ZINC HOT-DIPPED STEEL SHEETIn the range of 1/8 to 3/8 of the thickness, centering on 1/4 of the thickness, from the surface of a parent material steel sheet, the ferrite phase has a volume fraction of 50% to 97%, the total of hard structures comprising one or more of the bainite phase, bainitic ferrite phase, fresh martensite phase and tempered martensite phase accounts for a volume fraction of at least 3%, retained austenite phase accounts for a volume fraction of 0% to 8%, the total of pearlite phase and coarse cementite phase accounts for a volume fraction of 0% to 8%, and at the interface between the zinc hot-dippedlayer and the parent material steel sheet, there is an Fe-Al alloy layer having an average thickness of 0.1 microns to 2.0 microns and a difference between the maximum and minimum thickness in the steel sheet width direction of within 0.5 microns, and in a refined layer which is in direct contact with the Fe-Al alloy layer, the difference between the maximum and minimum thickness of the refined layer in the steel sheet width direction is within 2.0 microns.A hot-dip galvanized steel sheet characterized in that: which is a hot-dip galvanized steel sheet having a hot-dip galvanized layer on at least one side of a base steel sheet,the base steel sheet has a chemical composition containing, in mass%:c：0.040％～0.280％、si：0.05％～2.00％、mn：0.50％～3.50％、p：0.0001％～0.1000％、s：0.0001％～0.0100％、al：0.001％～1.500％、n：0.0001％～0.0100％、o：0.0001％～0.0100％、ti：0％～0.150％、nb：0％～0.100％、v：0％～0.300％、cr：0％～2.00％、ni：0％～2.00％、cu：0％～2.00％、mo：0％～2.00％、b：0％～0.0100％、w: 0% to 2.00%, andca. total of ce, mg, zr, la and rem: 0 to 0.0100 percent of the total weight of the composition,the remainder comprising fe and impurities;a base steel sheet having a thickness ranging from 1/8 to 3/8 about a position 1/4 from the surface,the volume fraction of the ferrite phase is 50-97%,the total of hard structures consisting of 1 or more kinds of bainite phase, bainitic ferrite phase, primary martensite phase and tempered martensite phase is 3% or more by volume fraction,the volume fraction of the retained austenite phase is 0-8%,the total volume fraction of the pearlite phase and the coarse cementite phase is 0% to 8%;in the surface layer portion of 20 μm depth from the interface between the hot dip galvanized layer and the base steel sheet to the steel sheet direction,the volume fraction of the retained austenite is 0-3%;a microstructure having a ratio of v1/v2 between a volume fraction v1 of the hard structure in the surface layer portion and a volume fraction v2 of the hard structure in a range of 1/8 to 3/8 thickness from a position 1/4 thickness from the surface of the steel sheet as a center, the ratio being in a range of 0.10 to 0.90;the fe content in the hot-dip galvanized layer is more than 0% and less than 3.0%, the al content is more than 0% and less than 1.0%,an fe-al alloy layer having an average thickness of 0.1 to 2.0 [ mu ] m and a difference between a maximum thickness and a minimum thickness in a steel sheet width direction of 0.5 [ mu ] m or less at an interface between the hot-dip galvanized layer and the base steel sheet,the base steel sheet has a fine layer in direct contact with the fe-al alloy layer, the fine layer has an average thickness of 0.1 to 5.0 [ mu ] m, the ferrite phase in the fine layer has an average particle diameter of 0.1 to 3.0 [ mu ] m, the fine layer contains 1 or 2 or more oxides of si and mn, the oxides have a maximum diameter of 0.01 to 0.4 [ mu ] m, and the difference between the maximum thickness and the minimum thickness of the fine layer in the steel sheet width direction is within 2.0 [ mu ] m.
