POLYPHENYLENE SULFIDE RESIN COMPOSITION AND METHOD FOR MANUFACTURING SAMEA polyphenylene sulfide resin composition including a polyphenylene sulfide resin (a) of 90 to 50% by weight and a polyphenylene sulfide resin (b) and/or a polyphenylene sulfide resin (c) of the total of 10 to 50% by weight blended with the polyphenylene sulfide resin (a), relative to the total of the polyphenylene sulfide resins (a) to (c) as 100% by weight, in which the polyphenylene sulfide resin composition has a change rate of viscosity of 1.5 times or less when the composition is heated at 320°C for 5 hours. Polyphenylene sulfide resin (a): a polyphenylene sulfide resin having a weight average molecular weight of 50,000 or more and having a weight reduction ratio ΔWr of 0.18% or less when the resin is heated, in which the ratio is represented by the below-mentioned Equation (1); Polyphenylene sulfide resin (b): a polyphenylene sulfide resin having a weight average molecular weight of less than 50,000 and an alkaline earth metal content of less than 200 ppm, and having an increase rate of molecular weight of 5.0% or less when the resin is heated at 320°C for 10 minutes together with 0.5% by weight 2-(3,4-epoxycyclohexyl)ethyltrimethoxysilane added thereto; Polyphenylene sulfide resin (c): a polyphenylene sulfide resin containing 200 to 800 ppm of an alkaline earth metal (d) and having a weight reduction ratio ΔWr of more than 0.18% when the resin is heated, in which the ratio is represented by the below-mentioned Equation (1): ΔWr = (W1 - W2) / W1 × 100(%) --- (1) (wherein ΔWr is a weight reduction ratio (%), which is a value determined from a sample weight (W1) at 100°C reached and a sample weight (W2) at 330°C reached in thermogravimetric analysis carried out under a non-oxidizing atmosphere at normal pressure at a temperature raising rate of 20°C/minute); A PPS resin composition that has a smaller viscosity change during melt residence and generates a smaller amount of gas when heated is provided.A polyphenylene sulfide resin composition comprising 90 to 50% by weight of a polyphenylene sulfide resin (a) and total of 10 to 50% by weight of a polyphenylene sulfide resin (b) and/or a polyphenylene sulfide resin (c) blended with the polyphenylene sulfide resin (a), relative to the total of the polyphenylene sulfide resins (a) to (c) as 100% by weight, wherein the polyphenylene sulfide resin composition has a change rate of viscosity of 1.5 times or less when the composition is heated at 320°C for 5 hours; wherein the polyphenylene sulfide resin (a) is a polyphenylene sulfide resin having a weight average molecular weight of 50,000 or more and having a weight reduction ratio ΔWr of 0.18% or less when the resin is heated, wherein the ratio is represented by the below-mentioned Equation (1); wherein the polyphenylene sulfide resin (b) is a polyphenylene sulfide resin having a weight average molecular weight of less than 50,000 and an alkaline earth metal content of less than 200 ppm, and having an increase rate of molecular weight of 5.0% or less when the resin is heated at 320°C for 10 minutes together with 0.5% by weight of 2-(3,4-epoxycyclohexyl)ethyltrimethoxysilane added thereto; and wherein the polyphenylene sulfide resin (c) is a polyphenylene sulfide resin containing 200 to 800 ppm of an alkaline earth metal (d), and has a weight reduction ratio ΔWr of more than 0.18% when the resin is heated, wherein the ratio is represented by the below-mentioned Equation (1): ΔWr=W1−W2/W1×100% (wherein ΔWr is a weight reduction ratio (%), which is a value determined from a sample weight (W1) at 100°C reached and a sample weight (W2) at 330°C reached in thermogravimetric analysis carried out under a non-oxidizing atmosphere at normal pressure at a temperature raising rate of 20°C/minute).
