in order to provide a clear and consistent understanding of the specification and claims , including the scope to be given such terms , the following definitions are provided . cosmetic composition . by the term “ cosmetic composition ” is intended for the purposes of the present invention any composition or agent for external application to human or animal skin , nails , or hair for the purpose of beautifying , coloring , conditioning , or protecting the body surface containing a cosmetically effective amount of marine invertebrate type v telopeptide containing collagen . a cosmetically effective amount of such collagen is that amount required to bring about the desired cosmetic effect , with from 0 . 001 wt % to 30 . 000 wt % being preferred , 0 . 1 wt % to 10 . 0 wt % more preferred , and 0 . 5 wt % to 5 . 0 wt % being most preferred . one of ordinary skill in the art to which the present invention pertains can readily determine what constitutes a “ cosmetically effective amount ” without undue experimentation . the present cosmetic composition can be in any form including for example : a gel , cream , lotion , makeup , colored cosmetic formulations , shampoo , hair conditioner , cleanser , toner , aftershave , fragrance , nail enamel , and nail treatment product . colored cosmetic formulation . by the term “ colored cosmetic formulation ” is intended for the purposes of the present invention those cosmetics containing pigment including for example eye shadow , lipsticks and glosses , lip and eye pencils , mascara , and blush . conditioning agent . by the term “ conditioning agent ” is intended any agent or composition which exerts a conditioning effect on the body including the skin , hair and / or nails upon external application and includes for example humectants ; emollients ; oils including for example mineral oil ; proteins including the present collagen ; and shine enhancers including for example dimethicone and cyclomethicone . the present conditioning agents may be included in any of the present pharmacological and / or cosmetic compositions . telopeptide containing . by the term “ telopeptide containing ” is intended for the purposes of the present invention a marine invertebrate type v collagen composition where the composition includes collagen molecules where the nonhelical terminal portions of the native collagen molecule , the telopeptides which extend as random coils from the amino and carboxyl ends of the collagen molecule , are retained . atelopeptide containing . by the term “ atelopeptide containing ” is intended for the purposes of the present invention a marine invertebrate type v collagen composition where the composition includes collagen molecules where the nonhelical terminal portions of the native collagen molecule , the telopeptides , have been removed for example by enzymatic cleavage . fibrillar collagen . by the term “ fibrillar collagen ” is intended for the purposes of the present invention , a natural polymeric form of collagen which is essentially insoluble in its aqueous environment yet forms a viscous gel - like matrix . invertebrate marine animal by the term “ invertebrate marine animal ” is intended for the purposes of the present invention , invertebrate animals present in a salt - water or fresh - water marine environment and include for example members of the phylum coelenterata , members of the class scyphozoa and the phylum coelenterata including for example jellyfish . pharmacological compositions . by the term “ pharmacological compositions ” is intended for the purposes of the present invention any composition or agent applied externally to the skin , hair , or nails of the human or a animal body for therapeutic purposes containing a pharmacologically effective amount of the present marring invertebrate type v telopeptide containing collagen . a “ pharmacologically effective amount ” is that amount required to bring about the desired therapeutic effect , with 0 . 001 wt % to 30 . 000 wt % being preferred , 0 . 1 wt % to 10 . 0 wt % more preferred , and 0 . 5 wt % to 5 . 0 wt % being most preferred . one of ordinary skill in the art to which the present invention pertains can readily determine what constitutes a “ pharmacologically effective amount ” without undue experimentation . examples of phannaceutical agents or compositions in accordance with the invention include ointments , creams , lotions , gels , solutions , and shampoos . more specific examples include for example , acne treatment preparations including creams , soaps , cleansers , moisturizers , ointments and lotions ; anti - aging preparations including creams , cleansers , moisturizers and lotions ; anti - dandruff preparations including shampoos and conditioners ; antibiotic preparations ; sunburn preparations ; anti - itch preparations ; and anti - fungal preparations . the present non - cross - linked or cross - linked fibrillar telopeptide containing collagen may be used directly as a gcl . as a gel , the fibrillar collagen can be used as a vitreous body or as dispersions / solutions for the preparation of cosmetic and pharmacological compositions . the fibrillar collagen can be cast into various forms at varying collagen fiber density and cross - linked to form mat or sponge - like structures which may be used in a variety of applications such as delivery of pharmaceutical agents to hair or