one embodiment of the present disclosure relates to a drug eluting device comprising an expandable member and at least one coating on the expandable member comprising at least one layer , wherein the at least one layer of the at least one coating comprises an adjustable matrix composition comprising a sol gel material and a bioactive material . as used herein adjustable matrix refers to an admixture that can be optimized to control retention time on an expandable member &# 39 ; s surface as well as the bioactive agent dose delivered to a treatment site . a sol gel material is defined herein broadly to cover the product of a sol - gel process . this typically involves preparation of a sol , gelation of the sol and removal of the solvent . the sol may be produced from inorganic or organic precursors ( e . g . nitrates or alkoxides ) and may consist of dense oxide particles or polymeric clusters . a sol is defined as a colloidal suspension of solid particles in a liquid . there can be particulate sols and polymeric sols : the difference can be defined in terms of size . particulate sols contain dense oxide particle typically about 1 nm in size . polymeric sols generally contain long , hairy , branched suspensions of particles . any precursor consisting of a metal or metalloid element surrounded by a set of ligands , which includes alkoxides , can be used to prepare a colloidal system . this colloidal system can then be used to form a gel in accordance with the present disclosure . a gel herein is defined as a substance that contains a continuous solid skeleton enclosing a continuous liquid phase . the sol gel process typically involves the manufacture of inorganic matrices or ceramics through the formation of a sol or suspension in solution . hydrolysis and condensation of appropriate precursors ( typically metal alkoxides or metal chlorides ) leads to the formation of colloidal or polymeric gels which extend throughout the liquid ( thereby entrapping the liquid ). hence , condensation drives the conversion process from sol to gel such that a continuous , globally connected solid polymeric matrix is produced and a wet gel is formed . polycondensation within a silicon based sol is possible due to the hydrolytic susceptibility of si — o — si based polymers . the labile nature of this bond fuels the growth of polymeric networks which then form gels which can then in turn form a porous solid material when the liquid is removed and the material is subsequently dried . ‘ aging ’ or perhaps additional high temperature drying can push the condensation process even further such that the material may shrink or its surface chemistry may change or its pore size distribution may shift . in one embodiment , the sol gel material may comprise at least one of an organic oxide , an inorganic oxide , an organically modified silane , and a hybrid oxide comprising an organically modified silane and an inorganic oxide . in another embodiment , the inorganic oxide comprises at least one of an oxide of silicon , an oxide of titanium , and an oxide of aluminum . the term “ organically modified ” refers to compounds that contain at least one organic ( carbon - based ) ligand ( in one embodiment a direct metal - carbon ( or semiconductor - carbon ) bond ). the term “ organically modified silane ” refers to a compound that contains at least one non - hydrolysable carbon - based ligand bonded to silicon . this class of compounds is also referred to as ormosils , silane coupling agents , silane couplers , silane adhesion promoters , or simply silanes . these compounds represent a wide variety of compounds because the non - hydrolysable ligand ( s ) can be any conceivable organic group ( s ) synthesized according to the principles of organic chemistry . non - limiting examples include alkylsilanes ( such as , but not limited to , methyltrimethoxysilane , methyltriethoxysilane , dimethyldiethoxysilane , trimethylethoxysilane , vinyltrimethoxysilane , vinyltriethoxysilane , ethyltriethoxysilane , isopropyltriethoxysilane , butyltriethoxysilane , octyltriethoxysilane , dodecyltriethoxysilane , octadecyltriethoxysilane , etc ), aryl - functional silanes ( e . g . phenyltriethoxysilane , etc . ), aminosilanes ( e . g . aminopropyltriethoxysilane , aminophenyltrimethoxysilane , aminopropyltrimethoxysilane , etc . ), acrylate - and methacrylate - functional silanes ( e . g . acryloxypropyltrimethoxysilane , ect ), carboxylate , phosphonate , ester , sulfonate , isocyanate , and epoxy functional silanes . it is important to realize that these compounds still contain hydrolysable groups that enable them to undergo hydrolysis / condensation reactions of sol - gel processes . therefore , each of them