referring to fig1 a and 1b , a stent 16 includes a generally tubular body 18 defining a lumen 20 . generally tubular body 18 is formed of bands 22 that are connected by struts 24 . as shown , both bands 22 and struts 24 include electrically conductive bioerodible portions 26 and non - bioerodible portions 28 , which enhance the mechanical characteristics of stent 16 . since portions 26 and portions 28 are electrically conductive , they form electrically conductive loops , such as the electrically conductive loop 29 shown in fig1 c . these electrically conductive loops can adversely affect the mri compatibility of stent 16 . however , by removing bioerodible portions 26 at a selected time after stent 16 has been implanted , stent 16 is capable of providing both mechanical performance and mri compatibility . as noted above , the presence of electrically conductive loops in a stent can adversely affect the mri - compatibility of the stent . without wishing to be bound by theory , it is believed that when a stent with electrically conductive loops is exposed to mri , the electrically conductive loops can conduct a current that limits the visibility of material within the lumen of the stent . specifically , during mri , an incident electromagnetic field is applied to a stent . the magnetic environment of the stent can be constant or variable , such as when the stent moves within the magnetic field ( e . g ., from a beating heart ) or when the incident magnetic field is varied . when there is a change in the magnetic environment of the stent , which can act as a coil or a solenoid , an induced electromotive force ( emf ) is generated , according to faraday &# 39 ; s law . the induced emf in turn can produce an eddy current that induces a magnetic field that opposes the change in magnetic field . the induced magnetic field can interact with the incident magnetic field to reduce ( e . g ., distort ) the visibility of material in the lumen of the stent . a similar effect can be caused by a radiofrequency pulse applied during mri . thus , the ability to use mri to view and assess the condition of a target site that includes a stent such as stent 16 can be limited . fig2 a shows stent 16 when the stent is disposed within a lumen 50 ( e . g ., an artery ) of a subject . stent 16 can be delivered to lumen 50 and expanded within lumen 50 using , for example , a stent delivery system such as a balloon catheter system . catheter systems are described in , for example , wang , u . s . pat . no . 5 , 195 , 969 , and hamlin , u . s . pat . no . 5 , 270 , 086 . stents and stent delivery are also exemplified by the radius ® or symbiot ® systems , available from boston scientific scimed , maple grove , minn . the shape and structure of stent 16 can allow the stent to be delivered into lumen 50 relatively easily . stent 16 has a somewhat symmetrical tubular shape , allowing it to be loaded onto a delivery device relatively easily , and a relatively low profile , allowing it to be navigated through lumen 50 relatively easily . as described above , the electrically conductive loops in stent 16 limit the mri visibility of material within lumen 20 of stent 16 . however , the generally tubular and somewhat symmetrical structure of stent 16 provides good support for lumen 50 , and uniformly transfers stress away from lumen 50 . furthermore , over time , tissue from wall 51 of lumen 50 can grow over stent 16 , effectively anchoring stent 16 into lumen 50 . referring now to fig2 b , as times passes , the body erodes and / or absorbs bioerodible portions 26 of stent 16 . eventually , this erosion and / or absorption causes electrical discontinuities 52 to form in bands 22 . in some embodiments , breathing can place a repeated stress on the stent that can contribute to the formation of electrical discontinuities 52 by causing bioerodible portions 26 to break . electrical discontinuities 52 break the electrically conductive loops in stent 16 by disrupting the flow of electrical current through bands 22 . as the number of electrically conductive loops in stent 16 decreases , the occurrence of an eddy current in stent 16 is reduced ( e . g ., eliminated ). accordingly , the occurrence of an induced magnetic field that can interact with the incident magnetic field is also reduced . as a result , the mri visibility of material in the lumen of stent 16 can increase . at the same time , the anchoring of stent 16 into lumen 50 by tissue from wall 51 limits the likelihood that stent 16 will collapse or significantly distort as the electrical discontinuities form . as a result , stent 16 continues to provide sufficient support for lumen 50 . in some embodiments , the formation of electrical discontinuities 52 in stent 16 may decrease the extent to which stent 16 shields lumen 50 from stress . however , this decrease in stress shielding can benefit lumen 50 by encouraging the lumen &# 39 ; s tissue to remodel and strengthen . as described above , stent 16 includes both bioerodible portions and non - bioerodible portions . the non - bioerodible portions of stent 16 can be formed of any mri - compatible biocompatible material , such as a non - ferromagnetic material . as an example , the non - bioerodible portions of stent 16 can be formed of one or more materials with a relatively low magnetic susceptibility . for example , the non - bioerodible portions of stent 16 can be formed of a material ( e . g ., a metal or a metal alloy ) with a magnetic susceptibility of less than 0 . 