skin , as artificial nails , as prosthetics , theatrical devices , etc . articles of matter produced using marine invertebrate type v telopeptide containing fibrillar collagen are different from similar articles of matter produced using collagen preparations obtained from vertebrate species . a method is provided for preparation of commercially useful amounts of essentially type v collagen from marine jellyfish which may be formed into a variety of formulations and / or products . the collagen is most conveniently prepared from the whole organism , but the hemispherical bell - shaped transparent umbrella may be separated from the numerous fine marginal tentacles and reproductive and / or digestive structures present in the umbrella may be removed and the partial umbrella used in the production of various collagen preparations . depending on the intended use of the derived fibrous materials , the native collagen may be freed of extraneous matter such as lipids , saccharides , and noncollagenous proteins so as to leave an essentially purified preparation of type v collagen . another approach includes using fibrous materials in the preparation of a “ natural ” cosmetic such as a hair or skin cleaning / conditioning preparation and in this application of the present invention , the native collagen may be less extensively purified such that the natural material components of the jellyfish are retained in the product ( s ). the nonhelical terminal portions of the native collagen molecule , the telopeptides , extend as random coils from the amino and carboxyl ends of the molecules and may be retained or enzymatically removed in preparation of the final product ( s ). the telopeptides serve a number of functions in the formation of the native collagen fiber . the telopeptides serve as the primary sites for cross - linking intramolecularly ( between the three constituent polypeptide chains in the native collagen molecule ) and intermolecularly ( between two or more native collagen molecules ). in a preferred embodiment of the present invention , native essentially type v marine invertebrate telopeptide containing collagen is produced essentially free of noncollagenous proteins and other substances naturally present in marine jellyfish . this collagen is soluble in dilute aqueous acid , e . g . 0 . 01 m acetic acid , and 0 . 001 n hcl , and any insoluble collagen , if present , may be removed by filtration , centrifugation , or other means . in another preferred embodiment of the present invention , native essentially type v marine invertebrate telopeptide containing collagen is produced which retains appropriate noncollagenous proteins and / or polysaccharides naturally present in marine jellyfish . this collagen preparation is soluble in dilute aqueous acids and nonsoluble components and or tissue structures may be removed by filtration , centrifugation , or other means . once the collagen solution is obtained , it may be employed for preparing fibrous aqueous solutions , fibrous aqueous gels , and dispersions / solutions of these products in surfactant solutions containing other ingredients suitable for the preparation of hair and skin treatments , and cosmetic and pharmacological compositions . the procedure for preparing the fibrous preparations involves a slow precipitation of the collagen from solution while subjecting the aqueous medium to mild shear ( stirring ). the conditions under which the precipitation of the collagen is achieved can vary . the temperatures employed are preferably in the range of from 0 ° c . to 42 ° c ., more preferably from 10 ° c . to 30 ° c ., and most preferably from 15 ° c . to 25 ° c . the ph is generally in the range of about 3 to 9 , preferably in the range of 5 to 8 , and more preferably between 6 and 7 . 5 . a wide variety of salts may be used , usually alkali metal salts , both neutral and alkaline , more particularly sodium and potassium , with mono and polyvalent cation salts , particularly halides , e . g . chloride . the concentration of the salt may vary widely with the other conditions employed , e . g . temperature , and protein concentration , as well as the particular salt employed . suitable concentrations are preferably in the range of from about 0 . 05 m to 4 . 0 m , more preferably from 1 . 0 m to 3 . 8 m , and most preferably between 2 . 5 m and 3 . 5 m . suitable concentrations of polyvalent salts are in the range of from about 0 . 5 m to 4 . 0 m , more preferably from 1 . 0 m to 4 . 0 m and most preferred concentrations ranging from 2 . 5 m to 4 . 0 m . the concentration of collagen in the solutions being precipitated may range between 0 . 01 mg / ml and 10 mg / ml , preferably in the range of from 0 . 1 mg / ml to 5 mg / ml , and most preferably from 0 . 5 mg / ml and 4 mg / ml . precipitation time varies from about 10 minutes to 5 hours , usually about 30 minutes to 2 hours , and preferably about 1 hour to 1 . 5 hours . various techniques may be used to obtain the desired rate of precipitation of collagen while applying the mild shearing . one technique is heat gelation , wherein a constant or slowly increasing temperature is employed to bring about precipitation of collagen in the presence of salt . generally , the temperature range is from about 4 ° c . to 45 ° c ., the temperature being slowly raised from about 4 ° c . to 10 ° c . to a temperature of about 20 ° c . to 37 ° c . salt concentrations generally vary from about 1 . 