the aliphatic polyoxaesters of the present invention are the reaction product of an aliphatic polyoxycarboxylic acid and at least one of the following compounds : a diol ( or polydiol ), a lactone ( or lactone oligomer ), a coupling agent or combination thereof . suitable aliphatic alpha - oxycarboxylic acids for use in the present invention generally have the following formula : wherein r 1 and r 2 are independently selected from the group consisting of hydrogen or an alkyl group containing from 1 to 8 carbon atoms and r3 is an alkylene containing from 2 to 12 carbon atoms or is an oxyalkylene group of the following formula : wherein c is an integer in the range of from about 2 to about 5 , d is an integer in the range of from about 0 to about 12 , and e is an integer in the range of from about 2 to about 5 . these aliphatic alpha - hydroxycarboxylic acids may be formed by reacting a diol or polydiol with an alpha - halocarboxylic acid such bromoacetic acid or chloroacetic acid under suitable conditions . suitable diols or polydiols for use in the present invention are diol or diol repeating units with up to 8 carbon atoms having the formulas : wherein r 4 is an alkylene unit containing from 2 to 8 methylene units ; a is an integer in the range of from 1 to about 1000 . examples of suitable diols include diols selected from the group consisting of 1 , 2 - ethanediol ( ethylene glycol ), 1 , 2 - propanediol ( propylene glycol ), 1 , 3 - propanediol , 1 , 4 - butanediol , 1 , 5 - pentanediol , 1 , 3 - cyclopentanediol , 1 , 6 - hexanediol , 1 , 4 - cyclohexanediol , 1 , 8 - octanediol and combinations thereof . examples of preferred polydiols include polydiols selected from the group consisting of polyethylene glycol ( h [-- o -- ch 2 -- ch 2 --] a oh ) and polypropylene glycol ( h [-- o -- ch 2 - ch ( ch 3 )--] a oh ). the polymer produced by reacting the aliphatic dioxycarboxylic acid with the diols discussed above should provide a polymer generally having the formula : wherein r 1 , r 2 , r 3 , r 4 and a are as described above ; and n is an integer in the range of from about 1 to about 10 , 000 and preferably is in the range of from about 10 to about 1 , 000 and most preferably in the range of from about 50 to about 200 . suitable lactone monomers that may be used in the present invention generally have the formula : ## str4 ## these lactone monomers may be polymerized to provide polymers of the following general structures : wherein r 5 is selected from the group consisting of -- c ( r 6 )( r 7 )--, --( ch 2 ) 3 -- o --, -- ch 2 -- ch 2 -- o -- ch 2 --, -- cr 8 h -- ch 2 --, --( ch 2 ) 4 --, --( ch 2 ) f -- o -- c ( o )-- and --( ch 2 ) f -- c ( o )-- ch 2 --; r 6 and r 7 are independently hydrogen or an alkyl containing from 1 to 8 carbon atoms ; r 8 is hydrogen or methyl ; f is an integer of from about 2 to 6 ; b is an integer in the range of from 1 to n such that the molecular weight of formula ix is less than about 40 , 000 ; p is an integer in the range of from 1 to m such that the molecular weight of formula x is less than about 40 , 000 ; g represents the residue minus from 1 to l hydrogen atoms from the hydroxyl groups of an alcohol previously containing from 2 to 12 hydroxyl groups ; and l is an integer from about 1 to about 12 . preferably g will 30 be the residue of a dihydroxy alcohol minus both hydroxyl groups and the molecular weights of formulas ix and x will be less than about 40 , 000 . suitable lactone - derived repeating units may be generated from the following monomers include but are not limited to lactone monomers selected from the group consisting of glycolide , d - lactide , 1 - lactide , meso - lactide , ε - caprolactone , p - dioxanone , trimethylene carbonate , 1 , 4 - dioxepan - 2 - one , 1 , 5 - dioxepan - 2 - one and combinations thereof . the polymer formed by reacting the above described diol ( or polydiol ) vi and the aliphatic polyoxycarboxylic acid v may also be copolymerized in a condensation polymerization with the lactone polymers ix described above to form a polymer generally of the formula : [(-- c ( o )-- c ( r 1 )( r 2 )-- o -- r 3 -- o -- c ( r 1 )( r 2 )-- c ( o )--( o -- r 4 ) a -- o ) s ( c ( o )-- r 5 -- o ) b ] w xii wherein s and w are independently integers in the range of from about 1 to about 1 , 000 . these polymers may be made in the form of random copolymers or block copolymers . to the diols , aliphatic polyoxycarboxylic acids and lactone monomers described above there may be added a coupling agent selected from the group consisting of trifunctional or tetrafunctional polyols , oxycarboxylic acids , and polybasic carboxylic acids ( or acid anhydrides thereof ). the addition of the coupling agents causes the branching of long chains , which can impart desirable properties in the molten state to the polyester prepolymer . examples of suitable polyfunctional coupling agents include trimethylol propane , glycerin , pentaerythritol , malic acid , citric acid , tartaric acid , trimesic acid , propane tricarboxylic acid , cyclopentane tetracarboxylic anhydride and combinations thereof . the amount of coupling agent to be added before gelation occurs is a function of the type of coupling agent used and the polymerization conditions of the polyoxaester or molecular weight of the prepolymer to which it is added . generally in the range of from about 0 . 