Reinforced Thermoplastic Resin Composition And Molded ArticleA reinforced thermoplastic resin composition including: a polycarbonate resin (A); a graft copolymer (B) obtained by polymerizing a monomer mixture including an aromatic alkenyl compound monomer (a) and a vinyl cyanide compound monomer (b) in the presence of a rubbery polymer (B1); a glass fiber (D) which is surface-treated with a water-soluble polyurethane and which has a ratio between a major axis and a minor axis in a fiber cross section of at least 2; a glycidyl ether unit-containing polymer (E) which includes a glycidyl ether unit and has a mass average molecular weight of 3,800 to 60,000; a phosphoric acid ester-based flame retardant (F1) having a mass average molecular weight of 300 to 430; a phosphoric acid ester-based flame retardant (F2) having a mass average molecular weight of 550 to 692; and a sulfonic acid metal salt (G), wherein a content ratio of the component (A) is from 93 to 99% by mass and a content ratio of the component (B) is from 1 to 7% by mass with respect to a total mass of 100% by mass of the component (A) and the component (B); a content ratio of the component (D) is from 30 to 50% by mass with respect to a total mass of 100% by mass of the component (A), the component (B), the component (D), the component (E), the component (F1), the component (F2) and the component (G); and with respect to a total of 100 parts by mass of the component (A) and the component (B), a content of the component (E) is from 1 to 10 parts by mass, a content of the component (F1) is from 0.5 to 5 parts by mass, a content of the component (F2) is from 19.5 to 25 parts by mass, a total of the contents of the component (F1) and the component (F2) is from 21 to 29 parts by mass, and a content of the component (G) is from 0.03 to 0.5 parts by mass.A reinforced thermoplastic resin composition comprising: a polycarbonate resin (A);a graft copolymer (B) obtained by polymerizing a monomer mixture including an aromatic alkenyl compound monomer (a) and a vinyl cyanide compound monomer (b) in the presence of a rubbery polymer (B1);a glass fiber (D) which is surface-treated with a water-soluble polyurethane and which has a ratio between a major axis and a minor axis ((major axis)/(minor axis)) on a fiber cross section of at least 2 and not more than 6;a glycidyl ether unit-containing polymer (E) which includes a glycidyl ether unit and has a mass average molecular weight of 3,800 to 60,000 (with a proviso that said graft copolymer (B) is excluded);a phosphoric acid ester-based flame retardant (F1) having a mass average molecular weight of 300 to 430;a phosphoric acid ester-based flame retardant (F2) having a mass average molecular weight of 550 to 692; anda sulfonic acid metal salt (G),wherein a content ratio of said polycarbonate resin (A) is from 93 to 99% by mass with respect to a total mass of 100% by mass of said polycarbonate resin (A) and said graft copolymer (B),a content ratio of said graft copolymer (B) is from 1 to 7% by mass with respect to a total mass of 100% by mass of said polycarbonate resin (A) and said graft copolymer (B),a content ratio of said glass fiber (D) is from 30 to 50% by mass with respect to a total mass of 100% by mass of said polycarbonate resin (A), said graft copolymer (B), said glass fiber (D), said glycidyl ether unit-containing polymer (E), said phosphoric acid ester-based flame retardant (F1), said phosphoric acid ester-based flame retardant (F2) and said sulfonic acid metal salt (G),a content of said glycidyl ether unit-containing polymer (E) is from 1 to 10 parts by mass with respect to a total of 100 parts by mass of said polycarbonate resin (A) and said graft copolymer (B),a content of said phosphoric acid ester-based flame retardant (F1) is from 0.5 to 5 parts by mass with respect to a total of 100 parts by mass of said polycarbonate resin (A) and said graft copolymer (B),a content of said phosphoric acid ester-based flame retardant (F2) is from 19.5 to 25 parts by mass with respect to a total of 100 parts by mass of said polycarbonate resin (A) and said graft copolymer (B),a total of the content of said phosphoric acid ester-based flame retardant (F1) and the content of said phosphoric acid ester-based flame retardant (F2) is from 21 to 29 parts by mass with respect to a total of 100 parts by mass of said polycarbonate resin (A) and said graft copolymer (B), anda content of said sulfonic acid metal salt (G) is from 0.03 to 0.5 parts by mass with respect to a total of 100 parts by mass of said polycarbonate resin (A) and said graft copolymer (B).