9 × 10 − 3 ( e . g ., less than 0 . 871 × 10 − 3 , less than 0 . 3 × 10 − 3 , less than − 0 . 2 × 10 − 3 ). in certain embodiments , stent 16 can include biocompatible material with a magnetic susceptibility that is lower than the magnetic susceptibility of stainless steel and / or nitinol . in some embodiments , a material with a relatively low magnetic susceptibility can be unlikely to move substantially and / or to experience a significant increase in temperature ( e . g ., a temperature increase of at least about 1 ° c .) as a result of being exposed to mri . the non - bioerodible portions of stent 16 can include a biocompatible material that can be used in a self - expandable stent , a balloon - expandable stent , or both . in embodiments in which stent 16 is a self - expandable stent , stent 16 can include a relatively elastic biocompatible material , such as a superelastic or pseudo - elastic metal alloy . such materials can cause stent 16 to be relatively flexible during delivery , thereby allowing stent 16 to be safely advanced through a lumen ( e . g ., through a relatively tortuous vessel ). alternatively or additionally , such materials can allow stent 16 to temporarily deform ( e . g ., upon experiencing a temporary extrinsic load ), and then regain its shape ( e . g ., after the load has been removed ), without experiencing a permanent deformation , which could lead to re - occlusion , embolization , and / or perforation of the lumen wall . examples of superelastic materials include a nitinol ( e . g ., 55 % nickel , 45 % titanium ), silver - cadmium ( ag — cd ), gold - cadmium ( au — cd ), gold - copper - zinc ( au — cu — zn ), copper - aluminum - nickel ( cu — al — ni ), copper - gold - zinc ( cu — au — zn ), copper - zinc ( cu — zn ), copper - zinc - aluminum ( cu — zn — al ), copper - zinc - tin ( cu — zn — sn ), copper - zinc - xenon ( cu — zn — xe ), indium - thallium ( in — tl ), nickel - titanium - vanadium ( ni — ti — v ), titanium - molybdenum ( ti — mo ), titanium - niobium - tantalum - zirconium ( ti — nb — ta — zr ), and copper - tin ( cu — sn ). see , e . g ., schetsky , l . mcdonald , “ shape memory alloys ”, encyclopedia of chemical technology ( 3rd ed . ), john wiley & amp ; sons , 1982 , vol . 20 . pp . 726 - 736 , for a full discussion of superelastic alloys . other examples of materials include one or more precursors of superelastic alloys , i . e ., those alloys that have the same chemical constituents as superelastic alloys , but have not been processed to impart the superelastic property under the conditions of use . such alloys are further described in pct application no . us91 / 02420 . in certain embodiments , stent 16 can include one or more materials that can be used for a balloon - expandable stent , such as noble metals ( e . g ., platinum , gold , palladium ), refractory metals ( e . g ., tantalum , tungsten , molybdenum , rhenium ), and alloys thereof . other examples of stent materials include titanium , titanium alloys ( e . g ., alloys containing noble and / or refractory metals ), vanadium alloys , stainless steels , stainless steels alloyed with noble and / or refractory metals , nickel - based alloys ( e . g ., those that contain platinum , gold , and / or tantalum ), iron - based alloys ( e . g ., those that contain platinum , gold , and / or tantalum ), cobalt - based alloys ( e . g ., those that contain platinum , gold , and / or tantalum ), aluminum alloys , zirconium alloys , and niobium alloys . for example , stent 16 can include titanium - tantalum ( ti — ta ), titanium - aluminum - vanadium - tantalum ( ti — al — v — ta ), titanium - iridium ( ti — ir ), titanium - rhenium ( ti — re ), titanium - tantalum - iridium ( ti — ta — ir ), titanium - tantalum - rhenium ( ti — ta — re ), and / or niobium - zirconium ( nb — zr ). metal alloys are described , for example , in u . s . ser . no . 10 / 672 , 891 , filed on sep . 26 , 2003 , and entitled “ medical devices and methods of making same ”. in some embodiments , stent 16 can include one or more radiopaque materials ( e . g ., metals , metal alloys ), which can cause stent 16 to be visible using x - ray fluoroscopy ( e . g ., allowing stent 16 to be tracked as it is delivered to a target site ). examples of radiopaque materials include metallic elements having atomic numbers greater than 26 ( e . g ., greater than 43 ), and / or those materials having a density greater than about eight grams per cubic centimeter ( e . g ., greater than about 9 . 