Water based coating composition containing an aminoplast-ether copolymer
BRIEF DESCRIPTION OF THE INVENTION 
     A water-based coating composition containing a water soluble linear aminoplast-ether copolymer containing aminoplast segments interlinked through ether segments. 
     BACKGROUND TO THE INVENTION 
     Aminoplasts are defined herein and in the claims as an A-stage class of thermosetting resin based on the reaction of an amine with an aldehyde and the related acetals containing amines or amides. The most commercially used aldehyde is formaldehyde, and the most important amines are urea and melamine. They are used in molding, adhesives, laminating, textile finishes, permanent-press fabrics, wash-and-wear apparel fabrics, protective coatings, paper manufacture, leather treatment, binders for fabrics, foundry sands, graphite resistors, plaster-of-paris fortification, foam structures, and ion-exchange resins. A significant structural component of an aminoplast resin is the amino group to which is bonded at least one alkylol or alkylol ether or ester functionaI group. Those functional groups enter into condensation (heterolytic) reactions and provide the leaving groups for the reaction. The aminoplast typically provides at least two of such amino groups per molecule and one or two functional groups per amino group. The condensation reaction can generate a low to moderate molecular weight polymer (as would occur in making a B-stage resin), a highly crosslinked polymer (as would occur in making a thermoset C-stage resin) by homopolymerization or copolymerization, or it can generate a modification of the resin that either provides other type functionality or eliminates such functionality from the resin. For example, a starting monomer that contains the amino group with an associated methylol or methylol ether or ester group can be partially condensed and modified with a monomer that possesses, in addition, different functionality (such as ethylenic unsaturation) and such partial modification allows the aminoplast to be dimerized, oligomerized or polymerizod by a homolyric reaction through such different functionality to form aminoplasts with a plethora of methylol and/or methylol ether and/or ester groups. This same result can be achieved by different route, by having the skeleton of the aminoplast possess other functional groups that can enter into heterolytic or homolyric reactions. For example, methacrylamide can be reacted with formaldehyde to form an aminoplast, and through the unsaturation, polymerization can be effected to create a linear polymer with pendant methylol or methylol ether or ester functional groups. Illustrative of such aminoplasts are the following: ##STR2## wherein R is hydrogen, alkyl containing 1 to about 4 carbon atoms, and acyl containing 1 to about 4 carbon atoms; R 0  is alkyl of from 1 to about 4 carbon atoms, aryl, cycloalkyl, and the like; R 1  is alkyl of from 1 to about 4 carbon atoms; and x is 0 or 1, and y is at least 2. 
     The RO-- functionality of such aminoplasts provide the leaving groups of the alkylol (e.g., methylol) or alkylol ether or ester (e.g., methylol ether or ester) functional groups. Alkylol (e.g., methylol), alkylol ether (e.g., methylol ether) or alkylol ester (e.g., methylol ester) groups can condense with themselves to form ROH volatile compounds or water. They can condense with complementary functional groups, such as compounds containing active hydrogen groups, e.g., primary and secondary amines, carboxylic acids, alcohols, phenols, mercaptans, carboxamides (including amides from urea, thiourea), and the like. 
     Most aminoplasts contain a minor amount of dimer and oligomer products. These products are formed in the making of the aminoplast and represent precondensation between aminoplast monomers. The dimer and oligomer products contain substantially more --OR functionality than the aminoplast monomer. 
     As noted above, aminoplasts are used to form thermoset resin structures. Because they contain at least two RO-- functional groups, they are used to react in systems that contain at least two complementary functional groups. Frequently, aminoplasts are added to resin formulations as one of many components. In such embodiments, there are no perceptible step-wise reactions between the aminoplast and any other component of the formulation. In such situations, it is not feasible to determine with any degree of accuracy as to which of the specific components of the formulation the aminoplast reacts. 
     The term &#34;associative thickener&#34; is art recognized to mean a nonionic hydrophobically modified water-soluble polymer capable of interacting in aqueous solution with itself and with other species such as latex particles. Typically they are made by polymerizing polyethylene oxide prepolymers with isocyanates. Mono-ols or diols with large aryl, alkyl, or aryl/alkyl groups are included to provide the hydrophobic modification. They are described in a number of patents. Hoy et al., U.S. Pat. No. 4,426,485, patented Jan. 17, 1984, broadly describes these materials as &#34;a water-soluble, thermoplastic, organic polymer . . . having segments of bunched monovalent hydrophobic groups.&#34; This patent, in its &#34;Description of the Prior Art,&#34; discusses a major segment of the prior art, and without endorsing the conclusions therein stated, reference is made to such description to offer a background to this invention. 
     The two Emmons et al. patents, U.S. Pat. No. 4,079,028 and U.S. Pat. No. 4,155,892, patented Mar. 14, 1978 and May 22, 1979, respectively, describe polyurethane associative thickeners that contain hydrophobic groups interconnected by hydrophilic polyether groups. The thickeners are nonionic. 
     There are a number of commercial associative thickeners based on the descriptions of the Hoy et al. and Emmons et al. patents. 
     Background on the use of thickeners in waterborne polymer systems, including those embraced in the characterization of this invention is set forth in the extensive literature on the subject, such as U.S. Pat. Nos. 4,426,485, 4,155,892, 4,079,028; 3,035,004; 2,795,564; 2,875,166 and 3,037,952, for example. The polymeric thickeners of this invention are also suitable as substitutes for the polymeric thickeners in the polymeric systems disclosed in U.S. Pat. Nos. 2,875,166 and 3,035,004 and in Canadian Pat. No. 623,617. 
     For the purposes of this invention and the discussion of the prior art, the skeletal unit of the aminoplast is the structure of the aminoplast minus the RO-- leaving groups bonded to alkylene of the alkylol or alkylol ether or ester of the aminoplast, regardless of whether any of the RO-- groups are removed from the aminoplast. That skeletal unit is referred to herein and in the claims as &#34;Amp.&#34; 
     In the following description and in the claims hereof, the term &#34;water dispersible,&#34; as such relates to aminoplast containing compositions and precursors to such compositions, that are water soluble or mechanically dispersible in water in a stable particulate form. A stable particulate form is one that retains its chemical characteristics after an extended period of time. It can be mechanically mixed in such particulate form in water, for an extended period of time at normal ambient conditions. 
     The term &#34;linear,&#34; when used herein and in the claims to characterize a polymer, relates to a polymer that is devoid of crosslinking or branching that renders the polymer solid and cured. A &#34;wholly linear&#34; polymer is a polymer that is devoid of crosslinking and branching. A linear polymer may or may not be a wholly linear polymer. 
     The symbols and designations used herein are intended to be consistently applied, especially as used in formulations and equations, unless specifically stated otherwise. 
     THE INVENTION 
     This invention relates to novel waterborne coating compositions. Such compositions are thickened or provided with wetting agent capabilities by the inclusion in the composition of an aminoplast-ether copolymer formed by a process that does not rely on an urethane-forming polymerization reaction in order to generate the copolymer&#39;s backbone structure. 
