fig1 is a graph illustrating the infrared spectra of ha / cmc films . fig2 is a graph illustrating the infrared spectra of ha / cmc reacted with edc in the presence of 1 - hydroxybenzotriazole sodium salt ( naobt ). the gels , foams , and films of the invention are made generally as follows . ha is dissolved in water and the ph of the resulting aqueous mixture is adjusted with acid ; then the dissolved ha is activated by admixing a suitable carbodiimide , and a suitable amino acid ester is admixed with the ha and allowed to stand until the desired gel has formed . the carbodiimide and the ester can be admixed in any sequence . the preferred method of making the lysine - modified gels and films of the invention will now be described in more detail . as one skilled in the art will appreciate , gels and films of the invention can be made using protocols that are within the method of the invention yet are different in particulars from those described here . a sample of hyaluronic acid or a salt of hyaluronic acid , such as sodium hyaluronate , is dissolved in water to make an aqueous mixture . ha from any of a variety of sources can be used . as is well - known , ha can be extracted from animal tissues or harvested as a product of bacterial fermentation . hyaluronic acid can be produced in commercial quantities by bioprocess technology , as described for example in pct publication no . wo 86 / 04355 . preferably the concentration of ha in this first aqueous mixture is in the range between 0 . 4 % and 2 . 5 % weight / weight (&# 34 ; w / w &# 34 ;). subsequent reactions are slower and less effective at significantly lower concentrations , while significantly higher concentrations are difficult to handle owing to their high viscosity . the aqueous ha mixture should be acidic , preferably having a ph between ph 3 . 5 and ph 5 . 0 , more preferably between ph 4 . 3 and ph 4 . 75 . at lower ph values the preferred activating agent , edc , is unstable , and at higher values the reaction rate is diminished . preferably hydrochloric acid is added to adjust the ph , although other known acids can be used . once the ph of the aqueous ha mixture has been adjusted , a carbodiimide is admixed with the ha . preferred . carbodiimides include edc ( in some references this substance is termed 1 -( 3 - dimethylaminopropyl )- 3 - ethyl - carbodiimide or &# 34 ; dec &# 34 ;) or etc ( 1 - ethyl - 3 -( 3 - dimethylaminopropyl ) carbodiimide methiodide ). in the next step , a nucleophilic amino acid ester is admixed with the aqueous ha carbodiimide mixture . preferred esters include methyl , ethyl , or t - butyl esters . the amino acid can be in the form of di - amino acid , tri - amino acid or polyamino acid , or their hydrochloride salts . preferred amino acids include lysine , leucine , isoleucine , valine , arginine , proline and histidine . the amino acid ester and the carbodiimide may be admixed with the ph adjusted ha mixture in any sequence , either all at once or gradually . if a colored product is desired , a solution of a dye or stain such as the blue dye &# 34 ; brilliant blue r &# 34 ; also known as &# 34 ; coomassie ™ brilliant blue r - 250 &# 34 ; distributed as &# 34 ; serva blue &# 34 ; by serva , can be admixed to the reaction mixture at this point . the resulting product has a blue color that can provide a good contrast to the color of body tissues , making the film or gel easy to see while it is handled during surgery and once it is in place . once the reagents ( and the stain or dye , if any ) have been admixed , the reaction mixture can be simply allowed to stand for a time , or it can be continually or occasionally stirred or agitated . upon admixing of the reagents the ph rises , and can be maintained at the desired ph by addition of acid as the reaction proceeds . we have found , however , that films and gels with various desired physical properties can be obtained by simply allowing the ph to rise as the reaction proceeds . the mode of addition of the reagents , particularly the edc and the amino acid ester , is not critical , but the ratios of these reagents