METHOD FOR MEASURING BIREFRINGENCE TEMPERATURE DEPENDENCE OF ADHESIVE, METHOD FOR DESIGNING AND MANUFACTURING ADHESIVE, ADHESIVE, DISPLAY, AND OPTICAL FILMThe present invention intends to provide a display, or an optical film with an adhesive, in which a bend of the display or peeling of the optical film does not occur even when the display or the optical film is used under an environment where a temperature change is large, and birefringence due to deformation of an adhesive can be suppressed stably irrespective of the temperature change, and occurrence of light leakage and the like is suppressed, so that the optical performance is more excellent, by pasting a glass plate and an optical film together with an adhesive in which temperature dependence of the birefringence is zero. The present invention relates to a technique for obtaining the above-described effects, the technique capable of stably providing an adhesive in which both the birefringence and the temperature dependence of the birefringence are zero, the adhesive having a measured value of birefringence of an adhesive Δn0 within a range of ±0.2×10?4 and having a temperature coefficient of the birefringence of an adhesive dΔn0/dT within a range of ±0.02×10?5/° C. The adhesive is utilized in a display having a structure obtained by pasting a transparent substrate and an optical film together through an adhesive layer, or is utilized in an adhesive layer of an optical film with an adhesive.A method for measuring temperature dependence of birefringence of an adhesive, the method comprising: a step of preparing a laminated film in which polymer films are used as supports, and an adhesive comprising a (meth)acrylate-containing acrylic-based copolymer and a hardener added to the acrylic-based copolymer is given between two sheets of the supports to form an adhesive layer;a step of hot-stretching the laminated film;a step of measuring retardation of the laminated film after the hot-stretching; anda step of measuring a thickness of the adhesive layer, wherein:birefringence of an adhesive for the adhesive is defined as a value obtained by dividing the retardation by the thickness;further, in the step of measuring the retardation, a temperature of the laminated film is controlled stepwise in a range of 15 to 70° C. to measure the retardation at each temperature, and from the obtained measurement results, a temperature coefficient of the birefringence of an adhesive dΔn0/dT is determined as an amount of change in the birefringence of an adhesive per 1° C. to quantify the temperature dependence of a birefringence value for the adhesive;the polymer films to be used as the supports for the adhesive, when uniaxially stretched, each have an intrinsic birefringence within a range of ±0.05×10?4, and the polymer films each have a temperature coefficient of the intrinsic birefringence dΔn0/dT within a range of ±0.005×10?5 between 25° C. to 60° C., the temperature coefficient determined as an amount of change in the intrinsic birefringence per 1° C. from measurement results obtained in such a way that the uniaxially stretched film is used, a temperature of the film is controlled stepwise in a range of 25° C. to 60° C. to measure the intrinsic birefringence Δn0 at each temperature; anda value of the birefringence of an adhesive at any temperature within a range of 15 to 70° C. for the adhesive to be used in quantifying the temperature dependence of the birefringence value for the adhesive is defined as a value obtained by dividing retardation measured with a birefringence measuring apparatus for a sample stretched to 2 times by the thickness of the adhesive layer, wherein the sample is prepared in such a way that the laminated film is cut into a dumbbell shape to make the sample, and the sample is mounted on a tensile testing machine with a thermostatic chamber, heated at a temperature of 102° C. for 120 seconds, thereafter stretched at a tension speed of 40 mm/min until a marked line becomes 2 times longer, then taken out after the stretching to be left to stand at room temperature for 24 hours, and thereafter further left to stand at any temperature within a range of 15 to 70° C. for 10 minutes.