     This invention relates to a novel water-based coating composition because of the presence in the composition, in addition to the coating vehicle, of a linear aminoplast-ether copolymer of the formula: ##STR3## where the divalent R 01  contains a divalent alkyleneoxy containing moiety, Amp is the skeletal residue of an aminoplast, as stated above, R is defined above, p is a positive number that is equal to the free valence of Amp minus 2, RO is bonded to alkylene units of Amp, and a is a number greater than 1, preferably greater than 2. Amp includes any dimer and oligomer component of the aminoplast. In a much preferred embodiment of the invention, R 01  is derived from a water dispersible alkylene polyether, preferably a water soluble alkylene polyether, and the novel linear aminoplast copolymer of the invention is water dispersible, and preferably, water soluble. 
     In addition, the invention relates to a novel water-based coating composition that contains a linear aminoplast-ether copolymer possessing one or more pendant groups, preferably hydrophobic pendant groups. Such a copolymer contains a unit of the formula: ##STR4## wherein 
     R 02  is a hydrophobic group, different from RO--, that is covalently bonded to Amp through a heteroatom and contains at least two carbon atoms, preferably at least two sequential carbon atoms, 
     p 2  is number that is equal to the free valence of Amp minus (2+q), and q is a positive number. The copolymer preferably contains a ratio of q/a that is at least about 0.01. 
     In another embodiment of the invention, the invention relates to a novel water-based coating composition that contains a linear aminoplast-ether copolymer possessing end groups characterized by a component of the units making up the copolymer, or a monofunctional group that effectively end-caps the copolymer, forming the end group. This yields a copolymer of the formula: ##STR5## wherein each R 00  is the same or different terminal group, such as hydrogen, --R 01  --H, Amp bonded --(OR) p1 , --Amp--(OR) p1 , or any other monofunctional organic groups, such as alkyl, cycloalkyl, aryl, alkaryl, aralkyl, alkyoxyalkyl, aroxyalkyl, cycloalkoxyalkyl, and the like, and p 1  is a positive number that is equal to the free valence of Amp minus 1. In addition, the invention encompasses the use in the coating composition of a copolymer of the formula: ##STR6## where each R 001  is the same or different, and is R 00  or R 02 . 
     A particularly preferred linear aminoplast-ether copolymer comprises units of the formula: ##STR7## wherein R 01  and R are described above, n has a value of at least 2, x is 0 or 1, s is (3+x)-2, and the average value of x in the copolymer is about 0 to about 0.05. Another preferred composition of the invention is a novel linear aminoplast-ether copolymer having the formula: ##STR8## where s+t equals (i) the free valence of the ##STR9## moiety and (ii) 4-x; and the average value of t/s+t is about 0.01 to about 0.5. 
     In a further preferred embodiment of the invention, the linear aminoplast-ether copolymer employed in the coating composition of the invention comprises a copolymer that possesses end groups as illustrated by the following structure: ##STR10## wherein each R 002  is the same or different terminal group, such as hydrogen, --R 01  --H, --(OR) p1 , --Amp 0  --(OR) p1 , or any other monofunctional organic groups, such as alkyl, cycloalkyl, aryl, alkaryl, aralkyl, alkyoxyalkyl, aroxyalkyl, cycloalkoxyalkyl, and the like, and p 1  is a positive number that is equal to the free valence of Amp 0  minus 1. Amp 0  is depicted in formula V. In a preferred embodiment of the invention, the linear aminoplast-ether copolymer comprises a copolymer that possesses end groups affecting the performance of the copolymer. Such embodiment is illustrated by the following structure: ##STR11## wherein each R 003  is the same or different terminal group, such as hydrogen, --R 01  --H, --(OR) p1 , --Amp 0  --(OR) p1 , --OR 02  or any other monofunctional organic groups, such as alkyl, cycloalkyl, aryl, alkaryl, aralkyl, alkyoxyalkyl, aroxyalkyl, cycloalkoxyalkyl, and the like, and p 1  is a positive number that is equal to the free valence of Amp 0  minus 1. Amp 0  has the same meaning as Amp. 
     In the foregoing characterizations set forth in formulae I, Ia, II, IIa, III, IIIa, IV, and IVa, each --OR and --OR 02  group is directly bonded to Amp through a hydrocarbyl moiety bonded to nitrogen therein. 
     This invention relates to aqueous coating systems that contain any one or more of the above defined compositions. For example, the invention relates to a thickened water-based latex coating composition in which water and the coating resin are present in a major amount and one or more of the following aminoplast-based compositions are present in a minor amount: ##STR12## which formulae are described above. Particularly preferred are thickened water containing coating systems in which the aminoplast-based compositions are of the following formulae: ##STR13## which formulae are described above. The coating composition may contain as little as 0.01 to as much as 10 weight percent of the aminoplast-ether copolymer, basis weight of the coating composition exclusive of fillers, pigments and like additives. The ultimate coating composition and its properties will dictate the amount of the copolymer that is employed. The preferred amount is that amount that contributes thickening or wetting agent properties to the coating composition. 
     In addition, the invention relates to a water-based coating composition that contains a major amount of water, and a minor amount of an associative thickener of the formula: ##STR14## wherein R 03  is a monovalent hydrophobe, and v has an average value of about 2 to about 10,000, and an amount of a &#34;dispersed coating polymer&#34; that is greater than the amount of the associative thickener, which dispersed coating polymer provides the basic coating attributes of the composition. In this sense, the dispersed coating polymer is typically solvent dispersible, i.e., it has the capacity of being dissolved by a solvent, and on drying the composition, i.e., removing water and solvent present, the dispersed polymer is curable to either a solid thermoset structure or a solid thermoplastic. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     The linear aminoplast-ether copolymers of formula I et seq. are made by the novel condensation reaction of a polyfunctional aminoplast with a di-functional polyether (alone or with another polyol, as characterized with respect to formulae XII and XIII) in the presence of an acid catalyst. In the prior art, as noted above, aminoplasts are condensed with polyfunctional compounds to produce thermosetting resins or thermoset products (i.e., C-stage resin). The reaction of this invention produces a linear copolymer. Thus, the copolymers of formulae I, II, III, IV, and V are either liquid or thermoplastic solids that are solvent soluble and water dispersible. 
     The linear aminoplast-ether copolymer are made by the copolymerization reaction of a polyfunctional aminoplast with an ether containing two active hydrogen terminal groups, in the presence of an acid catalyst, especially a Bronsted-Lowery acid provided in catalytically effective amounts. The reaction is continued until the desired molecular weight is achieved. The desired molecular weight of the copolymer is dependent on the intended use of the copolymer. The molecular weight of the copolymer may range from about 12,000 to about 800,000, preferably from about 20,000 to about 100,000, and most preferably from about 30,000 to about 80,000. The aminoplast is a polymerizable resin of the general formula: ##STR15## wherein z is a positive number having a value of at least 2. The ether containing two active hydrogen terminal groups comprises a wide variety of compositions. A preferred class of them is nonionic. Illustrative of a preferred class of such ethers are polyalkylene oxides of the formula: 
     