9 grams per cubic centimeter , at least about 25 grams per cubic centimeter , at least about 50 grams per cubic centimeter ). in some embodiments , a medical device can include a material ( e . g ., a metal , a metal alloy ) with a magnetic susceptibility of less than 0 . 9 × 10 − 3 and a density of greater than about eight grams per cubic centimeter . for example , a medical device can include platinum , tantalum , palladium , and / or molybdenum . in certain embodiments , a radiopaque material can be relatively absorptive of x - rays . for example , the radiopaque material can have a linear attenuation coefficient of at least 25 cm − 1 ( e . g ., at least 50 cm − 1 ) at 100 kev . examples of radiopaque materials include tantalum , platinum , iridium , palladium , tungsten , gold , ruthenium , niobium , and rhenium . the radiopaque material can include an alloy , such as a binary , a ternary or more complex alloy , containing one or more elements listed above with one or more other elements such as iron , nickel , cobalt , or titanium . the radiopaque material can , for example , be more radiopaque than stainless steel . in some embodiments , the radiopaque material can be more radiopaque than iron and / or nitinol . the bioerodible portions of stent 16 ( e . g ., portions 26 ) can be formed of one or more bioerodible materials , such as bioerodible metals and bioerodible metal alloys . examples of bioerodible metal alloys include metal alloys that have at least one metal selected from the group of alkali metals , alkaline earth metals , iron , zinc , or aluminum . in some embodiments , a bioerodible metal alloy can include at least one metal selected from magnesium , titanium , zirconium , niobium , tantalum , zinc , and silicon , and / or at least one metal selected from lithium , sodium , potassium , manganese , calcium , and iron . for example , a bioerodible metal alloy can be a lithium - magnesium alloy , a sodium - magnesium alloy , or a zinc - calcium alloy . other examples of bioerodible metal alloys include zinc - titanium alloys ( e . g ., zinc - titanium alloys including from about 0 . 1 percent by weight to about one percent by weight titanium , zinc - titanium - gold alloys including from about 0 . 1 percent by weight to about two percent by weight gold ). in some embodiments , a bioerodible metal alloy can include cobalt , nickel , chromium , copper , cadmium , lead , tin , thorium , silver , gold , palladium , platinum , rhenium , carbon , and / or sulfur . bioerodible materials are described , for example , in bolz et al ., u . s . pat . no . 6 , 287 , 332 , and u . s . patent application publication no . us 2002 / 0004060 a1 , published on jan . 10 , 2002 . in certain embodiments , bioerodible portions 26 can include a metal or a metal alloy capable of interacting with the material of non - bioerodible portions 28 such that the metal or metal alloy of bioerodible portions 26 selectively corrodes . for example , the material of bioerodible portions 26 can have a higher oxidation potential than the material of non - bioerodible portions 28 , such that upon exposure to the electrolytic environment of the body , bioerodible portions 26 can galvanically corrode . examples of combinations of materials include iron and copper ; tantalum and iron ; platinum and iron ; tantalum and magnesium ; platinum and magnesium ; tantalum and aluminum ; platinum and aluminum ; and copper and stainless steel . the erosion and / or absorption of bioerodible portions 26 of stent 16 , and the corresponding formation of electrical discontinuities 52 , can occur over a length of time that allows stent 16 to be delivered to a target site and expanded before a significant number of electrical discontinuities have been formed ( e . g ., before any electrical discontinuities have been formed ). in some embodiments , one or more bioerodible portions 26 of stent 16 can be eroded and / or absorbed over a period of at least about one week ( e . g ., at least about two weeks , at least about three weeks , at least about one month , at least about two months , at least about three months , at least about four months , at least about five months , at least about six months , at least about seven months , at least about eight months ), and / or at most about nine months ( e . g ., at most about eight months , at most about seven months , at most about six months , at most about five months , at most about four months , at most about three months , at most about two months , at most about one month , at most about three weeks , at most about two weeks ). stent 16 can be of any desired shape and size ( e . g ., a coronary stent , an aortic stent , a peripheral vascular stent , a gastrointestinal stent , a urology stent , a neurology stent ). depending on the application , stent 16 can have an expanded diameter of , for example , from about one millimeter to about 46 millimeters . in certain embodiments , a coronary stent can have an expanded diameter of from about 1 . 