0 m to 4 . 0 m . alkali metal halides , e . g . sodium chloride , are preferably employed . the ph is generally from 4 . 0 to 8 . 0 , preferably 5 . 0 to 6 . 0 . particularly preferred conditions are nonphysiological conditions for the jellyfish , namely 3 . 5 m nacl , ph 5 . 0 , with a final temperature of about 35 ° c . a second technique is to provide a slow increase in ionic strength , ph , and temperature with the collagen in solution . this can be achieved by employing dialysis with a monovalent or polyvalent salt dialysate , thereby slowly raising the salt concentration ( or ionic strength ) while the acid in the collagen solution diffuses from the collagen solution into the dialysate . the change in ph can be either continual or incremental , typically by employing alkali salts in the dialysate . usually the dialysate has a salt concentration of 1 . 0 m to 4 . 0 m , more usually to 2 . 5 m to 3 . 8 m , particularly of disodium phosphate . the final ph of the medium is generally 3 . 0 to 8 . 5 , more usually 4 . 0 to 6 . 5 , and preferably 5 . 0 to 5 . 5 . another procedure is that of continuous dialysis at moderately reduced to low temperatures while changing the dialysate from a dilute mildly acidic solution to ( generally a mild mono or dicarboxylic organic acid or dilute mineral acid such as hcl ) to a mildly basic salt solution , while increasing the ionic strength or salt concentration by using a dialysate of increasing salt concentration . with increasing ionic strength or salt concentration , the temperature of the solution may also be increased , until a fibrous mass of obtained . the fibrous mass is freed of any nonfibrous materials and may be treated in a variety of ways depending on the intended use . another use of the present collagen preparations include the addition of the preparation into solutions of surfactants , detergents , soaps , and similar formulations for use with treatment of hair and skin as a cosmetic , a cosmetic ingredient , and / or pharmacological agent . the term “ cosmetic ingredient ” is the same as “ cosmetic composition ” and means a composition applied externally to skin , nails , or hair of the human or animal body , for purposes of beautifying , coloring , conditioning , cleansing , or protecting the bodily surface . examples of cosmetic ingredients or cosmetic compositions in accordance with the invention include lotions , creams , moisturizers , gels , sun screens , makeup , cleansers , soaps , shampoos , hair conditioners , skin firming compositions , protein concentrates , after shaves , colored cosmetics including for example eye shadows and blushes , nail enamels , and so forth . animal collagen is known to have moisturizing and film forming properties , and is a popular additive to treatment cosmetics . the term “ pharmacological agent ” is the same as “ pharmacological composition ” and means a agent or composition applied externally to the skin , hair , or nails of the human or a animal body for therapeutic purposes . examples of pharmaceutical agents or compositions in accordance with the invention include ointments , creams , lotions , gcels , soaps , solutions , and shampoos . animal collagen protein is the main component of connective tissues and animal keratin is the main component of hair and fingernails . collagen is responsible for most of skin structure . in the course of aging the polypeptide chains of collagen polymerize . the result is “ cross - linking ”, which causes wrinkling of the skin as well as reduction in skin elasticity . keratin is responsible for the most of hair structure . in the course of hair growth , the keratins dry out and exhibit cracks in surface structure of hair . collagens are natural film forming agents and aid in prevention of drying . the present collagen preparation can be added to a typical shampoo composition by weight , an example of which is set forth below : in addition , the present material can be added to various formulations of skin care products generally described as lotions for application to human facial or body skin . these lotions generally contain from about 20 - 80 % oil and 10 - 80 % water in an emulsion form . in addition , the moisturizing lotion may contain humectants , emollients , surfactants , fragrances , preservatives , and so forth . about 5 - 10 % humectant , about 5 - 20 % emollient , and about 0 . 5 - 10 % surfactant are suggested . marine invertebrate type v telopeptide containing collagen ( at about 0 . 01 to 1 . 00 wt %) and hydrolyzed collagen ( at about 0 . 1 to 2 . 0 wt %) products may be incorporated into moisturizing creams . creams generally contain from about 20 - 70 % water and about 30 - 70 % oil . in addition , creams may contain a variety of humectants , emollients , surfactants , preservatives , and fragrances . about 5 - 10 % humectant , about 5 - 20 % emollient , and about 0 . 5 - 10 % surfactant are suggested . marine invertebrate type v telopeptide containing collagens ( incorporated at about 0 . 01 to 5 . 0 wt %) and hydrolyzed collagen ( incorporated at about 0 . 1 to 10 . 