         H-- Alkylene Oxide --H                                     VIII. 
    
     where &#34;alkylene oxide&#34; is a divalent moiety containing at least two alkylene oxide units in which 
     1. the alkylene oxide units form a linear chain and provide a terminal OH, or 
     2. the alkylene oxide are bonded to a starter molecule, such as a diamine, urea, carbamate, phenoxy, amide, bis-imide, and the like, and providing a terminal OH, and/or 
     3. in which alkylene oxide are bonded to a terminal group that possesses a moiety that provides the active hydrogen (--H in formula VIII). 
     Further illustrative of such a preferred class are the water dispersible polyether compounds of the formula: 
     
         H.sub.x1 X--(R.sub.04).sub.x4 (R.sub.05).sub.x5 (R.sub.06).sub.x6 (R.sub.07).sub.x7 (R.sub.08).sub.x8 --XH.sub.x2           IX. 
    
     wherein 
     X is an active hydrogen-attached functional moiety such as oxy (--O--), sulfidyl (--S--), amino (--N&lt;), carboxy (--COO--), carboxamido, silyl, phosphoryl, ureido, and the like; 
     R 04  and R 08  are alkyl of 2 to about 8 carbon atoms; 
     R 05  and R 07  are one or more alkylene oxide units, e.g., such as water dispersible ethylene oxide, propylene oxide, mixed ethylene oxide/1,2-propylene oxide, mixed ethylene oxide/1,3-propylene oxide, mixed ethylene oxide/1,2-butylene oxide, mixed ethylene oxide/1,4-butylene oxide, and the like; 
     R 06  is a divalent group such as alkyleneoxy, alkylenepolyamine, cycloalkylene polyamine, phenoxy, uriedo, carbamate, amide, and the like; 
     x1 and x2 are each equal to the free valence of X; 
     x3, x4, x5, x6 and x7 are each 0 or 1, and one or more of x4 and x6 is 1. 
     Specific illustrations of a limited class of polyethers encompassed by formula IX are the Carbowax® and Pluronic® polyether diols sold by Union Carbide Chemicals &amp; Plastics, Inc. and BASF Wyandotte, respectively. There are a variety of functional fluids based on alkylene oxides that are sold by Union Carbide Chemicals &amp; Plastics, Inc. and BASF Wyandotte that are encompassed by formula IX. The molecular weight of the polyether reagent may range from about 106 and lower, to about 35,000, and higher. 
     In the prior art, as noted above, aminoplasts are condensed with polyfunctional compounds to produce thermosetting resins or thermoset products (i.e., C-stage resin). The above method produces a linear copolymer. Thus, the copolymers of formulae I, II, III, IV, and V are either liquid or thermoplastic solids that are solvent soluble and water dispersible. 
     Aminoplast reagents include, but are not restricted to, aldehyde reaction products of melamines, ureas, benzoguanamines, glycolurils, and the like, to produce the array of aminoplasts, including but not limited to those described in FIG. 1 above. While any of these can be used to make associative thickeners, the glycolurils, such as those of formula X ##STR16## where R and x are defined above, have shown appropriate hydrolyric stability, when reacted with the polyether compounds, such as those encompassed by formula IX, to meet commercial criteria for associative thickener-containing coating compositions. However, the reaction products of such aminoplasts with, e.g., thiois and NH groups from amides and carbamates, encompassed by formula IX, are much more hydrolyrically stable than aminoplast ether linkages. The use of such reactants allow for the production of most hydrolytically stable aminoplast-based copolymers. 
     Suitable polyethers include such diverse polyalkylene polyethers as those having the formula: ##STR17## where x10 has a value of from about 1 to about 400, R 12  are alkyl of 1 to about 4 carbon atoms or acyl of 1 to about 3 carbon atoms. The preferred polyethers are water soluble. The most preferred polyethers are the alkylene polyethers where the predominant alkylene groups are ethylene. The most desirable polyethers are polyethylene oxide diols that possess molecular weights from about 1,000 to about 20,000. 
     Illustrative of the desirable polyethylene oxide diols are those of the formula: 
     
         HO--(--CH.sub.2 CH.sub.2 O).sub.x11 CH.sub.2 CH.sub.2 OH   XI. 
    
     wherein x11 has a value of about 20 to about 500, preferably from about 50 to about 350, and most preferably from about 100 to about 250. 
     A further desirable embodiment of the invention is the modification of the linear aminoplast-ether copolymers used in making the coatings of the invention by including a minor mole proportion of the following unit structure in the repeating structure of the copolymer: 
     
         --AmP--R.sub.15 --                                         XII. 
    