강화 열가소성 수지 조성물 및 성형품폴리카보네이트(polycarbonate) 수지(A); 고무질 중합체(B1)의 존재하에, 방향족 알케닐 화합물 단량체(a) 및 시안화 비닐 화합물 단량체(b)를 포함한 단량체 혼합물을 중합하여 얻어지는 그라프트 공중합체(B); 수용성 폴리우레탄으로 표면 처리되고 섬유 단면에 있어서의 장경과 단경과의 비가 2 이상인 유리 섬유(D); 글리시딜 에테르 단위를 가지고, 질량 평균 분자량이 3,800 ~ 60,000인 글리시딜 에테르 단위 함유 중합체(E); 질량 평균 분자량이 300 ~ 430인 인산 에스테르계 난연제(F1); 질량 평균 분자량이 550 ~ 692인 인산 에스테르계 난연제(F2); 및 설폰산 금속염(G)을 함유하고, (A)성분과 (B)성분의 합계 질량 100 질량%에 대해, (A)성분의 함유량의 비율이 93 ~ 99 질량%이며, (B)성분의 함유량의 비율이 1 ~ 7 질량%이며, (D)성분의 함유량의 비율이, (A)성분, (B)성분, (D)성분, (E)성분, (F1)성분, (F2)성분, 및 (G)성분의 합계 질량 100질량%에 대해, 30 ~ 50%이며, (A)성분과 (B)성분의 합계 100 질량부에 대해서, (E)성분의 함유량이 1 ~ 10 질량부이며, (F1)성분의 함유량이 0.5 ~ 5 질량부이며, (F2)성분의 함유량이 19.5 ~ 25 질량부이며, (F1)성분과 (F2)성분의 함유량의 합계가 21 ~ 29 질량부이며, (G)성분의 함유량이 0.03 ~ 0.5 질량부인 것을 특징으로 하는 강화 열가소성 수지 조성물.폴리카보네이트(polycarbonate) 수지(A);고무질 중합체(B1)의 존재 하에, 방향족 알케닐 화합물 단량체(a) 및 시안화 비닐 화합물 단량체(b)를 포함한 단량체 혼합물을 중합하여 얻어지는 그라프트 공중합체(B);수용성 폴리우레탄으로 표면 처리되고, 섬유 단면에 있어서의 장경과 단경의 비(장경/단경)가 2 이상 내지 6 이하인 유리 섬유(D);글리시딜 에테르 단위를 가지고, 질량 평균 분자량이 3,800 ~ 60,000인 글리시딜 에테르 단위 함유 중합체(E)(단, 상기 그라프트 공중합체(B)를 제외함);질량 평균 분자량이 300 ~ 430인 인산 에스테르계 난연제(F1);질량 평균 분자량이 550 ~ 692인 인산 에스테르계 난연제(F2); 및설폰산 금속염(G);을 함유하고,상기 폴리카보네이트 수지(A)의 함유량의 비율이, 상기 폴리카보네이트 수지(A)와 상기 그라프트 공중합체(B)의 합계 질량 100 질량%에 대해, 93 ~ 99 질량%이며,상기 그라프트 공중합체(B)의 함유량의 비율이, 상기 폴리카보네이트 수지(A)와 상기 그라프트 공중합체(B)의 합계 질량 100 질량%에 대해, 1 ~ 7 질량%이고,상기 유리 섬유(D)의 함유량의 비율이, 상기 폴리카보네이트 수지(A), 상기 그라프트 공중합체(B), 상기 유리 섬유(D), 상기 글리시딜 에테르 단위 함유 중합체(E), 상기 인산 에스테르계 난연제(F1), 상기 인산 에스테르계 난연제(F2), 및 상기 설폰산 금속염(G)의 합계 질량 100 질량%에 대해, 30 ~ 50 질량%이며,상기 글리시딜 에테르 단위 함유 중합체(E)의 함유량이, 상기 폴리카보네이트 수지(A)와 상기 그라프트 공중합체(B)의 합계 100 질량부에 대해, 1 ~ 10 질량부이고,상기 인산 에스테르계 난연제(F1)의 함유량이, 상기 폴리카보네이트 수지(A)와 상기 그라프트 공중합체(B)의 합계 100 질량부에 대해, 0.5 ~ 5 질량부이며,상기 인산 에스테르계 난연제(F2)의 함유량이, 상기 폴리카보네이트 수지(A)와 상기 그라프트 공중합체(B)의 합계 100 질량부에 대해, 19.5 ~ 25 질량부이고,상기 인산 에스테르계 난연제(F1)의 함유량과 상기 인산 에스테르계 난연제(F2)의 함유량의 합계가, 상기 폴리카보네이트 수지(A)와 상기 그라프트 공중합체(B)의 합계 100 질량부에 대해, 21 ~ 29 질량부이며,상기 설폰산 금속염(G)의 함유량이, 상기 폴리카보네이트 수지(A)와 상기 그라프트 공중합체(B)의 합계 100 질량부에 대해, 0.03 ~ 0.5 질량부인 것을 특징으로 하는 강화 열가소성 수지 조성물.