SURFACE-MODIFIED EFFECT PIGMENT AND NAIL VARNISH COMPOSITIONThe present invention relates to surface modification effect pigment and its production method comprising special additive.Invention further provides nail enamel compositions, the nail enamel composition carries out the modified effect pigment in surface with starting material (additive) comprising a) at least one, and wherein the effect pigment includes that laminar substrate and at least one optional are applied to the coating of the substrate；B) as at least one hydrocarbon resin of adhesive；And c) at least one solvent or solvent mixture, wherein the starting material (additive) for the modified effect pigment in surface is at least one compound from the following group, which is made of following item: phosphate ester-containing compound contains phosphonate compound, containing or mixtures thereof phosphinic acid compounds, fatty acids compound and/or siliceous hydride compounds.A kind of surface modification effect pigment, which includes that platelet like metal substrates or flake are nonmetallic substrate, the platelet like metal substrates are optionally coated at least one metal oxide, metal hydroxides and/or metal oxidation object hydrate, the flake non-metallic substrate are optionally coated at least one metal oxide, metal hydroxides and/or gold belong to oxide hydrate, whereina) platelet like metal substrates are to be produced by wet grinding and have h of the range from 20nm to less than 100nm50, and the starting material (additive) modified for surface bei) phosphoric acid spermaceti base ester or cetyl phosphate, in the range of from 2 weight % to less than 40 weight %, orii) phosphoric acid stearyl or stearyl phosphate, in the range of from 5 weight % to less than 20 weight %, oriii) there is formula r-p (o) (oh)2phosphonic acids, wherein r=has range from c8to c14carbochain straight chained alkyl, the phosphonic acids total amount preferred scope be from 4 weight % to 45 weight %, this tittle is based on the thin slice optionally coated in each case the total weight of shape metal base, orb) platelet like metal substrates are to be produced by pvd method and have average thickness h of the range from 13nm to 60nm50, and and the starting material (additive) modified for surface isi) phosphoric acid spermaceti base ester or cetyl phosphate, in the range of from 10 weight % to 50 weight %, orii) phosphoric acid stearyl or stearyl phosphate, in the range of from 13 weight % to 50 weight %, oriii) there is formula r-p (o) (oh)2phosphonic acids, wherein r=has range from c8to c14carbochain straight chained alkyl, the phosphonic acids total amount range be from 5 weight % to 50 weight %, this tittle is based on the flake gold that this optionally coats in each case belong to the total weight of substrate, orc) the flake non-metallic substrate has d of the range from 2 μm to 360 μm50, and the starting material modified for surface (additive) isi) phosphoric acid spermaceti base ester or cetyl phosphate, in the range of from 5 weight % to 30 weight %, orii) phosphoric acid stearyl or stearyl phosphate, in the range of from 2 weight % to 25 weight %,this tittle is based on the total weight of the laminar non-metallic substrate optionally coated in each case, ord) non-metallic substrate is glass flake, which is coated with metallic silver and with range from 2 μm to 360 μm d50with the average thickness h in the glass flake from 70nm to 530nm in range50, glassand from 9nm to 27nm in range the average thickness of the metal silver coating, and the starting material (additive) modified for surface isi) phosphoric acid spermaceti base ester or cetyl phosphate, in the range of from 3 weight % to less than 40 weight %, orii) phosphoric acid stearyl or stearyl phosphate, in the range of from 5 weight % to less than 30 weight %, oriii) phosphonic acids r-p (o) (oh)2, wherein r=has range from c8to c14carbochain linear alkyl moieties, the ratio of the phosphonic acids example range is from 15 weight % to 43 weight %, this tittle is based on the gross weight of the glass flake of silver coating in each case amount.
