the present invention is generally directed to an electrode with increased stability and method of manufacturing the same . in particular the present invention is directed to a new electrode design . the present invention provides an electrode for an implantable electrode array with an improved current distribution and adhesion for neural stimulation electrodes . sputtered thin film electrodes may not provide enough electrode material on the electrode array surface for chronic stimulation . the electrodes are too thin and smooth and dissolve easily . electroplating adds more material to increase the life time of the electrode . the electrodes are thicker and more solid . however , high stress problems , such as cracking or delaminating , limit the plating thickness to & lt ; 1 μm which is the thickness normal dense plating . according to the method of the present invention electrodes ( pt , ir , pd , iro ) were electroplated with a diameter of 50 μm - 500 μm and a thickness of 2 μm - 3 μm on a substrate , such as a polymer , like polyimide , silicone , peek or parylene , or mixtures thereof . one aspect of the invention is to provide a mesh or grid of a different metal , such as ti , zr , ta or mixtures or alloys thereof , or a polymer , such as silicone , polyimide , peek or parylene or mixtures thereof . the mesh or grid has a height of 5 μm - 35 μm , preferably 22 μm - 27 μm . another aspect of the invention includes an additional electroplating step on top of the mesh or grid . in this case an embedded mesh or grid can be obtained . another aspect of the invention is to plate micro sticks with a dense structure on sputtered electrode surface as a support . as next step a porous and loose layer with low stress is applied on top of the electrode to cover the electrode surface . fig1 depicts a sem imaging (× 2 , 500 ) of electroplated platinum filled with grids of insulation polymers . the electrode of platinum containing the grid of polymer can be produced according to the process shown in fig3 . by adding insulated lines on the metal surface more edges are created . an increase of the edges minimizes the edge effect or electrical discharge . for example , an electrode surface has a metal disk with a diameter of d , the edge length is π * d . if an insulated cross is added on the metal surface , the edge length is increased from π * d to ( 4d + π * d ), which is over 120 % increase in edge length . for a square metal surface , it has a 100 % increase from 4d to 8d . in thin - film electrodes added insulation lines also serve as a protector for the metal layer to hold it from delaminating . in thick - film electrodes , a cut on the electrode surface will provide similar effect as an insulated line . the impedance is much higher inside the cut due to lower conductivity of electrolyte , which will force current flow through the edge of the cut . fig2 depicts a spherical view of an electrode with micro sticks / posts . first a sputtered metal layer 1 is provided , then micro stick / post 2 are produced and finally the gabs are filled in by polymer such as pdms or epoxy wherein a plated soft low stress layer 3 is provide . the process is shown in fig3 and in fig5 . thin - film techniques can &# 39 ; t provide enough electrode materials on the electrode surface for chronic stimulation . by electroplating a layer of electrode material on sputtered metal layer increases array &# 39 ; s life time to several folds . however , normal electroplating technique presents stress problem that limited the plated layer to & lt ; 1 μm . 2 - 3 μm thick of metal layer is successfully plated on thin - film pt electrode with disk opening up to 500 μm . micro sticks of au and pt can be plated up to 25 μm . there are several methods to reduce stress in plated metal layer according to the present invention which include : 1 . optimizing plating conditions to increase plated layer to 4 - 5 μm : surface pre - treatment ( include cleaning or surface modification , redox status ), surfactant , solution concentration , complex compounds , temperature , ph , stirring , current or voltage control ( amplitude , waveform and frequency ), or gas purge . 2 . plating micro sticks with dense structure on the electrode surface as support structure , then plate a porous and loose layer with low stress to cover the electrode surface . 3 . plating 2 - 3 μm thick of metal layer , then sputtering a mesh ( or grid ) of ti to fix or hold the plated layer . repeating above step until desired thickness ( layer ) is obtained . each plated layer will be softer than the layer below . top layer can be a porous material such as pt black . 4 . add grids of polyimide on sputtered pt surface . then plate soft pt on sputtered surface . the polyimide grids will separate or isolate plated surface and reduce stress . materials for sticks can be same as or different from plated surface layer . for example , stick is dense pt and plated layer is pt black ; or stick is pt and plated layer is irox ; support mesh grid can be metal or polymer , such as ti or polyimide . the metal for electroplating the posts can be pt , ir , au , ru , pd , or alloys thereof . fig3 depicts a process scheme for manufacturing electroplated sticks / posts 3 and polymer filling 2 . in particularly six steps of the process are shown . in step i a thin film 5 of pt , ir , au , ru , pd , or alloys thereof is applied by sputtering on a substrate 4 . in step ii a polymer 6 covering the edge of the electrode is applied . in step iii a photoresist layer 7 is applied and a patterning by mems is performed whereby holes 8 are created . the holes 8 are filled with electroplated metal 9 like pt in step iv . in step v the photoresist 7 is removed leaving spaces 10 between the metal sticks or posts 9 . the spaces 10 between