0 wt %) products may be incorporated into treatment makeups . generally , makeup formulations comprising 5 - 70 % oil , 10 - 95 % water , and about 5 - 40 % pigment , are suitable . in addition , the makeup as well as any of the present cosmetic or pharmacologic compositions may contain other components known and readily selected by those of ordinary skill in the art to which the present invention pertains . for makeup formulations such components may include for example surfactants , preservatives , silicone , humectants , emollients , and fragrances . generally 0 . 5 - 10 % surfactant , 0 . 1 - 30 % silicone , 5 - 10 % humectant , 0 . 1 - 30 % emollient , and 0 . 1 - 5 % preservative are included . marine invertebrate type v telopeptide containing collagens ( about 0 . 2 to 2 . 0 wt %) and hydrolyzed collagen ( about 0 . 01 to 5 . 00 wt %) products may be incorporated into colored cosmetics such as eye shadow or blush . for example , a suitable eye shadow comprises 5 - 40 % pigment , 1 - 50 % oil , and 1 - 20 % waxes . additionally , the composition may contain one or more of 10 - 60 % water , 0 . 5 - 30 % surfactant , 1 - 10 % humectants , 0 . 1 - 5 % preservative , and 0 . 1 - 20 % silicone . invertebrate type v collagens ( about 0 . 01 to 2 . 00 wt %) and hydrolyzed collagen ( about 0 . 01 to 5 . 00wt %) products may suitable for incorporation into shampoos and hair conditioners . suitable shampoo formulations include 1 - 40 % surfactant and 10 - 90 % water . suitable hair condition formulations include 30 - 95 % water , 0 . 5 - 30 % conditioning ingredients including for example , emollients , proteins , and shine enhancers , and 1 - 40 % surfactant . hair conditioners and shampoos may also contain thickeners and silicone . about 0 . 05 - 5 % silicone is suggested in shampoos and hair conditioners . the invention includes cosmetic and pharmaceutical compositions containing a cosmetically or pharmaceutically effective amount of invertebrate type v telopeptide containing collagen protein . a cosmetically and / or pharmacologically effective amount of collagen protein in accordance with the invention is that amount required to bring about the desired cosmetic and / or therapeutic effect . such amount can readily selected by one of ordinary skill in the art to which the present invention pertains based on the particular formulation and the desired effect , without undue experimentation . preferably , about 0 . 001 - 30 wt %, more preferably 0 . 1 - 10 wt %, and most preferably 0 . 5 - 5 wt % is employed . in describing the present invention , three stages will be considered . the first stage is the purification of native collagen and its transformation into collagen in solution . the second stage is the transformation of the collagen in solution into native fibrous polymers . the third stage is the use of the native collagen , collagen in solution , and fibrous polymers , for the fabrication of various articles or the formation of composites . suitable collagen sources include a wide variety of marine animals such as those of the phylum coelenterata . collagen dispersions or solutions obtained from the mantle , tentacles , and whole organism provide similar collagen dispersions or solutions . first the reproductive and digestive tissue structures and tentacles , are removed from the organism . the mantle portion of the jellyfish provides the most uniform materials for production of collagen dispersions or solutions with the least amount of noncollagenous protein material ( s ). for purposes of this invention , collagen dispersion or solutions are defined as aqueous compositions where the collagen does not settle away from the aqueous composition under normal conditions of preparation and storage . to enhance the ease of purification and facilitate dispersion / solubilization of collagens , the material is subjected to various mechanical treatments such as dissection , grinding , high speed shearing , and the like . depending on the particular treatment , the tissue may be wet or dry , frozen or cooled , high speed shearing is preferably carried out with frozen or cooled wet tissue , and grinding is preferably carried out with dry cooled tissue . coarsely divided tissues are swollen in aqueous acidic solutions under nondenaturing conditions . further dispersion is achieved using high speed shearing in short bursts . preferably dilute acid solutions at low temperatures are employed to minimize denaturation . suitable acids include acetic , citric , malonic , or lactic acids , or other carboxylic acids having pk values from about 2 to 5 at room temperature . dilute mineral acids such as hcl may also be used provided the ph of the dilute acid solution is approximately 2 to 5 . concentrations of the organic acid in the dispersion medium typically range from about 0 . 01 m to 1 . 0 m and the temperature may vary from 4 ° c . to about 25 ° c . preferably , 0 . 5 m acetic or citric acid solubilization for 2 - 3 days yields a collagen dispersion which may be filtered through cheesecloth . the acid soluble extract may be dialyzed against sodium phosphate buffer and the formed precipitate redissolved in 0 . 5 m acetic or citric acid . solid nacl may be slowly added to the acid solubilized preparation to a final concentration of about 3 . 