1 to about 10 mole percent of a trifunctional or a tetrafunctional coupling agent may be added based on the moles of aliphatic polyoxaester polymers present or anticipated from the synthesis . the polymerization of the aliphatic polyoxaester is preferably performed under melt polycondensation conditions in the presence of an organometallic catalyst at elevated temperatures . the organometallic catalyst is preferably a tin - based catalyst e . g . stannous octoate . the catalyst will preferably be present in the mixture at a mole ratio of diol , aliphatic polyoxycarboxylic acid and optionally lactone monomer to catalyst will be in the range of from about 15 , 000 to 80 , 000 / 1 . the reaction is preferably performed at a temperature no less than about 120 ° c . under reduced pressure . higher polymerization temperatures may lead to further increases in the molecular weight of the copolymer , which may be desirable for numerous applications . the exact reaction conditions chosen will depend on numerous factors , including the properties of the polymer desired , the viscosity of the reaction mixture , and the glass transition temperature and softening temperature of the polymer . the preferred reaction conditions of temperature , time and pressure can be readily determined by assessing these and other factors . generally , the reaction mixture will be maintained at about 220 ° c . the polymerization reaction can be allowed to proceed at this temperature until the desired molecular weight and percent conversion is achieved for the copolymer , which will typically take about 15 minutes to 24 hours . increasing the reaction temperature generally decreases the reaction time needed to achieve a particular molecular weight . in another embodiment , copolymers of aliphatic polyoxaester can be prepared by forming an aliphatic polyoxaester prepolymer polymerized under melt polycondensation conditions , then adding at least one lactone monomer or lactone prepolymer . the mixture would then be subjected to the desired conditions of temperature and time to copolymerize the prepolymer with the lactone monomers . the molecular weight of the prepolymer as well as its composition can be varied depending on the desired characteristic which the prepolymer is to impart to the copolymer . however , it is preferred that the aliphatic polyoxaester prepolymers from which the copolymer is prepared have a molecular weight that provides an inherent viscosity between about 0 . 2 to about 2 . 0 deciliters per gram ( dl / g ) as measured in a 0 . 1 g / dl solution of hexafluoroisopropanol at 25 ° c . those skilled in the art will recognize that the aliphatic polyoxaester prepolymers described herein can also be made from mixtures of more than one diol or dioxycarboxylic acid . one of the beneficial properties of the aliphatic polyoxaester made by the process of this invention is that the ester linkages are hydrolytically unstable , and therefore the polymer is bioabsorbable because it readily breaks down into small segments when exposed to moist bodily tissue . in this regard , while it is envisioned that co - reactants could be incorporated into the reaction mixture of the aliphatic dioxycarboxylic acid and the diol for the formation of the aliphatic polyoxaester prepolymer , it is preferable that the reaction mixture does not contain a concentration of any co - reactant which would render the subsequently prepared polymer nonabsorbable . preferably , the reaction mixture is substantially free of any such co - reactants if the resulting polymer is rendered nonabsorbable . the polymers of this invention can be melt processed by numerous methods to prepare a vast array of useful devices . these polymers can be injection or compression molded to make implantable medical and surgical devices , especially wound closure devices . the preferred wound closure devices are surgical clips , staples and sutures . alternatively , the aliphatic polyoxaesters can be extruded to prepare fibers . the filaments thus produced may be fabricated into sutures or ligatures , attached to surgical needles , packaged , and sterilized by known techniques . the polymers of the present