5 millimeters to about six millimeters ( e . g ., from about two millimeters to about six millimeters ). in some embodiments , a peripheral stent can have an expanded diameter of from about four millimeters to about 24 millimeters . in certain embodiments , a gastrointestinal and / or urology stent can have an expanded diameter of from about six millimeters to about 30 millimeters . in some embodiments , a neurology stent can have an expanded diameter of from about one millimeter to about 12 millimeters . an abdominal aortic aneurysm ( aaa ) stent and a thoracic aortic aneurysm ( taa ) stent can have an expanded diameter from about 20 millimeters to about 46 millimeters . stent 16 can be balloon - expandable , self - expandable , or a combination of both ( e . g ., andersen et al ., u . s . pat . no . 5 , 366 , 504 ). while a stent with bioerodible portions has been described , in some embodiments , as an alternative to or in addition to bioerodible portions , a stent can include one or more other types of weak regions . the weak regions can include , for example , one or more notches , slots , holes , thinned areas , grooves , and / or chamfers . the weak regions can be formed , for example , in a band and / or strut of the stent . over time , strain on these weak regions ( e . g ., as a result of vessel pressure pulsation or peristalsis ) can result in metal fatigue , which can eventually cause the weak regions to break apart . alternatively or additionally , the weak regions can be mechanically broken apart . for example , after a stent has been implanted at a target site and a desired amount of time ( e . g ., six months ) has passed , a balloon can be inserted into the stent ( e . g ., using a balloon catheter ) and expanded until the weak regions break . as an example , fig3 a shows a portion of a stent 100 that includes a band 102 with a weak region 104 formed of two hemispherical notches 106 and 108 . after stent 100 has been delivered to a target site , it can be expanded . this expansion can bend and / or stretch the stent , further weakening weak region 104 . after a certain amount of time , weak region 104 can break , thereby forming an electrical discontinuity in band 102 . in certain embodiments , weak region 104 may be further weakened or broken by other methods , such as exposure of weak region 104 to ultrasound , or additional expansion of stent 100 ( e . g ., by a balloon ). in some embodiments , the environment of the target site , such as the pressure of blood flow through the target site , can cause weak region 104 to break . other types of weak regions can be used . as an example , fig3 b shows a portion of a stent 150 that has a band 152 with a weak region 154 including a hole 156 . in certain embodiments , hole 156 can be filled with a bioerodible material that can erode upon delivery of stent 150 to a target site . the bioerodible material can , for example , temporarily enhance the strength of weak region 154 during delivery to the target site . as another example , fig3 c shows a portion of a stent 200 including a band 202 with a weak region 204 formed out of two v - shaped notches 206 and 208 . as an additional example , fig3 d shows a portion of a stent 250 that includes a band 252 with a weak region 254 formed out of two grooves 256 and 258 . as a further example , fig3 e shows a portion of a stent 300 that includes a band 302 with a weak region 304 including a slot ( a relatively long narrow opening ) 306 . as another example , fig3 f and 3 g show a portion of a stent 350 that includes a band 352 with a weak region 354 formed out of chamfers 356 , 357 , 358 , and 359 . in some embodiments , a weak region of a stent can include an oxide ( e . g ., a metal oxide ). for example , a weak region of a stent can include an oxide layer . in certain embodiments , an oxide layer can be formed in a region of a stent by selectively enriching the region of the stent with oxygen . for example , a localized region of a metal stent ( e . g ., a section of a strut ) can be isolated by covering other regions of the stent with a protective layer . the metal stent can include , for example , tantalum , niobium , titanium , and / or molybdenum . after a localized region of the stent has been isolated , the stent can be heated ( e . g ., at a temperature of from about 300 ° c . to about 800 ° c .) in an atmosphere that includes oxygen , such that the localized region of the stent is oxidized . thereafter , the protective layer can be removed from the stent ( e . g ., by dissolution ). other methods can be used to form an oxide layer on a stent . as an example , a metal stent can be heated ( e . g ., at a temperature of from about 300 ° c . to about 800 ° c .) in an atmosphere that includes oxygen , such that the entire stent surface is oxidized . thereafter , certain regions of the stent can be covered with a protective layer , and the oxide layer on the stent can be removed from the regions of the stent that are not covered by the protective layer . the oxide layer can be removed , for example , by dissolution ( e . g ., electropolishing ) and / or chemical etching ( e . g ., chemical milling ). after the oxide layer has been removed from the unprotected regions of the stent , the protective layer can be removed from the stent , revealing the regions of the stent that still have an oxide layer . as another example , an oxide layer can be formed on a selected region of a stent by treating that region of the stent with a laser in the presence of a fluid or a gas that includes oxygen . in certain embodiments , an oxide layer can be formed by an anodization process . anodization is described , for example , in u . s . ser . no . 