or any combination of two or more of them can be used as sol - gel precursors , or they can be used in combination with a fully hydrolysable sol - gel precursor , such as tetraethoxy silane ( teos ) or titanium isopropoxide . the sol - gel composition thus obtained will not be a stoichiometric inorganic oxide . instead it will be a hybrid sol - gel material that will exhibit bulk chemical , mechanical , physical and other properties characteristic of the particular combination of constituent components . exemplary organically modified silanes that can be particularly useful in this aspect include silane having the formula ( r 2 ) 3 — sir 1 , wherein r 1 is independently selected from substituted alkyl , substituted alkenyl , substituted alkynyl , substituted aralkyl , substituted heteroaryl , and substituted alkoxy with the proviso that r 1 contains a hydroxyl or amino group , or a functional group that can be transformed to a radical that contains a hydroxyl or amino group ; wherein r 2 is independently selected from halo , optionally substituted alkoxy , optionally substituted aryloxy , optionally substituted silyloxy , or optionally substituted alkyl with the proviso that all three r 2 substituents are not simultaneously substituted alkyl . alternatively , exemplary organically modified silanes may include tetraethoxysilane , tetramethoxysilane , methyltriethoxysilane , methyltrimethoxysilane , ethyltriethoxysilane , ethyltrimethoxysilane , tetrapropylorthosilicate , phenyltriethoxysilane , phenyltrimethoxysilane , isobutyltriethoxysilane , isobutyltrimethoxysilane , diphenyldiethoxysilane , diphenyldimethoxysilane , dimethyl ( diethoxy ) silane , dimethyl ( dimethoxy ) silane , propyltrimethoxysilane , propyltriethoxysilane , 3 - aminopropyltriethoxysilane ( aes ), 3 - aminopropyltrimethoxysilane , ( 3 - glycidoxypropyl ) trimethoxysilane , ( 3 - glycidoxypropyl ) triethoxysilane , hydroxymethyltriethoxysilane , hydroxymethyltrimethoxysilane , 3 -( hydroxyl ( polyethyleneoxy ) propyl )- heptamethyltrisiloxane , n -( 2 ′- aminoacyl )- 3 - aminopropyltriethoxysilane , 3 - gluconamidopropylsiloxane , 3 - methacryloxypropyltrimethoxysilane , 3 - methacryloxypropyltriethoxysilane , vinyltrimethoxysilane , vinyltriethoxysilane , n - β - aminoethyl - γ - aminopropyltrimethoxysilane , n - β - aminoethyl - γ - aminopropylmethyldimethoxysilane , n - methyl - γ - aminopropylmethyldiethoxysilane , acetoxypropyltrimethoxysilane , hydridotrimethylsilane , hydridotriethylsilane , chloromethyltrimethoxysilane , chloromethyltriethoxysilane , cyclohexyltrimethoxysilane , 3 -( 2 - aminoethylamino ) propyltrimethoxysilane ( edas ), 3 -( 2 - aminoethylamino ) propyltriethoxysilane ( edaes ), fluoroalkylsilanes , diethoxymethylvinylsilane , diethoxymethylphenylsilane , [( n , n - diethylamino ) propyl ] trimethoxysilane , anilinomethyltriethoxysilane , and anilinomethyltrimethoxysilane in another embodiment , the adjustable matrix composition can comprise an inorganic oxide and an agent that modifies a characteristic of the inorganic oxide selected from the group consisting of hydrophobicity , charge , biocompatibility , mechanical properties , bioactive material affinity , storage capacity ; and combinations thereof . an organically modified silane can be such an agent . by varying the properties of the sol - gel composition , different bioactive material delivery release rates and profiles can be achieved for various bioactive materials . for example , a bioactive material can be released with first order or second order kinetics . delivery can begin upon deployment of the bioactive material delivery device , or at a particular time after implantation , and can increase rapidly from zero to a maximal rate over a short period of time , for example less than an about 5 minutes . such maximal delivery can continue for a predetermined period until the delivery rate suddenly drops . in the field of sustained - release bioactive material delivery it is generally considered desirable to avoid a large bioactive material delivery “ burst ” wherein the majority of the bioactive material is delivered in a short amount of time . however in some cases the delivery of a “ burst ” of bioactive material is highly desirable such as a pcta or pta drug coated balloon whose residence time in the treatment area is short lived . the methods of the present disclosure that allow for incorporation of bioactive material into the forming sol - gel composition can be used to tailor the release kinetics . embodiments adopting treating the surface and / or channels of the sol - gel composition with an organically modified silane can also be used to either speed up or slow the rate of drug elution . in accordance with the present disclosure then , a variety of parameters can be adjusted to produce numerous variations in delivery profiles depending on what is desirable for a particular bioactive material / disease / patient combination . the expandable member according to the present disclosure can be a balloon or a basket . the expandable member can be in association with a fixed wire system . the basket can be self - expanding or manually expanding . in another embodiment , the basket comprises a material that comprises a shape memory metal , shape memory metal alloy , or a superelastic material . in another embodiment , the material is nickel titanium . superelastic materials possess superelasticity which is an impermanent response to relatively high stress caused by a phase transformation between the austenitic and martensitic phases . when mechanically loaded , a superelastic alloy deforms reversibly to very high strains by the creation of a stress - induced phase . when the load is removed , the new phase becomes unstable and the material regains its original shape . alternatively , the basket comprises a metal , polymer , ceramic , or other blends or combinations thereof . the term “ basket ” can also refer to a cage . in another embodiment , the balloon can be a cutting balloon . a cutting balloon has a special balloon tip with small blades which are activated when the balloon is inflated . the term “ bioactive material ( s )” as used herein refers to any organic , inorganic , or living agent that is biologically active or relevant . for example , a bioactive material can be a protein , a polypeptide , a polysaccharide ( e . g . heparin ), an oligosaccharide , a mono - or disaccharide , an organic compound , an organometallic compound , or an inorganic compound . it can include a biologically active molecule such as a hormone , a growth factor , a growth factor - producing virus , a growth factor inhibitor , a growth factor receptor , an anti - inflammatory agent , an antimetabolite , an integrin blocker , or a complete or partial functional insense or antisense gene . it can also include a man - made particle or material , which carries a biologically relevant or active material . an example is a nanoparticle comprising a core with a drug and a coating on the core . such nanoparticles can be post - loaded into pores or co - deposited with metal ions . bioactive materials also can include drugs such as chemical or biological compounds that can have a therapeutic effect on a biological organism . bioactive materials include those that are especially useful for long - term therapy such as hormonal treatment . examples include drugs for contraception and hormone replacement therapy , and for the treatment of diseases such as osteoporosis , cancer , epilepsy , parkinson &# 39 ; s disease and pain . suitable biological materials can include , without limitation , an anti - restenotic agent , an anti - inflammatory agent , an hmg - coa reductase inhibitor , an antimicrobial agent , an antineoplastic agent , an angiogenic agent , an anti - angiogenic agent , a thrombolytic agent , an antihypertensive agent , an anti - arrhythmic agent , a calcium channel blocker , a cholesterol - lowering agent , a psychoactive agent , an anti - depressive agent , an anti - seizure agent , a contraceptive , an analgesic , a bone growth factor , a bone remodeling factor , a neurotransmitter , a nucleic acid , an opiate antagonist and combinations thereof . additional bioactive materials include , without limitation , paclitaxel , rampamycin , everolimus , tacrolimus , sirolimus , des - aspartate angiotensin i , nitric oxide , apocynin , gamma - tocopheryl , pleiotrophin , estradiol , aspirin , statin , atorvastatin , cerivastatin , fluvastatin , lovastatin , pravastatin , rosuvastatin , simvastatin , and combinations thereof . bioactive materials also can include precursor materials that exhibit the relevant biological activity after being metabolized , broken - down ( e . g . cleaving molecular components ), or otherwise processed and modified within the body . these can include such precursor materials that might otherwise be considered relatively biologically inert or otherwise not effective for a particular result related to the medical condition to be treated prior to such modification . combinations , blends , or other preparations of any of the foregoing examples can be made and still be considered bioactive materials within the intended meaning herein . aspects of the present invention directed toward bioactive materials can include any or all of the foregoing examples . there are various ways to apply a bioactive active material to the expandable members including balloons of the present drug eluting devices . these methods include spraying or dip coating . more specifically , application methods include electrospinning , sol spinning , or electrostatic spraying . dip coating could include rotation of an expandable member such as a balloon . the balloon can be held above a solution containing a bioactive material and can be parallel to the surface . the balloon can be partially submerged such that it rotates a portion of the balloon to give it time to dry before it return to the solution on the next rotation . dip coating can also include vertical dipping . the teachings of u . s . pat . no . 