Phase transition-type liquid crystal composition
This application is a continuation of application Ser. No. 08/020,438, filed Feb. 22, 1993, now abandoned, which is a continuation of application Ser. No. 07/914,030, filed Jul. 15, 1992, now abandoned, which is a continuation, of application Ser. No. 07/465,633, filed Jan. 22, 1990, now abandoned. which is a continuation of copending application(s) Ser. No. 07/307,161, filed on Feb. 6, 1989, now which in turn is a continuation of application Ser. No. 07/143,307, filed on Jan. 11, 1988, (now abandoned) which in turn is a continuation of application Ser. No. 06/770,224, filed on Aug. 28, 1985 (now abandoned). 
    
    
     BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     This invention relates to phase transition-type liquid crystal compositions. In particular, this invention relates to cholesteric-nematic phase transition-type liquid crystal composition whose dielectric anisotropies are positive. Surprisingly, liquid crystal devices or elements produced using the liquid crystal composition of this invention may be effectively used in connection with keyboard inputting operations due to their East writing capabilities, and to provide large-scale or area display devices similar to those well-known in the art, such as cathode ray tube (CRT) display devices. 
     2. Description of the Related Art 
     A variety of X-Y dot matrix-type liquid crystal display devices based on different display modes have been proposed and used for display purposes. A conventional display modes is the dynamic scattering mode (DSM) which utilizes dynamic scattering effects. Liquid crystal display devices based on DSM, however, cannot be used in connection with large-scale displays. This is because, in large devices, cross-talk is undesirably caused with an increase of display area, and scanning lines, and there is a lower cut-off frequency. 
     Another display mode, mainly used in the field of liquid crystal displays, is the twisted nematic (TN) mode utilizing twisted nematic effects. However, as in the DSM-type devices, the TN-type liquid crystal devices suffer from cross-talk when they are used in a large-scale dot matrix display, because TN-type liquid crystals have no sudden rise characteristic. This means they are not suitable for large scaled displays. In addition to this, in a large-scale display, TN-type devices suffer from an unusually limited viewing angle and therefore have an unacceptably low contrast characteristic. Such narrowing of the viewing angle coupled with a need for an increase of the number of scanning lines is a critical drawback a need for in large-scale displays and must be overcome. 
     Numerous researchers have conducted experiments and studies in an effort to overcome the drawbacks of the above-discussed DSM-type and TN-type display devices Such work has led to the development of a new type of liquid crystal display device, i.e., a storage-type liquid crystal device characterized by being capable of maintaining written information or a display in a storage state after a single application of voltage and subsequent removal of the applied voltage (without further application of voltage) as a result of the memory effects of the selected specific liquid crystals. This phenomena enables realization of a large-scale display having as many as 500 or more scanning lines. Such large-scale display could not achieved with the conventional DSM-type and TN-type display devices of an X-Y dot matrix-type. 
     However, such storage-type liquid crystal display usually requires a driving voltage of ±20 V, an extremely high driving voltage for a liquid crystal display. When attempting to drive such storage-type liquid crystal display with a voltage in the range possible using a complementary metal oxide semiconductor (CMOS), even if writing is possible, essentially no storage time is obtained, making use of such storage-type liquid crystal display element in conjunction with a CMOS system impractical in a commercial sense. 
     For this reason, the above-mentioned storage-type liquid crystal display could not be driven using a CMOS integrated circuit (IC). Furthermore, while large scale dot matrix display have been possible in principle, because mounting of the driving circuit was difficult, large-scale dot matrix storage-type liquid crystal displays were unavailable for use in actual display devices. 
     Japanese Unexamined Patent Publication (Kokai) No. 50-159294 discloses a matrix-type liquid crystal device based on a nematic-cholesteric mixed liquid crystal display system, utilizing a Schiff-type cholesteric liquid crystal, for example, cholesteryl chloride. In such liquid crystal device the problem of cross-talk discussed above is avoided and increased contrast characteristics are provided in large-scale displays. However, such device has the drawback that in the case of an X-Y matrix display drive, when the liquid crystal is transferred to a storage state after the completion of the writing of picture, the entire picture becomes temporarily cloudy, e.g., for 10 seconds. The clouding of the entire picture means that the information on the display disappears, even if only temporarily, causing the operator to be uneasy. Furthermore, when the written-in picture is partially rewritten, the rewritten part becomes temporarily cloudy in the same manner each time, making the rewriting operation longer. 