invention may be spun as multifilament yarn and woven or knitted to form sponges or gauze , ( or non - woven sheets may be prepared ) or used in conjunction with other molded compressive structures as prosthetic devices within the body of a human or animal where it is desirable that the structure have high tensile strength and desirable levels of compliance and / or ductility . useful embodiments include tubes , including branched tubes , for artery , vein or intestinal repair , nerve splicing , tendon splicing , sheets for typing up and supporting damaged surface abrasions , particularly major abrasions , or areas where the skin and underlying tissues are damaged or surgically removed . additionally , the polymers can be molded to form films which , when sterilized , are useful as adhesion prevention barriers . another alternative processing technique for the polymers of this invention includes solvent casting , particularly for those applications where a drug delivery matrix is desired . in more detail , the surgical and medical uses of the filaments , films , and molded articles of the present invention include , but are not necessarily limited to : in another embodiment , the aliphatic polyoxaester is used to coat a surface of a surgical article to enhance the lubricity of the coated surface . the polymer may be applied as a coating using conventional techniques . for example , the polymer may be solubilized in a dilute solution of a volatile organic solvent , e . g . acetone , methanol , ethyl acetate or toluene , and then the article can be immersed in the solution to coat its surface . once the surface is coated , the surgical article can be removed from the solution where it can be dried at an elevated temperature until the solvent and any residual reactants are removed . for use in coating applications the aliphatic polyoxaesters should exhibit an inherent viscosity , as measured in a 0 . 1 gram per deciliter ( g / dl ) of hexafluoroisopropanol ( hfip ), between about 0 . 05 to about 2 . 0 dl / g , preferably about 0 . 10 to about 0 . 80 dl / g . if the inherent viscosity were less than about 0 . 05 dl / g , then the polymer may not have the integrity necessary for the preparation of films or coatings for the surfaces of various surgical and medical articles . on the other hand , 15 although it is possible to use polymers with an inherent viscosity greater than about 2 . 0 dl / g , it may be exceedingly difficult to do so . although it is contemplated that numerous surgical articles ( including but not limited to endoscopic instruments ) can be coated with the polymer of this invention to improve the surface properties of the article , the preferred surgical articles are surgical sutures and needles . the most preferred surgical article is a suture , most preferably attached to a needle . preferably , the suture is a synthetic absorbable suture . these sutures are derived , for example , from homopolymers and copolymers of lactone monomers such as glycolide , lactide , ε - caprolactone , 1 , 4 - dioxanone , and trimethylene carbonate . the preferred suture is a braided multifilament suture composed of polyglycolide or poly ( glycolide - co - lactide ). the amount of coating polymer to be applied on the surface of a braided suture can be readily determined empirically , and will depend on the particular copolymer and suture chosen . ideally , the amount of coating copolymer applied to the surface of the suture may range from about 0 . 5 to about 30 percent of the weight of the coated suture , more preferably from about 1 . 0 to about 20 weight percent , most preferably from 1 to about 5 percent by weight . if the amount of coating on the suture were greater than about 30 weight percent , then it may increase the risk that the coating may flake off when the suture is passed through tissue . sutures coated with the polymers of this invention are desirable because they have a more slippery feel , thus making it easier for the surgeon to slide a knot down the suture to the site of surgical trauma . in addition , the suture is more pliable , and therefore is easier for the surgeon to manipulate during use . these advantages are exhibited in comparison to sutures which do not have their surfaces coated with the polymer of this invention . in another embodiment of the present invention when the article is a surgical needle , the amount of coating applied to the surface of the article is an amount which creates a layer with a thickness ranging preferably between about 2 to about 20 microns on the needle , more preferably about 4 to about 8 microns . if the amount of coating on the needle were such that the thickness of the coating layer was greater than about 20 microns , or if the thickness was less than about 