6 , 764 , 690 are herein incorporated by reference in its entirety . u . s . pat . no . 6 , 764 , 690 generally teaches spraying drying particles onto a surface . in addition , the bioactive materials may be applied by vapor phase deposition . in another embodiment , the coating on the expandable member of the present drug eluting expandable devices may comprise two more layers , each layer comprising an adjustable matrix composition and a bioactive material . in another embodiment , the adjustable matrix is a sol gel material . in another embodiment , the two or more layers of the coating are different from each other . contrast media is any substance that is used to enhance the visibility of structures or fluids within the body . an example of this is the use of a radiopaque substance during an x - ray exam to highlight features that would otherwise be less distinguishable from nearby tissue . the contrast can either be positive or negative . positive contrast media has a higher attenuation density than the surrounding tissue . this means that the contrast looks more opaque than the surrounding tissue when seen on an x - ray . negative contrast media has a lower attenuation density than the surrounding tissue . this means that the contrast looks less opaque than the body . negative contrast is generally found as a gas . contrast can be used to produce images of almost any hollow structure in the body . in another embodiment , the coating ( s ) or the layer ( s ) on the expandable member of the present drug eluting devices may be non - uniform . without limitation , they may be contiguous or non - contiguous . without limitation , they may be in the form of dots or stripes . in another embodiment , the expandable member of the present drug eluting devices can comprise a porous or non - porous material . in another embodiment , the expandable member comprises a polymer . alternatively , the polymer may comprise polyamide , polyolefin , polyethylene , polyester , polyurethane , elastomer , thermoplastic elastormer , nylon elastomer , nylon , nylon blends , copolyamide block ether , polyether block amides ( pebax ), polyethylene terephthalate ( pet ), polytetrafluoroethylene ( ptfe ), expanded polytetrafluoroethylene ( eptfe ), latex , or silicone ; or blends or combinations thereof . fig1 depicts a drug eluting medical device having an expandable member in the compressed state which can be self or manually expanded . the expandable ribs are in the compressed state 1 . a flexible tip 2 is shown which can be associated with a guide wire or an over - the - wire type device . fig2 depicts a drug eluting medical device having expandable ribs 3 which are shown in their expanded state . for a manual expansion design , the center component 4 can act as a pull wire to activate the expansion of the ribs . fig3 depicts a drug eluting device having expandable ribs which are self expanding . when the ribs are self expanded , a sheath 5 could be retracted to allow the ribs 3 to expand . the ribs can be coated with bioactive materials . fig3 shows four ribs for the expandable member . however , the number of ribs can be greater than four in various embodiments . fig4 depicts a drug eluting medical device with twelve expandable ribs 3 in their expanded state . the ribs can be manually or self - expanded . the ribs can be coated with bioactive material . the ribs of fig1 - 4 can be a mesh , or weave , or can be filaments at various angles , unparallel to each other and can be of various shapes , widths , and thicknesses . fig5 shows a drug eluting medical device with a balloon having a coating on its surface 6 . fig6 depicts another drug eluting medical device with a balloon having coating on its working length ( shown by shading ). in this embodiment , the coating is on the middle cylindrical portion which would be in contact with a vessel when expanded . fig7 depicts a drug eluting medical device which allows for perfusion . the arrows show movement of blood during deployment . fig8 depicts a drug eluting medical device having an expandable member in association with a fixed wire 7 system , wherein the wire component is integrated with the expandable member device . fig9 a - 9d depict substrates with coatings . in fig9 a the drug matrix 8 is shown which has been applied to a substrate 9 . fig9 b shows an additional layer which is a tie layer 10 . fig9 c shows yet another additional layer which is a top layer 11 . fig9 d shows the tie layer 10 , drug matrix 8 , and a top layer 11 on a substrate 9 . fig1 a and 10b depict substrates with coatings and layers which are irregular or non - uniform . 