HIGH STRENGTH WELDED STEEL PIPE FOR LOW TEMPERATURE USE HAVING SUPERIOR BUCKLING RESISTANCE, AND METHOD FOR PRODUCING THE SAME, AND METHOD FOR PRODUCING STEEL SHEET FOR HIGH STRENGTH WELDED STEEL PIPE FOR LOW TEMPERATURE USE HAVING SUPERIOR BUCKLING RESISTANCETo provide a high strength steel pipe of API X100 grade, superior in buckling resistance and toughness at low temperatures after coating treatment, a method for producing the high strength steel pipe, and a method for producing a steel sheet serving as a base material. In a steel pipe, a base material includes, by mass%, more than 0.03% and 0.08% or less of C, 0.01-0.5% of Si, 1.5-3.0% of Mn, 0.01-0.08% of P, S and Al, 0.005-0.025% of Nb, 0.005-0.025% of Ti, 0.001-0.010% of N, 0.005% or less of O, and one or two or more of Cu, Ni, Cr, Mo, V and B, with 0.19≤PCM≤0.25 and the remainder being Fe and inevitable impurities, has a TS of 760-930 MPa, a uniform elongation of 5% or more and a YR of 85% or less; the micro structure of the base material mainly comprises bainite including island martensite, and includes 1-10% of a lower part bainite and 3% or less of residual austenite; seam welding by submerged arc welding is performed at a heat-input of 80 kJ/cm or less; and seam welding metal has a specified component composition.Component composition is% by weight, C: 0.03%, 0.08% or less, Si: 0.01 to 0.5%, MN: 1.5 to 3.0%, P: 0.015% or less, S: 0.003% or less, Al: 0.01 to 0.08% , Nb: 0.005 to 0.025%, Ti: 0.005 to 0.025%, N: 0.001 to 0.010%, O: 0.005% or less, further, Cu: 0.01 to 1.0%, Ni: 0.01 to 1.0%, CR: 0.01 to 1.0%, Mo: 0.01 to 1.0%, V: 0.01 to 0.1%, B: 0.0003 to 0.0020%, and the PCM value (% by weight) calculated by the following formula (1) is 0.19 ≦ PCM ≦ 0.25, the remainder is Fe and unavoidable impurities, and the tensile strength is 760 MPa or more and 930 MPa or less, and the uniform elongation is 5% or more, and the yield ratio is 90% or less, and the yield ratio is 90% or less, and the yield ratio is 90% or less, and the yield ratio is 90% or less. The base material of 230J or more and the component composition are mass%, C: 0.03 to 0.10%, Si: 0.5% or less, MN: 1.5 to 3.0%, P: 0.015% or less, S: 0.005% or less, Al: 0.05% or less, Nb: 0.005 to 0.05%, Ti: 0.005 to 0.03%, N: 0.010% or less, O: 0.015 to 0.045%, B: 0.0003 to 0.0050%, and further, Cu: 0.01 to 1.0 %, Ni: 0.01 to 2.5%, Cr: 0.01 to 1.0%, Mo: 0.01 to 1.5%, V: 0.1% or less, and the balance of welding metal of the seam weld is Fe and unavoidable impurities The micro-tissue of the base material is mainly mainly the bainite tissue containing island martensite, and the island-like martensite is 2 μm or less, and the bainite structure is surrounded at a boundary of 15 ° or more or less. The long axis diameter of the bainy ferrite is 20 μm or less, and the lower bainite is 1 to 10% with the area fraction, and the residual austenite is more than 3% or less in the area fraction, and the island-like martensite for the entire micro-tissue. A low temperature high-strength welded steel pipe excellent in firing resistance characterized by the area ratio of 3% or more and 12% or less. PCM (%) = C + Si / 30 + Mn / 20 + Cu / 20 + Ni / 60 + Cr / 20 + Mo / 15 + V / 10 + 5 × B ... (1) However, each element is content ( Mass%).