     wherein R 15  is the residue of a diol possessing greater hydrophobicity than R 01 , thereby providing for a linear copolymer containing the structure ##STR18## wherein x29 has a value that is greater than x30. Preferably, x30/x29 is less than about 1, preferably less than about 0.33. Illustrative of such R 15  groups are ##STR19## wherein x31 has a value of about 8 to about 20, x32 has a value of about 8 to about 23, x33 and x34 have values of 0 to about 8. The linear copolymer of formula XIII may be modified to possess the terminal groups of formulae Ia, IIa, IIIa, and IVa, discussed above. 
     The linear aminoplast-ether copolymers embraced by formulae I and XIII, may contain, as well, hydrophobe pendant groups. This is illustrated by the presence of significant hydrophobic groups extending from aminoplast component of the linear backbone of the aminoplast-ether copolymer. Such hydrophobe groups are typically bonded to the backbone through ether or ester groups, as illustrated in formula VI. The nature of the hydrophobe can enhance the performance of the resulting aminoplast-ether copolymer as an associative thickener in water-based coating compositions. Aromatic groups, e.g., phenyl, biphenyl, anthracyl, and the like, present in the hydrophobes are better than hydrophobes based on wholly aliphatic containing groups, especially for high shear viscosity attributes when used in water, and especially so with respect to the use of the associative thickeners in latex paints. Suitable hydrophobe groups are derived from alcohols, thiols, carboxylic acids, carboxamides, and carbamates of the formula: ##STR20## wherein R 09  is hydrogen, alkyl of 8 to about 24 carbon atoms, alkenyl of 8 to about 24 carbon atoms and alkynyl of 8 to about 24 carbon atoms, R 10  is mono, di and tri(aryl), R 11  is aryl, mono, di and tri(alkaryl), mono, di and tri(alkcycloalkyl), alkenyl and alkynyl where the alkyl, alkenyl and alkynyl contain 1 to about 24 carbon atoms and the cycloalkyl contains about 4 to about 8 carbon atoms, R 12  is one or more alkylene oxide, Y is an active hydrogen containing group such as OH, SH, COOH, CONHR 08 , NR 09  COOH, x13, x14, x15 and x16 are 0 or 1, and two or more of x13, x14, x15 and x16 have the value of 1 at the same time. Illustrative of such hydrophobe groups are the following precursor compounds from which the hydrophobe is derived: ##STR21## where the derived hydrophobe are ##STR22## and in which R 10  is aryl, or alkyl of 8 to 24 carbon atoms, x15 has a value of 7 to 23, x16 has a value of 1 to about 20, x19 has a value of 0 to about 120, x26 has a value of about 8 to about 60, x17 has a value of about 7 about 23, x18 has a value of 1 to about 23, x20 is 0 or 1, x21 is 0 or 1, the sum of x20 and x21 is 1 or 2, x22 is 1 to about 20, x23 is 1 to about 20, x27 is 0 or 1, x24 has a value of about 8 to 23, and x25 has a value of about 8 to 20. Another class of such hydrophobes are based on partially saponified fatty acid glycerides such as partially saponified linseed oil, tall oil, cottonseed oil, caster oil, coconut oil, corn oil, oiticica oil, perilia oil, poppyseed oil, rapeseed oil, and the like. A further class of such hydrophobes are ethoxylates of such partially saponified fatty acid glycerides. Illustrative of such esters are ##STR23## where R 16  are the hydrocarbyl portion of the natural fatty acid component of the fatty acid glycerides. Their ethoxylates are illustrated as ##STR24## where x28 has a value of 1 to about 200, and R 16  are the natural fatty acid component of the natural oil. 
     The choice of hydrophobe is primarily dependent on the use ascribed for the associative thickener of the invention. For example, the copolymer without the hydrophobe provides wetting agent and viscosity control features in water and with water-based compositions. In the demanding area of water-based coatings, it is desirable to include a hydrophobe as a component of the aminoplast-ether copolymer of the invention. Any of the aforementioned hydrophobes will affect the viscosity of a latex paint giving rise to benefits to the paint. However, certain of the hydrophobes in combination with certain of the aminoplast-ether copolymers, provide associative thickeners that essentially satisfy the most demanding commercial standards. For example, the use of dodecylphenol ethoxylates as the hydrophobe achieves particularly desirable high shear viscosity characteristics, resistance to spatter and gloss retention in semi-gloss paints when compared to nonylphenol and octylphenol ethoxylates which have often been employed in making associative thickeners with urethane in the polymer backbone. It has also been observed that using tristyrylphenol ethoxylates improves the gloss of semi-gloss paints even further and provides better high shear resistance according to the ICI cone and plate viscometer reading in flat latex paints. Reacting Bisphenol A into the associative thickeners (to form the copolymer of formula XIII) reduces the syneresis common when using associative thickeners in concert with cellulosics. 
     This invention relates to the use of any aminoplast, including those specifically recited in FIG. 1 above, to make the copolymer of the invention. Of these aminoplasts, exceptional performing associative thickeners are obtained from the reaction of glycolurils with alkylene oxide glycols to which are incorporated hydrophobic pendant moieties. 
