Method for calculating the combination of properties being established for a deformable lightweight steelA method is disclosed for calculating the combination of properties of phase components and of mechanical properties being established of a predefined alloy composition for a deformable lightweight steel having the elements in percent by weight C 0.02 to ≤1.0, Al 2.5 to ≤8.0, Si 0.0 to ≤1.5, Mn ≥5.0 to ≤35.0, Cr >1.0 to ≤14.0, total content of N, S, P ≤0.1, the remainder iron and other steel-accompanying elements with some contents of Cu, Mo, Ni, and Zn of up to 1.0 wt % in total by using specific formulas on the basis of the manganese content, wherein, in the formulas, the alloy contents are used as absolute numbers without dimensions, and the calculated, dimensionless values are assigned the units MPa for Rm and Rp and % for A80.A method for producing a formable lightweight steel with the elements in weight %C0.02 to ≤ 1.0Al??1 to 9Si?0.0 to ≤ 1.5Mn?6.0 to ≤ 35.0Cr>1.0 to ≤ 14.0With N, S, P in sum together ≤0.1, remainder iron and other steel accompanying elements, and optionally Cu, Mo, Ni and Zn in sum together up to 1.0 weight %, wherein the lightweight steel is made of a phase mixture of austenite and ferrite (A/F) with an austenite proportion between 100% and 5%, a strength Rm between 600 and 1200 MPa, a yield strength Rp0.2 between 300 and 1120 MPa, and a elongation at break A80 between 5 and 40% said method comprising:for a first given alloy composition of said formable lightweight steel in which Mn: 5 to maximal 11%, calculating a strength Rm and Rp in MPa and an elongation at break A80 in % of the formable lightweight steel according to the formulas: Rm=3182{C}+1224{Si}+847.6{Cr}+633.2{Al}?3354.8?140.7{Al}{Cr}?482.5{Cr}{C}?1372.3{Si}2 Rp=2509.2{C}+947{Si}+538{C}+367.8{Al}?2168.1?78.1{Al}{Cr}?381.9{Cr}{C}?923.2{Si}2 A80=267.4+48{Al}{C}?2.6{Cr}?16.8{Si}?41.1{Al}?275.4{C}Wherein the following content limits are to be observed: C: 0.2 to 0.7, Si: ≤1.0%, and a sum of Al+Cr: ≤12%;for a second given composition of said formable lightweight steel in which 22%≥Mn>11%, calculating the strength Rm and Rp in MPa and the elongation at break A80 in % of the formable lightweight steel according to the formulas: Rm=322.7{C}+103{Si}+847.6{Cr}+55{Al}+195.8{Cr}{C}?15{C}{Cr}2 Rp=132{Si}101.8{Cr}+60.6{Al}+91{Cr}{C}?11.9{Cr}2 A80=24+46.5{Si}+48{C}2?7.9{Cr}{C}?8.8{Al}{Si}, wherein the following content limits are to be observed: C <0.6%, Si >0.4 to 1.2, Al: 1 to <9% and Cr: ≤10%;for a third given composition of said formable lightweight steel in which Mn: >22% to 35%, calculating the strength Rm and Rp in MPa and the elongation at break A80 in % of the formable lightweight steel according to the formulas: Rm=104.3{Cr}+2766.6{Si}2+11.7{Al}2?172.8{Cr}{Si}?282.3{Al}{Si}2 Rp=3269{Si}+234.2{Cr}335.6{Al}{C}?1266.5?188.4{Al}{Si}?1391.6{Cr}{Si}{C}A80=33.5+88.7{Si}{C}?2.1{Cr}?4.5{Al}{C}?36{Si}2 wherein the following content limits are to observed: C: 0.2 to 0.7%, Si: 0.3 to 1.5%, and a sum of Al+Cr: ≥12%,wherein absolute numbers without dimension are inserted into the formulas and the unit MPa for Rm and Rp and % for A80 are assigned to the dimensionless values; and producing a hot strip with any of the first, second and third given composition by casting a melt in a horizontal strip casting system in the absence of bending into a pre-strip with a thickness in the range between 6 and 30 mm, and rolling the pre-strip into a hot strip with a degree of deformation of at least 50%.