to the ha is important . we have found that the best results are obtained when the ratio of ha : edc : amino acid ester ranges from 1 : 2 : 1 . to 1 : 4 : 10 . lower values typically result in weaker , less insoluble products , while higher values typically result in stronger , more insoluble products . the following examples of this aspect of the invention are given by way of illustration and are not intended to limit the invention except as set forth in the claims . in this example hydrogels were prepared using edc as an activating agent and leucine methyl ester hydrochloride as a nucleophile . sodium hyaluronate ( 400 mg ; 1 . 0 mmol of carboxyl groups ) having a molecular weight between 1 × 10 6 and 2 × 10 6 was dissolved in 10 ml of distilled water . the ph of the aqueous solution was adjusted to ph 4 . 75 by addition of 0 . 1n hcl . then 314 mg of edc ( 1 . 64 mmol ) was added all at once followed by 190 mg ( 1 . 05 mmol ) of l - leucine methyl ester hydrochloride . the ph of the reaction mixture then rose to 6 . 2 over two hours . the reaction mixture was kept at room temperature for five hours , after which time it had formed a thick insoluble hydrogel . this hydrogel could be washed with a 1m nacl solution to remove residual reagents without loss of its physical properties . in this example various edc / leucine : ha ratios were used for comparison of gel formation and properties . the procedure was as in example 1 , using sodium hyaluronate ( 400 mg ; 1 . 0 mmol of carboxyl groups ) in 15 ml of water . in separate experiments the following quantities of edc and leucine methyl ester hydrochloride were then added : 153 mg edc ( 0 . 8 mmol )/ 182 mg leucine methyl ester hydrochloride ( 1 . 0 mmol ); 76 mg edc ( 0 . 4 mmol )/ 90 mg leucine methyl ester hydrochloride ( 0 . 5 mmol ); and 38 mg edc ( 0 . 2 mmol )/ 45 mg leucine methyl ester hydrochloride ( 0 . 25 mmol ). strong hydrogels were obtained as in example 1 for the highest ratio of edc and leucine methyl ester hydrochloride . at the lowest ratio of reactants ( 0 . 2 mmol / 0 . 25 mmol to 1 . 0 mmol ha carboxyl groups ) a weak gel was obtained , which collapsed to a fluid after two weeks . in this example the ha concentration was reduced by one - half for comparison of resulting gel properties . the procedure was as in example 1 except the ha ( 400 mg ; 1 . 0 mmol of carboxyl groups ) was dissolved in 30 ml of water rather than 15 ml ( 11 / 3 % w / w ha ). a hydrogel was formed , although it was weaker than that obtained in example 1 . in this example films were prepared using edc as an activating agent and leucine methyl ester hydrochloride as a nucleophile . sodium hyaluronate ( 400 mg ; 1 . 0 mmol of carboxyl groups ) was dissolved in 40 ml of distilled water . the ph of the solution was adjusted to ph 4 . 75 by addition of 0 . 1n hcl . then edc ( 314 mg ; 1 . 64 mmol ) was added in a single portion , followed by 190 mg ( 1 . 05 mmol ) of l - leucine methyl ester hydrochloride . the ph of the reaction mixture rose to 6 . 2 during two hours , after which time the solution was poured into a petri dish of area 6360 mm 2 and allowed to dry to a film over a two day period . films produced in this manner were strong and insoluble in water and 1m aqueous nacl . the films could be washed with water or aqueous nacl as in example 1 to remove residual reagents without loss of their physical properties . infrared spectroscopic analysis of such films showed no carbodiimide absorption at about 2130 cm - 1 and displayed absorptions at about 1740 cm - 1 , 1700 cm - 1 1650 cm - 1 and 1550 cm - 1 . in this example various ha concentrations were used in making films for comparison of resulting film properties . the procedure described in example 4 was repeated , using three different initial ha concentrations made by dissolving the ha ( 400 mg ; 1 . 