fig1 through 3 represent a golf club head manufactured according to the method of the invention . the head is of the wood type and it comprises an actual head body 1 extended laterally and upwardly by a neck 2 adapted to receive , in a known manner , the club shaft ( not represented ). the body of the actual head is constituted by a shell 3 formed by an assembly of walls having fine thicknesses comprised between 2 and 5 mm . the assembly includes an upper wall 5 , a lower wall 6 , a peripheral wall 7 , and a front wall 8 whose front face 80 constitutes the striking surface adapted to hit the ball during the shot . moreover , the inner face 81 of the front wall 8 is in support on the front face 900 of the resistance wall 9 . according to the invention as illustrated , the shell 3 is made of a plastic material , reinforced or otherwise , of the injected thermoplastic type , such as polyamide , polypropylene or abs ( acrylonitrilebutadienestyrene ). shell 3 , forming an outer peripheral envelope and constituting an inner closed cavity 11 , is advantageously filled with a filler material 12 , such as a low density foam and , for example , a polyurethane foam . further , the head includes a resistance element 200 , for example , made of high - strength aluminum , constituted by the resistance wall 9 and by a lateral tubular portion 94 , preferably made of steel , and attached on the side of wall 9 . this tubular portion at least partially constitutes the rigid structure of the neck 2 on which the club shaft is adapted to be force - fitted . the resistance wall 9 has the overall shape of the striking surface and comprises a peripheral shoulder or edge 90 . according to an advantageous arrangement , the rear portion of the actual head includes an inertial weight 10 super - molded in the material 70 constituting the rear peripheral wall 7 . the weight 10 has the general shape of a cylindrical element comprising a throat or recess 24 and is made of a material having substantial density , such as brass , bronze , steel , or other material . the invention is directed to the method for producing the head such as described previously , such method comprising various successive phases . thus , in a preliminary step , a core 13 ( see fig5 , 7 , 8 ) is made of a material m2 having a low melting point and comprises , for example , a metallic core made of , for example , a tin , lead and bismuth alloy . the core 13 is produced , for example , by molding and has the general shape of the inner cavity 11 . thus , the core includes a front face 14 , an upper face 15 , a lower face 16 , and a lateral peripheral face 17 . it advantageously comprises three longitudinal vertical recesses 18 , 19 , 20 and , according to a complementary characteristic , a rear housing 21 extended by a retention hole 22 adapted to retain a weight 10 having , for example , a general cylindrical shape , and made of a high density material such as brass or bronze . it must be noted that the housing 21 has dimensions , especially diametrical dimensions , that are greater than those of the weight 10 so as to create a space el ( see fig1 ) between the walls of the housing and those of the weight . this space e1 is adapted to become filled with material during injection of the shell , as is explained below . in an intermediate step , the weight is engaged in the rear housing 21 ( see fig8 ) and is retained there by means of the retention hole 22 ( see fig9 ). however , the weight could be positioned at another place and , as represented in fig2 , it could be positioned and inserted from a lower portion of the club head . in another preliminary step ( see fig1 ), the resistance wall 9 of element 200 is made , for example , by aluminum molding . the resistance wall 9 has a front face 900 and a peripheral edge 90 . the thickness of the resistance wall 9 can be , for example , from 4 to 6 mm . it can be provided with inner reinforcement ribs , as is represented in fig2 . the wall can be made of any other appropriate material , such as a composite material . preferably , the resistance element comprises a tubular portion 94 made of steel which is attached and welded to or sunk in wall 9 . in addition , this portion comprises a neck 940 ( see fig2 ), facilitating the manipulation of the tubular portion so as to easily adjust the &# 34 ; lie &# 34 ; or &# 34 ; loft &# 34 ; angle of the head . in a step prior to the injection of the shell ( see fig1 , 13 ), the resistance element 200 and the meltable core 13 with its weight 10 are placed in an injection mold 25 . the retention of the resistance element 200 in the mold 25 is ensured by a retention shaft 26 engaged in hole 27 of neck 2 , whereas the retention of the core 13 in the mold is ensured by a transverse member 28 . once the mold is ready with resistance element 200 and meltable core 13 , the shell 3 is injected in a main step ( see fig1 ). the injected material m1 adapted to form the shell and to coat the core 13 and the resistance wall 9 is injected via injection hole 29 . the injection material m1 thus enters the peripheral space e left free between the wall of the mold and the elements occupying the inside thereof , in other words , core 13 and resistance wall 9 . in addition , the first material m1 enters into the space e1 left free between weight 10 and the walls of housing 21 , and even enters into throat 24 , thus ensuring the retention of the weight . as such , the weight is held by material m1 of the shell , and more particularly , by an extension 70 of the peripheral wall 7 ( see fig2 ). during injection , the injected material m1 also enters into the