12 and 14 are drug matrix on the substrate 13 . perfusion as used herein permits blood flow through the drug eluting expandable device from the proximal to the distal end during deployment . this reduces the risk of ischemic events . when the expandable member is a basket , there would be natural perfusion through the openings in the basket . when the expandable member is a balloon which can cause complete occlusion when deployed , openings may be necessary to allow blood flow . another embodiment of the present disclosure relates to a medical system comprising a stent and a drug eluting device comprising an expandable member and at least one coating on the expandable member comprising at least one layer , wherein the at least one layer of the at least one coating comprises an adjustable matrix composition comprising a sol gel material and a bioactive material . alternatively , the stent can be a bare metal stent or a drug eluting stent . a stent generally is a tube that is inserted into a natural conduit of the body to prevent or counteract a disease - induced localized flow constriction . a bare metal stent is made of metal and generally does not elute drug . a drug - eluting stent is a stent placed typically into narrowed , diseased arteries that slowly releases a drug to block cell proliferation . this prevents scar - tissue - like growth that , together with clots ( thrombus ), could otherwise block the stented artery , a process called restenosis . in another embodiment , the medical system allows for perfusion during deployment . in another embodiment the medical system further comprises a delivery catheter . a catheter is a tube that can be inserted into a body cavity , duct or vessel . catheters thereby allow drainage or injection of fluids or access by surgical instruments . a delivery catheter allows for delivery of medical equipment . a delivery catheter herein can be used to deliver the present medical system comprising a stent and a drug eluting device . or it can be used to delivery only a drug eluting device . in another embodiment , the drug eluting stent contains the same bioactive material as that of the drug eluting device . or the drug eluting stent can contain a different bioactive material from that of the drug eluting device . another embodiment of the present disclosure relates to a drug eluting device comprising a balloon and at least one coating on the balloon comprising at least one layer , wherein the at least one layer of the at least one coating comprises a bioactive material , wherein the device allows for perfusion during deployment . in another embodiment , the coating can further comprise of contrast media . in another embodiment , the coating further comprises a sol gel material . in another embodiment , the coating is non - uniform . alternatively , the coating can be in the form of dots or stripes . in another embodiment , the drug eluting device further comprises a multilumen tubular member comprising two or more lumens , the multilumen tubular member comprising a proximal end and a distal end extending through a balloon cavity defined by the balloon . in one embodiment , the multilumen tubular member is a bulilumen tubular member comprising at least one side opening arranged in the bilumen tubular member located both distal and proximal of the balloon and in fluid communication with one another via a first lumen in the bilumen tubular member , the first lumen extending from the proximal end of the bilumen tubular member through the tubular member to an end hole distal of the balloon ; and the second lumen is provided for receiving a pressure fluid for inflating the balloon . one of ordinary skill in the art is directed to the teachings of u . s . pat . no . 5 , 295 , 961 contents of which are herein incorporated by reference in its entirety . u . s . pat . no . 