용융 아연 도금 강판모재 강판의 표면으로부터 1/4 두께를 중심으로 한 1/8 두께∼3/8 두께의 범위에 있어서, 페라이트상이 체적분율로 50％ 이상 97％ 이하, 베이나이트상과 베이니틱 페라이트상과 프레시 마르텐사이트상과 템퍼링 마르텐사이트상 중 1종 이상으로 이루어지는 경질 조직의 합계가 체적분율로 3％ 이상, 잔류 오스테나이트상이 체적분율로 0％∼8％, 펄라이트상과 조대 시멘타이트상의 합계가 체적분율로 0％∼8％이고, 용융 아연 도금층과 상기 모재 강판의 계면에, 평균 두께가 0.1㎛∼2.0㎛이고, 강판 폭 방향에 있어서의 최대 두께와 최소 두께의 차가 0.5㎛ 이내인 Fe-Al 합금층을 갖고, 상기 Fe-Al 합금층에 직접 접하는 미세화층에 있어서, 강판 폭 방향에 있어서의 상기 미세화층의 최대 두께와 최소 두께의 차가 2.0㎛ 이내이다.모재 강판의 적어도 한쪽 측에 용융 아연 도금층을 갖는 용융 아연 도금 강판이며,상기 모재 강판은, 질량％로,C: 0.040％∼0.280％,Si: 0.05％∼2.00％,Mn: 0.50％∼3.50％,P: 0.0001％∼0.1000％,S: 0.0001％∼0.0100％,Al: 0.001％∼1.500％,N: 0.0001％∼0.0100％,O: 0.0001％∼0.0100％,Ti: 0％∼0.150％,Nb: 0％∼0.100％,V: 0％∼0.300％,Cr: 0％∼2.00％,Ni: 0％∼2.00％,Cu: 0％∼2.00％,Mo: 0％∼2.00％,B: 0％∼0.0100％,W: 0％∼2.00％, 및Ca, Ce, Mg, Zr, La, 및 REM: 합계로 0％∼0.0100％를포함하고,잔부가 Fe 및 불순물로 이루어지는 화학 성분을 갖고,상기 모재 강판의 전체 두께에 대해, 상기 모재 강판의 표면으로부터 1/4 두께를 중심으로 한 1/8 두께∼3/8 두께의 범위에 있어서,페라이트상이 체적분율로 50％ 이상 97％ 이하,베이나이트상과 베이니틱 페라이트상과 프레시 마르텐사이트상과 템퍼링 마르텐사이트상 중 1종 이상으로 이루어지는 경질 조직의 합계가 체적분율로 3％ 이상,잔류 오스테나이트상이 체적분율로 0％∼8％,펄라이트상과 조대 시멘타이트상의 합계가 체적분율로 0％∼8％이고,상기 용융 아연 도금층과 모재 강판의 계면으로부터 강판 방향 깊이 20㎛까지의 표층부에 있어서,잔류 오스테나이트가 체적분율로 0∼3％이고,상기 표층부에 있어서의 상기 경질 조직의 체적분율 V1과, 강판 표면으로부터 1/4 두께를 중심으로 한 1/8 두께∼3/8 두께의 범위에 있어서의 상기 경질 조직의 체적분율 V2의 비인 V1/V2를 0.10 이상 0.90 이하의 범위로 한 마이크로 조직을 갖고,상기 용융 아연 도금층에 있어서의 Fe 함유량이 0％ 초과 3.0％ 이하이고, Al 함유량이 0％ 초과 1.0％ 이하이고,상기 용융 아연 도금층과 상기 모재 강판의 계면에, 평균 두께가 0.1㎛∼2.0㎛이고, 강판 폭 방향에 있어서의 최대 두께와 최소 두께의 차가 0.5㎛ 이내인 Fe-Al 합금층을 갖고,상기 모재 강판 내에, 상기 Fe-Al 합금층에 직접 접하는 미세화층을 갖고, 상기 미세화층의 평균 두께가 0.1㎛∼5.0㎛, 상기 미세화층 내에 있어서의 페라이트상의 평균 입경이 0.1㎛∼3.0㎛이고, 상기 미세화층 중에 Si 및 Mn 중 1종 또는 2종 이상의 산화물을 함유하고, 상기 산화물의 최대 직경이 0.01㎛∼0.4㎛이고, 강판 폭 방향에 있어서의 상기 미세화층의 최대 두께와 최소 두께의 차가 2.0㎛ 이내인 것을 특징으로 하는, 용융 아연 도금 강판.