0 mmol of carboxyl groups ) in 30 ml , 40 ml , or 100 ml of distilled water . films produced using each of these initial concentrations of ha were strong and insoluble in water and 1 m aqueous nacl , showing that a range of concentrations of ha can be used . each of these films could be washed with water or aqueous nacl without loss of its physical properties . this example illustrates the effect of dialyzing the reaction mixture prior to casting to form a film , as compared with washing the film after forming it . sodium hyaluronate ( 400 mg in 40 ml of water ), edc ( 314 mg ; 1 . 64 mmol ) and l - leucine methyl ester hydrochloride ( 190 mg ; 1 . 05 mmol ) were allowed to react as in example 4 . upon completion of reaction ( 2 hours ) the reaction mixture was dialyzed against water , through 12 , 000 nmw cutoff dialysis tubing in order to remove residual reagents . the dialyzed mixture was then cast as a film as in example 4 . the film so obtained was strong and insoluble in water or 1m aqueous nacl . in this example films were formed by drying more thickly poured reaction mixtures , to compare the properties of films produced from drying mixtures at differing surface area / volume . a reaction mixture obtained as in example 4 ( 40 ml reaction volume ) was cast into a small petri dish ( area 3330 mm 2 ). the film so obtained was insoluble in 1m aqueous nacl and in water ( 100 ° c . ; 1 hour ). in this example films were prepared using other amino acid esters and ha activated with edc . a solution of ha ( 400 mg in 40 ml of h 2 o ) was brought to ph 4 . 7 using 0 . 1n hcl . then edc ( 314 mg ; 1 . 6 mmol ) was added all at once followed by 1 mmol of the amino acid derivative . the reaction mixture was poured into a petri dish and allowed to dry . insoluble films were obtained from l - valine methyl ester hydrochloride , l - isoleucine methyl ester hydrochloride , l - proline methyl ester hydrochloride , and l - phenylalanine methyl ester hydrochloride . in this example films were prepared using a simple primary amine ( aniline ) as a nucleophile . a solution of ha ( 400 mg in 40 ml of h 2 o ) was brought to ph 4 . 7 using 0 . 1 n hcl . then edc ( 314 mg ; 1 . 6 mmol ) was added all at once followed by 1 mmol of aniline . the reaction mixture was poured into a petri dish and allowed to dry , and insoluble films were obtained . in this example films were prepared using other esters of leucine . a solution of ha ( 400 mg in 40 ml of h 2 o ) was brought to ph 4 . 7 using 0 . 1n hcl . then edc ( 314 mg ; 1 . 6 mmol ) was added all at once followed by 1 mmol of the leucine ester . the reaction mixture was poured into a petri dish and allowed to dry . insoluble films were obtained from both l - leucine ethyl ester hydrochloride and l - leucine t - butyl ester hydrochloride . in this example gels were prepared using other amino acid methyl esters . a solution of ha ( 400 mg in 15 ml of h 2 o ) was brought to ph 4 . 7 and edc ( 314 mg ; 1 . 6 mmol ) was added , followed by the amino acid derivative ( 1 mmol ). the reaction mixture formed a thick gel within from 5 to 24 hours . water insoluble gels were obtained using l - valine methyl ester hydrochloride , l - isoleucine methyl ester hydrochloride , l - arginine methyl ester hydrochloride , l - proline methyl ester hydrochloride , and l - histidine methyl ester hydrochloride . in this example films were prepared using an amino acid amide ( leucinamide ) as a nucleophile . a solution of ha ( 400 mg in 40 ml of h 2 o ) was brought to ph 4 . 7 using 0 . 1n hcl . then edc ( 314 mg ; 1 . 6 mmol ) was added all at once followed by 1 mmol of l - leucinamide hydrochloride . the reaction mixture was poured into a petri dish and allowed to dry and insoluble films were obtained . in this example gels were prepared using leucine ethyl ester hydrochloride . a solution of ha ( 400 mg in 15 ml of h 2 o ) was brought to ph 4 . 7 and edc ( 314 mg ; 1 . 6 mmol ) was added , followed by leucine ethyl ester hydrochloride ( 1 . 0 mmol ). the mixture formed a thick , water insoluble gel within from 5 to 24 hours . in this example films and gels were prepared using etc as the ha activating agent . sodium hyaluronate ( 400 mg , 1 . 0 mmol of carboxyl groups ) having a molecular weight in the range between 1 × 10 6 and 2 × 10 6 daltons was dissolved in water ( 10 ml and 30 ml ). the ph of each aqueous solution was adjusted to ph 4 . 