5 , 295 , 961 offers a general teaching of a catheter system for mechanical dilatation of coronary stenoses . in another embodiment , the drug eluting device further comprises an axially elongate catheter shaft , constructed and arranged for insertion into a distal body lumen , said catheter shaft having an inflation conduit extending axially therethrough ; the balloon secured to said catheter shaft , the balloon in fluid communication with the inflation conduit and outwardly radially expandable to a preselected configuration in response to inflation thereof . in one embodiment , the balloon is multi - lobed . one of ordinary skill in the art is directed to the teachings of u . s . pat . no . 4 , 983 , 167 contents of which are herein incorporated by reference in its entirety . u . s . pat . no . 4 , 983 , 167 offers a general teaching of a catheter system which provides a path for conducting blood past a stenosis and inflated balloons ( perfusion ). in another embodiment , the balloon is multi - lobed . in another embodiment , the drug eluting device further comprises an inflatable member having generally a helically coiled portion , the helically coiled portion being inflatable from a deflated configuration to an inflated , configuration defining a generally open lumen . one of ordinary skill in the art is directed to the teachings of u . s . pat . no . 5 , 181 , 911 contents of which are herein incorporated by reference in its entirety . u . s . pat . no . 5 , 181 , 911 offers a general teaching of a helical balloon catheter which allows for perfusion . another embodiment of the present disclosure relates to a method of treating stenosis or restenosis or in - stent restenosis comprising deploying in a subject a drug eluting device comprising an expandable member and at least one coating on the expandable member comprising at least one layer , wherein the at least one layer of the at least one coating comprises an adjustable matrix composition comprising a sol gel material and a bioactive material . in another embodiment , the device allows for perfusion during deployment . another embodiment of the present disclosure relates to a method of treating stenosis or restenosis or in - stent restenosis comprising deploying in a subject a drug eluting device comprising an expandable member balloon and at least one coating on the device comprising at least one layer , wherein the at least one layer of the at least one coating comprises a bioactive material and a contrast media , wherein the device allows for perfusion during deployment . in another embodiment , the expandable member is a balloon and the at least one coating is deposited on and adhered to the balloon . coating of an expanded balloon with a paclitaxel containing sol - gel matrix a solution containing 0 . 2m of teos in a mixture of water and ethanol was hydrolyzed for 3 hours at ph 3 . paclitaxel was then added to the silane based solution such that the final concentration of drug was 5 mg / ml . this solution was then sprayed at a flow rate of 40 μl / min via an ultrasonic nozzle ( operating at 120 khz ) onto a balloon ( 3 . 25 mm × 19 mm ) which in turn was moving at a predefined lateral speed ( 10 mm / second ) and rotation rate ( 3 hz ) through the spray plume . the balloon was coated by moving the balloon back and forth through the ultrasonically generated spray plume a total of 5 times ( referred to as ‘ passes ’). a ‘ rest period ’ of 90 - 120 seconds was included between successive passes in order to allow the matrix to dry and in turn promote additional cross - linking within the sol - gel . at this time the balloon was allowed to dry for 16 - 24 hours before evaluating the elution characteristics of the encapsulated drug . the balloon was placed in different 1 ml aliquots of pbs ( phosphate buffered saline ) for a series of defined times in order to generate the appropriate elution profile . the aliquots of pbs were then analyzed by hplc to establish paclitaxel concentrations in solution at each time point . the data is presented in fig1 . a series of optical photographs and sem images were also collected prior to performing the elution analysis in order to evaluate coating adhesion and integrity of the coating . a fei xl - 30 sem was used to acquire the images shown in fig1 a and 11b . the following parameters were used to acquire the sem images : accelerating voltage = 2 kv , current = 2 ma , working distance = 10 mm to 30 mm . a solution containing 20 % isobutyltriethoxysilane and 80 % teos ( for a combined total concentration of 0 . 2m ) in a mixture of water and ethanol was hydrolyzed for 3 hours at ph 3 . cerivastatin was then added to the silane based solution such that the final concentration of drug was 5 mg / ml . this solution was then sprayed at a flow rate of 40 μl / min via an ultrasonic nozzle ( operating at 120 khz ) onto a balloon ( 3 . 