5 m to effect secondary precipitation . precipitated collagen dispersion may be redissolved in dilute acid and freeze - dried . preparation of atelopeptide collagen dispersion may be accomplished by solubilizing collagen or dissolving the freeze - dried collagen preparation in dilute acid and digesting the materials with 4 - 10 %, weight per weight , pepsin , ficin , collagenase , trypsin and pronase at 4 ° c . after 24 hours , the digest may be dialyzed against sodium phosphate and precipitated by addition of solid nacl and / or the dialysate may be concentrated by freeze - drying . the formed precipitate may be redissolved in dilute acid and freeze - dried . in the present invention , mantle from jellyfish is a preferable source of collagen , where the collagen - containing material is separated from adjacent tissues by dissection , soaked in dilute acid at room temperature and ground using short bursts of high speed shear ( for example , using a blender ). this technique provides a homogeneous dispersion of jellyfish which is readily available to subsequent treatment , so as to provide an efficient means for achieving collagen in solution . the dispersion which is obtained by treatment with acid is a viscous dispersion containing native ( telopeptide containing collagen ) fibrillary collagen and a small amount of native collagen in solution . the viscous product , i . e . dispersed swollen collagen , is marine invertebrate type v telopeptide containing collagen of the composition alpha1alpha2alpha3 . enzymatic treatment may be used at this point to remove telopeptides producing atelopeptide fibrillar collagen while leaving the major portion of the molecule intact . illustrative enzymes include for example , pepsin , ficin , collagenase , trypsin , and pronase . depending on the particular enzyme employed , conditions for enzymatic cleavage of the telopeptides vary . with pepsin an acidic solution is employed , generally at a ph of about 2 to 4 . the concentration of the enzyme varies from about 0 . 001 to 10 wt % based on the weight of collagen present . the collagen concentration generally varies from 0 . 5 g / l to 10 g / l , more usually from about 1 g / l to 5 g / l . preferably , the acidity is provided by an organic acid such as a carboxylic acid in a concentration of about 0 . 01 m to 1 . 0 m . if necessary , the ph can be adjusted by the addition of a mineral acid , e . g . hydrochloric . the solution of soluble fibrillar collagen is then treated to separate the soluble fibrillary collagen from soluble noncollagenous materials . primarily , the treatment involves separations , precipitations , and dialysis against various solutions of different ionic strength known to those of ordinary skill in the art , and readily selected and employed by those of ordinary skill in the art to which the present invention pertains without undue experimentation . moderate temperatures are employed , normally between 0 ° c . and 20 ° c ., and salt solutions of varying ionic strength and salt concentration , generally from about 0 . 01 m to 4 . 0 m . depending on the particular salt . neutral salt solutions , e . g . nacl , of about 0 . 5 m to 4 . 0 m may be employed as a dialysate in a free - flow dialysis at a ph of at least 5 and not greater than about 9 . non - soluble contaminants which have been precipitated during preparation of soluble fibrillar collagen are filtered off to yield a filtrate which contains atelopeptide containing collagen in solution . the collagen in dispersion / solution ( telopeptide and / or atelopeptide ) is precipitated as a part of a purification scheme , for example by adding a neutral salt to the solution to a concentration of about 1 . 0 m to 4 . 0 m , preferably 3 . 5 m . various alkali metal halides , e . g . nacl , may be used . the resulting precipitate is isolated , for example by centrifugation . further treatment includes exchanging with a dilute carboxylic acid , e . g . acetic acid ( 0 . 05 m to 0 . 5 m ) in the presence of aqueous nacl ( 0 . 001 to 0 . 1 weight percent ) with precipitation by addition of nacl ( 1 to 4 m ) and resolubilization to insure the purity of the collagen . specifically , the procedure may involve an initial precipitation by use of a neutral salt ( at least 10 to 30 wt %), isolation of the precipitate , redissolving in dilute acid , e . g . a carboxylic acid of about 0 . 05 m to 1 . 0 m , filtration , reprecipitation of the collagen with about 2 to 10 wt % aqueous salt solution , isolation , redissolution with a dilute carboxylic acid , with repetition of the purification process until the desired degree of purity . the collagen is then resuspended in dilute acid solution , generally a carboxylic acid such as acetic or citric acid at a concentration of about 0 . 01 m to 0 . 5 m . activated charcoal can be added in particle tight containers or the collagen can be dialyzed to remove low molecular weight solutes which might present undesirable odors or fragrances . precipitation of the collagen can be achieved in a variety of ways , including for example , the addition of neutral salt , and decrease in ph in the presence of neutral salt . preferably , mild conditions are employed to prevent denaturation and disruption of the natural fibrillar character of collagen . the collagen dispersion may then be concentrated , for example by dialysis , to a concentration of about 1 mg / ml to 20 mg / ml . the clear solution of collagen is relatively free of higher aggregates , is viscous , and consists essentially of marine invertebrate type v fibrillar collagen . in the preparation of cosmetic or pharmaceutical products using the present invention , marine invertebrate type v collagen can be used in effective amounts of about 0 . 