METHOD FOR PRODUCING A HIGH STRENGTH STEEL SHEET HAVING IMPROVED DUCTILITY AND FORMABILITY, AND OBTAINED STEEL SHEETA method for producing a steel sheet, the method containing the following successive steps:providing a cold-rolled steel sheet, the chemical composition of the steel containing in weight %: 0.15%≤C≤0.23%, 2.0%≤Mn≤2.8%, 1.0%≤Si≤2.1%, 0.02%≤Al≤1.0%, with 1.7%≤Si+Al≤2.1%, 0≤Nb≤0.035%, 0≤Mo≤0.3%, 0≤Cr≤0.4%, the remainder being Fe and unavoidable impurities,annealing the steel sheet at an annealing temperature TA so as to obtain a structure comprising at least 65% of austenite and up to 35% of intercritical ferrite,quenching the sheet at a cooling rate of at least 20° C./s from a temperature of at least 600° C. down to a quenching temperature QT comprised between Ms-170° C. and Ms-80° C.,heating the sheet up to a partitioning temperature PT between 350° C. and 450° C. and maintaining the sheet at this temperature for a partitioning time Pt comprised between 80 s and 440 s,immediately cooling the sheet down to the room temperature, the steel sheet having a final microstructure consisting of, in surface fraction: between 40% and 70% of tempered martensite,between 7% and 15% of retained austenite,between 15% and 35% of ferrite,at most 5% of fresh martensite,at most 15% of bainite.A method for producing a steel sheet having a tensile strength of at least 1180 MPa, a total elongation of at least 12%, measured according to the ISO standard 6892-1, and a hole expansion ratio HER of at least 25%, measured according to the ISO standard 16630:2009, wherein the method comprises the following successive steps: providing a cold-rolled steel sheet made of a steel having a chemical composition containing by weight: 0.15%≤C≤0.23%,2.0%≤Mn≤2.8%,1.0%≤Si≤2.1%,0.02%≤Al≤1.0%,with 1.7%≤Si+Al≤2.1%,0≤Nb≤0.035%,0≤Mo≤0.3%,0≤Cr≤0.4%, anda remainder, the remainder being Fe and unavoidable impurities,annealing the steel sheet at an annealing temperature TA so as to obtain a structure comprising at least 65% of austenite and up to 35% of intercritical ferrite,quenching the steel sheet to a quenching temperature QT comprised between Ms-170° C. and Ms-80° C., with a cooling rate of at least 20° C./s from a temperature of at least 600° C. down to the quenching temperature QT,heating the steel sheet from the quenching temperature QT up to a partitioning temperature PT comprised between 350° C. and 450° C.,maintaining the steel sheet at the partitioning temperature PT for a partitioning time Pt comprised between 80 s and 440 s, andimmediately cooling the steel sheet down to the room temperature,the steel sheet having a final microstructure consisting of, in surface fraction:between 40% and 70% of tempered martensite, the tempered martensite having a C content lower than 0.45%,between 7% and 15% of retained austenite,between 15% and 35% of ferrite,at most 5% of fresh martensite, andat most 15% of bainite.