2 microns , then the desired performance of the needle as it is passed through tissue may not be achieved . in another embodiment of the present invention , the aliphatic polyoxaester can be used as a pharmaceutical carrier in a drug delivery matrix . to form this matrix the polyoxaesters would be mixed with a therapeutic agent to form the matrix . the variety of different therapeutic agents which can be used in conjunction with the aliphatic polyoxaesters of the invention is vast . in general , therapeutic agents which may be administered via the pharmaceutical compositions of the invention include , without limitation : antiinfectives such as antibiotics and antiviral agents ; analgesics and analgesic combinations ; anorexics ; antihelmintics ; antiarthritics ; antiasthmatic agents ; anticonvulsants ; antidepressants ; antidiuretic agents ; antidiarrheals ; antihistamines ; antiinflammatory agents ; antimigraine preparations ; antinauseants ; antineoplastics ; antiparkinsonism drugs ; antipruritics ; antipsychotics ; antipyretics , antispasmodics ; anticholinergics ; sympathomimetics ; xanthine derivatives ; cardiovascular preparations including calcium channel blockers and beta - blockers such as pindolol and antiarrhythmics ; antihypertensives ; diuretics ; vasodilators including general coronary , peripheral and cerebral ; central nervous system stimulants ; cough and cold preparations , including decongestants ; hormones such as estradiol and other steroids , including corticosteroids ; hypnotics ; immunosuppressives ; muscle relaxants ; parasympatholytics ; psychostimulants ; sedatives ; and tranquilizers ; and naturally derived or genetically engineered proteins , polysaccharides , glycoproteins , or lipoproteins . the drug delivery matrix may be administered in any suitable dosage form such as oral , parenteral , a subcutaneously as an implant , vaginally or as a suppository . matrix formulations containing the aliphatic polyoxaester may be formulated by mixing one or more therapeutic agents with the polyoxaester . the therapeutic agent , may be present as a liquid , a finely divided solid , or any other appropriate physical form . typically , but optionally , the matrix will include one or more additives , e . g ., nontoxic auxiliary substances such as diluents , carriers , excipients , stabilizers or the like . other suitable additives may be formulated with the polyoxaester and pharmaceutically active agent or compound , however , if water is to be used it should be added immediately before administration . the amount of therapeutic agent will be dependent upon the particular drug employed and medical condition being treated . typically , the amount of drug represents about 0 . 001 % to about 70 %, more typically about 0 . 001 % to about 50 %, most typically about 0 . 001 % to about 20 % by weight of the matrix . the quantity and type of polyoxaester incorporated into the parenteral will vary depending on the release profile desired and the amount of drug employed . the product may contain blends of polyoxaester to provide the desired release profile or consistency to a given formulation . the polyoxaester , upon contact with body fluids including blood or the like , undergoes gradual degradation ( mainly through hydrolysis ) with concomitant release of the dispersed drug for a sustained or extended period ( as compared to the release from an isotonic saline solution ). this can result in prolonged delivery ( over , say 1 to 2 , 000 hours , preferably 2 to 800 hours ) of effective amounts ( say , 0 . 0001 mg / kg / hour to 10 mg / kg / hour ) of the drug . this dosage form can be administered as is necessary depending on the subject being treated , the severity of the affliction , the judgment of the prescribing physician , and the like . individual formulations of drugs and polyoxaester may be tested in appropriate in vitro and in vivo models to achieve the desired drug release profiles . for example , a drug could be formulated with a polyoxaester and orally administered to an animal . the drug release profile could then be monitored by appropriate means such as , by taking blood samples at specific times and assaying the samples for drug concentration . following this or similar procedures , those skilled in the art will be able to formulate a variety of formulations . the examples set forth below are for illustration purposes only , and are not intended to limit the scope of the claimed invention in any way . numerous additional embodiments within the scope and spirit of the invention will become readily apparent to those skilled in the art . the diacid , 3 , 6 - dioxaoctanedioic acid , was synthesized by oxidation of triethylene glycol . the oxidation was carried out in a 500 milliliter , three - neck round bottom flask equipped with a thermometer , an additional funnel , a gas absorption tube and a magnetic spinbar . the reaction flask was lowered into an oil bath resting upon a magnetic stirrer . to the reaction flask was added 157 . 