in order to make the main technical features and functions of the present invention more comprehensible , the present invention is further described below in detail with reference to the accompanying drawings . 1 . a bovine skin and tendon enriched with collagens were cut into cubes with a size of about 0 . 5 cm 3 , placed into 10 l 95 % alcohol , and stirred at 4 ° c . for 24 h . the bovine tendon was taken out of the 95 % alcohol , placed into 10 l 0 . 5 m acetic acid solution , and then stirred at 4 ° c . for 72 h . then , pepsin ( sigma p7000 , 4000 unit / ml ) was added , and the solution was continuously stirred at 4 ° c . for 24 h . 2 . the mixture of step 1 was filtered with a stainless steel mesh to remove the undecomposed residues . sodium chloride was added continuously till the concentration thereof reached 1 . 0 m , and then the solution was stirred at 4 ° c . for 30 min and centrifuged at a rotation speed of 10 , 000 g ( beckman avanti j - 20 ) for 30 min . 3 . after removing the supernatant , 10 l 50 mm tris - hcl buffer ( ph 7 . 4 ) was added , and stirred at 4 ° c . for 30 min . then , sodium chloride was added again till the concentration thereof reached 4 . 0 m . the solution was stirred at 4 ° c . for 30 min , and then centrifuged at a rotation speed of 10 , 000 g for 30 min . 4 . after removing the supernatant , 10 l 50 mm tris - hcl buffer ( ph 7 . 4 ) was added , and stirred at 4 ° c . for 30 min . then , sodium chloride was added again till the concentration thereof reached 2 . 5m . the solution was stirred at 4 ° c . for 30 min , and then centrifuged at a rotation speed of 10 , 000 g for 30 min . 5 . after removing the supernatant , 5 l of a mixed solution of isopropanol and pure water ( isopropanol : h 2 o = 1 : 4 ) was added , stirred at 4 ° c . for 30 min , and then centrifuged at a rotation speed of 10 , 000 g for 30 min . this step was repeated twice . 6 . after removing the supernatant , 5 l 0 . 05m acetic acid solution was added , and stirred thoroughly and uniformly and then placed at a temperature of − 90 ° c . for being frozen . then , the congelation was dried with a freeze dryer to a constant weight . the resulted dry product is type i collagen . 1 . the type i collagen was added into a weak acidic aqueous solution ( for example , 0 . 05 m aqueous acetic acid solution ), and stirred at a high speed into a homogenous slurry , in which the slurry contains the type i collagen at a concentration of about 2 wt %. then , glycosaminoglycans ( gags ) were dissolved into the weak acidic aqueous solution ( for example , 0 . 05 m aqueous acetic acid solution ) to get an aqueous solution at a weight concentration of about 0 . 4 wt %- 1 . 0 wt %. 2 . the aqueous gags solution was mixed with the type i collagen slurry , in which the ratio of the gags was about 2 . 0 wt %- 5 . 0 wt % based on the weight of the type i collagen , and then placed at room temperature for 48 h to remove a part of the moisture , so as to get a thicker slurry mixture . then , the resulted slurry mixture was made to pass through needle heads with a diameter of 0 . 9 mm and 0 . 5 mm to become homogenous . then , the mixture was filled into a mold for making the scleral buckling band . sequentially , a vacuum freeze - drying treatment was performed for about 36 h to remove the moisture in the solution . then , the mixture was heated at 105 ° c . in vacuum for 24 h , so as to be thermal dehydrated and cross - linked , and then , the 260 nm uv cross - link treatment was performed to get a predetermined scleral buckling band . thereafter , a cross - link treatment was performed with a natural cross - linker ( genipin ) or glutaraldehyde , such that the collagen and the gags were cross - linked , so as to enhance the mechanical strength of the scleral buckling band , thereby the decomposition rate thereof was controlled . finally , the scleral buckling band was washed with pure water and freeze dried to get a scleral buckling band with a slender cylindrical structure , as shown in fig1 . the resulted scleral buckling band ( with a length of 5 . 0 cm , a diameter of 0 . 2 cm ) is fixed on clamps of a material testing machine . the test length of the scleral buckling band confined between two clamps is 3 . 0 cm , and then a force is applied to stretch the scleral buckling band , till the scleral buckling band is broken . the force applied at the instance when the scleral buckling band is broken is recorded , and the tensile strength of the scleral buckling band is calculated as 2 . 37 mpa , as shown in fig2 . the resulted scleral buckling band is observed with a scanning electronic microscope ( sem ), and the average porosity of the scleral buckling band is calculated to be about 120 ± 40 μm , as shown in fig3 . as polymer materials are easily processed and have high mechanical strength and desirable biocompatibility , they have been widely used to develop thousands of medical products , such as disposable medical equipments and implantable biomedical materials in the past decade . natural polymers include collagen and polysaccharide biopolymer , for example , hyaluronic acid ( ha ) and chitosan , and chemical synthetic polymers include polylactic acid ( pla ), polyglycolic acid ( pga ), and polylactic acid - glycolic acid ( plga ). the pla , pga , and plga are all bio - absorbable polymer materials with desirable biocompatibility , and their co - polymers are decomposed into small molecular chain segments in a living body , and then discharged out of the living body as the metabolism process continues . therefore , the pla , pga , and plga have desirable biocompatibility , bio - absorbability , and capable of being discharged out of the body as the metabolism process continues , which thus can be processed into different types of implantable biomedical materials with slow degradability and capable of releasing different coated medicaments . ha is a polysaccharide biopolymer and widely exists in connective tissues , mucous tissues of vertebrates , crystalline lens of eyeballs , and capsules of some bacteria in the nature . regardless of