75 by addition of 0 . 1n hcl . then 475 mg of etc ( 1 . 6 mmol ) was added all at once , followed by 190 mg ( 1 . 05 mmol ) of l - leucine methyl ester hydrochloride . the ph of this reaction mixture rose to ph 6 . 2 over the next 2 hours . the reaction mixture containing 10 ml of water formed an insoluble gel . the reaction mixture containing 30 ml of water gave an insoluble film after drying . a solution of ha ( 400 mg in 30 ml of h 2 o ) was brought to ph 4 . 75 as in example 13 and then etc ( 475 mg ; 1 . 6 mmol ) and leucine methyl ester hydrochloride ( 190 mg ; 1 . 05 mmol ) were added . a dilute solution of &# 34 ; serva blue &# 34 ; ( 5 mg / ml ) dye in h 2 o ( 0 . 5 ml ) was then added to the reaction mixture . the resulting mixture was poured into a petri dish and a water insoluble blue film was obtained after 16 hours . the blue color was retained by the film when the film was washed with 1m nacl and then with h 2 o . this example illustrates the tissue biocompatibility of a film of chemically modified ha . four strips of films prepared according to the procedure described in example 4 , and two usp negative control strips were surgically implanted into the paravertebral muscle of white new zealand rabbits ( two per test ). the test sites were evaluated either macroscopically after 72 hours or with complete histopathology after 7 days . in accordance with the usp xxi , p . 1237 , the test material met the requirements of the usp implantation test for the evaluation of plastic materials . a 0 . 4 %( w / w ) solution of ha in water was prepared . the ph of this solution was adjusted to between 4 . 3 and 4 . 75 by addition of acid . to each 100 ml of this solution was added 0 . 76 g of edc with stirring until the edc had completely dissolved . to each 100 ml of the ha / edc solution was added 0 . 20 g of lysine methyl ester ( lme ) with stirring until the lme had completely dissolved . the addition of ha , edc , and lme was conducted at room temperature ; once the final ha / edc / lme solution had been formed , it was stored at 4 ° c . until needed . the lme - modified ha material can be processed into various shapes , sizes , and consistencies depending on the end application . if a thin sheet of the material is desired , the mixture can be poured onto a flat surface . this material can then be turned into a solid by allowing the water to evaporate under ambient or elevated temperatures . an alternative method of producing sheets of the material is to subject it to freeze drying . the pore size of the final product can be controlled by adjusting the initial freezing temperature . curved surfaces and other shapes can be produced in a similar manner by initially casting the gel onto a negative image surface and then processing as described . the dried sheet can be processed further , if desired , by pressing to a defined thickness in a carver laboratory press . this is particularly useful for applications requiring placing a thin film between anatomical structures where space is limited . mechanical testing of the freeze - dried material , rehydrated in normal saline , resulted in force to break values of 170 - 900 g / cm 2 . the elongation to break values for this material were between 33 and 62 %. the films can be conveniently examined by infrared multiple internal reflectance spectroscopy , an absorption at 1700 cm - 1 is found in all the films produced when no amine component has been added , and thus the absorption peak at 1700 cm - 1 cannot be due to an amide bond . the mechanism suggested for the reaction involves o - acylisoureas 3 ( a and b ), and is as follows . ## str1 ## in this reaction , the carboxyl group polyanionic polysaccharide 1 reacts with one of the double bonds of the carbodiimide to give both o - acylisourea derivatives 3 ( a and b ). the failure to detect or isolate 3 ( a and b ) was attributed to the occurrence of a rapid o → n acyl transfer to give the n - acylurea 4 ( a and b ). in the presence of a nucleophile , the reaction between the nucleophile ( e . g . an amine ) and 3a and 3b to give