점착제의 복굴절 온도 의존성의 측정방법, 점착제를 설계·제조하는 방법, 점착제, 디스플레이 및 광학필름유리판과 광학필름을 복굴절의 온도 의존성 제로의 점착제로 맞붙임으로써, 온도 변화가 큰 환경하에서 사용했다고 해도, 디스플레이의 휨이나 광학필름의 벗겨짐이 없고, 온도 변화에 의하지 않는 점착제의 변형에 기인한 복굴절을 안정되게 억제할 수 있어, 광 누락 등의 발생을 억제한 광학 성능에 의해 우수한 디스플레이나, 점착제 부착 광학필름을 제공하는 것을 목적으로 한다. 본 발명은, 상기한 효과를 얻기 위해, 투명 기판에 광학필름이 점착제층을 사이에 두고 맞붙여 이루어지는 구조를 가지는 디스플레이나, 점착제 부착 광학필름의 점착제층에 이용하는, 점착제 고유 복굴절(Δn0)의 측정치가, ±0.2×10－4의 범위 내에 있고, 또한, 점착제 고유 복굴절의 온도 계수(dΔn0/dT)가, ±0.02×10－5/℃의 범위 내에 있는 복굴절 및 복굴절 온도 의존성이 모두 제로의 점착제를, 안정되게 제공할 수 있는 기술에 관한 것이다.폴리머 필름을 지지체로서, 2매의 지지체 사이에 (메타)아크릴산 에스테르를 포함하는 아크릴계 공중합체에 경화제를 첨가하여 구성되어 이루어지는 점착제를 부여하여 점착제층을 형성한 적층 필름을 준비하는 공정과, 상기 적층 필름을 열 연신하는 공정과, 열 연신한 후의 적층 필름의 리타데이션(retardation)을 측정하는 공정과, 상기 점착제층의 두께를 측정하는 공정을 가지고, 상기 리타데이션을 상기 두께로 나눈 값을 상기 점착제의 점착제 고유 복굴절로 하고,또한, 상기 리타데이션을 측정하는 공정으로, 상기 적층 필름의 온도를 15∼70℃의 범위에서 단계적으로 제어한 상태에서, 개개의 온도에 있어서의 리타데이션을 측정하고, 얻어진 측정 결과로부터 1℃당 점착제 고유 복굴절의 변화량으로서 상기 점착제 고유 복굴절의 온도 계수(dΔn0/dT)를 구하여, 점착제의 복굴절치의 온도 의존성을 정량화하는 점착제 고유 복굴절의 온도 의존성의 측정방법에 있어서,상기 점착제의 지지체로서 이용하는 폴리머 필름이, 1축 연신했을 때의 고유 복굴절이 ±0.05×10－4의 범위 내에 있고, 또한, 상기 1축 연신 필름을 이용하여, 상기 필름의 온도를 25℃∼60℃의 범위에서 단계적으로 제어한 상태에서, 개개의 온도에 있어서의 고유 복굴절(Δn0)을 각각 측정하고, 얻어진 측정 결과로부터 1℃당 고유 복굴절의 변화량으로서 구한 25℃∼60℃에 있어서의 고유 복굴절 온도 계수(dΔn0/dT)가, ±0.005×10－5의 범위 내에 있는 것이며,상기 점착제의 복굴절치의 온도 의존성을 정량화할 때에 이용하는 상기 점착제의 15∼70℃의 범위 내의 어느 온도에 있어서의 점착제 고유 복굴절의 값을, 상기 적층 필름을 덤벨 형상(dumbbell shape)으로 잘라낸 샘플을, 항온조 부착 인장 시험기에 장착하고, 온도 102℃에서 120초간 가열 후, 인장 속도 40㎜/min로 표선이 2배가 될 때까지 연신하며, 연신 후에 꺼내 실온에 24시간 방치 후, 15∼70℃의 범위 내의 어느 온도로 10분간 두고 조정한 2배 연신한 샘플에 대하여, 복굴절 측정장치로 리타데이션을 측정하고, 상기 리타데이션을 상기 점착제층의 두께로 나눈 값으로 하는 것을 특징으로 하는 점착제의 복굴절 온도 의존성의 측정방법.