10 / 664 , 679 , filed on sep . 16 , 2003 , and entitled “ medical devices ”. in certain embodiments , one or more regions of a stent can be weakened and / or embrittled by selectively exposing the regions to hydrogen and / or nitrogen ( e . g ., using one or more of the methods described above with reference to forming an oxide layer on a selected region of a stent ). exposure of a region of a stent to hydrogen can result in the formation of a hydride that weakens the region , and exposure of a region of a stent to nitrogen can result in the formation of a nitride that weakens the region . in some embodiments , a weak region in a metal stent can include carbide particles . the carbide particles can be added to the stent by , for example , melting the stent material and adding solid carbon to the stent material in its melted state , and / or heat - treating the stent material in a gaseous atmosphere containing carbon ( e . g ., co , co 2 ). in certain embodiments , a weak region in a stent can include a carbide layer . a carbide layer can be formed on a metal stent by , for example , heat - treating the stent material in a gaseous atmosphere containing carbon . alternatively or additionally , a carbide layer can be formed on a metal stent by a pack diffusion process , in which the stent material is contacted with a carbon - containing solid material , so that carbon diffuses in the solid state from the carbon - containing solid material into the stent material . pack diffusion is described , for example , in asm handbook vol . 4 : heat treating ( asm international , 1991 ), pages 325 - 328 . in certain embodiments during the formation of an oxide , hydride , nitride , or carbide weak region , any of the above - described processes can be monitored to ensure that the oxide , hydride , nitride , or carbide does not extend too deeply into the stent material . in some embodiments , tests can be performed to determine the desirable depth to which an oxide , hydride , nitride , or carbide layer should be formed . for example , different thicknesses of oxide , hydride , nitride , and / or carbide layers can be formed on coupons of a metal stent material that have the same thickness as a metal stent strut . testing can then be performed on the coupons to measure the yield strength and elongation at fracture . the results of the testing can be evaluated in light of the extent of strain a stent strut is expected to experience while in service . the coupon that produces a fracture within that strain value can be selected . for example , if the stent strain limit during expansion is 30 percent , an oxide , hydride , nitride , or carbide layer depth that produces localized fracture at 20 percent strain can be selected . in some embodiments , there can be a difference between the strut strain upon expansion and the strut strain when the fracture occurs , such that the fracture faces move apart from each other as the stent continues to strain beyond the value at which the fracture occurs . separation between the fracture faces can , for example , provide a gap that is sufficient to avoid electrical conductivity between the two fracture faces . in some embodiments , a weak region can be formed on a metal stent ( e . g ., a stent including tantalum , niobium , titanium , molybdenum ) by forming a brittle intermetallic phase on the stent . the intermetallic phase can include , for example , niobium and rhenium ( e . g ., from 45 percent by weight to 65 percent by weight rhenium ), niobium and rhodium ( e . g ., from 28 percent by weight to 38 percent by weight rhodium ), niobium and silicon , or titanium and zinc ( e . g ., more than about five percent by weight zinc ). in certain embodiments , an intermetallic phase can be formed by applying a second metal ( e . g ., rhenium , rhodium , silicon ) to a localized area of a metal ( e . g ., niobium ) stent in solid form , and then heating the second metal to allow it to diffuse into the metal stent and form the brittle phase . the second metal can be applied to the stent by , for example , adhering metal powder to the localized region ( e . g ., a strut ) of the stent . the above - described stents can be formed by any of a number of different methods . in some embodiments , a weak region ( e . g ., a notch , a hole ) can be formed in a stent by laser cutting ( e . g ., using an excimer laser and / or an ultrashort pulse laser ). laser cutting is described , for example , in saunders , u . s . pat . no . 5 , 780 , 807 , and weber , u . s . pat . no . 