the sticks are filled with polymer 11 adhesive such as pdms or epoxy in step vi . the obtained electrode is the electrode shown in fig2 with micro stocks fig4 a depicts a sem imaging (× 850 ) of polymer surface with patterned holes 8 before pt plating 9 as shown in step iii . fig4 b depicts a sem imaging (× 850 ) of polymer surface with patterned holes after pt plating 9 as shown in step iv . fig5 depicts a process scheme for manufacturing electroplated sticks / posts 3 and polymer filling 2 . in particularly three steps of the process are shown . in step i to be seen as cross sectional view and top view a thin film 5 of pt , ir , au , ru , pd , or alloys thereof is applied by sputtering on a substrate 4 . in step ii a polymer 6 covering the edge of the electrode is applied and is patterned whereby holes 8 are created . the holes 8 are filled with electroplated metal 9 like pt in step iii . the obtained electrode is the electrode shown in fig2 with micro sticks 3 and polymer 6 in the spaces . fig6 depicts a spherical view of an electrode with mesh grid as fixture . first a sputtered metal layer 11 is provided , then a low stress layer 22 is plated and a grid is obtained and filled with a polymer like polyimide , silicone , peek or parylene , or mixtures thereof or metal pt , ir , au , ru , pd , or alloys thereof to create a mesh grid 23 . the steps can be repeated to apply a second low stress layer 32 which is plated and a grid is obtained and filled with a polymer like polyimide , silicone , peek or parylene , or mixtures thereof or metal pt , ir , au , ru , pd , or alloys thereof to create a mesh grid 33 are produced and finally the gabs are filled in by polymer such as pdms or epoxy wherein a plated soft low stress layer 3 is provide . the process is shown in fig3 and in fig5 . fig7 depicts an electrode with polymer rings as fixture . this is an alternative to the mesh grid as shown in fig6 . the rings can be polymer rings or exposed metal . a multi - ring electrode is achieved by selectively insulating a conductive pad in a appropriate pattern concentric rings such as to leave exposed concentric rings of metal in between successively larger isolation rings . novel design feature are small circles radially patterned in the metal pad exposing the substrate material . these circles serve as anchor points for the adhesion of the insulation rings to the substrate . fig8 depicts an electrode array with different shapes of fixtures . circle shapes , star shapes , square shapes and rings are shown in the electrode array . each of the shapes contains overlapping edges and mesh grids . this presents a series of new electrode geometries that control charge transfer characteristics by the strategic use of edges and corners to concentrate current delivery . these designs are an improvement on conventional surface electrode designs which are typically circles . the present invention will be further explained in detail by the following example . 0 . 3 g sodium dihydrogen phosphate ( nah 2 po 4 ) and 6 . 03 g disodium hydrogen phosphate ( na 2 hpo 4 ) [ fluka ] were dissolved in 100 ml deionized water , and stirred by magnetic stirring for 30 minutes . the concentrations for nah 2 po 4 and na 2 hpo 4 were 25 mm and 425 mm . then 0 . 5 g of platinum chloride ( ptcl 4 ) [ alfa aesar ] was added to the phosphate solution to form the platinum salt concentrations of 15 mm . the solution was then stirred for 30 minutes . different concentrations of ( ptcl 4 ) were used in the experiments and the range of pt salt concentrations was from 3 to 30 mm . the ph of the solution was measured at 7 . 9 . the color of the solution was amber . the solution was deaerated before the plating process by bubbling nitrogen through the solution . a thin - film platinum polyimide array was used for platinum plating . the array included 16 electrodes with 200 μm thin - film pt disk as exposed electrode surface . all the electrodes in the array were shorted to common contact points for the plating . the pt disk electrodes were first electrochemically cleaned by bubbling the surface with oxygen at + 2 . 8v vs ag / agcl in 0 . 5 m h 2 so 4 for 10 sec . then the surface was cleaned by bubbling with hydrogen at − 1 . 2 v vs ag / agcl in 0 . 5 m h 2 so 4 for 15 sec to remove surface contaminations and polymer residues . a classical pyrex glass three - electrode reaction cell was used for the electroplating . the reference electrode compartment was separated from the reaction compartment by a vicor porous frit , in order to avoid the migration of concentrated kcl and agcl from the inner filling solution of the reference electrode to the plating bath . the counter electrode was a platinized - platinum sheet of a real surface area equal to 1 . 8 cm 2 . a digital magnetic stirrer ( dataplate pmc720 ) was used to agitate the solution during plating . the solution temperatures were from 15 ° c . to 80 ° c . and were controlled by a vwr circulating water bath with a digital temperature controller ( vwr 1147p ). the potential was controlled by using an eg & amp ; g parc model 273 potentiostat - galvanostat and the response current , current density and charge were recorded by eg & amp ; g parc m270 software . the charge / charge density and average plating current / current density were calculated by integrating the area under the plating current vs . time curve . the plating time was from 1 minute to 60 minutes . a platinum polyimide electrode array having 16 electrodes ( fig1 ) having a diameter of 200 μm platinum disc on the array was cleaned electrochemically in 0 . 5 m h 2 so 4 . the electrode array was placed in an electroplating cell containing a plating solution having a concentration of 15 mm platinum chloride in 0 . 025 m sodium dihydrogen phosphate and 0 . 