표면-개질 효과 안료 및 네일 바니시 조성물본 발명은 특정 첨가제를 포함하는 표면-개질된 효과 안료 및 이의 생성에 관한 것이다. 본 발명은 네일 바니시 조성물을 추가로 제공하며, 상기 네일 바니시 조성물은 a) 소판 형태의 기재를 포함하고 선택적으로 기재에 도포된 적어도 하나의 코팅을 포함하는, 출발 재료(첨가제)로 표면-개질된 적어도 하나의 효과 안료, b) 결합제로서의 적어도 하나의 탄화수소 수지, 및 c) 적어도 하나의 용매 또는 용매 혼합물을 포함하며, 효과 안료의 표면 개질을 위한 출발 재료(첨가제)는 인산 에스테르-함유 화합물, 포스폰산 에스테르-함유 화합물, 포스폰산-함유 화합물, 지방산-함유 화합물 및/또는 실란-함유 화합물 또는 이들의 혼합물로 이루어진 군으로부터의 적어도 하나의 화합물이다.표면- 개질된 효과 안료로서,적어도 하나의 금속 산화물, 금속 수산화물 및/또는 금속 산화물 수화물로 선택적으로 코팅된 소판 형태의 금속 기재 또는 적어도 하나의 금속 산화물, 금속 수산화물 및/또는 금속 산화물 수화물로 선택적으로 코팅된 소판 형태의 비금속 기재를 포함하며,a) 소판 형태의 금속 기재는 습식 그라인딩에 의해 생성되고, h50이 20 nm 내지 100 nm 미만의 범위이고, 표면 개질에 사용되는 출발 재료(첨가제)가i) 2 중량% 내지 40 중량% 미만 범위의 인산 세틸 에스테르 또는 세틸인산 또는ii) 5 중량% 내지 20 중량% 미만 범위의 인산 스테아릴 에스테르 또는 스테아릴 포스페이트 또는iii) 총량이 바람직하게는 4 중량% 내지 45 중량% 범위인 화학식 R-P(O)(OH)2의 포스폰산(여기서, R은 C8 내지 C14 범위의 탄소 사슬을 갖는 선형 알킬 라디칼임)이며, 이때 각각의 경우는 선택적으로 코팅된 소판 형태의 금속 기재의 총 중량을 기준으로 하거나,b) 소판 형태의 금속 기재는 PVD 방법에 의해 생성되고, 평균 두께 h50이 13 nm 내지 60 nm 범위이고, 표면 개질에 사용되는 출발 재료(첨가제)가i) 10 중량% 내지 50 중량% 범위의 인산 세틸 에스테르 또는 세틸인산 또는ii) 13 중량% 내지 50 중량% 범위의 인산 스테아릴 에스테르 또는 스테아릴 포스페이트 또는iii) 총량이 5 중량% 내지 50 중량% 범위인 화학식 R-P(O)(OH)2의 포스폰산(여기서, R은 C8 내지 C14 범위의 탄소 사슬을 갖는 선형 알킬 라디칼임)이며, 이때 각각의 경우는 선택적으로 코팅된 소판 형태의 금속 기재의 총 중량을 기준으로 하거나,c) 소판 형태의 비금속 기재는 D50이 2 μm 내지 360 μm 범위이고, 표면 개질에 사용되는 출발 재료(첨가제)가i) 5 중량% 내지 30 중량% 범위의 인산 세틸 에스테르 또는 세틸인산 또는ii) 2 중량% 내지 25 중량% 범위의 인산 스테아릴 에스테르 또는 스테아릴 포스페이트이며,이때 각각의 경우는 선택적으로 코팅된 소판 형태의 비금속 기재의 총 중량을 기준으로 하거나, d) 비금속 기재는 금속 은으로 코팅되고 D50이 2 μm 내지 360 μm 범위인 유리 소판으로서, 유리 소판의 평균 두께 h50,유리가 70 nm 내지 530 nm 범위이고, 금속 은 코팅의 평균 두께가 9 nm 내지 27 nm 범위이고, 표면 개질에 사용되는 출발 재료(첨가제)가i) 3 중량% 내지 40 중량% 미만 범위의 인산 세틸 에스테르 또는 세틸인산 또는ii) 5 중량% 내지 30 중량% 미만 범위의 인산 스테아릴 에스테르 또는 스테아릴 포스페이트 또는iii) 15 중량% 내지 43 중량% 범위의 비율로 존재하는 포스폰산 R-P(O)(OH)2(여기서, R은 C8 내지 C14 범위의 탄소 사슬을 갖는 선형 알킬 모이어티임)이며, 이때 각각의 경우는 은-코팅된 유리 소판의 총 중량을 기준으로 하는, 표면-개질된 효과 안료.