the corresponding amide also occurrs . certain properties of the films depend to some extent on the amines and amino acids added . for example , the films prepared with histidine methyl ester swelled a little in h 2 o and were elastic while those prepared from leucine methyl ester were strong and inelastic and did not swell . however , in the absence of a nucleophile , the rearrangement of 3 ( a and b ) to 4 ( a and b ) appears also to compete . evidence for this reaction is : a ) films produced with edc and without any added amine or amino acid are strong and water insoluble . b ) the peak at 1700 cm - 1 in the infra red spectrum can be assigned to n - acylurea 4 c ) in the absence of added nucleophiles the intramolecular rearrangement from o - acylisourea to n - acylurea 4 occurs preferentially ( 67 %) to intermolecular reaction with h 2 o at ph & gt ; 3 . n - acylurea modified polyanionic polysaccharide ha gels and films are prepared generally by mixing ha ( as described above ) with a polyanionic polysaccharide and a carbodiimide to form a water - insoluble precipitate . the precipitate can be cast into thin membranes useful for postoperative adhesion prevention . it can also be colored as described above . to increase the strength of films cast from the precipitate , the films may be subjected to dehydrothermal treatment in which they are heated under vacuum at approximately 105 ° c . for 24 hours or at 105 ° c . with no vacuum for 6 - 24 hours . the polysaccharide and ha can be mixed together , after which the carbodiimide is added . alternatively , the polysaccharide may be reacted with the carbodiimide , followed by addition of ha . a third option is to combine the ha with the carbodiimide , followed by addition of the polysaccharide . preferred embodiments include edc and etc . the reaction is preferably carried out at a ph between 3 . 5 and 5 . the preferred polysaccharide concentration ranges from 0 . 005 to 0 . 1m , and is more preferably in the range 0 . 01 to 0 . 02m . the preferred molar ratio of polysaccharide to carbodiimide is at least 1 : 1 , more preferably about 1 : 4 . ha ( 0 . 4 % w / w , 0 . 01m ) and aqualon - type cmc having a molecular weight of 250 , 000 and a degree of substitution in the range 0 . 65 to 0 . 90 ( 0 . 19 % w / w , 0 . 01m ) were mixed together in aqueous solution at room temperature . the ph of the mixture was adjusted to and maintained at ph 4 . 5 - 5 . 3 by addition of 1m hcl . to each 100 ml of this solution was added 0 . 67 g ( 0 . 04m ) edc . during reaction with edc , the ph of the solution was maintained at ph 4 . 7 - 4 . 8 by addition of 0 . 1m hcl and the reaction allowed to proceed for 1 hour , during which time a precipitate formed . the unreacted edc was removed from the precipitate by dialysis against acidified water ( ph 4 . 0 ) for 24 hours with 2 dialysate changes at 3 and 19 hours . the ha / cmc slurry was then cast into flat molds and air dried for 24 hours at room temperature . ha / cmc membranes were shown to reduce the incidence of postoperative adhesion formation in experimental animal models . in experiments using the rat cecal abrasion model , ha / cmc membranes were placed around surgically abraded rat ceca ; previous studies had demonstrated that adhesions readily formed to the ceca of rats which had been abraded in controlled fashion . cecal adhesions in animal groups that received either ha / cmc membranes or orc membranes ( interceed tc7 membranes marketed by johnson & amp ; johnson for adhesion prevention ) were compared to adhesion controls in animals whose ceca were abraded but did not receive any membrane . the results of these experiments showed that the ha / cmc membranes consistently reduced adhesion formation compared to control animals and to animals that received the interceed tc7 film . in addition , ha / cmc films at various ph &# 39 ; s were tested for the presence of ph - insensitive ir absorbing functional groups . the presence of such groups would indicate that ester and / or anhydride functionality was forming in the treatment of ha / cmc with edc . the result of this assay is shown in fig1 where the spectra show a new absorbance at 1700 cm - 1 . this peak is consistent with the n - acylurea rearranged product from the edc reaction ( de los , f ., et al ., j . am . chem . soc . 