6 , 517 , 888 . other methods of forming a weak region include mechanical machining ( e . g ., micro - machining ), electrical discharge machining ( edm ), photoetching ( e . g ., acid photoetching ), and / or chemical etching . in certain embodiments , a weak region can be formed in a stent by bending and / or twisting the material ( e . g ., metal ) used to form the stent prior to forming the stent . in embodiments in which a stent includes one or more bioerodible portions , the bioerodible portions can be formed by cutting the stent using one of the above - described methods to form a discontinuity , and filling the discontinuity with a bioerodible material . the bioerodible material can be bonded to the stent by , for example , an adhesive ( e . g ., acrylic , cyanoacrylate , epoxy , polyurethane ). alternatively or additionally , the bioerodible material can be bonded to the stent using ultrasonic welding , laser welding , ultraviolet bonding , and / or heat bonding . in certain embodiments , the bioerodible material can be bonded to the stent by suspending the bioerodible material in a substrate ( e . g ., styrene - isobutylene - styrene ) that is attached to and / or coated on the stent . in some embodiments , a stent can further be finished ( e . g ., electropolished ) to a smooth finish , according to conventional methods . in certain embodiments , at least about 0 . 0001 inch ( e . g ., about 0 . 0005 inch ) of material can be removed from the interior and / or exterior surfaces of a stent by chemical milling and / or electropolishing . in some embodiments , a stent can be annealed at predetermined stages to refine the mechanical and physical properties of the stent . as an example , in some embodiments , an electrical discontinuity can be formed in a portion of a medical device by contacting the portion with an agent that dissolves the portion to form the electrical discontinuity . for example , a stent can be implanted and expanded at a target site , and thereafter , an agent can be injected in to the target site to dissolve one or more regions of the stent . in some embodiments , the environment of a stent ( e . g ., after delivery to a target site ) can cause one or more weak regions of the stent to dissolve . for example , one or more weak regions of a stent that has been delivered into the digestive tract may dissolve because of the relatively low ph of the region . in such embodiments , the weak region ( s ) of the stent may include a metal ( e . g ., magnesium , aluminum ), and / or a polymer . as an additional example , in certain embodiments , an electrical discontinuity can be formed in a portion of a medical device by heating the portion . for example , after the medical device has been delivered to a target site and expanded , the portion of the medical device can be heated ( e . g ., using an ablative laser ) to melt the portion and form an electrical discontinuity . in some embodiments , the portion may have a lower melting point than other regions of the stent , such that , when exposed to heat , the portion begins to melt before the other regions of the stent . as another example , in some embodiments , an electrical discontinuity can be formed in a portion of a medical device by cooling / freezing the portion . for example , after the medical device has been delivered to the target site and expanded , the portion of the medical device can be cooled / frozen . in some embodiments , the portion can be cooled / frozen using a cryo - balloon ( a balloon that is filled with liquid nitrous oxide ). the cooling / freezing of the portion can result in temperature - induced brittleness in the portion . thus , the portion can break from strain caused , for example , by changes in artery shape due to heart beating and / or respiration . examples of materials that can demonstrate brittleness at low temperatures include polymers , tantalum containing about 700 ppm oxygen or less , unrecrystallized molybdenum , and plain carbon and low alloy steels . as a further example , in some embodiments , a weak region of a medical device can be formed out of a metal that has a relatively small grain size ( e . g ., less than about 45 microns ), such that when the weak region breaks , it is relatively unlikely to form jagged and / or sharp edges . examples of materials with relatively small grain sizes include tantalum , niobium , and titanium . in some embodiments , a material with a relatively small grain size can have a grain size of about 7 . 0 or more according to astm standard e112 ( e . g ., astm e112 g of from 7 . 0 to 9 . 0 ). in certain embodiments , the grain size of a material can be varied by , for example , localized treatment of the material . for example , localized heat treatment of a stent including a metal or metal alloy ( e . g ., stainless steel ) can result in the metal stent having grain sizes ranging from 5 . 0 to 10 . 0 according to astm standard e112 . as an additional example , in certain embodiments , a weak region of a medical device can be formed out of a metal that has a relatively large grain size ( e . g ., astm e112 g of 1 . 0 - 3 . 