     Under these circumstances, we found an improved storage-type liquid crystal composition and an improved X-Y dot matrix-type liquid crystal display device using such Liquid crystal composition. Japanese Unexamined Patent Publication (Kokai) No. 59-126492 and the equivalent U.S. application Ser. No. 558,475 filed Dec. 6, 1983, now U.S. Pat. No. 4,547,309 disclose the use of a storage-type liquid crystal composition incorporates a nematic-cholesteric mixture liquid crystal exhibiting a positive anisotropy of dielectric constant. The composition comprises a cyclohexane-type liquid crystal having a high anisotropy of dielectric constant (Δε) and a low viscosity (η), as a nematic liquid crystal; an azoxy-type liquid crystal having an abrupt rising property; and a compensated cholesteric liquid crystal having a large spiral pitch and possessing the property of reducing the viscosity when admixed with the nematic liquid crystal and/or a cholesteric liquid crystal simply possessing the property of reducing the viscosity, such as, for example, cholesteryl oleate. 
     The storage-type liquid crystal composition of application Ser. No. 558,475 is effective to overcome many of the drawbacks of the above-discussed prior art liquid crystal compositions and devices. In fact, when such storage-type liquid crystal compositions are used, the necessary driving voltage is low, e.g., 7.0 V to 4.4 V, and no temporary clouding occurs. However, this liquid crystal composition is not completely satisfactory, since it can not provide a liquid crystal device having compatibility with the keyboard input system which are conventionally used for input in the display field. 
     Recently, we found a more improved storage-type liquid crystal display device using a new driving method (cf., for example, Japanese Patent Application No. 59-107404, filed May 29, 1984). The liquid crystal display device, as is disclosed such application, uses as the liquid crystal material a liquid crystal composition comprising 10% to 90% by weight of a cyanobiphenyl-type liquid crystal compound and 7% to 30% by weight of 4-cyano-4&#39;-2-methylbutylbiphenyl-type liquid crystal compound. In such display device, two optical states, i.e., focal-conic or F state (cloudy state) and homeotropic or H&#39; state (transparent state) can be produced and maintained With application of the same retention voltage. It has been found that such composition and such device are useful in connection with large size displays and employing a keyboard input system, provide a high contrast display, and result in the elimination of flicker. One drawback of such device is that stable homeotropic or H&#39; state cannot be attained with application of the retention voltage. In fact, the H&#39; state is metastable and therefore is changed to the focal-conic or F state after about 20 to 30 seconds. It is believed that such a change of state is caused because atmospheric conditions such as humidity, adversely affect the characteristics of the liquid crystal material. Another drawback is that the response speed of the device is relatively slow. It is therefore desirable to provide a still further improved novel liquid crystal composition having none of the drawbacks discussed above. 
     SUMMARY OF THE INVENTION 
     According to this invention, there is provided a liquid crystal composition comprising a mixture of an ester-type liquid crystal compound and a chiral nematic liquid crystal compound having added thereto, at least one of an ethane-type liquid crystal compound and a bicyclohexane-type liquid crystal compound. 
     The liquid crystal composition of this invention exhibits positive dielectric anisotropy and is of a cholesteric-nematic phase transition-type. 
     Unexpectedly, the described liquid crystal composition has an extended width (ΔV) of voltage hysteresis indicating two stable optical states (F and H&#39;), provides a fast response speed, and enables use of a large scale display and input operation employing keyboards. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     FIG. 1 is a graph illustrating the display principle of the phase transition-type liquid crystal composition of the present invention; 
     FIGS. 2a and 2b are illustrations showing an example of a liquid crystal driving method using polarizing plates; 
     FIGS. 3a and 3b are illustrations showing an example of a liquid crystal driving method using no polarizing plate; 
     FIGS. 4a and 4b are graphs showing a pattern of liquid crystal driving signals used in Example 1, and; 
     FIG. 5 is a graph illustrating the hysterisis curve of the liquid crystal display panel prepared in Example 1. 
    