88 : 1013 - 1020 , 1967 ). there are no strong absorbencies at 1745 - 1760 cm - 1 ( esters ) and / or at 1800 cm - 1 ( anhydrides ) ( silverstein et al ., eds . spectrometric identification of organic compounds , pp . 122 - 124 , j . wiley & amp ; sons , new york ( 1981 )) in any of these spectra . based on these results , there is no evidence for the formation of any inter - polymer covalent bonds . when n - hydroxysulfosuccinimide ( hososu ) or hydroxybenzotriazole sodium salt ( naobt ) are added to the edc reaction an entirely different spectrum is formed ( fig2 ). from this spectrum one can see that the peak at 1700 cm - 1 is greatly diminished relative to the carbonyl absorbance at ≈ 1600 cm - 1 . the disappearance of this peak at 1700 cm - 1 with the addition of hososu or naobt is consistent with this absorbance being due to the n - acylurea since both hososu and naobt are known to lower the amount of o → n rearranged material ( j . v . staros , accts . chem . res . 21 ( 12 ): 435 - 441 , 1988 ). polyanionic polysaccharide gels , films , and foams are prepared generally by mixing at least one polyanionic polysaccharide ( e . g ., ha , cmc , cma ) with a carbodiimide , such as edc or etc , to form a water - insoluble material . the reaction may be carried out at a ph between 3 . 5 and 8 , with optimal reaction conditions occurring between ph 4 . 6 and 5 . 3 . the preferred polysaccharide molecular weight used in the reaction may range from 9 . 0 × 10 4 to 3 . 0 × 10 6 daltons , but preferably is between 2 . 5 × 10 5 to 1 . 0 × 10 6 daltons . the preferred molar ratio of polysaccharide to carbodiimide is at least 1 : 1 , more preferably about 1 : 4 . the insoluble material formed by this method may be in the form of a gel or in the form of fibers and can be used directly for adhesion prevention or drug delivery , or can be cast onto flat molds and either air dried or lyophilized to yield thin films or foams . in addition , blends can be prepared by mixing various amounts of different unpurified or purified activated - polyanionic polysaccharides . these blends are made homogeneous by mixing with overhead stirrers and / or high shear mixers . unreacted carbodiimide may be removed from the unpurified mixture by molecular weight sizing , dialysis , diafiltration or fractional precipitation with a water - soluble solvent , according to standard methods , prior to use . the purified mixture can be used directly for adhesion prevention and / or drug delivery , or may be cast onto flat molds and either air dried or lyophilized to form films or foams . ha ( 1 . 0 × 106 daltons ) was dissolved in water to make a 0 . 8 % w / v solution by stirring overnight at 25 ° c . the ph of the reaction mixture was adjusted to ph 4 . 75 with 0 . 1n hcl . edc ( 4 : 1 molar ratio of edc to ha , 1 . 53 % w / v final concentration ) was added to this solution with continuous stirring and was maintained at a constant ph ( 4 . 7 - 5 . 1 ) for one hour by adding additional 0 . 1n hcl . removal of the unreacted edc and other low molecular weight impurities was performed by either molecular weight sizing , dialysis , or diafiltration using standard methods . a water - insoluble , clear gel was obtained after this process . this example illustrates the effect of fractional precipitation of n - acylurea modified ha with a water soluble solvent . the procedure described in example 19 was repeated with the exception that unreacted edc and other low molecular weight impurities were removed by fractional precipitation using a suitable water - soluble solvent ( e . g ., c 1 - c 3 alcohols , acetone ). under these conditions , water insoluble fibers were produced . cmc ( 250 × 10 3 daltons ) was dissolved in water to make a 0 . 8 % w / v solution by stirring at room ambient temperature ( 22 °- 25 ° c .) overnight . the ph of the reaction mixture was adjusted to ph 4 . 75 with 0 . 