3 ml of a 60 % nitric acid solution ; 37 . 0 g of triethylene glycol was added to the additional funnel . the contents of the flask were heated to 78 °- 80 ° c . a test tube containing 0 . 5 g of glycol and one milliliter of concentrated nitric acid was warmed in a water bath until brown fumes started appearing . the contents were then added to the reaction flask . the mixture was stirred for a few minutes ; the glycol was then carefully added . the rate of addition had to be monitored extremely carefully to keep the reaction under control . the addition rate was slow enough so that the temperature of the exothermic reaction mixture was maintained at 78 °- 82 ° c . after the addition was completed ( 80 minutes ), the temperature of the reaction mixture was maintained at 78 °- 80 ° c . for an additional hour . while continuing to maintain this temperature range , the excess nitric acid and water was then distilled off under reduced pressure ( water suction ). the syrupy residue was cooled ; some solids appeared . the reaction product had the ir and nmr spectra expected for the dicarboxylic acid ; the crude product was used as such for esterification . esterification of the crude 3 , 6 - dioxaoctanedioic acid was accomplished as follows : to the reaction flask containing 36 g of the crude diacid , was added 110 ml of methanol . this was stirred for 3 days at room temperature after which 15 g of sodium bicarbonate was added and stirred overnight . the mixture was filtered to remove solids . to the liquor was added an additional 10 g of sodium bicarbonate ; this mixture was stirred overnight . the mixture was again filtered ; the liquor was fractionally distilled . nmr analysis of the esterified product showed a mixture of dimethyl triglycolate ( 78 . 4 mole %) and monomethyltriglycolate ( 21 . 6 mole %). no significant condensation of diacid was observed . preparation of polyoxaester from the methyl esters of 3 , 6 - dioxaoctanedioic acid and ethylene glycol ## str6 ## a flame dried , mechanically stirred , 50 - milliliter glass reactor suitable for polycondensation reaction , was charged with 20 . 62 g ( approximately 0 . 1 mole ) of the methyl esters of 3 , 6 - dioxaoctanedioic acid from example 1 , 18 . 62 g ( 0 . 3 mole ) of distilled ethylene glycol , and 0 . 0606 ml of a solution of 0 . 33 m stannous octoate in toluene . after purging the reactor and venting with nitrogen , the temperature was gradually raised over the course of 26 hours to 180 ° c . a temperature of 180 ° c . was then maintained for another 20 hours ; all during these heating periods under nitrogen at one atmosphere , the methanol formed was collected . the reaction flask was allowed to cool to room temperature ; it was then slowly heated under reduced pressure ( 0 . 015 - 1 . 0 mm ) over the course of about 32 hours to 160 ° c ., during which time additional distillates were collected . a temperature of 160 ° c . was maintained for 4 hours after which a sample , a few grams in size , of the polymer formed was taken . the sample was found to have an inherent viscosity ( i . v .) of 0 . 28 dl / g , as determined in hexaflouroisopropanol ( hfip ) at 25 ° c . at a concentration of 0 . 1 g / dl . the polymerization was continued under reduced pressure while raising the temperature , in the course of about 16 hours , from 160 ° c . to 180 ° c . ; a temperature of 180 ° c . was maintained at for an additional 8 hours , at which time a polymer sample was taken and found to have an i . v . of 0 . 34 dl / g . the reaction was continued under reduced pressure for another 8 hours at 180 ° c . the resulting polymer has an inherent viscosity of 0 . 40 dl / g , as determined in hfip at 25 ° c . and at a concentration of 0 . 1 g / dl . a flame dried , mechanically stirred , 250 - milliliter glass reactor , suitable for polycondensation reaction , was charged with 44 . 44 g ( 0 . 2 mole ) of 3 , 6 , 9 - trioxaundecanedioic acid , 62 . 07 g ( 1 . 0 mole ) of distilled ethylene glycol , and 9 . 96 milligrams of dibutyltin oxide . after purging the reactor and venting with nitrogen , the contents of the reaction flask were gradually heated under nitrogen at one atmosphere , in the course of about 32 ## str7 ## hours , to 180 ° c ., during which time the water formed was collected . the reaction mass was allowed to cool to room temperature . the reaction mass was then heated under reduced pressure ( 0 , 015 - 1 . 