i have found , and hereby disclose , a process for preparing an absorptive , bacteriostatic non - woven medical substrate in which a solution of a specific silicone quaternary amine is applied conjointly with a member of a specific class of rewetting agents which in the system of the invention act as hydrophilic coupling agents . such rewetting agents impart the necessary water absorptive qualities in the product yet become substantive ( non - leachable ) on the fabric meeting the bioactivity , leachability , cytotoxicity , non - flammability , anti - static and absorptive properties enumerated above . i have found that an aqueous - based solution preferably containing : ( 1 ) from about 0 . 2 to about 1 . 1 % of 3 -( trimethoxysilyl )- propyloctadecyl dimethyl ammonium chloride as the microbiocide , together with ( 2 ) from about 0 . 5 to 1 . 5 weight % of an epoxy - polyoxyalkylene modified organosilicone as a hydrophilic coupling agent , sometimes referred to as a &# 34 ; rewetter &# 34 ; herein , when applied to a suitable non - woven cellulosic - based substrate will produce a waxy , water - insoluble , bioactive , absorbent , wettable finish on the material which retains both the bioactive material and the hydrophilic coupling agent yet conforms to the necessary cytotoxicity , non - flammability and anti - static requirements listed above . while not wishing to be bound by any particular theory it appears that a combination of the two materials , which may be applied separately but preferably together , produces a type of crosslinked matrix reactively bonded to the fiber of the substrate . the presence of the epoxy - polyoxyalkylene organosilicone material in the treatment bath serves not only to provide the necessary rewetting / absorptive qualities for the finished product but also prevents the silicone quaternary amine bioactive material from complexing and becoming gelled during processing operations thus extending shelf life and reducing the loss of microbiocide from the solution . the aqueous - based solutions used in the process of my invention are typically applied by padding onto a suitablee non - woven substrate although other application procedures may be used . over a period of continued use it was observed that a pad bath containing only an aqueous solution of the silicone quaternary amine bioactive material become contaminated with metal ions , such as sodium , calcium , lithium , barium , potassium and magnesium , which ions are frequently contained in the cellulosic substrate as a result of its manufacturing procedure . for instance , over a period of a few hours during continued application i have observed apparent homo - polymerization of the silicone quaternary amine bioactive compound pad bath which homo - polymerization eventually gells the entire pad bath . the bath must be discarded , however as the bioactive material is the subject of u . s . government regulations and must be carefully inventoried ; it is also necessary to &# 34 ; neutralize &# 34 ; the material prior to discharging the gelled pad bath . unexpectedly i have found that the presence of a rewetter / surfactant material in the pad bath prevents the bath from gelling . non - ionic surfactant materials present in amounts of from 0 . 5 to 3 . 0 times the solid concentration of the silicone quaternary amine bioactive material may be used . however , due to its superior value as a rewetter i prefer to use the epoxy polyoxyalkylene modified organosilicone material of the type mentioned above and described in more detail below . suitable non - woven substrates are used in the process of my invention are essentially all cellulosic in nature and include paper , cotton , rayon and possibly wool , but not the substrates composed essentially entirely of an acrylic , polyester or nylon fiber . the preferred substrate is a dry laid spray bonded paper toweling material which is bonded with acrylic resins and contains about 80 - 85 % by weight paper ( cellulose ) with 15 - 20 % by weight acrylic resin binder . this material is available from the fort howard paper company under their style designation e - 34 . also suitable is a wet - laid paper that is creped and print bonded and which is composed of about 90 % by weight cellulose and about 10 % by weight acrylic binder . such materials include the scott hi - loft materials under style designations 3051 and 3055 available from the scott paper company . non - woven substrates containing significantly less than about 80 % cellulosic content are not preferred . the procedure of my invention will now be described with reference to the attached drawing . as shown in the figure a non - woven substrate is directed from a supply reel through a pad bath ( the content of which are explained below ) and passed through a nip roll to achieve an overall wet pickup ( wpu ) of between about 75 and 125 % calculated on the weight of the non - woven substrate . preferably the wet pickup is in the range of about 85 to about 115 % also expressed on the weight of the substrate . next the impregnated substrate is passed through a stack of steam cans maintained at a suitable temperature so that dry / cure occurs at between about 280 ° and 360 ° f . as the wet material is passed over the series of steam cans the lower stack of cans tends to remove the water and dry the material while the upper stack of cans adds additional heat and cures the material setting the applied components to the substrate . preferably the material is subjected to a temperature in the range of 280 °- 300 ° f . for at least about 5 seconds . the dried , finished product is then led away from the stack of steam cans , rolled and stored wrapped in plastic bags or the like . the preferred silicone quaternary amine bioactive material is 3 -( trimethoxysilyl )- propyloctadecyl - dimethyl ammonium chloride which is described in u . s . pat . no . 