     The production of the aminoplast-ether copolymers are made by solvent or melt polymerization. The typical preparation of an aminoplast-, such as glycoluril-, based associative thickener involves dissolving the aminoplast (e.g., glycoluril), a polyether compounds within the scope of formula IX (such as a Carbowax® polyether sold by Union Carbide Chemical and Plastics, Inc., Danbury, Conn.), with or without the addition of a more hydrophobic polyol within the scope of formula XII, and an ethoxylated hydrophobe, in a stripping solvent, such as alkylated benzene (e.g., toluene or xylenes). Prior to the combination of these reagent, each may be dried by azeotropic distillation with toluene, xylenes, or a mixture of them, or by any other drying procedure. Total concentration of the reagents in the solvent may be maintained from about 10 to about 60 weight %. The temperature of the mixture may be brought to about 60°-140° C., preferably to about 80°-120° C. An acid catalyst, such as a sulfonic acid catalyst, is then added. The reaction mixture is placed under reduced pressure to bring about a steady distillation of the toluene/xylenes which azeotropes the alcohol byproduct that must be removed in order for the reaction to proceed. Fresh solvent is constantly added to maintain a constant level. The reaction is allowed to proceed until a given high viscosity is achieved as measured by Gardner bubble tubes or until viscosity increase ceases. Such viscosity increase indicates an increase in the molecular weight of the copolymer. 
     Specific Illustration of Solvent Process 
     1. Polyether polyol, hydrophobe and azeotroping solvent (e.g., toluene) are added to an appropriately sized container that accommodates a heater, temperature reading device, a nitrogen inlet, and a Dean Stark water trap and condenser. 
     2. The mixture of step 1 is heated to reflux to dry the mixture by azeotropic distillation. When water removal ceases, the mixture is cooled to about 100° C., and the water trap is removed. A distillation column and receiving vessel are installed in the container. 
     3. Glycoluril (e.g., Powderlink 1174) is added and allowed to melt. 
     4. The catalyst is added and vacuum is applied. The pressure is reduced to a level that causes a steady distillation of solvent at about 100° C. The solvent is continually replenished from a pressure equalizing add funnel. 
     5. As the reaction proceeds, samples are removed and cooled to room temperature, and the Gardner bubble viscosity is measured. 
     6. When the proper viscosity is reached, the heat is removed and the mixture is cooled in a water bath. When the temperature has been reduced to below 75° C., an amine neutralizing agent is added. When the temperature is reduced to below 65° C., the polymer solution is poured out onto trays to air dry. 
     7. The dried polymer is cut into strips and redissolved in water or water/cosolvent mixture. 
     Polymerization in the melt involves the admixture of the same reagents in the absence of a solvent with a heavy duty laboratory mixer (such as an Universal Sigma Blade Mixer, sold by Baker Perkins Guittard SA, Paris, France) at a temperature sufficient to generate leaving groups and remove the reaction condensation products. The ventilation of the reaction is necessary in order to shift the reaction to the right and prevent an equilibrium reaction from occurring that impedes the reaction before the desired degree of polymerization is achieved. 
     Catalysts useable for effecting the copolymerization reaction includes the standard Bronsted-Lowery acid catalysts typically used for the condensation of aminoplast resins. Such acid catalysts include mineral acids (e.g., HCl, H 2  SO 4 , H 3  PO 4 , and the like), aryl sulfonic and alkylated aryl sulfonic acids, such as benzene sulfonic acid, p-toluene sulfonic acid, 1-naphthalene sulfonic acid, 2-naphthalene sulfonic acid, naphthalene-1,5-disulfonic acid, naphthalene-2,7-disulfonic acid, 1,3,6-naphthalene trisulfonic acid, naphtholsulfonic acid, dinonylnaphthalene disulfonic acid, dodecylbenzene sulfonic acid, oxalic acid, maleic acid, hexamic acid, alkyl phosphate ester, phthalic acid, and copolymerized acrylic acid. Of these catalysts, the sulfonic acid catalysts are the most effective and efficient for making the copolymers of the invention and dodecylbenzene sulfonic acid is the most preferred sulfonic acid catalyst. 
     Glycolurils are marketed by Cytec Industries as Cymel 1170, 1171, 1175 and Powderlink 1174. The Cymel versions are either mixed methylolated species and typically contain a relatively high isomer content of up to about 20 weight percent. Powderlink 1174 is a purer form that is solely the methyl ester of the formula: ##STR25## with about 3-5 weight percent of a dimer-oligomer of the monomer form. The purer the monomeric form of the aminoplast, the better it is in forming the copolymers of the invention. In about 5-7 weight percent of Powderlink 1174, x is 0, and such monomer form is trifunctional. The dimer-oligomer forms provide greater amounts of methoxy per molecule. For example, the dimer contains 6 methoxy functional groups. Such tri- and hexa-functionality does not alter this invention. The glycoluril ether linkage is much more resistant to hydrolysis than other aminoplast ether bonds. The higher dimer-oligomer content of the less pure glycolurils is not as favored as the lower dimer-oligomer content of Powder link 1174. 1   
    