0 mm ), gradually increasing the temperature to 180 ° c . in about 40 hours ; during this time additional distillates were collected . the polymerization lo was continued under reduced pressure while maintaining 180 ° c . for an additional 16 hours . the resulting polymer has an inherent viscosity of 0 . 63 dl / g as determined in hfip at 25 ° c . and at a concentration of 0 . 1 g / dl . a flame dried , mechanically stirred , 500 - milliliter ## str8 ## glass reactor ( suitable for polycondensation reaction ) was charged with 123 . 8 g ( 0 . 2 mole ) polyglycol diacid ( molecular weight about 619 ), 62 . 07 g ( 1 . 0 mole ) of distilled ethylene glycol , and 9 . 96 milligrams of dibutyltin oxide . after purging the reactor and venting with nitrogen , the contents of the reaction flask was heated under nitrogen at one atmosphere , gradually increasing the temperature to 200 ° c . in about 32 hours ; during this time the water formed was collected . the reaction flask was heated gradually under reduced pressure ( 0 , 015 - 1 . 0 mm ) from room temperature to 140 ° c . in about 24 hours , during which time additional distillates were collected . a polymer sample of about ten grams was taken at this stage , and found to have an i . v . of 0 . 14 dl / g in hfip at 25 ° c ., 0 . 1 g / dl . the polymerization was continued under reduced pressure while heating from 140 ° c . to 180 ° c . in about 8 hours , and then maintained at 180 ° c . for an additional 8 hours . a polymer sample was again taken and found to have an i . v . of 0 . 17 dl / g . the reaction temperature was then increased to 190 ° c . and maintained there under reduced pressure for an additional 8 hours . the resulting polymer has an inherent viscosity of 0 . 70 dl / g as determined in hfip at 25 ° c . and at a concentration of 0 . 1 g / dl . a flame dried , 50 - milliliter , round bottom single - neck flask was charged with 5 grams of the aliquot of the polyoxaester of example 4 having an i . v . of 0 . 14 dl / g , 5 . 0 grams ( 0 . 0438 mole ) of ε - caprolactone , 5 . 0 grams ( 0 . 0490 mole ) of trimethylene carbonate , and 0 . 0094 milliliters of a 0 . 33 molar solution of stannous octoate in toluene . the flask was fitted with a magnetic stirrer bar . the reactor was purged with nitrogen three times before venting with nitrogen . the reaction mixture was heated to 160 ° c . and maintained at this temperature for about 6 hours . the copolymer was dried under vacuum ( 0 . 1 mm hg ) at 80 ° c . for about 16 hours to remove any unreacted monomer . the copolymer has an inherent viscosity of 0 . 34 dl / g , as determined in hfip at 25 ° c . and at a concentration of 0 . 1 g / dl . the copolymer is a viscous liquid at room temperature . the mole ratio of polyoxaester / pcl / ptmc was found by nmr analysis to be 47 . 83 / 23 . 73 / 28 . 45 . a flame dried , 25 - milliliter , round bottom , singleneck flask was charged with 6 grams of the polyoxaester of example 4 having an i . v . of 0 . 17 dl / g ., 8 . 1 grams ( 0 . 0731 mole ) of ε - caprolactone , 0 . 9 grams ( 0 . 008 ) mole of glycolide and 0 . 0080 milliliters of a 0 . 33 molar stannous octoate solution in toluene . the flask was fitted with a magnetic stirrer bar . the reactor was purged with nitrogen three times before venting with nitrogen . the reaction mixture was heated to 160 ° c . and maintained at this temperature for about 18 hours . the copolymer has an inherent viscosity of 0 . 26 dl / g in hfip at 25 ° c . and at a concentration of 0 . 1 g / dl . the copolymer is solid at room temperature . the mole ratio of polyoxaester / pcl / pga / caprolactone was found by nmr analysis to be 56 . 54 / 37 . 73 / 3 . 79 / 1 . 94 . the polyoxaester of example 3 was tested for in vitro hydrolysis at both 50 ° c . and at reflux temperature . a 100 mg sample of the polyoxaester , placed in 100 ml of a phosphate buffer solution ( 0 . 2 m in phosphate , ph 7 . 27 ), was completely hydrolyzed in about 7 days at 50 ° c ., whereas at reflux it was completely hydrolyzed in about 16 hours . polyoxaester of example 2 was tested for in vitro hydrolysis at 50 ° c . and at reflux temperature . a 100 mg sample of the polyoxaester , placed in a 100 ml buffer solution ( ph 7 . 27 ), was completely hydrolyzed in about 5 days at 50 ° c ., whereas at reflux it was completely hydrolyzed in about 16 hours .
the present invention describes a new aliphatic polyoxaesters that is bioabsorbable and may be used to produce surgical devices such as sutures , sutures with attached needles , molded devices , and the like . the invention also contemplates a process for producing these polyesters . the aliphatic polyoxaesters of the present invention have a first divalent repeating unit of formula i : -- c -- o ---- o -- c -- c -- ] i and a second repeating unit selected from the group of formulas consisting of : ## str1 ## and combinations thereof .