plate 5 with ion-exchanged water, the master plate 5 was dried for 10 minutes at 120° C. UV rays of 75 mJ/cm 2  were irradiated to the overall master plate 5 followed by heating the whole plate to 150° C. for 10 minutes. When developing with a 2.4 wt. % aqueous solution of tetramethyl ammonium hydroxide, the remaining positive type photosensitive coating film was all removed so that there remained a black-hued light-intercepting layer non-tacky at room temperature having a Film thickness of 2 μm, while a transparent electrically conductive layer was exposed in the region on the surface of the master plate 5 where there was no light-intercepting layer. The master plate was further heated for 30 minutes at 180° C. to cure the black-hued light-intercepting layer. A plate S in which the black-hued light-intercepting layer 4 was formed partially on the transparent electrically conductive layer was obtained. 
     A positive type photoresist (TOKYO OHKA KOGYO KK, &#34;OFPR-800&#34;) was applied by a spin-coater onto the surface of the electrically conductive layer and the black-hued light-intercepting layer on the plate 5 followed by drying at 80° C. for 10 minutes to form a photosensitive coating film having a film thickness of 2.5 μm. 
     A positive mask having three different degrees of light-transmittances was intimately contacted with the coating film and irradiated with UV rays of 70 mJ/cm 2  using a UV exposure device similar to Example 1. When UV rays were irradiated, 70 mJ/cm 2  of UV rays were irradiated to the photosensitive coating film portion corresponding to the largest light-transmittance portion of the positive mask, 20 mJ/cm 2  of UV rays were irradiated to the photosensitive coating film portion corresponding to the second largest light-transmittance portion of the positive mask, and no UV rays were irradiated to the photosensitive coating film portion corresponding to the smallest light-transmittance portion of the mask. 
     On development with a 2.4 wt. % aqueous solution of tetramethyl ammonium hydroxide, the photosensitive coating film portions corresponding to the largest light-transmittance portion of the mask were selectively removed to expose the ITO film. After washing with water and drying, electrodeposition was carried out for 20 seconds by applying a d.c. voltage of 28 V across the plate 5 as an anode and a stainless steel beaker containing a colored coating (Y-10) as a cathode. After washing the plate 5 with ion-exchanged waiter, followed by drying at 120° C. for 10 minutes to be partially cured, a red-hued colored layer was produced on the plate. 
     After development with a 3.5 wt. % aqueous solution of tetramethyl ammonium hydroxide, no changes were noticed in the red-hued colored layer, while only the positive type photosensitive coating film in register with the second largest light-transmittance portion of the mask were selectively removed. After washing with water and drying, the colored coating (Y-11) was electrodeposited for 40 seconds under conditions of a d.c. voltage of 25 V and a temperature of 25° C., in the same manner as when electrodepositing the colored coating (Y-10), and the resulting plate was washed with ion-exchanged water. It was found that there were no changes in the previously formed red-hued colored layer, and a green-hued colored layer was Formed on the plate portions freed of the coating film. After drying at 120° C. for 10 minutes to partially cure the colored layer, 75 mJ/cm 2  of UV rays were irradiated on the overall surface of the plate 5. 
     After development with a 2.4 wt. % aqueous solution of tetramethyl ammonium hydroxide, it was found that no changes were produced in the red-hued or green-hued colored layers, and only the positive type photosensitive coating film portions in register with the smallest light transmittance portion of the mask were selectively removed. After washing with water and drying, a colored coating (Y-12) was electrodeposited for 20 seconds in the same manner as for electrodepositing the colored coating (Y-10), under conditions of a d.c. voltage of 22 V and a temperature of 25° C. After washing the plate 5 with ion-exchanged water, it was found that no changes were produced in the previously formed red-hued or green-hued colored layers, and a blue-hued colored layer was formed on the plate portions freed of the coating film. For completing curing, the red, green and blue-hued colored layers were baked at 180° C. for 30 minutes to produce a color filter having the colored layers and the light-intercepting black-hued layer, each having a film thickness of 2 μm±0.1 μm, excellent in transparency and homogeneity. 
     Although the present invention has been described with reference to the preferred examples, it should be understood that various modifications and variations can be easily made by those skilled in the art without departing from the spirit of the invention. Accordingly, the foregoing disclosure should be interpreted as illustrative only and is not to be interpreted in a limiting sense. The present invention is limited only by the scope of the following claims.