001 to 30 wt % of the collagen protein preparation , with 0 . 01 to 10 wt % preferred , and 0 . 5 to 5 wt % most preferred . the collagen proteins may be incorporated into suitable cosmetic or pharmaceutical vehicles such as lotions , creams , ointments , gels , shampoos , conditioners , or solutions . suitable ointments are hydrophilic ointments ( usp ) or petrolatum and cosmetically effective amounts of collagen protein are incorporated into the ointment for topical application to skin or hair . suitable lotions and creams are as mentioned previously for cosmetic compositions . solutions are made by mixing solutions of collagen protein in deionized water for application to human or animal skin and hair . gels are made by mixing 1 - 90 % water with a suitable polymer . suitable humectants for use in the cosmetic compositions of the present invention include for example glycerin , propylene glycol , butylene glycol , urea , sorbitol , sodium pca , gelatin , polyethylene glycols , sodium lactate , and hyaluronic acid . suitable emollients include for example glyceryl stearate , cetyl alcohol , stearyl alcohol , isopropyl stearate , stearyl alcohol , stearyl stearate , isopropyl stearate , stearic acid , isobutyl palmitate , isocetyl stearate , oleyl alcohol , sebacates , myristates , palmitates , squalenes , glyceryl monooleate , oleic acids , lanolin , acetylated lanolin alcohols , petrolatum , mineral oils , palmitic acids , and isostearyl neopentanoate . a variety of surfactants can be used in the compositions of the invention including amphoteric , anionic , cationic , or nonionic surfactants . suitable amphoteric surfactants include imidazolines , betaines , and amino acid salts . suitable anionic surfactants include for example fatty acid soaps , salts of higher alkyl sulfates , n - acyl sarcosinates , salt or phosphates , sulfosuccinate salts , alkyl benzene sulfonatcs , salts of n - acyl glutamate , and polyoxyethylene alkyl ether carboxylic acids . cationic surfactants include for example alkyl trimethyl ammonium salts , alkyl pyridinium salts , alkyl quaternary ammonium salts , and polyamine fatty acid derivatives . nonionic surfactants include for example lipophilics such as sorbitan fatty acid esters , glycerol fatty acids , propylene glycol fatty acid esters ; hydrophilics including for example polyoxyethylene sorbitan fatty acid esters , polyoxyethylenc glycerol fatty acid esters , polyoxyethylene fatty acid esters , polyoxyethylene alkyl ethers , pluronics , polyoxyethylene alkyl phenyl ethers , and polyoxyethylene propylene glycol fatty acid esters . suitable pigments include for example organic and inorganic pigments such as talc , mica , titanium dioxide , titanated mica , iron oxides , ultramarines , chromium oxides , carmine , d & amp ; c , and fd & amp ; c colors and lakes , ferric and ferrous oxides . suitable waxes include for example beeswax , camauba , ceresin , microcrystalline , lanolin , candelilia , cetyl alcohol , cocoa butter , petrolatum , hydrogenated caster oil , spermaceti , bran wax , capok wax , and bayberry . the present invention is directed to a method of moisturizing and forming a film on human and animal skin , nails , or hair by applying to the surface and effective amount of invertebrate type v telopeptide containing collagen protein . an effective amount of collagen protein is about 0 . 001 - 30 wt %. the collagen protein may be applied directly to the surface in a solution form , or it may be incorporated into cosmetic or pharmaceutical compositions mentioned herein . the collagen protein or protein containing composition may be applied to the surface once or twice a day or as necessary . for example , if the collagen protein is incorporated into a facial moisturizer , usually one to two applications of moisturizer per day will provide a beneficial effect . if the collagen proteins are incorporated into shampoos or hair conditioners , usually application once a day or every other day will be sufficient to provide a beneficial effect . when collagen proteins are incorporated into makeups , blushes , or eye shadows , they provide a treatment effect to the skin when applied once a day or whenever makeup is worn . if incorporated into nail treatment products or nail enamels , consistent usage in a nail care regimen ( i . e . once or twice a week ) will provide beneficial results . the invention will be further described in connection with the following examples which are set forth for the purposes of illustration only . cannon - balljellyfish were dissected to separate the mantle from the tentacles and the reproductive and digestive organ was dissected from the mantle . the mantle was then cut into small pieces and placed into dilute ( 0 . 5 m ) citric acid such that 10 mantles of average sized jellyfish ( 8 - 12 inches in diameter ) were placed into 4 liters of citric acid solution . the container was covered to restrict evaporation and refrigerated at between 4 ° c . and 10 ° c . for three ( 3 ) days . the viscous collagen solution was filtered through 4 layers of cheese - cloth and the viscous materials precipitated by the addition of solid sodium chloride to a final concentration of 3 . 