폴리페닐렌술피드 수지 조성물 및 그 제조 방법폴리페닐렌술피드 수지 (a) 내지 (c)의 합계를 100중량％로 했을 때에, 폴리페닐렌술피드 수지 (a) 90 내지 50중량％에 대하여, 폴리페닐렌술피드 수지 (b) 및/또는 폴리페닐렌술피드 수지 (c)를 합계로 10 내지 50중량％ 배합하여 이루어지는 폴리페닐렌술피드 수지 조성물이며, 또한 320℃에서 5시간 가열했을 때의 점도 변화율이 1.5배 이하인 폴리페닐렌술피드 수지 조성물. 폴리페닐렌술피드 수지 (a): 중량 평균 분자량이 50,000 이상이며, 또한 하기 식 (1)로 표현되는, 가열했을 때의 중량 감소율 ΔWr이 0.18％ 이하인 폴리페닐렌술피드 수지 폴리페닐렌술피드 수지 (b): 중량 평균 분자량이 50,000 미만이며, 알칼리 토금속의 함유량이 200ppm 미만이며, 또한 2-(3,4-에폭시시클로헥실)에틸트리메톡시실란을 0.5중량％ 첨가하여 320℃에서 10분 가열했을 때의 분자량 증가율이 5.0％ 이하인 폴리페닐렌술피드 수지 폴리페닐렌술피드 수지 (c): 알칼리 토금속 (d)를 200 내지 800ppm 함유하고, 또한 하기 식 (1)로 표현되는, 가열했을 때의 중량 감소율 ΔWr이 0.18％를 초과하는 폴리페닐렌술피드 수지 (여기서 ΔWr은 중량 감소율(％)이고, 상압의 비산화성 분위기 하에서 승온 속도 20℃/분으로 열중량 분석을 행하였을 때에, 100℃ 도달 시의 시료 중량(W1)과, 330℃ 도달 시의 시료 중량(W2)으로부터 구해지는 값임.) 용융 체류 시의 점도 변화가 작고, 또한 가열 시의 가스 발생량이 적은 PPS 수지 조성물을 제공한다.폴리페닐렌술피드 수지 (a) 내지 (c)의 합계를 100중량％로 했을 때에, 폴리페닐렌술피드 수지 (a) 90 내지 50중량％에 대하여, 폴리페닐렌술피드 수지 (b) 및/또는 폴리페닐렌술피드 수지 (c)를 합계로 10 내지 50중량％ 배합하여 이루어지는 폴리페닐렌술피드 수지 조성물이며, 또한 320℃에서 5시간 가열했을 때의 점도 변화율이 1.5배 이하인 폴리페닐렌술피드 수지 조성물.폴리페닐렌술피드 수지 (a): 중량 평균 분자량이 50,000 이상이며, 또한 하기 식 (1)로 표현되는, 가열했을 때의 중량 감소율 ΔWr이 0.18％ 이하인 폴리페닐렌술피드 수지폴리페닐렌술피드 수지 (b): 중량 평균 분자량이 50,000 미만이며, 알칼리 토금속의 함유량이 200ppm 미만이며, 또한 2-(3,4-에폭시시클로헥실)에틸트리메톡시실란을 0.5중량％ 첨가하여 320℃에서 10분 가열했을 때의 분자량 증가율이 5.0％ 이하인 폴리페닐렌술피드 수지폴리페닐렌술피드 수지 (c): 알칼리 토금속 (d)를 200 내지 800ppm 함유하고, 또한 하기 식 (1)로 표현되는, 가열했을 때의 중량 감소율 ΔWr이 0.18％를 초과하는 폴리페닐렌술피드 수지(여기서 ΔWr은 중량 감소율(％)이고, 상압의 비산화성 분위기 하에서 승온 속도 20℃/분으로 열중량 분석을 행하였을 때에, 100℃ 도달 시의 시료 중량(W1)과, 330℃ 도달 시의 시료 중량(W2)으로부터 구해지는 값임.)