PROPYLENE-ETHYLENE COPOLYMER RESIN COMPOSITION AND FILM OR SHEETTo provide a propylene-ethylene copolymer resin composition and a film or the like having excellent extrusion moldability even during extrusion molding at low temperature while maintaining excellent properties such as excellent transparency or flexibility of a soft propylene-ethylene copolymer obtained by a metallocene catalyst. There is provided a propylene-ethylene copolymer resin composition containing 65 to 95 wt.% of a propylene resin composition (C) obtained by mixing a specific propylene polymer (A) of 0 to 99 wt.% and a specific propylene-ethylene copolymer (B) of 1 to 100 wt. by a method for removing a polymerization blend and 5 to 35 wt.% of a specific propylene-ethylene copolymer (D) and the propylene-ethylene copolymer (D) is a propylene-ethylene copolymer resin composition consisting of a specific propylene polymer component (D1) of 65 to 95 wt.% and a specific propylene-ethylene copolymer component (D2) of 5 to 35 wt.% or the like.Propylene-ethylene copolymer having a propylene-based polymer (A) 0 to 99% by weight having the following characteristics (A-I) to (A-IV) and the following characteristics (BI) to (B-III) (B 65 to 95% by weight of propylene-based resin composition (C) obtained by mixing 1 to 100% by weight with a method of excluding the polymerization blend, and the following characteristics (DI) to (D-II) Propylene-ethylene copolymer resin composition containing 5 to 35% by weight of propylene-ethylene copolymer (D) having 5 to 35% by weight, said propylene-ethylene copolymer (D) is (D1) and (D2 A total of 65 to 95% by weight of propylene-based polymer component (D1) having the following characteristics (D1-I) and a propylene having the following characteristics (D2-I) and (D2-II) based on the following characteristics (D1-I). A propylene-ethylene copolymer resin composition comprising 5 to 35% by weight of ethylene copolymer component (D2). Propylene-based polymer (A): (A-I) A polymerization obtained by using a metallocene catalyst. (A-ii) Melt Flow Rate [MFR (A)] is 0.1 to 100 g / 10 minutes. (A-III) Ethylene content [E (A)] is 0 to 6.0% by weight. (A-IV) The molecular weight distribution [Mw / Mn (A)] represented by the weight average molecular weight (Mw) and the number average molecular weight (Mn) determined by GPC measurement is 2 to 4. Propylene-ethylene copolymer (B): (B) (B-I) A polymerization obtained by using a metallocene catalyst. (B-ii) Ethylene content [E (B)] is 4 to 17% by weight. (B-III) The molecular weight distribution [Mw / Mn (b)] represented by the weight average molecular weight (Mw) and the number average molecular weight (Mn) determined by GPC measurement is 1 to 4. Propylene-ethylene copolymer (D): (D-I) The ethylene content [E (D)] in the copolymer (D) is in the range of 0.4 to 13% by weight. (D-II) Melt flow rate [MFR (D)] of copolymer (D) is in the range of 0.5 to 20 g / 10 minutes. Propylene-based polymer component (D1): (D1-I) The ethylene content [E (D1)] in the polymer component (D1) is in the range of 0 to 6.0% by weight. Propylene-ethylene copolymer component (D2): (D2-I) The ethylene content [E (D2)] in the copolymer component (D2) is in the range of 8 to 25% by weight. (D2-ii) Melt flow rate [MFR (D2)] of copolymer component (D2) is in the range of 0.0001 to 0.5 g / 10 min.
프로필렌 에틸렌 공중합체 수지 조성물 및 필름 또는 시트메탈로센계 촉매에 의해 얻어진 연질 프로필렌 에틸렌 공중합체의 투명성, 유연성이 우수한 등의 우수한 특성을 유지하면서 저온에서 압출 성형해도 우수한 압출 성형성을 가지는 프로필렌 에틸렌 공중합체 수지 조성물 및 필름 등을 제공한다. 특정 프로필렌계 중합체(A)0~99중량%과 특정 프로필렌 에틸렌 공중합체(B)1~100중량%를 중합 블렌드를 제외하는 방법으로 혼합됨으로써 얻어진 프로필렌계 수지 조성물(C)65~95중량%과 특정 프로필렌­에틸렌 공중합체(D)5~35중량%를 함유하는 프로필렌 에틸렌 공중합체 수지 조성물로서, 상기 프로필렌 에틸렌 공중합체(D)는 특정 프로필렌계 중합체 성분(D1)65~95중량%과 특정 프로필렌 에틸렌 공중합체 성분(D2)5~35중량%로 구성되는 프로필렌 에틸렌 공중합체 수지 조성물 등.하기 특성(A­i)~(A-iv)를 가지는 프로필렌계 중합체(A)0~99중량%과 하기 특성(B-i)~(B-iii)를 가지는 프로필렌 에틸렌 공중합체(B)1~100중량%를 중합 블렌드를 제외하는 방법으로 혼합됨으로써 얻어진 프로필렌계 수지 조성물(C)65~95중량%과 하기 특성(D-i)~(D-ii)를 가지는 프로필렌­에틸렌 공중합체(D)5~35중량%를 함유하는 프로필렌 에틸렌 공중합체 수지 조성물로서, 상기 프로필렌 에틸렌 공중합체(D)는 (D1) 및 (D2)의 합계 100 중량%기준으로 하기 특성(D1-i)을 가지는 프로필렌계 중합체 성분(D1)65~95중량%과 하기 특성(D2-i) 및 (D2-ii)을 가지는 프로필렌 에틸렌 공중합체 성분(D2)5~35중량%로 구성되는 것을 특징으로 하는 프로필렌 에틸렌 공중합체 수지 조성물. ·프로필렌계 중합체(A):(A-i) 메탈로센계 촉매를 이용한 중합에 의해 얻어진 것이다. (A-ii) 멜트 플로우 레이트[MFR(A)]가 0.1~100 g/10분이다. (A-iii) 에틸렌 함유량[E(A)]가0~6.0 중량%이다. (A-iv) GPC 측정에 의해 요구되는 중량 평균 분자량(Mw)과 수평균 분자량(Mn)의 비로 표시되는 분자량 분포[Mw/Mn(A)]가2~4이다. ·프로필렌 에틸렌 공중합체(B):(B-i) 메탈로센계 촉매를 이용한 중합에 의해 얻어진 것이다. (B-ii) 에틸렌 함유량[E(B)]가4~17중량%이다. (B-iii) GPC 측정에 의해 요구되는 중량 평균 분자량(Mw)과 수평균 분자량(Mn)의 비로 표시되는 분자량 분포[Mw/Mn(B)]가1~4이다. ·프로필렌 에틸렌 공중합체(D):(D-i) 공중합체(D) 중의 에틸렌 함유량[E(D)]가 0.4~13 중량%의 범위에 있다. (D-ii) 공중합체(D)의 멜트 플로우 레이트[MFR(D)]가 0.5~20 g/10분의 범위에 있다. ·프로필렌계 중합체 성분(D1):(D1-i) 중합체 성분(D1) 중의 에틸렌 함유량[E(D1)]가0~6.0 중량%의 범위에 있다. ·프로필렌 에틸렌 공중합체 성분(D2):(D2-i) 공중합체 성분(D2) 중의 에틸렌 함유량[E(D2)]가8~25중량%의 범위에 있다. (D2-ii) 공중합체 성분(D2)의 멜트 플로우 레이트[MFR(D2)]가 0.0001~0.5 g/10분의 범위에 있다.