0 ). in some cases , a region that is formed out of a metal with a relatively large grain size may be more likely to fracture at a lower strain value than a region with a relatively small grain size . as another example , in some embodiments , one of the above - described stents can be a part of a stent - graft . in certain embodiments , a stent can include and / or be attached to a graft including a biocompatible , non - porous or semi - porous polymer matrix made of polytetrafluoroethylene ( ptfe ), expanded ptfe , polyethylene , urethane , or polypropylene . as a further example , in some embodiments , a stent can include one or more releasable therapeutic agents , drugs , or pharmaceutically active compounds , such as anti - thrombogenic agents , antioxidants , anti - inflammatory agents , anesthetic agents , anti - coagulants , and antibiotics . for example , in embodiments in which the stent includes or more bioerodible portions , the bioerodible portions can include one or more therapeutic agents , drugs , or pharmaceutically active compounds . therapeutic agents , drugs , and pharmaceutically active compounds are described , for example , in phan et al ., u . s . pat . no . 5 , 674 , 242 ; weber , u . s . pat . no . 6 , 517 , 888 ; u . s . patent application publication no . us 2003 / 0003220 a1 , published on jan . 2 , 2003 ; and u . s . patent application publication no . us 2003 / 0185895 a1 , published on oct . 2 , 2003 . as an additional example , in some embodiments , one of the above - described stents can be coated . for example , the stent can be coated with a therapeutic agent , and can further be coated with a protective layer that is disposed over the therapeutic agent . coated stents are described , for example , in u . s . ser . no . 10 / 787 , 618 , filed on feb . 26 , 2004 , and entitled “ medical devices ”. as a further example , in some embodiments , one of the above - described stents can be used in a magnetic resonance angiography ( mra ) procedure . in such a procedure , the stent can be guided to an implantation site and implanted while being visualized with a magnetic - resonance scanner . in such embodiments , the stent can include one or more mri - compatible materials , and / or can have a design that is conducive to visualization using magnetic - resonance imaging . as an additional example , while stents including bioerodible metals and / or metal alloys have been described , in some embodiments , a medical device such as a stent can include other types of bioerodible materials . examples of other types of bioerodible materials include polysaccharides ( e . g ., alginate ); sugars ( e . g ., sucrose ( c 12 h 22 o 11 ), dextrose ( c 6 h 12 o 6 ), sorbose ( c 6 h 12 o 6 )); sugar derivatives ( e . g ., glucosamine ( c 6 h 13 no 5 ), sugar alcohols such as mannitol ( c 6 h 14 o 6 )); inorganic , ionic salts ( e . g ., sodium chloride ( nacl ), potassium chloride ( kcl ), sodium carbonate ( na 2 co 3 )); water soluble polymers ( e . g ., a polyvinyl alcohol , such as a polyvinyl alcohol that has not been cross - linked ); biodegradable poly dl - lactide - poly ethylene glycol ( pela ); hydrogels ( e . g ., polyacrylic acid , haluronic acid , gelatin , carboxymethyl cellulose ); polyethylene glycol ( peg ); chitosan ; polyesters ( e . g ., a polycaprolactone ); and poly ( lactic - co - glycolic ) acids ( e . g ., a poly ( d - lactic - co - glycolic ) acid ). bioerodible materials are described , for example , in u . s . ser . no . 10 / 787 , 618 , filed on feb . 26 , 2004 , and entitled “ medical devices ”. as another example , in certain embodiments , a weak region of a stent can be broken via electrolytic disintegration . when the stent is exposed to mri , a current can flow through the stent , as described above . in some embodiments , as the current flows through the weak region of a stent , the current can cause the weak region to electrolytically disintegrate , thereby forming an electrical discontinuity that prevents the current from being able to travel in a continuous loop . electrolytic disintegration is described , for example , in guglielmi et al ., u . s . pat . no . 5 , 895 , 385 . as a further example , in some embodiments , one or more regions of a stent can be broken by exposing the stent to an ultrasonic frequency that corresponds to a natural harmonic frequency of the stent structure , resulting in stent fracture . all publications , applications , references , and patents referred to in this application are herein incorporated by reference in their entirety .
medical devices , such as stents , and methods of making the devices , are described . in some embodiments , the invention features a medical device that includes a member having a first portion and a second portion that define an electrically conductive loop . the first portion is adapted to break or erode after expansion of the medical device , and the second portion is not adapted to break or erode after expansion of the medical device . the breaking or erosion of the first portion breaks the electrically conductive loop .