     The ratio of aminoplast resin to the difunctional polyether is not narrowly critical. Typically, either the aminoplast resin or the difunctional polyether may be used in molar excess or stoichiometrically equivalent amounts in making the linear copolymer of the invention. In characterizing stoichiometry of the aminoplast resin, the resin is treated as being difunctional since linearity, according to the invention, is achieved when the aminoplast resin functions as a difunctional monomer even though the resin has the capability of higher functionality, e.g., tri- and tetrafunctionality, as the case may be. Thus, more than one mole of a polyether diol to one mole of, e.g., a glycoluril such as Powderlink 1174, represents a stoichiometric excess of the polyether to the glycoluril. Using this characterization, one may use between 1-2 moles of one of these reagents to 1 mole of the other. Either the polyether or the aminoplast may be in excess. However, it is more typical to use a mole amount of one reagent of about 1-1.75 to 1 of the other reagent. Typically, one employs a molar excess of the aminoplast resin because one may incorporate more hydrophobicity into the copolymer this way. This is especially the case when the copolymer is dimeric to oligomeric (e.g., possessing less than about 15 repeating units). When making higher polymeric structures, one uses a greater proportion of the polyether reagent, up to a 1:1 mole ratio. In general, it is desirable to use a molar excess of aminoplast of about 1.001-1.5 moles to 1 mole of the difunctional polyether. The amount of monofunctional hydrophobe reagent, in the typical case, should not exceed about 2 moles, nor be less than about 0.001 mole, of the monofunctional hydrophobe per mole of reacted aminoplast resin in the copolymer of the invention. Usually, the amount of monofunctional hydrophobe ranges from about 1 mole to about 0.01 mole per mole of reacted aminoplast. 
     The use of aminoplast reagents leads to an unexpected degree of formulating latitude in polymer synthesis. By varying the ratios of polyether and hydrophobe components, it is possible to make a large number of associative thickener copolymers that impart ICI viscosity of 1.2 poise in flat paint at 4.5 lb. loading, but which give a range of 15,000 to 75,000 centipoise at low shear. This latitude permits the facile tailoring of associative thickeners for a wide variety of paint and nonpaint applications. 
     Waterborne coatings may be defined as coatings that contain water as the major volatile component and utilize water to dilute the coating to application consistency. These coatings consist mainly of resinous binder, pigments, water, and organic solvent. The type of pigmentation and the method of incorporation of the pigment vary widely. 
     Waterborne coatings can be made by dispersing, emulsifying or emulsion polymerizing the resin binder by use of added surfactants. This technique leads to opaque liquids. Because some hard resins are difficult or impossible to disperse directly into water, the resin sometimes can be dissolved in a water-immiscible solvent, and the resulting solution dispersed by the use of added surfactants. In this case, the solvent aids subsequent film coalescence. Surface activity or water dispersability also can be introduced into resin molecules by chemical modification of the resin by introducing functional polar groups such as the carboxyl group. 
     Some very finely dispersed resins appear as clear or slightly hazy liquids; they frequently are described as soluble, solubilized, colloidal dispersions, micro-emulsions, hydrosols, etc. These resins contain built-in functional groups that confer water &#34;solubility&#34; upon the resin, and, normally, external added surfactants are not used. 
     Waterborne resin binders can be classified as anionic, cationic, or non-ionic. Anionic dispersions are characterized by negative charges on the resin or by negative charges on the surfactant associated with the resin. Cationic dispersions have a positive charge on the resin or on the surfactant associated with the resin. Nonionic dispersions are those that have been dispersed by addition of nonionic surfactants or that contain a built-in hydrophilic segment such as polyethylene oxide which is part of the main chain of a relatively hydrophobic resin molecule. 
     The coating compositions may be of the thermosetting or thermoplastic varieties. The resin used in forming the coating may be insoluble in water, and the conversion of such a resin into a waterborne system typically involves converting the resin into an emulsion or dispersion. In the context of this invention, the waterborne composition contains the aminoplast-ether copolymer associative thickener of the invention. 
     The aqueous polymer dispersions may be prepared according to well known emulsion polymerization procedures, using one or more emulsifiers of an anionic, cationic, or nonionic type. Mixtures of two or more non-neutralizing emulsifiers regardless of type may be used. The amount of emulsifier may range from about 0.1 to 10% by weight or sometimes even more, based on the weight of the total monomer charge. In general, the molecular weight of these emulsion polymers is high, e.g., from about 100,000 to 10,000,000 number average molecular weight, most commonly above 500,000. 
     The water insoluble resin may be any of those known in the art, and may be a conventional natural or synthetic polymer latex emulsified with one of a nonionic, cationic or anionic surfactant. The primary resins are based on homopolymerized and copolymerized olefinic monomers such as vinyl acetate; vinyl chloride; styrene; butadiene; vinylidene chloride; acrylonitrile; methacrylonitrile; acrylic acid; methacrylic acid; alkyl acrylates; alkyl methacrylates; acrylamide; methacrylamide; hydroxyethyl methacrylate (&#34;HEMA&#34;); glycidyl methacrylate; dihydroxypropyl methacrylate; homopolymers of C 2  -C 40  alpha-olefins such as ethylene, isobutylene, octene, nonene, and styrene, and the like; copolymers of one or more of these hydrocarbons with one or more esters, nitriles or amides of acrylic acid or of methacrylic acid or with vinyl esters, such as vinyl acetate and vinyl chloride, or with vinylidene chloride; and diene polymers, such as copolymers of butadiene with one or more of styrene, vinyl toluene, acrylonitrile, methacrylonitrile, and esters of acrylic acid or methacrylic acid, and the like. It is also quite common to include a small amount, such as 0.1 to 5% or more, of an acid monomer in the monomer mixture used for making the copolymers mentioned above by emulsion polymerization. Acids used include acrylic, methacrylic, itaconic, crotonic, maleic, fumaric, and the like. 
     The vinyl acetate copolymers are well-known and include copolymers such as vinyl acetate/butyl acrylate/2-ethylhexyl acrylate, vinyl acetate/butyl maleate, vinyl acetate/ethylene, vinyl acetate/vinyl chloride/butyl acrylate and vinyl acetate/vinyl chloride/ethylene. 
     Other waterborne systems involve reactive copolymers that are crosslinked by the presence of complementary functional groups in the system. For example, a copolymer of acrylic ester/glycidylmethacrylate can be emulsified and crosslinked by the presence of a melamine-formaldehyde resin similarly emulsified in the system. In another system, a copolymer of HEMA and another acrylate, hydroxyl terminated polyesters, polyethers, or polyurethanes, can be emulsified and crosslinked by the presence of either an aminoplast resin, a polyisocyanate or blocked polyisocyanate. 
     The term &#34;acrylic polymer&#34; means any polymer wherein at least 50% by weight is an acrylic or methacrylic acid or ester, including mixtures of such acids and esters individually and together. The term &#34;vinyl acetate polymer&#34; means any polymer containing at least 50% by weight of vinyl acetate. 
     Even small particle size (about 0.1-0.15 micron) acrylic and other latices are thickened effectively, and flow and leveling improved, by thickeners of the invention. 
     The amount of the aminoplast-ether copolymer described herein that is employed in the coating composition of the invention is not narrowly critical. That amount will vary based on the resin system used, the water concentration, the amount of fillers and the choice of fillers, the presence or absence of thixotropic agents, and the like. Also, the amount of the copolymer will be based on how the copolymer is intended to be used in the formulation, e.g., used as a wetting agent or as a thickening agent. In that respect, the amount of the aminoplast-ether copolymer in the composition is sufficient to thicken the composition or the amount of the aminoplast-ether copolymer in the composition is sufficient to function as a wetting agent in or for the composition. However, in general, the amount of the copolymer will range from about 0.1 weight percent to about 15 weight percent, preferably from about 0.5 weight percent to about 10 weight percent, and most preferably from about 1 weight percent to about 8 weight percent, of the weight of the coating composition, exclusive of fillers, pigments and like additives. 
     EXAMPLE 1 
     Carbowax® 8000 2  (300 grams, 0.0357 moles), Igepal RC-620 3  (23.0 grams, 0.0338 moles), a mixture of dodecylphenolethoxylates, were combined with 1356 grams toluene in a 2 liter reaction vessel fitted with a Dean Stark water trap. The mixture was refiuxed under nitrogen to remove water by azeotropic distillation. The Dean Stark trap was removed, and a distillation column was fitted to the flask. Powderlink 1174 (15.92 grams, 0.050 moles) was added and the temperature was raised to 100° C. and Nacure 5076 4  (1.38 grams) (dodecylbenzene sulfonic acid) was added. Vacuum was applied to reduce the pressure inside the vessel to approximately 510 mm Hg. At this pressure the toluene distilled at a slow, steady rate. The toluene was constantly replenished to maintain a constant solvent level. This proceeded for 125 minutes at which time the viscosity was &#34;X&#34; on the Gardner bubble scale. The copolymer solution was cooled to 70° C. and dimethylethanolamine (0.53 gram) was added to quench the acid. The copolymer solution was cooled further to 60° C. and then poured out onto trays to air dry. The dried polymer was cut into small pieces and was dissolved at 20% polymer solids in a 4/1 water-diethylene glycol monobutyl ether mixture. 
    