5 m . the sodium chloride was added in small increments and the precipitated materials removed as formed by the salt precipitation . essentially all of the collagen was thus precipitated by the addition of sodium chloride and transferred to a separate container . the precipitated collagen was then gently and quickly washed with distilled water to remove associated salt crystals and then 1 liter of 0 . 5 m citric acid solution was added to resolubilize the precipitated collagen . this aqueous solution of invertebrate type v collagen was stored in a tight container , to prevent evaporation , under refrigeration until used . by sampling aliquots of this collagen preparation it was determined that the collagen content was 2 . 5 % by weight . a particle tight container of activated charcoal was added to the collagen preparation during storage to reduce odors . in this example , cannon - ball jellyfish were dissected to separate the mantle from the tentacles and the reproductive and digestive organ was dissected from the mantle . the tentacles were then cut into small pieces and placed into dilute ( 0 . 5 m ) citric acid such that tentacles from 10 average sized jellyfish ( 8 - 12 inches in diameter ) were placed into 2 liters of citric acid solution . the container was covered to restrict evaporation and refrigerated at between 4 ° c . and 10 ° c . for three ( 3 ) days . the viscous collagen solution was filtered through 4 layers of cheese - cloth and the viscous materials precipitated by the addition of solid sodium chloride to a final concentration of 3 . 5 m . the sodium chloride was added in small increments and the precipitated materials removed as formed by the salt precipitation . essentially all of the collagen was thus precipitated by the addition of sodium chloride and transferred to a separate container . the precipitated collagen was then gently and quickly washed with distilled water to remove associated salt crystals and then 1 liter of 0 . 5 m citric acid solution was added to resolubilize the precipitated collagen . this aqueous solution of invertebrate type v collagen was stored in a tight container , to prevent evaporation , under refrigeration until used . by sampling aliquots of this collagen preparation it was determined that the collagen content was 1 . 8 % by weight . in this example , cannon - ball jellyfish were dissected to separate the mantle from the tentacles and the reproductive and digestive organ was dissected from the mantle . the mantle was then cut into small pieces and placed into dilute ( 0 . 5 m ) citric acid such that 10 mantles of average sized jellyfish ( 8 - 12 inches in diameter ) were placed into 4 liters of citric acid solution . the container was covered to restrict evaporation and heated to a temperature of 65 ° c . for 15 minutes ( the solution appears to clear after approximately 10 minutes , however heating was continued until the solution temperature reached 70 ° c . at which time the collagen preparation was placed refrigerated at between 4 ° c . and 10 ° c . for three ( 3 ) days . the viscous gelatin solution was filtered through 4 layers of cheese - cloth and the viscous materials or aqueous solution of invertebrate type v gelatin was stored in a tight container , to prevent evaporation , under refrigeration until used . by sampling aliquots of this gelatin preparation it was determined that the collagen content was 2 . 8 % by weight . a particle tight container of activated charcoal was added to the gelatin preparation during storage to reduce odors . in this example , cannon - ball jellyfish were dissected to separate the mantle from the tentacles and the reproductive and digestive organ was dissected from the mantle . the mantle and tentacles were then cut into small pieces and placed into dilute ( 1 . 0 m ) acetic acid such that 10 mantles and associated tentacles of average sized jellyfish ( 8 - 12 inches in diameter ) were placed into 2 liters of acetic acid solution . the container was covered to restrict evaporation and refrigerated at between 4 ° c . and 10 ° c . for three ( 3 ) days . the viscous collagen solution was filtered through 4 layers of cheese - cloth and the viscous materials precipitated by the addition of solid sodium chloride to a final concentration of 3 . 5 m . the sodium chloride was added in small increments and the precipitated materials removed as formed by the salt precipitation . essentially all of the collagen was thus precipitated by the addition of sodium chloride and transferred to a separate container . the precipitated collagen was then gently and quickly washed with distilled water to remove associated salt crystals and then 1 liter of 0 . 5 m citric acid solution was added to resolubilize the precipitated collagen . this aqueous solution of invertebrate type v telopeptide containing collagen was stored in a tight container , to prevent evaporation , under refrigeration until used . by sampling aliquots of this collagen preparation it was determined that the collagen content was 3 . 2 % by weight . a particle tight container of activated charcoal was added to the collagen preparation during storage to reduce odors . in this example , cannon - ball jellyfish were dissected to separate the mantle from the tentacles and the reproductive and digestive organ was dissected from the mantle . the mantle and tentacles were then cut into small pieces and placed into dilute ( 1 . 