    
     DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     Before discussing of the liquid crystal compounds used in the composition of the present invention, it will be explained how we discovered the described combination of liquid crystal compounds which provides many unexpected effects. 
     First, in order to achieve stabilization of the metastable homeotropic or H&#39; state, we studied hysteresis curves of cholesteric-nematic mixed liquid crystals. We learned from such study that the H&#39; state will be stabilized if the width (ΔV) of the voltage hysteresis is extended (see FIG. 1). If the voltage hysteresis width (ΔV) is extended conversion of from the H&#39; state to the F state will be effectively prevented, because such extension of width results in a widening of the range of the retention voltage (Vd) to be applied and accordingly facilitates application of the Vd at a higher level. The higher voltage Vd results in a stabilized H&#39; state. 
     Second, we learned during our study of liquid crystal materials suitable for extension of the voltage hysteresis width (ΔV) that there is a certain relationship between the molecular structure of the liquid crystal compound and the (ΔV) characteristic of the resulting liquid crystal, and therefore that there are limited numbers of the liquid crystal compounds which have the certain molecular structures that result in a largely extended ΔV. 
     As a result of our study, as described above, we determined that a surprisingly extended width of the voltage hysteresis can be achieved if a mixture of at least one ester-type liquid crystal compound having an ester linkage in its molecular structure and at least one chiral nematic liquid crystal compound is combined with at least one compound selected from the group consisting of ethane-type liquid crystal compounds having an ethylenic linkage, --CH 2  CH 2  --, between two adjacent ring structures and bicyclohexane-type liquid crystal compounds having two directly bonded cyclohexane rings, ##STR1## 
     In the present invention, the liquid crystal composition containing all of the above-described four liquid crystal compounds is the most preferred. Such preferred composition has a fast writting speed and a wide mesorange, indicating that it is a liquid crystal at room temperature, in addition to a large voltage hysteresis width. 
     The liquid crystal composition containing three essential components, namely, ethane-type, ester-type, and chiral nematic liquid crystal compounds, has a larger hysteresis width than that of the last-described one, but tends to have a narrower mesorange. Further, a liquid crystal composition containing bicyclohexane-type, ester-type, and chiral nematic liquid crystal compounds is effective to reduce the viscosity of the resulting liquid crystal and extend its hysteresis width, although the degree of hysteresis width extension is smaller than that of the composition of the invention containing only ethane-type liquid crystal compound. 
     The ethane-type liquid crystal compounds used in the present invention are considered to be effective to extend the voltage hysteresis width AV because of the ethylenic linkage positioned as a central group between two ring structures. In fact, due to the molecular structure of the ethane-type compounds, they can freely move by rotation or flexure. Such compounds freely move due to rotation about the single bond of the ethylenic linkage, stretching vibration, bending vibration, and twisting or wagging. Due to the ethylenic linkage, the two carbon atoms are connected by a single bond, and two carbon tetrahedra are free to rotate about single bond, so various arrangements of their atoms of the molecule arise by rotation about such single bonds, such as staggered conformation, eclipsed conformation or skew conformation. As a result, these ethane-type compounds have increased flexibility and are capable of moderating the conversion from a nematic phase (H&#39; state) to a cholesteric phase (F state). Further, such compounds act stably. 
     The ethane-type liquid crystal compounds which are useful in the liquid crystal composition of the present invention are represented generally by the following formulas: ##STR2## in which R 1 , R 3 , R 5 , and R 7  may be the same or different and each represents an alkyl group of 2 to 7 carbon atoms, 
     R 2 , R 4 , R 6 , and R 8  may be the same or different and each represents an alkyl group of 2 to 7 carbon atoms, an alkoxy group of 1 to 6 carbon atoms, ##STR3## a fluorine atom (F), a bromine atom (Br), or a cyano group (--CN), 
     R represents an alkyl group of 2 to 7 carbon atoms, a fluorine atom, or a bromine atom, 
     R 9 , R 11 , R 13 , R 15 , R 17 , R 19 , and R 21  may be the same or different and each represents an alkyl group of 2 to 7 carbon atoms or an alkoxy group of 1 to 6 carbon atoms, and 
     R 10 , R 12 , R 14 , R 16 , R 18 , R 20 , and R 22  may be the same or different and each represents an alkyl group of 2 to 7 carbon atoms, a fluorine atom, a chlorine atom, a bromine atom, or a cyano group. 
     Typical specific examples of the ethane-type liquid crystal compounds useful herein include: ##STR4## or the like. 
     The described ethane-type liquid crystal compounds can be used in an amount of about 10% to 70% by weight, preferably about 10% to 40% by weight, based on the total weight of the liquid crystal composition. The above range of the described compounds is the most preferred one for balancing the viscosity characteristics and ensuring a satisfactory mesorange in which the compound acts as a liquid crystal. On the other hand, a wider ΔV (hysteresis width) may be achieved if the compounds are used in any amount exceeding the upper limit. Similarly, the other three liquid crystal compounds discussed in detail hereinafter may also be used in the specified range. 
     The bicyclohexane-type liquid crystal compounds useful in connection with the present invention, due to their cyclohexane ring structure, can freely move (or flex). This is because the cyclohexane ring structure is capable of assuming two configurations; i.e., chair-type and boat-type, and the molecule is free to change from one such configuration to the other. Bicyclohexane, having, two cyclohexane rings, also revolves freely around their common axis. Further, such compounds may contribute to an extension of the voltage hysteresis width, a reduction of the viscosity of the liquid crystal composition, and a speeding up of writing. They also act stably. 
     The bicyclohexane-type liquid crystal compounds useful separately, or in combination with the above-discussed ethane-type one in the liquid crystal composition of this invention are represented generally by the formula: ##STR5## in which 
     R 23  represents an alkyl group of 2 to 7 carbon atoms and 
     R 24  represents an alkyl group of 2 to 7 carbon atoms or a cyano group. 
     Typical examples of specific bicyclohexane-type liquid crystal compounds useful herein are as follows: ##STR6## or the like. These liquid crystal compounds may be used in the composition in an amount of about 10% to 60% by weight, preferably about 20% to 40% by weight, based on the total weight of the liquid crystal composition. 