the source , the chemical composition and structure of ha are the same . therefore , if ha is used as a medical polymer material , it can be decomposed and absorbed by the living body , without causing any immune response . recently , ha has been gradually developed for the applications of post - operation tissue anti - adhesion and medicament release . chitosan is a biopolymer prepared by extracting from natural biological organism , and mostly exists in crustacean , which has desirable biocompatibility with cells of biological organisms , has no toxicity , and can be decomposed by biological organisms , and thus it can be developed as a carrier for drug release . collagen is a polymer for forming various extra - cellular matrixes and serves as combination tissues in animal cells . collagen mainly exists in the form of an insoluble fibrin , and takes about 25 %- 30 % of the proteins in human body . therefore , the collagen has desirable biocompatibility , and can prevent human body from generating rejection response and can be absorbed by the tissues after being decomposed . the collagen can be extracted and purified from biological tissues . then , the mechanical strength of the material can be enhanced by physical or chemical cross - linking treatment , and can also be made into a porous structure , which is suitable for being used as a temporary tissue filling material and can also be made into a base material for various artificial tissues . according to the present invention , the material for making the scleral buckling band includes , but not limited to , collagen , pla , pga , plga , pcl , ha , and chitosan , and another polymer material . preferably , the material is collagen . according to the present invention , the scleral buckling band may have different strengths , and when an oculist performs an operation , the scleral buckling bands with different strengths may be selected to control the residence time of the scleral buckling band within the human body , so as to cater to different recovery speeds of different patients . it is known to those of ordinary skill in the art that , collagens with different strengths can be made according to the content of collagens , type and cross - linking manner of the cross - linker . however , the present invention is not intended to limit the content of collagens , type , and cross - lining manner of the cross - linker . the conventional methods for making collagens with different strengths all can be used in the present invention for making the scleral buckling band . referring to fig4 and 5 , the distortion of eyeballs is measured by sonography as time elapsed . as the conventional scleral buckling band used in the operation is made of silicon , it cannot be metabolized and decomposed by enzymes and other substances within the human body , so that the buckling effect generated on the sclera after the scleral buckling band is implanted lasts for a long time , and the eyeball maintains a certain distortion , as a result , the vision is affected . the scleral buckling band of the present invention is mainly made of collagens and is metabolized and decomposed by the enzymes within the body , and accordingly , after the scleral buckling band is implanted , the buckling effect on the sclera is decreased as time elapsed . besides achieving the functions of the conventional scleral buckling band , the scleral buckling band further makes the distortion of the eyeball be decreased as time elapsed , which means that the eyeballs return to the original shape , as shown in fig6 , so that the scleral buckling band of the present invention does not bring any influences on vision . according to the present invention , the scleral buckling band optionally contains medicaments , such as an anti - microbial agent , an anti - inflammatory agent , a growth factor , or another suitable medicine . it is well known to those skilled in the art that , the polymer biomedical material is characterized in containing therapeutic or preventive medicaments therein when being prepared . the common biomedical materials are generally applied on parts under operation or wounds , and carry specific medicaments according to different requirements of different patients through the function of carrying drugs , so as to enhance the delivery efficiency of the medicaments . according to the present invention , the scleral buckling band is made by combining collagens with different strengths and contains different medicaments , and since the collagens with different strengths have different decomposition rates and different medicaments are contained therein , the scleral buckling band releases specific medicaments required by different periods of treatment as time elapsed , which thus enhances the barrier effect , and improves the effects of wound healing and tissue regeneration . in view of the above , the scleral buckling band of the present invention can be industrialized and has novelty and inventive step , and thus meets the patent requirements . the above description is merely a preferred embodiment of the present invention , but not intended to limit the scope of the present invention .
a scleral buckling band and a method for making the same are described . the scleral buckling band is used for an ophthalmic operation , which is biocompatible and has a slender cylindrical structure formed by a decomposable and absorbable material . when being implanted into human body , the scleral buckling band is degraded and absorbed by the human body , without causing any immune response . after the patient is recovered , the scleral buckling band does not need to be taken out through another operation . meanwhile , the decomposition rate of the scleral buckling band within the human body can be controlled through different preparation manners , so as to cater to different recovery speeds of different patients . furthermore , the scleral buckling band contains different medicine , and after being implanted into human body and being decomposed , the scleral buckling band releases different specific medicine as time elapsed .