    
    
     EXAMPLE 2 
     Procedure For Making Associative Thickeners Without Solvent 
     Carbowax 8000 (2204 grams, 0.262 moles) Igepal RC620 (168.9 grams, 0.248 moles), and 500 grams of toluene were placed in a 12 liter vessel equipped with a Dean Stark water trap. The materials were heated to reflux to azeotrope off water. Once the mixture was dry the remainder of the toluene was removed with vacuum. Powderlink 1174 (117.0 grams, 0.367 moles) was added and allowed to melt out. After the Powderlink had melted the material in the vessel was transferred to a 5 liter sigma blade mixer preheated to 105° C. The mixer was turned to run at 20 rpm. Nacure 5076 catalyst (7.10 grams) was added and the top was placed on the mixer. Vacuum was applied (27/30 in. achieved) and held for 1.75 hours as the viscosity increased. When the material had become quite viscous the heat was removed and dimethylethanolamine (3.87 grams, 0.043 mole) in 10 grams of toluene was added and the mixture was allowed to stir for a further 30 minutes. Diethyleneglycol monobutyl ether (1850 grams) and aleionized water (7200 grams) were added and the mixture was allowed to stir until the material had dissolved. The resulting solution was filtered through a cone filter. Paint results are as follows: 
     
         ______________________________________                                    
flat vinyl acrylic     semi-gloss vinyl acrylic                           
(formulation below):   (formulation below):                               
______________________________________                                    
ICI:      1.05 poise   ICI:      0.90 poise                               
Stormer:  104 KU       Stormer:  78 KU                                    
Brookfield:                                                               
          49,000 cps   Brookfield:                                        
                                 8,000 cps                                
______________________________________                                    
 
    
     EXAMPLE 3 
     Using the procedure of Example 1, with the indicated modifications, the following other aminoplast-ether copolymers were made: 
     Aminoplast-ether Copolymer Formulation 
     
         ______________________________________                                    
Reagent                Concentration                                      
______________________________________                                    
Cymel 1171 (mixed ether glycoluril).sup.5                                 
                       0.0628  moles                                      
Carbowax 8000          0.0349  moles                                      
Tergitol NP-10.sup.6   0.0489  moles                                      
p-Toluene sulfonic acid                                                   
                       0.53    grams                                      
toluene                1412    grams                                      
______________________________________                                    
 .sup.5 Cytec Industries, Inc.                                            
 .sup.6 Ethoxylated nonyl phenol, sold by Union Carbide Chemical &amp;        
 Plastics, Inc.                                                           
 
    
     Conditions: The maximum reaction temperature was 100° C. The reaction was carried out at atmospheric pressure (no vacuum pulled). The Gardner scale was used in monitoring viscosity. 
     
         ______________________________________                                    
Reagent                 Concentration                                     
______________________________________                                    
Cymel 303 (hexamethoxymethylmelamine).sup.7                               
                        0.070   moles                                     
Carbowax 8000           0.047   moles                                     
Tergitol NP-10          0.052   moles                                     
p-Toluene sulfonic acid 0.94    grams                                     
toluene                 1,665   grams                                     
______________________________________                                    
 .sup.7 Cytec Industries, Inc.                                            
 
    
     Conditions: The maximum reaction temperature was 100° C. The reaction was carried out at atmospheric pressure (no vacuum pulled). The Gardner scale was used in monitoring viscosity. 
     Evaluation In Semi-Gloss Latex Paint Formulation 
     The 20% solution of example 1 was evaluated in a semi-gloss trade paint formulation, which consisted of a 24.4% PVC system using UCAR 376 vinyl-acrylic latex with Ti-Pure R-900 TiO 2 . Listed below are the rheological and application results for example 1 and two commercial nonionic associative thickeners. 
     
         __________________________________________________________________________
Associative                                                               
         Loading, active                                                  
                 Brookfield                                               
                         Stormer                                          
                              ICI   60°                            
Thickeners                                                                
         lbs/100 gallons                                                  
                 cps @ 0.5 rpm                                            
                         KU   poise                                       
                                 Sag                                      
                                    gloss                                 
__________________________________________________________________________
Example 1                                                                 
         5.0     9,720   85   1.00                                        
                                 10.0                                     
                                    45                                    
Acrysol SCT-270.sup.8                                                     
         5.0     13,200  95   1.22                                        
                                 13.6                                     
                                    59                                    
Acrysol RM-825.sup.9                                                      
         5.0     2,640   85   1.14                                        
                                  6.8                                     
                                    37                                    
__________________________________________________________________________
 .sup.8 Rohm &amp; Haas Company, Philadelphia, PA                             
 .sup.9 Rohm &amp; Haas Company, Philadelphia, PA                             
 
    
     Evaluation In Flat Latex Paint Formulation 
     
         __________________________________________________________________________
Associative                                                               
         Loading, active                                                  
                 Brookfield                                               
                         Stormer                                          
                              ICI                                         
                                 Spatter                                  
Thickeners                                                                
         lbs/100 gallons                                                  
                 cps @ 0.5 rpm                                            
                         KU   poise                                       
                                 amount                                   
__________________________________________________________________________
Example 1                                                                 
         4.5     36,240  106  1.22                                        
                                 trace                                    
Acrysol SCT-270                                                           
         4.5     59,600  118  1.40                                        
                                 nil                                      
Acrysol RM-825                                                            
         4.5     10,000   95  1.25                                        
                                 trace                                    
__________________________________________________________________________
 
    
     Procedure For Making and Testing Latex Paint Using Aminoplast Based Associative Thickeners 
     The following are the two primary formulations for evaluating aminoplast based associative thickeners. One is of a flat vinyl acrylic and the other is a semi-gloss vinyl acrylic. Typically both formulations are made in 5 gallon batches that are split into pints after the grind and let-down stage, but prior to the addition of the premix which contains the associative thickener. 
     The premix is added while the paint is being well agitated to ensure that the associative thickener is well incorporated into the paint. The paint is then allowed to sit at rest for 60 minutes to allow the material to further equilibrate followed by rheological measurements which involve 
     1. viscosity measurement in Krebs Units (KU) on a Stormer viscometer (ASTM D 562-81) 
     2. high shear measurement in poise at 10,000 s -1  on an ICI cone and plate viscometer (ASTM D 4287-83) 
     3. pH and temperature measurements are obtained. 
     The paints are maintained at room temperature (˜23.5° C.) and are evaluated as above at 24 hours, 1 week, 1, 2, 3, 6, and 12 months with the following additions: 
     1. a syneresis measurement is obtained by determining the amount in millimeters of the clear liquid that may separate to the top of the paint 
     2. a low shear measurement is obtained in centipoise (cps) at 0.5 rpm on a Brookfield RVT viscometer (ASTM D 2196-86). 
     After the 24 hour rheological measurements the flat paints are evaluated for spatter resistance according to ASTM procedure D 4707-87 with the exception that the paints are rated by the amount of spatter produced from nil, trace, slight, definite and pronounced. After the 24 hour rheological measurements the semi-gloss paints are evaluated for gloss at 60° C. after 1 day and 1 week room temperature air dry of a 0.004 mil draw down. Also the semi-gloss paints are evaluated for sag and leveling according to ASTM procedures D 4400-84 and D 2801-69. 
     The hydrolytic stability of the associative thickeners are determined by subjecting the paints to an elevated temperature (48.9° C.) for 4 weeks with rheological measurements obtained at 1 week intervals. The associative thickeners are determined to be stable if the Stormer viscosity does not lose more than 10% of the initial value. 
     Procedure for Making Latex Paint 
     1. Add water (and propylene glycol for semi-gloss) to 5-gallon container, begin agitation on a Hockmeyer Model Lab 2 type disperser equipped with a 4 inch dispersing blade. 
     2. Add HEC for the flat formulation and let mix agitate 5 minutes at low speed (˜1000 rpm). 
     3. Add dispersant and mix 5 minutes, add other additives and pigment(s) and grind at high speed (˜2000 rpm) for the specified time. 
     4. For the semi-gloss formulation prepare a premix in a separate container consisting of the water, HEC and ammonia, ensuring that the HEC is well dispersed in the water prior to the addition of the ammonia. 
     5. Add remaining let-down ingredients and agitate for 40 minutes, check weight per gallon and pH, divide into pint containers. 
     