연성 및 성형성이 개선된 고강도 강 시트를 제조하기 위한 방법, 및 얻어진 강 시트본 발명은 ISO 표준 6892-1 에 따라 측정된 인장 강도가 적어도 1180 MPa 이고 또한 총 연신율이 적어도 12% 이고, ISO 표준 16630:2009 에 따라 측정된 구멍 확장비 (HER) 가 적어도 25% 인 강 시트를 제조하는 방법에 관한 것으로, 상기 방법은, - 강의 화학 조성이, 중량% 로, 0.15% ≤ C ≤ 0.23%, 2.0% ≤ Mn ≤ 2.8%, 1.0% ≤ Si ≤ 2.1%, 0.02% ≤ Al ≤ 1.0%, 이때 1.7% ≤ Si+Al ≤ 2.1%, 0 ≤ Nb ≤ 0.035%, 0 ≤ Mo ≤ 0.3%, 0 ≤ Cr ≤ 0.4%, Fe 및 불가피한 불순물인 잔부를 함유하는 냉간 압연된 강 시트를 제공하는 단계, - 65% 이상의 오스테나이트 및 35% 이하의 이상영역 페라이트를 포함하는 조직을 얻기 위하여 어닐링 온도 (TA) 에서 강 시트를 어닐링하는 단계, - 적어도 600℃ 의 온도로부터 Ms-170℃ ~ Ms-80℃ 의 ?칭 온도 (QT) 로 적어도 20℃/s 의 냉각 속도로 상기 강 시트를 ?칭하는 단계, - 상기 ?칭 온도 (QT) 로부터 350℃ ~ 450℃ 의 파티셔닝 온도 (PT) 까지 상기 강 시트를 가열하고, 상기 온도에서 80s ~ 440s 의 파티셔닝 시간 (Pt) 동안 상기 강 시트를 유지시키는 단계, - 상기 강 시트를 실온으로 즉시 냉각시키는 단계를 포함하고, 상기 강 시트는, 표면 분율에 있어서, - 0.45% 미만의 C 함량을 가지는, 40% ~ 70% 의 템퍼링된 마텐자이트, - 7% ~ 15% 의 잔류 오스테나이트, - 15% ~ 35% 의 페라이트, - 최대 5% 의 프레시 마텐자이트, - 최대 15% 의 베이나이트를 함유하는 최종 미세조직을 갖는다.ISO 표준 6892-1 에 따라 측정된 인장 강도가 적어도 1180 MPa 이고 또한 총 연신율이 적어도 12% 이고, ISO 표준 16630:2009 에 따라 측정된 구멍 확장비 (HER) 가 적어도 25% 인 강 시트를 제조하는 방법으로서, 상기 방법은,- 강의 화학 조성이, 중량% 로,0.15% ≤ C ≤ 0.23%,2.0% ≤ Mn ≤ 2.8%,1.0% ≤ Si ≤ 2.1%,0.02% ≤ Al ≤ 1.0%,이때 1.7% ≤ Si+Al ≤ 2.1%,0 ≤ Nb ≤ 0.035%,0 ≤ Mo ≤ 0.3%,0 ≤ Cr ≤ 0.4%,Fe 및 불가피한 불순물인 잔부를 함유하는 냉간 압연된 강 시트를 제공하는 단계,- 65% 이상의 오스테나이트 및 35% 이하의 이상영역 (intercritical) 페라이트를 포함하는 조직을 얻기 위하여 어닐링 온도 (TA) 에서 상기 강 시트를 어닐링하는 단계,- 적어도 600℃ 의 온도로부터 Ms-170℃ ~ Ms-80℃ 의 ?칭 온도 (QT) 로 적어도 20℃/s 의 냉각 속도로 상기 강 시트를 ?칭하는 단계,- 상기 ?칭 온도 (QT) 로부터 350℃ ~ 450℃ 의 파티셔닝 (partitioning) 온도 (PT) 로 상기 강 시트를 가열하고, 상기 온도에서 80s ~ 440s 의 파티셔닝 시간 (Pt) 동안 상기 강 시트를 유지시키는 단계,- 상기 강 시트를 실온으로 즉시 냉각시키는 단계를 포함하고,상기 강 시트는, 표면 분율에 있어서,- 0.45% 미만의 C 함량을 가지는, 40% ~ 70% 의 템퍼링된 마텐자이트,- 7% ~ 15% 의 잔류 오스테나이트, - 15% ~ 35% 의 페라이트, - 최대 5% 의 프레시 (fresh) 마텐자이트,- 최대 15% 의 베이나이트로 이루어지는 최종 미세조직을 가지는, 강 시트를 제조하는 방법.