longitudinal recesses 18 , 19 of the core , so as to form with the walls of the shell , reinforcement ribs . the meltable core 13 is made of a material m2 whose melting point is lower than the melting point of material m1 from which the shell is obtained . preferably , it is a tin - alloy , lead , or bismuth based alloy . as an example , the composition by weight is as follows : as ( trace ); sn = 15 to 20 %; bi = 40 to 45 %; pb = remainder . the melting temperature of this alloy is less than 100 ° c . the injection temperature of material m1 when it is a polyamide of the reinforced &# 34 ; zytel &# 34 ; type is approximately 280 ° c . the front wall 8 of the shell is in contact with the resistance wall 9 and the peripheral edge 90 ensures a good connection between the shell and the resistance element 200 . in a first complementary step , the mold 25 is opened ( see fig1 ) so as to extract therefrom the club head thus formed ( fig1 ), whereas in a second complementary step ( see fig1 , 18 ), the head is heated so as to obtain the melting of meltable core 13 , and thus , by the elimination of the melted material , an inner cavity 11 is created . in a third complementary step ( see fig1 , 20 ), a low density material m3 such as polyurethane foam , is poured into the inner cavity 11 to form the filling 12 of the cavity . the pouring is undertaken , for example , via hole 30 left by the transverse member 28 in the peripheral wall 7 . fig2 is a perspective view of a first variation according to which the rear face of the resistance wall 9 comprises reinforcement ribs enabling the thickness of the wall to be reduced and to substantially lighten the element . it includes , for example , a peripheral rib 91 and two vertical ribs 92a , 92b . fig2 and 23 represent a second variation according to which the lower rear portion of the resistance wall 9 comprises two protuberances extending in parallel towards the rear so as to at least partially project from the lower wall 6 of the shell 3 . fig2 is a view similar to fig1 , illustrating a variation according to which the weight 10 is rendered affixed to core 13 by virtue of a fixing pin or axle 130 . in a variation of the method , the weight could be affixed to the meltable core during the molding thereof . before being placed in the mold 25 , the core 13 with the weight 10 is affixed to the resistance wall 9 so as to constitute an integral sub - assembly , as is represented in fig2 . the affixation of the core 13 with the resistance element can be accomplished by any appropriate means and especially by nesting , adhesion , welding , or screwing . the weight 10 can take any appropriate shape and any position without , however , exceeding the scope of the invention . fig2 represents a variation in a partial sectional top view illustration . in this variation , the weight 10 is constituted by a peripheral metallic wall 100 comprising a succession of holes 240 enabling the injection material of the shell to penetrate inside it and to ensure the retention of the weight . the invention is not limited to a golf club head of the &# 34 ; wood &# 34 ; type . more specifically , the head could be of any other type , and especially a head of the &# 34 ; iron &# 34 ; type , as is illustrated in fig2 . in order to facilitate an understanding of this illustration , those elements that are similar to the embodiment described previously bear the same reference numerals employed in the previous description . the thickness e2 of the front wall 8 can vary and especially be reduced from the base ( ba ) upwards ( ha ) so that the striking surface 80 can be given the desired general inclination a . thus , on the basis of one common resistance element 200 , it would be possible to mold an entire series of heads whose striking surfaces have different inclinations . the thickness e2 can vary horizontally ( see fig2 ). in a variation , it could be provided that the weight ( s ) be retained in one or more housings provided in the resistance wall . the weight ( s ) can also be fixed to the wall by other means , such as by screwing or adhesion . fig2 represents a variation in which the starting meltable core is constituted of several separate parts 130 , 131 , 132 . as such , only some parts of the core can be eliminated after the injection operation . the other parts can act as weights , localized at pre - determined and advantageous positions . fig2 shows , for example , a head according to the invention whose central part was the only one to be eliminated . the two lateral parts 130 , 132 act as weights in the context of a lateral distribution of the masses of the head , as is known . the invention is not limited to the particular embodiments described and represented as examples herein , but also comprises all technical equivalents and combinations thereof .
a method of manufacturing a golf club head that includes a peripheral shell constituted by an assembly of walls obtained by injecting a plastic material forming an inner cavity enclosing at least one inner insert kept immobilized by a partial plastic material coating of the shell . prior to the injection step of the shell , an assembly is placed and immobilized in the mold which is comprised of a meltable core made of a second material having a melting point that is lower than the melting point of the plastic material in the space left free between the walls of the mold and the assembly , so as to coat the meltable core and all or a part of the free portion of the insert . finally , all or a portion of the meltable core is eliminated to enable an inner volume to be freed so as to form the inner cavity .