         __________________________________________________________________________
Flat vinyl acrylic                                                        
                  Supplier      Pounds                                    
                                    Gallons                               
__________________________________________________________________________
Grind Stage                                                               
Water                           170.94                                    
                                    20.52                                 
Cellosize ER-15K (HEC thickener)                                          
                  Union Carbide 1.00                                      
                                    0.09                                  
Mix HEC 5 minutes at low speed.                                           
Tamol 731 (dispersant)                                                    
                  Rohm &amp; Haas   10.50                                     
                                    1.14                                  
Proxel GXL (preservative)                                                 
                  Zeneca Biocides                                         
                                1.00                                      
                                    0.10                                  
Colloids 643 (defoamer)                                                   
                  Rhone.sub.-- Poulenc                                    
                                2.00                                      
                                    0.26                                  
AMP-95 (Co-dispersant)                                                    
                  Angus Chemical                                          
                                1.00                                      
                                    0.13                                  
Tergitol NP-10 (Nonionic surfactant)                                      
                  Rohm &amp; Haas   1.00                                      
                                    0.11                                  
TI-Pure R-901 (TiO.sub.2 Primary Hiding                                   
                  DuPont        200.00                                    
                                    6.40                                  
Pigment)                                                                  
Grind TiO.sub.2 @ high speed 20 minutes                                   
ASP-400 (Aluminum Minerals &amp; Chemicals                                    
                                125.0                                     
                                    5.82                                  
Silicate extender pigment)                                                
Duramite CaCO.sub.3 (extender pigment)                                    
                  Thompson, Weinman &amp; Co.                                 
                                201.2                                     
                                    8.91                                  
Grind @ high speed 20 minutes                                             
Record maximum grind temperature                                          
Let Down                                                                  
Water                           50.00                                     
                                    6.00                                  
UCAR 376 (Vinyl-acrylic latex                                             
                  Union Carbide 271.5                                     
                                    30.00                                 
55% solids)                                                               
Texanol (Coalescing Agent)                                                
                  Eastman Chemical                                        
                                7.90                                      
                                    1.00                                  
Ammonia (pH adjusting agent)                                              
                  Aldrich       1.00                                      
                                    0.12                                  
Sub total:                      1044.04                                   
Mix at low speed 30 minutes                                               
Weight/Gallon 12.95                                                       
Record pH:                                                                
Remove and divide into pints (522 grams/pint)                             
Premix:                                                                   
Propylene glycol (freeze thaw agent)                                      
                  Chemcentral   18.60                                     
                                    2.15                                  
Water                           117.70                                    
                                    14.13                                 
Associative thickener at 20% solids                                       
                  Example 1 above                                         
                                22.50                                     
                                    2.60                                  
Colloids 643 (defoamer)                                                   
                  Rhone-Poulenc 4.00                                      
                                    0.52                                  
Total:                          1206.84                                   
                                    100.00                                
Pigment volume concentration % 55.34                                      
Volume Solids % 38.19                                                     
__________________________________________________________________________
 
    
     
         __________________________________________________________________________
Semi-gloss vinyl acrylic                                                  
                   Supplier   Pounds                                      
                                  Gallons                                 
__________________________________________________________________________
Grind Stage                                                               
Water                         9.58                                        
                                  1.15                                    
Propylene glycol   Chemcentral                                            
                              60.00                                       
                                  6.94                                    
Tamol 731 (dispersant)                                                    
                   Rohm &amp; Haas                                            
                              10.20                                       
                                  1.11                                    
Colloids 643 (defoamer)                                                   
                   Rhone Poulenc                                          
                              1.25                                        
                                  0.16                                    
Ti-Pure R-900 (TiO.sub.2 Hiding Pigment)                                  
                   DuPont     255.00                                      
                                  7.66                                    
Grind TiO.sub.2 @ high speed 30 minutes; record maximum grind             
temperature:                                                              
Let Down                                                                  
Water                         130.00                                      
                                  15.61                                   
Cellocize ER-15,000 (HEC thickener)                                       
                              1.00                                        
                                  0.09                                    
Premix water and HEC, add ammonia, agitate 10 minutes                     
UCAR 376 (Vinyl-acrylic latex                                             
                   Union Carbide                                          
                              417.00                                      
                                  46.08                                   
55% solids)                                                               
Ammonia                       2.00                                        
                                  0.24                                    
Texanol (Coalescing Agent)                                                
                   Eastman Chemical                                       
                              11.50                                       
                                  1.45                                    
Triton GR-7M (Anionic surfactant)                                         
                   Rohm &amp; Haas                                            
                              1.00                                        
                                  0.12                                    
Colloids 643 (defoamer)                                                   
                   Rhone Poulenc                                          
                              1.25                                        
                                  0.16                                    
Nuosept 95 (biocide)                                                      
                   Huls America                                           
                              3.00                                        
                                  0.33                                    
Sub Total                     902.78                                      
Mix at low speed 30 minutes                                               
Premix:                                                                   
Water                         129.80                                      
                                  15.58                                   
Triton × 114 (nonionic surfactant)                                  
                   Rohm &amp; Haas                                            
                              1.00                                        
                                  0.11                                    
Associative Thickener at 20% solids                                       
                   Example 1 above                                        
                              25.00                                       
                                  2.89                                    
Coloids 643 (defoamer)                                                    
                   Rhone Poulenc                                          
                              2.50                                        
                                  0.33                                    
Total:                        1061.08                                     
                                  100.00                                  
Pigment volume concentration %: 23.19                                     
Volume solids %: 33.03                                                    
__________________________________________________________________________