25 mm × 19 mm ) which in turn was moving at a predefined lateral speed ( 10 mm / second ) and rotation rate ( 3 hz ) through the spray plume . the balloon was coated by moving the balloon back and forth through the ultrasonically generated spray plume a total of 5 times . a ‘ rest period ’ of 90 - 120 seconds was included between successive passes in order to allow the matrix to dry and in turn promote additional cross - linking within the sol - gel . this procedure was repeated with different balloons ( 10 and 20 times respectively ) to include variable numbers of passes and hence therefore variable quantities of drug within the matrix ( and hence on the balloon ). at this point the balloon was allowed to dry for 16 - 24 hours before evaluating the elution characteristics of the encapsulated drug . the balloon was placed in different 1 ml aliquots of pbs for a series of times in order to generate the appropriate elution profile . the aliquots of pbs were then analyzed by hplc to establish cerivastatin concentrations in solution at each time point . the data is presented below in fig1 . a series of optical photographs and sem images were also collected prior to performing the elution analysis in order to evaluate coating adhesion and integrity of the coating . a fei xl - 30 sem was used to acquire the images shown in fig1 and 13 . the following parameters were used to acquire these images : accelerating voltage = 2 kv , current = 2 ma , working distance = 10 mm to 30 mm . coating of an expanded balloon with a paclitaxel containing sol - gel matrix a solution containing 10 % isobutyltriethoxysilane and 90 % teos ( for a combined total concentration of 0 . 2m ) in a mixture of water and ethanol was hydrolyzed for 3 hours at ph 3 . paclitaxel was then added to the silane based solution such that the final concentration of drug was 12 mg / ml . this solution was then sprayed at a flow rate of 40 μl / min via an ultrasonic nozzle ( operating at 120 khz ) onto a balloon ( 3 . 25 mm × 19 mm ) which in turn was moving at a predefined lateral speed ( 10 mm / second ) and rotation rate ( 3 hz ) through the spray plume . the balloon was coated by moving the balloon back and forth through the ultrasonically generated spray plume a total of 5 times . a ‘ rest period ’ of 90 - 120 seconds was included between successive passes in order to allow the matrix to dry and in turn promote additional cross - linking within the sol - gel . this procedure was repeated with another balloon a total of 10 times such that twice as much drug was placed on the balloon within the sol - gel based matrix . at this time the balloon was allowed to dry for 16 - 24 hours before evaluating the elution characteristics of the encapsulated drug . the balloon was placed in different 1 ml aliquots of pbs for a series of defined times in order to generate the appropriate elution profile . the aliquots of pbs were then analyzed by hplc to establish paclitaxel concentrations in solution at each time point . the data is presented below in fig1 . coating of an expanded balloon with a cerivastatin containing sol - gel matrix a solution containing 20 % isobutyltriethoxysilane and 80 % teos ( for a combined total concentration of 0 . 2m ) in a mixture of water and ethanol was hydrolyzed for 3 hours at ph 3 . cerivastatin was then added to the silane based solution such that the final concentration of drug was either 8 . 5 mg / ml or 12 . 4 mg / ml . these solutions were then sprayed at a flow rate of 40 μl / min via an ultrasonic nozzle ( operating at 120 khz ) onto a balloon ( 3 . 25 mm × 19 mm ) which in turn was moving at a predefined lateral speed ( 10 mm / second ) and rotation rate ( 3 hz ) through the spray plume . in using this approach , the quantity of drug contained within a set amount of matrix material was varied . this , in turn , allows the user to vary the amount of drug that elutes from the matrix within a set time . the balloon was coated by moving the balloon back and forth through the ultrasonically generated spray plume a total of 5 times . a ‘ rest period ’ of 90 - 120 seconds was included between successive passes in order to allow the matrix to dry and in turn promote additional cross - linking within the sol - gel . at this point the balloon was allowed to dry for 16 - 24 hours before evaluating the elution characteristics of the encapsulated drug . the balloon was placed in different 1 ml aliquots of pbs for a series of times in order to generate the appropriate elution profile . the aliquots of pbs were then analyzed by hplc to establish cerivastatin concentrations in solution at each time point , for each variable set of passes . the data is presented below in fig1 . unless otherwise indicated , all numbers expressing quantities of ingredients , properties such as molecular weight , reaction conditions , and