내좌굴 기능이 우수한 저온용 고강도 용접 강관과 그 제조 방법 및 내좌굴 기능이 우수한 저온용 고강도 용접 강관용 강판의 제조 방법코팅 처리 후에 내좌굴 성능과 저온 인성이 우수한 API의 X100급 고강도 강관과 그 제조 방법 및 모재가 되는 강판 제조 방법을 제공한다. 모재가 질량%로 C:0.03%초과해 0.08%이하, Si:0.01~0.5%, Mn:1.5~3.0%, P, S, Al:0.01~0.08%, Nb:0.005~0.025%, Ti:0.005~0.025%, N:0.001~0.010%, O:0.005% 이하, 또한 Cu, Ni, Cr, Mo, V, B의 일종 또는 2종 이상, 0.19≦PCM≦0.25, 잔부 Fe 및 불가피한 불순물로 TS760~930 MPa,5% 이상의 동일 성장, YR85%이하에서 마이크로 조직이 섬 형상 마르텐사이트를 포함한 베이나이트를 주체로 하고, 하부 베이나이트를1~10%, 또한 잔류 오스테나이트를3% 이하를 구비하고, 서브머지드 아크 용접에 의한 심 용접이 입열 80 kJ/cm이하에서 특정 심 용접 금속의 성분 조성을 가지는 강관.성분 조성이 질량%로 C:0.03%초과해 0.08%이하, Si:0.01~0.5%, Mn:1.5~3.0%, P:0.015% 이하, S:0.003% 이하, Al:0.01~0.08%, Nb:0.005~0.025%, Ti:0.005~0.025%, N:0.001~0.010%, O:0.005% 이하를 함유하고 또한 Cu:0.01~1.0%, Ni:0.01~1.0%, Cr:0.01~1.0%, Mo:0.01~1.0%, V:0.01~0.1%, B:0.0003~0.0020%의 일종 이상을 함유하고 하기 식(1)에서 계산되는 PCM값(단위는 질량%)이 0.19≦PCM≦0.25를 만족하고 잔부가 Fe 및 불가피한 불순물로 인장 강도가 760 MPa 이상 930 MPa 이하, 동일 성장이5% 이상, 항복비가90% 이하, 시험 온도-15℃에서의 샤르피 흡수에너지가 230 J 이상의 모재부와 성분 조성이 질량%로 C:0.03~0.10%, Si:0.5% 이하, Mn:1.5~3.0%, P:0.015% 이하, S:0.005% 이하, Al:0.05% 이하, Nb:0.005~0.05%, Ti:0.005~0.03%, N:0.010% 이하, O:0.015~0.045%, B:0.0003~0.0050%를 함유하고 또한 Cu:0.01~1.0%, Ni:0.01~2.5%, Cr:0.01~1.0%, Mo:0.01~1.5%, V:0.1% 이하의 일종 이상을 함유하고 잔부가 Fe 및 불가피한 불순물인 심 용접부의 용접 금속을 구비하고, 모재부의 마이크로 조직이 섬 형상 마르텐사이트를 포함한 베이나이트 조직을 주체로 하고, 상기 섬 형상 마르텐사이트는 긴 축 지름이 2μm이하, 상기 베이나이트 조직은 방위차각 15° 이상의 경계에서 둘러싸이는 베이나이틱 페라이트의 긴 축 지름이 20μm이하이고 하부 베이나이트를 면적분율로1~10%, 또한 잔류 오스테나이트를 면적분율로3% 이하를 포함하고 마이크로 조직 전체에 대한 상기 섬 형상 마르텐사이트의 면적률이3% 이상12% 이하인 것을 특징으로 하는 내좌굴 성능이 우수한 저온용 고강도 용접 강관. PCM(%) =C+Si/30+Mn/20+Cu/20+Ni/60+Cr/20+Mo/15+V/10+5×B…(1) 단, 각 원소는 함유량(질량%)을 나타낸다.