     Further, the ester-type liquid crystal compounds useful in connection with the present invention can mainly contribute to an extension of the mesorange of the resulting liquid crystal composition when one or more of such compounds are used in combination with the above-discussed ethane-type and/or bicyclohexane-type liquid crystal compounds. 
     Typical examples of specific ester-type liquid crystal compounds useful in the practice of the present invention are as follows: ##STR7## or the like. 
     Optionally, an oxygen atom of the central group --COO-- of the described liquid crystal compounds may be substituted with a sulfur atom to form the corresponding thioester-type liquid crystal compounds, for example: ##STR8## 
     The above-described ester-type and thioester-type liquid crystal compounds can be used in an amount of abut 15% to 85% by weight, preferably about 20% to 55% by weight, based on the total weight of the liquid crystal composition. 
     Furthermore, the chiral nematic liquid crystal compounds used in the present invention are effectively used to give a helical structure to the resulting liquid crystal composition. 
     Typical examples of chiral nematic liquid crystal compounds useful in the practice of the present invention are as follows: ##STR9## in which C* indicates an asymmetric carbon atom. 
     These chiral nematic liquid crystal compounds can be generally used in an amount of about 8% to 40% by weight, preferably about 10% to 30% by weight, based on the total weight of the liquid crystal composition. In the production of a cholesteric storage-type liquid crystal display device, they must be used in an amount of from about 4% to 80% by weight, since the chiral nematic liquid crystal compounds belong to a group of the cholesteric liquid crystals. 
     In the practice of the present invention, if desired, additional amounts of conventional liquid crystal compounds such as biphenyl-type, dioxane-type, pyrimidine-type, cyclohexane-benzene type, terphenyl-type or cyclohexanebiphenyl-type liquid crystal compounds may be added to the liquid crystal composition to improve its characteristics. Practically, we used, some of these conventional liquid crystal compounds as additives in the hereinafter-described working examples. 
     Generally, the biphenyl-type liquid crystal compounds are effectively used to reduce the required driving voltage, because they have large positive dielectric anisotropys. In particular, ##STR10## having a low viscosity, is effective to also reduce the viscosity of the resulting liquid crystal composition. These compounds are generally used in an amount of several percent by weight to 20% by weight, because an increase in these compounds having rather straight and hard structures at the central bonds, results in a narrowing of ΔV. 
     The dioxane-type liquid crystal compounds have a very large dielectric anisotropy and therefore are effective to reduce a driving voltage. However, in phase transition-type liquid crystal, the driving voltage mainly depends on Δε and viscosity, so dioxane-type compounds should not be used in higher amount since they tend to increase the viscosity. Generally, the compounds should be used in an amount of from several percent by weight to 15% or 20% by weight. 
     Further, it is contemplated to use pyrimidine-type liquid crystal compounds in combination with bicyclohexane-type, ethane-type, or other liquid crystal compounds, to extend the voltage hysteresis, width (ΔV). The freedom of movement in the molecule which is considered to be caused due to heterocyclic compounds contained in the molecule, is in conformity with other liquid crystal compounds. The pyrimidine-type liquid crystal compounds should be used in at most 15% by weight because they have an increased viscosity. 
     In addition to these conventional liquid crystal compounds, cyclohexane-type liquid crystal compounds may also be useful. The cyclohexane-type compounds, due to their low viscosity, are effectively used to reduce the driving voltage as a result of a reduction of the viscosity of the resulting composition. However, due to the small refractive anisotropy of these compounds, the greater the amount used, the smaller the intensity of light scattering and the lower the contrast. These compounds are preferably used in an amount of from several percent by weight to 20% by weight. 
     Small amounts, for example 10% by weight or less, of the terphenyl-type or cyclohexanebiphenyl-type liquid crystal compounds are also useful. These compounds can be useful to increase the light scattering intensity. However, the addition of these compounds, due to their high viscosity, results in an increase in the driving voltage. 
     This invention will be further described with reference to the accompany drawings. 
     Referring now to the drawings, FIG. 1 illustrates the display principle of the liquid crystal composition according to the present invention. From this illustration it can be seen that the display principle is based on a cholesteric-nematic phase transition phenomenon. 
     The relationships between light transmittance and applied voltages for nematic-cholesteric phase transition-type liquid crystals having positive dielectric anisotropy are as shown in FIG. 1. By increasing the electric field applied to the liquid crystal, the liquid crystal display panel changes from a cloudy state (cholesteric phase:F) to a transparent state (nematic phase:H). By decreasing the electric field applied to the liquid crystal, the liquid crystal display panel changes from a nematic phase H to a cholesteric phase F viametastable transparent state (nematic phase:H&#39;). 
     At F phase, the liquid crystal in the panel has a spiral or helical structure as shown in FIG. 1, and the helical axis of the liquid crystal structure is parallel to the substrate of the panel. Thus, incident light on the panel is scattered by the liquid crystal and the panel is cloudy. On the other hand, at the H phase the helical structure of the liquid crystal in the panel has dissapated and the liquid crystal molecules are aligned perpendicularly to the substrate of the panel, as shown in FIG. 1. Thus, the liquid crystal has a homeotropic transparent state. 
     At the H&#39; phase, the liquid crystal has an essentially homeotropic state, but the liquid crystal molecules at the central portion of the liquid crystal mass and away from the substrates of the panel are inclined somewhat relative to the liquid crystal molecules near the substrates panel which are vertically aligned relative to the substrates, as shown in FIG. 1. Thus, at the H&#39; phase, there is difference in the inclination of the liquid crystal molecules between those near the substrate and those at the central portion the mass and away from the substrates of the panel. In this state, a high state of freedom of the movements of the liquid crystal molecule, by rotation, bending or flexing, is useful and effective for stabilizing the retention of the homeotropic transparent state. On the other hand, in such circumstances, the axis of inclination of the liquid crystal molecules having relatively rigid or hard structures at the central portion of the mass during such circumstance is transmitted to the molecules near the panel substrates, and the liquid crystal rapidly changes its phase from homeotropic state to focal-conic state. Further, the H&#39; phase is a meta-stable state resulting in a change to the F phase by such phenomena as heat disturbance. The meta-stability of the H&#39; phase affects the magnitude of the hysteresis effect and stability of the liquid crystal. 