변형가능한 경량강을 위해 설정되는 특성의 조합을 계산하기 위한 방법본 발명은 망가니즈 함유량에 기초한 특정 식을 사용하여 C 0.02 내지 1.0 이하, Al 2.5 내지 8.0 이하, Si 0.0 내지 1.5 이하, Mn 5.0 이상 35.0 이하, Cr 1.0 초과 14.0 이하, N + S + P ≤ 0.1, 잔부의 철, 및 기타 강-수반 원소인 Cu + Mo + Ni + Zn ≤ 1.0(중량%)의 원소를 갖는 변형가능한 경량강을 위한 사전정의된 합금 조성의 설정된 상 성분 및 기계적 특성의 특성의 조합을 계산하기 위한 방법에 관한 것으로, 이 식에서 합금 함유량은 무차원의 절대수로서 사용되고, 계산된 무차원의 값은 Rm 및 Rp의 경우에는 MPa 단위를, 그리고 A80의 경우에는 %가 할당된다. 본 발명은 또한 열간 압연 스트립을 형성하기 위해 사전정의된 합금 조성을 갖는 제조된 경량강을 추가로 가공처리하기 위한 방법에 관한 것이다.성형가능한 경량강을 위한 소정의 합금 조성의 상 비율 및 기계적 특성의 최종적인 특성의 조합을 계산하기 위한 방법으로서, 상기 합금 조성은 중량%로, C 0.02 내지 1.0 이하Al 2.5 내지 8.0 이하Si 0.0 내지 1.5 이하Mn 5.0 내지 35.0 이하Cr 1.0 초과 14.0 이하N + S + P ≤ 0.1,잔부의 철, 및가능한 함유량의 강에 수반되는 기타 원소 Cu + Mo + Ni + Zn ≤ 1.0 중량%를 함유하고,상기 경량강은 오스테나이트와 페라이트(A/F)의 상 혼합물로 이루어지고, 오스테나이트의 비율은 100% 내지 5%이고, 강도(Rm)는 600 내지 1200 MPa이고, 항복강도(Rp0.2)는 300 내지 1120 MPa이고, 파단신율(A80)은 5 내지 40%이고, 망가니즈 함유량에 관한 다음의 의존도 식에 따라, 무차원의 절대수가 다음의 식에 삽입되고, Rm 및 Rp의 경우에는 MPa 단위가, 그리고 A80의 경우에는 %가 상기 무차원 값에 할당되고, 5 내지 최대 11%의 Mn 함유량에 대해서는 다음의 식이 적용되고,[이미지] Rm = 3182{C}+1224{Si}+847.6{Cr}+633.2{Al}-3354.8-140.7{Al}{Cr}-482.5{Cr}{C}-1372.3{Si}2[이미지] Rp = 2509,2{C}+947{Si}+538{C}+367.8{Al}-2168.1-78.1{Al}{Cr}-381.9{Cr}{C}-923.2{Si}2[이미지] A80 = 267.4+48{Al}{C}-2.6{Cr}-16.8{Si}-41.1{Al}-275.4{C}다음의 함유량 한계가 중량%로서 관측되고,C: 0.2 내지 0.7Si ≤ 1.0Al + Cr ≤ 1211 초과 최대 22%의 Mn 함유량에 대해서는 다음의 식이 적용되고,[이미지] Rm = 322.7{C}+103{Si}+847.6{Cr}+55{Al}+195.8{Cr}{C}-15{C}{Cr}2[이미지] Rp = 132{Si}101.8{Cr}+60.6{Al}+91{Cr}{C}-11.9{Cr}2[이미지] A80 = 24+46.5{Si}+48{C}2-7.9{Cr}{C}-8.8{Al}{Si}다음의 함유량 한계가 중량%로서 관측되고,C: 0.6 미만Si: 0.4 내지 1.2Al: 1 내지 9Cr: 10 이하22 초과 최대 35%의 Mn 함유량에 대해서는 다음의 식이 적용되고,[이미지] Rm = 104.3{Cr}+2766.6{Si}2+11.7{Al}2-172.8{Cr}{Si}-282.3{Al}{Si}2[이미지] Rp = 3269{Si}+234.2{Cr}335.6{Al}{C}-1266.5-188.4{Al}{Si}-1391.6{Cr}{Si}{C}[이미지] A80 = 33.5+88.7{Si}{C}-2.1{Cr}-4.5{Al}{C}-36{Si}2다음의 함유량 한계가 중량%로서 관측되는,C: 0.2 내지 0.7Si: 0.3 내지 1.5Al + Cr ≤ 12경량강의 특성 조합을 계산하는 방법.