HOT-DIP GALVANIZED STEEL SHEETA hot-dip galvanized steel sheet wherein the hot-dip galvanized steel sheet comprises a base steel sheet and a hot-dip galvanized layer, a ferrite phase is, by volume fraction, 50% or less in a range of 1/8 thickness to 3/8 thickness centered at a position of 1/4 thickness from the surface of the base steel sheet, a hard structure is 50% or more, wherein the hot-dip galvanized steel sheet has the hot-dip galvanized layer in which Fe is 5.0% or less and Al is 1.0% or less, and columnar grains formed of a ζ phase is 20% or more in an entire interface between the plated layer and the base steel sheet, on the surface of the base steel sheet in which a volume fraction of a residual austenite is 3% or less and a ratio of a volume fraction of the hard structure is 0.10 times or more to 0.90 times or less of that of the hard structure in the range of 1/8 thickness to 3/8 thickness in a range of 20 µm depth in a steel sheet direction originating an interface between the hot-dip galvanized layer and the base steel sheet, and wherein the hot-dip galvanized steel sheet has a refined layer at the side of the interface in the base steel sheet, and wherein an average thickness of the refined layer, an average grain size of ferrite in the refined layer and a maximum size of the oxide included in the refined layer are defined respectively.A hot-dip galvanized steel sheet comprising: a steel sheet; and a hot-dip galvanized layer formed on at least one surface of the steel sheet, wherein: the steel sheet includes, a chemical composition comprising, % by mass, C: 0.040% to 0.280%, Si: 0.05% to 2.00%, Mn: 0.50% to 3.50%, P: 0.0001% to 0.1000%, S: 0.0001 % to 0.0100%, Al: 0.001% to 1.500%, N: 0.0001 % to 0.0100%, O: 0.0001% to 0.0100%, and a remainder of Fe and impurities; further, in a range of 1/8 thickness to 3/8 thickness centered at a position of 1/4 thickness from the surface of the steel sheet, by volume fraction, 0 to 50% of a ferrite phase, a total of 50% or more of a hard structure comprising one or more of a bainite structure, a bainitic ferrite phase, a fresh martensite phase and a tempered martensite phase, a residual austenite phase is 0 to 8%, a total of a pearlite phase and a coarse cementite phase is 0 to 8%, and in a surface layer range of 20 µm depth in a steel sheet direction from an interface between the hot-dip galvanized layer and a base steel, a residual austenite is 0 to 3%, the base steel sheet includes a microstructure in which V1/V2 which is a ratio of a volume fraction V1 of the hard structure in the surface layer range and a volume fraction V2 of the hard structure in the range of 1/8 thickness to 3/8 thickness centered at the position of 1/4 thickness from the surface of the base steel sheet is limited within a range of 0.10 or more and 0.90 or less, a Fe content is 5.0% or less and an Al content is 1.0% or less in the hot-dip galvanized layer, and columnar grains formed of a ζ phase are included, and further a ratio ((A*/A)×100) of an interface (A*) between the ζ phase and the base steel sheet in an entire interface (A) between the hot-dip galvanized plated layer and the base steel sheet is 20% or more, a refined layer is formed at the side of the interface in the base steel sheet, an average thickness of the refined layer is 0.1 to 5.0 µm, an average grain size of ferrite in the refined layer is 0.1 to 3.0 µm, one or two or more of oxides of Si and Mn are contained, and a maximum size of the oxide is 0.01 to 0.4 µm.
용융 아연 도금 강판모재 강판과 용융 아연 도금층을 포함하고, 모재 강판 표면으로부터 1/8 두께 내지 3/8 두께의 범위에서 체적 분율로 페라이트상이 50％ 이하, 경질 조직 50％ 이상이며, 도금층과 모재 강판의 계면을 기점으로 하는 모재 강판 깊이 20㎛까지의 범위에서 잔류 오스테나이트의 체적 분율 3％ 이하, 경질 조직의 체적 분율을, 1/8 두께 내지 3/8 두께의 범위에서의 체적 분율의 0.10 내지 0.90배로 한 모재 강판의 표면에, Fe: 5％ 이하, Al: 1.0％ 이하, ζ상을 포함하는 주상 결정을 도금층과 강판의 전체 계면 중 20％ 이상에 개재시키고 있는 용융 아연 도금층을 갖고, 모재 강판의 계면측에 미세화층을 갖고, 미세화층의 평균 두께, 미세화층 내의 페라이트상의 평균 입경, 미세화층에 포함되는 산화물의 최대 직경이 개별적으로 규정된 용융 아연 도금 강판.강판과 상기 강판 중 적어도 한쪽의 표면에 형성된 용융 아연 도금층을 포함하고,상기 강판은, 질량％로,C: 0.040 내지 0.280％,Si: 0.05 내지 2.00％,Mn: 0.50 내지 3.50％,P: 0.0001 내지 0.1000％,S: 0.0001 내지 0.0100％,Al: 0.001 내지 1.500％,N: 0.0001 내지 0.0100％,O: 0.0001 내지 0.0100％,잔부가 Fe 및 불순물을 포함하는 화학 성분을 갖고, 또한,상기 강판의 표면으로부터 1/4 두께를 중심으로 한 1/8 두께 내지 3/8 두께의 범위에서,체적 분율로, 0％ 내지 50％의 페라이트상과,베이나이트 조직과 베이나이틱 페라이트상과 프레시 마르텐사이트상과 템퍼링 마르텐사이트상 중 1종 이상을 포함하는 경질 조직을 합계 50％ 이상 갖고, 잔류 오스테나이트상이 0 내지 8％, 펄라이트상과 조대 시멘타이트상의 합계가 0 내지 8％이며,또한, 상기 용융 아연 도금층과 지철의 계면으로부터 강판 방향 깊이 20㎛까지의 표층 범위에서,잔류 오스테나이트가 0 내지 3％이며, 상기 표층 범위에서의 상기 경질 조직의 체적 분율(V1)과, 강판 표면으로부터 1/4 두께를 중심으로 한 1/8 두께 내지 3/8 두께의 범위에서의 상기 경질 조직의 체적 분율(V2)의 비인 V1/V2을 0.10 이상 0.90 이하의 범위로 제한한 마이크로 조직을 갖고,상기 용융 아연 도금층은, Fe 함유량이 5％ 이하이며, Al 함유량이 1.0％ 이하이며, ζ상을 포함하는 주상 결정을 포함하고, 또한상기 용융 아연 도금층과 모재 강판의 전체 계면(A) 중, 상기 ζ상과 모재 강판의 계면(A*)이 차지하는 비율((A*/A)×100)이 20％ 이상이며, 상기 모재 강판에 있어서 상기 계면측에 미세화층이 형성되고, 상기 미세화층의 평균 두께가 0.1 내지 5.0㎛, 상기 미세화층에서의 페라이트상의 평균 입경이 0.1 내지 3.0㎛이며, 상기 미세화층 내에 Si 및 Mn의 1종 또는 2종 이상의 산화물이 함유되고, 상기 산화물의 최대 직경이 0.01㎛ 내지 0.4㎛인, 용융 아연 도금 강판.