     To evaluate the magnitude and stability of the hysteresis effect of the liquid crystal, it is necessary to define ΔV. As shown in FIG. 1, ΔV is defined such that ΔV=Vu 20  -Vd 90  wherein Vu 20  is the voltage applied to the pane to produce a light transmittance of 20% on the cholesteric→nematic phase transition curve of FIG. 1 and Vd 90  is the voltage applied to produce a light transmittance of 90% on the nematic→cholesteric phase transition curve of FIG. 1. ΔV is thus a parameter which indicates the magnitude of the hysteresis. 
     In the measurement of the voltage hysteresis width (ΔV) which corresponds to the actual driving mode, a two step procedure is used. The first step is made to ascertain the relationship of between light transmittance and applied voltage in the phase transition from cholesteric phase to nematic phase. 
     Initiates a selected voltage V 0  is applied to a selected point of the substrate of the panel and the time dependency of the light transmittance ratio is measured. Next, a voltage V 1 , which is slightly higher than voltage V 0 , is applied to the selected point of the panel and again the time dependency of the light transmittance ratio is measured. In the same manner, the voltage applied to the selected point of the panel is gradually and slightly increased until the voltage becomes equal to or higher than the voltage V H , and at each voltage increase the time dependency of the light transmittance ratio is measured. 
     The light transmittance data for the point in time 10 seconds after the application of the voltage was determined from the data thus obtained, and the relationship between applied voltage and light transmittance was plotted in FIG. 1. 
     The second step is to ascertain the relationship between light transmittance and applied voltage during the phase transition from the nematic phase to the cholesteric phase. 
     Measurements were made as in the first step described above, except that the applied voltage to the panel was gradually decreased from a voltage equal or higher than voltage V H , at which voltage the liquid crystal has a completely homeotropic transparent phase, to V o . Thus, the relationship between light transmittance and applied voltage during the nematic→cholesteric phase transition is obtained. From such two step procedure, the hysteresis loop of the nematic-cholesteric phase transition is obtained. Further, ΔV is determined from the hysteresis loop by measuring the value of the applied voltages Vu 20  and Vd 90 , respectively. 
     The display principle of the liquid crystal composition is of the invention is described hereinafter. 
     First, a voltage of V H  (=2 Vd) is applied across all electrodes of an X-Y matrix-type liquid crystal display device to cause the liquid crystal 1 to be in its H state, which consists of a nematic phase (see FIG. 1 and FIG. 2b). In the H state, as is shown in FIG. 2b, all molecules of the liquid crystal 1 are orientated in the same direction relative to the direction of electrical field, i.e., in a direction perpendicular to substrates 2 and 3. The incident radiation 6, after successively passing through a polarizing plate 4, the substrate 2, the liquid crystal 1 and the substrate 3, reaches another polarizing plate 5 and stops there. The radiation 6 is not transmitted through the polarizing plate 5 since the plates 4 and 5 have different polarization angles and the difference between such angles is just 90°. Accordingly, liquid crystal 1 is in a dark state. 
     When the applied voltage is reduced to zero. (V o ) liquid crystal 1 its dark state is converted from the H state to the F 0  state, which consists of a cholesteric phase (see FIG. 1 and FIG. 2a). After liquid crystal 1, has been converted to the F 0  state, the retention voltage V d  is applied thereto to transform the crystal into its F state, which is optically the same as the F 0  state. In both the F o  and F states, the liquid crystal 1 has a helical structure, which means that the radiation is rotated or scattered during transmittance. Accordingly, as is shown in FIG. 2a, the radiation 6 is at least partially transmitted through polarizing plate 5. Liquid crystal 1 is thus transformed into its lighted state. 
     On the other hand, the initial H state can be constantly maintained due to the hysteresis characteristics of the liquid crystal, even if the applied voltage of 2 Vd (=V H ) is reduced to Vd. Such new or second H state under the application of the voltage Vd, is particularly referred to herein as the H&#39; state, in order to distinguish it from the H state existing under the applied voltage V H . 
     As is apparent from the above description, a display device using the liquid crystal composition of this invention exhibits bistable behavior, that is, it has two stable optical states F and H&#39; under the application of the same voltage Vd. Therefore, we can optionally select either one of these states with the application of the voltage Vd. 
     In the above description, we referred to FIGS. 2a  and 2b, and explained the principle of driving the liquid crystal display device of this invention using two polarizing plates. Alternatively, we can drive the liquid crystal display device without using the polarizing plate. This will be described hereinafter referring to FIGS. 3a and 3b. 
     As is illustrated in FIGS. 3a and 3b, the liquid crystal 1 is sandwiched with two substrates 2 and 3 to form a liquid crystal display panel. The back surface of the display panel is provided with a black plate 7. The illustrated liquid crystal display panel, when it is converted to the F or F o  state, is in a lighted state. This is because, as is shown in FIG. 3a, the incident radiation 6 is scattered or reflected upon irradiation on the liquid crystal 1 (the scattered or reflected radiation is indicated with arrow 8) and therefore is not absorbed in the backing black plate 7. On the other hand, the liquid crystal display panel, when the crystal is in its H&#39; or H state as in FIG. 3b, is dark, because the incident radiation 6 is passed through a layer of the liquid crystal 1 and is finally absorbed into the black plate 7. It is contemplated that a lustrous black plate may be used to increase the contrast between the light state and dark state. 
     EXAMPLES 
     Hereinafter, the present invention will be furthermore described with reference to some working examples. 
     The following is a list of the liquid crystal compositions used in the examples, in which the compositions A, B, E, F and G each is a composition within the scope of the present invention, and the compositions C 1 , C 2 , D, H and I each is a control composition. 
     