3 , 730 , 701 , the disclosure of which is hereby incorporated by reference . a class of suitable bioactive silyl quaternary amine compounds have the formula : ## str1 ## in which r is a c 11 - 22 alkyl group and r 1 is chlorine or bromine . the preferred silicone quaternary amine is 3 -( trimethoxysilyl )- propyloctadecyl dimethyl ammonium chloride and is available as a 42 % active solids in methanol from dow corning corporation of midland , michigan under the designation dc - 5700 ( formerly q9 - 5700 ). this material is well accepted in commerce and has been approved not only as a bacteriostatic textile treatment but also as a bactericidal component for medical device / non - drug applications . as the hydrophilic coupling agent there is used a member of the class of the epoxy - polyoxyalkylene modified organosilicones described in u . s . pat . no . 4 , 184 , 004 , the disclosure of which is incorporated herein by reference . the preferred material is available in commerce from union carbide corporation and is believed to respond to the following general structure : in which the units are end - capping units and are identical to each other , the various &# 34 ; d &# 34 ; and &# 34 ; m &# 34 ; units having the following configuration : enlarged structure ## str2 ## as disclosed in u . s . pat . no . 4 , 184 , 004 . in the above formula r represents either hydrogen or methyl and the total of a + b is believed to be from 5 to 200 . the average values of x , y and z are as follows : as disclosed at column 3 lines 35 - 50 of u . s . pat . no . 4 , 184 , 004 . this particular combination of hydrophilic coupling agent and bioactive compound is believed to be substantive on the fabric in accordance with the following scheme : for purposes of illustration the natural fiber , i . e . cellulose , surface may be depicted as having a series of hydroxyl groups extending therefrom . thus a possible linking reaction between the bioactive silyl quaternary amine and the cellulose may be : ## str3 ## a possible linking reaction between the hydrophilic organosilicone terpolymer may be : ## str4 ## and linking between the quaternary amine and the organosilicone terpolyer may be : ## str5 ## as illustrated , the cyclohexyl epoxy group of the coupling agent combines with the trihydroxy silyl group of the bioactive compound to form a complex which , when contacted with a cellulosic substrate , forms a carbon - oxygen bond , probably a covalent bond , with the substrate by removal of one mole of water . the manner in which the bioactive compound plus hydrophilic coupling agent are placed onto the substrate may be by brushing , spraying or other suitable means known in the textile arts . i prefer to apply the required components onto the substrate by padding them using a pad bath having generally the following ingredients and amounts : ______________________________________ range example______________________________________bioactive compound 0 . 2 - 1 . 1 % 1 . 0 % epoxy - polyoxyalkylene 0 . 5 - 1 . 5 % 1 . 0 % hydrophilic couplingagentalcohol ( solvent ) 1 - 3 % 1 . 0 % water balance balance______________________________________ as shown in the above table , the amount of the bioactive compound is prferably within the range of about 0 . 2 to about 1 . 1 % calculated on the weight of the solids present in the pad bath . an amount substantially greater than 1 . 1 % is difficult to retain on the medical substrate without leachability difficulties . the alcohol is used to solubilize the hydrophilic coupling agent which is then added to the bioactive compound to formulate the pad bath . the pad bath must be applied to the substrate within reasonable temperature limits , for instance room temperature up to about 35 ° f . otherwise the bath may become unstable and the pad bath itself will react with the sides of its container . accordingly it is appropriate to prepare the pad bath using cold water and to protect the bath from extreme temperature conditions during storage and operations . the medical substrate so produced must exhibit an absorptive capacity generally in accordance with astm d1117 and demonstrate a suitable ability to absorb and retain water . applications for the materials produced by the herein described process include various medical - type substrates such as non - woven bed covers , liners and sheets , bandages , dressings , instrument wraps , instrument tray liners , hospital gowns , caps and garments , surgical drapes as well as many other applications .
an absorbent , highly wettable , bioactive fabric useful as a surgical drape , dressing or the like comprised of a non - cellulosic substrate having a non - leachable silicone quaternary bioactive compound together with a hydrophilic organosilicone terpolymer incorporated thereon is described . the fabric is used to isolate a surgical incision site and provides an absorbent antimicrobial field to destroy migrating and cross - contaminating bacteria , fungi and algae . procedures for producing the fabric are also disclosed .