1n hcl . edc ( 4 : 1 molar ratio of edc to cmc , 1 . 53 % w / v final concentration ) was added to this solution with constant stirring and the ph was maintained between 4 . 70 and 5 . 10 for one hour by adding additional 0 . 1n hcl . removal of the unreacted edc and other low molecular weight impurities was performed by either molecular weight sezing chromatography , dialysis , diafiltration , or fractional precipitation of the cmc with a suitable water - soluble solvent ( e . g ., c 1 - c 3 alcohols , acetone ). water insoluble fibers , approximately 300 - 800 μm long and 10 - 20 μm wide , are produced from these reaction conditions . this example illustrates the preparation of a blend of edc - activated n - acylurea modified ha with edc - activated cmc . edc - activated ha and cmc were prepared separately as described in examples 19 and 21 but each reaction product was not purified prior to blending . three hundred ml of the activated ha and 300 ml of the activated cmc were placed in a 1000 ml beaker and blended with a turrax brand blender at 6000 rpm for 10 minutes at 25 ° c . this resulted mixture was purified by dialysis against ph 4 . 0 water for 24 hours at a 20 : 1 ratio with 3 dialysate exchanges . after dialysis the mixture was poured into a flat mold and air dried to a thin water insoluble film . the quantity of fibers in the mixture can be controlled by varying the relative amount of activated cmc and activated ha that are blended together . polyanionic polysaccharides modified according to the above descriptions can be cast as films in a straightforward manner . typically the reaction mixture is poured into a vessel having the desired size and shape and allowed to air dry . in general films formed by drying mixtures poured thickly , so that they have a lower surface area / volume , possess greater strength than films formed by drying thinner , higher surface area / volume mixtures . alternatively a film can be formed by compressing a gel under conditions that permit escape of water , as , for example , by compressing the gel between two surfaces , at least one of which is porous , as described , for example , in epo 0 193 510 . if desired , a gel or film can be washed prior to use by , for example , perfusion with water or 1m aqueous sodium chloride . alternatively the reaction mixture can be dialyzed to remove residual reagents prior to casting as a film . washing to remove residual reagents or reagent - derived material such as substituted ureas is desirable if the film or gel is to be used for therapeutic applications . gels or films colored blue with brilliant blue r as described above do not lose their coloration during such washing . the removal of reagents or reaction products can be monitored by high pressure liquid chromatography . films , foams , or gels of the invention can be used as a surgical aid , to prevent adhesions or accretions of body tissues during a post - operation or healing period , following procedures known in the surgical arts , as described , for example , in debelder et al ., pct publication no . wo 86 / 00912 . during surgery one or more pieces of the gel or film , as appropriate , are inserted or injected between or among the tissues that are to be kept separate . films , fibers , or gels of the invention can also be used for sustained release drug delivery . the drug to be delivered can be covalently bonded to the gel , fibers , or film , as described , for example , in r . v . sparer et al ., 1983 , chapter 6 , pages 107 - 119 , in t . j . roseman et al ., controlled release delivery systems , marcel dekker , inc ., new york ; and the gel , fibers , or film can then be implanted or injected at the locus where delivery is desired . products of the invention can also be used as wound healing agents by providing a framework for the infiltration and attachment of undifferentiated cells and thus allowing cell proliferation and augmented wound healing to occur .
a water insoluble , biocompatible composition composed of an acyl derivative of a polyanionic polysaccharide , a carbodiimide , and optionally , a nucleophile .