         ______________________________________                                    
Liquid Crystal Composition A                                              
                           % by                                           
Liquid Crystal Compounds   weight                                         
______________________________________                                    
 ##STR11##                 18.2                                           
 ##STR12##                 18.2                                           
 ##STR13##                  9.1                                           
 ##STR14##                 12.1                                           
 ##STR15##                  9.1                                           
 ##STR16##                 21.2                                           
 ##STR17##                 12.1                                           
______________________________________                                    
 
    
     
         ______________________________________                                    
Liquid Crystal Composition B                                              
                           % by                                           
Liquid Crystal Compounds   weight                                         
______________________________________                                    
 ##STR18##                 6.5                                            
 ##STR19##                 9.8                                            
 ##STR20##                 9.8                                            
 ##STR21##                 9.8                                            
 ##STR22##                 9.8                                            
 ##STR23##                 13.0                                           
 ##STR24##                 3.3                                            
 ##STR25##                 9.8                                            
 ##STR26##                 9.8                                            
 ##STR27##                 6.5                                            
 ##STR28##                 11.9                                           
______________________________________                                    
 
    
     
         __________________________________________________________________________
Liquid Crystal Composition C.sub.1                                        
Liquid Crystal Compounds  % by weight                                     
__________________________________________________________________________
 ##STR29##                25.0                                            
 ##STR30##                14.3                                            
 ##STR31##                17.9                                            
 ##STR32##                 7.2                                            
 ##STR33##                 7.2                                            
 ##STR34##                16.7                                            
 ##STR35##                11.7                                            
__________________________________________________________________________
 
    
     
         __________________________________________________________________________
Liquid Crystal Composition C.sub.2                                        
Liquid Crystal Compounds  % by weight                                     
__________________________________________________________________________
 ##STR36##                25.0                                            
 ##STR37##                14.3                                            
 ##STR38##                17.9                                            
 ##STR39##                 7.2                                            
 ##STR40##                 7.2                                            
 ##STR41##                16.7                                            
 ##STR42##                11.7                                            
__________________________________________________________________________
 
    
     
         __________________________________________________________________________
Liquid Crystal Composition D                                              
Liquid Crystal Compounds      % by weight                                 
__________________________________________________________________________
 ##STR43##                    14.2                                        
 ##STR44##                    14.2                                        
 ##STR45##                    14.2                                        
 ##STR46##                    10.6                                        
 ##STR47##                     7.1                                        
 ##STR48##                    24.8                                        
C.sub.27 H.sub.45 Br           7.0                                        
CH.sub.3 (CH.sub.2).sub.12 COOC.sub.27 H.sub.45                           
                               7.9                                        
__________________________________________________________________________
 
    
     
         __________________________________________________________________________
Liquid Crystal Composition E                                              
Liquid Crystal Compounds        % by weight                               
__________________________________________________________________________
 ##STR49##                      7.7                                       
 ##STR50##                      7.7                                       
 ##STR51##                      7.7                                       
 ##STR52##                      7.7                                       
 ##STR53##                      7.7                                       
 ##STR54##                      7.7                                       
 ##STR55##                      7.7                                       
 ##STR56##                      7.7                                       
 ##STR57##                      5.1                                       
 ##STR58##                      2.6                                       
 ##STR59##                      2.6                                       
 ##STR60##                      2.6                                       
 ##STR61##                      8.0                                       
 ##STR62##                      2.6                                       
 ##STR63##                      14.9                                      
__________________________________________________________________________
 
    
     