so forth used in the specification and claims are to be understood as being modified in all instances by the term “ about .” accordingly , unless indicated to the contrary , the numerical parameters set forth in the specification and attached claims are approximations that may vary depending upon the desired properties sought to be obtained by the present invention . at the very least , and not as an attempt to limit the application of the doctrine of equivalents to the scope of the claims , each numerical parameter should at least be construed in light of the number of reported significant digits and by applying ordinary rounding techniques . notwithstanding that the numerical ranges and parameters setting forth the broad scope of the invention are approximations , the numerical values set forth in the specific examples are reported as precisely as possible . any numerical value , however , inherently contains certain errors necessarily resulting from the standard deviation found in their respective testing measurements . the terms “ a ,” “ an ,” “ the ” and similar referents used in the context of describing the invention ( especially in the context of the following claims ) are to be construed to cover both the singular and the plural , unless otherwise indicated herein or clearly contradicted by context . recitation of ranges of values herein is merely intended to serve as a shorthand method of referring individually to each separate value falling within the range . unless otherwise indicated herein , each individual value is incorporated into the specification as if it were individually recited herein . all methods described herein can be performed in any suitable order unless otherwise indicated herein or otherwise clearly contradicted by context . the use of any and all examples , or exemplary language ( e . g ., “ such as ”) provided herein is intended merely to better illuminate the invention and does not pose a limitation on the scope of the invention otherwise claimed . no language in the specification should be construed as indicating any non - claimed element essential to the practice of the invention . groupings of alternative elements or embodiments of the invention disclosed herein are not to be construed as limitations . each group member may be referred to and claimed individually or in any combination with other members of the group or other elements found herein . it is anticipated that one or more members of a group may be included in , or deleted from , a group for reasons of convenience and / or patentability . when any such inclusion or deletion occurs , the specification is deemed to contain the group as modified thus fulfilling the written description of all markush groups used in the appended claims . certain embodiments of this invention are described herein , including the best mode known to the inventors for carrying out the invention . of course , variations on these described embodiments will become apparent to those of ordinary skill in the art upon reading the foregoing description . the inventor expects skilled artisans to employ such variations as appropriate , and the inventors intend for the invention to be practiced otherwise than specifically described herein . accordingly , this invention includes all modifications and equivalents of the subject matter recited in the claims appended hereto as permitted by applicable law . moreover , any combination of the above - described elements in all possible variations thereof is encompassed by the invention unless otherwise indicated herein or otherwise clearly contradicted by context . furthermore , numerous references have been made to patents and printed publications throughout this specification . each of the above - cited references and printed publications are individually incorporated herein by reference in their entirety . in closing , it is to be understood that the embodiments of the invention disclosed herein are illustrative of the principles of the present invention . other modifications that may be employed are within the scope of the invention . thus , by way of example , but not of limitation , alternative configurations of the present invention may be utilized in accordance with the teachings herein . accordingly , the present invention is not limited to that precisely as shown and described .
the present disclosure relates to drug eluting devices , and their uses . the drug eluting devices can allow for perfusion during deployment . the coatings the may contain bioactive materials which elute once deployed in a patient and can have anti - proliferative , anti - inflammation , or anti - thrombotic effects . sol gel technology can be used to coat the devices .