0 m ) acetic acid such that 10 mantles and associated tentacles of average sized jellyfish ( 8 - 12 inches in diameter ) were placed into 2 liters of acetic acid solution . the container was covered to restrict evaporation and refrigerated at between 4 ° c . and 10 ° c . for three ( 3 ) days . the viscous collagen solution was filtered through 4 layers of cheese - cloth and the viscous materials precipitated by the addition of solid sodium chloride to a final concentration of 3 . 5 m . the sodium chloride was added in small increments and the precipitated materials removed as formed by the salt precipitation . essentially all of the collagen was thus precipitated by the addition of sodium chloride and transferred to a separate container . the precipitated collagen was then gently and quickly washed with distilled water to remove associated salt crystals and then 1 liter of 0 . 5 m citric acid solution was added to resolubilize the precipitated collagen . this organic acid dispersion / solution of invertebrate type v collagen was then placed into dialysis bags and exhaustively dialyzed against deionized water at 0 ° c . ( against crushed ice made with deionized water ). this aqueous solution of invertebrate type v collagen was stored in a tight container , to prevent evaporation , under refrigeration until freeze - dried . by sampling aliquots of this collagen preparation it was determined that the collagen content was 3 . 2 % by weight . a particle tight container of activated charcoal was added to the collagen preparation during storage to reduce odors . this deionized water dispersion of invertebrate type v collagen was carefully frozen in a freeze - drying vessel as to maximize the surface area to volume ratio , and freeze - dried . the freeze - dried collagen preparation was sealed under vacuum and stored at room temperature ( for prolonged storage it is also possible to store this freeze - dried materials in a freezer at minus 20 ° c .). prior to use in formulation of compositions containing this materials , the collagen was sheared in a waring blender to achieve a fine powder and then reconstituted in 0 . 25 m citric acid . a collagen / gelatin containing oil in water moisturizing lotion was made as follows : marine invertebrate type v telopeptide containing collagen was used , preferably made according to example 1 or 2 . marine invertebrate type v telopeptide containing collagen was used , made according to any one of examples 1 - 5 , more preferably made according to example 3 , 4 , or 5 . marine invertebrate type v telopeptide containing collagen was used , made according to any one of examples 1 - 6 . marine invertebrate type v telopeptide containing collagen was used , made according to any one of examples 1 - 6 . cannon - ball jellyfish were gently homogenized using a mechanical grinder similar to that used to grind hamburger meat . the group materials were collected into suitable containers ( 5 gallon plastic pails with locking lids are suitable as are 55 gallon tanks ) and citric acid was added in dry powder form to a final concentration of 0 . 5 m with constant stirring to dissolve and disperse the citric acid . the container was closed and stored under refrigeration ( 4 - 10 ° c .) for a minimum of 2 weeks . after two weeks , the containers were opened and the materials stirred using an electrically driven stirring device ( an appropriate stirring device is one such as used to stir paint ) to further homogenize the now viscous collagen preparation . the viscous collagen preparation was then filtered through fine screen wire to remove residual fragments of reproductive organs , and non - dispersed collagen / protein materials . the viscous clarified materials were returned to storage containers and stored under refrigeration until use . the produced natural collagen preparation is useful in formulations of a variety of products both hydrolyzed and non - hydrolyzed the natural collagen retains the natural salt and small molecular weight materials present in the source materials and can be preserved using chemical preservatives for storage without refrigeration , it can be diluted to provide less viscous collagen preparations , it can be heated to produce gelatin preparations . more specifically , this natural material is a base material which can be used with additional processing to produce the materials described in all other examples . although the present invention has been described with reference to the presently preferred embodiments , the skilled artisan will appreciate the various modifications , substitutions , omissions , and changes may be made without departing from the spirit of the invention . accordingly , it is intended that the scope of the present invention be limited only be the scope of the following claims , including equivalents thereof . all references cited herein are hereby incorporated by reference in their entirety .
the present invention relates to a process for the production of marine invertebrate type v telopeptide containing collagen preparations from marine invertebrates , compositions containing preparations , and methods of using these preparations . the collagen preparation includes telopeptide containing and optionally invertebrate atelopeptide containing , type v fibrillar collagen . the present collagen preparations may be employed in a variety of products including for example , cosmetic , pharmacological , dental , and cell culture products .