425 m disodium hydrogen phosphate . the plating bath temperature was at 22 ° c . a constant voltage of − 0 . 525 v vs ag / agcl reference electrode was applied on the electrode and terminated after 10 minutes . the electrode array was thoroughly rinsed in deionized water . the charge / charge density and average plating current / current density were calculated by integrating the area under the plating current vs . time curve . the current density was near linearly increased from initial 11 . 1 a / cm 2 to final 15 . 2 a / cm 2 . the electrochemical capacitance of the electrode array with the surface coating of rough platinum was 1462 μf / cm 2 , measured in a 10 mm phosphate buffered saline solution . the thin - film pt disks only have an average capacitance of less than 20 μf / cm 2 before plating measured at the same condition . the optimal voltage drop across the electrodes for producing rough platinum was from − 0 . 4 to − 0 . 7 volts vs . ag / agcl reference electrode . the plated platinum surface coating thickness is about 3 . 5 μm . the electrochemical active surface area increase is about 73 fold . the relation of surface area to the thickness of the platinum surface coating is 4 . 18 f / cm 3 [ surface coating of rough platinum 1462 μf / cm 2 per thickness of the platinum coating of 3 . 5 μm .] the platinum surface coating adhesive strength was 55 mn . on a glass substrate , a 5 μm polyimide was spin coated on . a thin - layer pt (˜ 5000 a ) is sputtered then coated with polyimide having a thickness of about 5 μm with openings ranged from 30 μm to 400 μm . on each sample , 16 such openings are exposed as electrode surfaces for plating . a photoresist mask is coated on these electrode openings with some holes patterned . the electrode sample was electrochemically cleaned in 0 . 5 m sulphric acid by applying a dc voltage to cause water hydrolysis . then the sample was rinsed with di water thoroughly . 150 ml glass beakers are used as the electroplating cell . a large surface area pt sheet was used as a common electrode ( anode ). the reference electrode was an ag / agcl electrode ( silver - silver chloride electrode ). about 100 ml of 18 mm ammonium hexachloroplatinate in phosphate buffer solution was used to plating pt . arrange the electrode in the test cell , so that the plating electrode ( cathode ) is in parallel with the common electrode ( anode ). the reference electrode is positioned beside the cathode . add the plating solution with specified concentration . turn on the magnetic stirrer . the solution agitation is controlled by a magnetic stirrer ( vwr thermolyne cimarec 1 ). the typical plating temperature was about 24 - 26 ° c . a voltage waveform ( 1 ms pulse width square wave ) is generated by hp 33120a arbitrary waveform generator , which is converted to current signal through a fhc isolator . the pulse current is a square wave at 500 hz with a 1 ms pulse width . apply this pulse current on the plating electrode vs anode . the electrode voltage vs ag / agcl reference electrode is monitored using an oscilloscope ( tektronix tds3014b oscilloscope ). the current amplitude was adjusted so that the cathodic peak voltage reaches about − 0 . 6v vs ag / agcl reference electrode . during plating , the electrode voltage tends to decrease with plating time . the current amplitude is frequently adjusted so that the electrode voltage is kept within − 0 . 5 to − 0 . 7 v range vs ag / agcl reference electrode . when specified plating time is reached , terminate the current pulse . rinse the cathode in di water thoroughly . the photoresist mask was dissolved in solvent to leave electroplated pt posts exposed on the thin film metal surface . the plated samples are profiled to measure the height of the plated posts . the plated posts have a height of 8 μm , ranging from 4 to 25 μm . the gaps around the pt posts were then filled with a layer of pdms or polyimide . the final sample was examined under a microscope . after plating , the current amplitudes are averaged for the whole plating time . it is found that the charge density increases exponentially with sample opening decrease . the smaller the sample openings , the higher the charge density required . accordingly , what has been shown is an improved flexible circuit with an electronics control unit attached thereto , which is suitable for implantation in living tissue and to transmit electrical impulses to the living tissue . obviously , many modifications and variations of the present invention are possible in light of the above teachings . it is therefore to be understood that , within the scope of the appended claims , the invention may be practiced other than as specifically described .
an implantable electrode with increased stability having a clustered structure wherein the surface of the electrode is covered with a material comprising openings which are filled with sticks or posts . an implantable electrode with increased stability wherein the surface is of the electrode comprises mesh grids which are filled with sticks which are filed with a conducting or insulating material . a method of manufacturing an electrode with increased stability , comprising : depositing a metal layer on an base layer ; applying photoresist layer on the metal layer ; patterning the photoresist layer providing openings ; electroplating the openings with metal ; removing the photoresist layer leaving spaces ; and filling the spaces with polymer . a method of manufacturing an electrode with increased stability , comprising : depositing a metal layer on an base layer ; applying a polymer layer on the metal layer ; applying photoresist layer on the polymer layer ; patterning the photoresist layer providing openings ; electroplating the openings with metal ; and removing the photoresist layer .