         ______________________________________                                    
Liquid Crystal Composition F                                              
                           % by                                           
Liquid Crystal Compounds   weight                                         
______________________________________                                    
 ##STR64##                 18.2                                           
 ##STR65##                 18.2                                           
 ##STR66##                  9.1                                           
 ##STR67##                 12.1                                           
 ##STR68##                  9.1                                           
 ##STR69##                 21.2                                           
 ##STR70##                 12.1                                           
______________________________________                                    
 
    
     
         ______________________________________                                    
Liquid Crystal Composition G                                              
Liquid Crystal Compounds                                                  
                       % by weight                                        
______________________________________                                    
 ##STR71##             11.4                                               
 ##STR72##             11.4                                               
 ##STR73##             11.4                                               
 ##STR74##             11.4                                               
 ##STR75##             18.9                                               
 ##STR76##             15.1                                               
 ##STR77##              7.6                                               
 ##STR78##             12.8                                               
______________________________________                                    
 
    
     
         __________________________________________________________________________
Liquid Crystal Composition H                                              
Liquid Crystal Compounds        % by weight                               
__________________________________________________________________________
 ##STR79##                      56.1                                      
 ##STR80##                      12.2                                      
 ##STR81##                      12.2                                      
 ##STR82##                       2.4                                      
 ##STR83##                      17.1                                      
__________________________________________________________________________
 
    
     
         ______________________________________                                    
Liquid Crystal Compostion I                                               
Liquid Crystal Compounds                                                  
                       % by weight                                        
______________________________________                                    
 ##STR84##             8.7                                                
 ##STR85##             5.8                                                
 ##STR86##             8.7                                                
 ##STR87##             8.7                                                
 ##STR88##             8.7                                                
 ##STR89##             8.7                                                
 ##STR90##             11.6                                               
 ##STR91##             17.4                                               
 ##STR92##             8.7                                                
 ##STR93##             13.0                                               
______________________________________                                    
 
    
     Example 1 
     Two glass substrates having a ITO (indium oxide In 2  O 3 ) coating were first washed with a detergent and then subsequently washed with isopropyl alcohol, acetone, and pure water. These substrates were then treated with oxygen plasma to improve their surface properties. The substrates were then bonded through a spacer of 12 μm thick polyester film, commercially available from E. I. du Pont Co. under the trade name Mylar®, and sealed with an epoxy adhesive to form a panel. The panel was filled with the above-listed four liquid crystal compositions A, B, C 1 , and D. Four types of liquid crystal display panels; P-A (present invention), P-B (present invention), P-C 1  (control), and P-D (control) were thus prepared. 
     Each of these four liquid crystal display panels were tested to determine their voltage hysteresis width (ΔV). First, a predetermined voltage Vd 1  was set, and the liquid crystal display panel was driven following the driving wave patterns shown in FIGS. 4a and 4b. After writing, the variation of the light transmittance of the panel was recorded as time versus variation of the light transmittance. Similarly, the time variation of the light transmittance of the panel was recorded upon application of a voltage Vd 2 , which is slightly higher than the previously set voltage Vd 1 . Similar recordings were repeated except that the applied voltage was gradually increased in such a manner that Vd 3  →Vd 4 , Vd 4  →Vd 5 , . . . , until a phase transition from the cholesteric phase to nematic phase was caused. Subsequently, a high voltage sufficient to maintain the crystals in its nematic phase was applied to the panel, and then the applied voltage was gradually reduced. During reduction of the voltage, the time variation of the light transmittance of the panel was repeatedly recorded in the manner described above. The results of such recording were plotted in a graph of time versus variation of the light transmittance. Based on the plotted graph of time versus variation of light transmittance, another graph showing light transmittance (determined at a certain time lapse after writing) versus applied voltage was plotted. One of these plotted graphs is set forth in FIG. 5, which concerns the liquid crystal display panel P-B of the present invention. The light transmittance was determined using a photocell and is in mV, and the applied voltage is in volts. 
     The voltage hysteresis width (ΔV) of each of the liquid crystal display panels was evaluated from the graph of light transmittance versus applied voltage. In this evaluation, the writing time was 6 ms/line, and the width was evaluated as 10 sec after writing. The results are summarized in the following Table I. 
     
                       TABLE I                                                     
______________________________________                                    
Liquid crystal                                                            
           Hysteresis width                                               
                         Possible* writing speed                          
display panels                                                            
           (ΔV)    (ms/line)                                        
______________________________________                                    
P-A        0.9           4                                                
P-B        2.5           3                                                
P-C.sub.1 (control)                                                       
           0.3           6                                                
P-D (control)                                                             
           0             15                                               
______________________________________                                    
 *The term &#34;possible&#34; was used herein to indicate that the writting speed 
 varies depending upon the hysteresis width. Generally, the faster the    
 writing speed, the narrower the hysteresis width.                        
 
