STRETCH MATERIALA stretch material comprises a thermoplastic polymer material that meets the following conditions: (i) it contains: (a) 100 parts by mass of a hydrogenated block copolymer having a number average molecular weight of 50,000 to 140,000 and including at least two polymer blocks (A) composed mainly of a vinyl aromatic compound and at least one hydrogenated polymer block (B) composed mainly of a conjugated diene compound, wherein the amount of the polymer block (A) is in the range of 10 to 40% by mass, and 50% or more of the double bonds present in the copolymer block (B) that originate from the conjugated diene compound are hydrogenated; (b) 0 to 120 parts by mass of a non-aromatic rubber softening agent; (c) 0 to 80 parts by mass of polyethylene that has an MFR of 15g/10min or above when measured at 190°C under a load of 2.16kg; and (d) 0 to 40 parts by mass of polystyrene that has an MFR of 5g/10min or above when measured at 200°C under a load of 5.00kg; (ii) it has a residual strain of 15% or less after having stretched to 150% elongation at 25°C in a stretch test; (iii) it has a permanent tensile set of 10% or less when the thermoplastic material is stretched by 100% elongation, held stretched for 120 minutes at 25°C, released and then left for 30 minutes; (iv) it shows a 15% or less deviation in the value of the melt tension when tested in a melt tension test performed under a temperature condition that allows an MFR of 5 to 15g/10min; and (v) it melts and breaks when wound at a winding speed of 60m/min or more in a melt tension test performed under a temperature condition that allows an MFR of 5 to 15g/10min. This stretch material exhibits a good processability and a good stress relaxation property, bears a small residual strain, and is as nearly as stretchable and flexible as vulcanized rubber. Also safe and clean, the stretch material of the present invention is particularly suitable for use in disposable diapers, sanitary products, and other various medical products.A stretch material comprising a thermoplastic polymer material that meets the following conditions:(i) it contains:(a) 100 parts by mass of a hydrogenated block copolymer having a number average molecular weight of 50,000 to 140,000 and including at least two polymer blocks (A) composed mainly of a vinyl aromatic compound and at least one hydrogenated polymer block (B) composed mainly of a conjugated diene compound, wherein the amount of the polymer block (A) is in the range of 10 to 40% by mass, and 50% or more of the double bonds present in the copolymer block (B) that originate from the conjugated diene compound are hydrogenated;(b) 0 to 120 parts by mass of a non-aromatic rubber softening agent;(c) 0 to 80 parts by mass of polyethylene that has an MFR of 15g/10min or above when measured at 190°C under a load of 2.16kg; and(d) 0 to 40 parts by mass of polystyrene that has an MFR of 5g/10min or above when measured at 200°C under a load of 5.00kg; (ii) it has a residual strain of 15% or less after having stretched to 150% elongation at 25°C in a stretch test;(iii) it has a permanent tensile set of 10% or less when the thermoplastic material is stretched by 100% elongation, held stretched for 120 minutes at 25°C, released and then left for 30 minutes;(iv) it shows a 15% or less deviation in the value of the melt tension when tested in a melt tension test performed under a temperature condition that allows an MFR of 5 to 15g/10min; and(v) it melts and breaks when wound at a winding speed of 60m/min or more in a melt tension test performed under a temperature condition that allows an MFR of 5 to 15g/10min.
신축성 재료(ⅰ) 성분 (A) 함량은 10 내지 40 질량% 범위이고, 2 이상의 비닐 방향족 중합체 블록 (A) 및 1 이상의 공액 디엔 중합체 블록 (B)를 갖고, 50,000 내지 140,000의 수평균 분자량을 가지는 수소화 블록 공중합체 100 질량부(성분 수소화율은 50% 이상이다); 비방향족 고무 연화제 0 내지 120 질량부; 2.16kg의 하중, 190 ℃ 에서 15g/10분 이상의 MFR을 나타내는 폴리에틸렌 0 내지 80 질량부; 및 5.00kg의 하중, 200 ℃에서 5g/10분 이상의 MFR을 나타내는 폴리스티렌 0 내지 40 질량부를 함유하고, (ii) 25。C에서 150 % 로 신장 시험 후에, 15 % 이하의 잔류 비틀림을 나타내고, (iii) 25。C에서 120 분 동안 100 % 신장 후에, 30분이 지나서 10% 이하의 영구 인장 변형을 나타내고, (iv) 5 내지 15 g/10분의 MFR을 나타내는 온도 조건 하에서 수행된 용융 장력 시험에서, 15 % 이하의 용융 장력 진폭을 나타내고, (v) 5 내지 15 g/10분의 MFR을 나타내는 온도 조건 하에서 수행된 용융 장력시험에서, 60m/분 이상의 용융 부분 정격(take-up)속도를 나타내는 것을 특징으로 하는 신축성 재료.하기의 조건을 만족하는 열가소성 중합체 재료를 함유하는 신축성 재료: (i) 하기를 함유하며: (a) 수평균 분자량이 50,000 내지 140,000 이고, 주로 비닐 방향족 화합물로 구성된 2 이상의 중합체 블록 (A) 및 주로 공액 디엔 화합물로 구성된 1 이상의 수소화 중합체 블록 (B)를 포함하는 수소화 블록 공중합체 100 질량부(여기서, 중합체 블록 (A) 함량은 10 내지 40 질량 % 범위이고, 공액 디엔 화합물로부터 유래된 중합체 블록 (B) 에 존재하는 이중 결합의 50% 이상이 수소화된다); (b) 비방향족 고무 연화제 0 내지 120 질량부; (c) 2.16kg의 하중, 190 ℃ 에서 측정시 15 g/10분 이상의 MFR을 가지는 폴리에틸렌 0 내지 80 질량부; 및 (d) 5.00kg의 하중, 200 ℃에서 측정시 5 g/10분 이상의 MFR을 가지는 폴리스티렌 0 내지 40 질량부; (ii) 신축성 시험에서 25。C에서 150 % 로 신장한 후에, 15 % 이하의 잔류 비틀림을 가지며; (iii) 열가소성 재료를 25。C에서 100 % 신장하여 120 분 동안 유지한 후, 이완하여 30분 간 그 상태로 유지할 때, 10% 이하의 영구 인장 변형을 가지며; (iv) MFR이 5 내지 15 g/10분을 나타내는 온도 조건 하에서 수행된 용융 장력 시험에서 측정시, 용융 장력 값의 15 % 이하의 진폭을 나타내고; (v) MFR이 5 내지 15 g/10분을 나타내는 온도 조건 하에서 수행된 용융 장력시험에서 60m/분 이상의 권취 속도로 감았을 때, 용융 및 파단된다.