    
     The above results indicate that the display panels P-A and P-B prepared using the liquid crystal compositions of the present invention has larger hysteresis widths and faster writing speeds than the controls P-C 1  and P-D. The display panels of this invention are therefore compatible with scroll operation. In contrast, prior art display panels are not adapted to scroll operation in a large scale display since they require a long writing time for each scanning line. Further, unexpectedly, the display panels of this invention can have a satisfactory hysteresis width in spite of their shortened writing time, while, in prior art panels, shortening of the writing time tends to narrow the hysteresis width. 
     Example 2 
     The procedure of Example 1 was repeated except that the liquid crystal compositions were replaced by the following five liquid crystal compositions E, F, G, H, and I. Liquid crystal display panels P-E (present invention), P-F (present invention), P-G.(present invention), P-H (control), and P-I (control) were produced. 
     The results are summarized in the following Table II. 
     
                       TABLE II                                                    
______________________________________                                    
Liquid crystal                                                            
           Hysteresis width                                               
                        Possible writing speed                            
display panels                                                            
           (ΔV)   (ms/line)                                         
______________________________________                                    
P-E        3.3          3                                                 
P-F        1.5          4                                                 
P-G        2.7          3                                                 
P-H (control)                                                             
           0.2          5                                                 
P-I (control)                                                             
           1.1          5                                                 
______________________________________                                    
 
    
     It is evident from the above results that the display panels according to this invention exhibit satisfactory hysteresis widths and improved possible writing speed. 
     Example 3 
     The procedure of Example 1 was repeated except that, in this example, the liquid crystal composition C 1  was replaced with the liquid crystal composition C 2 . Similar results were obtained. 
     For further understanding of this invention, the results of the above Examples 1 to 3 are summarized in the following Table III. 
     
                                           TABLE III                               
__________________________________________________________________________
Liquid crys                                                               
        Composition of liquid crystal compounds (% by weight)             
tal display      Ester-type Cyclohexane-phenyl-type                       
Penals  ET BH CHi                                                         
                 ES  TH Total                                             
                            Cy-1                                          
                                Cy-2                                      
                                   Cy-3                                   
                                       Cy-4                               
                                          Total                           
__________________________________________________________________________
P-A        36.4                                                           
              12.1                                                        
                 (51.5) 51.5                                              
P-B     16.3                                                              
           19.6                                                           
              11.9                                                        
                 (16.3)                                                   
                     (9.8)                                                
                        26.1                                              
                            (9.8)  (13.0)                                 
                                       (3.3)                              
                                          26.1                            
P-E     30.8                                                              
           15.4                                                           
              14.9                                                        
                 (5.2)                                                    
                     (2.6)                                                
                        7.8 (7.7)                                         
                                (8.0)                                     
                                   (7.7)  23.4                            
P-F     36.4  12.1                                                        
                 (51.5) 51.5                                              
P-G        45.6                                                           
              12.8                                                        
                 (15.1)                                                   
                     (7.6)                                                
                        22.7       (18.9)                                 
P-H (control) 13.0                                                        
                 (69.6) 69.6       (17.4)                                 
P-I (control) 17.1                                                        
                 (2.4)  2.4 (12.2) (56.1) 68.3                            
P-C.sub.1 (control)                                                       
              11.7                                                        
                 (7.2)                                                    
                     (7.2)                                                
                        14.4                                              
                            (17.9) (39.3) 57.2                            
P-C.sub.2 (control)                                                       
              11.7                                                        
                 (7.2)                                                    
                     (7.2)                                                
                        14.4                                              
                            (17.9) (39.3) 57.2                            
P-D (control)    (7.1)  7.1 (42.6)        42.6                            
__________________________________________________________________________
                   Composition of liquid crystal                          
                                     Characteristics                      
           Liquid crys                                                    
                   compounds (% by weight)                                
                                         Writing                          
           tal display                                                    
                   Heterocyclic type ΔV                             
                                         speed                            
           Penals  DI  Py  Total                                          
                               AZ CHo                                     
                                     (volts)                              
                                         (ms/line)                        
__________________________________________________________________________
           P-A                       0.9 4                                
           P-B                       2.5 3                                
           P-E     (5.1)                                                  
                       (2.6)                                              
                           7.7       3.5 3                                
           P-F                       1.5 4                                
           P-G                       2.7 3                                
           P-H (control)             1.1 5                                
           P-I (control)                                                  
                   (12.2)  12.2      0.2 5                                
           P-C.sub.1 (control)                                            
                   (16.7)  16.7      0.3 6                                
           P-C.sub.2 (control)                                            
                       (16.7)                                             
                           16.7      0.3 6                                
           P-D (control)                                                  
                   (10.6)  10.6                                           
                               24.8                                       
                                  14.9                                    
                                     0   15                               
__________________________________________________________________________
 Liquid crystal compounds:                                                
 ET . . . Ethanetype;                                                     
 BH . . . Bicyclohexanetype;                                              
 CHi . . . Chiral nematic type;                                           
 ES . . . Estertype;                                                      
 TH . . . thioestertype;                                                  
 ##STR94##                                                                
 ##STR95##                                                                
 ##STR96##                                                                
 ##STR97##                                                                
 DI . . . Dioxanetype;                                                    
 Py . . . Pyrimidinetype;                                                 
 Az . . . Azoxytype, and;                                                 
 CH.sub.0 . . . Cholesteric type.